JP6368911B2 - 透過投映スクリーン - Google Patents
透過投映スクリーン Download PDFInfo
- Publication number
- JP6368911B2 JP6368911B2 JP2014119256A JP2014119256A JP6368911B2 JP 6368911 B2 JP6368911 B2 JP 6368911B2 JP 2014119256 A JP2014119256 A JP 2014119256A JP 2014119256 A JP2014119256 A JP 2014119256A JP 6368911 B2 JP6368911 B2 JP 6368911B2
- Authority
- JP
- Japan
- Prior art keywords
- composite oxide
- colorant
- light
- cobalt
- chromium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
実施例及び比較例で作成した透過投映スクリーンについて以下の評価を行った。透過投映スクリーンのサイズはたて1.5m×よこ2.0mとして、背面に映像投映装置として液晶式ビデオプロジェクター(セイコーエプソン社製EH−TW500S)を使用した。
<プロジェクター光源の視認性:ホットスポットの有無>
たて1.5m×よこ2.0mの透過投映スクリーンの裏面2mの距離にビデオプロジェクターを配置した。投映映像をシート真正面から観察し、以下の基準で評価した。
1:ホットスポット無:プロジェクター光源位置が認知できない
2:軽微なホットスポットを認める:おぼろにプロジェクター光源位置が認知できる
3:ホットスポット有:プロジェクター光源位置がはっきりと認知できる
<映像の発色鮮明性(コントラスト性)>
1:輝度が高く鮮明
2:輝度が高く不鮮明
3:輝度が低く不鮮明
<可視光透過率>
透過投映スクリーンの可視光透過率を、分光側色計CM−3600d(コニカミノルタ社製)を使用しJIS Z8722に従って測定した。
<マンセル明度>
透過投映スクリーンのマンセル明度(JIS Z8721)をMUNSELL BOOK OF COLOR 標準色見本に照合させた。
<熱線反射効果>
室内でASTM D4803-97法による250W赤外線ランプ照射による昇温曲線を30分間測定し、30分後の温度を求めた。
<遮熱効果>
幅100cm×高さ100cm×奥ゆき100cmの立方体の骨組みをアルミ製L型アングル(幅35mm)で組み立て、立方体骨組の底面を除く全面に透過投映スクリーンを貼付固定し試験箱体を作製した。この試験箱体を正午〜13時の太陽光が直射される環境(埼玉県草加市5月:晴天:気温28℃)での試験箱体内部温度を温度センサー(試験箱体内部中心に温度センサーを床上50cmに宙吊固定)で測定した。
環状オレフィンコポリマーとして、エチレンとノルボルネンとの共重合体(ノルボルネン含有率78質量%):商標「TOPAS」:品番6015:ポリプラスチックス社製:屈折率1.53(ISO489):光線透過率(2mmt)91(ISO13468−2)、光拡散性粒子として、架橋ポリメタクリル酸メチル球状粒子(平均粒子径20μm):商標「テクポリマー」:品番MBX−20:積水化成品工業社製:屈折率1.49を用いた。また、黄色系着色剤としてクロム−アンチモン−チタン複合酸化物、赤色系着色剤としてC.I.PR122、青色系着色剤としてC.I.PB15:3を用い、下記配合1により、165℃の熱ロール条件でカレンダー成形を行い、厚さ0.2mm、可視光透過率60%、マンセル明度3.0のシートを得た。
<配合1>
環状オレフィンコポリマー 100質量部
光拡散性粒子 15質量部
黄色系着色剤(クロム−アンチモン−チタン複合酸化物) 0.5質量部
赤色系着色剤(C.I.PR122) 0.5質量部
青色系着色剤(C.I.PB15:3) 0.5質量部
実施例1の配合1を下記配合2に変更した以外は実施例1と同様にして、厚さ0.2mm、可視光透過率56%、マンセル明度2.5のシートを得た。
<配合2>
環状オレフィンコポリマー 100質量部
光拡散性粒子 15質量部
黄色系着色剤(C.I.PY110) 0.5質量部
赤色系着色剤(C.I.PR122) 0.5質量部
青色系着色剤(コバルト−アルミニウム−クロム複合酸化物) 0.5質量部
実施例1の配合1を下記配合3に変更した以外は実施例1と同様にして、厚さ0.2mm、可視光透過率55%、マンセル明度2.0のシートを得た。
<配合3>
環状オレフィンコポリマー 100質量部
光拡散性粒子 15質量部
黄色系着色剤(クロム−アンチモン−チタン複合酸化物) 0.3質量部
赤色系着色剤(C.I.PR122) 0.3質量部
青色系着色剤(C.I.PB15:3) 0.3質量部
黒色系着色剤(鉄−クロム複合酸化物) 0.3質量部
実施例1の配合1を下記配合4に変更した以外は実施例1と同様にして、厚さ0.2mm、可視光透過率57%、マンセル明度2.5のシートを得た。
<配合4>
環状オレフィンコポリマー 100質量部
光拡散性粒子(光半透過性黒色粒子) 15質量部
※黒色色素C.I. Pigment Black7をメタクリル酸メチル樹脂に対して0.3質量%濃
度で含有する可視光透過率が40%の、平均粒子径20μmの光半透過性黒色粒子で、
コントラスト引締効果に寄与する
黄色系着色剤(クロム−アンチモン−チタン複合酸化物) 0.3質量部
赤色系着色剤(C.I.PR122) 0.3質量部
青色系着色剤(C.I.PB15:3) 0.3質量部
実施例1の配合1において、環状オレフィンコポリマーを軟質塩化ビニル樹脂に変更した配合5とした以外は実施例1と同様にして、厚さ0.2mm、可視光透過率56%、マンセル明度3.0のシートを得た。
<配合5>
ポリ塩化ビニル樹脂 100質量部
DOP(可塑剤) 65質量部
エポキシ化大豆油 2質量部
Ba−Zn系複合安定剤 1.5質量部
ステアリン酸バリウム(滑剤) 0.2質量部
ベンゾトリアゾール系紫外線吸収剤 0.3質量部
光拡散性粒子(架橋ポリメタクリル酸メチル球状粒子:20μm) 15質量部
黄色系着色剤(クロム−アンチモン−チタン複合酸化物) 0.5質量部
赤色系着色剤(C.I.PR122) 0.5質量部
青色系着色剤(C.I.PB15:3) 0.5質量部
実施例2の配合2において、環状オレフィンコポリマーを軟質塩化ビニル樹脂に変更した配合6とした以外は実施例2と同様にして、厚さ0.2mm、可視光透過率54%、マンセル明度2.5のシートを得た。
<配合6>
ポリ塩化ビニル樹脂 100質量部
DOP(可塑剤) 65質量部
エポキシ化大豆油 2質量部
Ba−Zn系複合安定剤 1.5質量部
ステアリン酸バリウム(滑剤) 0.2質量部
ベンゾトリアゾール系紫外線吸収剤 0.3質量部
光拡散性粒子(架橋ポリメタクリル酸メチル球状粒子:20μm) 15質量部
黄色系着色剤(C.I.PY110) 0.5質量部
赤色系着色剤(C.I.PR122) 0.5質量部
青色系着色剤(コバルト−アルミニウム−クロム複合酸化物) 0.5質量部
実施例3の配合3において、環状オレフィンコポリマーを軟質塩化ビニル樹脂に変更した配合7とした以外は実施例3と同様にして、厚さ0.2mm、可視光透過率53%、マンセル明度2.0のシートを得た。
<配合7>
ポリ塩化ビニル樹脂 100質量部
DOP(可塑剤) 65質量部
エポキシ化大豆油 2質量部
Ba−Zn系複合安定剤 1.5質量部
ステアリン酸バリウム(滑剤) 0.2質量部
ベンゾトリアゾール系紫外線吸収剤 0.3質量部
光拡散性粒子(架橋ポリメタクリル酸メチル球状粒子:20μm) 15質量部
黄色系着色剤(クロム−アンチモン−チタン複合酸化物) 0.3質量部
赤色系着色剤(C.I.PR122) 0.3質量部
青色系着色剤(C.I.PB15:3) 0.3質量部
黒色系着色剤(鉄−クロム複合酸化物) 0.3質量部
実施例4の配合4において、環状オレフィンコポリマーを軟質塩化ビニル樹脂に変更した配合8とした以外は実施例4と同様にして、厚さ0.2mm、可視光透過率55%、マンセル明度2.5のシートを得た。
<配合8>
ポリ塩化ビニル樹脂 100質量部
DOP(可塑剤) 65質量部
エポキシ化大豆油 2質量部
Ba−Zn系複合安定剤 1.5質量部
ステアリン酸バリウム(滑剤) 0.2質量部
ベンゾトリアゾール系紫外線吸収剤 0.3質量部
光拡散性粒子(光半透過性黒色粒子) 15質量部
※黒色色素C.I. Pigment Black7をメタクリル酸メチル樹脂に対して0.3質量%濃
度で含有する可視光透過率が40%の、平均粒子径20μmの光半透過性黒色粒子で、
コントラスト引締効果に寄与する
黄色系着色剤(クロム−アンチモン−チタン複合酸化物) 0.3質量部
赤色系着色剤(C.I.PR122) 0.3質量部
青色系着色剤(C.I.PB15:3) 0.3質量部
実施例1のシートと下記ガラス織布とを積層し、ガラス織布の片面に光透過性樹脂シートを有する、厚さ0.45mm、可視光透過率36%、マンセル明度3.0のスクリーンを得た。
<ガラス織布>
375dtexのEガラス(屈折率1.558)無撚扁平マルチフィラメント糸条を経糸及び緯糸として、経糸打込密度32本/inch、緯糸打込密度32本/inchで平織してなる空隙率1.0%未満、質量100g/m2のガラス織布(シランカップリング処理)
実施例5のシートと実施例9で用いたガラス織布とを積層し、ガラス織布の片面に光透過性樹脂シートを有する、厚さ0.45mm、可視光透過率36%、マンセル明度3.0のスクリーンを得た。
実施例1のシートの厚さを0.1mmに変更し、実施例9で用いたガラス織布の両面に積層し、ガラス織布の両面に光透過性樹脂シートを有する、厚さ0.45mm、可視光透過率36%、マンセル明度3.5のスクリーンを得た。
実施例5のシートの厚さを0.1mmに変更し、実施例9で用いたガラス織布の両面に積層し、ガラス織布の両面に光透過性樹脂シートを有する、厚さ0.45mm、可視光透過率36%、マンセル明度3.5のスクリーンを得た。
環状オレフィンコポリマーとして、エチレンとノルボルネンとの共重合体(ノルボルネン含有率78質量%):商標「TOPAS」:品番6015:ポリプラスチックス社製:屈折率1.53(ISO489):光線透過率(2mmt)91(ISO13468−2)、光拡散性粒子として、架橋ポリメタクリル酸メチル球状粒子(平均粒子径20μm):商標「テクポリマー」:品番MBX−20:積水化成品工業社製:屈折率1.49を用い、下記配合9により、165℃の熱ロール条件でカレンダー成形を行い、厚さ0.1mmのシート(光拡散性粒子を含有する層)を得た。
<配合9>
環状オレフィンコポリマー 100質量部
光拡散性粒子 15質量部
次に同じ品番の環状オレフィンコポリマーに対し、黄色系着色剤としてクロム−アンチモン−チタン複合酸化物、赤色系着色剤としてC.I.PR122、青色系着色剤としてC.I.PB15:3を用い、下記配合10により、165℃の熱ロール条件でカレンダー成形を行い、厚さ0.2mmのシート(着色剤を含有する層)を得た。次にこの2枚のシートを165℃の熱ロール条件でラミネートを行い、厚さ0.3mm、可視光透過率55%、マンセル明度3.0のシートを得た。
<配合10>
環状オレフィンコポリマー 100質量部
黄色系着色剤(クロム−アンチモン−チタン複合酸化物) 0.3質量部
赤色系着色剤(C.I.PR122) 0.3質量部
青色系着色剤(C.I.PB15:3) 0.3質量部
黒色系着色剤(鉄−クロム複合酸化物) 0.3質量部
実施例13の配合9を下記配合11に変更し、また実施例13の配合10を下記配合12に変更した以外は実施例13と同様とし、厚さ0.3mm、可視光透過率58%、マンセル明度3.0のシートを得た。
<配合11>
環状オレフィンコポリマー 100質量部
光拡散性粒子(光半透過性黒色粒子) 15質量部
※黒色色素C.I. Pigment Black7をメタクリル酸メチル樹脂に対して0.3質量%濃
度で含有する可視光透過率が40%の、平均粒子径20μmの光半透過性黒色粒子で、
コントラスト引締効果に寄与する
<配合12>
環状オレフィンコポリマー 100質量部
黄色系着色剤(クロム−アンチモン−チタン複合酸化物) 0.3質量部
赤色系着色剤(C.I.PR122) 0.3質量部
青色系着色剤(C.I.PB15:3) 0.3質量部
実施例13の配合9において、環状オレフィンコポリマーを軟質塩化ビニル樹脂に変更した下記配合13とした以外は実施例13と同様にして、厚さ0.1mmのシート(光拡散性粒子を含有する層)を得た。
<配合13>
ポリ塩化ビニル樹脂 100質量部
DOP(可塑剤) 65質量部
エポキシ化大豆油 2質量部
Ba−Zn系複合安定剤 1.5質量部
ステアリン酸バリウム(滑剤) 0.2質量部
ベンゾトリアゾール系紫外線吸収剤 0.3質量部
光拡散性粒子(架橋ポリメタクリル酸メチル球状粒子:20μm) 15質量部
次に実施例13の配合10において、環状オレフィンコポリマーを軟質塩化ビニル樹脂に変更した下記配合14とした以外は実施例13と同様にして、厚さ0.2mmのシート(着色剤を含有する層)を得た。次にこの2枚のシートを165℃の熱ロール条件でラミネートを行い、厚さ0.3mm、可視光透過率53%、マンセル明度3.0のシートを得た。
<配合14>
ポリ塩化ビニル樹脂 100質量部
DOP(可塑剤) 65質量部
エポキシ化大豆油 2質量部
Ba−Zn系複合安定剤 1.5質量部
ステアリン酸バリウム(滑剤) 0.2質量部
ベンゾトリアゾール系紫外線吸収剤 0.3質量部
黄色系着色剤(クロム−アンチモン−チタン複合酸化物) 0.5質量部
赤色系着色剤(C.I.PR122) 0.5質量部
青色系着色剤(C.I.PB15:3) 0.5質量部
実施例15の配合13を下記配合15に変更し、また実施例15の配合14を下記配合16に変更した以外は実施例15と同様とし、厚さ0.3mm、可視光透過率56%、マンセル明度3.0のシートを得た。
<配合15>
ポリ塩化ビニル樹脂 100質量部
DOP(可塑剤) 65質量部
エポキシ化大豆油 2質量部
Ba−Zn系複合安定剤 1.5質量部
ステアリン酸バリウム(滑剤) 0.2質量部
ベンゾトリアゾール系紫外線吸収剤 0.3質量部
光拡散性粒子(光半透過性黒色粒子) 15質量部
※黒色色素C.I. Pigment Black7をメタクリル酸メチル樹脂に対して0.3質量%濃
度で含有する可視光透過率が40%の、平均粒子径20μmの光半透過性黒色粒子で、
コントラスト引締効果に寄与する
<配合16>
ポリ塩化ビニル樹脂 100質量部
DOP(可塑剤) 65質量部
エポキシ化大豆油 2質量部
Ba−Zn系複合安定剤 1.5質量部
ステアリン酸バリウム(滑剤) 0.2質量部
ベンゾトリアゾール系紫外線吸収剤 0.3質量部
黄色系着色剤(クロム−アンチモン−チタン複合酸化物) 0.3質量部
赤色系着色剤(C.I.PR122) 0.3質量部
青色系着色剤(C.I.PB15:3) 0.3質量部
実施例1〜16のスクリーンの両面に下記配合17による塗液組成物を100メッシュグラビアロールで塗布し、これを乾燥し数日養生してゾルゲル硬化を完了させ防汚層兼帯電防止層を形成した。
<配合17>防汚層兼帯電防止層
シリカゾル(粒子径20〜30nm:固形分48質量%の無機コロイド)100質量部
ビニルトリエトキシシラン(シランカップリング剤) 50質量部
ベンゾトリアゾール化合物(紫外線吸収剤) 1質量部
ポリエチレングリコール型非イオン活性剤(帯電防止剤) 1質量部
希釈剤(水) 100質量部
実施例1において、光拡散性粒子の配合を省略した以外は実施例1と同様として、厚さ0.2mm、可視光透過率56%、マンセル明度3.0のシートを得た。
実施例1において、黄色系着色剤(クロム−アンチモン−チタン複合酸化物)、赤色系着色剤(C.I.PR122)、及び青色系着色剤(C.I.PB15:3)の各0.5質量部の配合を省略した以外は実施例1と同様として、厚さ0.2mm、可視光透過率90%、マンセル明度8.5のシートを得た。
実施例1において、黄色系着色剤(クロム−アンチモン−チタン複合酸化物)の配合を省略した以外は実施例1と同様として、厚さ0.2mm、可視光透過率62%、マンセル明度5.5のシートを得た。
実施例1において、黄色系着色剤(クロム−アンチモン−チタン複合酸化物)0.5質量部を、黄色系着色剤(C.I.PY110)0.5質量部に置換した以外は実施例1と同様として、厚さ0.2mm、可視光透過率59%、マンセル明度3.5のシートを得た。
実施例1において、黄色系着色剤(クロム−アンチモン−チタン複合酸化物)、赤色系着色剤(C.I.PR122)、及び青色系着色剤(C.I.PB15:3)の各0.5質量部の配合を省略し、代わりに黒色系着色剤を用いた配合10とした以外は実施例1と同様として、厚さ0.2mm、可視光透過率35%、マンセル明度1.5のシートを得た。
<配合10>
環状オレフィンコポリマー 100質量部
光拡散性粒子 15質量部
黒色色素(C.I. Pigment Black7) 1.5質量部
2:熱可塑性樹脂
2−1:光拡散性粒子を含有する層
2−2:着色剤を含有する層
3:光拡散性粒子
3−1:光半透過性黒色粒子
4:黄色系着色剤(Y)
5:赤色系着色剤(R)
6:青色系着色剤(B)
7:黒色系着色剤(K)
8:光透過性織布
Claims (6)
- 平均粒子径5〜30μmの光拡散性粒子を含有する光透過性樹脂シートであって、前記光透過性樹脂シートが、赤色系着色剤、青色系着色剤、及び黄色系着色剤との減色混合によりマンセル明度0〜4(マンセル表色系)に調整され、前記赤色系着色剤、前記青色系着色剤、及び前記黄色系着色剤の何れか1種の着色系が金属複合酸化物のみを着色剤に含み、かつ、残り2種の着色系には有機色素及び/または有機顔料のみを含み、1)前記赤色系着色剤に前記金属複合酸化物を含む場合には、亜鉛−鉄−クロム複合酸化物、亜鉛−鉄−クロム−アルミニウム複合酸化物から選ばれた1種以上を用い、2)前記青色系着色剤に前記金属複合酸化物を含む場合には、コバルト−アルミニウム複合酸化物、コバルト−アルミニウム−クロム複合酸化物、コバルト−アルミニウム−マグネシウム複合酸化物、コバルト−アルミニウム−亜鉛複合酸化物、コバルト−錫複合酸化物、コバルト−ニッケル−亜鉛複合酸化物、コバルト−ニッケル−チタン−亜鉛複合酸化物、コバルト−亜鉛−マグネシウム複合酸化物、コバルト−亜鉛−クロム−チタン複合酸化物、コバルト−亜鉛−ニッケル−チタン複合酸化物から選ばれた1種以上を用い、3)前記黄色系着色剤に前記金属複合酸化物を含む場合には、ビスマス−バナジウム−アルミニウム複合酸化物、ニッケル−バリウム−チタン複合酸化物、ニッケル−チタン複合酸化物、ニッケル−アンチモン−チタン複合酸化物、クロム−アンチモン−チタン複合酸化物、鉛−アンチモン−チタン複合酸化物から選ばれた1種以上を用いることによって近赤外線反射性を発現することを特徴とする透過投映スクリーン。
- 前記光透過性樹脂シートが、さらに黒色系着色剤を含み、この黒色系着色剤が、鉄−クロム複合酸化物、鉄−クロム−コバルト複合酸化物、鉄−クロム−コバルト−マンガン複合酸化物、銅−クロム複合酸化物、銅−マグネシウム複合酸化物、銅−クロム−マンガン複合酸化物、銅−ビスマス複合酸化物、マンガン−ビスマス複合酸化物から選ばれた1種以上の金属複合酸化物であり、それによってコントラスト調整能を補助し、かつ近赤外線反射性を補助する請求項1記載の透過投映スクリーン。
- 前記光拡散性粒子が光半透過性黒色粒子である請求項1または2に記載の透過投映スクリーン。
- 前記光拡散性樹脂シートが光透過性織布を芯材に含む請求項1〜3のいずれか1項に記載の透過投映スクリーン。
- 前記光透過性樹脂シートが積層構造を有し、前記光拡散性粒子を含有する層と、前記着色剤を含有する層とに分れている請求項1〜4のいずれか1項に記載の透過投映スクリーン。
- 前記光透過性樹脂シートの表面抵抗値(測定方法:JIS K6911、測定条件:湿度30%RH−温度23℃)が、1.0E+12Ω未満である請求項1〜5のいずれか1項に記載の透過投映スクリーン。