JP6443615B2 - FUEL CELL UNIT, METHOD FOR PRODUCING THE FUEL CELL UNIT, AND FUEL CELL STACK - Google Patents

FUEL CELL UNIT, METHOD FOR PRODUCING THE FUEL CELL UNIT, AND FUEL CELL STACK Download PDF

Info

Publication number
JP6443615B2
JP6443615B2 JP2014163286A JP2014163286A JP6443615B2 JP 6443615 B2 JP6443615 B2 JP 6443615B2 JP 2014163286 A JP2014163286 A JP 2014163286A JP 2014163286 A JP2014163286 A JP 2014163286A JP 6443615 B2 JP6443615 B2 JP 6443615B2
Authority
JP
Japan
Prior art keywords
fuel cell
separator
cell unit
solid oxide
oxide fuel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2014163286A
Other languages
Japanese (ja)
Other versions
JP2016039099A (en
JP2016039099A5 (en
Inventor
矢島　健太郎
健太郎 矢島
隆夫 和泉
隆夫 和泉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nissan Motor Co Ltd
Original Assignee
Nissan Motor Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nissan Motor Co Ltd filed Critical Nissan Motor Co Ltd
Priority to JP2014163286A priority Critical patent/JP6443615B2/en
Publication of JP2016039099A publication Critical patent/JP2016039099A/en
Publication of JP2016039099A5 publication Critical patent/JP2016039099A5/ja
Application granted granted Critical
Publication of JP6443615B2 publication Critical patent/JP6443615B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、電極とセパレータ間との接合部の抵抗を減少させて発電性能を向上させた燃料電池ユニット、該燃料電池ユニットの製造方法、及び燃料電池スタックに関する。   The present invention relates to a fuel cell unit that improves the power generation performance by reducing the resistance at the joint between an electrode and a separator, a method for manufacturing the fuel cell unit, and a fuel cell stack.

燃料電池は、化学エネルギーを電気化学的な反応により電気エネルギーに変換する装置であり、セパレータを介して発電セルを複数積層して形成された燃料電池が知られている。   BACKGROUND ART A fuel cell is a device that converts chemical energy into electric energy by an electrochemical reaction, and a fuel cell formed by stacking a plurality of power generation cells via a separator is known.

例えば、特許文献１には、電解質膜の両側にアノード極とカソード極を接合した複数のセルと、一方のセルのアノード極と他方のセルのカソード極との間に、アノードガス、カソードガスを流通させるためのアノード極側ガス流通部、カソード極側ガス流通部を形成するセパレータを配設した燃料電池ユニットが開示されている。
この燃料電池ユニットは、流路長が異なる複数のアノード極側ガス流通路を有し、流路長が長くなるに従い、流通路断面形状の重心をアノード極から離間させるように形成することで、流通路における流量分配を均一にして発電効率を高めることができるものである。 For example, in Patent Document 1, an anode gas and a cathode gas are provided between a plurality of cells in which an anode electrode and a cathode electrode are joined to both sides of an electrolyte membrane, and an anode electrode of one cell and a cathode electrode of the other cell. A fuel cell unit is disclosed in which a separator that forms an anode electrode side gas circulation part and a cathode electrode side gas circulation part for distribution is disposed.
This fuel cell unit has a plurality of anode electrode side gas flow passages with different flow path lengths, and the center of gravity of the flow passage cross-sectional shape is formed so as to be separated from the anode electrode as the flow path length increases. It is possible to increase the power generation efficiency by making the flow distribution in the flow passage uniform.

特開２０１３−１９７０７５号公報Japanese Unexamined Patent Publication No. 2013-197075

特許文献１に記載の燃料電池は、発電効率を向上できるものであるが、稼働停止を繰り返した後には電池出力が低下することがある。   The fuel cell described in Patent Document 1 can improve power generation efficiency, but the battery output may decrease after repeated operation stoppage.

本発明者らは、稼働・停止を繰り返すことで、電池出力が低下する原因について調べたところ、セパレータと電極との接合部の端部から細かな亀裂・剥離が生じ、接触抵抗が増加して電池出力低下することがわかった。   The inventors have investigated the cause of the decrease in battery output by repeating the operation and stoppage, and as a result, fine cracks and separation occurred from the end of the joint between the separator and the electrode, and the contact resistance increased. It was found that the battery output decreased.

つまり、６５０℃〜１０００℃程度の高温で稼働する燃料電池等は、作動時の熱によりセパレータ等が膨張する一方で、発電セルは筐体に固定されているため発電セル間は広がらずに発電セル間のセパレータが圧縮されて塑性変形する。そして、停止してセルの温度が下がると、セパレータが塑性変形したまま収縮する。
すると、発電セル間に接合されたセパレータの接合部間の長さが足りなくなって、セパレータと電極との接合部に引張り応力がかかり、接合部内部に亀裂・剥離が生じ、導電面積が減少し、これに伴って接触抵抗が増大して発電性能が低下する。 In other words, a fuel cell or the like that operates at a high temperature of about 650 ° C. to 1000 ° C. generates power without spreading between the power generation cells because the separator and the like expand due to heat during operation, and the power generation cells are fixed to the casing. The separator between cells is compressed and plastically deformed. And when it stops and the temperature of a cell falls, a separator will shrink | contract, with plastic deformation.
As a result, the length between the joints of the separator joined between the power generation cells becomes insufficient, tensile stress is applied to the joint between the separator and the electrode, cracks and separation occur inside the joint, and the conductive area decreases. Along with this, the contact resistance increases and the power generation performance decreases.

本発明は、このような従来技術の有する課題及び所見に鑑みてなされたものであり、その目的とするところは、稼働・停止を繰り返しても電池出力が低下しない、高耐久な燃料電池、及び、該燃料電池の製造方法を提供することにある。   The present invention has been made in view of the problems and findings of the prior art, and the object of the present invention is a highly durable fuel cell in which the battery output does not decrease even after repeated operation and stop, and An object of the present invention is to provide a method for manufacturing the fuel cell.

本発明者らは、このような接触抵抗の増大による電池出力の低下を防止すべく鋭意検討を重ねた。その結果、セパレータに平面接合部を設けると共に、該接合部と電極との接合を完全にするために、セパレータの接合部の周囲をも含めて広範囲を接合するのではなく、セパレータの平面接合部のみを接合し、該平面部の端から立ち上がる屈曲部に対応する接点材部分に逃げを設けることで、該屈曲部に応力が集中して変形し、接点材にかかる応力が軽減され、クラックの発生を防止できることを見出し、本発明を完成するに至った。   The inventors of the present invention have made extensive studies to prevent such a decrease in battery output due to an increase in contact resistance. As a result, the separator is provided with a flat joint, and in order to complete the joining between the joint and the electrode, the flat joint of the separator is not joined over a wide area including the periphery of the joint of the separator. The contact material portion corresponding to the bent portion that rises from the end of the flat surface portion is deformed by stress concentration on the bent portion, the stress applied to the contact material is reduced, and cracks are generated. The inventors have found that generation can be prevented, and have completed the present invention.

本発明は、上記知見に基づくものであって、本発明の燃料電池ユニットは、隣り合う発電セル間に配設されたセパレータに、電極と接合する平面状の接合部を設け、該平面部のみを接合し、該平面部の端から立ち上がる屈曲部に対応する接点材部分に逃げを設けたことを特徴とする。   The present invention is based on the above knowledge, and the fuel cell unit of the present invention is provided with a planar joint portion that joins an electrode on a separator disposed between adjacent power generation cells, and only the planar portion. And a relief is provided in the contact material portion corresponding to the bent portion rising from the end of the flat portion.

また、本発明の燃料電池ユニットの製造方法は、上記燃料電池ユニットを製造する方法であって、セパレータの平面状の接合部以外を可燃性コート材で被覆し、平面部の端から立ち上がる屈曲部に対応する接点材部分に逃げを設けたことを特徴とする。   The fuel cell unit manufacturing method of the present invention is a method for manufacturing the above fuel cell unit, wherein the separator is covered with a combustible coating material other than the flat joint and is bent from the end of the flat portion. A relief is provided in the contact material portion corresponding to.

また、本発明の燃料電池ユニットの製造方法は、上記燃料電池ユニットを製造する方法であって、電極面に線状の凸部を形成し、該凸部とセパレータの平面部とを接合し、平面部の端から立ち上がる屈曲部に対応する接点材部分に逃げを設けたことを特徴とする。   Further, the method for producing a fuel cell unit of the present invention is a method for producing the fuel cell unit, wherein a linear convex portion is formed on the electrode surface, and the convex portion and the flat portion of the separator are joined, A relief is provided in the contact material portion corresponding to the bent portion rising from the end of the flat portion.

さらに、本発明の燃料電池ユニットの製造方法は、上記燃料電池ユニットを製造する方法であって、セパレータの平面状の接合部以外を撥水化処理し、平面部の端から立ち上がる屈曲部に対応する接点材部分に逃げを設けたことを特徴とする。 Furthermore, the method for manufacturing a fuel cell unit according to the present invention is a method for manufacturing the fuel cell unit described above, wherein the surface of the separator other than the planar joining portion is subjected to water repellent treatment and corresponds to a bent portion rising from the end of the planar portion. It is characterized in that a relief is provided in the contact material portion to be performed.

加えて、本発明の燃料電池スタックは、上記燃料電池ユニットを複数積層したことを特徴とする。
In addition, the fuel cell stack of the present invention is characterized in that a plurality of the fuel cell units are stacked.

本発明によれば、隣り合う発電セル間に配設されたセパレータに、電極と接合する平面接合部を設け、該平面部のみを接合し、該平面部の端から立ち上がる屈曲部に対応する接点材部分に逃げを設けることとしたため、作動・停止の繰り返しによって接合箇所にクラックが生じて導電面積が減少して抵抗が増加することを防止でき、長期に亘り電池出力の低下が防止された燃料電池ユニット、該ユニットを複数積層した燃料電池ユニットを提供できる。
According to the present invention, the separator disposed between the adjacent power generation cells is provided with the planar joining portion that joins the electrode, only the planar portion is joined, and the contact corresponding to the bent portion rising from the end of the planar portion. Because the material part is provided with relief, it is possible to prevent cracks from occurring in the joints due to repeated operation and stop, reducing the conductive area and increasing the resistance, and preventing the battery output from decreasing for a long time A battery unit and a fuel cell unit in which a plurality of the units are stacked can be provided.

本発明の燃料電池の内部構造の一例を示す断面図である。It is sectional drawing which shows an example of the internal structure of the fuel cell of this invention. 従来の接合方法による接合箇所の断面図である。It is sectional drawing of the joining location by the conventional joining method. 本発明の接合箇所の例を示す断面図である。It is sectional drawing which shows the example of the joining location of this invention. セパレータの形状の例を示す断面図である。It is sectional drawing which shows the example of the shape of a separator. セパレータを高さ方向から押圧したときのセパレータ形状の例を示す図である。It is a figure which shows the example of a separator shape when a separator is pressed from a height direction. 本発明の電極とセパレータの接合状態の例を示す図である。It is a figure which shows the example of the joining state of the electrode and separator of this invention. 本発明の電極とセパレータの接合状態の他の例を示す図である。It is a figure which shows the other example of the joining state of the electrode and separator of this invention. 本発明の電極とセパレータの接合状態のさらに他の例を示す図である。It is a figure which shows the further another example of the joining state of the electrode and separator of this invention. 実施例と比較例の燃料電池を作動・停止させたときの接触抵抗の変化を示すグラフである。It is a graph which shows the change of contact resistance when the fuel cell of an Example and a comparative example is started and stopped. 実施例と比較例の燃料電池の接点材の断面写真である。It is a cross-sectional photograph of the contact material of the fuel cell of an Example and a comparative example.

本発明の燃料電池を、図面を参照して説明する。図１は、本発明の燃料電池の内部構造の一例を示す断面図である。この燃料電池１は、それ自体で燃料電池として機能する発電セル２とセパレータ３とで燃料電池ユニットを形成し、燃料電池ユニットは、複数積層され筐体４に支持されて燃料電池スタックを構成する。
隣り合う発電セル間に設けられたセパレータ３は、発電セル２と共に燃料ガスを供給する燃料ガス通路と酸化剤ガスを供給する空気通路とを形成し、かつ、隣り合う発電セルを電気的に接続する。
このセパレータ３は、電極との接合を完全にして集電効率を向上させるため平面接合部を有する。また、上記発電セル２は、図示しない燃料極、電解質、空気極が順に積層されたものであり、多孔質のメタルサポート上に設けられてもよい。 The fuel cell of the present invention will be described with reference to the drawings. FIG. 1 is a cross-sectional view showing an example of the internal structure of the fuel cell of the present invention. In this fuel cell 1, a fuel cell unit is formed by a power generation cell 2 that functions as a fuel cell itself and a separator 3, and a plurality of fuel cell units are stacked and supported by a casing 4 to constitute a fuel cell stack. .
The separator 3 provided between the adjacent power generation cells forms a fuel gas passage for supplying the fuel gas together with the power generation cell 2 and an air passage for supplying the oxidant gas, and electrically connects the adjacent power generation cells. To do.
The separator 3 has a flat joint portion in order to improve the current collection efficiency by completely joining the electrode. Further, the power generation cell 2 is formed by sequentially laminating a fuel electrode, an electrolyte, and an air electrode (not shown), and may be provided on a porous metal support.

発電セルの電極とセパレータとの接合は、図２（Ａ）に示すように、発電セル２の電極面及び／又はセパレータの平面接合部３Ａに、ペースト状の接点材５を付与し、電極とセパレータとを押し付け、８００℃〜１３００℃で接点材５を焼結固化させることで行われる。したがって、従来の方法での接合では、セパレータの平面接合部３Ａだけでなく、図２（Ｂ）中の点線丸で示す、平面接合部の端部から立ち上がる屈曲部にも接点材５が付与され、該屈曲部をも含めて固定される。
そして、燃料電池の作動による熱膨張によってセパレータが塑性変形した後、燃料電池を停止すると、図２（Ｃ）中矢印の方向に引張応力が生じ、接点材５の端部がセパレータ３に引きずられ、図２（Ｃ）の拡大図のように、接点材５の端部から亀裂が生じる。 As shown in FIG. 2A, the bonding between the electrode of the power generation cell and the separator is performed by applying a paste-like contact material 5 to the electrode surface of the power generation cell 2 and / or the planar bonding portion 3A of the separator. It is performed by pressing the separator and sintering and solidifying the contact material 5 at 800 ° C. to 1300 ° C. Therefore, in the joining by the conventional method, the contact material 5 is applied not only to the planar joining portion 3A of the separator but also to the bent portion rising from the end of the planar joining portion, which is indicated by a dotted circle in FIG. , Including the bent portion.
When the fuel cell is stopped after the separator is plastically deformed by thermal expansion due to the operation of the fuel cell, tensile stress is generated in the direction of the arrow in FIG. 2C, and the end of the contact material 5 is dragged by the separator 3. As shown in the enlarged view of FIG. 2C, a crack is generated from the end of the contact material 5.

本発明においては、図３（Ａ）、図３（Ｂ）に示すように、セパレータの平面接合部３Ａのみを接合し、該平面部の端から立ち上がる屈曲部に対応する接点材部分に逃げ３Ｂを設ける。したがって、セパレータ３が引っ張られても接点材５がセパレータ３に引きずられることはない。また、セパレータ３に生じる引張応力は、セパレータ３の屈曲部が変位して吸収するため、セパレータが塑性変形していても接点材５にかかる応力が低減され、亀裂・剥離の発生が防止される。   In the present invention, as shown in FIGS. 3A and 3B, only the planar joining portion 3A of the separator is joined, and the contact 3B escapes to the contact material portion corresponding to the bent portion rising from the end of the planar portion. Is provided. Therefore, even if the separator 3 is pulled, the contact material 5 is not dragged by the separator 3. Further, since the tensile stress generated in the separator 3 is absorbed by the bending portion of the separator 3 being displaced, the stress applied to the contact material 5 is reduced even if the separator is plastically deformed, and cracking and peeling are prevented. .

本発明のセパレータは、発電セルと接合する平面接合部と傾斜部とが、上記平面接合部の端部から立ち上がる屈曲部で連続した断面形状を有するものである。
図４（Ａ）に示すように、平面接合部３Ａの端部から立ち上がる屈曲部間に、屈曲部を有さない波型セパレータであってもよいが、図４（Ｂ）に示すような、平面接合部３Ａの端部から立ち上がる屈曲部間に、複数の屈曲部を有する段付きセパレータであることが好ましい。
複数の屈曲部を有することで、温度変化による膨張・収縮によって生じる応力が屈曲部に吸収されてセパレータの塑性変形が低減され、接点材の亀裂・剥離が防止されると共に、組み立て積層の際にセパレータを押し付けることで、発電セルを損傷させることを防止できる。 The separator of the present invention has a cross-sectional shape in which a flat joint portion and an inclined portion joined to a power generation cell are continuous at a bent portion rising from an end portion of the flat joint portion.
As shown in FIG. 4 (A), it may be a wave-type separator that does not have a bent portion between bent portions that rise from the end of the flat joint portion 3A, but as shown in FIG. 4 (B), A stepped separator having a plurality of bent portions between the bent portions rising from the end portion of the flat joint portion 3A is preferable.
By having multiple bends, the stress caused by expansion and contraction due to temperature changes is absorbed by the bends, reducing the plastic deformation of the separator, preventing cracking and peeling of the contact material, and during assembly lamination By pressing the separator, it is possible to prevent the power generation cell from being damaged.

図５は、セパレータを高さ方向（発電セルの積層方向）に押圧し、５０μｍ強制変位させたときの波型セパレータと段付きセパレータの形状の変化を示す図である。図５中、Ｙ方向０．０が発電セルの電極面であり、Ｘ方向の０．０〜０．２５が平面接合部である。
図５（Ａ）に示す、波型セパレータでは、押圧により接合部となる下端の平面部が凸状に変形し、接合部が剥離する方向の応力が生じると共に、接合部端部には大きな押圧力がかかっており、塑性変形しやすいことがわかる。一方、図５（Ｂ）の段付きセパレータでは、屈曲部が多く、弾性変形して押圧力を吸収しているため、セパレータの接合部の平面性が維持され、局所的な押圧力がかからず、塑性変形を低減できることがわかる。 FIG. 5 is a diagram showing changes in the shapes of the corrugated separator and the stepped separator when the separator is pressed in the height direction (the stacking direction of the power generation cells) and forcedly displaced by 50 μm. In FIG. 5, the Y direction 0.0 is the electrode surface of the power generation cell, and the X direction 0.0 to 0.25 is the planar junction.
In the corrugated separator shown in FIG. 5 (A), the flat surface at the lower end that becomes the joint is deformed into a convex shape by pressing, and stress is generated in the direction in which the joint is peeled off. It can be seen that pressure is applied and plastic deformation is likely to occur. On the other hand, in the stepped separator of FIG. 5 (B), since there are many bent portions and elastically deforms to absorb the pressing force, the flatness of the joining portion of the separator is maintained, and a local pressing force is applied. It can be seen that plastic deformation can be reduced.

次に本発明の燃料電池の製造方法について説明する。
本発明の燃料電池の製造方法は、セパレータの平面接合部のみを接合し、該平面部の端から立ち上がる屈曲部に対応する接点材部分に逃げを設けるものである。 Next, the manufacturing method of the fuel cell of this invention is demonstrated.
In the fuel cell manufacturing method of the present invention, only the flat joint portion of the separator is joined, and a relief is provided in the contact material portion corresponding to the bent portion rising from the end of the flat portion.

上記屈曲部に対応する接点材部分に逃げを設ける方法としては、（ｉ）屈曲部を可燃性材料でコートし接点材を付与しない方法や、（ｉｉ）発電セルの電極面にセパレータと接合する凸部を設け、該凸部とセパレータの平面接合部とを接合する方法、（ｉｉｉ）屈曲部を撥水化処理し、接点材が付着しないようにする方法が挙げられる。 As a method of providing relief in the contact material portion corresponding to the bent portion, (i) a method in which the bent portion is coated with a flammable material and no contact material is provided, or (ii) a separator is joined to the electrode surface of the power generation cell. Examples include a method of providing a convex part and joining the convex part and the flat joint part of the separator, and (iii) a method of making the bent part water repellent so that the contact material does not adhere.

（ｉ）屈曲部を可燃性材料でコートする方法
セパレータの平面接合部から立ち上がる屈曲部を可燃性コート材で被覆し、ペースト状の接点材を介して電極とセパレータとを接合した後、焼成する。この方法によれば、図６に示すように、セパレータ３の屈曲部が可燃性コート材６で被覆されているため、屈曲部には接点材５が付着せず、該屈曲部は電極と接合されず、屈曲部に対応する接点材が可燃性コート材６に押し退けられて逃げが形成される。そして、可燃性コート材６は、焼成により揮発して除去される。 (I) Method of coating the bent portion with a flammable material The bent portion rising from the flat joint portion of the separator is covered with the flammable coating material, and the electrode and the separator are bonded via the paste-like contact material, followed by firing. . According to this method, as shown in FIG. 6, since the bent portion of the separator 3 is covered with the combustible coating material 6, the contact material 5 does not adhere to the bent portion, and the bent portion is bonded to the electrode. Instead, the contact material corresponding to the bent portion is pushed away by the combustible coating material 6 to form a relief. And the combustible coating material 6 volatilizes and is removed by baking.

可燃性コート材は吹き付けて被覆することが好ましい。吹き付けることにより厚さをμｍオーダーに設定できるため、積層の際に、セパレータを接点材に押し付けることで、セパレータが変位しても可燃性コート材が追従し剥がれることがない。 The flammable coating material is preferably coated by spraying. Since the thickness can be set to the μm order by spraying, the flammable coating material does not follow and peel even when the separator is displaced by pressing the separator against the contact material during lamination.

可燃性コート材の膜厚は、屈曲部に接点材が付着することを防止できればよいが、厚いことが好ましく、その上限は、焼成後のセパレータと電極面との距離、すなわち、接点材の厚さ以下である。可燃性コート材の膜厚を厚くすることで、燃料電池の稼働によりセパレータが熱膨張しても、セパレータの屈曲部の下に隙間（逃げ）が生じ、屈曲部が下方に変位できるため、セパレータの塑性変形が防止される。 The film thickness of the combustible coating material only needs to prevent the contact material from adhering to the bent portion, but is preferably thick, and the upper limit is the distance between the separator and the electrode surface after firing, that is, the thickness of the contact material. Is less than By increasing the film thickness of the combustible coating material, even if the separator thermally expands due to the operation of the fuel cell, a gap (escape) is generated under the bent portion of the separator, and the bent portion can be displaced downward. The plastic deformation of is prevented.

可燃性コート材を被覆する箇所には、予め、微細な凹凸を形成することが好ましい。凹凸を形成することで可燃性コート材とセパレータとの機械的接合が担保され、積層の際に、セパレータを接点材に押し付けることで、セパレータが変位しても可燃性コート材が剥がれることがない。また、後述するマスク材を除去する際の可燃性コート材の剥離を防止できる。 It is preferable to form fine irregularities in advance at the locations where the combustible coating material is coated. By forming irregularities, mechanical bonding between the flammable coating material and the separator is ensured, and the flammable coating material is not peeled even if the separator is displaced by pressing the separator against the contact material during lamination. . Moreover, peeling of the combustible coating material at the time of removing the mask material described later can be prevented.

可燃性コート材としては、燃焼により接点材やセパレータ等の電池部材を侵食するガスを生成しないものであれば使用することができ、窒素、塩素、硫黄等を含まない樹脂、例えば炭化水素系樹脂を使用することができる。炭化水素系樹脂としては、ポリエチレン（ＰＥ）、ポリプロピレン（ＰＰ）、ポリスチレン（ＰＳ）等を挙げることができ、ポリプロピレン（ＰＰ）であることが好ましい。 The flammable coating material can be used as long as it does not generate gas that erodes battery members such as contact materials and separators by combustion, and does not contain nitrogen, chlorine, sulfur, etc., for example, hydrocarbon resin Can be used. Examples of the hydrocarbon resin include polyethylene (PE), polypropylene (PP), polystyrene (PS) and the like, and polypropylene (PP) is preferable.

上記微細な凹凸を形成する方法としては、エアロゾルデポジション（ＡＤ法）や溶射法で微粒子を衝突・付着させる方法や、腐食処理で凹凸を形成する方法等を挙げることができる。中でも、セパレータが薄膜化したり、熱劣化したりすることがないエアロゾルデポジションであることが好ましい。 Examples of the method for forming the fine irregularities include a method of colliding and adhering fine particles by aerosol deposition (AD method) or a thermal spraying method, a method of forming irregularities by a corrosion treatment, and the like. Among them, it is preferable that the deposition is an aerosol deposition in which the separator is not thinned or thermally deteriorated.

セパレータの平面接合部以外を可燃性コート材で被覆する方法としては、セパレータの平面接合部をマスキングして可燃性コート材で被覆し、マスキング材ごと可燃性コート材を剥離する方法や、可燃性コートで被覆し、余剰の可燃性コート材を剥離する方法等が挙げられる。 As a method of covering the separator other than the flat joint part with the flammable coating material, masking the flat joint part of the separator and covering it with the flammable coating material, peeling the flammable coating material together with the masking material, or flammability Examples of the method include a method of covering with a coat and peeling off an excessive combustible coating material.

上記マスキング材としては、マスキングゾルや、マスキングテープを使用することができ、これらは水溶性であることが好ましい。水溶性のマスキング材は水系媒体に浸漬することで、余剰の可燃性コート材を除去できる。
上記水溶性のマスキング材としては、ポリビニルアルコール等の水溶性樹脂を主成分とするものが挙げられる。 As the masking material, a masking sol or a masking tape can be used, and these are preferably water-soluble. Excessive combustible coating material can be removed by immersing the water-soluble masking material in an aqueous medium.
As said water-soluble masking material, what has water-soluble resin, such as polyvinyl alcohol, as a main component is mentioned.

また、可燃性コート剤被覆後に余剰の可燃性コート材を剥離する方法としては、可燃性コート材を溶解する有機溶媒で溶解し除去する方法や、カッター加工等で機械的に除去する方法が挙げられる。 In addition, as a method of peeling off the excess flammable coating material after coating the flammable coating agent, a method of dissolving and removing the flammable coating material with an organic solvent that dissolves the flammable coating material, a method of mechanically removing by a cutter process, etc. It is done.

（ｉｉ）電極面に凸部を設ける方法
発電セルの電極面にセパレータの平面接合部に対応する幅の線状凸部を設けることで、図７に示すように、凸部の上部から余剰の接点材がこぼれて逃げが形成され、セパレータの平面接合部以外に、接点材が付着することを防止できる。
本発明において、上記凸部とは、電極面に設けられたセパレータとの接合箇所が、その周囲よりも高ければたり、電極面上に凸部を形成するだけでなく、電極面の接合箇所に沿って凹部を形成することで、該凹部よりも相対的に高い凸部を形成してもよい。
上記凸部は、電極面に電極材粉末粒子を選択的に吹き付けることで形成してもよく、電極を切削して凹部を形成することで凸部を形成してもよい。
電極面に凸部を設けることで、焼成処理によらず屈曲部に対応する接点材部分に逃げを設けることができる。 (Ii) Method of providing a convex portion on the electrode surface By providing a linear convex portion having a width corresponding to the flat joint portion of the separator on the electrode surface of the power generation cell, as shown in FIG. The contact material is spilled and a relief is formed, and it is possible to prevent the contact material from adhering to other than the flat joint portion of the separator.
In the present invention, the above-mentioned convex part is not only the part where the separator provided on the electrode surface is higher than the surrounding area, or the convex part is formed on the electrode surface. You may form a convex part relatively higher than this recessed part by forming a recessed part along.
The convex portion may be formed by selectively spraying electrode material powder particles on the electrode surface, or the convex portion may be formed by cutting the electrode to form a concave portion.
By providing the convex portion on the electrode surface, it is possible to provide relief in the contact material portion corresponding to the bent portion regardless of the baking treatment.

（ｉｉｉ）屈曲部を撥水化処理する方法
セパレータの屈曲部を撥水化処理することで、撥水化処理部７の表面エネルギーが低下して接点材が忌避されて付着せず、焼成により接点材が収縮して剥がれて逃げが形成され、図８に示すように、屈曲部と電極とが接合されることを防止できる。
上記撥水化処理による接点材ペーストとセパレータとの接触角は、９０°を超えることが好ましい。 (Iii) Method of water-repellent treatment of the bent portion By subjecting the bent portion of the separator to water-repellent treatment, the surface energy of the water-repellent treated portion 7 is reduced and the contact material is repelled and does not adhere. The contact material contracts and peels to form a relief, and as shown in FIG. 8, the bent portion and the electrode can be prevented from being joined.
The contact angle between the contact material paste and the separator by the water repellent treatment is preferably more than 90 °.

上記撥水化処理は、フッ素コートや、無限大の長さと頂点をもつフラクタル構造に類似した面を形成し、セパレータ面−接点材ペースト面の点接触をできる限り多くすることで、行うことができる。上記フッ素コートはフッ素系のガスを用いたプラズマを照射により行うことができ、フラクタル構造に類似した面の形成は、プラズマや腐食性流体などを利用したエッチング等により行うことができる The water-repellent treatment can be performed by forming a surface similar to a fluorine coat or a fractal structure having an infinite length and apex, and increasing the point contact between the separator surface and the contact material paste surface as much as possible. it can. The fluorine coating can be performed by irradiation with plasma using a fluorine-based gas, and the formation of a surface similar to a fractal structure can be performed by etching using plasma or corrosive fluid.

次に、燃料電池を構成する部材について説明する。
発電セルは、電解質の一方の面に燃料極を有し、他方の面に空気極を有する。 Next, members constituting the fuel cell will be described.
The power generation cell has a fuel electrode on one surface of the electrolyte and an air electrode on the other surface.

上記電解質は固体電解質であることが好ましく、固体電解質としては、一般的に、酸化イットリウム（Ｙ２Ｏ３）や酸化ネオジム（Ｎｄ２Ｏ３）、酸化サマリウム（Ｓｍ２Ｏ３）、酸化ガドリニウム（Ｇｄ２Ｏ３）、酸化スカンジウム（Ｓｃ２Ｏ３）などを固溶した安定化ジルコニアが用いられる他、酸化セリウム（ＣｅＯ２）系固溶体や、酸化ビスマス（Ｂｉ２Ｏ３）や、ＬａＧａＯ３などの酸化物粉末結晶粒子が用いられる。 The electrolyte is preferably a solid electrolyte. Generally, as the solid electrolyte, yttrium oxide (Y 2 O 3 ), neodymium oxide (Nd 2 O 3 ), samarium oxide (Sm 2 O 3 ), gadolinium oxide ( In addition to using stabilized zirconia in which Gd 2 O 3 ), scandium oxide (Sc 2 O 3 ), and the like are used as solid solutions, cerium oxide (CeO 2 ) -based solid solutions, bismuth oxide (Bi 2 O 3 ), LaGaO 3, etc. These oxide powder crystal particles are used.

上記燃料極は、還元雰囲気に強く、燃料ガスを透過し、電気伝導度が高く、水素分子をプロトンに変換する触媒作用を有すればよく、例えば、ニッケル（Ｎｉ）やコバルト（Ｃｏ）、白金（Ｐｔ）などの貴金属、あるいはニッケル（Ｎｉ）と固体電解質のサーメットなどが一般的に用いられる。
なお、燃料極の電解質と反対側の面には、多孔質のメタルサポートを設けてもよい。 The fuel electrode is strong in a reducing atmosphere, permeates the fuel gas, has high electrical conductivity, and has a catalytic action to convert hydrogen molecules into protons. For example, nickel (Ni), cobalt (Co), platinum A noble metal such as (Pt) or nickel (Ni) and a solid electrolyte cermet is generally used.
A porous metal support may be provided on the surface of the fuel electrode opposite to the electrolyte.

上記空気極としては、酸化に強く、酸化剤ガスを透過し、電気伝導度が高く、酸素分子を酸素イオンに変換する触媒作用を有すればよく、ＡｇやＰｔなどの金属系粉末結晶粒子を使用できるが、ＬａＳｒＭｎＯ（ＬＳＭ）やＬａＳｒＣｏＯ（ＬＳＣ）、（Ｌａ，Ｓｒ）（Ｃｏ，Ｆｅ）Ｏ３（ＬＳＣＦ）に代表されるペロブスカイト構造の酸化物粉末結晶粒子が好ましく用いられる。空気極は、２種以上を積層して用いてもよい。例えば、ＬＳＣＦ等の通常電極上にＬＳＣ等の高性能電極を積層することができる。 As the air electrode, it is sufficient that it is resistant to oxidation, permeates oxidant gas, has high electrical conductivity, and has a catalytic action for converting oxygen molecules into oxygen ions. Metal powder crystal particles such as Ag and Pt are used. Although usable, oxide powder crystal particles having a perovskite structure typified by LaSrMnO (LSM), LaSrCoO (LSC), and (La, Sr) (Co, Fe) O 3 (LSCF) are preferably used. Two or more kinds of air electrodes may be laminated and used. For example, a high performance electrode such as LSC can be laminated on a normal electrode such as LSCF.

上記発電セル間に配設されるセパレータは、耐熱性及び導電性を有すればよく、ＳＵＳ材や、フェライト材等から構成される。また、発電セルとセパレータとを接合する接点材としては、導電性を有し、セパレータを接合できればよく、例えば、上記電極を構成する電極材から成るペーストを使用できる。
The separator disposed between the power generation cells only needs to have heat resistance and conductivity, and is made of a SUS material, a ferrite material, or the like. Moreover, as a contact material which joins a power generation cell and a separator, it should just have electroconductivity and can join a separator, For example, the paste which consists of the electrode material which comprises the said electrode can be used.

以下、本発明を実施例により詳細に説明するが、本発明は下記実施例に限定されるものではない。   EXAMPLES Hereinafter, although an Example demonstrates this invention in detail, this invention is not limited to the following Example.

［実施例１］
厚さ０．１ｍｍのフェライト板材をプレス法によって段付きセパレータに成型した。この段付セパレータの平面接合部の端部から立ち上がる屈曲部に、ガスデポジション法を用いた衝撃法で凹凸を形成した。
上記凹凸の形成は以下のようにして行った。
ステンレス鋼（ＳＵＳ）のマスクを用いて、セパレータの平面接合部をカバーして、真空チャンバー内にセットして減圧し、常温で、ステンレス鋼（ＳＵＳ）粒子を超音速ノズルによって８００ｍ／ｓ以上のＮ２ガス流に乗せて吹き付け、フェライト板材にステンレス鋼（ＳＵＳ）粒子を付着させてセパレータの屈曲部に凹凸を形成した。 [Example 1]
A ferrite plate material having a thickness of 0.1 mm was molded into a stepped separator by a pressing method. Concavities and convexities were formed by an impact method using a gas deposition method at the bent portion rising from the end of the flat junction of the stepped separator.
The unevenness was formed as follows.
Using a stainless steel (SUS) mask, the flat joint of the separator is covered, set in a vacuum chamber and depressurized, and at room temperature, stainless steel (SUS) particles are 800 m / s or more by a supersonic nozzle. It was sprayed on an N 2 gas flow, and stainless steel (SUS) particles were adhered to the ferrite plate material to form irregularities on the bent portion of the separator.

次に、セパレータの平面接合部を、ポリビニルアルコールを主成分とする水溶性のマスク用ゾル液でコーティングした後、常温２４ｈｒの乾燥処理を行ってゲル化させ、水溶性マスク処理を行った。
ポリプロピレン樹脂を有機溶媒に溶かした樹脂溶液をセパレータに噴霧し、常温で２４時間以上の乾燥処理を実施することで可燃性樹脂をコーティングした。
可燃性樹脂をコーティングしたセパレータを３０〜４５℃程度の水に浸漬させて、超音波処理を実施することで水溶性マスクを水に溶出させ、水溶性マスク上の可燃性樹脂と共に除去し、可燃性樹脂をコーティングしたセパレータを作製した。
このセパレータを確認したところ、屈曲部をコートした可燃性樹脂の剥離はなかった。 Next, after the flat joint portion of the separator was coated with a water-soluble sol solution for a mask containing polyvinyl alcohol as a main component, it was gelled by performing a drying process at room temperature for 24 hours to perform a water-soluble mask process.
A resin solution in which a polypropylene resin was dissolved in an organic solvent was sprayed on a separator, and a flammable resin was coated by performing a drying treatment at room temperature for 24 hours or more.
A separator coated with a flammable resin is immersed in water at about 30 to 45 ° C. and subjected to ultrasonic treatment to elute the water-soluble mask into water and removed together with the flammable resin on the water-soluble mask. A separator coated with a conductive resin was produced.
When this separator was confirmed, there was no peeling of the combustible resin which coated the bending part.

アノード側メタルサポート、アノード、固体電解質（ＹＳＺ）、カソードが積層された発電セルのカソード上に、ＬＳＣＦ電極材から成る接点材ペーストを塗布し、樹脂コートしたセパレータを接点材ペーストに押し付け、大気中において８００℃で焼成し固体酸化物形燃料電池を作製した。
焼結後（樹脂コート焼結除去後）に集電体屈曲部を観察した結果、凹凸が確認された。さらに、焼結後の接点材厚みは約１００μｍであった。 A contact material paste made of LSCF electrode material is applied onto the cathode of a power generation cell in which the anode side metal support, anode, solid electrolyte (YSZ), and cathode are laminated, and a resin-coated separator is pressed against the contact material paste in the atmosphere. Were fired at 800 ° C. to produce a solid oxide fuel cell.
As a result of observing the bent portion of the current collector after sintering (after removing the resin coat), irregularities were confirmed. Furthermore, the contact material thickness after sintering was about 100 μm.

［実施例２］
屈曲部に凹凸が形成された段付きセパレータを実施例１と同様にして作製した。
このセパレータに、ポリプロピレン樹脂を有機溶媒に溶かした樹脂溶液を噴霧し、常温２４ｈｒ以上の乾燥処理を実施することで可燃性樹脂をコーティングした。
このセパレータの平面接合部と屈曲部の境にカッターを押付けて可燃性樹脂を裁断し、平面接合部の可燃性樹脂のみに６０〜１００℃程度の熱風を吹付けて軟化させ、平面接合部の可燃性樹脂を捲り剥離させ、可燃性樹脂をコーティングしたセパレータを作製した。
このセパレータを用いる他は、実施例１と同様にして、固体酸化物形燃料電池を作製した。 [Example 2]
A stepped separator in which irregularities were formed in the bent portion was produced in the same manner as in Example 1.
The separator was sprayed with a resin solution obtained by dissolving a polypropylene resin in an organic solvent, and a flammable resin was coated by performing a drying treatment at room temperature for 24 hours or more.
A cutter is pressed against the boundary between the flat joint and the bent portion of the separator to cut the flammable resin, and hot air of about 60 to 100 ° C. is blown and softened only to the flammable resin of the flat joint, A combustible resin was peeled off and a separator coated with the combustible resin was produced.
A solid oxide fuel cell was produced in the same manner as in Example 1 except that this separator was used.

［実施例３］
アノード側メタルサポート、アノード、固体電解質（ＹＳＺ）が積層された部材の固体電解質を上面にして真空チャンバーに入れ、チャンバーを負圧にした後、噴霧ノズルを用いて、電極粉末粒子（ＬＳＣＦ粉）を高速のＨｅガスに乗せて吹き付け、平面状のカソード電極を作製した。
さらに、ノズル径を変更して、先に成膜したカソード電極上に、幅がセパレータの平面接合部の幅よりも狭くなるように、線状に電極粉末粒子（ＬＳＣＦ粉）を吹付けて、線状の凸部を形成した。 [Example 3]
Put the solid electrolyte of the anode side metal support, anode, and solid electrolyte (YSZ) in the vacuum chamber with the top surface into the vacuum chamber, and make the chamber negative pressure, then use the spray nozzle to make the electrode powder particles (LSCF powder) Was put on a high-speed He gas and sprayed to prepare a flat cathode electrode.
Furthermore, by changing the nozzle diameter, the electrode powder particles (LSCF powder) are sprayed linearly on the previously formed cathode electrode so that the width is narrower than the width of the flat joint portion of the separator, A linear protrusion was formed.

上記線状の凸部上面にＬＳＣＦ電極材から成る接点材ペーストを塗布し、厚さ０．１ｍｍのフェライト板材をプレス法によって成形した段付きセパレータの平面接合部と線状の凸部とを合わせ、大気中８００℃で焼成し固体酸化物形燃料電池を作製した。 Apply the contact material paste made of LSCF electrode material on the upper surface of the above-mentioned linear convex part, and align the planar joint part of the stepped separator formed by pressing the ferrite plate material with a thickness of 0.1 mm and the linear convex part. The solid oxide fuel cell was manufactured by firing at 800 ° C. in the atmosphere.

［実施例４］
厚さ０．１ｍｍのフェライト板材をプレス法によって成形した段付きセパレータの平面接合部の端部から立ち上がる屈曲部にフッ素系のガスを用いたプラズマを照射し、フッ素コートして撥水化処理を行った。
このセパレータを用いる他は、実施例１と同様にして、固体酸化物形燃料電池を作製した。 [Example 4]
Irradiate plasma using fluorine-based gas to the bent part rising from the end of the flat joint of the stepped separator formed by pressing the ferrite plate material with a thickness of 0.1 mm, and coat it with fluorine to make it water repellent went.
A solid oxide fuel cell was produced in the same manner as in Example 1 except that this separator was used.

［比較例１］
厚さ０．１ｍｍのフェライト板材をプレスし、実施例１で用いた段付きセパレータの平面接合部の幅と、屈曲部まで接点材を付着させたときに、接点材と接触する幅とが同じになるように、実施例１よりも平面接合部の幅を狭くした段付きセパレータを得た。
アノード側メタルサポート、アノード、固体電解質（ＹＳＺ）、カソードが順に積層された発電セルのカソード上に、接点材（ＬＳＣＦペースト）を塗布し、セパレータの平面接合部を押し付け、大気中において８００℃で焼成し固体酸化物形燃料電池を作製した。
焼結後の接点材厚みは約１００μｍであった。 [Comparative Example 1]
The width of the flat joint portion of the stepped separator used in Example 1 is the same as the contact width with the contact material when the ferrite plate material having a thickness of 0.1 mm is pressed and the contact material is attached to the bent portion. As a result, a stepped separator having a flat junction width narrower than that of Example 1 was obtained.
A contact material (LSCF paste) is applied onto the cathode of the power generation cell in which the anode-side metal support, anode, solid electrolyte (YSZ), and cathode are laminated in this order, and the flat joint of the separator is pressed at 800 ° C. in the atmosphere. Firing was performed to produce a solid oxide fuel cell.
The contact material thickness after sintering was about 100 μm.

［評価］
上記固体酸化物形燃料電池の接触抵抗を以下の条件で測定した。
測定条件：
発電セル下のメタルサポートと、セパレータ上のメタルサポートとの、間の抵抗を、４Ｖとして一定電圧負荷において電流最大１Ａまで変化させ、８５０℃で稼働させ、停止後再稼働させて接触抵抗を測定した。
測定結果を図９に示す。なお、図９には、実施例１と比較例１のみを記載したが、実施例２〜４は、実施例１と同じ結果が得られた。 [Evaluation]
The contact resistance of the solid oxide fuel cell was measured under the following conditions.
Measurement condition:
The resistance between the metal support under the power generation cell and the metal support on the separator is changed to 4V with a constant voltage load up to a maximum current of 1A, operated at 850 ° C, and restarted after stopping to measure contact resistance. did.
The measurement results are shown in FIG. In FIG. 9, only Example 1 and Comparative Example 1 are shown, but Examples 2 to 4 gave the same results as Example 1.

図９より、停止・再始動を含む８５０℃−１１ｈｒの耐久試験後、実施例１〜４は、比較例１に対して接触抵抗が１割低いことがわかる。
比較例１は、停止・再始動後に接触抵抗が増加した。これは起動停止による接点時部のクラックによる集電部の電子パス減少によるものであると思われる。
一方、実施例１〜４は停止・再始動後に顕著な接触抵抗の上昇は見られなかった。 From FIG. 9, it can be seen that the contact resistance of Examples 1 to 4 is 10% lower than that of Comparative Example 1 after the endurance test of 850 ° C. and 11 hr including stop / restart.
In Comparative Example 1, the contact resistance increased after stopping / restarting. This seems to be due to a decrease in the electronic path of the current collector due to a crack at the contact point due to start and stop.
On the other hand, in Examples 1 to 4, no significant increase in contact resistance was observed after stopping and restarting.

実施例１と比較例１の接合部の断面写真を図１０に示す。
図１０から、比較例１は接点材内にクラックが発生しているが、実施例１は接点材内にクラック等が発生しておらず、セパレータの平面接合部の端部から立ち上がる屈曲部を固定しないことによる効果が確認された。 A cross-sectional photograph of the joint between Example 1 and Comparative Example 1 is shown in FIG.
From FIG. 10, Comparative Example 1 has cracks in the contact material, but Example 1 has no cracks or the like in the contact material, and has a bent portion that rises from the end of the flat joint portion of the separator. The effect by not fixing was confirmed.

１ 燃料電池
２ 発電セル
３ セパレータ
３Ａ 平面接合部
３Ｂ 逃げ
４ 筐体
５ 接点材
６ 可燃性コート材
７ 撥水処理部
DESCRIPTION OF SYMBOLS 1 Fuel cell 2 Power generation cell 3 Separator 3A Planar junction part 3B Escape 4 Case 5 Contact material 6 Flammable coating material 7 Water repellent treatment part

Claims (15)

隣り合う発電セル間にセパレータを有する固体酸化物形燃料電池ユニットであって、
上記セパレータが、平面接合部と傾斜部とが、上記平面接合部の端部から立ち上がり前記発電セルの積層方向の応力を吸収する屈曲部で連続した断面形状を有するものであり、
上記セパレータのうち平面接合部のみが接点材で発電セルに接合されて上記発電セルとで燃料ガス通路及び空気通路を形成したことを特徴とする固体酸化物形燃料電池ユニット。 A solid oxide fuel cell unit having a separator between adjacent power generation cells,
The separator has a cross-sectional shape in which a flat joint and an inclined part are continuous from a bent part that rises from an end of the flat joint and absorbs stress in the stacking direction of the power generation cell,
A solid oxide fuel cell unit characterized in that only a flat joint portion of the separator is joined to a power generation cell with a contact material to form a fuel gas passage and an air passage with the power generation cell. 隣り合う発電セル間にセパレータを有する固体酸化物形燃料電池ユニットであって、
上記セパレータが、平面接合部と傾斜部とが上記平面接合部の端部から立ち上がる屈曲部で連続した断面形状を有するものであり、
上記平面接合部のみが接点材で発電セルに接合されて上記発電セルとで燃料ガス通路及び空気通路を形成し、
上記屈曲部に対応する接点材部分に逃げを設けたことを特徴とする固体酸化物形燃料電池ユニット。 A solid oxide fuel cell unit having a separator between adjacent power generation cells,
The separator has a cross-sectional shape in which a flat joint portion and an inclined portion are continuous at a bent portion rising from an end portion of the flat joint portion,
Only the flat joint is joined to the power generation cell with a contact material to form a fuel gas passage and an air passage with the power generation cell,
A solid oxide fuel cell unit characterized in that a relief is provided in a contact material portion corresponding to the bent portion. 上記セパレータが、傾斜部に複数の屈曲部を有する段付きセパレータであることを特徴とする請求項１又は２に記載の固体酸化物形燃料電池ユニット。 The solid oxide fuel cell unit according to claim 1 or 2, wherein the separator is a stepped separator having a plurality of bent portions in an inclined portion. 発電セルの電極面に線状の凸部を有し、該凸部の上部とセパレータの平面部のみが接合したものであることを特徴とする請求項１〜３のいずれか１つの項に記載の固体酸化物形燃料電池ユニット。 It has a linear convex part in the electrode surface of a power generation cell, and only the upper part of this convex part and the plane part of a separator join, The statement of any one of Claims 1-3 characterized by the above-mentioned. Solid oxide fuel cell unit. 上記請求項２〜４のいずれか１つの項に記載の固体酸化物形燃料電池ユニットの製造方法であって、
セパレータの平面接合部以外を可燃性コート材で被覆し、接点材を付与して焼成し、電極とセパレータを接合することを特徴とする固体酸化物形燃料電池ユニットの製造方法。 A method for producing a solid oxide fuel cell unit according to any one of claims 2 to 4,
A method for producing a solid oxide fuel cell unit comprising: coating a portion other than a flat joint portion of a separator with a combustible coating material; applying a contact material; firing; and joining an electrode and a separator. 平面接合部をマスキングし、可燃性コート材で被覆した後、マスキング材と共に可燃性コート剤を剥離することを特徴とする請求項５に記載の固体酸化物形燃料電池ユニットの製造方法。 6. The method for producing a solid oxide fuel cell unit according to claim 5, wherein the flat joint portion is masked and coated with a combustible coating material, and then the combustible coating agent is peeled off together with the masking material. 上記可燃性コート剤を吹き付けて被覆することを特徴とする請求項５又は６に記載の固体酸化物形燃料電池ユニットの製造方法。 The method for producing a solid oxide fuel cell unit according to claim 5 or 6, wherein the flammable coating agent is applied by spraying. 平面接合部の端部から立ち上がる屈曲部に凹凸を形成することを特徴とする請求項５〜７のいずれか１つの項に記載の固体酸化物形燃料電池ユニットの製造方法。 The method for producing a solid oxide fuel cell unit according to any one of claims 5 to 7, wherein irregularities are formed in a bent portion rising from an end portion of the flat joint portion. 上記凹凸が、微粒子を衝突・付着させて形成したものであることを特徴とする請求項８に記載の固体酸化物形燃料電池ユニットの製造方法。 9. The method for producing a solid oxide fuel cell unit according to claim 8, wherein the irregularities are formed by colliding and adhering fine particles. 上記凹凸が、腐食処理により形成したものであることを特徴とする請求項８に記載の固体酸化物形燃料電池ユニットの製造方法。 9. The method for producing a solid oxide fuel cell unit according to claim 8, wherein the unevenness is formed by a corrosion treatment. 上記請求項２〜４のいずれか１つの項に記載の固体酸化物形燃料電池ユニットの製造方法であって、電極面に線状の凸部を形成し、該凸部とセパレータの平面接合部とを接点材を介して接合することを特徴とする固体酸化物形燃料電池ユニットの製造方法。 A method for producing a solid oxide fuel cell unit according to any one of claims 2 to 4, wherein a linear convex portion is formed on an electrode surface, and the planar joint portion between the convex portion and the separator is formed. And a solid oxide fuel cell unit. 上記凸部が電極材の微粒子を電極面に吹き付けて形成されたものであることを特徴とする請求項１１に記載の固体酸化物形燃料電池ユニットの製造方法。 12. The method of manufacturing a solid oxide fuel cell unit according to claim 11, wherein the convex portion is formed by spraying fine particles of an electrode material on the electrode surface. 上記請求項２〜４のいずれか１つの項に記載の固体酸化物形燃料電池ユニットの製造方法であって、平面接合部以外を撥水化処理し、接点材を付与して電極とセパレータを接合することを特徴とする固体酸化物形燃料電池ユニットの製造方法。 A method for producing a solid oxide fuel cell unit according to any one of claims 2 to 4, wherein a water repellent treatment is applied to a portion other than the flat joint portion, a contact material is provided, and an electrode and a separator are provided. A method for producing a solid oxide fuel cell unit, characterized by joining. 上記撥水化が、フッ素コートであることを特徴とする請求項１３に記載の固体酸化物形燃料電池ユニットの製造方法。 The method for producing a solid oxide fuel cell unit according to claim 13, wherein the water repellency is a fluorine coating. 請求項１〜４のいずれか１つの項に記載の固体酸化物形燃料電池ユニットが、複数積層されたことを特徴とする固体酸化物形燃料電池スタック。 Any one of the solid oxide fuel cell unit according to claim is, a solid oxide fuel cell stack, characterized in that it is stacked in claims 1-4.
JP2014163286A 2014-08-11 2014-08-11 FUEL CELL UNIT, METHOD FOR PRODUCING THE FUEL CELL UNIT, AND FUEL CELL STACK Active JP6443615B2 (en)