JP5952100B2 - Curable resin composition - Google Patents
Curable resin composition Download PDFInfo
- Publication number
- JP5952100B2 JP5952100B2 JP2012136135A JP2012136135A JP5952100B2 JP 5952100 B2 JP5952100 B2 JP 5952100B2 JP 2012136135 A JP2012136135 A JP 2012136135A JP 2012136135 A JP2012136135 A JP 2012136135A JP 5952100 B2 JP5952100 B2 JP 5952100B2
- Authority
- JP
- Japan
- Prior art keywords
- polyphenylene ether
- mass
- resin composition
- curable resin
- molecular weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、電子基板材料として好適な、ポリフェニレンエーテルを含む硬化性樹脂組成物に関する。更に本発明は、該硬化性樹脂組成物と基材とを含むプリント配線板用プリプレグ、及び該硬化性樹脂組成物の硬化物と基材とを含むプリント配線板に関する。 The present invention relates to a curable resin composition containing polyphenylene ether suitable as an electronic substrate material. Furthermore, the present invention relates to a printed wiring board prepreg comprising the curable resin composition and a substrate, and a printed wiring board comprising a cured product of the curable resin composition and a substrate.
近年、接合、実装技術の向上とともに、電子機器に搭載される半導体デバイスの高集積化、パッケージの精緻化、及びプリント配線板の高密度配線化に伴い、電子機器は継続して進展している。この種の電子機器を構成するプリント配線板では、多層化及び微細配線化の両者が進行している。情報処理の高速化のために要求される信号伝達速度の高速化を実現するためには、使用される材料の誘電率を低減することが有効である。ポリフェニレンエーテルは誘電率、誘電正接等の高周波特性（すなわち誘電特性）が優れているため、高周波数帯を利用する電子機器のプリント配線板用の材料として好適である。 In recent years, along with improvements in bonding and mounting technologies, electronic devices have been continuously developed along with higher integration of semiconductor devices mounted on electronic devices, more sophisticated packages, and higher density of printed wiring boards. . In a printed wiring board constituting this type of electronic device, both multilayering and fine wiring have progressed. It is effective to reduce the dielectric constant of the material used in order to realize a high signal transmission speed required for high-speed information processing. Polyphenylene ether is suitable as a material for printed wiring boards of electronic equipment using a high frequency band because polyphenylene ether has excellent high-frequency characteristics (that is, dielectric characteristics) such as dielectric constant and dielectric loss tangent.
特許文献１には、熱可塑性樹脂であるポリフェニレンエーテルの耐熱性及び寸法安定性を向上させる技術として、ポリフェニレンエーテルとトリアリルイソシアヌレート（ＴＡＩＣ）とを含む樹脂組成物が記載されている。特許文献２では、耐薬品性を向上させる技術として、ポリフェニレンエーテルと無水マレイン酸との反応物であるマレイン化ポリフェニレンエーテルと、ＴＡＩＣとを含む樹脂組成物が記載されている。しかしながら、特許文献１又は２に記載されている樹脂組成物においては、樹脂自身の融点が高く、通常のプレス成形温度では溶融時の粘度が高すぎ、多層プリント配線板の内層導体パターン層を形成するための充填が困難である。よって配線板の多層化が困難であるという課題が存在していた。 Patent Document 1 describes a resin composition containing polyphenylene ether and triallyl isocyanurate (TAIC) as a technique for improving the heat resistance and dimensional stability of polyphenylene ether which is a thermoplastic resin. In Patent Document 2, as a technique for improving chemical resistance, a resin composition containing maleated polyphenylene ether which is a reaction product of polyphenylene ether and maleic anhydride and TAIC is described. However, in the resin composition described in Patent Document 1 or 2, the melting point of the resin itself is high, and the viscosity at the time of melting is too high at a normal press molding temperature, so that an inner conductor pattern layer of a multilayer printed wiring board is formed. Filling is difficult. Therefore, there is a problem that it is difficult to make a multilayer wiring board.
上記のような成形性の課題を改善する目的で、特許文献３には、低分子量のポリフェニレンエーテルを用いることにより、溶融樹脂の流動性が良好で、通常のプレス成形温度において、成形性に優れ、多層化が可能なポリフェニレンエーテル樹脂組成物が記載されている。しかしながら、ポリフェニレンエーテルの分子量を小さくすることは、得られる積層板の耐熱性が低下するという問題、及びポリフェニレンエーテルの末端水酸基の数が増加するために誘電率及び誘電正接が大きくなるという問題を招来する。よって上記技術もまた、プリント配線板に用いるには十分なものではなかった。 For the purpose of improving the above-described problems of moldability, Patent Document 3 uses a low-molecular-weight polyphenylene ether, so that the fluidity of the molten resin is good and the moldability is excellent at a normal press molding temperature. A polyphenylene ether resin composition that can be multilayered is described. However, reducing the molecular weight of polyphenylene ether causes problems such as a decrease in heat resistance of the resulting laminate and an increase in dielectric constant and dielectric loss tangent due to an increase in the number of terminal hydroxyl groups of polyphenylene ether. To do. Therefore, the above technique is also not sufficient for use in a printed wiring board.
ポリフェニレンエーテルの低分子量化に伴うこれら問題を改善する目的で、特許文献４及び５には、低分子量ポリフェニレンエーテルの末端水酸基を反応性の官能基で封止した、低分子量・末端封止ポリフェニレンエーテルを用いることが記載されている。これら該ポリフェニレンエーテルを用いることで、プレス成形時の良好な成形性が維持されたまま、耐熱性の低下、又は誘電率及び誘電正の低下が生じない硬化物が得られることが記載されている。また、特許文献４には、低分子量・末端封止ポリフェニレンエーテルと通常ポリフェニレンエーテルとを混合して用いる方法も記載されている。特許文献４の参考例７では数平均分子量１４，０００のポリフェニレンエーテルと数平均分子量２，５００の末端エテニルベンジル化ポリフェニレンエーテルとが５：７０の混合比で用いられており、参考例８では数平均分子量１４，０００のポリフェニレンエーテルと数平均分子量２，５００の末端エテニルベンジル化ポリフェニレンエーテルとが５０：６０の混合比で用いられている。 For the purpose of improving these problems associated with the lowering of the molecular weight of polyphenylene ether, Patent Documents 4 and 5 disclose low molecular weight / end-capped polyphenylene ethers in which the terminal hydroxyl groups of low molecular weight polyphenylene ethers are sealed with reactive functional groups. Is described. It is described that by using these polyphenylene ethers, a cured product that does not cause a decrease in heat resistance or a decrease in dielectric constant and dielectric positive while maintaining good moldability during press molding is described. . Patent Document 4 also describes a method in which a low molecular weight / end-capped polyphenylene ether and a normal polyphenylene ether are mixed and used. In Reference Example 7 of Patent Document 4, polyphenylene ether having a number average molecular weight of 14,000 and terminal ethenylbenzylated polyphenylene ether having a number average molecular weight of 2,500 are used in a mixing ratio of 5:70. A polyphenylene ether having a number average molecular weight of 14,000 and a terminal ethenylbenzylated polyphenylene ether having a number average molecular weight of 2,500 are used in a mixing ratio of 50:60.
通常分子量のポリフェニレンエーテルと低分子量化したポリフェニレンエーテルとを混合して用いる方法は、特許文献６、７等にも記載されている。特許文献６には、低分子量・末端官能化ポリフェニレンエーテルの耐熱性を向上させる目的で、低分子量・末端官能化ポリフェニレンエーテルに通常ポリフェニレンエーテルを０．１％〜９．１％配合させる技術が記載されている。 A method of using a mixture of a normal molecular weight polyphenylene ether and a low molecular weight polyphenylene ether is also described in Patent Documents 6, 7 and the like. Patent Document 6 describes a technique in which 0.1% to 9.1% of polyphenylene ether is usually added to low molecular weight / terminal functionalized polyphenylene ether for the purpose of improving the heat resistance of the low molecular weight / terminal functionalized polyphenylene ether. Has been.
特許文献７には、アシル基又は求電子基で官能化した通常分子量ポリフェニレンエーテル（固有粘度０．３５ｄｌ／ｇ以上）と官能化しない低分子量化ポリフェニレンエーテル（固有粘度約０．１５〜０．３５ｄｌ／ｇ）とを、４０〜５５：６０〜４５の割合で混合したポリフェニレンエーテルを用いる樹脂組成物が記載されている。 Patent Document 7 discloses a normal molecular weight polyphenylene ether functionalized with an acyl group or an electrophilic group (inherent viscosity of 0.35 dl / g or more) and a non-functionalized low molecular weight polyphenylene ether (inherent viscosity of about 0.15 to 0.35 dl). / G) is described in a resin composition using polyphenylene ether mixed at a ratio of 40 to 55:60 to 45.
しかしながら、特許文献４及び５に記載の低分子量・末端官能化ポリフェニレンエーテルは、末端の水酸基を封止していることに起因すると推測される問題を有していた。すなわち、このようなポリフェニレンエーテルは、ガラスクロス等の基材又は銅箔等との接着性が十分でなく、積層板の場合の層間の剥離強度、又は該ポリフェニレンエーテルと銅箔等との剥離強度が低い、或いは耐吸水性及びはんだ耐熱性が十分でないという問題があった。また、特許文献４の参考例７及び８に記載されている積層板では、Ｔｇ、誘電率、誘電正接、吸湿率、はんだ耐熱性等の特性が、末端エテニルベンジル化ポリフェニレンエーテル単独のものと同等であり、低分子量・末端エテニルベンジル化ポリフェニレンエーテルと通常ポリフェニレンエーテルとを混合して用いることにより何ら特性が向上されているものではなかった。 However, the low molecular weight and terminal functionalized polyphenylene ethers described in Patent Documents 4 and 5 have a problem that is presumed to be caused by sealing the terminal hydroxyl group. That is, such polyphenylene ether has insufficient adhesion to a substrate such as a glass cloth or copper foil, and the peel strength between layers in the case of a laminated board, or the peel strength between the polyphenylene ether and copper foil, etc. However, there is a problem that water resistance is low or water absorption resistance and solder heat resistance are not sufficient. Further, in the laminates described in Reference Examples 7 and 8 of Patent Document 4, characteristics such as Tg, dielectric constant, dielectric loss tangent, moisture absorption, solder heat resistance, etc. are those of terminal ethenylbenzylated polyphenylene ether alone. The characteristics were not improved by using a mixture of low molecular weight, terminal ethenylbenzylated polyphenylene ether and normal polyphenylene ether.
また、特許文献６には、通常分子量のポリフェニレンエーテルを配合することにより、硬化樹脂板の熱変形温度（ＨＤＴ）が約１００℃から約１１０℃まで向上することが記載されているのみで、本発明の用途であるプリント配線板に必要な、樹脂硬化物と基材との複合体の特性（特に成形性、剥離強度、耐吸水性、はんだ耐熱性等）については何ら記載されてない。 Further, Patent Document 6 only describes that the heat distortion temperature (HDT) of a cured resin plate is improved from about 100 ° C. to about 110 ° C. by adding polyphenylene ether having a normal molecular weight. There is no description about the properties (particularly moldability, peel strength, water absorption resistance, solder heat resistance, etc.) of the composite of the cured resin and the base material necessary for the printed wiring board, which is an application of the invention.
そして、特許文献７には、押出し成形品の衝撃強度等が向上することが記載されているのみで、特許文献６同様、本発明の用途であるプリント配線板に必要な、樹脂硬化物と基材との複合体の特性（特に成形性、剥離強度、耐吸水性、はんだ耐熱性等）については何ら記載されてない。 Patent Document 7 only describes that the impact strength and the like of the extrusion-molded product are improved. Like Patent Document 6, the resin cured product and the base necessary for the printed wiring board that is an application of the present invention are disclosed. There is no description of the properties (particularly moldability, peel strength, water absorption resistance, solder heat resistance, etc.) of the composite with the material.
以上のように、ポリフェニレンエーテルが本来有する低い誘電率及び誘電正接を有し、かつ、通常のプレス温度での成形性、耐熱性、及び接着性に優れるプリント配線板用の絶縁樹脂は従来技術においては見出されていないのが現状である。従って、ポリフェニレンエーテルを構成成分としつつ上記のような特性を有するプリント配線板用の絶縁樹脂が強く望まれていた。また、このような絶縁樹脂においては、絶縁不良の原因となりうる異物混入の問題が生じる場合があるが、ポリフェニレンエーテルを構成成分としつつ異物を容易に発見できるような絶縁樹脂は未だ提案されていない。従って、ポリフェニレンエーテルを構成成分とし、且つ異物の発見が容易な絶縁樹脂が望まれていた。 As described above, insulating resins for printed wiring boards that have the low dielectric constant and dielectric loss tangent inherent in polyphenylene ether and that are excellent in moldability, heat resistance, and adhesiveness at normal press temperatures are the prior art. Is currently not found. Therefore, there has been a strong demand for an insulating resin for a printed wiring board having the above-described characteristics while using polyphenylene ether as a constituent component. In addition, in such an insulating resin, there may be a problem of contamination by foreign matter that may cause insulation failure. However, an insulating resin that can easily find foreign matter while using polyphenylene ether as a constituent component has not been proposed yet. . Therefore, there has been a demand for an insulating resin that contains polyphenylene ether as a constituent component and that can easily find foreign matter.
前記した状況の下、本発明が解決しようとする課題は、ポリフェニレンエーテルが本来有する低い誘電率及び誘電正接を有する硬化物を与え、通常のプレス成形温度での成形性に優れ、更には優れた耐熱性及び接着性（例えば、多層板における層間の剥離強度、又は硬化性樹脂組成物の硬化物と銅箔等の金属箔との剥離強度）を有し、しかも異物発見が容易である硬化物を与える硬化性樹脂組成物、該樹脂組成物と基材とを含むプリント配線板用プリプレグ、及び該樹脂組成物の硬化物と基材とを含むプリント配線板を提供することである。 Under the circumstances described above, the problem to be solved by the present invention is to provide a cured product having a low dielectric constant and dielectric loss tangent inherent in polyphenylene ether, and is excellent in moldability at a normal press molding temperature, and more excellent. A cured product that has heat resistance and adhesiveness (for example, peel strength between layers in a multilayer board, or peel strength between a cured product of a curable resin composition and a metal foil such as a copper foil), and foreign matter can be easily detected. A curable resin composition that provides a prepreg, a prepreg for a printed wiring board including the resin composition and a base material, and a printed wiring board including a cured product of the resin composition and a base material.
本発明者らは、上記課題を解決すべく、ポリフェニレンエーテルの分子量及び末端水酸基数が、プリント配線板用材料に必要な様々な特性に及ぼす影響に着目して鋭意検討し実験を重ねた。その結果、ポリフェニレンエーテルの１分子当たりの平均フェノール性水酸基数を特定範囲に制御すること、更に好ましくは、主成分を通常分子量ポリフェニレンエーテルとするとともに低分子量ポリフェニレンエーテルを特定量配合することによって、成形性に優れる硬化性樹脂組成物、並びに耐熱性及び接着性に優れ、誘電率及び誘電正接が低い硬化物を形成できることを見出した。
すなわち、本発明は以下の通りである。
In order to solve the above-mentioned problems, the present inventors have conducted intensive studies and experiments while paying attention to the influence of the molecular weight and the number of terminal hydroxyl groups of polyphenylene ether on various properties required for printed wiring board materials. As a result, the average number of phenolic hydroxyl groups per molecule of polyphenylene ether is controlled within a specific range, and more preferably, the main component is a normal molecular weight polyphenylene ether and a low molecular weight polyphenylene ether is blended in a specific amount. The present inventors have found that a curable resin composition having excellent properties and a cured product having excellent heat resistance and adhesiveness and low dielectric constant and dielectric loss tangent can be formed.
That is, the present invention is as follows.
［１］ ポリフェニレンエーテルを含む硬化性樹脂組成物であって、
該ポリフェニレンエーテル１分子当たりの平均フェノール性水酸基数が０．３個以上であり、
該ポリフェニレンエーテルが、数平均分子量が８，０００を超えるポリフェニレンエーテル成分を、ポリフェニレンエーテル全量に対して７５質量％以上の量で含み、
該硬化性樹脂組成物の下記条件で測定される硬化時樹脂フロー量が０．３％以上１５％以下であり、
該硬化性樹脂組成物から下記条件で作製された誘電正接測定用試料が、１ＧＨｚでの誘電正接：０．００５以下を有し、
該硬化性樹脂組成物から下記条件で作製されたガラス転移温度測定用及び色示測定用の試料が、ガラス転移温度：１７０℃以上を有し、
該硬化性樹脂組成物から下記条件で作製された白色度測定用試料が、L*ａ*ｂ*表色系での白色度：８５以上、及びｂ*値：９以下を有し、
該硬化時樹脂フロー量は、該硬化性樹脂組成物が樹脂含量６０±２質量％となるよう、ＩＰＣ Ｓｔｙｌｅ ２１１６規格ガラスクロスに含浸されてなる１５０ｍｍ角のプリプレグを２枚重ねて積層板前駆体を得て、該積層板前駆体を下記条件（ａ）にて成形し、流れ出した樹脂部を取り除いて積層板を作製したときにおける、該積層板の質量（ｇ）、及び該積層板前駆体の質量（ｇ）から、下記式：
硬化時樹脂フロー量（％）＝（積層板前駆体の質量（ｇ）−積層板の質量（ｇ））／積層板前駆体の質量（ｇ）×１００
に従って算出される値であり、
該誘電正接測定用試料は、該硬化性樹脂組成物が樹脂含量６０±２質量％となるようＩＰＣ Ｓｔｙｌｅ ２１１６規格ガラスクロスに含浸されてなるプリプレグを１６枚重ね、下記条件（ａ）にて成形されており、
該ガラス転移温度測定用試料は、該硬化性樹脂組成物が樹脂含量６０±２質量％となるようＩＰＣ Ｓｔｙｌｅ ２１１６規格ガラスクロスに含浸されてなるプリプレグを２枚重ね、下記条件（ａ）にて成形されており、
該白色度測定用試料は、該硬化性樹脂組成物が樹脂含量６０±２質量％となるようＩＰＣ Ｓｔｙｌｅ ２１１６規格ガラスクロスに含浸されてなるプリプレグである、
硬化性樹脂組成物。
条件（ａ）
室温から昇温速度３℃／分で加熱しながら圧力５ｋｇ／ｃｍ2の条件で真空プレスを行い、１３０℃まで達したら昇温速度３℃／分で加熱しながら圧力３０ｋｇ／ｃｍ2の条件で真空プレスを行い、２００℃まで達したら温度を２００℃に保ったまま圧力３０ｋｇ／ｃｍ2、時間６０分間の条件で真空プレスを行う。
［２］ 該ポリフェニレンエーテルが、
（Ａ−１）１分子当たりの平均フェノール性水酸基数が０．５個未満であり、かつ数平均分子量が１，０００以上８，０００以下であるポリフェニレンエーテル成分、及び
（Ａ−２）該数平均分子量が８，０００を超えるポリフェニレンエーテル成分、
を含み、該（Ａ−１）と該（Ａ−２）との合計質量１００質量％を基準として、該（Ａ−１）の含有量が１質量％以上２５質量％以下であり、かつ該（Ａ−２）の含有量が７５質量％以上９９質量％以下である、上記［１］に記載の硬化性樹脂組成物。
［３］ 該（Ａ−１）１分子当たりの平均フェノール性水酸基数が０．５個未満であり、かつ数平均分子量が１，０００以上８，０００以下であるポリフェニレンエーテル成分が、ポリフェニレンエーテルの分子末端の少なくとも１個のフェノール性水酸基がベンジル基に置換された構造を有するベンジル化ポリフェニレンエーテルである、上記［２］に記載の硬化性樹脂組成物。
［４］ 該ポリフェニレンエーテル（Ａ）と、分子内に２個以上のビニル基を持つモノマー（Ｂ）と、反応開始剤（Ｃ）とを含み、該ポリフェニレンエーテル（Ａ）と該モノマー（Ｂ）との合計１００質量部に対して、該モノマー（Ｂ）の含有量が１０質量部以上７０質量部以下であり、かつ該反応開始剤（Ｃ）の含有量が１質量部以上１０質量部以下である、上記［１］〜［３］のいずれかに記載の硬化性樹脂組成物。
［５］ 該モノマー（Ｂ）がトリアリルイソシアヌレート（ＴＡＩＣ）である、上記［４］に記載の硬化性樹脂組成物。
［６］ 更に難燃剤を含む、上記［４］又は［５］に記載の硬化性樹脂組成物。
［７］ 上記［１］〜［６］のいずれかに記載の硬化性樹脂組成物と基材とを含み、L*ａ*ｂ*表色系での白色度：８５以上、及びｂ*値：９以下を有する、プリント配線板用プリプレグ。
［８］ 上記［１］〜［６］のいずれかに記載の硬化性樹脂組成物の硬化物と基材とを含む、プリント配線板。
[1] A curable resin composition containing polyphenylene ether,
The average number of phenolic hydroxyl groups per molecule of the polyphenylene ether is 0.3 or more,
The polyphenylene ether contains a polyphenylene ether component having a number average molecular weight exceeding 8,000 in an amount of 75% by mass or more based on the total amount of the polyphenylene ether,
The resin flow amount during curing measured under the following conditions of the curable resin composition is 0.3% or more and 15% or less,
A dielectric loss tangent measurement sample produced from the curable resin composition under the following conditions has a dielectric loss tangent at 1 GHz: 0.005 or less,
A sample for measuring the glass transition temperature and measuring the color indication prepared from the curable resin composition under the following conditions has a glass transition temperature of 170 ° C. or higher.
A whiteness measurement sample prepared from the curable resin composition under the following conditions has a whiteness in the L * a * b * color system: 85 or more, and a b * value: 9 or less,
The amount of resin flow at the time of curing is such that two prepregs of 150 mm square each impregnated with IPC Style 2116 standard glass cloth are laminated so that the curable resin composition has a resin content of 60 ± 2% by mass. The laminated plate precursor is molded under the following conditions (a), and the mass (g) of the laminated plate when the flowed resin part is removed to produce a laminated plate, and the laminated plate precursor From the mass (g) of the following formula:
Resin flow rate during curing (%) = (mass of laminate precursor (g) −mass of laminate (g)) / mass of laminate precursor (g) × 100
Is calculated according to
The dielectric loss tangent measurement sample was formed by stacking 16 prepregs impregnated with IPC Style 2116 standard glass cloth so that the curable resin composition had a resin content of 60 ± 2% by mass, and molded under the following conditions (a): Has been
The glass transition temperature measurement sample is formed by stacking two prepregs impregnated with IPC Style 2116 standard glass cloth so that the curable resin composition has a resin content of 60 ± 2% by mass, and the following conditions (a) Molded,
The whiteness measurement sample is a prepreg that is impregnated with an IPC Style 2116 standard glass cloth so that the curable resin composition has a resin content of 60 ± 2% by mass.
Curable resin composition.
Condition (a)
Vacuum pressing is performed from room temperature at a heating rate of 3 ° C./min and a pressure of 5 kg / cm 2. When reaching 130 ° C., heating is performed at a heating rate of 3 ° C./min and a pressure of 30 kg / cm 2 . When the temperature reaches 200 ° C., the vacuum press is performed under the conditions of a pressure of 30 kg / cm 2 and a time of 60 minutes.
[2] The polyphenylene ether is
(A-1) a polyphenylene ether component having an average number of phenolic hydroxyl groups per molecule of less than 0.5 and a number average molecular weight of 1,000 or more and 8,000 or less, and (A-2) the number A polyphenylene ether component having an average molecular weight exceeding 8,000,
The content of (A-1) is 1% by mass or more and 25% by mass or less based on the total mass of 100% by mass of (A-1) and (A-2), and Curable resin composition as described in said [1] whose content of (A-2) is 75 mass% or more and 99 mass% or less.
[3] The (A-1) polyphenylene ether component having an average number of phenolic hydroxyl groups per molecule of less than 0.5 and a number average molecular weight of 1,000 to 8,000 is polyphenylene ether. The curable resin composition according to the above [2], which is a benzylated polyphenylene ether having a structure in which at least one phenolic hydroxyl group at the molecular end is substituted with a benzyl group.
[4] The polyphenylene ether (A), a monomer (B) having two or more vinyl groups in the molecule, and a reaction initiator (C), the polyphenylene ether (A) and the monomer (B) The content of the monomer (B) is 10 parts by mass or more and 70 parts by mass or less, and the content of the reaction initiator (C) is 1 part by mass or more and 10 parts by mass or less with respect to 100 parts by mass in total. The curable resin composition according to any one of the above [1] to [3].
[5] The curable resin composition according to the above [4], wherein the monomer (B) is triallyl isocyanurate (TAIC).
[6] The curable resin composition according to [4] or [5], further including a flame retardant.
[7] The curable resin composition according to any one of [1] to [6] above and a substrate, and whiteness in L * a * b * color system: 85 or more, and b * value : A prepreg for a printed wiring board having 9 or less.
[8] A printed wiring board comprising a cured product of the curable resin composition according to any one of [1] to [6] and a base material.
本発明によれば、ポリフェニレンエーテルの本来有する低い誘電率及び誘電正接を有する硬化物を与え、かつ、通常のプレス成形温度での成形性に優れ、更には優れた耐熱性及び接着性（例えば、多層板における層間の剥離強度、又は硬化性樹脂組成物の硬化物と銅箔等の金属箔との剥離強度）を有し、異物発見が容易であり異物混入による絶縁不良等の欠点を低減可能な硬化物を与える、硬化性樹脂組成物、並びに該樹脂組成物と基材とを含むプリント配線板用プリプレグ、及び該樹脂組成物の硬化物と基材とを含むプリント配線板を提供することができる。 According to the present invention, a cured product having a low dielectric constant and dielectric loss tangent inherent in polyphenylene ether is obtained, and excellent in moldability at a normal press molding temperature, and further excellent in heat resistance and adhesiveness (for example, It has a peel strength between layers in a multilayer board or a peel strength between a cured product of a curable resin composition and a metal foil such as a copper foil), and can easily detect foreign matter and reduce defects such as poor insulation due to foreign matter contamination. A curable resin composition that provides a cured product, a prepreg for a printed wiring board that includes the resin composition and a substrate, and a printed wiring board that includes the cured product of the resin composition and a substrate. Can do.
以下、本発明の態様の例を詳細に説明するが、本発明はこれらの態様に限定されない。 Examples of aspects of the present invention will be described in detail below, but the present invention is not limited to these aspects.
本態様の硬化性樹脂組成物が含むポリフェニレンエーテルは、好ましくは、下記一般式（１）： The polyphenylene ether contained in the curable resin composition of this embodiment is preferably the following general formula (1):
（式中、Ｒ１、Ｒ２、Ｒ３及びＲ４は、各々独立して、水素原子、ハロゲン原子、置換基を有してもよいアルキル基、置換基を有してもよいアルコキシ基、置換基を有してもよいアリール基、置換基を有してもよいアミノ基、ニトロ基、又はカルボキシル基を表す。）で表される繰返し構造単位を含む。 (In the formula, R1, R2, R3 and R4 each independently have a hydrogen atom, a halogen atom, an alkyl group which may have a substituent, an alkoxy group which may have a substituent, or a substituent. An aryl group that may be substituted, an amino group that may have a substituent, a nitro group, or a carboxyl group.
ポリフェニレンエーテルの具体例としては、例えばポリ（２，６−ジメチル−１，４−フェニレンエーテル）、ポリ（２−メチル−６−エチル−１，４−フェニレンエーテル）、ポリ（２−メチル−６−フェニル−１，４−フェニレンエーテル）、ポリ（２，６−ジクロロ−１，４−フェニレンエーテル）等、更に、２，６−ジメチルフェノールと他のフェノール類（例えば２，３，６−トリメチルフェノール、２−メチル−６−ブチルフェノール等）との共重合体、及び、２，６−ジメチルフェノールとビフェノール類又はビスフェノール類とをカップリングさせて得られるポリフェニレンエーテル共重合体、等が挙げられ、好ましい例はポリ（２，６−ジメチル−１，４−フェニレンエーテル）である。 Specific examples of polyphenylene ether include poly (2,6-dimethyl-1,4-phenylene ether), poly (2-methyl-6-ethyl-1,4-phenylene ether), and poly (2-methyl-6). -Phenyl-1,4-phenylene ether), poly (2,6-dichloro-1,4-phenylene ether) and the like, and 2,6-dimethylphenol and other phenols (for example, 2,3,6-trimethyl) Phenol, 2-methyl-6-butylphenol, etc.) and polyphenylene ether copolymers obtained by coupling 2,6-dimethylphenol and biphenols or bisphenols, etc. A preferred example is poly (2,6-dimethyl-1,4-phenylene ether).
なお本開示において、ポリフェニレンエーテルとは、置換又は非置換のフェニレンエーテル単位構造から構成されるポリマーを意味するが、本発明の効果を損なわない範囲で他の共重合成分を含んでもよい。 In the present disclosure, polyphenylene ether means a polymer composed of a substituted or unsubstituted phenylene ether unit structure, but may contain other copolymerization components as long as the effects of the present invention are not impaired.
本発明の一態様は、ポリフェニレンエーテルを含む硬化性樹脂組成物（以下、ポリフェニレンエーテル含有組成物ともいう）を提供する。 One embodiment of the present invention provides a curable resin composition containing polyphenylene ether (hereinafter also referred to as a polyphenylene ether-containing composition).
本発明の一態様において、ポリフェニレンエーテル１分子当たりの平均フェノール性水酸基数は、０．３個以上である。一態様において、硬化性樹脂組成物の下記条件で測定される硬化時樹脂フロー量は、０．３％以上１５％以下である。一態様において、硬化性樹脂組成物から下記条件で作製された誘電正接測定用試料は、１ＧＨｚでの誘電正接：０．００５以下を有する。一態様において、硬化性樹脂組成物から下記条件で作製されたガラス転移温度測定用試料は、ガラス転移温度：１７０℃以上を有する。 In one embodiment of the present invention, the average number of phenolic hydroxyl groups per molecule of polyphenylene ether is 0.3 or more. In one aspect, the resin flow amount during curing measured under the following conditions of the curable resin composition is 0.3% or more and 15% or less. In one embodiment, a dielectric loss tangent measurement sample prepared from the curable resin composition under the following conditions has a dielectric loss tangent at 1 GHz: 0.005 or less. In one embodiment, the glass transition temperature measurement sample produced from the curable resin composition under the following conditions has a glass transition temperature of 170 ° C. or higher.
該硬化時樹脂フロー量は、該硬化性樹脂組成物が樹脂含量６０±２質量％となるよう、ＩＰＣ Ｓｔｙｌｅ ２１１６規格ガラスクロスに含浸されてなる１５０ｍｍ角のプリプレグを２枚重ねて積層板前駆体を得て、該積層板前駆体を下記条件（ａ）にて成形し、流れ出した樹脂部を取り除いて積層板を作製したときにおける、該積層板の質量（ｇ）、及び該積層板前駆体の質量（ｇ）から、下記式：
硬化時樹脂フロー量（％）＝（積層板前駆体の質量（ｇ）−積層板の質量（ｇ））／積層板前駆体の質量（ｇ）×１００
に従って算出される値である。
The amount of resin flow at the time of curing is such that two prepregs of 150 mm square each impregnated with IPC Style 2116 standard glass cloth are laminated so that the curable resin composition has a resin content of 60 ± 2% by mass. The laminated plate precursor is molded under the following conditions (a), and the mass (g) of the laminated plate when the flowed resin part is removed to produce a laminated plate, and the laminated plate precursor From the mass (g) of the following formula:
Resin flow rate during curing (%) = (mass of laminate precursor (g) −mass of laminate (g)) / mass of laminate precursor (g) × 100
Is a value calculated according to
ここで、条件（ａ）は次のように定義される。室温から昇温速度３℃／分で加熱しながら圧力５ｋｇ／ｃｍ2の条件で真空プレスを行い、１３０℃まで達したら昇温速度３℃／分で加熱しながら圧力３０ｋｇ／ｃｍ2の条件で真空プレスを行い、２００℃まで達したら温度を２００℃に保ったまま圧力３０ｋｇ／ｃｍ2、時間６０分間の条件で真空プレスを行う。 Here, the condition (a) is defined as follows. Vacuum pressing is performed from room temperature at a heating rate of 3 ° C./min and a pressure of 5 kg / cm 2. When reaching 130 ° C., heating is performed at a heating rate of 3 ° C./min and a pressure of 30 kg / cm 2 . When the temperature reaches 200 ° C., the vacuum press is performed under the conditions of a pressure of 30 kg / cm 2 and a time of 60 minutes.
該誘電正接測定用試料は、該硬化性樹脂組成物が樹脂含量６０±２質量％となるようＩＰＣ Ｓｔｙｌｅ ２１１６規格ガラスクロスに含浸されてなるプリプレグを１６枚重ね、上記条件（ａ）にて成形されている。 The dielectric loss tangent measurement sample was formed by stacking 16 prepregs impregnated with IPC Style 2116 standard glass cloth so that the curable resin composition had a resin content of 60 ± 2% by mass, and molded under the above condition (a). Has been.
該ガラス転移温度測定用試料は、該硬化性樹脂組成物が樹脂含量６０±２質量％となるようＩＰＣ Ｓｔｙｌｅ ２１１６規格ガラスクロスに含浸されてなるプリプレグを２枚重ね、上記条件（ａ）にて成形されている。 The glass transition temperature measurement sample is formed by stacking two prepregs impregnated with an IPC Style 2116 standard glass cloth so that the curable resin composition has a resin content of 60 ± 2% by mass. Molded.
ＩＰＣ Ｓｔｙｌｅ ２１１６規格ガラスクロスは、市販で入手可能であり、例えば旭シュエーベル株式会社製の商品名「２１１６」として入手可能である。 The IPC Style 2116 standard glass cloth is commercially available, and is available, for example, under the trade name “2116” manufactured by Asahi Schwer Corporation.
本発明の硬化性樹脂組成物の硬化時樹脂フロー量は、０．３％以上１５％以下であり、好ましくは０．５％以上１２％以下、より好ましくは１％以上１０％以下である。該樹脂フロー量が０．３％以上であれば、通常のプレス成形温度での成形性に優れ、かすれ及びボイドが低減された硬化物、更にはこれを含む積層板を形成できる。一方で、該樹脂フロー量が１５％以下であれば、例えば硬化性樹脂組成物の硬化物と基材とを含む積層板を形成する場合に、積層板の積層位置ずれを小さくできる。 The resin flow amount during curing of the curable resin composition of the present invention is 0.3% or more and 15% or less, preferably 0.5% or more and 12% or less, more preferably 1% or more and 10% or less. When the resin flow amount is 0.3% or more, a cured product having excellent moldability at a normal press molding temperature and reduced haze and voids, and a laminate including the cured product can be formed. On the other hand, when the resin flow amount is 15% or less, for example, when forming a laminated board including a cured product of the curable resin composition and a base material, it is possible to reduce the lamination position deviation of the laminated board.
ここで、硬化性樹脂組成物の硬化時樹脂フロー量は本開示の次の方法で求めた値と定義され、より具体的には、下記方法を用いて算出できる。 Here, the amount of resin flow during curing of the curable resin composition is defined as a value obtained by the following method of the present disclosure, and more specifically, can be calculated using the following method.
該該硬化時樹脂フロー量は、該硬化性樹脂組成物が樹脂含量６０±２質量％となるようＩＰＣ Ｓｔｙｌｅ ２１１６規格ガラスクロスガラスクロス（ＩＰＣ Ｓｔｙｌｅ ２１１６）に含浸されてなる１５０ｍｍ角のプリプレグを試験片とする。予め、試験片２枚の質量（ｇ）を求めておき、積層板前駆体の質量とする。次いで、該試験片を２枚重ね、上記条件（ａ）にて加熱加圧を行う。得られたものについて、１５０ｍｍ角から流れ出した樹脂部を取り除き、積層板とする。この積層板について質量を求めて、積層板の質量（ｇ）とする。このようにして得られた質量を上記の式に代入し、硬化時樹脂フロー量を求める。 The amount of resin flow during curing was determined by testing a 150 mm square prepreg impregnated with IPC Style 2116 standard glass cloth glass cloth (IPC Style 2116) so that the curable resin composition had a resin content of 60 ± 2% by mass. A piece. The mass (g) of two test pieces is obtained in advance, and is defined as the mass of the laminated plate precursor. Next, two test pieces are stacked and heated and pressurized under the above condition (a). About the obtained thing, the resin part which flowed out from 150 square mm is removed, and it is set as a laminated board. The mass of this laminate is determined and is defined as the mass (g) of the laminate. The mass thus obtained is substituted into the above formula, and the amount of resin flow during curing is determined.
硬化時樹脂フロー量を上記範囲に調整する方法の例は、ポリフェニレンエーテルの１分子当たりの平均フェノール性水酸基数を調製する方法、後述する（Ａ−１）低分子量・末端官能化ポリフェニレンエーテルと、（Ａ−２）成分とを混合しその混合比を変えることによって調整する方法、後述する分子内に２個以上のビニル基を持つモノマーを配合し用い、その使用配合量を調製する方法、等である。 An example of a method for adjusting the resin flow amount during curing to the above range is a method of adjusting the average number of phenolic hydroxyl groups per molecule of polyphenylene ether, (A-1) a low molecular weight / terminal functionalized polyphenylene ether described later, (A-2) A method of adjusting by mixing the components and changing the mixing ratio, a method of blending and using a monomer having two or more vinyl groups in the molecule, which will be described later, etc., etc. It is.
また、本態様の硬化性樹脂組成物から本開示の下記条件で作製された硬化物試料の誘電正接は１ＧＨｚで０．００５以下である。誘電正接が１ＧＨｚで０．００５以下のプリント配線板は、情報処理の高速化に要求される信号伝達速度の高速化に対応するために所望されている。本発明が提供する硬化性樹脂組成物は、誘電正接が１ＧＨｚで０．００５以下である硬化物複合体を与えることができる。よってこのような硬化性樹脂組成物を用いることにより、信号伝達速度の高速化を可能にするプリント配線版を形成できる。 Moreover, the dielectric loss tangent of the hardened | cured material sample produced on the following conditions of this indication from the curable resin composition of this aspect is 0.005 or less at 1 GHz. A printed wiring board having a dielectric loss tangent of 1 GHz at 0.005 or less is desired in order to cope with an increase in signal transmission speed required for an increase in information processing. The curable resin composition provided by the present invention can provide a cured product composite having a dielectric loss tangent of 0.005 or less at 1 GHz. Therefore, by using such a curable resin composition, a printed wiring board capable of increasing the signal transmission speed can be formed.
上記硬化物誘電正接測定用試料は、該硬化性樹脂組成物が樹脂含量６０±２質量％となるようＩＰＣ Ｓｔｙｌｅ ２１１６規格ガラスクロスガラスクロス（ＩＰＣ Ｓｔｙｌｅ ２１１６）に含浸されてなるプリプレグを１６枚重ね、上記条件（ａ）にて加熱加圧成形する方法で作製される。 The cured material dielectric loss tangent measurement sample is a stack of 16 prepregs impregnated with IPC Style 2116 standard glass cloth glass cloth (IPC Style 2116) so that the curable resin composition has a resin content of 60 ± 2 mass%. It is produced by the method of heating and pressing under the above condition (a).
上記試料硬化物の１ＧＨｚでの誘電正接は、好ましくは０．００３以下、より好ましくは０．００１以下である。該誘電正接は小さいほど好ましいが、ポリフェニレンエーテルが本来有する電気特性の観点から、好ましくは０．０００７以上、より好ましくは０．０００５以上であることができる。 The dielectric loss tangent at 1 GHz of the cured sample is preferably 0.003 or less, more preferably 0.001 or less. The smaller the dielectric loss tangent, the better. However, from the viewpoint of the electrical properties inherent in the polyphenylene ether, it can be preferably 0.0007 or more, more preferably 0.0005 or more.
硬化物上記試料の誘電正接は、インピーダンスアナライザー法により、５００ｍＶの条件で、１ＭＨｚ〜１ＧＨｚの静電容量Ｃｐ［Ｆ］とコンダクタンスＧ［Ｓ］とを測定し、下記式を用いて求められる値である。
εｒ＝（ｔ×Ｃｐ）／｛π×（ｄ／２）2×ε0
（ｔ：試料厚み〔ｍ〕、ｄ：電極直径、ｆ：測定周波数〔Ｈｚ〕、ε0：真空の誘電率＝８．８５４×１０-12〔Ｆ／ｍ〕）
Cured material The dielectric loss tangent of the above sample is a value obtained by measuring the capacitance Cp [F] and conductance G [S] of 1 MHz to 1 GHz under the condition of 500 mV by the impedance analyzer method and using the following equation. is there.
εr = (t × Cp) / {π × (d / 2) 2 × ε0
(T: sample thickness [m], d: electrode diameter, f: measurement frequency [Hz], ε0: vacuum permittivity = 8.854 × 10 −12 [F / m])
また、本態様の硬化性樹脂組成物においては、本開示の上述の方法で作製された試料（具体的には、プリプレグを１６枚重ねることに代えてプリプレグを２枚重ねること以外は誘電正接測定用試料の作製方法と同様の方法で作製される試料）硬化物のガラス転移温度が１７０℃以上であり、好ましくは１８０℃以上、より好ましくは１９０℃以上である。該試料のガラス転移温度は、硬化性樹脂組成物を典型的な使用条件で硬化させて得られる硬化物のガラス転移温度に対応する。ガラス転移温度が１７０℃以上である硬化物は良好な耐熱性（特に鉛フリーはんだに対応するはんだ耐熱性）を発現する。硬化物のガラス転移温度は高い方が好ましいが、該硬化物の使用環境への適用性の観点で、該試料のガラス転移温度は、好ましくは３００℃以下、より好ましくは２５０℃以下であることができる。 Further, in the curable resin composition of this embodiment, the sample produced by the above-described method of the present disclosure (specifically, dielectric loss tangent measurement except that two prepregs are stacked instead of 16 prepregs) Sample prepared by the same method as the sample preparation method) The glass transition temperature of the cured product is 170 ° C. or higher, preferably 180 ° C. or higher, more preferably 190 ° C. or higher. The glass transition temperature of the sample corresponds to the glass transition temperature of a cured product obtained by curing the curable resin composition under typical use conditions. A cured product having a glass transition temperature of 170 ° C. or higher exhibits good heat resistance (particularly solder heat resistance corresponding to lead-free solder). The glass transition temperature of the cured product is preferably higher, but from the viewpoint of applicability to the use environment of the cured product, the glass transition temperature of the sample is preferably 300 ° C. or less, more preferably 250 ° C. or less. Can do.
ここで、試料硬化物のガラス転移温度は、粘弾性スペクトロメーターを用いて、ひねりモード、周波数１０ｒａｄ／ｓの条件で測定される値である。 Here, the glass transition temperature of the sample cured product is a value measured using a viscoelastic spectrometer under conditions of a twist mode and a frequency of 10 rad / s.
ガラス転移温度を上記範囲に調整する方法の例は、ポリフェニレンエーテルの１分子当たりの平均フェノール性水酸基数を調製する方法、後述する（Ａ−１）成分と（Ａ−２）成分とを混合し、その混合比を調整する方法、
後述する分子内に２個以上のビニル基を持つモノマーを使用配合し、その使用配合量を調製する方法、等である。
An example of a method for adjusting the glass transition temperature to the above range is a method of adjusting the average number of phenolic hydroxyl groups per molecule of polyphenylene ether, and the components (A-1) and (A-2) described later are mixed. , How to adjust its mixing ratio,
A method of using and blending a monomer having two or more vinyl groups in the molecule, and preparing the blending amount thereof;
本態様の硬化性樹脂組成物においては、硬化性樹脂組成物が樹脂含量６０±２質量％となるようＩＰＣ Ｓｔｙｌｅ ２１１６規格ガラスクロスに含浸されてなるプリプレグである白色度測定用試料が、L*ａ*ｂ*表色系での白色度（すなわちハンター白色度）：８５以上、及びｂ*値：９以下を有する。白色度が８５％以上であること、及びｂ*値（これは黄色度の指標である）が９以下であることは、異物発見の容易性の観点から有利である。白色度は、好ましくは８７以上、より好ましくは８８以上である。白色度は高いほど好ましいが、例えば黒色、茶色、銀色、灰色等の異物を十分に判別できる観点から９８以下、更に９３以下であってもよい。ｂ*値は、好ましくは８以下、より好ましくは７以下である。ｂ*値は低いほど好ましいが、例えば黒色、茶色、銀色、灰色等の異物を十分に判別できる点から、２以上、更に４以上であってもよい。 In the curable resin composition of this embodiment, a whiteness measurement sample, which is a prepreg impregnated in an IPC Style 2116 standard glass cloth so that the curable resin composition has a resin content of 60 ± 2% by mass, is L *. Whiteness in a * b * color system (ie Hunter whiteness): 85 or more, and b * value: 9 or less. A whiteness of 85% or more and a b * value (which is an index of yellowness) of 9 or less are advantageous from the viewpoint of easy detection of foreign matter. The whiteness is preferably 87 or more, more preferably 88 or more. Higher whiteness is more preferable, but it may be 98 or less, or 93 or less from the viewpoint of sufficiently distinguishing foreign matters such as black, brown, silver, and gray. The b * value is preferably 8 or less, more preferably 7 or less. The b * value is preferably as low as possible, but it may be 2 or more, or 4 or more from the viewpoint that foreign matters such as black, brown, silver, and gray can be sufficiently distinguished.
上記の白色度及びｂ*値を上記範囲に制御する具体的な手段としては、後述の（Ａ−１）のポリフェニレンエーテル成分の量をポリフェニレンエーテル全量の１質量％以上２５質量％以下に制御すること、後述の（Ａ−２）のポリフェニレンエーテル成分の平均フェノール性水酸基数を０．５個以上に制御すること等が挙げられる。 As a specific means for controlling the whiteness and b * value within the above ranges, the amount of the polyphenylene ether component (A-1) described later is controlled to 1% by mass or more and 25% by mass or less of the total amount of polyphenylene ether. And controlling the average number of phenolic hydroxyl groups of the polyphenylene ether component (A-2) described later to 0.5 or more.
本態様の硬化性樹脂組成物に含まれるポリフェニレンエーテルの１分子当たりの平均フェノール性水酸基数は、０．３個以上である。ポリフェニレンエーテルの１分子当たりの平均フェノール性水酸基数は好ましくは０．７個以上であり、より好ましくは０．９個以上であり、更に好ましくは１．０５個以上である。１分子当たりの平均フェノール性水酸基数が０．３個以上のポリフェニレンエーテルを硬化性樹脂組成物において用いると、該樹脂組成物の硬化物と基材（例えばガラスクロス等）との接着性、又は該樹脂組成物の硬化物と銅箔等の金属箔との接着性が良好となり、プリント配線板の耐吸水性、はんだ耐熱性、及び接着性（例えば、多層板における層間の剥離強度、又は硬化物と銅箔等との剥離強度）に優れるため好ましい。該平均フェノール性水酸基数は、硬化性樹脂組成物の硬化物と基材とを含む複合体（例えば積層板）の吸水性が高くなるのを抑制できる観点、又は、該複合体の誘電率と誘電正接が高くなるのを抑制できる観点から、好ましくは２．０個以下、より好ましくは１．８５個以下、更に好ましくは１．６個以下である。 The average number of phenolic hydroxyl groups per molecule of the polyphenylene ether contained in the curable resin composition of this embodiment is 0.3 or more. The average number of phenolic hydroxyl groups per molecule of polyphenylene ether is preferably 0.7 or more, more preferably 0.9 or more, and further preferably 1.05 or more. When polyphenylene ether having an average number of phenolic hydroxyl groups per molecule of 0.3 or more is used in the curable resin composition, the adhesion between the cured product of the resin composition and a substrate (for example, glass cloth), or Adhesiveness between the cured product of the resin composition and a metal foil such as copper foil is improved, and water absorption resistance, solder heat resistance, and adhesiveness of a printed wiring board (for example, peeling strength between layers in a multilayer board, or curing) This is preferable because it is excellent in the peel strength between the product and the copper foil. The average number of phenolic hydroxyl groups is a viewpoint that can suppress an increase in water absorption of a composite (for example, a laminate) containing a cured product of the curable resin composition and a substrate, or a dielectric constant of the composite From the viewpoint of suppressing an increase in dielectric loss tangent, it is preferably 2.0 or less, more preferably 1.85 or less, and still more preferably 1.6 or less.
本開示におけるポリフェニレンエーテルの１分子当たりの平均フェノール性水酸基数は、それぞれ、次の方法で求めた値と定義される。高分子論文集，ｖｏｌ．５１，Ｎｏ．７（１９９４），第４８０頁記載の方法に準拠し、ポリフェニレンエーテルの塩化メチレン溶液にテトラメチルアンモニウムハイドロオキシド溶液を加えて得たサンプルの波長３１８ｎｍにおける吸光度変化を紫外可視吸光光度計で測定した値から水酸基の数を求める。別途、ポリフェニレンエーテルの数平均分子量を、ゲルパーミエーションクロマトグラフィにより求め、この値を用いてポリフェニレンエーテルの分子数を求める。これらの値から、下記式に従って、ポリフェニレンエーテルの１分子当たりの平均水酸基数を算出する。
１分子当たりの平均フェノール性水酸基数＝水酸基の数／数平均分子数
The average number of phenolic hydroxyl groups per molecule of polyphenylene ether in the present disclosure is defined as a value obtained by the following method. Polymer Papers, vol. 51, no. 7 (1994), in accordance with the method described on page 480, a value obtained by measuring an absorbance change at a wavelength of 318 nm of a sample obtained by adding a tetramethylammonium hydroxide solution to a methylene chloride solution of polyphenylene ether with an ultraviolet-visible spectrophotometer. To determine the number of hydroxyl groups. Separately, the number average molecular weight of polyphenylene ether is determined by gel permeation chromatography, and the molecular number of polyphenylene ether is determined using this value. From these values, the average number of hydroxyl groups per molecule of polyphenylene ether is calculated according to the following formula.
Average number of phenolic hydroxyl groups per molecule = number of hydroxyl groups / number average number of molecules
ポリフェニレンエーテルの１分子当たりの平均フェノール性水酸基数は、例えば、分子末端のフェノール性水酸基が残存しているポリフェニレンエーテルと、分子末端のフェノール性水酸基が他の官能基で変性されているポリフェニレンエーテルとを混合し、その混合比を変えることによって調整することができる。又は、分子末端のフェノール性水酸基の他の官能基による置換度合を変えることによっても調整することができる。上記の官能基の態様は特に限定されるものではなく、ベンジル基、アリル基、プロパギル基、グリシジル基、ビニルベンジル基、メタクリル基等であることができる。その中でも、反応効率が良いため産業的に入手しやすいこと、自身の反応性がなく安定性に優れること、プレス成形時にポリフェニレンエーテル含有組成物の溶融粘度を低下させる効果が著しいこと等の理由で、好ましくは、ベンジル基である。 The average number of phenolic hydroxyl groups per molecule of polyphenylene ether is, for example, polyphenylene ether in which the phenolic hydroxyl group at the molecular end remains and polyphenylene ether in which the phenolic hydroxyl group at the molecular end is modified with another functional group Can be adjusted by changing the mixing ratio. Or it can adjust also by changing the substitution degree by the other functional group of the phenolic hydroxyl group of a molecule terminal. The mode of the functional group is not particularly limited, and may be a benzyl group, an allyl group, a propargyl group, a glycidyl group, a vinylbenzyl group, a methacryl group, or the like. Among them, because of its high reaction efficiency, it is easy to obtain industrially, it has no reactivity and is excellent in stability, and the effect of reducing the melt viscosity of the polyphenylene ether-containing composition during press molding is remarkable. Preferably, it is a benzyl group.
本態様に用いられるポリフェニレンエーテルは、数平均分子量が８，０００を超えるポリフェニレンエーテル成分（以下、高分子量ポリフェニレンエーテル成分ともいう）を、ポリフェニレンエーテル全量に対して７５質量％以上の量で含有する。これにより、分子量の大きいポリフェニレンエーテルに由来する高いガラス転移温度が得られるため、耐熱性及び機械特性に優れる硬化物が得られる。また上記の高分子量ポリフェニレンエーテル成分は、白色度及びｂ*値を所望の範囲内に制御することに寄与する。上記含有量は、分子量の大きいポリフェニレンエーテルに由来する高いガラス転移温度が得られるため、耐熱性及び機械特性に優れる硬化物が得られる観点、また白色度及びｂ*値を所望の範囲内に制御する観点から、７５質量％であり、好ましくは７７質量％以上、更に好ましくは７９質量％以上である。上記含有量は１００質量％であることができるが、成形時の硬化性樹脂組成物の溶融粘度を小さくし、良好な成形性を得るという観点からは、好ましくは９９質量％以下、より好ましくは９８．８質量％以下、更に好ましくは９８．５質量％以下である。 The polyphenylene ether used in this embodiment contains a polyphenylene ether component having a number average molecular weight exceeding 8,000 (hereinafter also referred to as a high molecular weight polyphenylene ether component) in an amount of 75% by mass or more based on the total amount of polyphenylene ether. Thereby, since a high glass transition temperature derived from polyphenylene ether having a large molecular weight can be obtained, a cured product having excellent heat resistance and mechanical properties can be obtained. The high molecular weight polyphenylene ether component contributes to controlling the whiteness and b * value within a desired range. The above content provides a high glass transition temperature derived from polyphenylene ether having a large molecular weight, so that a cured product having excellent heat resistance and mechanical properties can be obtained, and whiteness and b * value are controlled within a desired range. From this viewpoint, it is 75% by mass, preferably 77% by mass or more, and more preferably 79% by mass or more. The content can be 100% by mass, but from the viewpoint of reducing the melt viscosity of the curable resin composition during molding and obtaining good moldability, it is preferably 99% by mass or less, more preferably It is 98.8 mass% or less, More preferably, it is 98.5 mass% or less.
高分子量ポリフェニレンエーテル成分の数平均分子量は、好ましくは８，０００を超え４０，０００以下であり、より好ましい範囲は９，５００以上２８，０００以下であり、更に好ましい範囲は１０，０００以上２０，０００以下である。数平均分子量が４０，０００以下である場合、通常のプレス成形温度での溶融粘度が低く保たれ、良好な成形性が得られるため好ましい。 The number average molecular weight of the high molecular weight polyphenylene ether component is preferably more than 8,000 and not more than 40,000, more preferably 9,500 to 28,000, and still more preferably 10,000 to 20,000. 000 or less. A number average molecular weight of 40,000 or less is preferable because the melt viscosity at a normal press molding temperature can be kept low and good moldability can be obtained.
本開示におけるポリフェニレンエーテルの数平均分子量は、それぞれゲルパーミエーションクロマトグラフィ（ＧＰＣ）を用い、標準ポリスチレン換算で測定される値である。典型的には、カラムにＳｈｏｄｅｘ ＬＦ−８０４×２（昭和電工株式会社製）、溶離液に５０℃のクロロホルム検出器にＲＩ（屈折率計）を用いてＧＰＣ測定を行い、同条件で測定した標準ポリスチレン試料の分子量と溶出時間との関係式から、数平均分子量を算出する。 The number average molecular weight of the polyphenylene ether in the present disclosure is a value measured in terms of standard polystyrene using gel permeation chromatography (GPC). Typically, GPC measurement was performed under the same conditions using Shodex LF-804 × 2 (manufactured by Showa Denko KK) for the column, RI (refractometer) for the chloroform detector at 50 ° C. for the eluent. The number average molecular weight is calculated from the relational expression between the molecular weight of the standard polystyrene sample and the elution time.
高分子量ポリフェニレンエーテル成分においては、１分子当たりの平均フェノール性水酸基数が０．５個以上である（本開示で未官能化ポリフェニレンエーテルということもある）ことが好ましい。この場合、末端水酸基に由来する良好な接着性が更に得られ、優れた耐熱性、機械特性、及び接着性という利点が得られる。該高分子量ポリフェニレンエーテル成分の１分子当たりの平均フェノール性水酸基数は、より好ましくは０．８個以上、更に好ましくは１．６個以上である。該平均フェノール性水酸基数は多い方が上記の効果を得る点で好ましいが、硬化性樹脂組成物の硬化物と基材とを含む硬化物複合体の吸水性が高くなるのを防ぐ、或いは、誘電率と誘電正接が高くなるのを防ぐ観点から、好ましくは２個以下、より好ましくは１．８５個以下、更に好ましくは１．６個以下であることができる。 In the high molecular weight polyphenylene ether component, the average number of phenolic hydroxyl groups per molecule is preferably 0.5 or more (sometimes referred to as unfunctionalized polyphenylene ether in the present disclosure). In this case, good adhesiveness derived from the terminal hydroxyl group is further obtained, and the advantages of excellent heat resistance, mechanical properties, and adhesiveness are obtained. The average number of phenolic hydroxyl groups per molecule of the high molecular weight polyphenylene ether component is more preferably 0.8 or more, still more preferably 1.6 or more. Although it is preferable in terms of obtaining the above effect that the average number of phenolic hydroxyl groups is large, the water absorption of the cured product composite containing the cured product of the curable resin composition and the substrate is prevented from being increased, or From the viewpoint of preventing increase in dielectric constant and dielectric loss tangent, it is preferably 2 or less, more preferably 1.85 or less, and still more preferably 1.6 or less.
本態様に用いられるポリフェニレンエーテルは、更に、（Ａ−１）１分子当たりの平均フェノール性水酸基数が０．５個未満であり、かつ数平均分子量が１，０００以上８，０００以下であるポリフェニレンエーテル成分（以下、低分子量・末端官能化ポリフェニレンエーテルともいう）を含有することが好ましく、その含有量は、ポリフェニレンエーテル全量に対して１質量％以上２５質量％以下であることが好ましい。該低分子量・末端官能化ポリフェニレンエーテルの含有量のより好ましい範囲は１．２質量％以上２３質量％以下であり、更に好ましい範囲は１．５質量％以上２１質量％以下である。 The polyphenylene ether used in this embodiment further comprises (A-1) a polyphenylene having an average number of phenolic hydroxyl groups per molecule of less than 0.5 and a number average molecular weight of 1,000 or more and 8,000 or less. It is preferable to contain an ether component (hereinafter also referred to as low molecular weight / terminal-functionalized polyphenylene ether), and the content thereof is preferably 1% by mass or more and 25% by mass or less based on the total amount of polyphenylene ether. A more preferable range of the content of the low molecular weight / end-functionalized polyphenylene ether is 1.2% by mass or more and 23% by mass or less, and a further preferable range is 1.5% by mass or more and 21% by mass or less.
該（Ａ−１）低分子量・末端官能化ポリフェニレンエーテルを１質量％以上含有するポリフェニレンエーテルを含む硬化性樹脂組成物は、成形時の硬化性樹脂組成物の溶融粘度が小さく、良好な成形性が得られる点で有利である。一方、該低分子量・末端官能化ポリフェニレンエーテルを２５質量％以下含有するポリフェニレンエーテルを含む硬化性樹脂組成物は、接着性に劣るという該低分子量・末端官能化ポリフェニレンエーテルの特性が顕著に表れるのを抑制することができ、プリント配線板等において所望される、硬化物の耐吸水性、はんだ耐熱性、及び接着性（例えば、多層板における層間の剥離強度、又は硬化性樹脂組成物の硬化物と銅箔等との剥離強度）を良好に与える点で有利である。そして、ポリフェニレンエーテル中の（Ａ−１）低分子量・末端官能化ポリフェニレンエーテルの割合を上記範囲内に設定することは、白色度及びｂ*値を所望の範囲内に制御することに良好に寄与する。 The (A-1) curable resin composition containing a polyphenylene ether containing 1% by mass or more of a low molecular weight, terminal-functionalized polyphenylene ether has a low melt viscosity of the curable resin composition at the time of molding and good moldability. Is advantageous in that On the other hand, the curable resin composition containing polyphenylene ether containing 25% by mass or less of the low molecular weight terminal-functionalized polyphenylene ether exhibits the characteristic of the low molecular weight terminal-functionalized polyphenylene ether that the adhesiveness is poor. The water absorption resistance, solder heat resistance, and adhesiveness of a cured product (for example, the peel strength between layers in a multilayer board, or the cured product of a curable resin composition, which is desired in a printed wiring board, etc. This is advantageous in that it provides a good peel strength between the copper foil and the copper foil. And, setting the proportion of (A-1) low molecular weight / end-functionalized polyphenylene ether in the polyphenylene ether within the above range contributes well to controlling the whiteness and b * value within the desired range. To do.
また、該（Ａ−１）低分子量・末端官能化ポリフェニレンエーテルの１分子当たりの平均フェノール性水酸基数は０．５個未満であることが好ましいが、より好ましくは０．２個以下であり、更に好ましくは０．１個以下である。該平均フェノール性水酸基数が０．５個未満であれば、低分子量・末端官能化ポリフェニレンエーテルを含有する硬化性樹脂組成物が低い誘電率及び誘電正接の硬化物を形成できることに加えて良好な硬化反応性を有するため、機械特性及び耐熱性に優れた硬化物が得られる。平均フェノール性水酸基数は少ないほど好ましく、０個であっても良いが、フェノール性水酸基を他の官能基で変性させる効率の観点から、好ましくは０．００１個以上、より好ましくは０．０１個以上であることができる。 The average number of phenolic hydroxyl groups per molecule of the (A-1) low molecular weight / end-functionalized polyphenylene ether is preferably less than 0.5, more preferably 0.2 or less, More preferably, it is 0.1 or less. If the average number of phenolic hydroxyl groups is less than 0.5, the curable resin composition containing a low molecular weight and terminal-functionalized polyphenylene ether can form a cured product having a low dielectric constant and dielectric loss tangent. Since it has curing reactivity, a cured product having excellent mechanical properties and heat resistance can be obtained. The average number of phenolic hydroxyl groups is preferably as small as possible, and may be 0, but from the viewpoint of the efficiency of modifying the phenolic hydroxyl groups with other functional groups, it is preferably 0.001 or more, more preferably 0.01. That can be the end.
また、該（Ａ−１）低分子量・末端官能化ポリフェニレンエーテルの数平均分子量は１，０００以上８，０００以下の範囲にあることが好ましく、より好ましい範囲は１，０００以上５，０００以下であり、更に好ましい範囲は２，０００以上４，０００以下である。数平均分子量が８，０００以下であれば、該低分子量・末端官能化ポリフェニレンエーテルを含む硬化性樹脂組成物の成形時の溶融粘度が小さく、良好な成形性が得られる。一方、該数平均分子量が１，０００以上であれば、該低分子量・末端官能化ポリフェニレンエーテルを含む硬化性樹脂組成物が、低い誘電率及び誘電正接、並びに良好な耐熱性及び機械特性を有する硬化物を形成できる。 In addition, the number average molecular weight of the (A-1) low molecular weight / end-functionalized polyphenylene ether is preferably in the range of 1,000 to 8,000, more preferably 1,000 to 5,000. And a more preferable range is 2,000 or more and 4,000 or less. When the number average molecular weight is 8,000 or less, the melt viscosity at the time of molding of the curable resin composition containing the low molecular weight and terminal-functionalized polyphenylene ether is small, and good moldability is obtained. On the other hand, if the number average molecular weight is 1,000 or more, the curable resin composition containing the low molecular weight / end-functionalized polyphenylene ether has low dielectric constant and dielectric loss tangent, and good heat resistance and mechanical properties. A cured product can be formed.
上述の（Ａ−１）低分子量・末端官能化ポリフェニレンエーテルと、（Ａ−２）高分子量ポリフェニレンエーテル成分とを組合せる場合、（Ａ−２）高分子量ポリフェニレンエーテル成分は、好ましくは、該低分子量・末端官能化ポリフェニレンエーテルよりも多い末端フェノール性水酸基を有し，より好ましくは、１分子当たりの平均フェノール性水酸基数０．５個以上を有する。 When combining the above-mentioned (A-1) low molecular weight / terminal functionalized polyphenylene ether with (A-2) high molecular weight polyphenylene ether component, (A-2) high molecular weight polyphenylene ether component is preferably It has more terminal phenolic hydroxyl groups than the molecular weight / terminal functionalized polyphenylene ether, more preferably 0.5 or more average phenolic hydroxyl groups per molecule.
特に好ましい態様において、ポリフェニレンエーテルは、
（Ａ−１）１分子当たりの平均フェノール性水酸基数が０．５個未満であり、かつ数平均分子量が１，０００以上８，０００以下であるポリフェニレンエーテル成分、及び
（Ａ−２）数平均分子量が８，０００を超えるポリフェニレンエーテル成分
を含み、（Ａ−１）と（Ａ−２）との合計質量１００質量％を基準として、（Ａ−１）の含有量が１質量％以上２５質量％以下であり、かつ（Ａ−２）の含有量が７５質量％以上９９質量％以下である。
In a particularly preferred embodiment, the polyphenylene ether is
(A-1) a polyphenylene ether component having an average number of phenolic hydroxyl groups per molecule of less than 0.5 and a number average molecular weight of 1,000 to 8,000, and (A-2) number average A polyphenylene ether component having a molecular weight exceeding 8,000 is included, and the content of (A-1) is 1% by mass or more and 25% by mass based on the total mass of 100% by mass of (A-1) and (A-2). % And the content of (A-2) is 75% by mass or more and 99% by mass or less.
本態様において、ポリフェニレンエーテルは、好ましくは、（Ａ−１）及び（Ａ−２）から実質的になり、より好ましくは（Ａ−１）及び（Ａ−２）からなる。 In this embodiment, the polyphenylene ether preferably consists essentially of (A-1) and (A-2), more preferably (A-1) and (A-2).
（Ａ−１）低分子量・末端官能化ポリフェニレンエーテルにおける末端の官能基の態様は特に限定されるものではなく、ベンジル基、アリル基、プロパギル基、グリシジル基、ビニルベンジル基、メタクリル基等であることができる。その中でも、反応効率が良いため産業的に入手しやすいこと、自身の反応性がなく安定性に優れること、プレス成形時に後述の（Ａ−２）成分の溶融粘度を低下させる効果が著しいこと等の理由で、低分子量・末端官能化ポリフェニレンエーテルは、好ましくは、ポリフェニレンエーテルの分子末端の少なくとも１個のフェノール性水酸基がベンジル基に置換された構造を有するベンジル化ポリフェニレンエーテルである。 (A-1) The mode of the terminal functional group in the low molecular weight / end-functionalized polyphenylene ether is not particularly limited, and is a benzyl group, an allyl group, a propargyl group, a glycidyl group, a vinylbenzyl group, a methacryl group or the like. be able to. Among them, since the reaction efficiency is good, it is easy to obtain industrially, it has no reactivity and is excellent in stability, and the effect of reducing the melt viscosity of the component (A-2) described later during press molding is remarkable. For this reason, the low molecular weight and terminally functionalized polyphenylene ether is preferably a benzylated polyphenylene ether having a structure in which at least one phenolic hydroxyl group at the molecular end of the polyphenylene ether is substituted with a benzyl group.
上記ベンジル化ポリフェニレンエーテルは、１分子当たりの平均フェノール性水酸基数が０．５個未満であり、かつ数平均分子量が１，０００〜８，０００であることができる。ベンジル化ポリフェニレンエーテルとは、置換又は非置換のポリフェニレンエーテルの分子鎖末端に置換又は非置換のベンジル基が結合した構造を持つポリマーを意味する。 The benzylated polyphenylene ether may have an average number of phenolic hydroxyl groups per molecule of less than 0.5 and a number average molecular weight of 1,000 to 8,000. The benzylated polyphenylene ether means a polymer having a structure in which a substituted or unsubstituted benzyl group is bonded to the molecular chain end of the substituted or unsubstituted polyphenylene ether.
より典型的には、本開示のベンジル化ポリフェニレンエーテルは、下記一般式（２）： More typically, the benzylated polyphenylene ether of the present disclosure has the following general formula (2):
［式中、Ｒ５、Ｒ６、Ｒ７、Ｒ８、及びＲ９は各々独立して、水素原子、アルキル基又はハロゲン原子を表し、Ｚは１〜５の整数であり、Ｊは下記一般式（１）： [Wherein, R5, R6, R7, R8 and R9 each independently represent a hydrogen atom, an alkyl group or a halogen atom, Z is an integer of 1 to 5, and J is the following general formula (1):
（式中、Ｒ１、Ｒ２、３及びＲ４は先に定義した通りである。）
で表される単位構造を含むポリフェニレンエーテル分子鎖を表す。］
で表される構造を有する。
(Wherein R1, R2, 3 and R4 are as defined above.)
The polyphenylene ether molecular chain containing the unit structure represented by these is represented. ]
It has the structure represented by these.
Ｊは、実質的に上記一般式（１）で表される構造のみを単位構造として構成されてもよいが、目的に応じて、上記一般式（１）で表される単位構造の他に共重合成分を含んでもよい。 J may be substantially composed of only the structure represented by the general formula (1) as a unit structure. However, depending on the purpose, J may be combined with the unit structure represented by the general formula (1). A polymerization component may be included.
上記一般式（２）において、反応効率の観点から、Ｒ５、Ｒ６、Ｒ７、Ｒ８及びＲ９が、全て水素原子であることが好ましい。 In the general formula (2), from the viewpoint of reaction efficiency, it is preferable that R5, R6, R7, R8 and R9 are all hydrogen atoms.
上記一般式（２）において、重合の際に分子量の制御が比較的容易なため、用途に最適な分子量分布をもつポリマーの合成が容易なことから、Ｊは、ポリ（２，６−ジメチル−１，４−フェニレンエーテル）構造であることが好ましい。また、ポリ（２，６−ジメチル−１，４−フェニレンエーテル）とフェノール化合物とを有機過酸化物存在下で反応させて得られる共重合体構造であることが好ましい。この場合に用いるフェノール化合物は分子内に１個以上のフェノール性水酸基を持てば特に限定されないが、具体的にはフェノール、クレゾール、２，６−キシレノール、２，３，６−トリメチルフェノール、ビスフェノールＡ，ビフェノール、クレゾール・ノボラック骨格フェノール等が挙げられ、反応率の高さの観点から２，６−キシレノール、ビスフェノールＡ、及びクレゾール・ノボラック骨格フェノールが好ましく用いられる。 In the above general formula (2), since the molecular weight can be controlled relatively easily during the polymerization, it is easy to synthesize a polymer having a molecular weight distribution that is optimal for the application. Therefore, J represents poly (2,6-dimethyl- 1,4-phenylene ether) structure is preferable. A copolymer structure obtained by reacting poly (2,6-dimethyl-1,4-phenylene ether) with a phenol compound in the presence of an organic peroxide is preferable. The phenol compound used in this case is not particularly limited as long as it has one or more phenolic hydroxyl groups in the molecule. Specifically, phenol, cresol, 2,6-xylenol, 2,3,6-trimethylphenol, bisphenol A , Biphenol, cresol / novolak skeleton phenol and the like, and 2,6-xylenol, bisphenol A, and cresol / novolak skeleton phenol are preferably used from the viewpoint of high reaction rate.
上記ベンジル化ポリフェニレンエーテルは、数平均分子量が１，０００〜８，０００の範囲であることができ、より好ましい範囲は１，０００〜５，０００、特に好ましい範囲は２，０００〜４，０００である。該数平均分子量が８，０００以下であれば、ベンジル化ポリフェニレンエーテルは溶剤に対する溶解性に優れ、特に４，０００以下では室温（２３℃）でトルエンに３０質量％以上の濃度で溶解する。一方、該数平均分子量が１，０００以上であれば、ベンジル化ポリフェニレンエーテルを含有する硬化性樹脂組成物の硬化物の誘電率及び誘電正接が低くできるとともに硬化物の耐熱性と機械特性とが優れ、特に２，０００以上では誘電率及び誘電正接をより低くすることが可能であるため好ましい。 The benzylated polyphenylene ether may have a number average molecular weight in the range of 1,000 to 8,000, more preferably 1,000 to 5,000, and particularly preferably 2,000 to 4,000. is there. If the number average molecular weight is 8,000 or less, the benzylated polyphenylene ether is excellent in solubility in a solvent, and particularly 4,000 or less dissolves in toluene at a concentration of 30% by mass or more at room temperature (23 ° C.). On the other hand, when the number average molecular weight is 1,000 or more, the dielectric constant and dielectric loss tangent of the cured product of the curable resin composition containing benzylated polyphenylene ether can be lowered, and the heat resistance and mechanical properties of the cured product can be reduced. Excellent, especially 2,000 or more is preferable because the dielectric constant and dielectric loss tangent can be lowered.
上記ベンジル化ポリフェニレンエーテルの１分子当たりの平均フェノール性水酸基数は０．５個未満であることができ、より好ましくは０．２個未満、特に好ましくは０．１個未満である。該平均フェノール性水酸基数が０．５個未満であれば、ベンジル化ポリフェニレンエーテルを含有する硬化性樹脂組成物の硬化物の誘電率及び誘電正接が低い上に、該組成物の硬化反応性が高いため機械特性及び耐熱性に優れた硬化物が得られる。該平均フェノール性水酸基数は小さい程好ましく、０個であってもよいが、フェノール性水酸基を他の官能基で変性させる効率の観点から、好ましくは０．００１個以上、より好ましくは０．０１個以上であることができる。 The average number of phenolic hydroxyl groups per molecule of the benzylated polyphenylene ether can be less than 0.5, more preferably less than 0.2, and particularly preferably less than 0.1. If the average number of phenolic hydroxyl groups is less than 0.5, the cured product of the curable resin composition containing benzylated polyphenylene ether has a low dielectric constant and dielectric loss tangent, and the composition has a curing reactivity. Since it is high, a cured product having excellent mechanical properties and heat resistance can be obtained. The average number of phenolic hydroxyl groups is preferably as small as possible, and may be 0. However, from the viewpoint of the efficiency of modifying the phenolic hydroxyl group with other functional groups, it is preferably 0.001 or more, more preferably 0.01. It can be more than one.
上記ベンジル化ポリフェニレンエーテルは、典型的には、ポリフェニレンエーテルとベンジル化合物との反応によって得ることができる。例えば、ベンジル化ポリフェニレンエーテルは、原料のポリフェニレンエーテル（例えば上記一般式（１）で表される単位構造を含むポリフェニレンエーテル）が持つフェノール性水酸基と、下記一般式（３）： The benzylated polyphenylene ether can typically be obtained by reaction of polyphenylene ether and a benzyl compound. For example, the benzylated polyphenylene ether includes a phenolic hydroxyl group possessed by a raw material polyphenylene ether (for example, a polyphenylene ether containing a unit structure represented by the above general formula (1)), and the following general formula (3):
（式中、Ｒ５、Ｒ６、Ｒ７、Ｒ８及びＲ９は一般式（２）において定義した通りであり、Ｘはハロゲン原子又はシアノ基を表す。）
で表されるベンジル化合物との反応によって得られる。
(In the formula, R5, R6, R7, R8 and R9 are as defined in the general formula (2), and X represents a halogen atom or a cyano group.)
It is obtained by reaction with a benzyl compound represented by
上記一般式（３）において、ＸとしてはＦ、Ｃｌ、Ｂｒ、Ｉ、ＣＮ等が挙げられる。一般式（３）で表されるベンジル化合物の具体例としては、塩化ベンジル、ベンジルシアニド、臭化ベンジル、メチルベンジルクロライド、メチルベンジルブロマイド、ジメチルベンジルクロライド、ジメチルベンジルブロマイド、トリメチルベンジルクロライド、トリメチルベンジルブロマイド等が挙げられるが、中でも塩化ベンジルはフェノール性水酸基との反応性が高く、フェノール性水酸基の個数が少ないベンジル化ポリフェニレンエーテルを容易に製造できる点で好ましい。 In the general formula (3), examples of X include F, Cl, Br, I, CN, and the like. Specific examples of the benzyl compound represented by the general formula (3) include benzyl chloride, benzyl cyanide, benzyl bromide, methyl benzyl chloride, methyl benzyl bromide, dimethyl benzyl chloride, dimethyl benzyl bromide, trimethyl benzyl chloride, trimethyl benzyl. Of these, benzyl chloride is preferred because it has high reactivity with phenolic hydroxyl groups and can easily produce benzylated polyphenylene ethers with a small number of phenolic hydroxyl groups.
上記ベンジル化ポリフェニレンエーテルの製造方法は特に限定されないが、例えばポリフェニレンエーテルとベンジル化合物とをトルエン、キシレン等の溶液中で、強アルカリ化合物を触媒に用いて反応させる方法が挙げられる。強アルカリ化合物としては水酸化ナトリウム、水酸化カリウム、水酸化カルシウム等の金属水酸化物、ナトリウムメチラート、ナトリウムエチラート等のアルコラートが例として挙げられる。 Although the manufacturing method of the said benzylated polyphenylene ether is not specifically limited, For example, the method of making a polyphenylene ether and a benzyl compound react in a solution, such as toluene and xylene, using a strong alkali compound as a catalyst is mentioned. Examples of strong alkali compounds include metal hydroxides such as sodium hydroxide, potassium hydroxide and calcium hydroxide, and alcoholates such as sodium methylate and sodium ethylate.
本発明の別の態様は、上述したポリフェニレンエーテルであるポリフェニレンエーテル（Ａ）と、分子内に２個以上のビニル基を持つモノマー（Ｂ）とを含有する、硬化性樹脂組成物を提供する。該硬化性樹脂組成物は、ポリフェニレンエーテル（Ａ）と分子内に２個以上のビニル基を持つモノマー（Ｂ）との合計１００質量部に対して、分子内に２個以上のビニル基を持つモノマー（Ｂ）を好ましくは５〜９５質量部、より好ましくは１０〜８０質量部、更に好ましくは１０〜７０質量部、更に好ましくは２０〜７０質量部含有する。該モノマー（Ｂ）の量が５質量部以上である場合、成形性が良好である点で好ましく、９５質量部以下である場合、誘電率及び誘電正接が低い硬化物を形成できる点で好ましい。 Another aspect of the present invention provides a curable resin composition containing the polyphenylene ether (A), which is the polyphenylene ether described above, and a monomer (B) having two or more vinyl groups in the molecule. The curable resin composition has two or more vinyl groups in the molecule with respect to 100 parts by mass in total of the polyphenylene ether (A) and the monomer (B) having two or more vinyl groups in the molecule. The monomer (B) is preferably contained in an amount of 5 to 95 parts by mass, more preferably 10 to 80 parts by mass, still more preferably 10 to 70 parts by mass, and still more preferably 20 to 70 parts by mass. When the amount of the monomer (B) is 5 parts by mass or more, it is preferable in terms of good moldability, and when it is 95 parts by mass or less, it is preferable in that a cured product having a low dielectric constant and dielectric loss tangent can be formed.
また、硬化性組成物中、上記の（Ａ−１）成分の含有量（ａ）の、分子内に２個以上のビニル基を持つモノマー（特に好ましくはＴＡＩＣ）の含有量（ｂ）に対する組成比（ａ）／（ｂ）は、５／９５〜９５／５（質量比）であることが好ましい。上記組成比が５／９５以上である場合、得られる硬化物の誘電率と誘電正接とが低く好ましく、９５／５以下である場合成形性が良好である。上記組成比は、より好ましくは２０／８０〜９０／１０、特に好ましくは３０／７０〜８０／２０である。 Further, the composition of the content (a) of the component (A-1) in the curable composition with respect to the content (b) of the monomer having two or more vinyl groups in the molecule (particularly preferably TAIC). The ratio (a) / (b) is preferably 5/95 to 95/5 (mass ratio). When the composition ratio is 5/95 or more, the obtained cured product preferably has a low dielectric constant and dielectric loss tangent, and when it is 95/5 or less, the moldability is good. The composition ratio is more preferably 20/80 to 90/10, and particularly preferably 30/70 to 80/20.
本開示において、分子内に２個以上のビニル基を持つモノマーとしてはトリアリルイソシアヌレート（ＴＡＩＣ）、トリアリルシアヌレート、トリアリルアミン、トリアリルメセート、ジビニルベンゼン、ジビニルナフタレン、ジビニルビフェニル等が挙げられるが、ポリフェニレンエーテルとの相溶性が良好なＴＡＩＣが好ましい。 In the present disclosure, examples of the monomer having two or more vinyl groups in the molecule include triallyl isocyanurate (TAIC), triallyl cyanurate, triallylamine, triallyl mesate, divinylbenzene, divinylnaphthalene, and divinylbiphenyl. However, TAIC having good compatibility with polyphenylene ether is preferable.
本態様の硬化性樹脂組成物は、更に好ましくは、ポリフェニレンエーテル（Ａ）と、分子内に２個以上のビニル基を持つモノマー（Ｂ）と、反応開始剤（Ｃ）とを含む。 More preferably, the curable resin composition of this embodiment contains polyphenylene ether (A), a monomer (B) having two or more vinyl groups in the molecule, and a reaction initiator (C).
反応開始剤（Ｃ）としては、ビニルモノマーの重合反応を促進する能力を有する任意の開始剤を使用でき、例えば、ベンゾイルパーオキサイド、クメンハイドロパーオキサイド、２，５−ジメチルヘキサン−２，５−ジハイドロパーオキサイド、２，５−ジメチル−２，５−ジ（ｔ−ブチルパーオキシ）ヘキシン−３、ジ−ｔ−ブチルパーオキサイド、ｔ−ブチルクミルパーオキサイド、α，α’−ビス（ｔ−ブチルパーオキシ−ｍ−イソプロピル）ベンゼン、２，５−ジメチル−２，５−ジ（ｔ−ブチルパーオキシ）ヘキサン、ジクミルパーオキサイド、ジ−ｔ−ブチルパーオキシイソフタレート、ｔ−ブチルパーオキシベンゾエート、２，２−ビス（ｔ−ブチルパーオキシ）ブタン、２，２−ビス（ｔ−ブチルパーオキシ）オクタン、２，５−ジメチル−２，５−ジ（ベンゾイルパーオキシ）ヘキサン、ジ（トリメチルシリル）パーオキサイド、トリメチルシリルトリフェニルシリルパーオキサイド等の過酸化物が挙げられる。また、２，３−ジメチル−２，３−ジフェニルブタン等のラジカル発生剤も反応開始剤として使用できる。中でも、得られる耐熱性及び機械特性に優れ、更に低い誘電率及び誘電正接を有する硬化物を与えることができるの観点から、２，５−ジメチル−２，５−ジ（ｔ−ブチルパーオキシ）ヘキシン−３、α，α’−ビス（ｔ−ブチルパーオキシ−ｍ−イソプロピル）ベンゼン、２，５−ジメチル−２，５−ジ（ｔ−ブチルパーオキシ）ヘキサンが好ましい。 As the reaction initiator (C), any initiator having the ability to promote the polymerization reaction of vinyl monomers can be used. For example, benzoyl peroxide, cumene hydroperoxide, 2,5-dimethylhexane-2,5- Dihydroperoxide, 2,5-dimethyl-2,5-di (t-butylperoxy) hexyne-3, di-t-butyl peroxide, t-butylcumyl peroxide, α, α′-bis (t -Butylperoxy-m-isopropyl) benzene, 2,5-dimethyl-2,5-di (t-butylperoxy) hexane, dicumyl peroxide, di-t-butylperoxyisophthalate, t-butylper Oxybenzoate, 2,2-bis (t-butylperoxy) butane, 2,2-bis (t-butylperoxy) octane, 2, Examples thereof include peroxides such as 5-dimethyl-2,5-di (benzoylperoxy) hexane, di (trimethylsilyl) peroxide, and trimethylsilyltriphenylsilyl peroxide. A radical generator such as 2,3-dimethyl-2,3-diphenylbutane can also be used as a reaction initiator. Among them, 2,5-dimethyl-2,5-di (t-butylperoxy) is preferable from the viewpoint of obtaining a cured product having excellent heat resistance and mechanical properties and having a lower dielectric constant and dielectric loss tangent. Hexin-3, α, α′-bis (t-butylperoxy-m-isopropyl) benzene and 2,5-dimethyl-2,5-di (t-butylperoxy) hexane are preferred.
ポリフェニレンエーテル（Ａ）とモノマー（Ｂ）との合計１００質量部に対して、反応開始剤（Ｃ）の含有量は、反応率を高くできる観点から好ましくは０．５質量部以上、より好ましくは１質量部以上、更に好ましくは１．５質量部以上であり、得られる硬化物の誘電率及び誘電正接を低く抑えることができる観点から、好ましくは１５質量部以下、より好ましくは１０質量部以下、更に好ましくは７質量部以下である。 The content of the reaction initiator (C) is preferably 0.5 parts by mass or more, more preferably from the viewpoint of increasing the reaction rate, with respect to a total of 100 parts by mass of the polyphenylene ether (A) and the monomer (B). 1 part by mass or more, more preferably 1.5 parts by mass or more, and from the viewpoint that the dielectric constant and dielectric loss tangent of the obtained cured product can be kept low, preferably 15 parts by mass or less, more preferably 10 parts by mass or less. More preferably, it is 7 parts by mass or less.
好ましい態様において、ポリフェニレンエーテル（Ａ）とモノマー（Ｂ）との合計１００質量部に対して、モノマー（Ｂ）の含有量が１０質量部以上７０質量部以下、及び反応開始剤（Ｃ）の含有量が１質量部以上１０質量部以下である。 In a preferred embodiment, the content of the monomer (B) is 10 parts by mass or more and 70 parts by mass or less, and the reaction initiator (C) is contained with respect to 100 parts by mass in total of the polyphenylene ether (A) and the monomer (B). The amount is 1 part by mass or more and 10 parts by mass or less.
本発明の硬化性樹脂組成物には別の樹脂（例えば熱可塑性樹脂、硬化性樹脂等）を更に含有させることもできる。熱可塑性樹脂としては、エチレン、プロピレン、ブタジエン、イソプレン、スチレン、ジビニルベンゼン、メタクリル酸、アクリル酸、メタクリル酸エステル、アクリル酸エステル、塩化ビニル、アクリロニトリル、無水マレイン酸、酢酸ビニル、四フッ化エチレン等のビニル化合物の単独重合体及び２種以上のビニル化合物の共重合体、並びに、ポリアミド、ポリイミド、ポリカーボネート、ポリエステル、ポリアセタール、ポリフェニレンスルフィド、ポリエチレングリコール等を例として挙げることができる。これらの中でもスチレンの単独重合体、スチレン−ブタジエン共重合体、及びスチレン−エチレン−ブタジエン共重合体が、硬化性樹脂組成物の溶剤への溶解性及び成形性の観点から好ましく用いることができる。硬化性樹脂としては、フェノール樹脂、エポキシ樹脂、及びシアネートエステル類を例として挙げることができる。上記熱可塑性樹脂及び硬化性樹脂は、酸無水物、エポキシ化合物、アミン等の官能化化合物で変成されたものでもよい。このような別の樹脂の使用量は、上記ポリフェニレンエーテル（Ａ）と上記モノマー（Ｂ）との合計１００質量部に対して、好ましくは１０〜９０質量部、より好ましくは２０〜７０質量部である。 The curable resin composition of the present invention may further contain another resin (for example, a thermoplastic resin or a curable resin). Thermoplastic resins include ethylene, propylene, butadiene, isoprene, styrene, divinylbenzene, methacrylic acid, acrylic acid, methacrylic ester, acrylic ester, vinyl chloride, acrylonitrile, maleic anhydride, vinyl acetate, ethylene tetrafluoride, etc. Examples thereof include homopolymers of vinyl compounds and copolymers of two or more vinyl compounds, and polyamides, polyimides, polycarbonates, polyesters, polyacetals, polyphenylene sulfides, polyethylene glycols, and the like. Among these, a styrene homopolymer, a styrene-butadiene copolymer, and a styrene-ethylene-butadiene copolymer can be preferably used from the viewpoints of solubility of the curable resin composition in a solvent and moldability. Examples of the curable resin include phenol resins, epoxy resins, and cyanate esters. The thermoplastic resin and curable resin may be modified with a functional compound such as an acid anhydride, an epoxy compound, or an amine. The amount of such another resin used is preferably 10 to 90 parts by mass, more preferably 20 to 70 parts by mass with respect to 100 parts by mass in total of the polyphenylene ether (A) and the monomer (B). is there.
本発明の硬化性樹脂組成物は目的に応じ適当な添加剤を更に含有してもよい。添加剤としては、難燃剤、熱安定剤、酸化防止剤、ＵＶ吸収剤、界面活性剤、滑剤、充填剤、ポリマー添加剤等が挙げられる。 The curable resin composition of the present invention may further contain an appropriate additive depending on the purpose. Examples of the additive include a flame retardant, a heat stabilizer, an antioxidant, a UV absorber, a surfactant, a lubricant, a filler, and a polymer additive.
特に、本発明の硬化性樹脂組成物が更に難燃剤を含む場合、本発明の有する良好な成形性、耐吸水性、はんだ耐熱性、及び接着性（例えば、多層板における層間の剥離強度、又は硬化物と銅箔等との剥離強度）に優れるプリント配線板等が得られる利点に加え、難燃性を付与できる点で好適である。 In particular, when the curable resin composition of the present invention further contains a flame retardant, the good moldability, water absorption resistance, solder heat resistance, and adhesiveness of the present invention (for example, peel strength between layers in a multilayer board, or In addition to the advantage that a printed wiring board having excellent peel strength between a cured product and copper foil or the like can be obtained, it is preferable in terms of imparting flame retardancy.
難燃剤としては、燃焼のメカニズムを阻害する機能を有するものであれば特に制限されず、三酸化アンチモン、水酸化アルミニウム、水酸化マグネシウム、ほう酸亜鉛等の無機難燃剤、ヘキサブロモベンゼン、デカブロモジェフェニルエタン、４，４−ジフブロモフェニル、エチレンビステトラブロモフタルイミド等の芳香族臭素化合物、等が挙げられる。中でも、得られる硬化物の誘電率及び誘電正接を低く抑えられる観点からデカブロモジェフェニルエタン等が好ましい。 The flame retardant is not particularly limited as long as it has a function of hindering the combustion mechanism. Inorganic flame retardants such as antimony trioxide, aluminum hydroxide, magnesium hydroxide, zinc borate, hexabromobenzene, decabromobenzene And aromatic bromine compounds such as phenylethane, 4,4-diphbromophenyl, and ethylenebistetrabromophthalimide. Of these, decabromojephenylethane is preferred from the viewpoint of keeping the dielectric constant and dielectric loss tangent of the cured product low.
難燃剤の使用量は、使用する難燃剤によって異なり、特に限定するものでないが、ＵＬ規格９４Ｖ−０レベルの難燃性を維持する観点から、ポリフェニレンエーテル（Ａ）とモノマー（Ｂ）との合計１００質量部に対して好ましくは５質量部以上、より好ましくは１０質量部以上、更に好ましくは１５質量部以上である。また、得られる硬化物の誘電率及び誘電正接を小さく維持できる観点から、好ましくは５０質量部以下、より好ましくは４５質量部以下、更に好ましくは４０質量部以下である。 The amount of flame retardant used varies depending on the flame retardant used, and is not particularly limited. From the viewpoint of maintaining flame retardancy at the UL standard 94V-0 level, the total of polyphenylene ether (A) and monomer (B) Preferably it is 5 mass parts or more with respect to 100 mass parts, More preferably, it is 10 mass parts or more, More preferably, it is 15 mass parts or more. Moreover, from a viewpoint which can maintain the dielectric constant and dielectric loss tangent of the hardened | cured material small, Preferably it is 50 mass parts or less, More preferably, it is 45 mass parts or less, More preferably, it is 40 mass parts or less.
上述した硬化性樹脂組成物を含有するワニスもまた開示される。該ワニスは、本発明の硬化性樹脂組成物を溶剤に溶解又は分散させることによって形成できる。このワニスを、例えばガラスクロス等である基材に含浸させた後、溶剤分を乾燥除去することにより、例えば基板材料の絶縁層の材料として好適なプリプレグを製造できる。 A varnish containing the curable resin composition described above is also disclosed. The varnish can be formed by dissolving or dispersing the curable resin composition of the present invention in a solvent. After impregnating the varnish with a base material such as glass cloth, the solvent content is removed by drying, whereby a prepreg suitable as a material for the insulating layer of the substrate material can be produced.
上記ワニスに用いられる溶剤としては、トルエン、キシレン、メチルエチルケトン、アセトン等を挙げることができる。これらの溶剤は単独でも２種以上を混合しても使用できる。また、例えば上記各種の溶剤の１種以上とメタノール等のアルコール類とを組合せてもよい。ワニスに占める硬化性樹脂組成物の割合は、基材へのワニス含浸性及び基材への樹脂付着量を良好に制御する観点から、ワニス全量１００質量部に対して、５〜９５質量部であることが好ましく、２０〜８０質量部であることがより好ましい。 Examples of the solvent used for the varnish include toluene, xylene, methyl ethyl ketone, and acetone. These solvents can be used alone or in combination of two or more. For example, you may combine 1 or more types of said various solvents, and alcohols, such as methanol. The ratio of the curable resin composition in the varnish is 5 to 95 parts by mass with respect to 100 parts by mass of the varnish from the viewpoint of satisfactorily controlling the varnish impregnation property to the substrate and the resin adhesion amount to the substrate. It is preferable that it is 20 to 80 parts by mass.
本発明の別の態様は、上述した本発明の硬化性樹脂組成物と、基材とを含むプリプレグを提供する。プリプレグは典型的にはプリント配線板用プリプレグである。典型的なプリプレグは、該硬化性樹脂組成物を含有するワニスを基材に含浸させた後、熱風乾燥機等で溶剤分を揮発させて得られる、硬化性樹脂組成物と基材との複合体である。基材としては、ロービングクロス、クロス、チョップドマット、サーフェシングマット等の各種ガラス布；アスベスト布、金属繊維布、及びその他合成若しくは天然の無機繊維布；全芳香族ポリアミド繊維、全芳香族ポリエステル繊維、ポリベンゾオキサゾール繊維等の液晶繊維から得られる織布又は不織布；綿布、麻布、フェルト等の天然繊維布；カーボン繊維布、クラフト紙、コットン紙、紙−ガラス混繊糸から得られる布等の天然セルロース系基材；ポリテトラフルオロエチレン多孔質フィルム；等を単独で、又は２種以上組合せて用いることができる。 Another aspect of the present invention provides a prepreg comprising the curable resin composition of the present invention described above and a substrate. The prepreg is typically a printed circuit board prepreg. A typical prepreg is a composite of a curable resin composition and a substrate obtained by impregnating a varnish containing the curable resin composition into a substrate and then volatilizing the solvent with a hot air dryer or the like. Is the body. As the base material, various glass cloths such as roving cloth, cloth, chopped mat, and surfacing mat; asbestos cloth, metal fiber cloth, and other synthetic or natural inorganic fiber cloth; wholly aromatic polyamide fiber, wholly aromatic polyester fiber Woven or non-woven fabrics obtained from liquid crystal fibers such as polybenzoxazole fibers; natural fiber fabrics such as cotton cloth, linen cloth and felt; carbon fiber cloth, kraft paper, cotton paper, cloth obtained from paper-glass mixed yarn, etc. Natural cellulose base materials; polytetrafluoroethylene porous films; etc. can be used alone or in combination of two or more.
上記プリプレグに占める硬化性樹脂組成物の割合は、プリプレグ全量１００質量部に対して、３０〜８０質量部であることが好ましく、より好ましくは４０〜７０質量部である。上記割合が３０質量部以上である場合、プリプレグを例えば電子基板形成用として使用した際に優れた絶縁信頼性が得られ、８０質量部以下である場合、例えば得られる電子基板が曲げ弾性率等の機械特性に優れる。 The proportion of the curable resin composition in the prepreg is preferably 30 to 80 parts by mass, more preferably 40 to 70 parts by mass with respect to 100 parts by mass of the total amount of prepreg. When the proportion is 30 parts by mass or more, excellent insulation reliability is obtained when the prepreg is used for forming an electronic substrate, for example. When the ratio is 80 parts by mass or less, the obtained electronic substrate has a flexural modulus, etc. Excellent mechanical properties.
プリプレグは、L*ａ*ｂ*表色系での白色度：８５以上、及びｂ*値：９以下を有することが好ましい。白色度及びｂ*値が上記範囲内であることは異物発見の容易性の観点から有利である。白色度及びｂ*値のより好ましい範囲は、硬化性樹脂組成物から作製される白色度測定用試料について前述したのと同様であることができる。 The prepreg preferably has a whiteness in the L * a * b * color system: 85 or more and a b * value: 9 or less. The whiteness and b * values being within the above ranges are advantageous from the viewpoint of easy detection of foreign matter. More preferable ranges of the whiteness and the b * value can be the same as those described above for the whiteness measurement sample prepared from the curable resin composition.
上述した本発明の硬化性樹脂組成物を用い、該硬化性樹脂組成物の硬化物と基材とを含む硬化物複合体と、金属箔とが積層されている積層板を形成できる。該積層板は、好ましくは、上記硬化物複合体と金属箔とが重なって密着しているもので、電子基板の材料として好適に用いられる。金属箔としては例えばアルミ箔及び銅箔を用いることができ、中でも銅箔は電気抵抗が低いため好ましい。金属箔と組合せる硬化物複合体は１枚でも複数枚でもよく、用途に応じて複合体の片面又は両面に金属箔を重ねて積層板に加工する。積層板の製造方法としては、例えば、硬化性樹脂組成物と基材とから構成される複合体（例えば前述のプリプレグ）を形成し、これを金属箔と重ねた後、硬化性樹脂組成物を硬化させることにより、硬化物積層体と金属箔とが積層されている積層板を得る方法が挙げられる。該積層板の特に好ましい用途の１つはプリント配線板である。 By using the curable resin composition of the present invention described above, a laminate in which a cured product composite containing a cured product of the curable resin composition and a substrate and a metal foil are laminated can be formed. The laminate is preferably one in which the cured product composite and the metal foil are in close contact with each other, and is suitably used as a material for an electronic substrate. As the metal foil, for example, an aluminum foil and a copper foil can be used, and among them, the copper foil is preferable because of its low electric resistance. The cured product composite to be combined with the metal foil may be one sheet or a plurality of sheets, and the metal foil is overlapped on one side or both sides of the composite to be processed into a laminate according to the use. As a manufacturing method of a laminated board, for example, a composite composed of a curable resin composition and a base material (for example, the above-described prepreg) is formed, and this is overlapped with a metal foil. The method of obtaining the laminated board on which the hardened | cured material laminated body and metal foil are laminated | stacked by making it harden | cure is mentioned. One particularly preferred application of the laminate is a printed wiring board.
本発明の別の態様は、上述した本発明の硬化性樹脂組成物の硬化物と、基材とを含むプリント配線板を提供する。本発明のプリント配線板は、典型的には、上述した本発明のプリプレグを用いて、加圧加熱成型する方法で形成できる。基材としてはプリプレグに関して前述したのと同様のものが挙げられる。本発明のプリント配線板は、上述したような硬化性樹脂組成物を用いて形成されていることにより、優れた絶縁信頼性及び機械特性を有することができる。 Another aspect of the present invention provides a printed wiring board comprising a cured product of the curable resin composition of the present invention described above and a base material. The printed wiring board of the present invention can typically be formed by a method of pressure and heat molding using the prepreg of the present invention described above. Examples of the substrate include the same materials as described above with respect to the prepreg. Since the printed wiring board of the present invention is formed using the curable resin composition as described above, it can have excellent insulation reliability and mechanical properties.
以下、実施例により、本実施形態を更に詳しく説明するが、本実施形態は以下の実施例により何ら限定されるものではない。 Hereinafter, the present embodiment will be described in more detail by way of examples. However, the present embodiment is not limited to the following examples.
実施例、比較例及び製造例中の各物性は、以下の方法によって測定した。 Each physical property in Examples, Comparative Examples and Production Examples was measured by the following method.
（１）ポリフェニレンエーテルの数平均分子量
ゲルパーミエーションクロマトグラフィ分析（ＧＰＣ）を用い、分子量既知の標準ポリスチレンの溶出時間との比較で数平均分子量を求めた。
測定装置にはＨＬＣ−８２２０ＧＰＣ（東ソー株式会社製）を用い、カラム：Ｓｈｏｄｅｘ ＬＦ−８０４×２（昭和電工株式会社製）、溶離液：５０℃のクロロホルム、検出器：ＲＩ、の条件で測定を行った。
(1) Number average molecular weight of polyphenylene ether Using gel permeation chromatography analysis (GPC), the number average molecular weight was determined by comparison with the elution time of standard polystyrene having a known molecular weight.
HLC-8220GPC (manufactured by Tosoh Corporation) is used as a measuring apparatus, and measurement is performed under the conditions of column: Shodex LF-804 × 2 (manufactured by Showa Denko KK), eluent: chloroform at 50 ° C., detector: RI. went.
（２）ポリフェニレンエーテル１分子当たりの平均フェノール性水酸基数
吸光度から求めたポリフェニンエーテルに含まれるフェノール性水酸基数と、平均分子量から求めたポリフェニンエーテルの分子数とを用い、１分子当たりの平均フェノール性水酸基数を求めた。
先ず、高分子論文集，ｖｏｌ．５１，Ｎｏ．７（１９９４），第４８０頁記載の方法に準拠し、ポリフェニレンエーテルの塩化メチレン溶液にテトラメチルアンモニウムハイドロオキシド溶液を加えて得た試料の波長３１８ｎｍにおける吸光度変化を紫外可視吸光光度計で測定した値から水酸基の数を求めた。
別途、ポリフェニレンエーテルの数平均分子量を、上記（１）に従いゲルパーミエーションクロマトグラフィにより求め、この値を用いて、ポリフェニレンエーテルの分子数を求めた。これらの値から、下記式に従って、ポリフェニレンエーテルの１分子当たりの平均水酸基数を算出した。
１分子当たりの平均フェノール性水酸基数＝水酸基の数／数平均分子数
(2) Average number of phenolic hydroxyl groups per molecule of polyphenylene ether Using the number of phenolic hydroxyl groups contained in polyphenine ether determined from absorbance and the number of molecules of polyphenine ether determined from average molecular weight, the average per molecule The number of phenolic hydroxyl groups was determined.
First, collection of polymer papers, vol. 51, no. 7 (1994), in accordance with the method described on page 480, a value obtained by measuring an absorbance change at a wavelength of 318 nm of a sample obtained by adding a tetramethylammonium hydroxide solution to a methylene chloride solution of polyphenylene ether with an ultraviolet-visible spectrophotometer. From this, the number of hydroxyl groups was determined.
Separately, the number average molecular weight of polyphenylene ether was determined by gel permeation chromatography according to (1) above, and the number of molecules of polyphenylene ether was determined using this value. From these values, the average number of hydroxyl groups per molecule of polyphenylene ether was calculated according to the following formula.
Average number of phenolic hydroxyl groups per molecule = number of hydroxyl groups / number average number of molecules
（３）硬化性樹脂組成物の硬化時の樹脂フロー量
プリプレグを加熱加圧成形して積層板を作製する際に、流れ出した樹脂の質量の、もとの質量（加熱加圧成形に供したプリプレグ）に対する割合として求めた。
(3) Resin flow amount during curing of the curable resin composition When a prepreg was heated and pressed to produce a laminate, the original mass of the flowed out resin (subjected to heating and pressing) It was calculated | required as a ratio with respect to a prepreg.
硬化性樹脂組成物をトルエンと混合してワニスを作製し、該ワニスをガラスクロス（２１１６ 旭化成シェーベル株式会社製）に含浸させた後、乾燥してトルエン溶剤を除き、樹脂含量約６０質量％のプリプレグを作製した。該プリプレグを１５０ｍｍ角に２枚切り出し、試験片とした。ここで、試験片２枚の質量（ｇ）を求めておき、積層板前駆体の質量とした。 The curable resin composition is mixed with toluene to prepare a varnish, and the varnish is impregnated into a glass cloth (2116 manufactured by Asahi Kasei Shovel Co., Ltd.), then dried to remove the toluene solvent, and the resin content is about 60% by mass. A prepreg was prepared. Two pieces of the prepreg were cut into 150 mm squares to obtain test pieces. Here, the mass (g) of the two test pieces was determined and used as the mass of the laminate precursor.
次いで、該試験片２枚を重ね、室温から昇温速度３℃／分で加熱しながら圧力５ｋｇ／ｃｍ2の条件で真空プレスを行い、１３０℃まで達したら昇温速度３℃／分で加熱しながら圧力３０ｋｇ／ｃｍ2の条件で真空プレスを行い、２００℃まで達したら温度を２００℃に保ったまま圧力３０ｋｇ／ｃｍ2、時間６０分間の条件で真空プレスを行い、１５０ｍｍ角部から流れ出した樹脂を取り除いて積層板を得た。この積層板について質量を求め、積層板の質量（ｇ）とした。
積層板前駆体の質量（ｇ）と積層板の質量（ｇ）とを用い、下記式より、硬化性樹脂組成物の硬化時樹脂フロー量（％）を求めた。
硬化時樹脂フロー量（％）＝（積層板前駆体の質量（ｇ）−積層板の質量（ｇ））／積層板前駆体の質量（ｇ）×１００
Next, the two test pieces were stacked and vacuum-pressed under the condition of a pressure of 5 kg / cm 2 while heating from room temperature at a heating rate of 3 ° C./min. When reaching 130 ° C., heating was performed at a heating rate of 3 ° C./min. While pressing at a pressure of 30 kg / cm 2, when the temperature reaches 200 ° C., the pressure is kept at 200 ° C. and the pressure is 30 kg / cm 2 for 60 minutes. The resin was removed to obtain a laminate. Mass was calculated | required about this laminated board, and it was set as the mass (g) of the laminated board.
Using the mass (g) of the laminate precursor and the mass (g) of the laminate, the resin flow amount (%) during curing of the curable resin composition was determined from the following formula.
Resin flow rate during curing (%) = (mass of laminate precursor (g) −mass of laminate (g)) / mass of laminate precursor (g) × 100
（４）積層板のガラス転移温度
積層板の動的粘弾性を測定し、ｔａｎδが最大となる温度を求めた。
測定装置としてＡＲＥＳＳ（ＴＡインスツルメンツ社製）を用い、試験片：長さ約４５ｍｍ、幅約１２．５ｍｍ及び厚さ約３ｍｍ、ひねりモード、周波数：１０ｒａｄ／ｓの条件で測定を行った。
(4) Glass transition temperature of laminated board The dynamic viscoelasticity of the laminated board was measured, and the temperature at which tan δ was maximum was determined.
Measurement was performed using ARESS (manufactured by TA Instruments) as a measuring apparatus under the conditions of a test piece: length of about 45 mm, width of about 12.5 mm, thickness of about 3 mm, twist mode, and frequency: 10 rad / s.
（５）積層板の誘電率、誘電正接
積層板の１ＧＨｚにおける誘電率及び誘電正接を、インピーダンスアナライザーを用いて測定した。
測定装置としてインピーダンスアナライザー（４２９１Ｂ ｏｐ．００２ ｗｉｔｈ １６４５３Ａ，１６４５４Ａ、ＡｇｉｌｅｎｔＴｅｃｈｎｏｌｏｇｉｅｓ社製）を用い、試験片厚さ：約２ｍｍ、電圧：１００ｍＶ、周波数：１ＭＨｚ〜１．８ＧＨｚの条件で測定し、掃引回数１００回の平均値として求めた。
(5) Dielectric constant and dielectric loss tangent of laminated plate The dielectric constant and dielectric loss tangent of the laminated plate at 1 GHz were measured using an impedance analyzer.
Using an impedance analyzer (4291B op.002 with 16453A, 16454A, manufactured by Agilent Technologies) as a measuring device, the test piece thickness is about 2 mm, the voltage is 100 mV, the frequency is 1 MHz to 1.8 GHz, and the number of sweeps is 100. It calculated | required as an average value of times.
（６）積層板の吸水率
積層板を吸水加速試験に供し、増加した質量から吸水率を求めた。
積層板を５０ｍｍ角に切り出し試験片を作製した。該試験片を１３０℃で３０分乾燥した後、質量を測定し、加速試験前の質量（ｇ）とした。次いで、温度：１２１℃、圧力：２ａｔｍ、時間：４時間、の条件で加速試験を行った後の質量を測定し、加速試験後の質量（ｇ）とした。
加速試験前の質量（ｇ）と加速試験後の質量（ｇ）とを用い、下記式により吸水率を算出し、試験片４枚の測定値の平均値を求めた。
吸水率（質量％）＝（加速試験前の質量―加速試験後質量）／加速試験前の質量×１００
(6) Water Absorption Rate of Laminate Plate The laminate plate was subjected to a water absorption acceleration test, and the water absorption rate was determined from the increased mass.
The laminate was cut into 50 mm squares to produce test pieces. After the test piece was dried at 130 ° C. for 30 minutes, the mass was measured to obtain the mass (g) before the acceleration test. Subsequently, the mass after the acceleration test was performed under the conditions of temperature: 121 ° C., pressure: 2 atm, and time: 4 hours, and the mass (g) after the acceleration test was measured.
Using the mass (g) before the acceleration test and the mass (g) after the acceleration test, the water absorption was calculated by the following formula, and the average value of the measured values of the four test pieces was obtained.
Water absorption (mass%) = (mass before acceleration test−mass after acceleration test) / mass before acceleration test × 100
（７）積層板の吸水試験後のはんだ耐熱性
上記（６）に記載の吸水率の測定後の積層板を用い、２８８℃及び２６０℃でのはんだ耐熱試験を行った。吸水加速試験後の積層板を、２８８℃又は２６０℃のはんだ浴に２０秒間浸漬し、目視による観察を行った。２８８℃のはんだ浴へ浸漬しても、膨れ、剥離及び白化の何れも確認されなかった積層板については「はんだ耐熱２８８℃」と評価した。また、２８８℃のはんだ浴への浸漬により、膨れ、剥離及び白化の何れか１つ以上が発生したが、２６０℃のはんだ浴へ浸漬しても、膨れ、剥離及び白化の何れも確認されなかった積層板については「はんだ耐熱２６０℃」と評価した。また、２６０℃のはんだ浴への浸漬により、膨れ、剥離及び白化の何れか１つ以上が発生した積層板は「不合格」と評価した。
(7) Solder heat resistance after water absorption test of laminated board A solder heat resistance test was performed at 288 ° C and 260 ° C using the laminated board after measuring the water absorption rate described in (6) above. The laminated board after the water absorption acceleration test was immersed in a solder bath at 288 ° C. or 260 ° C. for 20 seconds, and visually observed. A laminated board in which neither swelling, peeling or whitening was confirmed even when immersed in a solder bath at 288 ° C. was evaluated as “solder heat resistance 288 ° C.”. In addition, any one or more of swelling, peeling and whitening occurred by immersion in a solder bath at 288 ° C., but neither swelling nor peeling or whitening was confirmed even when immersed in a solder bath at 260 ° C. The laminated board was evaluated as “solder heat resistance 260 ° C.”. Moreover, the laminated board which generate | occur | produced any one or more of a swelling, peeling, and whitening by immersion in a 260 degreeC solder bath was evaluated as "failed."
（８）積層板の銅箔引き剥がし強さ
銅張積層板の銅箔を一定速度で引き剥がす際の応力を測定した。後述の方法で作製した、３５μｍ銅箔（ＧＴＳ−ＭＰ箔、古川電気工業株式会社製）を用いた銅張積層板を、幅１５ｍｍ×長さ１５０ｍｍのサイズに切り出し、オートグラフ（ＡＧ−５０００Ｄ、株式会社島津製作所製）を用い、銅箔を除去面に対し９０℃の角度で５０ｍｍ／分の速度で引き剥がした際の荷重の平均値を測定し、５回の測定の平均値を求めた。
(8) Copper foil peeling strength of laminated board The stress at the time of peeling the copper foil of a copper clad laminated board at a fixed speed was measured. A copper-clad laminate using a 35 μm copper foil (GTS-MP foil, manufactured by Furukawa Electric Co., Ltd.) produced by the method described below was cut into a size of 15 mm wide × 150 mm long, and an autograph (AG-5000D, Shimadzu Corporation) was used to measure the average value of the load when the copper foil was peeled off at a speed of 50 mm / min at an angle of 90 ° C. with respect to the removal surface, and the average value of five measurements was obtained. .
（９）Ｌ*ａ*ｂ*表色系評価
分光測色計（ＣＭ−２６００ｄ／ＫＯＮＩＣＡ ＭＩＮＯＬＴＡ ＳＥＮＳＩＮＧ社製）を用いて測定した。
ＳＣＩ（正反射光含む）モードのＬ*値、ａ*値、ｂ*値を用い、ハンター白色度、及びｂ*を求めた。
なお、ハンター白色度は下式より算出して求めた。
ハンター白色度＝１００−（（１００−Ｌ）2＋（ａ2＋ｂ2））1/2
(9) L * a * b * Color system evaluation Measurement was performed using a spectrocolorimeter (CM-2600d / KONICA MINOLTA SENSING).
Hunter whiteness and b * were determined using the L * value, a * value, and b * value of the SCI (including specular reflection light) mode.
Hunter whiteness was calculated from the following formula.
Hunter whiteness = 100 − ((100−L) 2 + (a 2 + b 2 )) 1/2
（１０）異物検査
任意に選出した検査員３人により、同一のプリプレグ（５００ｍｍ×５５０ｍｍ、１００枚）の異物数を目視で評価した。
検査環境は１２００〜１５００ルクス、検査時間は１０分とした。
なお、プリプレグとの色調の違い（例えば、黒色、茶色、銀色、灰色等）等により、明らかに外来混入物と判断できるものを異物とした。
(10) Foreign matter inspection The number of foreign matters of the same prepreg (500 mm × 550 mm, 100 sheets) was visually evaluated by three arbitrarily selected inspectors.
The inspection environment was 1200 to 1500 lux, and the inspection time was 10 minutes.
In addition, the thing which can be judged to be an extraneous substance by the difference in color tone (for example, black, brown, silver, gray, etc.) with a prepreg was made into the foreign material.
実施例、比較例及び製造例において使用した原材料を以下に示す。
ポリフェニレンエーテル：Ｓ２０２Ａ（旭化成ケミカルズ製、数平均分子量１９，０００、１分子当たりの平均フェノール性水酸基数１．８４個）
低分子量・メタクリル化ポリフェニレンエーテル：ＭＸ９０００（ＳＡＢＩＣ製、数平均分子量１，１００、１分子当たりの平均フェノール性水酸基数０．０４個）
ビスフェノールＡ：東京化成工業製
６質量％ナフテン酸コバルトミネラルスピリット溶液：和光純薬工業製
ベンゾイルパーオキサイド溶液：ナイパーＢＭＴ Ｋ−４０（日油製、ベンゾイルパーオキサイドの４０質量％キシレン溶液）
テトラブチルアンモニウムヨージド：和光純薬工業製
塩化ベンジル：東京化成工業製
クロロメチルスチレン：和光純薬工業製
トリアリルイソシアヌレート：ＴＡＩＣ（日本化成製）
水添スチレン系熱可塑性エラストマー：タフテックＨ１０４１（旭化成製）
シリカ：球状シリカ（龍森製）
デカブロモジフェニルエタン：ＳＡＹＴＥＸ８０１０（アルベマールジャパン製）
α，α’−ビス（ｔ−ブチルパーオキシ−ｍ−イソプロピル）ベンゼン：パーブチルＰ（日油製）
クレゾール・ノボラック骨格フェノール樹脂：郡栄化学工業社製 グレード：レヂトップＰＳＭ−４２６１
２，６−キシレノール：東京化成工業製
ｔ−ブチルパーオキシイソプロピルカーボネート：Ｐｅｒｂｕｔｙｌ Ｉ（日油製）
The raw materials used in Examples, Comparative Examples and Production Examples are shown below.
Polyphenylene ether: S202A (manufactured by Asahi Kasei Chemicals, number average molecular weight 19,000, average number of phenolic hydroxyl groups per molecule 1.84)
Low molecular weight / methacrylic polyphenylene ether: MX9000 (manufactured by SABIC, number average molecular weight 1,100, average phenolic hydroxyl group number 0.04 per molecule)
Bisphenol A: Tokyo Chemical Industry Co., Ltd. 6 mass% cobalt naphthenate mineral spirit solution: Wako Pure Chemical Industries, Ltd. Benzoyl peroxide solution: Niper BMT K-40 (manufactured by NOF, 40 mass% xylene solution of benzoyl peroxide)
Tetrabutylammonium iodide: Wako Pure Chemical Industries, Ltd. Benzyl Chloride: Tokyo Kasei Kogyo Co., Ltd. Chloromethylstyrene: Wako Pure Chemical Industries, Ltd. Triallyl Isocyanurate: TAIC (Nippon Kasei)
Hydrogenated styrene thermoplastic elastomer: Tuftec H1041 (Asahi Kasei)
Silica: Spherical silica (manufactured by Tatsumori)
Decabromodiphenylethane: SAYTEX8010 (manufactured by Albemarle Japan)
α, α'-bis (t-butylperoxy-m-isopropyl) benzene: perbutyl P (manufactured by NOF Corporation)
Cresol / novolak skeleton phenolic resin: manufactured by Gunei Chemical Industry Co., Ltd. Grade: Resitop PSM-4261
2,6-xylenol: manufactured by Tokyo Chemical Industry Co., Ltd. t-butyl peroxyisopropyl carbonate: Perbutyl I (manufactured by NOF Corporation)
＜製造例１：低分子量・ポリフェニレンエーテル＞
９０℃に加温されたオイルバスに１０Ｌのフラスコを設置し、フラスコ内部に毎分３０ｍｌで窒素ガスを導入した。以降、操作は常に窒素ガス気流下で行った。ここにポリフェニレンエーテル１ｋｇ、及びトルエン３ｋｇを入れ、攪拌溶解させた。更に８０ｇのビスフェノールＡをメタノール３５０ｇに溶かした溶液を上記フラスコに攪拌しながら加えた。５分間攪拌を続けた後、６質量％ナフテン酸コバルトミネラルスピリット溶液３ｍｌを注射器で加え、５分間攪拌を続けた。続いてベンゾイルパーオキサイド溶液３７５ｇにトルエン１１２５ｇを加えて、ベンゾイルパーオキサイド濃度が１０質量％になるように希釈した溶液を滴下ロートに入れ、上記フラスコに２時間かけて滴下していった。滴下終了後、更に２時間加熱及び攪拌を続け、低分子量化ポリフェニレンエーテルを得た。得られた低分子量化ポリフェニレンエーテルの数平均分子量は２，８００であり、１分子当たりの平均フェノール性水酸基数は１．９６個であった。
<Production Example 1: Low molecular weight polyphenylene ether>
A 10 L flask was placed in an oil bath heated to 90 ° C., and nitrogen gas was introduced into the flask at a rate of 30 ml per minute. Thereafter, the operation was always performed under a nitrogen gas stream. 1 kg of polyphenylene ether and 3 kg of toluene were added and dissolved by stirring. Further, a solution obtained by dissolving 80 g of bisphenol A in 350 g of methanol was added to the flask with stirring. After stirring for 5 minutes, 3 ml of 6 mass% cobalt naphthenate mineral spirit solution was added with a syringe, and stirring was continued for 5 minutes. Subsequently, 1125 g of toluene was added to 375 g of the benzoyl peroxide solution, and a solution diluted so that the benzoyl peroxide concentration was 10% by mass was placed in a dropping funnel and dropped into the flask over 2 hours. After completion of the dropwise addition, the mixture was further heated and stirred for 2 hours to obtain a low molecular weight polyphenylene ether. The number average molecular weight of the obtained low molecular weight polyphenylene ether was 2,800, and the average number of phenolic hydroxyl groups per molecule was 1.96.
＜製造例２：低分子量・ベンジル化ポリフェニレンエーテル−１＞
製造例１と同様の方法で、メタノールを添加してポリフェニレンエーテルを沈殿させる前の工程まで行い、低分子量・ポリフェニレンエーテルを含む反応液を得た。該反応液の温度を５０℃に下げ、水酸化ナトリウム３４０ｇをイオン交換水３０５０ｇに溶解させた水溶液とテトラブチルアンモニウムヨード３１ｇとを加えて、５分間撹拌した。続いて、塩化ベンジル１０７０ｇを加えてから温度５０℃で４時間撹拌を続け、低分子量・ベンジル化ポリフェニレンエーテルを含む反応液を得た。これに多量のメタノールを加え、低分子量・ベンジル化ポリフェニレネーテルを沈殿させ、ろ別後、乾燥させて低分子量・ベンジル化ポリフェニレンエーテル−１を得た。
得られた低分子量・ベンジル化ポリフェニレンエーテル−１の数平均分子量は３，０００、１分子当たりの平均フェノール性水酸基数は０．０１個であった。
<Production Example 2: Low molecular weight / benzylated polyphenylene ether-1>
The same process as in Production Example 1 was carried out up to the step before methanol was added to precipitate polyphenylene ether to obtain a reaction solution containing low molecular weight polyphenylene ether. The temperature of the reaction solution was lowered to 50 ° C., an aqueous solution in which 340 g of sodium hydroxide was dissolved in 3050 g of ion-exchanged water and 31 g of tetrabutylammonium iodide were added and stirred for 5 minutes. Subsequently, after adding 1070 g of benzyl chloride, stirring was continued for 4 hours at a temperature of 50 ° C. to obtain a reaction solution containing a low molecular weight / benzylated polyphenylene ether. A large amount of methanol was added thereto to precipitate a low molecular weight / benzylated polyphenylene ether, which was filtered and dried to obtain a low molecular weight / benzylated polyphenylene ether-1.
The number average molecular weight of the obtained low molecular weight / benzylated polyphenylene ether-1 was 3,000, and the average number of phenolic hydroxyl groups per molecule was 0.01.
＜製造例３：低分子量・ベンジル化ポリフェニレンエーテル−２＞
ビスフェノールＡを１００ｇ、ビスフェノールＡを溶解させるメタノールを４４０ｇとし、さらにベンゾイルパーオキサイド溶液を４２５ｇとする以外は製造例１と同様にして低分子量・ポリフェニレンエーテルを製造し、該低分子量・ポリフェニレンエーテルを用いて製造例２と同様の方法で低分子量・ベンジル化ポリフェニレンエーテル−２を得た。
得られた低分子量・ベンジル化ポリフェニレンエーテル−２の数平均分子量は２，４００、１分子当たりの平均フェノール性水酸基数は０．０２個であった。
<Production Example 3: Low molecular weight / benzylated polyphenylene ether-2>
A low molecular weight polyphenylene ether was produced in the same manner as in Production Example 1 except that 100 g of bisphenol A, 440 g of methanol for dissolving bisphenol A, and 425 g of benzoyl peroxide solution were used. In the same manner as in Production Example 2, low molecular weight and benzylated polyphenylene ether-2 was obtained.
The number average molecular weight of the obtained low molecular weight / benzylated polyphenylene ether-2 was 2,400, and the average number of phenolic hydroxyl groups per molecule was 0.02.
＜製造例４：低分子量・ベンジル化ポリフェニレンエーテル−３＞
ビスフェノールＡを１３０ｇ、ビスフェノールＡを溶解させるメタノールを５７０ｇとし、さらにベンゾイルパーオキサイド溶液を４７５ｇとする以外は製造例１と同様にして低分子量・ポリフェニレンエーテルを製造し、該低分子量・ポリフェニレンエーテルを用いて製造例２と同様の方法で低分子量・ベンジル化ポリフェニレンエーテル−２を得た。
得られた低分子量・ベンジル化ポリフェニレンエーテルの数平均分子量は１，５００、１分子当たりの平均フェノール性水酸基数は０．０４個であった。
<Production Example 4: Low molecular weight / benzylated polyphenylene ether-3>
A low molecular weight polyphenylene ether is produced in the same manner as in Production Example 1 except that 130 g of bisphenol A, 570 g of methanol in which bisphenol A is dissolved, and 475 g of benzoyl peroxide solution are used, and the low molecular weight polyphenylene ether is used. In the same manner as in Production Example 2, low molecular weight and benzylated polyphenylene ether-2 was obtained.
The number average molecular weight of the obtained low molecular weight / benzylated polyphenylene ether was 1,500, and the average number of phenolic hydroxyl groups per molecule was 0.04.
＜製造例５：低分子量・ビニルベンジル化ポリフェニレンエーテル＞
塩化ベンジル１０７０ｇをクロロメチルスチレン１２９０ｇに変更する以外は製造例２と同様の方法で、低分子量・ビニルベンジル化ポリフェニレンエーテルを得た。
得られた低分子量・ビニルベンジル化ポリフェニレンエーテルの数平均分子量は３，１００、１分子当たりの平均フェノール性水酸基数は０．０５個であった。
<Production Example 5: Low molecular weight vinylbenzylated polyphenylene ether>
A low molecular weight vinylbenzylated polyphenylene ether was obtained in the same manner as in Production Example 2, except that 1070 g of benzyl chloride was changed to 1290 g of chloromethylstyrene.
The number average molecular weight of the obtained low molecular weight / vinylbenzylated polyphenylene ether was 3,100, and the average number of phenolic hydroxyl groups per molecule was 0.05.
＜実施例１〜６、比較例１〜８＞
表１に示す樹脂組成のワニスをトルエンを用いて混合し、ワニスを調製した。上記ワニスをガラスクロス（旭シュエーベル株式会社製、商品名「２１１６」）に含浸させ、乾燥することにより樹脂含有量６０質量％のプリプレグを得た。このプリプレグを用いて、前述の方法で硬化時樹脂フロー量を測定した。
<Examples 1-6, Comparative Examples 1-8>
The varnish of the resin composition shown in Table 1 was mixed using toluene to prepare a varnish. The varnish was impregnated in a glass cloth (trade name “2116”, manufactured by Asahi Sebel Co., Ltd.) and dried to obtain a prepreg having a resin content of 60% by mass. Using this prepreg, the amount of resin flow during curing was measured by the method described above.
また、上記得られたプリプレグを２枚重ね、その上下に厚み１２μｍの銅箔（ＧＴＳ−ＭＰ箔、古川電気工業株式会社製）を重ね合わせたものを、室温から昇温速度３℃／分で加熱しながら圧力５ｋｇ／ｃｍ2の条件で真空プレスを行い、１３０℃まで達したら昇温速度３℃／分で加熱しながら圧力３０ｋｇ／ｃｍ2の条件で真空プレスを行い、２００℃まで達したら温度を２００℃に保ったまま圧力３０ｋｇ／ｃｍ2、時間６０分間の条件で真空プレスを行うことによって両面銅張積層板を得た。次いで、該銅張積層板を１００ｍｍ角に切り出し、銅箔をエッチングにて除去し、ガラス転移温度、異物検査、吸水率、及び吸水試験後のはんだ耐熱性を評価するための試料を得た。 In addition, two prepregs obtained as described above were stacked, and a copper foil having a thickness of 12 μm (GTS-MP foil, manufactured by Furukawa Electric Co., Ltd.) was stacked on the top and bottom at a temperature rising rate of 3 ° C./min from room temperature. Perform vacuum pressing under heating at a pressure of 5 kg / cm 2 , and when reaching 130 ° C, perform vacuum pressing under a pressure of 30 kg / cm 2 while heating at a heating rate of 3 ° C / min. A double-sided copper-clad laminate was obtained by performing vacuum pressing under the conditions of a pressure of 30 kg / cm 2 and a time of 60 minutes while maintaining the temperature at 200 ° C. Next, the copper clad laminate was cut into a 100 mm square, and the copper foil was removed by etching to obtain a sample for evaluating the glass transition temperature, foreign matter inspection, water absorption rate, and solder heat resistance after the water absorption test.
また、上記で得られたプリプレグを２枚重ね、その上下に厚み３５μｍの銅箔（ＧＴＳ−ＭＰ箔、古川電気工業株式会社製）を重ね合わせたものを、室温から昇温速度３℃／分で加熱しながら圧力５ｋｇ／ｃｍ2の条件で真空プレスを行い、１３０℃まで達したら昇温速度３℃／分で加熱しながら圧力３０ｋｇ／ｃｍ2の条件で真空プレスを行い、２００℃まで達したら温度を２００℃に保ったまま圧力３０ｋｇ／ｃｍ2、時間６０分間の条件で真空プレスを行うことによって両面銅張積層板を作製した。この両面銅張積層板を銅箔剥離強度測定用の試料として用いた。 In addition, two prepregs obtained as described above are stacked, and a copper foil having a thickness of 35 μm (GTS-MP foil, manufactured by Furukawa Electric Co., Ltd.) is stacked on the top and bottom of the prepreg. Vacuum pressing under the condition of pressure 5 kg / cm 2 while heating at 130 ° C, and when reaching 130 ° C, vacuum pressing is performed under the condition of pressure 30 kg / cm 2 while heating at a heating rate of 3 ° C / min, reaching 200 ° C. Then, a double-sided copper-clad laminate was produced by performing vacuum pressing under the conditions of a pressure of 30 kg / cm 2 and a time of 60 minutes while maintaining the temperature at 200 ° C. This double-sided copper-clad laminate was used as a sample for measuring the copper foil peel strength.
また、上記で得られたプリプレグを１６枚重ね、室温から昇温速度３℃／分で加熱しながら圧力５ｋｇ／ｃｍ2の条件で真空プレスを行い、１３０℃まで達したら昇温速度３℃／分で加熱しながら圧力３０ｋｇ／ｃｍ2の条件で真空プレスを行い、２００℃まで達したら温度を２００℃に保ったまま圧力３０ｋｇ／ｃｍ2、時間６０分間の条件で真空プレスを行うことによって積層板を作製した。該積層板を、１００ｍｍ角に切り出し、誘電率及び誘電正接の測定用試料とした。 Also, 16 prepregs obtained as described above were stacked and vacuum-pressed under the condition of a pressure of 5 kg / cm 2 while heating from room temperature at a heating rate of 3 ° C./min. Stacking is performed by performing vacuum pressing under the condition of a pressure of 30 kg / cm 2 while heating in minutes, and when the pressure reaches 200 ° C., the pressure is maintained at a pressure of 30 kg / cm 2 for 60 minutes while maintaining the temperature at 200 ° C. A plate was made. The laminate was cut into a 100 mm square and used as a sample for measuring dielectric constant and dielectric loss tangent.
上記のように、プリプレグ、両面銅張積層板（銅箔：１２μｍ及び３５μｍの２種）、又は積層板を用い、ガラス転移温度、硬化時の樹脂フロー量、銅箔剥離強度、誘電率、誘電正接、吸水率、及び吸水後のはんだ耐熱性を測定し、表１に示した。 As mentioned above, using prepreg, double-sided copper-clad laminate (copper foil: 12 μm and 35 μm), or laminate, glass transition temperature, amount of resin flow during curing, copper foil peel strength, dielectric constant, dielectric The tangent, water absorption, and solder heat resistance after water absorption were measured and shown in Table 1.
表１に示されるように、実施例１〜６においては、いずれも樹脂フロー量が０．３％以上と大きく、誘電正接が０．００５以下と小さく、ガラス転移温度も１７０℃以上と高い。実施例１〜６の積層板は、銅箔剥離強度が高く、耐吸水性が良好で、更にはんだ耐熱性にも優れるものであった。また、実施例１〜６においては、プリプレグについて、白色度が８５％以上、ｂ*値が９以下であり、白い基板を形成できた。 As shown in Table 1, in Examples 1 to 6, the resin flow amount is as large as 0.3% or more, the dielectric loss tangent is as small as 0.005 or less, and the glass transition temperature is as high as 170 ° C. or more. The laminates of Examples 1 to 6 had high copper foil peel strength, good water absorption resistance, and excellent solder heat resistance. Moreover, in Examples 1-6, about the prepreg, the whiteness was 85% or more, b * value was 9 or less, and the white board | substrate was able to be formed.
一方、比較例１〜８は、樹脂フロー量、誘電正接、ガラス転移温度、銅箔剥離強度、耐吸水性、及びはんだ耐熱性の少なくとも何れかが劣るものであった。末端を官能化していないポリフェニレンエーテルと、多い量の低分子量・ベンジル化ポリフェニレンエーテルとの混合物を用いた比較例１及び2に関し、比較例１においては、白色度が低く、ｂ*値が高かった。また比較例２においては、白色度が低かった。未官能化ポリフェニレンエーテルを用いた比較例３及び４に関し、比較例３においては、ガラス転移温度が低く、誘電正接が高く、耐熱性が悪かった。また比較例４においては成形性が悪く、積層板にかすれが生じてしまった。この例では、評価に十分耐える積層板が得られなかったため、他の項目は評価できなかった。未官能化ポリフェニレンエーテルを用い、トリアシルイソシアヌレートを多く用いた比較例５においては、誘電正接が高く、銅箔剥離強度が小さかった。未官能化ポリフェニレンエーテルと低分子量・ベンジル化ポリフェニレンエーテルとを５０：５０（質量比）の割合で混合した比較例６においては、ガラス転移温度が低く、銅箔剥離強度及びはんだ耐熱性が悪く、白色度が低く、ｂ*値が高かった。未官能化ポリフェニレンエーテルと低分子量・ビニルベンジル化ポリフェニレンエーテルとを、４６：５４（質量比）の混合比で用いた比較例７においては、銅箔剥離強度が低く、はんだ耐熱性が悪く、白色度が低く、ｂ*値が高かった。低分子量・ビニルベンジル化ポリフェニレンエーテルを用いた比較例８においては、銅箔剥離強度が小さく、はんだ耐熱性が悪く、白色度が低く、ｂ*値が高かった。また、特に比較例６〜８においては、白色度が低く、ｂ*値が高く、黄色味が強い基板であった。これら比較例６〜８の基板は、異物検査の結果にバラツキが多く、異物量の正確な計測性に欠けるものであった。 On the other hand, Comparative Examples 1 to 8 were inferior in at least one of resin flow amount, dielectric loss tangent, glass transition temperature, copper foil peel strength, water absorption resistance, and solder heat resistance. Regarding Comparative Examples 1 and 2 using a mixture of polyphenylene ether having no terminal functionalization and a large amount of low molecular weight / benzylated polyphenylene ether, Comparative Example 1 had low whiteness and high b * value. . In Comparative Example 2, the whiteness was low. Regarding Comparative Examples 3 and 4 using unfunctionalized polyphenylene ether, Comparative Example 3 had a low glass transition temperature, a high dielectric loss tangent, and poor heat resistance. Moreover, in the comparative example 4, the moldability was bad and the laminated board was faint. In this example, since a laminated board that can sufficiently withstand the evaluation could not be obtained, other items could not be evaluated. In Comparative Example 5 using unfunctionalized polyphenylene ether and using a large amount of triacyl isocyanurate, the dielectric loss tangent was high and the copper foil peel strength was low. In Comparative Example 6 in which unfunctionalized polyphenylene ether and low molecular weight / benzylated polyphenylene ether were mixed at a ratio of 50:50 (mass ratio), the glass transition temperature was low, the copper foil peel strength and the solder heat resistance were poor, Whiteness was low and b * value was high. In Comparative Example 7 where unfunctionalized polyphenylene ether and low molecular weight / vinylbenzylated polyphenylene ether were used in a mixing ratio of 46:54 (mass ratio), the copper foil peel strength was low, the solder heat resistance was poor, and white The degree was low and the b * value was high. In Comparative Example 8 using a low molecular weight vinylbenzylated polyphenylene ether, the copper foil peel strength was low, the solder heat resistance was poor, the whiteness was low, and the b * value was high. In particular, Comparative Examples 6 to 8 were substrates having low whiteness, high b * values, and strong yellowness. The substrates of Comparative Examples 6 to 8 had a large variation in the results of foreign matter inspection, and lacked accurate measurement of the amount of foreign matter.
本発明の態様の例を上記したが、本発明はこれらの態様に限定されず、特許請求の範囲の精神及び範囲の中で種々の改変が可能であることが理解されよう。 While examples of aspects of the invention have been described above, it will be understood that the invention is not limited to these aspects and that various modifications are possible within the spirit and scope of the appended claims.
Claims (8)
前記ポリフェニレンエーテル１分子当たりの平均フェノール性水酸基数が０．３個以上であり、
前記ポリフェニレンエーテルが、数平均分子量が８，０００を超えるポリフェニレンエーテル成分を、ポリフェニレンエーテル全量に対して７５質量％以上の量で含み、
前記硬化性樹脂組成物の下記条件で測定される硬化時樹脂フロー量が０．３％以上１５％以下であり、
前記硬化性樹脂組成物から下記条件で作製された誘電正接測定用試料が、１ＧＨｚでの誘電正接：０．００５以下を有し、
前記硬化性樹脂組成物から下記条件で作製されたガラス転移温度測定用試料が、ガラス転移温度：１７０℃以上を有し、
前記硬化性樹脂組成物から下記条件で作製された白色度測定用試料が、L*ａ*ｂ*表色系での白色度：８５以上、及びｂ*値：９以下を有し、
前記硬化時樹脂フロー量は、前記硬化性樹脂組成物が樹脂含量６０±２質量％となるよう、ＩＰＣ Ｓｔｙｌｅ ２１１６規格ガラスクロスに含浸されてなる１５０ｍｍ角のプリプレグを２枚重ねて積層板前駆体を得て、前記積層板前駆体を下記条件（ａ）にて成形し、流れ出した樹脂部を取り除いて積層板を作製したときにおける、前記積層板の質量（ｇ）、及び前記積層板前駆体の質量（ｇ）から、下記式：
硬化時樹脂フロー量（％）＝（積層板前駆体の質量（ｇ）−積層板の質量（ｇ））／積層板前駆体の質量（ｇ）×１００
に従って算出される値であり、
前記誘電正接測定用試料は、前記硬化性樹脂組成物が樹脂含量６０±２質量％となるようＩＰＣ Ｓｔｙｌｅ ２１１６規格ガラスクロスに含浸されてなるプリプレグを１６枚重ね、下記条件（ａ）にて成形されており、
前記ガラス転移温度測定用試料は、前記硬化性樹脂組成物が樹脂含量６０±２質量％となるようＩＰＣ Ｓｔｙｌｅ ２１１６規格ガラスクロスに含浸されてなるプリプレグを２枚重ね、下記条件（ａ）にて成形されており、
前記白色度測定用試料は、前記硬化性樹脂組成物が樹脂含量６０±２質量％となるようＩＰＣ Ｓｔｙｌｅ ２１１６規格ガラスクロスに含浸されてなるプリプレグである、
硬化性樹脂組成物。
条件（ａ）
室温から昇温速度３℃／分で加熱しながら圧力５ｋｇ／ｃｍ2の条件で真空プレスを行い、１３０℃まで達したら昇温速度３℃／分で加熱しながら圧力３０ｋｇ／ｃｍ2の条件で真空プレスを行い、２００℃まで達したら温度を２００℃に保ったまま圧力３０ｋｇ／ｃｍ2、時間６０分間の条件で真空プレスを行う。 A curable resin composition containing polyphenylene ether,
The average number of phenolic hydroxyl groups per molecule of the polyphenylene ether is 0.3 or more,
The polyphenylene ether contains a polyphenylene ether component having a number average molecular weight exceeding 8,000 in an amount of 75% by mass or more based on the total amount of the polyphenylene ether,
The resin flow amount during curing measured under the following conditions of the curable resin composition is 0.3% or more and 15% or less,
A dielectric loss tangent measurement sample prepared from the curable resin composition under the following conditions has a dielectric loss tangent at 1 GHz: 0.005 or less,
The glass transition temperature measurement sample prepared from the curable resin composition under the following conditions has a glass transition temperature: 170 ° C. or higher,
The whiteness measurement sample produced from the curable resin composition under the following conditions has a whiteness in the L * a * b * color system: 85 or more, and a b * value: 9 or less,
The amount of resin flow at the time of curing is a laminate precursor obtained by stacking two 150 mm square prepregs impregnated with IPC Style 2116 standard glass cloth so that the curable resin composition has a resin content of 60 ± 2% by mass. The laminate precursor was molded under the following conditions (a), and the flowed resin part was removed to produce a laminate, and the laminate precursor (g) and the laminate precursor. From the mass (g) of the following formula:
Resin flow rate during curing (%) = (mass of laminate precursor (g) −mass of laminate (g)) / mass of laminate precursor (g) × 100
Is calculated according to
The dielectric loss tangent measurement sample was formed by stacking 16 prepregs impregnated with IPC Style 2116 standard glass cloth so that the curable resin composition had a resin content of 60 ± 2% by mass, and molded under the following conditions (a): Has been
The sample for measuring the glass transition temperature is formed by stacking two prepregs impregnated with IPC Style 2116 standard glass cloth so that the curable resin composition has a resin content of 60 ± 2% by mass, and the following conditions (a) Molded,
The whiteness measurement sample is a prepreg impregnated with an IPC Style 2116 standard glass cloth so that the curable resin composition has a resin content of 60 ± 2% by mass.
Curable resin composition.
Condition (a)
Vacuum pressing is performed from room temperature at a heating rate of 3 ° C./min and a pressure of 5 kg / cm 2. When reaching 130 ° C., heating is performed at a heating rate of 3 ° C./min and a pressure of 30 kg / cm 2 . When the temperature reaches 200 ° C., the vacuum press is performed under the conditions of a pressure of 30 kg / cm 2 and a time of 60 minutes.
（Ａ−１）１分子当たりの平均フェノール性水酸基数が０．５個未満であり、かつ数平均分子量が１，０００以上８，０００以下であるポリフェニレンエーテル成分、及び
（Ａ−２）前記数平均分子量が８，０００を超えるポリフェニレンエーテル成分、
を含み、前記（Ａ−１）と前記（Ａ−２）との合計質量１００質量％を基準として、前記（Ａ−１）の含有量が１質量％以上２５質量％以下であり、かつ前記（Ａ−２）の含有量が７５質量％以上９９質量％以下である、請求項１に記載の硬化性樹脂組成物。 The polyphenylene ether is
(A-1) a polyphenylene ether component having an average number of phenolic hydroxyl groups per molecule of less than 0.5 and a number average molecular weight of 1,000 to 8,000, and (A-2) the number A polyphenylene ether component having an average molecular weight exceeding 8,000,
The content of (A-1) is 1% by mass or more and 25% by mass or less based on the total mass of 100% by mass of (A-1) and (A-2), and The curable resin composition of Claim 1 whose content of (A-2) is 75 mass% or more and 99 mass% or less.