JP5909916B2 - Resin production method, thermosetting resin composition, prepreg and laminate - Google Patents
Resin production method, thermosetting resin composition, prepreg and laminate Download PDFInfo
- Publication number
- JP5909916B2 JP5909916B2 JP2011172359A JP2011172359A JP5909916B2 JP 5909916 B2 JP5909916 B2 JP 5909916B2 JP 2011172359 A JP2011172359 A JP 2011172359A JP 2011172359 A JP2011172359 A JP 2011172359A JP 5909916 B2 JP5909916 B2 JP 5909916B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- component
- resin
- parts
- reaction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、低熱膨張性、銅箔接着性、耐熱性、難燃性、銅付き耐熱性（Ｔ-３００）、誘電特性、ドリル加工性に優れる熱硬化性樹脂組成物が得られる樹脂の製造法、熱硬化性樹脂組成物、プリプレグ及び積層板に関する。 The present invention is, low thermal expansion, a copper foil adhesive property, heat resistance, flame retardancy, copper with heat resistance (T-300), dielectric properties, tree fat that thermosetting resin composition excellent in drilling processability is obtained The manufacturing method, thermosetting resin composition, prepreg and laminate.
熱硬化性樹脂組成物は、架橋構造を有し、高い耐熱性や寸法安定性を発現するため、電子部品等の分野において広く使われる。特に銅張積層板や層間絶縁材料においては、近年の高密度化や高信頼性への要求から、高い銅箔接着性や耐熱性、良好な低熱膨張性等の特性を有することが必要とされる。 Thermosetting resin compositions have a cross-linked structure and exhibit high heat resistance and dimensional stability, and thus are widely used in the field of electronic components and the like. In particular, copper-clad laminates and interlayer insulation materials are required to have characteristics such as high copper foil adhesion, heat resistance, and good low thermal expansion due to the recent demand for higher density and higher reliability. The
即ち、積層板材料には近年の高密度化や高信頼性への要求から、高い銅箔接着性や耐熱性、良好な低熱膨張性等が必要とされるが、微細配線形成のため銅箔接着性は、銅箔ピール強度が１．０ｋＮ／ｍ以上であることが望ましく、１．２ｋＮ／ｍ以上であることがより望ましい。また、高密度化のためビルドアップ材等を用いてより高多層化することも必要であり、高いリフロー耐熱性が必要であるが、リフロー耐熱性評価の指針となる銅付き耐熱性（Ｔ−３００）は、３０分以上ふくれ等が生じないことが望ましい。 In other words, due to recent demands for higher density and higher reliability, laminated board materials require high copper foil adhesion, heat resistance, good low thermal expansion, etc. As for the adhesiveness, the copper foil peel strength is desirably 1.0 kN / m or more, and more desirably 1.2 kN / m or more. In addition, it is necessary to increase the number of layers using a build-up material or the like for high density, and high reflow heat resistance is required. However, heat resistance with copper (T- 300) is preferably free from blistering for 30 minutes or more.
さらに、積層板材料の高密度化に伴い基材はより薄型化される方向にあり、熱処理時における基材のそりが小さいことが必要となる。低そり化のためには基材の面方向が低熱膨張性であることが有効であり、その線膨張係数は７ｐｐｍ／℃以下であることが望ましく、５ｐｐｍ／℃以下であることがより望ましい。また、高密度化に伴い基材はより信頼性が要求される方向にあり、ドリル加工時のドリル穴の内壁粗さも小さいことが必要となる。ドリル穴の内壁粗さの評価は、めっき銅の染み込み性により評価され、めっき染み込み長さの最大が２０μｍ以下であることが望ましく、１５μｍ以下であることがより望ましい。さらに、高速応答性の要求も増え続けており、基材の比誘電率は４．７以下であること、また誘電正接は０．０１０以下であることが望ましい。 Furthermore, as the density of the laminated plate material increases, the base material tends to be thinner, and the warp of the base material during heat treatment needs to be small. In order to reduce warpage, it is effective that the surface direction of the substrate has a low thermal expansion, and the linear expansion coefficient is preferably 7 ppm / ° C. or less, more preferably 5 ppm / ° C. or less. Further, as the density is increased, the base material is in a direction that requires more reliability, and the inner wall roughness of the drill hole during drilling is required to be small. The evaluation of the inner wall roughness of the drill hole is evaluated by the penetration property of the plated copper, and the maximum plating penetration length is desirably 20 μm or less, and more desirably 15 μm or less. Furthermore, the demand for high-speed response continues to increase, and it is desirable that the relative dielectric constant of the base material is 4.7 or less and the dielectric loss tangent is 0.010 or less.
このように積層板材料の高密度化や高信頼性への要求から、絶縁樹脂として用いられる熱硬化性樹脂組成物は高度の特性が要求されており、これらの特性を全て満たす樹脂組成物の開発が進められている。
また、近年の環境問題から、鉛フリーはんだによる電子部品の搭載やハロゲンフリーによる難燃化が要求され、そのため従来のものよりも高い耐熱性及び難燃性が必要とされる。さらに、製品の安全性や作業環境の向上化のため、毒性の低い成分のみで構成され、毒性ガス等が発生しない熱硬化性樹脂組成物が望まれている。
As described above, the thermosetting resin composition used as the insulating resin is required to have a high level of properties because of the demand for higher density and high reliability of the laminated board material, and the resin composition satisfying all these characteristics is required. Development is underway.
Moreover, due to recent environmental problems, mounting of electronic parts using lead-free solder and flame resistance using halogen-free are required, and therefore higher heat resistance and flame resistance than conventional ones are required. Furthermore, in order to improve the safety of the product and the working environment, there is a demand for a thermosetting resin composition that is composed only of low-toxic components and does not generate toxic gases.
熱硬化性樹脂であるシアネート化合物は、誘電特性、難燃性に優れる樹脂であるが、エポキシ硬化系の熱硬化性樹脂にそのまま使用した場合、耐熱性や強靭性が充分でなく、また、次世代に対応する熱硬化性樹脂として更に低熱膨張性が望まれている。
このため、シアネート化合物と無機充填剤からなる低熱膨張性を発現させる樹脂組成物が開示されている（例えば、特許文献１、２および３参照）。しかし、これらは低熱膨張性を発現させるため無機充填剤の配合使用量が多く、銅張積層板や層間絶縁材料として使用した場合にドリル加工性や成形性が不足する。
Cyanate compound, which is a thermosetting resin, is a resin with excellent dielectric properties and flame retardancy, but when used as it is in an epoxy curable thermosetting resin, it does not have sufficient heat resistance and toughness. Further, low thermal expansion is desired as a thermosetting resin corresponding to the generation.
For this reason, the resin composition which expresses the low thermal expansibility which consists of a cyanate compound and an inorganic filler is disclosed (for example, refer patent document 1, 2, and 3). However, since these exhibit low thermal expansibility, the amount of inorganic filler used is large, and when used as a copper-clad laminate or an interlayer insulating material, drill workability and formability are insufficient.
また、低熱膨張性を発現させるためにシアネート樹脂とアラルキル変性エポキシ樹脂を必須成分として含有する熱硬化性樹脂が開示されている（例えば、特許文献４および５参照）。しかし、この必須成分であるシアネート樹脂が靭性や硬化反応性に劣る樹脂であるため、硬化反応性や強靭性の改良が依然不足であり、これらを銅張積層板や層間絶縁材料として使用した場合も、耐熱性や信頼性、加工性等が不足である。 In addition, thermosetting resins containing a cyanate resin and an aralkyl-modified epoxy resin as essential components in order to exhibit low thermal expansibility are disclosed (for example, see Patent Documents 4 and 5). However, since the cyanate resin, which is an essential component, is a resin with poor toughness and curing reactivity, improvement in curing reactivity and toughness is still insufficient, and when these are used as copper-clad laminates and interlayer insulation materials However, heat resistance, reliability, workability, etc. are insufficient.
本発明の目的は、こうした現状に鑑み、熱硬化性樹脂であるシアネート化合物を用いる場合の上記問題点を解決し、低熱膨張性、銅箔接着性、耐熱性、難燃性、銅付き耐熱性（Ｔ-３００）、誘電特性、ドリル加工性の全てに優れる熱硬化性樹脂組成物、及びこれを用いたプリプレグ、積層板及び配線板を提供することである。 In view of the current situation, the object of the present invention is to solve the above-mentioned problems when using a cyanate compound that is a thermosetting resin, low thermal expansion, copper foil adhesion, heat resistance, flame resistance, and heat resistance with copper. (T-300), a thermosetting resin composition excellent in all of dielectric properties and drill workability, and a prepreg, a laminate and a wiring board using the same.
本発明は、上記の課題を解決するために鋭意研究した結果、シアネート化合物と末端に水酸基を有するシロキサン樹脂及びエポキシ樹脂を特定の反応率に反応させて得られる樹脂（Ａ）とトリメトキシシラン化合物により表面処理された溶融シリカ（Ｂ）を含有する樹脂組成物を用いることにより、上記のような特性を有する優れた熱硬化性樹脂組成物が得られること見出し、本発明を完成するに至った。本発明は、かかる知見に基づいて完成したものである。
即ち本発明は、以下の樹脂の製造方法、熱硬化性樹脂組成物、プリプレグ、積層板及び配線板を提供するものである。
The present invention is a result of intensive study to solve the above problems, the cyanate compound and terminated siloxane resin and an epoxy resin having a hydroxyl group is reacted to a specific reaction rate obtained that tree fat (A) trimethoxy To find out that an excellent thermosetting resin composition having the above-mentioned characteristics can be obtained by using a resin composition containing fused silica (B) surface-treated with a silane compound, and to complete the present invention. It came. The present invention has been completed based on such findings.
That is, the present invention provides a method of manufacturing the following tree butter, thermosetting resin composition, there is provided a prepreg, a laminated board and a wiring board.
１．下記一般式（Ｉ）で示される末端に水酸基を有するシロキサン樹脂（ａ）、１分子中に少なくとも２個のシアネート基を有する化合物（ｂ）及び１分子中に少なくとも２個のエポキシ基を有する化合物（ｃ）を、（ａ）〜（ｃ）成分の合計量１００質量部当たり、（ａ）成分１０〜５０質量部、（ｂ）成分４０〜８０質量部、（ｃ）成分１０〜５０質量部として、有機金属塩（ｄ）の存在下、トルエン、キシレン及びメシチレンから選ばれる溶媒中で８０〜１２０℃で反応させ、（ｂ）成分の反応率が３０〜７０モル％であることを特徴とするイミノカーボネート構造及びトリアジン構造を有する樹脂の製造方法。 1. A siloxane resin having a hydroxyl group at the terminal represented by the following general formula (I) (a), a compound (b) having at least two cyanate groups in one molecule, and a compound having at least two epoxy groups in one molecule (C) per 100 parts by mass of the total amount of components (a) to (c), (a) component 10 to 50 parts by mass, (b) component 40 to 80 parts by mass, (c) component 10 to 50 parts by mass The reaction is carried out at 80 to 120 ° C. in a solvent selected from toluene, xylene and mesitylene in the presence of the organometallic salt (d), and the reaction rate of the component (b) is 30 to 70 mol%. imino carbonates structure and tree butter manufacturing method of that having a triazine structure are.
２．上記１の方法により製造された樹脂（Ａ）及び、下記式（II）で示されるトリメトキシシラン化合物により表面処理された溶融シリカ（Ｂ）を含有することを特徴とする熱硬化性樹脂組成物。
３．上記２の熱硬化性樹脂組成物を基材中に含浸又は塗工した後、Ｂステージ化したプリプレグ。
４．上記３のプリプレグを用いて形成された積層板。
3. After containing immersion or coating a thermosetting resin composition of the two in the substrate, B-staged prepreg.
4). A laminate formed by using the prepreg of 3 above.
本発明の熱硬化性樹脂組成物を基材に含浸、又は塗工して得たプリプレグ、及び該プリプレグを積層成形することにより製造した積層板は、低熱膨張性、銅箔接着性、耐熱性、難燃性、銅付き耐熱性（Ｔ-３００）、誘電特性、ドリル加工性の全てに優れ、環境問題がなく、製品の安全性にも優れることから、電子機器用プリント配線板として極めて有用である。 A prepreg obtained by impregnating or coating a base material with the thermosetting resin composition of the present invention, and a laminate produced by laminating the prepreg, have low thermal expansion, copper foil adhesion, heat resistance. , Flame retardant, heat resistance with copper (T-300), dielectric properties, drilling workability, no environmental problems, and excellent product safety It is.
以下、本発明について詳細に説明する。
先ず、本発明の樹脂の製造方法は、下記一般式（Ｉ）で示される末端に水酸基を有するシロキサン樹脂（ａ）、１分子中に少なくとも２個のシアネート基を有する化合物（ｂ）及び１分子中に少なくとも２個のエポキシ基を有する化合物（ｃ）を、（ａ）〜（ｃ）成分の合計量１００質量部当たり、（ａ）成分１０〜５０質量部、（ｂ）成分４０〜８０質量部、（ｃ）成分１０〜５０質量部として、有機金属塩（ｄ）の存在下、トルエン、キシレン及びメシチレンから選ばれる溶媒中で８０〜１２０℃でイミノカーボネート化反応及びトリアジン環形成反応をさせ、（ｂ）成分の反応率が３０〜７０モル％であることを特徴とする方法である。
Hereinafter, the present invention will be described in detail.
First, the method of producing dendritic fat of the present invention, a siloxane resin having a hydroxyl group at the end represented by the following general formula (I) (a), a compound having at least two cyanate groups per molecule (b) and 1 Compound (c) having at least two epoxy groups in the molecule is composed of (a) component (10) to 50 parts by mass and (b) component 40 to 80 per 100 parts by mass of the total amount of components (a) to (c). In the presence of the organometallic salt (d), the iminocarbonate reaction and the triazine ring formation reaction are carried out at 80 to 120 ° C. in a solvent selected from toluene, xylene and mesitylene, as 10 to 50 parts by mass of the component (c). The reaction rate of component (b) is 30 to 70 mol%.
本発明の樹脂の製造に用いられる（ａ）成分のシロキサン樹脂は、上記一般式（Ｉ）で示される構造の水酸基を含有するシロキサン樹脂であれば特に限定されない。例えば両末端がフェノール性水酸基である信越化学工業（株）製の商品名Ｘ−２２−１８２１（水酸基価：３５ＫＯＨｍｇ/ｇ）、商品名Ｘ−２２−１８２２（水酸基価：２０ＫＯＨｍｇ/ｇ）、東レ・ダウコーニング（株）製の商品名ＢＹ１６−７５２Ａ（水酸基価：３０ＫＯＨｍｇ/ｇ）、及び両末端がアルコール性水酸基である信越化学工業（株）製の商品名Ｘ−２２−１６０ＡＳ（水酸基価：１１２ＫＯＨｍｇ/ｇ）、商品名ＫＦ−６００１（水酸基価：６２ＫＯＨｍｇ/ｇ）、商品名ＫＦ−６００２（水酸基価：３５ＫＯＨｍｇ/ｇ）、商品名ＫＦ−６００３（水酸基価：２０ＫＯＨｍｇ/ｇ）、商品名Ｘ−２２−４０１５（水酸基価：２７ＫＯＨｍｇ/ｇ）等が挙げられる。 Used in the manufacture of wood fat of the present invention component (a) of siloxane resin is not particularly limited as long as the siloxane resin containing a hydroxyl group in the structure represented by the general formula (I). For example, trade names X-22-1821 (hydroxyl value: 35 KOHmg / g), trade names X-22-1822 (hydroxyl value: 20 KOHmg / g) manufactured by Shin-Etsu Chemical Co., Ltd., which are both phenolic hydroxyl groups, Toray -Trade name BY16-752A (hydroxyl value: 30 KOHmg / g) manufactured by Dow Corning Co., Ltd., and trade name X-22-160AS (hydroxyl value: manufactured by Shin-Etsu Chemical Co., Ltd.) where both ends are alcoholic hydroxyl groups. 112 KOH mg / g), trade name KF-6001 (hydroxyl value: 62 KOH mg / g), trade name KF-6002 (hydroxyl value: 35 KOH mg / g), trade name KF-6003 (hydroxyl value: 20 KOH mg / g), trade name X -22-4015 (hydroxyl value: 27 KOHmg / g).
本発明の樹脂の製造に用いられる（ｂ）成分の１分子中に少なくとも２個のシアネート基を有する化合物としては、例えば、ノボラック型シアネート樹脂、ビスフェノールＡ型シアネート樹脂、ビスフェノールＥ型シアネート樹脂、ビスフェノールＦ型シアネート樹脂、テトラメチルビスフェノールＦ型シアネート樹脂等が挙げられ、１種又は２種以上を混合して使用することができる。これらの中で、誘電特性、耐熱性、難燃性、低熱膨張性、及び安価である点から、ビスフェノールＡ型シアネート樹脂、下記一般式（III）に示すノボラック型シアネート樹脂が特に好ましい。 Examples of the compound having at least two cyanate groups in one molecule of the component (b) used in the production of the resin of the present invention include novolac type cyanate resin, bisphenol A type cyanate resin, bisphenol E type cyanate resin, and bisphenol. F type cyanate resin, tetramethylbisphenol F type cyanate resin, etc. are mentioned, 1 type (s) or 2 or more types can be mixed and used. Among these, bisphenol A type cyanate resins and novolak type cyanate resins represented by the following general formula (III) are particularly preferred from the viewpoints of dielectric properties, heat resistance, flame retardancy, low thermal expansibility, and low cost.
上記の一般式（III）のｎは、ノボラック型シアネート樹脂の平均繰り返し数であり、特に限定されないが、平均値として０．１〜３０が好ましい。これより小さいと結晶化しやすくなり取り扱いが困難となる場合がある。また、これより大きいと硬化物が脆くなる場合がある。 N in the above general formula (III) is the average number of repeats of the novolak-type cyanate resin and is not particularly limited, but is preferably 0.1 to 30 as an average value. If it is smaller than this, it may be easy to crystallize and it may be difficult to handle. Moreover, when larger than this, hardened | cured material may become weak.
本発明の樹脂の製造に用いられる（ｃ）成分の１分子中に少なくとも２個のエポキシ基を有する化合物としては、例えば、ビスフェノールＡ系、ビスフェノールＦ系、ビフェニル系、ノボラック系、多官能フェノール系、ナフタレン系、脂環式系及びアルコール系等のグリシジルエーテル系、グリシジルアミン系並びにグリシジルエステル系等が挙げられ、１種又は２種以上を混合して使用することができる。
これらの中で、高剛性、誘電特性、耐熱性、難燃性、耐湿性及び低熱膨張性の点からナフタレン型エポキシ樹脂、ナフトールアラルキル型エポキシ樹脂、ジヒドロキシナフタレンアラルキル型エポキシ樹脂、ナフトールアラルキル・クレゾール共重合型エポキシ樹脂等のナフタレン環含有エポキシ樹脂、ビフェニル型エポキシ樹脂、ビフェニルアラルキル型エポキシ樹脂等のビフェニル基含有エポキシ樹脂が好ましく、芳香族系有機溶剤への溶解性の点からナフトールアラルキル型エポキシ樹脂、ナフトールアラルキル・クレゾール共重合型エポキシ樹脂、ビフェニル型エポキシ樹脂がより好ましく、安価であることやエポキシ当量が小さく少量の配合でよいことから、下記式（IV）に示すビフェニル型エポキシ樹脂が特に好ましい。
Examples of the compound having at least two epoxy groups in one molecule of the component (c) used for producing the resin of the present invention include, for example, bisphenol A, bisphenol F, biphenyl, novolac, and polyfunctional phenol. These include glycidyl ethers such as naphthalene, alicyclic and alcohols, glycidylamines and glycidyl esters, and can be used alone or in combination.
Among these, naphthalene type epoxy resin, naphthol aralkyl type epoxy resin, dihydroxynaphthalene aralkyl type epoxy resin, naphthol aralkyl cresol and naphthol aralkyl / cresol are used in terms of high rigidity, dielectric properties, heat resistance, flame resistance, moisture resistance and low thermal expansion. Naphthalene ring-containing epoxy resins such as polymerization type epoxy resins, biphenyl type epoxy resins, biphenyl group-containing epoxy resins such as biphenyl aralkyl type epoxy resins are preferred, and naphthol aralkyl type epoxy resins from the viewpoint of solubility in aromatic organic solvents, A naphthol aralkyl / cresol copolymer type epoxy resin and a biphenyl type epoxy resin are more preferable, and a biphenyl type epoxy resin represented by the following formula (IV) is particularly preferable because it is inexpensive and has a small epoxy equivalent and may contain a small amount.
本発明の樹脂の製造方法において、原料組成を（ａ）〜（ｃ）成分の合計量１００質量部当たり、（ａ）成分１０〜５０質量部、（ｂ）成分４０〜８０質量部、（ｃ）成分１０〜５０質量部として、有機金属塩（ｄ）の存在下、トルエン、キシレン及びメシチレンから選ばれる溶媒中で８０〜１２０℃で反応させ、（ｂ）成分の反応率が３０〜７０モル％とする。
（ｄ）成分の有機金属塩は反応触媒となるものであり、例えば、ナフテン酸亜鉛、ナフテン酸コバルト、オクチル酸錫、オクチル酸コバルト等が挙げられる。アミン系やイミダゾール系の窒素原子含有反応触媒は得られる樹脂の硬化物が脆くなり、耐熱性や接着性が低下するので好ましくない。
In the resin production method of the present invention, the raw material composition is (a) component 10 to 50 parts by mass, (b) component 40 to 80 parts by mass, (c) per 100 parts by mass of the total amount of components (a) to (c). ) In the presence of the organometallic salt (d) as component 10-50 parts by mass, the reaction is carried out in a solvent selected from toluene, xylene and mesitylene at 80-120 ° C., and the reaction rate of component (b) is 30-70 mol. %.
The organometallic salt of component (d) serves as a reaction catalyst, and examples thereof include zinc naphthenate, cobalt naphthenate, tin octylate, and cobalt octylate. An amine-based or imidazole-based nitrogen atom-containing reaction catalyst is not preferable because a cured resin obtained is brittle and heat resistance and adhesiveness are lowered.
即ち、本発明の樹脂の製造方法は（ａ）〜（ｃ）成分を予めトルエン、キシレン及びメシチレンから選ばれる溶媒中に均一に溶解し、８０〜１２０℃の反応温度でイミノカーボネ−ト化反応、及びトリアジン環化反応させ、シアネート基を有する化合物（ｂ）の反応率を３０〜７０モル％となるようにプレ反応を行うものである。
ここで、反応溶媒にはトルエン、キシレン及びメシチレンから選ばれる芳香族系溶媒を用いる。必要により少量の他の溶剤を用いてもよいが、他の溶剤では所望の反応が進行せず、耐熱性等が低下する。また、ベンゼンは毒性が強く、メシチレンよりも分子量の大きい芳香族系溶媒はプリプレグの製造塗工時に残溶剤となりやすいので好ましくない。
That is, the manufacturing method of the tree fat of the present invention is uniformly dissolved in a solvent selected from the advance toluene, xylene and mesitylene (a) ~ (c) component, Iminokabone at a reaction temperature of 80 to 120 ° C. - DOO reaction And a triazine cyclization reaction, and a pre-reaction is performed so that the reaction rate of the compound (b) having a cyanate group is 30 to 70 mol%.
Here, an aromatic solvent selected from toluene, xylene and mesitylene is used as the reaction solvent. A small amount of other solvent may be used if necessary, but the desired reaction does not proceed with the other solvent, and heat resistance and the like are lowered. In addition, benzene is highly toxic, and an aromatic solvent having a molecular weight larger than that of mesitylene is not preferable because it tends to be a residual solvent during prepreg production coating.
なお、イミノカーボネ−ト化反応は、水酸基とシアネート基の付加反応によりイミノカーボネ−ト結合（−Ｏ−（Ｃ＝ＮＨ）−Ｏ−）が生成される反応であり、トリアジン環化反応は、シアネート基が３量化しトリアジン環を形成する反応である。また、このシアネート基が３量化しトリアジン環を形成する反応により３次元網目構造化が進行するが、この時、１分子中に少なくとも２個のエポキシ基を有する化合物（ｃ）が３次元網目構造中に均一に分散され、これによって（ａ）成分、（ｂ）成分及び（ｃ）成分が均一に分散された樹脂が製造される。 The iminocarbonation reaction is a reaction in which an iminocarbonate bond (—O— (C═NH) —O—) is generated by the addition reaction of a hydroxyl group and a cyanate group, and the triazine cyclization reaction is a cyanate group. Is a reaction to form a triazine ring by trimerization. In addition, a three-dimensional network structure is formed by a reaction in which the cyanate group is trimerized to form a triazine ring. At this time, the compound (c) having at least two epoxy groups in one molecule is converted into a three-dimensional network structure. are uniformly dispersed in, whereby component (a), (b) component and (c) tree butter component is uniformly dispersed can be produced.
本発明の樹脂の製造における原料組成は（ａ）〜（ｃ）成分の合計量１００質量部当たり、（ａ）成分１０〜５０質量部、（ｂ）成分４０〜８０質量部、（ｃ）成分１０〜５０質量部であり、（ａ）成分１０〜３０質量部、（ｂ）成分５０〜７０質量部、（ｃ）成分１０〜４０質量部とすることが好ましい。ここで、（ａ）成分が１０質量部未満であると、得られる基材の面方向の低熱膨張性が低下する場合があり、また（ａ）成分が５０質量部を超えると、耐熱性や耐薬品性が低下する場合がある。（ｂ）成分が４０質量部未満であると得られる樹脂の相容性が低下する場合があり、また（ｂ）成分が８０質量部を超えると、得られる基材の面方向の低熱膨張性が低下する場合がある。（ｃ）成分が１０質量部未満であると、耐湿耐熱性が低下する場合があり、また（ｃ）成分が５０質量部を超えると、銅箔接着性や誘電特性が低下する場合がある。 The raw material composition in the production of the resin of the present invention is (a) component 10 to 50 parts by mass, (b) component 40 to 80 parts by mass, and (c) component per 100 parts by mass of the total amount of components (a) to (c). 10 to 50 parts by mass, preferably (a) component 10 to 30 parts by mass, (b) component 50 to 70 parts by mass, and (c) component 10 to 40 parts by mass. Here, when the component (a) is less than 10 parts by mass, the low thermal expansion in the surface direction of the obtained base material may be reduced, and when the component (a) exceeds 50 parts by mass, Chemical resistance may decrease. When the component (b) is less than 40 parts by mass, the compatibility of the obtained resin may be reduced, and when the component (b) exceeds 80 parts by mass, the low thermal expansion in the surface direction of the obtained substrate is obtained. May decrease. When the component (c) is less than 10 parts by mass, the moisture and heat resistance may be reduced, and when the component (c) is more than 50 parts by mass, the copper foil adhesion and dielectric properties may be reduced.
有機金属塩（ｄ）の使用量は、（ａ）〜（ｃ）成分の合計量１００質量部に対して、０．０００１〜０．００４質量部が好ましい。０．０００１質量部以上とすることにより、反応に長時間を要することなく所望の反応率に達することができる。また、０．００４質量部以下とすることにより、反応速度が速すぎて終点管理が難しくなることがない。ここで、シアネート基を有する化合物（ｂ）の反応率は、ＧＰＣ測定により反応開始時の（ｂ）のシアネート基を有する化合物のピーク面積と、所定時間反応後のピーク面積を比較し、ピーク面積の消失率から求められる。 The amount of the organic metal salt (d) used is preferably 0.0001 to 0.004 parts by mass with respect to 100 parts by mass of the total amount of the components (a) to (c). By setting it to 0.0001 parts by mass or more, a desired reaction rate can be achieved without requiring a long time for the reaction. Moreover, by setting it as 0.004 mass part or less, reaction rate is not too fast and end point management becomes difficult. Here, the reaction rate of the compound (b) having a cyanate group is determined by comparing the peak area of the compound having the cyanate group (b) at the start of the reaction with the peak area after reaction for a predetermined time by GPC measurement. It is calculated from the disappearance rate.
このようなプレ反応の反応温度は８０〜１２０℃であり、好ましくは１００〜１１０℃である。反応温度が８０℃未満であると製造時間（反応時間）が長くなりすぎる場合があり、１２０℃を超えるとエポキシ樹脂の副反応が生じるためゲル化する場合がある。
プレ反応の反応率は、シアネート基を有する化合物（ｂ）の反応率（消失率）を３０〜７０モル％となるようにし、好ましくは４０〜６８モル％となるようにする。反応率が３０モル％未満であると、得られる樹脂が相容化されておらず、樹脂が分離して白濁し、Ｂステージの塗工布が製造できない。また、反応率が７０モル％を超えると、得られる熱硬化性樹脂が溶剤に不溶化し、Ａステージのワニス（熱硬化性樹脂組成物）が製造できなくなったり、プリプレグのゲルタイムが短くなり過ぎ、プレスの際に成形性が低下する場合がある。
The reaction temperature of such a pre-reaction is 80 to 120 ° C, preferably 100 to 110 ° C. If the reaction temperature is less than 80 ° C., the production time (reaction time) may be too long, and if it exceeds 120 ° C., a side reaction of the epoxy resin occurs, which may cause gelation.
The reaction rate of the pre-reaction, and compounds having a cyanate group reaction rate of (b) a (loss rate) so as to be 30 to 70 mol%, preferably made to be 40 to 68 mol%. When the reaction rate is less than 30 mol%, the resulting resin has not been compatibilized resin is clouded separated, coated cloth in a B-stage is unable to manufacture. When the reaction rate exceeds 70 mol%, the resulting thermosetting resin is insolubilized in the solvent, and the A-stage varnish (thermosetting resin composition) cannot be produced, or the gel time of the prepreg becomes too short. Formability may be reduced during pressing.
本発明の熱硬化性樹脂組成物は、以上の方法により製造された樹脂（Ａ）及び、下記式（II）で示されるトリメトキシシラン化合物により表面処理された溶融シリカ（Ｂ）を含有することを特徴とするものである。 The thermosetting resin composition of the present invention, more trees fat produced by the method (A) and contains a surface-treated fused silica (B) by trimethoxysilane compound represented by the following formula (II) It is characterized by this.
（Ｂ）成分の表面処理された溶融シリカは、溶融シリカを上記の式（II）で示されるトリメトキシシラン化合物を使用し、表面処理することにより得られる。（Ｂ）成分は、例えば、メチルエチルケトン、メチルイソブチルケトン、シクロヘキサノン等のケトン系有機溶剤やエチレングリコールモノメチルエーテル、プロピレングリコールモノメチルエーテル等のアルコール系有機溶剤に、溶融シリカを添加して混合した後、上記の式（II）で示されるトリメトキシシラン化合物を添加して６０〜１２０℃で、０．５〜５時間程度攪拌しながら表面処理（湿式処理）させることにより得られる。該溶融シリカは、アドマテックス社等から商業的にも入手でき、例えば、アドマテックス社製の商品名ＳＣ-２０５０ＫＮＫや、ＳＣ-２０５０ＨＮＫ等がある。 The surface-treated fused silica of component (B) can be obtained by surface-treating fused silica using the trimethoxysilane compound represented by the above formula (II). (B) component, for example, after adding fused silica to a ketone organic solvent such as methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, or alcohol organic solvent such as ethylene glycol monomethyl ether, propylene glycol monomethyl ether, and the like, The trimethoxysilane compound represented by the formula (II) is added and subjected to surface treatment (wet treatment) at 60 to 120 ° C. with stirring for about 0.5 to 5 hours. The fused silica is also commercially available from Admatechs and others, for example, trade names SC-2050KNK and SC-2050HNK manufactured by Admatechs.
（Ｂ）成分の溶融シリカの使用量は、固形分換算の（Ａ）成分１００質量部に対し、１０〜３００質量部とすることが好ましく、１００〜２５０質量部とすることがより好ましく、１５０〜２５０質量部とすることが特に好ましい。１０質量部以上であることにより、基材の剛性や、耐湿耐熱性、難燃性が不足することがなく、また、３００質量部以下とすることにより、成形性や耐めっき液性等の耐薬品性が低下することがない。 The amount of component (B) fused silica used is preferably 10 to 300 parts by weight, more preferably 100 to 250 parts by weight, with respect to 100 parts by weight of component (A) in terms of solid content. It is especially preferable to set it as -250 mass parts. By being 10 parts by mass or more, the rigidity of the base material, moisture heat resistance, and flame resistance are not insufficient, and by being 300 parts by mass or less, resistance to moldability, plating solution resistance, etc. There is no deterioration in chemical properties.
本発明の熱硬化性樹脂組成物には、（Ｂ）成分以外の無機充填剤（Ｃ）を使用しても良い。無機充填剤（Ｃ）としては、例えば、破砕シリカ、マイカ、タルク、ガラス短繊維又は微粉末及び中空ガラス、炭酸カルシウム、石英粉末、金属水和物等が挙げられる。これらの中で、低熱膨張性や高弾性、耐熱性、難燃性の点から、水酸化アルミニウム、水酸化マグネシウム等の金属水和物が好ましい。さらに金属水和物の中でも、高い耐熱性と難燃性が両立する点から熱分解温度が３００℃以上である金属水和物、例えばベーマイト型水酸化アルミニウム（ＡｌＯＯＨ）、あるいはギブサイト型水酸化アルミニウム（Ａｌ(ＯＨ)３）を熱処理によりその熱分解温度を３００℃以上に調整した化合物、水酸化マグネシウム等がより好ましく、特に、安価であり、３５０℃以上の特に高い熱分解温度と、高い耐薬品性を有するベーマイト型水酸化アルミニウム（ＡｌＯＯＨ）が特に好ましい。 In the thermosetting resin composition of the present invention, an inorganic filler (C) other than the component (B) may be used. Examples of the inorganic filler (C) include crushed silica, mica, talc, short glass fiber or fine powder, hollow glass, calcium carbonate, quartz powder, and metal hydrate. Among these, metal hydrates such as aluminum hydroxide and magnesium hydroxide are preferable from the viewpoint of low thermal expansion, high elasticity, heat resistance, and flame retardancy. Furthermore, among metal hydrates, metal hydrates having a thermal decomposition temperature of 300 ° C. or higher, such as boehmite type aluminum hydroxide (AlOOH), or gibbsite type aluminum hydroxide, because both high heat resistance and flame retardancy are compatible. More preferred is a compound in which the thermal decomposition temperature of (Al (OH) 3) is adjusted to 300 ° C. or higher by heat treatment, magnesium hydroxide, etc., particularly inexpensive, a particularly high thermal decomposition temperature of 350 ° C. or higher, and a high resistance to resistance. Boehmite type aluminum hydroxide (AlOOH) having chemical properties is particularly preferable.
無機充填剤（Ｃ）の使用量は、固形分換算の（Ａ）成分１００質量部に対し、０〜２００質量部とすることが好ましく、１０〜１５０質量部とすることがより好ましく、５０〜１５０質量部とすることが特に好ましい。１０質量部以上であると難燃性が不足することがなく、２００質量部以下であると耐めっき液性等の耐薬品性や成形性が低下することがない。 The amount of the inorganic filler (C) used is preferably 0 to 200 parts by weight, more preferably 10 to 150 parts by weight, with respect to 100 parts by weight of the component (A) in terms of solid content. It is especially preferable to set it as 150 mass parts. If it is 10 parts by mass or more, the flame retardancy will not be insufficient, and if it is 200 parts by mass or less, chemical resistance such as plating solution resistance and moldability will not be reduced.
本発明の熱硬化性樹脂組成物には、耐熱性や難燃性、銅箔接着性等の向上化のため硬化促進剤を用いることが望ましく、硬化促進剤の例としては、ナフテン酸亜鉛、ナフテン酸コバルト、オクチル酸錫、オクチル酸コバルト等の有機金属塩、イミダゾール類及びその誘導体、第三級アミン類及び第四級アンモニウム塩等が挙げられる。硬化促進剤を使用することにより、耐熱性や難燃性、銅箔接着性等が不足することがない。 In the thermosetting resin composition of the present invention, it is desirable to use a curing accelerator for improving heat resistance, flame retardancy, copper foil adhesion, etc., examples of the curing accelerator include zinc naphthenate, Examples include organic metal salts such as cobalt naphthenate, tin octylate, and cobalt octylate, imidazoles and derivatives thereof, tertiary amines, and quaternary ammonium salts. By using a curing accelerator, heat resistance, flame retardancy, copper foil adhesion, etc. are not insufficient.
本発明の熱硬化性樹脂組成物には、任意に（Ｂ）、（Ｃ）成分以外の無機難燃助剤（Ｄ）の併用ができる。しかし、臭素や塩素を含有する含ハロゲン系難燃剤や熱分解温度が３００℃未満である金属水酸化物等は本発明の目的にそぐわないものである。
無機難燃助剤（Ｄ）の例としては、トリフェニルホスフェート、トリクレジルホスフェート、トリスジクロロプロピルホスフェート、リン酸エステル系化合物、ホスファゼン、赤リン等のリン系難燃剤、三酸化アンチモン、モリブデン酸亜鉛等の無機難燃助剤等が挙げられる。特に、モリブデン酸亜鉛をタルク等の無機充填剤に担持した無機難燃助剤は、難燃性のみならずドリル加工性をも著しく向上化させるので、特に好ましい無機難燃助剤である。モリブデン酸亜鉛の使用量は樹脂（Ａ）１００質量部に対し、５〜２０質量部とすることが好ましい。５質量部以上とすることにより、難燃性やドリル加工性が向上し、また２０質量部以下とすることにより、ワニスのゲルタイムが短くなり過ぎてプレスにより積層板を成形する際に成形性が低下することがない。
In the thermosetting resin composition of the present invention, an inorganic flame retardant aid (D) other than the components (B) and (C) can be arbitrarily used. However, halogen-containing flame retardants containing bromine and chlorine and metal hydroxides having a thermal decomposition temperature of less than 300 ° C. are not suitable for the purpose of the present invention.
Examples of inorganic flame retardant aids (D) include triphenyl phosphate, tricresyl phosphate, trisdichloropropyl phosphate, phosphoric ester compounds, phosphazenes, phosphorous flame retardants such as red phosphorus, antimony trioxide, molybdic acid Examples include inorganic flame retardant aids such as zinc. In particular, an inorganic flame retardant aid in which zinc molybdate is supported on an inorganic filler such as talc is a particularly preferred inorganic flame retardant aid because it significantly improves not only the flame retardancy but also the drill workability. The amount of zinc molybdate whereas trees fat (A) 100 parts by mass of, preferably 5 to 20 parts by weight. By setting it to 5 parts by mass or more, flame retardancy and drilling workability are improved, and by setting it to 20 parts by mass or less, the gel time of the varnish becomes too short and the moldability is improved when a laminate is formed by pressing. There is no decline.
本発明の熱硬化性樹脂組成物には、任意に公知の熱可塑性樹脂、エラストマー、難燃剤、有機充填剤を含有させることができる。
熱可塑性樹脂の例としては、ポリテトラフルオロエチレン、ポリエチレン、ポリプロピレン、ポリスチレン、ポリフェニレンエーテル樹脂、フェノキシ樹脂、ポリカーボネート樹脂、ポリエステル樹脂、ポリアミド樹脂、ポリイミド樹脂、キシレン樹脂、石油樹脂及びシリコーン樹脂等が挙げられる。
エラストマーの例としては、ポリブタジエン、ＡＢＳ樹脂、エポキシ変性ポリブタジエン、無水マレイン酸変性ポリブタジエン、フェノール変性ポリブタジエン及びカルボキシ変性アクリロニトリル等が挙げられる。
難燃剤の例としては、前記の無機充填剤（Ｃ）が挙げられる。
有機充填剤の例としては、シリコーンパウダー、ポリテトラフルオロエチレン、ポリエチレン、ポリプロピレン、ポリスチレン、並びにポリフェニレンエーテル等の有機物粉末等が挙げられる。
The thermosetting resin composition of the present invention can optionally contain a known thermoplastic resin, elastomer, flame retardant, and organic filler.
Examples of the thermoplastic resin include polytetrafluoroethylene, polyethylene, polypropylene, polystyrene, polyphenylene ether resin, phenoxy resin, polycarbonate resin, polyester resin, polyamide resin, polyimide resin, xylene resin, petroleum resin, and silicone resin. .
Examples of the elastomer include polybutadiene, ABS resin, epoxy-modified polybutadiene, maleic anhydride-modified polybutadiene, phenol-modified polybutadiene, and carboxy-modified acrylonitrile.
Examples of the flame retardant include the inorganic filler (C).
Examples of organic fillers include organic powders such as silicone powder, polytetrafluoroethylene, polyethylene, polypropylene, polystyrene, and polyphenylene ether.
本発明において、任意に該樹脂組成物に対して、紫外線吸収剤、酸化防止剤、光重合開始剤、蛍光増白剤及び密着性向上剤等の添加も可能であり、特に限定されない。これらの例としては、ベンゾトリアゾール系等の紫外線吸収剤、ヒンダードフェノール系やスチレン化フェノール等の酸化防止剤、ベンゾフェノン類、ベンジルケタール類、チオキサントン系等の光重合開始剤、スチルベン誘導体等の蛍光増白剤、尿素シラン等の尿素化合物やシランカップリング剤等の密着性向上剤等が挙げられる。 In the present invention, an ultraviolet absorber, an antioxidant, a photopolymerization initiator, a fluorescent whitening agent, an adhesion improver, and the like can be arbitrarily added to the resin composition, and the resin composition is not particularly limited. Examples of these include UV absorbers such as benzotriazoles, antioxidants such as hindered phenols and styrenated phenols, photopolymerization initiators such as benzophenones, benzyl ketals, and thioxanthones, and fluorescence such as stilbene derivatives. Examples include brighteners, urea compounds such as urea silane, and adhesion improvers such as silane coupling agents.
本発明のプリプレグは、前記した本発明の熱硬化性樹脂組成物を基材中に含浸又は塗工した後、Ｂステージ化したものである。以下、本発明のプリプレグについて詳述する。
即ち、本発明のプリプレグは、本発明の熱硬化性樹脂組成物を、基材に含浸又は塗工し、加熱等により半硬化（Ｂステージ化）して本発明のプリプレグを製造することができる。
The prepreg of the present invention, after containing immersion or coating a thermosetting resin composition of the present invention described above in the substrate is obtained by B-staging. Hereinafter, the prepreg of the present invention will be described in detail.
That is, the prepreg of the present invention can be produced by impregnating or coating the base material with the thermosetting resin composition of the present invention and semi-curing (B-stage) by heating or the like. .
プリプレグに用いられる基材には、各種の電気絶縁材料用積層板に用いられている周知のものが使用できる。その材質の例としては、Ｅガラス、Ｄガラス、Ｓガラス及びＱガラス等の無機物繊維、ポリイミド、ポリエステル及びテトラフルオロエチレン等の有機繊維、並びにそれらの混合物等が挙げられる。これらの基材は、例えば、織布、不織布、ロービンク、チョップドストランドマット及びサーフェシングマット等の形状を有するが、材質及び形状は、目的とする成形物の用途や性能により選択され、必要により、単独又は２種類以上の材質及び形状を組み合わせることができる。 As the base material used for the prepreg, known materials used for various types of laminates for electrical insulating materials can be used. Examples of the material include inorganic fibers such as E glass, D glass, S glass, and Q glass, organic fibers such as polyimide, polyester, and tetrafluoroethylene, and mixtures thereof. These base materials have, for example, shapes such as woven fabric, non-woven fabric, robink, chopped strand mat, and surfacing mat, but the material and shape are selected depending on the intended use and performance of the molded product, and if necessary, A single material or two or more materials and shapes can be combined.
基材の厚さは、特に制限されず、例えば、約０．０３〜０．５ｍｍのものを使用することができ、シランカップリング剤等で表面処理したもの又は機械的に開繊処理を施したものが、耐熱性や耐湿性、加工性の面から好適である。
本発明のプリプレグは、該基材に対する熱硬化性樹脂組成物の付着量が、乾燥後のプリプレグの樹脂含有率で２０〜９０質量％となるように基材に含浸又は塗工した後、通常、１００〜２００℃の温度で１〜３０分加熱乾燥し、半硬化（Ｂステージ化）させて得ることができる。
The thickness of the substrate is not particularly limited. For example, a substrate having a thickness of about 0.03 to 0.5 mm can be used, and the substrate is surface-treated with a silane coupling agent or the like, or mechanically opened. Is suitable from the viewpoints of heat resistance, moisture resistance and processability.
After the prepreg of the present invention is impregnated or coated on the base material so that the amount of the thermosetting resin composition attached to the base material is 20 to 90% by mass in terms of the resin content of the prepreg after drying, It can be obtained by heating and drying at a temperature of 100 to 200 ° C. for 1 to 30 minutes and semi-curing (B-stage).
本発明の積層板は本発明のプリプレグを用いて形成されたものであり、前述のプリプレグを用いて、積層成形して、形成することができる。
即ち、本発明の積層板は前述のプリプレグを、例えば１〜２０枚重ね、その片面又は両面に銅及びアルミニウム等の金属箔を配置した構成で積層成形することにより製造することができる。金属箔は、電気絶縁材料用途で用いるものであれば特に制限されない。
また、成形条件は、例えば、電気絶縁材料用積層板及び多層板の手法が適用でき、例えば多段プレス、多段真空プレス、連続成形、オートクレーブ成形機等を使用し、温度１００〜２５０℃、圧力２〜１００ｋｇ/ｃｍ２（０．２〜１０ＭＰａ）、加熱時間０．１〜５時間の範囲で成形することができる。また、本発明のプリプレグと内層用配線板とを組合せ、積層成形して、多層板を製造することもできる。
The laminate of the present invention is formed using the prepreg of the present invention, and can be formed by laminate molding using the prepreg described above.
That is, the laminated board of this invention can be manufactured by laminating | molding the above-mentioned prepreg, for example by the structure which laminated | stacked 1-20 sheets, and arrange | positioned metal foil, such as copper and aluminum, on the single side | surface or both surfaces. The metal foil is not particularly limited as long as it is used for electrical insulating material applications.
In addition, as the molding conditions, for example, a method of a laminated plate for an electrical insulating material and a multilayer plate can be applied. For example, a multi-stage press, a multi-stage vacuum press, continuous molding, an autoclave molding machine, etc. are used, and It can be molded in a range of ˜100 kg / cm 2 (0.2 to 10 MPa) and a heating time of 0.1 to 5 hours. Further, the prepreg of the present invention and the inner layer wiring board can be combined and laminated to produce a multilayer board.
次に、下記の実施例により本発明を更に詳しく説明するが、これらの実施例は本発明をいかなる意味においても制限するものではない。
なお、以下の実施例および比較例において得られた銅張積層板を以下の方法により測定し、評価を行った。
Next, the present invention will be described in more detail with reference to the following examples, but these examples do not limit the present invention in any way.
In addition, the copper clad laminated board obtained in the following examples and comparative examples was measured by the following method and evaluated.
（１）銅箔接着性（銅箔ピール強度）
銅張積層板を銅エッチング液に浸漬することにより１cm幅の銅箔を形成して評価基板を作製し、引張り試験機を用いて銅箔の接着性（ピール強度）を測定した。
(1) Copper foil adhesion (copper foil peel strength)
A 1 cm wide copper foil was formed by immersing the copper clad laminate in a copper etching solution to produce an evaluation substrate, and the adhesion (peel strength) of the copper foil was measured using a tensile tester.
（２）ガラス転移温度（Ｔｇ）
銅張積層板を銅エッチング液に浸漬することにより銅箔を取り除いた５ｍｍ角の評価基板を作製し、ＴＭＡ試験装置（デュポン社製、ＴＭＡ２９４０）を用い、評価基板の面方向の熱膨張特性を観察することにより評価した。
(2) Glass transition temperature (Tg)
A 5 mm square evaluation board from which the copper foil was removed by immersing the copper clad laminate in a copper etching solution was prepared, and the thermal expansion characteristics in the surface direction of the evaluation board were measured using a TMA test apparatus (manufactured by DuPont, TMA2940). Evaluation was made by observation.
（３）はんだ耐熱性
銅張積層板を銅エッチング液に浸漬することにより銅箔を取り除いた５ｃｍ角の評価基板を作製し、平山製作所（株）製プレッシャー・クッカー試験装置を用いて、１２１℃、２ａｔｍの条件で４時間までプレッシャー・クッカー処理を行った後、温度２８８℃のはんだ浴に、評価基板を２０秒間浸漬した後、外観を観察することによりはんだ耐熱性を評価した。
(3) Solder heat resistance A 5 cm square evaluation board from which the copper foil has been removed by immersing a copper clad laminate in a copper etching solution is prepared and 121 ° C. using a pressure cooker test apparatus manufactured by Hirayama Seisakusho. After performing the pressure-cooker treatment for up to 4 hours under the condition of 2 atm, the evaluation substrate was immersed in a solder bath at a temperature of 288 ° C. for 20 seconds, and then the solder heat resistance was evaluated by observing the appearance.
（４）線熱膨張係数
銅張積層板を銅エッチング液に浸漬することにより銅箔を取り除いた５ｍｍ角の評価基板を作製し、ＴＭＡ試験装置（デュポン社製、ＴＭＡ２９４０）を用い、評価基板の面方向の３０℃〜１００℃の線熱膨張率を測定した。
(4) Linear thermal expansion coefficient A 5-mm square evaluation board | substrate which removed the copper foil by immersing a copper clad laminated board in a copper etching liquid was produced, and the evaluation board | substrate was used using the TMA test apparatus (made by DuPont, TMA2940). The linear thermal expansion coefficient of 30 to 100 ° C. in the plane direction was measured.
（５）難燃性
銅張積層板を銅エッチング液に浸漬することにより銅箔を取り除いた評価基板から、長さ１２７ｍｍ、幅１２．７ｍｍに切り出した試験片を作製し、ＵＬ９４の試験法（Ｖ法）に準じて評価した。
(5) Flame retardance A test piece cut out to a length of 127 mm and a width of 12.7 mm was prepared from an evaluation substrate obtained by removing a copper foil by immersing a copper clad laminate in a copper etching solution, and a UL94 test method ( Evaluation was made according to V method.
（６）銅付き耐熱性（Ｔ-３００）
銅張積層板から５ｍｍ角の評価基板を作製し、ＴＭＡ試験装置（デュポン社製、ＴＭＡ２９４０）を用い、３００℃で評価基板の膨れが発生するまでの時間を測定することにより評価した。
(6) Heat resistance with copper (T-300)
A 5 mm square evaluation board was produced from the copper clad laminate, and evaluation was performed by measuring the time until the evaluation board swells at 300 ° C. using a TMA test apparatus (manufactured by DuPont, TMA2940).
（７）誘電特性（比誘電率及び誘電正接）
得られた銅張積層板を銅エッチング液に浸漬することにより銅箔を取り除いた評価基板を作製し、Ｈｅｗｌｌｅｔ・Ｐａｃｋｅｒｄ社製比誘電率測定装置（製品名：ＨＰ４２９１Ｂ）を用いて、周波数１ＧＨｚでの比誘電率及び誘電正接を測定した。
(7) Dielectric properties (dielectric constant and dielectric loss tangent)
The obtained copper-clad laminate was immersed in a copper etching solution to prepare an evaluation substrate from which the copper foil was removed, and a relative dielectric constant measuring apparatus (product name: HP4291B) manufactured by Hewlett-Packard Company was used at a frequency of 1 GHz. The relative dielectric constant and dielectric loss tangent of were measured.
（８）ドリル加工性
ドリルに径０．１０５ｍｍ（ユニオンツールＭＶ Ｊ６７６）を用い、回転数:１６０，０００ｒｐｍ、送り速度：０．８ｍ／分、重ね枚数：1枚でドリル加工を行い、６０００ヒットさせて評価基板を作製し、ドリル穴の内壁粗さを評価した。内壁粗さの評価は、無電解銅めっきを行い（めっき厚：１５μｍ）、穴壁へのめっき染み込み長さの最大値を測定することにより評価した。
(8) Drill workability Using a drill with a diameter of 0.105 mm (Union Tool MV J676), the number of rotations: 160,000 rpm, feed rate: 0.8 m / min, the number of stacked sheets: one, 6000 hits Thus, an evaluation substrate was produced, and the inner wall roughness of the drill hole was evaluated. The inner wall roughness was evaluated by performing electroless copper plating (plating thickness: 15 μm) and measuring the maximum value of the plating penetration length into the hole wall.
製造例１：樹脂（Ａ−１）の製造
温度計、攪拌装置、還流冷却管の付いた加熱及び冷却可能な容積３リットルの反応容器に、ビスフェノールＡ型シアネート樹脂（ロンザジャパン社製；商品名Ｐｒｉｍａｓｅｔ ＢＡＤＣｙ）：６００．０ｇ、下記の式（Ｖ）に示すシロキサン樹脂（信越化学社製；商品名Ｘ−２２−１８２１、水酸基当量；１，６００）：２００．０ｇ、ビフェニル型エポキシ樹脂（ジャパンエポキシレジン社製；商品名ＹＸ−４０００、エポキシ当量；１８６）：２００．０ｇ及びトルエン：１０００．０ｇを投入した。次いで、攪拌しながら１２０℃に昇温し、樹脂固形分が溶解し均一な溶液になっていることを確認した後、ナフテン酸亜鉛の８質量％ミネラルスピリット溶液を０．０１ｇ添加し、約１１０℃で４時間反応を行った。その後、室温に冷却し樹脂（Ａ−１）の溶液を得た。
この反応溶液を少量取り出し、ＧＰＣ測定（ポリスチレン換算、溶離液：テトラヒドロフラン）を行ったところ、溶出時間が約１２．４分付近に出現する合成原料のビスフェノールＡ型シアネート樹脂のピーク面積が、反応開始時のビスフェノールＡ型シアネート樹脂のピーク面積と比較し、ピーク面積の消失率〔（ｂ）成分の反応率〕が６８％であった。また、約１０．９分付近、及び８．０〜１０．０付近に出現する熱硬化性樹脂の生成物のピークが確認された。さらに、少量取り出した反応溶液を、メタノールとベンゼンの混合溶媒（混合重量比１：１）に滴下して再沈殿させることにより、精製された固形分を取り出し、ＦＴ−ＩＲ測定を行ったところ、イミノカーボネート基に起因する１７００ｃｍ−１付近のピーク、また、トリアジン環に起因する１５６０ｃｍ−１付近、及び１３８０ｃｍ−１付近の強いピークが確認でき、樹脂（Ａ−１）が製造されていることを確認した。
Production Example 1: Production thermometer tree fat (A-1), a stirring device and a reaction vessel heating and cooling capacity capable of 3 liters equipped with a reflux condenser, a bisphenol A type cyanate resin (Lonza Japan Ltd., trade Name Primaset BADCy): 600.0 g, siloxane resin represented by the following formula (V) (manufactured by Shin-Etsu Chemical Co., Ltd .; trade name X-22-1821, hydroxyl equivalent: 1,600): 200.0 g, biphenyl type epoxy resin ( Made by Japan Epoxy Resin Co., Ltd .; trade name YX-4000, epoxy equivalent; 186): 200.0 g and toluene: 1000.0 g were charged. Next, the temperature was raised to 120 ° C. with stirring, and after confirming that the resin solids had dissolved and became a uniform solution, 0.01 g of an 8% by mass mineral spirit solution of zinc naphthenate was added, and about 110 The reaction was carried out at 4 ° C. for 4 hours. Then, to obtain a solution was cooled to room temperature resins (A-1).
A small amount of this reaction solution was taken out and subjected to GPC measurement (polystyrene conversion, eluent: tetrahydrofuran). As a result, the peak area of the bisphenol A type cyanate resin, which is a synthetic raw material and the elution time appears around 12.4 minutes, is the start of the reaction. Compared with the peak area of the bisphenol A type cyanate resin at the time, the disappearance rate of the peak area [reaction rate of the component (b)] was 68%. Moreover, the peak of the product of the thermosetting resin which appears at about 10.9 minutes vicinity and 8.0-10.0 vicinity was confirmed. Furthermore, the reaction solution taken out in a small amount was dropped into a mixed solvent of methanol and benzene (mixing weight ratio 1: 1) and reprecipitated to take out the purified solid, and FT-IR measurement was performed. imino carbonates due to group 1700 cm -1 vicinity of the peak also, around 1560 cm -1 due to the triazine ring, and 1380cm of around -1 can strong peaks confirmed that the dendritic fat (a-1) is produced It was confirmed.
製造例２：樹脂（Ａ−２）の製造
温度計、攪拌装置、還流冷却管の付いた加熱及び冷却可能な容積３リットルの反応容器に、ノボラック型シアネート樹脂（ロンザジャパン社製；商品名Ｐｒｉｍａｓｅｔ ＰＴ−１５，質量平均分子量５００〜１，０００）：８００．０ｇと、下記の式（VI）に示すシロキサン樹脂（信越化学社製；商品名ＫＦ−６００３、水酸基当量；２８００）：１００．０ｇ、ナフトールアラルキル・クレゾール共重合型エポキシ樹脂（日本化薬社製；商品名ＮＣ−７０００Ｌ、エポキシ当量；２３０）：１００．０ｇ及びトルエン：１０００．０ｇを投入した。次いで、攪拌しながら１２０℃に昇温し、樹脂固形分が溶解し均一な溶液になっていることを確認した後、ナフテン酸亜鉛の８質量％ミネラルスピリット溶液を０．０１ｇ添加し、約１１０℃で４時間反応を行った。その後、室温に冷却し樹脂（Ａ−２）の溶液を得た。
この反応溶液を少量取り出し、ＧＰＣ測定（ポリスチレン換算、溶離液：テトラヒドロフラン）を行ったところ、溶出時間が約１２．１分付近に出現する合成原料のノボラック型シアネート樹脂のピーク面積が、反応開始時のノボラック型シアネート樹脂のピーク面積と比較し、ピーク面積の消失率〔（ｂ）成分の反応率〕が４３％であった。また、約１０．９分付近、及び８．０〜１０．０付近に出現する熱硬化性樹脂の生成物のピークが確認された。さらに、少量取り出した反応溶液を、メタノールとベンゼンの混合溶媒（混合重量比１：１）に滴下して再沈殿させることにより、精製された固形分を取り出し、ＦＴ−ＩＲ測定を行ったところ、イミノカーボネート基に起因する１７００ｃｍ−１付近のピーク、また、トリアジン環に起因する１５６０ｃｍ−１付近、及び１３８０ｃｍ−１付近の強いピークが確認でき、樹脂（Ａ−２）が製造されていることを確認した。
Production Example 2: Production thermometer tree fat (A-2), a stirring device and a reaction vessel heating and cooling capacity capable of 3 liters equipped with a reflux condenser, a novolac type cyanate resin (Lonza Japan Ltd., trade name Primaset PT-15, mass average molecular weight 500 to 1,000): 800.0 g and a siloxane resin represented by the following formula (VI) (manufactured by Shin-Etsu Chemical Co., Ltd .; trade name KF-6003, hydroxyl group equivalent; 2800): 100. 0 g, naphthol aralkyl-cresol copolymer epoxy resin (manufactured by Nippon Kayaku Co., Ltd .; trade name NC-7000L, epoxy equivalent: 230): 100.0 g and toluene: 1000.0 g were added. Next, the temperature was raised to 120 ° C. with stirring, and after confirming that the resin solids had dissolved and became a uniform solution, 0.01 g of an 8% by mass mineral spirit solution of zinc naphthenate was added, and about 110 The reaction was carried out at 4 ° C. for 4 hours. Then, to obtain a solution was cooled to room temperature resins (A-2).
A small amount of this reaction solution was taken out and subjected to GPC measurement (polystyrene conversion, eluent: tetrahydrofuran). As a result, the peak area of the novolac-type cyanate resin, which is a synthetic raw material with an elution time of about 12.1 minutes, As compared with the peak area of the novolak-type cyanate resin, the disappearance rate of the peak area [reaction rate of the component (b)] was 43%. Moreover, the peak of the product of the thermosetting resin which appears at about 10.9 minutes vicinity and 8.0-10.0 vicinity was confirmed. Furthermore, the reaction solution taken out in a small amount was dropped into a mixed solvent of methanol and benzene (mixing weight ratio 1: 1) and reprecipitated to take out the purified solid, and FT-IR measurement was performed. imino carbonate group peak near 1700 cm -1 due to the addition, the vicinity of 1560 cm -1 attributable to the triazine ring, and 1380cm can strong peaks confirmed the vicinity of -1, the tree fat (a-2) is prepared It was confirmed.
製造例３：樹脂（Ａ−３）の製造
温度計、攪拌装置、還流冷却管の付いた加熱及び冷却可能な容積３リットルの反応容器に、ジシクロペンタジエン型シアネート樹脂（ロンザジャパン社製；商品名Ｐｒｉｍａｓｅｔ ＤＴ−４０００，質量平均分子量５００〜１，０００）：４００．０ｇ、下記式（VII）に示すシロキサン樹脂（信越化学社製；商品名Ｘ−２２−１６０ＡＳ、水酸基当量；５００）：１００．０g、ビフェニルアラルキル型エポキシ樹脂（日本化薬社製；商品名ＮＣ−３０００Ｈ、エポキシ当量；２８０）：５００．０ｇ及びシチレン：１０００．０ｇを投入した。
次いで、攪拌しながら１２０℃に昇温し、樹脂固形分が溶解し均一な溶液になっていることを確認した後、ナフテン酸亜鉛の８質量％ミネラルスピリット溶液を０．３０ｇ添加し、約１１０℃で４時間反応を行った。その後、室温に冷却し、樹脂（Ａ−３）の溶液を得た。
この反応溶液を少量取り出し、ＧＰＣ測定（ポリスチレン換算、溶離液：テトラヒドロフラン）を行ったところ、溶出時間が約１２．０分付近に出現する合成原料のノボラック型シアネート樹脂のピーク面積が、反応開始時のノボラック型シアネート樹脂のピーク面積と比較し、ピーク面積の消失率〔（ｂ）成分の反応率〕が４３％であった。また、約１０．９分付近、及び８．０〜１０．０付近に出現する熱硬化性樹脂の生成物のピークが確認された。さらに、少量取り出した反応溶液を、メタノールとベンゼンの混合溶媒（混合質量比１：１）に滴下して再沈殿させることにより、精製された固形分を取り出し、ＦＴ−ＩＲ測定を行ったところ、イミノカーボネート基に起因する１７００ｃｍ−１付近のピーク、また、トリアジン環に起因する１５６０ｃｍ−１付近、及び１３８０ｃｍ−１付近の強いピークが確認でき、樹脂（Ａ−３）が製造されていることを確認した。
Production Example 3: Production thermometer tree fat (A-3), a stirring device and a reaction vessel heating and cooling capacity capable of 3 liters equipped with a reflux condenser, dicyclopentadiene type cyanate resin (Lonza Japan Ltd.; Brand name Primaset DT-4000, mass average molecular weight 500-1,000): 400.0 g, siloxane resin represented by the following formula (VII) (manufactured by Shin-Etsu Chemical Co., Ltd .; trade name X-22-160AS, hydroxyl equivalent: 500): 100.0 g, biphenyl aralkyl type epoxy resin (manufactured by Nippon Kayaku Co., Ltd .; trade name NC-3000H, epoxy equivalent; 280): 500.0 g and styrene: 1000.0 g were added.
Next, the temperature was raised to 120 ° C. while stirring, and after confirming that the resin solids had dissolved and became a uniform solution, 0.30 g of an 8% by mass mineral spirit solution of zinc naphthenate was added, and about 110 The reaction was carried out at 4 ° C. for 4 hours. Then cooled to room temperature to obtain a solution of dendritic fat (A-3).
A small amount of this reaction solution was taken out and subjected to GPC measurement (polystyrene conversion, eluent: tetrahydrofuran). As a result, the peak area of the novolak-type cyanate resin, which is a synthetic raw material that appears in the vicinity of about 12.0 minutes, is shown at the start of the reaction. As compared with the peak area of the novolak-type cyanate resin, the disappearance rate of the peak area [reaction rate of the component (b)] was 43%. Moreover, the peak of the product of the thermosetting resin which appears at about 10.9 minutes vicinity and 8.0-10.0 vicinity was confirmed. Furthermore, when the reaction solution taken out in a small amount was dropped into a mixed solvent of methanol and benzene (mixing mass ratio 1: 1) and reprecipitated, the purified solid content was taken out and subjected to FT-IR measurement. imino carbonate group peak near 1700 cm -1 due to the addition, the vicinity of 1560 cm -1 attributable to the triazine ring, and 1380cm can strong peaks confirmed the vicinity of -1, the tree fat (a-3) is prepared It was confirmed.
製造例４：樹脂（Ａ−４）の製造
温度計、攪拌装置、還流冷却管の付いた加熱及び冷却可能な容積３リットルの反応容器に、ビスフェノールＡ型シアネート樹脂（ロンザジャパン社製；商品名Ｐｒｉｍａｓｅｔ ＢＡＤＣｙ）：４００．０ｇと、前記の式（Ｖ）に示すシロキサン樹脂（信越化学社製；商品名Ｘ−２２−１８２１、水酸基当量；１，６００）：５００．０gと、ナフタレン型エポキシ樹脂（大日本インキ化学社製；商品名エピクロンＨＰ−４０３２、エポキシ当量；１５０）：１００．０ｇと、トルエン：１０００．０ｇを投入した。次いで、攪拌しながら１２０℃に昇温し、樹脂固形分が溶解し均一な溶液になっていることを確認した後、ナフテン酸亜鉛の８質量％ミネラルスピリット溶液を０．０１ｇ添加し、約１１０℃で４時間反応を行った。その後、室温に冷却し樹脂（Ａ−４）の溶液を得た。
この反応溶液を少量取り出し、ＧＰＣ測定（ポリスチレン換算、溶離液：テトラヒドロフラン）を行ったところ、溶出時間が約１２．４分付近に出現する合成原料のビスフェノールＡ型シアネート樹脂のピーク面積が、反応開始時のビスフェノールＡ型シアネート樹脂のピーク面積と比較し、ピーク面積の消失率〔（ｂ）成分の反応率〕が５５％であった。また、約１０．９分付近、及び８．０〜１０．０付近に出現する熱硬化性樹脂の生成物のピークが確認された。さらに、少量取り出した反応溶液を、メタノールとベンゼンの混合溶媒（混合重量比１：１）に滴下して再沈殿させることにより、精製された固形分を取り出し、ＦＴ−ＩＲ測定を行ったところ、イミノカーボネート基に起因する１７００ｃｍ−１付近のピーク、また、トリアジン環に起因する１５６０ｃｍ−１付近、及び１３８０ｃｍ−１付近の強いピークが確認でき、樹脂（Ａ−４）が製造されていることを確認した。
Production Example 4: Production thermometer tree fat (A-4), a stirring device and a reaction vessel heating and cooling capacity capable of 3 liters equipped with a reflux condenser, a bisphenol A type cyanate resin (Lonza Japan Ltd., trade Name Primaset BADCy): 400.0 g and siloxane resin represented by the above formula (V) (manufactured by Shin-Etsu Chemical Co., Ltd .; trade name X-22-1821, hydroxyl equivalent: 1,600): 500.0 g, naphthalene type epoxy Resin (Dainippon Ink Chemical Co., Ltd .; trade name: Epiklon HP-4032, epoxy equivalent: 150): 100.0 g and toluene: 1000.0 g were charged. Next, the temperature was raised to 120 ° C. with stirring, and after confirming that the resin solids had dissolved and became a uniform solution, 0.01 g of an 8% by mass mineral spirit solution of zinc naphthenate was added, and about 110 The reaction was carried out at 4 ° C. for 4 hours. Then, to obtain a solution was cooled to room temperature resins (A-4).
A small amount of this reaction solution was taken out and subjected to GPC measurement (polystyrene conversion, eluent: tetrahydrofuran). As a result, the peak area of the bisphenol A type cyanate resin, which is a synthetic raw material and the elution time appears around 12.4 minutes, is the start of the reaction. Compared with the peak area of the bisphenol A type cyanate resin at the time, the disappearance rate of the peak area [reaction rate of the component (b)] was 55%. Moreover, the peak of the product of the thermosetting resin which appears at about 10.9 minutes vicinity and 8.0-10.0 vicinity was confirmed. Furthermore, the reaction solution taken out in a small amount was dropped into a mixed solvent of methanol and benzene (mixing weight ratio 1: 1) and reprecipitated to take out the purified solid, and FT-IR measurement was performed. imino carbonates due to group 1700 cm -1 vicinity of the peak also, around 1560 cm -1 due to the triazine ring, and 1380cm vicinity of can strong peak is confirmed -1, the tree fat (a-4) is prepared It was confirmed.
製造例５：トリメトキシシラン化合物により表面処理された溶融シリカ（Ｂ−１）の製造
温度計、攪拌装置、還流冷却管の付いた加熱及び冷却可能な容積３リットルの反応容器に、溶融シリカ（アドマテックス社製；商品名ＳＯ−２５Ｒ）：７００．０ｇと、プロピレングリコールモノメチルエーテル：１０００．０ｇを配合し、攪拌しながらＮ−フェニル−３−アミノプロピルトリメトキシシラン（信越化学社製；商品名ＫＢＭ−５７３）：７．０ｇを添加した。次いで８０℃に昇温し、８０℃で１時間反応を行い溶融シリカの表面処理（湿式処理）を行った後、室温に冷却し、Ｎ−フェニル−３−アミノプロピルトリメトキシシランにより表面処理（湿式処理）された溶融シリカ（Ｂ−１）の溶液を得た。
Production Example 5: Production of fused silica (B-1) surface-treated with a trimethoxysilane compound In a 3 liter reaction vessel equipped with a thermometer, a stirrer, a reflux condenser and capable of heating and cooling, fused silica ( Admatechs Co., Ltd .; trade name SO-25R): 700.0 g and propylene glycol monomethyl ether: 1000.0 g were mixed and stirred with N-phenyl-3-aminopropyltrimethoxysilane (Shin-Etsu Chemical Co., Ltd .; product) Name KBM-573): 7.0 g was added. Next, the temperature was raised to 80 ° C., reacted at 80 ° C. for 1 hour to perform surface treatment of the fused silica (wet treatment), then cooled to room temperature, and surface treatment with N-phenyl-3-aminopropyltrimethoxysilane ( A wet-processed fused silica (B-1) solution was obtained.
比較製造例１：（樹脂（Ａ−５）：（ｂ）成分の反応率１８％）の製造
温度計、攪拌装置、還流冷却管の付いた加熱及び冷却可能な容積３リットルの反応容器に、ビスフェノールＡ型シアネート樹脂（ロンザジャパン社製；商品名Ｐｒｉｍａｓｅｔ ＢＡＤＣｙ）：６００．０ｇと、前記の式（Ｖ）に示すシロキサン樹脂（信越化学社製；商品名Ｘ−２２−１８２１、水酸基当量；１，６００）：２００．０gと、ビフェニル型エポキシ樹脂（ジャパンエポキシレジン社製；商品名ＹＸ−４０００、エポキシ当量；１８６）：２００．０ｇと、トルエン：１０００．０ｇを投入した。次いで、攪拌しながら１２０℃に昇温し、樹脂固形分が溶解し均一な溶液になっていることを確認した後、ナフテン酸亜鉛の８質量％ミネラルスピリット溶液を０．０１ｇ添加し、約１１０℃で１時間反応を行った。その後、室温に冷却し、樹脂（Ａ−５）の溶液を得た。
この反応溶液を少量取り出し、ＧＰＣ測定（ポリスチレン換算、溶離液：テトラヒドロフラン）を行ったところ、溶出時間が約１２．４分付近に出現する合成原料のビスフェノールＡ型シアネート樹脂のピーク面積が、反応開始時のビスフェノールＡ型シアネート樹脂のピーク面積と比較し、ピーク面積の消失率〔（ｂ）成分の反応率〕が１８％であった。また、この溶液は翌日結晶化により沈殿物が生じた。
Comparative Production Example 1: Production of (Resin (A-5): Reaction Rate of Component (b) 18%) In a reaction vessel with a volume of 3 liters that can be heated and cooled with a thermometer, a stirrer, a reflux condenser, Bisphenol A type cyanate resin (manufactured by Lonza Japan; trade name Primaset BADCy): 600.0 g and a siloxane resin represented by the above formula (V) (manufactured by Shin-Etsu Chemical Co., Ltd .; trade name X-22-1821, hydroxyl equivalent: 1 , 600): 200.0 g and biphenyl type epoxy resin (manufactured by Japan Epoxy Resin; trade name YX-4000, epoxy equivalent; 186): 200.0 g and toluene: 1000.0 g. Next, the temperature was raised to 120 ° C. with stirring, and after confirming that the resin solids had dissolved and became a uniform solution, 0.01 g of an 8% by mass mineral spirit solution of zinc naphthenate was added, and about 110 The reaction was carried out at 1 ° C. for 1 hour. Then, it cooled to room temperature and obtained the solution of resin (A-5).
A small amount of this reaction solution was taken out and subjected to GPC measurement (polystyrene conversion, eluent: tetrahydrofuran). As a result, the peak area of the bisphenol A type cyanate resin, which is a synthetic raw material and the elution time appears around 12.4 minutes, is the start of the reaction. Compared with the peak area of the bisphenol A type cyanate resin at the time, the disappearance rate of the peak area [reaction rate of the component (b)] was 18%. In addition, a precipitate was formed in the solution by crystallization the next day.
比較製造例２：（樹脂（Ａ−６）：（ｂ）成分の反応率７６％）の製造
温度計、攪拌装置、還流冷却管の付いた加熱及び冷却可能な容積３リットルの反応容器に、ビスフェノールＡ型シアネート樹脂（ロンザジャパン社製；商品名Ｐｒｉｍａｓｅｔ ＢＡＤＣｙ）：６００．０ｇ、前記の式（Ｖ）に示すシロキサン樹脂（信越化学社製；商品名Ｘ−２２−１８２１、水酸基当量；１，６００）：２００．０g、ビフェニル型エポキシ樹脂（ジャパンエポキシレジン社製；商品名ＹＸ−４０００、エポキシ当量；１８６）：２００．０ｇ及びトルエン：１０００．０ｇを投入した。次いで、攪拌しながら１２０℃に昇温し、樹脂固形分が溶解し均一な溶液になっていることを確認した後、ナフテン酸亜鉛の８質量％ミネラルスピリット溶液を０．０１ｇ添加し、約１２０℃で６時間反応を行った。その後、室温に冷却し、樹脂（Ａ−６）の溶液を得た。
この反応溶液を少量取り出し、ＧＰＣ測定（ポリスチレン換算、溶離液：テトラヒドロフラン）を行ったところ、溶出時間が約１２．４分付近に出現する合成原料のビスフェノールＡ型シアネート樹脂のピーク面積が、反応開始時のビスフェノールＡ型シアネート樹脂のピーク面積と比較し、ピーク面積の消失率〔（ｂ）成分の反応率〕が７６％であった。
Comparative Production Example 2: Production of (Resin (A-6): (b) Component Reaction Rate 76%) In a reaction vessel with a volume of 3 liters that can be heated and cooled with a thermometer, a stirrer, a reflux condenser, Bisphenol A type cyanate resin (manufactured by Lonza Japan; trade name Primaset BADCy): 600.0 g, siloxane resin represented by the above formula (V) (manufactured by Shin-Etsu Chemical Co., Ltd .; trade name X-22-1821, hydroxyl group equivalent; 1, 600): 200.0 g, biphenyl type epoxy resin (manufactured by Japan Epoxy Resin; trade name YX-4000, epoxy equivalent; 186): 200.0 g and toluene: 1000.0 g were charged. Next, the temperature was raised to 120 ° C. while stirring, and after confirming that the resin solids had dissolved and became a uniform solution, 0.01 g of an 8% by mass mineral spirit solution of zinc naphthenate was added, and about 120 The reaction was carried out at 6 ° C. for 6 hours. Then, it cooled to room temperature and obtained the solution of resin (A-6).
A small amount of this reaction solution was taken out and subjected to GPC measurement (polystyrene conversion, eluent: tetrahydrofuran). As a result, the peak area of the bisphenol A type cyanate resin, which is a synthetic raw material and the elution time appears around 12.4 minutes, is the start of the reaction. Compared with the peak area of the bisphenol A type cyanate resin at the time, the disappearance rate of the peak area [reaction rate of the component (b)] was 76%.
比較製造例３：（樹脂（Ａ−７）：（ｂ）成分の反応率５３％、（ｃ）成分無）の製造
温度計、攪拌装置、還流冷却管の付いた加熱及び冷却可能な容積２リットルの反応容器に、ビスフェノールＡ型シアネート樹脂（ロンザジャパン社製；商品名Ｐｒｉｍａｓｅｔ ＢＡＤＣｙ）：６００．０ｇと、前記の式（Ｖ）に示すシロキサン樹脂（信越化学社製；商品名Ｘ−２２−１８２１、水酸基当量；１，６００）：２００．０gと、トルエン：８００．０ｇを投入した。次いで、攪拌しながら１２０℃に昇温し、樹脂固形分が溶解し均一な溶液になっていることを確認した後、ナフテン酸亜鉛の８質量％ミネラルスピリット溶液を０．０１ｇ添加し、約１１０℃で４時間反応を行った。その後、室温に冷却し、樹脂（Ａ−７）の溶液を得た。
この反応溶液を少量取り出し、ＧＰＣ測定（ポリスチレン換算、溶離液：テトラヒドロフラン）を行ったところ、溶出時間が約１２．４分付近に出現する合成原料のビスフェノールＡ型シアネート樹脂のピーク面積が、反応開始時のビスフェノールＡ型シアネート樹脂のピーク面積と比較し、ピーク面積の消失率〔（ｂ）成分の反応率〕が５３％であった。
Comparative Production Example 3: Production of (Resin (A-7): (b) Component Reaction Rate 53%, (c) No Component) Heating and Cooling Volume 2 with Thermometer, Stirrer, Reflux Cooling Tube 2 In a reaction vessel of 1 liter, bisphenol A type cyanate resin (Lonza Japan Co., Ltd .; trade name Primaset BADCy): 600.0 g and the siloxane resin represented by the above formula (V) (Shin-Etsu Chemical Co., Ltd .; trade name X-22-) 1821, hydroxyl equivalent: 1,600): 200.0 g and toluene: 800.0 g. Next, the temperature was raised to 120 ° C. with stirring, and after confirming that the resin solids had dissolved and became a uniform solution, 0.01 g of an 8% by mass mineral spirit solution of zinc naphthenate was added, and about 110 The reaction was carried out at 4 ° C. for 4 hours. Then, it cooled to room temperature and obtained the solution of resin (A-7).
A small amount of this reaction solution was taken out and subjected to GPC measurement (polystyrene conversion, eluent: tetrahydrofuran). As a result, the peak area of the bisphenol A type cyanate resin, which is a synthetic raw material and the elution time appears around 12.4 minutes, is the start of the reaction. Compared with the peak area of the bisphenol A type cyanate resin at the time, the disappearance rate of the peak area [reaction rate of the component (b)] was 53%.
実施例１〜６、比較例１〜５
製造例１〜４により得られた（Ａ）成分の樹脂、又は比較製造例１〜３で得られた樹脂、製造例５又は商業的に入手した（Ｂ）成分、また必要により（Ｃ）成分、（Ｄ）成分、及び硬化促進剤に、希釈溶剤としてメチルエチルケトンを使用して、第１表及び第２表に示した配合割合（質量部）で混合して樹脂分６０質量％の均一なワニスを得た。
次に、得られたワニスを厚さ０．２ｍｍのＳガラスクロスに含浸塗工し、１６０℃で１０分加熱乾燥して樹脂含有量５５質量％のプリプレグを得た。
このプリプレグを４枚重ね、１８μｍの電解銅箔を上下に配置し、圧力２５ｋｇ/ｃｍ２（２．５ＭＰａ）、温度１８５℃で９０分間プレスを行って、銅張積層板を得た。
このようにして得られた銅張積層板を用いて、銅箔接着性（銅箔ピール強度）、ガラス転移温度、はんだ耐熱性、線膨張係数、難燃性、銅付き耐熱性（Ｔ-３００）、比誘電率（１ＧＨｚ）、誘電正接（１ＧＨｚ）及びドリル加工性について前記の方法で測定・評価した。評価結果を第１表及び第２表に示す。
Examples 1-6, Comparative Examples 1-5
Obtained in Production Example 1 to 4 (A) component of the tree butter, or a resin obtained in Comparative Production Example 1-3 Production Example 5 or commercially Obtained component (B), also if necessary (C) Component, component (D), and curing accelerator were mixed in a blending ratio (parts by mass) shown in Tables 1 and 2 using methyl ethyl ketone as a diluent solvent, and a uniform resin content of 60% by mass. A varnish was obtained.
Next, the obtained varnish was impregnated and applied to an S glass cloth having a thickness of 0.2 mm and dried by heating at 160 ° C. for 10 minutes to obtain a prepreg having a resin content of 55% by mass.
Four prepregs were stacked, 18 μm electrolytic copper foils were placed one above the other, and pressed at a pressure of 25 kg / cm 2 (2.5 MPa) and a temperature of 185 ° C. for 90 minutes to obtain a copper clad laminate.
Using the copper-clad laminate thus obtained, copper foil adhesion (copper foil peel strength), glass transition temperature, solder heat resistance, linear expansion coefficient, flame resistance, heat resistance with copper (T-300) ), Relative dielectric constant (1 GHz), dielectric loss tangent (1 GHz) and drill workability were measured and evaluated by the methods described above. The evaluation results are shown in Tables 1 and 2.
第１表及び第２表において、商業的に入手した（Ｂ）成分、任意に用いた（Ｃ）成分、（Ｄ）成分、硬化促進剤、比較例で用いたエポキシ樹脂及び溶融シリカは次の通りである。 In Tables 1 and 2, commercially available (B) component, optionally used (C) component, (D) component, curing accelerator, epoxy resin and fused silica used in Comparative Examples are as follows: Street.
（Ｂ）成分
溶融シリカ（Ｂ−２）：溶融シリカに対し１．０質量％のＮ−フェニル−３−アミノプロピルトリメトキシシランにより表面処理された溶融シリカ（アドマテック社製；商品名ＳＣ−２０５０ＫＮＫ，希釈溶剤；メチルイソブチルケトン）
溶融シリカ（Ｂ−３）：溶融シリカに対し１．０質量％のＮ−フェニル−３−アミノプロピルトリメトキシシランにより表面処理された溶融シリカ（アドマテック社製；商品名ＳＣ−２０５０ＨＮＫ，希釈溶剤；シクロヘキサノン）
溶融シリカ（Ｂ−４）：溶融シリカ（アドマテック社製；商品名ＳＯ−２５Ｒ）
溶融シリカ（Ｂ−５）：溶融シリカに対し１．０質量％の下記式(VIII)に示しγ−グリシドキシプロピルトリメトキシシランにより表面処理された溶融シリカ（アドマテック社製；商品名ＳＣ１０３０−ＭＪＡ、希釈溶剤；メチルエチルケトン）
Component (B) Fused silica (B-2): Fused silica surface-treated with 1.0% by mass of N-phenyl-3-aminopropyltrimethoxysilane based on fused silica (manufactured by Admatech; trade name SC-2050KNK) , Diluent solvent; methyl isobutyl ketone)
Fused silica (B-3): Fused silica surface-treated with 1.0% by mass of N-phenyl-3-aminopropyltrimethoxysilane with respect to fused silica (manufactured by Admatech; trade name SC-2050HNK, diluent solvent; Cyclohexanone)
Fused silica (B-4): Fused silica (manufactured by Admatech; trade name SO-25R)
Fused silica (B-5): 1.0% by mass of fused silica represented by the following formula (VIII) and surface-treated with γ-glycidoxypropyltrimethoxysilane (manufactured by Admatech; trade name SC1030- MJA, diluent solvent; methyl ethyl ketone)
（Ｃ）無機充填剤（ＡｌＯＯＨ）：ベーマイト型水酸化アルミニウム（河合石灰社製；商品名ＢＭＴ−３Ｌ、熱分解温度：４００℃）
（Ｄ）無機難燃助剤（ＫＧ−１１００）：モリブデン酸亜鉛をタルクに担持した無機難燃助剤（シャーウィン・ウィリアムス社製；商品名 ケムガード１１００）
硬化促進剤：ナフテン酸亜鉛の８質量％ミネラルスピリット溶液
比較例３で用いたエポキシ樹脂（ＹＸ−４０００）：ビフェニル型エポキシ樹脂（ジャパンエポキシレジン社製；商品名ＹＸ−４０００、エポキシ当量；１８６）
(C) Inorganic filler (AlOOH): Boehmite type aluminum hydroxide (manufactured by Kawai Lime Co., Ltd .; trade name BMT-3L, thermal decomposition temperature: 400 ° C.)
(D) Inorganic flame retardant aid (KG-1100): Inorganic flame retardant aid having zinc molybdate supported on talc (manufactured by Sherwin Williams; trade name Chemguard 1100)
Curing accelerator: 8% by mass mineral spirit solution of zinc naphthenate Epoxy resin (YX-4000) used in Comparative Example 3: Biphenyl type epoxy resin (manufactured by Japan Epoxy Resin; trade name YX-4000, epoxy equivalent; 186)
第２表において比較例１〜３は下記の理由により積層板の性能が評価できなかった。
比較例１：熱硬化性樹脂が析出しワニスを製造できなかった。
比較例２：成形性が不良であり積層板を作製できなかった。
比較例３：樹脂が分離し、プリプレグ及び積層板を作製できなかった。
In Table 2, Comparative Examples 1 to 3 could not evaluate the performance of the laminate for the following reasons.
Comparative Example 1: A thermosetting resin precipitated and a varnish could not be produced.
Comparative Example 2: The moldability was poor and a laminate could not be produced.
Comparative Example 3: The resin separated and a prepreg and a laminate could not be produced.
第１表から明らかなように、本発明の実施例は、銅箔ピール強度、カラス転移温度（Ｔｇ）、はんだ耐熱性、低熱膨張性、難燃性、銅付き耐熱性（Ｔ−３００）、低誘電特性、低誘電正接性、ドリル加工性の全てに優れている。
一方、第２表から明らかなように、比較例は、銅箔ピール強度、カラス転移温度（Ｔｇ）、はんだ耐熱性、低熱膨張性、難燃性、銅付き耐熱性（Ｔ−３００）、低誘電特性、低誘電正接性、ドリル加工性の全てを満たすものは無く、いずれかの特性に劣っている。
As is apparent from Table 1, the examples of the present invention are copper foil peel strength, crow transition temperature (Tg), solder heat resistance, low thermal expansion, flame resistance, heat resistance with copper (T-300), Excellent low dielectric properties, low dielectric loss tangent, and drillability.
On the other hand, as is clear from Table 2, the comparative examples are copper foil peel strength, crow transition temperature (Tg), solder heat resistance, low thermal expansion, flame retardancy, heat resistance with copper (T-300), low None of them satisfy all of the dielectric characteristics, low dielectric loss tangent, and drillability, and are inferior to any of the characteristics.
本発明の熱硬化性樹脂組成物は、はんだ耐熱性や難燃性に優れるのみならず、背景技術で述べた銅箔接着性（銅箔ピール強度）、銅付き耐熱性（Ｔ−３００）、ドリル加工性、比誘電率、誘電正接の全ての特性において近年の高密度化や高信頼性で要求されているレベルに達するものである。
従って、本発明の熱硬化性樹脂組成物を使用することにより、今日要求される配線板の高密度化や高信頼性が達成され、本発明の熱硬化性樹脂組成物を電子機器などの製造に広く用いることができる。
The thermosetting resin composition of the present invention is not only excellent in solder heat resistance and flame retardancy, but also described in the background art, copper foil adhesion (copper foil peel strength), heat resistance with copper (T-300), All the characteristics of drill workability, relative permittivity, and dielectric loss tangent have reached the level required for high density and high reliability in recent years.
Therefore, by using the thermosetting resin composition of the present invention, high density and high reliability of the wiring board required today are achieved, and the thermosetting resin composition of the present invention is manufactured for electronic devices and the like. Can be widely used.
Claims (4)