JP5558314B2 - Construction method of soil cement composite pile - Google Patents

Construction method of soil cement composite pile Download PDF

Info

Publication number
JP5558314B2
JP5558314B2 JP2010247595A JP2010247595A JP5558314B2 JP 5558314 B2 JP5558314 B2 JP 5558314B2 JP 2010247595 A JP2010247595 A JP 2010247595A JP 2010247595 A JP2010247595 A JP 2010247595A JP 5558314 B2 JP5558314 B2 JP 5558314B2
Authority
JP
Japan
Prior art keywords
soil cement
cement
insertion tube
depth
soil
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2010247595A
Other languages
Japanese (ja)
Other versions
JP2012097511A (en
Inventor
陽治 植山
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tenox Kyusyu Corp
Original Assignee
Tenox Kyusyu Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tenox Kyusyu Corp filed Critical Tenox Kyusyu Corp
Priority to JP2010247595A priority Critical patent/JP5558314B2/en
Publication of JP2012097511A publication Critical patent/JP2012097511A/en
Application granted granted Critical
Publication of JP5558314B2 publication Critical patent/JP5558314B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、土木、建築分野において、地盤中にセメント硬化材を注入するソイルセメント合成杭の造成方法に関するものである。   The present invention relates to a method for constructing a soil cement synthetic pile in which a cement hardening material is injected into the ground in the civil engineering and construction fields.

特許文献１（特開昭６０−２３８５１５号公報）、特許文献２（特許第２７３１８０６号公報）、特許文献３（特開２００１−３１７０５０号公報）、特許文献４（特開２００２−２９４６９８号公報）に開示されるように、従来ソイルセメント柱体内に、鋼管等を補強部材として挿入するソイルセメント合成杭が知られている。   Patent Document 1 (Japanese Patent Laid-Open No. 60-238515), Patent Document 2 (Japanese Patent No. 2731806), Patent Document 3 (Japanese Patent Laid-Open No. 2001-31050), Patent Document 4 (Japanese Patent Laid-Open No. 2002-294698) Conventionally, a soil cement synthetic pile in which a steel pipe or the like is inserted as a reinforcing member in a soil cement column is known.

さらに、特許文献５（特開２００６−６３５６８号公報）は、加工コストを低減するための技術を開示するが、圧入される管体は、有底状をなし、圧入しただけでは、管体の内部にソイルセメントが入らず、セメント硬化材を別途管体内へ充填する必要があるなど、作業効率に欠点があり、それ故、不必要なコストアップを招来する。   Furthermore, Patent Document 5 (Japanese Patent Laid-Open No. 2006-63568) discloses a technique for reducing the processing cost, but the press-fitted tube has a bottomed shape. There is a drawback in work efficiency, such as no need for soil cement inside, and the need to fill the pipe with a hardened cement material separately, thus leading to unnecessary cost increases.

さらに、これら従来技術は、いずれも形成されるソイルセメント柱体の深度を、いずれも所定深度を一致させ、補強部材を挿入する域を脱するものではなく、不経済であることはかわりない。言い換えれば、経済性が優れた新工法が求められている。
特開昭６０−２３８５１５号公報 特許第２７３１８０６号公報 特開２００１−３１７０５０号公報 特開２００２−２９４６９８号公報 特開２００６−６３５６８号公報 Furthermore, none of these conventional techniques is uneconomical because the depths of the soil cement pillars to be formed do not coincide with the predetermined depths, and do not escape from the region where the reinforcing member is inserted. In other words, there is a demand for a new construction method with excellent economic efficiency.
JP-A-60-238515 Japanese Patent No. 2731806 JP 2001-317050 A JP 2002-294698 A JP 2006-63568 A

そこで本発明は、加工の手間や加工のコストをより低減できるソイルセメント合成杭の造成方法を提供することを目的とする。   Then, an object of this invention is to provide the construction method of the soil cement synthetic | combination pile which can reduce the effort of a process and the cost of a process more.

第１の発明に係るソイルセメント合成杭の造成方法は、通常の造成深度よりも浅い設定深度を定め、セメント硬化材を注入して所定直径のソイルセメント状改良体を、地盤中において設定深度までであるが、通常の造成深度には至らないように造成し、ソイルセメント状改良体が固化しないうちに、所定直径よりも外径が小径であって、既設コンクリートパイル又は鋼管杭からなる挿入管を挿入し、ソイルセメント状改良体が固化することにより、ソイルセメント状改良体と挿入管とを一体化するソイルセメント合成杭の造成方法であって、挿入管は、内部を軸方向に貫通する空洞を有する中空構造をなし、かつ、挿入管の外側面には凹凸が形成され、外側面は非平滑面となっている。   The method for constructing a soil cement synthetic pile according to the first invention is to set a set depth shallower than a normal constructed depth, and to inject a cement hardened material into a soil cement-like improvement body having a predetermined diameter up to the set depth in the ground. However, it is constructed so as not to reach the normal construction depth, and before the soil cement-like improved body is solidified, the outer diameter is smaller than the predetermined diameter, and the insertion pipe is made of an existing concrete pile or steel pipe pile. Is inserted, and the soil cement-like improvement body is solidified, so that the soil cement-like improvement body and the insertion pipe are integrated, and the insertion pipe penetrates the inside in the axial direction. A hollow structure having a cavity is formed, and irregularities are formed on the outer surface of the insertion tube, and the outer surface is a non-smooth surface.

この構成において、通常の造成深度よりも浅い設定深度が定められ、ソイルセメント状改良体を、地盤中において設定深度までであるが、通常の造成深度には至らない。   In this configuration, a set depth shallower than the normal creation depth is determined, and the soil cement-like improved body is up to the set depth in the ground, but does not reach the normal creation depth.

要するに、通常よりも浅いソイルセメント状改良体が造成される。これにより、ソイルセメント状改良体の造成に要する手間及びコストを大幅に削減できる。このようにしても、挿入管がソイルセメント状改良体に密着し、ソイルセメント状改良体の強度を補強するため、ソイルセメント合成杭全体としては、通常の造成深度までソイルセメント状改良体のみを造成した場合に比べ、遜色のない強度を得ることができるから、支障はない。   In short, a soil cement-like improvement body shallower than usual is created. Thereby, the effort and cost which are required for the creation of the soil cement-like improved body can be greatly reduced. Even in this case, since the insertion tube is in close contact with the soil cement-like improved body and reinforces the strength of the soil cement-like improved body, only the soil cement-like improved body is used up to the normal construction depth as a whole soil cement synthetic pile. Compared to the case where it is formed, it is possible to obtain an inferior strength, so there is no problem.

挿入管は、内部を軸方向に貫通する空洞を有する中空構造をなすため、ソイルセメント状改良体が固化する前に、挿入管が改良体内部に挿入されるのであるが、挿入しさえすれば、ソイルセメント状改良体を構成するセメントで未固化のものが、空洞内へ進入するため、後に空洞内へ充填材等を挿入する必要はない。   Since the insertion tube has a hollow structure having a cavity that penetrates the inside in the axial direction, the insertion tube is inserted into the improvement body before the soil cement-like improvement body is solidified. Since the cement constituting the soil cement-like improved body that has not been solidified enters the cavity, there is no need to insert a filler or the like into the cavity later.

挿入管を改良体の内部へ挿入すると、挿入管の外側に位置する未固化のセメントは、改良体を包囲する土壌に押しつけられて土壌と良く密着する。また、挿入管の外側面には凹凸が形成され、外側面は非平滑面となっているため、未固化のセメントと挿入管の外側面が良く入り交じり、セメントが固化すると、挿入管とセメントとは、強固に結合し、ソイルセメント合成杭全体としての強度が一層高められる。   When the insertion tube is inserted into the improved body, the unsolidified cement located outside the insertion tube is pressed against the soil surrounding the improved body and adheres well to the soil. In addition, since the outer surface of the insertion tube is uneven and the outer surface is a non-smooth surface, the unsolidified cement and the outer surface of the insertion tube mix well, and when the cement is solidified, the insertion tube and cement Is firmly bonded, and the strength of the soil cement synthetic pile as a whole is further enhanced.

第２の発明に係るソイルセメント合成杭の造成方法では、第１の発明に加え、外側面には、外側面を周回する溝部が形成されている。   In the method for building a soil cement synthetic pile according to the second invention, in addition to the first invention, a groove portion that goes around the outer surface is formed on the outer surface.

この構成により、溝部へセメントが出入りすることにより、未固化のセメントと挿入管の外側面が良く入り交じり、セメントが固化すると、挿入管とセメントとは、強固に結合し、ソイルセメント合成杭全体としての強度が一層高められる。   With this configuration, the cement enters and exits the groove so that the unsolidified cement and the outer surface of the insertion tube mix well, and when the cement solidifies, the insertion tube and the cement are firmly bonded, and the entire soil cement composite pile As a result, the strength is further increased.

第３の発明に係るソイルセメント合成杭の造成方法では、第１の発明に加え、外側面は、粗面となっている。   In the method for producing a soil cement synthetic pile according to the third invention, in addition to the first invention, the outer surface is a rough surface.

この構成により、粗面の凹凸へセメントが出入りすることにより、未固化のセメントと挿入管の外側面が良く入り交じり、セメントが固化すると、挿入管とセメントとは、強固に結合し、ソイルセメント合成杭全体としての強度が一層高められる。   With this structure, the cement enters and exits the rough surface, and the unsolidified cement and the outer surface of the insertion tube mix well. When the cement is solidified, the insertion tube and the cement are firmly bonded, and the soil cement The strength of the composite pile as a whole is further increased.

第４の発明に係るソイルセメント合成杭の造成方法では、第３の発明に加え、粗面は、無機系砂混塗料を塗布することにより形成される。   In the method for producing a soil cement synthetic pile according to the fourth invention, in addition to the third invention, the rough surface is formed by applying an inorganic sand mixed paint.

この構成により、挿入管の外側面に、容易にしかも安価に粗面を形成できるし、既存の安価な挿入管を、本願発明への適用に適するものへと変更できる。   With this configuration, a rough surface can be easily and inexpensively formed on the outer surface of the insertion tube, and an existing inexpensive insertion tube can be changed to one suitable for application to the present invention.

本発明によれば、より浅いソイルセメント状改良体を造成することにより、ソイルセメント状改良体の造成に要する手間及びコストを大幅に削減できるし、通常の造成深度までソイルセメント状改良体のみを造成した場合に比べて、遜色のない強度が得られる。   According to the present invention, by creating a shallow soil cement-like improvement body, it is possible to greatly reduce the labor and cost required for the formation of the soil cement-like improvement body, and only the soil cement-like improvement body can be obtained up to a normal formation depth. Compared to the case of forming, strength comparable to that obtained can be obtained.

挿入管の空洞内へ充填材等を別途挿入する必要はなく作業性が良好であるだけでなく、挿入管の外側面とセメントとが強固に結合し、強度を向上できる。   There is no need to separately insert a filler or the like into the cavity of the insertion tube, and not only the workability is good, but also the outer surface of the insertion tube and the cement are firmly bonded to improve the strength.

以下図面を参照しながら、本発明の実施の形態を説明する。   Embodiments of the present invention will be described below with reference to the drawings.

（実施の形態１）
図１（ａ）〜図１（ｃ）は、本発明の実施の形態１におけるソイルセメント合成杭の造成方法の工程説明であり、図２は、本発明の実施の形態１における挿入管の一部切欠斜視図である。 (Embodiment 1)
1 (a) to 1 (c) are process descriptions of a method for constructing a soil cement synthetic pile according to the first embodiment of the present invention, and FIG. 2 shows one of the insertion pipes according to the first embodiment of the present invention. It is a part notch perspective view.

図１（ａ）に示すように、まず、通常の造成深度Ｈ１よりも浅い設定深度Ｈ２を定める。このように、設定深度Ｈ２を通常の造成深度Ｈ１よりも浅くできるのは、後述するように、挿入管３のために、固化したソイルセメント状改良体２の全体の強度が通常よりも大幅に改善されるためである。   As shown in FIG. 1A, first, a set depth H2 that is shallower than the normal creation depth H1 is determined. Thus, the set depth H2 can be made shallower than the normal creation depth H1, as described later, because of the insertion tube 3, the overall strength of the solidified soil cement-like improved body 2 is significantly larger than usual. It is because it is improved.

ここで、設定深度Ｈ２は、通常の造成深度Ｈ１を１００％としたとき、地盤条件によるが、例えば４０％〜７０％とすることができる。   Here, the set depth H2 can be set to 40% to 70%, for example, although it depends on the ground condition when the normal creation depth H1 is 100%.

そして、造成装置１を用いて、セメント硬化材を注入して所定直径のソイルセメント状改良体２を、地盤中において設定深度までであるが、通常の造成深度には至らないように造成する。例えば、パイルドライバー等を使用し、オーガーモータと特殊ロッドにより、機械的撹拌装置を回転させながら、この装置の先端部からセメントミルクを注入しつつ、土とセメントミルクとを撹拌混合し、挿入管３よりも大径のソイルセメントコラムを造成する。   Then, using the forming device 1, the cement hardener is injected to form the soil cement-like improvement body 2 having a predetermined diameter up to a set depth in the ground so as not to reach the normal forming depth. For example, using a pile driver, etc., while rotating the mechanical stirring device with an auger motor and special rod, while mixing cement milk from the tip of this device, stirring and mixing soil and cement milk, insert tube A soil cement column with a diameter larger than 3 is created.

挿入管３の外径よりも、ソイルセメントコラムの外径が、例えば、１０ｃｍから８０ｃｍ程度大きくすると好適である。   The outer diameter of the soil cement column is preferably larger than the outer diameter of the insertion tube 3 by, for example, about 10 cm to 80 cm.

この工程は、通常の機械式深層混合処理工法によって差し支えない。具体的には、セメント或いはセメントを主成分とした固化材と水を混練して作成したスラリーを地盤中に注入しながら、掘削翼と攪拌翼を用いて攪拌混合し、地盤とスラリーを機械的に攪拌混合してソイルセメント状改良体２を造成するとよい。   This step may be performed by a normal mechanical deep mixing method. Specifically, cement or a solidified material mainly composed of cement and a slurry prepared by kneading water are poured into the ground while stirring and mixing using an excavation blade and a stirring blade, and the ground and the slurry are mechanically mixed. The soil cement-like improved body 2 is preferably prepared by stirring and mixing.

あるいは、図示していないが、先端部に掘削ビットが設けられる掘削ロッドを用いてもよい。   Or although not shown in figure, you may use the excavation rod in which a excavation bit is provided in a front-end | tip part.

一方、上述した造成を行う前に、本形態では、図２に示すような既設の挿入管３を用意しておく。挿入管３は、既設コンクリートパイル又は鋼管杭からなる。   On the other hand, before performing the above-described creation, in the present embodiment, an existing insertion tube 3 as shown in FIG. 2 is prepared. The insertion pipe 3 consists of an existing concrete pile or a steel pipe pile.

図２に示すように、挿入管３は、内部を軸方向に貫通する空洞４を有する中空構造をなし、図１（ｂ）に示すように、ソイルセメント状改良体２が固化する前に、改良体２の内部に挿入される。ここで、図１（ｂ）に示すように、挿入に伴い、ソイルセメント状改良体２を構成するセメントで未固化のものが、空洞４内へ進入するため、後に空洞４内へ充填材等を挿入するような余分の手間は、不要である。   As shown in FIG. 2, the insertion tube 3 has a hollow structure having a cavity 4 penetrating the inside in the axial direction. As shown in FIG. 1 (b), before the soil cement-like improvement body 2 is solidified, It is inserted into the improved body 2. Here, as shown in FIG. 1 (b), as the cement constituting the soil cement-like improved body 2 is not solidified as it enters, the cement enters the cavity 4, so that a filler or the like enters the cavity 4 later. No extra effort is required to insert the.

図１（ｂ）に示すように、挿入管３を改良体２の内部へ挿入すると、挿入管３の外側に位置する未固化のセメントは、改良体２を包囲する土壌側に押圧され、土壌（一般的には、その周側面には凹凸がある）と良く密着する。   As shown in FIG. 1 (b), when the insertion tube 3 is inserted into the improved body 2, the unsolidified cement located outside the insertion tube 3 is pressed toward the soil surrounding the improved body 2, (Generally, the peripheral side surface has irregularities) and adheres well.

本形態では、挿入管３の外側面には、外側面を周回する溝部５が形成されており、挿入管３の外側面には、段差が形成されている。ここで、溝部５の深さは、例えば、５ｍｍから１０ｍｍ程度とするのが好適である。   In this embodiment, a groove portion 5 that goes around the outer surface is formed on the outer surface of the insertion tube 3, and a step is formed on the outer surface of the insertion tube 3. Here, the depth of the groove portion 5 is preferably about 5 mm to 10 mm, for example.

これにより、挿入管３の外側面は、凹凸を有する非平滑面となっている。土壌とと同様に、未固化のセメントは、挿入管３の外側面、特に溝部５と、良く入り交じり、接触面積が増加している。   Thereby, the outer surface of the insertion tube 3 is a non-smooth surface having irregularities. Similar to the soil, the unsolidified cement mixes well with the outer surface of the insertion tube 3, particularly the groove portion 5, and the contact area increases.

このため、セメントが固化すると、挿入管３の外側面とセメントとが強固に結合し、ソイルセメント合成杭全体としての強度が向上する。   For this reason, when the cement is solidified, the outer surface of the insertion tube 3 and the cement are firmly bonded, and the strength of the entire soil cement synthetic pile is improved.

ここで、図１（ｂ）に示す挿入管３の挿入工程では、セメントが未固化の状態において、改良体２に圧入されても回転貫入されてもよいし、あるいはこれらを組み合わせて挿入されても良い。   Here, in the insertion step of the insertion tube 3 shown in FIG. 1 (b), the cement may be pressed into the improved body 2 or may be rotationally penetrated, or may be inserted in combination in an unsolidified state. Also good.

圧入とは垂直方向に挿入管３を加圧し、改良体２に挿入管３を入れることであり、回転貫入とは、挿入管３の上部を機械で直接把持したり、あるいは、治具を介して、挿入管３に回転力（図１（ｂ）の矢印参照。）を付加しながら、垂直方向の推進力を付与することである。   The press-fitting is to pressurize the insertion tube 3 in the vertical direction and insert the insertion tube 3 into the improved body 2, and the rotary penetration is to directly grip the upper part of the insertion tube 3 with a machine or through a jig. Thus, a vertical driving force is applied to the insertion tube 3 while applying a rotational force (see the arrow in FIG. 1B).

一般には、回転貫入の方が圧入よりもスムーズであり望ましいが、要は、図１（ｃ）に示すように、挿入管３と改良体２とが、ほぼ同軸状となり、挿入管３の上部が改良体２の上端部から上向きに突出しないようになれば十分である。   In general, the rotation penetration is smoother and more desirable than the press-fitting, but the point is that the insertion tube 3 and the improved body 2 are substantially coaxial as shown in FIG. Is sufficient if it does not protrude upward from the upper end of the improved body 2.

なお、挿入管３の下端部に、未固化のセメントをかき乱す突起物を取付けても良いが、これは必須ではなく省略しても本願発明に包含される。   In addition, although the protrusion which disturbs unsolidified cement may be attached to the lower end part of the insertion pipe 3, this is not essential and it is included in this invention even if it omits.

この挿入工程も、周知手段によって差し支えないので、挿入のための機械等の詳細の説明は省略する。   Since this insertion step may also be performed by well-known means, detailed description of the machine for insertion will be omitted.

図１（ｃ）の状態を維持し、セメントの養生が完成すれば、セメントは固化し、改良体２と挿入管３とが一体化したソイルセメント合成杭の造成が完了する。即ち、図１（ｃ）から明らかなように、挿入管３は、改良体２の内部に残置されて一体化するものであって、改良体２から引き抜かれるものではない。   If the state of FIG. 1C is maintained and the curing of the cement is completed, the cement is solidified, and the formation of the soil cement synthetic pile in which the improved body 2 and the insertion pipe 3 are integrated is completed. That is, as is clear from FIG. 1C, the insertion tube 3 is left inside the improved body 2 and integrated, and is not pulled out from the improved body 2.

なお、図１（ｃ）に示すように、挿入管３の底部は、改良体２の底部よりやや高い位置にあるのが望ましいが、挿入管３の底部を改良体２の底部と一致させても良い。   1C, the bottom of the insertion tube 3 is preferably slightly higher than the bottom of the improved body 2, but the bottom of the insertion tube 3 is aligned with the bottom of the improved body 2. Also good.

以上のように、通常（深さＨ１）よりも浅い（深さＨ２）ソイルセメント状改良体が造成される。造成に要する手間及びコストは、この深さに大きく依存するため、浅くすることによって、この手間及びコストを大幅に削減できる。しかも、十分なソイルセメント状改良体の強度を保持できる。   As described above, a soil cement-like improvement body that is shallower (depth H2) than normal (depth H1) is formed. Since the labor and cost required for creation greatly depend on this depth, the labor and cost can be greatly reduced by making it shallow. Moreover, sufficient strength of the soil cement-like improved body can be maintained.

即ち、本形態によれば、従来の技術による杭、例えば、場所打ち杭、圧入工法、打撃工法、先端拡大根固め工法等の杭と比較して、造成の経済性を著しく向上することができる。   That is, according to the present embodiment, the economic efficiency of the creation can be remarkably improved as compared with piles according to conventional techniques, for example, cast-in-place piles, press-fitting methods, hammering methods, tip enlarged rooting methods, and the like. .

（実施の形態２）
図３は、本発明の実施の形態２における挿入管の一部切欠斜視図である。実施の形態１に比べ、実施の形態２では、挿入管３の外側面が異なる。他の点は、実施の形態１と同様であるため、以下、相違点のみを説明する。 (Embodiment 2)
FIG. 3 is a partially cutaway perspective view of the insertion tube according to Embodiment 2 of the present invention. Compared to the first embodiment, the outer surface of the insertion tube 3 is different in the second embodiment. Since the other points are the same as in the first embodiment, only the differences will be described below.

本形態では、挿入管３の外側面は、粗面６となっている。この粗面６は、好ましくは、無機系砂混塗料を塗布することにより形成される。   In this embodiment, the outer surface of the insertion tube 3 is a rough surface 6. The rough surface 6 is preferably formed by applying an inorganic sand mixed paint.

この無機系砂混塗料としては、無機系防錆塗料（例えば、マイテイ株式会社製、マイテイＣＦ（商標）等）が好適に使用できる。   As the inorganic sand mixed paint, an inorganic rust preventive paint (for example, Mighty CF (trademark) manufactured by Mighty Co., Ltd.) can be suitably used.

粗面６が形成されるため、実施の形態２によると、実施の形態１に比べ、未固化のセメントとの接触面積が大きくなり、より細かに接触することとなり、有利となる。   Since the rough surface 6 is formed, according to the second embodiment, compared with the first embodiment, the contact area with the unsolidified cement is increased, and a finer contact is obtained, which is advantageous.

即ち、粗面６の凹凸へ未固化のセメントが出入りして良く入り交じり、セメントが固化すると、挿入管とセメントとは、強固に結合し、ソイルセメント合成杭全体としての強度が一層高められる。   That is, when the unsolidified cement enters and exits the unevenness of the rough surface 6 and mixes well and the cement is solidified, the insertion tube and the cement are firmly bonded, and the strength of the entire soil cement synthetic pile is further enhanced.

その他の点は、実施の形態１と同様である。   Other points are the same as in the first embodiment.

本発明に係るソイルセメント合成杭の造成方法は、例えば、地盤改良等を行う分野において好適に利用できる。   The method for constructing a soil cement synthetic pile according to the present invention can be suitably used, for example, in the field of ground improvement.

（ａ）本発明の実施の形態１におけるソイルセメント合成杭の造成方法の工程説明図 （ｂ）本発明の実施の形態１におけるソイルセメント合成杭の造成方法の工程説明図 （ｃ）本発明の実施の形態１におけるソイルセメント合成杭の造成方法の工程説明図(A) Process explanatory view of the method for building a soil cement synthetic pile according to Embodiment 1 of the present invention (b) Process explanatory view of the method for forming a soil cement synthetic pile according to Embodiment 1 of the present invention (c) Process explanatory drawing of the construction method of the soil cement synthetic pile in Embodiment 1 本発明の実施の形態１における挿入管の一部切欠斜視図Partially cutaway perspective view of an insertion tube according to Embodiment 1 of the present invention 本発明の実施の形態２における挿入管の一部切欠斜視図Partially cutaway perspective view of an insertion tube according to Embodiment 2 of the present invention

Ｈ１ 通常の造成深さ
Ｈ２ 設定深さ
１ 造成装置
２ ソイルセメント状改良体
３ 挿入管
４ 空洞
５ 溝部
６ 粗面 H1 Normal creation depth H2 Set depth 1 Creation device 2 Soil cement improvement 3 Insertion tube 4 Cavity 5 Groove 6 Rough surface

Claims (2)

通常の造成深度よりも浅い設定深度を定め、
セメント硬化材を注入して所定直径のソイルセメント状改良体を、地盤中において前記設定深度までであるが、前記通常の造成深度には至らないように造成し、
前記ソイルセメント状改良体が固化しないうちに、前記所定直径よりも外径が小径であって、既設コンクリートパイル又は鋼管杭からなる挿入管を挿入し、
前記ソイルセメント状改良体が固化することにより、前記ソイルセメント状改良体と前記挿入管とを一体化するソイルセメント合成杭の造成方法であって、
前記挿入管は、内部を軸方向に貫通する空洞を有する中空構造をなし、かつ、前記挿入管の外側面には凹凸が形成され、前記外側面は非平滑面となっており、
前記外側面は、粗面となっていると共に、前記粗面は、無機系砂混塗料を塗布することにより形成されることを特徴とするソイルセメント合成杭の造成方法。 Set a set depth shallower than the normal creation depth,
Soil cement-like improvement body of a predetermined diameter by injecting cement hardener, up to the set depth in the ground, but so as not to reach the normal formation depth,
Before the soil cement-like improvement body is solidified, the outer diameter is smaller than the predetermined diameter, and an insertion pipe made of an existing concrete pile or a steel pipe pile is inserted,
A method of constructing a soil cement synthetic pile that integrates the soil cement-like improved body and the insertion pipe by solidifying the soil cement-like improved body,
The insertion tube has a hollow structure having a cavity that penetrates the inside in the axial direction, and the outer surface of the insertion tube is uneven, and the outer surface is a non-smooth surface ,
The outer surface is a rough surface, and the rough surface is formed by applying an inorganic sand-mixed paint . 前記外側面には、前記外側面を周回する溝部が形成されている請求項１記載のソイルセメント合成杭の造成方法。 The method for producing a soil cement synthetic pile according to claim 1, wherein a groove portion that goes around the outer surface is formed on the outer surface.
JP2010247595A 2010-11-04 2010-11-04 Construction method of soil cement composite pile Active JP5558314B2 (en)