JP6178126B2 - SOLAR CELL SEALING MATERIAL COMPOSITION, PROCESS FOR PRODUCING THE SAME, SOLAR CELL SEALING MATERIAL LAYER USING THE SAME, AND SOLAR CELL MODULE - Google Patents

SOLAR CELL SEALING MATERIAL COMPOSITION, PROCESS FOR PRODUCING THE SAME, SOLAR CELL SEALING MATERIAL LAYER USING THE SAME, AND SOLAR CELL MODULE Download PDF

Info

Publication number
JP6178126B2
JP6178126B2 JP2013125401A JP2013125401A JP6178126B2 JP 6178126 B2 JP6178126 B2 JP 6178126B2 JP 2013125401 A JP2013125401 A JP 2013125401A JP 2013125401 A JP2013125401 A JP 2013125401A JP 6178126 B2 JP6178126 B2 JP 6178126B2
Authority
JP
Japan
Prior art keywords
solar cell
sealing material
ethylene
manufacturing
material composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2013125401A
Other languages
Japanese (ja)
Other versions
JP2015000902A (en
Inventor
洋毅 千田
洋毅 千田
久成 尾之内
久成 尾之内
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nitto Denko Corp
Original Assignee
Nitto Denko Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nitto Denko Corp filed Critical Nitto Denko Corp
Priority to JP2013125401A priority Critical patent/JP6178126B2/en
Priority to KR1020167000063A priority patent/KR20160019921A/en
Priority to CN201480033780.8A priority patent/CN105308113B/en
Priority to PCT/JP2014/064943 priority patent/WO2014199892A1/en
Publication of JP2015000902A publication Critical patent/JP2015000902A/en
Application granted granted Critical
Publication of JP6178126B2 publication Critical patent/JP6178126B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、太陽電池用封止材組成物およびその製造方法、ならびに、それを用いた太陽電池用封止材層および太陽電池モジュールに関する。   The present invention relates to a solar cell encapsulant composition, a method for producing the same, and a solar cell encapsulant layer and a solar cell module using the same.

太陽電池モジュールは、一般に、ガラス基板、太陽電池封止材、発電素子、太陽電池封止材、およびバックシートを順次積層した構造を有する。そして上記太陽電池封止材には、低コストや高透過率等の観点から、エチレン系共重合体をマトリックスとする樹脂シートが用いられている。   A solar cell module generally has a structure in which a glass substrate, a solar cell encapsulant, a power generation element, a solar cell encapsulant, and a back sheet are sequentially laminated. And the said solar cell sealing material uses the resin sheet which uses an ethylene-type copolymer as a matrix from viewpoints, such as low cost and high transmittance | permeability.

上記エチレン系共重合体には、耐久性を向上させるために有機過酸化物や架橋助剤などが含有されている。また、耐候性を付与するために、紫外線吸収剤のような紫外光領域に吸収領域を有する有機物やガラス、太陽電池素子の接着性を確保するために、シランカップリング剤が一般的に配合されている。   The ethylene-based copolymer contains an organic peroxide, a crosslinking aid, and the like in order to improve durability. In addition, in order to provide weather resistance, a silane coupling agent is generally blended in order to ensure the adhesiveness of organic substances, glass, and solar cell elements having an absorption region in the ultraviolet region such as an ultraviolet absorber. ing.

シート状太陽電池封止材の成形は、Ｔダイ押出成膜機やカレンダー成形機などによって行われる。たとえば、エチレン系共重合体に、上述のような添加剤をあらかじめドライブレンドした後に、Ｔダイ押出機のホッパーから供給し、有機過酸化物が実質的に分解しない成形温度でシート状に押出成形する方法がある（たとえば、特許文献１参照）。   The sheet-shaped solar cell encapsulant is molded by a T-die extrusion film forming machine or a calendar molding machine. For example, the above-mentioned additives are pre-dry blended into an ethylene copolymer, then supplied from a hopper of a T-die extruder, and extruded into a sheet at a molding temperature at which the organic peroxide is not substantially decomposed. There is a method (see, for example, Patent Document 1).

しかしながら、上記添加剤の中で、その融点が成形温度より高いものは溶融しないため、エチレン系共重合体に均一に分散しにくい問題があった。そのため、融点以上の温度で一度有機物を融解させる必要がある。しかし、高融点の有機物を、有機過酸化物が分解する温度以上の温度で融解させた場合、有機過酸化物の分解に伴う架橋反応が開始・進行し、シート表面にブツ等の不具合が発生したり、最終的な物性にも影響を及ぼすおそれがある。また、スクリュー回転数を上げて分散性を向上させる方法もあるが、せん断発熱の影響で樹脂温度が高くなり、結果的に過酸化物が分解する恐れがある。このため、高融点の有機物を、有機過酸化物が分解しない温度以下で分散させる方法が必要である。   However, among the above additives, those having a melting point higher than the molding temperature are not melted, so that there is a problem that it is difficult to uniformly disperse in the ethylene-based copolymer. Therefore, it is necessary to melt the organic substance once at a temperature equal to or higher than the melting point. However, if a high melting point organic substance is melted at a temperature higher than the temperature at which the organic peroxide decomposes, the cross-linking reaction accompanying the decomposition of the organic peroxide starts and proceeds, causing defects such as bumps on the sheet surface. And may affect the final physical properties. There is also a method of improving dispersibility by increasing the screw rotation speed, but the resin temperature becomes high due to the effect of shearing heat generation, which may result in decomposition of the peroxide. For this reason, a method of dispersing a high-melting-point organic substance at a temperature or lower at which the organic peroxide is not decomposed is necessary.

一つの手段として、二軸押出機のような溶融混練機でエチレン系共重合体にあらかじめ高融点の有機物のみをその融点以上で練りこんだマスターバッチを作製し、マスターバッチをエチレン系共重合体と有機過酸化物と一緒に低温で溶融混練しシート化する方法があげられる。しかしながら、上記手法でも、マスターバッチの工程が増えてしまうことで、材料のロスによるコスト増加や、熱履歴が増えることによるエチレン系共重合体自体の劣化が生じる問題がある。   As one means, a masterbatch is prepared by kneading only an organic substance having a high melting point above its melting point into the ethylene copolymer in advance using a melt kneader such as a twin-screw extruder, and the masterbatch is obtained as an ethylene copolymer. And a method of melting and kneading together with an organic peroxide at a low temperature to form a sheet. However, even with the above-described method, there are problems in that the number of master batch steps increases, resulting in an increase in cost due to material loss and deterioration of the ethylene-based copolymer itself due to an increase in thermal history.

特開２００６−１８６２３３号公報JP 2006-186233 A

本発明は、このような事情に照らし、有機過酸化物が実質的に分解しない成形温度で、成形温度よりも高い融点を有する有機化合物添加剤をエチレン系共重合体に均一に分散された太陽電池用組成物およびその製造方法を提供することを目的とする。   In light of such circumstances, the present invention is a solar in which an organic compound additive having a melting point higher than the molding temperature is uniformly dispersed in an ethylene copolymer at a molding temperature at which the organic peroxide is not substantially decomposed. It aims at providing the composition for batteries, and its manufacturing method.

また、本発明は、成形温度よりも高い融点を有する有機化合物添加剤がエチレン系共重合体に均一に分散された太陽電池用封止材層、および、それを用いた太陽電池モジュールを提供することを目的とする。   The present invention also provides a solar cell encapsulant layer in which an organic compound additive having a melting point higher than the molding temperature is uniformly dispersed in an ethylene copolymer, and a solar cell module using the same. For the purpose.

本発明者らは、上記課題を解決するため鋭意検討した結果、以下に示す太陽電池用封止材組成物およびその製造方法、ならびに、それを用いた太陽電池用封止材層および太陽電池モジュールにより上記目的を達成できることを見出して、本発明を完成するに至った。   As a result of intensive studies to solve the above-mentioned problems, the present inventors have found the following solar cell encapsulant composition and method for producing the same, and solar cell encapsulant layer and solar cell module using the same. Thus, the inventors have found that the above object can be achieved, and have completed the present invention.

本発明の太陽電池用封止材組成物の製造方法は、エチレン系共重合体（Ａ）および有機化合物添加剤（Ｂ）を含む太陽電池用封止材組成物の製造方法であって、
上記エチレン系共重合体（Ａ）のビカット軟化点以上、上記エチレン系共重合体（Ａ）の融点より１０℃低い温度以下の温度範囲内で、上記エチレン系共重合体（Ａ）および上記有機化合物添加剤（Ｂ）を混合するブレンド工程を含むことを特徴とする。 The manufacturing method of the sealing material composition for solar cells of this invention is a manufacturing method of the sealing material composition for solar cells containing an ethylene-type copolymer (A) and an organic compound additive (B),
The ethylene copolymer (A) and the organic polymer are within a temperature range from the Vicat softening point of the ethylene copolymer (A) to 10 ° C. below the melting point of the ethylene copolymer (A). A blending step of mixing the compound additive (B) is included.

本発明の太陽電池用封止材組成物の製造方法を用いることにより、有機過酸化物が実質的に分解しない成形温度で、成形温度よりも高い融点を有する有機化合物添加剤をエチレン系共重合体に均一に分散させることが可能となる。また、液状添加剤を含む場合であっても、樹脂内部に含浸や分散する等により樹脂表面に液体成分が残ることなく、またブロッキングしない樹脂組成物を容易に得ることができる。   By using the method for producing a solar cell encapsulant composition of the present invention, an organic compound additive having a melting point higher than the molding temperature at an molding temperature at which the organic peroxide is not substantially decomposed is ethylene-based. It becomes possible to disperse uniformly in the coalescence. Further, even when a liquid additive is contained, a resin composition that does not block and that does not block the liquid component does not remain on the resin surface due to impregnation or dispersion inside the resin.

本発明では、上記温度範囲で撹拌混合することで、高融点の有機化合物の分散状態が良くなる。一方、上記ビカット軟化点以下で行うと、高融点化合物が（特にペレット状の場合に）樹脂に付着しにくくなり、また上記融点より１０℃低い温度以下ではない場合には、樹脂同士がブロッキングしてしまう。より詳細には、従来のように上記ブレンド工程（プレブレンド）時に温度制御を行わずに長時間ブレンドを行うと、ペレットと回転羽との摩擦やペレット同士の摩擦等により内部温度が上昇してしまい、樹脂同士がブロッキングしてしまう恐れがある。一方、本願発明における上記温度範囲内でプレブレンドを行うことにより、上記問題を効果的に回避することができる。   In the present invention, the dispersion state of the organic compound having a high melting point is improved by stirring and mixing in the above temperature range. On the other hand, when the temperature is below the Vicat softening point, the high melting point compound is difficult to adhere to the resin (particularly in the case of pellets), and when the temperature is not lower than 10 ° C. below the melting point, the resins block each other. End up. More specifically, when blending for a long time without controlling the temperature during the blending step (pre-blending) as in the past, the internal temperature increases due to friction between the pellets and rotating blades, friction between the pellets, and the like. Therefore, the resins may be blocked. On the other hand, by performing pre-blending within the above temperature range in the present invention, the above problem can be effectively avoided.

本発明の太陽電池用封止材組成物の製造方法において、上記エチレン系共重合体（Ａ）がペレット状であることが好ましい。上記製造方法を用いることにより、一般に粉状よりも添加剤を混合・分散しにくいペレット状のエチレン系共重合体であっても、得られる太陽電池用封止材層のマトリックス樹脂であるエチレン系共重合体に均一に分散させることが可能となる。また、ペレットを用いることが可能となり、太陽電池用封止材組成物の生産加工性が向上する。   In the manufacturing method of the sealing material composition for solar cells of this invention, it is preferable that the said ethylene-type copolymer (A) is a pellet form. By using the above-described production method, an ethylene-based resin that is a matrix resin for a solar cell encapsulant layer, even if it is a pellet-shaped ethylene copolymer that is generally less likely to mix and disperse additives than powder. It becomes possible to disperse uniformly in the copolymer. Moreover, it becomes possible to use a pellet and the production workability of the solar cell sealing material composition is improved.

なお、上記ペレット状とは、主に加工性向上のために、たとえば、直径または長さが１〜１０ｍｍ程度の粒子状にしたものをいい、たとえば、略円柱状、略球状、略円盤状、略三角柱状、略四角柱状、略多面体状、楕円球状などの形態の粒体などをあげることができる。   In addition, the said pellet form means what was made into the particle form whose diameter or length is about 1-10 mm, mainly for workability improvement, for example, a substantially cylindrical shape, a substantially spherical shape, a substantially disk shape, Examples thereof include grains having a substantially triangular prism shape, a substantially quadrangular prism shape, a substantially polyhedral shape, an elliptical spherical shape, and the like.

また、本発明の太陽電池用封止材組成物の製造方法において、上記ブレンド工程において、さらに有機過酸化物（Ｃ）を含み、かつ、上記有機化合物添加剤（Ｂ）の融点が、上記有機過酸化物（Ｃ）の一時間半減期温度より１０℃低い温度以上であることが好ましい。本発明の製造方法を用いることにより、通常均一な分散が困難である、上記有機過酸化物（Ｃ）の一時間半減期温度付近またはより高い融点を持つ上記有機化合物添加剤（Ｂ）であっても、有機過酸化物が実質的に分解させずに、上記有機化合物添加剤（Ｂ）をエチレン系共重合体に均一に分散させることが可能となる。   Moreover, in the manufacturing method of the sealing material composition for solar cells of this invention, in the said blending process, the organic peroxide (C) is further included, and melting | fusing point of the said organic compound additive (B) is said organic The temperature is preferably 10 ° C. or more lower than the one-hour half-life temperature of the peroxide (C). By using the production method of the present invention, the organic compound additive (B) having a melting point near or higher than the one-hour half-life temperature of the organic peroxide (C), which is usually difficult to disperse uniformly. However, the organic compound additive (B) can be uniformly dispersed in the ethylene copolymer without substantially decomposing the organic peroxide.

また、本発明の太陽電池用封止材組成物の製造方法において、上記ブレンド工程において、溶剤を用いないことが好ましい。上記製造方法においては、液状添加剤などの太陽電池用封止材組成物の構成成分以外には別途溶剤を用いることなく（ドライプロセス）、有機過酸化物が実質的に分解しない成形温度で、成形温度よりも高い融点を有する有機化合物添加剤をエチレン系共重合体に均一に分散させることが可能となる。   Moreover, in the manufacturing method of the sealing material composition for solar cells of this invention, it is preferable not to use a solvent in the said blending process. In the above production method, without using a separate solvent other than the components of the solar cell encapsulant composition such as a liquid additive (dry process), at a molding temperature at which the organic peroxide is not substantially decomposed, An organic compound additive having a melting point higher than the molding temperature can be uniformly dispersed in the ethylene-based copolymer.

また、本発明の太陽電池用封止材組成物の製造方法において、上記ブレンド工程において、さらに液状添加剤を含むことができる。上記製造方法においては、シランカップリング剤や液状の架橋助剤などの液状添加剤を含む場合であっても、樹脂内部に含浸や分散する等により樹脂表面に液体成分が残ることなく、またブロッキングしない樹脂組成物を得ることができる。簡易にマスターバッチを作製することもできる。なお、上記液状添加剤とは、ブレンド工程時に液状である添加剤をいい、ブレンド工程時の温度よりも融点が低い化合物が該当する。   Moreover, in the manufacturing method of the sealing material composition for solar cells of this invention, a liquid additive can be further included in the said blending process. In the above production method, even when a liquid additive such as a silane coupling agent or a liquid crosslinking aid is contained, liquid components do not remain on the resin surface due to impregnation or dispersion inside the resin, and blocking is also possible. Can be obtained. A master batch can also be easily produced. In addition, the said liquid additive means the additive which is liquid at the time of a blending process, and the compound whose melting | fusing point is lower than the temperature at the time of a blending process corresponds.

また、本発明の太陽電池用封止材組成物の製造方法において、上記ブレンド工程に次いで、溶融混練工程を含むことが好ましい。上記ブレンド工程を先に経由するより、溶融混練工程後に成形温度よりも高い融点を有する有機化合物添加剤をエチレン系共重合体に均一に分散された太陽電池用組成物を容易に得ることができる。さらには、上記ブレンド工程を先に経由することで、通常より低温の溶融混練工程であっても、高融点の有機化合物の分散性が良いシートを形成することができる。   Moreover, in the manufacturing method of the sealing material composition for solar cells of this invention, it is preferable that a melt-kneading process is included after the said blending process. A composition for a solar cell in which an organic compound additive having a melting point higher than the molding temperature after the melt-kneading step is uniformly dispersed in the ethylene copolymer can be easily obtained, rather than going through the blending step first. . Furthermore, by passing through the blending process first, a sheet having a high dispersibility of the organic compound having a high melting point can be formed even in a melt-kneading process at a temperature lower than usual.

また、本発明の太陽電池用封止材組成物の製造方法において、上記溶融混練工程が、一軸押出機、二軸押出機、バンバリーミキサー、ニーダー、またはミキシングロールによりなされることが好ましい。上記構成を用いることにより、より効果的に、有機化合物添加剤をエチレン系共重合体に均一に分散された上記太陽電池用組成物を得ることができる。また、シートの成形は（封止材層の形成）は、カレンダー成形、Ｔダイ、またはインフレーション等による溶融押出成形によりなされることが好ましい。   Moreover, in the manufacturing method of the sealing material composition for solar cells of this invention, it is preferable that the said melt-kneading process is made | formed with a single screw extruder, a twin screw extruder, a Banbury mixer, a kneader, or a mixing roll. By using the said structure, the said composition for solar cells in which the organic compound additive was uniformly disperse | distributed to the ethylene-type copolymer can be obtained more effectively. Moreover, it is preferable that the sheet is formed (formation of the sealing material layer) by calendar extrusion, T-die, or melt extrusion by inflation.

また、本発明の太陽電池用封止材組成物の製造方法において、上記有機化合物添加剤（Ｂ）が、紫外線吸収剤、酸化防止剤、光安定化剤、老化防止剤、または、固形の架橋助剤であることが好ましい。上記化合物を用いることにより、上記組成物により形成される太陽電池用封止材層をより多機能にすることができる。   Moreover, in the manufacturing method of the sealing material composition for solar cells of this invention, the said organic compound additive (B) is a ultraviolet absorber, antioxidant, light stabilizer, anti-aging agent, or solid bridge | crosslinking. An auxiliary is preferred. By using the said compound, the sealing material layer for solar cells formed with the said composition can be made more multifunctional.

また、本発明の太陽電池用封止材組成物において、上記エチレン系共重合体が、エチレン−酢酸ビニル共重合体を主成分とすることが好ましい。上記エチレン系共重合体としてエチレン−酢酸ビニル共重合体を主成分とすることにより、より確実に光透過性や耐久性に優れた太陽電池用封止材層を得ることができる。   Moreover, in the solar cell encapsulant composition of the present invention, it is preferable that the ethylene copolymer contains an ethylene-vinyl acetate copolymer as a main component. By using an ethylene-vinyl acetate copolymer as a main component as the ethylene copolymer, a solar cell encapsulant layer excellent in light transmission and durability can be obtained more reliably.

なお、上記主成分とするとは、上記太陽電池用封止材組成物のマトリックス樹脂が複数の樹脂の混合物である場合、重量比で５０重量％以上含む場合をいうものとする。上記重量比は、７０重量％以上であることがより好ましく、９０重量％以上であることがさらに好ましい。   In addition, the said main component shall mean the case where 50 weight% or more is contained by weight ratio, when the matrix resin of the said solar cell sealing material composition is a mixture of several resin. The weight ratio is more preferably 70% by weight or more, and still more preferably 90% by weight or more.

一方、本発明の太陽電池用封止材層は、上記太陽電池用封止材組成物を用いて形成されたことを特徴とする。上記組成物を用いて形成されることにより、成形温度よりも高い融点を有する有機化合物添加剤がエチレン系共重合体に均一に分散された太陽電池用封止材層となる。   On the other hand, the solar cell encapsulant layer of the present invention is formed using the above solar cell encapsulant composition. By forming using the said composition, it becomes the sealing material layer for solar cells in which the organic compound additive which has melting | fusing point higher than molding temperature was disperse | distributed uniformly in the ethylene-type copolymer.

また、本発明の太陽電池モジュールは、上記太陽電池用封止材組成物を用いて形成された太陽電池用封止材層を含むことを特徴とする。上記太陽電池モジュールは、上記太陽電池用封止材層を有するため、成形温度よりも高い融点を有する有機化合物添加剤がエチレン系共重合体に均一に分散された太陽電池モジュールとなる。   Moreover, the solar cell module of this invention is characterized by including the solar cell sealing material layer formed using the said solar cell sealing material composition. Since the said solar cell module has the said solar cell sealing material layer, it becomes a solar cell module by which the organic compound additive which has melting | fusing point higher than molding temperature was uniformly disperse | distributed to the ethylene-type copolymer.

また、本発明の太陽電池モジュールにおいて、上記太陽電池セルが、結晶シリコン太陽電池、硫化カドミウム／テルル化カドミウム太陽電池、銅インジウムガリウム二セレン化物太陽電池、非晶質シリコン太陽電池、または微結晶シリコン太陽電池であることが好ましい。上記太陽電池モジュールは、上記太陽電池セルを積層する太陽電池モジュールに用いることでより効果的に光電変換効率をより向上させることができる。   Further, in the solar cell module of the present invention, the solar cell is a crystalline silicon solar cell, a cadmium sulfide / cadmium telluride solar cell, a copper indium gallium diselenide solar cell, an amorphous silicon solar cell, or a microcrystalline silicon. A solar cell is preferred. The said solar cell module can improve photoelectric conversion efficiency more effectively by using it for the solar cell module which laminates | stacks the said photovoltaic cell.

本発明の太陽電池用封止材層を用いた太陽電池モジュールの例を示す。The example of the solar cell module using the sealing material layer for solar cells of this invention is shown. 本発明の太陽電池用封止材層を用いた太陽電池モジュールの例を示す。The example of the solar cell module using the sealing material layer for solar cells of this invention is shown.

以下、本発明の実施の形態について説明する。   Embodiments of the present invention will be described below.

本発明の太陽電池用封止材組成物の製造方法は、エチレン系共重合体（Ａ）および有機化合物添加剤（Ｂ）を含む太陽電池用封止材組成物の製造方法であって、
上記エチレン系共重合体（Ａ）のビカット軟化点以上、上記エチレン系共重合体（Ａ）の融点より１０℃低い温度以下の温度範囲内で、上記エチレン系共重合体（Ａ）および上記有機化合物添加剤（Ｂ）を混合するブレンド工程を含むことを特徴とする。 The manufacturing method of the sealing material composition for solar cells of this invention is a manufacturing method of the sealing material composition for solar cells containing an ethylene-type copolymer (A) and an organic compound additive (B),
The ethylene copolymer (A) and the organic polymer are within a temperature range from the Vicat softening point of the ethylene copolymer (A) to 10 ° C. below the melting point of the ethylene copolymer (A). A blending step of mixing the compound additive (B) is included.

（太陽電池用封止材組成物）
本発明の太陽電池用封止材組成物は、少なくともエチレン系共重合体（Ａ）および有機化合物添加剤（Ｂ）を含むことを特徴とする。上記太陽電池用封止材組成物は、たとえば、エチレン系共重合体（Ａ）を主成分として含む、光学的に透明なマトリックス樹脂の中に、少なくとも有機化合物添加剤（Ｂ）を分散させること等により形成することができる。 (Encapsulant composition for solar cell)
The solar cell encapsulant composition of the present invention is characterized by containing at least an ethylene copolymer (A) and an organic compound additive (B). The solar cell encapsulant composition includes, for example, at least an organic compound additive (B) dispersed in an optically transparent matrix resin containing an ethylene copolymer (A) as a main component. Or the like.

上記エチレン系共重合体（Ａ）として、たとえば、エチレンと極性モノマーの共重合体、エチレンと炭素数３以上のα−オレフィンの共重合体などをあげることができる。   Examples of the ethylene copolymer (A) include a copolymer of ethylene and a polar monomer, and a copolymer of ethylene and an α-olefin having 3 or more carbon atoms.

上記エチレン系共重合体（Ａ）において、エチレン単位含有量が５０〜９０重量％であることが好ましく、６０〜８０重量％であることがより好ましく、６５〜７５重量％であることがさらに好ましい。上記含有量とすることにより、より確実に、柔軟性、透明性、成形性、耐ブロッキング性、太陽電池素子保護性に優れた太陽電池用封止材を得ることができる。   In the ethylene copolymer (A), the ethylene unit content is preferably 50 to 90% by weight, more preferably 60 to 80% by weight, and even more preferably 65 to 75% by weight. . By setting it as the said content, the sealing material for solar cells excellent in the softness | flexibility, transparency, a moldability, blocking resistance, and a solar cell element protective property can be obtained more reliably.

上記極性モノマーとして、たとえば、酢酸ビニル、プロピオン酸ビニルのようなビニルエステル、アクリル酸メチル、アクリル酸エチル、アクリル酸イソプロピル、アクリル酸イソブチル、アクリル酸ｎ−ブチル、アクリル酸イソオクチル、メタクリル酸メチル、メタクリル酸イソブチル、マレイン酸ジメチル等の不飽和カルボン酸エステル、アクリル酸、メタクリル酸、フマル酸、イタコン酸、マレイン酸モノメチル、マレイン酸モノエチル、無水マレイン酸、無水イタコン酸等の不飽和カルボン酸、および、これらのカルボン酸塩などの塩などをあげることができる。上記カルボン酸の塩として、たとえば、リチウム、ナトリウム、カリウムなどの１価金属、マグネシウム、カルシウム、亜鉛などの多価金属の塩などをあげることができる。これらは単独で使用してもよく、また２種以上を混合して使用してもよい。   Examples of the polar monomer include vinyl esters such as vinyl acetate and vinyl propionate, methyl acrylate, ethyl acrylate, isopropyl acrylate, isobutyl acrylate, n-butyl acrylate, isooctyl acrylate, methyl methacrylate, and methacrylic acid. Unsaturated carboxylic acid esters such as isobutyl acid, dimethyl maleate, acrylic acid, methacrylic acid, fumaric acid, itaconic acid, monomethyl maleate, monoethyl maleate, maleic anhydride, itaconic anhydride, and the like, and Examples of these salts include carboxylates. Examples of the carboxylic acid salt include monovalent metals such as lithium, sodium and potassium, and salts of polyvalent metals such as magnesium, calcium and zinc. These may be used singly or in combination of two or more.

上記炭素数３以上のα−オレフィンとして、たとえば、プロピレン、１−ブテン、２−ブテン、１−ヘキセン、１−オクテン、４−メチル−１−ペンテンなどをあげることができる。これらは単独で使用してもよく、また２種以上を混合して使用してもよい。   Examples of the α-olefin having 3 or more carbon atoms include propylene, 1-butene, 2-butene, 1-hexene, 1-octene, 4-methyl-1-pentene and the like. These may be used singly or in combination of two or more.

上記エチレン系共重合体（Ａ）として、たとえば、エチレン−酢酸ビニル共重合体のようなエチレン−ビニルエステル共重合体、エチレン−アクリル酸メチル共重合体、エチレン−アクリル酸エチル共重合体、エチレン−メタクリル酸メチル共重合体、エチレン−アクリル酸イソブチル共重合体、エチレン・アクリル酸ｎ−ブチル共重合体のようなエチレン−不飽和カルボン酸エステル共重合体、エチレン−アクリル酸共重合体、エチレン−メタクリル酸共重合体、エチレン・アクリル酸イソブチル−メタクリル酸共重合体のようなエチレン−不飽和カルボン酸共重合体およびそのアイオノマーなどをあげることができる。これらは単独で使用してもよく、また２種以上を混合して使用してもよい。   Examples of the ethylene copolymer (A) include ethylene-vinyl ester copolymers such as ethylene-vinyl acetate copolymers, ethylene-methyl acrylate copolymers, ethylene-ethyl acrylate copolymers, and ethylene. -Methyl methacrylate copolymer, ethylene-isobutyl acrylate copolymer, ethylene-unsaturated carboxylic acid ester copolymer such as ethylene / n-butyl acrylate copolymer, ethylene-acrylic acid copolymer, ethylene -Ethylene-unsaturated carboxylic acid copolymer such as methacrylic acid copolymer, ethylene / isobutyl acrylate-methacrylic acid copolymer and its ionomer. These may be used singly or in combination of two or more.

上記エチレン系共重合体（Ａ）として、エチレン−酢酸ビニル共重合体を主成分とすることが好ましい。上記エチレン系共重合体としてエチレン−酢酸ビニル共重合体を主成分とすることにより、より確実に光透過性や耐久性に優れた太陽電池用封止材層を得ることができる。   The ethylene-based copolymer (A) preferably contains an ethylene-vinyl acetate copolymer as a main component. By using an ethylene-vinyl acetate copolymer as a main component as the ethylene copolymer, a solar cell encapsulant layer excellent in light transmission and durability can be obtained more reliably.

上記エチレン−酢酸ビニル共重合体（Ａ）として、エチレン−酢酸ビニル共重合体１００重量部に対して、酢酸ビニル単量体単位の含有率が２０〜４０重量部であることが好ましく、２５〜３５重量部であることがより好ましく、上記含有率の場合には希土類錯体などのマトリックス樹脂中への均一分散性の観点から好ましい。   As said ethylene-vinyl acetate copolymer (A), it is preferable that the content rate of a vinyl acetate monomer unit is 20-40 weight part with respect to 100 weight part of ethylene-vinyl acetate copolymer. The content is more preferably 35 parts by weight, and the above content is preferable from the viewpoint of uniform dispersibility in a matrix resin such as a rare earth complex.

上記エチレン−酢酸ビニル共重合体（Ａ）を用いる場合には、市販品を適宜使用することができる。上記エチレン−酢酸ビニル共重合体の市販品として、たとえば、ウルトラセン（東ソー株式会社製）、エバフレックス（三井・デュポンポリケミカル株式会社製）、サンテックＥＶＡ（旭化成ケミカルズ社製）、ＵＢＥ ＥＶＡコポリマー（宇部丸善ポリエチレン社製）、エバテート（住友化学社製）、ノバテックＥＶＡ（日本ポリエチレン社製）、スミテート（住友化学社製）、ニポフレックス（東ソー社製）などをあげることができる。これらは単独で使用してもよく、また２種以上を混合して使用してもよい。   When using the said ethylene-vinyl acetate copolymer (A), a commercial item can be used suitably. Commercially available products of the ethylene-vinyl acetate copolymer include, for example, Ultrasen (manufactured by Tosoh Corporation), Everflex (manufactured by Mitsui DuPont Polychemical Co., Ltd.), Suntec EVA (manufactured by Asahi Kasei Chemicals Corporation), UBE EVA copolymer ( Ube Maruzen Polyethylene Co., Ltd.), Evertate (Sumitomo Chemical Co., Ltd.), Novatec EVA (Nihon Polyethylene Co., Ltd.), Smitate (Sumitomo Chemical Co., Ltd.), Nipoflex (Tosoh Corp.), and the like. These may be used singly or in combination of two or more.

上記エチレン−酢酸ビニル共重合体（Ａ）の屈折率として、たとえば、１．４〜１．７の範囲、１．４５〜１．６５の範囲、または、１．４５〜１．５５の範囲である。いくつかの実施形態において、エチレン−酢酸ビニル共重合体（Ａ）の屈折率が１．５である。   The refractive index of the ethylene-vinyl acetate copolymer (A) is, for example, in the range of 1.4 to 1.7, in the range of 1.45 to 1.65, or in the range of 1.45 to 1.55. is there. In some embodiments, the refractive index of the ethylene-vinyl acetate copolymer (A) is 1.5.

上記太陽電池用封止材組成物として、光学的に透明なマトリックス樹脂を用いることが好ましい。上記マトリックス樹脂として、上記エチレン系共重合体（Ａ）とともに、上記エチレン系共重合体（Ａ）の特性を損なわない限り、他のマトリックス樹脂を適宜用いてもよい。上記他のマトリックス樹脂として、たとえば、ポリエチレンテレフタレート、ポリ（メタ）アクリレート、ポリエチレンテトラフルオロエチレンなどのポリオレフィン類、ポリイミド、非晶質ポリカーボネート、シロキサンゾル−ゲル、ポリウレタン、ポリスチレン、ポリエーテルサルフォン、ポリアリレート、エポキシ樹脂、および、シリコーン樹脂などをあげることができる。これらのマトリックス樹脂は単独で使用してもよく、また２種以上を混合して使用してもよい。   As the solar cell encapsulant composition, an optically transparent matrix resin is preferably used. As said matrix resin, you may use suitably other matrix resin with the said ethylene-type copolymer (A), unless the characteristic of the said ethylene-type copolymer (A) is impaired. Examples of the other matrix resins include polyolefins such as polyethylene terephthalate, poly (meth) acrylate, polyethylene tetrafluoroethylene, polyimide, amorphous polycarbonate, siloxane sol-gel, polyurethane, polystyrene, polyethersulfone, polyarylate And epoxy resins and silicone resins. These matrix resins may be used alone or in admixture of two or more.

上記マトリックス樹脂（上記エチレン系共重合体（Ａ）のみ、または他のマトリックス樹脂との併用）において、架橋性モノマーを加えて、架橋構造を有する樹脂としてもよい。   In the matrix resin (the ethylene copolymer (A) alone or in combination with another matrix resin), a crosslinkable monomer may be added to form a resin having a crosslinked structure.

上記架橋性モノマーとして、たとえば、ジシクロペンテニル（メタ）アクリレート、テトラヒドロフルフリル（メタ）アクリレート、ベンジル（メタ）アクリレート、多価アルコールにα，β−不飽和カルボン酸を反応させて得られる化合物（たとえば、ポリエチレングリコールジ（メタ）アクリレート（エチレン基の数が２〜１４のもの）、トリメチロールプロパンジ（メタ）アクリレート、トリメチロールプロパントリ（メタ）アクリレート、トリメチロールプロパンエトキシトリ（メタ）アクリレート、トリメチロールプロパンプロポキシトリ（メタ）アクリレート、テトラメチロールメタントリ（メタ）アクリレート、テトラメチロールメタンテトラ（メタ）アクリレート、ポリプロピレングリコールジ（メタ）アクリレート（プロピレン基の数が２〜１４のもの）、ジペンタエリスリトールペンタ（メタ）アクリレート、ジペンタエリスリトールヘキサ（メタ）アクリレート、ビスフェノールＡポリオキシエチレンジ（メタ）アクリレート、ビスフェノールＡジオキシエチレンジ（メタ）アクリレート、ビスフェノールＡトリオキシエチレンジ（メタ）アクリレート、ビスフェノールＡデカオキシエチレンジ（メタ）アクリレート等）、グリシジル基含有化合物にα，β−不飽和カルボン酸を付加して得られる化合物（たとえば、トリメチロールプロパントリグリシジルエーテルトリアクリレート、ビスフェノールＡジグリシジルエーテルジアクリレート等）、多価カルボン酸（たとえば、無水フタル酸）と水酸基およびエチレン性不飽和基を有する物質（たとえば、β−ヒドロキシエチル（メタ）アクリレート）とのエステル化物、アクリル酸若しくはメタクリル酸のアルキルエステル（たとえば、（メタ）アクリル酸メチルエステル、（メタ）アクリル酸エチルエステル、（メタ）アクリル酸ブチルエステル、（メタ）アクリル酸２−エチルヘキシルエステル）、ウレタン（メタ）アクリレート（たとえば、トリレンジイソシアネートと２−ヒドロキシエチル（メタ）アクリル酸エステルとの反応物、トリメチルヘキサメチレンジイソシアネートとシクロヘキサンジメタノールと２−ヒドロキシエチル（メタ）アクリル酸エステルとの反応物等）、などをあげることができる。これらの架橋性モノマーは単独で使用してもよく、また２種以上を混合して使用してもよい。なかでも、上記架橋性モノマーにおいて、トリメチロールプロパントリ（メタ）アクリレート、ジペンタエリスリトールテトラ（メタ）アクリレート、ジペンタエリスリトールヘキサ（メタ）アクリレート、ビスフェノールＡポリオキシエチレンジメタクリレートが好ましいものとしてあげられる。   Examples of the crosslinkable monomer include compounds obtained by reacting α, β-unsaturated carboxylic acid with dicyclopentenyl (meth) acrylate, tetrahydrofurfuryl (meth) acrylate, benzyl (meth) acrylate, and polyhydric alcohol ( For example, polyethylene glycol di (meth) acrylate (having 2 to 14 ethylene groups), trimethylolpropane di (meth) acrylate, trimethylolpropane tri (meth) acrylate, trimethylolpropane ethoxytri (meth) acrylate, Trimethylolpropane propoxytri (meth) acrylate, tetramethylolmethane tri (meth) acrylate, tetramethylolmethane tetra (meth) acrylate, polypropylene glycol di (meth) acrylate (propiol Having 2 to 14 ren groups), dipentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) acrylate, bisphenol A polyoxyethylene di (meth) acrylate, bisphenol A dioxyethylene di (meth) Acrylate, bisphenol A trioxyethylene di (meth) acrylate, bisphenol A decaoxyethylene di (meth) acrylate, etc.), a compound obtained by adding an α, β-unsaturated carboxylic acid to a glycidyl group-containing compound (for example, tri Methylolpropane triglycidyl ether triacrylate, bisphenol A diglycidyl ether diacrylate, etc.), polyvalent carboxylic acid (for example, phthalic anhydride), a substance having a hydroxyl group and an ethylenically unsaturated group (for example, β-hydroxy Roxyethyl (meth) acrylate) esterified product, alkyl ester of acrylic acid or methacrylic acid (for example, (meth) acrylic acid methyl ester, (meth) acrylic acid ethyl ester, (meth) acrylic acid butyl ester, (meth) acrylic Acid 2-ethylhexyl ester), urethane (meth) acrylate (for example, reaction product of tolylene diisocyanate and 2-hydroxyethyl (meth) acrylic acid ester, trimethylhexamethylene diisocyanate, cyclohexanedimethanol and 2-hydroxyethyl (meth) A reaction product with an acrylate ester, etc.). These crosslinkable monomers may be used alone or in admixture of two or more. Of these, trimethylolpropane tri (meth) acrylate, dipentaerythritol tetra (meth) acrylate, dipentaerythritol hexa (meth) acrylate, and bisphenol A polyoxyethylene dimethacrylate are preferred as the crosslinkable monomer.

上記架橋性モノマーを含むマトリックス樹脂を用いる場合、たとえば、上記架橋モノマーに熱重合開始剤または光重合開始剤を加えて、加熱または光照射によって重合・架橋させ架橋構造を形成することができる。   When the matrix resin containing the crosslinkable monomer is used, for example, a thermal polymerization initiator or a photopolymerization initiator is added to the crosslinkable monomer, and polymerization and crosslinking can be performed by heating or light irradiation to form a crosslinked structure.

上記熱重合開始剤として、公知の過酸化物を適宜用いることができる。上記熱可塑性樹脂重合開始剤としては、たとえば、２，５−ジメチルヘキサン−２，５−ジハイドロパーオキサイド、２，５−ジメチル−２，５−ジ（ｔ−ブチルパーオキシ）ヘキサン−３、ジ−ｔ−ブチルパーオキサイド、ジクミルパーオキサイド、２，５−ジメチル−２，５−ジ（ｔ−ブチルパーオキシ）ヘキサン、ジクミルパーオキサイド、α，α’−ビス（ｔ−ブチルパーオキシイソプロピル）ベンゼン、ｎ−ブチル−４，４−ビス（ｔ−ブチルパーオキシ）ブタン、２，２−ビス（ｔ−ブチルパーオキシ）ブタン、１，１−ビス（ｔ−ブチルパーオキシ）シクロヘキサン、１，１−ビス（ｔ−ブチルパーオキシ）３，３，５−トリメチルシクロヘキサン、ｔ−ブチルパーオキシベンズエート、ベンゾイルパーオキサイドなどをあげることができる。これらの化合物は単独で使用してもよく、また２種以上を混合して使用してもよい。   A known peroxide can be appropriately used as the thermal polymerization initiator. Examples of the thermoplastic resin polymerization initiator include 2,5-dimethylhexane-2,5-dihydroperoxide, 2,5-dimethyl-2,5-di (t-butylperoxy) hexane-3, Di-t-butyl peroxide, dicumyl peroxide, 2,5-dimethyl-2,5-di (t-butylperoxy) hexane, dicumyl peroxide, α, α'-bis (t-butylperoxy) Isopropyl) benzene, n-butyl-4,4-bis (t-butylperoxy) butane, 2,2-bis (t-butylperoxy) butane, 1,1-bis (t-butylperoxy) cyclohexane, 1,1-bis (t-butylperoxy) 3,3,5-trimethylcyclohexane, t-butylperoxybenzate, benzoyl peroxide, etc. be able to. These compounds may be used alone or in combination of two or more.

上記熱重合開始剤の配合量は、たとえば、上記マトリックス樹脂１００重量部に対して、０．１〜２重量部用いることができる。   The blending amount of the thermal polymerization initiator can be 0.1 to 2 parts by weight with respect to 100 parts by weight of the matrix resin, for example.

上記光重合開始剤としては、紫外線または可視光線により遊離ラジカルを生成する公知の光開始剤を適宜用いることができる。上記光重合開始剤として、たとえば、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインプロピルエーテル、ベンゾインイソブチルエーテル、ベンゾインフェニルエーテルなどのベンゾインエーテル類、ベンゾフェノン、Ｎ，Ｎ’−テトラメチル−４，４’−ジアミノベンゾフェノン（ミヒラーケトン）、Ｎ，Ｎ’−テトラエチル−４，４’−ジアミノベンゾフェノンなどのベンゾフェノン類、ベンジルジメチルケタール（チバ・ジャパン・ケミカルズ社製、イルガキュア６５１）、ベンジルジエチルケタールなどのベンジルケタール類、２，２−ジメトキシ−２−フェニルアセトフェノン、ｐ−ｔｅｒｔ−ブチルジクロロアセトフェノン、ｐ−ジメチルアミノアセトフェノンなどのアセトフェノン類、２，４−ジメチルチオキサントン、２，４−ジイソプロピルチオキサントンなどのキサントン類、あるいはヒドロキシシクロヘキシルフェニルケトン（チバ・スペシャルティ・ケミカルズ社製、イルガキュア１８４）、１−（４−イソプロピルフェニル）−２−ビトロキシ−２−メチルプロパン−１−オン（チバ・ジャパン・ケミカルズ社製、ダロキュア１１１６）、２−ヒドロキシ−２−メチル−１−フェニルプロパン−１−オン（メルク社製、ダロキュア１１７３）などをあげることができる。これらは単独で使用してもよく、また２種以上を混合して使用してもよい。   As said photoinitiator, the well-known photoinitiator which produces | generates a free radical by an ultraviolet-ray or visible light can be used suitably. Examples of the photopolymerization initiator include benzoin ethers such as benzoin methyl ether, benzoin ethyl ether, benzoin propyl ether, benzoin isobutyl ether, and benzoin phenyl ether, benzophenone, N, N′-tetramethyl-4,4′-diamino, and the like. Benzophenones (Michler ketone), benzophenones such as N, N′-tetraethyl-4,4′-diaminobenzophenone, benzyl ketals such as benzyldimethyl ketal (manufactured by Ciba Japan Chemicals, Irgacure 651), benzyl diethyl ketal, 2 , 2-dimethoxy-2-phenylacetophenone, p-tert-butyldichloroacetophenone, acetophenones such as p-dimethylaminoacetophenone, 2,4-dimethylthio Xanthones such as xanthone and 2,4-diisopropylthioxanthone, or hydroxycyclohexyl phenyl ketone (manufactured by Ciba Specialty Chemicals, Irgacure 184), 1- (4-isopropylphenyl) -2-vitoxy-2-methylpropane-1 -On (Ciba Japan Chemicals, Darocur 1116), 2-hydroxy-2-methyl-1-phenylpropan-1-one (Merck, Darocur 1173) and the like can be mentioned. These may be used singly or in combination of two or more.

また、上記光重合開始剤として、たとえば、２，４，５−トリアリルイミダゾール二量体と２−メルカプトベンゾオキサゾール、ロイコクリスタルバイオレット、トリス（４−ジエチルアミノ−２−メチルフェニル）メタン等との組み合わせなどをあげることができる。また、たとえば、ベンゾフェノンに対するトリエタノールアミン等の三級アミンのように、適宜公知の添加剤を用いてもよい。   Further, as the photopolymerization initiator, for example, a combination of 2,4,5-triallylimidazole dimer and 2-mercaptobenzoxazole, leucocrystal violet, tris (4-diethylamino-2-methylphenyl) methane, etc. Etc. Further, for example, known additives may be used as appropriate, such as tertiary amines such as triethanolamine for benzophenone.

上記光重合開始剤の配合量は、たとえば、上記マトリックス樹脂１００重量部に対して、通常、０．１〜５重量部用いることができる。   The blending amount of the photopolymerization initiator is usually 0.1 to 5 parts by weight with respect to 100 parts by weight of the matrix resin, for example.

上記有機化合物添加剤（Ｂ）として、上記エチレン系共重合体（Ａ）の融点よりも高い融点をもつ有機化合物であることが好ましい。本願発明の製造方法を用いることにより、特に、成形温度よりも高い融点を有する有機化合物添加剤をエチレン系共重合体に均一に分散させることが可能になる。   The organic compound additive (B) is preferably an organic compound having a higher melting point than the melting point of the ethylene copolymer (A). By using the production method of the present invention, in particular, an organic compound additive having a melting point higher than the molding temperature can be uniformly dispersed in the ethylene copolymer.

上記有機化合物添加剤（Ｂ）として、たとえば、紫外線吸収剤、酸化防止剤、光安定剤、老化防止剤、または、固形の架橋助剤であることが好ましい。これらは単独で使用してもよく、また２種以上を混合して使用してもよい。   The organic compound additive (B) is preferably, for example, an ultraviolet absorber, an antioxidant, a light stabilizer, an antiaging agent, or a solid crosslinking aid. These may be used singly or in combination of two or more.

有機化合物添加剤（Ｂ）として、たとえば、融点が１００〜２５０℃であることが好ましく、１５０〜２００℃であることがより好ましく、１６０〜１８０℃であることがさらに好ましい。なお、上記融点の測定は、昇温過程（１０℃／分）における結晶状態から液体状態に転移する温度を観察しておこなうものとする。   As an organic compound additive (B), it is preferable that melting | fusing point is 100-250 degreeC, for example, it is more preferable that it is 150-200 degreeC, and it is further more preferable that it is 160-180 degreeC. The above melting point is measured by observing the temperature at which the crystalline state changes to the liquid state in the temperature raising process (10 ° C./min).

上記有機化合物添加剤（Ｂ）の含有量は、上記マトリックス樹脂１００重量部に対して０．０１〜１０重量部含有することが好ましく、０．０５〜５重量部であることがより好ましく、０．１〜１重量部であることがさらに好ましい。   The content of the organic compound additive (B) is preferably 0.01 to 10 parts by weight, more preferably 0.05 to 5 parts by weight, based on 100 parts by weight of the matrix resin. More preferably, it is 1-1 weight part.

上記紫外線吸収化合物として、公知のものを適宜用いることができる。上記紫外線吸収化合物として、たとえば、ベンゾフェノン系、ベンゾトリアゾール系、トリアジン系、サリチル酸系、シアノアクリレート系などをあげることができる。これらの化合物は単独で使用してもよく、また２種以上を混合して使用してもよい。   As the ultraviolet absorbing compound, known compounds can be appropriately used. Examples of the ultraviolet absorbing compound include benzophenone, benzotriazole, triazine, salicylic acid, and cyanoacrylate. These compounds may be used alone or in combination of two or more.

上記ベンゾフェノン系紫外線吸収化合物としては、たとえば、２，２’−ジヒドロキシ−４，４’−ジ（ヒドロキシメチル）ベンゾフェノン、２，２’−ジヒドロキシ−４，４’−ジ（２−ヒドロキシエチル）ベンゾフェノン、２，２’−ジヒドロキシ−３，３’−ジメトキシ−５，５’−ジ（ヒドロキシメチル）ベンゾフェノン、２，２’−ジヒドロキシ−３，３’−ジメトキシ−５，５’−ジ（２−ヒドロキシエチル）ベンゾフェノン、２，２’−ジヒドロキシ−３，３’−ジ（ヒドロキシメチル）−５，５’−ジメトキシベンゾフェノン、２，２’−ジヒドロキシ−３，３’−ジ（２−ヒドロキシエチル）−５，５’−ジメトキシベンゾフェノン、２，２−ジヒドロキシ−４，４−ジメトキシベンゾフェノンなどをあげることができる。   Examples of the benzophenone-based ultraviolet absorbing compound include 2,2′-dihydroxy-4,4′-di (hydroxymethyl) benzophenone and 2,2′-dihydroxy-4,4′-di (2-hydroxyethyl) benzophenone. 2,2′-dihydroxy-3,3′-dimethoxy-5,5′-di (hydroxymethyl) benzophenone, 2,2′-dihydroxy-3,3′-dimethoxy-5,5′-di (2- Hydroxyethyl) benzophenone, 2,2′-dihydroxy-3,3′-di (hydroxymethyl) -5,5′-dimethoxybenzophenone, 2,2′-dihydroxy-3,3′-di (2-hydroxyethyl) -5,5'-dimethoxybenzophenone, 2,2-dihydroxy-4,4-dimethoxybenzophenone and the like can be mentioned.

上記ベンゾトリアゾール系紫外線吸収化合物としては、たとえば、２−〔２’−ヒドロキシ−５’−（ヒドロキシメチル）フェニル〕−２Ｈ−ベンゾトリアゾール、２−〔２’−ヒドロキシ−５’−（２−ヒドロキシエチル）フェニル〕−２Ｈ−ベンゾトリアゾール、２−〔２’−ヒドロキシ−５’−（３−ヒドロキシプロピル）フェニル〕−２Ｈ−ベンゾトリアゾール、２−〔２’−ヒドロキシ−３’−メチル−５’−（ヒドロキシメチル）フェニル〕−２Ｈ−ベンゾトリアゾール、２−〔２’−ヒドロキシ−３’−メチル−５’−（２−ヒドロキシエチル）フェニル〕−２Ｈ−ベンゾトリアゾール、２−〔２’−ヒドロキシ−３’−メチル−５’−（３−ヒドロキシプロピル）フェニル〕−２Ｈ−ベンゾトリアゾール、２−〔２’−ヒドロキシ−３’−ｔ−ブチル−５’−（ヒドロキシメチル）フェニル〕−２Ｈ−ベンゾトリアゾール、２−〔２’−ヒドロキシ−３’−ｔ−ブチル−５’−（２−ヒドロキシエチル）フェニル〕−２Ｈ−ベンゾトリアゾール、２−〔２’−ヒドロキシ−３’−ｔ−ブチル−５’−（２−ヒドロキシエチル）フェニル〕−５−クロロ−２Ｈ−ベンゾトリアゾール、２−〔２’−ヒドロキシ−３’−ｔ−ブチル−５’−（３−ヒドロキシプロピル）フェニル〕−２Ｈ−ベンゾトリアゾール、２−〔２’−ヒドロキシ−３’−ｔ−オクチル−５’−（ヒドロキシメチル）フェニル〕−２Ｈ−ベンゾトリアゾール、２−〔２’−ヒドロキシ−３’−ｔ−オクチル−５’−（２−ヒドロキシエチル）フェニル〕−２Ｈ−ベンゾトリアゾール、２−〔２’−ヒドロキシ−３’−ｔ−オクチル−５’−（３−ヒドロキシプロピル）フェニル〕−２Ｈ−ベンゾトリアゾール等、あるいは２，２’−メチレンビス〔６−（２Ｈ−ベンゾトリアゾリ−２−イル）−４−（ヒドロキシメチル）フェノール〕、２，２’−メチレンビス〔６−（２Ｈ−ベンゾトリアゾリ−２−イル）−４−（２−ヒドロキシエチル）フェノール〕、２，２’−メチレンビス〔６−（５−クロロ−２Ｈ−ベンゾトリアゾリ−２−イル）−４−（２−ヒドロキシエチル）フェノール〕、２，２’−メチレンビス〔６−（５−ブロモ−２Ｈ−ベンゾトリアゾリ−２−イル）−４−（２−ヒドロキシエチル）フェノール〕、２，２’−メチレンビス〔６−（２Ｈ−ベンゾトリアゾリ−２−イル）−４−（３−ヒドロキシプロピル）フェノール〕、２，２’−メチレンビス〔６−（５−クロロ−２Ｈ−ベンゾトリアゾリ−２−イル）−４−（３−ヒドロキシプロピル）フェノール〕、２，２’−メチレンビス〔６−（５−ブロモ−２Ｈ−ベンゾトリアゾリ−２−イル）−４−（３−ヒドロキシプロピル）フェノール〕、２，２’−メチレンビス〔６−（２Ｈ−ベンゾトリアゾリ−２−イル）−４−（４−ヒドロキシブチル）フェノール〕、２，２’−メチレンビス〔６−（５−クロロ−２Ｈ−ベンゾトリアゾリ−２−イル）−４−（４−ヒドロキシブチル）フェノール〕、２，２’−メチレンビス〔６−（５−ブロモ−２Ｈ−ベンゾトリアゾリ−２−イル）−４−（４−ヒドロキシブチル）フェノール〕、３，３−｛２，２’−ビス〔６−（２Ｈ−ベンゾトリアゾリ−２−イル）−１−ヒドロキシ−４−（２−ヒドロキシエチル）フェニル〕｝プロパン、２，２−｛２，２’−ビス〔６−（２Ｈ−ベンゾトリアゾリ−２−イル）−１−ヒドロキシ−４−（２−ヒドロキシエチル）フェニル〕｝ブタン、２，２’−オキシビス〔６−（２Ｈ−ベンゾトリアゾリ−２−イル）−４−（２−ヒドロキシエチル）フェノール〕、２，２’−ビス〔６−（２Ｈ−ベンゾトリアゾリ−２−イル）−４−（２−ヒドロキシエチル）フェノール〕スルフィド、２，２’−ビス〔６−（２Ｈ−ベンゾトリアゾリ−２−イル）−４−（２−ヒドロキシエチル）フェノール〕スルホキシド、２，２’−ビス〔６−（２Ｈ−ベンゾトリアゾリ−２−イル）−４−（２−ヒドロキシエチル）フェノール〕スルホン、２，２’−ビス〔６−（２Ｈ−ベンゾトリアゾリ−２−イル）−４−（２−ヒドロキシエチル）フェノール〕アミンなどをあげることができる。   Examples of the benzotriazole ultraviolet absorbing compound include 2- [2′-hydroxy-5 ′-(hydroxymethyl) phenyl] -2H-benzotriazole, 2- [2′-hydroxy-5 ′-(2-hydroxy). Ethyl) phenyl] -2H-benzotriazole, 2- [2′-hydroxy-5 ′-(3-hydroxypropyl) phenyl] -2H-benzotriazole, 2- [2′-hydroxy-3′-methyl-5 ′ -(Hydroxymethyl) phenyl] -2H-benzotriazole, 2- [2'-hydroxy-3'-methyl-5 '-(2-hydroxyethyl) phenyl] -2H-benzotriazole, 2- [2'-hydroxy -3'-methyl-5 '-(3-hydroxypropyl) phenyl] -2H-benzotriazole, 2- [2'-hydride Xy-3'-t-butyl-5 '-(hydroxymethyl) phenyl] -2H-benzotriazole, 2- [2'-hydroxy-3'-t-butyl-5'-(2-hydroxyethyl) phenyl] -2H-benzotriazole, 2- [2'-hydroxy-3'-t-butyl-5 '-(2-hydroxyethyl) phenyl] -5-chloro-2H-benzotriazole, 2- [2'-hydroxy- 3′-t-butyl-5 ′-(3-hydroxypropyl) phenyl] -2H-benzotriazole, 2- [2′-hydroxy-3′-t-octyl-5 ′-(hydroxymethyl) phenyl] -2H -Benzotriazole, 2- [2'-hydroxy-3'-t-octyl-5 '-(2-hydroxyethyl) phenyl] -2H-benzotriazole, 2- [2'- Droxy-3′-t-octyl-5 ′-(3-hydroxypropyl) phenyl] -2H-benzotriazole or the like, or 2,2′-methylenebis [6- (2H-benzotriazoly-2-yl) -4- ( Hydroxymethyl) phenol], 2,2'-methylenebis [6- (2H-benzotriazoly-2-yl) -4- (2-hydroxyethyl) phenol], 2,2'-methylenebis [6- (5-chloro- 2H-benzotriazoly-2-yl) -4- (2-hydroxyethyl) phenol], 2,2′-methylenebis [6- (5-bromo-2H-benzotriazoly-2-yl) -4- (2-hydroxyethyl) ) Phenol], 2,2'-methylenebis [6- (2H-benzotriazoly-2-yl) -4- (3-hydroxypropyl) pheno 2,2′-methylenebis [6- (5-chloro-2H-benzotriazoly-2-yl) -4- (3-hydroxypropyl) phenol], 2,2′-methylenebis [6- (5-bromo) -2H-benzotriazoly-2-yl) -4- (3-hydroxypropyl) phenol], 2,2'-methylenebis [6- (2H-benzotriazoly-2-yl) -4- (4-hydroxybutyl) phenol] 2,2′-methylenebis [6- (5-chloro-2H-benzotriazoly-2-yl) -4- (4-hydroxybutyl) phenol], 2,2′-methylenebis [6- (5-bromo-2H -Benzotriazoly-2-yl) -4- (4-hydroxybutyl) phenol], 3,3- {2,2'-bis [6- (2H-benzotriazoly-2-yl)- -Hydroxy-4- (2-hydroxyethyl) phenyl]} propane, 2,2- {2,2'-bis [6- (2H-benzotriazoli-2-yl) -1-hydroxy-4- (2-hydroxy) Ethyl) phenyl]} butane, 2,2′-oxybis [6- (2H-benzotriazoly-2-yl) -4- (2-hydroxyethyl) phenol], 2,2′-bis [6- (2H-benzotriazolyl) -2-yl) -4- (2-hydroxyethyl) phenol] sulfide, 2,2′-bis [6- (2H-benzotriazoly-2-yl) -4- (2-hydroxyethyl) phenol] sulfoxide, 2 2,2'-bis [6- (2H-benzotriazoly-2-yl) -4- (2-hydroxyethyl) phenol] sulfone, 2,2'-bis [6- (2H-ben Toriazori 2-yl), etc. -4- (2-hydroxyethyl) phenol] amine can be exemplified.

上記トリアジン系紫外線吸収化合物としては、たとえば、２−（２−ヒドロキシ−４−ヒドロキシメチルフェニル）−４，６−ジフェニル−ｓ−トリアジン、２−（２−ヒドロキシ−４−ヒドロキシメチルフェニル）−４，６−ビス（２，４−ジメチルフェニル）−ｓ−トリアジン、２−〔２−ヒドロキシ−４−（２−ヒドロキシエチル）フェニル〕−４，６−ジフェニル−ｓ−トリアジン、２−〔２−ヒドロキシ−４−（２−ヒドロキシエチル）フェニル〕−４，６−ビス（２，４−ジメチルフェニル）−ｓ−トリアジン、２−〔２−ヒドロキシ−４−（２−ヒドロキシエトキシ）フェニル〕−４，６−ジフェニル−ｓ−トリアジン、２−〔２−ヒドロキシ−４−（２−ヒドロキシエトキシ）フェニル〕−４，６−ビス（２，４−ジメチルフェニル）−ｓ−トリアジン、２−〔２−ヒドロキシ−４−（３−ヒドロキシプロピル）フェニル〕−４，６−ジフェニル−ｓ−トリアジン、２−〔２−ヒドロキシ−４−（３−ヒドロキシプロピル）フェニル〕−４，６−ビス（２，４−ジメチルフェニル）−ｓ−トリアジン、２−〔２−ヒドロキシ−４−（３−ヒドロキシプロポキシ）フェニル〕−４，６−ジフェニル−ｓ−トリアジン、２−〔２−ヒドロキシ−４−（３−ヒドロキシプロポキシ）フェニル〕−４，６−ビス（２，４−ジメチルフェニル）−ｓ−トリアジン、２−〔２−ヒドロキシ−４−（４−ヒドロキシブチル）フェニル〕−４，６−ジフェニル−ｓ−トリアジン、２−〔２−ヒドロキシ−４−（４−ヒドロキシブチル）フェニル〕−４，６−ビス（２，４−ジメチルフェニル）−ｓ−トリアジン、２−〔２−ヒドロキシ−４−（４−ヒドロキシブトキシ）フェニル〕−４，６−ジフェニル−ｓ−トリアジン、２−〔２−ヒドロキシ−４−（４−ヒドロキシブトキシ）フェニル〕−４，６−ビス（２，４−ジメチルフェニル）−ｓ−トリアジン、２−（２−ヒドロキシ−４−ヒドロキシメチルフェニル）−４，６−ビス（２−ヒドロキシ−４−メチルフェニル）−ｓ−トリアジン、２−〔２−ヒドロキシ−４−（２−ヒドロキシエチル）フェニル〕−４，６−ビス（２−ヒドロキシ−４−メチルフェニル）−ｓ−トリアジン、２−〔２−ヒドロキシ−４−（２−ヒドロキシエトキシ）フェニル〕−４，６−ビス（２−ヒドロキシ−４−メチルフェニル）−ｓ−トリアジン、２−〔２−ヒドロキシ−４−（３−ヒドロキシプロピル）フェニル〕−４，６−ビス（２−ヒドロキシ−４−メチルフェニル）−ｓ−トリアジン、２−〔２−ヒドロキシ−４−（３−ヒドロキシプロポキシ）フェニル〕−４，６−ビス（２−ヒドロキシ−４−メチルフェニル）−ｓ−トリアジン、２−［４，６−ビス（２，４−ジメチルフェニル）−１，３，５−トリアジン−２−イル］−５−（オクチロキシ）フェノール、２−（４，６−ジフェニル−１，３，５−トリアジン−２−イル）−５−［（ヘキシル）オキシ］−フェノールなどをあげることができる。   Examples of the triazine-based ultraviolet absorbing compound include 2- (2-hydroxy-4-hydroxymethylphenyl) -4,6-diphenyl-s-triazine and 2- (2-hydroxy-4-hydroxymethylphenyl) -4. , 6-Bis (2,4-dimethylphenyl) -s-triazine, 2- [2-hydroxy-4- (2-hydroxyethyl) phenyl] -4,6-diphenyl-s-triazine, 2- [2- Hydroxy-4- (2-hydroxyethyl) phenyl] -4,6-bis (2,4-dimethylphenyl) -s-triazine, 2- [2-hydroxy-4- (2-hydroxyethoxy) phenyl] -4 , 6-Diphenyl-s-triazine, 2- [2-hydroxy-4- (2-hydroxyethoxy) phenyl] -4,6-bis (2,4-dimethyl) Enyl) -s-triazine, 2- [2-hydroxy-4- (3-hydroxypropyl) phenyl] -4,6-diphenyl-s-triazine, 2- [2-hydroxy-4- (3-hydroxypropyl) Phenyl] -4,6-bis (2,4-dimethylphenyl) -s-triazine, 2- [2-hydroxy-4- (3-hydroxypropoxy) phenyl] -4,6-diphenyl-s-triazine, 2 -[2-hydroxy-4- (3-hydroxypropoxy) phenyl] -4,6-bis (2,4-dimethylphenyl) -s-triazine, 2- [2-hydroxy-4- (4-hydroxybutyl) Phenyl] -4,6-diphenyl-s-triazine, 2- [2-hydroxy-4- (4-hydroxybutyl) phenyl] -4,6-bis (2,4-dimethyl) Enyl) -s-triazine, 2- [2-hydroxy-4- (4-hydroxybutoxy) phenyl] -4,6-diphenyl-s-triazine, 2- [2-hydroxy-4- (4-hydroxybutoxy) Phenyl] -4,6-bis (2,4-dimethylphenyl) -s-triazine, 2- (2-hydroxy-4-hydroxymethylphenyl) -4,6-bis (2-hydroxy-4-methylphenyl) -S-triazine, 2- [2-hydroxy-4- (2-hydroxyethyl) phenyl] -4,6-bis (2-hydroxy-4-methylphenyl) -s-triazine, 2- [2-hydroxy- 4- (2-hydroxyethoxy) phenyl] -4,6-bis (2-hydroxy-4-methylphenyl) -s-triazine, 2- [2-hydroxy-4- (3-H Droxypropyl) phenyl] -4,6-bis (2-hydroxy-4-methylphenyl) -s-triazine, 2- [2-hydroxy-4- (3-hydroxypropoxy) phenyl] -4,6-bis (2-hydroxy-4-methylphenyl) -s-triazine, 2- [4,6-bis (2,4-dimethylphenyl) -1,3,5-triazin-2-yl] -5- (octyloxy) Examples thereof include phenol and 2- (4,6-diphenyl-1,3,5-triazin-2-yl) -5-[(hexyl) oxy] -phenol.

上記サリチル酸系紫外線吸収化合物としては、たとえば、フェニルサリシレート、ｐ−ｔｅｒｔ−ブチルフェニルサリシレート、ｐ−オクチルフェニルサリシレートなどをあげることができる。   Examples of the salicylic acid-based ultraviolet absorbing compound include phenyl salicylate, p-tert-butylphenyl salicylate, p-octylphenyl salicylate, and the like.

上記シアノアクリレート系紫外線吸収化合物としては、たとえば、２−エチルヘキシル−２−シアノ−３，３’−ジフェニルアクリレート、エチル−２−シアノ−３，３’−ジフェニルアクリレートなどをあげることができる。   Examples of the cyanoacrylate-based ultraviolet absorbing compound include 2-ethylhexyl-2-cyano-3,3'-diphenyl acrylate, ethyl-2-cyano-3,3'-diphenyl acrylate, and the like.

また、上記紫外線吸収化合物に波長変換機能を有するものを用いる場合、上記紫外線吸収化合物として、たとえば、波長域３５０〜４００ｎｍの光を、４００ｎｍを超える波長域の光よりも多く吸収する蛍光化合物をあげることができる。上記蛍光化合物として、有機蛍光化合物、および、無機蛍光化合物などをあげることができる。   Moreover, when using what has a wavelength conversion function to the said ultraviolet absorption compound, the fluorescent compound which absorbs more light of the wavelength range 350-400 nm than the light of the wavelength range exceeding 400 nm as the said ultraviolet absorption compound is mention | raise | lifted, for example. be able to. Examples of the fluorescent compound include organic fluorescent compounds and inorganic fluorescent compounds.

上記有機蛍光化合物として、公知の有機色素化合物（有機蛍光染料など）を用いることができる。上記有機蛍光化合物として、たとえば、ナフタルイミド、ペリレン、アントラキンノン、クマリン、ベンゾクマリン、キサンテン、フェノキサジン、ベンゾ［ａ］フェノキサジン、ベンゾ［ｂ］フェノキサジン、ベンゾ［ｃ］フェノキサジン、ナフタルイミド、ナフトラクタム、アズラクトン、メチン、オキサジン、チアジン、ジケトピロロピロール、キナクリドン、ベンゾキサンテン、チオーエピンドリン、ラクタムイミド、ジフェニルマレイミド、アセトアセトアミド、イミダゾチアジン、ベンズアントロン、ペリレンモノイミド、フタルイミド、ベンゾトリアゾール、ベンゾチアジアゾール、ベンゾオキサゾール、ピリミジン、ピラジン、トリアゾール、ジベンゾフラン、トリアジン、および、ハルビツール酸誘導体などをあげることができる。これらの化合物は単独で使用してもよく、また２種以上を混合して使用してもよい。   As the organic fluorescent compound, a known organic coloring compound (such as an organic fluorescent dye) can be used. Examples of the organic fluorescent compound include naphthalimide, perylene, anthraquinone, coumarin, benzocoumarin, xanthene, phenoxazine, benzo [a] phenoxazine, benzo [b] phenoxazine, benzo [c] phenoxazine, and naphthalimide. , Naphtholactam, azlactone, methine, oxazine, thiazine, diketopyrrolopyrrole, quinacridone, benzoxanthene, thioepiindrin, lactamimide, diphenylmaleimide, acetoacetamide, imidazothiazine, benzanthrone, perylenemonoimide, phthalimide, benzotriazole Benzothiadiazole, benzoxazole, pyrimidine, pyrazine, triazole, dibenzofuran, triazine, harbituric acid derivatives, etc. It can be. These compounds may be used alone or in combination of two or more.

上記無機蛍光化合物として、たとえば、発光中心としてユーロピウムやサマリウムを有する錯体化合物などをあげることができる。これらの化合物は単独で使用してもよく、また２種以上を混合して使用してもよい。   Examples of the inorganic fluorescent compound include complex compounds having europium or samarium as the emission center. These compounds may be used alone or in combination of two or more.

上記蛍光化合物の吸光度として、たとえば、０．１〜６であることが好ましく、０．５〜４であることがより好ましく、０．８〜３であることがさらに好ましい。   The absorbance of the fluorescent compound is, for example, preferably from 0.1 to 6, more preferably from 0.5 to 4, and even more preferably from 0.8 to 3.

また、上記紫外線吸収化合物は、２００〜４００ｎｍ、特に２８０〜３８０ｎｍの範囲内に最大吸収波長を有するものが好ましい。上記紫外線吸収化合物を用いることにより、照射光に含まれる紫外線のうち、特にエチレン−酢酸ビニル共重合体などのエチレン系共重合体の光劣化を招く恐れのある紫外線をより効果的に吸収できる。なお、上記紫外線吸収化合物の最大吸収波長は、公知の手法を用いて市販の紫外線測定装置等を用いて測定することができる。   The ultraviolet absorbing compound preferably has a maximum absorption wavelength in the range of 200 to 400 nm, particularly 280 to 380 nm. By using the ultraviolet absorbing compound, it is possible to more effectively absorb ultraviolet rays that may cause photodegradation of an ethylene copolymer such as an ethylene-vinyl acetate copolymer, among ultraviolet rays contained in irradiation light. In addition, the maximum absorption wavelength of the said ultraviolet absorption compound can be measured using a commercially available ultraviolet ray measuring apparatus etc. using a well-known method.

上記紫外線吸収化合物のうち、特にエチレン−酢酸ビニル共重合体の光劣化の防止の観点からはベンゾフェノン系紫外線吸収化合物を用いるのが好ましく、一分子中にヒドロキシル基を２個以下含むベンゾフェノン系紫外線吸収化合物を用いるのが特に好ましい。上記紫外線吸収化合物として、たとえば、２−ヒドロキシ−４−メトキシベンゾフェノン、２，４−ジヒドロキシベンゾフェノン、および２−ヒドロキシ−４−ｎ−オクトキシ−ベンゾフェノンなどをあげることができる。上記化合物は、３２０〜３５０ｎｍの範囲内に最大吸収波長を有し、エチレン−酢酸ビニル共重合体等のエチレン系共重合体（Ａ）の光劣化をより効果的に抑制することができる。   Among the above ultraviolet absorbing compounds, it is preferable to use a benzophenone-based ultraviolet absorbing compound from the viewpoint of preventing photodegradation of an ethylene-vinyl acetate copolymer, and a benzophenone-based ultraviolet absorbing containing two or less hydroxyl groups in one molecule. It is particularly preferred to use a compound. Examples of the ultraviolet absorbing compound include 2-hydroxy-4-methoxybenzophenone, 2,4-dihydroxybenzophenone, and 2-hydroxy-4-n-octoxy-benzophenone. The said compound has the maximum absorption wavelength in the range of 320-350 nm, and can suppress the photodegradation of ethylene-type copolymers (A), such as an ethylene-vinyl acetate copolymer, more effectively.

上記酸化防止剤として、公知のものを適宜用いることができる。上記光酸化防止剤として、たとえば、フェノール系酸化防止剤、リン系酸化防止剤、イオウ系酸化防止剤、アミン系酸化防止剤、ラクトン系酸化防止剤、ビタミンＥ系酸化防止剤などをあげることができる。これらの化合物は単独で使用してもよく、また２種以上を混合して使用してもよい。   A well-known thing can be used suitably as said antioxidant. Examples of the photo-antioxidant include phenol-based antioxidants, phosphorus-based antioxidants, sulfur-based antioxidants, amine-based antioxidants, lactone-based antioxidants, vitamin E-based antioxidants, and the like. it can. These compounds may be used alone or in combination of two or more.

上記酸化防止剤のなかでも、着色を抑制する効果が大きいことから、フェノール系酸化防止剤である２，６−ジ−ｔ−ブチル−４−メチルフェノール、ペンタエリスリトールテトラキス（３−（３，５−ジ−ｔ−ブチル−４−ヒドロキシフェニル）プロピオネート）などが好ましい。   Among the above antioxidants, since the effect of suppressing coloring is large, 2,6-di-t-butyl-4-methylphenol and pentaerythritol tetrakis (3- (3,5), which are phenolic antioxidants, are used. -Di-t-butyl-4-hydroxyphenyl) propionate) and the like are preferred.

上記光安定剤として、公知のものを適宜用いることができる。上記光安定剤として、ポリマーに対して有害なラジカル種を補足し、新たなラジカルを発生しないようにする機能を有する化合物があげられる。上記光安定剤として、たとえば、ヒンダードアミン系光安定剤などをあげることができる。これらの化合物は単独で使用してもよく、また２種以上を混合して使用してもよい。上記光安定剤を含むことによって、照射された光などの影響によってマトリックス樹脂の劣化し、太陽電池用封止膜が黄変するのを抑制することができる。   Known light stabilizers can be used as appropriate. Examples of the light stabilizer include compounds having a function of capturing radical species harmful to the polymer and preventing generation of new radicals. Examples of the light stabilizer include hindered amine light stabilizers. These compounds may be used alone or in combination of two or more. By including the light stabilizer, it is possible to suppress degradation of the matrix resin due to the influence of irradiated light and the like, and yellowing of the solar cell sealing film.

低分子量の上記ヒンダードアミン系光安定剤としては、たとえば、デカン二酸ビス（２，２，６，６−テトラメチル−１（オクチルオキシ）−４−ピペリジニル）エステル、１，１−ジメチルエチルヒドロパーオキサイドおよびオクタンの反応生成物（分子量７３７）７０重量％とポリプロピレン３０重量％からなるもの；ビス（１，２，２，６，６−ペンタメチル−４−ピペリジル）［［３，５−ビス（１，１−ジメチルエチル）−４−ヒドロキシフェニル］メチル］ブチルマロネート（分子量６８５）；ビス（１，２，２，６，６−ペンタメチル−４−ピペリジル）セバケートおよびメチル−１，２，２，６，６−ペンタメチル−４−ピペリジルセバケート混合物（分子量５０９）；ビス（２，２，６，６−テトラメチル−４−ピペリジル）セバケート（分子量４８１）；テトラキス（２，２，６，６−テトラメチル−４−ピペリジル）−１，２，３，４−ブタンテトラカルボキシレート（分子量７９１）；テトラキス（１，２，２，６，６−ペンタメチル−４−ピペリジル）−１，２，３，４−ブタンテトラカルボキシレート（分子量８４７）；２，２，６，６−テトラメチル−４−ピペリジル−１，２，３，４−ブタンテトラカルボキシレートとトリデシル−１，２，３，４−ブタンテトラカルボキシレートの混合物（分子量９００）；１，２，２，６，６−ペンタメチル−４−ピペリジル−１，２，３，４−ブタンテトラカルボキシレートとトリデシル−１，２，３，４−ブタンテトラカルボキシレートの混合物（分子量９００）などをあげることができる。   Examples of the low molecular weight hindered amine light stabilizer include decanedioic acid bis (2,2,6,6-tetramethyl-1 (octyloxy) -4-piperidinyl) ester, 1,1-dimethylethyl hydroper 70% by weight of a reaction product of oxide and octane (molecular weight 737) and 30% by weight of polypropylene; bis (1,2,2,6,6-pentamethyl-4-piperidyl) [[3,5-bis (1 , 1-dimethylethyl) -4-hydroxyphenyl] methyl] butyl malonate (molecular weight 685); bis (1,2,2,6,6-pentamethyl-4-piperidyl) sebacate and methyl-1,2,2, 6,6-pentamethyl-4-piperidyl sebacate mixture (molecular weight 509); bis (2,2,6,6-tetramethyl-4-piperidi ) Sebacate (molecular weight 481); tetrakis (2,2,6,6-tetramethyl-4-piperidyl) -1,2,3,4-butanetetracarboxylate (molecular weight 791); tetrakis (1,2,2, 6,6-pentamethyl-4-piperidyl) -1,2,3,4-butanetetracarboxylate (molecular weight 847); 2,2,6,6-tetramethyl-4-piperidyl-1,2,3,4 A mixture of butanetetracarboxylate and tridecyl-1,2,3,4-butanetetracarboxylate (molecular weight 900); 1,2,2,6,6-pentamethyl-4-piperidyl-1,2,3,4 Examples thereof include a mixture (molecular weight 900) of butanetetracarboxylate and tridecyl-1,2,3,4-butanetetracarboxylate.

高分子量の上記ヒンダードアミン系光安定剤としては、ポリ［｛６−（１，１，３，３−テトラメチルブチル）アミノ−１，３，５−トリアジン−２，４−ジイル｝｛（２，２，６，６−テトラメチル−４−ピペリジル）イミノ｝ヘキサメチレン｛（２，２，６，６−テトラメチル−４−ピペリジル）イミノ｝］（分子量２，０００〜３，１００）；コハク酸ジメチルと４−ヒドロキシ−２，２，６，６−テトラメチル−１−ピペリジンエタノールの重合物（分子量３，１００〜４，０００）；Ｎ，Ｎ’，Ｎ”，Ｎ”’−テトラキス−（４，６−ビス−（ブチル−（Ｎ−メチル−２，２，６，６−テトラメチルピペリジン−４−イル）アミノ）−トリアジン−２−イル）−４，７−ジアザデカン−１，１０−ジアミン（分子量２，２８６）と上記コハク酸ジメチルと４−ヒドロキシ−２，２，６，６−テトラメチル−１−ピペリジンエタノールの重合物の混合物；ジブチルアミン・１，３，５−トリアジン・Ｎ，Ｎ’−ビス（２，２，６，６−テトラメチル−４−ピペリジル−１，６−ヘキサメチレンジアミンとＮ−（２，２，６，６−テトラメチル−４−ピペリジル）ブチルアミンの重縮合物（分子量２，６００〜３，４００）などをあげることができる。   Examples of the high molecular weight hindered amine light stabilizer include poly [{6- (1,1,3,3-tetramethylbutyl) amino-1,3,5-triazine-2,4-diyl} {(2, 2,6,6-tetramethyl-4-piperidyl) imino} hexamethylene {(2,2,6,6-tetramethyl-4-piperidyl) imino}] (molecular weight 2,000-3,100); succinic acid Polymer of dimethyl and 4-hydroxy-2,2,6,6-tetramethyl-1-piperidineethanol (molecular weight 3,100 to 4,000); N, N ′, N ″, N ″ ′-tetrakis- ( 4,6-bis- (butyl- (N-methyl-2,2,6,6-tetramethylpiperidin-4-yl) amino) -triazin-2-yl) -4,7-diazadecane-1,10- Diamine (molecular weight 2,286) and A mixture of a polymer of dimethyl succinate and 4-hydroxy-2,2,6,6-tetramethyl-1-piperidineethanol; dibutylamine, 1,3,5-triazine, N, N′-bis (2, Polycondensate of 2,6,6-tetramethyl-4-piperidyl-1,6-hexamethylenediamine and N- (2,2,6,6-tetramethyl-4-piperidyl) butylamine (molecular weight 2,600- 3,400).

また、上記ヒンダードアミン系光安定剤の市販品として、たとえば、ＬＡ−５２、ＬＡ−５７、ＬＡ−６２、ＬＡ−６３ＬＡ−６３ｐ、ＬＡ−６７、ＬＡ−６８（いずれもＡＤＥＫＡ社製）、Ｔｉｎｕｖｉｎ７４４、Ｔｉｎｕｖｉｎ７７０、Ｔｉｎｕｖｉｎ ７６５、Ｔｉｎｕｖｉｎ１２３、Ｔｉｎｕｖｉｎ１４４、Ｔｉｎｕｖｉｎ６２２ＬＤ、ＣＨＩＭＡＳＳＯＲＢ ９４４ＬＤ（いずれもＢＡＳＦ社製）、ＵＶ−３０３４（Ｂ．Ｆ．グッドリッチ社製）などをあげることができる。   Moreover, as a commercial item of the said hindered amine light stabilizer, for example, LA-52, LA-57, LA-62, LA-63LA-63p, LA-67, LA-68 (all manufactured by ADEKA), Tinuvin 744, Tinuvin 770, Tinuvin 765, Tinuvin 123, Tinuvin 144, Tinuvin 622LD, CHIMASORB 944LD (all manufactured by BASF), UV-3034 (manufactured by BF Goodrich), and the like can be mentioned.

上記架橋助剤として、公知のものを適宜用いることができる。上記架橋助剤として、官能基としてラジカル重合性基を有する化合物があげられる。上記架橋助剤として、たとえば、トリアリルシアヌレート、トリアリルイソシアヌレート等の３官能架橋助剤、（メタ）アクリルエステル（ＮＫエステルなど）の単官能または２官能の架橋助剤などをあげることができる。これらは単独で使用してもよく、また２種以上を混合して使用してもよい。上記架橋助剤を用いることにより、より確実にマトリックス樹脂のゲル分率を向上させ、封止材層の接着性および耐久性を向上させることができる。また、上記架橋助剤は、上記液状添加剤として用いることがより好ましいが、固形の架橋助剤も単独使用または液状の架橋助剤と併用してもよい。   As the crosslinking aid, known ones can be used as appropriate. Examples of the crosslinking aid include compounds having a radical polymerizable group as a functional group. Examples of the crosslinking aid include trifunctional crosslinking aids such as triallyl cyanurate and triallyl isocyanurate, and monofunctional or bifunctional crosslinking aids such as (meth) acrylic esters (NK esters, etc.). it can. These may be used singly or in combination of two or more. By using the said crosslinking adjuvant, the gel fraction of matrix resin can be improved more reliably and the adhesiveness and durability of a sealing material layer can be improved. The crosslinking aid is more preferably used as the liquid additive, but a solid crosslinking aid may be used alone or in combination with a liquid crosslinking aid.

上記老化防止剤として、公知のものを適宜用いることができる。上記老化防止剤として、たとえば、Ｎ，Ｎ’−ヘキサン−１，６−ジイルビス〔３−（３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシフェニル）プロピオナミド〕等のヒンダードフェノール系酸化防止剤、リン系熱安定剤、ラクトン系熱安定剤、ビタミンＥ系熱安定剤、イオウ系熱安定剤などをあげることができる。これらの化合物は単独で使用してもよく、また２種以上を混合して使用してもよい。   A well-known thing can be used suitably as said anti-aging agent. Examples of the antioxidant include hindered phenol antioxidants such as N, N′-hexane-1,6-diylbis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionamide]. , Phosphorus heat stabilizers, lactone heat stabilizers, vitamin E heat stabilizers, sulfur heat stabilizers, and the like. These compounds may be used alone or in combination of two or more.

上記太陽電池用封止材組成物においては、上記マトリックス樹脂に上記各成分（化合物）が混合・分散されている。上記太陽電池用封止材組成物において、所望の性能を損なわない範囲で、適宜公知の添加剤を含むことができる。上記添加剤として、たとえば、熱可塑性ポリマー、充填剤、可塑剤、シランカップリング剤、受酸剤、クレイ等があげられる。これらは単独で使用してもよく、また２種以上を混合して使用してもよい。また、これらの他の添加剤のうち有機化合物であれば、上記有機化合物添加剤（Ｂ）として用いてもよい。   In the solar cell encapsulant composition, the respective components (compounds) are mixed and dispersed in the matrix resin. The solar cell encapsulant composition may contain a known additive as long as the desired performance is not impaired. Examples of the additive include a thermoplastic polymer, a filler, a plasticizer, a silane coupling agent, an acid acceptor, and clay. These may be used singly or in combination of two or more. Moreover, as long as it is an organic compound among these other additives, you may use as said organic compound additive (B).

上記ブレンド工程において、さらに有機過酸化物（Ｃ）を含み、かつ、上記有機化合物添加剤（Ｂ）の融点が、上記有機過酸化物（Ｃ）の一時間半減期温度より１０℃低い温度以上であることが好ましい。   In the blending step, an organic peroxide (C) is further included, and the melting point of the organic compound additive (B) is 10 ° C. or more lower than the one-hour half-life temperature of the organic peroxide (C). It is preferable that

上記有機過酸化物（Ｃ）として、上記熱重合開始剤を適宜用いることができる。上記重合開始剤において、なかでも、一時間半減期温度（半減期が一時間となる温度）が９０〜１８０℃であることが好ましく、１００〜１６０℃であることがより好ましく、１１０〜１４０℃であることがさらに好ましい。上記重合開始剤として、たとえば、第３ブチルパーオキシイソプロピルカーボネート、第３ブチルパーオキシアセテート、第３ブチルパーオキシベンゾエート、ジクミルパーオキサイド、２，５−ジメチル−２，５−ビス（第３ブチルパーオキシ）ヘキサン、ジ第３ブチルパーオキサイド、２，５−ジメチル−２，５−ビス（第３ブチルパーオキシ）ヘキシン−３、１，１−ビス（第３ブチルパーオキシ）−３，３，５−トリメチルシクロヘキサン、１，１−ビス（第３ブチルパーオキシ）シクロヘキサン、メチルエチルケトンパーオキサイド、２，５−ジメチルヘキシル−２，５−ビスパーオキシベンゾエート、第３ブチルハイドロパーオキサイド、ｐ−メンタンハイドロパーオキサイド、ベンゾイルパーオキサイド、ｐ−クロルベンゾイルパーオキサイド、第３ブチルパーオキシイソブチレート、ヒドロキシヘプチルパーオキサイド、ジクロヘキサノンパーオキサイドなどをあげることができる。これらは単独で使用してもよく、また２種以上を混合して使用してもよい。   As the organic peroxide (C), the thermal polymerization initiator can be appropriately used. Among the above polymerization initiators, the one-hour half-life temperature (temperature at which the half-life is one hour) is preferably 90 to 180 ° C, more preferably 100 to 160 ° C, and more preferably 110 to 140 ° C. More preferably. Examples of the polymerization initiator include tertiary butyl peroxyisopropyl carbonate, tertiary butyl peroxyacetate, tertiary butyl peroxybenzoate, dicumyl peroxide, 2,5-dimethyl-2,5-bis (tertiary butyl Peroxy) hexane, di-tert-butyl peroxide, 2,5-dimethyl-2,5-bis (tert-butylperoxy) hexyne-3, 1,1-bis (tert-butylperoxy) -3,3 , 5-trimethylcyclohexane, 1,1-bis (tert-butylperoxy) cyclohexane, methyl ethyl ketone peroxide, 2,5-dimethylhexyl-2,5-bisperoxybenzoate, tert-butyl hydroperoxide, p-menthane Hydroperoxide, benzoyl peroxide, p-chlorobenzoy Peroxide, tert-butylperoxy isobutyrate, hydroxyheptyl peroxide, and the like di cyclohexanone peroxide. These may be used singly or in combination of two or more.

上記有機化合物添加剤（Ｂ）の融点が、上記有機過酸化物（Ｃ）の一時間半減期温度より１０℃低い温度以上であることが好ましく、その他、２０℃低い温度以上であるとしてもよく、３０℃低い温度以上であるとしてもよく、４０℃低い温度以上であるとしてもよい。本発明の製造方法を用いることにより、通常困難である上記有機過酸化物（Ｃ）の一時間半減期温度付近またはより高い融点を持つ上記有機化合物添加剤（Ｂ）であっても、有機過酸化物が実質的に分解させずに、成形温度よりも高い融点を有する有機化合物添加剤をエチレン系共重合体に均一に分散させることが可能となる。   The melting point of the organic compound additive (B) is preferably at least 10 ° C lower than the one-hour half-life temperature of the organic peroxide (C), and may be at least 20 ° C lower than the temperature. The temperature may be 30 ° C. or lower, or 40 ° C. or lower. By using the production method of the present invention, even if the organic compound additive (B) has a melting point of about 1 hour half-life or higher, which is usually difficult, the organic peroxide (C) It is possible to uniformly disperse the organic compound additive having a melting point higher than the molding temperature in the ethylene-based copolymer without substantially decomposing the oxide.

（太陽電池用封止材層の製造方法）
本発明の太陽電池用封止材組成物の製造方法は、エチレン系共重合体（Ａ）および有機化合物添加剤（Ｂ）を含む太陽電池用封止材組成物の製造方法であって、
上記エチレン系共重合体（Ａ）のビカット軟化点以上、上記エチレン系共重合体（Ａ）の融点より１０℃低い温度以下の温度範囲内で、上記エチレン系共重合体（Ａ）および上記有機化合物添加剤（Ｂ）を混合するブレンド工程を含むことを特徴とする。 (Method for producing solar cell encapsulant layer)
The manufacturing method of the sealing material composition for solar cells of this invention is a manufacturing method of the sealing material composition for solar cells containing an ethylene-type copolymer (A) and an organic compound additive (B),
The ethylene copolymer (A) and the organic polymer are within a temperature range from the Vicat softening point of the ethylene copolymer (A) to 10 ° C. below the melting point of the ethylene copolymer (A). A blending step of mixing the compound additive (B) is included.

上記エチレン系共重合体（Ａ）のビカット軟化点（Ｖｉｃａｔ Ｓｏｆｔｅｎｉｎｇ Ｔｅｍｐｅｒａｔｕｒｅ、ＶＳＴ）とは、ＪＩＳ Ｋ７２０６（試験荷重はＡ法（１０Ｎ）、伝熱媒体の昇温速度は５０℃／時の条件）によって測定された値を意味する。なお、断面積１ｍｍ２の端面が１ｍｍ食い込んだ時点の温度を上記ビカット軟化点温度とする。 The Vicat Softening Temperature (VST) of the ethylene copolymer (A) is JIS K7206 (test load is Method A (10N), heating rate of heat transfer medium is 50 ° C / hour) Means the value measured by The temperature at the time when the end surface having a cross-sectional area of 1 mm 2 bites in by 1 mm is defined as the Vicat softening point temperature.

上記ブレンド工程は、上記エチレン系共重合体（Ａ）のビカット軟化点以上、上記エチレン系共重合体（Ａ）の融点より１０℃低い温度以下の温度範囲内で、上記エチレン系共重合体（Ａ）および上記有機化合物添加剤（Ｂ）を混合することを特徴とする。   The blending step is carried out within a temperature range from the Vicat softening point of the ethylene copolymer (A) to 10 ° C lower than the melting point of the ethylene copolymer (A). A) and the organic compound additive (B) are mixed.

たとえば、上記エチレン系共重合体（Ａ）のビカット軟化点がＸ℃、上記エチレン系共重合体（Ａ）の融点がＹ℃であった場合、上記ブレンド工程が行われる温度範囲は、Ｘ℃以上（Ｙ−１０）℃以下となる。   For example, when the Vicat softening point of the ethylene copolymer (A) is X ° C. and the melting point of the ethylene copolymer (A) is Y ° C., the temperature range in which the blending process is performed is X ° C. Above (Y-10) ° C.

上記温度範囲の下限として、上記エチレン系共重合体（Ａ）のビカット軟化点より３℃高い温度、５℃高い温度、１０℃高い温度、１５℃高い温度、２０℃高い温度等とすることができる。   As a lower limit of the temperature range, a temperature 3 ° C. higher than the Vicat softening point of the ethylene copolymer (A), 5 ° C. higher temperature, 10 ° C. higher temperature, 15 ° C. higher temperature, 20 ° C. higher temperature, etc. it can.

上記温度範囲の上限として、上記エチレン系共重合体（Ａ）の融点より１３℃低い温度、１５℃低い温度、２０℃低い温度、２５℃低い温度等とすることができる。   The upper limit of the temperature range may be a temperature lower by 13 ° C., a temperature lower by 15 ° C., a temperature lower by 20 ° C., a temperature lower by 25 ° C., or the like than the melting point of the ethylene copolymer (A).

上記ブレンド工程の混合時間は、たとえば、１分〜６０分で行うことができ、３分〜４０分で行うことができ、５分〜３０分で行うことができ、１０分〜１５分で行うことができる。   The mixing time for the blending step can be, for example, 1 minute to 60 minutes, 3 minutes to 40 minutes, 5 minutes to 30 minutes, 10 minutes to 15 minutes. be able to.

上記ブレンド工程において、適宜公知の方法を用いて各材料（化合物）を混合（撹拌混合）することができる。たとえば、上記エチレン系共重合体（Ａ）に上記有機化合物添加剤（Ｂ）を添加する方法、上記有機化合物添加剤（Ｂ）に上記エチレン系共重合体（Ａ）を添加する方法、両者を同時または順次混練機器内に投入して機内で混合する方法、上記エチレン系共重合体（Ａ）と上記有機化合物添加剤（Ｂ）と上記液体添加剤とを同時または順次投入する方法などをあげることができる。特に、上記エチレン系共重合体（Ａ）がペレット状である場合、ペレット表面に上記有機化合物添加剤（Ｂ）を混合撹拌して付着させる方法を用いることが好ましい。さらに、上記エチレン系共重合体（Ａ）がペレット状であって、かつ液状添加剤を用いる場合には、上記液状添加剤を混合撹拌してペレット内部に含浸させる方法を用いることが好ましい。また、上記ブレンド工程は、液状添加剤などの太陽電池用封止材組成物の構成成分以外には別途溶剤を用いない方法（ドライプロセスで行うこと）が好ましい。   In the blending step, each material (compound) can be mixed (stirred and mixed) using a known method as appropriate. For example, a method of adding the organic compound additive (B) to the ethylene copolymer (A), a method of adding the ethylene copolymer (A) to the organic compound additive (B), Examples include a method of simultaneously or sequentially charging in a kneading apparatus and mixing in the apparatus, a method of simultaneously or sequentially charging the ethylene copolymer (A), the organic compound additive (B), and the liquid additive. be able to. In particular, when the ethylene copolymer (A) is in the form of pellets, it is preferable to use a method in which the organic compound additive (B) is mixed and stirred to adhere to the pellet surface. Furthermore, when the ethylene-based copolymer (A) is in the form of pellets and a liquid additive is used, it is preferable to use a method in which the liquid additive is mixed and stirred and impregnated inside the pellet. Moreover, the said blending process has the preferable method (it performs by a dry process) which does not use a solvent separately except the structural component of solar cell sealing material compositions, such as a liquid additive.

上記製造方法において、上記エチレン系共重合体（Ａ）がペレット状であることが好ましい。   In the said manufacturing method, it is preferable that the said ethylene-type copolymer (A) is a pellet form.

なお、上記ペレット状とは、たとえば、直径または長さが１〜１０ｍｍ程度の粒子状にしたものをいい、たとえば、２〜７ｍｍとすることができ、３〜５ｍｍとすることができる。また、上記ペレット状とは、たとえば、略円柱状、略球状、略円盤状、略三角柱状、略四角柱状、略多面体状、楕円球状などの形態の粒体などをあげることができる。   In addition, the said pellet form means what was made into the particle form whose diameter or length is about 1-10 mm, for example, can be 2-7 mm, for example, can be 3-5 mm. Further, examples of the pellet shape include particles in the form of a substantially columnar shape, a substantially spherical shape, a substantially disc shape, a substantially triangular prism shape, a substantially quadrangular prism shape, a substantially polyhedral shape, an elliptical sphere, and the like.

上記ブレンド工程において、ブレンド混合物（マトリックス樹脂等）の温度制御は、たとえば、ジャケットや冷却器などを用いて行うことが好ましい。   In the blending step, the temperature control of the blend mixture (matrix resin or the like) is preferably performed using, for example, a jacket or a cooler.

上記ブレンド工程に使用する機器として、たとえば、一軸押出機、二軸押出機、バンバリーミキサー、ニーダー、ミキシングロールなどを好ましいものとしてあげることができる。   Preferred examples of the equipment used in the blending step include a single screw extruder, a twin screw extruder, a Banbury mixer, a kneader, a mixing roll, and the like.

上記製造方法において、上記ブレンド工程に次いで、溶融混練工程を含むことが好ましい。   In the manufacturing method, it is preferable that a melt-kneading step is included after the blending step.

上記溶融混練工程として、適宜公知の方法を用いることができる。上記溶融混練工程として、たとえば、加熱混練、ロールミル、プラストミル、溶融押出機、バンバリーミキサー、ニーダーなどにより行うことができる。また、上記溶融混練工程を経由して直接太陽電池用封止材層として成形してもよい。   As the melt-kneading step, a known method can be used as appropriate. The melt kneading step can be performed by, for example, heat kneading, a roll mill, a plast mill, a melt extruder, a Banbury mixer, a kneader, or the like. Moreover, you may shape | mold directly as a sealing material layer for solar cells through the said melt-kneading process.

上記溶融混練工程の混合温度は、たとえば、４０〜１５０℃で行うことができ、８０〜１４０℃で行うことができ、９０〜１２０℃で行うことができ、１００〜１１０℃で行うことができる。過酸化物によるゲル化を防ぐために、１１０℃以下で行うことが好ましい。   The mixing temperature in the melt-kneading step can be, for example, 40 to 150 ° C, 80 to 140 ° C, 90 to 120 ° C, or 100 to 110 ° C. . In order to prevent gelation due to peroxide, it is preferably performed at 110 ° C. or lower.

上記溶融混練工程の混合時間は、たとえば、１分〜２０分で行うことができ、３分〜１０分で行うことができ、３分〜７分で行うことができ、３分〜５分で行うことができる。   The mixing time of the melt-kneading step can be performed, for example, from 1 minute to 20 minutes, from 3 minutes to 10 minutes, from 3 minutes to 7 minutes, from 3 minutes to 5 minutes. It can be carried out.

（太陽電池用封止材層）
一方、本発明の太陽電池用封止材層は、上記製造方法で得られた太陽電池用封止材組成物を用いて形成されたことを特徴とする。 (Sealant layer for solar cells)
On the other hand, the solar cell encapsulant layer of the present invention is formed using the solar cell encapsulant composition obtained by the above-described production method.

上記太陽電池用封止材層を製造するには、適宜公知の方法を用いることができる。たとえば、上記の太陽電池用封止材組成物（またはその各材料）を加熱混練、ロールミル、プラストミル等を用いて公知の方法で加熱混合した組成物を、通常の押出成形、カレンダー成形（カレンダリング）、真空熱加圧等により成形してシート状物を得る方法により適宜製造することができる。また、ＰＥＴフィルム等の上に上記層を形成した後、表面保護層に転写する方法により製造することができる。また、ホットメルトアプリケーターにより、混練溶融と塗布を同時に行う方法を用いることができる。特に、本発明では上記ブレンド工程および上記溶融混練工程を溶融押出機等の混練機器内で行い、シート状、フィルム状等の封止材層としての成形まで連続して行う方法が好ましい。   In order to produce the solar cell encapsulant layer, a known method can be used as appropriate. For example, a composition obtained by heating and mixing the above-described solar cell encapsulant composition (or each material thereof) with a known method using heat kneading, a roll mill, a plast mill, etc., is subjected to ordinary extrusion molding, calendar molding (calendering). ), And can be appropriately produced by a method of forming a sheet-like material by vacuum hot pressing or the like. Moreover, after forming the said layer on PET film etc., it can manufacture by the method of transcribe | transferring to a surface protective layer. Further, a method of simultaneously kneading and melting and applying with a hot melt applicator can be used. In particular, in the present invention, a method is preferred in which the blending step and the melt-kneading step are performed in a kneading apparatus such as a melt extruder, and the molding is continuously performed as a sealing material layer such as a sheet or film.

より具体的には、たとえば、上記製造方法で得られた上記太陽電池用封止材組成物を、表面保護層またはセパレーターなどにそのまま塗布・形成してもよし、上記材料を他の材料と混合組成物として塗布・形成してもよい。   More specifically, for example, the solar cell encapsulant composition obtained by the production method may be applied and formed as it is on a surface protective layer or a separator, or the material may be mixed with other materials. You may apply | coat and form as a composition.

上記太陽電池用封止材組成物を塗布する場合、たとえば、上記太陽電池用封止材組成物のマトリックス樹脂の融点が５０〜１２０℃であれば、上記組成物の混練溶融および塗布温度は、上記融点に３０〜１００℃加えた温度で行うことが好ましい。   When the solar cell encapsulant composition is applied, for example, if the melting point of the matrix resin of the solar cell encapsulant composition is 50 to 120 ° C., the kneading and melting and application temperature of the composition are: It is preferable to carry out at the temperature which added 30-100 degreeC to the said melting | fusing point.

特に、本発明では上記ブレンド工程および上記溶融混練工程を溶融押出機等の混練機器内で行い、シート状、フィルム状等の封止材層としての成形まで連続して行う方法が好ましい。その他の方法として、いくつかの実施形態において、太陽電池用封止材層が下記の工程によって薄膜構造体に製造される：（ｉ）ポリマー（マトリックス樹脂）粉末が所定の比率で溶媒（たとえば、テトラクロロエチレン（ＴＣＥ）、シクロペンタノン、ジオキサンなど）に溶解されたポリマー溶液を調製する工程、（ｉｉ）ポリマー混合物を含有する発光色素（蛍光化合物）を、ポリマー溶液を所定の重量比で発光色素と混合して、色素含有ポリマー溶液を得ることによって調製する工程、（ｉｉｉ）色素／ポリマー薄膜を、色素含有ポリマー溶液をガラス基板の上に直接に流し込み、その後、基板を２時間で室温から最高で１００℃まで熱処理し、残留溶媒を１３０℃での一晩のさらなる真空加熱によって完全に除くことによって形成する工程、および、（ｉｖ）使用前に、色素／ポリマー薄膜を水の中で剥がし、その後、自立型ポリマーフィルムを完全に乾燥する工程；（ｖ）フィルムの厚さを、色素／ポリマー溶液の濃度および蒸発速度を変化させることによって制御することができる。   In particular, in the present invention, a method is preferred in which the blending step and the melt-kneading step are performed in a kneading apparatus such as a melt extruder, and the molding is continuously performed as a sealing material layer such as a sheet or film. Alternatively, in some embodiments, a solar cell encapsulant layer is produced into a thin film structure by the following steps: (i) polymer (matrix resin) powder is a solvent (eg, A step of preparing a polymer solution dissolved in tetrachloroethylene (TCE), cyclopentanone, dioxane, etc.), (ii) a luminescent dye (fluorescent compound) containing the polymer mixture, and the polymer solution with a luminescent dye at a predetermined weight ratio Mixing to obtain a dye-containing polymer solution, (iii) pouring the dye / polymer thin film directly onto the glass substrate, after which the substrate is allowed to warm up from room temperature in 2 hours Formed by heat treatment to 100 ° C and complete removal of residual solvent by further vacuum heating overnight at 130 ° C And (iv) peeling the dye / polymer thin film in water before use and then completely drying the free-standing polymer film; (v) the thickness of the film, the concentration of the dye / polymer solution And can be controlled by changing the evaporation rate.

上記太陽電池用封止材層の厚みは、２０〜２０００μｍであることが好ましく、５０〜１０００μｍであることがより好ましく、１００〜８００μｍであることがさらに好ましい。２０μｍよりも薄くなると、封止材機能が発現しにくくなってしまう。一方、２０００μｍより厚くなると、太陽電池モジュールの厚みが大きくなり、コスト的にも不利益である。   The thickness of the solar cell encapsulant layer is preferably 20 to 2000 μm, more preferably 50 to 1000 μm, and still more preferably 100 to 800 μm. When the thickness is less than 20 μm, the sealing material function is hardly exhibited. On the other hand, when it becomes thicker than 2000 micrometers, the thickness of a solar cell module will become large and it will be disadvantageous also in cost.

上記太陽電池用封止材層は、通常、太陽電池セルの封止に用いられるが、必要に応じて、インターコネクタ材、電極なども適宜封止するように積層される。上記太陽電池用封止材層の上記機能を損なわない限り、各層間などの適宜必要に応じて、他の層を介在してもよい。   The solar cell encapsulant layer is usually used for encapsulating solar cells, and is laminated so as to appropriately seal interconnector materials, electrodes, and the like as necessary. As long as the function of the solar cell encapsulant layer is not impaired, other layers such as each layer may be interposed as required.

（太陽電池モジュール）
本発明の太陽電池モジュール１は、表面保護層１０、上記太陽電池用封止材層２０および太陽電池セル３０を含むことを特徴とする。一例として図１、２に簡易な模式図を示すが、本発明がこれらに限定されるものではない。また、太陽電池セルの背面側にさらに封止材層４０、バックシート５０を適宜備えることもできる。また、これらの各層間に、上記太陽電池用封止材層の上記機能を損なわない限り、接着材層、粘着剤層などの他の層を適宜介在してもよい。また、上記背面用の封止材層として、適宜、本発明の太陽電池用封止材層を用いてもよい。 (Solar cell module)
The solar cell module 1 of the present invention includes a surface protective layer 10, the solar cell sealing material layer 20, and solar cells 30. 1 and 2 show simple schematic diagrams as an example, but the present invention is not limited to these. Moreover, the sealing material layer 40 and the back sheet | seat 50 can also be further suitably provided in the back side of a photovoltaic cell. Moreover, as long as the said function of the said solar cell sealing material layer is not impaired between these each layers, you may interpose other layers, such as an adhesive material layer and an adhesive layer, suitably. Moreover, you may use the sealing material layer for solar cells of this invention suitably as said sealing material layer for back surfaces.

上記太陽電池セルとして、たとえば、硫化カドミウム／テルル化カドミウム太陽電池、銅インジウムガリウム二セレン化物太陽電池、非晶質シリコン太陽電池、微結晶シリコン太陽電池または結晶シリコン太陽電池を用いることができる。上記太陽電池セルとして、結晶シリコン太陽電池であることが好ましい。   As the solar cell, for example, a cadmium sulfide / cadmium telluride solar cell, a copper indium gallium diselenide solar cell, an amorphous silicon solar cell, a microcrystalline silicon solar cell, or a crystalline silicon solar cell can be used. The solar battery cell is preferably a crystalline silicon solar battery.

上記太陽電池モジュールの製造において、上記太陽電池用封止材層を上記太陽電池セル等に転写してもよく、直接上記太陽電池セル上に塗布形成してもよい。また、上記太陽電池用封止材層と他の層を同時に形成してもよい。   In the production of the solar cell module, the solar cell encapsulant layer may be transferred to the solar cell or the like, or may be directly coated on the solar cell. Moreover, you may form the said sealing material layer for solar cells, and another layer simultaneously.

以下、本発明の構成と効果を具体的に示す実施例等について説明する。   Examples and the like specifically showing the configuration and effects of the present invention will be described below.

（表中の化合物）
実施例・比較例では、以下の化合物を用いた。
［エチレン系共重合体（Ａ）］
・スミテートＫＡ３０：マトリックス樹脂、エチレンビニルアセテート樹脂（ＥＶＡ）（住友化学社製、融点７４℃、ビカット軟化点３９℃）
・ウルトラセン７１０：マトリックス樹脂、エチレンビニルアセテート樹脂（ＥＶＡ）（東ソー社製、融点７１℃、ビカット軟化点４０℃）
・スミテートＭＡ１０：マトリックス樹脂、エチレンビニルアセテート樹脂（ＥＶＡ）（住友化学社製、融点５７℃、ビカット軟化点３３℃）
［有機化合物添加剤（Ｂ）］
・化合物Ｂ１：４，７−ビス（４−メトキシフェニル）−２，１，３−ベンゾチアジアゾール（融点２０１℃）
・化合物Ｂ２：４，７−ビス（４−イソブチルオキシフェニル）−２−イソブチル−２Ｈ−ベンゾトリアゾール（融点１６７℃）
・Ｔｉｎｕｖｉｎ９００：２−（２Ｈ−ベンゾチアジアゾール−２−イル）−４，６−（１−メチル−１−フェニルエチル）フェノール（ＢＡＳＦ社製、融点１３８℃）
［有機過酸化物（Ｃ）］
・Ｐｅｒｂｕｔｙｌ Ｅ：ｔ−ブチルパーオキシ−２−エチルヘキシルモノカルボネート（日油社製、一時間半減期温度１１９℃）
［シランカップリング剤］
・ＫＢＭ５０３：３−メタクリロキシプロピルトリメトキシシラン（信越シリコーン社製）
［架橋助剤］
・ＴＡＩＣ：架橋助剤、トリアリルイソシアヌレート（日本化成社製） (Compounds in the table)
In the examples and comparative examples, the following compounds were used.
[Ethylene copolymer (A)]
・ Smitate KA30: matrix resin, ethylene vinyl acetate resin (EVA) (manufactured by Sumitomo Chemical Co., Ltd., melting point 74 ° C., Vicat softening point 39 ° C.)
Ultrasen 710: Matrix resin, ethylene vinyl acetate resin (EVA) (manufactured by Tosoh Corporation, melting point 71 ° C., Vicat softening point 40 ° C.)
・ Smitate MA10: Matrix resin, ethylene vinyl acetate resin (EVA) (manufactured by Sumitomo Chemical Co., Ltd., melting point 57 ° C., Vicat softening point 33 ° C.)
[Organic compound additive (B)]
Compound B1: 4,7-bis (4-methoxyphenyl) -2,1,3-benzothiadiazole (melting point: 201 ° C.)
Compound B2: 4,7-bis (4-isobutyloxyphenyl) -2-isobutyl-2H-benzotriazole (melting point: 167 ° C.)
Tinuvin 900: 2- (2H-benzothiadiazol-2-yl) -4,6- (1-methyl-1-phenylethyl) phenol (BASF, melting point 138 ° C.)
[Organic peroxide (C)]
Perbutyl E: t-butylperoxy-2-ethylhexyl monocarbonate (manufactured by NOF Corporation, one hour half-life temperature 119 ° C.)
[Silane coupling agent]
KBM503: 3-methacryloxypropyltrimethoxysilane (manufactured by Shin-Etsu Silicone)
[Crosslinking aid]
-TAIC: Crosslinking aid, triallyl isocyanurate (manufactured by Nippon Kasei Co., Ltd.)

（樹脂シートの作製）
実施例・比較例において、各化合物を表１の配合に基づき、各封止材層（封止材シート）を下記方法により製造した。 (Production of resin sheet)
In Examples and Comparative Examples, each sealing material layer (sealing material sheet) was produced by the following method based on the compounds shown in Table 1.

各実施例・比較例において、小型粉砕機（アズワン社製）を用いて、各所定の温度範囲になるように冷却器で系中の温度制御しながら、各材料（化合物）を混合撹拌してプレブレンド（５分）を行った。その後、プレブレンドした樹脂組成物をラボプラストミル４Ｃ１５０型（ローラ形状：シグマ型、東洋精機社製）に投入し、８０℃、１０ｒｐｍで５分間混練した。得られた混練物を真空熱加圧装置ＶＳ２０−３４３０（ミカドテクノス社製）を用いて１００℃、２０ｋＮで５分間プレスを行い、厚み４００μｍの封止材シートを成型した。   In each Example / Comparative Example, each material (compound) was mixed and stirred using a small pulverizer (manufactured by ASONE Co., Ltd.) while controlling the temperature in the system with a cooler so as to be in each predetermined temperature range. Pre-blending (5 minutes) was performed. Thereafter, the pre-blended resin composition was put into a Laboplast Mill 4C150 type (roller shape: Sigma type, manufactured by Toyo Seiki Co., Ltd.) and kneaded at 80 ° C. and 10 rpm for 5 minutes. The obtained kneaded product was pressed at 100 ° C. and 20 kN for 5 minutes using a vacuum heat press VS20-3430 (manufactured by Mikado Technos Co., Ltd.) to mold a sealing material sheet having a thickness of 400 μm.

（プレブレンド後の樹脂の評価）
プレブレンド後の樹脂組成物に対し、肉眼での外観形状の評価を実施した。評価基準は以下のように行った。
・ブロッキングの発生がなかった場合、液体成分が表面に残っていなかった場合：○
・樹脂同士のブロッキングが生じていた場合、液体成分が樹脂表面に残っていた場合：× (Evaluation of resin after pre-blending)
The appearance of the naked eye was evaluated on the resin composition after pre-blending. The evaluation criteria were as follows.
・ When there was no blocking, or when no liquid component remained on the surface: ○
・ When blocking between resins occurs, or when liquid components remain on the resin surface: ×

（シート分散性の評価）
まず、得られた封止材シートに対し、肉眼での外観形状の評価を行い、上記有機化合物添加剤（Ｂ）が残っていた場合は不合格とした。一方、肉眼では上記化合物の残存が判別できないものに対して、以下の評価を続けた。 (Evaluation of sheet dispersibility)
First, the appearance shape with the naked eye was evaluated with respect to the obtained sealing material sheet, and when the said organic compound additive (B) remained, it was set as the rejection. On the other hand, the following evaluation was continued for those in which the remaining of the above compound could not be discerned with the naked eye.

成型した封止材シートを２ｃｍ角で切り出し、有機化合物添加剤の吸光度をＭＣＰＤ−９８００（大塚電子社製）で測定し、吸光度／厚みをｎ＝５の標準偏差を求め、分散性の評価を実施した。評価基準は以下のように行った。
・標準偏差が０．１未満であった場合：○
・標準偏差が０．１以上であった場合：× The molded encapsulant sheet was cut out at 2 cm square, the absorbance of the organic compound additive was measured with MCPD-9800 (manufactured by Otsuka Electronics Co., Ltd.), the absorbance / thickness was determined as the standard deviation of n = 5, and the dispersibility was evaluated. Carried out. The evaluation criteria were as follows.
・ When the standard deviation is less than 0.1: ○
・ When the standard deviation is 0.1 or more: ×

下記表１、表２に、各配合（重量部単位）および得られた封止材層樹脂シートを用いたときの各測定結果を示す。
Tables 1 and 2 below show the respective measurement results when each compounding (part by weight) and the obtained sealing material layer resin sheet were used.

測定・評価の結果、いずれの実施例においても、プレブレンド後の樹脂の評価およびシート分散性の評価はともに良好であった。一方、比較例１では、分散性が悪かった。また、比較例２では、分散性が悪く、液体成分が樹脂表面に残ってしまった。また、比較例３〜５では、プレブレンド時の温度が本願発明よりも高く、ブロッキングしてしまった。   As a result of the measurement / evaluation, the evaluation of the resin after pre-blending and the evaluation of the sheet dispersibility were good in any of the examples. On the other hand, in Comparative Example 1, the dispersibility was poor. Moreover, in the comparative example 2, the dispersibility was bad and the liquid component remained on the resin surface. Moreover, in Comparative Examples 3-5, the temperature at the time of pre-blending was higher than this invention, and it blocked.

１ 太陽電池モジュール
１０ 表面保護層
２０ 太陽電池用封止材層
３０ 太陽電池セル
４０ 裏面用封止材層
５０ バックシート DESCRIPTION OF SYMBOLS 1 Solar cell module 10 Surface protective layer 20 Solar cell sealing material layer 30 Solar cell 40 Back surface sealing material layer 50 Back sheet

Claims (11)

エチレン系共重合体（Ａ）および有機化合物添加剤（Ｂ）を含む太陽電池用封止材組成物の製造方法であって、
前記エチレン系共重合体（Ａ）のビカット軟化点以上、前記エチレン系共重合体（Ａ）の融点より１０℃低い温度以下の温度範囲内で、前記エチレン系共重合体（Ａ）および前記有機化合物添加剤（Ｂ）を混合するブレンド工程を含み、
前記有機化合物添加剤（Ｂ）が、紫外線吸収剤、酸化防止剤、光安定剤、老化防止剤、または、架橋助剤であることを特徴とする、太陽電池用封止材組成物の製造方法。 A method for producing a solar cell encapsulant composition comprising an ethylene copolymer (A) and an organic compound additive (B),
The ethylene copolymer (A) and the organic polymer are within a temperature range from the Vicat softening point of the ethylene copolymer (A) to 10 ° C. below the melting point of the ethylene copolymer (A). A blending step of mixing the compound additive (B),
The said organic compound additive (B) is a ultraviolet absorber, antioxidant, light stabilizer, anti-aging agent, or crosslinking adjuvant, The manufacturing method of the sealing material composition for solar cells characterized by the above-mentioned . 前記エチレン系共重合体（Ａ）がペレット状である、請求項１に記載の太陽電池用封止材組成物の製造方法。   The manufacturing method of the sealing material composition for solar cells of Claim 1 whose said ethylene-type copolymer (A) is a pellet form. 前記ブレンド工程において、さらに有機過酸化物（Ｃ）を含み、かつ、前記有機化合物添加剤（Ｂ）の融点が、前記有機過酸化物（Ｃ）の一時間半減期温度より１０℃低い温度以上である、請求項１または２に記載の太陽電池用封止材組成物の製造方法。   In the blending step, an organic peroxide (C) is further included, and the melting point of the organic compound additive (B) is 10 ° C. or more lower than the one-hour half-life temperature of the organic peroxide (C). The manufacturing method of the sealing material composition for solar cells of Claim 1 or 2 which is. 前記ブレンド工程において、溶剤を用いない、請求項１〜３のいずれかに記載の太陽電池用封止材組成物の製造方法。   The manufacturing method of the sealing material composition for solar cells in any one of Claims 1-3 which does not use a solvent in the said blending process. 前記ブレンド工程において、さらに液状添加剤を含む、請求項１〜４のいずれかに記載の太陽電池用封止材組成物の製造方法。   The manufacturing method of the sealing material composition for solar cells in any one of Claims 1-4 which further contains a liquid additive in the said blending process. 前記ブレンド工程に次いで、溶融混練工程を含む、請求項１〜５のいずれかに記載の太陽電池用封止材組成物の製造方法。   The manufacturing method of the sealing material composition for solar cells in any one of Claims 1-5 including a melt-kneading process following the said blending process. 前記溶融混練工程が一軸押出機、二軸押出機、バンバリーミキサー、ニーダー、またはミキシングロールによりなされる、請求項１〜６のいずれかに記載の太陽電池用封止材組成物の製造方法。   The manufacturing method of the sealing material composition for solar cells in any one of Claims 1-6 with which the said melt-kneading process is made | formed with a single screw extruder, a twin screw extruder, a Banbury mixer, a kneader, or a mixing roll. 前記エチレン系共重合体（Ａ）が、エチレン−酢酸ビニル共重合体を主成分とする、請求項１〜７のいずれかに記載の太陽電池用封止材組成物の製造方法。   The manufacturing method of the sealing material composition for solar cells in any one of Claims 1-7 in which the said ethylene-type copolymer (A) has an ethylene-vinyl acetate copolymer as a main component. 請求項１〜８のいずれかに記載の方法により太陽電池用封止材組成物を得る工程、および、
前記太陽電池用封止材組成物を用いて太陽電池用封止材層を形成する工程、
を含む、太陽電池用封止材層の製造方法。 The process of obtaining the sealing material composition for solar cells by the method in any one of Claims 1-8 , and
Forming a sealing material layer for a solar cell using the solar cell encapsulant composition,
The manufacturing method of the sealing material layer for solar cells containing . 請求項１〜８のいずれかに記載の方法により太陽電池用封止材組成物を得る工程、
前記太陽電池用封止材組成物を用いて太陽電池用封止材層を形成する工程、および、
前記太陽電池用封止材層、および、太陽電池セルを用いて太陽電池モジュールを形成する工程、を含む、太陽電池モジュールの製造方法。 The process of obtaining the sealing material composition for solar cells by the method in any one of Claims 1-8 ,
Step of forming a sealing material layer for a solar cell using the solar cell encapsulating material composition and,
The manufacturing method of a solar cell module including the process of forming a solar cell module using the said sealing material layer for solar cells, and a photovoltaic cell. 前記太陽電池セルが、結晶シリコン太陽電池、硫化カドミウム／テルル化カドミウム太陽電池、銅インジウムガリウム二セレン化物太陽電池、非晶質シリコン太陽電池、または微結晶シリコン太陽電池である、請求項１０に記載の太陽電池モジュールの製造方法。 The solar cell, crystalline silicon solar cell, a cadmium sulfide / cadmium telluride solar cell, copper indium gallium diselenide solar cell, amorphous silicon solar cell or a microcrystalline silicon solar cell, according to claim 10 Manufacturing method for solar cell module.
JP2013125401A 2013-06-14 2013-06-14 SOLAR CELL SEALING MATERIAL COMPOSITION, PROCESS FOR PRODUCING THE SAME, SOLAR CELL SEALING MATERIAL LAYER USING THE SAME, AND SOLAR CELL MODULE Active JP6178126B2 (en)