JP6325692B2 - Combination diamond jewelry and method of manufacturing the same - Google Patents
Combination diamond jewelry and method of manufacturing the same Download PDFInfo
- Publication number
- JP6325692B2 JP6325692B2 JP2016569988A JP2016569988A JP6325692B2 JP 6325692 B2 JP6325692 B2 JP 6325692B2 JP 2016569988 A JP2016569988 A JP 2016569988A JP 2016569988 A JP2016569988 A JP 2016569988A JP 6325692 B2 JP6325692 B2 JP 6325692B2
- Authority
- JP
- Japan
- Prior art keywords
- diamond
- pedestal
- small
- fitting hole
- peripheral
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明はダイヤモンド装身具の製造技術の分野に関し、特に組合せ型ダイヤモンド装身具及びその製造方法に関する。 The present invention relates to the field of diamond jewelry manufacturing technology, and more particularly to a combination diamond jewelry and a method for manufacturing the same.
ダイヤモンド資源がだんだん無くなるのに伴って、大きなダイヤモンドの価格はますます高くなる。装身具の分野において、１カラット以上のダイヤモンドが嵌合された装身具の価格は、普通の消費者にとっては負担し難い。しかしながら、より小さなダイヤモンドは価格が高くないが、大きなダイヤモンドに対する消費者の好みを満たすことが困難である。 As diamond resources run out, the price of large diamonds will increase. In the field of jewelry, the price of a jewelry fitted with a diamond of 1 carat or more is difficult to bear for ordinary consumers. However, while smaller diamonds are not expensive, it is difficult to meet consumer preferences for large diamonds.
近年、普通の消費者がより低い価格で、大きなダイヤモンドの効果を有する装身具を身につけることを可能にするために、ダイヤモンド装身具の製造分野の技術者は、小さなダイヤモンドの組み合わせにより大きなダイヤモンドの効果を模擬する様々なダイヤモンド組合せ技術を開発した。 In recent years, to allow ordinary consumers to wear jewelry with large diamond effect at a lower price, engineers in the field of diamond jewelry have increased the effectiveness of large diamonds by combining small diamonds. We have developed various diamond combination techniques to simulate
例えば、中国特許番号ＣＮ２００７１００７６７３８．６では、「部品型嵌合の穴ダイヤモンド装身具」が開示された。該特許は下記の技術を採用した。「貴金属台座であって、その底面は錐形であり、上面にはダイヤモンドを置くための複数のダイヤモンド用穴部が設けられており、前記貴金属台座の周辺に沿った前記ダイヤモンド用穴部間には係止突出部が設けられており、前記係止突出部は半径方向に外側へ幅の広い三角形であり、前記貴金属台座の周辺のダイヤモンドは一緒に、前記貴金属台座の中央に位置するダイヤモンドを押圧し、且つ前記貴金属台座の周辺と周辺のダイヤモンドのエッジとは同一平面にあり、複数のダイヤモンドと前記貴金属台座とは、１個の大きなダイヤモンドに似ている全体的な外観を形成する」。 For example, in Chinese Patent No. CN200710076738.6, “part type fitting hole diamond jewelry” was disclosed. The patent employed the following technology. “A noble metal pedestal having a conical bottom surface and a plurality of diamond hole portions for placing diamonds on the upper surface, and between the diamond hole portions along the periphery of the noble metal pedestal. Is provided with a locking projection, the locking projection is a triangle that is wide outward in the radial direction, and the diamond around the noble metal pedestal together with the diamond located in the center of the noble metal pedestal. The periphery of the precious metal pedestal and the edge of the surrounding diamond are coplanar, and the plurality of diamonds and the precious metal pedestal form an overall appearance resembling a single large diamond.
他の例として、中国特許番号ＣＮ２０１２１００３４５００．８では、「６個が１個を囲む氷花ダイヤモンド」が開示された。該特許は下記のとおりである。「金属台座鋳造、仕上げ、電解・研磨、石留め、エッジ取り除き、手彫り、精密研摩、金属メッキ、品質検査の９つのステップにより構成される。金属台座の形状は小さな円錐台であり、上下層はいずれも内向きに傾斜する角度を有し、その角度設計はダイヤモンドのカット面角度と一致している。小さなダイヤモンドの嵌合は、三層の円形ダイヤモンドを積み重ねる石留め技術によって、金属台座の底層の金属の露出する全部位置をカバーする。さらに、台面の三角金属爪の位置に手彫りの効果を作り、露出する金属を減らすことで屈折度を増加し、台面全体の屈折により１個の大きなダイヤモンドの効果を作る」。 As another example, in Chinese Patent No. CN2012010034500.8, “6 ice diamonds surrounding one” was disclosed. The patent is as follows. “Metal pedestal casting, finishing, electrolysis / polishing, stone fixing, edge removal, hand-carving, precision polishing, metal plating, quality inspection. The shape of the metal pedestal is a small truncated cone, the upper and lower layers are Each has an inwardly inclined angle, and the angle design matches the cut face angle of the diamond.The small diamond fitting is achieved by a stone-clamping technique that stacks three layers of circular diamonds, In addition, it covers all the exposed positions of the metal, and also creates a hand-carved effect on the position of the triangular metal claw on the surface, increases the refraction by reducing the exposed metal, and refraction of the entire surface makes one large diamond Make an effect. "
上述した特許及び従来技術は、複数の小さなダイヤモンドの組み合わせにより１個の大きなダイヤモンドの効果を作ることを実現したが、従来技術には、まだ完全に解決されていない以下の技術問題が存在する。
まず、複数の小さなダイヤモンドをしっかりと嵌合し、小さなダイヤモンドの脱落を防止するために、主に金属での係止の方式により中央ダイヤモンドを固定し、その周りを複数の小さなダイヤモンドで囲む。しかしながら、このような構造の欠点は、中央ダイヤモンドと小さなダイヤモンドとの間には隙間があり、実際に身につける過程において、時間の経過とともに、ほこりや汚れが隙間に進入して掃除が難しくなり、さらにダイヤモンド装身具の全体的な効果に影響を与えることである。
Although the above-mentioned patents and the prior art have realized the effect of one large diamond by combining a plurality of small diamonds, there are the following technical problems that have not yet been completely solved in the prior art.
First, in order to fit a plurality of small diamonds firmly and prevent the small diamonds from falling off, the central diamond is fixed mainly by a metal locking method, and the periphery is surrounded by a plurality of small diamonds. However, the disadvantage of such a structure is that there is a gap between the central diamond and the small diamond, and in the process of wearing, over time, dust and dirt will enter the gap and become difficult to clean. And even affect the overall effect of diamond jewelry.
次に、従来技術の組み合わせ型ダイヤモンドは、本物のダイヤモンドのカット角度に基づいて、この組み合わせ型ダイヤモンドが含む小さなダイヤモンドのサイズ及び円錐形台座の角度を設計し、複数の小さなダイヤモンド及び金属を用いて、特定のサイズ割り当て比率及び形状設計により、これらをできるだけ互いに屈折させて全体的な輝かしい視覚効果を形成することをしていないため、形状および視覚の点でそれと本物の大きなダイヤモンドとの間に一定の差がある。 Next, prior art combination diamonds are designed based on the cut angle of real diamonds, designing the size of the small diamonds contained in this combination diamond and the angle of the conical pedestal, using multiple small diamonds and metals. Because of the specific size allocation ratio and shape design, they are not refracted as much as possible to form an overall brilliant visual effect, so there is a constant between shape and vision in terms of it and a real large diamond There is a difference.
本発明が解決しようとする問題は、ダイヤモンド間に隙間がないことにより、既存の組合せ型ダイヤモンド装身具のダイヤモンド間に隙間があり、ほこりや汚れが隙間に進入し、掃除がしにくいという問題を解決するとともに、複数の小さなダイヤモンド及び金属を用いて、特定のサイズ割り当て比率及び形状設計により、これらをできるだけ互いに屈折させて全体的な輝かしい視覚効果を形成する組合せ型ダイヤモンド装身具を提供することである。同時に、本発明は該組合せ型ダイヤモンド装身具の製造方法をさらに提供する。 The problem to be solved by the present invention is that there is no gap between diamonds, there is a gap between diamonds of existing combination diamond jewelry, dust and dirt enter the gap and difficult to clean In addition, it is to provide a combinatorial diamond jewelry that uses a plurality of small diamonds and metals and, with a specific size allocation ratio and shape design, refracts them as much as possible to form an overall brilliant visual effect. At the same time, the present invention further provides a method for manufacturing the combination diamond jewelry.
上述した技術的問題を解決するために、本発明は組合せ型ダイヤモンド装身具を提供する。この組合せ型ダイヤモンド装身具は、上面に彫刻が設けられた幾つかの金属爪が上表面の縁に配置された金属台座と、前記台座の上表面と金属爪の間に嵌合された幾つかの小さいサイズのダイヤモンドとを備え、
前記台座の上表面には、少なくとも１つの大嵌合穴、及び幾つかの中嵌合穴と小嵌合穴が設けられており、
前記小さいサイズのダイヤモンドは、少なくとも１個のメインダイヤモンド、及び幾つかの底部ダイヤモンドと周辺ダイヤモンドを含み、
前記幾つかの底部ダイヤモンドは、前記台座の上表面の隙間内の小嵌合穴に嵌合され、かつ前記周辺ダイヤモンドの下方に位置しており、
前記周辺ダイヤモンドは、隣接する前記底部ダイヤモンドの隣の中嵌合穴に嵌合され、かつ前記底部ダイヤモンドと互いに当接し固定されており、
前記メインダイヤモンドは、前記大嵌合穴に嵌合され、かつ隣接する幾つかの前記周辺ダイヤモンドと互いに押圧し固定されており、
前記メインダイヤモンド、周辺ダイヤモンド及び底部ダイヤモンドは、上、中、下の三層構造により密着して押圧し、前記台座の上表面に固定され、且つ前記金属爪とダイヤモンドの各カット面の傾斜角に一致する構造を形成する。
In order to solve the above technical problems, the present invention provides a combination diamond jewelry. This combination type diamond jewelry includes a metal pedestal in which several metal claws provided with engraving on the upper surface are arranged on the edge of the upper surface, and several metal claws fitted between the upper surface of the pedestal and the metal claws. With a small diamond,
The upper surface of the pedestal is provided with at least one large fitting hole, and some middle fitting holes and small fitting holes,
The small size diamond includes at least one main diamond, and several bottom and peripheral diamonds;
The several bottom diamonds are fitted in small fitting holes in the gaps on the upper surface of the pedestal and are located below the peripheral diamonds;
The peripheral diamond is fitted in a middle fitting hole adjacent to the adjacent bottom diamond, and is fixed in contact with the bottom diamond.
The main diamond is fitted into the large fitting hole, and is pressed against and fixed to some adjacent peripheral diamonds,
The main diamond, peripheral diamond, and bottom diamond are intimately pressed by an upper, middle, and lower three-layer structure, fixed to the upper surface of the pedestal, and at an inclination angle of each cut surface of the metal claw and diamond. Form a matching structure.
好ましくは、前記メインダイヤモンド、底部ダイヤモンド及び周辺ダイヤモンドは、パヴェ留め、チャネル留めまたは爪留めの方式のうちの１つ以上により前記台座の上表面に嵌合されている。 Preferably, the main diamond, bottom diamond and peripheral diamond are fitted to the upper surface of the pedestal by one or more of pave, channel or claw schemes.
好ましくは、前記台座の断面は円形であり、前記台座の上表面には、大嵌合穴と、中嵌合穴と、前記大嵌合穴の周りにおいて同じ円周に位置する小円柱体とが設けられており、前記底部ダイヤモンドは、パヴェ留めの方式により前記幾つかの小円柱体の間に固定されている。 Preferably, the cross section of the pedestal is circular, and on the upper surface of the pedestal, there are a large fitting hole, a middle fitting hole, and a small cylindrical body located on the same circumference around the large fitting hole. The bottom diamond is fixed between the small cylinders by a pave fastening method.
好ましくは、前記台座の断面はハート形であり、前記台座の上表面には、前記金属爪の高さに相当する２つの小円柱体がさらに設けられており、前記底部ダイヤモンドは、パヴェ留めとチャネル留めを組み合わせる方式により前記小嵌合穴に固定されている。 Preferably, the cross section of the pedestal has a heart shape, and on the upper surface of the pedestal, two small cylinders corresponding to the height of the metal claws are further provided, and the bottom diamond is formed by pave fastening. It is fixed to the small fitting hole by a method combining channel fastening.
好ましくは、前記台座の断面は楕円形、水滴形または八角形である。 Preferably, the cross section of the pedestal is oval, waterdrop or octagonal.
好ましくは、前記台座の上部の幅は６．５ｍｍであり、下部の幅は６．１ｍｍであり、側面と上表面との間の角度は３０°であり、側面と底面との間の角度は６０°である。 Preferably, the width of the upper portion of the pedestal is 6.5 mm, the width of the lower portion is 6.1 mm, the angle between the side surface and the upper surface is 30 °, and the angle between the side surface and the bottom surface is 60 °.
好ましくは、前記底部ダイヤモンドの直径は０．８０ｍｍから０．９０ｍｍの間であり、メインダイヤモンドの直径は２．３０ｍｍから２．４０ｍｍの間であり、周辺ダイヤモンドの直径は１．３５ｍｍから１．４５ｍｍの間である。 Preferably, the diameter of the bottom diamond is between 0.80 mm and 0.90 mm, the diameter of the main diamond is between 2.30 mm and 2.40 mm, and the diameter of the peripheral diamond is 1.35 mm to 1.45 mm. Between.
好ましくは、前記金属爪の上面の傾斜角はダイヤモンドのカット面の傾斜角に一致する角度を有する。 Preferably, the inclination angle of the upper surface of the metal claw has an angle that matches the inclination angle of the cut surface of the diamond.
本発明は組合せ型ダイヤモンド装身具の製造方法をさらに提供する。この製造方法は、（１）原型作成のステップと、（２）鋳造のステップと、（３）仕上げのステップと、（４）研磨のステップと、（５）石留めのステップと、（６）溶接のステップと、（７）研磨のステップと、（８）電気メッキのステップとを含む。
前記（５）石留めのステップは、
（１）前記台座の底層の隙間を埋めるように、前記底部ダイヤモンドを前記小嵌合穴に嵌合するステップと、
（２）前記周辺ダイヤモンドと隣接する前記底部ダイヤモンドとが互いに当接し互いに固定するように、前記周辺ダイヤモンドを、前記大嵌合穴と隣接する前記中嵌合穴に嵌合するステップと、
（３）前記メインダイヤモンドと隣接する前記周辺ダイヤモンドとが互いに押圧し堅固に固定するように、前記メインダイヤモンドを前記大嵌合穴に嵌合するステップと、
（４）前記メインダイヤモンドをさらに当接し押圧するように、残りの前記周辺ダイヤモンドを残りの前記中嵌合穴に嵌合するステップと、
（５）前記金属爪を前記台座の側面、前記メインダイヤモンド、及び前記周辺ダイヤモンドと一緒にダイヤモンドの各屈折面に形成するように、前記金属爪を９０°に彫刻処理するステップと、
（６）金属の光沢と反射度をさらに増強するように、前記台座及び金属爪に対して電気メッキまたはロジウムメッキ処理を行うステップとをさらに含む。
前記（８）電気メッキのステップは、ロジウムメッキ液の調製ステップと、電気メッキのステップと、洗浄のステップとをさらに含み、
ロジウムメッキ液の調製ステップにおいて、
計量コップを用いて、３０ｍｌのロジウム溶液を取ってロジウムメッキ槽に入れ、均一に撹拌し、ロジウム溶液の添加後に、ロジウム溶液が均一になるように、超音波を使って約３０秒間振動させ、ロジウム溶液専用の超音波洗浄機の電源スイッチをオンし、振動完了後に、超音波洗浄機の電源スイッチをオフし、
電気メッキのステップにおいて、
ａ． メッキ液槽を入れた後、水タンクの水位が超音波清洗浄機の縁より１．５〜２．５ｃｍ低くなるように、超音波洗浄タンク内に水を入れ、
ｂ． 超音波洗浄機の電源をオンし、温度設定ノブを４５℃に回転して、超音波洗浄機の過熱を開始し、
ｃ． 温度計の指示温度が４５±３℃となると、電気メッキを行い、電気メッキの電圧は３Ｖ〜５Ｖであり、電気メッキは時間が２５ｓ〜３０ｓであり、
洗浄のステップにおいて、
電気メッキが完了した後、製品を液面から取り出し、電極クランプをリリースし製品を取得し、清水により洗浄する。
The present invention further provides a method of manufacturing a combination diamond jewelry. The manufacturing method includes (1) a step of making a prototype, (2) a casting step, (3) a finishing step, (4) a polishing step, (5) a stone fixing step, and (6) A welding step, (7) a polishing step, and (8) an electroplating step.
The step (5)
(1) fitting the bottom diamond into the small fitting hole so as to fill a gap in the bottom layer of the pedestal;
(2) fitting the peripheral diamond into the middle fitting hole adjacent to the large fitting hole so that the peripheral diamond and the adjacent bottom diamond are in contact with each other and fixed to each other;
(3) fitting the main diamond into the large fitting hole so that the main diamond and the neighboring diamond adjacent to each other are pressed against each other and firmly fixed;
(4) a step of fitting the remaining peripheral diamond into the remaining middle fitting hole so as to further abut and press the main diamond;
(5) engraving the metal claws at 90 ° so that the metal claws are formed on each refracting surface of the diamond together with the side surface of the pedestal, the main diamond, and the peripheral diamond;
(6) The method further includes the step of performing electroplating or rhodium plating on the pedestal and the metal claws so as to further enhance the gloss and reflectivity of the metal.
(8) The electroplating step further includes a rhodium plating solution preparation step, an electroplating step, and a cleaning step.
In the rhodium plating solution preparation step,
Using a measuring cup, take 30 ml of rhodium solution into a rhodium plating tank, stir uniformly, and after addition of the rhodium solution, vibrate using ultrasonic waves for about 30 seconds so that the rhodium solution is uniform, Turn on the power switch of the ultrasonic cleaner dedicated to the rhodium solution, and after the vibration is completed, turn off the power switch of the ultrasonic cleaner.
In the electroplating step,
a. After putting the plating solution tank, put water in the ultrasonic cleaning tank so that the water level of the water tank is 1.5 to 2.5 cm lower than the edge of the ultrasonic cleaning machine,
b. Turn on the power of the ultrasonic cleaner, rotate the temperature setting knob to 45 ° C and start overheating the ultrasonic cleaner,
c. When the temperature indicated by the thermometer is 45 ± 3 ° C., electroplating is performed, the electroplating voltage is 3 V to 5 V, and the electroplating time is 25 s to 30 s.
In the washing step,
After the electroplating is completed, the product is removed from the liquid surface, the electrode clamp is released, the product is obtained, and washed with fresh water.
ここで、前記小嵌合穴は小円柱体であり、前記底部ダイヤモンドをパヴェ留めの方式により前記小円柱体間に嵌合する。 Here, the small fitting hole is a small cylindrical body, and the bottom diamond is fitted between the small cylindrical bodies by a pave fastening method.
本発明の組合せ型ダイヤモンド装身具は、メインダイヤモンド、周辺ダイヤモンド及び底部ダイヤモンドを用いて、上、中、下の三層構造により互いに密着させ押圧し、前記台座の上表面に固定し、且つ金属爪とダイヤモンドの各カット面の傾斜角に一致する構造を形成するため、該組合せ型ダイヤモンド装身具のダイヤモンド間に隙間がないことにより、既存の組合せ型ダイヤモンド装身具のダイヤモンド間に隙間があり、ほこりや汚れが隙間に進入し、掃除しにくいという問題を解決するとともに、複数の小さなダイヤモンド及び金属を用いて、特定のサイズ割り当て比率及び形状設計により、これらをできるだけ互いに屈折させて全体的な輝かしい視覚効果を形成する。 The combined diamond jewelry of the present invention uses a main diamond, a peripheral diamond, and a bottom diamond, and is brought into close contact with each other by an upper, middle, and lower three-layer structure, fixed to the upper surface of the pedestal, and a metal claw In order to form a structure that matches the inclination angle of each cut surface of diamond, there is no gap between diamonds of the combination diamond jewelry, so there is a gap between diamonds of existing combination diamond jewelry, and dust and dirt are Solves the problem of entering gaps and is difficult to clean, and uses multiple small diamonds and metals to refract each other as much as possible with a specific size allocation ratio and shape design to create an overall brilliant visual effect To do.
以下、添付図面を参照しながら、本発明の好適な実施形態を詳細に説明する。これらの実施例は本発明を例示するものに過ぎず、本発明の範囲を限定するものではないことを理解すべきである。また、本発明の教示内容を読んだ後、当業者は本発明に対して様々な変更又は修正を行えば、これらの等価物は本願の特許請求の範囲内に収まることを理解すべきである。 Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. It should be understood that these examples are merely illustrative of the invention and do not limit the scope of the invention. In addition, after reading the teachings of the present invention, those skilled in the art should understand that various changes or modifications can be made to the present invention and their equivalents fall within the scope of the claims. .
〈実施例１〉
図１、２及び３に示されるように、本発明の組合せ型ダイヤモンド装身具は貴金属台座１を備える。この貴金属台座１の断面は円形であり、その側面は大きいサイズのダイヤモンドの側面構造に基づいて加工されて、本発明の大きいサイズの本物のダイヤモンドの形状に対する模擬性が向上する。
<Example 1>
As shown in FIGS. 1, 2, and 3, the combination diamond jewelry of the present invention includes a noble metal pedestal 1. The cross section of the noble metal pedestal 1 is circular, and its side surface is processed based on the side surface structure of a large size diamond, thereby improving the simulation of the shape of a real diamond of a large size of the present invention.
上述した台座１の中心位置には１つの大嵌合穴７が設けられる。該大嵌合穴７の周りに、同じ円周に沿って、６つの中嵌合穴６１が均一に配置され、即ち該６つの中嵌合穴６１の円心は同じ円周に位置する。上述した大嵌合穴７の周りにおいて同じ円周には１２個の小円柱体５が均一に配置される。該小円柱体５は、２つずつを１組として、６組の小円柱体５を形成する。上述した６つの中嵌合穴６１のそれぞれ２つ間に、特定の屈折角度を有する６つの金属爪８が設けられる。該金属爪８は彫刻により造形され、彫刻の角度は９０°とすることが好ましい。 One large fitting hole 7 is provided at the center position of the base 1 described above. Six middle fitting holes 61 are uniformly arranged around the large fitting hole 7 along the same circumference, that is, the centers of the six middle fitting holes 61 are located on the same circumference. Around the large fitting hole 7 described above, twelve small cylindrical bodies 5 are uniformly arranged on the same circumference. The small cylinders 5 form six sets of small cylinders 5 with two as one set. Six metal claws 8 having a specific refraction angle are provided between two of the six middle fitting holes 61 described above. The metal claws 8 are formed by engraving, and the engraving angle is preferably 90 °.
本実施例において、組合せ型ダイヤモンド装身具の嵌合工程は下記のとおりである。
１．６個の小さいサイズの底部ダイヤモンド２を６組の小円柱体５の間の隙間に嵌合し、その後、小円柱体５において小さな爪を作り、パヴェ留めの方式によりこれらの６個の小さいサイズの底部ダイヤモンド２を固定する。上述した６個の小さいサイズの底部ダイヤモンド２は、台座１の底層の余分な金属部分を埋める。
In this example, the fitting process of the combination diamond jewelry is as follows.
1.6 small sized bottom diamonds 2 are fitted into the gaps between the 6 small cylinders 5, then small nails are made in the small cylinders 5, and these 6 A small sized bottom diamond 2 is fixed. The six small sized bottom diamonds 2 mentioned above fill the extra metal part of the bottom layer of the pedestal 1.
２．対角線に位置する任意２個の小さいサイズの周辺ダイヤモンド３を、チャネル留めの方式により、２つの金属爪８の間の中嵌合穴６１に嵌合する。同時に、該周辺ダイヤモンド３と隣接する２個の底部ダイヤモンド２とは互いに当接し、互いに固定される。 2. Arbitrary two small-sized peripheral diamonds 3 located in a diagonal line are fitted into the middle fitting holes 61 between the two metal claws 8 by a channel fastening method. At the same time, the peripheral diamond 3 and the two adjacent bottom diamonds 2 come into contact with each other and are fixed to each other.
３．１個の小さいサイズのメインダイヤモンド４を大嵌合穴７により中央に嵌合する。同時に、該メインダイヤモンド４と対角線における２個の小さいサイズの周辺ダイヤモンド３とは互いに押圧して堅固に固定される。台座１の中心大嵌合穴７に嵌合されたメインダイヤモンド４はその下層の６個の小さいサイズの底部ダイヤモンド２とちょうど密着し、上層のメインダイヤモンド４と下層底部ダイヤモンド２の間に隙間が形成されないため、ほこりや汚れが装身具の内部に進入する問題は解決される。 3. One small size main diamond 4 is fitted in the center by the large fitting hole 7. At the same time, the main diamond 4 and two small peripheral diamonds 3 on the diagonal are pressed against each other and firmly fixed. The main diamond 4 fitted in the center large fitting hole 7 of the pedestal 1 is in intimate contact with the six lower sized bottom diamonds 2 in the lower layer, and a gap is formed between the upper main diamond 4 and the lower layer bottom diamond 2. Since it is not formed, the problem of dust and dirt entering the interior of the jewelry is solved.
４．残りの４個の小さいサイズの周辺ダイヤモンド３を金属爪８により、爪留めとチャネル留めの組み合わせで、それ自体が安定するとともに、中央のメインダイヤモンド４を押圧する。組合せダイヤモンドが隙間を形成することによるほこりや汚れの進入問題はさらに解決される。 4). The remaining four small-sized peripheral diamonds 3 are stabilized by metal claws 8 by a combination of claws and channel clamps, and the central main diamond 4 is pressed. The problem of dust and dirt entry due to the combination diamond forming gaps is further solved.
５．６つの金属爪８に対して特定の角度の彫刻９の効果を作る。金属爪８と台座１の側面の嵌合と台座１上のダイヤモンドとは全体として、一体的に削って仕上げられたダイヤモンドの屈折角度を模倣して、組み合わせダイヤモンドの見た目をさらに向上させる。 5. Create the effect of engraving 9 at a specific angle on the six metal claws 8. The fitting of the side surfaces of the metal claws 8 and the pedestal 1 and the diamond on the pedestal 1 as a whole imitate the refraction angle of the diamond that is integrally cut and finished, and further improve the appearance of the combined diamond.
６．電気メッキまたはロジウムメッキの方式により、装身具の金属部分を電気メッキする。金属の光沢を増強して、装身具全体の輝きと光沢を向上させる。 6). The metal part of the jewelry is electroplated by electroplating or rhodium plating. Increases the gloss of metal and improves the overall shine and luster of jewelry.
〈実施例２〉
図４、５及び６に示されるように、本発明の組合せ型ダイヤモンド装身具は貴金属台座１を備える。この貴金属台座１の断面はハート形であり、その側面は大きいサイズのダイヤモンドの側面構造に基づいて加工されて、本発明の大きいサイズの本物のダイヤモンドの形状に対する模擬性が向上する。
<Example 2>
As shown in FIGS. 4, 5 and 6, the combination diamond jewelry of the present invention includes a noble metal pedestal 1. The cross section of the noble metal pedestal 1 has a heart shape, and its side surface is processed based on the side surface structure of a large size diamond, thereby improving the simulation of the shape of a real diamond of a large size of the present invention.
上述した台座１の周りに間隔をあけて１２個の金属爪８が設けられている。ここで、ハート形の先端部に位置する２つの金属爪８は一体化され、残りの金属爪８は均一に同一の角度で分布し配置されている。各２つの上述した金属爪８の間にはいずれも中嵌合穴６１が設けられている。台座１の対称線の２分の１及び４分の１の位置にそれぞれ小円柱体５が設けられ、該小円柱体５の高さは金属爪８に相当し、その最先端には彫刻が設けられている。好ましくは、該彫刻は８等分されたものであり、彫刻角度は９０°である。台座１の対称線の２分の１の位置の小円柱体５の周りに、均一に同一の角度で、三角形状分布の３つの大嵌合穴７が設けられている。上述した台座１のハート形の凹部において、小円柱体５を対称軸として２つの小嵌合穴６が設けられている。ハート形の先端部に近接する上述した大嵌合穴７の両側において、小円柱体５を対称軸として２つの小嵌合穴６が設けられている。上述した４つの小嵌合穴６の接続線は等辺台形を構成し、４つの小嵌合穴６はそれぞれ等辺台形の４つのコーナーに位置する。 Twelve metal claws 8 are provided around the pedestal 1 described above at intervals. Here, the two metal claws 8 located at the tip of the heart shape are integrated, and the remaining metal claws 8 are uniformly distributed and arranged at the same angle. An intermediate fitting hole 61 is provided between each of the two metal claws 8 described above. Small cylinders 5 are provided at positions one-half and one-fourth of the symmetry line of the pedestal 1, and the height of the small cylinders 5 corresponds to the metal claws 8. Is provided. Preferably, the engraving is divided into eight equal parts and the engraving angle is 90 °. Three large fitting holes 7 having a triangular distribution are provided around the small cylindrical body 5 at a position half the symmetry line of the base 1 at the same angle. In the heart-shaped recess of the pedestal 1 described above, two small fitting holes 6 are provided with the small cylindrical body 5 as the axis of symmetry. Two small fitting holes 6 are provided on both sides of the above-described large fitting hole 7 close to the heart-shaped tip, with the small cylindrical body 5 as the axis of symmetry. The connection lines of the four small fitting holes 6 described above form an isosceles trapezoid, and the four small fitting holes 6 are located at four corners of the equilateral trapezoid, respectively.
本実施例において、組合せ型ダイヤモンド装身具の嵌合工程は下記のとおりである。
１．４個の小さいサイズの底部ダイヤモンド２を４つの小嵌合穴６の隙間に嵌合する。ここで、小円柱体５に近接する２個の底部ダイヤモンド２について、小円柱体５において小さな爪を作り、パヴェ留めの方式によりこれらの２個の小さいサイズの底部ダイヤモンド２を固定する。上述した４個の小さいサイズの底部ダイヤモンド２は、台座１の底層の余分な金属部分を埋める。
In this example, the fitting process of the combination diamond jewelry is as follows.
1.4 small-sized bottom diamonds 2 are fitted into the gaps of the four small fitting holes 6. Here, with respect to the two bottom diamonds 2 adjacent to the small cylindrical body 5, small nails are formed in the small cylindrical body 5, and these two small-sized bottom diamonds 2 are fixed by a pave fastening method. The four small sized bottom diamonds 2 mentioned above fill the extra metal part of the bottom layer of the pedestal 1.
２．上述した底部ダイヤモンド２と隣接する中嵌合穴６１内において、チャネル留め及び爪留めの方式により、６個の小さいサイズの周辺ダイヤモンド３を、６つの金属爪８の間に嵌合する。同時に、該周辺ダイヤモンド３と隣接する２個の底部ダイヤモンド２とは互いに当接し、互いに固定される。 2. In the middle fitting hole 61 adjacent to the bottom diamond 2 described above, six peripheral diamonds 3 having a small size are fitted between the six metal claws 8 by a channel fastening method and a claw fastening method. At the same time, the peripheral diamond 3 and the two adjacent bottom diamonds 2 come into contact with each other and are fixed to each other.
３．３個の小さいサイズのメインダイヤモンド４を大嵌合穴７により中央に嵌合する。同時に、該メインダイヤモンド４と周りの小さいサイズの周辺ダイヤモンド３とは互いに押圧して堅固に固定される。台座１の中心大嵌合穴７に嵌合されたメインダイヤモンド４はその下層の２個の小さいサイズの底部ダイヤモンド２とちょうど密着し、上層のメインダイヤモンド４と下層底部ダイヤモンド２の間に隙間が形成されないため、ほこりや汚れが装身具の内部に進入する問題は解決される。 3. Three small sized main diamonds 4 are fitted in the center by the large fitting holes 7. At the same time, the main diamond 4 and the surrounding small-sized peripheral diamond 3 are pressed against each other and firmly fixed. The main diamond 4 fitted in the center large fitting hole 7 of the pedestal 1 is in intimate contact with the two lower-sized bottom diamonds 2 in the lower layer, and there is a gap between the upper main diamond 4 and the lower layer bottom diamond 2. Since it is not formed, the problem of dust and dirt entering the interior of the jewelry is solved.
４．残りの４個の小さいサイズの周辺ダイヤモンド３を金属爪８により、爪留めとチャネル留めの組み合わせで、それ自体が安定するとともに、中央のメインダイヤモンド４を押圧する。組合せダイヤモンドが隙間を形成することによるほこりや汚れの進入問題はさらに解決される。 4). The remaining four small-sized peripheral diamonds 3 are stabilized by metal claws 8 by a combination of claws and channel clamps, and the central main diamond 4 is pressed. The problem of dust and dirt entry due to the combination diamond forming gaps is further solved.
５．１２個の金属爪８に対して特定の角度の彫刻９の効果を作る。金属爪８と台座１の側面の嵌合と台座１上のダイヤモンドとは全体として、一体的に削って仕上げられたダイヤモンドの屈折角度を模倣して、組み合わせダイヤモンドの見た目をさらに向上させる。 5. Create the effect of engraving 9 at a specific angle on 12 metal claws 8. The fitting of the side surfaces of the metal claws 8 and the pedestal 1 and the diamond on the pedestal 1 as a whole imitate the refraction angle of the diamond that is integrally cut and finished, and further improve the appearance of the combined diamond.
６．電気メッキまたはロジウムメッキの方式により、装身具の金属部分を電気メッキする。金属の光沢を増強して、装身具全体の輝きと光沢を向上させる。 6). The metal part of the jewelry is electroplated by electroplating or rhodium plating. Increases the gloss of metal and improves the overall shine and luster of jewelry.
上記実施例に加えて、上述した台座１の断面は水滴形、楕円形、洋ナシ形、五角星形などであってもよい。
本発明の上記実施例１〜４において、好適な技術パラメータは下記のとおりである。
小さいサイズの底部ダイヤモンド２は０．８５ｍｍであり、その変動範囲は±０．０５ｍｍである。
小さいサイズのメインダイヤモンド４は２．３５ｍｍであり、その変動範囲は±０．０５ｍｍである。
小さいサイズの周辺ダイヤモンド３は１．４ｍｍであり、その変動範囲は±０．０５ｍｍである。
In addition to the embodiments described above, the cross section of the pedestal 1 described above may be a water drop shape, an oval shape, a pear shape, a pentagonal star shape, or the like.
In the said Examples 1-4 of this invention, a suitable technical parameter is as follows.
The small size bottom diamond 2 is 0.85 mm, and its variation range is ± 0.05 mm.
The small size main diamond 4 is 2.35 mm, and its variation range is ± 0.05 mm.
The small size peripheral diamond 3 is 1.4 mm, and its variation range is ± 0.05 mm.
台座１の上部の幅は６．５ｍｍであり、下部の幅は６．１ｍｍであり、台座１の側面と上表面との間の角度は３０°であり、側面と底面との間の角度は６０°である。これによって、本物のダイヤモンドの側面と同じ傾斜角が形成される。金属爪の上面の最高点から台座１の底面までの高さは３ｍｍであり、金属爪の上面の最低点から台座１の底面までの高さは２．４ｍｍである。本物のダイヤモンドと同じ傾斜角が形成される。金属爪の上面の彫刻角度は９０°であることによって、光線の屈折により本物のダイヤモンドと同じ反射効果を得る。 The upper width of the pedestal 1 is 6.5 mm, the lower width is 6.1 mm, the angle between the side surface and the upper surface of the pedestal 1 is 30 °, and the angle between the side surface and the bottom surface is 60 °. This creates the same tilt angle as the side of a real diamond. The height from the highest point on the top surface of the metal claw to the bottom surface of the pedestal 1 is 3 mm, and the height from the lowest point on the top surface of the metal claw to the bottom surface of the pedestal 1 is 2.4 mm. The same tilt angle as real diamond is formed. Since the engraving angle of the upper surface of the metal nail is 90 °, the same reflection effect as that of real diamond is obtained by refraction of light rays.
本発明の組合せ型ダイヤモンド装身具は、上述した実施例１〜４の装身具の製造方法のプロセスステップは下記のとおりである。
（１）原型作成
装身具スタイルに対応する金属部材の原型を銀で作成し、ワックス製品を作成して鋳型を作り、ダイヤモンドの嵌合スタイルに応じて、対応する金属台座を作る。嵌合されるダイヤモンドのサイズに基づいて、金属台座のダイヤモンドの配置用空間位置が決まる。
In the combined diamond jewelry of the present invention, the process steps of the jewelry manufacturing method of Examples 1 to 4 described above are as follows.
(1) Prototype creation Create a metal member prototype corresponding to the jewelry style with silver, create a wax product to make a mold, and make a corresponding metal pedestal according to the diamond fitting style. Based on the size of the diamond to be fitted, the space position for placing the diamond on the metal pedestal is determined.
（２）鋳造
鋳型内に黄金／白金溶液を注入し、冷却後に離型する。これによって、ワックス製品によって金属装身具を作成する。
(2) A golden / platinum solution is poured into a casting mold, and is released after cooling. As a result, a metal accessory is created from the wax product.
（３）仕上げ
金属装身具を仕上げて、ラインが美しく、角度がすっきりとする無傷の半製品を得る。
(3) Finishing Finish metal accessories and get an intact semi-finished product with beautiful lines and clean angles.
（４）研磨
仕上げが完了した金属台座に対して、表面研磨処理を行って、装身具の金属光沢を有する外観を造る。
(4) A surface polishing process is performed on the metal pedestal that has been polished to create an appearance having a metallic luster of the accessory.
（５）石留め
金属台座上の予め決められた位置にダイヤモンドを置く。ダイヤモンドの嵌合スタイルに基づいて、ダイヤモンドの上方に金属ワイヤーを設け、若しくはダイヤモンドの斜めの方向に金属ブロックを設ける。ダイヤモンドのセッティング面の上方に設けられた金属ワイヤーとダイヤモンドのテーブル面との間には隙間を残し、金属台座とダイヤモンドのセッティング面との間及びダイヤモンドと金属台座の凹溝との間には隙間を残す。
(5) A diamond is placed at a predetermined position on the stone metal base. Based on the diamond fitting style, a metal wire is provided above the diamond, or a metal block is provided in an oblique direction of the diamond. Leave a gap between the metal wire provided above the diamond setting surface and the diamond table surface, and a gap between the metal pedestal and the diamond setting surface and between the diamond and the groove in the metal pedestal. Leave.
（６）溶接
ダイヤモンド上方の金属ワイヤーまたはダイヤモンド下方の金属ブロックを金属台座に堅固に溶接する。
(6) The metal wire above the weld diamond or the metal block below the diamond is firmly welded to the metal base.
（７）研磨
溶接が完了した後、金属台座全体の表面に対して研磨処理を行う。
(7) After polishing welding is completed, a polishing process is performed on the entire surface of the metal base.
（８）電気メッキ
嵌合されたダイヤモンド装身具に対して電気メッキ処理を行う。上述した電気メッキ処理のステップは下記のとおりである。
I．ロジウムメッキ液の調製ステップ
計量コップを用いて、３０ｍｌのロジウム溶液を取ってロジウムメッキ槽に入れ、均一に撹拌する。ロジウム溶液の添加後に、ロジウム溶液が均一になるように、超音波を使って約３０秒間振動する必要があり、ロジウム溶液専用の超音波洗浄機の電源スイッチをオンし、振動完了後に、超音波洗浄機の電源スイッチをオフする。
(8) Electroplating is performed on the diamond jewelry fitted with electroplating. The steps of the electroplating process described above are as follows.
I. Step of preparing rhodium plating solution Using a measuring cup, take 30 ml of the rhodium solution and put it in the rhodium plating tank, and stir it uniformly. After addition of the rhodium solution, it is necessary to vibrate using ultrasonic waves for about 30 seconds so that the rhodium solution becomes uniform. The power switch of the ultrasonic cleaning machine dedicated to the rhodium solution is turned on. Turn off the machine power switch.
II．電気メッキのステップ
ａ．メッキ液槽を入れた後、水タンクの水位が超音波清洗浄機の縁より１．５〜２．５ｃｍ低くなるように、超音波洗浄タンク内に水を入れる。
ｂ．超音波洗浄機の電源をオンし、温度設定ノブを４５℃に回転して、超音波洗浄機の過熱を開始する。
ｃ． 温度計の指示温度が４５±３℃となると、電気メッキを行い、電気メッキの電圧は３Ｖ〜５Ｖであり、電気メッキの時間は２５ｓ〜３０ｓである。
II. Electroplating steps a. After putting the plating bath, water is put into the ultrasonic cleaning tank so that the water level of the water tank is 1.5 to 2.5 cm lower than the edge of the ultrasonic cleaning machine.
b. Turn on the power of the ultrasonic cleaner and rotate the temperature setting knob to 45 ° C. to start overheating the ultrasonic cleaner.
c. When the temperature indicated by the thermometer reaches 45 ± 3 ° C., electroplating is performed, the electroplating voltage is 3 V to 5 V, and the electroplating time is 25 s to 30 s.
III．洗浄のステップにおいて、
電気メッキが完了した後、製品を液面から取り出し、電極クランプをリリースして製品を取得し、清水により洗浄する。
III. In the washing step,
After the electroplating is completed, the product is taken out from the liquid surface, the electrode clamp is released, the product is obtained, and washed with fresh water.
最後に、以上は本発明の好適な実施例に過ぎず、本発明の技術案を限定するものでなく、本発明の技術特徴に対して行った同等の置き換えまたは相応の改良は、いずれも本発明の保護範囲内に含まれることを理解すべきである。 Finally, the above is only a preferred embodiment of the present invention, and does not limit the technical solution of the present invention. Any equivalent replacement or corresponding improvement made to the technical features of the present invention will It should be understood that it falls within the protection scope of the invention.
１、 台座
２、 底部ダイヤモンド
３、 周辺ダイヤモンド
４ 、メインダイヤモンド
５、 小円柱体
６、 小嵌合穴
６１、 中嵌合穴
７ 、大嵌合穴
８、 金属爪
９、 彫刻
1, pedestal 2, bottom diamond 3, peripheral diamond 4, main diamond 5, small cylinder 6, small fitting hole 61, medium fitting hole 7, large fitting hole 8, metal claw 9, sculpture
Claims (9)
前記台座の上表面には、少なくとも１つの大嵌合穴、及び幾つかの中嵌合穴と小嵌合穴が設けられており、
前記小さいサイズのダイヤモンドは、少なくとも１個のメインダイヤモンド、及び幾つかの底部ダイヤモンドと周辺ダイヤモンドを含み、
前記幾つかの底部ダイヤモンドは、前記台座の上表面の隙間内の小嵌合穴に嵌合され、かつ前記周辺ダイヤモンドの下方に位置しており、
前記周辺ダイヤモンドは、隣接する前記底部ダイヤモンドの隣の中嵌合穴に嵌合され、かつ前記底部ダイヤモンドと互いに当接し固定されており、
前記メインダイヤモンドは、前記大嵌合穴に嵌合され、かつ隣接する幾つかの前記周辺ダイヤモンドと互いに押圧し固定されており、
前記メインダイヤモンド、周辺ダイヤモンド及び底部ダイヤモンドは、上、中、下の三層構造により密着して押圧し、前記台座の上表面に固定され、且つ前記金属爪の上面の傾斜角は、前記メインダイヤモンド又は前記周辺ダイヤモンドのカット面の上表面の傾斜角に一致する角度を有する構造を形成する、組合せ型ダイヤモンド装身具。 A combination-type diamond jewelery, the metal pedestal some metal nail sculpture on the upper surface is provided is located on the edge of the upper surface, it mated number between surface and the metal claw on the pedestal With a small diamond,
The upper surface of the pedestal is provided with at least one large fitting hole, and some middle fitting holes and small fitting holes,
The small size diamond includes at least one main diamond, and several bottom and peripheral diamonds;
The several bottom diamonds are fitted in small fitting holes in the gaps on the upper surface of the pedestal and are located below the peripheral diamonds;
The peripheral diamond is fitted in a middle fitting hole adjacent to the adjacent bottom diamond, and is fixed in contact with the bottom diamond.
The main diamond is fitted into the large fitting hole, and is pressed against and fixed to some adjacent peripheral diamonds,
The main diamond, the peripheral diamond and the bottom diamond are intimately pressed by an upper, middle, and lower three-layer structure, fixed to the upper surface of the pedestal, and the inclination angle of the upper surface of the metal claw is the main diamond. Alternatively , a combined diamond accessory that forms a structure having an angle that matches the inclination angle of the upper surface of the cut surface of the peripheral diamond .
前記（５）石留めのステップは、
a．前記台座の底層の隙間を埋めるように、前記底部ダイヤモンドを前記小嵌合穴に嵌合するステップと、
b．前記周辺ダイヤモンドと隣接する前記底部ダイヤモンドとが互いに当接し互いに固定するように、前記周辺ダイヤモンドを、前記大嵌合穴と隣接する前記中嵌合穴に嵌合するステップと、
c．前記メインダイヤモンドと隣接する前記周辺ダイヤモンドとが互いに押圧し堅固に固定するように、前記メインダイヤモンドを前記大嵌合穴に嵌合するステップと、
d．前記メインダイヤモンドをさらに当接し押圧するように、残りの前記周辺ダイヤモンドを残りの前記中嵌合穴に嵌合するステップとをさらに含み、
前記（８）電気メッキのステップは、ロジウムメッキ液の調製ステップと、電気メッキのステップと、洗浄のステップとをさらに含み、
ロジウムメッキ液の調製ステップにおいて、
計量コップを用いて、３０ｍｌのロジウム溶液を取ってロジウムメッキ槽に入れ、均一に撹拌し、ロジウム溶液の添加後に、ロジウム溶液が均一になるように、超音波を使って約３０秒間振動させ、ロジウム溶液専用の超音波洗浄機の電源スイッチをオンし、振動完了後に、超音波洗浄機の電源スイッチをオフし、
電気メッキのステップにおいて、
ａ．メッキ液槽を入れた後、水タンクの水位が超音波洗浄機の縁より１．５〜２．５ｃｍ低くなるように、超音波洗浄タンク内に水を入れ、
ｂ．超音波洗浄機の電源をオンし、温度設定ノブを４５℃に回転して、超音波洗浄機の過熱を開始して、
ｃ．温度計の指示温度が４５±３℃となると、電気メッキを行い、電気メッキの電圧は３Ｖ〜５Ｖであり、電気メッキの時間は２５ｓ〜３０ｓであり、
洗浄のステップにおいて、
電気メッキが完了した後、製品を液面から取り出し、電極クランプをリリースし製品を取得し、清水により洗浄する、組合せ型ダイヤモンド装身具の製造方法。 It is a manufacturing method of the combination type diamond jewelry of Claim 1, Comprising: (1) Prototype creation step, (2) Casting step, (3) Finishing step, (4) Polishing step, (5) a stone fixing step, (6) a welding step, (7) a polishing step, and (8) an electroplating step,
The step (5)
a. Fitting the bottom diamond into the small fitting hole so as to fill a gap in the bottom layer of the pedestal;
b. Fitting the peripheral diamond into the middle fitting hole adjacent to the large fitting hole so that the peripheral diamond and the adjacent bottom diamond abut each other and are fixed to each other;
c. Fitting the main diamond into the large fitting hole such that the main diamond and the adjacent diamond adjacent to each other are pressed against each other and firmly fixed;
d. It said to press further abuts the main diamond, further comprising the step of fitting the remainder of the peripheral diamond remaining in said fitting Goana,
(8) The electroplating step further includes a rhodium plating solution preparation step, an electroplating step, and a cleaning step.
In the rhodium plating solution preparation step,
Using a measuring cup, take 30 ml of rhodium solution into a rhodium plating tank, stir uniformly, and after addition of the rhodium solution, vibrate using ultrasonic waves for about 30 seconds so that the rhodium solution is uniform, Turn on the power switch of the ultrasonic cleaner dedicated to the rhodium solution, and after the vibration is completed, turn off the power switch of the ultrasonic cleaner.
In the electroplating step,
a. After placing the plating tank, as the water level in the water tank is lower 1.5~2.5cm of the edge of the ultrasonic cleaning machine, put water in an ultrasonic cleaning tank,
b. Turn on the power of the ultrasonic cleaner, rotate the temperature setting knob to 45 ° C, start overheating the ultrasonic cleaner,
c. When the temperature indicated by the thermometer is 45 ± 3 ° C., electroplating is performed, the electroplating voltage is 3V to 5V, and the electroplating time is 25s to 30s.
In the washing step,
After electroplating is completed, the product is removed from the liquid surface, the electrode clamp is released, the product is obtained, and washed with fresh water.