JP6448462B2 - Anode active material for nonaqueous electrolyte secondary battery, nonaqueous electrolyte secondary battery, and method for producing anode active material for nonaqueous electrolyte secondary battery - Google Patents

Anode active material for nonaqueous electrolyte secondary battery, nonaqueous electrolyte secondary battery, and method for producing anode active material for nonaqueous electrolyte secondary battery Download PDF

Info

Publication number
JP6448462B2
JP6448462B2 JP2015101328A JP2015101328A JP6448462B2 JP 6448462 B2 JP6448462 B2 JP 6448462B2 JP 2015101328 A JP2015101328 A JP 2015101328A JP 2015101328 A JP2015101328 A JP 2015101328A JP 6448462 B2 JP6448462 B2 JP 6448462B2
Authority
JP
Japan
Prior art keywords
active material
negative electrode
electrode active
cyclic carbonate
secondary battery
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2015101328A
Other languages
Japanese (ja)
Other versions
JP2016219190A (en
Inventor
貴一 廣瀬
貴一 廣瀬
博道 加茂
博道 加茂
吉川　博樹
博樹 吉川
拓史 松野
拓史 松野
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shin Etsu Chemical Co Ltd
Original Assignee
Shin Etsu Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shin Etsu Chemical Co Ltd filed Critical Shin Etsu Chemical Co Ltd
Priority to JP2015101328A priority Critical patent/JP6448462B2/en
Priority to PCT/JP2016/002013 priority patent/WO2016185663A1/en
Priority to TW105112574A priority patent/TW201709593A/en
Publication of JP2016219190A publication Critical patent/JP2016219190A/en
Application granted granted Critical
Publication of JP6448462B2 publication Critical patent/JP6448462B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、非水電解質二次電池用負極活物質に関する。また、本発明は、この負極活物質を含む非水電解質二次電池にも関する。さらに、本発明は、非水電解質二次電池用負極材の製造方法にも関する。   The present invention relates to a negative electrode active material for a non-aqueous electrolyte secondary battery. Moreover, this invention relates also to the nonaqueous electrolyte secondary battery containing this negative electrode active material. Furthermore, this invention relates also to the manufacturing method of the negative electrode material for nonaqueous electrolyte secondary batteries.

近年、モバイル端末などに代表される小型の電子機器が広く普及しており、さらなる小型化、軽量化及び長寿命化が強く求められている。このような市場要求に対し、特に小型かつ軽量で高エネルギー密度を得ることが可能な二次電池の開発が進められている。この二次電池は、小型の電子機器に限らず、自動車などに代表される大型の電子機器、家屋などに代表される電力貯蔵システムへの適用も検討されている。   In recent years, small electronic devices typified by mobile terminals have been widely used, and further downsizing, weight reduction, and long life have been strongly demanded. In response to such market demands, development of secondary batteries capable of obtaining a high energy density, in particular, being small and light is underway. This secondary battery is not limited to a small electronic device, but is also considered to be applied to a large-sized electronic device represented by an automobile or the like, or an electric power storage system represented by a house.

その中でも、リチウムイオン二次電池は小型かつ高容量化が行いやすく、また、鉛電池、ニッケルカドミウム電池よりも高いエネルギー密度が得られるため、大いに期待されている。   Among them, lithium ion secondary batteries are highly expected because they are small and easy to increase in capacity, and can obtain higher energy density than lead batteries and nickel cadmium batteries.

上記のリチウムイオン二次電池は、正極および負極、セパレータと共に電解液を備えており、負極は充放電反応に関わる負極活物質を含んでいる。   Said lithium ion secondary battery is equipped with the electrolyte solution with the positive electrode, the negative electrode, and the separator, and the negative electrode contains the negative electrode active material in connection with charging / discharging reaction.

この負極活物質としては、炭素材料が広く使用されている一方で、最近の市場要求から電池容量のさらなる向上が求められている。電池容量向上のために、負極活物質材としてケイ素を用いることが検討されている。なぜならば、ケイ素の理論容量（４１９９ｍＡｈ／ｇ）は黒鉛の理論容量（３７２ｍＡｈ／ｇ）よりも１０倍以上大きいため、電池容量の大幅な向上を期待できるからである。負極活物質材としてのケイ素材の開発はケイ素単体だけではなく、合金、酸化物に代表される化合物などについても検討されている。また、活物質形状は、炭素材では標準的な塗布型から、集電体に直接堆積する一体型まで検討されている。   As this negative electrode active material, a carbon material is widely used, but further improvement in battery capacity is required due to recent market demand. In order to improve battery capacity, use of silicon as a negative electrode active material has been studied. This is because the theoretical capacity of silicon (4199 mAh / g) is 10 times or more larger than the theoretical capacity of graphite (372 mAh / g), so that significant improvement in battery capacity can be expected. The development of a siliceous material as a negative electrode active material has been examined not only for silicon itself but also for compounds represented by alloys and oxides. In addition, the shape of the active material has been studied from a standard coating type for carbon materials to an integrated type directly deposited on a current collector.

しかしながら、負極活物質としてケイ素を主原料として用いると、充放電時に負極活物質が膨張及び収縮するため、主に負極活物質表層近傍で割れやすくなる。また、活物質内部にイオン性物質が生成し、負極活物質が割れやすい物質となる。負極活物質表層が割れると、それによって新表面が生じ、活物質の反応面積が増加する。この時、新表面において電解液の分解反応が生じるとともに、新表面に電解液の分解物である被膜が形成されるため電解液が消費される。このためサイクル特性が低下しやすくなる。   However, when silicon is used as the negative electrode active material as the main raw material, the negative electrode active material expands and contracts during charge and discharge, and therefore, it tends to break mainly near the surface of the negative electrode active material. Further, an ionic material is generated inside the active material, and the negative electrode active material is easily broken. When the negative electrode active material surface layer is cracked, a new surface is generated thereby increasing the reaction area of the active material. At this time, a decomposition reaction of the electrolytic solution occurs on the new surface, and a coating that is a decomposition product of the electrolytic solution is formed on the new surface, so that the electrolytic solution is consumed. For this reason, the cycle characteristics are likely to deteriorate.

これまでに、電池初期効率やサイクル特性を向上させるために、ケイ素材を主材としたリチウムイオン二次電池用負極材料、電極構成についてさまざまな検討がなされている。   To date, various studies have been made on negative electrode materials and electrode configurations for lithium ion secondary batteries mainly composed of a siliceous material in order to improve battery initial efficiency and cycle characteristics.

具体的には、良好なサイクル特性や高い安全性を得る目的で、気相法を用いケイ素及びアモルファス二酸化ケイ素を同時に堆積させている（例えば特許文献１参照）。また、高い電池容量や安全性を得るために、ケイ素酸化物粒子の表層に炭素材（電子伝導材）を設けている（例えば特許文献２参照）。さらに、サイクル特性を改善するとともに高入出力特性を得るために、ケイ素及び酸素を含有する活物質を作製し、かつ、集電体近傍での酸素比率が高い活物質層を形成している（例えば特許文献３参照）。また、サイクル特性を向上させるために、ケイ素活物質中に酸素を含有させ、平均酸素含有量が４０ａｔ％以下であり、かつ集電体に近い場所で酸素含有量が多くなるように形成している（例えば特許文献４参照）。   Specifically, for the purpose of obtaining good cycle characteristics and high safety, silicon and amorphous silicon dioxide are deposited simultaneously using a vapor phase method (see, for example, Patent Document 1). Further, in order to obtain a high battery capacity and safety, a carbon material (electron conductive material) is provided on the surface layer of the silicon oxide particles (see, for example, Patent Document 2). Furthermore, in order to improve cycle characteristics and obtain high input / output characteristics, an active material containing silicon and oxygen is produced, and an active material layer having a high oxygen ratio in the vicinity of the current collector is formed ( For example, see Patent Document 3). Further, in order to improve the cycle characteristics, oxygen is contained in the silicon active material, the average oxygen content is 40 at% or less, and the oxygen content is increased at a location close to the current collector. (For example, refer to Patent Document 4).

また、初回充放電効率を改善するためにＳｉ相、ＳｉＯ２、ＭｙＯ金属酸化物を含有するナノ複合体を用いている（例えば特許文献５参照）。また、サイクル特性改善のため、ＳｉＯｘ（０．８≦ｘ≦１．５、粒径範囲＝１μｍ〜５０μｍ）と炭素材を混合して高温焼成している（例えば特許文献６参照）。また、サイクル特性改善のために、負極活物質中におけるケイ素に対する酸素のモル比を０．１〜１．２とし、活物質、集電体界面近傍におけるモル比の最大値、最小値との差が０．４以下となる範囲で活物質の制御を行っている（例えば特許文献７参照）。また、電池負荷特性を向上させるため、リチウムを含有した金属酸化物を用いている（例えば特許文献８参照）。また、サイクル特性を改善させるために、ケイ素材表層にシラン化合物などの疎水層を形成している（例えば特許文献９参照）。 Further, Si phase, (for example, see Patent Document 5) by using a nanocomposite containing SiO 2, M y O metal oxide in order to improve the initial charge and discharge efficiency. In order to improve cycle characteristics, SiO x (0.8 ≦ x ≦ 1.5, particle size range = 1 μm to 50 μm) and a carbon material are mixed and fired at a high temperature (see, for example, Patent Document 6). Further, in order to improve cycle characteristics, the molar ratio of oxygen to silicon in the negative electrode active material is set to 0.1 to 1.2, and the difference between the maximum value and the minimum value of the molar ratio in the vicinity of the active material and current collector interface The active material is controlled within a range of 0.4 or less (see, for example, Patent Document 7). Further, in order to improve battery load characteristics, a metal oxide containing lithium is used (see, for example, Patent Document 8). Further, in order to improve cycle characteristics, a hydrophobic layer such as a silane compound is formed on the surface layer of the siliceous material (see, for example, Patent Document 9).

また、サイクル特性改善のため、酸化ケイ素を用い、その表層に黒鉛被膜を形成することで導電性を付与している（例えば特許文献１０参照）。特許文献１０において、黒鉛被膜に関するラマンスペクトルから得られるシフト値に関して、１３３０ｃｍ−１及び１５８０ｃｍ−１にブロードなピークが現れるとともに、それらの強度比Ｉ１３３０／Ｉ１５８０が１．５＜Ｉ１３３０／Ｉ１５８０＜３となっている。また、高い電池容量、サイクル特性の改善のため、二酸化ケイ素中に分散されたケイ素微結晶相を有する粒子を用いている（例えば、特許文献１１参照）。また、過充電、過放電特性を向上させるために、ケイ素と酸素の原子数比を１：ｙ（０＜ｙ＜２）に制御したケイ素酸化物を用いている（例えば特許文献１２参照）。また、高い電池容量、サイクル特性の改善のため、ケイ素と炭素の混合電極を作成しケイ素比率を５ｗｔ％以上１３ｗｔ％以下で設計している（例えば、特許文献１３参照）。 Further, in order to improve cycle characteristics, conductivity is imparted by using silicon oxide and forming a graphite film on the surface layer (see, for example, Patent Document 10). In Patent Document 10, with respect to the shift value obtained from the Raman spectra for graphite coating, with broad peaks appearing at 1330 cm -1 and 1580 cm -1, their intensity ratio I 1330 / I 1580 is 1.5 <I 1330 / I 1580 <3. In addition, particles having a silicon microcrystalline phase dispersed in silicon dioxide are used in order to improve high battery capacity and cycle characteristics (see, for example, Patent Document 11). Further, in order to improve overcharge and overdischarge characteristics, silicon oxide in which the atomic ratio of silicon and oxygen is controlled to 1: y (0 <y <2) is used (see, for example, Patent Document 12). In addition, in order to improve high battery capacity and cycle characteristics, a mixed electrode of silicon and carbon is prepared and the silicon ratio is designed to be 5 wt% or more and 13 wt% or less (see, for example, Patent Document 13).

特開２００１−１８５１２７号公報JP 2001-185127 A 特開２００２−０４２８０６号公報JP 2002-042806 A 特開２００６−１６４９５４号公報JP 2006-164955 A 特開２００６−１１４４５４号公報JP 2006-114454 A 特開２００９−０７０８２５号公報JP 2009-070825 A 特開２００８−２８２８１９号公報JP 2008-282819 A 特開２００８−２５１３６９号公報JP 2008-251369 A 特開２００８−１７７３４６号公報JP 2008-177346 A 特開２００７−２３４２５５号公報JP 2007-234255 A 特開２００９−２１２０７４号公報JP 2009-212074 A 特開２００９−２０５９５０号公報JP 2009-205950 A 特許第２９９７７４１号明細書Japanese Patent No. 2,997,741 特開２０１０−０９２８３０号公報JP 2010-092830 A

上述したように、近年、モバイル端末などに代表される小型の電子機器は高性能化、多機能化がすすめられており、その主電源であるリチウムイオン二次電池は電池容量の増加が求められている。この問題を解決する１つの手法として、ケイ素材を主材として用いた負極からなるリチウムイオン二次電池の開発が望まれている。   As described above, in recent years, small electronic devices typified by mobile terminals and the like have been improved in performance and multifunction, and the lithium ion secondary battery as the main power source is required to increase the battery capacity. ing. As one method for solving this problem, development of a lithium ion secondary battery composed of a negative electrode using a siliceous material as a main material is desired.

また、ケイ素材を用いたリチウムイオン二次電池は、炭素材を用いたリチウムイオン二次電池と同等に近い電池特性が望まれている。そこで、Ｌｉの挿入、脱離により改質されたケイ素酸化物を負極活物質として使用することで、電池のサイクル維持率、及び初回効率を改善してきた。しかしながら、改質後のケイ素酸化物はＬｉを用いて改質されたため、耐水性が低い。そのため、負極の製造時に作製する、上記改質後のケイ素酸化物を含むスラリーの安定化が不十分となり、炭素系活物質の塗布に従来から一般的に使われている装置等を使用することができない、または使用しづらいという問題があった。このように、Ｌｉを用いた改質によって、初期効率及びサイクル維持率を改善したケイ素酸化物を使用する場合、水を含むスラリーの安定性が不十分となるため、二次電池の工業的な生産において優位な非水電解質二次電池用負極活物質を提案するには至っていなかった。   Moreover, the lithium ion secondary battery using a siliceous material is desired to have a battery characteristic close to that of a lithium ion secondary battery using a carbon material. Thus, the use of silicon oxide modified by insertion and desorption of Li as the negative electrode active material has improved the cycle retention rate and initial efficiency of the battery. However, since the modified silicon oxide has been modified using Li, its water resistance is low. For this reason, the slurry containing the modified silicon oxide prepared at the time of manufacturing the negative electrode is not sufficiently stabilized, and an apparatus generally used for coating a carbon-based active material must be used. There was a problem that could not be used or was difficult to use. As described above, when using silicon oxide whose initial efficiency and cycle retention ratio are improved by modification with Li, the stability of the slurry containing water becomes insufficient. A negative electrode active material for a non-aqueous electrolyte secondary battery superior in production has not been proposed.

本発明は、上記問題点に鑑みてなされたものであって、水系スラリーに対する安定性が高く、高容量であるとともに、サイクル特性及び初回効率が良好な非水電解質二次電池用負極活物質を提供することを目的とする。   The present invention has been made in view of the above problems, and provides a negative electrode active material for a non-aqueous electrolyte secondary battery that has high stability with respect to an aqueous slurry, high capacity, and excellent cycle characteristics and initial efficiency. The purpose is to provide.

上記目的を達成するために、本発明は、負極活物質粒子を有し、該負極活物質粒子はＬｉ化合物が含まれるケイ素化合物（ＳｉＯｘ：０．５≦ｘ≦１．６）を含有するものである非水電解質二次電池用負極活物質であって、前記負極活物質粒子が、環状カーボネートを含む環状カーボネート層を表面に有し、該環状カーボネート層が、さらにＬｉ塩を含むものであることを特徴とする非水電解質二次電池用負極活物質を提供する。 In order to achieve the above object, the present invention has negative electrode active material particles, and the negative electrode active material particles contain a silicon compound containing a Li compound (SiO x : 0.5 ≦ x ≦ 1.6). A negative electrode active material for a non-aqueous electrolyte secondary battery, wherein the negative electrode active material particles have a cyclic carbonate layer containing a cyclic carbonate on the surface, and the cyclic carbonate layer further contains a Li salt. A negative electrode active material for a non-aqueous electrolyte secondary battery is provided.

本発明の負極活物質は、ケイ素化合物を含有する負極活物質粒子（以下、ケイ素系活物質粒子とも呼称する）が、その表面に、環状カーボネートからなり、Ｌｉ塩を含む環状カーボネート層を有しているので、水系スラリーに対しての耐水性が高いものとなる。また、従来、Ｌｉの挿入、脱離によって改質したケイ素酸化物を含む水系スラリーは、ｐＨがアルカリ側にふれやすかった。そのため、アルカリに比較的弱い増粘剤（結着剤）であるカルボキシメチルセルロース又はそのナトリウム塩等を安定して用いることができないため、スラリーが不安定化し易かった。しかしながら、本発明では、ケイ素系活物質粒子が、上記のようなＬｉ塩を含む環状カーボネート層を有することで、スラリーのｐＨがアルカリ側にふれにくくなり、特に増粘剤が変質しづらいことから、安定した塗膜を得る事ができ、結着性を十分に確保することができる。そのため、本発明の負極活物質を使用すれば、Ｌｉを用いて改質されたケイ素酸化物本来の特性を生かした高い電池容量及び良好なサイクル維持率を有する非水電解質二次電池を工業的な生産において優位に製造可能となる。   In the negative electrode active material of the present invention, negative electrode active material particles containing a silicon compound (hereinafter also referred to as silicon-based active material particles) have a cyclic carbonate layer made of cyclic carbonate and containing a Li salt on the surface thereof. Therefore, the water resistance against the aqueous slurry is high. Conventionally, aqueous slurries containing silicon oxide modified by Li insertion and desorption have been liable to touch the alkali side in pH. For this reason, carboxymethyl cellulose or a sodium salt thereof, which is a thickener (binder) that is relatively weak against alkali, cannot be used stably, so that the slurry is easily destabilized. However, in the present invention, since the silicon-based active material particles have the cyclic carbonate layer containing the Li salt as described above, the pH of the slurry becomes difficult to touch the alkali side, and in particular, the thickener is difficult to change. Thus, a stable coating film can be obtained, and sufficient binding properties can be secured. Therefore, if the negative electrode active material of the present invention is used, a non-aqueous electrolyte secondary battery having a high battery capacity and a good cycle maintenance ratio utilizing the original characteristics of silicon oxide modified with Li can be industrially produced. Manufacturing in an advantageous production.

このとき、前記環状カーボネート層に含まれるＬｉ塩が、ＬｉＰＦ６、ＬｉＢＦ４、ＬｉＣｌＯ４、ＬｉＢＯＢ（リチウムビスオキサレートボラート）、ＬｉＦＳＡ（リチウムビス（フルオロスルホニル）アミド）、ＬｉＴＦＳＡ（リチウム（トリフルオロメタンスルホニル）アミド）、及びＬｉＴＦＳＩ（リチウムビス（トリフルオロメタンスルホニル）イミド）のうち１種以上を含むものであることが好ましい。 At this time, the Li salt contained in the cyclic carbonate layer is LiPF 6 , LiBF 4 , LiClO 4 , LiBOB (lithium bisoxalate borate), LiFSA (lithium bis (fluorosulfonyl) amide), LiTFSA (lithium (trifluoromethane). (Sulfonyl) amide) and LiTFSI (lithium bis (trifluoromethanesulfonyl) imide) are preferably included.

環状カーボネート層に含まれるＬｉ塩として、具体的には上記のようなものが挙げられる。この中でも、特に、Ｌｉ塩として、ＬｉＰＦ６、ＬｉＢＦ４、ＬｉＣｌＯ４が環状カーボネート層に含まれることにより、スラリーがより安定する。 Specific examples of the Li salt contained in the cyclic carbonate layer include those described above. Among these, especially, as the Li salt, LiPF 6 , LiBF 4 , and LiClO 4 are contained in the cyclic carbonate layer, so that the slurry becomes more stable.

またこのとき、前記環状カーボネート層に含まれる環状カーボネートが、エチレンカーボネート、プロピレンカーボネート、フルオロエチレンカーボネート、ジフルオロエチレンカーボネート、及びビニレンカーボネートのうち１種以上を含むものであることが好ましい。   At this time, it is preferable that the cyclic carbonate contained in the cyclic carbonate layer contains one or more of ethylene carbonate, propylene carbonate, fluoroethylene carbonate, difluoroethylene carbonate, and vinylene carbonate.

上記のような環状カーボネートは常温で固体であるため、これらを含む環状カーボネート層であれば、より安定した耐水層となる。この中でも、エチレンカーボネート又はフルオロエチレンカーボネートを含む場合、特に安定した電池特性を得ることができる。   Since the cyclic carbonates as described above are solid at normal temperature, a cyclic carbonate layer containing these will provide a more stable water-resistant layer. Among these, when ethylene carbonate or fluoroethylene carbonate is included, particularly stable battery characteristics can be obtained.

このとき、前記環状カーボネート層の質量が、前記ケイ素化合物の質量に対し１５質量％以下のものであることが好ましい。   At this time, the mass of the cyclic carbonate layer is preferably 15% by mass or less based on the mass of the silicon compound.

上記のような割合で環状カーボネート層が形成されていれば、環状カーボネート層が厚くなり過ぎないため、負極活物質は高い導電性を有するものとなる。また、負極活物質中での環状カーボネート層の割合が適切な範囲内であるため、負極活物質は十分な量のケイ素化合物を含むことができ、高い電池容量を有するものとなる。   If the cyclic carbonate layer is formed at the above ratio, the cyclic carbonate layer does not become too thick, so that the negative electrode active material has high conductivity. Moreover, since the ratio of the cyclic carbonate layer in the negative electrode active material is within an appropriate range, the negative electrode active material can contain a sufficient amount of a silicon compound and has a high battery capacity.

またこのとき、前記環状カーボネート層が、さらに鎖状カーボネートを含むものであることが好ましい。   At this time, it is preferable that the cyclic carbonate layer further contains a chain carbonate.

環状カーボネート層に鎖状カーボネートが含まれることで、スラリーのｐＨがアルカリ側に、さらにふれ難くなる。   When the chain carbonate is contained in the cyclic carbonate layer, the pH of the slurry becomes more difficult to touch the alkali side.

このとき、前記負極活物質粒子は、前記ケイ素化合物と前記環状カーボネート層との間に、炭酸リチウム及びフッ化リチウムのうち１種以上を含むものであることが好ましい。   At this time, it is preferable that the negative electrode active material particles include at least one of lithium carbonate and lithium fluoride between the silicon compound and the cyclic carbonate layer.

このように、炭酸リチウム又はフッ化リチウムを、ケイ素化合物と環状カーボネート層の間の少なくとも一部に形成しておくことで、電池として充電する時に消費するＬｉ量を低減することができる。   Thus, by forming lithium carbonate or lithium fluoride in at least a part between the silicon compound and the cyclic carbonate layer, the amount of Li consumed when charging as a battery can be reduced.

またこのとき、前記ケイ素化合物に含まれるＬｉ化合物として、Ｌｉ２ＳｉＯ３、及びＬｉ４ＳｉＯ４のうち１種以上が存在するものであることが好ましい。 At this time, it is preferable that at least one of Li 2 SiO 3 and Li 4 SiO 4 is present as the Li compound contained in the silicon compound.

Ｌｉ２ＳｉＯ３、及びＬｉ４ＳｉＯ４のようなＬｉシリケートは、Ｌｉ化合物として比較的安定しているため、より良好な電池特性が得られる。 Since Li silicates such as Li 2 SiO 3 and Li 4 SiO 4 are relatively stable as Li compounds, better battery characteristics can be obtained.

このとき、前記負極活物質粒子が、前記ケイ素化合物の表面に炭素被膜を有するものであることが好ましい。   At this time, the negative electrode active material particles preferably have a carbon film on the surface of the silicon compound.

炭素被膜を有することで、負極活物質粒子の導電性が向上するため、より良好な電池特性が得られるものとなる。   By having the carbon coating, the conductivity of the negative electrode active material particles is improved, so that better battery characteristics can be obtained.

またこのとき、前記ケイ素化合物は、電気化学的手法によりＬｉが挿入、脱離されることで、改質されたものであることが好ましい。   At this time, it is preferable that the silicon compound is modified by inserting and removing Li by an electrochemical method.

電気化学的手法であれば、外部電位及び参照極などを用いる事で、ケイ素化合物の電位を制御しやすくなると共に、不必要な領域に挿入されたＬｉは放電過程を用いることで除去できる。そのためこのような手法で改質されたケイ素化合物は所望の特性を有するものとなる。   If it is an electrochemical method, it becomes easy to control the potential of the silicon compound by using an external potential and a reference electrode, and Li inserted in an unnecessary region can be removed by using a discharge process. Therefore, the silicon compound modified by such a method has desired characteristics.

このとき、前記ケイ素化合物が、Ｘ線回折により得られるＳｉ（１１１）結晶面に起因する回折ピークの半値幅（２θ）が１．２°以上であると共に、その結晶面に起因する結晶子サイズが７．５ｎｍ以下のものであることが好ましい。   At this time, the half width (2θ) of the diffraction peak attributed to the Si (111) crystal plane obtained by X-ray diffraction of the silicon compound is 1.2 ° or more, and the crystallite size attributed to the crystal plane Is preferably 7.5 nm or less.

このような半値幅及び結晶子サイズを有するケイ素系活物質は、結晶性が低くＳｉ結晶の存在量が少ないため、電池特性を向上させることができる。   Since the silicon-based active material having such a half-value width and crystallite size has low crystallinity and a small amount of Si crystals, battery characteristics can be improved.

またこのとき、前記ケイ素化合物のメディアン径が０．５μｍ以上２０μｍ以下のものであることが好ましい。   At this time, the median diameter of the silicon compound is preferably 0.5 μm or more and 20 μm or less.

メディアン径が０．５μｍ以上であれば、ケイ素化合物の表面における副反応が起きる面積が小さいため、Ｌｉを余分に消費せず、電池のサイクル維持率を高く維持できる。また、メディアン径が２０μｍ以下であれば、Ｌｉ挿入時の膨張が小さく、割れ難くなり、かつ、亀裂が生じにくい。さらに、ケイ素化合物の膨張が小さいため、例えば一般的に使用されているケイ素系活物質に炭素活物質を混合した負極活物質層などが破壊され難い。   When the median diameter is 0.5 μm or more, the area where the side reaction occurs on the surface of the silicon compound is small, so that Li is not consumed excessively and the cycle maintenance rate of the battery can be maintained high. Further, if the median diameter is 20 μm or less, the expansion at the time of inserting Li is small, it is difficult to crack, and cracks are hardly generated. Furthermore, since the expansion of the silicon compound is small, for example, a negative electrode active material layer in which a carbon active material is mixed with a commonly used silicon-based active material is not easily destroyed.

また、上記目的を達成するために、本発明は、上記のいずれかの非水電解質二次電池用負極活物質を含むことを特徴とする非水電解質二次電池を提供する。   Moreover, in order to achieve the said objective, this invention provides the nonaqueous electrolyte secondary battery characterized by including any one of said negative electrode active materials for nonaqueous electrolyte secondary batteries.

このような二次電池は、高いサイクル維持率及び初回効率を有するとともに、工業的に優位に製造することが可能なものである。   Such a secondary battery has a high cycle maintenance ratio and initial efficiency, and can be manufactured industrially.

また、上記目的を達成するために、本発明は、負極活物質粒子を含む非水電解質二次電池用負極材の製造方法であって、一般式ＳｉＯｘ（０．５≦ｘ≦１．６）で表される酸化珪素粒子を作製する工程と、前記酸化珪素粒子に、Ｌｉを挿入、脱離することで、前記酸化珪素粒子を改質する工程と、前記改質後の酸化珪素粒子の表面に、Ｌｉ塩を含む環状カーボネートからなる環状カーボネート層を形成する工程とを有し、前記環状カーボネート層が形成された酸化珪素粒子を前記負極活物質粒子として用いて、非水電解質二次電池用負極材を製造することを特徴とする非水電解質二次電池用負極材の製造方法を提供する。 In order to achieve the above object, the present invention provides a method for producing a negative electrode material for a non-aqueous electrolyte secondary battery including negative electrode active material particles, which has a general formula SiO x (0.5 ≦ x ≦ 1.6). ), A step of modifying the silicon oxide particles by inserting and removing Li from the silicon oxide particles, and a step of forming the modified silicon oxide particles. Forming a cyclic carbonate layer made of cyclic carbonate containing Li salt on the surface, and using the silicon oxide particles with the cyclic carbonate layer formed as the negative electrode active material particles, a non-aqueous electrolyte secondary battery The manufacturing method of the negative electrode material for nonaqueous electrolyte secondary batteries characterized by manufacturing the negative electrode material for batteries is provided.

このような非水電解質二次電池用負極材の製造方法であれば、Ｌｉを用いて改質されたケイ素酸化物本来の特性を生かした高い電池容量及び良好なサイクル維持率を有する非水負極材を得ることができる。さらにこのようにして製造された負極材は、上記のような環状カーボネート層を有するケイ素系活物質粒子を含有しているため、負極の製造時に作製するスラリーが安定なものとなる。すなわち、二次電池を工業的に優位に生産可能な負極材を得ることができる。   If it is a manufacturing method of such a negative electrode material for nonaqueous electrolyte secondary batteries, the nonaqueous negative electrode which has the high battery capacity and the favorable cycle maintenance factor which utilized the original characteristic of the silicon oxide modified using Li A material can be obtained. Furthermore, since the negative electrode material manufactured in this manner contains silicon-based active material particles having the cyclic carbonate layer as described above, the slurry produced at the time of manufacturing the negative electrode becomes stable. That is, a negative electrode material capable of industrially producing a secondary battery can be obtained.

このとき、前記環状カーボネート層を形成する工程において、環状カーボネート及びＬｉ塩を含む溶液で前記改質後の酸化珪素粒子を洗浄し、該洗浄後の酸化珪素粒子を乾燥させることで、前記改質後の酸化珪素粒子の表面に、前記Ｌｉ塩を含む環状カーボネートからなる環状カーボネート層を形成することが好ましい。   At this time, in the step of forming the cyclic carbonate layer, the modified silicon oxide particles are washed with a solution containing the cyclic carbonate and the Li salt, and the washed silicon oxide particles are dried, whereby the modified It is preferable to form a cyclic carbonate layer made of a cyclic carbonate containing the Li salt on the surface of the subsequent silicon oxide particles.

具体的にはこのような方法で、Ｌｉ塩を含む環状カーボネート層を形成することができる。   Specifically, a cyclic carbonate layer containing a Li salt can be formed by such a method.

本発明の負極活物質は、二次電池の製造時に作製するスラリーの安定性を向上させることができ、このスラリーを用いれば、工業的に使用可能な塗膜を形成できるので、実質的に電池容量、サイクル特性、及び初回充放電特性を向上させることができる。また、この負極活物質を含む本発明の二次電池は、工業的に優位に生産可能であり、電池容量、サイクル特性、及び初回充放電特性が良好なものとなる。また、本発明の二次電池を用いた電子機器、電動工具、電気自動車及び電力貯蔵システム等でも同様の効果を得ることができる。   The negative electrode active material of the present invention can improve the stability of the slurry produced during the production of the secondary battery, and if this slurry is used, an industrially usable coating film can be formed. Capacity, cycle characteristics, and initial charge / discharge characteristics can be improved. Moreover, the secondary battery of the present invention containing this negative electrode active material can be produced industrially superiorly, and the battery capacity, cycle characteristics, and initial charge / discharge characteristics are good. Moreover, the same effect can be acquired also in the electronic device, electric tool, electric vehicle, electric power storage system, etc. which used the secondary battery of this invention.

また、本発明の負極材の製造方法は、二次電池の製造時に作製するスラリーの安定性を向上させ、かつ、電池容量、サイクル特性、及び初回充放電特性を向上させることができる負極材を製造できる。   Further, the method for producing a negative electrode material of the present invention provides a negative electrode material that can improve the stability of a slurry produced during the production of a secondary battery and can improve battery capacity, cycle characteristics, and initial charge / discharge characteristics. Can be manufactured.

本発明の負極活物質を含む負極の構成を示す断面図である。It is sectional drawing which shows the structure of the negative electrode containing the negative electrode active material of this invention. 本発明の負極活物質を製造する際に使われるバルク内改質装置である。It is the reformer in the bulk used when manufacturing the negative electrode active material of this invention. 本発明の負極活物質を含むリチウム二次電池の構成例（ラミネートフィルム型）を表す図である。It is a figure showing the structural example (laminate film type) of the lithium secondary battery containing the negative electrode active material of this invention.

以下、本発明について実施の形態を説明するが、本発明はこれに限定されるものではない。   Hereinafter, although an embodiment is described about the present invention, the present invention is not limited to this.

前述のように、リチウムイオン二次電池の電池容量を増加させる１つの手法として、ケイ素系活物質を主材として用いた負極をリチウムイオン二次電池の負極として用いることが検討されている。ケイ素系活物質を主材として用いたリチウムイオン二次電池は、炭素材を用いたリチウムイオン二次電池と同等に近いサイクル特性、初期効率が望まれているが、炭素材を用いたリチウムイオン二次電池と同等に近いサイクル特性、初期効率を得るためにＬｉを用いて改質したケイ素系活物質では安定したスラリーの作製が難しく、良質な負極電極を製造することは困難であった。   As described above, as one method for increasing the battery capacity of a lithium ion secondary battery, the use of a negative electrode using a silicon-based active material as a main material as a negative electrode of a lithium ion secondary battery has been studied. Lithium ion secondary batteries using silicon-based active materials as the main material are expected to have cycle characteristics and initial efficiency close to those of lithium ion secondary batteries using carbon materials. With a silicon-based active material modified with Li in order to obtain cycle characteristics and initial efficiency close to those of a secondary battery, it is difficult to produce a stable slurry, and it is difficult to produce a good quality negative electrode.

そこで、本発明者らは、高電池容量であるとともに、サイクル特性及び初回効率が良好な非水電解質二次電池を容易に製造することが可能な負極活物質を得るために鋭意検討を重ね、本発明に至った。   Therefore, the present inventors have made extensive studies in order to obtain a negative electrode active material capable of easily producing a nonaqueous electrolyte secondary battery having a high battery capacity and good cycle characteristics and initial efficiency. The present invention has been reached.

本発明の負極活物質は、負極活物質粒子を有し、この負極活物質粒子はＬｉ化合物が含まれるケイ素化合物（一般式ＳｉＯｘ：０．５≦ｘ≦１．６）を含有するケイ素系活物質粒子である。また、負極活物質粒子が、環状カーボネートを含む環状カーボネート層を表面に有する。そして、この環状カーボネート層が、さらにＬｉ塩を含む。 The negative electrode active material of the present invention has negative electrode active material particles, and the negative electrode active material particles contain a silicon compound containing a Li compound (general formula SiO x : 0.5 ≦ x ≦ 1.6). Active material particles. Moreover, the negative electrode active material particles have a cyclic carbonate layer containing cyclic carbonate on the surface. And this cyclic carbonate layer contains Li salt further.

このような負極活物質は、Ｌｉ塩を含有した環状カーボネート層を表面の少なくとも一部に形成されたケイ素系活物質粒子を含むので、負極の製造時に水系スラリーを作製する際、スラリーのｐＨがアルカリ側にふれ難い。そのため、アルカリに弱い増粘剤（結着剤）への悪影響を低減することができる。また、環状カーボネート層は耐水性に優れる。さらに、環状カーボネート層の内部にＬｉ塩が含まれることで、二次電池の充放電時に、Ｌｉイオンをよりスムーズに授受しやすくなる。これらの作用から、Ｌｉを用いて改質したケイ素系活物質粒子を使用する場合であっても、安定的に水系スラリーを作製することができ、高容量で、サイクル性及び初回効率が良好な二次電池の工業的な量産がし易い負極活物質となる。   Since such a negative electrode active material includes silicon-based active material particles in which a cyclic carbonate layer containing a Li salt is formed on at least a part of the surface, when preparing an aqueous slurry during the production of the negative electrode, the pH of the slurry is Hard to touch the alkali side. Therefore, the adverse effect on the thickener (binder) that is weak against alkali can be reduced. Moreover, the cyclic carbonate layer is excellent in water resistance. Furthermore, since the Li salt is contained inside the cyclic carbonate layer, it becomes easier to smoothly transfer and receive Li ions during charging and discharging of the secondary battery. Because of these effects, even when using silicon-based active material particles modified with Li, it is possible to stably produce an aqueous slurry, high capacity, good cycleability and good initial efficiency. The negative electrode active material is easily mass-produced industrially for secondary batteries.

［負極の構成］
続いて、このような本発明の負極活物質を含む二次電池の負極の構成について説明する。 [Configuration of negative electrode]
Then, the structure of the negative electrode of the secondary battery containing such a negative electrode active material of this invention is demonstrated.

図１は、本発明の負極活物質を含む負極の断面図を表している。図１に示すように、負極１０は、負極集電体１１の上に負極活物質層１２を有する構成になっている。この負極活物質層１２は負極集電体１１の両面、又は、片面だけに設けられていても良い。さらに、本発明の非水電解質二次電池の負極においては、負極集電体１１はなくてもよい。   FIG. 1 shows a cross-sectional view of a negative electrode containing the negative electrode active material of the present invention. As shown in FIG. 1, the negative electrode 10 is configured to have a negative electrode active material layer 12 on a negative electrode current collector 11. The negative electrode active material layer 12 may be provided on both surfaces or only one surface of the negative electrode current collector 11. Furthermore, the negative electrode current collector 11 may not be provided in the negative electrode of the nonaqueous electrolyte secondary battery of the present invention.

［負極集電体］
負極集電体１１は、優れた導電性材料であり、かつ、機械的な強度に長けた物で構成される。負極集電体１１に用いることができる導電性材料として、例えば銅（Ｃｕ）やニッケル（Ｎｉ）があげられる。この導電性材料は、リチウム（Ｌｉ）と金属間化合物を形成しない材料であることが好ましい。 [Negative electrode current collector]
The negative electrode current collector 11 is an excellent conductive material and is made of a material that is excellent in mechanical strength. Examples of the conductive material that can be used for the negative electrode current collector 11 include copper (Cu) and nickel (Ni). This conductive material is preferably a material that does not form an intermetallic compound with lithium (Li).

負極集電体１１は、主元素以外に炭素（Ｃ）や硫黄（Ｓ）を含んでいることが好ましい。負極集電体の物理的強度が向上するためである。特に、充電時に膨張する活物質層を有する場合、集電体が上記の元素を含んでいれば、集電体を含む電極変形を抑制する効果があるからである。上記の含有元素の含有量は、特に限定されないが、中でも、１００ｐｐｍ以下であることが好ましい。これは、より高い変形抑制効果が得られるからである。   The negative electrode current collector 11 preferably contains carbon (C) or sulfur (S) in addition to the main element. This is because the physical strength of the negative electrode current collector is improved. In particular, in the case of having an active material layer that expands during charging, if the current collector contains the above-described element, there is an effect of suppressing electrode deformation including the current collector. Although content of said content element is not specifically limited, Especially, it is preferable that it is 100 ppm or less. This is because a higher deformation suppressing effect can be obtained.

負極集電体１１の表面は、粗化されていても良いし、粗化されていなくても良い。粗化されている負極集電体は、例えば、電解処理、エンボス処理、又は化学エッチングされた金属箔などである。粗化されていない負極集電体は例えば、圧延金属箔などである。   The surface of the negative electrode current collector 11 may be roughened or may not be roughened. The roughened negative electrode current collector is, for example, a metal foil subjected to electrolytic treatment, embossing treatment, or chemical etching. The non-roughened negative electrode current collector is, for example, a rolled metal foil.

［負極活物質層］
負極活物質層１２は、ケイ素系活物質粒子の他に炭素系活物質などの複数の種類の負極活物質を含んでいて良い。さらに、電池設計上、増粘剤（「結着剤」、「バインダー」とも呼称する）や導電助剤等の他の材料を含んでいても良い。また、負極活物質の形状は粒子状であって良い。 [Negative electrode active material layer]
The negative electrode active material layer 12 may contain a plurality of types of negative electrode active materials such as carbon-based active materials in addition to silicon-based active material particles. Furthermore, other materials such as a thickener (also referred to as “binder” or “binder”) or a conductive aid may be included in battery design. The shape of the negative electrode active material may be particulate.

上述のように、本発明の二次電池の負極はケイ素系活物質として、ＳｉＯｘ（０．５≦ｘ≦１．６）からなるケイ素系活物質粒子を含む。このケイ素系活物質粒子は酸化ケイ素材（ＳｉＯｘ：０．５≦ｘ≦１．６）であり、その組成としてはｘが１に近い方が好ましい。これは、高いサイクル特性が得られるからである。なお、本発明における酸化ケイ素材の組成は必ずしも純度１００％を意味しているわけではなく、微量の不純物元素を含んでいても良い。 As described above, the negative electrode of the secondary battery of the present invention includes silicon-based active material particles made of SiO x (0.5 ≦ x ≦ 1.6) as the silicon-based active material. The silicon-based active material particles are a silicon oxide material (SiO x : 0.5 ≦ x ≦ 1.6), and the composition is preferably such that x is close to 1. This is because high cycle characteristics can be obtained. The composition of the silicon oxide material in the present invention does not necessarily mean 100% purity, and may contain a trace amount of impurity elements.

また、本発明において、負極に含まれるケイ素化合物の結晶性は低いほどよい。具体的には、ケイ素系活物質のＸ線回折により得られる（１１１）結晶面に起因する回折ピークの半値幅（２θ）が１．２°以上であるとともに、その結晶面に起因する結晶子サイズが７．５ｎｍ以下であることが望ましい。このように、特に結晶性が低くＳｉ結晶の存在量が少ないことにより、電池特性を向上させるだけでなく、安定的なＬｉ化合物の生成をすることができる。   In the present invention, the lower the crystallinity of the silicon compound contained in the negative electrode, the better. Specifically, the full width at half maximum (2θ) of a diffraction peak attributed to a (111) crystal plane obtained by X-ray diffraction of a silicon-based active material is 1.2 ° or more, and a crystallite attributed to the crystal plane It is desirable that the size is 7.5 nm or less. As described above, since the crystallinity is low and the amount of Si crystals present is small, not only the battery characteristics are improved, but also a stable Li compound can be generated.

また、ケイ素化合物のメディアン径は特に限定されないが、中でも０．５μｍ以上２０μｍ以下であることが好ましい。この範囲であれば、充放電時においてリチウムイオンの吸蔵放出がされやすくなるとともに、ケイ素系活物質粒子が割れにくくなるからである。このメディアン径が０．５μｍ以上であれば、表面積が大きすぎないため、充放電時に副反応を起こしにくく、電池不可逆容量を低減することができる。一方、メディアン径が２０μｍ以下であれば、ケイ素系活物質粒子が割れにくく新生面が出にくいため好ましい。   In addition, the median diameter of the silicon compound is not particularly limited, but is preferably 0.5 μm or more and 20 μm or less. This is because, within this range, it is easy to occlude and release lithium ions during charging and discharging, and the silicon-based active material particles are difficult to break. If the median diameter is 0.5 μm or more, the surface area is not too large, so that side reactions are unlikely to occur during charging and discharging, and the battery irreversible capacity can be reduced. On the other hand, a median diameter of 20 μm or less is preferable because the silicon-based active material particles are difficult to break and a new surface is difficult to appear.

更に、本発明において、ケイ素系活物質は、ケイ素化合物に含まれるＬｉ化合物として、Ｌｉ２ＳｉＯ３及びＬｉ４ＳｉＯ４のうち１種以上が存在するものであることが好ましい。Ｌｉ２ＳｉＯ３及びＬｉ４ＳｉＯ４のようなＬｉシリケートは、他のＬｉ化合物よりも比較的安定しているため、これらのＬｉ化合物を含むケイ素系活物質は、より安定した電池特性を得ることができる。これらのＬｉ化合物は、ケイ素化合物の内部に生成するＳｉＯ２成分の一部をＬｉ化合物へ選択的に変更することにより得ることができる。 Furthermore, in the present invention, the silicon-based active material is preferably one in which one or more of Li 2 SiO 3 and Li 4 SiO 4 are present as the Li compound contained in the silicon compound. Since Li silicates such as Li 2 SiO 3 and Li 4 SiO 4 are relatively more stable than other Li compounds, silicon-based active materials containing these Li compounds can obtain more stable battery characteristics. Can do. These Li compounds can be obtained by selectively changing a part of the SiO 2 component generated inside the silicon compound to a Li compound.

特に、このようなケイ素化合物は、電気化学的手法によりＬｉが挿入、脱離されることで、改質されたものであることが好ましい。電気化学的手法では、リチウム対極に対する電位規制や電流規制などを行い、条件を変更することで選択的にＬｉ化合物の作製が可能となる。さらに、電気化学的手法であれば、外部電位及び参照極などを用いる事で、ケイ素化合物の電位を制御しやすくなると共に、不必要な領域に挿入されたＬｉは放電過程を用いることで除去できる。そのためこのような手法で、改質されたケイ素化合物は所望の特性を有するものとなる。   In particular, it is preferable that such a silicon compound is modified by inserting and desorbing Li by an electrochemical method. In the electrochemical method, potential regulation or current regulation with respect to the lithium counter electrode is performed, and the Li compound can be selectively produced by changing the conditions. Furthermore, if it is an electrochemical method, it becomes easy to control the potential of the silicon compound by using an external potential and a reference electrode, and Li inserted in an unnecessary region can be removed by using a discharge process. . Therefore, the silicon compound modified by such a method has desired characteristics.

ケイ素活物質の内部のＬｉ化合物はＮＭＲ（核磁気共鳴）とＸＰＳ（Ｘ線光電子分光）で定量可能である。ＸＰＳとＮＭＲの測定は、例えば、以下の条件により行うことができる。
ＸＰＳ
・装置： Ｘ線光電子分光装置、
・Ｘ線源： 単色化Ａｌ Ｋα線、
・Ｘ線スポット径： １００μｍ、
・Ａｒイオン銃スパッタ条件： ０．５ｋＶ ２ｍｍ×２ｍｍ。
２９Ｓｉ ＭＡＳ ＮＭＲ（マジック角回転核磁気共鳴）
・装置： Ｂｒｕｋｅｒ社製７００ＮＭＲ分光器、
・プローブ： ４ｍｍＨＲ−ＭＡＳローター ５０μＬ、
・試料回転速度： １０ｋＨｚ、
・測定環境温度： ２５℃。 The Li compound inside the silicon active material can be quantified by NMR (nuclear magnetic resonance) and XPS (X-ray photoelectron spectroscopy). The XPS and NMR measurements can be performed, for example, under the following conditions.
XPS
・ Device: X-ray photoelectron spectrometer,
・ X-ray source: Monochromatic Al Kα ray,
・ X-ray spot diameter: 100 μm,
Ar ion gun sputtering conditions: 0.5 kV 2 mm × 2 mm.
29 Si MAS NMR (magic angle rotating nuclear magnetic resonance)
Apparatus: 700 NMR spectrometer manufactured by Bruker,
Probe: 4 mm HR-MAS rotor 50 μL,
Sample rotation speed: 10 kHz,
-Measurement environment temperature: 25 ° C.

このような改質（バルク内改質）方法を用いて負極活物質を製造することで、Ｓｉ領域のＬｉ化合物化を低減、又は避けることが可能であり、大気中、又は水系スラリー中、溶剤スラリー中で安定した物質となる。また、電気化学的手法により改質を行うことにより、ランダムに化合物化する熱改質（熱ドープ法）に対し、より安定した物質を作ることが可能である。   By producing a negative electrode active material using such a modification (in-bulk modification) method, it is possible to reduce or avoid the formation of a Li compound in the Si region, and in the atmosphere or in an aqueous slurry, a solvent It becomes a stable substance in the slurry. Further, by performing the modification by an electrochemical method, it is possible to make a more stable substance with respect to the thermal modification (thermal doping method) in which the compound is randomly formed.

ケイ素系活物質のバルク内部に生成したＬｉ４ＳｉＯ４、Ｌｉ２ＳｉＯ３は少なくとも１種以上存在することで特性向上となるが、より特性向上となるのはこれら２種の共存状態である。 Although at least one kind of Li 4 SiO 4 and Li 2 SiO 3 produced in the bulk of the silicon-based active material improves the characteristics, it is the coexistence state of these two kinds that further improves the characteristics.

また、ケイ素系活物質粒子が、ケイ素化合物の表面に炭素被膜を有するものであることが望ましい。これは、導電性が得られやすいからである。   Moreover, it is desirable that the silicon-based active material particles have a carbon film on the surface of the silicon compound. This is because conductivity is easily obtained.

また、上述のような電気化学的手法でケイ素系化合物の改質を行う場合、改質前にケイ素化合物の表面に炭素被膜を形成しておくことが好ましい。これは、電気化学的手法によるバルク内改質処理において、ケイ素化合物の表面に炭素被膜が存在することで、電位分布の低減ができ、生成するＬｉ化合物のより均一な制御が可能となるためである。   Further, when the silicon compound is modified by the electrochemical method as described above, it is preferable to form a carbon film on the surface of the silicon compound before the modification. This is because, in the reforming process in the bulk by the electrochemical method, the presence of the carbon film on the surface of the silicon compound enables the potential distribution to be reduced, and the generated Li compound can be more uniformly controlled. is there.

また、本発明において、負極活物質粒子は、ケイ素化合物と環状カーボネート層との間に、炭酸リチウム及びフッ化リチウムのうち１種以上を含むものであることが好ましい。炭酸リチウム及びフッ化リチウムなどを、ケイ素化合物と環状カーボネート層との間の少なくとも一部に形成しておくことで、電池として初期充電する時に正極側から放出されるＬｉを負極で消費する量が減るため、電池の初期効率が向上する。なお、炭酸リチウム及びフッ化リチウムは、負極活物質粒子を電気化学的に改質する際に、ケイ素化合物の表面にＳＥＩ（Ｓｏｌｉｄ−Ｅｌｅｃｔｒｏｌｙｔｅ Ｉｎｔｅｒｆａｃｅ）として形成することができ、また、上記のＬｉシリケートと同時に生成可能である。   In the present invention, the negative electrode active material particles preferably include one or more of lithium carbonate and lithium fluoride between the silicon compound and the cyclic carbonate layer. By forming lithium carbonate and lithium fluoride at least partially between the silicon compound and the cyclic carbonate layer, the amount of Li released from the positive electrode side when the battery is initially charged can be consumed by the negative electrode. Therefore, the initial efficiency of the battery is improved. The lithium carbonate and lithium fluoride can be formed as SEI (Solid-Electrolyte Interface) on the surface of the silicon compound when the negative electrode active material particles are electrochemically modified, and the above-described Li silicate. It can be generated at the same time.

また、上記のように、ケイ素化合物の改質前に炭素被膜を形成しておく場合、炭素被膜の表面に炭酸リチウム及びフッ化リチウムのうち１種以上を含む層が形成される。   Further, as described above, when the carbon film is formed before the modification of the silicon compound, a layer containing at least one of lithium carbonate and lithium fluoride is formed on the surface of the carbon film.

ケイ素系活物質粒子が、炭素被膜、炭酸リチウム及びフッ化リチウムのうち１種以上を含む層、及び環状カーボネート層を有する場合、炭素被膜と、炭素被膜の上部を覆う炭酸リチウム及び／又はフッ化リチウム層、及び最表層を覆う耐水層である環状カーボネート層の順で各層が積層されていることが好ましい。また、上述のように、この環状カーボネート層にはＬｉ塩を含む。このような積層を有する負極活物質であれば、スラリーを安定に保ち、良質な塗膜を得ることができるため、電池特性が向上する。   When the silicon-based active material particles have a carbon coating, a layer containing at least one of lithium carbonate and lithium fluoride, and a cyclic carbonate layer, the carbon coating and lithium carbonate and / or fluoride covering the top of the carbon coating Each layer is preferably laminated in the order of a lithium layer and a cyclic carbonate layer which is a water-resistant layer covering the outermost layer. Further, as described above, this cyclic carbonate layer contains a Li salt. If it is a negative electrode active material which has such a lamination | stacking, since a slurry can be kept stable and a good-quality coating film can be obtained, battery characteristics will improve.

また、本発明において、環状カーボネート層に含まれる環状カーボネートが、エチレンカーボネート、プロピレンカーボネート、フルオロエチレンカーボネート、ジフルオロエチレンカーボネート、及びビニレンカーボネートのうち１種以上を含むものであることが好ましい。上記のような環状カーボネートは常温で固体であるため、これらを含む環状カーボネート層であれば、より安定した耐水層となる。この中でも、エチレンカーボネート又はフルオロエチレンカーボネートを含む場合、特に安定した電池特性を得ることができる。   In the present invention, the cyclic carbonate contained in the cyclic carbonate layer preferably contains one or more of ethylene carbonate, propylene carbonate, fluoroethylene carbonate, difluoroethylene carbonate, and vinylene carbonate. Since the cyclic carbonates as described above are solid at normal temperature, a cyclic carbonate layer containing these will provide a more stable water-resistant layer. Among these, when ethylene carbonate or fluoroethylene carbonate is included, particularly stable battery characteristics can be obtained.

また、環状カーボネート層に含まれるＬｉ塩が、ＬｉＰＦ６、ＬｉＢＦ４、ＬｉＣｌＯ４、ＬｉＢＯＢ、ＬｉＦＳＡ、ＬｉＴＦＳＡ、及びＬｉＴＦＳＩのうち１種以上を含むものであることが好ましい。環状カーボネート層に含まれるＬｉ塩として、具体的には上記のようなものが挙げられる。この中でも、特に、Ｌｉ塩として、ＬｉＰＦ６、ＬｉＢＦ４、ＬｉＣｌＯ４が環状カーボネート層に含まれることにより、スラリーがより安定する。また、環状カーボネート層の内部に存在するＬｉ塩はＸＰＳで確認することができる。ＸＰＳの条件としては、上述のケイ素活物質内のＬｉ化合物を測定する場合と同様の条件でよい。 Also, Li salt contained in the cyclic carbonate layer, LiPF 6, LiBF 4, LiClO 4, LiBOB, LiFSA, it preferably contains LiTFSA, and one or more of LiTFSI. Specific examples of the Li salt contained in the cyclic carbonate layer include those described above. Among these, especially, as the Li salt, LiPF 6 , LiBF 4 , and LiClO 4 are contained in the cyclic carbonate layer, so that the slurry becomes more stable. Moreover, Li salt which exists in the inside of a cyclic carbonate layer can be confirmed by XPS. The XPS conditions may be the same as those for measuring the Li compound in the silicon active material described above.

また、本発明では、環状カーボネート層の質量が、ケイ素化合物の質量に対し１５質量％以下のものであることが好ましい。上記割合が１５質量％以下となるような厚さで環状カーボネート層を形成すれば導電性の低下を防止することができる。また、十分な量のケイ素化合物が存在するので、高い電池容量が得られる。また、環状カーボネート層を極力薄くするために、環状カーボネート層の被覆量は最少量であることが望ましいが、スラリーの保持方法に応じて必要量被覆することが望ましい。環状カーボネート層が、より薄い状態でも、上述の効果は発現する。   Moreover, in this invention, it is preferable that the mass of a cyclic carbonate layer is 15 mass% or less with respect to the mass of a silicon compound. If the cyclic carbonate layer is formed with such a thickness that the ratio is 15% by mass or less, the decrease in conductivity can be prevented. Moreover, since a sufficient amount of silicon compound is present, a high battery capacity can be obtained. In order to make the cyclic carbonate layer as thin as possible, it is desirable that the cyclic carbonate layer be coated in a minimum amount, but it is desirable to coat the required amount according to the slurry holding method. Even when the cyclic carbonate layer is thinner, the above-described effects are exhibited.

またこのとき、環状カーボネート層が、さらに鎖状カーボネートを含むものであることが好ましい。環状カーボネート層に鎖状カーボネートが含まれることで、負極作製時、スラリーのｐＨがアルカリに、さらにふれ難くなるため、スラリーがより安定する。   At this time, the cyclic carbonate layer preferably further contains a chain carbonate. When the chain carbonate is contained in the cyclic carbonate layer, the pH of the slurry becomes more difficult to touch the alkali during the production of the negative electrode, so that the slurry becomes more stable.

［負極の製造方法］
続いて、本発明の非水電解質二次電池の負極の製造方法の一例を説明する。 [Production method of negative electrode]
Then, an example of the manufacturing method of the negative electrode of the nonaqueous electrolyte secondary battery of this invention is demonstrated.

最初に負極に含まれる負極材の製造方法を説明する。まず、ＳｉＯｘ（０．５≦ｘ≦１．６）で表される酸化珪素粒子を作製する。次に、酸化珪素粒子にＬｉを挿入、脱離することにより、酸化珪素粒子を改質する。このとき、同時に酸化珪素粒子の内部や表面にＬｉ化合物を生成させることができる。そして、改質後の酸化珪素粒子の表面に、Ｌｉ塩を含む環状カーボネートからなる環状カーボネート層を形成する。そしてこのような酸化珪素粒子を負極活物質粒子として、導電剤やバインダーと混合するなどして負極材を製造できる。 First, a method for producing a negative electrode material included in the negative electrode will be described. First, silicon oxide particles represented by SiO x (0.5 ≦ x ≦ 1.6) are produced. Next, the silicon oxide particles are modified by inserting and removing Li from the silicon oxide particles. At the same time, a Li compound can be generated inside or on the surface of the silicon oxide particles. And the cyclic carbonate layer which consists of cyclic carbonate containing Li salt is formed in the surface of the silicon oxide particle after modification | reformation. A negative electrode material can be produced by mixing such silicon oxide particles as negative electrode active material particles with a conductive agent or a binder.

より具体的には、負極材は、例えば、以下の手順により製造される。   More specifically, the negative electrode material is manufactured by the following procedure, for example.

まず、酸化珪素ガスを発生する原料を不活性ガスの存在下もしくは減圧下９００℃〜１６００℃の温度範囲で加熱し、酸化ケイ素ガスを発生させる。この場合、原料は金属珪素粉末と二酸化珪素粉末との混合であり、金属珪素粉末の表面酸素及び反応炉中の微量酸素の存在を考慮すると、混合モル比が、０．８＜金属珪素粉末／二酸化珪素粉末＜１．３の範囲であることが望ましい。粒子中のＳｉ結晶子は仕込み範囲や気化温度の変更、また生成後の熱処理で制御される。発生したガスは吸着板に堆積される。反応炉内温度を１００℃以下に下げた状態で堆積物を取出し、ボールミル、ジェットミルなどを用いて粉砕、粉末化を行う。   First, a raw material that generates silicon oxide gas is heated in a temperature range of 900 ° C. to 1600 ° C. in the presence of an inert gas or under reduced pressure to generate silicon oxide gas. In this case, the raw material is a mixture of metal silicon powder and silicon dioxide powder, and considering the surface oxygen of the metal silicon powder and the presence of trace amounts of oxygen in the reactor, the mixing molar ratio is 0.8 <metal silicon powder / It is desirable that the silicon dioxide powder is in the range of <1.3. The Si crystallites in the particles are controlled by changing the preparation range and vaporization temperature, and by heat treatment after generation. The generated gas is deposited on the adsorption plate. The deposit is taken out with the temperature in the reactor lowered to 100 ° C. or lower, and pulverized and powdered using a ball mill, a jet mill or the like.

次に、得られた粉末材料の表面に炭素被膜を生成することができるが、この工程は必須ではない。しかしながら、より電池特性を向上させるには効果的である。   Next, a carbon film can be formed on the surface of the obtained powder material, but this step is not essential. However, it is effective for improving battery characteristics.

得られた粉末材料の表層に炭素被膜を形成する手法としては、熱分解ＣＶＤが望ましい。熱分解ＣＶＤは炉内に酸化ケイ素粉末をセットし、炉内に炭化水素ガスを充満させ炉内温度を昇温させる。分解温度は特に限定しないが特に１２００℃以下が望ましい。より望ましいのは９５０℃以下であり、意図しないケイ素酸化物の不均化を抑制することが可能である。炭化水素ガスは特に限定することはないが、ＣｎＨｍ組成のうち３≧ｎが望ましい。低製造コスト及び分解生成物の物性が良いからである。 As a method for forming a carbon film on the surface layer of the obtained powder material, pyrolytic CVD is desirable. In pyrolysis CVD, silicon oxide powder is set in a furnace, the furnace is filled with hydrocarbon gas, and the temperature in the furnace is raised. The decomposition temperature is not particularly limited, but is particularly preferably 1200 ° C. or lower. More desirably, the temperature is 950 ° C. or lower, and unintended disproportionation of silicon oxide can be suppressed. Hydrocarbon gas is not particularly limited, 3 ≧ n of C n H m composition it is desirable. This is because the low production cost and the physical properties of the decomposition products are good.

バルク内改質は電気化学的にＬｉを挿入・脱離し得る装置を用いて行うことが望ましい。特に装置構造を限定することはないが、例えば図２に示すバルク内改質装置２０を用いて、バルク内改質を行うことができる。バルク内改質装置２０は、有機溶媒２３で満たされた浴槽２７と、浴槽２７内に配置され、電源２６の一方に接続された陽電極（リチウム源、改質源）２１と、浴槽２７内に配置され、電源２６の他方に接続された粉末格納容器２５と、陽電極２１と粉末格納容器２５との間に設けられたセパレータ２４とを有している。粉末格納容器２５には、酸化ケイ素の粉末２２が格納される。そして、粉末格納容器には、酸化珪素粒子を格納し、電源により酸化珪素粒子を格納した粉末格納容器と陽電極（リチウム源）に電圧をかける。これにより、酸化珪素粒子にリチウムを挿入、脱離することができるため、酸化珪素の粉末２２を改質できる。   In-bulk reforming is desirably performed using an apparatus capable of electrochemically inserting and extracting Li. Although the apparatus structure is not particularly limited, for example, the bulk reforming can be performed using the bulk reforming apparatus 20 shown in FIG. The in-bulk reformer 20 includes a bathtub 27 filled with an organic solvent 23, a positive electrode (lithium source, reforming source) 21 disposed in the bathtub 27 and connected to one of the power sources 26, And a separator 24 provided between the positive electrode 21 and the powder storage container 25. The powder storage container 25 is connected to the other side of the power source 26. The powder storage container 25 stores silicon oxide powder 22. The powder storage container stores silicon oxide particles, and a voltage is applied to the powder storage container and the positive electrode (lithium source) storing the silicon oxide particles by a power source. Thereby, since lithium can be inserted into and desorbed from the silicon oxide particles, the silicon oxide powder 22 can be modified.

尚、改質により、酸化珪素の粉末２２の内部にＬｉシリケートを生成するとともに、酸化珪素の粉末２２の表面に、炭酸リチウム（Ｌｉ２ＣＯ３）及びフッ化リチウム（ＬｉＦ）のうち１種以上を含む層も同時に形成できる。改質前にケイ素活物質粒子の表面に炭素被膜を形成している場合、上述のように、炭素被膜の上に上記炭酸リチウム等を含む層が形成される。 The modification produces Li silicate in the silicon oxide powder 22 and at least one of lithium carbonate (Li 2 CO 3 ) and lithium fluoride (LiF) on the surface of the silicon oxide powder 22. A layer containing can be formed at the same time. When the carbon film is formed on the surface of the silicon active material particles before the modification, as described above, the layer containing the lithium carbonate or the like is formed on the carbon film.

また、上記のように、炭素被膜の形成は必須ではない。ただし、ケイ素化合物の表面に炭素被膜が存在することで、電位分布の低減ができ、生成するＬｉ化合物のより均一な制御が可能となるため、改質前に炭素被膜を酸化ケイ素の粉末２２の表面に形成しておくことが望ましい。   Further, as described above, the formation of the carbon film is not essential. However, since the carbon coating is present on the surface of the silicon compound, the potential distribution can be reduced and the generated Li compound can be more uniformly controlled. It is desirable to form on the surface.

浴槽２７内の有機溶媒２３として、炭酸エチレン、炭酸プロピレン、炭酸ジメチル、炭酸ジエチル、炭酸エチルメチル、炭酸フルオロメチルメチル、炭酸ジフルオロメチルメチルなどを用いることができる。また、有機溶媒２３に含まれる電解質塩として、六フッ化リン酸リチウム（ＬｉＰＦ６）、四フッ化ホウ酸リチウム（ＬｉＢＦ４）などを用いることができる。 As the organic solvent 23 in the bathtub 27, ethylene carbonate, propylene carbonate, dimethyl carbonate, diethyl carbonate, ethyl methyl carbonate, fluoromethyl methyl carbonate, difluoromethyl methyl carbonate, or the like can be used. As the electrolyte salt contained in the organic solvent 23, lithium hexafluorophosphate (LiPF 6 ), lithium tetrafluoroborate (LiBF 4 ), or the like can be used.

陽電極２１はＬｉ箔を用いてもよく、また、Ｌｉ含有化合物を用いてもよい。Ｌｉ含有化合物として、炭酸リチウム、酸化リチウム、コバルト酸リチウム、オリビン鉄リチウム、ニッケル酸リチウム、リン酸バナジウムリチウムなどがあげられる。   The positive electrode 21 may use a Li foil or a Li-containing compound. Examples of the Li-containing compound include lithium carbonate, lithium oxide, lithium cobaltate, lithium olivine, lithium nickelate, and lithium vanadium phosphate.

続いて、改質後の酸化珪素粒子の表面に、Ｌｉ塩を含む環状カーボネートからなる環状カーボネート層を形成する。例えば、以下のような手順で環状カーボネート層を形成できる。   Subsequently, a cyclic carbonate layer made of cyclic carbonate containing Li salt is formed on the surface of the modified silicon oxide particles. For example, the cyclic carbonate layer can be formed by the following procedure.

まず、改質後の酸化珪素粒子を、環状カーボネート及びＬｉ塩を含む溶液で洗浄する。例えば、エチレンカーボネート（環状カーボネート）とジエチルカーボネート（鎖状カーボネート）とＬｉＢＦ４（リチウム塩）を混合した溶液で３０分程度洗浄する。この時、環状カーボネートと鎖状カーボネートの種類や比を制御することで、環状カーボネート層の被覆量を制御する事ができる。例えば、導電性や電池容量の確保のために、環状カーボネート層の被覆量を小さくする場合、鎖状カーボネートとしてジメチルカーボネートを用いれば、表面に被覆するエチレンカーボネートの量を大幅に低減することができる。また、溶液中のリチウム塩の濃度は、例えば１ｍｏｌ／Ｋｇ程度とすることができる。またプロピレンカーボネート又はエチレンカーボネートを環状カーボネートとして用いれば、被覆効率をより向上させることができる。そして、洗浄後の酸化珪素粒子を乾燥させることで環状カーボネート層を形成できる。 First, the modified silicon oxide particles are washed with a solution containing cyclic carbonate and Li salt. For example, ethylene carbonate (cyclic carbonate) and diethyl carbonate (chain carbonate) and LiBF 4 and washed for about 30 minutes with a solution of a mixture of (lithium salt). At this time, the coating amount of the cyclic carbonate layer can be controlled by controlling the type and ratio of the cyclic carbonate and the chain carbonate. For example, when reducing the coating amount of the cyclic carbonate layer to ensure conductivity and battery capacity, if dimethyl carbonate is used as the chain carbonate, the amount of ethylene carbonate coated on the surface can be greatly reduced. . The concentration of the lithium salt in the solution can be set to, for example, about 1 mol / Kg. If propylene carbonate or ethylene carbonate is used as the cyclic carbonate, the coating efficiency can be further improved. And a cyclic carbonate layer can be formed by drying the silicon oxide particles after washing.

続いて、上記の環状カーボネート層を有する酸化珪素粒子を含むケイ素系活物質と必要に応じて炭素系活物質を混合するとともに、これらの負極活物質とバインダー、導電助剤など他の材料とを混合し負極合剤としたのち、有機溶剤又は水などを加えてスラリーとする。   Subsequently, while mixing a silicon-based active material containing silicon oxide particles having the above cyclic carbonate layer and a carbon-based active material as necessary, these negative electrode active material and other materials such as a binder and a conductive auxiliary agent are mixed. After mixing to form a negative electrode mixture, an organic solvent or water is added to form a slurry.

次に、負極集電体１１の表面に、この負極合剤のスラリーを塗布し、乾燥させて図１に示す負極活物質層１２を形成する。この時、必要に応じて加熱プレスなどを行っても良い。以上のようにして、本発明の非水電解質二次電池の負極を製造することができる。   Next, the negative electrode mixture slurry is applied to the surface of the negative electrode current collector 11 and dried to form the negative electrode active material layer 12 shown in FIG. At this time, a heating press or the like may be performed as necessary. As described above, the negative electrode of the nonaqueous electrolyte secondary battery of the present invention can be produced.

＜リチウムイオン二次電池＞
次に、上記した本発明の非水電解質二次電池の具体例として、ラミネートフィルム型のリチウムイオン二次電池について説明する。 <Lithium ion secondary battery>
Next, a laminated film type lithium ion secondary battery will be described as a specific example of the nonaqueous electrolyte secondary battery of the present invention.

［ラミネートフィルム型二次電池の構成］
図３に示すラミネートフィルム型のリチウムイオン二次電池３０は、主にシート状の外装部材３５の内部に巻回電極体３１が収納されたものである。この巻回電極体３１は正極、負極間にセパレータを有し、巻回されたものである。また正極、負極間にセパレータを有し積層体を収納した場合も存在する。どちらの電極体においても、正極に正極リード３２が取り付けられ、負極に負極リード３３が取り付けられている。電極体の最外周部は保護テープにより保護されている。 [Configuration of laminated film type secondary battery]
A laminated film type lithium ion secondary battery 30 shown in FIG. 3 is one in which a wound electrode body 31 is accommodated mainly in a sheet-like exterior member 35. The wound electrode body 31 has a separator between a positive electrode and a negative electrode, and is wound. There is also a case where a separator is provided between the positive electrode and the negative electrode and a laminate is accommodated. In both electrode bodies, the positive electrode lead 32 is attached to the positive electrode, and the negative electrode lead 33 is attached to the negative electrode. The outermost peripheral part of the electrode body is protected by a protective tape.

正負極リード３２、３３は、例えば、外装部材３５の内部から外部に向かって一方向で導出されている。正極リード３２は、例えば、アルミニウムなどの導電性材料により形成され、負極リード３３は、例えば、ニッケル、銅などの導電性材料により形成される。   The positive and negative leads 32 and 33 are led out in one direction from the inside of the exterior member 35 to the outside, for example. The positive electrode lead 32 is formed of a conductive material such as aluminum, and the negative electrode lead 33 is formed of a conductive material such as nickel or copper.

外装部材３５は、例えば、融着層、金属層、表面保護層がこの順に積層されたラミネートフィルムであり、このラミネートフィルムは融着層が電極体３１と対向するように、２枚のフィルムの融着層における外周縁部同士が融着、又は、接着剤などで張り合わされている。融着部は、例えばポリエチレンやポリプロピレンなどのフィルムであり、金属部はアルミ箔などである。保護層は例えば、ナイロンなどである。   The exterior member 35 is, for example, a laminate film in which a fusion layer, a metal layer, and a surface protective layer are laminated in this order. This laminate film is formed of two films so that the fusion layer faces the electrode body 31. The outer peripheral edges of the fusion layer are bonded together with an adhesive or an adhesive. The fused part is, for example, a film such as polyethylene or polypropylene, and the metal part is aluminum foil or the like. The protective layer is, for example, nylon.

外装部材３５と正負極リードとの間には、外気侵入防止のため密着フィルム３４が挿入されている。この材料は、例えば、ポリエチレン、ポリプロピレン、ポリオレフィン樹脂である。   An adhesion film 34 is inserted between the exterior member 35 and the positive and negative electrode leads to prevent intrusion of outside air. This material is, for example, polyethylene, polypropylene, or polyolefin resin.

［正極］
正極は、例えば、図１の負極１０と同様に、正極集電体の両面又は片面に正極活物質層を有している。 [Positive electrode]
The positive electrode has, for example, a positive electrode active material layer on both sides or one side of the positive electrode current collector, similarly to the negative electrode 10 of FIG.

正極集電体は、例えば、アルミニウムなどの導電性材により形成されている。   The positive electrode current collector is formed of, for example, a conductive material such as aluminum.

正極活物質層は、リチウムイオンの吸蔵放出可能な正極材のいずれか１種又は２種以上を含んでおり、設計に応じて正極結着剤、正極導電助剤、分散剤などの他の材料を含んでいても良い。この場合、正極結着剤、正極導電助剤に関する詳細は、例えば既に記述した負極結着剤、負極導電助剤と同様である。   The positive electrode active material layer includes any one or more of positive electrode materials capable of occluding and releasing lithium ions, and other materials such as a positive electrode binder, a positive electrode conductive additive, and a dispersant depending on the design. May be included. In this case, details regarding the positive electrode binder and the positive electrode conductive additive are the same as, for example, the negative electrode binder and negative electrode conductive additive already described.

正極材料としては、リチウム含有化合物が望ましい。このリチウム含有化合物は、例えばリチウムと遷移金属元素からなる複合酸化物、又はリチウムと遷移金属元素を有するリン酸化合物があげられる。これら記述される正極材の中でもニッケル、鉄、マンガン、コバルトの少なくとも１種以上を有する化合物が好ましい。これらの化学式として、例えば、ＬｉｘＭ１Ｏ２あるいはＬｉｙＭ２ＰＯ４で表される。式中、Ｍ１、Ｍ２は少なくとも１種以上の遷移金属元素を示す。ｘ、ｙの値は電池充放電状態によって異なる値を示すが、一般的に０．０５≦ｘ≦１．１０、０．０５≦ｙ≦１．１０で示される。 As the positive electrode material, a lithium-containing compound is desirable. Examples of the lithium-containing compound include a composite oxide composed of lithium and a transition metal element, or a phosphate compound having lithium and a transition metal element. Among these described positive electrode materials, compounds having at least one of nickel, iron, manganese, and cobalt are preferable. These chemical formulas are represented by, for example, Li x M 1 O 2 or Li y M 2 PO 4 . In the formula, M 1 and M 2 represent at least one transition metal element. The values of x and y vary depending on the battery charge / discharge state, but are generally expressed as 0.05 ≦ x ≦ 1.10 and 0.05 ≦ y ≦ 1.10.

リチウムと遷移金属元素とを有する複合酸化物としては、例えば、リチウムコバルト複合酸化物（ＬｉｘＣｏＯ２）、リチウムニッケル複合酸化物（ＬｉｘＮｉＯ２）、リチウムニッケルコバルト複合酸化物などが挙げられる。リチウムニッケルコバルト複合酸化物としては、例えばリチウムニッケルコバルトアルミニウム複合酸化物（ＮＣＡ）やリチウムニッケルコバルトマンガン複合酸化物（ＮＣＭ）などが挙げられる。 Examples of the composite oxide having lithium and a transition metal element include lithium cobalt composite oxide (Li x CoO 2 ), lithium nickel composite oxide (Li x NiO 2 ), and lithium nickel cobalt composite oxide. . Examples of the lithium nickel cobalt composite oxide include lithium nickel cobalt aluminum composite oxide (NCA) and lithium nickel cobalt manganese composite oxide (NCM).

リチウムと遷移金属元素とを有するリン酸化合物としては、例えば、リチウム鉄リン酸化合物（ＬｉＦｅＰＯ４）あるいはリチウム鉄マンガンリン酸化合物（ＬｉＦｅ１−ｕＭｎｕＰＯ４（０＜ｕ＜１））などが挙げられる。これらの正極材を用いれば、高い電池容量を得ることができるとともに、優れたサイクル特性も得ることができる。 Examples of the phosphate compound having lithium and a transition metal element include a lithium iron phosphate compound (LiFePO 4 ) or a lithium iron manganese phosphate compound (LiFe 1-u Mn u PO 4 (0 <u <1)). Is mentioned. If these positive electrode materials are used, a high battery capacity can be obtained, and excellent cycle characteristics can also be obtained.

［負極］
負極は、上記した図１のリチウムイオン二次電池用負極１０と同様の構成を有し、例えば、集電体の両面に負極活物質層を有している。この負極は、正極活物質剤から得られる電気容量（電池としての充電容量）に対して、負極充電容量が大きくなることが好ましい。これにより、負極上でのリチウム金属の析出を抑制することができる。 [Negative electrode]
The negative electrode has the same configuration as the negative electrode 10 for lithium ion secondary battery in FIG. 1 described above, and has, for example, a negative electrode active material layer on both sides of the current collector. This negative electrode preferably has a negative electrode charge capacity larger than the electric capacity (charge capacity as a battery) obtained from the positive electrode active material agent. Thereby, precipitation of lithium metal on the negative electrode can be suppressed.

正極活物質層は、正極集電体の両面の一部に設けられており、同様に負極活物質層も負極集電体の両面の一部に設けられている。この場合、例えば、負極集電体上に設けられた負極活物質層は対向する正極活物質層が存在しない領域が設けられている。これは、安定した電池設計を行うためである。   The positive electrode active material layer is provided on part of both surfaces of the positive electrode current collector, and similarly, the negative electrode active material layer is provided on part of both surfaces of the negative electrode current collector. In this case, for example, the negative electrode active material layer provided on the negative electrode current collector is provided with a region where there is no opposing positive electrode active material layer. This is to perform a stable battery design.

上記の負極活物質層と正極活物質層とが対向しない領域では、充放電の影響をほとんど受けることが無い。そのため、負極活物質層の状態が形成直後のまま維持され、これによって負極活物質の組成などを、充放電の有無に依存せずに再現性良く正確に調べることができる。   In the region where the negative electrode active material layer and the positive electrode active material layer do not face each other, there is almost no influence of charge / discharge. Therefore, the state of the negative electrode active material layer is maintained as it is immediately after formation, whereby the composition of the negative electrode active material can be accurately examined with good reproducibility without depending on the presence or absence of charge / discharge.

［セパレータ］
セパレータは正極と負極を隔離し、両極接触に伴う電流短絡を防止しつつ、リチウムイオンを通過させるものである。このセパレータは、例えば合成樹脂、あるいはセラミックからなる多孔質膜により形成されており、２種以上の多孔質膜が積層された積層構造を有しても良い。合成樹脂として例えば、ポリテトラフルオロエチレン、ポリプロピレン、ポリエチレンなどが挙げられる。 [Separator]
The separator separates the positive electrode and the negative electrode, and allows lithium ions to pass through while preventing a short circuit due to contact between the two electrodes. This separator is formed of, for example, a porous film made of synthetic resin or ceramic, and may have a laminated structure in which two or more kinds of porous films are laminated. Examples of the synthetic resin include polytetrafluoroethylene, polypropylene, and polyethylene.

［電解液］
活物質層の少なくとも一部、又は、セパレータには、液状の電解質（電解液）が含浸されている。この電解液は、溶媒中に電解質塩が溶解されており、添加剤など他の材料を含んでいても良い。 [Electrolyte]
At least a part of the active material layer or the separator is impregnated with a liquid electrolyte (electrolytic solution). This electrolytic solution has an electrolyte salt dissolved in a solvent, and may contain other materials such as additives.

溶媒は、例えば、非水溶媒を用いることができる。非水溶媒としては、例えば、炭酸エチレン、炭酸プロピレン、炭酸ブチレン、炭酸ジメチル、炭酸ジエチル、炭酸エチルメチル、炭酸メチルプロピル、１，２−ジメトキシエタン、又はテトラヒドロフランなどが挙げられる。この中でも、炭酸エチレン、炭酸プロピレン、炭酸ジメチル、炭酸ジエチル、炭酸エチルメチルのうちの少なくとも１種以上を用いることが望ましい。より良い特性が得られるからである。またこの場合、炭酸エチレン、炭酸プロピレンなどの高粘度溶媒と、炭酸ジメチル、炭酸エチルメチル、炭酸ジエチルなどの低粘度溶媒を組み合わせることにより、より優位な特性を得ることができる。これは、電解質塩の解離性やイオン移動度が向上するためである。   For example, a non-aqueous solvent can be used as the solvent. Examples of the non-aqueous solvent include ethylene carbonate, propylene carbonate, butylene carbonate, dimethyl carbonate, diethyl carbonate, ethyl methyl carbonate, methyl propyl carbonate, 1,2-dimethoxyethane, and tetrahydrofuran. Among these, it is desirable to use at least one of ethylene carbonate, propylene carbonate, dimethyl carbonate, diethyl carbonate, and ethyl methyl carbonate. This is because better characteristics can be obtained. In this case, more advantageous characteristics can be obtained by combining a high viscosity solvent such as ethylene carbonate or propylene carbonate and a low viscosity solvent such as dimethyl carbonate, ethyl methyl carbonate or diethyl carbonate. This is because the dissociation property and ion mobility of the electrolyte salt are improved.

溶媒添加物として、不飽和炭素結合環状炭酸エステルを含んでいることが好ましい。充放電時に負極表面に安定な被膜が形成され、電解液の分解反応が抑制できるからである。不飽和炭素結合環状炭酸エステルとして、例えば炭酸ビニレン又は炭酸ビニルエチレンなどが挙げられる。   The solvent additive preferably contains an unsaturated carbon bond cyclic carbonate. This is because a stable film is formed on the surface of the negative electrode during charging and discharging, and the decomposition reaction of the electrolytic solution can be suppressed. Examples of the unsaturated carbon bond cyclic ester carbonate include vinylene carbonate and vinyl ethylene carbonate.

また溶媒添加物として、スルトン（環状スルホン酸エステル）を含んでいることが好ましい。電池の化学的安定性が向上するからである。スルトンとしては、例えばプロパンスルトン、プロペンスルトンが挙げられる。   The solvent additive preferably contains sultone (cyclic sulfonic acid ester). This is because the chemical stability of the battery is improved. Examples of sultone include propane sultone and propene sultone.

さらに、溶媒は、酸無水物を含んでいることが好ましい。電解液の化学的安定性が向上するからである。酸無水物としては、例えば、プロパンジスルホン酸無水物が挙げられる。   Furthermore, it is preferable that the solvent contains an acid anhydride. This is because the chemical stability of the electrolytic solution is improved. Examples of the acid anhydride include propanedisulfonic acid anhydride.

電解質塩は、例えば、リチウム塩などの軽金属塩のいずれか１種類以上含むことができる。リチウム塩として、例えば、六フッ化リン酸リチウム（ＬｉＰＦ６）、四フッ化ホウ酸リチウム（ＬｉＢＦ４）などが挙げられる。   The electrolyte salt can contain, for example, any one or more of light metal salts such as lithium salts. Examples of the lithium salt include lithium hexafluorophosphate (LiPF6) and lithium tetrafluoroborate (LiBF4).

電解質塩の含有量は、溶媒に対して０．５ｍｏｌ／ｋｇ以上２．５ｍｏｌ／ｋｇ以下であることが好ましい。これは、高いイオン伝導性が得られるからである。   The content of the electrolyte salt is preferably 0.5 mol / kg or more and 2.5 mol / kg or less with respect to the solvent. This is because high ion conductivity is obtained.

［ラミネートフィルム型二次電池の製造方法］ [Production method of laminated film type secondary battery]

最初に上記した正極材を用い正極電極を作製する。まず、正極活物質と、必要に応じて正極結着剤、正極導電助剤などを混合し正極合剤としたのち、有機溶剤に分散させ正極合剤スラリーとする。続いて、ナイフロール又はダイヘッドを有するダイコーターなどのコーティング装置で正極集電体に合剤スラリーを塗布し、熱風乾燥させて正極活物質層を得る。最後に、ロールプレス機などで正極活物質層を圧縮成型する。この時、加熱しても良く、また圧縮を複数回繰り返しても良い。   First, a positive electrode is manufactured using the positive electrode material described above. First, a positive electrode active material and, if necessary, a positive electrode binder and a positive electrode conductive additive are mixed to form a positive electrode mixture, which is then dispersed in an organic solvent to form a positive electrode mixture slurry. Subsequently, the mixture slurry is applied to the positive electrode current collector with a coating apparatus such as a die coater having a knife roll or a die head, and dried with hot air to obtain a positive electrode active material layer. Finally, the positive electrode active material layer is compression molded with a roll press or the like. At this time, heating may be performed or compression may be repeated a plurality of times.

次に、上記したリチウムイオン二次電池用負極１０の作製と同様の作業手順を用い、負極集電体に負極活物質層を形成し負極を作製する。   Next, a negative electrode is produced by forming a negative electrode active material layer on the negative electrode current collector, using the same operation procedure as the production of the negative electrode 10 for a lithium ion secondary battery described above.

正極及び負極を作製する際に、正極及び負極集電体の両面にそれぞれの活物質層を形成する。この時、どちらの電極においても両面部の活物質塗布長がずれていても良い（図１を参照）。   When producing the positive electrode and the negative electrode, respective active material layers are formed on both surfaces of the positive electrode and the negative electrode current collector. At this time, the active material application length of both surface portions may be shifted in either electrode (see FIG. 1).

続いて、電解液を調整する。続いて、超音波溶接などにより、正極集電体に正極リード３２を取り付けると共に、負極集電体に負極リード３３を取り付ける。続いて、正極と負極とをセパレータを介して積層、又は巻回させて巻回電極体３１を作製し、その最外周部に保護テープを接着させる。次に、扁平な形状となるように巻回体を成型する。続いて、折りたたんだフィルム状の外装部材３５の間に巻回電極体を挟み込んだ後、熱融着法により外装部材の絶縁部同士を接着させ、一方向のみ解放状態にて、巻回電極体を封入する。続いて、正極リード、及び負極リードと外装部材の間に密着フィルムを挿入する。続いて、解放部から上記調整した電解液を所定量投入し、真空含浸を行う。含浸後、解放部を真空熱融着法により接着させる。以上のようにして、ラミネートフィルム型二次電池３０を製造することができる。   Subsequently, the electrolytic solution is adjusted. Subsequently, the positive electrode lead 32 is attached to the positive electrode current collector and the negative electrode lead 33 is attached to the negative electrode current collector by ultrasonic welding or the like. Subsequently, the positive electrode and the negative electrode are laminated or wound via a separator to produce a wound electrode body 31, and a protective tape is bonded to the outermost periphery. Next, the wound body is molded so as to have a flat shape. Subsequently, after sandwiching the wound electrode body between the folded film-shaped exterior member 35, the insulating portions of the exterior member are bonded to each other by a thermal fusion method, and the wound electrode body is released in only one direction. Enclose. Subsequently, an adhesion film is inserted between the positive electrode lead and the negative electrode lead and the exterior member. Subsequently, a predetermined amount of the adjusted electrolytic solution is introduced from the release portion, and vacuum impregnation is performed. After impregnation, the release part is bonded by a vacuum heat fusion method. The laminated film type secondary battery 30 can be manufactured as described above.

上記作製したラミネートフィルム型二次電池３０等の本発明の非水電解質二次電池において、充放電時の負極利用率が９３％以上９９％以下であることが好ましい。負極利用率を９３％以上の範囲とすれば、初回充電効率が低下せず、電池容量の向上を大きくできる。また、負極利用率を９９％以下の範囲とすれば、Ｌｉが析出してしまうことがなく安全性を確保できる。   In the non-aqueous electrolyte secondary battery of the present invention such as the laminated film type secondary battery 30 produced as described above, the negative electrode utilization rate during charge / discharge is preferably 93% or more and 99% or less. If the negative electrode utilization rate is in the range of 93% or more, the initial charge efficiency does not decrease, and the battery capacity can be greatly improved. Moreover, if the negative electrode utilization rate is in the range of 99% or less, Li is not precipitated and safety can be ensured.

以下、本発明の実施例及び比較例を示して本発明をより具体的に説明するが、本発明はこれら実施例に限定されるものではない。   EXAMPLES Hereinafter, the present invention will be described more specifically with reference to examples and comparative examples of the present invention, but the present invention is not limited to these examples.

（実施例１−１）
以下の手順により、図３に示したラミネートフィルム型の二次電池３０を作製した。 (Example 1-1)
The laminate film type secondary battery 30 shown in FIG. 3 was produced by the following procedure.

最初に正極を作製した。正極活物質はリチウムニッケルコバルトアルミニウム複合酸化物（ＬｉＮｉ０．７Ｃｏ０．２５Ａｌ０．０５Ｏ）９５質量部と、正極導電助剤（アセチレンブラック）２．５質量部と、正極結着剤（ポリフッ化ビニリデン、ＰＶＤＦ）２．５質量部とを混合し正極合剤とした。続いて正極合剤を有機溶剤（Ｎ−メチル−２−ピロリドン、ＮＭＰ）に分散させてペースト状のスラリーとした。続いてダイヘッドを有するコーティング装置で正極集電体の両面にスラリーを塗布し、熱風式乾燥装置で乾燥した。この時、正極集電体は厚み１５μｍのものを用いた。最後にロールプレスで圧縮成型を行った。 First, a positive electrode was produced. The positive electrode active material is 95 parts by mass of lithium nickel cobalt aluminum composite oxide (LiNi 0.7 Co 0.25 Al 0.05 O), 2.5 parts by mass of positive electrode conductive additive (acetylene black), and a positive electrode binder. (Polyvinylidene fluoride, PVDF) 2.5 parts by mass were mixed to obtain a positive electrode mixture. Subsequently, the positive electrode mixture was dispersed in an organic solvent (N-methyl-2-pyrrolidone, NMP) to obtain a paste slurry. Subsequently, the slurry was applied to both surfaces of the positive electrode current collector with a coating apparatus having a die head, and dried with a hot air drying apparatus. At this time, a positive electrode current collector having a thickness of 15 μm was used. Finally, compression molding was performed with a roll press.

次に負極を作製した。まず、ケイ素系活物質を以下のように作製した。金属ケイ素と二酸化ケイ素を混合した原料を反応炉へ設置し、１０Ｐａの真空度の雰囲気中で気化させたものを吸着板上に堆積させ、十分に冷却した後、堆積物を取出しボールミルで粉砕した。粒径を調整した後、熱ＣＶＤを行うことで炭素被膜を被覆した。作製した粉末はエチレンカーボネート及びジメチルカーボネートの体積比が３：７の混合溶媒（電解質塩を１．３ｍｏｌ／ｋｇの濃度で含んでいる。）中で電気化学法を用いバルク改質を行った。次に、改質後の酸化珪素粒子をエチレンカーボネート（ＥＣ）、ジエチルカーボネート（ＤＥＣ）、ＬｉＢＦ４の混合溶液で洗浄し、濾過、乾燥しＤＥＣを除去した。これにより、エチレンカーボネート及びＬｉＢＦ４を含む環状カーボネート層を形成した。 Next, a negative electrode was produced. First, a silicon-based active material was prepared as follows. A raw material mixed with metallic silicon and silicon dioxide was placed in a reaction furnace, and vaporized in a 10 Pa vacuum atmosphere was deposited on an adsorption plate, cooled sufficiently, and the deposit was taken out and pulverized with a ball mill. . After adjusting the particle size, the carbon film was coated by performing thermal CVD. The produced powder was subjected to bulk reforming using an electrochemical method in a mixed solvent having an ethylene carbonate and dimethyl carbonate volume ratio of 3: 7 (containing an electrolyte salt at a concentration of 1.3 mol / kg). Next, the modified silicon oxide particles were washed with a mixed solution of ethylene carbonate (EC), diethyl carbonate (DEC), and LiBF 4 , filtered and dried to remove DEC. Thereby, the cyclic carbonate layer containing ethylene carbonate and LiBF 4 was formed.

以上のようにして作製したケイ素系活物質と、炭素系活物質を１：９の質量比で配合し、負極活物質を作製した。ここで、炭素系活物質としては、ピッチ層で被覆した天然黒鉛及び人造黒鉛を５：５の質量比で混合したものを使用した。また、炭素系活物質のメディアン径は２０μｍであった。   The negative electrode active material was produced by blending the silicon-based active material prepared as described above and the carbon-based active material in a mass ratio of 1: 9. Here, as the carbon-based active material, a mixture of natural graphite and artificial graphite coated with a pitch layer at a mass ratio of 5: 5 was used. The median diameter of the carbon-based active material was 20 μm.

次に、作製した負極活物質、導電助剤１（カーボンナノチューブ、ＣＮＴ）、導電助剤２（メディアン径が約５０nｍの炭素微粒子）、スチレンブタジエンゴム（スチレンブタジエンコポリマー、以下、ＳＢＲと称する）、カルボキシメチルセルロース（以下、ＣＭＣと称する）９２.５：１：１：２．５：３の乾燥重量比で混合した後、純水で希釈し負極合剤スラリーとした。尚、上記のＳＢＲ、ＣＭＣ、は負極バインダー（負極結着剤）である。ここで、負極合剤スラリーのｐＨを測定し、スラリーの安定性を評価した。なお、負極合剤スラリーのｐＨは、負極合剤スラリーを作製して１時間経過した後に測定を行った。   Next, the produced negative electrode active material, conductive additive 1 (carbon nanotube, CNT), conductive additive 2 (carbon fine particles having a median diameter of about 50 nm), styrene butadiene rubber (styrene butadiene copolymer, hereinafter referred to as SBR), Carboxymethyl cellulose (hereinafter referred to as CMC) was mixed at a dry weight ratio of 92.5: 1: 1: 2.5: 3, and then diluted with pure water to obtain a negative electrode mixture slurry. In addition, said SBR and CMC are negative electrode binders (negative electrode binder). Here, the pH of the negative electrode mixture slurry was measured to evaluate the stability of the slurry. The pH of the negative electrode mixture slurry was measured after 1 hour had elapsed after the negative electrode mixture slurry was prepared.

また、負極集電体としては、電解銅箔（厚さ１５μｍ）を用いた。最後に、負極合剤スラリーを負極集電体に塗布し真空雰囲気中で１００℃×１時間の乾燥を行った。乾燥後の、負極の片面における単位面積あたりの負極活物質層の堆積量（面積密度とも称する）は５ｍｇ／ｃｍ２であった。 Further, as the negative electrode current collector, an electrolytic copper foil (thickness 15 μm) was used. Finally, the negative electrode mixture slurry was applied to the negative electrode current collector and dried in a vacuum atmosphere at 100 ° C. for 1 hour. The amount of deposition (also referred to as area density) of the negative electrode active material layer per unit area on one side of the negative electrode after drying was 5 mg / cm 2 .

次に、溶媒として、フルオロエチレンカーボネート（ＦＥＣ）、エチレンカーボネート（ＥＣ）及びジエチルカーボネート（ＤＥＣ））を混合したのち、電解質塩（六フッ化リン酸リチウム：ＬｉＰＦ６）を溶解させて電解液を調製した。この場合には、溶媒の組成を体積比でＦＥＣ：ＥＣ：ＤＥＣ＝1：２：７とし、電解質塩の含有量を溶媒に対して１．０ｍｏｌ／ｋｇとした。さらに、得られた電解液にビニレンカーボネート（ＶＣ）を１．５質量％添加した。 Next, after mixing fluoroethylene carbonate (FEC), ethylene carbonate (EC) and diethyl carbonate (DEC) as a solvent, an electrolyte salt (lithium hexafluorophosphate: LiPF 6 ) is dissolved to obtain an electrolyte solution. Prepared. In this case, the composition of the solvent was FEC: EC: DEC = 1: 2: 7 by volume, and the content of the electrolyte salt was 1.0 mol / kg with respect to the solvent. Furthermore, 1.5% by mass of vinylene carbonate (VC) was added to the obtained electrolytic solution.

次に、以下のようにして二次電池を組み立てた。最初に、正極集電体の一端にアルミリードを超音波溶接し、負極集電体にはニッケルリードを溶接した。続いて、正極、セパレータ、負極、セパレータをこの順に積層し、長手方向に巻回させ巻回電極体を得た。その捲き終わり部分をＰＥＴ保護テープで固定した。セパレータは多孔性ポリプロピレンを主成分とするフィルムにより多孔性ポリエチレンを主成分とするフィルムに挟まれた積層フィルム１２μｍを用いた。続いて、外装部材間に電極体を挟んだのち、一辺を除く外周縁部同士を熱融着し、内部に電極体を収納した。外装部材はナイロンフィルム、アルミ箔及び、ポリプロピレンフィルムが積層されたアルミラミネートフィルムを用いた。続いて、開口部から調整した電解液を注入し、真空雰囲気下で含浸した後、熱融着し封止した。   Next, a secondary battery was assembled as follows. First, an aluminum lead was ultrasonically welded to one end of the positive electrode current collector, and a nickel lead was welded to the negative electrode current collector. Subsequently, a positive electrode, a separator, a negative electrode, and a separator were laminated in this order and wound in the longitudinal direction to obtain a wound electrode body. The end portion was fixed with PET protective tape. As the separator, a laminated film of 12 μm sandwiched between a film mainly composed of porous polyethylene and a film mainly composed of porous polypropylene was used. Subsequently, after sandwiching the electrode body between the exterior members, the outer peripheral edges except for one side were heat-sealed, and the electrode body was housed inside. As the exterior member, a nylon film, an aluminum foil, and an aluminum laminate film in which a polypropylene film was laminated were used. Subsequently, the prepared electrolyte was injected from the opening, impregnated in a vacuum atmosphere, and then heat-sealed and sealed.

以上のようにして作製した二次電池のサイクル特性及び初回充放電特性を評価した。   The cycle characteristics and initial charge / discharge characteristics of the secondary batteries produced as described above were evaluated.

サイクル特性については、以下のようにして調べた。最初に、電池安定化のため２５℃の雰囲気下、０．２Ｃで２サイクル充放電を行い、２サイクル目の放電容量を測定した。続いて、総サイクル数が４９９サイクルとなるまで充放電を行い、その都度放電容量を測定した。最後に、０．２Ｃ充放電で得られた５００サイクル目の放電容量を２サイクル目の放電容量で割り、容量維持率（以下、単に維持率ともいう）を算出した。通常サイクル、すなわち３サイクル目から４９９サイクル目までは、充電０．７Ｃ、放電０．５Ｃで充放電を行った。   The cycle characteristics were examined as follows. First, in order to stabilize the battery, charge and discharge was performed for 2 cycles at 0.2 C in an atmosphere at 25 ° C., and the discharge capacity at the second cycle was measured. Subsequently, charge and discharge were performed until the total number of cycles reached 499 cycles, and the discharge capacity was measured each time. Finally, the discharge capacity at the 500th cycle obtained by 0.2 C charge / discharge was divided by the discharge capacity at the second cycle to calculate a capacity retention rate (hereinafter also simply referred to as a maintenance rate). In the normal cycle, that is, from the 3rd cycle to the 499th cycle, charging and discharging were performed with a charge of 0.7 C and a discharge of 0.5 C.

初回充放電特性を調べる場合には、初回効率（以下では初期効率と呼ぶ場合もある）を算出した。初回効率は、初回効率（％）＝（初回放電容量／初回充電容量）×１００で表される式から算出した。雰囲気温度は、サイクル特性を調べた場合と同様にした。   When examining the initial charge / discharge characteristics, the initial efficiency (hereinafter sometimes referred to as initial efficiency) was calculated. The initial efficiency was calculated from an equation represented by initial efficiency (%) = (initial discharge capacity / initial charge capacity) × 100. The ambient temperature was the same as when the cycle characteristics were examined.

実施例１−１及び後述の実施例１−２〜実施例１−９、比較例１−１〜比較例１−４の負極合剤スラリーの安定性（ｐＨ）、二次電池のサイクル特性（維持率％）、初回充放電特性（初期効率％）を調べたところ、表１に示した結果が得られた。   The stability (pH) of the negative electrode mixture slurry of Example 1-1 and Examples 1-2 to 1-9 and Comparative Examples 1-1 to 1-4 described later, and cycle characteristics of the secondary battery ( Maintenance rate%) and initial charge / discharge characteristics (initial efficiency%) were examined. The results shown in Table 1 were obtained.

（実施例１−２〜実施例１−９）
ケイ素化合物の質量に対する環状カーボネート層の質量の割合を表１に示すように変更したこと以外、基本的に実施例１−１と同様にして二次電池を作製した。環状カーボネート層の被覆量の調整はＥＣとＤＥＣの比率を変えることで調整できる。例えば、上記質量の割合が２質量％となるように環状カーボネート層を被覆する場合、ＥＣ：ＤＥＣ＝５：９５の比に調整する。 (Example 1-2 to Example 1-9)
A secondary battery was fabricated basically in the same manner as in Example 1-1 except that the ratio of the mass of the cyclic carbonate layer to the mass of the silicon compound was changed as shown in Table 1. Adjustment of the coating amount of the cyclic carbonate layer can be adjusted by changing the ratio of EC and DEC. For example, when the cyclic carbonate layer is coated so that the mass ratio is 2 mass%, the ratio is adjusted to EC: DEC = 5: 95.

また、実施例１−１と同様に、スラリーの安定性、作製した二次電池のサイクル特性及び初回充放電特性を評価した。   Further, as in Example 1-1, the stability of the slurry, the cycle characteristics of the produced secondary battery, and the initial charge / discharge characteristics were evaluated.

（比較例１−１）
ケイ素化合物にＬｉ化合物を生成しなかったことと、環状カーボネート層を形成しなかったこと以外、基本的に実施例１−１と同様にして二次電池を作製した。また、実施例１−１と同様に、スラリーの安定性、作製した二次電池のサイクル特性及び初回充放電特性を評価した。 (Comparative Example 1-1)
A secondary battery was fabricated basically in the same manner as in Example 1-1 except that no Li compound was produced in the silicon compound and no cyclic carbonate layer was formed. Further, as in Example 1-1, the stability of the slurry, the cycle characteristics of the produced secondary battery, and the initial charge / discharge characteristics were evaluated.

（比較例１−２〜比較例１−３）
環状カーボネート層を形成しなかったこと以外、基本的に実施例１−１と同様にして二次電池を作製した。また、実施例１−１と同様に、スラリーの安定性、作製した二次電池のサイクル特性及び初回充放電特性を評価した。なお、比較例１−３では、環状カーボネート層は形成しなかったが、ＬｉＢＦ４を含む層を、その質量がケイ素化合物の質量に対し０．１質量％となるようにケイ素化合物の表面に形成した。 (Comparative Example 1-2 to Comparative Example 1-3)
A secondary battery was fabricated basically in the same manner as in Example 1-1 except that the cyclic carbonate layer was not formed. Further, as in Example 1-1, the stability of the slurry, the cycle characteristics of the produced secondary battery, and the initial charge / discharge characteristics were evaluated. In Comparative Example 1-3, the cyclic carbonate layer was not formed, but the layer containing LiBF 4 was formed on the surface of the silicon compound so that the mass thereof was 0.1% by mass with respect to the mass of the silicon compound. did.

（比較例１−４）
環状カーボネート層を形成したが、Ｌｉ塩を含ませなかったこと以外、基本的に実施例１−１と同様にして二次電池を作製した。また、実施例１−１と同様に、スラリーの安定性、作製した二次電池のサイクル特性及び初回充放電特性を評価した。 (Comparative Example 1-4)
A secondary battery was fabricated basically in the same manner as in Example 1-1 except that a cyclic carbonate layer was formed but no Li salt was included. Further, as in Example 1-1, the stability of the slurry, the cycle characteristics of the produced secondary battery, and the initial charge / discharge characteristics were evaluated.

このとき、実施例１−１〜１−９及び比較例１−１〜１−４のケイ素系活物質粒子は以下のような性質を有していた。環状カーボネート層の有無、被覆量、環状カーボネート種、Ｌｉ塩の有無、Ｌｉ塩種、ケイ素化合物に含まれるＬｉ化合物、炭酸リチウム及びフッ化リチウムのうち１種以上を含む層の有無については表１の通りである。   At this time, the silicon-based active material particles of Examples 1-1 to 1-9 and Comparative Examples 1-1 to 1-4 had the following properties. Table 1 shows the presence or absence of a cyclic carbonate layer, the amount of coating, the presence or absence of a cyclic carbonate species, the presence or absence of a Li salt, the presence or absence of a Li salt species, a Li compound contained in a silicon compound, lithium carbonate and lithium fluoride. It is as follows.

ケイ素系活物質粒子は、ＳｉＯｘで表されるケイ素化合物のｘの値が１．０であり、ケイ素化合物のメディアン径Ｄ５０は４μｍであった。また、Ｘ線回折により得られるＳｉ（１１１）結晶面に起因する回折ピークの半値幅（２θ）は２．５９３°であり、その結晶面Ｓｉ（１１１）に起因する結晶子サイズは３．２９ｎｍであった。また、炭素被膜の被覆量が、ケイ素化合物と炭素被膜の合計に対し、５質量％であった。 In the silicon-based active material particles, the value of x of the silicon compound represented by SiO x was 1.0, and the median diameter D 50 of the silicon compound was 4 μm. Further, the half width (2θ) of the diffraction peak attributed to the Si (111) crystal plane obtained by X-ray diffraction is 2.593 °, and the crystallite size attributed to the crystal plane Si (111) is 3.29 nm. Met. Moreover, the coating amount of the carbon coating was 5% by mass with respect to the total of the silicon compound and the carbon coating.

Figure 0006448462
Figure 0006448462

スラリーのｐＨが１０を超えると、アルカリ性が強く、バインダーに悪影響を及ぼすので、電極塗布時に安定した塗膜を得ることが難しくなる。表１に示すように、実施例１−１〜１−９では、スラリーのｐＨは全て１０を下回り、安定した塗膜を得ることができることが確認された。一方で、ケイ素化合物が内部にＬｉ化合物を含み、かつ、環状カーボネート層を形成しなかった比較例１−２、１−３では、スラリーのｐＨが１０を超えてしまった。また、環状カーボネート層にＬｉ塩を含まない比較例１−４でもｐＨが１０を超え、アルカリ側に大きくふれてしまった。また、ケイ素化合物にＬｉ化合物を生成しなかった比較例１−１では、サイクル維持率及び初期効率が低下した。比較例１−１のように、ケイ素化合物にＬｉ化合物を生成しない場合、特に初回効率が低く、不可逆容量が大きいため、電池容量の向上が難しい。   When the pH of the slurry exceeds 10, the alkalinity is strong and adversely affects the binder, so that it is difficult to obtain a stable coating film at the time of electrode application. As shown in Table 1, in Examples 1-1 to 1-9, it was confirmed that the pH of the slurry was less than 10 and a stable coating film could be obtained. On the other hand, in Comparative Examples 1-2 and 1-3 in which the silicon compound contained a Li compound therein and no cyclic carbonate layer was formed, the pH of the slurry exceeded 10. Further, even in Comparative Example 1-4 in which the cyclic carbonate layer did not contain an Li salt, the pH exceeded 10 and the alkali side was greatly touched. Moreover, in Comparative Example 1-1 in which the Li compound was not generated in the silicon compound, the cycle retention rate and the initial efficiency were lowered. When the Li compound is not generated in the silicon compound as in Comparative Example 1-1, it is difficult to improve the battery capacity because the initial efficiency is particularly low and the irreversible capacity is large.

また、特に、環状カーボネート層の質量が、ケイ素化合物の質量に対し１５質量％以下である実施例１−１〜１−８では、特に良好なサイクル維持率が得られた。なお、ケイ素化合物の質量に対する環状カーボネート層の質量の割合は、環状カーボネート層の被覆後のケイ素化合物の粉末を２００℃で真空下４時間熱処理し、熱処理の前後の質量変化から算出した。   In particular, in Examples 1-1 to 1-8 in which the mass of the cyclic carbonate layer was 15% by mass or less with respect to the mass of the silicon compound, a particularly good cycle retention rate was obtained. The ratio of the mass of the cyclic carbonate layer to the mass of the silicon compound was calculated from the change in mass before and after the heat treatment of the silicon compound powder coated with the cyclic carbonate layer at 200 ° C. under vacuum for 4 hours.

（実施例２−１〜実施例２−６）
環状カーボネート層に含ませるＬｉ塩の種類を表２に示すように変更したこと以外、基本的に実施例１−４と同様にして二次電池を作製した。また、実施例１−４と同様に、スラリーの安定性、作製した二次電池のサイクル特性及び初回充放電特性を評価した。その結果を表２に示す。 (Example 2-1 to Example 2-6)
A secondary battery was made basically in the same manner as in Example 1-4, except that the type of Li salt contained in the cyclic carbonate layer was changed as shown in Table 2. Further, in the same manner as in Example 1-4, the stability of the slurry, the cycle characteristics of the produced secondary battery, and the initial charge / discharge characteristics were evaluated. The results are shown in Table 2.

Figure 0006448462
Figure 0006448462

表２に示すように、実施例２−１〜２−６で、ｐＨは１０以下となり、かつ良好なサイクル維持率及び初回効率が得られた。特に、環状カーボネート層に、ＬｉＰＦ６、ＬｉＣｌＯ４を含有させた場合に、ＬｉＢＦ４を含有させた場合と同様、ｐＨをより小さくできた。 As shown in Table 2, in Examples 2-1 to 2-6, the pH was 10 or less, and good cycle retention and initial efficiency were obtained. In particular, when LiPF 6 and LiClO 4 were included in the cyclic carbonate layer, the pH could be further reduced as in the case where LiBF 4 was included.

（実施例３−１〜実施例３−６）
環状カーボネートの種類を表３に示すように変更したこと以外、基本的に実施例１−４と同様にして二次電池を作製した。また、実施例１−４と同様に、スラリーの安定性、作製した二次電池のサイクル特性及び初回充放電特性を評価した。その結果を表３に示す。なお、表３において、ＦＥＣはフルオロエチレンカーボネート、ＰＣはプロピレンカーボネート、ＤＦＥＣはジフルオロエチレンカーボネート、ＶＣはビニレンカーボネートを表している。実施例３−１、３−６におけるそれぞれの環状カーボネートの混合比率は５０：５０（体積比）である。 (Example 3-1 to Example 3-6)
A secondary battery was made basically in the same manner as in Example 1-4, except that the type of cyclic carbonate was changed as shown in Table 3. Further, in the same manner as in Example 1-4, the stability of the slurry, the cycle characteristics of the produced secondary battery, and the initial charge / discharge characteristics were evaluated. The results are shown in Table 3. In Table 3, FEC represents fluoroethylene carbonate, PC represents propylene carbonate, DFEC represents difluoroethylene carbonate, and VC represents vinylene carbonate. The mixing ratio of each cyclic carbonate in Examples 3-1 and 3-6 is 50:50 (volume ratio).

Figure 0006448462
Figure 0006448462

表３に示すように、実施例３−１〜３−６で、ｐＨは１０以下となり、かつ良好なサイクル維持率及び初回効率が得られた。環状カーボネートとしてＦＥＣを含む場合、特に良好なサイクル維持率及び初回効率が得られた。   As shown in Table 3, in Examples 3-1 to 3-6, the pH was 10 or less, and good cycle maintenance ratio and initial efficiency were obtained. When FEC was included as the cyclic carbonate, particularly good cycle retention and initial efficiency were obtained.

（実施例４−１、４−２、比較例４−１、４−２）
ＳｉＯｘで表わされるケイ素化合物において、酸素量を調整したこと以外、基本的に実施例１−４と同様に、二次電池を作製した。また、実施例１−４と同様に、スラリーの安定性、作製した二次電池のサイクル特性及び初回充放電特性を評価した。その結果を表４に示す。 (Examples 4-1, 4-2, Comparative examples 4-1, 4-2)
A secondary battery was fabricated basically in the same manner as in Example 1-4 except that the amount of oxygen was adjusted in the silicon compound represented by SiOx. Further, in the same manner as in Example 1-4, the stability of the slurry, the cycle characteristics of the produced secondary battery, and the initial charge / discharge characteristics were evaluated. The results are shown in Table 4.

Figure 0006448462
Figure 0006448462

ケイ素化合物中の酸素量が減る、すなわちｘ＜０．５となると、Ｓｉリッチとなり、サイクル維持率が大幅に低下した。また酸素リッチの場合、すなわちｘ＞１．６となる場合、ケイ素酸化物の抵抗が高くなり、サイクル維持率が大幅に低下した。   When the amount of oxygen in the silicon compound was reduced, that is, when x <0.5, Si was rich, and the cycle retention rate was significantly reduced. Further, in the case of oxygen rich, that is, when x> 1.6, the resistance of the silicon oxide was increased, and the cycle maintenance ratio was greatly reduced.

（実施例５−１）
ケイ素化合物の表面に炭素被膜を形成しなかったこと以外、基本的に実施例１−４と同様に、二次電池を作製した。また、実施例１−４と同様に、スラリーの安定性、作製した二次電池のサイクル特性及び初回充放電特性を評価した。その結果を表５に示す。 (Example 5-1)
A secondary battery was produced basically in the same manner as in Example 1-4, except that no carbon film was formed on the surface of the silicon compound. Further, in the same manner as in Example 1-4, the stability of the slurry, the cycle characteristics of the produced secondary battery, and the initial charge / discharge characteristics were evaluated. The results are shown in Table 5.

Figure 0006448462
Figure 0006448462

表５に示すように、ケイ素化合物が炭素被膜を有する場合、サイクル特性が大きく向上した。   As shown in Table 5, when the silicon compound had a carbon film, the cycle characteristics were greatly improved.

（実施例６−１〜実施例６−９）
ケイ素化合物の結晶性を変化させたこと以外、基本的に実施例１−４と同様に二次電池の製造を行った。また、実施例１−４と同様に、スラリーの安定性、作製した二次電池のサイクル特性及び初回充放電特性を評価した。なお、結晶性の変化は非大気雰囲気下の熱処理で制御可能である。ケイ素系活物質のＸ線回折により得られる（１１１）結晶面に起因する回折ピークの半値幅２θ（°）を表６に示す。なお、実施例６−９では半値幅を２０°以上と算出しているが、解析ソフトを用いフィッティングした結果であり、実質的にピークは得られていない。よって実施例６−９のケイ素化合物は、実質的に非晶質であると言える。 (Example 6-1 to Example 6-9)
A secondary battery was produced basically in the same manner as in Example 1-4 except that the crystallinity of the silicon compound was changed. Further, in the same manner as in Example 1-4, the stability of the slurry, the cycle characteristics of the produced secondary battery, and the initial charge / discharge characteristics were evaluated. Note that the change in crystallinity can be controlled by heat treatment in a non-atmospheric atmosphere. Table 6 shows the half-value width 2θ (°) of the diffraction peak caused by the (111) crystal plane obtained by X-ray diffraction of the silicon-based active material. In Example 6-9, the half-value width is calculated to be 20 ° or more, but it is a result of fitting using analysis software, and a peak is not substantially obtained. Therefore, it can be said that the silicon compound of Example 6-9 is substantially amorphous.

Figure 0006448462
Figure 0006448462

表６に示すように、特に半値幅（２θ）が１．２°以上で、尚且つＳｉ（１１１）面に起因する結晶子サイズが７．５ｎｍ以下の低結晶性材料で、高い容量維持率及び安定したスラリー特性が得られた。   As shown in Table 6, a high capacity retention ratio is obtained with a low crystalline material having a half width (2θ) of 1.2 ° or more and a crystallite size due to the Si (111) plane of 7.5 nm or less. And stable slurry properties were obtained.

（実施例７−１〜実施例７−６）
ケイ素系化合物のメディアン径を表７に示すように変化させたこと以外、基本的に実施例１−４と同様に二次電池の製造を行った。また、実施例１−４と同様に、スラリーの安定性、作製した二次電池のサイクル特性及び初回充放電特性を評価した。その結果を表７に示す。 (Example 7-1 to Example 7-6)
A secondary battery was produced basically in the same manner as in Example 1-4, except that the median diameter of the silicon compound was changed as shown in Table 7. Further, in the same manner as in Example 1-4, the stability of the slurry, the cycle characteristics of the produced secondary battery, and the initial charge / discharge characteristics were evaluated. The results are shown in Table 7.

Figure 0006448462
Figure 0006448462

表７に示すように、ケイ素化合物のメディアン径が０．５μｍ以上であれば、維持率が向上し、かつ、スラリーのｐＨが小さくなった。これは、ケイ素化合物の表面積が大すぎず、副反応が起きる面積を小さくできたためと考えられる。一方、メディアン径が２０μｍ以下であれば、充電時に粒子が割れ難く、表面の耐水効果が低下することが無い。さらに、メディアン径が２０μｍ以下であれば、粒子の表面に新生面が生成し難く、充放電時に新生面によるＳＥＩが生成し難いため、可逆Ｌｉの損失を抑制することができる。   As shown in Table 7, when the median diameter of the silicon compound was 0.5 μm or more, the maintenance ratio was improved, and the pH of the slurry was reduced. This is presumably because the surface area of the silicon compound was not too large and the area where the side reaction occurred could be reduced. On the other hand, if the median diameter is 20 μm or less, the particles are difficult to break during charging, and the water resistance effect on the surface does not deteriorate. Furthermore, if the median diameter is 20 μm or less, a new surface is hardly generated on the surface of the particles, and SEI due to the new surface is difficult to be generated during charging and discharging, and therefore loss of reversible Li can be suppressed.

（実施例８−１〜実施例８−３、比較例８−１）
負極活物質中のケイ素系活物質と炭素系活物質の質量比を変化させたこと以外、基本的に実施例１−４と同様に二次電池の製造を行った。なお、ケイ素系活物質の量を増やす場合、導電助剤、及びバインダーの量は実施例１−４と同様とし、炭素系活物質の比率のみ変化させた。実施例１−４と同様に、スラリーの安定性、作製した二次電池のサイクル特性及び初回充放電特性を評価した。その結果を表８に示す。 (Example 8-1 to Example 8-3, Comparative Example 8-1)
A secondary battery was produced basically in the same manner as in Example 1-4, except that the mass ratio of the silicon-based active material and the carbon-based active material in the negative electrode active material was changed. In addition, when increasing the quantity of a silicon type active material, the quantity of the conductive support agent and the binder was made the same as that of Example 1-4, and only the ratio of the carbon type active material was changed. In the same manner as in Example 1-4, the stability of the slurry, the cycle characteristics of the produced secondary battery, and the initial charge / discharge characteristics were evaluated. The results are shown in Table 8.

Figure 0006448462
Figure 0006448462

負極活物質中のケイ素系活物質の割合を高くするほど高い電池容量が得られるが、表８に示すように、維持率、初期効率が低下する。また、Ｌｉを用いて改質したケイ素系活物質の割合を高くしても、スラリーのｐＨは１０を下回っていた。一方、表８から分かるように、改質されていないケイ素化合物はスラリー耐性が高いが初回効率が極端に低くなるため、高容量化がはかり難い。   As the ratio of the silicon-based active material in the negative electrode active material is increased, a higher battery capacity is obtained. However, as shown in Table 8, the maintenance ratio and the initial efficiency are lowered. Moreover, even if the ratio of the silicon-based active material modified with Li was increased, the pH of the slurry was lower than 10. On the other hand, as can be seen from Table 8, the unmodified silicon compound has high slurry resistance, but the initial efficiency is extremely low, so it is difficult to increase the capacity.

（実施例９−１〜実施例９−３）
環状カーボネート層に表９に示すような鎖状カーボネートを含有させたこと以外、基本的に実施例１−４と同様に二次電池の製造を行った。ケイ素化合物の洗浄後の濾過において、急激に濾過を行う、つまり濾過にかかる時間を短くすることで、環状カーボネート層内の一部に微量ではあるが、鎖状カーボネートを封止する事ができる。また、封止する鎖状カーボネートの種類を変えるには、洗浄に使用する混合溶液に含ませる鎖状カーボネートの種類を変更すればよい。 (Example 9-1 to Example 9-3)
A secondary battery was produced basically in the same manner as in Example 1-4 except that the cyclic carbonate layer contained a chain carbonate as shown in Table 9. In the filtration after washing the silicon compound, the chain carbonate can be sealed in a part of the cyclic carbonate layer by abrupt filtration, that is, by shortening the time required for filtration. Moreover, what is necessary is just to change the kind of chain carbonate contained in the mixed solution used for washing | cleaning, in order to change the kind of chain carbonate to seal.

実施例１−４と同様に、スラリーの安定性、作製した二次電池のサイクル特性及び初回充放電特性を評価した。その結果を表９に示す。なお。表９における、ＤＭＣはジメチルカーボネート、ＥＭＣはエチルメチルカーボネートを表す。   In the same manner as in Example 1-4, the stability of the slurry, the cycle characteristics of the produced secondary battery, and the initial charge / discharge characteristics were evaluated. The results are shown in Table 9. Note that. In Table 9, DMC represents dimethyl carbonate, and EMC represents ethyl methyl carbonate.

Figure 0006448462
Figure 0006448462

表９から分かるように、環状カーボネート層が鎖状カーボネートを含めば、ｐＨはより小さくなり、スラリーの安定性がより向上することが分かった。   As can be seen from Table 9, it was found that if the cyclic carbonate layer contains a chain carbonate, the pH becomes smaller and the stability of the slurry is further improved.

なお、本発明は、上記実施形態に限定されるものではない。上記実施形態は例示であり、本発明の特許請求の範囲に記載された技術的思想と実質的に同一な構成を有し、同様な作用効果を奏するものは、いかなるものであっても本発明の技術的範囲に包含される。   The present invention is not limited to the above embodiment. The above-described embodiment is an exemplification, and the present invention has any configuration that has substantially the same configuration as the technical idea described in the claims of the present invention and that exhibits the same effects. Are included in the technical scope.

１０…負極、 １１…負極集電体、 １２…負極活物質層、
２０…Ｌｉドープ改質装置、 ２１…陽電極（リチウム源、改質源）、
２２…酸化ケイ素の粉末、 ２３…有機溶媒、 ２４…セパレータ、
２５…粉末格納容器、 ２６…電源、 ２７…浴槽、
３０…リチウムイオン二次電池（ラミネートフィルム型）、 ３１…電極体、
３２…正極リード（正極アルミリード）、
３３…負極リード（負極ニッケルリード）、 ３４…密着フィルム、
３５…外装部材。 10 ... negative electrode, 11 ... negative electrode current collector, 12 ... negative electrode active material layer,
20 ... Li doping reformer, 21 ... Positive electrode (lithium source, reforming source),
22 ... Silicon oxide powder, 23 ... Organic solvent, 24 ... Separator,
25 ... Powder container, 26 ... Power supply, 27 ... Bathtub,
30 ... Lithium ion secondary battery (laminate film type), 31 ... Electrode body,
32 ... Positive electrode lead (positive electrode aluminum lead),
33 ... negative electrode lead (negative electrode nickel lead), 34 ... adhesion film,
35 ... exterior member.

Claims (12)

負極活物質粒子を有し、該負極活物質粒子はＬｉ化合物が含まれるケイ素化合物（ＳｉＯｘ：０．５≦ｘ≦１．６）を含有するものである水系スラリー用の非水電解質二次電池用負極活物質であって、
前記負極活物質粒子が、前記ケイ素化合物の表面に炭素被膜を有し、
前記負極活物質粒子が、環状カーボネートを含む環状カーボネート層を表面に有し、
該環状カーボネート層の質量が、前記ケイ素化合物の質量に対し１５質量％以下のものであり、
前記環状カーボネート層が、さらにＬｉ塩を含むものであることを特徴とする水系スラリー用の非水電解質二次電池用負極活物質。 Non-aqueous electrolyte secondary for aqueous slurry , having negative electrode active material particles, wherein the negative electrode active material particles contain a silicon compound containing Li compound (SiO x : 0.5 ≦ x ≦ 1.6) A negative electrode active material for a battery,
The negative electrode active material particles have a carbon coating on the surface of the silicon compound;
The negative electrode active material particles have a cyclic carbonate layer containing cyclic carbonate on the surface,
The mass of the cyclic carbonate layer is 15% by mass or less based on the mass of the silicon compound,
The negative electrode active material for a non-aqueous electrolyte secondary battery for aqueous slurry , wherein the cyclic carbonate layer further contains a Li salt. 前記環状カーボネート層に含まれるＬｉ塩が、ＬｉＰＦ６、ＬｉＢＦ４、ＬｉＣｌＯ４、ＬｉＢＯＢ、ＬｉＦＳＡ、ＬｉＴＦＳＡ、及びＬｉＴＦＳＩのうち１種以上を含むものであることを特徴とする請求項１に記載の水系スラリー用の非水電解質二次電池用負極活物質。 2. The aqueous slurry according to claim 1, wherein the Li salt contained in the cyclic carbonate layer contains one or more of LiPF 6 , LiBF 4 , LiClO 4 , LiBOB, LiFSA, LiTFSA, and LiTFSI . negative electrode active material for a non-aqueous electrolyte secondary battery of. 前記環状カーボネート層に含まれる環状カーボネートが、エチレンカーボネート、プロピレンカーボネート、フルオロエチレンカーボネート、ジフルオロエチレンカーボネート、及びビニレンカーボネートのうち１種以上を含むものであることを特徴とする請求項１又は請求項２に記載の水系スラリー用の非水電解質二次電池用負極活物質。 The cyclic carbonate contained in the cyclic carbonate layer contains one or more of ethylene carbonate, propylene carbonate, fluoroethylene carbonate, difluoroethylene carbonate, and vinylene carbonate. Negative electrode active material for non-aqueous electrolyte secondary battery for aqueous slurry . 前記環状カーボネート層が、さらに鎖状カーボネートを含むものであることを特徴とする請求項１から請求項３のいずれか１項に記載の水系スラリー用の非水電解質二次電池用負極活物質。 The negative electrode active material for a non-aqueous electrolyte secondary battery for an aqueous slurry according to any one of claims 1 to 3 , wherein the cyclic carbonate layer further contains a chain carbonate. 前記負極活物質粒子は、前記ケイ素化合物と前記環状カーボネート層との間に、炭酸リチウム及びフッ化リチウムのうち１種以上を含むものであることを特徴とする請求項１から請求項４のいずれか１項に記載の水系スラリー用の非水電解質二次電池用負極活物質。 The negative active material particles, between the cyclic carbonate layer and the silicon compound, any one of claims 1 to 4, characterized in that it is intended to include one or more of lithium carbonate and lithium fluoride The negative electrode active material for nonaqueous electrolyte secondary batteries for aqueous slurry as described in an item. 前記ケイ素化合物に含まれるＬｉ化合物として、Ｌｉ２ＳｉＯ３、及びＬｉ４ＳｉＯ４のうち１種以上が存在するものであることを特徴とする請求項１から請求項５のいずれか１項に記載の水系スラリー用の非水電解質二次電池用負極活物質。 The Li compound contained in the silicon compound includes one or more of Li 2 SiO 3 and Li 4 SiO 4 , according to any one of claims 1 to 5. Negative electrode active material for non-aqueous electrolyte secondary battery for aqueous slurry . 前記ケイ素化合物は、電気化学的手法によりＬｉが挿入、脱離されることで、改質されたものであることを特徴とする請求項１から請求項６のいずれか１項に記載の水系スラリー用の非水電解質二次電池用負極活物質。 The water-based slurry according to any one of claims 1 to 6 , wherein the silicon compound is modified by insertion and desorption of Li by an electrochemical method . negative electrode active material for a non-aqueous electrolyte secondary battery of. 前記ケイ素化合物が、Ｘ線回折により得られるＳｉ（１１１）結晶面に起因する回折ピークの半値幅（２θ）が１．２°以上であると共に、その結晶面に起因する結晶子サイズが７．５ｎｍ以下のものであることを特徴とする請求項１から請求項７のいずれか１項に記載の水系スラリー用の非水電解質二次電池用負極活物質。 The silicon compound has a half-width (2θ) of a diffraction peak due to the Si (111) crystal plane obtained by X-ray diffraction of 1.2 ° or more and a crystallite size due to the crystal plane of 7. The negative electrode active material for a nonaqueous electrolyte secondary battery for an aqueous slurry according to any one of claims 1 to 7 , wherein the negative electrode active material is 5 nm or less. 前記ケイ素化合物のメディアン径が０．５μｍ以上２０μｍ以下のものであることを特徴とする請求項１から請求項８のいずれか１項に記載の水系スラリー用の非水電解質二次電池用負極活物質。 Negative active for a non-aqueous electrolyte secondary batteries for aqueous slurry as claimed in any one of claims 8, wherein the median diameter of the silicon compound is of 0.5μm or 20μm or less material. 請求項１から請求項９のいずれか１項に記載の水系スラリー用の非水電解質二次電池用負極活物質を含むことを特徴とする非水電解質二次電池。 A nonaqueous electrolyte secondary battery comprising the negative electrode active material for a nonaqueous electrolyte secondary battery for an aqueous slurry according to any one of claims 1 to 9 . 負極活物質粒子を含む水系スラリー用の非水電解質二次電池用負極活物質の製造方法であって、
一般式ＳｉＯｘ（０．５≦ｘ≦１．６）で表される酸化珪素粒子を作製する工程と、
該酸化珪素粒子の表面を炭素被膜で被覆する工程と、
前記酸化珪素粒子に、Ｌｉを挿入、脱離することで、前記酸化珪素粒子を改質する工程と、
前記改質後の酸化珪素粒子の表面に、Ｌｉ塩を含む環状カーボネートからなる環状カーボネート層を形成する工程とを有し、
該環状カーボネート層を形成する工程において、前記環状カーボネート層の質量を、前記酸化珪素粒子の質量に対し１５質量％以下とし、
前記環状カーボネート層が形成された酸化珪素粒子を前記負極活物質粒子として用いて、水系スラリー用の非水電解質二次電池用負極活物質を製造することを特徴とする水系スラリー用の非水電解質二次電池用負極活物質の製造方法。 A method of manufacturing a negative electrode active material for a non-aqueous electrolyte secondary batteries for aqueous slurry containing the negative electrode active material particles,
Producing silicon oxide particles represented by the general formula SiO x (0.5 ≦ x ≦ 1.6);
Coating the surface of the silicon oxide particles with a carbon coating;
Modifying the silicon oxide particles by inserting and desorbing Li from the silicon oxide particles;
Forming a cyclic carbonate layer made of cyclic carbonate containing Li salt on the surface of the modified silicon oxide particles,
In the step of forming the cyclic carbonate layer, the mass of the cyclic carbonate layer is 15% by mass or less based on the mass of the silicon oxide particles,
By using silicon oxide particles, wherein the cyclic carbonate layer was formed as the anode active material particles, a non-aqueous electrolyte for the aqueous slurry, which comprises a negative electrode active material for a non-aqueous electrolyte secondary batteries for aqueous slurry method of preparing a negative electrode active material for a secondary battery. 前記環状カーボネート層を形成する工程において、環状カーボネート及びＬｉ塩を含む溶液で前記改質後の酸化珪素粒子を洗浄し、該洗浄後の酸化珪素粒子を乾燥させることで、前記改質後の酸化珪素粒子の表面に、前記Ｌｉ塩を含む環状カーボネートからなる環状カーボネート層を形成することを特徴とする請求項１１に記載の水系スラリー用の非水電解質二次電池用負極活物質の製造方法。 In the step of forming the cyclic carbonate layer, the modified silicon oxide particles are washed with a solution containing the cyclic carbonate and the Li salt, and the washed silicon oxide particles are dried, whereby the oxidized oxide after the modification. on the surface of the silicon particles, the production method of the negative electrode active material for a non-aqueous electrolyte secondary batteries for aqueous slurry according to claim 11, characterized in that to form a cyclic carbonate layer consisting of a cyclic carbonate containing the Li salt.
JP2015101328A 2015-05-18 2015-05-18 Anode active material for nonaqueous electrolyte secondary battery, nonaqueous electrolyte secondary battery, and method for producing anode active material for nonaqueous electrolyte secondary battery Active JP6448462B2 (en)