JP5515609B2 - Photo-curable coating composition - Google Patents
Photo-curable coating composition Download PDFInfo
- Publication number
- JP5515609B2 JP5515609B2 JP2009242866A JP2009242866A JP5515609B2 JP 5515609 B2 JP5515609 B2 JP 5515609B2 JP 2009242866 A JP2009242866 A JP 2009242866A JP 2009242866 A JP2009242866 A JP 2009242866A JP 5515609 B2 JP5515609 B2 JP 5515609B2
- Authority
- JP
- Japan
- Prior art keywords
- meth
- component
- acrylate
- group
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、光硬化型塗料組成物に関し、光硬化型組成物及び塗料の技術分野に属する。 The present invention relates to a photocurable coating composition, and belongs to the technical field of photocurable compositions and coatings.
従来、木材、金属、コンクリート及びプラスチック等の種々の基材に対しては、基材表面を保護したり、美観や意匠性を付与する目的で、塗料組成物を使用して塗装がされることが多い。
特に、プラスチック基材は、軽量であり、耐衝撃性及び易成形性等に優れているが、表面が傷つきやすく硬度が低いため、そのまま使用すると外観を著しく損なうという欠点がある。このため、プラスチック基材の表面を塗料組成物で塗装し、いわゆるハードコート処理して、耐磨耗性及び耐擦傷性等を付与することが多い。
Conventionally, various base materials such as wood, metal, concrete, and plastic are coated with a coating composition for the purpose of protecting the surface of the base material and imparting aesthetics and design. There are many.
In particular, the plastic substrate is lightweight and excellent in impact resistance, easy moldability, and the like. However, since the surface is easily damaged and has low hardness, there is a drawback that the appearance is remarkably impaired when used as it is. For this reason, the surface of a plastic substrate is often painted with a coating composition and subjected to a so-called hard coat treatment to impart abrasion resistance, scratch resistance, and the like.
従来の塗料組成物は、樹脂を溶剤に溶解させた塗料組成物を使用し、基材に塗装した後乾燥して樹脂被膜を形成させるものであったが、生産性を改善する等の目的で、光硬化型組成物や熱硬化型組成物も検討されるようになってきている。
プラスチック基材のハードコートにおいては、紫外線硬化型のアクリル系ハードコート剤、熱硬化型のシリコン系ハードコート剤が提案されている。
熱硬化型のシリコン系ハードコート剤は耐磨耗性及び耐擦傷性に優れるが、硬化時間が長く生産性に劣ることと硬化時に高温を必要とするため基材の変形等の問題がある。これに対して、紫外線硬化型のアクリル系ハードコート剤は、耐磨耗性及び耐擦傷性が劣るものの硬化時間が短く生産性に優れている。
The conventional coating composition uses a coating composition in which a resin is dissolved in a solvent, and is applied to a substrate and then dried to form a resin film. For the purpose of improving productivity, etc. In addition, photocurable compositions and thermosetting compositions have been studied.
As hard coatings for plastic substrates, ultraviolet curable acrylic hard coating agents and thermosetting silicon hard coating agents have been proposed.
The thermosetting silicone hard coat agent is excellent in abrasion resistance and scratch resistance, but has problems such as deformation of the base material because of a long curing time and inferior productivity and a high temperature required for curing. On the other hand, the ultraviolet curable acrylic hard coating agent is inferior in abrasion resistance and scratch resistance, but has a short curing time and excellent productivity.
紫外線硬化型アクリル系ハードコート剤は、熱硬化型組成物に対して生産性及び省エネルギーの観点で優れており、この特長を生かすため、不十分な性能であった硬化膜の耐磨耗性及び耐擦傷性を向上させる検討が行われている。
例えば、組成物に、コロイダルシリカを配合したり、（メタ）アクリロイルオキシ基を有するシラン化合物を配合する方法が知られている。
具体的には、コロイダルシリカ、（メタ）アクリロイルオキシ基を有するアルコキシシラン及びアクリレートを含む紫外線硬化型塗料組成物（特許文献１）、イソシアネート含有アルコキシシランと分子内に水酸基と３個以上のアクリロイル基を有する多官能アクリレートとの反応物、３個以上のアクリロイル基を有する多官能アクリレート及びコロイダルシリカを含む紫外線硬化型塗料組成物（特許文献２）が知られている。
しかしながら、これら塗料組成物は、従来の紫外線硬化型塗料組成物と比較して硬化膜の耐磨耗性及び耐擦傷性に優れるものの、耐磨耗性及び耐擦傷性の両方を同時に満足できなかったり、実用上満足な性能を有していなかったりするものであった。又、使用する基材によっては密着性が不十分となることがあった。
The UV curable acrylic hard coating agent is superior to the thermosetting composition in terms of productivity and energy saving, and in order to take advantage of this feature, the abrasion resistance of the cured film, which was insufficient performance, and Studies are being made to improve the scratch resistance.
For example, a method of blending a composition with colloidal silica or a silane compound having a (meth) acryloyloxy group is known.
Specifically, colloidal silica, an ultraviolet curable coating composition containing an alkoxysilane and acrylate having a (meth) acryloyloxy group (Patent Document 1), an isocyanate-containing alkoxysilane, a hydroxyl group and three or more acryloyl groups in the molecule There is known an ultraviolet curable coating composition (Patent Document 2) containing a reaction product with a polyfunctional acrylate having a polyfunctional acrylate, a polyfunctional acrylate having three or more acryloyl groups, and colloidal silica.
However, these coating compositions are excellent in abrasion resistance and scratch resistance of the cured film as compared with conventional UV curable coating compositions, but cannot satisfy both abrasion resistance and scratch resistance at the same time. Or did not have satisfactory performance in practice. In addition, the adhesion may be insufficient depending on the substrate used.
本発明者らは、種々の基材に対して、特にプラスチック基材に対して、硬化膜が耐磨耗性、耐擦傷性及び密着性に優れる光硬化型塗料組成物を見出すため鋭意検討を行ったのである。 The present inventors have intensively studied to find a photocurable coating composition having a cured film excellent in abrasion resistance, scratch resistance and adhesion to various substrates, particularly plastic substrates. I went there.
本発明者らは、前記課題を解決するため鋭意検討した結果、水酸基を１個以上有する特定の（メタ）アクリレートとイソシアネートを反応させたウレタンアダクト化合物、特定の多官能（メタ）アクリレート、特定の製造方法で得られた（メタ）アクリロイル基を有するシラン化合物を含む組成物が、耐磨耗性、耐擦傷性及び密着性に優れた性能を発揮することを見出し、本発明を完成するに至った。
以下、本発明を詳細に説明する。
As a result of intensive studies to solve the above problems, the present inventors have found that a urethane adduct compound obtained by reacting a specific (meth) acrylate having one or more hydroxyl groups with an isocyanate, a specific polyfunctional (meth) acrylate, a specific The composition containing a silane compound having a (meth) acryloyl group obtained by the production method has been found to exhibit excellent performance in abrasion resistance, scratch resistance and adhesion, and the present invention has been completed. It was.
Hereinafter, the present invention will be described in detail.
本発明の組成物によれば、種々の基材に対して、特にプラスチック基材に対して、硬化膜が耐磨耗性、耐擦傷性及び密着性に優れたものとなる。 According to the composition of the present invention, the cured film is excellent in wear resistance, scratch resistance and adhesion to various substrates, particularly to a plastic substrate.
本発明は、後記（Ａ）成分及び後記（Ｂ）成分の合計１００重量部に対して、
（Ａ）成分を９７〜４０重量部、
（Ｂ）成分を３〜６０重量部、
光重合開始剤（Ｃ）を０．１〜１０重量部及び
有機溶剤（Ｄ）を１０〜１０００重量部
含有する光硬化型塗料組成物に関する。
以下、それぞれの成分及び組成物の詳細について説明する。
尚、本明細書においては、アクリロイル基又はメタクリロイル基を（メタ）アクリロイル基と表し、又、アクリレート又はメタクリレートを（メタ）アクリレートと表す。
The present invention is based on a total of 100 parts by weight of the component (A) and the component (B) described later,
97 to 40 parts by weight of component (A)
(B) 3-60 parts by weight of component,
The present invention relates to a photocurable coating composition containing 0.1 to 10 parts by weight of a photopolymerization initiator (C) and 10 to 1000 parts by weight of an organic solvent (D).
Hereinafter, the detail of each component and a composition is demonstrated.
In the present specification, an acryloyl group or a methacryloyl group is represented as a (meth) acryloyl group, and an acrylate or methacrylate is represented as a (meth) acrylate.
１．（Ａ）成分
本発明の（Ａ）成分は、３価以上の脂肪族多価アルコールから誘導される（メタ）アクリレートであって、（メタ）アクリロイル基を２個以上有し、水酸基を１個以上有する（メタ）アクリレートとポリイソシアネートとの付加反応で得られるウレタンアダクト化合物（ａ１）（以下、「（ａ１）成分」という）及び
３価以上の脂肪族多価アルコールから誘導される（メタ）アクリレートであって、（メタ）アクリロイル基を３個以上有し、水酸基を有さない（メタ）アクリレート（ａ２）（以下、「（ａ２）成分」という）から構成される（メタ）アクリレート混合物である。
1. Component (A) Component (A) of the present invention is a (meth) acrylate derived from a trihydric or higher aliphatic polyhydric alcohol, having two or more (meth) acryloyl groups and one hydroxyl group. (Meth) derived from urethane adduct compound (a1) (hereinafter referred to as “component (a1)”) obtained by addition reaction of (meth) acrylate and polyisocyanate having the above and trivalent or higher aliphatic polyhydric alcohol (Meth) acrylate mixture composed of (meth) acrylate (a2) (hereinafter referred to as “component (a2)”) having 3 or more (meth) acryloyl groups and no hydroxyl group is there.
（ａ１）成分の原料化合物は、３価以上の脂肪族多価アルコールから誘導される（メタ）アクリレートであって、（メタ）アクリロイル基を２個以上有し、水酸基を１個以上有する（メタ）アクリレート（以下、水酸基含有多官能（メタ）アクリレート」という）である。
水酸基含有多官能（メタ）アクリレートの原料化合物である３価以上の脂肪族多価アルコールとしては、種々の化合物が使用でき、トリメチロールプロパン、ペンタエリスリトール、ジトリメチロールプロパン及びジペンタエリスリトール等が挙げられる。
水酸基含有多官能（メタ）アクリレートとしては、種々の化合物が使用でき、具体的には、トリメチロールプロパンジ（メタ）アクリレート、ペンタエリスリトールのジ又はトリ（メタ）アクリレート、ジトリメチロールプロパンのジ又はトリ（メタ）アクリレート及びジペンタエリスリトールのジ、トリ、テトラ又はペンタ（メタ）アクリレート等が挙げられる。
これらの中でも、硬化膜が耐磨耗性と耐擦傷性に優れる点で、３個以上の（メタ）アクリロイル基を有し、水酸基を１個有する化合物が好ましく、具体的には、ペンタエリスリトールトリ（メタ）アクリレート、ジトリメチロールプロパントリ（メタ）アクリレート及びジペンタエリスリトールペンタ（メタ）アクリレート等が挙げられる。
The raw material compound of the component (a1) is a (meth) acrylate derived from a trihydric or higher aliphatic polyhydric alcohol, having two or more (meth) acryloyl groups and one or more hydroxyl groups (meta ) Acrylate (hereinafter referred to as “hydroxyl-containing polyfunctional (meth) acrylate”).
Various compounds can be used as the trihydric or higher aliphatic polyhydric alcohol which is a raw material compound of a hydroxyl group-containing polyfunctional (meth) acrylate, and examples include trimethylolpropane, pentaerythritol, ditrimethylolpropane, and dipentaerythritol. .
As the hydroxyl group-containing polyfunctional (meth) acrylate, various compounds can be used, specifically, trimethylolpropane di (meth) acrylate, pentaerythritol di- or tri (meth) acrylate, ditrimethylolpropane di- or tri- Examples include (meth) acrylate and dipentaerythritol di, tri, tetra, or penta (meth) acrylate.
Among these, a compound having three or more (meth) acryloyl groups and one hydroxyl group is preferable in that the cured film is excellent in abrasion resistance and scratch resistance. Specifically, pentaerythritol trisitol is preferable. (Meth) acrylate, ditrimethylolpropane tri (meth) acrylate, dipentaerythritol penta (meth) acrylate, and the like.
（ａ１）成分のもう一方の合成原料である、ポリイソシアネートとしては、種々の化合物が使用可能である。
好ましいポリイソシアネートの例としては、イソホロンジイソシアネート、ヘキサメチレンジイソシアネート、４，４’−ジシクロヘキシルメタンジイソシアネート、ノルボルナンジイソシアネート、２，４−トリレンジイソシアネート及びこれらのヌレート型三量体等が挙げられる。
Various compounds can be used as the polyisocyanate, which is the other synthetic raw material of the component (a1).
Examples of preferred polyisocyanates include isophorone diisocyanate, hexamethylene diisocyanate, 4,4′-dicyclohexylmethane diisocyanate, norbornane diisocyanate, 2,4-tolylene diisocyanate, and their nurate type trimers.
（ａ１）成分は、水酸基含有多官能（メタ）アクリレートとポリイソシアネートとの付加反応により合成される。この付加反応は無触媒でも可能であるが、反応を効率的に進めるために、ジブチルスズジラウレート等の錫系触媒や、トリエチルアミン等のアミン系触媒等を添加しても良い。 The component (a1) is synthesized by an addition reaction between a hydroxyl group-containing polyfunctional (meth) acrylate and a polyisocyanate. Although this addition reaction can be performed without a catalyst, a tin-based catalyst such as dibutyltin dilaurate, an amine-based catalyst such as triethylamine, or the like may be added in order to advance the reaction efficiently.
（ａ２）成分は、３価以上の脂肪族多価アルコールから誘導される（メタ）アクリレートである。
（ａ２）成分の原料化合物である３価以上の脂肪族多価アルコールとしては、前記で挙げたものと同様のものが使用できる。
（ａ２）成分の具体例としては、トリメチロールプロパントリ（メタ）アクリレート、ペンタエリスリトールテトラ（メタ）アクリレート、ジトリメチロールプロパンテトラ（メタ）アクリレート及びジペンタエリスリトールヘキサ（メタ）アクリレート等が挙げられる。
これらの中でも、硬化膜が耐磨耗性と耐擦傷性に優れる点で、４個以上の（メタ）アクリロイル基を有する化合物が好ましく、具体的には、ペンタエリスリトールテトラ（メタ）アクリレート、ジトリメチロールプロパンテトラ（メタ）アクリレート及びジペンタエリスリトールヘキサ（メタ）アクリレート等が挙げられる。
The component (a2) is a (meth) acrylate derived from a trihydric or higher aliphatic polyhydric alcohol.
As the trihydric or higher aliphatic polyhydric alcohol which is a raw material compound of the component (a2), the same as those mentioned above can be used.
Specific examples of the component (a2) include trimethylolpropane tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, ditrimethylolpropane tetra (meth) acrylate, dipentaerythritol hexa (meth) acrylate, and the like.
Among these, a compound having four or more (meth) acryloyl groups is preferable in that the cured film is excellent in wear resistance and scratch resistance. Specifically, pentaerythritol tetra (meth) acrylate and ditrimethylol are preferable. Examples include propanetetra (meth) acrylate and dipentaerythritol hexa (meth) acrylate.
本発明の（Ａ）成分は、（ａ１）成分と（ａ２）成分の混合物である。
（ａ１）成分と（ａ２）成分の割合は目的に応じて適宜設定すれば良いが、（ａ１）：（ａ２）＝１０：９０〜７５：２５の重量比で含む混合物が好ましく、より好ましくは（ａ１）：（ａ２）＝３０：７０〜７０：３０の重量比で含む混合物である。
（ａ１）と（ａ２）の重量比をこの範囲とすることで、硬化膜が耐磨耗性と耐擦傷性に優れた組成物を得ることができる。
The component (A) of the present invention is a mixture of the component (a1) and the component (a2).
The ratio of the component (a1) and the component (a2) may be appropriately set according to the purpose, but a mixture containing (a1) :( a2) = 10: 90 to 75:25 is preferred, more preferably (A1) :( a2) = a mixture containing a weight ratio of 30:70 to 70:30.
By setting the weight ratio of (a1) and (a2) within this range, a composition in which the cured film is excellent in wear resistance and scratch resistance can be obtained.
本発明の組成物における（Ａ）成分の含有割合は、（Ａ）成分及び（Ｂ）成分の合計１００重量部に対して、９７〜４０重量部であり、より好ましくは８０〜５０重量部である。
（Ａ）成分の含有割合を９７〜４０重量部とすることで、硬化膜が耐磨耗性と耐擦傷性に優れた組成物とすることができる。
The content ratio of the component (A) in the composition of the present invention is 97 to 40 parts by weight, more preferably 80 to 50 parts by weight, based on 100 parts by weight of the total of the components (A) and (B). is there.
By setting the content ratio of the component (A) to 97 to 40 parts by weight, the cured film can be made into a composition having excellent wear resistance and scratch resistance.
２．（Ｂ）成分
本発明の（Ｂ）成分は、下記一般式（１）で表される（メタ）アクリロイル基含有ケイ素化合物（ｂ１）（以下、「化合物（ｂ１）」という）と下記一般式（２）で表されるケイ素化合物（ｂ２）（以下、「化合物（ｂ２）」という）とを、化合物（ｂ１）１モルに対して、化合物（ｂ２）０．３〜１．８モルの割合で、アルカリ性条件下で加水分解共重縮合させて得られる有機ケイ素化合物である。
2. Component (B) The component (B) of the present invention comprises a (meth) acryloyl group-containing silicon compound (b1) (hereinafter referred to as “compound (b1)”) represented by the following general formula (1) and the following general formula ( 2) The silicon compound (b2) represented by (2) (hereinafter referred to as “compound (b2)”) at a ratio of 0.3 to 1.8 mol of compound (b2) to 1 mol of compound (b1). An organosilicon compound obtained by hydrolytic copolycondensation under alkaline conditions.
（一般式（１）において、Ｒ1は炭素数１〜６のアルキル基、炭素数７〜１０のアラルキル基又は炭素数６〜１０のアリール基を有する有機基であり、Ｒ2は炭素数１〜６の２価の飽和炭化水素基であり、Ｒ3は水素原子又はメチル基であり、Ｘは加水分解性基であり、Ｘは同一であっても異なっていても良く、ｎは０又は１である。） (In General Formula (1), R 1 is an organic group having an alkyl group having 1 to 6 carbon atoms, an aralkyl group having 7 to 10 carbon atoms, or an aryl group having 6 to 10 carbon atoms, and R 2 is 1 carbon atom. To 6 divalent saturated hydrocarbon groups, R 3 is a hydrogen atom or a methyl group, X is a hydrolyzable group, X may be the same or different, and n is 0 or 1)
ＳｉＹ4 （２）
（一般式（２）において、Ｙはシロキサン結合生成基であり、Ｙは同一であっても異なっていても良い。）
SiY 4 (2)
(In general formula (2), Y is a siloxane bond-forming group, and Y may be the same or different.)
一般式（１）において、Ｒ1は炭素数１〜６のアルキル基、炭素数７〜１０のアラルキル基又は炭素数６〜１０のアリール基を有する有機基である。
これらの中でも、炭素数１〜６のアルキル基が好ましく、得られる組成物の硬化膜が耐磨耗性に優れる点で、メチル基がより好ましい。
Ｒ2は炭素数１〜６の２価の飽和炭化水素基であり、アルキレン基が好ましい。アルキレン基としては、得られる組成物の硬化膜が耐磨耗性に優れるものとなり、原料コストの点から、トリメチレン基がより好ましい。Ｒ3は水素原子又はメチル基である。
Ｘは加水分解性基であり、Ｘは同一であっても異なっていても良い。加水分解性基としては、加水分解性を有する基であれば種々の基が可能である。具体的には、水素原子、アルコキシ基、シクロアルコキシ基、アリールオキシ基及びアリールアルコキシ基が挙げられる。これらの中でもアルコキシ基が好ましく、炭素数１〜６のアルコキシ基がより好ましい。アルコキシ基の具体例としては、メトキシ基、エトキシ基、プロポキシ基、ブトキシ基、ペンチルオキシ基及びヘキシルオキシ基等が挙げられる。
又、ｎは０又は１であり、得られる組成物の硬化膜が耐磨耗性に優れる点で、好ましくは０である。
In the general formula (1), R 1 is an organic group having an alkyl group, an aralkyl group or an aryl group having 6 to 10 carbon atoms of 7 to 10 carbon atoms having 1 to 6 carbon atoms.
Among these, a C1-C6 alkyl group is preferable and a methyl group is more preferable at the point which the cured film of the composition obtained is excellent in abrasion resistance.
R 2 is a divalent saturated hydrocarbon group having 1 to 6 carbon atoms, preferably an alkylene group. As the alkylene group, a cured film of the resulting composition has excellent wear resistance, and a trimethylene group is more preferable from the viewpoint of raw material cost. R 3 is a hydrogen atom or a methyl group.
X is a hydrolyzable group, and X may be the same or different. As the hydrolyzable group, various groups can be used as long as they are hydrolyzable groups. Specific examples include a hydrogen atom, an alkoxy group, a cycloalkoxy group, an aryloxy group, and an arylalkoxy group. Among these, an alkoxy group is preferable, and an alkoxy group having 1 to 6 carbon atoms is more preferable. Specific examples of the alkoxy group include a methoxy group, an ethoxy group, a propoxy group, a butoxy group, a pentyloxy group, and a hexyloxy group.
Further, n is 0 or 1, and is preferably 0 in that the cured film of the resulting composition is excellent in wear resistance.
一般式（１）において、好ましい化合物であるｎが０でＸがアルコキシ基である化合物の具体例としては、２−（メタ）アクリロイルオキシエチルトリエトキシシラン、３−（メタ）アクリロイルオキシプロピルトリメトキシシラン及び３−（メタ）アクリロイルオキシプロピルエチルトリエトキシシラン等が挙げられる。 In the general formula (1), specific examples of a compound where n is 0 and X is an alkoxy group are preferable compounds: 2- (meth) acryloyloxyethyltriethoxysilane, 3- (meth) acryloyloxypropyltrimethoxy Examples thereof include silane and 3- (meth) acryloyloxypropylethyltriethoxysilane.
一般式（２）において、Ｙはシロキサン結合生成基であり、１分子中のシロキサン結合生成基は同一であっても異なっていても良い。
シロキサン結合生成基としては、アルコキシ基が好ましい。アルコキシ基の好ましい例としては、メトキシ基、エトキシ基、ｎ−プロポキシ基、ｉｓｏ−プロポキシ基、ｎ−ブトキシ基及びｓｅｃ−ブトキシ基等の炭素数１〜４のアルコキシ基が挙げられる。
化合物（ｂ２）の好ましい具体例は、テトラ−ｎ−プロポキシシラン、トリメトキシ−ｎ−プロポキシシラン、ジメトキシジ−ｎ−プロポキシシラン、メトキシトリ−ｎ−プロポキシシラン等のｎ−プロポキシ基を有するアルコキシシラン化合物である。
ｎ−プロポキシ基含有アルコキシシラン化合物は、１種の化合物でも、ｎ−プロポキシ基を有し、他のアルコキシ基を有する化合物の混合物でも良い。
ｎ−プロポキシ基含有アルコキシシラン化合物の混合物は、複数種の成分を混合して使用することもできるが、アルコール交換によって製造したものをそのまま使用することもできる。例えば、上記一般式（２）で表されるケイ素化合物であり、且つｎ−プロポキシ基を有さない化合物（例えば、テトラメトキシシラン）を、１−プロパノール中でアルコール交換反応させることにより得ることができる。又、この反応により得られた反応生成物をそのまま用いることもできる。
In the general formula (2), Y is a siloxane bond generating group, and the siloxane bond generating groups in one molecule may be the same or different.
As the siloxane bond-forming group, an alkoxy group is preferable. Preferable examples of the alkoxy group include an alkoxy group having 1 to 4 carbon atoms such as a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group and a sec-butoxy group.
Preferred specific examples of the compound (b2) are alkoxysilane compounds having an n-propoxy group such as tetra-n-propoxysilane, trimethoxy-n-propoxysilane, dimethoxydi-n-propoxysilane, methoxytri-n-propoxysilane and the like. .
The n-propoxy group-containing alkoxysilane compound may be a single compound or a mixture of compounds having an n-propoxy group and other alkoxy groups.
The mixture of the n-propoxy group-containing alkoxysilane compound can be used by mixing plural kinds of components, but can also be used as it is produced by alcohol exchange. For example, it can be obtained by subjecting a silicon compound represented by the above general formula (2) and having no n-propoxy group (for example, tetramethoxysilane) to alcohol exchange reaction in 1-propanol. it can. Moreover, the reaction product obtained by this reaction can also be used as it is.
（Ｂ）成分は、化合物（ｂ１）と化合物（ｂ２）とを、化合物（ｂ１）１モルに対して、化合物（ｂ２）０．３〜１．８モルの割合で、アルカリ性条件下で加水分解共重縮合させ（以下、「第１工程」という）得られるものである。 The component (B) hydrolyzes the compound (b1) and the compound (b2) at a ratio of 0.3 to 1.8 mol of the compound (b2) with respect to 1 mol of the compound (b1) under alkaline conditions. It is obtained by copolycondensation (hereinafter referred to as “first step”).
化合物（ｂ１）と化合物（ｂ２）との反応割合は、化合物（ｂ１）１モルに対して、化合物（ｂ２）０．３〜１．８モルであり、好ましくは化合物（ｂ２）が０．８〜１．８モルの割合で、より好ましくは化合物（ｂ２）が１〜１．８モルである。この割合で反応させることにより、反応中及び反応後のゲル化を生じることなく、（Ｂ）成分を効率よく製造することができる。
上記第１工程はアルカリ性条件下での反応であり、これにより反応後のゲル化を防止することができ、高収率で（Ｂ）成分を製造することができる。
具体的には、反応液のｐＨが７を超える値であり、好ましくｐＨが８以上であり、更に好ましくはｐＨが９以上である。尚、上限は、通常、ｐＨ１３である。反応系を上記ｐＨとすることにより、保存安定性に優れた（Ｂ）成分を高い収率で製造することができる。
酸性条件下（ｐＨ７未満）で加水分解共重縮合させて得られる有機ケイ素化合物は、保存安定性に劣るものとなり、反応条件等によっては保存中にゲル化することもある。
又、中性条件下（ｐＨ７付近）では、加水分解共重縮合反応が進行し難く、有機ケイ素化合物を収率よく得ることができない。
The reaction ratio of the compound (b1) and the compound (b2) is 0.3 to 1.8 mol of the compound (b2) with respect to 1 mol of the compound (b1), preferably 0.8% of the compound (b2). In a proportion of ˜1.8 mol, more preferably the compound (b2) is 1 to 1.8 mol. By reacting at this ratio, the component (B) can be efficiently produced without causing gelation during and after the reaction.
The first step is a reaction under alkaline conditions, whereby gelation after the reaction can be prevented, and the component (B) can be produced in a high yield.
Specifically, the pH of the reaction solution is a value exceeding 7, preferably 8 or more, more preferably 9 or more. The upper limit is usually pH 13. By setting the reaction system to the above pH, the component (B) having excellent storage stability can be produced in a high yield.
The organosilicon compound obtained by hydrolytic copolycondensation under acidic conditions (less than pH 7) is inferior in storage stability and may gel during storage depending on reaction conditions and the like.
Also, under neutral conditions (around pH 7), the hydrolysis copolycondensation reaction does not proceed easily, and the organosilicon compound cannot be obtained in good yield.
上記（Ｂ）成分の製造方法により、化合物（ｂ１）及び化合物（ｂ２）の縮合率は、９２％以上とすることができ、より好ましくは９５％以上、更に好ましくは９８％以上である。シロキサン結合生成基（加水分解性基を含む）は実質的に全てが縮合されていることが最も好ましいが、縮合率の上限は、通常、９９．９％である。 Depending on the method for producing the component (B), the condensation rate of the compound (b1) and the compound (b2) can be 92% or more, more preferably 95% or more, and still more preferably 98% or more. It is most preferable that substantially all of the siloxane bond-forming groups (including hydrolyzable groups) are condensed, but the upper limit of the condensation rate is usually 99.9%.
（Ｂ）成分の製造において、反応系、（Ｂ）成分を含む反応液、中和液、有機系液及び有機溶液の少なくとも１つに対して、（メタ）アクリロイル基の重合を禁止する重合禁止剤を添加することもできる。 In the production of the component (B), a polymerization prohibition prohibiting the polymerization of the (meth) acryloyl group in at least one of the reaction system, the reaction solution containing the component (B), the neutralization solution, the organic solution and the organic solution. An agent can also be added.
公知の方法では、酸性条件での製造方法等有機ケイ素化合物を製造する方法が知られているが、原料化合物の化合物（ｂ１）と化合物（ｂ２）の両者を均一に反応させることは難しく、ゲルが生じ易いものであった。このため、トリメチルアルコキシシランやヘキサメチルジシロキサン等の、シロキサン結合生成基を１つのみ有するケイ素化合物（以下、「Ｍモノマー」という）を末端封止剤として作用させることでゲル化を回避する方法が知られている。
しかしながら、所定量以上のＭモノマーを併用することで、ゲル化は回避できても、得られる有機ケイ素化合物の無機的性質は低下する傾向にある。
一方、前記製造方法によれば、化合物（ｂ１）と化合物（ｂ２）をゲル化させずに共重縮合させることができ、その上、得られる硬化物の無機的性質を低下することがないという効果を奏する。
In the known method, a method for producing an organosilicon compound such as a production method under acidic conditions is known, but it is difficult to uniformly react both the compound (b1) and the compound (b2) of the raw material compound. It was easy to occur. Therefore, a method of avoiding gelation by causing a silicon compound having only one siloxane bond-forming group (hereinafter referred to as “M monomer”), such as trimethylalkoxysilane or hexamethyldisiloxane, to act as an end-capping agent. It has been known.
However, even when gelation can be avoided by using a predetermined amount or more of the M monomer, the inorganic properties of the resulting organosilicon compound tend to decrease.
On the other hand, according to the production method, the compound (b1) and the compound (b2) can be copolycondensed without gelation, and the inorganic properties of the resulting cured product are not deteriorated. There is an effect.
（Ｂ）成分は、前記第１工程を必須として製造されるものであるが、必要に応じて更に以下の工程を含むことができる。
（第２工程）第１工程で得られた反応液を、酸により中和する工程。
（第３工程）第２工程で得られた中和液から揮発性成分を除去する工程。
（第４工程）第３工程で得られた濃縮物と、洗浄用有機溶剤とを、混合及び接触させて、少なくとも有機ケイ素化合物（Ｂ）を洗浄用有機溶剤に溶解する工程。
（第５工程）第４工程で得られた有機系液を水により洗浄した後、有機ケイ素化合物（Ｂ）を含む有機溶液を得る工程。
（第６工程）第５工程で得られた有機溶液から揮発性成分を除去する工程。
（Ｂ）成分の製造方法としては、第１工程、第２工程及び第５工程を含むことが好ましい。
The component (B) is manufactured by using the first step as an essential component, and may further include the following steps as necessary.
(Second step) A step of neutralizing the reaction solution obtained in the first step with an acid.
(Third step) A step of removing volatile components from the neutralized liquid obtained in the second step.
(Fourth step) A step of dissolving and at least dissolving the organosilicon compound (B) in the cleaning organic solvent by mixing and contacting the concentrate obtained in the third step with the cleaning organic solvent.
(5th process) The process of obtaining the organic solution containing an organosilicon compound (B), after wash | cleaning the organic type liquid obtained at the 4th process with water.
(Sixth Step) A step of removing volatile components from the organic solution obtained in the fifth step.
(B) As a manufacturing method of a component, it is preferable to include a 1st process, a 2nd process, and a 5th process.
本発明の組成物における（Ｂ）成分の含有割合は、（Ａ）成分及び（Ｂ）成分の合計１００重量部に対して、３〜７０重量部であり、より好ましくは２０〜５５重量部である。
（Ｂ）成分の含有割合を５〜７０重量部とすることで、硬化膜が耐磨耗性と耐擦傷性に優れた組成物とすることができる。
The content ratio of the component (B) in the composition of the present invention is 3 to 70 parts by weight, more preferably 20 to 55 parts by weight with respect to 100 parts by weight as a total of the components (A) and (B). is there.
By making the content rate of (B) component into 5-70 weight part, it can be set as the composition which the cured film was excellent in abrasion resistance and abrasion resistance.
３．光重合開始剤（Ｃ）
本発明の（Ｃ）成分は、光重合開始剤であり、種々の化合物を使用することができる。
光重合開始剤の具体例としては、２，２−ジメトキシ−１，２−ジフェニルエタン−１−オン、１−ヒドロキシシクロヘキシル−フェニル−ケトン、２−ヒドロキシ−２−メチル−１−フェニル−プロパン−１−オン、１−〔４−（２−ヒドロキシエトキシ）−フェニル〕−２−ヒドロキシ−２−メチル−１−プロパン−１−オン、２−メチル−１−〔４−（メチルチオ）フェニル〕−２−モルフォリノプロパン−１−オン、２−ベンジル−２−ジメチルアミノ−１−（４−モルフォリノフェニル）−ブタン−１−オン、ジエトキシアセトフェノン、オリゴ｛２−ヒドロキシ−２−メチル−１−〔４−（１−メチルビニル）フェニル〕プロパノン｝及び２−ヒドロキシ−１−｛４−〔４−（２−ヒドロキシ−２−メチルプロピオニル）ベンジル〕フェニル｝−２−メチル−プロパン−１−オン等のアセトフェノン系化合物；ベンゾフェノン、４−フェニルベンゾフェノン、２，４，６−トリメチルベンゾフェノン及び４−ベンゾイル−４’−メチル−ジフェニルスルファイド等のベンゾフェノン系化合物；メチルベンゾイルフォルメート、オキシフェニル酢酸の２−（２−オキソ−２−フェニルアセトキシエトキシ）エチルエステル及びオキシフェニル酢酸の２−（２−ヒドロキシエトキシ）エチルエステル等のα−ケトエステル系化合物；２，４，６−トリメチルベンゾイルジフェニルフォスフィンオキサイド、ビス（２，４，６−トリメチルベンゾイル）フェニルフォスフィンオキサイド、ビス（２，６−ジメトキシベンゾイル）−２，４，４−トリメチルペンチルフォスフィンオキサイド等のフォスフィンオキサイド系化合物；ベンゾイン、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインイソプロピルエーテル及びベンゾインイソブチルエーテル等のベンゾイン系化合物；チタノセン系化合物；１−〔４−（４−ベンゾイルフェニルスルファニル）フェニル〕−２−メチル−２−（４−メチルフェニルスルフィニル）プロパン−１−オン等のアセトフェノン／ベンゾフェノンハイブリッド系光開始剤；２−（Ｏ−ベンゾイルオキシム）−１−〔４−（フェニルチオ）〕−１，２−オクタンジオン等のオキシムエステル系光重合開始剤；並びにカンファーキノン等が挙げられる。
3. Photopolymerization initiator (C)
The component (C) of the present invention is a photopolymerization initiator, and various compounds can be used.
Specific examples of the photopolymerization initiator include 2,2-dimethoxy-1,2-diphenylethane-1-one, 1-hydroxycyclohexyl-phenyl-ketone, 2-hydroxy-2-methyl-1-phenyl-propane- 1-one, 1- [4- (2-hydroxyethoxy) -phenyl] -2-hydroxy-2-methyl-1-propan-1-one, 2-methyl-1- [4- (methylthio) phenyl]- 2-morpholinopropan-1-one, 2-benzyl-2-dimethylamino-1- (4-morpholinophenyl) -butan-1-one, diethoxyacetophenone, oligo {2-hydroxy-2-methyl-1 -[4- (1-methylvinyl) phenyl] propanone} and 2-hydroxy-1- {4- [4- (2-hydroxy-2-methylpropionyl) benzyl Acetophenone compounds such as phenyl} -2-methyl-propan-1-one; benzophenones such as benzophenone, 4-phenylbenzophenone, 2,4,6-trimethylbenzophenone and 4-benzoyl-4′-methyl-diphenylsulfide Α-ketoester compounds such as methylbenzoylformate, 2- (2-oxo-2-phenylacetoxyethoxy) ethyl ester of oxyphenylacetic acid and 2- (2-hydroxyethoxy) ethyl ester of oxyphenylacetic acid; 2,4,6-trimethylbenzoyldiphenylphosphine oxide, bis (2,4,6-trimethylbenzoyl) phenylphosphine oxide, bis (2,6-dimethoxybenzoyl) -2,4,4-trimethylpentylphosphine Phosphine oxide compounds such as oxides; benzoin compounds such as benzoin, benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether and benzoin isobutyl ether; titanocene compounds; 1- [4- (4-benzoylphenylsulfanyl) phenyl] Acetophenone / benzophenone hybrid photoinitiators such as 2-methyl-2- (4-methylphenylsulfinyl) propan-1-one; 2- (O-benzoyloxime) -1- [4- (phenylthio)]-1 Oxime ester-based photopolymerization initiators such as 2-octanedione; and camphorquinone.
本発明の組成物における（Ｃ）成分の含有割合は、（Ａ）成分及び（Ｂ）成分の合計を１００重量部に対して、０．１〜１０重量部であり、より好ましくは０．５〜７重量部、特に好ましくは１〜５重量部である。
（Ｃ）成分の含有割合を０．１〜１０重量部とすることで、組成物が硬化性に優れるものとなり、組成物の硬化膜が耐磨耗性及び耐擦傷性に優れたものとなる。
The content ratio of the component (C) in the composition of the present invention is 0.1 to 10 parts by weight, more preferably 0.5 to 100 parts by weight of the sum of the components (A) and (B). -7 parts by weight, particularly preferably 1-5 parts by weight.
By setting the content ratio of the component (C) to 0.1 to 10 parts by weight, the composition has excellent curability, and the cured film of the composition has excellent wear resistance and scratch resistance. .
４．有機溶剤（Ｄ）
本発明の（Ｄ）成分は溶剤であり、種々の化合物を使用することができる。
（Ｄ）成分としては、（Ａ）成分、（Ｂ）成分及び（Ｃ）成分を溶解するものが好ましい。
4). Organic solvent (D)
The component (D) of the present invention is a solvent, and various compounds can be used.
As (D) component, what melt | dissolves (A) component, (B) component, and (C) component is preferable.
好ましい溶剤の具体例としては、エタノール及びイソプロパノール等のアルコール；エチレングリコールモノメチルエーテル及びプロピレングリコールモノメチルエーテル等のアルキレングリコールモノエーテル；ダイアセトンアルコール等のアセトンアルコール；トルエン及びキシレン等の芳香族化合物；プロピレングリコールモノメチルエーテルアセテート、酢酸エチル、酢酸ブチル等のエステル；アセトン、メチルエチルケトン及びメチルイソブチルケトン等のケトン；ジブチルエーテル等のエーテル；並びにＮ−メチルピロリドン等が挙げられる。 Specific examples of preferred solvents include alcohols such as ethanol and isopropanol; alkylene glycol monoethers such as ethylene glycol monomethyl ether and propylene glycol monomethyl ether; acetone alcohols such as diacetone alcohol; aromatic compounds such as toluene and xylene; propylene glycol Examples thereof include esters such as monomethyl ether acetate, ethyl acetate and butyl acetate; ketones such as acetone, methyl ethyl ketone and methyl isobutyl ketone; ethers such as dibutyl ether; and N-methylpyrrolidone.
本発明の組成物における（Ｄ）成分の含有割合は、（Ａ）成分及び（Ｂ）成分の合計１００重量部に対して、１０〜１０００重量部であり、より好ましくは５０〜５００重量部、さらに好ましくは５０〜３００重量部である。
（Ｄ）成分の含有割合を１０〜１０００重量部とすることで、公知の塗布方法（バーコート、ロールコート、スピンコート、ディップコート、グラビアコート、フローコート、スプレーコート等）に対応した塗料組成物とすることができる。
The content ratio of the component (D) in the composition of the present invention is 10 to 1000 parts by weight, more preferably 50 to 500 parts by weight, with respect to 100 parts by weight of the total of the components (A) and (B). More preferably, it is 50-300 weight part.
(D) The coating composition corresponding to a well-known coating method (bar coat, roll coat, spin coat, dip coat, gravure coat, flow coat, spray coat, etc.) by setting the content ratio of the component to 10 to 1000 parts by weight. It can be a thing.
５．光硬化型塗料組成物
本発明の組成物は、前記（Ａ）〜（Ｄ）成分を必須とする光硬化型塗料組成物に関する。
組成物の製造方法としては、常法に従えば良く、前記必須成分及び必要に応じてその他成分を、攪拌・混合して製造することができる
5). Photocurable coating composition The composition of the present invention relates to a photocurable coating composition comprising the components (A) to (D) as essential components.
As a method for producing the composition, a conventional method may be followed, and the essential components and, if necessary, other components can be produced by stirring and mixing.
本発明の組成物は、前記（Ａ）〜（Ｄ）成分を必須とするものであるが、目的に応じて、顔料、染料、表面調整剤、紫外線吸収剤、ラジカル重合性不飽和基を有する化合物及びポリマー等の種々の成分を配合することができる。 The composition of the present invention essentially comprises the components (A) to (D), but has a pigment, a dye, a surface conditioner, an ultraviolet absorber, and a radical polymerizable unsaturated group depending on the purpose. Various components such as compounds and polymers can be blended.
本発明の組成物には、塗布時のレベリング性を高める目的や、硬化塗膜の防汚性や滑り性を高める目的等のため、各種表面調整剤を添加しても良い。表面調整剤としては、シリコーン系表面調整剤や、フッ素系表面調整剤が好適である。具体例としては、シリコーン鎖とポリアルキレンオキサイド鎖を有するシリコーン系ポリマー、パーフルオロアルキル基とポリアルキレンオキサイド鎖を有するフッ素系ポリマー、及びパーフルオロアルキルエーテル鎖とポリアルキレンオキサイド鎖を有するフッ素系ポリマーが挙げられる。 Various surface conditioners may be added to the composition of the present invention for the purpose of enhancing the leveling property at the time of application, the purpose of enhancing the antifouling property and slipperiness of the cured coating film, and the like. As the surface conditioner, a silicone-based surface conditioner or a fluorine-based surface conditioner is suitable. Specific examples include a silicone polymer having a silicone chain and a polyalkylene oxide chain, a fluorine polymer having a perfluoroalkyl group and a polyalkylene oxide chain, and a fluorine polymer having a perfluoroalkyl ether chain and a polyalkylene oxide chain. Can be mentioned.
表面調整剤の好ましい配合量は、（Ａ）及び（Ｂ）成分の合計１００重量部に対して０．０１〜３重量部であり、より好ましくは０．０２〜０．５重量部とすることで、塗膜の表面平滑性を高め、塗布時の気泡を抑制することができる。 The preferable compounding amount of the surface conditioner is 0.01 to 3 parts by weight, more preferably 0.02 to 0.5 parts by weight, based on 100 parts by weight of the total of the components (A) and (B). Thus, the surface smoothness of the coating film can be improved and bubbles during application can be suppressed.
本発明の組成物には、１分子中に１個以上のラジカル重合性不飽和基を有する、（Ａ）成分及び（Ｂ）成分以外の化合物を配合しても良い。 You may mix | blend compounds other than (A) component and (B) component which have 1 or more radically polymerizable unsaturated groups in 1 molecule in the composition of this invention.
１分子中に１個のラジカル重合性不飽和基を有する化合物（以下、「不飽和化合物」という）は、プラスチック基材への密着性を高めるために配合することができる。
不飽和化合物におけるラジカル重合性不飽和基としては、（メタ）アクリロイル基が好ましい。
不飽和化合物の配合割合としては、耐磨耗性が悪化するのを防ぐ観点から、（Ａ）成分、（Ｂ）成分及び不飽和化合物の合計１００重量部に対して、２０重量部以下とすることが好ましい。
A compound having one radical polymerizable unsaturated group in one molecule (hereinafter referred to as “unsaturated compound”) can be blended in order to improve adhesion to a plastic substrate.
The radically polymerizable unsaturated group in the unsaturated compound is preferably a (meth) acryloyl group.
The blending ratio of the unsaturated compound is 20 parts by weight or less with respect to a total of 100 parts by weight of the component (A), the component (B) and the unsaturated compound from the viewpoint of preventing the wear resistance from deteriorating. It is preferable.
不飽和化合物において、１分子中に１個のラジカル重合性不飽和基を有する化合物の具体例としては、（メタ）アクリル酸、アクリル酸のマイケル付加型のダイマー、ω−カルボキシ−ポリカプロラクトンモノ（メタ）アクリレート、フタル酸モノヒドロキシエチル（メタ）アクリレート、メチル（メタ）アクリレート、エチル（メタ）アクリレート、ブチル（メタ）アクリレート、２−エチルヘキシル（メタ）アクリレート、ベンジル（メタ）アクリレート、フェニル（メタ）アクリレート、フェノールのアルキレンオキサイド付加物の（メタ）アクリレート、アルキルフェノールのアルキレンオキサイド付加物の（メタ）アクリレート、シクロヘキシル（メタ）アクリレート、ｔｅｒｔ−ブチルシクロヘキシル（メタ）アクリレート、２−ヒドロキシエチル（メタ）アクリレート、２−ヒドロキシプロピル（メタ）アクリレート、４−ヒドロキシブチルアクリレート、パラクミルフェノールのアルキレンオキサイド付加物の（メタ）アクリレート、オルトフェニルフェノール（メタ）アクリレート、オルトフェニルフェノールのアルキレンオキサイド付加物の（メタ）アクリレート、テトラヒドロフルフリル（メタ）アクリレート、イソボルニル（メタ）アクリレート、トリシクロデカンメチロール（メタ）アクリレート、２−ヒドロキシ−３−フェノキシプロピル（メタ）アクリレート、Ｎ−（２−（メタ）アクリロキシエチル）ヘキサヒドロフタルイミド、Ｎ−（２−（メタ）アクリロキシエチル）テトラヒドロフタルイミド、Ｎ，Ｎ−ジメチルアクリルアミド、アクリロイルモルフォリン、Ｎ−ビニルピロリドン、Ｎ−ビニルカプロラクタム等が挙げられる。 Specific examples of the unsaturated compound having one radical polymerizable unsaturated group in one molecule include (meth) acrylic acid, Michael addition dimer of acrylic acid, ω-carboxy-polycaprolactone mono ( (Meth) acrylate, monohydroxyethyl phthalate (meth) acrylate, methyl (meth) acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, benzyl (meth) acrylate, phenyl (meth) (Meth) acrylate of acrylate, alkylene oxide adduct of phenol, (meth) acrylate of alkylene oxide adduct of alkylphenol, cyclohexyl (meth) acrylate, tert-butylcyclohexyl (meth) acrylate, 2 Hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 4-hydroxybutyl acrylate, (meth) acrylate of alkylene oxide adduct of paracumylphenol, orthophenylphenol (meth) acrylate, alkylene oxide of orthophenylphenol Adduct (meth) acrylate, tetrahydrofurfuryl (meth) acrylate, isobornyl (meth) acrylate, tricyclodecanemethylol (meth) acrylate, 2-hydroxy-3-phenoxypropyl (meth) acrylate, N- (2- ( (Meth) acryloxyethyl) hexahydrophthalimide, N- (2- (meth) acryloxyethyl) tetrahydrophthalimide, N, N-dimethylacrylamide, acryloyl Lumorpholine, N-vinylpyrrolidone, N-vinylcaprolactam and the like can be mentioned.
不飽和化合物において、１分子中に２個以上のラジカル重合性不飽和基を有する化合物（以下、「多官能不飽和化合物」という）は、密着性や耐磨耗性、耐擦傷性を改善させる目的等で配合しても良い。
多官能不飽和化合物におけるラジカル重合性不飽和基の数は、耐磨耗性、耐擦傷性を低下させないためには１分子中に２個以上であることが好ましく、３〜２０個であることがより好ましい。
In unsaturated compounds, a compound having two or more radically polymerizable unsaturated groups in one molecule (hereinafter referred to as “polyfunctional unsaturated compound”) improves adhesion, abrasion resistance, and scratch resistance. You may mix | blend for the objective etc.
The number of radically polymerizable unsaturated groups in the polyfunctional unsaturated compound is preferably 2 or more, and 3 to 20 in one molecule so as not to lower the abrasion resistance and scratch resistance. Is more preferable.
多官能不飽和化合物としては、１分子中に２個以上の（メタ）アクリロイル基を有する化合物が好ましく、具体例としては、以下の化合物が挙げられる。
ビスフェノールＡのアルキレンオキサイド付加物のジ（メタ）アクリレート、ビスフェノールＦのアルキレンオキサイド付加物のジ（メタ）アクリレート、ビスフェノールＺのアルキレンオキサイド付加物のジ（メタ）アクリレート、ビスフェノールＳのアルキレンオキサイド付加物のジ（メタ）アクリレート、チオビスフェノールのアルキレンオキサイド付加物のジ（メタ）アクリレート、ビスフェノールＡのジ（メタ）アクリレート、ビスフェノールＦのジ（メタ）アクリレート、ビスフェノールＺのジ（メタ）アクリレート、ビスフェノールＳのジ（メタ）アクリレート、チオビスフェノールのジ（メタ）アクリレート、トリシクロデカンジメチロールジ（メタ）アクリレート、エチレングリコールジ（メタ）アクリレート、ポリエチレングリコールジ（メタ）アクリレート、プロピレングリコールジ（メタ）アクリレート、ポリプロピレングリコールジ（メタ）アクリレート、ネオペンチルグリコールジ（メタ）アクリレート、１，６−ヘキサンジオールジ（メタ）アクリレート、１，９−ノナンジオールジ（メタ）アクリレート、グリセリンジ（メタ）アクリレート、グリセリンのアルキレンオキサイド付加物のジ（メタ）アクリレート、ダイマー酸ジオールジ（メタ）アクリレート、シクロヘキサンジメチロールジ（メタ）アクリレート、トリメチロールプロパントリ（メタ）アクリレート、トリメチロールプロパンのアルキレンオキサイド付加物のトリ（メタ）アクリレート、ペンタエリスリトールのトリ及びテトラアクリレート、ペンタエリスリトールのアルキレンオキサイド付加物のトリ及びテトラアクリレート、ジトリメチロールプロパンテトラ（メタ）アクリレート、ジペンタエリスリトールヘキサ及びペンタアクリレート、ポリエステル（メタ）アクリレート、エポキシ（メタ）アクリレート、ウレタン（メタ）アクリレート、末端に（メタ）アクリロイル基を有するシリコーン樹脂等が挙げられる。
As the polyfunctional unsaturated compound, a compound having two or more (meth) acryloyl groups in one molecule is preferable, and specific examples thereof include the following compounds.
Di (meth) acrylate of bisphenol A alkylene oxide adduct, di (meth) acrylate of alkylene oxide adduct of bisphenol F, di (meth) acrylate of alkylene oxide adduct of bisphenol Z, alkylene oxide adduct of bisphenol S Di (meth) acrylate, di (meth) acrylate of alkylene oxide adduct of thiobisphenol, di (meth) acrylate of bisphenol A, di (meth) acrylate of bisphenol F, di (meth) acrylate of bisphenol Z, bisphenol S Di (meth) acrylate, di (meth) acrylate of thiobisphenol, tricyclodecane dimethylol di (meth) acrylate, ethylene glycol di (meth) acrylate, polyethylene Glycol di (meth) acrylate, propylene glycol di (meth) acrylate, polypropylene glycol di (meth) acrylate, neopentyl glycol di (meth) acrylate, 1,6-hexanediol di (meth) acrylate, 1,9-nonane Di (meth) acrylate, glycerin di (meth) acrylate, di (meth) acrylate of glycerin alkylene oxide adduct, dimer acid diol di (meth) acrylate, cyclohexane dimethylol di (meth) acrylate, trimethylolpropane tri (meth) ) Acrylate, trimethylolpropane alkylene oxide adduct tri (meth) acrylate, pentaerythritol tri- and tetraacrylate, pentaerythritol alkyle Oxide adduct tri- and tetraacrylate, ditrimethylolpropane tetra (meth) acrylate, dipentaerythritol hexa and pentaacrylate, polyester (meth) acrylate, epoxy (meth) acrylate, urethane (meth) acrylate, terminal (meth) acryloyl Examples thereof include a silicone resin having a group.
ポリエステル（メタ）アクリレートとしては、ポリエステルポリオールと（メタ）アクリル酸との脱水縮合物が挙げられる。ポリエステルポリオールとしては、エチレングリコール、ポリエチレングリコール、シクロヘキサンジメチロール、３−メチル−１，５−ペンタンジオール、プロピレングリコール、ポリプロピレングリコール、１，６−ヘキサンジオール、及びトリメチロールプロパン等の低分子量ポリオール、並びにこれらのアルキレンオキシド付加物等のポリオールと、アジピン酸、コハク酸、フタル酸、ヘキサヒドロフタル酸及びテレフタル酸等の二塩基酸又はその無水物等の酸成分とからの反応物等が挙げられる。又、各種デンドリマー型ポリオールと（メタ）アクリル酸との脱水縮合物が挙げられる。 As a polyester (meth) acrylate, the dehydration condensate of a polyester polyol and (meth) acrylic acid is mentioned. Polyester polyols include low molecular weight polyols such as ethylene glycol, polyethylene glycol, cyclohexane dimethylol, 3-methyl-1,5-pentanediol, propylene glycol, polypropylene glycol, 1,6-hexanediol, and trimethylolpropane, and Examples include reactants from polyols such as these alkylene oxide adducts and acid components such as dibasic acids such as adipic acid, succinic acid, phthalic acid, hexahydrophthalic acid and terephthalic acid, or anhydrides thereof. Moreover, the dehydration condensate of various dendrimer type polyols and (meth) acrylic acid is mentioned.
エポキシ（メタ）アクリレートとしては、ビスフェノールＡ型エポキシ樹脂の（メタ）アクリル酸付加物、水素添加ビスフェノールＡ型エポキシ樹脂の（メタ）アクリル酸付加物、フェノール又はクレゾールノボラック型エポキシ樹脂の（メタ）アクリル酸付加物、ビフェニル型エポキシ樹脂の（メタ）アクリル酸付加物、ポリテトラメチレングリコール等のポリエーテルのジグリシジルエーテルの（メタ）アクリル酸付加物、ポリブタジエンのジグリシジルエーテルの（メタ）アクリル酸付加物、ポリブタジエン内部エポキシ化物の（メタ）アクリル酸付加物、エポキシ基を有するシリコーン樹脂の（メタ）アクリル酸付加物、リモネンジオキサイドの（メタ）アクリル酸付加物、３，４−エポキシシクロヘキシルメチル−３，４−エポキシシクロヘキサンカルボキシレートの（メタ）アクリル酸付加物等が挙げられる。 As epoxy (meth) acrylate, (meth) acrylic acid adduct of bisphenol A type epoxy resin, (meth) acrylic acid adduct of hydrogenated bisphenol A type epoxy resin, (meth) acrylic of phenol or cresol novolac type epoxy resin Acid addition products, (meth) acrylic acid addition products of biphenyl type epoxy resins, (meth) acrylic acid addition products of diglycidyl ether of polyethers such as polytetramethylene glycol, (meth) acrylic acid addition of diglycidyl ether of polybutadiene Products, (meth) acrylic acid adducts of polybutadiene internal epoxidized products, (meth) acrylic acid adducts of silicone resins having epoxy groups, (meth) acrylic acid adducts of limonene dioxide, 3,4-epoxycyclohexylmethyl- 3,4-epoxy Cyclohexanecarboxylate (meth) acrylic acid adduct and the like.
ウレタン（メタ）アクリレートとしては、有機ポリイソシアネートとヒドロキシル基含有（メタ）アクリレートを付加反応させた化合物や、有機ポリイソシアネートとポリオールとヒドロキシル基含有（メタ）アクリレートを付加反応させた化合物が挙げられる。
ここで、ポリオールとしては、低分子量ポリオール、ポリエーテルポリオール、ポリエステルポリオール、ポリカーボネートポリオール等が挙げられる。
低分子量ポリオールとしては、エチレングリコール、プロピレングリコール、ネオペンチルグリコール、シクロヘキサンジメチロール、３−メチル−１，５−ペンタンジオール、及びグリセリン等が挙げられる。
ポリエーテルポリオールとしては、ポリプロピレングリコールやポリテトラメチレングリコール等が挙げられる。
ポリエステルポリオールとしては、これら低分子量ポリオール及び／又はポリエーテルポリオールと、アジピン酸、コハク酸、フタル酸、ヘキサヒドロフタル酸及びテレフタル酸等の二塩基酸又はその無水物等の酸成分との反応物が挙げられる。
有機ポリイソシアネートとしては、トリレンジイソシアネート、キシリレンジイソシアネート、テトラメチルキシリレンジイソシアネート、４，４’−ジフェニルメタンジイソシアネート、４，４’−ジシクロヘキシルメタンジイソシアネート、ヘキサメチレンジイソシアネート、及びイソホロンジイソシアネート等が挙げられる。
ヒドロキシル基含有（メタ）アクリレートとしては、２−ヒドロキシエチル（メタ）アクリレート、２−ヒドロキシプロピル（メタ）アクリレート、４−ヒドロキシブチル（メタ）アクリレート等のヒドロキシアルキル（メタ）アクリレートのヒドロキシル基含有（メタ）アクリレート等が挙げられる。
Examples of the urethane (meth) acrylate include compounds obtained by addition reaction of organic polyisocyanate and hydroxyl group-containing (meth) acrylate, and compounds obtained by addition reaction of organic polyisocyanate, polyol and hydroxyl group-containing (meth) acrylate.
Here, examples of the polyol include a low molecular weight polyol, a polyether polyol, a polyester polyol, and a polycarbonate polyol.
Examples of the low molecular weight polyol include ethylene glycol, propylene glycol, neopentyl glycol, cyclohexane dimethylol, 3-methyl-1,5-pentanediol, and glycerin.
Examples of the polyether polyol include polypropylene glycol and polytetramethylene glycol.
As the polyester polyol, a reaction product of these low molecular weight polyols and / or polyether polyols and an acid component such as adipic acid, succinic acid, phthalic acid, hexahydrophthalic acid and terephthalic acid, or a dibasic acid or its anhydride. Is mentioned.
Examples of the organic polyisocyanate include tolylene diisocyanate, xylylene diisocyanate, tetramethylxylylene diisocyanate, 4,4′-diphenylmethane diisocyanate, 4,4′-dicyclohexylmethane diisocyanate, hexamethylene diisocyanate, and isophorone diisocyanate.
As hydroxyl group-containing (meth) acrylate, hydroxyl group-containing (meta) of hydroxyalkyl (meth) acrylate such as 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, etc. ) Acrylate and the like.
本発明の組成物には、透明性を維持しながら硬化時のソリを低減させる目的等で、有機ポリマーを配合することもできる。好適なポリマーとしては、（メタ）アクリル系ポリマーが挙げられ、好適な構成モノマーとしては、メチル（メタ）アクリレート、シクロヘキシル（メタ）アクリレート、（メタ）アクリル酸、グリシジル（メタ）アクリレート、Ｎ−（２−（メタ）アクリロキシエチル）テトラヒドロフタルイミド等が挙げられる。（メタ）アクリル酸を共重合したポリマーの場合、グリシジル（メタ）アクリレートを付加させて（メタ）アクリロイル基をポリマー鎖に導入しても良い。 An organic polymer can also be blended with the composition of the present invention for the purpose of reducing warping during curing while maintaining transparency. Suitable polymers include (meth) acrylic polymers, and suitable constituent monomers include methyl (meth) acrylate, cyclohexyl (meth) acrylate, (meth) acrylic acid, glycidyl (meth) acrylate, N- ( 2- (meth) acryloxyethyl) tetrahydrophthalimide and the like. In the case of a polymer copolymerized with (meth) acrylic acid, glycidyl (meth) acrylate may be added to introduce a (meth) acryloyl group into the polymer chain.
７．塗装方法
本発明の組成物が適用できる基材としては、種々の材料に適用でき、木材、金属、無機材料及びプラスチック等が挙げられる。
無機材料としては、モルタル、コンクリート及びガラス等が挙げられる。
プラスチックの具体例としては、ポリメチルメタクリレート、ポリエチレンテレフタレート、ポリ塩化ビニル、ポリカーボネート樹脂、エポキシ樹脂及びポリウレタン樹脂等が挙げられる。
7). Coating method The substrate to which the composition of the present invention can be applied is applicable to various materials, and examples thereof include wood, metal, inorganic materials, and plastics.
Examples of the inorganic material include mortar, concrete, and glass.
Specific examples of the plastic include polymethyl methacrylate, polyethylene terephthalate, polyvinyl chloride, polycarbonate resin, epoxy resin, and polyurethane resin.
本発明の組成物の塗装方法としては、常法に従えば良い。
具体的には、組成物を基材に塗布した後乾燥し、紫外線等の光を照射する方法等が挙げられる。
本発明の組成物の基材への塗布方法としては、常法に従えば良く、バーコート、ロールコート、スピンコート、ディップコート、グラビアコート、フローコート及びスプレーコート等が挙げられる。
What is necessary is just to follow a conventional method as a coating method of the composition of this invention.
Specifically, a method of applying the composition to a substrate, drying it, and irradiating it with light such as ultraviolet rays can be mentioned.
As a method for applying the composition of the present invention to the substrate, conventional methods may be used, and examples thereof include bar coating, roll coating, spin coating, dip coating, gravure coating, flow coating, and spray coating.
基材に対する組成物の塗装方法及び乾燥後の膜厚は、目的に応じて適宜設定すれば良い。
乾燥温度は、適用する基材が変形等の問題を生じない温度以下であれば特に限定されるものではない。
What is necessary is just to set the coating method of the composition with respect to a base material, and the film thickness after drying suitably according to the objective.
The drying temperature is not particularly limited as long as the applied substrate is at a temperature that does not cause a problem such as deformation.
本発明の組成物を硬化させるための光としては、紫外線及び可視光線が挙げられるが、紫外線が特に好ましい。
紫外線照射装置としては、高圧水銀ランプ、メタルハライドランプ、ＵＶ無電極ランプ、ＬＥＤ等が挙げられる。
照射エネルギーは、活性エネルギー線の種類や配合組成に応じて適宜設定すべきものであるが、一例として高圧水銀ランプを使用する場合を挙げると、ＵＶ−Ａ領域の照射エネルギーで１００〜５，０００ｍＪ／ｃｍ2が好ましく、２００〜１，０００ｍＪ／ｃｍ2がより好ましい。
Examples of light for curing the composition of the present invention include ultraviolet rays and visible rays, and ultraviolet rays are particularly preferable.
Examples of the ultraviolet irradiation device include a high-pressure mercury lamp, a metal halide lamp, a UV electrodeless lamp, and an LED.
The irradiation energy should be appropriately set according to the type and composition of the active energy ray. As an example, when a high-pressure mercury lamp is used, the irradiation energy in the UV-A region is 100 to 5,000 mJ / cm 2 is preferable, and 200 to 1,000 mJ / cm 2 is more preferable.
本発明の組成物の硬化膜は、耐磨耗性及び耐擦傷性に優れるものであり、本発明の組成物の硬化膜を有する材料は、この特性を生かして種々の用途に使用することができる。
例えば、表示板用前面板、建材用途、照明器具、携帯電話のディスプレイや筐体、家電製品の筐体、眼鏡等の各種レンズが挙げられる。
表示板用前面板の具体例としては、電光掲示板、ディスプレイ、看板、広告及び標識等が挙げられる。
基材として木材使用した例としては、階段、床及び家具等の木工製品が挙げられる。基材として金属を使用した例としては、台所用キッチンパネル及びステンレスシンク等の金属製品等が挙げられる。
The cured film of the composition of the present invention is excellent in wear resistance and scratch resistance, and the material having the cured film of the composition of the present invention can be used for various applications by taking advantage of this property. it can.
For example, various lenses such as a front plate for a display panel, a building material application, a lighting fixture, a display and a casing of a mobile phone, a casing of a household electric appliance, and glasses.
Specific examples of the front plate for the display board include an electric bulletin board, a display, a signboard, an advertisement, and a sign.
Examples of using wood as a base material include woodwork products such as stairs, floors and furniture. Examples of using metal as the substrate include metal products such as kitchen panels for kitchens and stainless steel sinks.
以下に、実施例及び比較例を示し、本発明をより具体的に説明する。尚、本発明は、これらの実施例によって限定されるものではない。
又、以下において「部」とは重量部を意味し、「％」とは重量％を意味する。
Hereinafter, the present invention will be described in more detail with reference to Examples and Comparative Examples. In addition, this invention is not limited by these Examples.
In the following, “part” means part by weight, and “%” means% by weight.
○製造例１〔（Ａ）成分の製造（ＨＤＩ−Ｍ３０５）〕
攪拌装置及び空気の吹き込み管を備えた０．５Ｌセパラブルフラスコに、ペンタエリスリトールトリアクリレート（ＰＥＴｒｉ）とペンタエリスリトールテトラアクリレート（ＰＥＴｅｔ）の混合物(東亞合成（株）製アロニックスＭ−３０５。以下、「Ｍ−３０５」という。〕１５９．２ｇ（ＰＥＴｒｉ０．３モルとＰＥＴｅｔ０．２モル含有）、２，６−ジ−ｔｅｒｔ−ブチル−４−メチルフェノール（以下、「ＢＨＴ」という）０．０９２ｇ、ジブチルスズジラウレート（以下、「ＤＢＴＬ」という）０．０５５ｇを仕込み、液温を７０〜７５℃で攪拌しながら、ヘキサメチレンジイソシアネート（以下、「ＨＤＩ」という）２５．２ｇ（０．１５モル）を滴下した。
滴下終了後、８０℃で３時間攪拌し、反応生成物のＩＲ（赤外吸収）分析でイソシアネート基が消失していることを確認して反応を終了した。以下、この反応生成物をＨＤＩ−Ｍ３０５と呼ぶ。
○ Production Example 1 [Production of component (A) (HDI-M305)]
In a 0.5 L separable flask equipped with a stirrer and an air blowing tube, a mixture of pentaerythritol triacrylate (PETri) and pentaerythritol tetraacrylate (PETet) (Aronix M-305 manufactured by Toagosei Co., Ltd., hereinafter “ M9.2 ”] 159.2 g (containing 0.3 mol of PETri and 0.2 mol of PETet), 0.092 g of 2,6-di-tert-butyl-4-methylphenol (hereinafter referred to as“ BHT ”), dibutyltin 0.055 g of dilaurate (hereinafter referred to as “DBTL”) was charged, and 25.2 g (0.15 mol) of hexamethylene diisocyanate (hereinafter referred to as “HDI”) was added dropwise while stirring at a liquid temperature of 70 to 75 ° C. .
After completion of dropping, the mixture was stirred at 80 ° C. for 3 hours, and the reaction was completed after confirming that the isocyanate group had disappeared by IR (infrared absorption) analysis of the reaction product. Hereinafter, this reaction product is referred to as HDI-M305.
ＨＤＩ−Ｍ３０５は、ＰＥＴｒｉとＨＤＩのウレタンアダクト化合物（ａ１）とＰＥＴｅｔ（ａ２）を含み、（ａ１）と（ａ２）の重量比が（ａ１）：（ａ２）＝６：４で含有する混合物である。 HDI-M305 is a mixture containing a urethane adduct compound (a1) of PETri and HDI and PETet (a2), wherein the weight ratio of (a1) and (a2) is (a1) :( a2) = 6: 4. is there.
○製造例２〔（Ａ）成分の製造（ＩＰＤＩ−Ｍ４５１）〕
製造例１と同様のフラスコに、ＰＥＴｒｉとＰＥＴｅｔの混合物〔東亞合成（株）製アロニックスＭ−４５１。以下、「Ｍ−４５１」という。〕の２４８．１ｇ（ＰＥＴｒｉを０．３モルとＰＥＴｅｔ０．４５モル含有）、ＢＨＴの０．１４１ｇ、ＤＢＴＬの０．０８４ｇを仕込み、液温を７０〜７５℃で攪拌しながら、イソホロンジイソシアネート（以下、「ＩＰＤＩ」という）３３．３ｇ（０．１５モル）を滴下した。
滴下終了後、８０℃で３時間攪拌し、反応生成物のＩＲ（赤外吸収）分析でイソシアネート基が消失していることを確認して反応を終了した。以下、この反応生成物をＩＰＤＩ−Ｍ４５１と呼ぶ。
○ Production Example 2 [Production of Component (A) (IPDI-M451)]
In a flask similar to Production Example 1, a mixture of PETri and PETet [Aronix M-451 manufactured by Toagosei Co., Ltd. Hereinafter, it is referred to as “M-451”. ], 248.1 g (containing 0.3 mol of PETri and 0.45 mol of PETet), 0.141 g of BHT, and 0.084 g of DBTL, while stirring at a liquid temperature of 70 to 75 ° C. 33.3 g (0.15 mol) was added dropwise.
After completion of dropping, the mixture was stirred at 80 ° C. for 3 hours, and the reaction was completed after confirming that the isocyanate group had disappeared by IR (infrared absorption) analysis of the reaction product. Hereinafter, this reaction product is referred to as IPDI-M451.
ＩＰＤＩ−Ｍ４５１は、ＰＥＴｒｉとＩＰＤＩのウレタンアダクト化合物（ａ１）とＰＥＴｅｔ（ａ２）を含み、（ａ１）と（ａ２）の重量比が（ａ１）：（ａ２）＝４：６で含有する混合物である。 IPDI-M451 is a mixture containing urethane adduct compound (a1) and PETet (a2) of PETri and IPDI, and the weight ratio of (a1) and (a2) is (a1) :( a2) = 4: 6. is there.
○製造例３〔（Ｂ）成分の製造（Ｍａｃ−ＴＱ）〕
攪拌機及び温度計を備えた反応器に、アルコール交換反応用の１−プロパノール１５０ｇとテトラメトキシシラン（以下、「ＴＭＯＳ」という）３６．５３ｇ（０．２４モル）とを仕込んだ後、これらを撹拌しながら、２５質量％水酸化テトラメチルアンモニウムメタノール溶液４．３７ｇ（メタノール０．１モル、水酸化テトラメチルアンモニウム１２ミリモル）を徐々に加えて、温度２５℃、ｐＨ９で６時間反応させた。その後、内温を６０℃にして攪拌しながら更に１時間反応させた。ここで、反応液をガスクロマトグラフ分析（ＴＣＤ検出器）したところ、ＴＭＯＳのメトキシ基がｎ−プロポキシ基に置換された化合物（１置換体から４置換体）及び未反応のＴＭＯＳが検出された。ＴＭＯＳは痕跡量しか検出されなかった。これらのうちのｎ−プロポキシ基含有化合物の割合は、合計でほぼ１００％であった。ガスクロマトグラムにおける生成物のピーク面積に基づいて、１−プロパノールの置換数（ｎ−プロポキシ基含有化合物１分子あたりのｎ−プロポキシ基の数の平均）を求めたところ、２．７であった。
次に、上記反応液に、３−メタクリロキシプロピルトリメトキシシラン５９．６２ｇ（０．２４モル）を加え、さらに水３０．２ｇを加えた。そして、２５％水酸化テトラメチルアンモニウムメタノール溶液７．８８ｇ（メタノール０．１８モル、水酸化テトラメチルアンモニウム２１．６ミリモル）を加えて、撹拌しながら、温度２５℃、ｐＨ９で２４時間反応させた。その後、１０質量％硝酸水溶液２２．２ｇ（３５．３ミリモル）加えて中和した。次いで、この中和液を、ジイソプロピルエーテル１２０ｇ及び水１８０ｇの混合液の中に加えて抽出を行った。このジイソプロピルエーテル層を水洗することで塩類や過剰の酸を除去し、その後、重合禁止剤としてＮ−ニトロソフェニルヒドロキシルアミシアルミニウム塩〔商品名「Ｑ−１３０１」、和光純薬工業（株）製。〕を１１．５ｍｇ加えた。得られたジイソプロピルエーテル溶液から、減圧下で有機溶剤を留去し、無色透明な固体の有機ケイ素化合物（Ｂ１）を得た。その収量は５７．７２ｇであった。以後、こうして得られる収量を「単離収量」と呼ぶ。
○ Production Example 3 [Production of Component (B) (Mac-TQ)]
A reactor equipped with a stirrer and a thermometer was charged with 150 g of 1-propanol for alcohol exchange reaction and 36.53 g (0.24 mol) of tetramethoxysilane (hereinafter referred to as “TMOS”), and then stirred. Then, 4.37 g of a 25 mass% tetramethylammonium hydroxide methanol solution (0.1 mol of methanol, 12 mmol of tetramethylammonium hydroxide) was gradually added and reacted at a temperature of 25 ° C. and pH 9 for 6 hours. Thereafter, the internal temperature was set to 60 ° C., and the reaction was further continued for 1 hour with stirring. Here, when the reaction solution was subjected to gas chromatographic analysis (TCD detector), a compound in which the methoxy group of TMOS was substituted with an n-propoxy group (1 to 4 substitutes) and unreacted TMOS were detected. Only trace amounts of TMOS were detected. Among these, the ratio of the n-propoxy group-containing compound was almost 100% in total. Based on the peak area of the product in the gas chromatogram, the number of 1-propanol substitutions (average of the number of n-propoxy groups per molecule of n-propoxy group-containing compound) was determined to be 2.7.
Next, 59.62 g (0.24 mol) of 3-methacryloxypropyltrimethoxysilane was added to the reaction solution, and 30.2 g of water was further added. Then, 7.88 g of a 25% tetramethylammonium hydroxide methanol solution (0.18 mol of methanol, 21.6 mmol of tetramethylammonium hydroxide) was added and reacted for 24 hours at a temperature of 25 ° C. and a pH of 9 while stirring. . Thereafter, the mixture was neutralized by adding 22.2 g (35.3 mmol) of a 10% by mass nitric acid aqueous solution. Next, this neutralized solution was added to a mixed solution of 120 g of diisopropyl ether and 180 g of water for extraction. The diisopropyl ether layer is washed with water to remove salts and excess acid, and then N-nitrosophenylhydroxylami aluminum salt [trade name “Q-1301”, manufactured by Wako Pure Chemical Industries, Ltd.] as a polymerization inhibitor. . 11.5 mg was added. From the obtained diisopropyl ether solution, the organic solvent was distilled off under reduced pressure to obtain a colorless and transparent solid organosilicon compound (B1). The yield was 57.72g. Hereinafter, the yield thus obtained is referred to as “isolated yield”.
有機ケイ素化合物（Ｂ１）を1Ｈ−ＮＭＲ分析し、得られた有機ケイ素化合物（Ｂ１）は、化合物（ｂ１）及び化合物（ｂ２）が化学量論的に反応して得られた共重縮合物であることが確認された。
有機ケイ素化合物（Ｂ１）の1Ｈ−ＮＭＲチャートから算出したアルコキシ基（ケイ素原子に結合したｎ−プロポキシ基）の含有割合は、仕込み原料に含まれていたアルコキシ基の全体に対して２．５％に相当する量であった。
又、Ｍｎは９，６００であった。
以下、この反応生成物をＭａｃ−ＴＱと呼ぶ。
The organosilicon compound (B1) was analyzed by 1 H-NMR, and the resulting organosilicon compound (B1) was a copolycondensate obtained by reacting the compound (b1) and the compound (b2) stoichiometrically. It was confirmed that.
The content ratio of the alkoxy group (n-propoxy group bonded to the silicon atom) calculated from the 1 H-NMR chart of the organosilicon compound (B1) is 2.5 with respect to the entire alkoxy group contained in the raw material. %.
Moreover, Mn was 9,600.
Hereinafter, this reaction product is referred to as Mac-TQ.
（実施例１〜実施例４）
表１に示す成分を常法に従い攪拌・混合し、光硬化型塗料組成物を製造した。
尚、表１の数値は、重量部数を表す。又、表中の略称は、以下の化合物を表す。
(Example 1 to Example 4)
The components shown in Table 1 were stirred and mixed according to a conventional method to produce a photocurable coating composition.
In addition, the numerical value of Table 1 represents a weight part number. Abbreviations in the table represent the following compounds.
○略称
（Ｃ）成分
・Ｉｒｇ−１８４：チバ・ジャパン（株）製光ラジカル重合開始剤、商品名イルガキュア１８４；１−ヒドロキシ−シクロヘキシル−フェニル−ケトン。
（Ｄ）成分
・ＰＧＭ：プロピレングリコールモノメチルエーテル。
○ Abbreviation
Component (C) Irg-184: Photo radical polymerization initiator manufactured by Ciba Japan, trade name Irgacure 184; 1-hydroxy-cyclohexyl-phenyl-ketone.
(D) Component PGM: Propylene glycol monomethyl ether.
（比較例１〜比較例５）
表２に示す成分を常法に従い攪拌・混合し、光硬化型塗料組成物を製造した。
尚、表２の数値は、重量部数を表す。又、表中の略称は、以下の化合物を表す。
(Comparative Examples 1 to 5)
The components shown in Table 2 were stirred and mixed according to a conventional method to produce a photocurable coating composition.
In addition, the numerical value of Table 2 represents a weight part number. Abbreviations in the table represent the following compounds.
○略称
（Ｂ）'成分
・ＰＧＭ−ＳＴ：日産化学工業(株)製ＰＧＭ−ＳＴ、プロピレングリコールモノメチルエーテル分散コロイダルシリカ（シリカ濃度３０％）。
○ Abbreviation
(B) ′ component PGM-ST: PGM-ST manufactured by Nissan Chemical Industries, Ltd., propylene glycol monomethyl ether dispersed colloidal silica (silica concentration 30%).
表１及び表２に示す組成物を、１０ｃｍ四方のポリメチルメタクリレート樹脂板に、乾燥後の塗膜厚さが約１０μｍとなるようにバーコータで塗布し、７０℃の熱風乾燥機で１０分間乾燥した後、すぐに紫外線照射を行って硬化膜を作成した。
紫外線照射は、アイグラフィックス（株）製紫外線照射機（高圧水銀ランプ）を使用し、ランプ高さを２４ｃｍ、コンベア速度８．８ｍ／分で３パス照射した。１パス当りの照射エネルギーは、ＥＩＴ社製のＵＶ ＰＯＷＥＲ ＰＵＣＫのＵＶ−Ａ領域で、２００ｍＪ／ｃｍ2であった（合計６００ｍＪ／ｃｍ2）。又、ピーク照度はＵＶ−Ａ領域で２２０ｍＷ／ｃｍ2であった。
得られた硬化膜について、耐磨耗性、耐擦傷性、密着性及び透明性を、以下に示す方法で評価した。それらの評価結果を表４に示す。
The composition shown in Table 1 and Table 2 was applied to a 10 cm square polymethyl methacrylate resin plate with a bar coater so that the coating thickness after drying was about 10 μm, and dried for 10 minutes with a hot air dryer at 70 ° C. After that, ultraviolet rays were irradiated immediately to form a cured film.
For ultraviolet irradiation, an ultraviolet ray irradiator (high pressure mercury lamp) manufactured by Eye Graphics Co., Ltd. was used, and the lamp height was 24 cm and the conveyor speed was 8.8 m / min. The irradiation energy per pass was 200 mJ / cm 2 in the UV-A region of UV POWER PUCK manufactured by EIT (total 600 mJ / cm 2 ). The peak illuminance was 220 mW / cm 2 in the UV-A region.
About the obtained cured film, abrasion resistance, abrasion resistance, adhesiveness, and transparency were evaluated by the method shown below. The evaluation results are shown in Table 4.
○耐磨耗性
耐磨耗性は、テーバー式磨耗試験機を使用し、テーバー磨耗試験前後のヘイズの差ΔＨ（％）を測定して評価した。ここで、磨耗輪はＣＳ−１０Ｆ、荷重は各５００ｇ、回転数は３００回とした。ΔＨ（％）が小さいものほど耐磨耗性良好と評価した。
Abrasion resistance Abrasion resistance was evaluated by measuring a haze difference ΔH (%) before and after the Taber abrasion test using a Taber abrasion tester. Here, the wear wheel was CS-10F, the load was 500 g, and the rotation speed was 300 times. The smaller the ΔH (%), the better the wear resistance.
○耐擦傷性
耐擦傷性は、日本スチールウール(株)製ボンスター＃００００に５００ｇ荷重をかけ５０往復擦ったときのキズの本数に基づき下記表３の基準で判定した。評価Ｂ以上を耐擦傷性良好とした。
Scratch resistance Scratch resistance was determined according to the criteria shown in Table 3 below based on the number of scratches when a 500 g load was applied to Nippon Steel Wool Co., Ltd. Bonstar # 0000 and rubbed 50 times. The evaluation B or higher was regarded as good scratch resistance.
○密着性
硬化塗膜にカッターナイフで縦横各１１本の１ｍｍ間隔の切り込みを入れて１００枡の碁盤目を形成し、この碁盤目上にニチバン(株)製＃４０５のセロハンテープを貼り付け、ＪＩＳ Ｋ５４００に準じてセロハンテープを剥離した。セロハンテープ剥離後の残存膜の割合（％）が１００％のものを密着性良好と評価した。
○ Adhesion Cut the cured coating film with a 1mm interval of 11mm each in length and width with a cutter knife to form a 100mm grid, and paste Nichiban Co., Ltd. # 405 cellophane tape on this grid. The cellophane tape was peeled off according to JIS K5400. A film with a residual film ratio (%) of 100% after peeling of the cellophane tape was evaluated as having good adhesion.
○透明性
硬化膜のヘイズ（％）はＪＩＳ Ｋ７１３６に準拠、全光線透過率（％）はＪＩＳ Ｋ７３６１に準拠して濁度計ＮＤＨ−２０００（日本電色工業製）を用いて測定し、ヘイズ＜１、全光線透過率＞９０を透明性良好とした。
○ Transparency The haze (%) of the cured film is measured according to JIS K7136, and the total light transmittance (%) is measured using a turbidimeter NDH-2000 (manufactured by Nippon Denshoku Industries Co., Ltd.) according to JIS K7361. <1, Total light transmittance> 90 was defined as good transparency.
実施例１〜同４の組成物は、密着性、耐磨耗性、耐擦傷性及び透明性のいずれにも優れるものであった。
これに対して、（Ａ）成分及び（Ｂ）成分を含むが、（Ａ）成分を本発明の下限４０％に満たない１０％で含み、（Ｂ）成分の上限６０％を超過する９０％で含む比較例１の組成物は、透明性は問題ないものの、密着性、耐磨耗性及び耐擦傷性が不十分なものとなった。コロイダルシリカを含有するが（Ｂ）成分を含まない比較例２の組成物は、密着性及び耐磨耗性は問題ないものの、耐擦傷性及び透明性が不十分なものとなった。（Ａ）成分を含まない比較例３の組成物は、耐擦傷性及び透明性は問題ないものの、密着性がやや不十分なものとなり、耐磨耗性が不十分なものとなった。（Ｂ）成分を含まない比較例４及び同５の組成物は、密着性、耐擦傷性及び透明性は問題ないものの、耐磨耗性が不十分なものとなった。
The compositions of Examples 1 to 4 were excellent in all of adhesion, abrasion resistance, scratch resistance and transparency.
On the other hand, the component (A) and the component (B) are included, but the component (A) is included in 10% which is less than the lower limit of 40% of the present invention, and 90% exceeding the upper limit 60% of the component (B). Although the composition of Comparative Example 1 contained in the above has no problem with transparency, adhesion, abrasion resistance and scratch resistance are insufficient. Although the composition of Comparative Example 2 containing colloidal silica but no component (B) had no problems with adhesion and abrasion resistance, it had insufficient scratch resistance and transparency. Although the composition of Comparative Example 3 containing no component (A) had no problem with scratch resistance and transparency, the adhesion was slightly insufficient and the wear resistance was insufficient. The compositions of Comparative Examples 4 and 5 that did not contain the component (B) had insufficient wear resistance, although there were no problems with adhesion, scratch resistance and transparency.
本発明の光硬化型塗料組成物は、木材、金属、無機材料及びプラスチック等の種々の基材の塗装に好適に使用することができる。 The photocurable coating composition of the present invention can be suitably used for coating various substrates such as wood, metal, inorganic material and plastic.
Claims (4)
（Ａ）成分を９７〜４０重量部、
（Ｂ）成分を３〜６０重量部、
光重合開始剤（Ｃ）を０．１〜１０重量部及び
有機溶剤（Ｄ）を１０〜１０００重量部
含有する光硬化型塗料組成物。
（Ａ）成分：３価以上の脂肪族多価アルコールから誘導される（メタ）アクリレートであって、（メタ）アクリロイル基を２個以上有し、水酸基を１個以上有する（メタ）アクリレートとポリイソシアネートとの付加反応で得られるウレタンアダクト化合物（ａ１）及び３価以上の脂肪族多価アルコールから誘導される（メタ）アクリレートであって、（メタ）アクリロイル基を３個以上有し、水酸基を有さない（メタ）アクリレート（ａ２）から構成される(メタ)アクリレート混合物。
（Ｂ）成分：下記一般式（１）で表される（メタ）アクリロイル基含有ケイ素化合物（ｂ１）と、下記一般式（２）で表されるケイ素化合物（ｂ２）とを、上記ケイ素化合物（ｂ１）１モルに対して、上記ケイ素化合物（ｂ２）０．３〜１．８モルの割合で、アルカリ性条件下で加水分解共重縮合させて得られる有機ケイ素化合物。
ＳｉＹ4 （２）
（一般式（２）において、Ｙはシロキサン結合生成基であり、Ｙは同一であっても異なっていても良い。） For a total of 100 parts by weight of the following component (A) and component (B) below,
97 to 40 parts by weight of component (A)
(B) 3-60 parts by weight of component,
A photocurable coating composition containing 0.1 to 10 parts by weight of a photopolymerization initiator (C) and 10 to 1000 parts by weight of an organic solvent (D).
Component (A): a (meth) acrylate derived from a trihydric or higher aliphatic polyhydric alcohol, comprising (meth) acrylate having at least two (meth) acryloyl groups and at least one hydroxyl group, and poly A (meth) acrylate derived from an urethane adduct compound (a1) obtained by an addition reaction with an isocyanate and a trihydric or higher aliphatic polyhydric alcohol, having 3 or more (meth) acryloyl groups, and having a hydroxyl group (Meth) acrylate mixture composed of (meth) acrylate (a2) not present.
Component (B): The (meth) acryloyl group-containing silicon compound (b1) represented by the following general formula (1) and the silicon compound (b2) represented by the following general formula (2) are combined with the above silicon compound ( b1) An organosilicon compound obtained by hydrolytic copolycondensation under alkaline conditions at a ratio of 0.3 to 1.8 mol of the silicon compound (b2) with respect to 1 mol.
SiY 4 (2)
(In general formula (2), Y is a siloxane bond-forming group, and Y may be the same or different.)
化合物（ｂ２）は、一般式（２）におけるＹがアルコキシ基である請求項１〜請求項３のいずれかに記載の光硬化型塗料組成物。 In the component (B), the compound (b1) is a compound in which X in the general formula (1) is an alkoxy group and n is 0.
The photocurable coating composition according to any one of claims 1 to 3, wherein in the compound (b2), Y in the general formula (2) is an alkoxy group.