JP5686463B2 - Flame shielding and smoke shielding cloth and shutter screen using the same - Google Patents

Flame shielding and smoke shielding cloth and shutter screen using the same Download PDF

Info

Publication number
JP5686463B2
JP5686463B2 JP2010133614A JP2010133614A JP5686463B2 JP 5686463 B2 JP5686463 B2 JP 5686463B2 JP 2010133614 A JP2010133614 A JP 2010133614A JP 2010133614 A JP2010133614 A JP 2010133614A JP 5686463 B2 JP5686463 B2 JP 5686463B2
Authority
JP
Japan
Prior art keywords
yarn
yarns
cloth
incombustible
flameproof
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2010133614A
Other languages
Japanese (ja)
Other versions
JP2011255066A (en
Inventor
進司 丸山
進司 丸山
中塚　宏文
宏文 中塚
崇介 森本
崇介 森本
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ashimori Industry Co Ltd
Original Assignee
Ashimori Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ashimori Industry Co Ltd filed Critical Ashimori Industry Co Ltd
Priority to JP2010133614A priority Critical patent/JP5686463B2/en
Publication of JP2011255066A publication Critical patent/JP2011255066A/en
Application granted granted Critical
Publication of JP5686463B2 publication Critical patent/JP5686463B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、不燃性の糸で製織された遮炎遮煙布、および、この遮炎遮煙布を用いたシャッタースクリーンに関する。   The present invention relates to a flameproof and smokeproof cloth woven with nonflammable yarn, and a shutter screen using the flameproof and smokeproof cloth.

従来から、例えば建物で火災が発生した際に炎や煙が広がるのを食い止める延焼防止装置に用いられるシャッタースクリーン等において、耐熱性を有する糸で製織された不燃性織布が使用されている（例えば、特許文献１参照）。このような不燃性織布を構成する織糸としては、シリカ繊維等の単糸を複数本撚り合わせた撚糸が用いられている。   Conventionally, non-combustible woven fabrics woven with heat-resistant yarn have been used in shutter screens and the like used in fire spread prevention devices that prevent flames and smoke from spreading when a fire occurs in a building, for example ( For example, see Patent Document 1). As the woven yarn constituting such a noncombustible woven fabric, a twisted yarn obtained by twisting a plurality of single yarns such as silica fibers is used.

特開平９−１８７５２４号公報JP-A-9-187524

しかしながら、シリカ繊維等は加熱により収縮するため、このシリカ繊維等の糸で製織された従来の不燃性織布は加熱により収縮する。熱収縮率が高いと不燃性織布の用途によっては問題が生じる。例えば、シャッタースクリーンの場合、火災時に熱収縮してしまうと、壁や床面との間に隙間を生じてしまい、十分な遮炎・遮煙性能が得られなくなる。
この対策として、従来では、製織後に、７００〜８００℃で熱処理を行って、織布をそれ以上熱収縮しないようにしてから、シャッタースクリーン等の製品に使用していた。しかし、この方法では製造コストが高くなる。 However, since silica fibers and the like shrink by heating, conventional non-combustible woven fabrics woven with yarns such as silica fibers shrink by heating. When the heat shrinkage rate is high, a problem occurs depending on the use of the noncombustible woven fabric. For example, in the case of a shutter screen, if the heat shrinks in the event of a fire, a gap is generated between the wall and the floor surface, and sufficient flameproof / smokeproof performance cannot be obtained.
As a countermeasure, conventionally, after weaving, heat treatment is performed at 700 to 800 ° C. so that the woven fabric is not further heat shrunk and used for products such as a shutter screen. However, this method increases the manufacturing cost.

そこで、本発明は、熱収縮率の低い遮炎遮煙布、および、この遮炎遮煙布を用いたシャッタースクリーンを提供することを目的とする。   Accordingly, an object of the present invention is to provide a flameproof and smokeproof cloth having a low heat shrinkage rate, and a shutter screen using the flameproof and smokeproof cloth.

課題を解決するための手段及び発明の効果Means for Solving the Problems and Effects of the Invention

本発明の遮炎遮煙布は、耐熱性および難燃性の高い有機繊維を混紡した紡績糸からなる２本の不燃ヤーンを、前記不燃ヤーンよりも熱収縮率が低い金属線に逆向きに巻き付けて形成されるダブルカバーリング糸で製織されていることを特徴とする。 The flameproof and smokeproof cloth of the present invention has two incombustible yarns made of spun yarn blended with organic fibers having high heat resistance and flame retardancy , opposite to a metal wire having a thermal contraction rate lower than that of the incombustible yarn. It is woven with a double covering yarn formed by winding.

この構成によると、遮炎遮煙布が加熱された際に、たとえ不燃ヤーンが熱収縮しても、金属線によってダブルカバーリング糸の熱収縮を防止することができる。したがって、熱収縮率の低い遮炎遮煙布が得られる。
また、遮炎遮煙の熱収縮率が低いため、従来の遮炎遮煙布のように、製織後、熱処理工程が不要となり、製造コストを低減することができる。
また、ダブルカバーリング糸は、不燃ヤーンを、この不燃ヤーンよりも熱収縮率の低い金属線の周囲に巻き付けた構成であるため、ダブルカバーリング糸が加熱された際にたとえ不燃ヤーンが熱収縮しても、ダブルカバーリング糸自体は熱収縮しにくい。したがって、このダブルカバーリング糸で製織された遮炎遮煙布も熱収縮しにくいため、熱収縮率の低い遮炎遮煙布を得ることができる。
また、不燃ヤーンの巻き密度を変えるだけで、ダブルカバーリング糸の太さを容易に調整することができる。また、金属線または不燃ヤーンの太さを変えることによっても、ダブルカバーリング糸の太さを容易に調整することができる。このようにダブルカバーリング糸の太さを容易に調整できるため、遮炎遮煙布の厚さを容易に調整することができる。
また、金属線は、ダブルカバーリング糸の芯材であるため、ねじれにくい。そのため、金属線のねじれによる強度低下を防止することができる。
また、ダブルカバーリング糸は、巻き強度や巻き密度を調整することで、嵩高にすることができるため、遮炎遮煙布を目が詰まった構造にすることができ、遮炎・遮煙性能を向上させることができる。
According to this configuration, even when the incombustible yarn is thermally contracted when the flameproof and smokeproof cloth is heated, the thermal contraction of the double covering yarn can be prevented by the metal wire. Accordingly, a flameproof and smokeproof cloth having a low heat shrinkage rate can be obtained.
Moreover, since the heat shrinkage rate of flame shielding and smoke shielding is low, a heat treatment step is not required after weaving as in the case of conventional flame shielding and smoke shielding cloth, and the manufacturing cost can be reduced.
In addition, the double covering yarn has a configuration in which an incombustible yarn is wound around a metal wire having a lower heat shrinkage rate than the incombustible yarn, so even when the double covering yarn is heated, the incombustible yarn is thermally contracted. Even so, the double covering yarn itself is less likely to heat shrink. Therefore, the flame-proof and smoke-proof cloth woven with this double covering yarn is not easily heat-shrinked, so that a flame-proof and smoke-proof cloth having a low heat shrinkage rate can be obtained.
In addition, the thickness of the double covering yarn can be easily adjusted simply by changing the winding density of the incombustible yarn. Further, the thickness of the double covering yarn can be easily adjusted by changing the thickness of the metal wire or the non-combustible yarn. Since the thickness of the double covering yarn can be easily adjusted in this way, the thickness of the flameproof and smokeproof cloth can be easily adjusted.
Moreover, since the metal wire is the core material of the double covering yarn, it is difficult to twist. Therefore, it is possible to prevent a decrease in strength due to the twist of the metal wire.
In addition, the double covering yarn can be made bulky by adjusting the winding strength and winding density, so the flameproof and smokeproof cloth can be made clogged, and the flameproof and smokeproof performance. Can be improved.

また、紡績糸は比較的安価であるため、遮炎遮煙布の材料コストを低減できる。また、紡績糸は嵩高であるため、遮炎遮煙布を目が詰まった構造にすることができる。そのため、遮炎遮煙布の遮炎・遮煙性能を向上させることができる。
 Moreover, since the spun yarn is relatively inexpensive, the material cost of the flameproof and smokeproof cloth can be reduced. Moreover, since the spun yarn is bulky, the flameproof and smokeproof cloth can be made to have a clogged structure. Therefore, it is possible to improve the flameproof / smokeproof performance of the flameproof / smokeproof cloth.

本発明のシャッタースクリーンは、上述の本発明の遮炎遮煙布を用いたことを特徴とする。 The shutter screen of the present invention is characterized by using the above-described flameproof and smokeproof cloth of the present invention.

この構成によると、低熱収縮率で、製造コストの低いシャッタースクリーンを得ることができる。   According to this configuration, it is possible to obtain a shutter screen with a low heat shrinkage rate and low manufacturing cost.

本発明の実施形態に係るシャッタースクリーンの斜視図である。It is a perspective view of the shutter screen which concerns on embodiment of this invention. シャッタースクリーンに適用される遮炎遮煙布の拡大平面図である。It is an enlarged plan view of the flame-proof smoke-proof cloth applied to a shutter screen. 遮炎遮煙布を構成する織糸を示す図である。It is a figure which shows the woven yarn which comprises a flame-proof smoke-proof cloth. 本発明の他の実施形態の遮炎遮煙布を構成する織糸を示す図である。It is a figure which shows the woven yarn which comprises the flame-proof smoke-proof cloth of other embodiment of this invention. 本発明の他の実施形態の遮炎遮煙布を構成する織糸を示す図である。It is a figure which shows the woven yarn which comprises the flame-proof smoke-proof cloth of other embodiment of this invention. 本発明の他の実施形態の遮炎遮煙布を構成する織糸を示す図である。It is a figure which shows the woven yarn which comprises the flame-proof smoke-proof cloth of other embodiment of this invention. 本発明の他の実施形態の遮炎遮煙布を構成する織糸を示す図である。It is a figure which shows the woven yarn which comprises the flame-proof smoke-proof cloth of other embodiment of this invention. 本発明の他の実施形態の遮炎遮煙布を構成する織糸を示す図である。It is a figure which shows the woven yarn which comprises the flame-proof smoke-proof cloth of other embodiment of this invention.

以下、本発明の実施の形態について説明する。
図１に示すように、本実施形態のシャッタースクリーン１は、建物の天井部に設置される巻取軸３と、この巻取軸３に巻き取られるスクリーン本体２と、巻取軸３の駆動手段（図示省略）等を備えている。火災発生時には、スクリーン本体２が巻取軸３から繰り出されて、建物の床面付近まで垂下されるようになっており、このスクリーン本体２によって、火災の延焼と、煙の拡大が防止される。また、スクリーン本体２には、避難通路として、縦方向のスリットが形成されていてもよい。 Embodiments of the present invention will be described below.
As shown in FIG. 1, the shutter screen 1 of the present embodiment includes a winding shaft 3 installed on a ceiling portion of a building, a screen body 2 wound around the winding shaft 3, and driving of the winding shaft 3. Means (not shown) and the like are provided. In the event of a fire, the screen body 2 is drawn from the take-up shaft 3 and hangs down to the vicinity of the floor of the building. This screen body 2 prevents the spread of fire and the spread of smoke. . The screen body 2 may be formed with a vertical slit as an escape passage.

スクリーン本体２は、遮炎遮煙布１０で構成されている。図２に示すように、遮炎遮煙布１０は、平織りの織布であり、織布を構成する経糸および緯糸としては、ダブルカバーリング糸（複合糸）１１が用いられている。   The screen body 2 is composed of a flameproof and smokeproof cloth 10. As shown in FIG. 2, the flameproof and smokeproof cloth 10 is a plain woven cloth, and double covering yarn (composite yarn) 11 is used as the warp and weft constituting the woven cloth.

図３に示すように、ダブルカバーリング糸１１は、金属線１４に、２本の不燃ヤーン１２、１３を逆向きに巻き付けることで形成されている。   As shown in FIG. 3, the double covering yarn 11 is formed by winding two incombustible yarns 12 and 13 around a metal wire 14 in opposite directions.

不燃ヤーン１２、１３は、スクリーン本体２において、主に遮炎・遮煙性能を担うものである。不燃ヤーン１２、１３の材料としては、シリカ繊維、ガラス繊維、バザルトクロス、ロックウール等の無機系繊維が用いられる。無機系繊維の中でも、特に、シリカ繊維を用いることが好ましい。シリカ繊維は１０００℃以上の耐熱性があるため、遮炎遮煙布が加熱されても不燃ヤーンから発炎を生じたり、繊維が焼失してその隙間から火炎が貫通することがないからである。不燃ヤーン１２、１３の糸の構造としては、モノフィフィラメント糸、マルチフィラメント糸、紡績糸（スパン糸）、上記構造の糸（モノフィラメント糸、マルチフィラメント糸、紡績糸）を複数本撚り合わせて形成される撚糸、上記構造の糸を複数本引き揃えて形成される引き揃え糸の何れであってもよい。不燃ヤーン１２、１３は、上記無機系繊維のいずれかの単体であっても、複数組み合わせたものであってもよい。
２本の不燃ヤーン１２、１３の構成（材料、構造、直径等）は、同じであっても、異なっていてもよい。
なお、モノフィラメント糸とは、１本の長繊維（フィラメント）からなる糸のことであり、マルチフィラメント糸とは、複数の長繊維（フィラメント）を引き揃えまたは撚り合わせて形成される糸である。以下、モノフィラメント糸とマルチフィラメント糸とをまとめてフィラメント糸という場合がある。また、紡績糸（スパン糸）とは、短繊維を紡いで形成される糸である。 The non-combustible yarns 12 and 13 are mainly responsible for the flame shielding and smoke shielding performance in the screen body 2. As a material for the incombustible yarns 12 and 13, inorganic fibers such as silica fiber, glass fiber, bazaruto cloth, rock wool and the like are used. Among inorganic fibers, it is particularly preferable to use silica fibers. This is because silica fibers have a heat resistance of 1000 ° C. or higher, so that even if the flameproof smoke shielding cloth is heated, no flame is generated from the noncombustible yarn, and the fibers are not burned out and the flame does not penetrate through the gap. . The structure of the non-combustible yarns 12 and 13 is formed by twisting a plurality of monofilament yarns, multifilament yarns, spun yarns (spun yarns), and yarns having the above structure (monofilament yarns, multifilament yarns, spun yarns). Any of a twisted yarn that is formed and an aligned yarn that is formed by aligning a plurality of yarns having the structure described above may be used. The non-combustible yarns 12 and 13 may be any one of the above inorganic fibers or a combination thereof.
The configuration (material, structure, diameter, etc.) of the two incombustible yarns 12 and 13 may be the same or different.
The monofilament yarn is a yarn composed of a single long fiber (filament), and the multifilament yarn is a yarn formed by drawing or twisting a plurality of long fibers (filaments). Hereinafter, the monofilament yarn and the multifilament yarn may be collectively referred to as a filament yarn. A spun yarn (spun yarn) is a yarn formed by spinning short fibers.

また、不燃ヤーン１２、１３として紡績糸（複数本の紡績糸からなる撚糸または引き揃え糸を含む）を用いる場合、アラミド繊維やポリアリレート繊維等の耐熱性および難燃性の高い有機系繊維を混紡した紡績糸を用いてもよい。シリカ繊維等の無機系繊維の短繊維は剛直であるため、単体では紡績しにくいが、上記有機系繊維を混紡することにより、上記有機系繊維がシリカ短繊維同士をつなぐ役目を果たし、紡績しやすくなる。さらに、遮炎遮煙布１０が柔軟になるという効果も得られる。アラミド繊維を混紡する場合の混合比率の一例を挙げると、質量比でシリカ繊維８０％に対してアラミド繊維２０％である。また、上記有機系繊維以外に、カーボン繊維等を混紡してもよい。   In addition, when using spun yarn (including twisted or drawn yarns composed of a plurality of spun yarns) as the incombustible yarns 12 and 13, organic fibers having high heat resistance and flame retardancy such as aramid fibers and polyarylate fibers are used. A blended spun yarn may be used. The short fibers of inorganic fibers such as silica fibers are rigid and difficult to spin by themselves, but by blending the organic fibers, the organic fibers play a role in connecting the silica short fibers together. It becomes easy. Furthermore, the effect that the flame barrier smoke proof cloth 10 becomes flexible is also acquired. An example of the mixing ratio in the case of blending aramid fibers is 20% aramid fibers with respect to 80% silica fibers by mass ratio. In addition to the organic fibers, carbon fibers or the like may be blended.

また、不燃ヤーン１２、１３としてマルチフィラメント糸を用いる場合、マルチフィラメント糸を構成する長繊維の少なくとも１つに、アラミド繊維やポリアリレート繊維等の耐熱性および難燃性の高い有機系繊維を用いてもよい。これにより、不燃ヤーン１２、１３の引張強度と柔軟性を向上させることができる。また、上記有機系繊維以外に、カーボン繊維等を混合して、マルチフィラメント糸を形成してもよい。   When multifilament yarns are used as the incombustible yarns 12 and 13, organic fibers having high heat resistance and flame retardancy such as aramid fibers and polyarylate fibers are used for at least one of the long fibers constituting the multifilament yarns. May be. Thereby, the tensile strength and softness | flexibility of the incombustible yarns 12 and 13 can be improved. In addition to the organic fibers, carbon fibers or the like may be mixed to form a multifilament yarn.

金属線１４は、スクリーン本体２において、主に遮炎遮煙布１０の強度と、詳細は後述する熱収縮防止機能を担うものである。金属線１４は、引張強度が高く、且つ、不燃ヤーン１２、１３よりも熱収縮率が低い線材で構成されている。線材の具体例としては、例えば、ステンレス鋼線、鉄線、ピアノ線等の金属線が挙げられる。熱収縮性、耐食性、経済性等の観点から、特にステンレス鋼線を用いることが好ましい。   In the screen main body 2, the metal wire 14 mainly bears the strength of the flame-proof and smoke-proof cloth 10 and the heat shrinkage prevention function described later in detail. The metal wire 14 is made of a wire having a high tensile strength and a lower thermal shrinkage than the non-combustible yarns 12 and 13. Specific examples of the wire include metal wires such as stainless steel wires, iron wires, and piano wires. In view of heat shrinkability, corrosion resistance, economy, etc., it is particularly preferable to use a stainless steel wire.

金属線１４の直径は、例えば０．１ｍｍ〜０．３ｍｍ程度であって、不燃ヤーン１２、１３の直径は、例えば０．１ｍｍ〜３ｍｍ程度である。２本の不燃ヤーン１２、１３の直径は同じであっても異なっていてもよい。
また、例えば、直径０．１５ｍｍの金属線１４に、直径１ｍｍの不燃ヤーン１２、１３をカバーリングする場合のカバーリングの巻き密度は、１５０回／ｍ〜２５０回／ｍである。 The diameter of the metal wire 14 is, for example, about 0.1 mm to 0.3 mm, and the diameter of the incombustible yarns 12 and 13 is, for example, about 0.1 mm to 3 mm. The diameters of the two incombustible yarns 12 and 13 may be the same or different.
Further, for example, when covering the incombustible yarns 12 and 13 having a diameter of 1 mm on the metal wire 14 having a diameter of 0.15 mm, the winding density of the covering is 150 times / m to 250 times / m.

上述したように、ダブルカバーリング糸１１は、シリカ繊維等の無機系繊維を用いて形成された不燃ヤーン１２、１３を、この不燃ヤーン１２、１３よりも熱収縮率の低い金属線１４の周囲に巻き付けた構成であるため、ダブルカバーリング糸１１が加熱された際に不燃ヤーン１２、１３が熱収縮しても、ダブルカバーリング糸１１自体は熱収縮しにくい。したがって、このダブルカバーリング糸１１で製織された遮炎遮煙布１０も熱収縮しにくいため、熱収縮率の低い遮炎遮煙布１０を得ることができる。   As described above, the double covering yarn 11 includes the non-combustible yarns 12 and 13 formed using inorganic fibers such as silica fibers around the metal wire 14 having a lower thermal shrinkage than the non-combustible yarns 12 and 13. Therefore, even when the non-combustible yarns 12 and 13 are thermally contracted when the double covering yarn 11 is heated, the double covering yarn 11 itself is not likely to thermally contract. Therefore, since the flameproof smoke-proof cloth 10 woven with the double covering yarn 11 is also difficult to heat shrink, the flameproof smoke-proof cloth 10 having a low heat shrinkage rate can be obtained.

従来の遮炎遮煙布は、シリカ繊維の単糸を撚り合わせて形成された撚糸で製織されている。このような撚糸は、加熱されるとシリカの熱収縮に伴って熱収縮するため、この撚糸で製織された織布は熱収縮率が高くなる。そのため、従来では、製織後、スクリーン本体に加工する前に、織布を加熱処理して予め熱収縮させて、それ以上熱収縮しないようにしている。
一方、本実施形態の遮炎遮煙布１０は、加熱処理をしなくても熱収縮率が低いため、上述したような、熱処理工程が不要となる。したがって、製造コストを低減することができる。 Conventional flameproof and smokeproof cloths are woven with twisted yarns formed by twisting together single yarns of silica fibers. When such a twisted yarn is heated, it thermally contracts with the thermal contraction of silica, so that the woven fabric woven with this twisted yarn has a high thermal shrinkage rate. For this reason, conventionally, after weaving and before processing into a screen body, the woven fabric is heat-treated and preliminarily heat-shrinked to prevent further heat-shrinking.
On the other hand, the flameproof and smokeproof cloth 10 of the present embodiment has a low thermal shrinkage rate even without heat treatment, and thus the heat treatment step as described above is not necessary. Therefore, the manufacturing cost can be reduced.

また、ダブルカバーリング糸１１は、金属線１４に２本の不燃ヤーン１２、１３を巻き付けた構造であるため、不燃ヤーン１２、１３の巻き密度を変えるだけで、ダブルカバーリング糸１１の太さを容易に調整することができる。また、金属線１４および２本の不燃ヤーン１２、１３のうちのいずれかの太さを変えることによっても、ダブルカバーリング糸１１の太さを容易に調整することができる。このようにダブルカバーリング糸１１の太さを容易に調整できるため、遮炎遮煙布１０の厚さを容易に調整することができる。
また、金属線１４は、ダブルカバーリング糸１１の芯材であるため、ねじれにくい。そのため、金属線１４のねじれによる強度低下を防止することができる。
また、ダブルカバーリング糸１１は、巻き強度や巻き密度を調整することで、嵩高にすることができるため、遮炎遮煙布１０を目が詰まった構造にすることができ、遮炎・遮煙性能を向上させることができる。 Further, since the double covering yarn 11 has a structure in which the two noncombustible yarns 12 and 13 are wound around the metal wire 14, the thickness of the double covering yarn 11 can be changed only by changing the winding density of the noncombustible yarns 12 and 13. Can be adjusted easily. Also, the thickness of the double covering yarn 11 can be easily adjusted by changing the thickness of one of the metal wire 14 and the two incombustible yarns 12 and 13. Thus, since the thickness of the double covering yarn 11 can be adjusted easily, the thickness of the flameproof smoke shielding cloth 10 can be adjusted easily.
Moreover, since the metal wire 14 is a core material of the double covering yarn 11, it is hard to twist. Therefore, the strength reduction due to the twist of the metal wire 14 can be prevented.
Further, since the double covering yarn 11 can be made bulky by adjusting the winding strength and winding density, the flame shielding and smoke shielding cloth 10 can be made in a clogged structure, and the flame shielding / shielding can be achieved. Smoke performance can be improved.

また、不燃ヤーン１２、１３として紡績糸（複数本の紡績糸からなる撚糸または引き揃え糸を含む）を用いた場合、紡績糸はフィラメント糸に比べて安価であるため、コストを低減できる。また、紡績糸は嵩高であるため、遮炎遮煙布１０を目が詰まった構造にすることができる。そのため、遮炎遮煙布１０の遮炎・遮煙性能を向上させることができる。   Further, when spun yarn (including twisted yarns or aligned yarns composed of a plurality of spun yarns) is used as the incombustible yarns 12 and 13, the spun yarn is less expensive than the filament yarn, so that the cost can be reduced. Moreover, since the spun yarn is bulky, the flameproof and smokeproof cloth 10 can be made to have a clogged structure. Therefore, it is possible to improve the flameproof / smokeproof performance of the flameproof / smokeproof cloth 10.

また、不燃ヤーン１２、１３としてフィラメント糸を用いた場合、表面が平滑なので意匠性に優れる。   Moreover, when filament yarn is used as the incombustible yarns 12 and 13, the surface is smooth and the design is excellent.

以上、本発明の好適な実施形態を説明したが、上記の実施形態は以下のように変更して実施することができる。また、下記の変更形態は、適宜組み合わせて実施することもできる。なお、上記実施形態と同様の構成を有するものについては、同じ符号を用いて適宜その説明を省略する。   The preferred embodiment of the present invention has been described above, but the above embodiment can be modified as follows. Also, the following modifications can be implemented in combination as appropriate. In addition, about the thing which has the structure similar to the said embodiment, the description is abbreviate | omitted suitably using the same code | symbol.

１］上記実施形態では、金属線１４に巻き付けられる２本の不燃ヤーン１２、１３は、共に、シリカ繊維等の無機系繊維を含んでいるが、２本の不燃ヤーン１２、１３の一方が、シリカ繊維等の無機系繊維を含む糸であれば、他方の不燃ヤーンは、シリカ繊維等の無機系繊維を含まない糸であってもよい。シリカ繊維等の無機系繊維を含まない不燃ヤーンの具体例としては、アラミド繊維やポリアリレート繊維等の有機系繊維の紡績糸またはフィラメント糸が挙げられる。 1] In the above embodiment, the two incombustible yarns 12 and 13 wound around the metal wire 14 both contain inorganic fibers such as silica fibers, but one of the two incombustible yarns 12 and 13 As long as the yarn includes inorganic fibers such as silica fibers, the other non-combustible yarn may be a yarn not including inorganic fibers such as silica fibers. Specific examples of incombustible yarns that do not contain inorganic fibers such as silica fibers include spun yarns or filament yarns of organic fibers such as aramid fibers and polyarylate fibers.

２］上記実施形態では、ダブルカバーリング糸１１は、１本の金属線１４を芯材とした構造であるが、２本以上の金属線を芯材としてもよい。この場合、芯材に用いる２本の金属線の構成（材料、構造、直径等）は、同じであっても、異なっていてもよい。 2] In the above embodiment, the double covering yarn 11 has a structure in which one metal wire 14 is used as a core material, but two or more metal wires may be used as a core material. In this case, the configuration (material, structure, diameter, etc.) of the two metal wires used for the core material may be the same or different.

３］上記実施形態では、本発明の複合糸として、金属線１４に２本の不燃ヤーン１２、１３を逆向きに巻き付けた構造のダブルカバーリング糸１１が用いられているが、本発明の複合糸に使用可能なカバーリング糸の構成はこれに限定されるものではない。
また、例えば、図４に示すように、金属線１４に、２本の不燃ヤーン１２、１３を同じ向きに交互に巻き付けた構造のカバーリング糸１１１でもよい。
また、例えば、金属線１４に、１本の不燃ヤーンを巻き付けた構造のシングルカバーリング糸でもよい。
また、例えば図５に示すように、金属線１４に、１本または複数本（図５では２本）の不燃ヤーン１２、１３を引き揃えたものを巻き付けた構造のカバーリング糸２１１でもよい。
また、例えば図６に示すように、金属線１４に、複数本（図６では２本）の不燃ヤーン１２、１３を撚り合わせたものを巻き付けた構造のカバーリング糸３１１でもよい。
また、例えば、ダブルカバーリング糸１１にさらに１本または複数本の不燃ヤーンを巻き付けた構造（合計３本以上の不燃ヤーンを巻き付けた構造）のカバーリング糸でもよい。
なお、複数本の不燃ヤーンを用いる場合、各不燃ヤーンの構成は、同じであっても、異なっていてもよい。 3] In the above embodiment, as the composite yarn of the present invention, the double covering yarn 11 having a structure in which the two incombustible yarns 12 and 13 are wound in the opposite directions around the metal wire 14 is used. The configuration of the covering yarn that can be used for the yarn is not limited to this.
For example, as shown in FIG. 4, a covering yarn 111 having a structure in which two incombustible yarns 12 and 13 are alternately wound around a metal wire 14 in the same direction may be used.
Further, for example, a single covering yarn having a structure in which one incombustible yarn is wound around the metal wire 14 may be used.
For example, as shown in FIG. 5, a covering yarn 211 having a structure in which one or a plurality (two in FIG. 5) of non-combustible yarns 12 and 13 are wound around a metal wire 14 may be wound.
For example, as shown in FIG. 6, a covering yarn 311 having a structure in which a plurality of (two in FIG. 6) non-combustible yarns 12 and 13 are twisted around a metal wire 14 may be wound.
Further, for example, a covering yarn having a structure in which one or more incombustible yarns are wound around the double covering yarn 11 (a structure in which a total of three or more incombustible yarns are wound) may be used.
In addition, when using a plurality of incombustible yarns, the configuration of each incombustible yarn may be the same or different.

４］本発明の複合糸は、カバーリング糸に限定されるものではない。
例えば図７に示すように、１本または複数本（図７では１本）の不燃ヤーンと金属線１４とからなる複数本の糸を、例えば３撚や８撚と呼ばれる撚り構造によって撚り合わせた撚糸４１１でもよい。但し、熱収縮を防止する観点と、金属線１４の露出を抑える観点からは、金属線１４を芯材としたカバーリング糸を用いる方が好ましい。
また、例えば、複数本の不燃ヤーンを引き揃えたものと、金属線１４とを撚り合わせた撚糸でもよい。
また、例えば、複数本の不燃ヤーンを撚り合わせたものと、金属線１４とを撚り合わせた撚糸でもよい。
また、例えば図８に示すように、上記実施形態のダブルカバーリング糸１１または上記した変更形態の複合糸を、複数本撚り合わせた複合糸５１１でもよい。なお、図８に示す複合糸５１１は、図４に示すカバーリング糸１１１を２本撚り合わせた構造である。
また、例えば、１本または複数本の不燃ヤーンと、１本または複数本の金属線を、引き揃えただけの複合糸（織糸）でもよい。
なお、複数本の不燃ヤーンを用いる場合、各不燃ヤーンの構成は、同じであっても、異なっていてもよい。複数本の金属線を用いる場合についても同様である。 4] The composite yarn of the present invention is not limited to the covering yarn.
For example, as shown in FIG. 7, a plurality of yarns composed of one or a plurality of (one in FIG. 7) non-combustible yarns and a metal wire 14 are twisted together by a twist structure called, for example, 3 twist or 8 twist. A twisted yarn 411 may be used. However, from the viewpoint of preventing thermal shrinkage and suppressing the exposure of the metal wire 14, it is preferable to use a covering yarn having the metal wire 14 as a core material.
Further, for example, a twisted yarn in which a plurality of incombustible yarns are aligned and a metal wire 14 is twisted may be used.
Further, for example, a twisted yarn obtained by twisting a plurality of incombustible yarns and a metal wire 14 may be used.
For example, as shown in FIG. 8, a double covering yarn 11 of the above embodiment or a composite yarn 511 obtained by twisting a plurality of composite yarns of the above-described modification may be used. The composite yarn 511 shown in FIG. 8 has a structure in which two covering yarns 111 shown in FIG. 4 are twisted together.
Further, for example, it may be a composite yarn (weaving yarn) in which one or more incombustible yarns and one or more metal wires are simply aligned.
In addition, when using a plurality of incombustible yarns, the configuration of each incombustible yarn may be the same or different. The same applies to the case of using a plurality of metal wires.

５］上記実施形態では、遮炎遮煙布１０を構成する経糸と緯糸には、同じダブルカバーリング糸１１が用いられているが、異なる構成（構造、材料、直径）の糸を用いてもよい。 5] In the above embodiment, the same double covering yarn 11 is used for the warp and the weft constituting the flameproof smoke-proof cloth 10, but a yarn having a different configuration (structure, material, diameter) may be used. Good.

６］上記実施形態では、遮炎遮煙布１０を構成する多数の経糸は、全て同じダブルカバーリング糸１１が用いられているが、構成（構造、材料、直径）の異なる２種類以上の糸を経糸に用いてもよい。緯糸についても同様である。 6] In the above embodiment, the same double covering yarn 11 is used for many warp yarns constituting the flameproof smoke-proof cloth 10, but two or more types of yarns having different configurations (structure, material, diameter) are used. May be used for warp. The same applies to the weft.

７］上記実施形態の遮炎遮煙布１０の織り構造は、平織りであるが、例えば、綾織り、朱子織り、斜紋織り等の平織り以外の織り構造であってもよい。 7] The woven structure of the flameproof and smoke-proof cloth 10 of the above embodiment is a plain weave, but may be a woven structure other than a plain weave such as a twill weave, satin weave, or a diagonal weave.

以上説明した実施形態及び変更形態では、本発明の遮炎遮煙布をシャッタースクリーンに適用した場合について説明したが、本発明の遮炎遮煙布の適用対象は、これに限られるものではない。   In the embodiment and the modified embodiment described above, the case where the flameproof and smokeproof cloth of the present invention is applied to the shutter screen has been described, but the application target of the flameproof and smokeproof cloth of the present invention is not limited to this. .

１ シャッタースクリーン
２ スクリーン本体
１０ 遮炎遮煙布
１１ ダブルカバーリング糸（複合糸）
１２、１３ 不燃ヤーン
１４ 金属線 1 Shutter screen 2 Screen body 10 Flameproof and smoke-proof cloth 11 Double covering yarn (composite yarn)
12, 13 Non-combustible yarn 14 Metal wire

Claims (2)

耐熱性および難燃性の高い有機繊維を混紡した紡績糸からなる２本の不燃ヤーンを、前記不燃ヤーンよりも熱収縮率が低い金属線に逆向きに巻き付けて形成されるダブルカバーリング糸で製織されていることを特徴とする遮炎遮煙布。 A double covering yarn formed by wrapping two incombustible yarns made of spun yarn blended with organic fibers having high heat resistance and flame retardancy around a metal wire having a heat shrinkage rate lower than that of the incombustible yarn. Flameproof and smokeproof cloth characterized by being woven. 前記請求項１に記載の遮炎遮煙布を用いたことを特徴とするシャッタースクリーン。 A shutter screen using the flameproof and smokeproof cloth according to claim 1 .
JP2010133614A 2010-06-11 2010-06-11 Flame shielding and smoke shielding cloth and shutter screen using the same Active JP5686463B2 (en)