JP6089921B2 - ガラスペースト - Google Patents
ガラスペースト Download PDFInfo
- Publication number
- JP6089921B2 JP6089921B2 JP2013090516A JP2013090516A JP6089921B2 JP 6089921 B2 JP6089921 B2 JP 6089921B2 JP 2013090516 A JP2013090516 A JP 2013090516A JP 2013090516 A JP2013090516 A JP 2013090516A JP 6089921 B2 JP6089921 B2 JP 6089921B2
- Authority
- JP
- Japan
- Prior art keywords
- glass
- glass paste
- organic solvent
- lead
- paste
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
また、一方では、極性の小さい有機溶剤については、該バインダ樹脂を十分に溶解することができないため、該バインダ樹脂を用いたガラスペーストの適用が困難であった。
totHSP=sqrt(dD×dD+dP×dP+dH×dH)
dD:分子間の分散力に由来するエネルギー
dP:分子間の極性力に由来するエネルギー
dH:分子間の水素結合力に由来するエネルギー
本発明のガラスペーストが含有する上記有機溶剤は、エステル系溶剤およびグリコールエーテル系溶剤から選ばれる少なくとも1種を含むことが好ましい。
上記有機溶剤として、具体的には、クエン酸アセチルトリエチル、プロピレングリコールジアセテート、コハク酸ジエチル、エチルカルビトールアセテート、トリアセチン、アジピン酸ジメチル、安息香酸エチルおよび、プロピレングリコールモノフェニルエーテルとトリエチレングリコールジメチルエーテルの混合物からなる群から選ばれる少なくとも1種が好ましい。
本発明のガラスペーストは、ガラス転移点が300℃以下の無鉛ガラス(A)と、バインダ樹脂(B)と、totHSPが19.0〜20.0である有機溶剤(C)とを含有するガラスペーストである。
本発明のガラスペーストが含有する各成分について以下に具体的に説明する。
本発明のガラスペーストには、ガラス転移点(以下、必要に応じて「Tg」と記す。)が300℃以下の無鉛ガラス(A)が用いられる。
ここで、ガラス転移点とは、ガラスの構造が変化する温度であり、粘度が1013.3(dPa・s)になる温度である。被加工物に対する熱的影響を低減するためには、低温域で被加工物表面にガラス質の被膜を生成する必要があり、ガラス転移点が300℃以下であることが必要である。無鉛ガラス(A)のTgは、240〜300℃が好ましく、さらに240〜280℃がより好ましい。
P2O5は、ガラス形成酸化物であり、ガラスの熱安定性を高める必須成分である。P2O5の含有量が20%未満では、ガラス化が困難になることがあり、50%超では、得られる絶縁パターンや封着物の耐水性が低下することがある。P2O5の含有量は上記範囲中、特に20〜37%が好ましい。
発明のガラスペーストは、ビヒクルの一成分としてバインダ樹脂(B)を含有する。バインダ樹脂(B)としては、これを含有する本発明のガラスペーストを焼成する際に除去される樹脂であれば特に制限されない。本発明のガラスペーストは、上記無鉛ガラス(A)を含有することにより、その焼成温度は、概ね350〜485℃の範囲に設定することが好ましい。したがって、バインダ樹脂(B)は、該温度範囲で分解等により除去され、焼成後に残渣が生じない樹脂が好ましい。
バインダ樹脂(B)は、これらの1種を単独で用いてもよく、2種以上を併用してもよい。
本発明のガラスペーストは、ビヒクルの一成分として、totHSPが19.0〜20.0の有機溶剤(C)を含有する。有機溶剤(C)のtotHSPが上記範囲にあることで、本発明のガラスペーストは長期保存において分離沈降もなく、その粘度を安定して維持できるとともに、使用に際しては吸湿による粘度変化の影響が少ない。また、上記バインダ樹脂(B)に対する溶解性、特にポリプロピレンカーボネート等のポリアルキレンカーボネートに対する溶解性が良好である。
本発明のガラスペーストは、上記無鉛ガラス(A)、バインダ樹脂(B)、および有機溶剤(C)を含有する。本発明のガラスペーストにおける成分(A)〜(C)の含有量は上記のとおりであり、必要に応じて本発明の効果を損なわない範囲で任意成分の配合が可能である。
耐火性フィラー(D)は、ガラス質材料の熱膨張係数を調整する機能を有する。すなわち、ガラス質材料の熱膨張係数は、無鉛ガラス(A)と組み合わせる耐火性フィラー(D)の種類と配合量により適宜調整可能である。本発明のガラスペーストにおけるガラス質材料の熱膨張係数については、被加工物との接着強度などの観点から50×10−7〜110×10−7/℃とすることが好ましく、60×10−7〜100×10−7/℃がより好ましい。無鉛ガラス(A)の熱膨張係数を考慮すると、組合せて用いる耐火性フィラー(D)の熱膨張係数は、無鉛ガラス(A)の熱膨張係数より低いことが好ましく、具体的には、−20×10−7〜70×10−7/℃とすることが好ましく、20×10−7〜50×10−7/℃がより好ましい。
表1に示す有機溶剤(C)およびその他の有機溶剤について、有機溶剤の95質量部に対して、ポリプロピレンカーボネート(分子量:280,000)5質量部となる割合で密閉容器に投入し、80℃で24時間放置した後、目視で未融物の有無を確認した。未融物が無く溶解性が良好な場合を「○」と判定し、未融物が確認された場合を溶解不良「×」と判定した。結果を各有機溶剤のtotHSPおよび沸点とともに表1に示す。
(ガラス粉末(A11)の製造)
酸化物基準のモル百分率組成が、SnO:66.5%、P2O5:28.5%、ZnO:5%(ガラス転移点:280℃、熱膨張係数:128×10−7/℃)である無鉛ガラスを次のようにして製造した。
原料を上記組成となるように調合混合し、1100℃〜1200℃の電気炉中で石英ルツボを用いて2時間加熱し原料を溶解し溶融ガラスを得た。得られた溶融ガラスを急冷してフレーク状ガラスに成形した。該フレーク状ガラスをボールミルで粉砕した後、気流分級にて50%粒径(D50)が1.5μmのガラス粉末(A11)とした。
以下の無鉛ガラス(A)、耐火性フィラー(D)、有機溶剤(C)またはその他の有機溶剤、バインダ樹脂(B)を表2に示す組成で含有するガラスペーストを以下のようにして製造した。
バインダ樹脂(B):ポリプロピレンカーボネート(分子量:280,000)、ポリエチレンカーボネート(分子量:130,000)
耐火性フィラー(D):コージェライト(50%粒径(D50)2μm)、リン酸ジルコニウム(50%粒径(D50)10μm)、β−ユークリプタイト(50%粒径(D50)1μm)
有機溶剤(C):totHSPが19.0〜20.0の各種有機溶剤(なお、例13で用いた有機溶剤(C)は、プロピレングリコールモノフェニルエーテルとトリエチレングリコールジメチルエーテルを質量比1:1で混合した混合溶剤である。)
その他の有機溶剤:totHSPが19.0〜20.0の範囲外の各種有機溶剤
上記例1において、有機溶剤(C)に相当するトリアセチンを用いる変わりに、有機溶剤(C)に相当しない、すなわち、totHSPが19.0〜20.0の範囲外にあるその他の有機溶剤(炭酸プロピレンまたはN−メチル−2−ピロリドン)を用いる以外は、同様にして炭酸プロピレンを使った例14のガラスペースト14と、N−メチル−2−ピロリドンを用いた例16のガラスペースト16を製造した。また、例14において、バインダ樹脂(B)をポリエチレンカーボネートに変えた以外は、同様にして例15のガラスペースト15を製造した。最終的に得られたガラスペースト14〜16における組成(質量%)、および回転数10rpm時の粘度を表3に示す。
上記で得られた、ガラスペースト1〜16について、以下の方法で貯蔵安定性の評価を行った。また、ガラスペースト1、2、13およびガラスペースト14、16について以下の方法で加湿安定性評価を行った。評価結果を表2および表3に示す。
上記各例で得られたガラスペースト1〜16を、25℃、湿度50%の環境下に一週間、静置した後の粘度を測定し、予め測定しておいた初期粘度と比較した。粘度比較は、せん断速度10s-1での初期粘度をlogηA、上記環境で一週間静置した後のせん断速度10s-1での粘度をlogηB1として、次式:[logηB1−logηA]/[logηA]×100により粘度変化率(%)を評価した。なお、ここでの粘度logηは、コーンプレート型(25φ、2°)の粘弾性測定装置を用いて、25℃の条件下にて測定した。
さらに、上記環境で一週間静置した後のガラスペースト1〜16について、目視で分離沈殿の有無を確認した。結果を粘度変化率と合わせて表2および表3の評価欄に示す。
上記で得られたガラスペースト1、2、13およびガラスペースト14、16を、25℃、湿度70%の恒温恒湿槽内で0.5時間、曝露放置した後の粘度を測定し、予め測定しておいた初期粘度と比較した。粘度比較は、せん断速度10s-1での初期粘度をlogηA、上記条件で0.5時間曝露放置した後のせん断速度10s-1での粘度をlogηB2として、次式:[logηB2−logηA]/[logηA]×100を粘度変化率として評価した。結果を表2の評価欄に示す。なお、ここでの粘度logηは、コーンプレート型(25φ、2°)の粘弾性測定装置を用いて、25℃の条件下にて測定した。
また、ガラスペースト1およびガラスペースト2とガラスペースト13の結果では、70%の加湿環境下に置かれても粘度変化率が小さく、吸湿による影響が低いため粘度は安定である。それらに比べ、ガラスペースト14では、粘弾性測定装置の測定限界以上(推定変化率70%以上)の粘度変化が生じ、吸湿の影響を受けて極めて不安定である。同じく、ガラスペースト16においても、加湿後の粘度変化が大きく、粘度安定性は悪い。
Claims (6)
- ガラス転移点が300℃以下の無鉛ガラスと、ポリプロピレンカーボネートと、totHSPが19.0〜20.0である有機溶剤とを含有するガラスペースト。
- さらに耐火性フィラーを含有する請求項1記載のガラスペースト。
- 前記有機溶剤としてエステル系溶剤およびグリコールエーテル系溶剤から選ばれる少なくとも1種を含む請求項1または2記載のガラスペースト。
- 前記有機溶剤が、クエン酸アセチルトリエチル、プロピレングリコールジアセテート、コハク酸ジエチル、エチルカルビトールアセテート、トリアセチン、アジピン酸ジメチル、安息香酸エチルおよび、プロピレングリコールモノフェニルエーテルとトリエチレングリコールジメチルエーテルの混合物からなる群から選ばれる少なくとも1種である請求項1〜3のいずれか1項に記載のガラスペースト。
- 前記無鉛ガラスが、酸化物基準のモル百分率表示で、P2O5を20〜50%、SnOを30〜70%の、ZnOを0〜15%、R2O(RはLi、NaおよびKからなる群から選ばれる少なくとも1種)を0〜25%、B2O3を0〜20%、Al2O3を0〜5%、WO3を0〜5%含有する請求項1〜4のいずれか1項に記載のガラスペースト。
- 前記無鉛ガラスが、酸化物基準のモル百分率表示で、P2O5を20〜37%、SnOを59〜69%、ZnOを2〜7%、B2O3を0〜15%、Al2O3を0〜2%含有する請求項5記載のガラスペースト。