JP6367260B2 - 抗菌性製品及びその製造方法 - Google Patents
抗菌性製品及びその製造方法 Download PDFInfo
- Publication number
- JP6367260B2 JP6367260B2 JP2016093034A JP2016093034A JP6367260B2 JP 6367260 B2 JP6367260 B2 JP 6367260B2 JP 2016093034 A JP2016093034 A JP 2016093034A JP 2016093034 A JP2016093034 A JP 2016093034A JP 6367260 B2 JP6367260 B2 JP 6367260B2
- Authority
- JP
- Japan
- Prior art keywords
- silver
- antibacterial
- nitrogen atmosphere
- sintered
- particulate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明に係る抗菌性製品は一つ以上の抗菌部を含み、前記抗菌部は窒素雰囲気下焼結銀含有表面層を含むことができる。
食品容器の内壁及び/又は唇接触部の一部若しくは全体であり得る。本発明の一実施形態
に係る食品容器は、食品容器の内壁の一部または全体上に第1窒素雰囲気下焼結銀含有表面層を含むことができ、前記食品容器の唇接触部の一部または全体上に第2窒素雰囲気下焼結銀含有表面層を含むことができる。
照すると、真空水筒が外筒10、内筒20及び唇接触部30で構成される。前記内筒20
の内壁の一部または全体上に第1窒素雰囲気下焼結銀含有表面層が含まれ、前記唇接触部30の一部または全体上に第2窒素雰囲気下焼結銀含有表面層が含まれる。図2、図3及び図4はそれぞれ本発明の一実施形態に係る食品容器(真空水筒)の抗菌部(唇接触部;30)の断面図、側面図及び斜視図である。
本発明の一実施形態に係る一つ以上の抗菌部を含む抗菌性製品の製造方法は、水または極性有機溶媒に銀塩類化合物粉末を添加し、溶解させて銀塩類溶解液を製造する第1工程と、前記銀塩類溶解液を抗菌部上に塗布する第2工程と、前記抗菌部に塗布された銀塩類化合物を窒素雰囲気の下で焼結して前記抗菌部上に層状窒素雰囲気下焼結銀含有表面層を形成する第3工程とを含むことができる。
μmであり得る。本発明の一実施形態において、前記粒子状窒素雰囲気下焼結銀における窒素雰囲気下焼結銀の厚さ(粒子状窒素雰囲気下焼結銀の中心から表面までの半径から鉱物系または岩石系粒子の半径を除いた距離)を0.1μm乃至20μmにすることができる。この範囲の場合、優れた抗菌効果を示すことができる。
試験用銀真空焼結ボトルを用いた。
非酸化銀ボトルの抗菌試験
次の抗菌試験は日本食品分析センターに依頼して行った。前記銀真空焼結ボトルの大腸菌に対する抗菌力を試験した。
検体:銀真空焼結ボトルに大腸菌含有ミネラルウォーター200mLを入れてそのまま置いたもの
対照:滅菌合成樹脂製の容器に大腸菌含有精製水200mLを入れてそのまま置いたもの
それぞれの検体を20℃で保存しながら時間の経過による大腸菌数を測定し、その結果を次の表1に示した。
前記表1及び図4を参照すると、試験用銀真空焼結ボトルは、大腸菌を含むミネラルウォーターの流入6時間後にも、その大腸菌をほとんど死滅させなかったことが分かる。
図1のように上部にねじ山が形成された内壁(ステンレス鋼製)、外筒(ステンレス鋼製)、内壁と外筒との間の真空部、及び外面にねじ山が形成された唇接触部(アルミ合金製)で構成された円筒状の食品容器(高さ:20cm、直径:5cm)を製作した。水100重量部に硝酸銀粉末1.5重量部を添加し、溶解させて硝酸銀水溶液を製造した。硝酸銀水溶液を食品容器の内壁及び唇接触部の上に塗布した。塗布部を大気下に440℃で120分間焼結して、内壁の上に第1酸化銀焼結表面層を形成し、唇接触部の上に第2酸化銀焼結表面層を形成し、温度を20℃に降温した。水で洗浄した後、室温で乾燥させ、内壁と唇接触部に酸化銀焼結表面層が形成されたボトルを製造した。
酸化銀ボトルの抗菌試験
次の抗菌試験は日本食品分析センターに依頼して行った。前述のように製造された酸化銀ボトルの大腸菌に対する抗菌力を試験した。
検体1)酸化銀ボトルに大腸菌含有ミネラルウォーター200mLを入れてそのまま置いたもの
検体2)酸化銀ボトルに大腸菌含有ミネラルウォーター200mLを入れて逆さまに置いたもの
対照:滅菌合成樹脂製の容器に大腸菌含有精製水200mLを入れてそのまま置いたもの
それぞれの検体を20℃で保存しながら時間の経過による大腸菌数を測定し、その結果を次の表2に示した。
前記表2と図10を参照すると、酸化銀ボトルは大腸菌含有ミネラルウォーターの流入6時間後にその大腸菌を完全に死滅させたことが分かる。
水1000mLにタルク粒子(E553b:EU認可番号)0.5Kgと硝酸銀粉末10gを添加し、混合して乾燥した後、大気下で前記乾燥粉末を440℃で120分間焼結することにより、その内部コアにタルク粒子を含む粒子状酸化銀焼結体を製造した。プラスチック材料(ポリプロピレン)100重量部と前記粒子状酸化銀焼結体40重量部とを混合し、加熱してペレットに製造した。当該ペレットによりまな板(横:34cm、縦:23cm、高さ:0.3cm)を成形した。まな板の上下使用面の全域にサンドブラスト加工を行い、まな板の上下面に粒子状酸化銀焼結体を露出させた。製造されたまな板を検体2として使用した。
まな板の抗菌試験
次の抗菌試験は日本食品分析センターに依頼して行った。次の検体に対して、大腸菌に対する抗菌力を試験した。
無加工1)ポリエチレンフィルムに大腸菌含有ミネラルウォーター200mLを振り撒いた直後
検体1)サンドブラスト加工を行っていない以外は上記の方法で製造されたまな板に大腸菌含有ミネラルウォーター200mLを撒いて35℃で24時間そのまま置いたもの
検体2)上記の方法で製造されたまな板に大腸菌含有ミネラルウォーター200mLを撒いて35℃で24時間そのまま置いたもの
無加工2)ポリエチレンフィルムに大腸菌含有ミネラルウォーター200mLを撒いて35℃で24時間そのまま置いたもの
それぞれの検体で大腸菌数を測定し、その結果を次の表3に示した。
抗菌能力試験結果評価について抗菌能力試験実施機関たる日本食品分析センターでの抗菌能力の有無判定要件として、残存生菌数比較で2桁以上の残存生菌数差確認によって抗菌能力有無の判定を為す規定が存在するが、これによれば、3桁の格差を示した本発明の一実施形態のまな板は十分な抗菌性能が確認されて有用と認められる。
図1のように上部にねじ山が形成された内壁(ステンレス鋼製)、外筒(ステンレス鋼製)、内壁と外筒との間の真空部、及び外面にねじ山が形成された唇接触部(アルミ合金製)で構成された円筒状の食品容器(高さ:20cm、直径:5cm)を製作した。水100重量部に硝酸銀粉末1.5重量部を添加し、溶解させて硝酸銀水溶液を製造した。硝酸銀水溶液を食品容器の内壁と唇接触部の上に塗布した。塗布部を窒素雰囲気(窒素99〜100体積%)下において440℃で120分間焼結して、内壁の上に第1窒素雰囲気下焼結銀表面層を形成し、唇接触部の上に第2窒素雰囲気下焼結銀表面層を形成し、温度を20℃に降温した。水で洗浄した後、室温で乾燥することにより、内壁と唇接触部に窒素雰囲気下焼結銀表面層が形成されたボトルを製造した。
窒素雰囲気下焼結銀ボトルの抗菌試験
次の抗菌試験は日本食品分析センターに依頼して行った。前述のように製造された窒素雰囲気下焼結銀ボトルの大腸菌に対する抗菌力を試験した。
検体)窒素雰囲気下焼結銀ボトルに大腸菌含有ミネラルウォーター200mLを入れてそのまま置いたもの
対照:滅菌合成樹脂製の容器に大腸菌含有精製水200mLを入れてそのまま置いたもの
それぞれの検体を20℃で保存しながら時間の経過による大腸菌数を測定し、その結果を下記表4に示した。
前記表4及び図12を参照すると、窒素雰囲気下焼結銀ボトルは大腸菌含有ミネラルウォーターの流入2時間後にその大腸菌を完全に死滅させたことが分かる。
ステンレス鋼製のプレート(10cm×10cm×1cm)を製作した。水100重量部に硝酸銀粉末1.5重量部を添加し、溶解させて硝酸銀水溶液を製造した。硝酸銀水溶液をプレート上に塗布した。塗布部を窒素雰囲気(窒素99ないし100体積%)下において440℃で120分間焼結して、プレート上に窒素雰囲気下焼結銀表面層を形成し、温度を20℃に降温した。水で洗浄した後、室温で乾燥させ、その上に窒素雰囲気下焼結銀表面層を含むプレートを製造した。
窒素雰囲気下焼結銀プレート抗菌試験
次の抗菌試験は日本食品分析センターに依頼して行った。前述のように製造された窒素雰囲気下焼結銀プレートに対してストレプトコッカス・ミュータンスに対する抗菌力を試験した。
検体) 窒素雰囲気下焼結銀プレートにストレプトコッカス・ミュータンスを含むミネラルウォーター200mLを塗布してそのまま置いたもの
無加工) ポリエチレンフィルムにストレプトコッカス・ミュータンスを含む精製水200mLを塗布してそのまま置いたもの
それぞれの検体を35℃で保存しながら時間の経過によるストレプトコッカス・ミュータンスの数を測定し、その結果を次の表5に示した。
(付記1)
抗菌性製品において、
前記抗菌性製品は一つ以上の抗菌部を含み、前記抗菌部は窒素雰囲気下焼結銀含有表面層を含む、抗菌性製品。
前記抗菌部または前記抗菌性製品の材料が、金属、硝子、セラミック、石材、鉱物、プラスチック及びこれらの組み合わせから選ばれる材料を含む、付記1に記載の抗菌性製品。
前記抗菌部が、板状、球状、棒状、塊状、粒状、砂状または抗菌性製品の形状から選ばれる形状を有する、付記1に記載の抗菌性製品。
前記窒素雰囲気下焼結銀含有表面層は、基材として層状窒素雰囲気下焼結銀を含み、抗菌部の表面に位置する層(層状窒素雰囲気下焼結銀含有表面層)であるか、または、基材としてプラスチックを含み、基材の表面に露出した粒子状窒素雰囲気下焼結銀、若しくは基材の表面に露出した粒子状窒素雰囲気下焼結銀と基材内に分散した粒子状窒素雰囲気下焼結銀とを含み、抗菌部の表面に位置する層(粒子状窒素雰囲気下焼結銀含有表面層)である、付記1に記載の抗菌性製品。
前記層状窒素雰囲気下焼結銀含有表面層の下の抗菌部の一部若しくは全体が粗面であり、または粒子状窒素雰囲気下焼結銀含有表面層の一部若しくは全体が粗面である、付記4に記載の抗菌性製品。
前記粗面がサンドブラスト加工によって形成された、付記5に記載の抗菌性製品。
前記層状窒素雰囲気下焼結銀含有表面層の厚さが0.1μm乃至20μmであり、または前記粒子状窒素雰囲気下焼結銀含有表面層の厚さが10μm乃至20μmである、付記4に記載の抗菌性製品。
前記粒子状窒素雰囲気下焼結銀含有表面層と前記抗菌部とが一体に形成された、付記4に記載の抗菌性製品。
前記抗菌部と前記粒子状窒素雰囲気下焼結銀含有表面層が、粒子状窒素雰囲気下焼結銀をプラスチック100重量部に対して1乃至60重量部で含む、付記8に記載の抗菌性製品。
前記粒子状窒素雰囲気下焼結銀の内部コアが鉱物系または岩石系粒子を含む、付記4に記載の抗菌性製品。
前記鉱物系または岩石系粒子と前記窒素雰囲気下焼結銀との重量比が100:0.1乃至10である、付記10に記載の抗菌性製品。
一つ以上の抗菌部を含む抗菌性製品の製造方法において、
水または極性有機溶媒に銀塩類化合物粉末を添加し、溶解させて銀塩類溶解液を製造する第1工程と、
前記銀塩類溶解液を前記抗菌部上に塗布する第2工程と、
前記抗菌部上に塗布された銀塩類化合物を窒素雰囲気下で焼結して、前記抗菌部上に層状窒素雰囲気下焼結銀含有表面層を形成する第3工程と、
を含む、抗菌性製品の製造方法。
前記抗菌部の材料が金属、硝子、セラミック、石材、鉱物及びこれらの組み合わせから選択される材料を含む、付記12に記載の抗菌性製品の製造方法。
前記第1工程で、前記水または極性有機溶媒100重量部に前記銀塩類化合物粉末1〜10重量部を添加する、付記12に記載の抗菌性製品の製造方法。
前記銀塩類化合物が炭酸銀、塩素酸銀、塩化銀、クロム酸銀、バナジウム酸銀、マンガン酸銀、硝酸銀、亜硝酸銀、過塩素酸銀、リン酸銀、酢酸銀及びこれらの混合物から選択される、付記12に記載の抗菌性製品の製造方法。
前記第3工程で、焼結温度が440℃以上である、付記12に記載の抗菌性製品の製造方法。
前記第2工程の前に、前記抗菌部に粗面を形成し、前記第2工程で、前記銀塩類溶解液を前記粗面の上に塗布する、付記12に記載の抗菌性製品の製造方法。
前記粗面をサンドブラスト加工で形成する、付記17に記載の抗菌性製品の製造方法。
前記層状窒素雰囲気下焼結銀含有表面層を0.1μm〜20μmの厚さに形成する、付記12に記載の抗菌性製品の製造方法。
前記第3工程の後に、前記抗菌部を含む抗菌性製品を製造する工程をさらに含む、付記12に記載の抗菌性製品の製造方法。
一つ以上の抗菌部を含む抗菌性製品の製造方法において、
水または極性有機溶媒100重量部に銀塩類化合物粉末1〜10重量部を添加し、溶解させて銀塩類溶解液を製造する第1工程と、
前記銀塩類溶解液を抗菌部上に塗布する第2工程と、
前記抗菌部に塗布された銀塩類化合物を窒素雰囲気または大気下で焼結して、前記抗菌部上に層状窒素雰囲気下焼結銀含有表面層または層状酸化銀焼結体含有表面層を形成する第3工程と、
を含む、抗菌性製品の製造方法。
一つ以上の抗菌部を含む抗菌性製品の製造方法において、
水または極性有機溶媒に鉱物系または岩石系粒子と銀塩類化合物粉末を添加し、混合した後、窒素雰囲気下で前記銀塩類化合物を焼結して、その内部コアに鉱物系または岩石系粒子を含む粒子状窒素雰囲気下焼結銀を製造する第1工程と、
プラスチック材料と前記粒子状窒素雰囲気下焼結銀とを混合し、加熱してペレットに製造する第2工程と、
前記ペレットを用いて前記抗菌部を成形する第3工程と、
前記抗菌部にサンドブラスト加工を行い、前記抗菌部の表面に前記粒子状窒素雰囲気下焼結銀を露出させる第4工程と、
を含む、抗菌性製品の製造方法。
前記第1工程で、鉱物系または岩石系粒子と銀塩類化合物粉末との重量比が100:0.1〜10であり、前記鉱物系または岩石系粒子及び銀塩類化合物粉末の混合物と前記水または極性有機溶媒との重量比が1〜70:100である、付記22に記載の抗菌性製品の製造方法。
前記銀塩類化合物が炭酸銀、塩素酸銀、塩化銀、クロム酸銀、バナジウム酸銀、マンガン酸銀、硝酸銀、亜硝酸銀、過塩素酸銀、リン酸銀、酢酸銀及びこれらの混合物から選択される、付記22に記載の抗菌性製品の製造方法。
前記第1工程で、焼結温度が440℃以上である、付記22に記載の抗菌性製品の製造方法。
前記第2工程で、前記プラスチック材料と前記粒子状窒素雰囲気下焼結銀との重量比が100:1〜60である、付記22に記載の抗菌性製品の製造方法。
一つ以上の抗菌部を含む抗菌性製品の製造方法において、
水または極性有機溶媒に鉱物系または岩石系粒子と銀塩類化合物粉末を添加し、混合した後、窒素雰囲気または大気下で前記銀塩類化合物を焼結して、その内部コアに鉱物系または岩石系粒子を含む粒子状窒素雰囲気下焼結銀または粒子状酸化銀焼結体を製造する第1工程と、
プラスチック材料と前記粒子状窒素雰囲気下焼結銀または粒子状酸化銀焼結体とを混合し、加熱してペレットに製造する第2工程と、
前記ペレットを用いて前記抗菌部を成形する第3工程と、
前記抗菌部にサンドブラスト加工を行い、前記抗菌部の表面に前記粒子状窒素雰囲気下焼結銀または粒子状酸化銀焼結体を露出させる第4工程と、
を含む、抗菌性製品の製造方法。
水または極性有機溶媒100重量部に銀塩類化合物粉末1ないし10重量部を添加し、溶解させて銀塩類溶解液を製造する第1工程と、
前記銀塩類溶解液に金属纎維からなる金属たわしを浸漬し、前記銀塩類溶解液を前記金属たわしの繊維の部分または全体表面上に塗布する第2工程と、
前記金属たわしの繊維の部分または全体表面上に塗布された銀塩類化合物を窒素雰囲気下で440℃以上の温度で焼結し、前記金属たわしの繊維の部分または全体表面上に窒素雰囲気下焼結銀含有表面層を形成する第3工程と、
を含む、製造方法により製造された抗菌性金属たわし。
Claims (28)
- 抗菌性製品において、
前記抗菌性製品は一つ以上の抗菌部を含み、前記抗菌部は窒素雰囲気下焼結銀含有表面層を含み、
窒素雰囲気下焼結銀は、銀塩類化合物を、窒素雰囲気下で440〜1000℃で焼結した銀である、抗菌性製品。 - 前記抗菌部または前記抗菌性製品の材料が、金属、硝子、セラミック、石材、鉱物、プラスチック及びこれらの組み合わせから選ばれる材料を含む、請求項1に記載の抗菌性製品。
- 前記抗菌部が、板状、球状、棒状、塊状、粒状、砂状または抗菌性製品の形状から選ばれる形状を有する、請求項1に記載の抗菌性製品。
- 前記窒素雰囲気下焼結銀含有表面層は、基材として層状窒素雰囲気下焼結銀を含み、抗菌部の表面に位置する層(層状窒素雰囲気下焼結銀含有表面層)であるか、または、基材としてプラスチックを含み、基材の表面に露出した粒子状窒素雰囲気下焼結銀、若しくは基材の表面に露出した粒子状窒素雰囲気下焼結銀と基材内に分散した粒子状窒素雰囲気下焼結銀とを含み、抗菌部の表面に位置する層(粒子状窒素雰囲気下焼結銀含有表面層)である、請求項1に記載の抗菌性製品。
- 前記層状窒素雰囲気下焼結銀含有表面層の下の抗菌部の一部若しくは全体が粗面であり、または粒子状窒素雰囲気下焼結銀含有表面層の一部若しくは全体が粗面である、請求項4に記載の抗菌性製品。
- 前記粗面がサンドブラスト加工によって形成された、請求項5に記載の抗菌性製品。
- 前記層状窒素雰囲気下焼結銀含有表面層の厚さが0.1μm乃至20μmであり、または前記粒子状窒素雰囲気下焼結銀含有表面層の厚さが10μm乃至20μmである、請求項4に記載の抗菌性製品。
- 前記粒子状窒素雰囲気下焼結銀含有表面層と前記抗菌部とが一体に形成された、請求項4に記載の抗菌性製品。
- 前記抗菌部と前記粒子状窒素雰囲気下焼結銀含有表面層が、粒子状窒素雰囲気下焼結銀をプラスチック100重量部に対して1乃至60重量部で含む、請求項8に記載の抗菌性製品。
- 前記粒子状窒素雰囲気下焼結銀の内部コアが鉱物系または岩石系粒子を含む、請求項4に記載の抗菌性製品。
- 前記鉱物系または岩石系粒子と前記窒素雰囲気下焼結銀との重量比が100:0.1乃至10である、請求項10に記載の抗菌性製品。
- 一つ以上の抗菌部を含む抗菌性製品の製造方法において、
水または極性有機溶媒に銀塩類化合物粉末を添加し、溶解させて銀塩類溶解液を製造する第1工程と、
前記銀塩類溶解液を前記抗菌部上に塗布する第2工程と、
前記抗菌部上に塗布された銀塩類化合物を窒素雰囲気下で焼結して、前記抗菌部上に層状窒素雰囲気下焼結銀含有表面層を形成する第3工程と、
を含み、
窒素雰囲気下焼結銀は、銀塩類化合物を、窒素雰囲気下で440〜1000℃で焼結した銀である、抗菌性製品の製造方法。 - 前記抗菌部の材料が金属、硝子、セラミック、石材、鉱物及びこれらの組み合わせから選択される材料を含む、請求項12に記載の抗菌性製品の製造方法。
- 前記第1工程で、前記水または極性有機溶媒100重量部に前記銀塩類化合物粉末1〜10重量部を添加する、請求項12に記載の抗菌性製品の製造方法。
- 前記銀塩類化合物が炭酸銀、塩素酸銀、塩化銀、クロム酸銀、バナジウム酸銀、マンガン酸銀、硝酸銀、亜硝酸銀、過塩素酸銀、リン酸銀、酢酸銀及びこれらの混合物から選択される、請求項12に記載の抗菌性製品の製造方法。
- 前記第3工程で、焼結温度が440℃以上である、請求項12に記載の抗菌性製品の製造方法。
- 前記第2工程の前に、前記抗菌部に粗面を形成し、前記第2工程で、前記銀塩類溶解液を前記粗面の上に塗布する、請求項12に記載の抗菌性製品の製造方法。
- 前記粗面をサンドブラスト加工で形成する、請求項17に記載の抗菌性製品の製造方法。
- 前記層状窒素雰囲気下焼結銀含有表面層を0.1μm〜20μmの厚さに形成する、請求項12に記載の抗菌性製品の製造方法。
- 前記第3工程の後に、前記抗菌部を含む抗菌性製品を製造する工程をさらに含む、請求項12に記載の抗菌性製品の製造方法。
- 一つ以上の抗菌部を含む抗菌性製品の製造方法において、
水または極性有機溶媒100重量部に銀塩類化合物粉末1〜10重量部を添加し、溶解させて銀塩類溶解液を製造する第1工程と、
前記銀塩類溶解液を抗菌部上に塗布する第2工程と、
前記抗菌部に塗布された銀塩類化合物を窒素雰囲気または大気下で焼結して、前記抗菌部上に層状窒素雰囲気下焼結銀含有表面層または層状酸化銀焼結体含有表面層を形成する第3工程と、
を含み、
窒素雰囲気下焼結銀は、銀塩類化合物を、窒素雰囲気下で440〜1000℃で焼結した銀である、抗菌性製品の製造方法。 - 一つ以上の抗菌部を含む抗菌性製品の製造方法において、
水または極性有機溶媒に鉱物系または岩石系粒子と銀塩類化合物粉末を添加し、混合した後、窒素雰囲気下で前記銀塩類化合物を焼結して、その内部コアに鉱物系または岩石系粒子を含む粒子状窒素雰囲気下焼結銀を製造する第1工程と、
プラスチック材料と前記粒子状窒素雰囲気下焼結銀とを混合し、加熱してペレットに製造する第2工程と、
前記ペレットを用いて前記抗菌部を成形する第3工程と、
前記抗菌部にサンドブラスト加工を行い、前記抗菌部の表面に前記粒子状窒素雰囲気下焼結銀を露出させる第4工程と、
を含み、
窒素雰囲気下焼結銀は、銀塩類化合物を、窒素雰囲気下で440〜1000℃で焼結した銀である、抗菌性製品の製造方法。 - 前記第1工程で、鉱物系または岩石系粒子と銀塩類化合物粉末との重量比が100:0.1〜10であり、前記鉱物系または岩石系粒子及び銀塩類化合物粉末の混合物と前記水または極性有機溶媒との重量比が1〜70:100である、請求項22に記載の抗菌性製品の製造方法。
- 前記銀塩類化合物が炭酸銀、塩素酸銀、塩化銀、クロム酸銀、バナジウム酸銀、マンガン酸銀、硝酸銀、亜硝酸銀、過塩素酸銀、リン酸銀、酢酸銀及びこれらの混合物から選択される、請求項22に記載の抗菌性製品の製造方法。
- 前記第1工程で、焼結温度が440℃以上である、請求項22に記載の抗菌性製品の製造方法。
- 前記第2工程で、前記プラスチック材料と前記粒子状窒素雰囲気下焼結銀との重量比が100:1〜60である、請求項22に記載の抗菌性製品の製造方法。
- 一つ以上の抗菌部を含む抗菌性製品の製造方法において、
水または極性有機溶媒に鉱物系または岩石系粒子と銀塩類化合物粉末を添加し、混合した後、窒素雰囲気または大気下で前記銀塩類化合物を焼結して、その内部コアに鉱物系または岩石系粒子を含む粒子状窒素雰囲気下焼結銀または粒子状酸化銀焼結体を製造する第1工程と、
プラスチック材料と前記粒子状窒素雰囲気下焼結銀または粒子状酸化銀焼結体とを混合し、加熱してペレットに製造する第2工程と、
前記ペレットを用いて前記抗菌部を成形する第3工程と、
前記抗菌部にサンドブラスト加工を行い、前記抗菌部の表面に前記粒子状窒素雰囲気下焼結銀または粒子状酸化銀焼結体を露出させる第4工程と、
を含み、
窒素雰囲気下焼結銀は、銀塩類化合物を、窒素雰囲気下で440〜1000℃で焼結した銀である、抗菌性製品の製造方法。 - 前記抗菌性製品は、抗菌性金属たわしである、
請求項1に記載の抗菌性製品。