JP5428492B2 - Packaging material with printing information - Google Patents
Packaging material with printing information Download PDFInfo
- Publication number
- JP5428492B2 JP5428492B2 JP2009105373A JP2009105373A JP5428492B2 JP 5428492 B2 JP5428492 B2 JP 5428492B2 JP 2009105373 A JP2009105373 A JP 2009105373A JP 2009105373 A JP2009105373 A JP 2009105373A JP 5428492 B2 JP5428492 B2 JP 5428492B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- printing
- information
- packaging material
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
微細な文字や図形からなる可変情報等を印字可能で、印字された可変情報等の改竄を防止すると共に、可変情報等の高精度の読取を可能とした印字情報付き包装材に関する。 The present invention relates to a packaging material with print information capable of printing variable information including fine characters and figures, preventing falsification of the printed variable information, and enabling high-precision reading of variable information.
紙素材を用いた紙箱や紙カップ、プラスチック素材を用いた包装容器や包装袋は、あらゆる分野の製品或いは商品の包装体として利用されており、これに用いられる包装材への、商品名や商品デザイン、商品の特性や取り扱いの説明、商品の容量や原材料の表示等、多岐に亘る表示がオフセット印刷やグラビア印刷などの印刷方法により施されて使用されている。一般的に、上記のような表示は、長期間に亘って変化しないものである。これに対し、「可変情報」すなわち、製造年月日や製造ロット番号、内容物が食品の場合には、賞味期限や品質保持期限等、刻々と変化する情報については、例えば、別個に製造され可変情報が印刷されたラベルを貼付したり、インクジェットプリンター等により、包装材の外面に直接可変情報を印字することが一般に行われている。最近では、商品情報やキャンペーン情報など大量の情報を二次元コード等によって告知することも行なわれ、特にキャンペーンの告知情報は、短期間の可変情報として扱われることも一般化している。 Paper boxes and paper cups using paper materials, and packaging containers and bags using plastic materials are used as products or product packaging in all fields. Product names and product designs for the packaging materials used for these products are used. A wide variety of displays such as product characteristics and explanation of handling, display of product capacity and raw materials, etc. are applied by printing methods such as offset printing and gravure printing. In general, the display as described above does not change over a long period of time. On the other hand, “variable information”, that is, production date, production lot number, and information that changes every moment, such as the expiration date and the quality retention date when the contents are food, are manufactured separately, for example. Generally, the variable information is directly printed on the outer surface of the packaging material by attaching a label on which the variable information is printed, or by an ink jet printer or the like. Recently, a large amount of information such as product information and campaign information is also notified by a two-dimensional code or the like, and in particular, campaign notification information is generally handled as short-term variable information.
従来、インクジェット受容層を表面に形成した紙製素材と、紙製素材の他方の面にヒートシール層を積層した積層体からなり、インクジェット方式により表面に画像、文字等の情報を記録可能とした包装材が提案されている(例えば、特許文献1)。
また、製品が包装された状態では、外面から目視できず、製品購入後に包装材を開封し内容物を取り出した状態で、包装材の内面から印字されたユニークナンバーなどの情報を目視にて確認可能とし、例えばキャンペーン等の懸賞サイトに接続し、ユニークナンバーを入力して応募できるようにした包装袋が提案されている(例えば、特許文献2)。
Conventionally, it consists of a paper material with an inkjet receptive layer formed on the surface and a laminate with a heat seal layer laminated on the other side of the paper material, making it possible to record information such as images and characters on the surface by the inkjet method. A packaging material has been proposed (for example, Patent Document 1).
In addition, when the product is packaged, it cannot be seen from the outside. After purchasing the product, the packaging material is opened and the contents are taken out, and the information such as the unique number printed from the inside of the packaging material is visually confirmed. There has been proposed a packaging bag that can be applied and connected to a prize site such as a campaign and can be applied by inputting a unique number (for example, Patent Document 2).
しかしながら、特許文献1の発明は、紙カップのように紙製の素材からなるもので、耐水性やヒートシール性の付与のために、例えばポリエチレン等の樹脂の積層等によりインキ吸収能力の低い素材において、素材の一方の面にインクジェット受容層を形成することにより、表面への印字を可能にしたものであるが、包装形態としては紙カップや紙箱等に限られ、包装袋やPETボトル等の表示ラベル等のフィルムからなる包装材には使用できず、用途が限定されてしまうという問題がある。包装容器や包装袋に用いられるプラスチックフィルム表面へのインクジェットプリントによる印字は、プラスチック素材と印字されるインキとの接着性が強固でなく、インキが受容吸収されないために滲みが発生し易く、特に、微細な文字や図形については再現性の低いものであった。
However, the invention of
また、特許文献2の発明は、その請求項1に示された構成「最外フィルム層、透明バリア層、ヒートシール層を順次積層する積層材からなり、最外フィルム層の裏面にインキ層からなる隠蔽層、白色インキ層、インクジェット記録方式で印字した隠蔽情報層を順に設けた隠蔽層付き包装容器」に関するものであり、プラスチックフィルムにインクジェット方式で印字した後、印字面をヒートシール層により保護したものである。上記構成によれば、印字する内容がユニークナンバー等のように目視にて確認できる情報であれば白色インキ層上に設けられる印字情報の読み取りに問題はないが、大量の情報をエンコードした二次元コード等の印字情報の場合は、バーコードリーダーや携帯電話等の読み取り端末による読み取りが行なわれるため、例えばカーボンブラック等の無機顔料を着色剤とするインキ層からなる隠蔽層の発色を白色インキ層で十分に隠蔽できず、白色インキ層上に設けられる印字情報の読み取りエラーとなる惧れがあった。
In addition, the invention of
そこで、本発明の目的は、インクジェット方式で、微細な可変情報等を印字可能とし、特に二次元コード等の印字を明瞭なものとすると共に、包装材に施された印刷部分に影響されることなく可変情報を読み取ることができ、且つ、印字された可変情報等の改竄を防止することが可能な印字情報付き包装材を提供することにある。 Accordingly, an object of the present invention is to enable printing of minute variable information and the like by an ink jet method, in particular, to make clear printing of a two-dimensional code and the like, and to be influenced by a printed portion applied to a packaging material. It is another object of the present invention to provide a packaging material with print information that can read variable information without any alteration and prevent falsification of the printed variable information.
上記課題を解決するため、請求項1の発明は、裏面に印刷層を設けた基材層と隠蔽層と最内層となる熱接着性樹脂層とが順次積層されており、前記隠蔽層の前記熱接着性樹脂層側の面にインキ受容層とインクジェット方式で印字される可変情報印字層とが順次形成されており、前記印刷層と前記可変情報印字層との間に全面にわたって形成された隠蔽層が介在していることを特徴とする印字情報付き包装材であって、一般の印刷用インキにより印刷される印刷層とインクジェット方式で印字される可変情報印字層との間に、隠蔽層を設けることにより、特にバーコードリーダーや携帯電話等の読み取り端末による読み取り精度を向上させ、さらに隠蔽層の可変情報印字面にインキ受容層を設けることにより、滲みのない高精細な印字を可能にし、印字により伝達できる情報量を増大させる。
In order to solve the above-mentioned problem, the invention of
請求項2の発明は、前記隠蔽層が金属蒸着膜を有するプラスチックフィルムからなることを特徴とする請求項1記載の印字情報付き包装材、また、請求項3の発明は、前記隠蔽層が金属箔からなることを特徴とする請求項1記載の印字情報付き包装材であって、金属蒸着膜を有するプラスチックフィルムまたはアルミニウム等の金属箔からなる隠蔽層とインクジェット方式で印字される可変情報印字とのコントラストが形成でき、バーコードリーダーや携帯電話等の読み取り端末による読み取りが行い易い。
The invention according to
請求項4の発明は、前記隠蔽層が白色顔料を含んだプラスチックフィルムからなることを特徴とする請求項1記載の印字情報付き包装材であって、白色顔料を含んだプラスチックフィルムからなる隠蔽層とインクジェット方式で印字される可変情報印字とのコントラストが形成でき、バーコードリーダーや携帯電話等の読み取り端末による読み取りが行い易く、また目視もし易い。
The invention according to
請求項5の発明は、前記可変情報印字層に印字される情報が、縦80dpi以上×横80dpi以上の可変情報であることを特徴とする請求項1〜4のいずれかに記載の印字情報付き包装材であって、より微細で情報量の大きな印字を再現することができるので、販売者側から消費者へのより大量の情報提供が可能となり、消費者には情報取得による商品への信頼性や利便性の向上が可能となる。
The invention according to
請求項6の発明は、前記可変情報印字層に印字される情報が、読み取り端末により認識可能とした可変情報であることを特徴とする請求項1〜5のいずれかに記載の印字情報付き包装材であって、読み取り端末で認識可能な、より微細で大きな情報量の印字を行うので、大量の情報の提供と取得が可能となる。
The invention according to
本発明の印字情報付き包装材は、隠蔽層の熱接着性樹脂層側の面にインキ受容層を設けたので、隠蔽層を形成する金属蒸着膜を有するプラスチックフィルム等にインクジェット方式で多量の情報量の高精細な印字が可能で、包装材の開封前には外部から印字情報が視認できず、開封後に確認でき、且つ、印刷層と可変情報印字層との間に金属蒸着膜を有するプラスチックフィルム、または、アルミニウム等の金属箔、或いは、白色顔料を含むプラスチックフィルム等による隠蔽層を設けることにより、印刷層に影響されることが無く、バーコードリーダーや携帯電話等の読み取り端末による読み取り精度を向上させた包装材を提供できる。 Since the packaging material with printing information of the present invention is provided with an ink receiving layer on the surface of the concealing layer on the side of the heat-adhesive resin layer, a large amount of information is obtained by an ink jet method on a plastic film having a metal vapor deposition film for forming the concealing layer. High-definition printing is possible, printing information is not visible from the outside before opening the packaging material, and can be confirmed after opening, and has a metal vapor deposition film between the printing layer and the variable information printing layer By providing a concealing layer made of a film, a metal foil such as aluminum, or a plastic film containing a white pigment, it is not affected by the printing layer, and reading accuracy by a reading terminal such as a barcode reader or a mobile phone. The packaging material which improved can be provided.
特に、可変情報の印字面となる隠蔽層面にインキ受容層を設けることで、情報量の多い可変情報(二次元コード等)の印字を高精細に行なうことができ、エンドユーザーへの伝達情報量を増加させることが可能となり、販売者側として商品情報(商品の生産・流通等の履歴情報、商品の特性情報等)やキャンペーン告知情報(募集情報等)の表示が行え、消費者側には取り扱い情報(調理情報等)等による利便性の向上が可能となる。 In particular, by providing an ink-receiving layer on the concealing layer surface, which is the variable information printing surface, variable information with a large amount of information (two-dimensional code, etc.) can be printed with high definition and the amount of information transmitted to the end user The seller can display product information (history information on product production / distribution, product characteristic information, etc.) and campaign notification information (recruitment information, etc.) on the consumer side. Convenience can be improved by handling information (such as cooking information).
さらに、インクジェット方式で印字された可変情報印字層が、隠蔽層と熱接着性樹脂層との間に設けられているため、包装材同士や内容物との擦過等での印字面の汚損による印字情報の毀損や、印字情報の改竄を防止することができる。 Furthermore, since the variable information printing layer printed by the ink jet method is provided between the concealing layer and the heat-adhesive resin layer, printing due to the printing surface being damaged due to rubbing between packaging materials or contents. It is possible to prevent information damage and falsification of print information.
本発明につき、図面等を用いて以下に詳述する。
図1は本発明に係る印字情報付き包装材の積層構成の一例を示す説明用拡大断面図で、包装材Sは外側から基材層1、接着層2、隠蔽層3、接着層2’、熱接着性樹脂層4を順に積層しており、基材層1の内面に印刷層5、隠蔽層3の内面にインキ受容層6、可変情報印字層7を順次設けた積層構成からなるものであり、例えば、二軸延伸ポリエチレンテレフタレートフィルム12μm/印刷/接着/アルミニウム蒸着したポリエチレンテレフタレートフィルム12μm/インキ受容層/可変情報印字層/接着/線状低密度ポリエチレン60μmで構成される。上記積層構成は一例であって、本発明を限定するものではない。
The present invention will be described in detail below with reference to the drawings.
FIG. 1 is an enlarged cross-sectional view for explaining an example of a laminated structure of a packaging material with printing information according to the present invention. A packaging material S includes a
本発明の包装材において、一般的な表示等の印刷が可能な基材としては、低密度ポリエチレン、中密度ポリエチレン、高密度ポリエチレン、直鎖状低密度ポリエチレン、ポリプロピレン、エチレン−プロピレン共重合体等のポリオレフィン系樹脂、エチレン−酢酸ビニル系樹脂、アイオノマー樹脂、エチレン−アクリル酸共重合体、エチレン−アクリル酸エチル共重合体、ポリブテン系樹脂、ポリメチルペンテン系樹脂、ポリアクリル系樹脂、ポリアクリルニトリル系樹脂、ポリエステル系樹脂、ポリアミド系樹脂、ポリスチレン系樹脂、ポリ塩化ビニル系樹脂、ポリ塩化ビニリデン系樹脂、エチレン−酢酸ビニル共重合体ケン化物、ポリカーボネート系樹脂、フッ素系樹脂、ビニロン、セロハン等の合成樹脂を主体とする各種の樹脂のフィルムないしシートを使用することができる。
上記のフィルムないしシートは、未延伸あるいは一軸方向または二軸方向等に延伸されたものであってもよい。フィルムないしシートの厚さとしては、個々の包装の課題等により任意であるが、凡そ10〜200μm程度が好ましい。
In the packaging material of the present invention, as a base material capable of printing such as general display, low density polyethylene, medium density polyethylene, high density polyethylene, linear low density polyethylene, polypropylene, ethylene-propylene copolymer, etc. Polyolefin resin, ethylene-vinyl acetate resin, ionomer resin, ethylene-acrylic acid copolymer, ethylene-ethyl acrylate copolymer, polybutene resin, polymethylpentene resin, polyacrylic resin, polyacrylonitrile Resin, polyester resin, polyamide resin, polystyrene resin, polyvinyl chloride resin, polyvinylidene chloride resin, saponified ethylene-vinyl acetate copolymer, polycarbonate resin, fluorine resin, vinylon, cellophane, etc. Various resin materials mainly made of synthetic resin It can be used beam or sheet.
The film or sheet may be unstretched or stretched in a uniaxial direction or a biaxial direction. The thickness of the film or sheet is arbitrary depending on the problem of individual packaging, but is preferably about 10 to 200 μm.
基材層1に設けた印刷層5には、内容物の表示、装飾、賞味期間の表示、製造者、販売者等の表示、その他の表示のために、文字、絵柄、図形、記号等の任意の印刷を、基材層1の裏面、又は表面に設けることができる。尚、図1に示すように印刷層5を基材層1の裏面に設けることで、基材層1により印刷層5が保護されるので、表面からの擦れ等によるインキ剥がれを防止できる。又、基材層1の表面に設ける場合には、さらに表面保護層を設けることが一般的に行なわれている。
印刷層5は、例えば、通常のインキ組成物を使用してグラビア印刷或いはオフセット印刷、フレキソ印刷、凸版印刷、シルクスクリーン印刷、その他等の通常の印刷法によって、形成することができる。
The printed
The
隠蔽層3は、印刷層5と可変情報印字層7との間に、印刷以外の方法で隠蔽する層を設け、前記可変情報印字層7の印字部分が前記印刷層5の文字や絵柄の影響を受けずに読み取りを可能とするもので、例えば、アルミニウム等の金属をプラスチックフィルムに真空蒸着して蒸着膜を形成したフィルム、アルミニウム等の金属箔、ポリオレフィン樹脂を主材として白色顔料を含んだ着色フィルムを好ましく用いることができ、読み取り機による認識精度を向上させることができる。
金属蒸着膜を形成する金属としては、アルミニウム(Al)、クロム(Cr)、銀(Ag)、銅(Cu)、錫(Sn)等の金属を使用することができる。
着色フィルムに使用される白色顔料としては、酸化チタン、酸化亜鉛、体質顔料である水酸化アルミニウム、炭酸マグネシウム、炭酸カルシウム、沈降性硫酸バリウム、シリカ、タルク等がある。
The concealing
As a metal forming the metal vapor deposition film, a metal such as aluminum (Al), chromium (Cr), silver (Ag), copper (Cu), tin (Sn), or the like can be used.
Examples of the white pigment used in the colored film include titanium oxide, zinc oxide, extender pigments such as aluminum hydroxide, magnesium carbonate, calcium carbonate, precipitated barium sulfate, silica, and talc.
インキ受容層6は、インクジェットプリンターにより印字されるインキを受容するため、隠蔽層3を形成するフィルムの印字面に予め塗布等により形成されるもので、インキ受容層6を形成する材料は、ポリエステル系樹脂、ポリアミド系樹脂、ポリウレタン系樹脂、エポキシ樹脂、フェノール系樹脂、(メタ)アクリル系樹脂、ポリ酢酸ビニル系樹脂、ポリエチレンあるいはポリプロピレン等のポリオレフィン系樹脂あるいはその共重合体ないし変性樹脂、セルロース系樹脂、その他等をビヒクルの主成分とする樹脂組成物を使用することができる。
また、インキ受容層6の材料には、インキを受容する空隙を有する多孔質材料(白顔料やシリカ粒子等)を分散させるが、特に、印字部分の読み取りにバーコードリーダーや携帯電話等の読み取り端末を使用する場合、白の顔料、例えば酸化チタン、炭酸カルシウム、硫酸バリウム等を分散させることが、インキ受容層と印字部分とのコントラストを上げ認識し易くするために、効果的である。
塗布法として、例えば、グラビアコート法、リバースロールコート法、ナイフコート法、キスコート法、その他等の方法で塗布することができ、その固形分塗布量としては、乾燥状態で0.1g/m2〜5g/m2が好ましく用いることができ、望ましくは0.5g/m2〜2g/m2である。
The
In addition, a porous material (white pigment, silica particles, etc.) having voids for receiving ink is dispersed in the material of the
As a coating method, for example, a gravure coating method, a reverse roll coating method, a knife coating method, a kiss coating method, and the like can be applied, and the solid content coating amount is 0.1 g / m 2 in a dry state. to 5 g / m 2 can be preferably used, preferably from 0.5g / m 2 ~2g / m 2 .
可変情報印字層7は、インクジェット方式のインクジェットプリンターを用いた印字により形成される層である。インクジェット方式は記録用インキを微細な圧電素子の圧力、あるいは発熱抵抗体素子の加熱によって発生するエアーの圧力によってノズルから噴射し、受像層に付着させることにより記録を行なう方式である。
可変情報には、製造年月日、加工年月日、消費期限、賞味期限等の商品に表示が必要とされ且つ目視できる状態とされた可変情報と、生産や流通の履歴情報、商品情報、キャンペーンの告知情報等、大量の情報をエンコードした二次元コード等を、バーコードリーダーや携帯電話等の読み取り端末により認識可能とした可変情報とがあり、特に、二次元コード等は、滲み等の無い状態で印字されることが必要であるので、前述したようにインキ受容層6を設けることで、正確且つ再現性良く印字することができる。
また、可変情報印字層7は、隠蔽層3と熱接着性樹脂層4との間に設けられているので、包装材同士や内容物との擦過等で印字面が汚損されて印字情報が毀損したり、故意による印字情報の改竄を防止できる。
The variable
The variable information includes production date, processing date, expiry date, expiry date, variable information that is required to be displayed on the product and is in a visible state, production and distribution history information, product information, There is variable information that can be recognized by a reading terminal such as a barcode reader or mobile phone, such as a two-dimensional code that encodes a large amount of information, such as campaign notification information. Since it is necessary to print in the absence of ink, printing can be performed accurately and with good reproducibility by providing the
Further, since the variable
熱接着性樹脂層4を構成するプラスチックフィルムとしては、例えば、低密度ポリエチレン、中密度ポリエチレン、高密度ポリエチレン、直鎖状低密度ポリエチレン、ポリプロピレン、エチレン−プロピレン共重合体等のポリオレフィン系樹脂、エチレン−酢酸ビニル系樹脂、アイオノマー樹脂、エチレン−アクリル酸共重合体、エチレン−アクリル酸エチル共重合体、ポリブテン系樹脂、ポリメチルペンテン系樹脂、ポリアクリル系樹脂、ポリアクリルニトリル系樹脂、ポリエステル系樹脂、ポリアミド系樹脂、ポリスチレン系樹脂、ポリ塩化ビニル系樹脂、ポリ塩化ビニリデン系樹脂、エチレン−酢酸ビニル共重合体ケン化物、ポリカーボネート系樹脂、フッ素系樹脂、ビニロン、セロハン等の合成樹脂を主体とする各種の樹脂の透明なフィルムないしシートを使用することができる。
Examples of the plastic film constituting the heat-
基材層1と隠蔽層3及び熱接着性樹脂層4をそれぞれ接着する方法としては、ドライラミネート用接着剤を介して積層するドライラミネーション法、或いは、溶融押出し接着性樹脂を介して積層する押出しラミネーション法等で行うことができる。
ドライラミネート用接着剤としては、例えば、1液或いは2液硬化型ないしは非硬化型のビニル系、(メタ)アクリル系、ポリアミド系、ポリエステル系、ポリエーテル系、ポリウレタン系、エポキシ系、ゴム系、その他等の溶剤型、水性型、或いはエマルジョン型等のラミネート用接着剤を使用することができ、コーティング方法としては、例えば、ダイレクトグラビアロールコート法、グラビアロールコート法、キスコート法、リバースロールコート法、フォンテン法、トランスファーロールコート法、その他で塗布できる。
溶融押出し性樹脂としては、例えば、低密度ポリエチレン樹脂、中密度ポリエチレン樹脂、高密度ポリエチレン樹脂、直鎖状低密度ポリエチレン樹脂、メタロセン触媒を利用して重合したエチレン・αオレフィンとの共重合体樹脂、エチレン・ポリプロピレン共重合体樹脂、エチレン・酢酸ビニル共重合体樹脂、エチレン・アクリル酸共重合体樹脂、エチレン・アクリル酸エチル共重合体樹脂、エチレン・メタクリル酸共重合体樹脂、エチレン・メタクリル酸メチル共重合体樹脂、エチレン・マレイン酸共重合体樹脂、アイオノマー樹脂、ポリオレフィン樹脂に不飽和カルボン酸、不飽和カルボン酸、不飽和カルボン酸無水物、エステル単量体をグラフト重合、または、共重合した樹脂、無水マレイン酸をポリオレフィン樹脂にグラフト変性した樹脂等を使用できる。
As a method of bonding the
Examples of the adhesive for dry laminating include, for example, one-part or two-part curable or non-curable vinyl type, (meth) acrylic type, polyamide type, polyester type, polyether type, polyurethane type, epoxy type, rubber type, Other solvent-type, aqueous-type, or emulsion-type adhesives can be used. Examples of the coating method include direct gravure roll coating method, gravure roll coating method, kiss coating method, reverse roll coating method. It can be applied by the Fonten method, transfer roll coating method, and others.
Examples of the melt-extrusion resin include a low density polyethylene resin, a medium density polyethylene resin, a high density polyethylene resin, a linear low density polyethylene resin, and a copolymer resin of ethylene / α-olefin polymerized using a metallocene catalyst. , Ethylene / polypropylene copolymer resin, ethylene / vinyl acetate copolymer resin, ethylene / acrylic acid copolymer resin, ethylene / ethyl acrylate copolymer resin, ethylene / methacrylic acid copolymer resin, ethylene / methacrylic acid Graft polymerization or copolymerization of unsaturated carboxylic acid, unsaturated carboxylic acid, unsaturated carboxylic acid anhydride, ester monomer to methyl copolymer resin, ethylene / maleic acid copolymer resin, ionomer resin, polyolefin resin Grafted maleic anhydride to polyolefin resin The resin or the like can be used.
図2は、上記積層構成の包装材を用いて形成した包装袋の一例を示す説明用断面図で、本発明に係る包装材Sを用いて製造される包装袋Pは、包装材Sの互いに対向する端縁部を重ね合わせ熱接着して背シール部を形成し、形成された筒状の両端をそれぞれ重ね合わせて端部シール部を形成してなるピロータイプ袋であって、基材層1の裏面に通常のインキ組成物を使用して印刷層5を形成した後に隠蔽層3を接着層2を介して接着し、隠蔽層3の裏面にインキ受容層6を塗布し、インキ受容層6にインクジェットプリンター装置を使用して可変情報印字層7を印字した上で、隠蔽層3に接着層2’を介して熱接着性樹脂層4を積層して形成されており、可変情報印字層7は熱接着性樹脂層4により保護されている。尚、図の表示を明瞭にすべく、上記接着層2及び2’を省略して描画している。
上記は本発明に係る包装材を用いて形成した包装袋の一例であって、これに限定されるものではなく、本発明に係る包装材を用いて、上記のように包装材端縁の内層の面を対向させて折り曲げるか、或いは包装材端縁をそれぞれ重ね合わせ、さらに包装材の外周の周辺端部をヒートシールし、種々の包装袋に製造することができる。また、この包装袋の一例において、可変情報印字層7は、隠蔽層3の内面に印字され、包装袋Pの外面からは読み取られることがなく、開封することにより印字部分の読み取りが可能となるが、先述のように、可変情報のうちにも表示が義務付けられ目視されるべき情報と、キャンペーン情報や、「当り」「外れ」のように購入者を特定して取得が可能であるべき情報があり、包装材Sの積層構成において何れの位置に印字するかは適宜決定される。
FIG. 2 is an explanatory cross-sectional view showing an example of a packaging bag formed using the packaging material having the above-described laminated structure, and the packaging bag P manufactured using the packaging material S according to the present invention includes the packaging material S. A pillow-type bag in which opposing edge portions are overlapped and thermally bonded to form a back seal portion, and both formed cylindrical ends are overlapped to form an end seal portion, and a base material layer After forming the
The above is an example of a packaging bag formed using the packaging material according to the present invention, and is not limited to this, and using the packaging material according to the present invention, the inner layer of the packaging material edge as described above. These can be folded with the surfaces facing each other, or the edges of the packaging material can be overlapped, and the peripheral edge of the outer periphery of the packaging material can be heat sealed to produce various packaging bags. Moreover, in this example of the packaging bag, the variable
尚、本発明に係る包装材を用いて形成されるのは上記包装袋に限定されるものではなく、例えば、蓋材、壜体や缶体或いは前述の袋体等に用いられるラベル、単位商品や集積商品の帯体や外包体等にも使用することができる。 In addition, what is formed using the packaging material which concerns on this invention is not limited to the said packaging bag, For example, the label used for a cover material, a housing, a can or the above-mentioned bag body, unit goods It can also be used for a band or an outer package of an integrated product.
本発明の印字情報つき包装材について、以下の実施例等により説明を行う。 The packaging material with print information of the present invention will be described with reference to the following examples.
実施例1は、基材層となる厚み12μmの二軸延伸ポリエチレンテレフタレートフィルムの裏面にグラビア印刷方式にて印刷加工を行った後、厚み12μmのアルミニウム蒸着したポリエチレンテレフタレートフィルムを隠蔽層としてウレタン系ドライラミネート接着剤3.0g/m2を介してラミネートし、次いで可変情報の印字部分にメジウム(透明)インキをグラビアコート法にて塗布してインキ受容層とし、該インキ受容層にインクジェットプリンターを用いてQRコード(登録商標)を印字した後、ウレタン系ドライラミネート接着剤3.0g/m2を介して低密度ポリエチレン60μmを全面にラミネートしたものである。 In Example 1, a 12 μm-thick biaxially stretched polyethylene terephthalate film serving as a base material layer was printed on the back surface by a gravure printing method, and then a 12 μm-thick aluminum-deposited polyethylene terephthalate film was used as a concealing layer. Lamination is carried out through a laminating adhesive 3.0 g / m 2 , and then a medium (transparent) ink is applied to a variable information printing portion by a gravure coating method to form an ink receiving layer, and an ink jet printer is used for the ink receiving layer After printing the QR code (registered trademark), 60 μm of low-density polyethylene is laminated on the entire surface through a urethane dry laminate adhesive 3.0 g / m 2 .
実施例2は、基材層となる厚み12μmの二軸延伸ポリエチレンテレフタレートフィルムの裏面にグラビア印刷方式にて印刷加工を行った後、厚み12μmのアルミニウム蒸着したポリエチレンテレフタレートフィルムを隠蔽層としてウレタン系ドライラミネート接着剤3.0g/m2を介してラミネートし、次いで可変情報の印字部分に白色インキをグラビアコート法にて塗布してインキ受容層とし、該インキ受容層にインクジェットプリンターを用いてQRコード(登録商標)を印字した後、ウレタン系ドライラミネート接着剤3.0g/m2を介して低密度ポリエチレン60μmを全面にラミネートしたものである。 In Example 2, a 12 μm-thick biaxially stretched polyethylene terephthalate film serving as a base material layer was printed on the back surface by a gravure printing method, and then a 12 μm thick aluminum-deposited polyethylene terephthalate film was used as a concealing layer to form a urethane-based dry Lamination is performed through a laminating adhesive 3.0 g / m 2 , and then white ink is applied to a variable information printing portion by a gravure coating method to form an ink receiving layer, and an ink jet printer is used for the ink receiving layer. After printing (registered trademark), 60 μm of low density polyethylene is laminated on the entire surface through a urethane dry laminate adhesive of 3.0 g / m 2 .
比較例1は、基材層となる厚み12μmの二軸延伸ポリエチレンテレフタレートフィルムの裏面にグラビア印刷方式にて印刷加工を行った後、可変情報の印字部分に隠蔽層として墨色インキ、次いで白色インキをグラビアコート法にて塗布してインキ受容層とし、該インキ受容層にインクジェットプリンターを用いてQRコード(登録商標)を印字した後、ウレタン系ドライラミネート接着剤3.0g/m2を介して低密度ポリエチレン60μmを全面にラミネートしたものである。 In Comparative Example 1, after printing on the back surface of a biaxially stretched polyethylene terephthalate film having a thickness of 12 μm as a base material layer by a gravure printing method, black ink and then white ink were used as a concealing layer on a variable information printing portion. After applying a gravure coating method to form an ink receiving layer, and printing the QR code (registered trademark) using an ink jet printer on the ink receiving layer, it is reduced through a urethane dry laminate adhesive 3.0 g / m 2. A polyethylene film having a density of 60 μm is laminated on the entire surface.
比較例2は、基材層となる厚み12μmの二軸延伸ポリエチレンテレフタレートフィルムの裏面にグラビア印刷方式にて印刷加工を行った後、可変情報の印字部分に隠蔽層として墨色インキ、次いで白色インキを二層(二度刷)にグラビアコート法にて塗布してインキ受容層とし、該インキ受容層にインクジェットプリンターを用いてQRコード(登録商標)を印字した後、ウレタン系ドライラミネート接着剤3.0g/m2を介して低密度ポリエチレン60μmを全面にラミネートしたものである。 In Comparative Example 2, the back surface of a biaxially stretched polyethylene terephthalate film having a thickness of 12 μm serving as a base material layer was subjected to a printing process by a gravure printing method, and then black ink and then white ink was used as a concealing layer on a variable information printing portion. 2. Apply to two layers (twice printing) by gravure coating method to make an ink receiving layer, print QR code (registered trademark) on the ink receiving layer using an ink jet printer, and then dry urethane-based laminate adhesive. This is a laminate of 60 μm of low density polyethylene over the entire surface through 0 g / m 2 .
上記で得られた実施例1、2および、比較例1、2の構成からなるフィルムについて、印字されたQRコード(登録商標)の読み取りを異なる会社の携帯電話を読み取り端末A、Bとして読み取りを行った評価結果を表1に示す。 For the films having the configurations of Examples 1 and 2 and Comparative Examples 1 and 2 obtained above, the printed QR code (registered trademark) is read using a mobile phone of a different company as reading terminals A and B. The evaluation results are shown in Table 1.
上記の表1に示す読み取りの評価結果から明らかなように、実施例1、実施例2の構成からなるフィルムの印字については、読み取り端末A、Bのいずれによっても、良好に読み取ることができ、隠蔽層として設けたアルミニウム蒸着したポリエチレンテレフタレートフィルムが、印刷層を十分に隠蔽するとともに、インキ受容層のメジウムインキ及び白色インキと可変情報印字インキとのコントラストを明らかにして、読み取りが正確に行われた。これに対し、比較例1、2では、隠蔽層の墨色インキの発色が白色インキによって十分に隠し切れず、白色インキ層上に印字された可変情報の読み取りに時間を要したり、読み取りが出来ない結果となった。 As is clear from the reading evaluation results shown in Table 1 above, for the printing of the film comprising the configurations of Example 1 and Example 2, it can be read well by both reading terminals A and B, Aluminum-deposited polyethylene terephthalate film provided as a concealing layer sufficiently conceals the printed layer and reveals the contrast between the medium ink and white ink of the ink receiving layer and the variable information printing ink, so that reading is performed accurately. It was. On the other hand, in Comparative Examples 1 and 2, the color of the black ink in the hiding layer is not sufficiently hidden by the white ink, and it takes time to read the variable information printed on the white ink layer. No results.
P 包装袋
S 包装材
Q 内容物
1 基材層
2、2’ 接着層
3 隠蔽層
4 熱接着性樹脂層
5 印刷層
6 インキ受容層
7 可変情報印字層
P Packaging bag S Packaging
Claims (6)