JP6163142B2 - Recording sheet - Google Patents
Recording sheet Download PDFInfo
- Publication number
- JP6163142B2 JP6163142B2 JP2014148807A JP2014148807A JP6163142B2 JP 6163142 B2 JP6163142 B2 JP 6163142B2 JP 2014148807 A JP2014148807 A JP 2014148807A JP 2014148807 A JP2014148807 A JP 2014148807A JP 6163142 B2 JP6163142 B2 JP 6163142B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- pulp
- information recording
- paper
- recording
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は記録用紙に関する。更に詳しくは、インクジェット記録適性、オフセット印刷適性及び水性ペンでの筆記適性を有する記録用紙に関する。 The present invention relates to a recording sheet. More specifically, the present invention relates to a recording paper having ink jet recording suitability, offset printing suitability, and writing ability with a water-based pen.
従来、記録用紙への情報の記録方法としてインクジェット記録やオフセット印刷が知られている。また、水性ペンでの筆記による方法も行われている。これらの記録方法は、併用して行われることがある。例えば、定型文やイラスト等を事前にオフセット印刷し、その後に可変の固有情報をインクジェット記録や水性ペンでの筆記により行うといったものである。従って、記録用紙には、インクジェット記録適性、オフセット印刷適性及び水性ペンでの筆記適性の何れをも満足することが望まれている。 Conventionally, inkjet recording and offset printing are known as methods for recording information on recording paper. Moreover, the method by writing with a water-based pen is also performed. These recording methods may be performed in combination. For example, standard sentences, illustrations, and the like are offset printed in advance, and then variable unique information is performed by inkjet recording or writing with a water-based pen. Therefore, it is desired that the recording paper satisfy all of the ink jet recording suitability, the offset print suitability, and the writing ability with a water-based pen.
一方、記録用紙には各種記録適性とは別に、柔らかな和紙に見られるような、紙の自然な風合いを持つものが求められている。このような風合いを付与する方法としては、比較的柔らかなパルプであるコットンリンターパルプを使用することが知られている。コットンリンターパルプを使用した記録用紙として、特許文献１には、３０重量％以上がコットンパルプからなる製紙用繊維を用いた高級水彩紙が開示されている。また、特許文献２には、コットンリンターパルプを含有するコットン紙にインク受容層を設けたインクジェット記録適性を有する記録媒体が開示されている。また、特許文献３には、表層と裏層にコットンリンターパルプを配合した多層抄き紙に顔料塗工層を設けたカード用紙が開示されている。 On the other hand, the recording paper is required to have a natural paper texture as seen in soft Japanese paper, apart from various recording suitability. As a method for imparting such a texture, it is known to use cotton linter pulp, which is a relatively soft pulp. As a recording paper using cotton linter pulp, Patent Document 1 discloses a high-quality watercolor paper using a fiber for paper making of 30% by weight or more of cotton pulp. Patent Document 2 discloses a recording medium having ink jet recording suitability in which an ink receiving layer is provided on cotton paper containing cotton linter pulp. Patent Document 3 discloses a card paper in which a pigment coating layer is provided on a multi-layered paper in which cotton linter pulp is blended in a front layer and a back layer.
しかしながら、特許文献１の記録用紙は水彩画用の記録用紙であり、インクジェット記録適性やオフセット印刷適性を十分に満足できるものではなかった。また、特許文献２及び特許文献３の記録用紙は、何れも顔料塗工層を設けた記録用紙であり、紙の自然な風合いを持つものではない。 However, the recording paper of Patent Document 1 is a recording paper for watercolors, and cannot satisfy ink jet recording suitability and offset printing suitability sufficiently. The recording papers of Patent Document 2 and Patent Document 3 are both recording papers provided with a pigment coating layer and do not have a natural texture of paper.
このような問題に鑑み、本発明は、インクジェット記録による記録画像の滲みと印字ムラが生じにくく、オフセット印刷を好適に行える表面強度を有し、水性ペンによる筆記時も滲みが生じにくく、さらに、紙の自然な風合いを持つ記録用紙を提供することを目的とする。 In view of such a problem, the present invention is less likely to cause blurring and printing unevenness of a recorded image by ink jet recording, has a surface strength that can suitably perform offset printing, is less likely to blur even when writing with an aqueous pen, An object is to provide a recording paper having a natural texture of paper.
上記課題を解決するために、本発明の記録用紙は、２層抄き以上の記録用紙であって、少なくとも一つの情報記録層を有し、その内側の層として支持層を有し、前記情報記録層および前記支持層はパルプを主成分として含有し、前記情報記録層に含まれるパルプの２５〜８０質量％がコットンリンターパルプであり、前記情報記録層の表面には水溶性高分子が塗布されており、前記支持層には該支持層に含まれるパルプ１００質量部に対して０．１〜０．８質量部の内添サイズ剤が含まれていることを特徴とするものである。 In order to solve the above problems, the recording paper of the present invention is a recording paper having two or more layers, which has at least one information recording layer, and has a support layer as an inner layer, The recording layer and the support layer contain pulp as a main component, 25-80% by mass of the pulp contained in the information recording layer is cotton linter pulp, and a water-soluble polymer is applied to the surface of the information recording layer. The support layer includes 0.1 to 0.8 parts by mass of an internally added sizing agent with respect to 100 parts by mass of pulp contained in the support layer.
本発明の記録用紙は、前記情報記録層が内添サイズ剤を含んでいないか、又は、該情報記録層のパルプ１００質量部に対して０．０５質量部以下の割合で内添サイズ剤を含んでいてもよい。 In the recording paper of the present invention, the information recording layer does not contain an internal sizing agent, or the internal sizing agent is added at a ratio of 0.05 parts by mass or less with respect to 100 parts by mass of the pulp of the information recording layer. May be included.
本発明の記録用紙は、前記支持層のパルプのフリーネス（ＣＳＦ）が、３５０〜６００ｍｌであってもよい。 The recording paper of the present invention may have a pulp freeness (CSF) of the support layer of 350 to 600 ml.
本発明の記録用紙は、前記情報記録層の表面に塗布する水溶性高分子の塗布量が０．５〜１．５ｇ／ｍ２であってもよい。 In the recording paper of the present invention, the coating amount of the water-soluble polymer applied to the surface of the information recording layer may be 0.5 to 1.5 g / m 2 .
本発明によれば、インクジェット記録による記録画像の滲みと印字ムラが少なく、オフセット印刷を好適に行える表面強度を有し、水性ペンによる筆記時も滲みが生じ難く、更には、紙の自然な風合いを持つ記録用紙とすることができる。 According to the present invention, there is little blurring and printing unevenness of a recorded image by ink jet recording, it has a surface strength that can be suitably used for offset printing, hardly blurs even when writing with an aqueous pen, and further, the natural texture of paper Can be used as recording paper.
次に、本発明について実施形態を示して詳細に説明するが、本発明はこれらの記載に限定して解釈されない。本発明の効果を奏する限り、実施形態は種々の変形をしてもよい。 Next, the present invention will be described in detail with reference to embodiments, but the present invention is not construed as being limited to these descriptions. As long as the effect of the present invention is exhibited, the embodiment may be variously modified.
本発明の記録用紙の構成例を図１に示す。同図において、１は情報記録層、２は支持層、３は任意の層である。また、同図において各層の厚みは実際の比率を表すものではない。 A configuration example of the recording paper of the present invention is shown in FIG. In the figure, 1 is an information recording layer, 2 is a support layer, and 3 is an arbitrary layer. In the figure, the thickness of each layer does not represent an actual ratio.
本発明の記録用紙は、少なくとも一つの情報記録層を有し、それに接する一つ内側の層として支持層を有する２層以上の記録用紙である。２層の記録用紙の場合、その片面の最表層が情報記録層（表層）となり、反対側の最表層が支持層となる（裏層）。このような構成例を図１（ａ）に示す。情報記録層１と、支持層２とを１層ずつ設けた構成例である。このような構成とすれば、一方の面にのみ情報記録層を設けた２層抄き合わせの記録用紙となる。 The recording paper of the present invention is a recording paper having two or more layers having at least one information recording layer and having a support layer as one inner layer in contact therewith. In the case of a two-layer recording paper, the outermost layer on one side is an information recording layer (surface layer), and the outermost layer on the opposite side is a support layer (back layer). An example of such a configuration is shown in FIG. In this configuration example, the information recording layer 1 and the support layer 2 are provided one by one. With such a configuration, the recording sheet is a two-layer stitched recording sheet in which an information recording layer is provided only on one side.
本発明が３層以上の層を有する場合、少なくとも一つの情報記録層を有し、その内側の層に支持層を有する構成とし、情報記録層を少なくとも片面において最表層とすることが好ましい。そのような構成例としては、例えば、図１（ｂ）に示される構成例がある。すなわち、情報記録層１と、支持層２と、任意の層３とを１層ずつ設けた構成例である。このような構成とすれば、一方の面にのみ情報記録層を設けた３層抄き合わせの記録用紙となる。ここで任意の層３の構成は特に限定されるものではなく、本発明の目的とする効果を損なわない範囲で多層紙で用いられる各種公知の紙層とすることができる。また、同図には示していないが、任意の層３を情報記録層に置き換えることで、両面に情報記録層を設けた３層抄き合わせの記録用紙とすることもできる。 When the present invention has three or more layers, it is preferable to have at least one information recording layer and a support layer as an inner layer, and the information recording layer is at least one surface. As such a configuration example, for example, there is a configuration example shown in FIG. That is, this is a configuration example in which the information recording layer 1, the support layer 2, and the arbitrary layer 3 are provided one by one. With such a configuration, a three-layer stitched recording sheet having an information recording layer provided on only one side is obtained. Here, the configuration of the arbitrary layer 3 is not particularly limited, and various known paper layers used in multilayer paper can be used as long as the effects of the present invention are not impaired. Although not shown in the figure, by replacing the arbitrary layer 3 with an information recording layer, it is possible to obtain a three-layer combined recording sheet in which information recording layers are provided on both sides.
次いで、図１（ｃ）に示される構成例は、情報記録層１と、支持層２とを、任意の層３の両側に１層ずつ設けた構成例である。このような構成とすれば、両面に情報記録層を設けた５層抄き合わせの記録用紙となる。 Next, the configuration example shown in FIG. 1C is a configuration example in which the information recording layer 1 and the support layer 2 are provided on each side of the arbitrary layer 3. With such a configuration, a five-layer stitched recording sheet having information recording layers on both sides is obtained.
本発明の情報記録層および支持層はパルプを主成分とする。例えば、各層のための紙料中パルプを８０質量％以上、例えば、９０質量％以上、９５質量％以上、９８質量％以上含むことができる。 The information recording layer and the support layer of the present invention are mainly composed of pulp. For example, the pulp in the stock for each layer can be 80% by mass or more, for example, 90% by mass or more, 95% by mass or more, or 98% by mass or more.
本発明の記録用紙は、前述の各種記録方法により情報を記録する情報記録層にコットンリンターパルプを含有させる。コットンリンターパルプとは、綿種子の表皮繊維（リンター）を精製したパルプである。コットンリンターパルプは、比較的水分の吸収性が良く、柔らかいパルプである。本発明においては、情報記録層に含有させるパルプのうち２５〜８０質量％をコットンリンターパルプとする。好ましくは３５〜７５質量％、更に好ましくは５０〜７０質量％である。このような構成とすることで、インクジェット記録によるインクの吸収性が良好で、紙の自然な風合いを持つ記録用紙とすることができる。コットンリンターパルプの含有量が２５質量％未満となると、インクジェット記録によるインクの吸収性を満足できず、インクジェット記録による記録画像に滲みや印字ムラが生じやすくなる。逆に、８０質量％を超えると情報記録層の表面強度が過度に低下し、オフセット印刷適性が低下する。 The recording paper of the present invention contains cotton linter pulp in an information recording layer for recording information by the various recording methods described above. Cotton linter pulp is pulp obtained by purifying cotton seed skin fibers (linters). Cotton linter pulp is a soft pulp with relatively good moisture absorption. In this invention, 25-80 mass% is made into a cotton linter pulp among the pulps contained in an information recording layer. Preferably it is 35-75 mass%, More preferably, it is 50-70 mass%. By adopting such a configuration, it is possible to obtain a recording paper that has good ink absorbability by ink jet recording and has a natural texture of paper. When the content of the cotton linter pulp is less than 25% by mass, the ink absorbability by ink jet recording cannot be satisfied, and bleeding or uneven printing tends to occur in a recorded image by ink jet recording. On the contrary, when it exceeds 80% by mass, the surface strength of the information recording layer is excessively decreased, and the offset printability is deteriorated.
情報記録層のコットンリンターパルプ以外に用いるパルプ及び情報記録層以外の層に用いるパルプとしては、特に制限するものではなく、ＬＢＫＰ（広葉樹さらしクラフトパルプ）、ＮＢＫＰ（針葉樹さらしクラフトパルプ）などの化学パルプ、ＧＰ（砕木パルプ）、ＰＧＷ（加圧式砕木パルプ）、ＲＭＰ（リファイナーメカニカルパルプ）、ＴＭＰ（サーモメカニカルパルプ）、ＣＴＭＰ（ケミサーモメカニカルパルプ）、ＣＭＰ（ケミメカニカルパルプ）、ＣＧＰ（ケミグランドパルプ）などの機械パルプ、ＤＩＰ（脱インキパルプ）などの木材パルプ及びケナフ、バガス、竹などの非木材パルプを用いることができる。また、本発明の目的とする効果を損なわない範囲において、合成繊維を更に配合することができる。環境保全の観点から、ＥＣＦ（Ｅｌｅｍｅｎｔａｌ Ｃｈｌｏｒｉｎｅ Ｆｒｅｅ）パルプ、ＴＣＦ（Ｔｏｔａｌ Ｃｈｌｏｒｉｎｅ Ｆｒｅｅ）パルプ、古紙パルプ、植林木から得られるパルプを用いることができる。 The pulp used for the information recording layer other than the cotton linter pulp and the pulp used for the layer other than the information recording layer is not particularly limited, and chemical pulp such as LBKP (hardwood bleached kraft pulp), NBKP (softwood bleached kraft pulp), etc. , GP (crushed pulp), PGW (pressurized ground pulp), RMP (refiner mechanical pulp), TMP (thermomechanical pulp), CTMP (chemithermomechanical pulp), CMP (chemimechanical pulp), CGP (chemipulp pulp) Non-wood pulp such as mechanical pulp such as DIP (deinked pulp) and non-wood pulp such as kenaf, bagasse and bamboo can be used. In addition, a synthetic fiber can be further blended within a range that does not impair the intended effect of the present invention. From the viewpoint of environmental protection, ECF (Elemental Chlorine Free) pulp, TCF (Total Chlorine Free) pulp, waste paper pulp, and pulp obtained from planted trees can be used.
各層に用いるパルプのフリーネス（ＣＳＦ）は、特に限定するものではないが、カナダ標準濾水度（フリーネス）（ＪＩＳ Ｐ ８１２１−２：２０１２「パルプ−ろ水度試験方法−第２部：カナダ標準ろ水度法」）で、３００〜７００ｍｌとすることが好ましい。また、支持層に用いるパルプのフリーネス（ＣＳＦ）は３５０〜６００ｍｌであることが好ましく、より好ましくは４００〜５５０ｍｌである。支持層に用いるパルプのフリーネス（ＣＳＦ）が３５０ｍｌ未満となると、紙の自然な風合いを持つ記録用紙とすることができないおそれがある。逆に６００ｍｌを超えると記録用紙としての十分な強度を損ねるおそれがある。尚、情報記録層に用いるパルプはコットンリンターパルプと他のパルプとを混合するが、叩解は混合前であっても混合後であってもよい。 The pulp freeness (CSF) used in each layer is not particularly limited, but is Canadian Standard Freeness (JIS P 8121-2: 2012 “Pulp-Freeness Test Method—Part 2: Canadian Standard”). The freeness method ") is preferably 300 to 700 ml. Moreover, it is preferable that the freeness (CSF) of the pulp used for a support layer is 350-600 ml, More preferably, it is 400-550 ml. If the freeness (CSF) of the pulp used for the support layer is less than 350 ml, there is a possibility that the recording paper cannot have a natural texture of paper. On the other hand, if it exceeds 600 ml, there is a risk of impairing the sufficient strength as a recording sheet. In addition, although the pulp used for an information recording layer mixes cotton linter pulp and another pulp, beating may be before mixing or after mixing.
本発明においては、情報記録層の表面に水溶性高分子を塗布する。前述の通り、情報記録層はコットンリンターパルプを含むため、比較的表面強度が低くなりやすいが、水溶性高分子を塗布することでオフセット印刷に好適な表面強度を付与することができる。ここで用いる水溶性高分子としては、表面紙力剤として公知のものを使用でき、例えば、ポリアクリルアミド系樹脂、ポリアミド系樹脂、ポリビニルアルコール、酸化澱粉やカチオン化澱粉などの澱粉類、スチレンアクリル系樹脂、等である。また、水溶性高分子の塗布方法は特に限定されるものではなく、２本ロールサイズプレスのようなポンド式サイズプレスやゲートロールサイズプレス、シムサイザーのようなフィルムメタリングタイプやロッドコーター、エアーナイフコーターなどを用いることができる。 In the present invention, a water-soluble polymer is applied to the surface of the information recording layer. As described above, since the information recording layer contains cotton linter pulp, the surface strength tends to be relatively low, but by applying a water-soluble polymer, it is possible to impart surface strength suitable for offset printing. As the water-soluble polymer used here, those known as surface paper strength agents can be used, for example, polyacrylamide resins, polyamide resins, polyvinyl alcohol, starches such as oxidized starch and cationized starch, and styrene acrylic resins. Resin, etc. The method for applying the water-soluble polymer is not particularly limited, and a pound-type size press such as a two-roll size press, a gate roll size press, a film metering type such as a shim sizer, a rod coater, or an air knife. A coater or the like can be used.
本発明においては、前記情報記録層の表面に塗布する水溶性高分子の塗布量は、０．１〜２．０ｇ／ｍ２であってよく、０．５〜１．５ｇ／ｍ２であることが好ましい。より好ましくは０．８〜１．２ｍ２である。水溶性高分子の塗布量がこの範囲であれば、オフセット印刷に好適な表面強度を付与しつつ、インクジェット記録による記録画像の滲みと印字ムラを抑制しやすい。水溶性高分子の塗布量が０．１ｇ／ｍ２未満ではオフセット印刷に好適な表面強度とすることができないおそれがある。逆に２．０ｇ／ｍ２を超えるとインクジェット記録による記録画像に滲みと印字ムラが生じやすくなる。 In the present invention, the coating amount of the water-soluble polymer is applied to the surface of the information recording layer may be 0.1 to 2.0 g / m 2, is 0.5 to 1.5 g / m 2 It is preferable. More preferably 0.8~1.2m 2. If the application amount of the water-soluble polymer is within this range, it is easy to suppress bleeding of printed images and uneven printing due to inkjet recording while providing surface strength suitable for offset printing. If the coating amount of the water-soluble polymer is less than 0.1 g / m 2 , there is a possibility that the surface strength suitable for offset printing cannot be obtained. On the other hand, if it exceeds 2.0 g / m 2 , bleeding and uneven printing tend to occur in a recorded image by ink jet recording.
本発明の記録用紙においては、各層に内添サイズ剤を含有させることができる。内添サイズ剤としては、特に限定するものではなく、例えば、強化ロジンサイズ剤、酸性ロジンサイズ剤、弱酸性ロジンサイズ剤などのロジン系サイズ剤や、アルキルケテンダイマー、アルケニル無水コハク酸を使用することができる。 In the recording paper of the present invention, an internal sizing agent can be contained in each layer. The internal sizing agent is not particularly limited. For example, a rosin sizing agent such as a reinforced rosin sizing agent, an acidic rosin sizing agent, or a weak acidic rosin sizing agent, an alkyl ketene dimer, or an alkenyl succinic anhydride is used. be able to.
本発明の記録用紙においては、支持層に内添サイズ剤を、該支持層に含まれるパルプ１００質量部に対して０．１〜０．８質量部含有させる。好ましくは０．２〜０．７質量部であり、より好ましくは０．３〜０．６質量部である。本発明の記録用紙は、情報記録層がコットンリンターパルプを比較的多く含むこともあり、情報記録層の吸水性が比較的高い構成となっている。このため、インクジェット記録によるインクの吸収性は良好となるが、記録画像には滲みや印字ムラが生じやすく、また、水性ペンでの筆記においても滲みが生じやすい。一方、このような滲みや印字ムラを抑制するには、情報記録層にサイズ剤を含有させる方法が考えられるが、情報記録層に過度にサイズ剤を含有させると、インクジェット記録によるインクの吸収性を損ねてしまうおそれがある。そこで、本発明の記録用紙においては、支持層に内添サイズ剤を前記した範囲で含有させてインクの吸収性を維持させたまま、滲みや印字ムラを抑制させる。支持層中の内添サイズ剤の含有量が０．１質量部を下回ると、インクジェット記録による記録画像や水性ペンでの筆記時に滲みが生じやすくなる。逆に０．８質量部を超えると、インクの吸収性が悪化し、インクジェット記録による記録画像に印字ムラが生じやすくなる。 In the recording paper of the present invention, the support layer contains the internal sizing agent in an amount of 0.1 to 0.8 parts by mass with respect to 100 parts by mass of the pulp contained in the support layer. Preferably it is 0.2-0.7 mass part, More preferably, it is 0.3-0.6 mass part. In the recording paper of the present invention, the information recording layer may contain a relatively large amount of cotton linter pulp, and the information recording layer has a relatively high water absorption. For this reason, the ink absorbability by ink jet recording is good, but the recorded image is likely to have bleeding and uneven printing, and bleeding is also likely to occur when writing with an aqueous pen. On the other hand, in order to suppress such bleeding and printing unevenness, a method of including a sizing agent in the information recording layer is conceivable. However, if the information recording layer contains an excessively large sizing agent, the ink absorbency by ink jet recording can be considered. May be damaged. Therefore, in the recording paper of the present invention, the internal sizing agent is contained in the support layer in the above-described range, and bleeding and printing unevenness are suppressed while maintaining the ink absorbability. When the content of the internal sizing agent in the support layer is less than 0.1 part by mass, bleeding tends to occur during recording by ink jet recording or writing with an aqueous pen. On the other hand, if it exceeds 0.8 parts by mass, the ink absorbability deteriorates, and printing unevenness tends to occur in the recorded image by ink jet recording.
また、情報記録層は、内添サイズ剤を含んでいないか、又は、内添サイズ剤を含ませる場合でも、該情報記録層のパルプ１００質量部に対して０．０５質量部以下の割合で含んでいることが好ましい。情報記録層の内添サイズ剤の含有量が０．０５質量部を超えると、インクジェット記録によるインクの吸収性が損なわれるおそれがある。 Further, the information recording layer does not contain an internal additive sizing agent or includes an internal additive sizing agent at a ratio of 0.05 parts by mass or less with respect to 100 parts by mass of the pulp of the information recording layer. It is preferable to include. If the content of the internal sizing agent in the information recording layer exceeds 0.05 parts by mass, the ink absorbability by ink jet recording may be impaired.
本発明の記録用紙においては、前述した抄紙薬品の他に、本発明の目的とする効果を損ねない範囲で、填料、填料定着剤、凝集剤、歩留まり向上剤、紙力増強剤、濾水性向上剤、着色染料、着色顔料、蛍光増白剤、蛍光消色剤、ピッチコントロール剤などの各種助剤を配合することができる。 In the recording paper of the present invention, in addition to the above-mentioned papermaking chemicals, a filler, a filler fixing agent, a flocculant, a yield improver, a paper strength enhancer, and a freeness improvement within a range that does not impair the intended effect of the present invention. Various auxiliary agents such as an agent, a coloring dye, a coloring pigment, a fluorescent brightening agent, a fluorescent decoloring agent, and a pitch control agent can be blended.
本発明の記録用紙の抄紙方法は、特に限定されるものではなく、長網多層抄紙機、円網多層抄紙機、長網円網コンビ多層抄紙機などの各種装置で製造できる。 The paper making method of the recording paper of the present invention is not particularly limited, and can be produced by various apparatuses such as a long-mesh multi-layer paper machine, a circular net multi-layer paper machine, and a long-mesh circular net combination multi-layer paper machine.
本発明の記録用紙の坪量は、特に限定するものではないが、４０〜４００ｇ／ｍ２であることが好ましい。この範囲であれば好適にインクジェット記録とオフセット印刷を行うことができる。情報記録層の坪量は２０〜９０ｇ／ｍ２であることが好ましい。より好ましくは２５〜８０ｇ／ｍ２であり、更に好ましくは３０〜６０ｇ／ｍ２である。情報記録層の坪量が２０ｇ／ｍ２未満であると、インクジェット記録によるインクを十分に吸収できず、記録画像に滲みや印字ムラが生じやすくなる。逆に９０ｇ／ｍ２を超えると、水性ペンでの筆記時の滲みが生じやすくなり、更には、記録用紙としての強度を満足できないおそれがある。また、支持層の坪量は、インクジェット記録や水性ペンでの筆記時にインクが裏抜けしないよう３０ｇ／ｍ２以上、より好ましくは４０ｇ／ｍ２以上であることが好ましく、支持層の坪量の上限は特に制限はないが、例えば、２００ｇ／ｍ２以下であるとよい。 The basis weight of the recording paper of the present invention is not particularly limited, but is preferably 40 to 400 g / m 2 . Within this range, ink jet recording and offset printing can be suitably performed. The basis weight of the information recording layer is preferably 20 to 90 g / m 2 . More preferably, it is 25-80 g / m < 2 >, More preferably, it is 30-60 g / m < 2 >. If the basis weight of the information recording layer is less than 20 g / m 2 , ink by ink jet recording cannot be sufficiently absorbed, and bleeding or uneven printing tends to occur in the recorded image. On the other hand, if it exceeds 90 g / m 2 , bleeding at the time of writing with a water-based pen tends to occur, and furthermore, the strength as a recording paper may not be satisfied. Further, the basis weight of the support layer is preferably 30 g / m 2 or more, more preferably 40 g / m 2 or more so that the ink does not pass through during ink jet recording or writing with a water-based pen. Although an upper limit does not have a restriction | limiting in particular, For example, it is good in it being 200 g / m < 2 > or less.
次に、実施例を挙げて本発明をより具体的に説明するが、本発明はこれら実施例に限定されるものではない。また、例中の「部」、「％」は、特に断らない限りそれぞれ固形分換算での質量部又は質量％を示す。 Next, the present invention will be described more specifically with reference to examples. However, the present invention is not limited to these examples. Further, “parts” and “%” in the examples respectively represent parts by mass or mass% in terms of solid content unless otherwise specified.
（実施例１）
＜情報記録層用紙料の調製＞
コットンリンターパルプ２５部とＬＢＫＰ７５部からなるパルプ（ＣＳＦ：５００ｍｌ）を水中に分散してパルプスラリーとし、このパルプスラリーにタルク（商品名：タルクＮＴＬ／日本タルク社製）５部、両性タピオカスターチ（商品名：ＣＡＴＯ３２１０／イングレディオン・ジャパン社製）０．９部、硫酸バンド２部をそれぞれ添加して攪拌し、情報記録層用紙料を得た。
＜支持層用紙料の調製＞
ＬＢＫＰ１００部（ＣＳＦ：５００ｍｌ）を水中に分散してパルプスラリーとし、このパルプスラリーにタルク（商品名：タルクＮＴＬ／日本タルク社製）５部、両性タピオカスターチ（商品名：ＣＡＴＯ３２１０／イングレディオン・ジャパン社製）０．９部、硫酸バンド２部、ロジンサイズ剤（商品名：ＣＣ１４０４／星光ＰＭＣ社製）０．４部をそれぞれ添加して攪拌し、支持層用紙料を得た。
＜記録用紙の抄造＞
得られた情報記録層用紙料と支持層用紙料とを用いて、円網式抄紙機にて情報記録層／支持層を積層させた構成となるように２層抄き合わせで湿紙を抄紙し、プレスにて脱水後、乾燥させた。その後、２本ロールサイズプレスにてポリアクリルアミド系樹脂（商品名：ＳＴ−５０００／星光ＰＭＣ社製）を、情報記録層の表面への乾燥塗布量が０．５ｇ／ｍ２となるように塗布した後、シリンダードライヤーにて乾燥し、米坪１２０ｇ／ｍ２の記録用紙を得た。情報記録層の坪量は３０ｇ／ｍ２、支持層の坪量は９０ｇ／ｍ２であった。
Example 1
<Preparation of information recording layer paper fee>
Pulp consisting of 25 parts of cotton linter pulp and 75 parts of LBKP (CSF: 500 ml) is dispersed in water to obtain a pulp slurry. In this pulp slurry, 5 parts of talc (trade name: Talc NTL / manufactured by Nippon Talc Co., Ltd.), amphoteric tapioca starch ( (Product name: CATO 3210 / manufactured by Ingledion Japan) 0.9 parts and 2 parts of sulfuric acid band were added and stirred to obtain an information recording layer paper material.
<Preparation of support layer paper material>
100 parts of LBKP (CSF: 500 ml) is dispersed in water to obtain a pulp slurry, and 5 parts of talc (trade name: Talc NTL / manufactured by Nippon Talc Co., Ltd.), amphoteric tapioca starch (trade name: CATO3210 / Ingledion Japan) 0.9 parts, 2 parts of sulfuric acid band, and 0.4 parts of rosin sizing agent (trade name: CC1404 / manufactured by Seiko PMC) were added and stirred to obtain a support layer paper stock.
<Recording paper making>
Using the obtained information recording layer stock and support layer stock, wet paper is made by two-layer bonding so that the information recording layer / support layer is laminated by a circular net paper machine. Then, after dehydrating with a press, it was dried. Thereafter, a polyacrylamide resin (trade name: ST-5000 / manufactured by Seiko PMC) was applied with a two-roll size press so that the dry coating amount on the surface of the information recording layer was 0.5 g / m 2. Then, it was dried with a cylinder dryer to obtain a recording paper having a weight of 120 g / m 2 . The basis weight of the information recording layer was 30 g / m 2 , and the basis weight of the support layer was 90 g / m 2 .
（実施例２）
実施例１において、情報記録層用紙料の調製におけるパルプの配合を、コットンリンターパルプ５０部とＬＢＫＰ５０部に変更し、記録用紙の抄造におけるポリアクリルアミド系樹脂（商品名：ＳＴ−５０００／星光ＰＭＣ社製）の情報記録層の表面への乾燥塗布量を１ｇ／ｍ２とした以外は実施例１と同様にして記録用紙を得た。
(Example 2)
In Example 1, the composition of the pulp in the preparation of the information recording layer paper was changed to 50 parts of cotton linter pulp and 50 parts of LBKP, and polyacrylamide resin (trade name: ST-5000 / Seiko PMC) A recording paper was obtained in the same manner as in Example 1 except that the dry coating amount on the surface of the information recording layer was 1 g / m 2 .
（実施例３）
実施例１において、情報記録層用紙料の調製におけるパルプの配合を、コットンリンターパルプ７５部とＬＢＫＰ２５部に変更し、記録用紙の抄造におけるポリアクリルアミド系樹脂（商品名：ＳＴ−５０００／星光ＰＭＣ社製）の情報記録層の表面への乾燥塗布量を１．５ｇ／ｍ２とした以外は実施例１と同様にして記録用紙を得た。
(Example 3)
In Example 1, the composition of pulp in the preparation of the information recording layer paper was changed to 75 parts of cotton linter pulp and 25 parts of LBKP, and polyacrylamide resin (trade name: ST-5000 / Seiko PMC) A recording paper was obtained in the same manner as in Example 1 except that the dry coating amount on the surface of the information recording layer was 1.5 g / m 2 .
（実施例４）
実施例１において、支持層用紙料の調製におけるロジンサイズ剤（商品名：ＣＣ１４０４／星光ＰＭＣ社製）の添加量を０．１部に変更した以外は、実施例１と同様にして記録用紙を得た。
Example 4
In Example 1, the recording paper was prepared in the same manner as in Example 1 except that the addition amount of the rosin sizing agent (trade name: CC1404 / manufactured by Starlight PMC) in the preparation of the support layer paper material was changed to 0.1 part. Obtained.
（実施例５）
実施例１において、支持層用紙料の調製におけるロジンサイズ剤（商品名：ＣＣ１４０４／星光ＰＭＣ社製）の添加量を０．８部に変更した以外は、実施例１と同様にして記録用紙を得た。
(Example 5)
In Example 1, the recording paper was prepared in the same manner as in Example 1 except that the addition amount of the rosin sizing agent (trade name: CC1404 / manufactured by Seiko PMC) in the preparation of the support layer paper material was changed to 0.8 parts. Obtained.
（実施例６）
実施例１において、情報記録層の坪量を２０ｇ／ｍ２とし、支持層の坪量を１００ｇ／ｍ２とした以外は、実施例１と同様にして記録用紙を得た。
(Example 6)
A recording paper was obtained in the same manner as in Example 1, except that the basis weight of the information recording layer was 20 g / m 2 and the basis weight of the support layer was 100 g / m 2 .
（実施例７）
実施例１において、情報記録層用紙料の調製時に更にロジンサイズ剤（商品名：ＣＣ１４０４／星光ＰＭＣ社製）０．０３部を添加し、支持層用紙料の調製におけるロジンサイズ剤（商品名：ＣＣ１４０４／星光ＰＭＣ社製）の添加量を０．８部に変更し、情報記録層の坪量を９０ｇ／ｍ２とし、支持層の坪量を３０ｇ／ｍ２とした以外は実施例１と同様にして記録用紙を得た。
(Example 7)
In Example 1, 0.03 part of rosin sizing agent (trade name: CC1404 / manufactured by Seiko PMC) was further added at the time of preparation of the information recording layer stock, and rosin sizing agent (trade name: product name: CC1404 / manufactured by Starlight PMC) was changed to 0.8 parts, the basis weight of the information recording layer was 90 g / m 2, and the basis weight of the support layer was 30 g / m 2. A recording sheet was obtained in the same manner.
（実施例８）
実施例１において、記録用紙の抄造におけるポリアクリルアミド系樹脂（商品名：ＳＴ−５０００／星光ＰＭＣ社製）の情報記録層の表面への乾燥塗布量を０．３ｇ／ｍ２とした以外は実施例１と同様にして記録用紙を得た。
(Example 8)
In Example 1, except that the dry coating amount of the polyacrylamide resin (trade name: ST-5000 / manufactured by Seiko PMC) on the surface of the information recording layer was 0.3 g / m 2 in papermaking of recording paper. A recording paper was obtained in the same manner as in Example 1.
（実施例９）
実施例３において、記録用紙の抄造におけるポリアクリルアミド系樹脂（商品名：ＳＴ−５０００／星光ＰＭＣ社製）の情報記録層の表面への乾燥塗布量を１．７ｇ／ｍ２とした以外は実施例３と同様にして記録用紙を得た。
Example 9
In Example 3, it was carried out except that the dry coating amount on the surface of the information recording layer of polyacrylamide resin (trade name: ST-5000 / manufactured by Seiko PMC) in papermaking of recording paper was 1.7 g / m 2. A recording paper was obtained in the same manner as in Example 3.
（比較例１）
実施例１において、情報記録層用紙料の調製におけるパルプの配合を、コットンリンターパルプ２０部とＬＢＫＰ８０部に変更した以外は実施例１と同様にして記録用紙を得た。
(Comparative Example 1)
In Example 1, a recording paper was obtained in the same manner as in Example 1 except that the composition of the pulp in the preparation of the information recording layer stock was changed to 20 parts of cotton linter pulp and 80 parts of LBKP.
（比較例２）
実施例１において、支持層用紙料の調製におけるロジンサイズ剤（商品名：ＣＣ１４０４／星光ＰＭＣ社製）の添加量を０．０５部に変更した以外は、実施例１と同様にして記録用紙を得た。
(Comparative Example 2)
In Example 1, the recording paper was prepared in the same manner as in Example 1 except that the addition amount of the rosin sizing agent (trade name: CC1404 / manufactured by Starlight PMC) in the preparation of the support layer paper material was changed to 0.05 parts. Obtained.
（比較例３）
実施例１において、支持層用紙料の調製におけるロジンサイズ剤（商品名：ＣＣ１４０４／星光ＰＭＣ社製）の添加量を１．０部に変更した以外は、実施例１と同様にして記録用紙を得た。
(Comparative Example 3)
In Example 1, the recording paper was prepared in the same manner as in Example 1 except that the addition amount of the rosin sizing agent (trade name: CC1404 / manufactured by Starlight PMC) in the preparation of the support layer paper material was changed to 1.0 part. Obtained.
（比較例４）
実施例３において、情報記録層用紙料の調製におけるパルプの配合を、コットンリンターパルプ８５部とＬＢＫＰ１５部に変更した以外は実施例３と同様にして記録用紙を得た。
(Comparative Example 4)
In Example 3, a recording paper was obtained in the same manner as in Example 3 except that the composition of the pulp in the preparation of the information recording layer stock was changed to 85 parts of cotton linter pulp and 15 parts of LBKP.
各実施例及び比較例で得られた記録用紙の構成の概要と、評価結果が表１に示されている。尚、各評価は下記の方法により行った。
（１）滲み
インクジェットプリンターＭＰ９９０（キヤノン社製）を用い、記録用紙の情報記録層の表面に画像を印字後、印字画像の滲み具合を目視にて評価した。評価は５段階とし、最も滲みが生じていないものを５とし、最も滲みが生じているものを１とした。評価が２以下のものは実用上の問題がある。
（２）印字ムラ
インクジェットプリンターＭＰ９９０（キヤノン製）でブラック、シアン、マゼンタ、イエローを印字面にベタ印字後、印字部のムラの程度を目視で評価した。評価は５段階とし、最も印字部のムラが生じていないものを５とし、最も印字部のムラが生じているものを１とした。評価が２以下のものは、実使用上の問題がある。
（３）ペン書きサイズ度
ＪＡＰＡＮ ＴＡＰＰＩ紙パルプ試験方法Ｎｏ．１２：２０００「板紙−サイズ度試験方法−ペン書き法」に準拠し、情報記録面のペン書きサイズ度について評価した。評価は同規格の等級を用いて０から６で表した。評価が４以上のものは水性ペンによる筆記時に滲みが生じ難い記録用紙であり合格とし、評価が３以下のものは水性ペンによる筆記時に滲みが生じやすい記録用紙として不合格とした。
（４）表面強度
印刷適性試験機ＲＩ−３（明製作所製）を用いて、下記の印刷条件で情報記録層の表面に印刷を行い、下記評価基準で表面強度を評価した。
＜印刷条件＞
印刷インキ：ＳＭＸタックグレード２０（東洋インキ製）
インキ量：２ｇ
印刷速度：９０ｒｐｍ
＜評価基準＞
○：印刷時、紙ムケが発生しない。合格。
△：印刷時、紙ムケが発生するが僅かである。合格。
×：印刷時、紙ムケが多く発生する。不合格。
Table 1 shows an outline of the configuration of the recording paper obtained in each example and comparative example, and the evaluation results. In addition, each evaluation was performed by the following method.
(1) Bleeding Using an inkjet printer MP990 (manufactured by Canon Inc.), an image was printed on the surface of the information recording layer of the recording paper, and then the degree of bleeding of the printed image was visually evaluated. Evaluation was made into 5 grades, the thing with the least bleeding was set to 5, and the thing with the most bleeding was set to 1. Those with an evaluation of 2 or less have practical problems.
(2) Unevenness of printing After black, cyan, magenta, and yellow were printed on the printing surface with an inkjet printer MP990 (manufactured by Canon), the degree of unevenness of the printed portion was visually evaluated. The evaluation was made on a 5-level scale, with 5 being the least non-uniformity in the printed area and 1 being the most non-uniformity in the printed area. Those with an evaluation of 2 or less have problems in practical use.
(3) Pen writing size JAPAN TAPPI Paper Pulp Test Method No. 12: 2000 “Paperboard—Sizing test method—Pen writing method” The pen writing size of the information recording surface was evaluated. The evaluation was expressed from 0 to 6 using the grade of the same standard. Papers with an evaluation of 4 or more were judged to be acceptable recording papers that are less likely to bleed when written with a water-based pen, while papers with an evaluation of 3 or less were judged to be rejected as recording papers likely to bleed when written with an aqueous pen.
(4) Surface strength Using a printability tester RI-3 (manufactured by Meisei Seisakusho), printing was performed on the surface of the information recording layer under the following printing conditions, and the surface strength was evaluated according to the following evaluation criteria.
<Printing conditions>
Printing ink: SMX tack grade 20 (manufactured by Toyo Ink)
Ink amount: 2g
Printing speed: 90rpm
<Evaluation criteria>
○: Paper smear does not occur during printing. Pass.
Δ: Paper smearing occurs during printing, but slight. Pass.
×: Many paper smears occur during printing. failure.
表１から明らかなように、実施例１〜９の記録用紙は、滲み、印字ムラ、ペン書きサイズ度、表面強度の評価が良好であり、これより、インクジェット記録による記録画像の滲みと印字ムラが少なく、オフセット印刷を好適に行える表面強度を有し、水性ペンによる筆記時も滲みが生じ難い記録用紙であることが確認できた。また、実施例１〜９の記録用紙の外観や手触り感は、何れも紙の自然な風合いを持つものであった。 As is clear from Table 1, the recording papers of Examples 1 to 9 have good evaluation of bleeding, printing unevenness, pen writing sizing degree, and surface strength. Thus, it was confirmed that the recording paper had a surface strength suitable for offset printing, and hardly bleeds even when writing with an aqueous pen. Further, the appearance and feel of the recording papers of Examples 1 to 9 all had a natural texture of paper.
これに対して比較例１で得られた記録用紙は、情報記録層へのコットンリンターパルプの配合量が少なすぎるため、インクジェット記録によるインクの吸収性を満足できず、結果的に印字ムラを生じた。また、紙の自然な風合いを持つ記録用紙とは言えないものであった。比較例２で得られた記録用紙は、支持層中の内添サイズ剤の含有量が少なすぎるため、インクジェット記録による記録画像に滲みが生じ、また、ペン書きサイズ度の評価から水性ペンによる筆記時に滲みが生じやすいものであった。比較例３で得られた記録用紙は、支持層中の内添サイズ剤の含有量が多すぎるため、インクジェット記録による記録画像に印字ムラが生じた。比較例４で得られた記録用紙は、情報記録層へのコットンリンターパルプの配合量が多すぎるため、表面強度が低下してオフセット印刷に適さないものであった。 On the other hand, the recording paper obtained in Comparative Example 1 has too little blended amount of cotton linter pulp in the information recording layer, so that the ink absorbability by ink jet recording cannot be satisfied, resulting in uneven printing. It was. Further, it cannot be said to be a recording paper having a natural texture of paper. In the recording paper obtained in Comparative Example 2, the content of the internal sizing agent in the support layer is too small, so that a recorded image is blurred by ink jet recording, and writing with an aqueous pen is performed from the evaluation of pen writing size. Sometimes bleeding was likely to occur. Since the recording paper obtained in Comparative Example 3 contained too much content of the internal sizing agent in the support layer, printing unevenness occurred in the recorded image by ink jet recording. The recording paper obtained in Comparative Example 4 was unsuitable for offset printing because the amount of cotton linter pulp blended into the information recording layer was too large and the surface strength decreased.
Claims (5)