JP5636750B2 - Thread and anti-counterfeit paper - Google Patents
Thread and anti-counterfeit paper Download PDFInfo
- Publication number
- JP5636750B2 JP5636750B2 JP2010134850A JP2010134850A JP5636750B2 JP 5636750 B2 JP5636750 B2 JP 5636750B2 JP 2010134850 A JP2010134850 A JP 2010134850A JP 2010134850 A JP2010134850 A JP 2010134850A JP 5636750 B2 JP5636750 B2 JP 5636750B2
- Authority
- JP
- Japan
- Prior art keywords
- magnetic
- thread
- layer
- paper
- white
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、偽造防止効果を持たせた紙媒体に用いるスレッドおよびこのスレッドを抄き込んだスレッド用紙に関するもので、特に磁気読み取り検証を行うための磁性剤を導入したタイプのスレッドおよびスレッド用紙に関する。 The present invention relates to a thread used for a paper medium having an anti-counterfeit effect and a thread paper incorporating the thread, and more particularly to a thread and thread paper of a type into which a magnetic agent for performing magnetic reading verification is introduced. .
従来、銀行券やパスポート、公的証明書、商品券等のセキュリティが必要な媒体における偽造防止対策として、樹脂やアルミ箔等を材料としたスレッドを媒体となる紙に抄き込んで特有の光沢や反射光を持つようにし、コピーや印刷等による偽造を困難にして偽造防止手段とする方法がとられていた。 Conventionally, as a measure to prevent counterfeiting in security-sensitive media such as banknotes, passports, official certificates, gift certificates, etc., a special gloss is created by embedding threads made of resin or aluminum foil on the media paper. In other words, a method for preventing forgery by copying or printing is used as a means for preventing forgery.
このようなスレッドはセキュリティスレッドとも呼ばれ、これを抄き込んだ用紙は特殊な用紙製造技術が必要なため、コピーやスキャナーによる偽造、あるいは印刷段階での偽造は困難であり、偽造防止手段とすることができる。
しかし、近年はスレッドの偽造品が出回るようになり、単純なスレッドのみでは偽造防止手段としては不十分であった。そこで、スレッドに特殊な磁性剤を導入し、磁性剤の有無を検知して、これを磁気読み取り装置により読み取って媒体の真贋を判定できるようにした技術が提案されていた。(特許文献1参照)
Such a thread is also called a security thread, and the paper that has been engraved with it requires special paper manufacturing technology, so it is difficult to forge with a copy or scanner, or forgery at the printing stage. can do.
However, in recent years, forged products of threads have come to the market, and simple threads alone are insufficient as a means for preventing forgery. Therefore, a technique has been proposed in which a special magnetic agent is introduced into the thread, the presence or absence of the magnetic agent is detected, and this is read by a magnetic reader to determine the authenticity of the medium. (See Patent Document 1)
上記のような磁気を検知することができる磁気スレッド用紙は、特殊な製法によるために一般には材料入手が困難であること、また特有の磁気特性を持たせること等により、通常の手段では偽造することは殆ど不可能にできる。これにより、高いセキュリティを有する偽造防止手段を実現することができる。 Magnetic sled paper that can detect magnetism as described above is generally difficult to obtain due to its special manufacturing method, and it is counterfeited by ordinary means due to its unique magnetic properties. It can be almost impossible. Thereby, the forgery prevention means with high security is realizable.
前記磁気スレッドに用いる磁性剤の主材料として、従来は鉄やコバルト、ニッケル等の金属、あるいはフェライト(酸化鉄化合物)や酸化クロムなどの金属酸化物が用いられており、一般的にはこれらの磁性材料を微細な粉体としてインキや樹脂などに混合して使用されている。 Conventionally, as the main material of the magnetic agent used for the magnetic thread, metals such as iron, cobalt and nickel, or metal oxides such as ferrite (iron oxide compound) and chromium oxide have been used. Magnetic materials are used as fine powders mixed with ink or resin.
前記のスレッドに用いられる磁性剤は、その金属の光学的性質のため黒色や黒灰色または茶色で濃く着色している。しかし、このような磁性剤を導入したスレッドを紙に抄き込んだ場合、紙層を通して磁性剤の色が媒体表面に浮き出して見えてしまうため、紙面の意匠性や美観を大きく損ねてしまうことがあった。実際の製品で意匠性が低いと商品価値も低くなってしまうため、これは大きな問題であった。 The magnetic agent used for the thread is darkly colored black, black gray or brown due to the optical properties of the metal. However, if a thread with such a magnetic agent is incorporated on paper, the color of the magnetic agent will appear on the surface of the medium through the paper layer, which greatly impairs the design and aesthetics of the paper. was there. This is a big problem because the product value is low if the design of the actual product is low.
このような問題に対しては、非磁性剤の性質を持つ金属層を導入してスレッド内の磁性剤を隠蔽することにより、磁性剤の色が紙の表面から見えないようにするという提案がされている。(特許文献2参照) For such problems, a proposal has been made to hide the magnetic agent in the thread by introducing a metal layer having the property of a non-magnetic agent so that the color of the magnetic agent cannot be seen from the surface of the paper. Has been. (See Patent Document 2)
しかしながらこの方法では、スレッド製造時に非磁性剤の金属層を導入する工程を追加
する必要が生じ、そのために工程数が増加して製造のスループットが悪化し、さらに製品コストが増大してしまうという問題があった。
However, in this method, it is necessary to add a step of introducing a metal layer of a non-magnetic agent at the time of thread manufacture, which increases the number of steps, deteriorates the manufacturing throughput, and further increases the product cost. was there.
本発明は上記問題を解決するためになされたものであり、スレッドに抄き込まれた磁性剤の色が媒体表面からは見えないようにして、媒体の意匠性や美観を向上させることができ且つスレッド製造のスループットやコストが増大しないセキュリティスレッド、およびこれを用いた偽造防止用紙を提供することを目的とする。 The present invention has been made to solve the above-mentioned problems, and it is possible to improve the design and aesthetics of the medium by preventing the color of the magnetic agent engraved on the thread from being seen from the surface of the medium. It is another object of the present invention to provide a security thread that does not increase the throughput and cost of thread manufacture, and a forgery prevention sheet using the security thread.
請求項1の発明に係るスレッドは、多層干渉フィルムの一方の面に、白色磁性剤または無色透明磁性剤を含む磁気層を積層し、前記基材と磁気層との間に、厚さ1μmで凹凸溝が間隔0.3μm、深さ0.4μmで刻まれた回折格子を有するUV硬化型インキからなる回折構造形成層および厚さ50nmのアルミニウムからなる蒸着加工層を積層し、白色磁性剤を含有した塩化ビニル酢酸ビニル共重合樹脂からなるマスク用インキを、厚さ1μmでパターン状に印刷塗布し白色磁気マスク層とし、マスクされた領域以外の前記蒸着加工層の露出部分を、ディメタライズ処理を行って除去し、この積層体の両面に白色微粉末のシリカフィラーを分散させた塩化ビニル酢酸ビニル共重合樹脂からなる接着剤を形成してなることを特徴とするスレッドである。
The thread according to the invention of
請求項2の発明に係るスレッドは、前記基材と前記磁気層とを備えたスレッドの両面に接着剤を含む接着層を備えたことを特徴とする。
A thread according to a second aspect of the present invention is characterized in that an adhesive layer containing an adhesive is provided on both sides of the thread including the base material and the magnetic layer.
請求項3の発明に係るスレッドは、前記磁性剤が、酸化チタンと酸化鉄を含むことを特徴とする。
The thread according to the invention of claim 3 is characterized in that the magnetic agent contains titanium oxide and iron oxide.
請求項4の発明に係る偽造防止用紙は、前記請求項1から3のいずれか一項に記載のスレッドが用紙に抄き込まれていることを特徴とする。
The anti-counterfeit paper according to the invention of claim 4 is characterized in that the thread according to any one of
本発明によれば、白色または無色透明の磁性剤を導入したスレッドを抄き込んだ偽造防止用紙とすることによって、用紙の表面から磁気層が透けて見えてしまうことを防ぎ、偽造防止用紙としての意匠性や外見的美観を高め、且つスレッド製造のコストやスループットが増大することなく偽造防止用紙が製造できる。 According to the present invention, by making a forgery-preventing paper incorporating a thread into which a white or colorless and transparent magnetic agent is introduced, it is possible to prevent the magnetic layer from being seen through the surface of the paper, The anti-counterfeit paper can be manufactured without increasing the cost and throughput of the thread manufacturing and improving the design and appearance of the paper.
以下、本発明に係るスレッドおよび偽造防止用紙の実施の形態を、図面に基づいて詳細説明する。最初に、埋め込みスレッドとして利用した事例を示す。
図1は、本発明におけるスレッドの第一の実施例の構成を示す断面図であり、この実施例は、用紙に埋め込んで使用するための埋め込みスレッドの構成を示している。
Embodiments of a thread and anti-counterfeit paper according to the present invention will be described below in detail with reference to the drawings. First, an example of using it as an embedded thread is shown.
FIG. 1 is a cross-sectional view showing a configuration of a first embodiment of a thread according to the present invention, and this embodiment shows a configuration of an embedding thread for embedding in a sheet.
(第一の実施例)
図1に示すように、スレッド用基材2の一方の面に白色磁気層3が積層され、パターン形成されている。白色磁気層3は基材2に接してパターン形成されているか、あるいは全面に積層されていてもよい。白色磁気層3の形成方法は、例えば、印刷インキに白色磁性体粒子を混合させた磁性インキを用いて印刷法により印刷を行ってパターン形成すればよい。
(First embodiment)
As shown in FIG. 1, a white magnetic layer 3 is laminated on one surface of a thread base material 2 to form a pattern. The white magnetic layer 3 may be patterned in contact with the substrate 2 or may be laminated on the entire surface. The white magnetic layer 3 may be formed by, for example, printing by a printing method using magnetic ink in which white magnetic particles are mixed with printing ink to form a pattern.
さらに基材2と白色磁気層3を挟み、その表裏両面に接着層4が積層されており、全体でスレッド1を構成している。接着層4は、偽造防止用紙などの媒体に接着するための接着剤を塗布してあり、紙の中にこのスレッド1を抄き込んだ際に、この接着層によりスレッド1と紙とを接着する。
Further, the base material 2 and the white magnetic layer 3 are sandwiched, and the adhesive layer 4 is laminated on both the front and back surfaces, thereby constituting the
基材2としては一般的には光不透過性の材料を用いるが、目的、用途により透過性材料を用いることもできる。光不透過性の場合は白色基材が多い。
光不透過性基材の材料としては、例えば、セロファン、ポリプロピレン、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリアセタール、ポリフェニレンエーテル、液晶ポリマー、ポリ塩化ビニル、ポリエステル、ポリアミド、ポリカーボネート、ポリメタクリル酸エチル、ポリスチレン等の合成樹脂フィルムが用いられ、これらを単体または複合体として使用できる。
これらの材料は、特に耐水性や耐熱性等の特性を勘案して、スレッドを抄き込む媒体の使用目的に応じて適切な材料を用いることができる。
In general, a light-impermeable material is used as the substrate 2, but a light-transmitting material can be used depending on the purpose and application. In the case of light impermeability, there are many white base materials.
Examples of the material of the light-impermeable substrate include cellophane, polypropylene, polyethylene terephthalate, polybutylene terephthalate, polyacetal, polyphenylene ether, liquid crystal polymer, polyvinyl chloride, polyester, polyamide, polycarbonate, polyethyl methacrylate, and polystyrene. Synthetic resin films are used, and these can be used as a simple substance or a composite.
In consideration of characteristics such as water resistance and heat resistance, an appropriate material can be used for these materials according to the purpose of use of the medium into which the thread is formed.
また、これらの素材に酸化チタン、シリカ、炭酸カルシウム、硫酸カルシウム等の白色顔料を練り込んだりすることもある。さらに、白色以外の着色剤(顔料、染料など)を練りこませてもよく、基材2の表面に顔料を塗布することもある。 Further, white pigments such as titanium oxide, silica, calcium carbonate, calcium sulfate may be kneaded into these materials. Furthermore, colorants (pigments, dyes, etc.) other than white may be kneaded, and the pigment may be applied to the surface of the substrate 2.
基材2の厚さは特に制限はないが、一般に抄き込み用スレッドとしては5〜25μmの厚さにすることが好ましい。この厚さであれば、スレッドを抄き込んだ部分の紙の厚みが見た目に盛り上がったり、加工時に種々の問題を生じたりすることがない。 Although the thickness of the base material 2 is not particularly limited, it is generally preferable that the thickness of the paper making thread is 5 to 25 μm. If it is this thickness, the thickness of the paper in which the thread is engraved does not rise up visually or causes various problems during processing.
なお、基材2の光不透過性とは、完全に光を遮断することではなく、一方の面から透かして見た際に、反対面側の印刷層が透けて見えない程度であればよい。 In addition, the light impermeability of the base material 2 does not completely block light, but may be as long as the printed layer on the opposite side cannot be seen through when viewed through one side. .
白色磁気層3は、磁性材料を用いて層形成するが、印刷法によってパターン形成するためには印刷インキに磁性剤を含有させた磁性インキを材料とすることが望ましい。
磁性インキは、一般には磁性体粉末をバインダーおよび必要な添加剤(分散剤(界面活性剤)や潤滑剤、可塑剤など)とともに有機溶剤に加え、十分に混練して均一に分散させて得られる。このとき、例えば酸化チタン等からなる白色の磁性体粉末を用いれば白色磁性インキが得られる。また、磁性粒子を核として、その表面に白色顔料などの白色物質の微粒子を固着させたものを用いる場合もある。
The white magnetic layer 3 is formed by using a magnetic material. In order to form a pattern by a printing method, it is desirable to use a magnetic ink containing a magnetic agent in the printing ink as a material.
A magnetic ink is generally obtained by adding a magnetic powder to an organic solvent together with a binder and necessary additives (dispersant (surfactant), lubricant, plasticizer, etc.) and thoroughly kneading to uniformly disperse. . At this time, white magnetic ink can be obtained by using, for example, white magnetic powder made of titanium oxide or the like. In some cases, magnetic particles are used as nuclei and fine particles of a white substance such as a white pigment are fixed on the surface thereof.
このような白色磁性インキを用いて前記基材2上に印刷すれば白色磁気層3が得られるが、このとき全面にベタ印刷したり任意のパターンを印刷することができる。
基材2が白色であった場合、白色磁性インキを用いた印刷部分はほとんど目立たなくなり、結果として白色磁気層3は表裏どちらの面から見ても隠蔽されることになる。
The white magnetic layer 3 can be obtained by printing on the base material 2 using such a white magnetic ink. At this time, solid printing or an arbitrary pattern can be printed on the entire surface.
When the substrate 2 is white, the printed portion using the white magnetic ink is hardly noticeable, and as a result, the white magnetic layer 3 is concealed when viewed from either the front or back side.
また、無色透明な磁性剤を用いることもできる。無色透明な磁性剤としては、例えば磁性酸化鉄粒子にスズ酸化物を被着させた粉末状の磁性剤をインキに混合したものが用いられる。これを持ちいた場合、無色透明な磁気層が形成できるため、白色磁気層の場合と同
様に磁気層が隠蔽される効果を有する。
A colorless and transparent magnetic agent can also be used. As the colorless and transparent magnetic agent, for example, a powdery magnetic agent obtained by adhering tin oxide to magnetic iron oxide particles and mixed with ink is used. When this is held, a colorless and transparent magnetic layer can be formed, so that the magnetic layer is concealed as in the case of the white magnetic layer.
図1に示したスレッド1の構成はいわゆる埋め込みスレッドであり、例えば媒体が紙であれば、紙の中に前記スレッド1を抄き込むことにより、スレッド1内の白色磁気層3を磁性体とする偽造防止用紙として用いることができる。
The configuration of the
さらに、例えば励磁用磁気発生装置を用いて用紙に励磁させて磁気情報を記録すれば、磁気読み取り装置によってその情報を読み取ることができる。磁性材料や磁気記録方法、記録箇所、あるいは磁気信号の種類等を工夫することで多様な磁気情報を記録することができ、この磁気情報を読み取って照合することで偽造防止手段とすることができる。 Furthermore, if magnetic information is recorded by exciting the paper using, for example, an excitation magnetism generator, the information can be read by the magnetic reader. A variety of magnetic information can be recorded by devising the magnetic material, magnetic recording method, recording location, type of magnetic signal, etc., and forgery prevention means can be obtained by reading and collating this magnetic information. .
このような埋め込みスレッドを用いた偽造防止用紙の場合、用紙が殆どの場合白色かそれに近い色であるため、白色の磁気層は表面から透けて見えることがなく、用紙の美観や意匠性が損なわれることがない。 In the case of anti-counterfeit paper using such embedded threads, since the paper is almost white or a color close to it, the white magnetic layer is not seen through the surface, and the aesthetics and design of the paper are impaired. It will not be.
(第二の実施例)
次に、視覚的な効果を持たせたスレッドの構成を説明する。
図2は、本発明におけるスレッドの第二の実施例の構成を示す図であり、この実施例では、該スレッドの一部を用紙表面に露出させて使用する、いわゆるウィンドウ(窓空き)スレッドの構成を示している。
(Second embodiment)
Next, the configuration of a thread having a visual effect will be described.
FIG. 2 is a diagram showing the configuration of a second embodiment of the thread according to the present invention. In this embodiment, a so-called window thread is used in which a part of the thread is exposed on the paper surface. The configuration is shown.
図2において、基材11の一方の面に回折構造形成層12および蒸着加工層15、白色磁気層13がこの順に積層され、さらにその外側の両面に接着層14が積層されている。 In FIG. 2, a diffractive structure forming layer 12, a vapor-deposited layer 15 and a white magnetic layer 13 are laminated in this order on one surface of a substrate 11, and an adhesive layer 14 is laminated on both outer surfaces thereof.
この構成のスレッドには視覚的効果を持たせているため、基材11の材料としては光透過性の樹脂系材料が好ましく、例えば、酢酸ビニル樹脂、エチレン酢酸ビニル共重合樹脂、塩化ビニル酢酸ビニル共重合樹脂、ポリエステル樹脂、ポリエステルウレタン樹脂、アクリルウレタン樹脂、エポキシ樹脂、エポキシウレタン樹脂、ポリカーボネートウレタン樹脂、ブチラール樹脂、塩素化プロピレン樹脂などが用いられる。 Since the thread of this configuration has a visual effect, the material of the base material 11 is preferably a light-transmitting resin material, such as vinyl acetate resin, ethylene vinyl acetate copolymer resin, vinyl chloride vinyl acetate. Copolymer resins, polyester resins, polyester urethane resins, acrylic urethane resins, epoxy resins, epoxy urethane resins, polycarbonate urethane resins, butyral resins, chlorinated propylene resins, and the like are used.
回折構造形成層12は、一方の面に複数の凹凸構造の溝が二次元的に配置されてなる回折格子が形成されており、例えば光透過性の樹脂を用いてエンボス加工処理により形成される。蒸着加工層15は回折構造形成層の上に金属薄膜が蒸着加工されており、光反射層として作用する。 The diffraction structure forming layer 12 is formed with a diffraction grating in which a plurality of grooves having a concavo-convex structure are two-dimensionally arranged on one surface, and is formed by, for example, an embossing process using a light-transmitting resin. . The vapor deposition layer 15 has a metal thin film vapor-deposited on the diffractive structure forming layer and functions as a light reflection layer.
前記蒸着加工層15の金属薄膜は、例えばアルミニウム、銀、錫、クロム、ニッケル、銅、金、あるいはそれらの合金などから選択される金属材料が用いられ、真空蒸着法やスパッタリング法などの薄膜形成手段を用いて形成される。金属薄膜の膜厚は回折格子の溝の大きさ・深さなどに応じて適宜決めてよいが、一般的には1〜100μmの範囲が用いられる。 The metal thin film of the vapor deposition layer 15 is made of a metal material selected from, for example, aluminum, silver, tin, chromium, nickel, copper, gold, or an alloy thereof, and is formed into a thin film such as a vacuum vapor deposition method or a sputtering method. It is formed using means. The film thickness of the metal thin film may be appropriately determined according to the size and depth of the grooves of the diffraction grating, but generally a range of 1 to 100 μm is used.
白色磁気層13は前記第一の実施例と同様に磁性材料を用いており、例えば印刷インキに磁性剤を含有させた磁性インキを材料として、印刷法によりパターン形成される。
また、白色磁性材料の代わりに無色透明な磁性剤を用いることもできる。
The white magnetic layer 13 uses a magnetic material as in the first embodiment. For example, the white magnetic layer 13 is patterned by a printing method using a magnetic ink containing a magnetic agent in a printing ink.
Also, a colorless and transparent magnetic agent can be used in place of the white magnetic material.
図2のスレッド10は、偽造防止用紙に抄き込む際に、スレッドの一部が用紙の表面に間欠的に露出するようにした、いわゆるウィンドウスレッドとして用いることができる。図2に示すように基材11が近い側を窓開き側とし、用紙に開口部を設けて窓開き部として、用紙の窓開き部に該スレッド10を抄き込むことにより、窓開き部からスレッドが露出した状態となる。
The
このとき、窓開き部からは特殊な視覚効果が観察される。
すなわち、外部からの入射光が窓開き側から接着層14、基材11を通って回折構造形成層12に入射して蒸着加工層15で反射した際に、前記凹凸構造の溝により光の波長分散を伴う回折効果を生じ、観察者の視点の位置あるいは角度によって多彩な色にシフトして見える。また金属の蒸着加工層15からの反射光は金属光沢も生じて見える。
このような回折構造を擁するスレッドは偽造が困難であり、高い偽造防止効果を保持する。
At this time, a special visual effect is observed from the window opening.
That is, when incident light from the outside enters the diffraction structure forming layer 12 through the adhesive layer 14 and the base material 11 from the window opening side and is reflected by the vapor deposition processing layer 15, the wavelength of the light is reflected by the grooves of the concavo-convex structure. A diffraction effect with dispersion occurs, and the color appears to shift to various colors depending on the position or angle of the observer's viewpoint. The reflected light from the metal deposition layer 15 also appears to have a metallic luster.
A thread having such a diffractive structure is difficult to counterfeit and retains a high anti-counterfeit effect.
(第三の実施例)
次に、視覚効果を持たせたスレッドにおける他の実施例を説明する。
図3は、本発明のスレッドの第三の実施例として、ウィンドウスレッドの構成を示した図である。スレッド20において、基材21に回折構造形成層22が積層され、該回折構造形成層22の一方の面には複数の凹凸構造の溝が二次元的に配置された回折格子が第一界面部25aと第二界面部25bの二つの領域に配置され、さらに第二界面部25bに接して白色磁性マスク層23が積層して形成されている。
(Third embodiment)
Next, another embodiment of a thread having a visual effect will be described.
FIG. 3 is a diagram showing the configuration of a window thread as a third embodiment of the thread of the present invention. In the thread 20, a diffractive structure forming layer 22 is laminated on a base material 21, and a diffraction grating in which grooves of a plurality of uneven structures are two-dimensionally arranged on one surface of the diffractive structure forming layer 22 is a first interface portion. The white magnetic mask layer 23 is laminated and formed in two regions of 25a and the second interface portion 25b, and in contact with the second interface portion 25b.
基材21は前記第二の実施例と同様に、光透過性の樹脂材料が好ましい。 The substrate 21 is preferably a light transmissive resin material, as in the second embodiment.
第二界面部25bには蒸着加工による金属薄膜が積層されており、第一界面部24aには金属薄膜がない。
その製造方法としては、回折構造形成層22の全面に金属薄膜を蒸着した後、さらにその上に白色磁性マスク層23が印刷法により積層される。
次に、この白色磁性マスク層23を保護膜として、前記金属薄膜にディメタライズ処理を行うことにより、白色磁性マスク層23に保護された第二界面部24bは金属薄膜が残り、保護されない第一界面部24aは金属薄膜が除去される。
A metal thin film formed by vapor deposition is laminated on the second interface portion 25b, and there is no metal thin film on the first interface portion 24a.
As a manufacturing method thereof, after depositing a metal thin film on the entire surface of the diffraction structure forming layer 22, a white magnetic mask layer 23 is further laminated thereon by a printing method.
Next, by using the white magnetic mask layer 23 as a protective film, the metal thin film is subjected to a demetalization process, whereby the metal thin film remains in the second interface portion 24b protected by the white magnetic mask layer 23 and is not protected. The metal thin film is removed from the interface 24a.
さらに、両面に接着層24が積層されて、スレッド20が形成される。スレッド20は基材21に近い側を窓開き側とし、白色磁気マスク層23に近い側を窓なし側とするウィンドウスレッドとなる。 Furthermore, the adhesive layer 24 is laminated on both surfaces to form the thread 20. The thread 20 is a window thread in which the side close to the substrate 21 is the window opening side and the side close to the white magnetic mask layer 23 is the windowless side.
偽造防止用紙の窓開き部にスレッド20を抄き込むことにより、窓開き部からスレッド20が露出する。この窓開き部から入射した光は、回折構造形成層22の回折格子を通って金属薄膜を積層した第二界面部24bで反射されることにより、前記第二の実施例と同様に回折効果によって多彩な色にシフトして見える。
この回折構造を擁するスレッドは偽造が困難であり、高い偽造防止効果を保持することができる。
The thread 20 is exposed from the window opening by making the thread 20 into the window opening of the forgery prevention paper. The light incident from the window opening is reflected by the second interface 24b where the metal thin film is laminated through the diffraction grating of the diffractive structure forming layer 22, so that the diffraction effect is applied as in the second embodiment. It looks shifted to a variety of colors.
The thread having the diffractive structure is difficult to counterfeit and can retain a high anti-counterfeit effect.
また、基材21は多層の樹脂フィルムで構成することもできる。例えば、透過性であるが異なる光学特性を持つ材料からなるフィルムを複数積層した多層干渉フィルムを用いることができる。多層干渉フィルムは、入射光が該フィルム中で干渉効果による波長分散を生じることによって、窓開き側から見てさらに複雑な視覚効果が得られる。
そしてこのような目的で用いる多層干渉フィルム自体も偽造が困難であるため、より高い偽造防止効果が得られる。
Moreover, the base material 21 can also be comprised with a multilayer resin film. For example, a multilayer interference film in which a plurality of films made of materials that are transparent but have different optical characteristics can be used. In the multilayer interference film, incident light generates wavelength dispersion due to the interference effect in the film, so that a more complicated visual effect can be obtained when viewed from the window opening side.
And since the multilayer interference film itself used for such a purpose is also difficult to forge, a higher forgery prevention effect can be obtained.
(実施例の製造手順)
前記第三の実施例で示したスレッドの構成において、以下にスレッドの製造手順を説明する。
(i)厚さ16μmの多層干渉フィルムを基材として、その上に微細回折構造形成層となるUV硬化型インキをグラビアコーティング法を用いて厚さ1μmで塗布し、乾燥およびエ
ージングを行った。
(ii)凹凸溝が間隔0.3μm、深さ0.4μmで刻まれた回折格子パターンを有するエンボス原版を用意した。この原版を装着したシリンダーロールを加熱して、前記UV硬化型インキ塗布層に100℃でのエンボス加工を施した後、フィルム基材側から紫外線を照射してインキを硬化させ、回折格子パターンが形成された回折構造形成層を得た。
(iii)この回折構造形成層の上に、蒸着加工層として厚さ50nmのアルミニウム金属薄膜を蒸着法により積層した。
(iv)前記蒸着加工層の上に、白色磁性剤を含有した塩化ビニル酢酸ビニル共重合樹脂(塩酢ビ)からなるマスク用インキを、グラビア印刷法を用いて厚さ1μmでマスクパターンを印刷塗布し、白色磁気マスク層を得た。次に、マスクされた領域以外の前記蒸着加工層の露出部分を、アルカリ溶液でディメタライズ処理を行って除去した。
(v)白色微粉末のシリカフィラーを分散させた塩酢ビからなる接着剤を、(iv)で作製した積層体の表裏両面にグラビアコーティング法により厚さ2μmで塗布した。
(Production procedure of Example)
In the thread configuration shown in the third embodiment, a thread manufacturing procedure will be described below.
(i) Using a multilayer interference film having a thickness of 16 μm as a base material, a UV curable ink serving as a fine diffractive structure forming layer was applied thereon with a thickness of 1 μm using a gravure coating method, followed by drying and aging.
(ii) An embossed original plate having a diffraction grating pattern in which concave and convex grooves were carved at intervals of 0.3 μm and a depth of 0.4 μm was prepared. The cylinder roll equipped with this original plate is heated, and the UV curable ink coating layer is embossed at 100 ° C., and then the ink is cured by irradiating ultraviolet rays from the film substrate side. A formed diffraction structure forming layer was obtained.
(iii) An aluminum metal thin film having a thickness of 50 nm was laminated on the diffraction structure forming layer by a vapor deposition method as a vapor deposition processed layer.
(iv) On the vapor-deposited layer, a mask pattern made of a vinyl chloride vinyl acetate copolymer resin (vinyl acetate) containing a white magnetic agent is printed with a thickness of 1 μm using a gravure printing method. The white magnetic mask layer was obtained by coating. Next, the exposed portion of the vapor deposition processing layer other than the masked region was removed by demetalizing with an alkaline solution.
(v) An adhesive made of vinyl chloride in which a fine silica powder filler was dispersed was applied to the front and back surfaces of the laminate produced in (iv) at a thickness of 2 μm by a gravure coating method.
なお、前記(ii)のエンボス原版の製造手順を説明する。
基板となるガラス板上に感光性ポジレジストを塗布した後、電子線描画を行って回折格子パターンを描画し、現像処理を行ってレジストパターンを得た。このレジストパターン表面にスパッタリング法により導電膜を被膜して母型を作製し、ニッケル電鋳法を用いてエンボス原版を得た。
The manufacturing procedure of the embossed original plate (ii) will be described.
A photosensitive positive resist was applied onto a glass plate serving as a substrate, and then a diffraction grating pattern was drawn by electron beam drawing, followed by development processing to obtain a resist pattern. The resist pattern surface was coated with a conductive film by a sputtering method to produce a mother die, and an embossed original plate was obtained using a nickel electroforming method.
前記製造手順により得られたスレッドをウィンドウスレッドとして、開口部を形成した用紙にこのスレッドを抄き込むことにより、偽造防止用紙が得られた。
この偽造防止用紙を表裏から目視観察すると、スレッド中の磁気マスク層は用紙と色がほぼ同じであるため区別することができず、この偽造防止用紙を例えば商品券やパスポートなどに使用しても、券面の意匠性を損なうことがない。
即ちこれらの偽造防止用紙の意匠に制限を与えず、その用途を拡大する効果が得られた。
A forgery-preventing paper was obtained by using the thread obtained by the above-described manufacturing procedure as a window thread and making the thread into a paper having an opening.
When this anti-counterfeit paper is visually observed from the front and back, the magnetic mask layer in the thread is almost the same color as the paper and cannot be distinguished. , The design of the ticket will not be impaired.
That is, the effect of expanding the use without giving a restriction to the design of these anti-counterfeit papers was obtained.
また、前記製造手順によれば、磁気マスク層は通常の印刷法のみにより形成でき、意匠生性を損なわないために磁気マスク層を隠蔽するための金属マスク層を形成するようなことは必要がない。従って、製造工程を複雑にせず、製造負荷を増大することもない。 In addition, according to the manufacturing procedure, the magnetic mask layer can be formed only by a normal printing method, and it is not necessary to form a metal mask layer for concealing the magnetic mask layer so as not to impair the design productivity. . Therefore, the manufacturing process is not complicated and the manufacturing load is not increased.
なお、本発明は上記の実施例に特に限定するものでなく、種々の構成に応用することができる。 In addition, this invention is not specifically limited to said Example, It can apply to a various structure.
例えば、無色透明な磁性体材料を用いて磁気マスク層を形成すれば、磁気マスク層自体が見えなくなるので、これを用いたウィンドウスレッドも外側から磁気マスク層が見えることがなく、意匠性を損なうことがない。
無色透明な磁性材料は公知のものでよく、例えばスズ酸化物やスズ水酸化物が被着された酸化鉄粒子粉末などがある。
For example, if a magnetic mask layer is formed using a colorless and transparent magnetic material, the magnetic mask layer itself cannot be seen. Therefore, the window thread using the magnetic mask layer does not show the magnetic mask layer from the outside, which impairs the design. There is nothing.
The colorless and transparent magnetic material may be a known material, such as iron oxide particle powder coated with tin oxide or tin hydroxide.
本発明に係るスレッドおよび偽造防止用紙によれば、銀行券やパスポート、公的証明書、商品券など、磁気情報により様々なセキュリティを施した偽造防止媒体に応用できる。 The thread and anti-counterfeit paper according to the present invention can be applied to anti-counterfeit media with various security provided by magnetic information, such as banknotes, passports, public certificates, and gift certificates.
1,10,20 ・・・スレッド
2,11,21 ・・・基材
3,13 ・・・白色磁気層
23 ・・・白色磁気マスク層
4,14,24 ・・・接着層
12,22 ・・・回折構造形成層
15 ・・・蒸着加工層
25a ・・・第一界面部
25b ・・・第二界面部
DESCRIPTION OF
Claims (4)