JP5513177B2 - Humidity indicator and method for producing the same, and paint for humidity indicator used in the production method - Google Patents
Humidity indicator and method for producing the same, and paint for humidity indicator used in the production method Download PDFInfo
- Publication number
- JP5513177B2 JP5513177B2 JP2010050189A JP2010050189A JP5513177B2 JP 5513177 B2 JP5513177 B2 JP 5513177B2 JP 2010050189 A JP2010050189 A JP 2010050189A JP 2010050189 A JP2010050189 A JP 2010050189A JP 5513177 B2 JP5513177 B2 JP 5513177B2
- Authority
- JP
- Japan
- Prior art keywords
- humidity indicator
- humidity
- complex
- paint
- carrier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、変色により湿度の上昇を容易に視認しうる湿度インジケータとその製造方法、該湿度インジケータの製造に用いる湿度インジケータ用塗料に関する。 The present invention relates to a humidity indicator that can easily recognize an increase in humidity due to discoloration, a method for manufacturing the humidity indicator, and a humidity indicator paint used for manufacturing the humidity indicator.
従来より、商品包装に封入される乾燥剤として、シリカゲル入りの小袋が用いられており、この小袋内には、乾燥状態を把握するためのインジケータとして、青ゲルと呼ばれる塩化コバルト含浸シリカゲルが混入されていた。しかし、コバルトは重金属であるため、環境上、コバルトを含有しない湿度インジケータが望まれている。 Conventionally, a sachet containing silica gel has been used as a desiccant enclosed in product packaging, and cobalt chloride impregnated silica gel called blue gel is mixed in the sachet as an indicator for grasping the dry state. It was. However, since cobalt is a heavy metal, environmentally, a humidity indicator that does not contain cobalt is desired.
特許文献１には、電子供与性呈色化合物と、常温において固体である酸性化合物と、潮解物質と、水系樹脂エマルジョン又は水溶性高分子化合物とからなる湿度インジケータ用塗料を不織布等の担持体に付着させ、加熱乾燥させてなる湿度インジケータが開示されている。係る湿度インジケータは、重金属であるコバルトを含まず、微量の湿度にも鋭敏に反応して変色することから、湿度に対して厳重な管理が要求される電子部品の包装体に好ましく用いられる。 In Patent Document 1, a humidity indicator paint comprising an electron-donating color compound, an acidic compound that is solid at room temperature, a deliquescent material, and a water-based resin emulsion or a water-soluble polymer compound is applied to a carrier such as a nonwoven fabric. A humidity indicator is disclosed which is deposited and heat dried. Such a humidity indicator does not contain cobalt, which is a heavy metal, and is sensitive to a very small amount of humidity and discolors. Therefore, the humidity indicator is preferably used for a package of electronic parts that require strict management against humidity.
上記したように、電子部品の包装体には信頼性の高い湿度インジケータが要求されるが、包装体によって検知すべき湿度のレベルが異なり、使用者の要求に応じて検知湿度を任意のレベルに容易に調整しうる湿度インジケータが望まれている。 As described above, a highly reliable humidity indicator is required for a package of electronic components, but the level of humidity to be detected differs depending on the package, and the detected humidity can be set to an arbitrary level according to the user's request. A humidity indicator that can be easily adjusted is desired.
本発明の課題は、所望の検知湿度を検知しうる湿度インジケータを提供することにあり、特に、相対湿度３０〜６０％ＲＨにおいて検知湿度を所望のレベルに容易に調整しうる湿度インジケータを提供することにある。 An object of the present invention is to provide a humidity indicator that can detect a desired detection humidity, and in particular, to provide a humidity indicator that can easily adjust the detection humidity to a desired level at a relative humidity of 30 to 60% RH. There is.
本発明の第１は、少なくとも、電子供与性呈色化合物と、常温において固体である酸性化合物と、潮解物質と、水溶性の高級脂肪酸の錯塩またはアミノ酸の錯塩と、水系樹脂エマルジョンとからなり、前記高級脂肪酸の錯塩またはアミノ酸の錯塩の２０℃の水１００ｇに対する溶解度が３ｇ〜２００ｇであることを特徴とする湿度インジケータ用塗料である。 The first of the present invention comprises at least an electron donative coloration compound, an acidic compound which is solid at ordinary temperature, and deliquescent substance, and complex salts of complex or amino acid water-soluble higher fatty acid, Ri Do from an aqueous resin emulsion The humidity indicator paint , wherein the complex salt of the higher fatty acid or the complex salt of the amino acid has a solubility in 100 g of water at 20 ° C. of 3 g to 200 g .
本発明の第２は、担持体と、該担持体に担持された呈色組成物からなる湿度インジケータの製造方法であって、上記本発明の湿度インジケータ用塗料を担持体に付着させ、加熱乾燥させて呈色組成物を形成することを特徴とする湿度インジケータの製造方法である。 A second aspect of the present invention is a method for producing a humidity indicator comprising a carrier and a color composition carried on the carrier, and the humidity indicator paint of the present invention is adhered to the carrier, followed by drying by heating. It is made to form a color composition, It is a manufacturing method of the humidity indicator characterized by the above-mentioned.
本発明の第３は、担持体と、該担持体に担持された呈色組成物からなる湿度インジケータであって、該呈色組成物が、少なくとも、電子供与性呈色化合物と、常温において固体である酸性化合物と、潮解物質と、水溶性の高級脂肪酸の錯塩またはアミノ酸の錯塩と、樹脂バインダーからなり、前記高級脂肪酸の錯塩またはアミノ酸の錯塩の２０℃の水１００ｇに対する溶解度が３ｇ〜２００ｇであることを特徴とする湿度インジケータである。 A third aspect of the present invention is a humidity indicator comprising a support and a color composition supported on the support, the color composition comprising at least an electron-donating color compound and a solid at room temperature. an acidic compound is a deliquescent substance, and complex salts of complex or amino acid water-soluble higher fatty acid, Ri Do a resin binder, solubility 20 ° C. water 100g of complex salts of complex salts or acids of the higher fatty acid 3g~200g It is a humidity indicator characterized by being.
本発明によれば、水溶性の高級脂肪酸の錯塩またはアミノ酸の錯塩を用いることで、所望の湿度レベルを良好に検知しうる湿度インジケータを提供することができる。本発明においては、特に３０〜６０％ＲＨの範囲において所望の検知湿度に容易に調整することができ、本発明の湿度インジケータを内包することで、電子部品などの包装体において、より厳格な湿度管理を行うことができる。また、本発明の湿度インジケータは、検知湿度のレベルを容易に調整できることから、検知湿度が変更になった場合にも、大幅な設計変更をすることなく迅速に対応することができ、多種類の湿度インジケータの製造に好適に用いられる。 ADVANTAGE OF THE INVENTION According to this invention, the humidity indicator which can detect a desired humidity level favorably can be provided by using the complex salt of a water-soluble higher fatty acid or the complex salt of an amino acid. In the present invention, it can be easily adjusted to a desired detected humidity, particularly in the range of 30 to 60% RH, and by including the humidity indicator of the present invention, more stringent humidity can be obtained in a packaging body such as an electronic component. Management can be performed. In addition, since the humidity indicator of the present invention can easily adjust the level of the detected humidity, it can quickly respond to any change in the detected humidity without any significant design changes. It is suitably used for manufacturing a humidity indicator.
本発明の湿度インジケータは、担持体と、該担持体に担持された呈色組成物からなり、該呈色組成物は、少なくとも、電子供与性呈色化合物と、常温において固体である酸性化合物と、潮解物質と、水溶性の高級脂肪酸の錯塩またはアミノ酸の錯塩と、樹脂バインダーからなり、本発明の湿度インジケータ用塗料を担持体に付着させ、加熱乾燥することにより得られる。 The humidity indicator of the present invention comprises a carrier and a color composition carried on the carrier, and the color composition comprises at least an electron-donating color compound and an acidic compound that is solid at room temperature. It consists of a deliquescent substance, a water-soluble higher fatty acid complex salt or an amino acid complex salt, and a resin binder. The humidity indicator paint of the present invention is attached to a carrier and dried by heating.
本発明の湿度インジケータ用塗料は、少なくとも、電子供与性呈色化合物と、常温において固体である酸性化合物と、潮解物質と、水溶性の高級脂肪酸の錯塩またはアミノ酸の錯塩と、水系樹脂エマルジョンとからなる。即ち、本発明の湿度インジケータの呈色組成物中の樹脂バインダーは、水系樹脂エマルジョンの樹脂成分に由来する。 The humidity indicator paint of the present invention comprises at least an electron-donating color compound, an acidic compound that is solid at room temperature, a deliquescent material, a complex salt of a water-soluble higher fatty acid or an amino acid, and an aqueous resin emulsion. Become. That is, the resin binder in the coloring composition of the humidity indicator of the present invention is derived from the resin component of the aqueous resin emulsion.
本発明に用いられる担持体としては、紙や樹脂フィルム、布、不織布など水性塗料を付着させて加熱乾燥させることにより、該担持体の表面や内部に該塗料の成分を含む呈色組成物を担持させ得るものであればいかなる素材も用いることができる。樹脂フィルムとしては、ポリエチレンテレフタレート（ＰＥＴ）やポリプロピレン（ＰＰ）、ポリエチレン（ＰＥ）などのフィルム、或いはシートが好ましく用いられる。好ましくは、印刷に適したＰＥＴフィルムである。 As the carrier used in the present invention, a color composition containing the components of the paint on the surface or inside of the carrier is prepared by attaching a water-based paint such as paper, resin film, cloth, nonwoven fabric, etc. and drying it by heating. Any material that can be supported can be used. As the resin film, a film or sheet of polyethylene terephthalate (PET), polypropylene (PP), polyethylene (PE) or the like is preferably used. Preferably, it is a PET film suitable for printing.
電子供与性呈色化合物は、電子を放出することで変色する物質であり、酸性化合物と接することで電子を放出して変色する化合物であれば特に限定されないが、具体的にはロイコ染料が好ましく用いられ、例えば、酸性で発色或いは色変化を起こすようなｐＨ指示薬、トリアリールメタン誘導体、フルオラン誘導体等が使用される。具体的には、例えば、クリスタルバイオレットラクトン、３−インドリノ−３−ｐ−ジメチルアミノフェニル−６−ジメチルアミノフタリド、３−ジエチルアミノ−７−クロロフルオラン、２−（２−フルオロフェニルアミノ）−６−ジエチルアミノフルオラン、２−（２−フルオロフェニルアミノ）−６−ジ−ｎ−ブチルアミノフルオラン、３−ジエチルアミノ−７−シクロヘキシルアミノフルオラン、３−ジエチルアミノ−５−メチル−７−ｔｅｒｔ−ブチルフルオラン、３−ジエチルアミノ−６−メチル−７−アニリノフルオラン、３−ジエチルアミノ−６−メチル−７−ｐ−ブチルアニリノフルオラン、３−シクロヘキシルアミノ−６−クロロフルオラン、２−アニリノ−３−メチル−６−（Ｎ−エチル−ｐ−トルイジノ）−フルオラン、３−ピロリジノ−６−メチル−７−アニリノフルオラン、３−ピロリジノ−７−シクロヘキシルアミノフルオラン、３−Ｎ−メチルシクロヘキシルアミノ−６−メチル−７−アニリノフルオラン、３−Ｎ−エチルペンチルアミノ−６−メチル−７−アニリノフルオラン等が挙げられる。 The electron-donating coloring compound is a substance that changes color by emitting electrons, and is not particularly limited as long as it is a compound that emits electrons and changes color by contacting an acidic compound. Specifically, a leuco dye is preferable. For example, a pH indicator, a triarylmethane derivative, a fluorane derivative, or the like that causes acid development or color change is used. Specifically, for example, crystal violet lactone, 3-indolino-3-p-dimethylaminophenyl-6-dimethylaminophthalide, 3-diethylamino-7-chlorofluorane, 2- (2-fluorophenylamino)- 6-diethylaminofluorane, 2- (2-fluorophenylamino) -6-di-n-butylaminofluorane, 3-diethylamino-7-cyclohexylaminofluorane, 3-diethylamino-5-methyl-7-tert- Butylfluorane, 3-diethylamino-6-methyl-7-anilinofluorane, 3-diethylamino-6-methyl-7-p-butylanilinofluorane, 3-cyclohexylamino-6-chlorofluorane, 2- Anilino-3-methyl-6- (N-ethyl-p-toluidino) -fluoro 3-pyrrolidino-6-methyl-7-anilinofluorane, 3-pyrrolidino-7-cyclohexylaminofluorane, 3-N-methylcyclohexylamino-6-methyl-7-anilinofluorane, 3-N -Ethylpentylamino-6-methyl-7-anilinofluorane and the like.
酸性化合物としては、常温において固体であれば特に限定されないが、例えば、シュウ酸、マロン酸、クエン酸、サリチル酸、安息香酸、ほう酸、ｐ−トルエンスルホン酸、及びそれらの水和物等を挙げることができる。これらのうちでも、水に対する溶解度が高いという点で、シュウ酸、マロン酸、ｐ−トルエンスルホン酸及びそれらの水和物が好ましい。 The acidic compound is not particularly limited as long as it is solid at room temperature, and examples thereof include oxalic acid, malonic acid, citric acid, salicylic acid, benzoic acid, boric acid, p-toluenesulfonic acid, and hydrates thereof. Can do. Among these, oxalic acid, malonic acid, p-toluenesulfonic acid, and hydrates thereof are preferable because of high solubility in water.
潮解物質としては、潮解性を示す物質であれば特に限定されないが、好ましくは塩、より好ましくは金属塩である。潮解物質としては、例えば、臭化マグネシウム、塩化マグネシウム、塩化カルシウム、塩化カリウム、臭化カルシウム、塩化ナトリウム、硫酸マグネシウム、硫酸カルシウム、臭化ナトリウム、硝酸カルシウム、硝酸マグネシウム及びそれらの水和物などを挙げることができる。 The deliquescent material is not particularly limited as long as it exhibits deliquescence, but is preferably a salt, more preferably a metal salt. Examples of deliquescent materials include magnesium bromide, magnesium chloride, calcium chloride, potassium chloride, calcium bromide, sodium chloride, magnesium sulfate, calcium sulfate, sodium bromide, calcium nitrate, magnesium nitrate and hydrates thereof. Can be mentioned.
本発明の湿度インジケータにおいては、呈色組成物内において水溶性の高級脂肪酸の錯塩またはアミノ酸の錯塩が塗膜化して潮解物質を覆っていると考えられ、これにより、潮解物質の潮解を効率良く抑制することができるものと考えられる。係る作用は、水溶性の錯塩によって得られ、水に不溶或いは水に対する溶解度の低い錯塩の場合には、錯塩が結晶化してしまうため、潮解物質の潮解を抑制できないものと考えられる。よって、係る錯塩の添加量が増えるほど、湿度インジケータの検知湿度が高い領域にシフトして変色（或いは消色）する。 In the humidity indicator of the present invention, it is considered that a complex salt of a water-soluble higher fatty acid or an amino acid complex forms a coating film in the color composition and covers the deliquescent material, thereby efficiently deliquescent the deliquescent material. It is thought that it can be suppressed. Such an action is obtained by a water-soluble complex salt. In the case of a complex salt that is insoluble in water or low in solubility in water, the complex salt is crystallized, and thus it is considered that deliquescence of the deliquescent substance cannot be suppressed. Therefore, as the amount of the complex salt added increases, the humidity indicator shifts to a region where the humidity detected is high and discolors (or is decolored).
本発明において用いられる高級脂肪酸の錯塩またはアミノ酸の錯塩は、水溶性であり、好ましくは、２０℃の水１００ｇに対する溶解度が３ｇ〜２００ｇである。溶解度が３ｇ未満の場合には、係る錯塩を添加した効果が得られにくい。また、この溶解度が２００ｇを超えると、潮解物質の潮解を抑制する効果が劣ることになる。また、係る錯塩の湿度インジケータ用塗料への添加量は、潮解物質（固形成分）１０重量部に対して０．１〜１０重量部が好ましい。０．１重量部未満では検知湿度のシフトが生じにくく、１０重量部を超えると、呈色組成物とした時に色ムラが発生し易く、色変化前の青色の色調が鮮明とはならず、好ましくない。 The higher fatty acid complex salt or amino acid complex salt used in the present invention is water-soluble, and preferably has a solubility of 3 g to 200 g in 100 g of water at 20 ° C. When the solubility is less than 3 g, it is difficult to obtain the effect of adding the complex salt. Moreover, when this solubility exceeds 200 g, the effect which suppresses the deliquescent of a deliquescent substance will be inferior. Moreover, the addition amount of the complex salt to the humidity indicator paint is preferably 0.1 to 10 parts by weight with respect to 10 parts by weight of the deliquescent substance (solid component). If it is less than 0.1 part by weight, the detected humidity is less likely to shift, and if it exceeds 10 parts by weight, color unevenness is likely to occur when the color composition is formed, and the blue color tone before the color change is not clear, It is not preferable.
具体的には、高級脂肪酸の錯塩としては、水溶性があるステアリン酸、ラウリン酸やミリスチン酸のカリウム塩、ナトリウム塩などの各種塩が挙げられる。また、アミノ酸の錯塩としては、グルタミン酸カルシウム、グルタミン酸カリウム、グルタミン酸ナトリウムや、グリシン、Ｌ−アラニン、Ｌ−バリン、Ｌ−システイン、Ｌ−スレオニンの各種塩が挙げられる。 Specifically, the complex salts of higher fatty acids, stearic acid is a water-soluble potassium salt of lauric acid and myristic acid, and various salts such as sodium salts. Examples of complex salts of amino acids include calcium glutamate, potassium glutamate, sodium glutamate, and various salts of glycine, L-alanine, L-valine, L-cysteine, and L-threonine.
水系樹脂エマルジョンとしては、担持体に影響を及ぼさない程度の加熱乾燥によって固化し、上記成分（電子供与性呈色化合物、酸性化合物、潮解物質、高級脂肪酸の錯塩またはアミノ酸の錯塩）を担持する樹脂バインダーとなり、潮解物質や酸性化合物、錯塩と反応せず、また、これら成分の存在によって凝集しない水系樹脂エマルジョンであれば、特に限定されないが、具体的にはアクリル系エマルジョン、水系ポリウレタン、水系ポリエステルが好ましく用いられる。また、その他にも弱アニオンエマルジョンなどを好ましく用いることができる。 Water-based resin emulsion is a resin that solidifies by heating and drying to such an extent that it does not affect the support, and carries the above components (electron-donating color compound, acidic compound, deliquescent substance, higher fatty acid complex salt or amino acid complex salt). It is not particularly limited as long as it is a water-based resin emulsion that becomes a binder, does not react with deliquescent substances, acidic compounds, complex salts, and does not aggregate due to the presence of these components. Specifically, acrylic emulsions, water-based polyurethanes, water-based polyesters are used. Preferably used. In addition, a weak anion emulsion or the like can be preferably used.
本発明の湿度インジケータ用塗料は、少なくとも、電子供与性呈色化合物、潮解物質、酸性化合物、水溶性の高級脂肪酸の錯塩またはアミノ酸の錯塩、水系樹脂エマルジョンからなるが、係る塗料に、有機溶媒を添加する構成とすると、塗料の粘度コントロールが容易となり、印刷適性や塗料の分散性が向上する、乾燥時間の短縮などで好ましい。かかる有機溶媒としては、水に対する溶解度が５ｍｌ／１００ｍｌ以上で加熱によって揮発する極性溶媒が好ましく用いられる。具体的には、メタノール、エタノール、１−プロパノール、２−プロパノール（イソプロパノール、ＩＰＡ）、１−ブタノール、２−ブタノール、２−メチル−１−プロパノール、ｔｅｒｔ−ブチルアルコール、メチルエチルケトン、酢酸エチル、テトラヒドロフラン、シクロヘキサノン、アセトン、アセトニトリルのうちの１種の溶媒或いは２種以上からなる混合溶媒が好ましく用いられる。短い乾燥時間、塗料の相溶性、低価格を考慮すると、好ましくは、ＩＰＡ、メタノール、エタノールである。 The humidity indicator paint of the present invention comprises at least an electron-donating color compound, a deliquescent substance, an acidic compound, a complex salt of a water-soluble higher fatty acid or an amino acid complex, and an aqueous resin emulsion. The composition to be added is preferable because the viscosity of the paint can be easily controlled, the printability and the dispersibility of the paint are improved, and the drying time is shortened. As such an organic solvent, a polar solvent which has a solubility in water of 5 ml / 100 ml or more and volatilizes by heating is preferably used. Specifically, methanol, ethanol, 1-propanol, 2-propanol (isopropanol, IPA), 1-butanol, 2-butanol, 2-methyl-1-propanol, tert-butyl alcohol, methyl ethyl ketone, ethyl acetate, tetrahydrofuran, One solvent or a mixed solvent composed of two or more of cyclohexanone, acetone, and acetonitrile is preferably used. Considering short drying time, compatibility of paint and low price, IPA, methanol and ethanol are preferable.
上記溶媒は、上記電子供与性呈色化合物、潮解物質、酸性化合物、高級脂肪酸の錯塩またはアミノ酸の錯塩を水系樹脂エマルジョンに微分散或いは溶解させた後に添加する。即ち、電子供与性呈色化合物、潮解物質、酸性化合物、高級脂肪酸の錯塩またはアミノ酸の錯塩を有機溶媒添加前に水系樹脂エマルジョンに微分散或いは溶解させておくことにより、各成分を塗料中に均一に微分散或いは溶解させることができる。尚、有機溶媒の添加量は、上記電子供与性呈色化合物、潮解物質、酸性化合物、高級脂肪酸の錯塩またはアミノ酸の錯塩、水系樹脂エマルジョンの合計１００重量部に対して通常１０〜１００重量部である。 The solvent is added after finely dispersing or dissolving the electron donating color compound, deliquescent material, acidic compound, higher fatty acid complex salt or amino acid complex salt in an aqueous resin emulsion. That is, each component is uniformly dispersed in the paint by finely dispersing or dissolving the electron donating color compound, deliquescent material, acidic compound, higher fatty acid complex salt or amino acid complex salt in the aqueous resin emulsion before adding the organic solvent. Can be finely dispersed or dissolved. The addition amount of the organic solvent is usually 10 to 100 parts by weight with respect to 100 parts by weight in total of the electron donating color compound, deliquescent substance, acidic compound, higher fatty acid complex salt or amino acid complex salt, and aqueous resin emulsion. is there.
尚、上記塗料には本発明の効果を損ねない範囲で必要に応じて消泡剤や防腐剤等を加えてもかまわない。 It should be noted that an antifoaming agent, a preservative, and the like may be added to the coating material as necessary within a range that does not impair the effects of the present invention.
本発明においては、上記湿度インジケータ用塗料を上記担持体に付着させ、加熱して乾燥させることにより、該塗料に含まれる電子供与性呈色化合物、潮解物質、酸性化合物、高級脂肪酸の錯塩またはアミノ酸の錯塩、及び水系樹脂エマルジョン由来の樹脂バインダーからなる呈色組成物が該担持体に担持された湿度インジケータが得られる。上記塗料を担持体に付着させる方法としては、所望量の塗料を担持体に付着させることができれば特に限定されず、例えば担持体を塗料に浸漬する方法、ワイヤーバーやロールコーター等で塗布する方法、スプレー等で吹き付ける方法など、担持体や塗料の組成に応じて適宜選択される。 In the present invention, the paint for humidity indicator is attached to the support, heated and dried to thereby provide an electron donating color compound, a deliquescent substance, an acidic compound, a higher fatty acid complex salt or an amino acid. Thus, a humidity indicator is obtained in which a colored composition comprising a complex salt of the above and a resin binder derived from an aqueous resin emulsion is supported on the carrier. The method for adhering the paint to the carrier is not particularly limited as long as a desired amount of paint can be adhered to the carrier, for example, a method of immersing the carrier in the paint, a method of applying with a wire bar, a roll coater or the like. The method of spraying with a spray or the like is appropriately selected according to the composition of the carrier and the coating material.
加熱方法としてはオーブンなどを適宜用いることができる。加熱温度及び加熱時間は担持体の素材や塗料の組成にもよるが、好ましくは４０〜１５０℃、より好ましくは５０〜１３０℃で、好ましくは１０〜１８０秒間加熱する。また、塗料の付着と加熱乾燥を複数回繰り返して呈色組成物を所定量担持させることも可能である。乾燥後の湿度インジケータにおいて担持された呈色組成物の量は、例えばフィルムなどの平板の担持体において、好ましくは乾燥塗料で０．１〜１０ｇ／ｍ2である。 As the heating method, an oven or the like can be used as appropriate. The heating temperature and the heating time are preferably 40 to 150 ° C., more preferably 50 to 130 ° C., and preferably 10 to 180 seconds, although depending on the material of the carrier and the composition of the coating material. It is also possible to carry a predetermined amount of the colored composition by repeating the adhesion of the paint and heat drying a plurality of times. The amount of the color forming composition supported on the humidity indicator after drying is preferably 0.1 to 10 g / m 2 in a dry paint in a flat support such as a film.
本発明の湿度インジケータは、紙やフィルムなどの担持体に水性塗料を付着させて得られるため、大面積の担持体に呈色組成物を担持させた後に切断することにより、所望の大きさのインジケータを容易に量産することができる。尚、担持体に予め印刷、顔料の練り込みなどの方法で、呈色化合物の色調と異なる色調に着色しておくと、呈色化合物の色変化が容易に認識でき、便利である。 The humidity indicator of the present invention is obtained by adhering a water-based paint to a carrier such as paper or film. Therefore, by cutting the color composition on a carrier having a large area, the humidity indicator has a desired size. The indicator can be easily mass-produced. In addition, it is convenient that the color change of the coloring compound can be easily recognized if it is colored in a color tone different from the color tone of the coloring compound by a method such as printing or kneading the pigment in advance on the carrier.
上記のようにして得られた本発明の湿度インジケータは、担持体に担持された呈色組成物に含まれる潮解物質が湿気によって潮解し、この水分に酸性化合物が溶解して流動化し、電子供与性呈色化合物と反応し、変色（消色を含む）を示すことができる。一旦変色した呈色組成物はオーブン等で加熱することにより容易に変色前の色に戻すことができる。 In the humidity indicator of the present invention obtained as described above, the deliquescent substance contained in the color composition carried on the carrier is deliquescent by moisture, and the acidic compound dissolves and fluidizes in this moisture, thereby providing electron donation. It reacts with the sexually colored compound and can exhibit discoloration (including decoloring). The colored composition once discolored can be easily returned to the color before the discoloration by heating in an oven or the like.
本発明の湿度インジケータは、担持体に呈色組成物を担持させた状態で用いることができ、そのまま湿度管理が必要な各種用途に用いることができるが、さらに下記速度調整樹脂層を用いることができる。係る速度調整樹脂層は、変色速度が速い場合に、その速度を抑えるための部材であり、湿度インジケータの外側を速度調整樹脂層で覆うことで呈色組成物に接する湿気を制限し、変色速度を遅らせることができる。 The humidity indicator of the present invention can be used in a state where the colored composition is supported on the support, and can be used as it is for various applications that require humidity management. it can. The speed adjusting resin layer is a member for suppressing the color change rate when the color change rate is high, and limits the humidity in contact with the color forming composition by covering the outside of the humidity indicator with the speed adjusting resin layer. Can be delayed.
このような速度調整樹脂層としては、適当な透湿性を有する透明樹脂層を用いれば良く、樹脂素材を溶媒に溶解或いは分散させた樹脂塗料を、呈色組成物を担持した担持体に塗布して加熱乾燥させたり、担持体に樹脂シート或いはフィルムをラミネート等により積層することで形成される。 As such a speed adjusting resin layer, a transparent resin layer having an appropriate moisture permeability may be used, and a resin paint in which a resin material is dissolved or dispersed in a solvent is applied to a carrier carrying a color composition. It is formed by heating and drying, or by laminating a resin sheet or film on a carrier.
係る樹脂素材としては、樹脂層形成後に適当な透湿性と透明性とを示すものであれば用いることができる。本発明において速度調整樹脂層の透湿性は、厚さ１２μｍのＰＥＴフィルムの上に測定用の樹脂層を形成し、水蒸気透過率測定装置（ＭＯＣＯＮ社製「ＰＥＲＭＡＴＲＡＮ−Ｗ ３／３３シリーズ」）により測定し、透湿度（ｇ／ｍ2・ｄａｙ）で示す。 As such a resin material, any material can be used as long as it exhibits appropriate moisture permeability and transparency after the resin layer is formed. In the present invention, the moisture permeability of the speed adjusting resin layer is determined by forming a measurement resin layer on a PET film having a thickness of 12 μm and using a water vapor transmission rate measuring device (“PERMATRAN-W 3/33 series” manufactured by MOCON). Measured and indicated by moisture permeability (g / m 2 · day).
速度調整樹脂層の透湿度としては、速度調整作用が得られれば特に限定されないが、好ましくは０．５〜５０ｇ／ｍ2・ｄａｙである。透湿度が０．５ｇ／ｍ2・ｄａｙ未満では透湿性が低すぎるため湿気を検知しても変色速度が遅くなりすぎる。また、５０ｇ／ｍ2・ｄａｙを超えると透湿性が高すぎて速度抑制の効果が得られにくい。 The moisture permeability of the speed adjusting resin layer is not particularly limited as long as a speed adjusting action is obtained, but is preferably 0.5 to 50 g / m 2 · day. If the moisture permeability is less than 0.5 g / m 2 · day, the moisture permeability is too low, so even if moisture is detected, the discoloration rate is too slow. On the other hand, if it exceeds 50 g / m 2 · day, the moisture permeability is too high and it is difficult to obtain the effect of speed control.
具体的に樹脂素材として、ポリエチレンテレフタレート、ブチラール樹脂、ポリエステルウレタン、ポリアミド、ポリ塩化ビニリデン、スチレン化エポキシ樹脂、エポキシ樹脂、フェノキシ樹脂、ポリエステル樹脂、塩化酢酸ビニル、アクリル樹脂、ニトロセルロースなどを用いることができる。 Specifically, polyethylene terephthalate, butyral resin, polyester urethane, polyamide, polyvinylidene chloride, styrenated epoxy resin, epoxy resin, phenoxy resin, polyester resin, vinyl acetate, acrylic resin, nitrocellulose, etc. may be used as the resin material. it can.
係る速度調整樹脂層は、呈色組成物を覆って形成すればよいが、担持体が不織布のように通気性を有する場合には、呈色組成物を付着させた側とは反対側にも設けて、該反対側から呈色組成物に吸収される湿気を抑制することが好ましい。 The speed adjusting resin layer may be formed so as to cover the color composition, but when the carrier is breathable like a nonwoven fabric, the speed control resin layer is also formed on the side opposite to the side on which the color composition is adhered. It is preferable to provide and suppress moisture absorbed by the coloring composition from the opposite side.
電子供与性呈色化合物としてロイコ染料「ＢＬＵＥ−６３」（山本化成（株）製）１重量部、シュウ酸２水和物（和光純薬工業（株）製）１重量部、臭化マグネシウム６水和物（和光純薬工業（株）製）１０重量部（固形成分６．３重量部）、表１に示す錯塩を表１に示す重量部で、アクリルエマルジョン「ＤＩＣＮＡＬ Ｅ−８２０３ＷＨ」（大日本インキ化学工業（株）製；固形成分４５重量％）４０重量部に添加し、塗料が均一になるように攪拌した後、さらに、ＩＰＡ２０重量部を加え、塗料が均一になるように攪拌した。この塗料を、ＰＥＴフィルム（東洋紡績（株）製 １２μｍ厚み）にワイヤーバー♯１０を用いて塗工し、８０℃で１分間乾燥させ、湿度インジケータを得た。乾燥塗料の塗布量は３ｇ／ｍ2であった。 1 part by weight of leuco dye “BLUE-63” (manufactured by Yamamoto Kasei Co., Ltd.), 1 part by weight of oxalic acid dihydrate (manufactured by Wako Pure Chemical Industries, Ltd.), magnesium bromide 6 Hydrate (manufactured by Wako Pure Chemical Industries, Ltd.) 10 parts by weight (6.3 parts by weight of solid component), complex salt shown in Table 1 in parts by weight shown in Table 1, acrylic emulsion “DICNAL E-8203WH” (large Nihon Ink Chemical Co., Ltd .; solid component 45% by weight) was added to 40 parts by weight and stirred to make the paint uniform, and then 20 parts by weight of IPA was added and stirred to make the paint uniform. . This paint was applied on a PET film (12 μm thickness, manufactured by Toyobo Co., Ltd.) using a wire bar # 10 and dried at 80 ° C. for 1 minute to obtain a humidity indicator. The amount of dry paint applied was 3 g / m 2 .
得られた湿度インジケータを、２０〜６０％ＲＨの各環境下に２４時間放置し、色相の変化を目視で観察した。結果を表１に示す。 The obtained humidity indicator was left in each environment of 20 to 60% RH for 24 hours, and the change in hue was visually observed. The results are shown in Table 1.
上記したように、本発明の湿度インジケータにおいては、水溶性の高級脂肪酸の錯塩またはアミノ酸の錯塩を添加することにより、検知湿度を無添加の３０％ＲＨから４０〜６０％ＲＨにシフトさせることができた。また、Ｎｏ．９については、Ｎｏ．４と同様の検知湿度のシフトを生じたが、呈色組成物に色ムラが発生し、色変化前の青色の色調が鮮明とはならず（薄青と表現した）、湿度変化が明確に判別できず、製品としては不可であった。 As described above, in the humidity indicator of the present invention, the detection humidity can be shifted from 30% RH without addition to 40-60% RH by adding a complex salt of a water-soluble higher fatty acid or an amino acid complex. did it. No. For No. 9, no. The detected humidity shift occurred in the same manner as in No. 4, but color unevenness occurred in the colored composition, the blue color tone before the color change was not clear (expressed as light blue), and the humidity change was clear It could not be determined and was not possible as a product.
Claims (6)