JP5708459B2 - Solid reduction furnace - Google Patents
Solid reduction furnace Download PDFInfo
- Publication number
- JP5708459B2 JP5708459B2 JP2011261905A JP2011261905A JP5708459B2 JP 5708459 B2 JP5708459 B2 JP 5708459B2 JP 2011261905 A JP2011261905 A JP 2011261905A JP 2011261905 A JP2011261905 A JP 2011261905A JP 5708459 B2 JP5708459 B2 JP 5708459B2
- Authority
- JP
- Japan
- Prior art keywords
- furnace
- reduction furnace
- solid reduction
- waveguide
- partition wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、固体還元炉に関する。 The present invention relates to a solid reduction furnace.
電気炉による鋼材の製造が盛んになるにつれ、その主原料であるスクラップの需要は逼迫し、電気炉での高級鋼製造に対する要請から還元鉄の需要が増大しつつある。 As the production of steel materials by electric furnaces becomes popular, the demand for scrap, which is the main raw material, is tightened, and the demand for reduced iron is increasing due to the demand for high-grade steel production in electric furnaces.
還元鉄を製造するプロセスの一つとして、粉状の鉄鉱石と、粉状の石炭やコークス等の炭材とを混合して、例えばペレットやブリケットのような塊成化物とし、この塊成化物を回転炉床炉に装入して高温に加熱することで、鉄鉱石中の酸化鉄を還元して固体状金属鉄を得る方法がある(例えば、以下の特許文献1〜4を参照。)。
As one of the processes for producing reduced iron, powdered iron ore and powdered coal or coke are mixed into agglomerates such as pellets and briquettes. Is charged into a rotary hearth furnace and heated to a high temperature to reduce iron oxide in iron ore to obtain solid metallic iron (see, for example,
上述のような方法において、回転炉床の加熱には一般的にバーナーが用いられ、還元鉄の原料である塊成化物は、バーナー及び回転炉床炉の炉壁からの輻射熱によって、外部から伝熱的に加熱される。そのため、炉床上で原料が重なった部位では、裏面側の加熱が不足することとなって、塊成化物全体として不均一な還元となり、平均還元率が低下することとなる。 In the method as described above, a burner is generally used to heat the rotary hearth, and the agglomerated material that is the raw material of the reduced iron is transmitted from the outside by radiant heat from the furnace wall of the burner and the rotary hearth furnace. Heated thermally. Therefore, in the part where the raw material overlaps on the hearth, the heating on the back side is insufficient, resulting in nonuniform reduction of the entire agglomerated material, and the average reduction rate is reduced.
ここで、鉄酸化物と炭素質物質からなる原料の還元反応等に必要な熱は、まず、炉床上部に位置する空間部でのバーナー燃焼による輻射加熱によって原料層上面に供給された後、原料層内の伝導伝熱によって原料層の下部へと供給されることとなる。従って、生産性を増大させるために原料層の厚みを厚くすると、原料層の下部への伝熱が遅れることとなって層下部の還元速度が低下し、滞留時間が長くなるにもかかわらず、生産性が低下する結果となる。 Here, the heat necessary for the reduction reaction of the raw material composed of iron oxide and carbonaceous material is first supplied to the upper surface of the raw material layer by radiant heating by burner combustion in the space located in the upper part of the hearth, It will be supplied to the lower part of the raw material layer by conduction heat transfer in the raw material layer. Therefore, if the thickness of the raw material layer is increased in order to increase productivity, the heat transfer to the lower part of the raw material layer is delayed, the reduction rate of the lower part of the layer is reduced, and the residence time is increased, Productivity is reduced.
また、近年では、塊成化物の加熱を、バーナーではなく、マイクロ波の照射により行う技術も提案されるようになってきている(以下の特許文献5を参照。)。
In recent years, a technique has also been proposed in which the agglomerated material is heated not by a burner but by microwave irradiation (see
しかしながら、上記特許文献5に記載の方法では、同文献に記載されているように、照射すべきマイクロ波の電力量は、塊成塊1トンあたり100〜200kWhとする必要がある。しかしながら、マイクロ波発振装置の出力は、一般的に100kW/台程度が工業的に使用可能な上限であって、マイクロ波単独で、1日に数十トンもの大量の生産量を要求される塊成化物の加熱・還元処理を行うことは、極めて困難である。
However, in the method described in
そのため、本発明者らは、操業コストの増加を抑制しながら、塊成化物の加熱ムラの発生を更に抑制可能な方法について鋭意検討を行った結果、バーナーによる加熱とマイクロ波による加熱とを併用することに想到した。 Therefore, as a result of intensive studies on a method that can further suppress the occurrence of heating unevenness of the agglomerate while suppressing an increase in operating costs, the present inventors have combined heating with a burner and heating with a microwave. I came up with the idea.
本発明者らは、バーナーによる加熱とマイクロ波による加熱とを併用するために鋭意検討を行った結果、固体還元炉に装入される塊成化物の主たる原料は、マイクロ波を効率良く吸収可能であることが明らかとなった。しかしながら、更なる検討を進めた結果、以下で説明するように、固体還元炉の内部環境に起因して、固体還元炉の自由空間にマイクロ波を拡散放射させた場合には加熱対象外である固体還元炉の天井や側壁部にもマイクロ波が吸収されてしまい、塊成化物の加熱に使用されるマイクロ波のエネルギー効率が低下してしまうことが明らかとなった。 As a result of diligent studies to use both heating by a burner and heating by a microwave, the main raw material of the agglomerate charged into the solid reduction furnace can efficiently absorb microwaves. It became clear that. However, as a result of further investigation, as described below, due to the internal environment of the solid reduction furnace, when microwaves are diffused and radiated in the free space of the solid reduction furnace, they are not subject to heating. It has been clarified that microwaves are also absorbed in the ceiling and side walls of the solid reduction furnace, and the energy efficiency of the microwaves used for heating the agglomerates is reduced.
以上のような理由から、本発明者らは、固体還元炉においてマイクロ波による加熱をバーナーによる加熱と併用する場合には、固体還元炉へのマイクロ波の照射方法が重要であることに想到した。 For the reasons described above, the present inventors have conceived that the microwave irradiation method to the solid reduction furnace is important when the microwave heating is used together with the heating by the burner in the solid reduction furnace. .
そこで、本発明は、上記問題に鑑みてなされたものであり、本発明の目的とするところは、固体還元炉の内部に対してマイクロ波を効率良く照射することが可能な、固体還元炉を提供することにある。 Therefore, the present invention has been made in view of the above problems, and an object of the present invention is to provide a solid reduction furnace capable of efficiently irradiating the inside of the solid reduction furnace with microwaves. It is to provide.
上記課題を解決するために、本発明のある観点によれば、酸化鉄原料と還元材とを混合して成形した塊成化物を、バーナー及び炉壁からの輻射熱により加熱して還元鉄を製造する固体還元炉において、前記固体還元炉の炉天井から炉床に向けて突出形成され、炉内を複数のゾーンに区分する1又は複数の仕切り壁と、前記仕切り壁のうちの一部又は全ての前記仕切り壁の内部に配設されており、前記塊成化物を加熱するためのマイクロ波が導波される複数の導波管と、を備え、前記仕切り壁の前記炉床に対向する底面には、マイクロ波照射口として前記導波管の端部が配設される固体還元炉が提供される。 In order to solve the above problems, according to a certain aspect of the present invention, an agglomerated material formed by mixing an iron oxide raw material and a reducing material is heated by radiant heat from a burner and a furnace wall to produce reduced iron. In the solid reduction furnace, one or a plurality of partition walls that project from the ceiling of the solid reduction furnace toward the hearth and divide the furnace into a plurality of zones, and a part or all of the partition walls A plurality of waveguides through which microwaves for heating the agglomerated material are guided, the bottom surface of the partition wall facing the hearth Provides a solid reduction furnace in which the end of the waveguide is disposed as a microwave irradiation port.
前記仕切り壁の内部に配設された前記導波管と前記仕切り壁を形成する耐火材との間に、前記導波管を冷却する冷却機構が設けられることが好ましい。 It is preferable that a cooling mechanism for cooling the waveguide is provided between the waveguide disposed inside the partition wall and a refractory material forming the partition wall.
前記仕切り壁の内部では、前記固体還元炉の幅方向に隣り合う一方の前記導波管のE面と、もう一方の前記導波管のH面と、が対向するように、前記複数の導波管が配設されてもよい。 Inside the partition wall, the plurality of waveguides are arranged such that the E surface of one of the waveguides adjacent to the width direction of the solid reduction furnace faces the H surface of the other waveguide. A wave tube may be provided.
前記炉内において前記塊成化物の進行方向に沿って、内部に複数の前記導波管が配設された複数の前記仕切り壁が配設されており、互いに隣り合う前記仕切り壁では、一方の前記仕切り壁の内部に設けられた前記複数の導波管の配置と、もう一方の前記仕切り壁の内部に設けられた前記複数の導波管の配置とが、千鳥配置となっていてもよい。 In the furnace, a plurality of the partition walls in which a plurality of the waveguides are disposed are arranged along the advancing direction of the agglomerated material, and in the partition walls adjacent to each other, The arrangement of the plurality of waveguides provided inside the partition wall and the arrangement of the plurality of waveguides provided inside the other partition wall may be staggered. .
前記仕切り壁の内部では、前記固体還元炉の幅方向に沿って、前記複数の導波管が等間隔に配設されていてもよい。 Inside the partition wall, the plurality of waveguides may be arranged at equal intervals along the width direction of the solid reduction furnace.
前記仕切り壁の前記炉床に対向する底部には、炉床方向からのマイクロ波の反射波を更に反射させる金属板が配設されてもよい。 A metal plate that further reflects a reflected wave of microwaves from the hearth direction may be disposed on a bottom portion of the partition wall facing the hearth.
以上説明したように本発明によれば、固体還元炉の天井から突出形成された仕切り壁の内部に複数の導波管を設け、仕切り壁の底面からマイクロ波を照射することで、固体還元炉の内部に対してマイクロ波を効率良く照射することが可能となる。その結果、固体還元炉に装入された塊成化物にマイクロ波が効率良く吸収されることとなり、塊成化物の平均還元率を向上させることが可能となる。 As described above, according to the present invention, a solid reduction furnace is provided by providing a plurality of waveguides inside a partition wall protruding from the ceiling of the solid reduction furnace and irradiating microwaves from the bottom surface of the partition wall. It becomes possible to efficiently irradiate the inside of the microwave. As a result, microwaves are efficiently absorbed by the agglomerate charged in the solid reduction furnace, and the average reduction rate of the agglomerate can be improved.
以下に添付図面を参照しながら、本発明の好適な実施の形態について詳細に説明する。なお、本明細書及び図面において、実質的に同一の機能構成を有する構成要素については、同一の符号を付することにより重複説明を省略する。 Exemplary embodiments of the present invention will be described below in detail with reference to the accompanying drawings. In addition, in this specification and drawing, about the component which has the substantially same function structure, duplication description is abbreviate | omitted by attaching | subjecting the same code | symbol.
(還元鉄の製造工程について)
本発明の実施形態に係る固体還元炉について説明するに先立ち、まず、図1を参照しながら、一般的な還元鉄の製造工程について、詳細に説明する。図1は、一般的な還元鉄の製造工程を説明するための説明図である。
(About manufacturing process of reduced iron)
Prior to describing the solid reduction furnace according to the embodiment of the present invention, a general process for producing reduced iron will be described in detail with reference to FIG. FIG. 1 is an explanatory diagram for explaining a general manufacturing process of reduced iron.
まず、製鉄ダスト(酸化鉄粉)及び鉄鉱石、粉鉱石などの酸化鉄原料と、石炭、コークス、微粒カーボン等の還元材とは、予めホッパー1等に格納されている。酸化鉄原料及び還元材は、予め設定された配合比となるように配合されて、粉砕機2に装入される。
First, iron oxide raw materials such as iron dust (iron oxide powder), iron ore, and powder ore, and reducing materials such as coal, coke, and fine carbon are stored in the
ボールミル等の振動ミルに代表される粉砕機2は、装入された酸化鉄原料及び還元材を、混合しながら所定の粒径まで粉砕する。粉砕後の酸化鉄原料及び還元材の粒径は、還元鉄の製造に用いられる回転炉床炉、流動床炉、シャフト炉等の固体還元炉に適した値とすることができる。粉砕後の酸化鉄原料及び還元材からなる混合物は、混練機3に運搬される。
A
混練機3は、粉砕機2により所定の粒径に粉砕された混合物を混練する。また、混練機3は、混合物の混練に際して、還元鉄の製造に用いる固体還元炉に適した水分量となるまで混合物に加水を行う調湿処理を施してもよい。混練機3の一例として、例えば、ミックスマーラー等を挙げることができる。混練機3によって混練された混合物は、成型機4に搬送される。
The
パンペレタイザー(皿型造粒機)、ダブルロール圧縮機(ブリケット製造機)、押し出し成型機等の成型機4は、酸化鉄原料及び還元材を含む混合物を成型し、例えばペレットのような塊成化物とする。ここで、塊成化物とは、ペレット、ブリケット、押し出し成型して裁断した成型品、粒度調整された塊状物等の粒状物・塊状物をいう。成型機4は、後述する乾燥・加熱還元後、例えば熱間にて溶解炉7に装入する際、炉内上昇ガス流で飛散しない程度の粒径以上の大きさとなるように、上記混合物を塊成化する。生成された塊成化物は、乾燥炉5へと装入される。
A
乾燥炉5は、塊成化物を乾燥して、後述する加熱還元工程に適した水分含有率(換言すれば、還元鉄の製造に用いる固体還元炉ごとに適した水分含有率:例えば、1%以下)となるようにする。所定の水分含有率となった塊成化物は、後述する固体還元炉6へと搬送される。
The drying
例えば回転炉床炉(Rotary Hearth Furnace:RHF)、流動床炉、シャフト炉等のような固体還元炉6は、装入された塊成化物を、LNGバーナーやCOGバーナー等の加熱雰囲気で加熱および還元し、還元鉄とする。固体還元炉は、塊成化物を例えば1000〜1300℃程度まで加熱して塊成化物の還元処理を行い、還元鉄を製造する。製造された還元鉄は、溶解炉7に搬送される。溶解炉7では、固体還元炉6で製造された還元鉄を溶解し、溶銑を生成する。生成された溶銑は、脱硫/脱炭工程、二次精錬工程、連続鋳造工程、圧延工程等を経て、各種鉄鋼製品へと加工されることとなる。
For example, the
以下では、固体還元炉の一例として回転炉床炉を例にとって、説明を行うものとする。しかしながら、本発明の実施形態に係る固体還元炉が、回転炉床炉に限定されるわけではない。 In the following, a rotary hearth furnace will be described as an example of the solid reduction furnace. However, the solid reduction furnace according to the embodiment of the present invention is not limited to the rotary hearth furnace.
(回転炉床炉について)
続いて、図2を参照しながら、還元鉄の製造方法で用いられる固体還元炉の一例である回転炉床炉について、詳細に説明する。図2は、固体還元炉の一例である回転炉床炉を説明するための説明図である。
(About rotary hearth furnace)
Next, a rotary hearth furnace which is an example of a solid reduction furnace used in the method for producing reduced iron will be described in detail with reference to FIG. FIG. 2 is an explanatory diagram for explaining a rotary hearth furnace which is an example of a solid reduction furnace.
回転炉床炉21は、例えば図2上段に示したように略円柱状の形状を有しており、例えば回転炉床炉21の上面等に設けられた装入口から塊成化物が装入される。装入された塊成化物は、炉内を周方向に沿って移動しながら加熱・還元されて還元鉄となり、炉内から取り出される。
The
回転炉床炉21を周方向に沿って展開した場合の模式図を、図2下段に示す。
回転炉床炉21の内部には、回転炉床炉21内を周方向に沿って移動可能な回転炉床25が設けられている。装入口27から装入されたブリケットBは、回転炉床25上に展開される。ブリケットBは、熱間レベラー29によって平坦にならされ、炉内を回転炉床25の移動に伴って移動していく。ブリケットBは、移動の過程で、炉壁又は炉上のバーナー31によって生じた高温燃焼ガスの輻射熱により加熱され、ブリケットB中の還元材により酸化鉄原料が還元される。還元された酸化鉄原料である還元鉄は、ディスチャージャー33により回転炉床炉21の内部から払い出されることとなる。
A schematic diagram when the
Inside the
回転炉床炉21内を移動するブリケットBは、高温燃焼ガスの輻射熱によりブリケットBの外側から内部に向かって温度が上昇していき、ブリケットの還元反応は、ブリケットの外周から中心部に向かって進行する。この際、ブリケットBの内部では、ブリケット中に含まれる酸化鉄成分(FeOやFe2O3等)がブリケット中に含まれる還元材(炭素C)により還元され、還元鉄(Fe)となっていく。
The briquette B moving in the
ここで、回転炉床炉21の内部は、図2下段に示したように、仕切り壁(又は、たれ壁)35と呼ばれる、炉の天井から突出形成された壁により、複数のゾーンに区分されていることが多い。回転炉床炉21では、ゾーン毎に、バーナーの熱量や、気体雰囲気や、空気比や、2次空気量等の制御が行われ、還元鉄が製造される。仕切り壁35の高さ(回転炉床炉21の天井位置から仕切り壁35の下端までの高さ)は、回転炉床炉21の大きさ等に応じて適宜設定されるものであるが、例えば、回転炉床炉21の高さに対して2/3程度となるくらいまで、炉天井から突出形成される。従って、仕切り壁35の底面(炉床と対向する底面)と炉床との間の離隔距離は、回転炉床炉21の高さに対して、1/3程度となる。
Here, the interior of the
ブリケットの装入口27の近傍に位置する第1のゾーンおよび第1のゾーンに隣接するゾーンである第2のゾーンは、回転炉床炉21に装入されたブリケットBの昇温を主目的とするゾーンである。また、第2のゾーンに連続する第3のゾーン以降は、ブリケットBの還元を主目的とするゾーンである。ここで、第1のゾーンおよび第2のゾーンを総称して、加熱・還元の最初期と称することとし、第3のゾーン以降を還元期と称することとする。
The first zone located in the vicinity of the
バーナー31によって生じた高温燃焼ガスにより、加熱・還元の最初期における塊成化物の温度は、1200℃程度まで昇温し、還元期以降は、1200〜1300℃程度を保持することとなる。
Due to the high-temperature combustion gas generated by the
(バーナー加熱とマイクロ波加熱との併用について)
本発明者らは、先に説明したように、操業コストの増加を抑制しながら、塊成化物の加熱ムラの発生を更に抑制可能な方法について鋭意検討を行った結果、バーナーによる加熱とマイクロ波による加熱とを併用することに想到した。
(Combined use of burner heating and microwave heating)
As described above, the present inventors conducted extensive studies on a method that can further suppress the occurrence of heating unevenness of the agglomerate while suppressing an increase in operating cost. I came up with the combined use of heating.
本発明者らは、バーナーによる加熱とマイクロ波による加熱とを併用するために鋭意検討を行った結果、固体還元炉に装入される塊成化物の主たる原料は、マイクロ波を効率良く吸収可能であることが明らかとなった。以下、この点について、式を参照しながら詳細に説明する。 As a result of diligent studies to use both heating by a burner and heating by a microwave, the main raw material of the agglomerate charged into the solid reduction furnace can efficiently absorb microwaves. It became clear that. Hereinafter, this point will be described in detail with reference to equations.
物質に吸収される単位体積あたりのマイクロ波のエネルギーPabsは、以下の式11のように表される。以下の式11を参照するとわかるように、加熱される物質(被加熱物質)に吸収される単位体積あたりのマイクロ波のエネルギーPabsは、被加熱物質の導電率、誘電率及び透磁率に依存していることがわかる。従って、下記式11で表されるPabsは、被加熱物質のマイクロ波の吸収効率に関係する量であるともいえる。 The microwave energy P abs per unit volume absorbed by the substance is expressed as the following Expression 11. As can be seen by referring to Equation 11 below, the microwave energy P abs per unit volume absorbed by the substance to be heated (substance to be heated) depends on the conductivity, dielectric constant and permeability of the substance to be heated. You can see that Therefore, it can be said that P abs represented by the following formula 11 is an amount related to the microwave absorption efficiency of the heated material.
ここで、上記式11において、
σ :被加熱物質の導電率 [S/m]
f :マイクロ波の周波数 [Hz]
ε0:真空中の誘電率 [F/m]
ε”:被加熱物質の比誘電率の虚数部
μ0:真空中の透磁率 [H/m]
μ”:被加熱物質の比透磁率の虚数部
E :マイクロ波により形成される電界強度 [V/m]
H :マイクロ波により形成される磁界強度 [A/m]
π :円周率
である。
Here, in Equation 11 above,
σ: Conductivity of heated material [S / m]
f: Microwave frequency [Hz]
ε 0 : dielectric constant in vacuum [F / m]
ε ″: Imaginary part of relative permittivity of heated material μ 0 : Permeability in vacuum [H / m]
μ ”: Imaginary part of relative permeability of heated material E: Electric field strength formed by microwave [V / m]
H: intensity of magnetic field formed by microwave [A / m]
π: Pi ratio.
以下に、塊成化物の原料となる酸化鉄及び炭素材(還元材)と、一般的に使用される耐火炉材とについて、比誘電率の虚数部ε”の値をまとめて示す。 The values of the imaginary part ε ″ of the relative dielectric constant are collectively shown below for the iron oxide and carbon material (reducing material) that are the raw materials of the agglomerated material and the refractory furnace materials that are generally used.
比誘電率の虚数部ε”
・代表的な耐火炉材であるアルミナ:0.004〜0.01
・粉状の炭素粉:10〜50
・酸化鉄:0.1〜10
Imaginary part of dielectric constant ε ”
Alumina, which is a typical refractory furnace material: 0.004 to 0.01
・ Powdered carbon powder: 10-50
・ Iron oxide: 0.1-10
上記より明らかなように、塊成化物の原料となる酸化鉄及び炭素材は、乾燥炉等において一般的に使用される耐火炉材に対して比誘電率の虚数部ε”の値が大きく、酸化物及び炭素材(還元材)にマイクロ波のエネルギーをより多く吸収させることが可能である。また、酸化鉄及び炭素粉の値に比べ、代表的な耐火炉材であるアルミナの値は、1000分の1程度の小さな値となっており、耐火炉材は、マイクロ波のエネルギーを多く吸収しないことがわかる。従って、塊成化物が挿入された炉内でマイクロ波を照射した場合、耐火炉材で被覆されている炉壁等へのエネルギー供給は少なく、炉内温度の上昇を抑制したまま原料である塊成化物の温度のみを、効率よく上昇させることが可能となる。 As is clear from the above, the iron oxide and carbon material used as the raw material for the agglomerate have a large value of the imaginary part ε ″ of the relative dielectric constant relative to the refractory furnace material generally used in a drying furnace or the like, The oxide and carbon material (reducing material) can absorb more microwave energy, and the value of alumina, which is a typical refractory furnace material, compared to the values of iron oxide and carbon powder, The value is about 1/1000, and it can be seen that the refractory furnace material does not absorb much microwave energy, so when the microwave is irradiated in the furnace in which the agglomerates are inserted, There is little energy supply to the furnace wall etc. which are coat | covered with the furnace material, and it becomes possible to raise only the temperature of the agglomerate which is a raw material efficiently, suppressing the raise in furnace temperature.
しかしながら、本発明者らが更なる検討を進めた結果、粉塵や、原料から発生した有機ガスの蒸気、金属粒子等といったヒュームが固体還元炉の内部に存在しており、これら粉塵やヒュームが固体還元炉の天井や炉壁に付着することで、本来はマイクロ波吸収特性の低い固体還元炉内の耐火材内張りが、塊成化物原料と同等のマイクロ波吸収特性を有してしまうことが明らかとなった。 However, as a result of further studies by the present inventors, fumes such as dust, organic gas vapor generated from raw materials, metal particles, etc. are present inside the solid reduction furnace, and these dust and fumes are solid. It is clear that the refractory lining in the solid reduction furnace, which originally has low microwave absorption characteristics, has the same microwave absorption characteristics as the agglomerate material by adhering to the ceiling and wall of the reduction furnace. It became.
従って、固体還元炉の自由空間にマイクロ波を拡散放射させた場合には、加熱対象外である固体還元炉の天井や炉壁にもマイクロ波が吸収されてしまい、塊成化物の加熱に使用されるマイクロ波のエネルギー効率が低下してしまうことが明らかとなった。 Therefore, when microwaves are diffused and radiated into the free space of the solid reduction furnace, the microwaves are also absorbed by the ceiling and furnace wall of the solid reduction furnace, which is not subject to heating, and used to heat the agglomerates. It became clear that the energy efficiency of microwaves to be reduced.
そのため、固体還元炉においてマイクロ波加熱をバーナー加熱と併用するためには、原料である塊成化物に対してなるべく多くのマイクロ波を吸収させるマイクロ波導波機構が必要となり、また、粉塵やヒューム等が存在する中でマイクロ波を照射するためには、導波機構の耐熱・防塵機構が重要になる。 Therefore, in order to use microwave heating together with burner heating in a solid reduction furnace, a microwave waveguide mechanism that absorbs as much microwave as possible to the agglomerated material is necessary, and dust, fume, etc. In order to irradiate microwaves in the presence of a wave, a heat- and dust-proof mechanism of a waveguide mechanism is important.
これらの点について、本発明者らが検討した結果、マイクロ波導波機構を塊成化物原料に近接させることで、上記式11の電界強度が高い状態でマイクロ波を塊成化物原料に照射することが有効であることに想到した。このような方法で炉床に敷き詰められた塊成化物原料全てを加熱するためには、複数のマイクロ波導波機構(例えば、導波管等)を用いることが求められる。また、〜1300℃という雰囲気下でマイクロ波導波機構を炉内に設けるためには、マイクロ波導波機構の耐火物による耐熱保護も重要であることに想到した。 As a result of the examination by the present inventors on these points, the agglomerate material is irradiated with microwaves in a state where the electric field strength of Equation 11 is high by bringing the microwave waveguide mechanism close to the agglomerate material. I realized that is effective. In order to heat all the agglomerated raw materials spread on the hearth by such a method, it is required to use a plurality of microwave waveguide mechanisms (for example, waveguides). Moreover, in order to provide a microwave waveguide mechanism in a furnace under an atmosphere of ˜1300 ° C., it has been conceived that heat-resistant protection with a refractory of the microwave waveguide mechanism is important.
以上のような観点から本発明者らが鋭意検討を行った結果、以下で説明するような本発明の実施形態に係る固体還元炉に想到した。 As a result of intensive studies by the present inventors from the above viewpoint, the inventors have arrived at a solid reduction furnace according to an embodiment of the present invention described below.
(使用するマイクロ波について)
続いて、本発明の実施形態に係る固体還元炉に用いられるマイクロ波について、簡単に説明する。
(About the microwave used)
Next, the microwave used in the solid reduction furnace according to the embodiment of the present invention will be briefly described.
マイクロ波は、一般的には、波長1mm〜1m、周波数300MHz〜300GHzの電磁波をいう。しかしながら、本実施形態に係る固体還元炉で着目しているように、マイクロ波を加熱手段として用いる(いわゆるマイクロ波加熱を行う)場合には、マイクロ波とは、いわゆるISM(Industry−Science−Medical)バンドに属する周波数帯域の電磁波を指す。 The microwave generally refers to an electromagnetic wave having a wavelength of 1 mm to 1 m and a frequency of 300 MHz to 300 GHz. However, as noted in the solid reduction furnace according to the present embodiment, when microwaves are used as heating means (so-called microwave heating is performed), microwaves are so-called ISM (Industry-Science-Medical). ) Refers to electromagnetic waves in the frequency band belonging to the band.
以下で説明する本発明の実施形態では、IMSバンドに属する周波数を有する電磁波であれば特に限定されず、例えば、2.45GHz帯(2.40GHz〜2.50GHz)、5.8GHz帯(5.725GHz〜5.875GHz)、及び、24GHz帯(24.0GHz〜24.25GHz)に属する周波数等を適宜選択することが可能である。しかしながら、マイクロ波の被加熱物内部への浸透はマイクロ波の波長に比例するため、上記ISMバンドのマイクロ波では、2.45GHz帯の浸透深さが一番大きくなり、数少ない導波管の本数で、固体還元炉全幅にわたって塊成化物の加熱を行うことができる。また、2.45GHzは電子レンジやその他のマイクロ波加熱に広く用いられており装置が安価である点や、発振機1台で数十kWまでの大出力の放射が可能である点などから、kWクラスの大出力が求められる本発明の設備コストとしても、他の2種の周波数の装置よりも安価に導入することができる。このため、本発明に用いるISMバンドのマイクロ波装置としては、2.45GHzのマイクロ波を発振可能なものが好ましい。 In the embodiment of the present invention described below, there is no particular limitation as long as the electromagnetic wave has a frequency belonging to the IMS band. For example, a 2.45 GHz band (2.40 GHz to 2.50 GHz), a 5.8 GHz band (5. 725 GHz to 5.875 GHz) and frequencies belonging to the 24 GHz band (24.0 GHz to 24.25 GHz) can be selected as appropriate. However, since the penetration of the microwave into the object to be heated is proportional to the wavelength of the microwave, the penetration depth of the 2.45 GHz band is the largest in the microwave of the ISM band, and the number of the few waveguides is small. Thus, the agglomerate can be heated over the entire width of the solid reduction furnace. In addition, 2.45 GHz is widely used for microwave ovens and other microwave heating, and the device is inexpensive. From the point that a single oscillator can emit a large output up to several tens of kW, The equipment cost of the present invention that requires a large output of the kW class can also be introduced at a lower cost than the other two frequency devices. For this reason, the ISM band microwave device used in the present invention is preferably capable of oscillating 2.45 GHz microwave.
(マイクロ波乾燥装置の構成について)
次に、図3を参照しながら、本発明の実施形態に係るマイクロ波照射装置の構成について、詳細に説明する。図3は、本発明の実施形態に係るマイクロ波照射装置の構成を説明するための説明図である。
(About the configuration of the microwave dryer)
Next, the configuration of the microwave irradiation apparatus according to the embodiment of the present invention will be described in detail with reference to FIG. FIG. 3 is an explanatory diagram for explaining the configuration of the microwave irradiation apparatus according to the embodiment of the present invention.
本発明の実施形態に係るマイクロ波照射装置100は、酸化鉄原料と還元材とを混合して成形した塊成化物を、バーナー及び炉壁からの輻射熱により加熱して還元鉄を製造する固体還元炉に対して利用されるものである。
The
本発明の実施形態に係るマイクロ波照射装置100は、図3に示したように、マイクロ波発振機101と、サーキュレータ103と、自動整合器107と、マイクロ波照射部材109と、を主に備え、これらの機器が導波管111により接続されている。なお、図3では、マイクロ波照射部材109や導波管111等といった各部材を支持する支持機構は、図示していない。
As shown in FIG. 3, the
マイクロ波発振機101は、例えばISMバンドに属する周波数を有するマイクロ波を発振する機器である。このマイクロ波発振機101は、kWクラスの出力を有するマイクロ波を発振可能な機器であることが好ましい。このマイクロ波発振機101により、例えば2.45GHz帯に属する周波数のマイクロ波が、後述するサーキュレータ103へと出力されることとなる。このマイクロ波発振機101は、公知のものを適宜選択して使用することが可能である。
The
サーキュレータ103は、例えば磁石を利用したマイクロ波の進行制御を行うことで、サーキュレータ103に入力されるマイクロ波を、マイクロ波発振機101から出力された入射波と、後述する自動整合器107側から戻ってきた反射波とに分離する。サーキュレータ103は、分離した入射マイクロ波を後述する自動整合器107側へと導波するとともに、反射マイクロ波を、アイソレータ105の側へと導波する。これにより、反射マイクロ波は、アイソレータ105内に設けられたダミー負荷(例えば、水など)に吸収され、マイクロ波発振機101側に戻らないようにすることができる。このようなサーキュレータ103を設けることにより、本発明の実施形態に係るマイクロ波照射装置100では、安定したマイクロ波の出力を行うことができる。このサーキュレータ103は、公知のものを適宜選択して使用することが可能である。
The
自動整合器107は、入射側のインピーダンスと、負荷側(すなわち、塊成化物からなる原料層側)のインピーダンスとの整合を取ることで負荷側からの反射波を低減し、反射波をほぼゼロとする機器である。この自動整合器107は、反射電界の位相及び強度を測定し、インピーダンス整合を自動で行うことで、上記のような反射波の低減を実現する。自動整合器107を設けて負荷側のインピーダンスにあわせた自動整合処理を実現することで、後述するマイクロ波照射部材109から、マイクロ波エネルギーを、安定して効率良く塊成化物に照射することが可能となる。
The
マイクロ波照射部材109は、バーナーによる輻射熱を利用した固体還元炉6に装入された塊成化物に対してマイクロ波を照射する部材である。このマイクロ波照射部材109には、マイクロ波照射部材109の先端(固体還元炉6内に設けられた開口部)から炉内に存在する粉塵やヒュームが逆流してこないように、ドライエアあるいは窒素、アルゴン等の不活性ガスが、所定の流量・流速となるように供給されていてもよい。この場合、マイクロ波照射部材109内に供給されるドライエアや不活性ガスは、固体還元炉6の内部の温度低下を防止するために、加熱されたガスとすることが好ましい。また、マイクロ波照射部材109と自動整合器107とを連結する導波管111には、炉内に存在する粉塵やヒュームが自動整合器107に流入しないように、防塵ガラスが設けられる。
The
このようなマイクロ波照射部材109としては、公知のあらゆるものを利用することが可能であるが、以下では、マイクロ波照射部材109として断面矩形状の導波管を用いる場合を例に挙げて、説明を行うものとする。
As the
導波管111は、マイクロ波を導波して所望の箇所へと導く管である。この導波管111の形状については、マイクロ波の導波特性等を考慮して適宜決定すればよく、導波管111自体についても、使用するマイクロ波の周波数や出力強度等に応じて、公知のものを適宜選択することができる。
The
(第1の実施形態)
<仕切り壁の構造について>
以下では、図4〜図10を参照しながら、本発明の第1の実施形態に係る固体還元炉6が備える仕切り壁35の構造について、詳細に説明する。図4及び図5は、本実施形態に係る固体還元炉6が備える仕切り壁について示した説明図である。図6は、マイクロ波照射口から照射されるマイクロ波の電界強度について示した説明図である。図7及び図8は、本実施形態に係る固体還元炉の仕切り壁について示した説明図である。図9A〜図10は、本実施形態に係る導波管の冷却機構を説明するための説明図である。
(First embodiment)
<About the structure of the partition wall>
Below, the structure of the
[マイクロ波照射部材の設置方法について]
図4は、固体還元炉6(例えば、回転炉床炉)の内部に設けられている、耐火材を用いて形成された仕切り壁35の一つを図示したものである。本実施形態に係る固体還元炉6では、炉内に設けられた少なくとも一つの仕切り壁35の内部には、図4に例示したように、固体還元炉6の炉幅方向に沿って複数のマイクロ波照射部材(例えば、複数の導波管)109が等間隔に配設されている。なお、本実施形態に係る仕切り壁35の内部におけるマイクロ波照射部材109の配置は、等間隔での配置に限定されるわけではないが、以下で説明するような加熱分布の均一化を図るためには、マイクロ波照射部材109を等間隔に配設することが好ましい。
[Installation method of microwave irradiation member]
FIG. 4 illustrates one of the
図5は、図4に示した仕切り壁35を炉幅方向に切断した場合の断面を、模式的に示したものである。仕切り壁35の内部に設けられた各導波管109の炉床側の端部は開口部となっており、この開口部は仕切り壁35の底面に位置している。この導波管109の開口部が、マイクロ波照射口として機能し、仕切り壁35の炉床に対向する底部から炉床上に装入された塊成化物へと、マイクロ波が照射されることとなる。
FIG. 5 schematically shows a cross section when the
ここで、先だって説明したように、固体還元炉6の内部には、塊成化物原料に起因する粉化粉塵や、金属粒子や有機ガス蒸気(ヒューム)が存在しているため、これらの粉塵やヒュームが導波管109の内部に侵入すると、アーク放電が発生する可能性が高くなる。このような粉塵やヒューム等(以下、粉塵等ともいう。)の導波管内部への侵入を防止するために、導波管109の先端部(炉内に設けられた端部)に防塵板としてAl2O3、ガラス、ガラスファイバ等の耐火セラミックスを貼り付けて、導波管の先端を閉塞することが考えられる。しかしながら、このように先端部が閉塞された導波管を長期間使用すると、炉内の粉塵等が防塵板表面に付着してしまう。一方で、導波管の先端部はマイクロ波の電界強度が強い状態であるため、粉塵等の汚れが付着した防塵板表面でマイクロ波の吸収が発生し、防塵板が加熱により溶損してしまう可能性がある。
Here, as described above, since there are pulverized dust, metal particles, and organic gas vapor (fumes) due to the agglomerated material in the
そこで、本実施形態に係る固体還元炉6では、防塵板への炉内粉塵等の付着・積層によるマイクロ波吸収発生を抑制するために、導波管109の先端に上記のような防塵板は敷設せず、導波管109の先端は、開口端としている。更に、導波管の開口端から粉塵等の侵入を防止するために、導波管109の内部には、先述のように、ドライエア又は窒素、アルゴン等の不活性ガスを防塵ガスとして流し、導波管先端から適度なガス流が炉内に向けて噴射されるようにしている。
Therefore, in the
また、図5に示したように、仕切り壁35の底部には、マイクロ波を反射させるための金属板151が埋設されている。炉床に向けてマイクロ波照射口から放射されたマイクロ波は、炉床等によって反射されて、マイクロ波照射口へと戻ってくる場合がある。仕切り壁35の底部に、マイクロ波を反射させることが可能な金属板151を設けることで、炉床方向からのマイクロ波の反射波を更に反射させることが可能となり、仕切り壁35の底面と炉床との間の空間にマイクロ波を閉じ込めることが可能となる。その結果、マイクロ波の空間密度が増加することとなり、仕切り壁35の底面を通過する塊成化物に対して、効率良くマイクロ波を吸収させることができ、塊成化物の加熱効率を向上させることができる。
Further, as shown in FIG. 5, a
なお、本実施形態に係る金属板151は、仕切り壁35における耐火材の骨格として機能する強度部材として用いられていなくともよく、マイクロ波の反射部材(すなわち、導体)として機能すればよい。従って、仕切り壁35の底面に埋設させる金属板151は、導体として機能するものであれば、任意の金属を使用することが可能である。なお、以下で説明するような冷却機構153が導波管109の外周に設置されない場合には、金属板151の周囲の温度が1000℃超になる場合があるため、かかる金属板151としてステンレス系の金属板を用いることが好ましい。また、以下で説明するような冷却機構153が導波管109の外周に設置される場合には、金属板151として、ステンレス系の金属板の他に、アルミ系の金属板や、銅系の金属板も使用することが可能である。
The
また、本実施形態に係る仕切り壁35に設けられた導波管109の外周には、金属製の導波管109を冷却するための冷却機構153が設けられる。この冷却機構153は、導波管109を冷却するための水冷配管であることが好ましい。なお、この冷却機構153については、以下で改めて詳細に説明する。
A
導波管109、金属板151及び冷却機構153の周囲には、所定の耐火材155が配設されて、仕切り壁35を形成している。この耐火材155は、固体還元炉6の炉内温度を導波管109、金属板151及び冷却機構153に伝導することや、導波管109、金属板151及び冷却機構153が炉内の腐食雰囲気により腐食することを防止するとともに、冷却機構153により、固体還元炉6の内部温度が低下しないようにする。
A predetermined
図4及び図5に示したように、複数の導波管109を仕切り壁35の内部に配設することで、固体還元炉6の内部に新たな部材を設置しなくともよく、仕切り壁35による温度や雰囲気のゾーン管理に影響を与えることなく、塊成化物原料に効率良くマイクロ波を照射することが可能となる。
As shown in FIGS. 4 and 5, by arranging the plurality of
また、各導波管109の開口部から放射されるマイクロ波の電界強度は、図5下段に示したように、所定の広がりを持って分布している。ここで、上記式11からも明らかなように、塊成化物原料に吸収されるマイクロ波の量は、電界強度Eの2乗に比例する。塊成化物原料をなるべく炉幅方向に均一に加熱するために、各導波管109から放射されるマイクロ波の電界強度分布E2の和の炉幅方向の変動が、2倍を超えない程度であることが好ましい。
Further, the electric field intensity of the microwave radiated from the opening of each
ここで、各導波管109から放射されるマイクロ波の電界強度分布E2の和を考えるにあたって、図6に示したような正規化された電界強度分布を考える。図6に示したグラフ図は、塊成化物表面での電界強度の2乗の和の分布を示したものであり、縦軸は、正規化された電界強度の2乗の和に対応し、横軸は、炉幅方向位置を表している。実効的には、着目する導波管109から2つ離れた場所に位置する導波管109からの電界強度の影響はさほど大きくないため、着目する導波管109と、この導波管109に隣接する導波管109との和を考慮すればよい。このようにして電界強度E2の和を考えると、各導波管109から放射されるマイクロ波の電界強度E2の和は、図6に実線で示したような分布となる。
Here, when considering the sum of the electric field distribution E 2 of the microwave radiated from the
炉幅方向に沿って、電界強度E2の和の変動が2倍を超えない(換言すれば、電界強度E2の変動が±25%以下)であるためには、隣り合う導波管109の中間位置(図6における位置a)の電界強度(時間平均強度)が、導波管109の直下(図6における位置b)の電界強度の50%以上であればよい。このような条件が満たされることで、例えば図6に示したように、電界強度E2の和の分布は、強度0.75の位置を中心として、±25%以下の範囲に電界強度が存在することとなる。本実施形態に係る固体還元炉6では、この条件を満足するように、炉幅方向に隣り合う導波管109の離隔距離を決定する。
In order for the fluctuation of the sum of the electric field strengths E 2 not to exceed twice the furnace width direction (in other words, the fluctuation of the electric field intensity E 2 is ± 25% or less), the
なお、炉幅方向に隣り合う導波管109の離隔距離は、実際の仕切り壁35の寸法や、導波管109の寸法等に応じて、事前の実験により決定することができる。また、炉幅方向に隣り合う導波管109の離隔距離は、実際の仕切り壁35の寸法や、導波管109の寸法等を利用して、離隔距離をパラメータとして変化させながら、上記非特許文献1に示したような公知の有限要素法に基づく電界強度シミュレーションを行うことで、決定することができる。すなわち、隣り合う導波管109の離隔距離を変えながら、以下の式12で表されるヘルムホルツ方程式を有限要素法により解析し、上記のような条件を満足する離隔距離を決定すればよい。
The separation distance between the
なお、仕切り壁35の内部に設けられる導波管109の個数は、図4〜図6に示した例では5個となっているが、本実施形態に係る仕切り壁35の内部に設けられる導波管109の個数は、上記の例に限定されるわけではない。仕切り壁35の内部に設けられる導波管109の個数は、固体還元炉や導波管のサイズや、上記離隔距離等に応じて、適宜決定すればよい。
The number of
ここで、断面矩形状の導波管では、矩形状の断面を考えた場合に、長辺に対応する面と短辺に対応する面の2種類の面を考えることができる。ここで、長辺に対応する面は、E面(電界面)と呼ばれており、短辺に対応する面は、H面(磁界面)と呼ばれている。断面矩形状の方形導波管から放射されたマイクロ波は、E面の法線方向に広がり易いという性質を有している。 Here, in a waveguide having a rectangular cross section, when a rectangular cross section is considered, two types of surfaces, a surface corresponding to the long side and a surface corresponding to the short side, can be considered. Here, the surface corresponding to the long side is called an E surface (electric field surface), and the surface corresponding to the short side is called an H surface (magnetic field surface). Microwaves radiated from a rectangular waveguide having a rectangular cross section have a property of easily spreading in the normal direction of the E plane.
図4に示した例では、複数の導波管109は、仕切り壁35の炉幅方向に平行な面には各導波管109のE面が対向し、隣り合う導波管109のH面が互いに対向するように、仕切り壁35内に配置されている。しかしながら、本実施形態に係る固体還元炉6では、隣り合う導波管109のE面が互いに対向するように仕切り壁35内に配設されていてもよい。また、本実施形態に係る固体還元炉6では、図7に示したように、互いに隣り合う導波管109の向きが直交するように(換言すれば、隣り合う一方の導波管109のE面と、もう一方の導波管109のH面と、が対向するように)、仕切り壁35内に導波管109を配設してもよい。図7に示したように、E面とH面とを交互に配置することで、各導波管109から放射されるマイクロ波における干渉発生を抑制することができる。各導波管109から放射されるマイクロ波に干渉が発生した場合、干渉によって電界強度が高くなる部分と低くなる部分とが発生するため、加熱ムラが大きく発生する可能性が高くなる。従って、図7に示したように導波管109を配置して干渉の発生を抑制することにより、加熱ムラの発生を更に抑制することが可能となる。
In the example shown in FIG. 4, in the plurality of
なお、図7に示したように、導波管109の向きが直交するように導波管109を配置する場合であっても、図6と同様にして各導波管109から放射される電界強度Eの分布を考慮し、電界強度Eの2乗の和の炉幅方向の変動が2倍を超えないように、導波管109の間隔を決定することができる。
As shown in FIG. 7, even when the
[隣り合う仕切り壁間でのマイクロ波照射部材の設置方法について]
図8は、本実施形態に係る固体還元炉6の内部に設けられた仕切り壁35を、還元炉の天井側から見た場合の上面図である。
以上説明したように、本実施形態に係る固体還元炉6に設けられた複数の仕切り壁35の少なくとも一部には、マイクロ波を導波する複数の導波管109が設けられている。かかる場合において、塊成化物の進行方向(すなわち、炉床進行方向)に沿って設けられた複数の仕切り壁35における導波管109の配置は、図8に例示したように、進行方向前後の仕切り壁35に対して千鳥配置となっていることが好ましい。このような千鳥配置で導波管109を配設することで、固体還元炉6の幅方向全域を考えた場合の加熱ムラを低減することが可能となる。
[Installation method of microwave irradiation member between adjacent partition walls]
FIG. 8 is a top view when the
As described above, a plurality of
なお、図8に示した例では、一つの仕切り壁35の内部において、隣り合う導波管109のH面同士が対向するように配設されている場合について図示しているが、一つの仕切り壁35の内部に設けられた複数の導波管109の向きが図7に示したように直交している場合であっても、同様に千鳥配置とすることが可能である。
In the example illustrated in FIG. 8, the case where the H surfaces of the
[冷却機構について]
続いて、図9A〜図10を参照しながら、本実施形態に係る仕切り壁35に設けられる冷却機構について、簡単に説明する。
[Cooling mechanism]
Next, a cooling mechanism provided on the
図9Aは、本実施形態に係る仕切り壁35の一部を炉天井側から見た場合の上面図であり、図9Bは、仕切り壁35の内部に設けられる導波管109のうちの1本を、周囲の冷却配管153と共に、導波管周方向に展開した場合の展開図である。図9Aに示したように、本実施形態に係る導波管109と耐火物155との間には、導波管109の冷却を目的として、冷却機構153が導波管109の外面に沿って設けられている。導波管109に用いることが可能な金属は、約350℃超過の高温環境では強度が低下する可能性があるため、冷却機構153により導波管109を冷却して、導波管109の温度が約350℃以下となるようにする。このような冷却機構153の例としては、冷却水を通水させるための水冷配管を挙げることができる。なお、導波管109の温度が約350℃以下となるのであれば、冷却機構153は水冷配管に限定されるわけではない。
FIG. 9A is a top view when a part of the
本実施形態に係る冷却機構(例えば水冷配管)153は、図9Bに示したように、例えば、導波管の高さ方向に沿って導波管109の外周にジグザグに配設されていてもよく、導波管の周方向に沿ってラセン状に巻き付けられていてもよい。
As shown in FIG. 9B, the cooling mechanism (for example, water-cooled piping) 153 according to the present embodiment may be arranged in a zigzag manner on the outer periphery of the
水冷配管等の冷却機構153の外周には、図9Aに示したように耐火材155が設けられる。このような耐火材155を設けることで、冷却機構153を炉内雰囲気から遮断するとともに、冷却機構153によって炉内温度が低下することを防止する。
As shown in FIG. 9A, a
本実施形態に係る固体還元炉6では、既に敷設されている仕切り壁35の内部に冷却機構153を設けた導波管109を敷設すればよいため、冷却機構153の外周に設けるべき耐火材155として、仕切り壁35を形成している耐火材を利用することができる。
In the
なお、冷却機構153を備えた導波管109が埋設された仕切り壁35を新たに製造する場合には、冷却機構153の外周に耐火材155を敷設する作業が行われることとなるが、このような耐火材155の敷設方法については、公知の方法を適宜利用することが可能である。このような耐火物155の敷設方法として、例えば図10に示した方法を用いることが可能である。
In addition, when newly manufacturing the
すなわち、冷却機構(例えば水冷配管)153の外周に、まず、公知の断熱シートを配設したうえで、断熱シートの更に外周に、公知の背面断熱材を配設する。その上で、各種のステンレス(例えば、SUS310、SUS304等)を用いたスタッドをアンカーとして断熱シート及び背面断熱材に差し込んで敷設する。このようなスタッドとしては、図10に示したようなYスタッドを用いてもよいし、Vスタッドを用いてもよい。その上で、スタッドの敷設された背面断熱材上に、断熱性を有する耐火材を敷設する。固体還元炉6の内部は還元雰囲気となっているため、用いる耐火材は、アルカリ腐食性に優れた不定形耐火物を用いることが好ましい。このような不定形耐火物としては、例えば、CA6と呼ばれるCaO・6Al2O3等を用いることができる。
That is, after a known heat insulating sheet is first disposed on the outer periphery of the cooling mechanism (for example, water-cooled pipe) 153, a known back surface heat insulating material is disposed on the outer periphery of the heat insulating sheet. Then, studs using various stainless steels (for example, SUS310, SUS304, etc.) are used as anchors and inserted into the heat insulating sheet and the back heat insulating material and laid. As such a stud, a Y stud as shown in FIG. 10 or a V stud may be used. Then, a refractory material having a heat insulating property is laid on the back heat insulating material on which the stud is laid. Since the inside of the
以上、図9A〜図10を参照しながら、本実施形態に係る仕切り壁35に設けられる冷却機構について説明した。
The cooling mechanism provided on the
以上説明したように、本実施形態に係る固体還元炉6では、固体還元炉の炉天井から炉床に向けて突出形成され、炉内を複数のゾーンに区分する1又は複数の仕切り壁35の内部に、塊成化物を加熱するためのマイクロ波が導波される複数の導波管109が設けられ、仕切り壁の炉床に対向する底面に、マイクロ波照射口として導波管の端部が配設されている。このマイクロ波照射口から塊成化物に向けてマイクロ波が照射されることにより、塊成化物の近傍からマイクロ波を照射することが可能となり、塊成化物に対して効率良くマイクロ波を照射することができる。その結果、固体還元炉における加熱効率を更に向上させることが可能となる。
As described above, in the
以上、添付図面を参照しながら本発明の好適な実施形態について詳細に説明したが、本発明はかかる例に限定されない。本発明の属する技術の分野における通常の知識を有する者であれば、特許請求の範囲に記載された技術的思想の範疇内において、各種の変更例または修正例に想到し得ることは明らかであり、これらについても、当然に本発明の技術的範囲に属するものと了解される。 The preferred embodiments of the present invention have been described in detail above with reference to the accompanying drawings, but the present invention is not limited to such examples. It is obvious that a person having ordinary knowledge in the technical field to which the present invention pertains can come up with various changes or modifications within the scope of the technical idea described in the claims. Of course, it is understood that these also belong to the technical scope of the present invention.
例えば、鉄鉱石や製鉄ダスト等の酸化鉄粉と、炭材等の還元材とを混合した塊成化物を加熱して、固体状金属鉄を得る固体還元の機能のみを有する固体還元炉のみならず、固体還元の機能と、金属鉄とスラグの分離の機能と、を併せ持つ炉についても、本発明の技術的範囲に属するものである。 For example, if it is only a solid reduction furnace that has only the function of solid reduction to heat solid agglomerates by mixing iron oxide powders such as iron ore and iron-making dust and reducing materials such as charcoal, and obtaining solid metallic iron Of course, a furnace having both the function of solid reduction and the function of separating metallic iron and slag belongs to the technical scope of the present invention.
6 固体還元炉
35 仕切り壁
100 マイクロ波照射装置
101 マイクロ波発振機
103 サーキュレータ
105 アイソレータ
107 自動整合器
109 マイクロ波照射部材(導波管)
151 金属板
153 冷却機構
155 耐火物
6
151
Claims (6)
前記固体還元炉の炉天井から炉床に向けて突出形成され、炉内を複数のゾーンに区分する1又は複数の仕切り壁と、
前記仕切り壁のうちの一部又は全ての前記仕切り壁の内部に配設されており、前記塊成化物を加熱するためのマイクロ波が導波される複数の導波管と、
を備え、
前記仕切り壁の前記炉床に対向する底面には、マイクロ波照射口として前記導波管の端部が配設される
ことを特徴とする、固体還元炉。 In the solid reduction furnace for producing reduced iron by heating the agglomerate formed by mixing the iron oxide raw material and the reducing material with radiant heat from the burner and the furnace wall,
One or a plurality of partition walls formed to project from the ceiling of the solid reduction furnace toward the hearth, and divide the interior of the furnace into a plurality of zones;
A plurality of waveguides that are disposed inside a part or all of the partition walls and through which microwaves for heating the agglomerated material are guided;
With
A solid reduction furnace, wherein an end of the waveguide is disposed as a microwave irradiation port on a bottom surface of the partition wall facing the hearth.
ことを特徴とする、請求項1に記載の固体還元炉。 The cooling mechanism for cooling the waveguide is provided between the waveguide disposed inside the partition wall and a refractory material forming the partition wall. The solid reduction furnace described.
ことを特徴とする、請求項1又は2に記載の固体還元炉。 Inside the partition wall, the plurality of waveguides are arranged such that the E surface of one of the waveguides adjacent to the width direction of the solid reduction furnace faces the H surface of the other waveguide. The solid reduction furnace according to claim 1, wherein a wave tube is provided.
ことを特徴とする、請求項1〜3の何れか1項に記載の固体還元炉。 In the furnace, a plurality of the partition walls in which a plurality of the waveguides are disposed are arranged along the advancing direction of the agglomerated material, and in the partition walls adjacent to each other, The arrangement of the plurality of waveguides provided inside the partition wall and the arrangement of the plurality of waveguides provided inside the other partition wall are staggered. The solid reduction furnace according to any one of claims 1 to 3, wherein the solid reduction furnace is characterized.
ことを特徴とする、請求項1〜4の何れか1項に記載の固体還元炉。 The inside of the said partition wall WHEREIN: The said some waveguide is arrange | positioned at equal intervals along the width direction of the said solid reduction furnace, The any one of Claims 1-4 characterized by the above-mentioned. The solid reduction furnace described.
ことを特徴とする、請求項1〜5の何れか1項に記載の固体還元炉。
The metal plate for further reflecting the reflected wave of the microwave from the hearth direction is disposed at the bottom portion of the partition wall facing the hearth. The solid reduction furnace according to item.