JP6164552B2 - 鉄系焼結部品の製造方法 - Google Patents
鉄系焼結部品の製造方法 Download PDFInfo
- Publication number
- JP6164552B2 JP6164552B2 JP2013106751A JP2013106751A JP6164552B2 JP 6164552 B2 JP6164552 B2 JP 6164552B2 JP 2013106751 A JP2013106751 A JP 2013106751A JP 2013106751 A JP2013106751 A JP 2013106751A JP 6164552 B2 JP6164552 B2 JP 6164552B2
- Authority
- JP
- Japan
- Prior art keywords
- heat treatment
- iron
- sintered
- treatment
- steam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
2wt%Cu−0.8wt%C−残部Feの組成の原料粉末からなる密度6.9g/cm3と密度7.2g/cm3の焼結体(通常材)に対してスチーム温度550℃、処理時間1時間の条件でスチーム処理を行い、その後、その焼結体に高周波熱処理を施した。
このようにして得られた焼結体の表層部の断面の組織の写真を図5に示す。この図5は、密度7.2g/cm3の焼結体をスチーム処理後に3秒間高周波加熱した焼結部品の組織写真である。
2wt%Ni−0.5wt%Mo−0.6wt%C−残部Feの組成の原料粉末からなる密度7.2g/cm3の焼結体(高合金材)及び4wt%Ni−1.5wt%Cu−0.5wt%Mo−0.6wt%C−残部Feの組成の原料粉末からなる密度7.2g/cm3の焼結体(これも高合金材)に対してスチーム温度550℃、処理時間1時間の条件でスチーム処理を行い、その後、その焼結体に高周波熱処理を施した。
焼結材料は、通常材にこの発明の方法でスチーム処理と高周波熱処理を施して得られた
焼結材料よりもさらに高い硬度が得られる。
2 歯部
3 母材
4 マルテンサイト層
5 鉄の酸化被膜
6 空孔
Claims (1)
- 焼結工程を経た部品にスチーム処理を施してその部品の表面に鉄の酸化被膜を形成し、
しかる後、部品の所望箇所の表面に高周波熱処理を施して熱処理を行った部位の表層部に
マルテンサイト層を生じさせる鉄系焼結部品の製造方法であって、
前記スチーム処理を、スチーム温度:450℃〜600℃、処理時間:30分以上の条
件で実施し、さらに、前記高周波熱処理を、金属組織がオーステナイト化する温度として
温度:900℃〜1200℃、誘導加熱コイルによる加熱時間:30秒以下、加熱後の冷
却:連続冷却変態曲線でマルテンサイトが現われる冷却速度の条件で実施する鉄系焼結部品の製造方法。