JP6081822B2 - Synthetic resin molded article exhibiting metallic color brightness and its manufacturing method - Google Patents

Synthetic resin molded article exhibiting metallic color brightness and its manufacturing method Download PDF

Info

Publication number
JP6081822B2
JP6081822B2 JP2013042740A JP2013042740A JP6081822B2 JP 6081822 B2 JP6081822 B2 JP 6081822B2 JP 2013042740 A JP2013042740 A JP 2013042740A JP 2013042740 A JP2013042740 A JP 2013042740A JP 6081822 B2 JP6081822 B2 JP 6081822B2
Authority
JP
Japan
Prior art keywords
synthetic resin
coat layer
resin molded
layer
metallic color
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2013042740A
Other languages
Japanese (ja)
Other versions
JP2014168916A (en
Inventor
貴 草野
貴 草野
正裕 藤江
正裕 藤江
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sakae Riken Kogyo Co Ltd
Oike and Co Ltd
Original Assignee
Sakae Riken Kogyo Co Ltd
Oike and Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sakae Riken Kogyo Co Ltd, Oike and Co Ltd filed Critical Sakae Riken Kogyo Co Ltd
Priority to JP2013042740A priority Critical patent/JP6081822B2/en
Publication of JP2014168916A publication Critical patent/JP2014168916A/en
Application granted granted Critical
Publication of JP6081822B2 publication Critical patent/JP6081822B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、自動車を初めとした車両に用いられる内外装品であって、表面側に金属色からなるきキラキラ感を呈する合成樹脂成形品、すなわち、金属色調の光輝を呈する合成樹脂製成形体に関するものである。   The present invention is an interior / exterior product used for vehicles such as automobiles, and is a synthetic resin molded product that exhibits a glittering feeling of a metallic color on the surface side, that is, a synthetic resin molded product that exhibits a glitter of metallic color tone It is about.

一般に、金属色を呈する合成樹脂製成形体としては、例えば特開２０００−１５９０３９号公報記載のものの如く、所定の合成樹脂製成形体の表面側に金属色を呈する部材、例えばクロム装飾条片を取付けること等によって形成させるようにしたものが挙げられる。または、特開２００４−２５１８６８号公報記載のものの如く、所定の金属材の蒸着されたフィルムを合成樹脂製成形体の表面側に付着させることによって形成させるようにしたもの等が挙げられる。   In general, as a synthetic resin molded body exhibiting a metal color, for example, a member exhibiting a metal color on the surface side of a predetermined synthetic resin molded body, for example, a chromium decorative strip, as described in JP 2000-159039 A, for example. What was made to form by attaching etc. is mentioned. Or what was made to form by making the surface by which the film | membrane on which the predetermined | prescribed metal material was vapor-deposited was made to adhere to the surface side of a synthetic resin molded body like the thing of Unexamined-Japanese-Patent No. 2004-251868 is mentioned.

特開２０００−１５９０３９号（特許第３３６６２９９号）公報Japanese Unexamined Patent Publication No. 2000-159039 (Japanese Patent No. 3366299) 特開２００４−２５１８６８号公報JP 2004-251868 A

ところで、上記従来のものにおいては、金属色を呈するフィルムの形成、更にはこのようなフィルムの合成樹脂製成形体表面への貼付作業等が必要となり、所定の金属色を呈する合成樹脂製成形体の形成には多くの時間あるいは工数（手間）を要すると言う問題点がある。このような問題点を解決するために、所定の合成樹脂製成形体を基礎に、この表面側に、金属色を呈するメッキ層を設けるとともに、その表面側に所定の金属製の微細板状片を含む透明体からなるベースコート層等を、順次単純な塗布手段にて形成させるようにした金属色調のキラキラ感を呈する合成樹脂製成形体を得ようとするのが、本発明の目的（課題）である。   By the way, in the said conventional thing, formation of the film which exhibits a metal color, and the affixing operation | work to the surface of the synthetic resin molding body of such a film are required, and the synthetic resin molding body which exhibits a predetermined metal color etc. There is a problem that it takes a lot of time or man-hours (labor) to form. In order to solve such problems, a plating layer exhibiting a metallic color is provided on the surface side based on a predetermined synthetic resin molded body, and a predetermined metal fine plate-like piece is provided on the surface side. It is an object (problem) of the present invention to obtain a synthetic resin-made molded body that exhibits a metallic color glittering feeling in which a base coat layer made of a transparent body containing sucrose is sequentially formed by a simple coating means. It is.

上記課題を解決するために、本発明においては次のような手段を講ずることとした。すなわち、請求項１記載の発明である第一の発明においては、金属色調の光輝を呈する合成樹脂製成形体に関して、ＡＢＳ樹脂を含む所定の合成樹脂製成形体を基礎に形成される基盤層と、当該基盤層の表面上に形成されるものであって所定の金属色を呈するメッキ層と、当該メッキ層表面上に形成されるものであって、透明な合成樹脂成分からなる塗料を基礎に、その内部に微細なアルミニウム金属片を基に形成されるとともに、その平面形態が所定の平面面積を有する平滑な面からなる平板状微細金属片を無数に有するベースコート層と、当該ベースコート層の表面側に設けられるものであって透明な合成樹脂成分からなる塗料を基礎とするクリアコート層と、からなるようにした構成を採ることとした。 In order to solve the above problems, the following measures are taken in the present invention. That is, in the first invention which is the invention according to claim 1, the synthetic resin molded body exhibiting a metallic color brilliancy, and a base layer formed on the basis of a predetermined synthetic resin molded body containing an ABS resin; A plating layer formed on the surface of the base layer and exhibiting a predetermined metal color, and formed on the surface of the plating layer, and based on a paint composed of a transparent synthetic resin component A base coat layer that is formed on the basis of fine aluminum metal pieces and has innumerable flat fine metal pieces each having a flat surface having a predetermined plane area, and the surface of the base coat layer A clear coat layer based on a paint made of a transparent synthetic resin component and provided on the side was adopted.

請求項１記載の発明である第一の発明のものにおいては、本合成樹脂製成形体の表面からは、他の独立した光源からの光の照射に対して、金属色調のキラキラ感からなる光輝が発せられることとなる。そして、このような光輝は、夜間等の暗い場所において光が照射された場合に、より強く形成されることとなり、自動車等の車両の一部に使用された場合、視認性に優れた標識としての機能が発揮されることとなる。その結果、安全性がより高められることとなる。   In the first invention according to the first aspect of the present invention, the surface of the synthetic resin molded body has a glittering metallic color with respect to the irradiation of light from another independent light source. Will be emitted. And, such radiance will be formed stronger when light is irradiated in dark places such as at night, and as a sign with excellent visibility when used in a part of vehicles such as automobiles. The function of will be demonstrated. As a result, safety is further improved.

また、本発明のものにおいては、金属メッキ色を基礎に、その上側（表面側）に金属色調のキラキラ感からなる光輝が発せられることとなり、光り輝いたキラキラ感がより強調されることとなる。そして、このような光輝は、夜間等の暗い場所において光が照射された場合に、より強く形成されることとなり、自動車等の車両の一部に使用された場合、視認性に優れた標識としての機能が発揮されることとなる。その結果、安全性がより高められることとなる。 Moreover, in the thing of this invention, the brightness | luminance which consists of a metallic color tone glittering will be emitted on the upper side (surface side) based on a metal plating color, and the glittering glittering feeling will be emphasized more. And, such radiance will be formed stronger when light is irradiated in dark places such as at night, and as a sign with excellent visibility when used in a part of vehicles such as automobiles. The function of will be demonstrated. As a result, safety is further improved.

また、本発明のものにおいては、キラキラ感からなる光輝がより強く発せられることとなる。具体的には、キラキラ感を呈する金属片が、微細なものではあるが、その表面形態が平板状の平面形態を有するようになっており、微視的に見て平面部がより多く形成されるようになっている。従って、粒状の微細金属物体が存在するもの等に較べて、入射光に対して平面反射される割合が局部的に多くなり、光反射によって形成されるキラキラ感からなる光輝は、より増大化されることとなる。その結果、視認性の向上が、より図られることとなる。 Moreover, in the thing of this invention, the brightness which consists of a glittering feeling will be emitted more strongly. Specifically, although the metal piece exhibiting a glittering feeling is fine, its surface form has a flat plate form, and more planar parts are formed when viewed microscopically. It has become so. Therefore, compared to the case where there is a granular fine metal object, etc., the ratio of the plane reflection with respect to the incident light is locally increased, and the brightness of the glittering feeling formed by the light reflection is further increased. The Rukoto. As a result, the visibility is further improved.

また、本発明のものにおいては、金属色調のキラキラ感からなる光輝を呈する合成樹脂製成形体を、ＡＢＳ樹脂を初めとした所定の合成樹脂製成形体を基礎にして、その表面側に微細な金属製平板状片を有する透明な合成樹脂製溶材（合成樹脂製塗料）等の塗布にて形成させることができるようになる。すなわち、金属色調のキラキラ感からなる光輝を呈する合成樹脂製成形体が、簡単な手段（方法）にて効率良く形成されることとなる。 Further, in the present invention, a synthetic resin molded body exhibiting a brilliant feeling of metallic color glitter is formed on the surface side of a predetermined synthetic resin molded body such as an ABS resin. flat metal plate-shaped piece transparent with a synthetic resin welding material so that it is possible to form at (synthetic resin coating) such as a coating. That is, a synthetic resin molded body exhibiting a brilliant brightness with a metallic color glitter can be efficiently formed by a simple means (method).

また、本発明のものにおいては、金属色調のキラキラ感からなる光輝を呈する合成樹脂製成形体を、表面に金属メッキ層を有する合成樹脂製成形体を基礎にして、その表面側に微細な金属製平板状片を有する透明な合成樹脂製溶材（合成樹脂製塗料）等の塗布にて形成させることができるようになる。すなわち、金属色調のキラキラ感からなる光輝を呈する合成樹脂製成形体が、簡単な手段（方法）にて効率良く形成されることとなる。 Further, in the present invention, a synthetic resin molded body exhibiting a glitter composed of metallic color glitter is formed on the basis of a synthetic resin molded body having a metal plating layer on the surface, and a fine metal is formed on the surface side. it is possible to form by a coating such as a transparent synthetic resin welding material (synthetic resin coating) having a manufacturing flat plate-like pieces. That is, a synthetic resin molded body exhibiting a brilliant brightness with a metallic color glitter can be efficiently formed by a simple means (method).

本発明にかかる金属色調光輝を呈する合成樹脂製成形体の全体構成を示す断面図である。It is sectional drawing which shows the whole structure of the synthetic resin molded object which exhibits the metal color brightness effect concerning this invention. 本発明の主要部を成す金属製微細板状片の具体的構成を示す断面図である。It is sectional drawing which shows the specific structure of the metal fine plate-shaped piece which comprises the principal part of this invention. 本発明にかかる金属色調光輝を呈する合成樹脂製成形体の製造方法を示す工程図である。It is process drawing which shows the manufacturing method of the synthetic resin molded object which exhibits the metallic color brightness effect concerning this invention.

本発明を実施するための形態について、図１ないし図３を基に説明する。本実施の形態にかかるものは、図１に示す如く、ＡＢＳ樹脂を含む所定の合成樹脂製成形体を基礎に形成される基盤層５と、当該基盤層５の表面上に形成されるものであって所定の金属色を呈するメッキ層５５と、当該メッキ層５５表面上に形成されるものであって、透明な合成樹脂成分からなる塗料を基礎に、その内部に微細なアルミニウム金属片を基に形成される金属製微細板状片１を無数に有するベースコート層５１と、当該ベースコート層５１の表面側に設けられるものであって透明な合成樹脂成分からなる塗料を基礎とするクリアコート層５２と、からなることを基本とするものである。このような構成からなるものにおいて、上記ベースコート層５１内に設けられる金属製微細板状片１は、例えば図２に示す如く、所定の平面面積を有する平板状微細片１１を基礎に形成されるようになっているものである。なお、上記金属製微細板状片１としては、本実施の形態においては、２５〜５００μｍの大きさ（サイズ）のものが採用されるようになっている。そして、このような金属製微細板状片１が上記ベースコート層５１内に、その容量において０．１〜５％程度含まれるようになっている。   A mode for carrying out the present invention will be described with reference to FIGS. 1 to 3. As shown in FIG. 1, the present embodiment is formed on a base layer 5 formed on the basis of a predetermined synthetic resin molded body containing an ABS resin, and on the surface of the base layer 5. A plating layer 55 exhibiting a predetermined metal color, and formed on the surface of the plating layer 55, and based on a coating made of a transparent synthetic resin component, a fine aluminum metal piece is formed on the inside thereof. A base coat layer 51 having innumerable metal fine plate-like pieces 1 formed on the base coat layer 51 and a clear coat layer 52 provided on the surface side of the base coat layer 51 and based on a paint made of a transparent synthetic resin component. It is based on that consists of. In such a configuration, the metal fine plate-like piece 1 provided in the base coat layer 51 is formed on the basis of a plate-like fine piece 11 having a predetermined plane area, for example, as shown in FIG. It is something like that. In the present embodiment, the metal fine plate-like piece 1 has a size (size) of 25 to 500 μm. And such a metal fine plate-shaped piece 1 is contained in the base coat layer 51 by about 0.1 to 5% in its capacity.

なお、この金属製微細板状片１は、アルミニウム金属製箔を基に形成されるものであって、その具体的形状は、図２に示す如く、その表面が所定の平面面積を有する平滑な面１１１からなるようになっているものである。従って、その表面１１１に光（光線）が入射したとき（図１の入射光（イ）参照）に、この表面１１１を反射面とする反射光（図１の（ロ）参照）は、ある程度の幅をもった平行光線として反射するようになる。すなわち、一つの金属製微細板状片１について見れば、その表面１１１からの反射光（ロ）は、常に平行な光束となり、従来の粒状体による反射光のような乱反射状態を呈するようなことがない。その結果、一つの金属製微細板状片１からの反射光は強い状態となり、この一つの金属製微細板状片１からの反射光（ロ）にて認知される光輝（キラキラ感）は見る者にとって強く認識されることとなる。   The metal fine plate-like piece 1 is formed on the basis of an aluminum metal foil, and its specific shape is a smooth surface having a predetermined plane area as shown in FIG. The surface 111 is formed. Therefore, when light (light rays) is incident on the surface 111 (see incident light (A) in FIG. 1), the reflected light (see (B) in FIG. 1) having the surface 111 as a reflecting surface has a certain amount. Reflected as parallel rays with a width. In other words, when one metal fine plate-like piece 1 is viewed, the reflected light (b) from the surface 111 thereof is always a parallel light beam, and exhibits a diffuse reflection state like the reflected light by the conventional granular material. There is no. As a result, the reflected light from one metal fine plate-like piece 1 is in a strong state, and the brightness (brightness) recognized by the reflected light (b) from this one metal fine plate-like piece 1 is seen. Will be strongly recognized by the person.

なお、上記ベースコート層５１は、一般的な合成樹脂製塗料３を基礎に形成されるものであって、本塗料３の中に、上記金属製微細板状片１の他に所定の着色顔料２が含まれるようになっているものである。この着色顔料２の種類を適宜選ぶことによって、最終製品におけるメタリック調を基調とした色合いを適宜調整することができるようになる。なお、このような構成からなる本ベースコート層５１の厚さとしては約１５μｍ以上の厚味が必要とされる。そして、このようなベースコート層５１の、その上面側（表面側）には透明な性状を有するクリアコート層５２が設けられるようになっている。このクリアコート層５２は、主に透明な合成樹脂製塗料にて形成されるようになっているものであり、その厚さとしては約１５μｍ以上の厚味が必要とされる。なお、このような構成からなるものにおいて、本実施の形態においては、上記メッキ層５５を省略するようにしたものも考えられる。   The base coat layer 51 is formed on the basis of a general synthetic resin paint 3, and a predetermined color pigment 2 in addition to the metal fine plate-like piece 1 is included in the paint 3. Is to be included. By appropriately selecting the type of the color pigment 2, it is possible to appropriately adjust the color tone based on the metallic tone in the final product. The base coat layer 51 having such a structure needs to have a thickness of about 15 μm or more. And the clear coat layer 52 which has a transparent property is provided in the upper surface side (surface side) of such a base coat layer 51. As shown in FIG. The clear coat layer 52 is mainly formed of a transparent synthetic resin paint, and a thickness of about 15 μm or more is required. In addition, in the present embodiment, it is possible to omit the plating layer 55 in the present embodiment.

このような構成を採ることにより、本実施の形態のものにおいては、本合成樹脂製成形体からは、光（光束）の入射に対して強い反射光（光束）が発せられることとなる。特に、本実施の形態のものにおいては、本合成樹脂製成形体を形成するベースコート層５１内には、金属製微細板状片１が無数に存在している。そして、この金属製微細板状片１の、その表面は平滑な、かつ、微視的に見て、ある程度の平面面積を有するようになっているものである。従って、この金属製微細板状片１の表面に入射した光束は、平行な光束となって特定方向に反射することとなる。その結果、上記反射光（図１の（ロ）参照）は輝いた状態となり、全体的に金属色調のキラキラ感に優れた見栄えを呈することとなる。これによって、本製品が自動車等の車両の一部に使用された場合、夜間に光が照射されたような場合において、視認性に優れた標識としての機能が発揮されることとなる。その結果、安全性の向上等が図られることとなる。   By adopting such a configuration, in the present embodiment, the synthetic resin molded body emits reflected light (light beam) that is strong against the incidence of light (light beam). In particular, in the present embodiment, there are innumerable metal fine plate-like pieces 1 in the base coat layer 51 that forms the synthetic resin molded body. The surface of the metal fine plate-like piece 1 is smooth and has a certain planar area as viewed microscopically. Therefore, the light beam incident on the surface of the metal fine plate-like piece 1 becomes a parallel light beam and is reflected in a specific direction. As a result, the reflected light (see (b) in FIG. 1) is in a shining state, and the overall appearance is excellent in the glitter of the metallic tone. As a result, when this product is used in a part of a vehicle such as an automobile, it functions as a sign having excellent visibility when light is irradiated at night. As a result, the safety is improved.

次に、上記構成からなる本実施の形態のものに関する、その製造方法について説明する。このものは、図３に示す如く、ＡＢＳ樹脂を含む所定の合成樹脂製成形体からなる基盤層５の、その表面側に所定の金属色を呈するメッキ層５５を設けるメッキ工程（Ｂ）と、当該メッキ層５５の表面側に透明な合成樹脂成分からなる塗料３を基礎に、その内部に金属製微細板状片１を無数に有する溶材を塗布することによって得られるベースコート層５１を形成させるベースコート層形成工程（Ｃ）と、当該ベースコート層５１の表面側に設けられるものであって透明な合成樹脂成分からなる塗料を塗布することによって得られるクリアコート層５２を形成させるクリアコート層形成工程（Ｄ）と、からなることを基本とするものである。   Next, the manufacturing method relating to the present embodiment configured as described above will be described. As shown in FIG. 3, this is a plating step (B) in which a plating layer 55 having a predetermined metal color is provided on the surface side of a base layer 5 made of a predetermined synthetic resin molded body containing an ABS resin, A base coat for forming a base coat layer 51 obtained by applying a coating material made of a transparent synthetic resin component on the surface side of the plating layer 55 and applying an infinite number of metal fine plate-like pieces 1 therein. A layer forming step (C) and a clear coat layer forming step (formation step) for forming a clear coat layer 52 provided on the surface side of the base coat layer 51 and obtained by applying a paint made of a transparent synthetic resin component ( D).

このような基本工程からなるものにおいて、上記メッキ工程（Ｂ）の前には、表面をメッキが付き易い状態にするための前処理工程（Ａ）が施されるようになっている。また、上記メッキ工程（Ｂ）としては、主に一般的な電気メッキ工程が採られることとなる。なお、本メッキ処理（メッキ工程）に換わって、ＡＬ金属等の金属蒸着手段等が採られる場合もある。また、このような工程からなるものにおいて、メッキ工程（Ｂ）を省略することも考えられる。このようなメッキ工程（Ｂ）を省略することによって、その前処理工程（Ａ）も不要となり、本合成樹脂製成形体の製造工程が簡略化され、より製造コストの低減化が図られることとなる。    In such a basic process, before the plating process (B), a pretreatment process (A) for making the surface easy to be plated is performed. Moreover, as said plating process (B), a general electroplating process will be mainly taken. In place of the main plating process (plating process), metal vapor deposition means such as AL metal may be employed. Further, in the case of such a process, the plating process (B) may be omitted. By omitting such a plating step (B), the pretreatment step (A) is also unnecessary, the manufacturing process of the synthetic resin molded body is simplified, and the manufacturing cost is further reduced. Become.

次に、このようなメッキ処理の施された表面側に、本実施の形態においてはベースコート層５１を形成することとなるものであって内部に金属性微細板状片１を無数に有する合成樹脂製溶材からなる塗料を塗布する（ベースコート層形成工程（Ｃ））。なお、上記工程（Ｃ）における塗布手段としては、一般的なスプレイガンを用いたスプレイ塗装あるいは刷毛塗り等の手段が採られることとなる。そして、このような状態のものを乾燥室等へと送り、そこで乾燥処理を施す。なお、このような塗布工程（Ｃ）、（Ｄ）における塗装ブース内の条件としては、１５℃〜２５℃の温度、更にはブース内湿度が７８％以下に設定されるようになっている。    Next, in this embodiment, the base coat layer 51 is formed on the surface side subjected to such plating treatment, and a synthetic resin having innumerable metallic fine plate-like pieces 1 inside. A paint made of a melted material is applied (base coat layer forming step (C)). In addition, as an application | coating means in the said process (C), means, such as spray coating using a general spray gun, or brush coating, will be taken. And the thing of such a state is sent to a drying chamber etc., and a drying process is given there. In addition, as conditions in such a coating booth in such application | coating processes (C) and (D), the temperature of 15 degreeC-25 degreeC and also the humidity in a booth are set to 78% or less.

次に、上記工程（Ｃ）にてベースコート層５１の形成され、その後乾燥処理の施された状態のものの、そのベースコート層５１の表面側（上側）に、透明な合成樹脂製成形体を形成させるクリアコート層形成工程（Ｄ）を施す。このクリアコート層形成工程（Ｄ）は透明な合成樹脂製塗料の塗布によって形成される。なお、この塗布作業も、上記ベースコート層形成工程（Ｃ）のところで述べたと同様、一般的なスプレイ塗布手段あるいは刷毛塗り手段等が採られることとなる。なお、このクリアコート層５１は、必ずしも必要とされるものではなく、場合によってはクリアコート層５２形成のための工程（クリアコート層形成工程（Ｄ））を省略することも可能である。これによって、本合成樹脂製成形体の製造工程を簡略化し、製造コストの低減化を図ることができるようになる。そして、このようにして形成された合成樹脂製成形体を所定の乾燥炉等へと送り、ここで乾燥処理を施す。このような乾燥処理の施される乾燥炉内は、６０℃〜９０℃の温度状態に保たれるようになっている。このような工程を採ることにより、本実施の形態のものにおいては、金属色調のキラキラ感からなる光輝を呈する合成樹脂製成形体を、表面に金属メッキ層を有する合成樹脂製成形体を基礎にして、その表面側に微細な金属製微細板状片１を有する透明な合成樹脂製溶材（合成樹脂製塗料）の塗布手段にて形成させることができるようになる。すなわち、金属色調のキラキラ感からなる光輝を呈する合成樹脂製成形体を、簡単な手段（方法）にて効率良く形成させることができることとなる。    Next, a transparent synthetic resin molded body is formed on the surface side (upper side) of the base coat layer 51 in a state where the base coat layer 51 is formed in the step (C) and then dried. A clear coat layer forming step (D) is performed. This clear coat layer forming step (D) is formed by applying a transparent synthetic resin paint. In this application operation, as described in the base coat layer forming step (C), a general spray application means or brush application means is employed. The clear coat layer 51 is not necessarily required, and in some cases, the step for forming the clear coat layer 52 (clear coat layer forming step (D)) can be omitted. As a result, the manufacturing process of the synthetic resin molded body can be simplified, and the manufacturing cost can be reduced. Then, the synthetic resin molded body thus formed is sent to a predetermined drying furnace or the like, and is subjected to a drying process. The inside of the drying furnace subjected to such a drying process is kept at a temperature of 60 ° C. to 90 ° C. By adopting such a process, in the present embodiment, a synthetic resin molded body exhibiting a brilliant feeling of metallic color glitter is used as a basis. Thus, it can be formed by a coating means of a transparent synthetic resin solution (synthetic resin paint) having fine metal fine plate-like pieces 1 on the surface side. That is, a synthetic resin molded body exhibiting a brilliant brightness with a metallic tone can be efficiently formed by simple means (method).

１ 金属製微細板状片
１１ 平板状微細片
１１１ 表面
２ 着色顔料
３ 塗料
５ 基盤層
５１ ベースコート層
５２ クリアコート層
５５ メッキ層





DESCRIPTION OF SYMBOLS 1 Metal fine plate-like piece 11 Flat plate-like fine piece 111 Surface 2 Color pigment 3 Paint 5 Base layer 51 Base coat layer 52 Clear coat layer 55 Plating layer





Claims (1)

ＡＢＳ樹脂を含む所定の合成樹脂製成形体を基礎に形成される基盤層と、当該基盤層の表面上に形成されるものであって所定の金属色を呈するメッキ層と、当該メッキ層表面上に形成されるものであって、透明な合成樹脂成分からなる塗料を基礎に、その内部に微細なアルミニウム金属片を基に形成されるとともに、その平面形態が所定の平面面積を有する平滑な面からなる平板状微細金属片を無数に有するベースコート層と、当該ベースコート層の表面側に設けられるものであって透明な合成樹脂成分からなる塗料を基礎とするクリアコート層と、からなることを特徴とする金属色調光輝を呈する合成樹脂製成形体。 A foundation layer formed on the basis of predetermined synthetic resin molded article comprising ABS resin, and a plating layer that exhibits a predetermined metallic color be one that is formed on the surface of the base layer, the plating layer on the surface A smooth surface formed on the basis of a coating made of a transparent synthetic resin component and based on a fine aluminum metal piece and having a predetermined planar area A base coat layer having an infinite number of flat fine metal pieces , and a clear coat layer based on a paint made of a transparent synthetic resin component provided on the surface side of the base coat layer. A molded product made of synthetic resin exhibiting a metallic color brightness.
JP2013042740A 2013-03-05 2013-03-05 Synthetic resin molded article exhibiting metallic color brightness and its manufacturing method Active JP6081822B2 (en)