JP5515944B2 - アルミニウム合金 - Google Patents
アルミニウム合金 Download PDFInfo
- Publication number
- JP5515944B2 JP5515944B2 JP2010074228A JP2010074228A JP5515944B2 JP 5515944 B2 JP5515944 B2 JP 5515944B2 JP 2010074228 A JP2010074228 A JP 2010074228A JP 2010074228 A JP2010074228 A JP 2010074228A JP 5515944 B2 JP5515944 B2 JP 5515944B2
- Authority
- JP
- Japan
- Prior art keywords
- aluminum alloy
- present
- alloy
- content
- less
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
(1)化学組成
Mn:1.4%以上1.6%以下
Mnは金型への耐焼きつき性の向上に寄与する元素である。また、MnはAl−Fe−Mn系化合物を形成し、かかるAl−Fe−Mn系化合物の適正分布によって、延性も向上させる。これらの効果を確保するためには、1.4%以上の量のMnを含有させる必要があるが、Mnの含有量が1.6%を超えると、鋳造時に粗大な晶出物を生ぜしめて伸びを低下させる。したがって、Mnの含有量を1.4%以上1.6%以下の範囲としている。
Cuは、本発明のアルミニウム合金の引張強さ、0.2%耐力および伸びを向上させるために必要不可欠な元素である。こうした効果を得るには、0.75%以上のCuを含有させる必要がある。また、1.0%以上のCuを含有させれば、一層高い効果が得られる。しかしながら、2.1%を超える量のCuを含有させると、延性の低下を生じてしまう。そのため、Cuの含有量は0.75%以上2.1%以下とした。より好ましくは、Cuの含有量は1.0%以上2.1%以下である。
Feは鋳造に際し、合金溶湯の金型への焼き付きを防止する効果がある。Fe成分の含有量は、0.4%よりも少ないと、金型との焼き付きが生じ易くなる反面、0.7%よりも多いと、Mn成分と同様に化合物が生じ易くなり、伸びが従来の合金以下に低下するので、0.4%以上0.7%以下の範囲としている。
Mgは、Siと共存して熱処理によりMg2Siとして析出し、引張強さ及び耐力等の機械的強度を向上させる。しかし、その含有量が0.2%よりも少ないと、その効果が少なく、逆に0.5%を超えると延性が低下する。したがって、Mgの含有量を0.2%以上0.5%以下の範囲としている。
Tiは、鋳物の結晶粒を微細化することによりその特性を向上させて鋳造割れ性を改善させることができるが、その含有量が0.1%よりも少ないと、その効果が少なく、鋳造割れ性を十分に改善させることが困難となる。一方、Tiの含有量が0.2%よりも多いと、粗大化合物が生成されて伸びが低下し、溶湯の流動性も低下させるので、0.1%以上0.2%以下の範囲としている。
Siは、強度を高める作用を有するが、Siの含有量が0.03%未満では効果に乏しい。一方、Siの含有量が0.07%を超えると、SiはFeとともにAl−Fe−Siといった金属間化合物を形成して、延性を阻害する。このため、Siの下限を0.03%とし、その上限を0.07%とする。
(2)Al−Mg−Cu系化合物
Al−Mg−Cu系化合物は、強度を高める作用を有している。このため、本発明では0.75%以上のCuを含有させることで、積極的にAl−Mg−Cu系化合物を生成させてマトリックス(初晶α相)中に分散させるようにしている。しかしながら、Mgを含む合金に対して多量のCuを添加することは、熱間割れ性を低下させるおそれがあるため、上述の如くCuの含有量を制限している。
(3)Al−Fe−Mn系化合物
Al−Fe−Mn系化合物は、これを6〜15μmのサイズに制御することによって、延性を向上させるが、50μm以上の粗大なAl−Fe−Mn系晶出物が形成されると延性が著しく劣化し、とくにMnとFeの合計含有量が1.3%を越えると、鋳造時に粗大な晶出物が形成され延性を低下させる。このため、本発明ではマトリックス中ではなく、第2相中にAl−Fe−Mn系化合物が微細に分散するように、MnとFeの合計含有量を調整している。さらに、Cuの含有量を適切に調整することにより、Al−Fe−Mn系化合物をAl−Fe−Mn−Cu系化合物と混合状態で第2相中に分散させている。
Claims (4)
- 質量%で、Mn:1.4%以上1.6%以下、Cu:0.75%以上2.1%以下、Fe:0.4%以上0.7%以下、Mg:0.2%以上0.5%以下、Ti:0.1%以上0.2%以下、Si:0.03%以上0.07%以下を含有し、残部がAl及び不可避的不純物からなり、マトリックス中にAl−Mg−Cu系化合物が分散していることを特徴とするアルミニウム合金。
- 請求項1記載のアルミニウム合金において、
質量%で、Cuの含有量が1.0%以上2.1%以下であることを特徴とするアルミニウム合金。 - 請求項1又は2記載のアルミニウム合金において、
上記マトリックス中に第2相が分散しており、
上記第2相中にAl−Fe−Mn系化合物が分散していることを特徴とするアルミニウム合金。 - 請求項1〜3のいずれか1つに記載のアルミニウム合金において、
鋳造に用いられる鋳造用アルミニウム合金であることを特徴とするアルミニウム合金。