JP6190153B2 - Solid makeup cosmetics - Google Patents
Solid makeup cosmetics Download PDFInfo
- Publication number
- JP6190153B2 JP6190153B2 JP2013099713A JP2013099713A JP6190153B2 JP 6190153 B2 JP6190153 B2 JP 6190153B2 JP 2013099713 A JP2013099713 A JP 2013099713A JP 2013099713 A JP2013099713 A JP 2013099713A JP 6190153 B2 JP6190153 B2 JP 6190153B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- cosmetic
- powder
- cosmetics
- solid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、高い発色性を有し、充填成形性に優れ、弾力性のある新規感触を有する固形メークアップ化粧料に関するものである。 The present invention relates to a solid make-up cosmetic having a high color developability, excellent filling moldability, and a new elastic feel.
メークアップ化粧料は、持ち歩きの利便性から、油性固形、粉体固形等の固形化粧料が広く用いられる。また、油性化粧料のエモリエント効果や付着性と、粉体化粧料の伸び広がりが軽く、べたつきのないさらさらとした感触の両方を併せ持った固形化粧料として、油と粉との中間領域が検討されている。例えば、中空樹脂粉体の表面を無機粉体で被覆してなる複合粉体を含有し、全粉体量と油性成分量の質量比が７０：３０〜４０：６０であるエモリエント感が高く、化粧効果の持続性に優れる油性固形化粧料を得る技術（特許文献１）、また、架橋型オルガノポリシロキサンと液状シリコーン油と粉体とを含有することで弾力性のある独特の使用感触を有する固形油性化粧料を得る技術（特許文献２）多孔質粉体を含む粉体と油剤を多量に含有し、しっとりとした感触の固形化粧料を得る技術（特許文献３）等があった。これらの技術では、エモリエント感、付着性、パウダリィな感触を得ることができるが、油性成分を多く含有することで、化粧料が振動や衝撃により容器内でずれを生じ、容器壁との間に隙間ができてしまう場合があった。 For makeup cosmetics, solid cosmetics such as oily solids and powdered solids are widely used for convenience of carrying. In addition, an intermediate area between oil and powder has been studied as a solid cosmetic that combines the emollient effect and adhesion of oil-based cosmetics and the light spread of powdered cosmetics with a light and non-sticky feel. ing. For example, it contains a composite powder obtained by coating the surface of a hollow resin powder with an inorganic powder, and the mass ratio of the total powder amount to the oil component amount is 70:30 to 40:60, and the emollient feeling is high. A technique for obtaining an oily solid cosmetic material having excellent cosmetic effect durability (Patent Document 1), and having a unique use feeling with elasticity by containing a cross-linked organopolysiloxane, a liquid silicone oil and a powder. Technology for obtaining solid oily cosmetics (Patent Document 2) There is a technology for obtaining a moist feel of solid cosmetics (Patent Document 3) containing a large amount of powder and oil containing porous powder. With these technologies, emollient feeling, adhesion, and powdery feel can be obtained, but by containing a lot of oily components, cosmetics are displaced in the container due to vibration and impact, and between the container wall There was a case where a gap was formed.
本発明は、振動や衝撃に強く、発色に優れた、弾力のある新規な感触の固形メークアップ化粧料を提供する。 The present invention provides a solid make-up cosmetic material that is resistant to vibration and impact, excellent in color development, and has a new elastic feel.
本発明者は鋭意研究を行った結果、油性成分を４５〜５５質量％と粉体を４０〜５０質量％、部分架橋型オルガノポリシロキサン重合物を２．５〜７．５質量％含有し、油性成分として２−エチルヘキサン酸セチルを化粧料全量に対し２０〜３０質量％含む、固形メークアップ化粧料が、振動や衝撃に強く、弾力のある新規な感触を有し、更には高い発色有することを見出し、本発明を完成した。 As a result of intensive studies, the inventor contains 45 to 55% by mass of an oil component, 40 to 50% by mass of powder, and 2.5 to 7.5% by mass of a partially crosslinked organopolysiloxane polymer, Solid makeup cosmetics containing 20-30% by mass of cetyl 2-ethylhexanoate as an oil component, based on the total amount of cosmetics, are strong against vibrations and impacts, have a new elastic feel, and have high color development. As a result, the present invention has been completed.
本発明の固形メークアップ化粧料は、高い発色性と強度に優れた、弾力のある新規な感触を有する。 The solid make-up cosmetic composition of the present invention has a new elastic feel with excellent color development and strength.
以下、本発明を詳細に説明する。
本発明の固形メークアップ化粧料は、油性成分を４５〜５５％（以下、単に「％」と略す）、粉体成分を４０〜５０％、部分架橋型オルガノポリシロキサン重合物を２．５〜７．５％含有し、油性成分として２−エチルヘキサン酸セチルを２０〜３０％含有するものである。本発明品は、着手時に指等で押すと、ゆっくりと沈み、ゆっくりと戻る感触の良い低反発性の弾力があり、とれが良い柔らかさを有しているが、一方で輸送や落下の衝撃を受けても、化粧料が容器の中で、片方によってしまうズレや、容器から抜けたりすることのない優れた強度と、高い発色性を有している。、
Hereinafter, the present invention will be described in detail.
The solid makeup cosmetic of the present invention has an oily component of 45 to 55% (hereinafter simply referred to as “%”), a powder component of 40 to 50%, and a partially crosslinked organopolysiloxane polymer of 2.5 to It contains 7.5% and contains 20-30% cetyl 2-ethylhexanoate as an oil component. The product of the present invention has a low resilience elasticity with a good feel that sinks slowly and returns slowly when pushed with a finger or the like at the time of starting, and has a good softness. Even if it receives, cosmetics have the outstanding intensity | strength which does not slip | deviate by one side in a container, and do not come out of a container, and high coloring property. ,
本発明における油性成分は、化粧料に一般に使用されるものであれば特に制限なく使用することができる。動物油、植物油、合成油等の起源及び、固形油、半固形油、液体油、揮発性油等の性状を問わず、炭化水素類、油脂類、ロウ類、硬化油類、脂肪酸類、高級アルコール類、エステル類、シリコーン油類、フッ素系油類、ラノリン誘導体類等が挙げられる。具体的には、オリーブ油、ヒマシ油、ホホバ油、ミンク油等の油脂類、ミツロウ、ラノリン、キャンデリラ等のロウ類、流動パラフィン、スクワラン、ワセリン、ポリイソブチレン、ポリブテン、パラフィンワックス、マイクロクリスタリンワックス、モクロウ、モンタンワックス、フィッシュトロプスワックス、１２−ヒドロキシステアリン酸等の炭化水素類、エチルヘキサン酸セチル、ミリスチン酸イソプロピル、トリオクタン酸グリセリル、ジイソステアリン酸ポリグリセリル、トリイソステアリン酸ジグリセリル、トリベヘン酸グリセリル、ロジン酸ペンタエリトリットエステル、ジオクタン酸ネオペンチルグリコール等のエステル類、ラノリン脂肪酸イソプロピル、ラノリンアルコール等のラノリン誘導体、ステアリン酸、ミリスチン酸、ベヘニン酸、ロジン酸等の脂肪酸類、ステアリルアルコール、セチルアルコール、ベヘニルアルコール等の高級アルコール類、ジメチルポリシロキサン、メチルフェニルポリシロキサンのシリコーン類、パーフルオロポリエーテル、パーフルオロデカン、パーフルオロオクタン等のフッ素系油類等が挙げられ、これらを１種または２種以上用いることができる。油性成分の含有量は、化粧料中に４５〜５５％である。４５％より少ないと発色や弾力性のある新規な感触に乏しく、５５％より多いと弾力性が得られず、強度が低くなる。 The oil component in the present invention can be used without particular limitation as long as it is generally used in cosmetics. Regardless of the origin of animal oil, vegetable oil, synthetic oil, and the nature of solid oil, semi-solid oil, liquid oil, volatile oil, etc., hydrocarbons, fats and oils, waxes, hardened oils, fatty acids, higher alcohols , Esters, silicone oils, fluorinated oils, lanolin derivatives and the like. Specifically, oils such as olive oil, castor oil, jojoba oil, mink oil, waxes such as beeswax, lanolin, candelilla, liquid paraffin, squalane, petrolatum, polyisobutylene, polybutene, paraffin wax, microcrystalline wax, molasses , Montan wax, fish trops wax, hydrocarbons such as 12-hydroxystearic acid, cetyl ethylhexanoate, isopropyl myristate, glyceryl trioctanoate, polyglyceryl diisostearate, diglyceryl triisostearate, glyceryl tribehenate, pentalith rosinate Elite esters, esters such as neopentyl glycol dioctanoate, lanolin derivatives such as lanolin fatty acid isopropyl, lanolin alcohol, stearic acid, myris Acids, fatty acids such as behenic acid, rosin acid, higher alcohols such as stearyl alcohol, cetyl alcohol, and behenyl alcohol, dimethylpolysiloxane, silicones of methylphenylpolysiloxane, perfluoropolyether, perfluorodecane, perfluorooctane Fluorine-based oils and the like can be used, and one or more of these can be used. The content of the oil component is 45 to 55% in the cosmetic. If the amount is less than 45%, a novel touch with coloring or elasticity is poor, and if it is more than 55%, elasticity cannot be obtained and the strength is lowered.
本発明では油性成分として２−エチルヘキサン酸セチルを、化粧料中に２０〜３０％含有する。２−エチルヘキサン酸セチルは常温で液状であり、市販品としてはニッコールＣＩＯ（日光ケミカルズ社製）、サラコス８１６Ｔ（日清オイリオグループ社製）、ＣＥＴＩＯＬ ＳＮ−１（ＢＡＳＦ社製）等が挙げられる。２−エチルヘキサン酸セチルをこの範囲で含有すると、高い発色の固形メークアップ化粧料が得られる。 In this invention, 20-30% of cetyl 2-ethylhexanoate is contained in cosmetics as an oil-based component. Cetyl 2-ethylhexanoate is liquid at room temperature, and examples of commercially available products include Nikkor CIO (manufactured by Nikko Chemicals), Saracos 816T (manufactured by Nisshin Oillio Group), CETIOL SN-1 (manufactured by BASF), and the like. . When cetyl 2-ethylhexanoate is contained in this range, a highly colored solid makeup cosmetic can be obtained.
粉体成分としては、化粧料に一般に使用される粉体であれば、球状、板状、針状等の形状、煙霧状、微粒子、顔料級等の粒子径、多孔質、無孔質等の粒子構造等の制限なく使用することができ、無機粉体類、光輝性粉体類、有機粉体類、色素粉体類、複合粉体類等が挙げられる。具体的には、酸化チタン、黒色酸化チタン、コンジョウ、群青、ベンガラ、黄酸化鉄、黒酸化鉄、酸化亜鉛、酸化アルミニウム、無水ケイ酸、酸化マグネシウム、酸化ジルコニウム、炭酸マグネシウム、炭酸カルシウム、酸化クロム、水酸化クロム、カーボンブラック、ケイ酸アルミニウム、ケイ酸マグネシウム、ケイ酸アルミニウムマグネシウム、雲母、合成金雲母、セリサイト、タルク、カオリン、硫酸バリウム、窒化ホウ素、オキシ塩化ビスマス等の無機粉体類や、ナイロン、ポリメチルメタクリレート、ポリアクリル酸アルキル、オルガノポリシロキサンエラストマー、ポリメチルセスキオキサン、ポリスチレン、アクリロニトリル−メタクリル酸共重合体、塩化ビニリデン−メタクリル酸共重合体、ポリエチレン、ウレタン、ウール、シルク、結晶セルロース、Ｎ−アシルリジン等の有機粉体類、有機タール系顔料、有機色素等のレーキ顔料等の色素粉体類、微粒子酸化チタン被覆雲母チタン、微粒子酸化亜鉛被覆雲母チタン、硫酸バリウム被覆雲母チタン、酸化チタン含有無水ケイ酸、酸化亜鉛含有無水ケイ酸、酸化チタン被覆ガラス末、酸化チタン被覆合成金雲母、雲母チタン、酸化鉄被覆雲母チタン、紺青被覆雲母チタン、カルミン被覆雲母チタン等の複合粉体類や、ポリエチレンテレフタレート・アルミニウム・エポキシ積層末、ポリエチレンテレフタレート・ポリメチルメタクリレート積層末などの積層フィルム末類等が挙げられる。、これらは、本発明の効果を妨げない限りフッ素系化合物、シリコーン系化合物、金属石鹸、レシチン、水素添加レシチン、コラーゲン、炭化水素、高級脂肪酸、高級アルコール、エステル、ワックス、ロウ、界面活性剤等の表面処理を施してあってもよい。本発明では粉体成分を４０〜５０％含有する。この範囲であると、弾力性のある新規な感触を得ることができる。また、４０％より少ないと十分な強度が得られず、５０％より多くなると高い発色や弾力性が得られにくくなる。 As a powder component, as long as it is a powder generally used in cosmetics, spherical, plate-like, needle-like shapes, fumes, fine particles, pigment grades, etc., porous, non-porous, etc. It can be used without any limitation on the particle structure, and examples thereof include inorganic powders, glitter powders, organic powders, pigment powders, and composite powders. Specifically, titanium oxide, black titanium oxide, conger, ultramarine, bengara, yellow iron oxide, black iron oxide, zinc oxide, aluminum oxide, silicic anhydride, magnesium oxide, zirconium oxide, magnesium carbonate, calcium carbonate, chromium oxide Inorganic powders such as chromium hydroxide, carbon black, aluminum silicate, magnesium silicate, magnesium magnesium silicate, mica, synthetic phlogopite, sericite, talc, kaolin, barium sulfate, boron nitride, bismuth oxychloride, , Nylon, polymethyl methacrylate, polyalkyl acrylate, organopolysiloxane elastomer, polymethyl sesquioxane, polystyrene, acrylonitrile-methacrylic acid copolymer, vinylidene chloride-methacrylic acid copolymer, polyethylene, urethane, woo Organic powders such as silk, crystalline cellulose, N-acyl lysine, pigment powders such as organic tar pigments, lake pigments such as organic pigments, fine particle titanium oxide-coated mica titanium, fine particle zinc oxide-coated mica titanium, barium sulfate Coated mica titanium, titanium oxide containing silicic acid, zinc oxide containing silicic acid, titanium oxide coated glass powder, titanium oxide coated synthetic phlogopite, titanium mica, iron oxide coated mica titanium, bitumen coated mica titanium, carmine coated mica titanium And composite film powders such as polyethylene terephthalate / aluminum / epoxy laminated powder, polyethylene terephthalate / polymethyl methacrylate laminated powder, and the like. These are fluorine compounds, silicone compounds, metal soaps, lecithins, hydrogenated lecithins, collagens, hydrocarbons, higher fatty acids, higher alcohols, esters, waxes, waxes, surfactants, etc., as long as they do not interfere with the effects of the present invention. The surface treatment may be applied. In this invention, 40-50% of powder components are contained. Within this range, a new elastic feel can be obtained. Further, if it is less than 40%, sufficient strength cannot be obtained, and if it exceeds 50%, it is difficult to obtain high color development and elasticity.
本発明においては、粉体成分中に着色板状粉体を含むことが好ましい。着色板状粉体としては特に制限されないが、粉体が白色ではない酸化鉄被覆雲母、コンジョウ被覆雲母、カルミン被覆雲母、酸化鉄被覆雲母チタン、コンジョウ被覆雲母チタン、カルミン被覆雲母チタン、ベンガラ・カルミン被覆雲母チタン、ベンガラ・コンジョウ被覆雲母チタン、酸化鉄・酸化チタン被覆合成金雲母、酸化鉄被覆ガラス末、酸化鉄・酸化チタン被覆ガラス末、シリカ・酸化鉄被覆酸化鉄、シリカ・酸化鉄被覆アルミニウム、法定色素被覆雲母チタン等が挙げられる。本発明ではこれらの着色板状粉体を含有することで、肌上に密に伸び広がり高い発色をあたえることができる。中でも被覆層に酸化鉄を有する雲母や雲母チタンであると、本発明において、２−エチルヘキサン酸セチルを含む油剤と接触し高い発色が得られる。市販品としては、ＣＬＯＩＳＯＮＮＥ ＲＯＵＧＥ ＦＬＡＭＢＥ、ＣＬＯＩＳＯＮＮＥ ＣＥＲＩＳＥ ＦＬＡＭＢＥ、ＣＬＯＩＳＯＮＮＥ ＮＵ−ＡＮＴＩＱＵＥ ＢＲＯＮＺＥ、ＴＩＭＩＣＡ ＢＲＩＬＬＩＡＮＴ ＧＯＬＤ（以上ＢＡＳＦ社製）、ＣＯＬＯＲＯＮＡ ＢＲＯＮＺＥ（メルク社製）等が挙げられる。これらの着色板状粉体は、平均粒径５０μｍ以下、更には３０μｍ以下のものが好適に用いられる。これらの着色板状粉体は、化粧料中に１０〜３０％含有すると発色の点において、より効果を得られる。 In the present invention, the powder component preferably contains a colored plate-like powder. There are no particular restrictions on the colored plate-like powder, but the powder is not white iron oxide-coated mica, koji-coated mica, carmine-coated mica, iron oxide-coated mica titanium, kanji-coated mica titanium, carmine-coated mica titanium, Bengala carmine Coated Mica Titanium, Bengala / Kongyou Coated Mica Titanium, Iron Oxide / Titanium Oxide Coated Synthetic Gold Mica, Iron Oxide Coated Glass Powder, Iron Oxide / Titanium Oxide Glass Powder, Silica / Iron Oxide Coated Iron Oxide, Silica / Iron Oxide Coated Aluminum And legal dye-coated mica titanium. In the present invention, by containing these colored plate-like powders, it is possible to provide a high color development that spreads densely on the skin. Among them, when mica or titanium mica having iron oxide in the coating layer is contacted with an oil agent containing cetyl 2-ethylhexanoate in the present invention, high color development is obtained. Commercially available products include CLOISONE ROUGE FLAMBE, CLOSONNE CERISE FLAMBE, CLOISONE NU-ANTIQUE BRONZE, TIMICA BRILLIANT GOLD (manufactured by BASF), and COLORONA BRONZE. As these colored plate-like powders, those having an average particle size of 50 μm or less, further 30 μm or less are preferably used. When these colored plate-like powders are contained in the cosmetic in an amount of 10 to 30%, the effect can be further obtained in terms of color development.
更に、本発明においては、粉体成分中に酸化亜鉛を含有することで、強度を保ったまま、柔らかい感触を与えることができる。酸化亜鉛は化粧料中に０．１〜４％であると効果が得られやすい。 Furthermore, in the present invention, by containing zinc oxide in the powder component, it is possible to give a soft feel while maintaining the strength. When zinc oxide is 0.1 to 4% in the cosmetic, the effect is easily obtained.
本発明における部分架橋型オルガノポリシロキサン重合物は、ベンゼンに不溶であるが、自重と同重量以上のベンゼンを含みうる三次元架橋構造を有するオルガノポリシロキサン重合物であり、特公平８−６０３５号公報等に記載されているものが例示される。部分架橋型オルガノポリシロキサン重合物は、オルガノポリシロキサンを架橋結合させて得られる重合物であり、一部に三次元架橋構造を有し、Ｒ２ ２ＳｉＯ単位及びＲ２ＳｉＯ１．５単位よりなり、Ｒ２ ３ＳｉＯ０．５単位及び／又はＳｉＯ２単位を含んでいても良い。式中のＲ２は水素原子、メチル基、エチル基、プロピル基等のアルキル基、フェニル基、トリル基等などのアリール基、及びビニル基等の脂肪族不飽和基などが例示され、同種又は異なった種類であっても良い。 The partially crosslinked organopolysiloxane polymer in the present invention is an organopolysiloxane polymer that is insoluble in benzene but has a three-dimensional crosslinked structure that can contain benzene of the same weight or more as its own weight. Japanese Patent Publication No. 8-6035 What is described in the gazette etc. is illustrated. The partially cross-linked organopolysiloxane polymer is a polymer obtained by cross-linking organopolysiloxane, partially having a three-dimensional cross-linking structure, and from R 2 2 SiO units and R 2 SiO 1.5 units. It may contain R 2 3 SiO 0.5 unit and / or SiO 2 unit. R 2 in the formula is exemplified by a hydrogen atom, an alkyl group such as a methyl group, an ethyl group and a propyl group, an aryl group such as a phenyl group and a tolyl group, and an aliphatic unsaturated group such as a vinyl group. Different types may be used.
このような成分は、例えばＩＮＣＩ（International Nomenclature Cosmetic Ingredient labeling names）名で（ジメチコン／ビニルジメチコン）クロスポリマー、（ジメチコン／フェニルビニルジメチコン）、クロスポリマー、（ビニルジメチコン／ラウリルジメチコン）クロスポリマー等が挙げられる。市販品としては、シリコーン油や炭化水素、エステル油と混合しているものが一般的で、例えば、ＫＳＧ−１５（部分架橋型メチルポリシロキサン５部とデカメチルシクロペンタシロキサン９５部）、ＫＳＧ−１６（部分架橋型メチルポリシロキサン２０〜３０部とメチルポリシロキサン７０〜８０部）、ＫＳＧ−１７（部分架橋型メチルポリシロキサン５部とオクタメチルシクロテトラシロキサン９５部）、ＫＳＧ−１８（部分架橋型メチルポリシロキサン１０〜２０部とメチルフェニルポリシロキサン８０〜９０部）、ＫＳＧ−４１（部分架橋型オルガノポリシロキサン重合物３５〜２５部とミネラルオイル６５〜７５部）、ＫＳＧ−４２（部分架橋型オルガノポリシロキサン重合物３０〜２０部とイソドデカン７０〜８０部）、ＫＳＧ−４３（部分架橋型オルガノポリシロキサン重合物３５〜２５部とトリオクタノイン（トリ−２−エチルヘキサン酸グリセリル）６５〜７５部）、ＫＳＧ−４４（部分架橋型オルガノポリシロキサン重合物２５〜３５部とスクワラン６５〜７５部）（以上、信越化学工業社製）等を具体的に挙げることができる。 Such components include, for example, (Dimethicone / vinyl dimethicone) crosspolymer, (dimethicone / phenylvinyldimethicone), crosspolymer, (vinyl dimethicone / lauryl dimethicone) crosspolymer under the name of INCI (International Nomenclature Cosmetic Ingredient labeling names). It is done. Commercially available products are generally mixed with silicone oil, hydrocarbon or ester oil. For example, KSG-15 (5 parts of partially crosslinked methylpolysiloxane and 95 parts of decamethylcyclopentasiloxane), KSG- 16 (20-30 parts partially crosslinked methylpolysiloxane and 70-80 parts methylpolysiloxane), KSG-17 (5 parts partially crosslinked methylpolysiloxane and 95 parts octamethylcyclotetrasiloxane), KSG-18 (partially crosslinked) Type methylpolysiloxane 10-20 parts and methylphenylpolysiloxane 80-90 parts), KSG-41 (partially crosslinked organopolysiloxane polymer 35-25 parts and mineral oil 65-75 parts), KSG-42 (partially crosslinked) Type organopolysiloxane polymer 30-20 parts and isododecane 70-80 parts), KSG 43 (35 to 25 parts of partially crosslinked organopolysiloxane polymer and 65 to 75 parts of trioctanoin (glyceryl tri-2-ethylhexanoate)), KSG-44 (25 to 35 parts of partially crosslinked organopolysiloxane polymer) And Squalane 65 to 75 parts) (above, manufactured by Shin-Etsu Chemical Co., Ltd.) and the like.
本発明においては、これらの部分架橋型オルガノポリシロキサン重合物を１種又は２種以上を組み合わせて用いることができ、化粧料中に２．５〜７．５％含有する。含有量が２．５％未満であると感触に弾力が無くなり、さらに発色も十分に得られない。また、７．５％を超えると強度が保てない。更に、含有量が３．５〜６％であると、弾力、発色、強度の点でより優れた化粧料が得られる。 In the present invention, these partially crosslinked organopolysiloxane polymers can be used singly or in combination of two or more, and are contained in the cosmetic at 2.5 to 7.5%. If the content is less than 2.5%, the feel is not elastic, and color development cannot be sufficiently obtained. On the other hand, if it exceeds 7.5%, the strength cannot be maintained. Furthermore, if the content is from 3.5 to 6%, a cosmetic that is more excellent in terms of elasticity, coloring, and strength can be obtained.
本発明においては、特に構造単位中に炭素数が１０〜３０の長鎖アルキル基を含有する部分架橋型オルガノポリシロキサン重合物と長鎖アルキル基を含有しない部分架橋型オルガノポリシロキサン重合物を併用すると、高い発色性と、弾力のある新規感触の点で好ましい。例えば、長鎖アルキル基を含有しない部分架橋型オルガノポリシロキサン重合物として（ジメチコン／ビニルジメチコン）クロスポリマー、長鎖アルキル基を含有する部分架橋型オルガノポリシロキサン重合物としてビニルジメチコン／ラウリルジメチコン）クロスポリマーの組合せがあげられる。この場合の質量比は、長鎖アルキル基を含有しない部分架橋型オルガノポリシロキサン重合物１に対し、長鎖アルキル基を含有する部分架橋型オルガノポリシロキサン重合物が０．５〜２、更には０．６〜１．５であると、弾力、発色、強度の点でより好ましい。 In the present invention, a partially crosslinked organopolysiloxane polymer containing a long-chain alkyl group having 10 to 30 carbon atoms in the structural unit and a partially crosslinked organopolysiloxane polymer not containing a long-chain alkyl group are used in combination. Then, it is preferable at the point of high color developability and a new novel feeling with elasticity. For example, (dimethicone / vinyl dimethicone) crosspolymer as a partially crosslinked organopolysiloxane polymer containing no long chain alkyl group, and vinyl dimethicone / lauryl dimethicone as a partially crosslinked organopolysiloxane polymer containing a long chain alkyl group Examples include polymer combinations. The mass ratio in this case is such that the partially crosslinked organopolysiloxane polymer containing a long-chain alkyl group is 0.5 to 2 with respect to the partially crosslinked organopolysiloxane polymer 1 not containing a long-chain alkyl group, A value of 0.6 to 1.5 is more preferable in terms of elasticity, color development, and strength.
本発明の固形メークアップ化粧料は、上記必須成分の他に通常化粧料に用いられる成分を本発明の効果を妨げない範囲で、必要に応じて適宜含有することができる。例えば、界面活性剤、水や多価アルコール、低級アルコール、水溶性高分子、保湿剤等の水性成分、紫外線吸収剤、酸化防止剤、防腐剤、美容成分、清涼剤、色素、香料等が挙げられる。 The solid make-up cosmetic composition of the present invention can contain, as necessary, components other than the above-mentioned essential components, which are usually used in cosmetics, as long as the effects of the present invention are not impaired. For example, surfactants, water, polyhydric alcohols, lower alcohols, water-soluble polymers, aqueous components such as humectants, ultraviolet absorbers, antioxidants, preservatives, beauty ingredients, refreshing agents, pigments, fragrances, etc. It is done.
界面活性剤としては、化粧料に一般に用いられている界面活性剤であればいずれのものでも使用でき、非イオン性界面活性剤、アニオン性界面活性剤、カチオン性界面活性剤、両性界面活性剤等が挙げられる。例えば、グリセリン脂肪酸エステルおよびそのアルキレングリコール付加物、ポリグリセリン脂肪酸エステルおよびそのアルキレングリコール付加物、ショ糖脂肪酸エステル、ポリオキシエチレン硬化ヒマシ油、レシチン等を挙げることができ、これらを１種または２種以上用いることができる。 As the surfactant, any surfactant generally used in cosmetics can be used. Nonionic surfactant, anionic surfactant, cationic surfactant, amphoteric surfactant Etc. Examples include glycerin fatty acid esters and alkylene glycol adducts thereof, polyglycerin fatty acid esters and alkylene glycol adducts thereof, sucrose fatty acid esters, polyoxyethylene hydrogenated castor oil, lecithin, and the like. The above can be used.
水性成分としては、水の他に、例えば、エチルアルコール等のアルコール類、プロピレングリコール、１，３−ブチレングリコール、ジプロピレングリコール、ポリエチレングリコール等のグリコール類、グリセリン、ジグリセリン、ポリグリセリン等のグリセロール類、グアーガム、コンドロイチン硫酸ナトリウム、ヒアルロン酸ナトリウム、アラビアガム、アルギン酸ナトリウム、カラギーナン、セルロース、カルボキシビニルポリマー、、ポリビニルアルコール、ポリビニルピロリドン、ポリアクリル酸ナトリウム、タンパク質、ムコ多糖類、コラーゲン、エラスチン、ケラチン等の水溶性高分子類を挙げることができ、これらを１種または２種以上用いることができる。 As the aqueous component, in addition to water, for example, alcohols such as ethyl alcohol, glycols such as propylene glycol, 1,3-butylene glycol, dipropylene glycol and polyethylene glycol, glycerol such as glycerin, diglycerin and polyglycerin , Guar gum, sodium chondroitin sulfate, sodium hyaluronate, gum arabic, sodium alginate, carrageenan, cellulose, carboxyvinyl polymer, polyvinyl alcohol, polyvinylpyrrolidone, sodium polyacrylate, protein, mucopolysaccharide, collagen, elastin, keratin, etc. These water-soluble polymers can be mentioned, and one or more of these can be used.
紫外線吸収剤としては、例えば、ベンゾフェノン系、ＰＡＢＡ系、ケイ皮酸系、サリチル酸系、４−ｔｅｒｔ−ブチル−４’−メトキシベンゾイルメタン、オキシベンゾン等、酸化防止剤としては、例えば、トコフェロール、アスコルビン酸等、美容成分としては例えば、ビタミン類、消炎剤、植物抽出物、生薬等、防腐剤としては、例えば、パラオキシ安息香酸エステル、フェノキシエタノール、１，２−アルカンジオール等を挙げることができ、これらを１種または２種以上用いることができる。 Examples of the ultraviolet absorber include benzophenone-based, PABA-based, cinnamic acid-based, salicylic acid-based, 4-tert-butyl-4′-methoxybenzoylmethane, and oxybenzone. Examples of the antioxidant include tocopherol and ascorbic acid. Examples of cosmetic ingredients include vitamins, anti-inflammatory agents, plant extracts, herbal medicines, etc. Examples of preservatives include paraoxybenzoic acid esters, phenoxyethanol, 1,2-alkanediol, and the like. 1 type (s) or 2 or more types can be used.
本発明の固形メークアップ化粧料は、特に限定されないが、携帯されることの多いアイカラー、チークカラー、アイブロウ、ファンデーション等に用いられ、使用感や発色のよさの点からアイカラー、チークカラーにより好適に用いられる。 The solid make-up cosmetic composition of the present invention is not particularly limited, but is used for eye color, cheek color, eyebrow, foundation, etc., which are often carried around, depending on eye color and cheek color from the viewpoint of feeling of use and color development. Preferably used.
本発明の固形メークアップ化粧料は、特に限定されないが、上記の油性成分、粉体成分、部分架橋型オルガノポリシロキサン及びその他適宜含有される成分を、均一に混合、必要に応じて粉砕して組成物を調整する。これを容器に充填して圧縮成型、又は溶媒と混合してスラリー状としたものを容器に充填した後溶媒を除去する等して得ることができる。 The solid makeup cosmetic of the present invention is not particularly limited, but the above oily component, powder component, partially cross-linked organopolysiloxane and other appropriately contained components are uniformly mixed, and pulverized as necessary. Adjust the composition. This can be obtained by filling the container and compressing it, or mixing it with a solvent to form a slurry, filling the container and then removing the solvent.
以下に実施例をもって本発明をより詳細に説明するが、本発明はこれらにより、何ら限定されるものではない。 The present invention will be described in more detail with reference to the following examples, but the present invention is not limited thereto.
実施例１〜７及び比較例１〜６：アイシャドウ
表１に示す組成のアイシャドウを下記の製造方法により調製し、各試料について下記評価方法にて評価し、その結果も併せて表１に示した。
Examples 1 to 7 and Comparative Examples 1 to 6: Eye shadow Eye shadows having the compositions shown in Table 1 were prepared by the following production methods, and each sample was evaluated by the following evaluation method. The results are also shown in Table 1. Indicated.
※１：ＣＬＯＩＳＯＮＮＥ ＣＥＲＩＥＳＥ ＦＬＡＭＢＥ ５５０Ｚ（ＢＡＳＦ社製）
※２：ＦＬＡＭＥＮＣＯ ＲＥＤ ４２０Ｃ（ＢＡＳＦ社製）
※３：シリコン ＫＦ−９６（２０ｃｓ）（信越化学工業社製）
※４：パールリーム１８（日油社製）
※５：ＫＳＧ−４３（信越化学工業社製）
※６：ＫＳＧ−１６（信越化学工業社製）
※７：ＣＥＴＩＯＬ ＳＮ−１（ＢＡＳＦ社製）
※８：ＫＬＥＡＲＯＬ ＷＨＩＴＥ ＭＩＮＥＲＡＬ ＯＩＬ（ＳＯＮＮＥＢＯＲＮ社製）
* 1: CLOISONE CERISE FLAMBE 550Z (BASF)
* 2: FLAMENCO RED 420C (manufactured by BASF)
* 3: Silicon KF-96 (20cs) (manufactured by Shin-Etsu Chemical Co., Ltd.)
* 4: Pearl Dream 18 (manufactured by NOF Corporation)
* 5: KSG-43 (manufactured by Shin-Etsu Chemical Co., Ltd.)
* 6: KSG-16 (Shin-Etsu Chemical Co., Ltd.)
* 7: CETIOL SN-1 (BASF)
* 8: KLEAROL WHITE MINEAL OIL (manufactured by SONNEBORN)
（製造方法）
Ａ：成分１４〜１９を７０℃に加温し、混合する。
Ｂ：成分１〜１３を均一に攪拌混合する。
Ｃ：ＢにＡを加え均一に攪拌混合したものに溶媒として２−エチルヘキサン酸セチル（比較例５は１４と同じシリコーン油、比較例６は１９と同じ流動パラフィン）を加えスラリー状にする。
Ｄ：Ｃを皿状容器に充填し、化粧料と圧縮用ヘッドの間に溶媒吸取り用の紙を挟み、溶媒除去、圧縮成型して、表１の組成のアイシャドウを得た。
(Production method)
A: Ingredients 14 to 19 are heated to 70 ° C. and mixed.
B: Components 1 to 13 are stirred and mixed uniformly.
C: A mixture of B and B with uniform stirring and mixing is mixed with cetyl 2-ethylhexanoate (Comparative Example 5 is the same silicone oil as 14 and Comparative Example 6 is the same liquid paraffin as 19) to form a slurry.
D: C was filled in a dish-like container, and a solvent absorbing paper was sandwiched between the cosmetic and the compression head, and the solvent was removed and compression molded to obtain an eye shadow having the composition shown in Table 1.
（評価項目）
（イ） 高発色
（ロ） 弾力性のある新規な感触
（ハ） 充填成型性
（二） 落下試験
（評価方法）
下記評価項目について各々下記評価方法により評価を行った。
（イ）、（ロ）は専門パネル２０名が各試料を使用し、（イ）は化粧料塗布時の発色性を、（ロ）は着手時のプニョッとした弾力性のある感触が良好に感じられるかどうか、について下記絶対評価基準にて５段階に評価し評点をつけ、各試料のパネル全員の評点合計から、その平均値を算出し、下記４段階判定基準により判定した。（ハ）は皿状容器に充填し圧縮成型を行った際に、容器に均一に充填されているかの可否を判定した。（ニ）の落下試験については、化粧料をコンパクト容器に装填し、コンパクト容器のそれぞれ４方向を下にして、高さ５０ｃｍの位置から硬質な素材を用いた床材であるプラスチックタイルに落下させて、目視にて内容物のがズレの程度を判定した。
(Evaluation item)
(A) High color development (b) New elastic feel (c) Filling moldability (2) Drop test (evaluation method)
The following evaluation items were evaluated by the following evaluation methods.
(A), (B) 20 professional panels use each sample, (A) shows the color development when applying cosmetics, and (B) shows the supple and elastic feel when starting. Whether or not it was felt was evaluated in 5 grades based on the following absolute evaluation criteria, given a score, the average value was calculated from the total score of all the panels of each sample, and judged according to the following 4 criteria. In (c), it was determined whether or not the container was uniformly filled when the dish-shaped container was filled and compression molded. For the drop test of (d), cosmetics are loaded into a compact container, and each of the compact containers is placed in four directions down and dropped from a position of 50 cm in height onto a plastic tile that is a floor material using a hard material. The degree of deviation of the contents was visually determined.
（評価項目（イ）、（ロ）、の絶対評価基準）
評点 ：評価
５点：非常に良好
４点：良好
３点：普通
２点：やや不良
１点：不良
（評価項目（イ）、（ロ）、の判定基準）
判定 ：評点の平均点
◎：４．５点を越える
○：３．５点を越える４．５点以下
△：２点を越える３．５点以下
×：２点未満
（評価項目（ハ）の判定基準）
判定 ：充填後の状態
◎：化粧料が皿状容器内に均一に成型されている
○：化粧料が皿状容器内にわずかな歪みは見られるが、
ほぼ均一に成型されている
×：化粧料が皿状容器内に均一に成型されていない
（評価項目（ニ）の判定基準）
判定 ：落下試験後の状態
◎：変化が見られない
○：わずかな変化が見られる
×：皿状容器壁と化粧料の間に明らかな隙間が見られたり、
化粧料が抜けたりする
（ハ）（ニ）については×を不可とする。
(Absolute evaluation criteria for evaluation items (b) and (b))
Score: Evaluation 5 points: Very good 4 points: Good 3 points: Normal 2 points: Slightly bad 1 point: Bad (Evaluation criteria (b), (b))
Judgment: Average score ◎: Over 4.5 points ○: Over 3.5 points 4.5 or less △: Over 2 points 3.5 or less ×: Less than 2 points (evaluation item (c) Criteria)
Judgment: State after filling ◎: Cosmetics are uniformly molded in a dish-shaped container ○: Although slight distortion is seen in the dish-shaped container,
×: The cosmetic is not uniformly molded in the dish-like container
(Criteria for evaluation item (d))
Judgment: State after the drop test ◎: No change is observed ○: A slight change is observed ×: An obvious gap is seen between the dish-shaped container wall and the cosmetic,
“X” is not allowed for cosmetics that fall out.
表１の結果から明らかな如く、本発明の実施例１〜７のアイシャドウは比較例１〜６に比べ、高い発色性を有し、さらに低反発性の弾力のある新規感触を有しているものであった。一方、油性成分の含有量が少なく、粉体成分の含有量が多い比較例１、３、４は特に発色や感触の弾力性に劣り、油性成分の含有量が多く、粉体成分の含有量が少ない比較例２は感触の弾力性や充填成形性、落下試験に劣るものであった。また、２−エチルヘキサン酸セチルの代わりにシリコーン油や流動パラフィンを配合した比較例５、６は発色に劣るものであった。 As is apparent from the results in Table 1, the eye shadows of Examples 1 to 7 of the present invention have a higher color developability than those of Comparative Examples 1 to 6, and also have a new feel with low resilience and elasticity. It was something. On the other hand, Comparative Examples 1, 3, and 4 having a small content of oil component and a large content of powder component are particularly inferior in elasticity of color development and feel, a large content of oil component, and a content of powder component. Comparative Example 2 with a small amount was inferior to the feel elasticity, filling moldability, and drop test. Further, Comparative Examples 5 and 6 in which silicone oil or liquid paraffin was blended in place of cetyl 2-ethylhexanoate were inferior in color development.
実施例１０：チークカラー
（成分） （％）
１．マイカ 残量
２．タルク ５
３．合成金雲母 ５
４．パラオキシ安息香酸メチル ０．２
５．メタクリル酸メチルクロスポリマー ３
７．赤色２０２ ２
６．黄酸化鉄 ０．２
７．カオリン ０．２
８．紺青 ０．２
９．ベンガラ被覆雲母チタン ※９ ２０
９．酸化鉄被覆ガラス末 ※１０ １
１０．雲母チタン ２
１１．ワセリン ２
１２．流動パラフィン ３
１３．水添ポリイソブテン ※１１ ５
１４．部分架橋型オルガノポリシロキサン重合物 ※５ １０
１５．部分架橋型オルガノポリシロキサン重合物 ※６ ８
１６．２−エチルヘキサン酸セチル ※７ ２５
※９：ＣＬＯＩＳＯＮＮＥ ＲＯＵＧＥ ＦＬＡＭＢＥ（平均粒径２５μ ＢＡＳＦ社製）
※１０：マイクログラス メタシャイン ＭＴ１０８０ＲＲ（平均粒径８０μ 日本板硝子社製）
※１１：パールリーム２４（日油社製）
（製造方法）
Ａ：成分１１〜１６を７０℃に加温し、混合する。
Ｂ：成分１〜１０を均一に攪拌混合する。
Ｃ：ＢにＡを加え均一に攪拌混合したものに溶媒として２−エチルヘキサン酸セチルを加えスラリー状にする。
Ｄ：Ｃを皿状容器に充填し、化粧料と圧縮用ヘッドの間に溶媒吸取り用の紙を挟み、溶媒除去、圧縮成型してチークカラーを得た。
実施例１０は、高い発色性を有し、充填成形性に優れ、衝撃に強く、弾力性のある新規感触を有しているチークカラーであった。
Example 10: Teak color (component) (%)
1. 1. Mica remaining amount Talc 5
3. Synthetic phlogopite 5
4). Methyl paraoxybenzoate 0.2
5. Methyl methacrylate cross polymer 3
7). Red 202 2
6). Yellow iron oxide 0.2
7). Kaolin 0.2
8). Bitumen 0.2
9. Bengala coated mica titanium * 9 20
9. Iron oxide coated glass powder * 10 1
10. Mica titanium 2
11. Vaseline 2
12 Liquid paraffin 3
13. Hydrogenated polyisobutene * 11 5
14 Partially cross-linked organopolysiloxane polymer * 5 10
15. Partially cross-linked organopolysiloxane polymer * 6 8
16. Cetyl 2-ethylhexanoate * 7 25
* 9: CLOISNE ROUGE FLAMBE (average particle size 25μ, manufactured by BASF)
* 10: Microglass Metashine MT1080RR (average particle size 80μ, manufactured by Nippon Sheet Glass Co., Ltd.)
* 11: Pearl Dream 24 (manufactured by NOF Corporation)
(Production method)
A: Components 11 to 16 are heated to 70 ° C. and mixed.
B: Components 1 to 10 are stirred and mixed uniformly.
C: Add A to B and stir and mix uniformly to add cetyl 2-ethylhexanoate as a solvent to form a slurry.
D: C was filled into a dish-like container, a solvent absorbing paper was sandwiched between the cosmetic and the compression head, and the solvent was removed and compression molded to obtain a cheek color.
Example 10 was a cheek color having high color developability, excellent filling moldability, strong impact resistance, and a new elastic feel.
実施例１１ ファンデーション
（成分） （％）
１．マイカ※１ 残量
２．タルク ５
３．合成金雲母 ５
４．パラオキシ安息香酸メチル ０．２
５．メタクリル酸メチルクロスポリマー ３
６．ナイロン末 ２
７．シリカ ２
８．酸化チタン ８
９．ベンガラ ２
１０．黄酸化鉄 ０．５
１１．黒酸化鉄 ０．５
１２．紺青 ０．５
１３．酸化鉄被覆雲母 ※１２ １０
１４．雲母チタン ２
１５．ワセリン ２
１６．流動パラフィン ３
１７．トリ２−エチルヘキサン酸グリセリル※１３ ５
１８．ジメチルポリシロキサン ※１４ ５
１９．部分架橋型オルガノポリシロキサン重合物 ※５ ５
２０．部分架橋型オルガノポリシロキサン重合物 ※６ １０
２１．２−エチルヘキサン酸セチル ※７ ２０
２２．香料 ０．２
※１２：ＣＯＬＯＲＯＮＡ ＢＲＯＮＺＥ（メルク社製）
※１３：Ｔ．Ｉ．Ｏ（日清オイリオグループ社製）
※１４：ＫＦ−９６−１０ｃｓ（信越シリコーン社製）
（製造方法）
Ａ：成分１５〜２２を７０℃に加温し、混合する。
Ｂ：成分１〜１４を均一に攪拌混合する。
Ｃ：ＢにＡを加え均一に攪拌混合したものに溶媒として２−エチルヘキサン酸セチルを加えスラリー状にする。
Ｄ：Ｃを皿状容器に充填し、化粧料と圧縮用ヘッドの間に溶媒吸取り用の紙を挟み、溶媒除去、圧縮成型してファンデーションを得た。
実施例１１は、高い発色性を有し、充填成形性に優れ、衝撃に強く、さらに弾力性のある新規感触を有しているファンデーションであった。
Example 11 foundation (component) (%)
1. Mica * 1 Remaining amount 2. Talc 5
3. Synthetic phlogopite 5
4). Methyl paraoxybenzoate 0.2
5. Methyl methacrylate cross polymer 3
6). Nylon powder 2
7). Silica 2
8). Titanium oxide 8
9. Bengala 2
10. Yellow iron oxide 0.5
11. Black iron oxide 0.5
12 Bitumen 0.5
13. Iron oxide coated mica * 12 10
14 Mica titanium 2
15. Vaseline 2
16. Liquid paraffin 3
17. Glyceryl tri-2-ethylhexanoate * 13 5
18. Dimethylpolysiloxane * 14 5
19. Partially cross-linked organopolysiloxane polymer * 5 5
20. Partially cross-linked organopolysiloxane polymer * 6 10
21.2-cetylethyl hexanoate * 7 20
22. Fragrance 0.2
* 12: COLORONA BRONZE (Merck)
* 13: T.W. I. O (Nisshin Oillio Group)
* 14: KF-96-10cs (manufactured by Shin-Etsu Silicone)
(Production method)
A: Ingredients 15 to 22 are heated to 70 ° C. and mixed.
B: Components 1 to 14 are stirred and mixed uniformly.
C: Add A to B and stir and mix uniformly to add cetyl 2-ethylhexanoate as a solvent to form a slurry.
D: C was filled in a dish-like container, a paper for absorbing the solvent was sandwiched between the cosmetic and the compression head, and the solvent was removed and compression molded to obtain a foundation.
Example 11 was a foundation having a high color developability, excellent filling moldability, strong impact resistance, and a new elastic feel.
Claims (6)