JP5938523B2 - Secondary battery electrode, manufacturing method thereof, secondary battery including the same, and cable-type secondary battery - Google Patents
Secondary battery electrode, manufacturing method thereof, secondary battery including the same, and cable-type secondary battery Download PDFInfo
- Publication number
- JP5938523B2 JP5938523B2 JP2015515974A JP2015515974A JP5938523B2 JP 5938523 B2 JP5938523 B2 JP 5938523B2 JP 2015515974 A JP2015515974 A JP 2015515974A JP 2015515974 A JP2015515974 A JP 2015515974A JP 5938523 B2 JP5938523 B2 JP 5938523B2
- Authority
- JP
- Japan
- Prior art keywords
- electrode
- secondary battery
- layer
- cable
- battery according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、二次電池用電極、その製造方法、それを含む二次電池及びケーブル型二次電池に関し、より詳しくは、電極活物質層の脱離現象を防止し、電極の柔軟性を向上させた二次電池用電極、その製造方法、それを含む二次電池及びケーブル型二次電池に関する。 The present invention relates to an electrode for a secondary battery, a method for manufacturing the same, a secondary battery including the same, and a cable-type secondary battery. More specifically, the electrode active material layer is prevented from being detached and the flexibility of the electrode is improved. The present invention relates to an electrode for a secondary battery, a manufacturing method thereof, a secondary battery including the electrode, and a cable-type secondary battery.
本出願は、２０１３年５月７日出願の韓国特許出願第１０−２０１３−００５１５６５号、及び２０１４年５月７日出願の韓国特許出願第１０−２０１４−００５４２７９号に基づく優先権を主張し、該当出願の明細書及び図面に開示された内容は、すべて本出願に援用される。 This application claims priority based on Korean Patent Application No. 10-2013-0051565 filed on May 7, 2013 and Korean Patent Application No. 10-2014-0054279 filed on May 7, 2014, All the contents disclosed in the specification and drawings of the corresponding application are incorporated in the present application.
二次電池は、外部の電気エネルギーを化学エネルギーの形態に変換して貯蔵しておき、必要なときに電気を作る装置であり、充電を繰り返すことができるという意味で「充電式電池（ｒｅｃｈａｒｇｅａｂｌｅ ｂａｔｔｅｒｙ）」とも呼ばれる。広く使用される二次電池としては、鉛蓄電池、ニッケル‐カドミウム電池（ＮｉＣｄ）、ニッケル水素蓄電池（ＮｉＭＨ）、リチウムイオン電池（Ｌｉ‐ｉｏｎ）、リチウムイオンポリマー電池（Ｌｉ‐ｉｏｎ ｐｏｌｙｍｅｒ）がある。二次電池は使い捨ての一次電池に比べて経済的な利点と環境的な利点を共に提供する。 A secondary battery is a device that converts external electrical energy into a form of chemical energy, stores it, and produces electricity when needed. In the sense that rechargeable battery (rechargeable battery) can be repeated. ) ". Widely used secondary batteries include lead acid batteries, nickel-cadmium batteries (NiCd), nickel metal hydride batteries (NiMH), lithium ion batteries (Li-ion), and lithium ion polymer batteries (Li-ion polymer). Secondary batteries offer both economic and environmental advantages over disposable primary batteries.
現在、二次電池は低い電力を要する所に使用されている。例えば、自動車の始動を補助する機器、携帯用装置、道具、無停電電源装置が挙げられる。近年の無線通信技術の発展は携帯用装置の大衆化を主導しており、従来の多くの装置が無線化される傾向もあるため、二次電池に対する需要が爆発的に伸びている。また、環境汚染防止の面でハイブリッド自動車、電気自動車が実用化されているが、これら次世代自動車は二次電池を使用することで、コストと重量を下げ、寿命を伸ばす技術を採用している。 Currently, secondary batteries are used where low power is required. For example, a device that assists in starting an automobile, a portable device, a tool, and an uninterruptible power supply device may be used. The development of wireless communication technology in recent years has led to the popularization of portable devices, and many conventional devices tend to be wireless, so the demand for secondary batteries has been explosively growing. In addition, hybrid vehicles and electric vehicles have been put into practical use in terms of preventing environmental pollution, but these next-generation vehicles use technology that lowers cost and weight and extends life by using secondary batteries. .
一般に、二次電池は円筒型、角形、またはパウチ型の電池が殆どである。二次電池が、負極、正極及び分離膜で構成された電極組立体を円筒型または角形の金属缶またはアルミニウムラミネートシートのパウチ型ケースの内部に収納し、前記電極組立体に電解質を注入して製造されるためである。したがって、このような二次電池の装着には一定空間が必要となるため、二次電池の円筒型、角形、またはパウチ型の形態は多様な形態の携帯用装置の開発に制約となる。そこで、形態の変形が自在な新たな形態の二次電池が求められている。 In general, most of secondary batteries are cylindrical, square, or pouch type batteries. A secondary battery stores an electrode assembly composed of a negative electrode, a positive electrode, and a separation membrane in a cylindrical or square metal can or an aluminum laminated sheet pouch-type case, and an electrolyte is injected into the electrode assembly. This is because it is manufactured. Accordingly, since a certain space is required for mounting such a secondary battery, the cylindrical, square, or pouch-shaped form of the secondary battery is a restriction on the development of various types of portable devices. Therefore, there is a need for a new form of secondary battery that can be freely deformed.
このような要求に応えて、断面の直径に対する長さの比が非常に大きい電池である線型電池が提案された。このようなケーブル型二次電池は、形態の変形に伴う外力によるストレス、または、充放電時の電極活物質層の急激な体積膨張などによって電極活物質層が脱離し、容量減少及びサイクル寿命特性の劣化現象が発生する恐れがある。 In response to such a demand, a linear battery, which is a battery having a very large ratio of length to cross-sectional diameter, has been proposed. Such a cable type secondary battery has a reduced capacity and cycle life characteristics due to the electrode active material layer detaching due to stress due to external force accompanying deformation of the shape, or rapid volume expansion of the electrode active material layer during charge / discharge. There is a risk of deterioration.
このような問題点を解決するため、電極活物質層に含まれるバインダーの含量を増加させれば、曲げやねじれに対する柔軟性は有し得るものの、電極活物質層のバインダー含量の増加は電極抵抗を増加させ、電池性能低下の原因になる。また、電極が完全に折れるなどの過酷な外力が作用すれば、バインダーの含量を増加させても電極活物質層の脱離は防止できず、適切な解決方法になれない。 In order to solve such problems, if the binder content in the electrode active material layer is increased, flexibility in bending and twisting can be obtained, but an increase in the binder content of the electrode active material layer is an electrode resistance. Increases the battery performance. Further, if a severe external force such as the electrode is completely broken acts, even if the binder content is increased, the electrode active material layer cannot be prevented from being detached, and an appropriate solution cannot be obtained.
本発明は、上記問題点に鑑みてなされたものであり、電極活物質層に外力が作用しても電極活物質層にクラック（ｃｒａｃｋ）が発生することを緩和し、酷いクラックが発生しても集電体から脱離することを防止できる二次電池用電極、その製造方法、それを含む二次電池及びケーブル型二次電池を提供することを目的とする。 The present invention has been made in view of the above problems, and even if an external force is applied to the electrode active material layer, the generation of cracks in the electrode active material layer is alleviated, and severe cracks are generated. Another object of the present invention is to provide an electrode for a secondary battery, a method for producing the same, a secondary battery including the same, and a cable-type secondary battery that can be prevented from being detached from the current collector.
上記の課題を達成するため、本発明の一態様によれば、集電体；前記集電体の一面に形成された電極活物質層；前記電極活物質層上に形成され、無機物粒子及びバインダー高分子を含む有無機多孔性層；及び前記有無機多孔性層上に形成された多孔性の第１支持層；を含むシート型二次電池用電極が提供される。 To achieve the above object, according to one embodiment of the present invention, a current collector; an electrode active material layer formed on one surface of the current collector; an inorganic particle and a binder formed on the electrode active material layer There is provided an electrode for a sheet type secondary battery comprising: an organic / inorganic porous layer containing a polymer; and a porous first support layer formed on the organic / inorganic porous layer.
このとき、前記集電体は、ステンレススチール、アルミニウム、ニッケル、チタン、焼成炭素または銅；カーボン、ニッケル、チタンまたは銀で表面処理されたステンレススチール；アルミニウム‐カドミウム合金；導電材で表面処理された非伝導性高分子；伝導性高分子；Ｎｉ、Ａｌ、Ａｕ、Ａｇ、Ｐｄ／Ａｇ、Ｃｒ、Ｔａ、Ｃｕ、ＢａまたはＩＴＯである金属粉末を含む金属ペースト；若しくは黒鉛、カーボンブラックまたは炭素ナノチューブである炭素粉末を含む炭素ペースト；から製造されたものであり得る。 At this time, the current collector was stainless steel, aluminum, nickel, titanium, calcined carbon or copper; stainless steel surface-treated with carbon, nickel, titanium or silver; aluminum-cadmium alloy; surface treated with a conductive material Non-conductive polymer; conductive polymer; metal paste containing metal powder that is Ni, Al, Au, Ag, Pd / Ag, Cr, Ta, Cu, Ba or ITO; or graphite, carbon black or carbon nanotube It can be made from a carbon paste containing a carbon powder.
また、前記集電体は、メッシュ型集電体であり得る。 The current collector may be a mesh type current collector.
また、前記集電体は、導電材及びバインダーから構成された下塗層をさらに含むことができる。 The current collector may further include an undercoat layer composed of a conductive material and a binder.
ここで、前記導電材は、カーボンブラック、アセチレンブラック、ケッチェンブラック、炭素繊維、炭素ナノチューブ及びグラフェン（ｇｒａｐｈｅｎｅ）からなる群より選択されるいずれか１つまたはこれらのうち２種以上の混合物を含むことができる。 Here, the conductive material includes any one selected from the group consisting of carbon black, acetylene black, ketjen black, carbon fiber, carbon nanotube, and graphene, or a mixture of two or more thereof. be able to.
また、前記バインダーは、ポリフッ化ビニリデン（ＰＶｄＦ）、フッ化ビニリデン‐ヘキサフルオロプロピレン共重合体（ＰＶｄＦ‐ｃｏ‐ＨＦＰ）、ポリフッ化ビニリデン‐co-トリクロロエチレン（ＰＶｄＦ‐ｃｏ‐ＴＣＥ）、ポリブチルアクリレート、ポリメチルメタクリレート（ＰＭＭＡ）、ポリアクリロニトリル（ＰＡＮ）、ポリビニルピロリドン、ポリビニルアセテート（ＰＶＡｃ）、エチレンビニルアセテート共重合体（ｐｏｌｙｅｔｈｙｌｅｎｅ‐ｃｏ‐ｖｉｎｙｌａｃｅｔａｔｅ）、ポリエチレンオキサイド（ＰＥＯ）、ポリアリレート、セルロースアセテート、セルロースアセテートブチレート、セルロースアセテートプロピオネート、シアノエチルプルラン、シアノエチルポリビニルアルコール、シアノエチルセルロース、シアノエチルスクロース、プルラン、カルボキシルメチルセルロース、スチレンブタジエンゴム、アクリロニトリルスチレンブタジエン共重合体（ａｃｒｙｌｏｎｉｔｒｉｌｅ‐ｓｔｙｒｅｎｅ‐ｂｕｔａｄｉｅｎｅ ｃｏｐｏｌｙｍｅｒ）及びポリイミドからなる群より選択されたいずれか１つまたはこれらのうち２種以上の混合物であり得る。 The binder may be polyvinylidene fluoride (PVdF), vinylidene fluoride-hexafluoropropylene copolymer (PVdF-co-HFP), polyvinylidene fluoride-co-trichloroethylene (PVdF-co-TCE), polybutyl acrylate, Polymethyl methacrylate (PMMA), polyacrylonitrile (PAN), polyvinyl pyrrolidone, polyvinyl acetate (PVAc), ethylene vinyl acetate copolymer (polyethylene-co-vinylate), polyethylene oxide (PEO), polyarylate, cellulose acetate, cellulose acetate Butyrate, cellulose acetate propionate, cyanoethyl pullulan, cyanoethyl polyvinyl alcohol, cyanoethyl cellulose , Cyanoethyl sucrose, pullulan, carboxymethyl cellulose, styrene butadiene rubber, acrylonitrile-styrene-butadiene copolymer, and a mixture of two or more of these selected from the group consisting of polyimides possible.
また、前記集電体の少なくとも一面に、複数の凹部を形成することができる。 A plurality of recesses can be formed on at least one surface of the current collector.
このとき、前記複数の凹部は、連続的なパターンを有するか、または、断続的なパターンを有し得る。 At this time, the plurality of recesses may have a continuous pattern or an intermittent pattern.
また、前記第１支持層は、メッシュ型多孔性膜または不織布であり得る。 The first support layer may be a mesh type porous membrane or a nonwoven fabric.
また、前記第１支持層は、高密度ポリエチレン、低密度ポリエチレン、線形低密度ポリエチレン、超高分子量ポリエチレン、ポリプロピレン、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエステル、ポリアセタール、ポリアミド、ポリカーボネート、ポリイミド、ポリエーテルエーテルケトン、ポリエーテルスルホン、ポリフェニレンオキサイド、ポリフェニレンスルフィド及びポリエチレンナフタレートからなる群より選択されたいずれか１つまたはこれらのうち２種以上の混合物から形成することができる。 The first support layer is made of high density polyethylene, low density polyethylene, linear low density polyethylene, ultra high molecular weight polyethylene, polypropylene, polyethylene terephthalate, polybutylene terephthalate, polyester, polyacetal, polyamide, polycarbonate, polyimide, polyether ether ketone. , Polyethersulfone, polyphenylene oxide, polyphenylene sulfide, and polyethylene naphthalate, and one or a mixture of two or more thereof.
また、前記第１支持層上に、導電材及びバインダーを備える導電材コーティング層をさらに形成することができる。 In addition, a conductive material coating layer including a conductive material and a binder can be further formed on the first support layer.
このとき、前記導電材コーティング層は、前記導電材と前記バインダーとを８０：２０ないし９９：１の重量比で混合したものであり得る。 In this case, the conductive material coating layer may be a mixture of the conductive material and the binder in a weight ratio of 80:20 to 99: 1.
また、前記導電材は、カーボンブラック、アセチレンブラック、ケッチェンブラック、炭素繊維、炭素ナノチューブ及びグラフェンからなる群より選択されるいずれか１つまたはこれらのうち２種以上の混合物を含むことができる。 The conductive material may include any one selected from the group consisting of carbon black, acetylene black, ketjen black, carbon fiber, carbon nanotube, and graphene, or a mixture of two or more thereof.
一方、前記有無機多孔性層は、前記無機物粒子と前記バインダー高分子とを２０：８０ないし９５：５の重量比で混合して形成したものであり得る。 On the other hand, the porous organic layer may be formed by mixing the inorganic particles and the binder polymer in a weight ratio of 20:80 to 95: 5.
また、前記有無機多孔性層に形成された孔の大きさが、０．０１μｍないし１０μｍであり、気孔度が５ないし９５％であり得る。 The pores formed in the porous organic layer may have a size of 0.01 μm to 10 μm and a porosity of 5 to 95%.
また、前記無機物粒子は、誘電率定数が５以上の無機物粒子、リチウムイオン伝達能力を有する無機物粒子、またはこれらの混合物であり得る。 The inorganic particles may be inorganic particles having a dielectric constant of 5 or more, inorganic particles having lithium ion transfer capability, or a mixture thereof.
このとき、前記誘電率定数が５以上の無機物粒子は、ＢａＴｉＯ3、Ｐｂ（Ｚｒx、Ｔｉ1-x）Ｏ3（ＰＺＴ、０＜ｘ＜１）、Ｐｂ1-xＬａxＺｒ1-yＴｉyＯ3（ＰＬＺＴ、０＜ｘ＜１、０＜ｙ＜１）、（１−ｘ）Ｐｂ（Ｍｇ1/3Ｎｂ2/3）Ｏ3-xＰｂＴｉＯ3（ＰＭＮ‐ＰＴ、０＜ｘ＜１）、ハフニア（ＨｆＯ2）、ＳｒＴｉＯ3、ＳｎＯ2、ＣｅＯ2、ＭｇＯ、ＮｉＯ、ＣａＯ、ＺｎＯ、ＺｒＯ2、Ｙ2Ｏ3、Ａｌ2Ｏ3、ＳｉＣ、ＳｉＯ2、ＡｌＯＯＨ、Ａｌ（ＯＨ）3及びＴｉＯ2からなる群より選択されたいずれか１つまたはこれらのうち２種以上の混合物であり得る。 At this time, the inorganic particles having a dielectric constant of 5 or more are BaTiO 3 , Pb (Zr x , Ti 1-x ) O 3 (PZT, 0 <x <1), Pb 1-x La x Zr 1-y. Ti y O 3 (PLZT, 0 <x <1, 0 <y <1), (1-x) Pb (Mg 1/3 Nb 2/3 ) O 3-x PbTiO 3 (PMN-PT, 0 <x <1), hafnia (HfO 2 ), SrTiO 3 , SnO 2 , CeO 2 , MgO, NiO, CaO, ZnO, ZrO 2 , Y 2 O 3 , Al 2 O 3 , SiC, SiO 2 , AlOOH, Al (OH ) Any one selected from the group consisting of 3 and TiO 2, or a mixture of two or more thereof.
また、前記リチウムイオン伝達能力を有する無機物粒子は、リチウムホスフェート（Ｌｉ3ＰＯ4）、リチウムチタンホスフェート（ＬｉxＴｉy（ＰＯ4）3、０＜ｘ＜２、０＜ｙ＜３）、リチウムアルミニウムチタンホスフェート（ＬｉxＡｌyＴｉz（ＰＯ4）3、０＜ｘ＜２、０＜ｙ＜１、０＜ｚ＜３）、（ＬｉＡｌＴｉＰ）xＯy系列ガラス（０＜ｘ＜４、０＜ｙ＜１３）、リチウムランタンチタネート（ＬｉxＬａyＴｉＯ3、０＜ｘ＜２、０＜ｙ＜３）、リチウムゲルマニウムチオホスフェート（ＬｉxＧｅyＰzＳw、０＜ｘ＜４、０＜ｙ＜１、０＜ｚ＜１、０＜ｗ＜５）、リチウムナイトライド（ＬｉxＮy、０＜ｘ＜４、０＜ｙ＜２）、ＳｉＳ2系列ガラス（ＬｉxＳｉyＳz、０＜ｘ＜３、０＜ｙ＜２、０＜ｚ＜４）及びＰ2Ｓ5系列ガラス（ＬｉxＰyＳz、０＜ｘ＜３、０＜ｙ＜３、０＜ｚ＜７）からなる群より選択されたいずれか１つまたはこれらのうち２種以上の混合物であり得る。 The inorganic particles having lithium ion transfer capability include lithium phosphate (Li 3 PO 4 ), lithium titanium phosphate (Li x Ti y (PO 4 ) 3 , 0 <x <2, 0 <y <3), lithium aluminum titanium phosphate (Li x Al y Ti z ( PO 4) 3, 0 <x <2,0 <y <1,0 <z <3), (LiAlTiP) x O y series glass (0 <x <4, 0 <y <13), lithium lanthanum titanate (Li x La y TiO 3 , 0 <x <2, 0 <y <3), lithium germanium thiophosphate (Li x Ge y P z S w , 0 <x <4 , 0 <y <1, 0 <z <1, 0 <w <5), lithium nitride (Li x N y , 0 <x <4, 0 <y <2), SiS 2 series glass (Li x Si y S z , 0 <x <3, 0 <y <2, 0 <z <4) and And P 2 S 5 series glass (Li x P y S z , 0 <x <3, 0 <y <3, 0 <z <7), or one or two of them It can be a mixture of the above.
また、前記無機物粒子の平均粒径は、１０ｎｍないし５μｍであり得る。 The average particle size of the inorganic particles may be 10 nm to 5 μm.
また、前記バインダー高分子は、ポリフッ化ビニリデン、フッ化ビニリデン‐ヘキサフルオロプロピレン共重合体、ポリフッ化ビニリデン‐co-トリクロロエチレン、ポリブチルアクリレート、ポリメチルメタクリレート、ポリアクリロニトリル、ポリビニルピロリドン、ポリビニルアセテート、エチレンビニルアセテート共重合体、ポリエチレンオキサイド、ポリアリレート、セルロースアセテート、セルロースアセテートブチレート、セルロースアセテートプロピオネート、シアノエチルプルラン、シアノエチルポリビニルアルコール、シアノエチルセルロース、シアノエチルスクロース、プルラン、カルボキシルメチルセルロース、スチレンブタジエンゴム、アクリロニトリルスチレンブタジエン共重合体及びポリイミドからなる群より選択されたいずれか１つまたはこれらのうち２種以上の混合物であり得る。 The binder polymer may be polyvinylidene fluoride, vinylidene fluoride-hexafluoropropylene copolymer, polyvinylidene fluoride-co-trichloroethylene, polybutyl acrylate, polymethyl methacrylate, polyacrylonitrile, polyvinyl pyrrolidone, polyvinyl acetate, ethylene vinyl. Acetate copolymer, polyethylene oxide, polyarylate, cellulose acetate, cellulose acetate butyrate, cellulose acetate propionate, cyanoethyl pullulan, cyanoethyl polyvinyl alcohol, cyanoethyl cellulose, cyanoethyl sucrose, pullulan, carboxymethyl cellulose, styrene butadiene rubber, acrylonitrile styrene butadiene From the group consisting of copolymers and polyimides Is-option may be either one or a mixture of two or more thereof.
一方、前記第１支持層上に、無機物粒子とバインダー高分子との混合物から形成された多孔性コーティング層をさらに含むことができる。 Meanwhile, a porous coating layer formed of a mixture of inorganic particles and a binder polymer may be further included on the first support layer.
また、前記集電体の他面に形成された第２支持層をさらに含むことができる。 In addition, it may further include a second support layer formed on the other surface of the current collector.
このとき、前記第２支持層は、高分子フィルムであり得、前記高分子フィルムは、ポリオレフィン、ポリエステル、ポリイミド及びポリアミドからなる群より選択されるいずれか１つまたはこれらのうち２種以上の混合物から形成することができる。 At this time, the second support layer may be a polymer film, and the polymer film is selected from the group consisting of polyolefin, polyester, polyimide, and polyamide, or a mixture of two or more thereof. Can be formed from
一方、前記二次電池用電極が負極である場合、前記電極活物質層は、天然黒鉛、人造黒鉛または炭素質材料；リチウム含有チタン複合酸化物（ＬＴＯ）；Ｓｉ、Ｓｎ、Ｌｉ、Ｚｎ、Ｍｇ、Ｃｄ、Ｃｅ、ＮｉまたはＦｅである金属類（Ｍｅ）；前記金属類（Ｍｅ）の合金類；前記金属類（Ｍｅ）の酸化物（ＭｅＯｘ）；及び前記金属類（Ｍｅ）と炭素との複合体からなる群より選択されたいずれか１つの活物質またはこれらのうち２種以上の混合物を含み、前記二次電池用電極が正極である場合、前記電極活物質層は、ＬｉＣｏＯ2、ＬｉＮｉＯ2、ＬｉＭｎ2Ｏ4、ＬｉＣｏＰＯ4、ＬｉＦｅＰＯ4、ＬｉＮｉＭｎＣｏＯ2、及びＬｉＮｉ1-x-y-zＣｏxＭ１yＭ２zＯ2（Ｍ１及びＭ２は互いに独立して、Ａｌ、Ｎｉ、Ｃｏ、Ｆｅ、Ｍｎ、Ｖ、Ｃｒ、Ｔｉ、Ｗ、Ｔａ、Ｍｇ及びＭｏからなる群より選択され、ｘ、ｙ及びｚは互いに独立した酸化物組成元素の原子分率であって、０≦ｘ＜０．５、０≦ｙ＜０．５、０≦ｚ＜０．５、ｘ＋ｙ＋ｚ≦１である）からなる群より選択されたいずれか１つの活物質またはこれらのうち２種以上の混合物を含むことができる。 On the other hand, when the electrode for a secondary battery is a negative electrode, the electrode active material layer includes natural graphite, artificial graphite or carbonaceous material; lithium-containing titanium composite oxide (LTO); Si, Sn, Li, Zn, Mg Metals (Me) which are Cd, Ce, Ni or Fe; Alloys of the metals (Me); Oxides of the metals (Me) (MeOx); and Metals (Me) and carbon When any one active material selected from the group consisting of a composite or a mixture of two or more thereof is included, and the secondary battery electrode is a positive electrode, the electrode active material layer includes LiCoO 2 , LiNiO 2 , LiMn 2 O 4 , LiCoPO 4 , LiFePO 4 , LiNiMnCoO 2 , and LiNi 1-xyz Co x M1 y M2 z O 2 (M1 and M2 are independently of each other, Al, Ni, Co, Fe, Mn, V , Selected from the group consisting of Cr, Ti, W, Ta, Mg, and Mo, and x, y, and z are atomic fractions of oxide composition elements independent of each other, and 0 ≦ x <0.5, 0 ≦ y Any one active material selected from the group consisting of <0.5, 0 ≦ z <0.5, and x + y + z ≦ 1) or a mixture of two or more thereof may be included.
一方、本発明の他の態様によれば、（Ｓ１）集電体の一面に、電極活物質スラリーを塗布し乾燥して電極活物質層を形成する工程；（Ｓ２）前記電極活物質層上に、無機物粒子及びバインダー高分子を含む有無機混合スラリーを塗布する工程；（Ｓ３）前記塗布された有無機混合スラリー上に多孔性の第１支持層を形成する工程；及び（Ｓ４）前記（Ｓ３）工程の結果物を圧着し、前記電極活物質層と前記第１支持層との間に接着して一体化した有無機多孔性層を形成する工程；を含むシート型二次電池用電極の製造方法が提供される。 On the other hand, according to another aspect of the present invention, (S1) a step of applying an electrode active material slurry to one surface of a current collector and drying to form an electrode active material layer; (S2) on the electrode active material layer (S3) forming a porous first support layer on the applied presence / absence-machine mixing slurry; and (S4) S3) A sheet-type secondary battery electrode comprising: a step of pressure bonding the resultant product and forming an integrated porous layer bonded and integrated between the electrode active material layer and the first support layer A manufacturing method is provided.
このとき、前記（Ｓ３）工程では、前記バインダー高分子が硬化する前に、前記塗布された有無機混合スラリー上に前記多孔性の第１支持層を形成することができる。 At this time, in the step (S3), before the binder polymer is cured, the porous first support layer can be formed on the coated presence / absence machine mixed slurry.
また、前記（Ｓ４）工程では、前記バインダー高分子が硬化する前に、前記（Ｓ３）工程の結果物をコーティングブレードにより圧着し、前記電極活物質層と前記第１支持層との間に接着して一体化した有無機多孔性層を形成することができる。 Further, in the step (S4), before the binder polymer is cured, the result of the step (S3) is pressure-bonded with a coating blade, and is bonded between the electrode active material layer and the first support layer. Thus, an integrated presence / absence porous layer can be formed.
また、前記（Ｓ１）工程の前又は前記（Ｓ４）工程の後、前記集電体の他面に、第２支持層を圧着して形成する工程をさらに含むことができる。 In addition, the method may further include a step of pressing and forming a second support layer on the other surface of the current collector before the step (S1) or after the step (S4).
また、本発明のさらに他の態様によれば、正極、負極、前記正極と前記負極との間に介在されたセパレータ、及び電解質を含む二次電池において、前記正極及び前記負極の少なくとも１つが本発明の二次電池用電極である二次電池が提供される。 According to still another aspect of the present invention, in a secondary battery including a positive electrode, a negative electrode, a separator interposed between the positive electrode and the negative electrode, and an electrolyte, at least one of the positive electrode and the negative electrode is a book. A secondary battery which is an electrode for a secondary battery of the invention is provided.
一方、本発明のさらに他の態様によれば、内部電極；前記内部電極の外面を囲んで形成され、電極の短絡を防止する分離層；及び前記分離層の外面を囲んで螺旋状に巻き取られて形成された外部電極；を含み、前記内部電極及び前記外部電極の１種以上が本発明の二次電池用電極で形成されるケーブル型二次電池が提供される。 On the other hand, according to still another aspect of the present invention, an internal electrode; a separation layer formed around the outer surface of the internal electrode and preventing a short circuit of the electrode; and a spiral winding around the outer surface of the separation layer A cable-type secondary battery in which at least one of the internal electrode and the external electrode is formed of the secondary battery electrode of the present invention.
このとき、前記外部電極は、一方向に延びたストリップ構造であり得る。 At this time, the external electrode may have a strip structure extending in one direction.
また、前記外部電極は、互いに重ならないように螺旋状に巻き取られて形成されるか、または、互いに重なるように螺旋状に巻き取られて形成され得る。 The external electrodes may be formed by being wound in a spiral shape so as not to overlap each other, or may be formed by being wound in a spiral shape so as to overlap each other.
また、前記内部電極は、内部に空間が形成された中空型構造であり得る。 The internal electrode may have a hollow structure in which a space is formed.
このとき、前記内部電極は、螺旋状に巻き取られた１つ以上の前記二次電池用電極を含むことができる。 In this case, the internal electrode may include one or more secondary battery electrodes wound in a spiral shape.
また、前記内部電極の内部に形成された空間に、内部電極集電体コア部、電解質を含むリチウムイオン供給コア部、または充填コア部を形成することができる。 In addition, an internal electrode current collector core part, a lithium ion supply core part including an electrolyte, or a filled core part can be formed in a space formed inside the internal electrode.
このとき、前記リチウムイオン供給コア部は、ゲル型ポリマー電解質及び支持体をさらに含むことができ、液体電解質及び多孔性担体をさらに含むことができる。 In this case, the lithium ion supply core part may further include a gel polymer electrolyte and a support, and may further include a liquid electrolyte and a porous carrier.
一方、前記電解質は、エチレンカーボネート（ＥＣ）、プロピレンカーボネート（ＰＣ）、ブチレンカーボネート（ＢＣ）、ビニレンカーボネート（ＶＣ）、ジエチルカーボネート（ＤＥＣ）、ジメチルカーボネート（ＤＭＣ）、エチルメチルカーボネート（ＥＭＣ）、メチルホルメート（ＭＦ）、γ‐ブチロラクトン（γ‐ＢＬ）、スルホラン、メチルアセテート（ＭＡ）、またはメチルプロピオネート（ＭＰ）を使用した非水電解液；ＰＥＯ、ＰＶｄＦ、ＰＶｄＦ‐ＨＦＰ、ＰＭＭＡ、ＰＡＮまたはＰＶＡｃを使用したゲル型高分子電解質；及びＰＥＯ、ポリプロピレンオキサイド（ＰＰＯ）、ポリエーテルイミン（ＰＥＩ）、ポリエチレンスルフィド（ＰＥＳ）またはポリビニルアセテート（ＰＶＡｃ）を使用した固体電解質；からなる群より選択された電解質を含むことができる。 On the other hand, the electrolyte is ethylene carbonate (EC), propylene carbonate (PC), butylene carbonate (BC), vinylene carbonate (VC), diethyl carbonate (DEC), dimethyl carbonate (DMC), ethyl methyl carbonate (EMC), methyl Non-aqueous electrolyte using formate (MF), γ-butyrolactone (γ-BL), sulfolane, methyl acetate (MA), or methyl propionate (MP); PEO, PVdF, PVdF-HFP, PMMA, PAN Or a gel type polyelectrolyte using PVAc; and a solid electrolyte using PEO, polypropylene oxide (PPO), polyetherimine (PEI), polyethylene sulfide (PES) or polyvinyl acetate (PVAc). An electrolyte selected from the group can be included.
また、前記電解質は、リチウム塩をさらに含むことができ、このとき、前記リチウム塩は、ＬｉＣｌ、ＬｉＢｒ、ＬｉＩ、ＬｉＣｌＯ4、ＬｉＢＦ4、ＬｉＢ10Ｃｌ10、ＬｉＰＦ6、ＬｉＣＦ3ＳＯ3、ＬｉＣＦ3ＣＯ2、ＬｉＡｓＦ6、ＬｉＳｂＦ6、ＬｉＡｌＣｌ4、ＣＨ3ＳＯ3Ｌｉ、ＣＦ3ＳＯ3Ｌｉ、（ＣＦ3ＳＯ2）2ＮＬｉ、クロロホウ酸リチウム、低級脂肪族カルボン酸リチウム、及びテトラフェニルホウ酸リチウムからなる群より選択されたいずれか１つまたはこれらのうち２種以上の混合物であり得る。 The electrolyte may further include a lithium salt. In this case, the lithium salt may be LiCl, LiBr, LiI, LiClO 4 , LiBF 4 , LiB 10 Cl 10 , LiPF 6 , LiCF 3 SO 3 , LiCF 3. CO 2 , LiAsF 6 , LiSbF 6 , LiAlCl 4 , CH 3 SO 3 Li, CF 3 SO 3 Li, (CF 3 SO 2 ) 2 NLi, lithium chloroborate, lithium lower aliphatic carboxylate, and lithium tetraphenylborate It may be any one selected from the group consisting of or a mixture of two or more thereof.
一方、前記内部電極が負極であり、外部電極が正極であるか、または、内部電極が正極であり、外部電極が負極であり得る。 Meanwhile, the internal electrode may be a negative electrode and the external electrode may be a positive electrode, or the internal electrode may be a positive electrode and the external electrode may be a negative electrode.
また、前記分離層は、電解質層またはセパレータであり得る。 The separation layer may be an electrolyte layer or a separator.
このとき、前記電解質層は、ＰＥＯ、ＰＶｄＦ、ＰＶｄＦ‐ＨＦＰ、ＰＭＭＡ、ＰＡＮまたはＰＶＡｃを使用したゲル型高分子電解質；及びＰＥＯ、ＰＰＯ、ＰＥＩ、ＰＥＳまたはＰＶＡｃを使用した固体電解質；からなる群より選択された電解質を含むことができる。 At this time, the electrolyte layer includes a gel type polymer electrolyte using PEO, PVdF, PVdF-HFP, PMMA, PAN or PVAc; and a solid electrolyte using PEO, PPO, PEI, PES or PVAc. A selected electrolyte can be included.
また、前記電解質層は、リチウム塩をさらに含むことができ、前記リチウム塩は、ＬｉＣｌ、ＬｉＢｒ、ＬｉＩ、ＬｉＣｌＯ4、ＬｉＢＦ4、ＬｉＢ10Ｃｌ10、ＬｉＰＦ6、ＬｉＣＦ3ＳＯ3、ＬｉＣＦ3ＣＯ2、ＬｉＡｓＦ6、ＬｉＳｂＦ6、ＬｉＡｌＣｌ4、ＣＨ3ＳＯ3Ｌｉ、ＣＦ3ＳＯ3Ｌｉ、（ＣＦ3ＳＯ2）2ＮＬｉ、クロロホウ酸リチウム、低級脂肪族カルボン酸リチウム、及びテトラフェニルホウ酸リチウムからなる群より選択されたいずれか１つまたはこれらのうち２種以上の混合物であり得る。 The electrolyte layer may further include a lithium salt, and the lithium salt may be LiCl, LiBr, LiI, LiClO 4 , LiBF 4 , LiB 10 Cl 10 , LiPF 6 , LiCF 3 SO 3 , LiCF 3 CO 2. , LiAsF 6 , LiSbF 6 , LiAlCl 4 , CH 3 SO 3 Li, CF 3 SO 3 Li, (CF 3 SO 2 ) 2 NLi, lithium chloroborate, lithium lower aliphatic carboxylate, and lithium tetraphenylborate It may be any one selected from the group or a mixture of two or more thereof.
また、前記セパレータは、エチレン単独重合体、プロピレン単独重合体、エチレン‐ブテン共重合体、エチレン‐ヘキセン共重合体及びエチレン‐メタクリレート共重合体からなる群より選択されたポリオレフィン系高分子から製造された多孔性高分子基材；ポリエステル、ポリアセタール、ポリアミド、ポリカーボネート、ポリイミド、ポリエーテルエーテルケトン、ポリエーテルスルホン、ポリフェニレンオキサイド、ポリフェニレンスルフィド及びポリエチレンナフタレートからなる群より選択された高分子から製造された多孔性高分子基材；無機物粒子とバインダー高分子との混合物から形成された多孔性基材；または前記多孔性高分子基材の少なくとも一面上に無機物粒子とバインダー高分子との混合物から形成された多孔性コーティング層を備えたセパレータであり得る。 The separator is manufactured from a polyolefin polymer selected from the group consisting of an ethylene homopolymer, a propylene homopolymer, an ethylene-butene copolymer, an ethylene-hexene copolymer, and an ethylene-methacrylate copolymer. Porous polymer substrate; porous made from a polymer selected from the group consisting of polyester, polyacetal, polyamide, polycarbonate, polyimide, polyether ether ketone, polyether sulfone, polyphenylene oxide, polyphenylene sulfide and polyethylene naphthalate Porous polymer substrate; porous substrate formed from a mixture of inorganic particles and binder polymer; or formed from a mixture of inorganic particles and binder polymer on at least one surface of the porous polymer substrate Porous coating It may be a separator having a Ingu layer.
一方、本発明のさらに他の態様によれば、電解質を含むリチウムイオン供給コア部；前記リチウムイオン供給コア部の外面を囲んで形成され、集電体及び電極活物質層を備える内部電極；前記内部電極の外面を囲んで形成され、電極の短絡を防止する分離層；及び前記分離層の外面を囲んで螺旋状に巻き取られて形成され、集電体及び電極活物質層を備える外部電極；を含み、前記内部電極及び前記外部電極の１種以上が本発明の二次電池用電極で形成されるケーブル型二次電池が提供される。 On the other hand, according to still another aspect of the present invention, a lithium ion supply core part including an electrolyte; an internal electrode formed surrounding an outer surface of the lithium ion supply core part and including a current collector and an electrode active material layer; A separation layer that surrounds the outer surface of the internal electrode and prevents a short circuit of the electrode; and an external electrode that is formed by being wound spirally around the outer surface of the separation layer and includes a current collector and an electrode active material layer A cable type secondary battery in which at least one of the internal electrode and the external electrode is formed of the secondary battery electrode of the present invention is provided.
また、本発明のさらに他の態様によれば、互いに平行に配置された２以上の内部電極；前記内部電極の外面を一緒に囲んで形成され、電極の短絡を防止する分離層；及び前記分離層の外面を囲んで螺旋状に巻き取られて形成された外部電極；を含み、前記内部電極及び前記外部電極の１種以上が本発明の二次電池用電極で形成されるケーブル型二次電池が提供される。 According to still another aspect of the present invention, two or more internal electrodes arranged in parallel to each other; a separation layer formed by surrounding the outer surfaces of the internal electrodes together to prevent a short circuit of the electrodes; and the separation An external electrode formed by spirally winding the outer surface of the layer, and at least one of the internal electrode and the external electrode is formed by the secondary battery electrode of the present invention. A battery is provided.
また、本発明のさらに他の態様によれば、電解質を含む２以上のリチウムイオン供給コア部；それぞれの前記リチウムイオン供給コア部の外面を囲んで形成され、集電体及び電極活物質層を備えて互いに平行に配置される２以上の内部電極；前記内部電極の外面を一緒に囲んで形成され、電極の短絡を防止する分離層；及び前記分離層の外面を囲んで螺旋状に巻き取られて形成され、集電体及び電極活物質層を備える外部電極；を含み、前記内部電極及び前記外部電極の１種以上が本発明の二次電池用電極で形成されるケーブル型二次電池が提供される。 According to still another aspect of the present invention, two or more lithium ion supply core parts including an electrolyte; formed around the outer surface of each of the lithium ion supply core parts, and a current collector and an electrode active material layer are provided. Two or more internal electrodes arranged parallel to each other; a separation layer formed by surrounding the outer surfaces of the internal electrodes together to prevent short-circuiting of the electrodes; and a spiral winding around the outer surface of the separation layer A cable type secondary battery in which at least one of the internal electrode and the external electrode is formed of the electrode for a secondary battery of the present invention. Is provided.
このとき、前記内部電極は、螺旋状に巻き取られた１つ以上の前記二次電池用電極を含むことができる。 In this case, the internal electrode may include one or more secondary battery electrodes wound in a spiral shape.
本発明によれば、シート型電極の少なくとも一面に支持層を取り入れることで、電極の柔軟性を大幅に向上させることができる。 According to the present invention, the flexibility of the electrode can be greatly improved by incorporating the support layer on at least one surface of the sheet-type electrode.
また、電極が完全に折れるなどの過酷な外力が作用するとき、電極活物質層のバインダー含量を増加させなくても、前記支持層が緩衝作用をすることで、電極活物質層のクラック発生を緩和し、それにより、集電体から電極活物質層が脱離する現象を防止することができる。 In addition, when a severe external force such as a complete bend of the electrode acts, the support layer acts as a buffer without increasing the binder content of the electrode active material layer, thereby generating cracks in the electrode active material layer. It can be mitigated, thereby preventing the phenomenon that the electrode active material layer is detached from the current collector.
それにより、電池の容量減少を防止し、電池のサイクル寿命特性を向上させることができる。 Thereby, the capacity reduction of the battery can be prevented and the cycle life characteristics of the battery can be improved.
また、電極活物質層の上面に有無機多孔性層を備えることで、電極活物質層への電解液の流入を円滑にして電極抵抗の増加を防止することができる。 In addition, by providing the presence / absence porous layer on the upper surface of the electrode active material layer, it is possible to smoothly flow the electrolyte solution into the electrode active material layer and prevent an increase in electrode resistance.
さらに、多孔性の支持層を備えることで電極活物質層への電解液の流入が円滑になり、前記多孔性支持層の孔に電解液が含浸することで電池内の抵抗増加を防止し、電池の性能低下を防止することができる。 Furthermore, by providing a porous support layer, the flow of the electrolyte into the electrode active material layer becomes smooth, and by impregnating the electrolyte in the pores of the porous support layer, an increase in resistance in the battery is prevented, Battery performance degradation can be prevented.
本明細書に添付される次の図面は、本発明の望ましい実施例を例示するものであり、発明の詳細な説明とともに本発明の技術的な思想をさらに理解させる役割をするため、本発明は図面に記載された事項だけに限定されて解釈されてはならない。
以下、本発明を図面に基づいて詳しく説明する。本明細書及び請求範囲に使用された用語や単語は通常的や辞書的な意味に限定して解釈されてはならず、発明者自らは発明を最善の方法で説明するために用語の概念を適切に定義できるという原則に則して本発明の技術的な思想に応ずる意味及び概念で解釈されねばならない。 Hereinafter, the present invention will be described in detail with reference to the drawings. Terms and words used in this specification and claims should not be construed to be limited to ordinary or lexicographic meanings, and the inventor himself used the terminology concepts to best explain the invention. In accordance with the principle that it can be properly defined, it must be interpreted in the meaning and concept corresponding to the technical idea of the present invention.
また、本明細書に記載された実施例と図面に示された構成は、本発明の最も望ましい一実施例に過ぎず、本発明の技術的な思想の全てを代弁するものではないため、本出願の時点においてこれらに代替できる多様な均等物及び変形例があり得ることを理解せねばならない。 In addition, the embodiments described in the present specification and the configurations shown in the drawings are only the most preferred embodiments of the present invention, and do not represent all the technical ideas of the present invention. It should be understood that there are various equivalents and variations that can be substituted at the time of filing.
図１及び図２は本発明の一実施例によるシート型二次電池用電極の断面を示した図であり、図３は本発明の一実施例によるシート型二次電池用電極の望ましい製造方法を概略的に示した図である。 1 and 2 are cross-sectional views of a sheet-type secondary battery electrode according to an embodiment of the present invention, and FIG. 3 is a preferred method for manufacturing a sheet-type secondary battery electrode according to an embodiment of the present invention. FIG.
図１ないし図３を参照すれば、本発明によるシート型二次電池用電極は、集電体１０；前記集電体１０の一面に形成された電極活物質層２０；前記電極活物質層２０上に形成され、無機物粒子及びバインダー高分子を含む有無機多孔性層３０；及び前記有無機多孔性層３０上に形成された多孔性の第１支持層４０；を含む。
1 to 3, the electrode for a sheet-type secondary battery according to the present invention includes a
また、前記集電体１０の他面に形成された第２支持層５０をさらに含むこともできる。
Further, the
可撓性を有する電池を製造するためには、電極の可撓性が十分確保されなければならない。しかし、可撓性電池の一例である従来のケーブル型二次電池は、形態の変形に伴う外力によるストレス、または、Ｓｉ、Ｓｎ系の高容量負極活物質を適用したとき、充放電過程で電極活物質層の急激な体積膨張などによって電極活物質層の脱離現象が生じ、電池の容量減少及びサイクル寿命特性の劣化現象が発生した。このような問題を解決するための一環として、電極活物質層に含まれるバインダーの含量を増加させれば、曲げやねじれに対する柔軟性を有し得る。 In order to manufacture a battery having flexibility, the flexibility of the electrode must be sufficiently ensured. However, the conventional cable-type secondary battery, which is an example of a flexible battery, has an electrode in the charge / discharge process when stress due to external force accompanying deformation of the form or when a Si, Sn-based high capacity negative electrode active material is applied. The desorption phenomenon of the electrode active material layer occurred due to the rapid volume expansion of the active material layer, and the battery capacity decreased and the cycle life characteristics deteriorated. As part of solving such problems, if the content of the binder contained in the electrode active material layer is increased, flexibility for bending and twisting can be obtained.
しかし、電極活物質層のバインダー含量の増加は電極抵抗を増加させ、電池性能低下の原因になり、また、電極が完全に折れるなどの過酷な外力が作用すれば、バインダーの含量を増加させても電極活物質層の脱離は防止できず、適切な解決方法になれなかった。 However, an increase in the binder content of the electrode active material layer increases the electrode resistance and causes a decrease in battery performance.If a severe external force such as the electrode is completely broken acts, the binder content is increased. However, desorption of the electrode active material layer could not be prevented, and an appropriate solution could not be obtained.
そこで、本発明では、電極の外面に形成された多孔性の第１支持層４０と、集電体１０の他面に形成され得る第２支持層５０をさらに含むことで、上述した問題点を解決した。
Therefore, the present invention further includes the porous
すなわち、前記多孔性の第１支持層４０は、電極に曲げまたはねじれの外力が作用しても、電極活物質層２０に作用する外力を緩和する緩衝作用をすることで、電極活物質層２０の脱離現象を防止し、電極の柔軟性を向上させる。また、さらに形成され得る前記第２支持層５０は、集電体１０の断線を抑制し、集電体１０の柔軟性をさらに向上させることができる。
In other words, the porous
また、本発明は、前記多孔性の第１支持層４０と電極活物質層２０とが互いに接着して一体化できるように、その間に接着物として、無機物粒子及びバインダー高分子を含む有無機混合スラリーの乾燥結果物である有無機多孔性層３０を含む。
In addition, the present invention provides an organic / inorganic mixture containing inorganic particles and a binder polymer as an adhesive so that the porous
前記接着物として、一般的なバインダーを適用すれば、電極の抵抗として作用して電池の性能劣化が発生する恐れがあるが、前記有無機多孔性層３０を含むようになれば、多孔性構造を形成することで電極活物質層への電解液の流入を円滑にし、電極抵抗の増加を防止することができる。
If a general binder is used as the adhesive, it may act as a resistance of the electrode and may deteriorate the performance of the battery. However, if the presence / absence of the
図１ないし図３を参照して、シート型二次電池用電極の製造方法について説明する。参考までに、図３では集電体１０の下面に第２支持層５０が予め形成されている状態で有無機多孔性層を形成する場合を示しているが、これは本発明の一実施例に過ぎず、後述するように第２支持層５０が形成されていない状態で有無機多孔性層を形成することもできる。
With reference to FIG. 1 thru | or FIG. 3, the manufacturing method of the electrode for sheet type secondary batteries is demonstrated. For reference, FIG. 3 shows a case where the presence / absence porous layer is formed in a state where the
まず、集電体１０の一面に、電極活物質スラリーを塗布し乾燥して電極活物質層２０を形成する（Ｓ１）。
First, the electrode active material slurry is applied to one surface of the
ここで、前記集電体１０は、電極活物質の電気化学反応によって生成された電子を集めるか、または電気化学反応に必要な電子を供給する役割をするものであって、ステンレススチール、アルミニウム、ニッケル、チタン、焼成炭素または銅；カーボン、ニッケル、チタンまたは銀で表面処理されたステンレススチール；アルミニウム‐カドミウム合金；導電材で表面処理された非伝導性高分子；伝導性高分子；Ｎｉ、Ａｌ、Ａｕ、Ａｇ、Ｐｄ／Ａｇ、Ｃｒ、Ｔａ、Ｃｕ、ＢａまたはＩＴＯである金属粉末を含む金属ペースト；若しくは黒鉛、カーボンブラックまたは炭素ナノチューブである炭素粉末を含む炭素ペースト；から製造されたものであり得る。
Here, the
上述したように、二次電池に曲げまたはねじれなどの外力が作用すれば、電極活物質層が集電体から脱離する現象が発生することがある。したがって、電極の柔軟性のために電極活物質層に多量のバインダー成分を含有させるようになる。しかし、このような多量のバインダーは、電解液によって膨潤（ｓｗｅｌｌｉｎｇ）して集電体から脱離し易く、それにより電池性能の低下が発生する恐れがある。 As described above, when an external force such as bending or twisting acts on the secondary battery, the electrode active material layer may be detached from the current collector. Therefore, a large amount of binder component is contained in the electrode active material layer for flexibility of the electrode. However, such a large amount of binder is easily swelled by the electrolyte and easily detached from the current collector, which may cause a decrease in battery performance.
したがって、電極活物質層と集電体との間の接着力を向上させるため、前記集電体１０は、導電材及びバインダーから構成された下塗層をさらに含むことができる。
Therefore, in order to improve the adhesive force between the electrode active material layer and the current collector, the
このとき、前記導電材は、カーボンブラック、アセチレンブラック、ケッチェンブラック、炭素繊維、炭素ナノチューブ及びグラフェンからなる群より選択されるいずれか１つまたはこれらのうち２種以上の混合物を含むものであり得るが、これらに限定されることはない。 At this time, the conductive material includes any one selected from the group consisting of carbon black, acetylene black, ketjen black, carbon fiber, carbon nanotube, and graphene, or a mixture of two or more thereof. However, it is not limited to these.
また、前記バインダーは、ポリフッ化ビニリデン、フッ化ビニリデン‐ヘキサフルオロプロピレン共重合体、ポリフッ化ビニリデン‐co-トリクロロエチレン、ポリブチルアクリレート、ポリメチルメタクリレート、ポリアクリロニトリル、ポリビニルピロリドン、ポリビニルアセテート、エチレンビニルアセテート共重合体、ポリエチレンオキサイド、ポリアリレート、セルロースアセテート、セルロースアセテートブチレート、セルロースアセテートプロピオネート、シアノエチルプルラン、シアノエチルポリビニルアルコール、シアノエチルセルロース、シアノエチルスクロース、プルラン、カルボキシルメチルセルロース、スチレンブタジエンゴム、アクリロニトリルスチレンブタジエン共重合体及びポリイミドからなる群より選択されたいずれか１つまたはこれらのうち２種以上の混合物であり得るが、これらに限定されることはない。 The binder is a combination of polyvinylidene fluoride, vinylidene fluoride-hexafluoropropylene copolymer, polyvinylidene fluoride-co-trichloroethylene, polybutyl acrylate, polymethyl methacrylate, polyacrylonitrile, polyvinyl pyrrolidone, polyvinyl acetate, ethylene vinyl acetate. Polymer, polyethylene oxide, polyarylate, cellulose acetate, cellulose acetate butyrate, cellulose acetate propionate, cyanoethyl pullulan, cyanoethyl polyvinyl alcohol, cyanoethyl cellulose, cyanoethyl sucrose, pullulan, carboxymethyl cellulose, styrene butadiene rubber, acrylonitrile styrene butadiene copolymer Selected from the group consisting of coalescence and polyimide And it may be any one or a mixture of two or more of these, but not limited thereto.
また、図４ないし図６を参照すれば、前記集電体１０はメッシュ型の集電体であり得、集電体の表面積をさらに増加させるため、少なくとも一面に、複数の凹部を形成することができる。このとき、前記複数の凹部は、連続的なパターンを有するか、または、断続的なパターンを有し得る。すなわち、互いに離隔して長さ方向に形成された連続的なパターンの凹部を有するか、または、多数の孔が形成された断続的なパターンを有し得る。前記多数の孔は円形であってもよく、多角形であってもよい。
4 to 6, the
一方、前記二次電池用電極が負極である場合、前記電極活物質層２０は、天然黒鉛、人造黒鉛または炭素質材料；リチウム含有チタン複合酸化物（ＬＴＯ）；Ｓｉ、Ｓｎ、Ｌｉ、Ｚｎ、Ｍｇ、Ｃｄ、Ｃｅ、ＮｉまたはＦｅである金属類（Ｍｅ）；前記金属類（Ｍｅ）の合金類；前記金属類（Ｍｅ）の酸化物（ＭｅＯｘ）；及び前記金属類（Ｍｅ）と炭素との複合体からなる群より選択されたいずれか１つの活物質またはこれらのうち２種以上の混合物を含み、前記二次電池用電極が正極である場合、前記電極活物質層は、ＬｉＣｏＯ2、ＬｉＮｉＯ2、ＬｉＭｎ2Ｏ4、ＬｉＣｏＰＯ4、ＬｉＦｅＰＯ4、ＬｉＮｉＭｎＣｏＯ2、及びＬｉＮｉ1-x-y-zＣｏxＭ１yＭ２zＯ2（Ｍ１及びＭ２は互いに独立して、Ａｌ、Ｎｉ、Ｃｏ、Ｆｅ、Ｍｎ、Ｖ、Ｃｒ、Ｔｉ、Ｗ、Ｔａ、Ｍｇ及びＭｏからなる群より選択され、ｘ、ｙ及びｚは互いに独立した酸化物組成元素の原子分率であって、０≦ｘ＜０．５、０≦ｙ＜０．５、０≦ｚ＜０．５、ｘ＋ｙ＋ｚ≦１である）からなる群より選択されたいずれか１つの活物質またはこれらのうち２種以上の混合物を含むことができる。
On the other hand, when the electrode for the secondary battery is a negative electrode, the electrode
次いで、前記電極活物質層２０上に、無機物粒子及びバインダー高分子を含む有無機混合スラリー３０'を塗布する（Ｓ２）。
Next, on the electrode
このとき、前記有無機混合スラリー３０'は接着物として使用される。一般的なバイン
ダーのみを使用すれば、孔が形成されず電極活物質層に電解液が流入し難く、結局抵抗として作用して電池性能の劣化を生じさせる恐れがある。
At this time, the presence / absence machine mixed slurry 30 'is used as an adhesive. If only a general binder is used, pores are not formed, and the electrolyte does not easily flow into the electrode active material layer, which may eventually act as a resistance and cause deterioration in battery performance.
ここで、前記有無機混合スラリー３０'は、その後有無機多孔性層３０を形成するよう
になり、前記無機物粒子と前記バインダー高分子とを２０：８０ないし９５：５の重量比で混合して形成することができる。
Here, the presence / absence / inorganic mixing
このとき、前記無機物粒子は、誘電率定数が５以上の無機物粒子、リチウムイオン伝達能力を有する無機物粒子、またはこれらの混合物であり得る。 At this time, the inorganic particles may be inorganic particles having a dielectric constant of 5 or more, inorganic particles having lithium ion transfer capability, or a mixture thereof.
ここで、前記誘電率定数が５以上の無機物粒子は、ＢａＴｉＯ3、Ｐｂ（Ｚｒx、Ｔｉ1-x）Ｏ3（ＰＺＴ、０＜ｘ＜１）、Ｐｂ1-xＬａxＺｒ1-yＴｉyＯ3（ＰＬＺＴ、０＜ｘ＜１、０＜ｙ＜１）、（１−ｘ）Ｐｂ（Ｍｇ1/3Ｎｂ2/3）Ｏ3-xＰｂＴｉＯ3（ＰＭＮ‐ＰＴ、０＜ｘ＜１）、ハフニア（ＨｆＯ2）、ＳｒＴｉＯ3、ＳｎＯ2、ＣｅＯ2、ＭｇＯ、ＮｉＯ、ＣａＯ、ＺｎＯ、ＺｒＯ2、Ｙ2Ｏ3、Ａｌ2Ｏ3、ＳｉＣ、ＳｉＯ2、ＡｌＯＯＨ、Ａｌ（ＯＨ）3及びＴｉＯ2からなる群より選択されたいずれか１つまたはこれらのうち２種以上の混合物であり得る。 Here, the inorganic particles having a dielectric constant of 5 or more are BaTiO 3 , Pb (Zr x , Ti 1-x ) O 3 (PZT, 0 <x <1), Pb 1-x La x Zr 1-y. Ti y O 3 (PLZT, 0 <x <1, 0 <y <1), (1-x) Pb (Mg 1/3 Nb 2/3 ) O 3-x PbTiO 3 (PMN-PT, 0 <x <1), hafnia (HfO 2 ), SrTiO 3 , SnO 2 , CeO 2 , MgO, NiO, CaO, ZnO, ZrO 2 , Y 2 O 3 , Al 2 O 3 , SiC, SiO 2 , AlOOH, Al (OH ) Any one selected from the group consisting of 3 and TiO 2, or a mixture of two or more thereof.
また、前記リチウムイオン伝達能力を有する無機物粒子は、リチウムホスフェート（Ｌｉ3ＰＯ4）、リチウムチタンホスフェート（ＬｉxＴｉy（ＰＯ4）3、０＜ｘ＜２、０＜ｙ＜３）、リチウムアルミニウムチタンホスフェート（ＬｉxＡｌyＴｉz（ＰＯ4）3、０＜ｘ＜２、０＜ｙ＜１、０＜ｚ＜３）、（ＬｉＡｌＴｉＰ）xＯy系列ガラス（０＜ｘ＜４、０＜ｙ＜１３）、リチウムランタンチタネート（ＬｉxＬａyＴｉＯ3、０＜ｘ＜２、０＜ｙ＜３）、リチウムゲルマニウムチオホスフェート（ＬｉxＧｅyＰzＳw、０＜ｘ＜４、０＜ｙ＜１、０＜ｚ＜１、０＜ｗ＜５）、リチウムナイトライド（ＬｉxＮy、０＜ｘ＜４、０＜ｙ＜２）、ＳｉＳ2系列ガラス（ＬｉxＳｉyＳz、０＜ｘ＜３、０＜ｙ＜２、０＜ｚ＜４）及びＰ2Ｓ5系列ガラス（ＬｉxＰyＳz、０＜ｘ＜３、０＜ｙ＜３、０＜ｚ＜７）からなる群より選択されたいずれか１つまたはこれらのうち２種以上の混合物であり得る。 The inorganic particles having lithium ion transfer capability include lithium phosphate (Li 3 PO 4 ), lithium titanium phosphate (Li x Ti y (PO 4 ) 3 , 0 <x <2, 0 <y <3), lithium aluminum titanium phosphate (Li x Al y Ti z ( PO 4) 3, 0 <x <2,0 <y <1,0 <z <3), (LiAlTiP) x O y series glass (0 <x <4, 0 <y <13), lithium lanthanum titanate (Li x La y TiO 3 , 0 <x <2, 0 <y <3), lithium germanium thiophosphate (Li x Ge y P z S w , 0 <x <4 , 0 <y <1, 0 <z <1, 0 <w <5), lithium nitride (Li x N y , 0 <x <4, 0 <y <2), SiS 2 series glass (Li x Si y S z , 0 <x <3, 0 <y <2, 0 <z <4) and And P 2 S 5 series glass (Li x P y S z , 0 <x <3, 0 <y <3, 0 <z <7), or one or two of them It can be a mixture of the above.
また、前記無機物粒子の平均粒径は、１０ｎｍないし５μｍであり得る。 The average particle size of the inorganic particles may be 10 nm to 5 μm.
一方、前記バインダー高分子は、ポリフッ化ビニリデン、フッ化ビニリデン‐ヘキサフルオロプロピレン共重合体、ポリフッ化ビニリデン‐co-トリクロロエチレン、ポリブチルアクリレート、ポリメチルメタクリレート、ポリアクリロニトリル、ポリビニルピロリドン、ポリビニルアセテート、エチレンビニルアセテート共重合体、ポリエチレンオキサイド、ポリアリレート、セルロースアセテート、セルロースアセテートブチレート、セルロースアセテートプロピオネート、シアノエチルプルラン、シアノエチルポリビニルアルコール、シアノエチルセルロース、シアノエチルスクロース、プルラン、カルボキシルメチルセルロース、スチレンブタジエンゴム、アクリロニトリルスチレンブタジエン共重合体及びポリイミドからなる群より選択されたいずれか１つまたはこれらのうち２種以上の混合物であり得るが、これらに限定されることはない。 On the other hand, the binder polymer includes polyvinylidene fluoride, vinylidene fluoride-hexafluoropropylene copolymer, polyvinylidene fluoride-co-trichloroethylene, polybutyl acrylate, polymethyl methacrylate, polyacrylonitrile, polyvinyl pyrrolidone, polyvinyl acetate, ethylene vinyl. Acetate copolymer, polyethylene oxide, polyarylate, cellulose acetate, cellulose acetate butyrate, cellulose acetate propionate, cyanoethyl pullulan, cyanoethyl polyvinyl alcohol, cyanoethyl cellulose, cyanoethyl sucrose, pullulan, carboxymethyl cellulose, styrene butadiene rubber, acrylonitrile styrene butadiene From the group consisting of copolymers and polyimides One which is-option, or a mixture of two or more of these, but not limited thereto.
次いで、前記塗布された有無機混合スラリー３０'上に多孔性の第１支持層４０を形成
する（Ｓ３）。
Next, a porous
ここで、前記第１支持層４０は、メッシュ型多孔性膜または不織布であり得る。このように多孔性の構造を有することで、電極活物質層２０への電解液の流入を円滑にし、第１支持層４０自体でも電解液の含浸性に優れるため、イオン伝導性が確保されて電池内部の抵抗増加を防止し、電池の性能低下を防止することができる。
Here, the
また、前記第１支持層４０は、高密度ポリエチレン、低密度ポリエチレン、線形低密度ポリエチレン、超高分子量ポリエチレン、ポリプロピレン、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエステル、ポリアセタール、ポリアミド、ポリカーボネート、ポリイミド、ポリエーテルエーテルケトン、ポリエーテルスルホン、ポリフェニレンオキサイド、ポリフェニレンスルフィド及びポリエチレンナフタレートからなる群より選択されたいずれか１つまたはこれらのうち２種以上の混合物から形成することができる。
The
一方、前記第１支持層４０の上面に、導電材及びバインダーを備える導電材コーティング層をさらに含むことができる。前記導電材コーティング層は、電極活物質層の伝導性を向上させて電極の抵抗を減少させることで、電池の性能低下を防止する。
Meanwhile, the upper surface of the
このとき、前記導電材及びバインダーとしては、上述した下塗層に使用されたものと同じものなどを使用することができる。 At this time, as the conductive material and the binder, the same materials as those used for the undercoat layer described above can be used.
負極の場合、負極活物質層の伝導性が比較的に優れるため、前記導電材コーティング層を含まなくても、一般的な負極が使われた場合と同様の性能を示すが、正極の場合は、正極活物質層の伝導性が低く、電極抵抗の増加による性能低下が深刻になり得るため、電池内部の抵抗減少のために正極に適用されるとき特に有利である。 In the case of the negative electrode, since the conductivity of the negative electrode active material layer is relatively excellent, even if the conductive material coating layer is not included, the same performance as when a general negative electrode is used is shown. In addition, since the conductivity of the positive electrode active material layer is low and the performance degradation due to the increase in electrode resistance can be serious, it is particularly advantageous when applied to the positive electrode for reducing the resistance inside the battery.
このとき、前記導電材コーティング層は、前記導電材と前記バインダーとを８０：２０ないし９９：１の重量比で混合したものであり得る。バインダーの含量が増加すれば、電極の抵抗が過度に増加する恐れがあるが、上述した数値範囲の含量を満足すれば、電極の抵抗が過度に増加することを防止できる。さらに、上述したように、第１支持層が電極活物質層の脱離現象を防止する緩衝作用を果たすため、比較的少量のバインダーが含まれても、電極の柔軟性確保にはあまり差し支えない。 In this case, the conductive material coating layer may be a mixture of the conductive material and the binder in a weight ratio of 80:20 to 99: 1. If the binder content is increased, the resistance of the electrode may be excessively increased. However, if the content in the numerical range described above is satisfied, it is possible to prevent the electrode resistance from being excessively increased. Furthermore, as described above, since the first support layer functions as a buffer to prevent the electrode active material layer from being detached, even if a relatively small amount of binder is included, there is no problem in ensuring the flexibility of the electrode. .
次いで、前記（Ｓ３）工程の結果物を圧着し、前記電極活物質層２０と前記第１支持層４０との間に接着して一体化した有無機多孔性層３０を形成する（Ｓ４）。
Next, the resultant product of the step (S3) is pressure-bonded, and the presence / absence
前記有無機多孔性層３０は、多孔性構造を有することで電極活物質層への電解液の流入を円滑にする。前記有無機多孔性層３０に形成された孔の大きさは０．０１μｍないし１０μｍであり、気孔度は５ないし９５％であり得る。
The presence / absence
このとき、前記有無機多孔性層の多孔性構造は、その製造過程で、非溶媒（ｎｏｎ−ｓｏｌｖｅｎｔ）による相分離または相転換を通じて形成され得、バインダー高分子によって無機物粒子が連結及び固定されることで生ずる無機物粒子間のインタースティシャル・ボリューム（ｉｎｔｅｒｓｔｉｔｉａｌ ｖｏｌｕｍｅ）によって形成されることもできる。 At this time, the porous structure of the organic / non-organic porous layer may be formed through non-solvent phase separation or phase conversion in the manufacturing process, and the inorganic particles are connected and fixed by the binder polymer. It can also be formed by an interstitial volume between the inorganic particles.
一方、前記有無機混合スラリー３０'を前記電極活物質層２０の一面にコーティングし
た後、乾燥させて有無機多孔性層３０を形成した後、その上に第１支持層４０をラミネートなどを通じて形成すれば、前記電極活物質層２０と前記第１支持層４０とを互いに接着させる有無機混合スラリー３０'のバインダー成分が硬化し、両層間の強い接着力が維持
されないこともあり得る。
On the other hand, after coating the presence / absence organic
また、本発明の望ましい製造方法のように、予め製造された多孔性の第１支持層を使用せず、有無機多孔性層に高分子溶液をコーティングすることで多孔性の支持層を形成することもできる。しかし、高分子溶液をコーティングして形成した多孔性支持体は、本発明の望ましい製造方法によって製造された多孔性の第１支持層に比べて機械的物性が悪く、外部力による電極活物質層の脱離現象を効果的に抑制することができない。 In addition, unlike the preferred production method of the present invention, a porous support layer is formed by coating a polymer solution on the presence / absence porous layer without using a porous first support layer produced in advance. You can also. However, the porous support formed by coating the polymer solution has poor mechanical properties as compared with the porous first support layer manufactured by the preferable manufacturing method of the present invention, and the electrode active material layer due to external force. The desorption phenomenon cannot be effectively suppressed.
しかし、本発明の望ましい製造方法によれば、前記バインダー成分が硬化する前に、有無機混合スラリー３０'の上面に第１支持層４０を形成し、コーティングブレード６０に
より共にコーティングすることで、前記電極活物質層２０と前記第１支持層４０との間に接着し一体化した有無機多孔性層３０を形成することができる。
However, according to the preferred manufacturing method of the present invention, before the binder component is cured, the
一方、前記（Ｓ１）工程の前又は前記（Ｓ４）工程の後、前記集電体１０の他面に、第２支持層５０を圧着して形成する工程をさらに含むことができる。ここで、前記第２支持層５０は、前記集電体１０の断線を抑制し、前記集電体１０の柔軟性を一層向上させることができる。
On the other hand, before the (S1) step or after the (S4) step, a step of pressing the
このとき、前記第２支持層５０は、高分子フィルムであり得、このとき、前記高分子フィルムは、ポリオレフィン、ポリエステル、ポリイミド及びポリアミドからなる群より選択されるいずれか１つまたはこれらのうち２種以上の混合物から形成することができる。
At this time, the
一方、本発明の二次電池は、正極、負極、前記正極と前記負極との間に介在されたセパレータ、及び電解質を含むものであって、前記正極及び負極の少なくとも１つは上述した本発明の二次電池用電極である。 On the other hand, the secondary battery of the present invention includes a positive electrode, a negative electrode, a separator interposed between the positive electrode and the negative electrode, and an electrolyte, and at least one of the positive electrode and the negative electrode is the above-described present invention. This is an electrode for a secondary battery.
ここで、本発明の二次電池は、積層型、巻取型、積層／折畳型の一般的な形態の二次電池だけでなく、ケーブル型二次電池などの特殊な形態の二次電池でもあり得る。 Here, the secondary battery of the present invention is not only a secondary battery of a general type such as a stacked type, a winding type, and a stacked / folded type, but also a secondary battery of a special form such as a cable type secondary battery. But it can be.
一方、本発明によるケーブル型二次電池は、内部電極；前記内部電極の外面を囲んで形成され、電極の短絡を防止する分離層；及び前記分離層の外面を囲んで螺旋状に巻き取られて形成された外部電極；を含み、前記内部電極及び前記外部電極の１種以上が上述した本発明の二次電池用電極で形成される。 On the other hand, the cable type secondary battery according to the present invention includes an internal electrode; a separation layer formed around the outer surface of the internal electrode to prevent a short circuit of the electrode; and a spiral wound around the outer surface of the separation layer. And at least one of the internal electrode and the external electrode is formed of the secondary battery electrode of the present invention described above.
ここで、螺旋状とは、英語でスパイラル（ｓｐｉｒａｌ）またはヘリックス（ｈｅｌｉｘ）であって、一定範囲をねじれ曲がった形状であり、一般にバネ状と類似する形状を通称する。 Here, the spiral is a spiral or a helix in English, and is a shape in which a certain range is twisted, and generally refers to a shape similar to a spring shape.
このとき、前記外部電極は、一方向に延びたストリップ（ｓｔｒｉｐ、帯）構造であり得る。 In this case, the external electrode may have a strip structure extending in one direction.
また、前記外部電極は、互いに重ならないように螺旋状に巻き取られて形成され得る。このとき、前記外部電極は、電池の性能が低下しないように前記外部電極の幅の２倍以内の間隔を置いて互いに離隔し、重ならないように螺旋状に巻き取られて形成され得る。 In addition, the external electrodes may be formed by being spirally wound so as not to overlap each other. At this time, the external electrodes may be formed by being spirally wound so as to be spaced apart from each other at intervals of not more than twice the width of the external electrodes so as not to deteriorate battery performance.
また、前記外部電極は、互いに重なるように螺旋状に巻き取られて形成され得る。このとき、前記外部電極は、電池の内部抵抗の過度な上昇を抑制するため、互いに重なる部分の幅が前記外部電極の幅の０．９倍以内になるように螺旋状に巻き取られて形成され得る。 In addition, the external electrodes may be formed by being spirally wound so as to overlap each other. At this time, the external electrode is formed by being spirally wound so that the width of the overlapping portion is within 0.9 times the width of the external electrode in order to suppress an excessive increase in the internal resistance of the battery. Can be done.
一方、前記内部電極は、内部に空間が形成された中空型構造であり得る。 Meanwhile, the internal electrode may have a hollow structure in which a space is formed.
このとき、前記内部電極は、螺旋状に巻き取られた１つ以上の前記二次電池用電極を含むことができる。 In this case, the internal electrode may include one or more secondary battery electrodes wound in a spiral shape.
また、前記内部電極の内部に形成された空間に、内部電極集電体コア部が形成され得る。 In addition, an internal electrode current collector core portion may be formed in a space formed inside the internal electrode.
このとき、前記内部電極集電体コア部は、カーボンナノチューブ、ステンレススチール、アルミニウム、ニッケル、チタン、焼成炭素または銅；カーボン、ニッケル、チタンまたは銀で表面処理されたステンレススチール；アルミニウム‐カドミウム合金；導電材で表面処理された非伝導性高分子；若しくは伝導性高分子から製造され得る。 At this time, the internal electrode current collector core is formed of carbon nanotubes, stainless steel, aluminum, nickel, titanium, baked carbon or copper; stainless steel surface-treated with carbon, nickel, titanium or silver; aluminum-cadmium alloy; Non-conductive polymer surface-treated with a conductive material; or may be manufactured from a conductive polymer.
また、前記内部電極の内部に形成された空間に、電解質を含むリチウムイオン供給コア部が形成され得る。 In addition, a lithium ion supply core including an electrolyte may be formed in a space formed inside the internal electrode.
このとき、前記リチウムイオン供給コア部は、ゲル型ポリマー電解質及び支持体を含むことができる。 At this time, the lithium ion supply core may include a gel polymer electrolyte and a support.
また、前記リチウムイオン供給コア部は、液体電解質及び多孔性担体を含むことができる。 The lithium ion supply core may include a liquid electrolyte and a porous carrier.
また、前記内部電極の内部に形成された空間に、充填コア部が形成され得る。 In addition, a filling core portion may be formed in a space formed inside the internal electrode.
前記充填コア部は、上述した内部電極集電体コア部及びリチウムイオン供給コア部を形成する材料の外に、ケーブル型二次電池において多様な性能を改善させるための材料、例えば、高分子樹脂、ゴム、無機物などを、ワイヤ型、繊維状、粉末状、メッシュ、発泡体などの多様な形状で含むことができる。 In addition to the materials forming the internal electrode current collector core and the lithium ion supply core, the filling core is made of a material for improving various performances in the cable-type secondary battery, for example, a polymer resin. , Rubber, inorganic materials, etc. can be included in various shapes such as wire, fiber, powder, mesh, foam and the like.
一方、図７は、本発明の一実施例によるケーブル型二次電池であって、シート型内部電極がリチウムイオン供給コア部１１０の外面に巻き取られて形成されることを概略的に示した図であり、シート型の内部電極がケーブル型二次電池に適用される様子を示している。後述するシート型の外部電極が分離層の外面に巻き取られて形成される様子も同様である。
Meanwhile, FIG. 7 is a cable type secondary battery according to an embodiment of the present invention, and schematically illustrates that a sheet type internal electrode is formed by being wound around an outer surface of a lithium ion
このような本発明の一実施例によるケーブル型二次電池は、電解質を含むリチウムイオン供給コア部；前記リチウムイオン供給コア部の外面を囲んで形成され、集電体及び電極活物質層を備える内部電極；前記内部電極の外面を囲んで形成され、電極の短絡を防止する分離層；及び前記分離層の外面を囲んで螺旋状に巻き取られて形成され、集電体及び電極活物質層を備える外部電極；を含み、前記内部電極及び前記外部電極の１種以上が本発明の二次電池用電極で形成される。 Such a cable type secondary battery according to an embodiment of the present invention includes a lithium ion supply core part including an electrolyte; an outer surface of the lithium ion supply core part, and a current collector and an electrode active material layer. An inner electrode; a separation layer formed to surround the outer surface of the inner electrode and prevent a short circuit of the electrode; and a current collector and an electrode active material layer formed to be wound spirally around the outer surface of the separation layer And at least one of the internal electrode and the external electrode is formed of the secondary battery electrode of the present invention.
本発明の一実施例によるケーブル型二次電池は、所定形状の水平断面を有し、水平断面に対する長さ方向に長く延びた線型構造を有し得る。本発明の一実施例によるケーブル型二次電池は、可撓性を有するため、変形が自由である。ここで、所定の形状とは、特に形状を制限しないということであり、本発明の本質から逸脱しない如何なる形状も可能であるという意味である。 The cable type secondary battery according to an embodiment of the present invention may have a linear structure having a horizontal cross section having a predetermined shape and extending long in a length direction with respect to the horizontal cross section. The cable type secondary battery according to an embodiment of the present invention is flexible and thus can be freely deformed. Here, the predetermined shape means that the shape is not particularly limited, and means that any shape that does not depart from the essence of the present invention is possible.
図８には、内部電極に上述した本発明の二次電池用電極が導入されたケーブル型二次電池１００が示されている。
FIG. 8 shows a cable type
図８を参照すれば、電解質を含むリチウムイオン供給コア部１１０；前記リチウムイオン供給コア部１１０の外面を囲んで巻き取られて形成される内部電極；前記内部電極の外面を囲んで形成され、電極の短絡を防止する分離層１７０；及び前記分離層１７０の外面を囲んで螺旋状に巻き取られて形成され、外部集電体１９０及び外部電極活物質層１８０を備える外部電極；を含み、前記内部電極は、内部集電体１２０、前記内部集電体１２０の一面に形成された内部電極活物質層１３０、前記内部電極活物質層１３０の上面に形成され、無機物粒子及びバインダー高分子を含む有無機多孔性層１４０、前記有無機多孔性層１４０の上面に形成された多孔性の第１支持層１５０、及び前記内部集電体１２０の他面に形成された第２支持層１６０を含む。
Referring to FIG. 8, a lithium ion
上述したように、内部電極ではなく外部電極が上述した本発明のシート型の二次電池用電極であっても良く、内部電極と外部電極ともに本発明のシート型の二次電池用電極で形成されても良い。 As described above, the external electrode instead of the internal electrode may be the above-described sheet-type secondary battery electrode of the present invention, and both the internal electrode and the external electrode are formed of the sheet-type secondary battery electrode of the present invention. May be.
ここで、前記リチウムイオン供給コア部１１０は、電解質を含む。該電解質としては、その種類を特に限定しないが、エチレンカーボネート、プロピレンカーボネート、ブチレンカーボネート、ビニレンカーボネート、ジエチルカーボネート、ジメチルカーボネート、エチルメチルカーボネート、メチルホルメート、γ‐ブチロラクトン、スルホラン、メチルアセテート、またはメチルプロピオネートを使用した非水電解液；ＰＥＯ、ＰＶｄＦ、ＰＶｄＦ‐ＨＦＰ、ＰＭＭＡ、ＰＡＮまたはＰＶＡｃを使用したゲル型高分子電解質；若しくはＰＥＯ、ＰＰＯ、ポリエーテルイミン(ＰＥＩ）、ＰＥＳまたはＰＶＡｃを使用した固体電解質；などを使用することができる。また、このような電解質は、リチウム塩をさらに含むことができるが、このようなリチウム塩としては、ＬｉＣｌ、ＬｉＢｒ、ＬｉＩ、ＬｉＣｌＯ4、ＬｉＢＦ4、ＬｉＢ10Ｃｌ10、ＬｉＰＦ6、ＬｉＣＦ3ＳＯ3、ＬｉＣＦ3ＣＯ2、ＬｉＡｓＦ6、ＬｉＳｂＦ6、ＬｉＡｌＣｌ4、ＣＨ3ＳＯ3Ｌｉ、ＣＦ3ＳＯ3Ｌｉ、（ＣＦ3ＳＯ2）2ＮＬｉ、クロロホウ酸リチウム、低級脂肪族カルボン酸リチウム、及びテトラフェニルホウ酸リチウムなどを使用することが望ましい。また、このようなリチウムイオン供給コア部１１０は、電解質のみから構成でき、液相の電解液である場合は、多孔質の担体を使用して構成することもできる。
Here, the lithium ion
一方、前記内部電極が負極であり、外部電極が正極であるか、または、内部電極が正極であり、外部電極が負極であり得る。 Meanwhile, the internal electrode may be a negative electrode and the external electrode may be a positive electrode, or the internal electrode may be a positive electrode and the external electrode may be a negative electrode.
前記負極または正極に使用される電極活物質は、上述した通りである。 The electrode active material used for the negative electrode or the positive electrode is as described above.
また、本発明の分離層１７０としては、電解質層またはセパレータを使用することができる。
In addition, as the
イオンの通路になる電解質層としては、ＰＥＯ、ＰＶｄＦ、ＰＶｄＦ‐ＨＦＰ、ＰＭＭＡ、ＰＡＮまたはＰＶＡｃを使用したゲル型高分子電解質；若しくはＰＥＯ、ＰＰＯ、ポリエチレンイミン(ＰＥＩ）、ＰＥＳまたはＰＶＡｃを使用した固体電解質；などを使用する。固体電解質のマトリクスは、高分子またはセラミックガラスを基本骨格にすることが望ましい。一般の高分子電解質の場合は、イオン伝導度が満足できても反応速度の面でイオンの移動が非常に遅い恐れがあるため、固体よりは、イオンの移動が容易なゲル型高分子の電解質を使用することが望ましい。ゲル型高分子電解質は、機械的特性に優れないため、それを補うために支持体を含むことができ、このような支持体としては孔構造支持体または架橋高分子を使用することができる。本発明の電解質層は、セパレータの役割も果たせるため、別途のセパレータを使用しなくてもよい。 As an electrolyte layer for ion passage, gel type polymer electrolyte using PEO, PVdF, PVdF-HFP, PMMA, PAN or PVAc; or solid using PEO, PPO, polyethyleneimine (PEI), PES or PVAc Electrolytes; etc. are used. The matrix of the solid electrolyte is preferably based on a polymer or ceramic glass. In the case of general polymer electrolytes, even if ionic conductivity is satisfactory, the movement of ions may be very slow in terms of reaction rate. It is desirable to use Since the gel type polyelectrolyte is not excellent in mechanical properties, it can contain a support to supplement it, and as such a support, a pore structure support or a crosslinked polymer can be used. Since the electrolyte layer of the present invention can also serve as a separator, it is not necessary to use a separate separator.
本発明の電解質層は、リチウム塩をさらに含むことができる。リチウム塩は、イオン伝導度及び反応速度を向上させることができ、これらの非制限的な例としては、ＬｉＣｌ、ＬｉＢｒ、ＬｉＩ、ＬｉＣｌＯ4、ＬｉＢＦ4、ＬｉＢ10Ｃｌ10、ＬｉＰＦ6、ＬｉＣＦ3ＳＯ3、ＬｉＣＦ3ＣＯ2、ＬｉＡｓＦ6、ＬｉＳｂＦ6、ＬｉＡｌＣｌ4、ＣＨ3ＳＯ3Ｌｉ、ＣＦ3ＳＯ3Ｌｉ、（ＣＦ3ＳＯ2）2ＮＬｉ、クロロホウ酸リチウム、低級脂肪族カルボン酸リチウム、及びテトラフェニルホウ酸リチウムなどが挙げられる。 The electrolyte layer of the present invention can further include a lithium salt. Lithium salts can improve ionic conductivity and reaction rate, non-limiting examples of which include LiCl, LiBr, LiI, LiClO 4 , LiBF 4 , LiB 10 Cl 10 , LiPF 6 , LiCF 3 SO 3 , LiCF 3 CO 2 , LiAsF 6 , LiSbF 6 , LiAlCl 4 , CH 3 SO 3 Li, CF 3 SO 3 Li, (CF 3 SO 2 ) 2 NLi, lithium chloroborate, lower aliphatic lithium carboxylate, and tetra Examples thereof include lithium phenylborate.
前記セパレータとしては、その種類を限定しないが、エチレン単独重合体、プロピレン単独重合体、エチレン‐ブテン共重合体、エチレン‐ヘキセン共重合体及びエチレン‐メタクリレート共重合体からなる群より選択されたポリオレフィン系高分子から製造された多孔性高分子基材；ポリエステル、ポリアセタール、ポリアミド、ポリカーボネート、ポリイミド、ポリエーテルエーテルケトン、ポリエーテルスルホン、ポリフェニレンオキサイド、ポリフェニレンスルフィド及びポリエチレンナフタレートからなる群より選択された高分子から製造された多孔性高分子基材；無機物粒子とバインダー高分子との混合物から形成された多孔性基材；または前記多孔性高分子基材の少なくとも一面上に無機物粒子とバインダー高分子との混合物から形成された多孔性コーティング層を備えたセパレータなどを使用することができる。 The separator is not limited in its type, but is a polyolefin selected from the group consisting of ethylene homopolymer, propylene homopolymer, ethylene-butene copolymer, ethylene-hexene copolymer and ethylene-methacrylate copolymer. Porous polymer substrate made from a polymer based polymer; high selected from the group consisting of polyester, polyacetal, polyamide, polycarbonate, polyimide, polyetheretherketone, polyethersulfone, polyphenylene oxide, polyphenylene sulfide and polyethylene naphthalate A porous polymer substrate made from molecules; a porous substrate formed from a mixture of inorganic particles and a binder polymer; or inorganic particles and a binder polymer on at least one surface of the porous polymer substrate; Mixture of Etc. can be used a separator having a porous coating layer which is et formed.
このとき、無機物粒子とバインダー高分子との混合物から形成された前記多孔性コーティング層では、無機物粒子同士が互いに結着した状態を維持できるように、バインダー高分子がこれらを互いに付着（すなわち、バインダー高分子が無機物粒子同士の間を連結及び固定）しており、また、前記多孔性コーティング層は高分子バインダーによって前記多孔性高分子基材と結着した状態を維持する。このような多孔性コーティング層の無機物粒子は、実質的に互いに接触した状態で最密充填された構造で存在し、無機物粒子同士が接触した状態で生じるインタースティシャル・ボリューム（ｉｎｔｅｒｓｔｉｔｉａｌ ｖｏｌｕｍｅ）が前記多孔性コーティング層の孔になる。 At this time, in the porous coating layer formed from a mixture of inorganic particles and binder polymer, the binder polymer adheres to each other (that is, the binder particles are attached to each other so that the inorganic particles can be in a state of being bound to each other). The polymer is connected and fixed between inorganic particles), and the porous coating layer maintains a state of being bound to the porous polymer substrate by a polymer binder. The inorganic particles of the porous coating layer are present in a close-packed structure substantially in contact with each other, and the interstitial volume generated when the inorganic particles are in contact with each other is the above-described interstitial volume. It becomes pores of the porous coating layer.
特に、リチウムイオン供給コア部のリチウムイオンが外部電極にも容易に伝達されるためには、前記ポリエステル、ポリアセタール、ポリアミド、ポリカーボネート、ポリイミド、ポリエーテルエーテルケトン、ポリエーテルスルホン、ポリフェニレンオキサイド、ポリフェニレンスルフィド及びポリエチレンナフタレートからなる群より選択された高分子から製造された多孔性高分子基材に該当する不織布材質のセパレータを使用することが望ましい。 In particular, in order for lithium ions in the lithium ion supply core part to be easily transmitted to the external electrode, the polyester, polyacetal, polyamide, polycarbonate, polyimide, polyether ether ketone, polyether sulfone, polyphenylene oxide, polyphenylene sulfide and It is desirable to use a non-woven fabric separator corresponding to a porous polymer substrate made from a polymer selected from the group consisting of polyethylene naphthalate.
また、本発明は、保護被覆１９５を備える。保護被覆１９５は、絶縁体であって、空気中の水分及び外部衝撃から電極を保護するために外部集電体の外面に形成される。前記保護被覆としては、水分遮断層を含む通常の高分子樹脂を使用することができる。このとき、前記水分遮断層としては、水分遮断性能に優れたアルミニウムや液晶高分子などが使用でき、前記高分子樹脂としては、ＰＥＴ、ＰＶＣ、ＨＤＰＥまたはエポキシ樹脂などが使用できる。
The present invention also includes a
一方、本発明の他の態様による２以上の内部電極を含むケーブル型二次電池は、互いに平行に配置された２以上の内部電極；前記内部電極の外面を一緒に囲んで形成され、電極の短絡を防止する分離層；及び前記分離層の外面を囲んで螺旋状に巻き取られて形成された外部電極；を含み、前記内部電極及び前記外部電極の１種以上が上述した本発明の二次電池用電極で形成される。 Meanwhile, a cable type secondary battery including two or more internal electrodes according to another aspect of the present invention includes two or more internal electrodes disposed in parallel to each other; A separation layer that prevents a short circuit; and an external electrode that is wound around the outer surface of the separation layer in a spiral shape, and at least one of the internal electrode and the external electrode is the above-described two of the present invention. It is formed with a secondary battery electrode.
さらに、本発明のさらに他の態様による２以上の内部電極を含むケーブル型二次電池は、電解質を含む２以上のリチウムイオン供給コア部；それぞれの前記リチウムイオン供給コア部の外面を囲んで形成され、集電体及び電極活物質層を備えて互いに平行に配置される２以上の内部電極；前記内部電極の外面を一緒に囲んで形成され、電極の短絡を防止する分離層；及び前記分離層の外面を囲んで螺旋状に巻き取られて形成され、集電体及び電極活物質層を備える外部電極；を含み、前記内部電極及び前記外部電極の１種以上が上述した本発明の二次電池用電極で形成される。 Furthermore, a cable type secondary battery including two or more internal electrodes according to still another aspect of the present invention includes two or more lithium ion supply core parts including an electrolyte; and surrounds the outer surface of each of the lithium ion supply core parts. Two or more internal electrodes arranged in parallel to each other with a current collector and an electrode active material layer; a separation layer formed by surrounding the outer surfaces of the internal electrodes together to prevent a short circuit of the electrodes; and the separation An external electrode having a current collector and an electrode active material layer formed around the outer surface of the layer and having a current collector and an electrode active material layer. It is formed with a secondary battery electrode.
前記２以上の内部電極を含むケーブル型二次電池のうち、図９は内部電極に上述した本発明の二次電池用電極が導入されたケーブル型二次電池２００を示している。
Among the cable-type secondary batteries including two or more internal electrodes, FIG. 9 shows a cable-type
図９を参照すれば、電解質を含む２以上のリチウムイオン供給コア部２１０；それぞれの前記リチウムイオン供給コア部２１０の外面を囲んで巻き取られて形成され、互いに平行に配置される２以上の内部電極；前記内部電極の外面を一緒に囲んで形成され、電極の短絡を防止する分離層２７０；及び前記分離層２７０の外面を囲んで螺旋状に巻き取られて形成され、外部集電体２９０及び外部電極活物質層２８０を備える外部電極；を含み、前記内部電極は、内部集電体２２０、前記内部集電体２２０の一面に形成された内部電極活物質層２３０、前記内部電極活物質層２３０の上面に形成され、無機物粒子及びバインダー高分子を含む有無機多孔性層２４０、前記有無機多孔性層２４０の上面に形成された多孔性の第１支持層２５０、及び前記内部集電体２２０の他面に形成された第２支持層２６０を含む。
Referring to FIG. 9, two or more lithium
上述したように、内部電極ではなく外部電極が上述した本発明のシート型の二次電池用電極であっても良く、内部電極と外部電極ともに本発明のシート型の二次電池用電極で形成されても良い。 As described above, the external electrode instead of the internal electrode may be the above-described sheet-type secondary battery electrode of the present invention, and both the internal electrode and the external electrode are formed of the sheet-type secondary battery electrode of the present invention. May be.
このようなケーブル型二次電池２００は、複数の電極からなる内部電極を備えるため、内部電極の個数を調節することで電極活物質層のローディング量及び電池容量の調整が容易であり、複数の電極を備えることで断線の可能性を防止することができる。
Since the cable-type
なお、本明細書及び図面に開示された本発明の実施例は、理解を助けるために提示された特定例に過ぎず、本発明の範囲を限定するものではない。ここに開示された実施例の外にも本発明の技術的思想に基づいた他の変形例が実施可能であるということは、本発明が属する技術分野で通常の知識を持つ者にとって自明であろう。 It should be noted that the embodiments of the present invention disclosed in this specification and the drawings are merely specific examples presented for the sake of understanding, and do not limit the scope of the present invention. It is obvious to those skilled in the art to which the present invention belongs that other variations based on the technical idea of the present invention can be implemented in addition to the embodiments disclosed herein. Let's go.
１０ 集電体
２０ 電極活物質層
３０ 有無機多孔性層
３０' 有無機混合スラリー
４０ 第１支持層
５０ 第２支持層
６０ コーティングブレード
１００、２００ ケーブル型二次電池
１１０、２１０ リチウムイオン供給コア部
１２０、２２０ 内部集電体
１３０、２３０ 内部電極活物質層
１４０、２４０ 有無機多孔性層
１５０、２５０ 第１支持層
１６０、２６０ 第２支持層
１７０、２７０ 分離層
１８０、２８０ 外部電極活物質層
１９０、２９０ 外部集電体
１９５、２９５ 保護被覆
DESCRIPTION OF
Claims (67)
前記集電体の一面に形成された電極活物質層；
前記電極活物質層上に形成され、無機物粒子及びバインダー高分子を含む有無機多孔性層；及び
前記有無機多孔性層上に形成された多孔性の第１支持層；を含むシート型の二次電池用電極。 Current collector;
An electrode active material layer formed on one surface of the current collector;
A sheet-type two layer formed on the electrode active material layer and including an organic / inorganic porous layer containing inorganic particles and a binder polymer; and a porous first support layer formed on the organic / inorganic porous layer. Secondary battery electrode.
前記二次電池用電極が正極として用いられる場合、前記電極活物質層は、ＬｉＣｏＯ2、ＬｉＮｉＯ2、ＬｉＭｎ2Ｏ4、ＬｉＣｏＰＯ4、ＬｉＦｅＰＯ 4 、及びＬｉＮｉ1-x-y-zＣｏxＭ１yＭ２zＯ2（Ｍ１及びＭ２は互いに独立して、Ａｌ、Ｎｉ、Ｃｏ、Ｆｅ、Ｍｎ、Ｖ、Ｃｒ、Ｔｉ、Ｗ、Ｔａ、Ｍｇ及びＭｏからなる群より選択され、ｘ、ｙ及びｚは互いに独立した酸化物組成元素の原子分率であって、０≦ｘ＜０．５、０≦ｙ＜０．５、０≦ｚ＜０．５、０＜ｘ＋ｙ＋ｚ≦１である）からなる群より選択されたいずれか１つの活物質またはこれらのうち２種以上の混合物を含む請求項１〜２８のいずれか一項に記載の二次電池用電極。 When the secondary battery electrode is used as a negative electrode, the electrode active material layer includes natural graphite, artificial graphite, or carbonaceous material; lithium-containing titanium composite oxide (LTO); Si, Sn, Li, Zn, Mg, Metals (Me) which are Cd, Ce, Ni or Fe; alloys of the metals (Me); oxides of the metals (Me) (MeOx); and composites of the metals (Me) and carbon Any one active material selected from the group consisting of the body or a mixture of two or more thereof,
When the secondary battery electrode is used as a positive electrode, the electrode active material layer includes LiCoO 2 , LiNiO 2 , LiMn 2 O 4 , LiCoPO 4 , LiFePO 4 , and LiNi 1-xyz Co x M1 y M2 z O 2. (M1 and M2 are independently selected from the group consisting of Al, Ni, Co, Fe, Mn, V, Cr, Ti, W, Ta, Mg and Mo, and x, y and z are oxidations independent of each other. The atomic fraction of the compositional element is selected from the group consisting of 0 ≦ x <0.5, 0 ≦ y <0.5, 0 ≦ z <0.5, and 0 < x + y + z ≦ 1) The electrode for secondary batteries as described in any one of Claims 1-28 containing any one active material or 2 or more types of mixtures among these.
（Ｓ２）前記電極活物質層上に、無機物粒子及びバインダー高分子を含む有無機混合スラリーを塗布する工程；
（Ｓ３）前記塗布された有無機混合スラリー上に多孔性の第１支持層を形成する工程；及び
（Ｓ４）前記（Ｓ３）工程の結果物を圧迫し、前記電極活物質層と前記第１支持層との間に接着して互いに一体化した有無機多孔性層を形成する工程；を含むシート型二次電池用電極の製造方法。 (S1) A step of applying a slurry containing an electrode active material to one surface of the current collector and drying to form an electrode active material layer;
(S2) A step of applying a presence / absence machine mixed slurry containing inorganic particles and a binder polymer on the electrode active material layer;
(S3) forming a porous first support layer on the coated presence / absence machine mixed slurry; and (S4) pressing the result of the (S3) step, the electrode active material layer and the first A method for producing an electrode for a sheet-type secondary battery, comprising: forming a presence / absence porous layer that is bonded to a support layer and integrated with each other.
前記正極及び前記負極の少なくとも１つが、請求項１ないし請求項２９のうちいずれか１項に記載の二次電池用電極である二次電池。 In a secondary battery including a positive electrode, a negative electrode, a separator interposed between the positive electrode and the negative electrode, and a non-aqueous electrolyte,
30. A secondary battery in which at least one of the positive electrode and the negative electrode is an electrode for a secondary battery according to any one of claims 1 to 29.
前記内部電極の外面を囲み、電極の短絡を防止する分離層；及び
前記分離層の外面を囲んで螺旋状に巻き取られて形成された外部電極；を含み、
前記内部電極及び前記外部電極の１つ以上が、請求項１ないし請求項２９のうちいずれか１項に記載の二次電池用電極を用いて形成されるケーブル型二次電池。 Internal electrodes;
A separation layer that surrounds an outer surface of the internal electrode and prevents a short circuit of the electrode; and an external electrode that is formed by being spirally wound around the outer surface of the separation layer;
30. A cable-type secondary battery in which one or more of the internal electrode and the external electrode are formed using the secondary battery electrode according to any one of claims 1 to 29.
前記リチウムイオン供給コア部の外面を囲んで螺旋状に巻き取られて形成され、集電体及び電極活物質層を備える内部電極；
前記内部電極の外面を囲み、電極の短絡を防止する分離層；及び
前記分離層の外面を囲んで螺旋状に巻き取られて形成され、集電体及び電極活物質層を備える外部電極；を含み、
前記内部電極及び前記外部電極の１つ以上が、請求項１ないし請求項２９のうちいずれか１項に記載の二次電池用電極から形成されるケーブル型二次電池。 A lithium ion supply core containing an electrolyte;
An internal electrode formed by surrounding the outer surface of the lithium ion supply core and spirally wound, and comprising a current collector and an electrode active material layer;
A separation layer that surrounds the outer surface of the internal electrode and prevents a short circuit of the electrode; and an external electrode that is formed by being spirally wound around the outer surface of the separation layer and includes a current collector and an electrode active material layer; Including
30. A cable-type secondary battery in which one or more of the internal electrode and the external electrode are formed from the secondary battery electrode according to any one of claims 1 to 29.
前記内部電極の外面を囲み、電極の短絡を防止する分離層；及び
前記分離層の外面を囲んで螺旋状に巻き取られている外部電極；を含み、
前記内部電極及び前記外部電極の１つ以上が、請求項１ないし請求項２９のうちいずれか１項に記載の二次電池用電極を用いて形成されるケーブル型二次電池。 Two or more internal electrodes arranged parallel to each other;
A separation layer that surrounds the outer surface of the internal electrode and prevents a short circuit of the electrode; and an outer electrode that is wound in a spiral around the outer surface of the separation layer;
30. A cable-type secondary battery in which one or more of the internal electrode and the external electrode are formed using the secondary battery electrode according to any one of claims 1 to 29.
前記リチウムイオン供給コア部それぞれの外面を囲み、集電体及び電極活物質層をそれぞれ備えて互いに平行に配置される２以上の内部電極；
前記内部電極の外面を囲み、電極の短絡を防止する分離層；及び
前記分離層の外面を囲んで螺旋状に巻き取られて形成され、集電体及び電極活物質層を備える外部電極；を含み、
前記内部電極及び前記外部電極の１つ以上が、請求項１ないし請求項２９のうちいずれか１項に記載の二次電池用電極で形成されるケーブル型二次電池。 Two or more lithium ion supply cores containing electrolyte;
Two or more internal electrodes that surround the outer surface of each of the lithium ion supply cores and are arranged in parallel with each other, each including a current collector and an electrode active material layer;
A separation layer that surrounds the outer surface of the internal electrode and prevents a short circuit of the electrode; and an external electrode that is formed by being spirally wound around the outer surface of the separation layer and includes a current collector and an electrode active material layer; Including
30. A cable-type secondary battery in which one or more of the internal electrode and the external electrode are formed of the secondary battery electrode according to any one of claims 1 to 29.