JP5419337B2 - Nematic liquid crystalline organic semiconductor materials - Google Patents
Nematic liquid crystalline organic semiconductor materials Download PDFInfo
- Publication number
- JP5419337B2 JP5419337B2 JP2007258060A JP2007258060A JP5419337B2 JP 5419337 B2 JP5419337 B2 JP 5419337B2 JP 2007258060 A JP2007258060 A JP 2007258060A JP 2007258060 A JP2007258060 A JP 2007258060A JP 5419337 B2 JP5419337 B2 JP 5419337B2
- Authority
- JP
- Japan
- Prior art keywords
- organic semiconductor
- liquid crystal
- phase
- group
- mobility
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、液晶性を示す有機半導体材料に関し、特に、光学的に均一な大面積の材料の形成が可能で、かつ、分子配向による高い移動度と流動性を併せ持つネマティック液晶性を示す新しい有機半導体材料の実現方法、有機半導体構造物に関するものである。 The present invention relates to an organic semiconductor material exhibiting liquid crystallinity, and in particular, a new organic material capable of forming an optically uniform large-area material and exhibiting nematic liquid crystallinity having both high mobility and fluidity due to molecular orientation. The present invention relates to a method for realizing a semiconductor material and an organic semiconductor structure.
近年、低コスト、軽量、衝撃に対する信頼性などの点から、有機半導体層を電気的な活性層に用いた有機半導体デバイスが注目され、有機トランジスタ、光センサ、有機発光素子、太陽電池などの開発が進められている。これらのデバイスの有機半導体材料には、一般には、非液晶性の有機半導体材料のアモルファス薄膜や多結晶薄膜が用いられている。In recent years, organic semiconductor devices using an organic semiconductor layer as an electrically active layer have attracted attention in terms of low cost, light weight, and reliability against impact, and development of organic transistors, optical sensors, organic light emitting elements, solar cells, etc. Is underway. As the organic semiconductor material of these devices, an amorphous thin film or a polycrystalline thin film of a non-liquid crystalline organic semiconductor material is generally used.
１９９０年代になって、コア部に芳香族系部位をもつ、カラム状の分子凝集体を形成するディスコティック液晶や層状の凝集体を形成するスメクティック液晶物質が従来、広く有機半導体として用いられてきたアモルファス有機半導体が示す移動度をはるかに上回る、電子や正孔による高速の伝導を示すことが見出されて以来、これらの液晶物質が高品質な有機半導体となりうることが認識され、有機半導体部材への適用も検討されはじめた。
しかしながら、よく知られているように、これらの液晶物質では広い面積にわたって、単一の分子配向をもつドメインからなる液晶相を形成することは困難であるため、ドメインごとに分子配向が異なるポリドメイン構造を用いてデバイスの作製が行なわれている。このため、作製されるデバイスは光学的には不均一で、偏光を取り扱う光学的に活性なデバイスの作製に適用するとは不向きであった。However, as is well known, it is difficult for these liquid crystal materials to form a liquid crystal phase composed of domains having a single molecular orientation over a wide area. Devices are fabricated using the structure. For this reason, the device to be produced is optically non-uniform, and is not suitable for application to the production of an optically active device that handles polarized light.
この問題を解決するための手段として、単一な分子配向を実現しやすいネマティック液晶物質、中でも、分子配向が容易な低分子量のネマティックを有機半導体として用いることが有効である。しかし、
本発明は、上記要請に基づいてなされたもので、従来、有機半導体として用いることができなかった、芳香族低分子ネマティック液晶物質を有機半導体として液晶相において電子デバイスに適用可能にするための方法を提供することにある。また、そうした方法によって形成された有機半導体構造物を提供することにある。 The present invention has been made based on the above requirements, and a method for making an aromatic low-molecular nematic liquid crystal substance applicable to an electronic device in a liquid crystal phase as an organic semiconductor, which could not be conventionally used as an organic semiconductor. Is to provide. Another object of the present invention is to provide an organic semiconductor structure formed by such a method.
芳香族π−電子共役系をコア部にもつ低分子ネマティック液晶物質の電気伝導は、古くからイオン伝導によるもの考えられてきた
本発明者らは低分子ネマティック液晶物質の電荷輸送特性の関する詳細な検討から、イオン伝導が液晶物質の本来の性質によるものではなく、合成等の際に外的に混入した電荷のトラップとなるような不純物がイオン化して、粘性の低いネマティック液晶物質中を泳動することによる起こる現象であることが明らかにした。From the detailed examination of the charge transport property of the low molecular weight nematic liquid crystal material, the present inventors do not depend on the original property of the liquid crystal material, but serve as a trap for externally mixed charges during synthesis or the like. It has been clarified that this is a phenomenon that occurs when such impurities are ionized and migrate in a nematic liquid crystal material with low viscosity.
本発明は、上記、発見に基づいて、低分子ネマティック液晶物質に含まれる不純物の低減することにより、本来、ネマティック液晶物質が示す電子伝導特性を実現する方法を明らかにし、必要となる精製の目安を与えることにより、上記課題を解決する。Based on the above findings, the present invention has clarified a method for realizing the electron conduction characteristics inherent in the nematic liquid crystal material by reducing impurities contained in the low-molecular nematic liquid crystal material, and a necessary standard for purification. To solve the above problem.
具体的には、カラムクロマトグラフィー、再結晶、蒸留などの通常の有機合成的手段や、昇華などの物理的手段、あるいは、それらを組み合わせて用いることによって精製し、有機半導体としての利用を可能にする純度を測定による評価によって保障するものである。Specifically, it can be purified by using ordinary organic synthetic means such as column chromatography, recrystallization and distillation, physical means such as sublimation, or a combination thereof, and can be used as an organic semiconductor. The purity is guaranteed by evaluation by measurement.
目安となる純度は、液晶セルにつめた低分子ネマティック液晶物質を試料として、Ｔｉｍｅ−ｏｆ−ｆｌｉｇｈｔ（ＴＯＦ）法による過渡光電流の測定を行い、電荷の走行時間から、移動度が１０−４ｃｍ２／Ｖｓ以上の値を持つことを確認すること、次に、同一の低分子ネマティック液晶物質を蒸留によって精製した低粘度の炭化水素系の溶媒、例えばｎ−ヘキサン、ｎ−ヘプタン、ｎ−オクタン、ｎ−ノナン、ｎ−デカン、ｎ−ウンデカン、ｎ−ドデカン、ｎ−テトラデカン、ｎ−ペンタデカン、ｎ−ヘキサデカン、ｎ−ヘプタデカン、ｎ−オクタデカンなどを用いて相分離が起きない濃度に希釈したサンプルを液晶セルにつめ、同様に、Ｔｉｍｅ−ｏｆ−ｆｌｉｇｈｔ（ＴＯＦ）法による過渡光電流の測定を行うことによって、電荷の走行時間から求めた移動度が減少することを確認することによって、有機半導体としての利用が可能に十分な純度を保証することができる。The purity as a standard is measured by measuring the transient photocurrent by Time-of-flight (TOF) method using a low molecular weight nematic liquid crystal material packed in a liquid crystal cell as a sample, and the mobility is 10 −4 from the transit time of the charge. confirming that it has a value of cm 2 / Vs or higher, and then a low-viscosity hydrocarbon solvent obtained by purifying the same low-molecular nematic liquid crystal material by distillation, such as n-hexane, n-heptane, n- Diluted to a concentration at which phase separation does not occur using octane, n-nonane, n-decane, n-undecane, n-dodecane, n-tetradecane, n-pentadecane, n-hexadecane, n-heptadecane, n-octadecane, etc. The sample is packed in a liquid crystal cell, and similarly, the transient photocurrent is measured by the Time-of-flight (TOF) method, whereby the charge is By confirming that the mobility calculated | required from the driving | running | working time decreases, sufficient purity which can be utilized as an organic semiconductor can be ensured.
上記目的を達成するための本発明の第１形態に係る液晶性有機化合物は、下記化学式１のＬ個の６π電子系芳香環、Ｍ個の１０π電子系芳香環、Ｎ個の１４π電子系芳香環（ただし、Ｌ、Ｍ、Ｎはそれぞれ０〜４の整数を表わし、Ｌ＋Ｍ＋Ｎ＝１〜４とする。）を含む骨格構造を有し、当該骨格構造の末端に液晶性を発現する末端構造を有する棒状分子の有機半導体材料（Ｚ１）であり、下記化学式１中にＺ１として含まれることを特徴とする有機化合物。 In order to achieve the above object, the liquid crystalline organic compound according to the first embodiment of the present invention comprises L 6π-electron aromatic rings, M 10π-electron aromatic rings, and N 14π-electron aromatics represented by the following
この発明の液晶性有機化合物は、スメクティック液晶相（以下、Ｓｍ相）を利用していたことに加えて、低分子の液晶物質のネマティック液晶相（以下Ｎ相）も液晶相の電子伝導を使用した電荷輸送を実現する液晶性有機化合物を提供することを特徴とすることにより、高い電荷移動度の発現を可能にするＮ相を利用した液晶性有機化合物、及びその液晶性有機化合物を有する有機半導体構造物及び有機半導体装置、及びネマティック相を有する液晶性有機化合物の純度の評価方法を提供することにある。 The liquid crystalline organic compound of the present invention uses a smectic liquid crystal phase (hereinafter referred to as Sm phase), and the nematic liquid crystal phase (hereinafter referred to as N phase) of a low-molecular liquid crystal material also uses electronic conduction of the liquid crystal phase. The present invention provides a liquid crystalline organic compound that realizes the charge transport, and a liquid crystalline organic compound using an N phase that enables high charge mobility, and an organic having the liquid crystalline organic compound An object of the present invention is to provide a semiconductor structure, an organic semiconductor device, and a method for evaluating the purity of a liquid crystalline organic compound having a nematic phase.
上記目的を達成するための本発明の第２形態に係る液晶性有機化合物は、下記化学式２のＬ個の６π電子系芳香環、Ｍ個の１０π電子系芳香環、Ｎ個の１４π電子系芳香環（ただし、Ｌ、Ｍ、Ｎはそれぞれ０〜４の整数を表わし、Ｌ＋Ｍ＋Ｎ＝１〜４とする。）を含む骨格構造を有し、当該骨格構造の末端に液晶性を発現する末端構造を有する棒状分子の有機半導体材料（Ｚ１）であり、下記化学式２中にＺ１、Ｚ２として含まれることを特徴とする有機化合物。 In order to achieve the above object, the liquid crystalline organic compound according to the second embodiment of the present invention includes L 6π-electron aromatic rings, M 10π-electron aromatic rings, and N 14π-electron aromatic compounds represented by the following
本発明の液晶性有機化合物は、上記第１ないし第２形態に係る本発明のＮ相を有する液晶性有機化合物において、熱分解温度以下の温度において、少なくとも一種類のネマティック液晶相状態を有することを特徴とする。 The liquid crystalline organic compound of the present invention has at least one nematic liquid crystal phase state at a temperature equal to or lower than the thermal decomposition temperature in the liquid crystalline organic compound having the N phase of the present invention according to the first to second embodiments. It is characterized by.
この発明によれば、熱分解温度以下の温度で少なくとも一種類のＮ相液晶相状態を有するので、（ｉ）Ｎ相以外のＳｍ相とを組み合わせることも可能となり広い面積で均一且つ柔軟な分子配向薄膜を形成することが可能となる。（ｉｉ）加えて、本発明においては必ずしもＳｍ相を発現する必要がなく、Ｓｍ相以外にＮ相も利用できるため、合成の幅や材料の骨格も拡張できる。（ｉｉｉ）更に、Ｎ相で電子伝導が観測できるということは、純度が高いことを意味しており、Ｎ相の発現する有機材料の純度の評価が可能となる。 According to the present invention, since it has at least one N-phase liquid crystal phase state at a temperature equal to or lower than the thermal decomposition temperature, (i) it is possible to combine with an Sm phase other than the N phase, and a uniform and flexible molecule in a wide area. An oriented thin film can be formed. (Ii) In addition, in the present invention, it is not always necessary to develop the Sm phase, and since the N phase can be used in addition to the Sm phase, the synthesis width and the skeleton of the material can be expanded. (Iii) Furthermore, the fact that the electron conduction can be observed in the N phase means that the purity is high, and the purity of the organic material in which the N phase appears can be evaluated.
上記目的を達成する本発明の有機半導体構造物は、上記本発明の液晶性有機化合物からなる有機半導体層を有する有機半導体構造物であって、前記液晶性有機化合物が、熱分解温度以下の温度において、少なくとも一種類のネマティック液晶相状態を有し、前記有機半導体層が電子移動度１．０×１０−４ｃｍ２／Ｖ・ｓ以上、又は、正孔輸送移動度１．０×１０−４ｃｍ２／Ｖ・ｓ以上であることを特徴とする。The organic semiconductor structure of the present invention that achieves the above object is an organic semiconductor structure having an organic semiconductor layer comprising the liquid crystalline organic compound of the present invention, wherein the liquid crystalline organic compound has a temperature equal to or lower than a thermal decomposition temperature. The organic semiconductor layer has an electron mobility of 1.0 × 10 −4 cm 2 / V · s or higher, or a hole transport mobility of 1.0 × 10 −. It is characterized by being 4 cm 2 / V · s or more.
この発明によれば、有機半導体層を形成するための液晶性有機化合物が熱分解温度以下の温度において、少なくとも一種類のネマティック液晶相状態を有するので、広い面積で均一且つ柔軟な分子配向薄膜を形成することが可能となり、各種光センサ、有機ＥＬ素子、太陽電池やフレキシブルディスプレイ装置等に利用可能な薄膜トランジスタ等のデバイスに応用することができる。 According to the present invention, the liquid crystalline organic compound for forming the organic semiconductor layer has at least one nematic liquid crystal phase state at a temperature equal to or lower than the thermal decomposition temperature. It can be formed, and can be applied to devices such as thin film transistors that can be used for various optical sensors, organic EL elements, solar cells, flexible display devices, and the like.
上記目的を達成する本発明の有機半導体装置は、少なくとも基板、ゲート電極、ゲート絶縁層、有機半導体層、ドレイン電極、及びソース電極を有する有機半導体装置、あるいは、少なくとも、基板、一対の電極、有機半導体層からなるを有する有機半導体装置、であって、前記有機半導体層が、請求項１〜３のいずれか１項に記載の液晶性有機化合物で形成されていることを特徴とする。 An organic semiconductor device of the present invention that achieves the above object is an organic semiconductor device having at least a substrate, a gate electrode, a gate insulating layer, an organic semiconductor layer, a drain electrode, and a source electrode, or at least a substrate, a pair of electrodes, and an organic An organic semiconductor device comprising a semiconductor layer, wherein the organic semiconductor layer is formed of the liquid crystalline organic compound according to
Ｓｍ相以外にＮ相でも高移動度電子伝導発現する液晶性有機化合物を利用することにより、今まで液晶状態の利用範囲がＳｍ相に限定されてたがＮ相にまで拡張可能であり、より広範囲の液晶化温度範囲で利用可能であること。これにより、従来Ｓｍ相に限定されていた液晶状態をＮ相にまで拡張することにより、液晶状態を最大限に生かすことができる。 By using a liquid crystalline organic compound that exhibits high mobility electron conduction even in the N phase in addition to the Sm phase, the use range of the liquid crystal state has been limited to the Sm phase, but can be extended to the N phase. It can be used in a wide range of liquid crystal temperatures. As a result, the liquid crystal state can be maximized by expanding the liquid crystal state that has been conventionally limited to the Sm phase to the N phase.
本発明における有機化合物においては、必ずしもＳｍ相を発現する必要がなく、Ｓｍ相以外にＮ相が利用できるために（Ｎ相さえが発現すれば良い）合成のバリエーションや液晶性有機化合物の骨格も拡張できること。これにより、従来は電荷輸送に不利であったＮ相を発現させにくくするために、Ｓｍ相を優先的に発現させるために、液晶材料のコア部（化学式１のＺ１、化学式２のＺ１、Ｚ２）のアルキル鎖を調節する必要があったが、本発明によりＮ相を発現させるために側鎖のディスオーダーを大きくさせる要因となる短いアルキル基（化学式１のＲ１、Ｒ２、化学式２のＲ１、Ｒ２）の長さが短くても良く、合成のバリエーションや液晶性有機化合物の骨格も拡張が可能となる。 In the organic compound of the present invention, it is not always necessary to develop the Sm phase, and since the N phase can be used in addition to the Sm phase (only the N phase needs to be developed), there are variations in synthesis and the skeleton of the liquid crystalline organic compound. It can be expanded. Accordingly, in order to make it difficult to express the N phase, which has been disadvantageous for charge transport in the past, in order to preferentially express the Sm phase, the core portion of the liquid crystal material (Z1 in
低分子液晶物質のＮ相での電荷輸送は、本質的にイオン伝導が起こるものと考えられてきたが、そのイオン伝導は、▲１▼液晶物質に含まれる不純物による外因的なイオン伝導であり、▲２▼高純度の物質においては本質的に電子伝導が起こるものと結論される。そのため、Ｎ相を有する有機材料の純度の評価が可能となる。 The charge transport in the N phase of low-molecular liquid crystal materials has been considered to cause ionic conduction essentially, but the ionic conduction is (1) extrinsic ionic conduction by impurities contained in the liquid crystal material. (2) It is concluded that electron conduction essentially occurs in high-purity materials. Therefore, the purity of the organic material having an N phase can be evaluated.
一般的に精製が十分でない液晶物質では、電子伝導とイオン伝導の共存が見られる。 In general, liquid crystal substances that are not sufficiently purified exhibit coexistence of electron conduction and ion conduction.
ここで言うイオン伝導とは、伝導に関わるイオン種は必ずしもイオン性物貢の解離によって生じたイオン種に限られるものではなく、もともと電荷をもたない非イオン性の不純物が正孔や電子を捕獲したり、光イオン化によって生じた不純物イオンもイオンとして同様に伝導に寄与する。すなわち、液晶物質に電子や正孔のトラップとなる不純物が含まれる場合は、イオン化した不純物は前述のイオン伝導チャネルを介して輸送され、イオン伝導を誘起する。 Ion conduction here means that the ionic species involved in conduction are not necessarily limited to ionic species generated by dissociation of ionic contributors. Impurity ions that are trapped or generated by photoionization also contribute to conduction as ions. That is, in the case where the liquid crystal substance contains impurities that serve as traps for electrons and holes, the ionized impurities are transported through the above-described ion conduction channel and induce ion conduction.
イオン伝導は、一般に、粘性の小さな媒質の中で起こりやすいため、液晶相の中でも、粘性の低いＮ相、ＳｍＡ相、ＳｍＣでは、特に、イオン伝導が起こりやすく、実際にこの場合、ＴＯＦ法による過渡光電流の測定を利用すると、含まれる不純物濃度が０．１ｐｐｍ程度の微量であっても、イオン伝導を観測することができる。数十ｐｐｍ程度を超える不純物が含まれる場合は、電子伝導は完全に消失し、イオン伝導しか観測されなくなる。そのため、従来のＮ相での電荷輸送はこのイオン伝導であるため、Ｎ相で電子伝導が観測できるということは、液晶性有機化合物は純度が高いために、Ｎ相の発現する有機材料の純度の評価が可能なことを提供できる。 In general, ionic conduction is likely to occur in a medium having a small viscosity. Therefore, in the liquid crystal phase, especially in the N-phase, SmA phase, and SmC having a low viscosity, ionic conduction is likely to occur. When the measurement of transient photocurrent is used, ionic conduction can be observed even if the concentration of impurities contained is as small as about 0.1 ppm. When impurities exceeding about several tens of ppm are included, the electron conduction completely disappears and only ionic conduction is observed. Therefore, since the conventional charge transport in the N phase is this ionic conduction, the fact that the electron conduction can be observed in the N phase means that the liquid crystalline organic compound has a high purity, and therefore the purity of the organic material that the N phase develops. It can provide that it is possible to evaluate.
本発明による低分子ネマティック液晶物質の有機半導体としての適用化は、上記、従来のネマティック液晶物質の有機半導体としての利用を可能にする方法と異なり、高分子化やガラス化によりネマティック液晶物質の固体化や、あるいは、π−電子共役系のサイズの拡大などの分子設計に基づいた材料技術によるのではなく、精製とその精製の目安を評価によって保障するもので、芳香族ネマティック液晶物質であれば、どのような液晶物質であっても、有機半導体として用いることを原理的に可能にするもので、材料面から見ると、特定の低分子ネマティック液晶物質に限られるものではなく、極めて広範な液晶物質を有機半導体としての利用を可能にする。The application of the low molecular weight nematic liquid crystal material as an organic semiconductor according to the present invention is different from the above-described method that enables the use of the nematic liquid crystal material as an organic semiconductor, and the solid state of the nematic liquid crystal material by polymerizing or vitrifying. Rather than relying on material technology based on molecular design such as conversion or enlargement of the size of the π-electron conjugated system, it is guaranteed by the evaluation of the purification and the standard of purification, if it is an aromatic nematic liquid crystal substance Any liquid crystal substance can be used in principle as an organic semiconductor. From the viewpoint of materials, it is not limited to a specific low-molecular nematic liquid crystal substance. The substance can be used as an organic semiconductor.
本発明の液晶性有機化合物によれば、Ｌ個の６π電子系芳香環、Ｍ個の１０π電子系芳香環、Ｎ個の１４π電子系芳香環（ただし、Ｌ、Ｍ、Ｎはそれぞれ０〜４の整数を表わし、Ｌ＋Ｍ＋Ｎ＝１〜４とする。）を含む骨格構造を有し、当該骨格構造の末端に液晶性を発現する末端構造を有する棒状分子の有機半導体材料（Ｚ１）であり、下記化学式２中にＺ１、Ｚ２として含まれることを特徴とする化学構造を持つ。 According to the liquid crystalline organic compound of the present invention, L 6π-electron aromatic rings, M 10π-electron aromatic rings, and N 14π-electron aromatic rings (where L, M, and N are each 0-4). Is an organic semiconductor material (Z1) of a rod-like molecule having a skeleton structure including L + M + N = 1 to 4 and having a terminal structure that exhibits liquid crystallinity at the terminal of the skeleton structure. It has a chemical structure characterized by being contained as Z1 and Z2 in
本発明の有機半導体構造物及び有機半導体装置によれば、有機半導体層を本発明に係る液晶性有機化合物で形成するので、広い面積で均一且つ柔軟な有機半導体薄膜を形成することが可能となり、フレキシブルディスプレイ装置等に利用可能な薄膜トランジスタ等のデバイスに応用することができる。 According to the organic semiconductor structure and the organic semiconductor device of the present invention, since the organic semiconductor layer is formed of the liquid crystalline organic compound according to the present invention, it becomes possible to form a uniform and flexible organic semiconductor thin film over a wide area, The present invention can be applied to a device such as a thin film transistor that can be used for a flexible display device or the like.
本発明の液晶性有機化合物の製造方法によれば、電荷移動度を低下させる原因となる不純物を効果的に除去することができるので、この発明の液晶性有機化合物は、熱分解温度以下の温度で少なくとも一種類のＮ相液晶相状態を有する高い電荷移動度の発現を可能にする液晶性有機化合物を効率的に製造することができる。 According to the method for producing a liquid crystalline organic compound of the present invention, impurities that cause a decrease in charge mobility can be effectively removed. Therefore, the liquid crystalline organic compound of the present invention has a temperature equal to or lower than the thermal decomposition temperature. Thus, it is possible to efficiently produce a liquid crystalline organic compound that can exhibit high charge mobility having at least one N-phase liquid crystal phase state.
以下、本発明の液晶性有機化合物及びその製造方法について詳しく説明する。 Hereinafter, the liquid crystalline organic compound of the present invention and the production method thereof will be described in detail.
（液晶性有機化合物）
本発明の有機半導体材料は、棒状の液晶材料であり、その骨格構造（コア構造ともいう。）は、Ｌ個の６π電子系芳香環、Ｍ個の１０π電子系芳香環、Ｎ個の１４π電子系芳香環（ただし、Ｌ、Ｍ、Ｎはそれぞれ０〜４の整数を表わし、Ｌ＋Ｍ＋Ｎ＝１〜４とする。）を含み、その骨格構造の末端に液晶性を発現する末端構造（ターミナルグループともいう。）を有するものである。(Liquid crystalline organic compounds)
The organic semiconductor material of the present invention is a rod-like liquid crystal material, and its skeleton structure (also referred to as a core structure) has L 6π electron aromatic rings, M 10π electron aromatic rings, and N 14π electrons. A terminal structure that expresses liquid crystallinity at the end of its skeletal structure, including L-type aromatic rings (where L, M, and N each represent an integer of 0 to 4, and L + M + N = 1 to 4) Say).
骨格構造を構成する６π電子系芳香環としては、例えば、ベンゼン環、ピリジン環ピリミジン環、ピリダジン環、ピラジン環、トロポロン環等を挙げることができ、１０π電子系芳香環としては、例えば、ナフタレン環、アズレン環、ベンゾフラン環、インドール環、イミダゾール環、ベンゾチアゾール環、ベンゾオキサゾール環、ベンゾイミダゾール環、キノリン環、イソキノリン環、キナゾリン環、キノキサリン環等を挙げることができ、１４π電子系芳香環としては、例えば、フェナントレン環、アントラセン環等を挙げることができる。こうした骨格構造を有する化合物は、
この第１形態に係る液晶性有機化合物においては下記化学式１のＬ個の６π電子系芳香環、Ｍ個の１０π電子系芳香環、Ｎ個の１４π電子系芳香環（ただし、Ｌ、Ｍ、Ｎはそれぞれ０〜４の整数を表わし、Ｌ＋Ｍ＋Ｎ＝１〜４とする。）を含む骨格構造を有し、当該骨格構造の末端に液晶性を発現する末端構造を有する棒状分子の有機半導体材料（Ｚ１）であり、下記化学式１中にＺ１として含まれることを特徴とする有機化合物である。In the liquid crystalline organic compound according to the first embodiment, L 6π-electron aromatic rings, M 10π-electron aromatic rings, and N 14π-electron aromatic rings represented by the following chemical formula 1 (note that L, M, N Each represents an integer of 0 to 4, L + M + N = 1 to 4), and a rod-shaped organic semiconductor material (Z1) having a terminal structure that exhibits liquid crystallinity at the terminal of the skeleton structure. It is an organic compound characterized by being included as Z1 in the following
（化学式３において、Ｒ１とＲ２は、それぞれ独立に炭素数０〜２２の直鎖、分岐鎖又は環状構造を有する飽和又は不飽和炭化水素であり、化学式１の骨格構造のいずれかの部位に結合していることを特徴とし、Ｙ１又はＹ２を介さずにＺ１に結合してもよい。Ｙ１とＹ２は、酸素原子、硫黄原子、セレン原子、−ＣＯ−基、−ＯＣＯ−基、−ＣＯＯ−基、−Ｎ＝ＣＨ−基、−ＣＯＮＨ−基、−ＮＨ−基、−ＮＨＣＯＯ−基及び−ＣＨ２−基から選ばれる。）(In Chemical Formula 3, R1 and R2 are each independently a saturated or unsaturated hydrocarbon having a linear, branched or cyclic structure having 0 to 22 carbon atoms and bonded to any part of the skeleton structure of
また、本発明の第２形態に係る液晶性有機化合物は、下記化学式４のＬ個の６π電子系芳香環、Ｍ個の１０π電子系芳香環、Ｎ個の１４π電子系芳香環（ただし、Ｌ、Ｍ、Ｎはそれぞれ０〜４の整数を表わし、Ｌ＋Ｍ＋Ｎ＝１〜４とする。）を含む骨格構造を有し、当該骨格構造の末端に液晶性を発現する末端構造を有する棒状分子の有機半導体材料であり、下記化学式２中にＺ１、Ｚ２として含まれることを特徴とする有機化合物である。 In addition, the liquid crystalline organic compound according to the second embodiment of the present invention includes L 6π-electron aromatic rings, M 10π-electron aromatic rings, and N 14π-electron aromatic rings (provided that L 4 , M, and N each represents an integer of 0 to 4, and L + M + N = 1 to 4.), and a rod-like organic molecule having a terminal structure that exhibits liquid crystallinity at the terminal of the skeleton structure. It is a semiconductor material and is an organic compound characterized by being contained as Z1 and Z2 in the following
（化学式４において、Ｒ１とＲ２は、炭素数０〜２２の直鎖、分岐鎖又は環状構造を有する飽和又は不飽和炭化水素であり、化学式２の骨格構造のいずれかの部位に結合していることを特徴とし、Ｒ１とＲ２は、Ｙ１又はＹ２を介さずにＺ１、Ｚ２に結合してもよい。Ｙ１とＹ２は、酸素原子、硫黄原子、セレン原子、−ＣＯ−基、−ＯＣＯ−基、−ＣＯＯ−基、−Ｎ＝ＣＨ−基、−ＣＯＮＨ−基、−ＮＨ−基、−ＮＨＣＯＯ−基及び−ＣＨ２−基から選ばれる。Ｘは、炭素数１〜２２の直鎖、分岐鎖又は環状構造を有する飽和又は不飽和炭化水素であってもよいし、又は、Ｘは存在せずに直接Ｚ１とＺ２とが結合していてもよい。ｎ＝１以上の整数を表す。Ｚ１とＺ２は同じＬ個の６π電子系芳香環、Ｍ個の１０π電子系芳香環、Ｎ個の１４π電子系芳香環（ただし、Ｌ、Ｍ、Ｎはそれぞれ０〜４の整数を表わし、Ｌ＋Ｍ＋Ｎ＝１〜４とする。）を含む骨格構造または、異なるＬ個の６π電子系芳香環、Ｍ個の１０π電子系芳香環、Ｎ個の１４π電子系芳香環（ただし、Ｌ、Ｍ、Ｎはそれぞれ０〜４の整数を表わし、Ｌ＋Ｍ＋Ｎ＝１〜４とする。）を含む骨格構造でも良い。）である。(In Chemical Formula 4, R1 and R2 are saturated or unsaturated hydrocarbons having a linear, branched or cyclic structure having 0 to 22 carbon atoms, and are bonded to any part of the skeleton structure of
上述した第１形態及び第２形態に係る液晶性有機化合物において、Ｒ１、Ｒ２は、炭素数が０〜１５の直鎖、分岐鎖又は環状構造を有する飽和又は不飽和炭化水素であることが好ましい。炭素数が０〜１５のＲ１、Ｒ２を有する液晶性有機化合物は、液晶相（Ｎ相、Ｓｍ相）を発現し易く、且つ液晶化温度範囲を広くすることができるという利点がある。炭素数が、１５以上であると溶解性が悪くなり精製が困難になり易い、液晶化温度が高くなりすぎ、熱分解の恐れが生じるので好ましくない。 In the liquid crystalline organic compounds according to the first and second embodiments described above, R1 and R2 are preferably saturated or unsaturated hydrocarbons having a linear, branched or cyclic structure having 0 to 15 carbon atoms. . The liquid crystalline organic compound having R1 and R2 having 0 to 15 carbon atoms has an advantage that a liquid crystal phase (N phase, Sm phase) is easily developed and a liquid crystallizing temperature range can be widened. If the number of carbon atoms is 15 or more, the solubility tends to be poor and purification becomes difficult, the liquid crystallizing temperature becomes too high, and thermal decomposition may occur, which is not preferable.
炭素数１〜２２の直鎖、分岐鎖又は環状構造を有する飽和又は不飽和炭化水素の具体例としては、メチル、エチル、プロピル、イソプロピル、ブチル、イソブチル、ｔｅｒｔ−ブチル、ペンチル、ヘキシル、ヘプチル、オクチル、ノニル、デシル、ウンデシル、ドデシル、トリデシル、テトラデシル、ペンタデシル、ヘキサデシル、ヘプタデシル、オクタデシル、ノナデシル、イコシル、エイコシル、ヘンイコシル、ヘンエイコシル、ドコシル、エテン、プロペン、ブテン、ペンテン、ヘキセン、ヘプテン、オクテン、ノネン、デセン、ウンデセン、ドデセン、トリデセン、テトラデセン、ペンタデセン、ヘキサデセン、ヘプタデセン、オクタデセン、ノナデセン、イコセン、エイコセン、ヘンイコセン、ヘンエイコセン、ドコセン、エチン、プロピン、ブチン、ペンチン、ヘキシン、ヘプチン、オクチン、ノニン、デシン、ウンデシン、ドデシン、トリデシン、テトラデシン、ヘンタデシン、ヘキサデシン、ヘプタデシン、オクタデシン、ノナデシン、イコシン、エイコシン、ヘンイコシン、ヘンエイコシン、ドコシン、シクロペンチル、シクロヘキシル、シクロヘプチル等を挙げることができる。また、好ましく用いられる炭素数８〜１５の直鎖、分岐鎖又は環状構造を有する飽和又は不飽和炭化水素の具体例としては、オクチル、ノニル、デシル、ウンデシル、ドデシル、トリデシル、テトラデシル、ペンタデシル、ペンテン、ヘキセン、ヘプテン、オクテン、ノネン、デセン、ウンデセン、ドデセン、トリデセン、プロピン、ブチン、ペンチン、ヘキシン、ヘプチン、オクチン、ノニン、デシン、ウンデシン、ドデシン、トリデシン、テトラデシン、ペンタデシン、シクロペンチル、シクロヘキシル、シクロヘプチル等を挙げることができる。 Specific examples of the saturated or unsaturated hydrocarbon having a linear, branched or cyclic structure having 1 to 22 carbon atoms include methyl, ethyl, propyl, isopropyl, butyl, isobutyl, tert-butyl, pentyl, hexyl, heptyl, Octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, octadecyl, nonadecyl, icosyl, eicosyl, henicosyl, heneicosyl, docosyl, ethene, propene, butene, pentene, hexene, heptene, octene, nonene Decene, undecene, dodecene, tridecene, tetradecene, pentadecene, hexadecene, heptadecene, octadecene, nonadecene, icosene, eicosene, heicoscene, heneicosene, docosene, ethyne Propyne, butyne, pentyne, hexyne, heptine, octyne, nonine, decine, undecine, dodecin, tridecine, tetradecin, gentadecin, hexadecine, heptadecin, octadecin, nonadecin, icosine, eicosin, henicosin, heneicosin, docosin, cyclopentyl, cyclohexyl, cyclohexyl Etc. Specific examples of the saturated or unsaturated hydrocarbon having a straight chain, branched chain or cyclic structure having 8 to 15 carbon atoms preferably used include octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, pentene. , Hexene, heptene, octene, nonene, decene, undecene, dodecene, tridecene, propyne, butyne, pentine, hexyne, heptine, octyne, nonine, decyne, undecine, dodecin, tridecine, tetradecine, pentadecine, cyclopentyl, cyclohexyl, cycloheptyl, etc. Can be mentioned.
上述した第１形態及び第２形態に係る液晶性有機化合物において、Ｙ１及びＹ２が、酸素原子、硫黄原子、−ＣＯ−基、−ＯＣＯ−基、−ＣＯＯ−基、−Ｎ＝ＣＨ−基、−ＣＯＮＨ−基、−ＮＨ−基、−ＮＨＣＯＯ−基及び−ＣＨ２−基から選ばれることが、化学的な安定性の点で好ましく、酸素原子、−ＣＯ−基、−ＯＣＯ−基、−ＣＯＯ−基、−ＣＨ２−基から選ばれることがより好ましい。In the liquid crystalline organic compounds according to the first and second embodiments described above, Y1 and Y2 are oxygen atom, sulfur atom, -CO- group, -OCO- group, -COO- group, -N = CH- group, From the viewpoint of chemical stability, it is preferably selected from —CONH— group, —NH— group, —NHCOO— group and —CH 2 — group, and includes oxygen atom, —CO— group, —OCO— group, — More preferably, it is selected from a COO— group and a —CH 2 — group.
本発明の液晶性有機化合物は、熱分解温度以下の温度において、少なくとも一種類のネマティック液晶相状態を有している。ここで、「熱分解温度以下の温度」とは、液晶性有機化合物がそれ自身熱分解されない温度条件の下で、の意味であり、具体的には、本発明の液晶性有機化合物は、２００℃以下の温度範囲で液晶相を呈することができる。なお、熱分解温度は本発明の技術的範囲に含まれる個々の液晶性有機化合物によって異なる。また、「少なくとも一種類のネマティック液晶相状態を有している」とは、本発明の液晶性有機化合物の熱分解温度以下の温度条件下（すなわち、ネマティック液晶相と複数の液晶相もしくは最低一種類のネマティック液晶相を持っている、という意味である。例えば、ネマティック（以下、Ｎともいう）、スメクティック（以下、Ｓｍともいう）液晶相としてはＳｍＡ相、ＳｍＢ相、ＳｍＣ相、…等々の複数種類の液晶状態が知られている。 The liquid crystalline organic compound of the present invention has at least one nematic liquid crystal phase state at a temperature equal to or lower than the thermal decomposition temperature. Here, the “temperature below the thermal decomposition temperature” means under the temperature condition where the liquid crystalline organic compound itself is not thermally decomposed. Specifically, the liquid crystalline organic compound of the present invention is 200 A liquid crystal phase can be exhibited in a temperature range of 0 ° C. or lower. The thermal decomposition temperature varies depending on individual liquid crystalline organic compounds included in the technical scope of the present invention. Further, “having at least one type of nematic liquid crystal phase” means that the temperature is lower than the thermal decomposition temperature of the liquid crystalline organic compound of the present invention (that is, a nematic liquid crystal phase and a plurality of liquid crystal phases or at least one liquid crystal phase). For example, nematic (hereinafter also referred to as N), smectic (hereinafter also referred to as Sm) liquid crystal phases such as SmA phase, SmB phase, SmC phase, etc. Multiple types of liquid crystal states are known.
液晶性有機化合物で形成される有機半導体層は、ホッピング伝導に基づいた高い電子と正孔についていずれも高速の電荷輸送能が発現する、という電荷移動特性を有している。この理由は以下のように考えられる。 An organic semiconductor layer formed of a liquid crystalline organic compound has a charge transfer characteristic that high-speed charge transport ability is exhibited for both high electrons and holes based on hopping conduction. The reason is considered as follows.
図１は、従来の液晶性有機化合物が自己組織化してなる有機半導体層の一例を示すモデル図である。 FIG. 1 is a model diagram showing an example of an organic semiconductor layer formed by self-organizing a conventional liquid crystalline organic compound.
図１より従来の液晶性有機化合物は、例えば２−（４′−ヘプチルオキシフェニル）−６−ドデシルチオベンゾチアゾール（以下、７Ｏ−ＰＢＴ−Ｓ１２と略記する）。７Ｏ−ＰＢＴ−Ｓ１２は、Ｃｒｙｓｔ３（結晶相３）６２℃ Ｃｒｙｓｔ２（結晶相２）７７℃ Ｃｒｙｓｔ１（結晶相１）８７．９℃ ＳｍＡ（スメクティックＡ相）９９．７℃ Ｉｓｏ（等方相）の相転移温度を示す液晶材料である（降温下５℃／ｍｉｎで測定）。また、本材料はＳｍＡで正孔は１×１０−４ｃｍ２／Ｖｓ、エレクトロンで１×１０−４ｃｍ２／Ｖｓの両極性の電子伝導が発現する。更に、Ｃｒｙｓｔ１においては、正孔で８×１０−３ｃｍ２／Ｖｓの電子伝導が発現する材料である。From FIG. 1, the conventional liquid crystalline organic compound is, for example, 2- (4′-heptyloxyphenyl) -6-dodecylthiobenzothiazole (hereinafter abbreviated as 7O-PBT-S12). 7O-PBT-S12 is composed of Cryst 3 (crystalline phase 3) 62 ° C. Cryst 2 (crystalline phase 2) 77 ° C. Cryst 1 (crystalline phase 1) 87.9 ° C. SmA (smectic A phase) 99.7 ° C. Iso (isotropic phase). It is a liquid crystal material exhibiting a phase transition temperature (measured at a temperature drop of 5 ° C./min). In addition, this material is SmA, positive holes are 1 × 10 −4 cm 2 / Vs, and electrons are 1 × 10 −4 cm 2 / Vs. Furthermore, Cryst1 is a material that exhibits electron conduction of 8 × 10 −3 cm 2 / Vs by holes.
本液晶材料は７Ｏ−ＰＢＴ−Ｓ１２では両側鎖の炭化水素直鎖、分岐鎖又は環状構造を有する飽和又は不飽和炭化水素であるアルキル鎖の存在（ロ）により自己組織化を起こし、極めて秩序的に配向する。有機半導体層には、そうした液晶性有機化合物により高い自己組織性を有した分子凝集部分である領域（イ）が形成される。その領域（イ）においては、液晶性有機化合物の剛直な骨格部位（上記の化学式１及び２におけるＺ１とＺ２）が、隣接する液晶性有機化合物と極めて小さな距離で隣接する。その結果、液晶性有機化合物の領域（イ）では、分子間のπ電子軌道の重なりが大きくなることにより、ホッピング伝導に基づいた高速の電子伝導と高速のホール伝導が起こるので、形成された有機半導体層は、高い電荷輸送特性を示すこととなる。なお、この場合における骨格同士の間隔は、０．３〜０．５ｎｍ程度である。 In 7O-PBT-S12, this liquid crystal material undergoes self-organization due to the presence (b) of an alkyl chain which is a saturated or unsaturated hydrocarbon having a hydrocarbon straight chain, branched chain or cyclic structure on both sides, and is extremely ordered. Oriented to In the organic semiconductor layer, a region (A) that is a molecular aggregation portion having high self-organization property is formed by such a liquid crystalline organic compound. In the region (a), the rigid skeleton portion of the liquid crystal organic compound (Z1 and Z2 in the
また、本発明のＮ相における電荷輸送においても、Ｎ相は１軸の分子配向をもつ凝集相であるが、配向秩序は一般に小さいため、平均的な分子間距離は７〜９Å程度となる。この値はＳｍ相における分子間距離３〜６Åに比べるとはるかに大きいものの、隣接する分子への電荷の移動は十分に起こりうる距離である。実際、固体のアモルファス物質中では分子間距離が１０Åを超える場合であっても電子伝導が観測される。よって高純度に精製した液晶材料のＮ相においては、上記のような伝導も十分に考えられる。 Also, in the charge transport in the N phase of the present invention, the N phase is an aggregated phase having a uniaxial molecular orientation, but since the orientation order is generally small, the average intermolecular distance is about 7 to 9 mm. Although this value is much larger than the intermolecular distance of 3 to 6 mm in the Sm phase, it is a distance at which charge transfer to adjacent molecules can occur sufficiently. In fact, in a solid amorphous material, electron conduction is observed even when the intermolecular distance exceeds 10 mm. Therefore, in the N phase of the liquid crystal material purified to a high purity, the above-described conduction is sufficiently considered.
これまでの例から見ると、液晶相における移動度が１０−３〜１０−４ｃｍ２／Ｖｓを超える場合は電子伝導と考えて良いが、一般に、移動度の値やその温度依存性のデータだけでは、観測された伝導がイオン伝導であるか、電子伝導であるかを判断することは難しい。実験的にこれを区別する最も簡便な方法は、炭化水素などの電子伝導に関わらない粘性の小さな液体を用いて液晶物質を希釈し、希釈前後での移動度を比較することである。電子伝導の場合は、希釈によって電荷の移動に関わる分子間距離が増大するため、移動度の減少が見られ、イオン伝導の場合は希釈による粘性の減少のために、移動度は増大することになる。In view of the examples so far, when the mobility in the liquid crystal phase exceeds 10 −3 to 10 −4 cm 2 / Vs, it may be considered as electron conduction. However, in general, the mobility value and the temperature dependency data thereof are used. By itself, it is difficult to determine whether the observed conduction is ionic conduction or electronic conduction. The simplest way to distinguish this experimentally is to dilute the liquid crystal substance with a liquid having a low viscosity not related to electron conduction, such as hydrocarbons, and compare the mobility before and after dilution. In the case of electron conduction, the intermolecular distance involved in charge transfer increases due to dilution, and thus a decrease in mobility is observed. In the case of ionic conduction, mobility increases due to a decrease in viscosity due to dilution. Become.
本発明で用いられる液晶性有機化合物は、例えば
本発明の液晶性有機化合物は、最終的に形成される有機半導体層に要求される特性を考慮して選定される。選定基準の特性としては、電子又は正孔の電荷移動度が最低でも１．０×１０−４ｃｍ２／Ｖ・ｓ以上である。ここでいう電荷移動度とは、単位電界、１秒あたりの電荷の移動速度のことをいい、Ｔｉｍｅ ｏｆ ｆｌｉｇｈｔ法（以下、ＴＯＦ法という）により測定できる。The liquid crystalline organic compound of the present invention is selected in consideration of characteristics required for the finally formed organic semiconductor layer. As a characteristic of selection criteria, the charge mobility of electrons or holes is at least 1.0 × 10 −4 cm 2 / V · s or more. The charge mobility here refers to the unit electric field, the charge transfer rate per second, and can be measured by the Time of flight method (hereinafter referred to as TOF method).
以上、本発明の液晶性有機化合物によれば、
（有機半導体構造物）
本発明の有機半導体構造物は、上記本発明の液晶性有機化合物からなる有機半導体層を有するものであり、その液晶性有機化合物が熱分解温度以下の温度で少なくとも一種類のネマティック液晶相状態を有し、有機半導体層が電子移動度１．０×１０−４ｃｍ２／Ｖ・ｓ以上、又は、正孔輸送移動度１．０×１０−４ｃｍ２／Ｖ・ｓ以上であることに特徴を有している。(Organic semiconductor structure)
The organic semiconductor structure of the present invention has an organic semiconductor layer composed of the liquid crystalline organic compound of the present invention, and the liquid crystalline organic compound exhibits at least one nematic liquid crystal phase state at a temperature not higher than the thermal decomposition temperature. And the organic semiconductor layer has an electron mobility of 1.0 × 10 −4 cm 2 / V · s or more, or a hole transport mobility of 1.0 × 10 −4 cm 2 / V · s or more. It has characteristics.
有機半導体層は、本発明の液晶性有機化合物を配向させることにより形成される。配向手段としては、液晶性有機化合物を、例えばポリイミド系材料からなる液晶配向層上に積層したり、微少な凹凸を表面に有した硬化性樹脂からなる液晶配向層上に積層したりすることにより行うことができる。 The organic semiconductor layer is formed by aligning the liquid crystalline organic compound of the present invention. As alignment means, for example, by laminating a liquid crystalline organic compound on a liquid crystal alignment layer made of, for example, a polyimide material, or on a liquid crystal alignment layer made of a curable resin having minute irregularities on the surface. It can be carried out.
上述した液晶性有機化合物は、液晶状態を維持する温度以上において流動性を有するので、その状態で塗布することができる。こうした方法によれば、優れた電荷移動特性を有する大面積の有機半導体層を極めて容易に形成することができる。このときの塗布方法としては、各種の塗布方法および印刷方法を適用できる。 Since the above-mentioned liquid crystalline organic compound has fluidity at a temperature higher than the temperature at which the liquid crystal state is maintained, it can be applied in that state. According to such a method, a large-area organic semiconductor layer having excellent charge transfer characteristics can be formed very easily. Various coating methods and printing methods can be applied as the coating method at this time.
本発明の有機半導体構造物は、第一の態様として基板、液晶配向層、有機半導体層を順次積層したものを挙げることができ、第二の態様として、基板、有機半導体層、液晶配向層を順次積層したものを挙げることができ、第三の態様として、基板、液晶配向層、有機半導体層、液晶配向層を順次積層したものを挙げることができる。本発明においては、有機半導体層を、配向処理を施した層と接する形態となるように構成することによって、液晶性有機化合物を構成する液晶相に高い配向性を付与することができる。 In the organic semiconductor structure of the present invention, the first embodiment can include a substrate, a liquid crystal alignment layer, and an organic semiconductor layer sequentially laminated. The second embodiment includes a substrate, an organic semiconductor layer, and a liquid crystal alignment layer. One that is sequentially laminated can be exemplified, and a third aspect is one in which a substrate, a liquid crystal alignment layer, an organic semiconductor layer, and a liquid crystal alignment layer are sequentially laminated. In the present invention, a high orientation can be imparted to the liquid crystal phase constituting the liquid crystalline organic compound by configuring the organic semiconductor layer so as to be in contact with the layer subjected to the alignment treatment.
以上説明したように、本発明の有機半導体構造物は、広い温度範囲で高次の液晶相を示す液晶性有機化合物からなる有機半導体層を含むので、その有機半導体層は、液晶としての柔軟性を保持する均一な分子配向薄膜として使用することができる。また、その有機半導体層は、広い温度範囲において、液晶相を示すので、分子性結晶相に近い形態の密なパッキング構造を実現することができ、望ましくは１．０×１０−４ｃｍ２／Ｖ・ｓ以上の高い電荷移動特性を示すことができる。その結果、広い面積で均一且つ柔軟な分子配向薄膜を形成することが可能となり、光センサ、有機ＥＬ素子、太陽電池、やフレキシブルディスプレイ装置等に利用可能な薄膜トランジスタ等のデバイスに応用することができる。As described above, the organic semiconductor structure of the present invention includes an organic semiconductor layer made of a liquid crystalline organic compound exhibiting a high-order liquid crystal phase in a wide temperature range, and therefore the organic semiconductor layer is flexible as a liquid crystal. It can be used as a uniform molecular oriented thin film that holds In addition, since the organic semiconductor layer exhibits a liquid crystal phase in a wide temperature range, it is possible to realize a dense packing structure in a form close to a molecular crystal phase, and preferably 1.0 × 10 −4 cm 2 / High charge transfer characteristics of V · s or higher can be exhibited. As a result, a uniform and flexible molecular alignment thin film can be formed over a wide area, and can be applied to devices such as thin film transistors that can be used in optical sensors, organic EL elements, solar cells, flexible display devices, and the like. .
（有機半導体装置）
図２は、本発明の有機半導体装置のトランジスタの一例を示す断面図である。本発明の有機半導体装置１０は、少なくとも基板１１、ゲート電極１２、ゲート絶縁層１３、有機半導体層１４、ドレイン電極１５及びソース電極１６で構成される。この有機半導体装置１０は、有機半導体層１４が、上述した本発明の有機半導体構造物を構成する液晶性有機化合物で形成されている。(Organic semiconductor device)
FIG. 2 is a cross-sectional view showing an example of a transistor of the organic semiconductor device of the present invention. The
本発明の有機半導体装置１０の構成の一例としては、基板１１上に、ゲート電極１２、ゲート絶縁層１３、配向した有機半導体層１４、ドレイン電極１５とソース電極１６、保護膜（図示しない。）の順に構成される逆スタガー構造、又は、基板１１上に、ゲート電極１２、ゲート絶縁層１３、ドレイン電極１５とソース電極１６、有機半導体層１４、保護膜（図示しない。）の順に構成されるコプラナー構造、を挙げることができる。こうした構成からなる有機半導体装置１０は、ゲート電極１２に印加される電圧の極性に応じて、蓄積状態又は空乏状態の何れかで動作する。 As an example of the configuration of the
本発明の有機半導体装置の他の態様として、（ｉ）基板／ゲート電極／ゲート絶縁層（液晶配向層を兼ねる。）／ソース・ドレイン電極／液晶性有機半導体層（／保護層）、（ｉｉ）基板／ゲート電極／ゲート絶縁層／ソース・ドレイン電極／液晶配向層／液晶性有機半導体層（／保護層）、（ｉｉｉ）基板／ゲート電極／ゲート絶縁層（液晶配向層を兼ねる）／液晶性有機半導体層／ソース・ドレイン電極／（保護層）、（ｉｖ）基板／ゲート電極／ゲート絶縁層（液晶配向層を兼ねる）／液晶性有機半導体層／ソース・ドレイン電極がパターニングされた基板（保護層を兼ねる）、（ｖ）基板／ソース・ドレイン電極／液晶性有機半導体層／ゲート絶縁層（液晶配向層を兼ねる）／ゲート電極／基板（保護層を兼ねる）、（ｖｉ）基板（配向層を兼ねる）／ソース・ドレイン電極／液晶性有機半導体層／ゲート絶縁層／ゲート電極／基板（保護層を兼ねる）、又は、（ｖｉｉ）基板／ゲート電極／ゲート絶縁層／ソース・ドレイン電極／液晶性有機半導体層／基板（配向層を兼ねる）、とすることもできる。 As another aspect of the organic semiconductor device of the present invention, (i) substrate / gate electrode / gate insulating layer (also serving as a liquid crystal alignment layer) / source / drain electrode / liquid crystalline organic semiconductor layer (/ protective layer), (ii) ) Substrate / gate electrode / gate insulating layer / source / drain electrode / liquid crystal alignment layer / liquid crystalline organic semiconductor layer (/ protective layer), (iii) substrate / gate electrode / gate insulating layer (also serving as liquid crystal alignment layer) / liquid crystal Substrate having a patterned organic semiconductor layer / source / drain electrode / (protective layer), (iv) substrate / gate electrode / gate insulating layer (also serving as a liquid crystal alignment layer) / liquid crystalline organic semiconductor layer / source / drain electrode ( (Also serves as protective layer), (v) substrate / source / drain electrode / liquid crystal organic semiconductor layer / gate insulating layer (also serves as liquid crystal alignment layer) / gate electrode / substrate (also serves as protective layer), (vi) substrate ( (Also serves as the orientation layer) / source / drain electrode / liquid crystalline organic semiconductor layer / gate insulating layer / gate electrode / substrate (also serves as protective layer), or (vii) substrate / gate electrode / gate insulating layer / source / drain electrode / Liquid crystalline organic semiconductor layer / substrate (also serves as an alignment layer).
図３は、本発明の有機半導体装置のもう一つの例を示す断面図である。本発明の有機半導体装置１７は、少なくとも基板１８、電極１９、電極２０、スペーサー２１、有機半導体層２２で構成される。この有機半導体装置１７は、有機半導体層２２が、上述した本発明の有機半導体構造物を構成する液晶性有機化合物で形成されている。電極１９、２０は同一材料で構成されてもよく、また、別材料でもよい。FIG. 3 is a cross-sectional view showing another example of the organic semiconductor device of the present invention. The
本発明の有機半導体装置１７によれば、有機半導体層を本発明に係る液晶性有機化合物で形成するので、広い面積で均一且つ柔軟な有機半導体薄膜を形成することが可能となり、各種光センサ、有機ＥＬ素子、太陽電池に利用可能である。 According to the
（液晶物質の精製）
本発明における低分子ネマティック液晶の精製では、蒸留、カラムクロマトグラフィー、再結晶などの有機合成的精製手法や、昇華による物理的精製手法を適用することができる。特に、これらの精製法を、単独、あるいは、組み合わせて、２〜３回行なうことが、少ない労力によって、効率よく精製を行なうことに有効である。(Purification of liquid crystal substances)
In the purification of the low molecular nematic liquid crystal in the present invention, organic synthetic purification methods such as distillation, column chromatography, recrystallization, and physical purification methods by sublimation can be applied. In particular, performing these purification methods two or three times alone or in combination is effective for efficient purification with little effort.
（純度の確認方法）
Ｔｉｍｅ−ｏｆ−ｆｌｉｇｈｔ法による過渡光電流の測定は、材料中の電荷の移動速度を求め、移動度を決定する方法で、移動速度の異なる電荷がある場合は、その速度の違いに応じた信号を基本的に時間分解して測定することができる方法である。この測定法を用いると、イオン伝導の移動度は一般に１０−５ｃｍ２／Ｖｓ以下であるので、少なくとも電子伝導で輸送される電荷が１０−４ｃｍ２／Ｖｓ以上であれば、十分に信号としてその違いを識別できる。さらに、イオン伝導では移動度は媒質の粘度に逆比例するため、粘度の小さい溶媒、例えば、炭化水素などで希釈すると、媒質の粘度の方が大きい場合には希釈された媒質の粘度は小さくなるため移動度は増加する。媒質と希釈溶媒との粘度の差が小さい場合は希釈しても、希釈の有無により移動度には大きな違いは現れないことになる。これに対し、電荷が電子伝導で輸送されている場合には、同様に希釈すると、希釈の割合に応じて移動度は低下する。したがって、この二つの伝導の機構に違いにより、希釈による移動度の変化の方向が逆であるため、明確に、この二つ伝導機構の違いを区別することができることになる。このことについては、
Transient photocurrent measurement by the Time-of-flight method is a method for determining the mobility of charges in a material and determining the mobility. If there are charges with different migration speeds, a signal corresponding to the difference in speed is used. Is basically a method that can be time resolved and measured. When this measurement method is used, the mobility of ionic conduction is generally 10 −5 cm 2 / Vs or less, so that at least the charge transported by electron conduction is 10 −4 cm 2 / Vs or more, the signal is sufficient. The difference can be identified as Furthermore, since the mobility in ionic conduction is inversely proportional to the viscosity of the medium, when diluted with a solvent having a low viscosity, such as a hydrocarbon, the viscosity of the diluted medium decreases if the viscosity of the medium is larger. Therefore, mobility increases. If the difference in viscosity between the medium and the dilution solvent is small, even if the medium is diluted, there will be no significant difference in mobility depending on the presence or absence of dilution. On the other hand, in the case where charges are transported by electron conduction, if the dilution is performed in the same manner, the mobility decreases according to the ratio of dilution. Accordingly, the direction of change in mobility due to dilution is opposite due to the difference between the two conduction mechanisms, and therefore, the difference between the two conduction mechanisms can be clearly distinguished. About this,
具体的には、精製した低分子ネマティック液晶とそれを蒸留によって精製した純度の高い、ネマティック液晶相の液晶温度領域の温度よりも高い沸点を持つ粘性の低い溶媒、例えば、ｎ−ヘキサン、ｎ−ヘプタン、ｎ−オクタン、ｎ−ノナン、ｎ−デカン、ｎ−ウンデカン、ｎ−ドデカン、ｎ−テトラデカン、ｎ−ペンタデカン、ｎ−ヘキサデカン、ｎ−ヘプタデカン、ｎ−オクタデカン等の長鎖炭化水素、アルキルベンゼンなどを１〜２０モル％程度加え希釈した試料をＩＴＯ電極を設置した液晶セルにつめ、その液晶のネマティック相温度領域の温度で、その液晶物質のもつ吸収係数の大きな領域に発振波長をもつパルスレーザー光で励起し、同一条件（温度、電界強度）で過渡光電流の測定を行い、それぞれ液晶セルにおける移動度を求め、その移動度を比較する。この場合、希釈しない試料の移動度の値が１０−４ｃｍ２／Ｖｓ以上で、かつ、その移動度が希釈した試料の移動度に比べて大きい場合は精製が十分と評価できる。一方、希釈しない試料の移動度にくらべて、希釈した試料の移動度が大きくなる場合は、精製が不十分と判断できる。希釈しない試料の移動度の値が希釈した試料の移動度に比べて大きい場合であっても、移動度の値が１０−４ｃｍ２／Ｖｓより小さい場合は、その液晶物質のネマティック相での電子伝導の移動度が１０−４ｃｍ２／Ｖｓよりも小さいと考えられ、有機半導体として特性が劣ると考えることができる。Specifically, a purified low-molecular nematic liquid crystal and a low-viscosity solvent having a boiling point higher than the temperature in the liquid crystal temperature region of the nematic liquid crystal phase, which is purified by distillation, such as n-hexane, n- Long chain hydrocarbons such as heptane, n-octane, n-nonane, n-decane, n-undecane, n-dodecane, n-tetradecane, n-pentadecane, n-hexadecane, n-heptadecane, n-octadecane, alkylbenzene, etc. A sample that is diluted by adding about 1 to 20 mol% is put in a liquid crystal cell with an ITO electrode, and a pulse laser that has an oscillation wavelength in the region where the liquid crystal substance has a large absorption coefficient at the temperature of the nematic phase temperature region of the liquid crystal. Excited with light, measured the transient photocurrent under the same conditions (temperature, electric field strength), the mobility in the liquid crystal cell respectively Because, to compare its mobility. In this case, if the mobility value of the undiluted sample is 10 −4 cm 2 / Vs or more and the mobility is larger than the mobility of the diluted sample, it can be evaluated that the purification is sufficient. On the other hand, if the mobility of the diluted sample is higher than the mobility of the undiluted sample, it can be determined that the purification is insufficient. Even if the mobility value of the undiluted sample is larger than the mobility of the diluted sample, if the mobility value is smaller than 10 −4 cm 2 / Vs, the liquid crystal substance in the nematic phase The mobility of electron conduction is considered to be smaller than 10 −4 cm 2 / Vs, and it can be considered that the characteristics as an organic semiconductor are inferior.
次に実施例を挙げて本発明を更に具体的に説明するが、本発明はこれらの実施例には限定されない。 EXAMPLES Next, although an Example is given and this invention is demonstrated further more concretely, this invention is not limited to these Examples.
＜２−（４′−オクチルオキシフェニル）−６−ブトキシベンゾチアゾール（以下、８Ｏ−ＰＢＴ−Ｏ４と略記する）の液晶相における電荷輸送特性＞ <Charge Transport Characteristics in Liquid Crystal Phase of 2- (4′-Octyloxyphenyl) -6-butoxybenzothiazole (hereinafter referred to as 8O-PBT-O4)>
合成した８Ｏ−ＰＢＴ−０４について、ＤＳＣ（示差型走査熱分析）で相転移温度を測定した結果、相転移温度が「Ｃｒｙｓｔ２（結晶相２）４２．７℃ Ｃｒｙｓｔ１（結晶相１）６７．３℃ ＳｍＣ（スメクティックＣ相）１０１℃ Ｎ（ネマティック相）１２３．８℃ Ｉｓｏ（等方相）を示す液晶材料である（降温下５℃／ｍｉｎで測定）。 As a result of measuring the phase transition temperature of the synthesized 8O-PBT-04 by DSC (differential scanning calorimetry), the phase transition temperature was “Cryst2 (crystal phase 2) 42.7 ° C. Cryst1 (crystal phase 1) 67.3. C. SmC (smectic C phase) 101.degree. C. N (nematic phase) 123.8.degree. C. Liquid crystal material showing Iso (isotropic phase) (measured at 5.degree. C./min under cooling temperature).
各相間の温度は、相転移温度を示している。液晶相の同定はＸ線回折で行なった。 The temperature between the phases indicates the phase transition temperature. The liquid crystal phase was identified by X-ray diffraction.
液晶セルとしては、真空成膜によりＩＴＯ電極（表面抵抗１００〜２００Ω／□）を設けたセルギャップ９μｍのガラス基板を用いた。試料の精製は、カラムクロマトグラフィー、再結晶を組み合わせて、２〜３回行なった。試料の液晶セルへの注入は、ホットプレート上で加熱した液晶セルに等方相にまで昇温した試料を毛細管現象を利用してセルにしみ込ませた。移動度の測定は、光源３３７ｎｍの窒素レーザーを使用して液晶相でＴｉｍｅ ｏｆ Ｆｌｉｇｈｔ法による測定を行なった。このとき、Ｎ相での正孔の移動度は１．０×１０−４ｃｍ２／Ｖ・ｓ以上であった。As the liquid crystal cell, a glass substrate having a cell gap of 9 μm provided with an ITO electrode (surface resistance of 100 to 200Ω / □) by vacuum film formation was used. The sample was purified 2-3 times in combination with column chromatography and recrystallization. In the injection of the sample into the liquid crystal cell, the sample heated to the isotropic phase in the liquid crystal cell heated on the hot plate was impregnated into the cell using the capillary phenomenon. The mobility was measured by the Time of Flight method in a liquid crystal phase using a nitrogen laser with a light source of 337 nm. At this time, the mobility of holes in the N phase was 1.0 × 10 −4 cm 2 / V · s or more.
＜２−（４′−オクチルフェニル）−６−ブトキシベンゾチアゾール（以下、８−ＰＢＴ−Ｏ４と略記する）の液晶相における電荷輸送相特性＞ <Charge Transport Phase Characteristics of 2- (4′-Octylphenyl) -6-butoxybenzothiazole (hereinafter abbreviated as 8-PBT-O4) in liquid crystal phase>
合成した８Ｏ−ＰＢＴ−Ｏ１について、ＤＳＣ（示差型走査熱分析）で相転移温度を測定した結果、相転移温度が「Ｃｒｙｓｔ（結晶相）２０．３℃ Ｎ（ネマティック相）８４．８℃ Ｉｓｏ（等方相）を示す液晶材料である（降温下５℃／ｍｉｎで測定）。As a result of measuring the phase transition temperature of the synthesized 8O-PBT-O1 by DSC (differential scanning calorimetry), the phase transition temperature was “Cryst (crystalline phase) 20.3 ° C. N (nematic phase) 84.8 ° C. Iso. It is a liquid crystal material exhibiting (isotropic phase) (measured at 5 ° C./min under temperature drop).
各相間の温度は、相転移温度を示している。液晶相の同定はＸ線回折で行なった。The temperature between the phases indicates the phase transition temperature. The liquid crystal phase was identified by X-ray diffraction.
液晶セルとしては、真空成膜によりＩＴＯ電極（表面抵抗１００〜２００Ω／□）を設けたセルギャップ９μｍのガラス基板を用いた。試料の精製は、カラムクロマトグラフィー、再結晶を組み合わせて、２〜３回行なった。試料の液晶セルへの注入は、ホットプレート上で加熱した液晶セルに等方相にまで昇温した試料を毛細管現象を利用してセルにしみ込ませた。移動度の測定は、光源３３７ｎｍの窒素レーザーを使用して液晶相でＴｉｍｅ ｏｆ Ｆｌｉｇｈｔ法による測定を行なった。このとき、Ｎ相での正孔の移動度は１．０×１０−４ｃｍ２／Ｖ・ｓ以上であった。As the liquid crystal cell, a glass substrate having a cell gap of 9 μm provided with an ITO electrode (surface resistance of 100 to 200Ω / □) by vacuum film formation was used. The sample was purified 2-3 times in combination with column chromatography and recrystallization. In the injection of the sample into the liquid crystal cell, the sample heated to the isotropic phase in the liquid crystal cell heated on the hot plate was impregnated into the cell using the capillary phenomenon. The mobility was measured by the Time of Flight method in a liquid crystal phase using a nitrogen laser with a light source of 337 nm. At this time, the mobility of holes in the N phase was 1.0 × 10 −4 cm 2 / V · s or more.
＜２−（４′−オクチルフェニル）−６−メトキシベンゾチアゾール（以下、８−ＰＢＴ−０１と略記する）の液晶相における電荷輸送特性＞ <Charge Transport Characteristics of 2- (4′-Octylphenyl) -6-methoxybenzothiazole (hereinafter referred to as 8-PBT-01) in Liquid Crystal Phase>
合成した８−ＰＢＴ−Ｏ１について、ＤＳＣ（示差型走査熱分析）で相転移温度を測定した結果、相転移温度が「Ｃｒｙｓｔ（結晶相）５２．７℃ Ｎ（ネマティック相）７３．４℃ Ｉｓｏ（等方相）を示す液晶材料である（降温下５℃／ｍｉｎで測定）。As a result of measuring the phase transition temperature of the synthesized 8-PBT-O1 by DSC (differential scanning thermal analysis), the phase transition temperature was “Cryst (crystalline phase) 52.7 ° C. N (nematic phase) 73.4 ° C. Iso. It is a liquid crystal material exhibiting (isotropic phase) (measured at 5 ° C./min under temperature drop).
各相間の温度は、相転移温度を示している。液晶相の同定はＸ線回折で行なった。The temperature between the phases indicates the phase transition temperature. The liquid crystal phase was identified by X-ray diffraction.
液晶セルとしては、真空成膜によりＩＴＯ電極（表面抵抗１００〜２００Ω／□）を設けたセルギャップ９μｍのガラス基板を用いた。試料の精製は、カラムクロマトグラフィー、再結晶を組み合わせて、２〜３回行なった。試料の液晶セルへの注入は、ホットプレート上で加熱した液晶セルに等方相にまで昇温した試料を毛細管現象を利用してセルにしみ込ませた。移動度の測定は、光源３３７ｎｍの窒素レーザーを使用して液晶相でＴｉｍｅ ｏｆ Ｆｌｉｇｈｔ法による測定を行なった。このとき、Ｎ相での正孔の移動度は１．１×１０−４ｃｍ２／Ｖ・ｓ以上であった。As the liquid crystal cell, a glass substrate having a cell gap of 9 μm provided with an ITO electrode (surface resistance of 100 to 200Ω / □) by vacuum film formation was used. The sample was purified 2-3 times in combination with column chromatography and recrystallization. In the injection of the sample into the liquid crystal cell, the sample heated to the isotropic phase in the liquid crystal cell heated on the hot plate was impregnated into the cell using the capillary phenomenon. The mobility was measured by the Time of Flight method in a liquid crystal phase using a nitrogen laser with a light source of 337 nm. At this time, the mobility of holes in the N phase was 1.1 × 10 −4 cm 2 / V · s or more.
＜２−（４′−ペンチルオキシフェニル）−６−ドデシルベンゾチアゾール（以下、５Ｏ−ＰＢＴ−１２と略記する）の液晶相における電荷輸送特性＞ <Charge Transport Properties of 2- (4′-pentyloxyphenyl) -6-dodecylbenzothiazole (hereinafter abbreviated as 5O-PBT-12) in liquid crystal phase>
合成した５Ｏ−ＰＢＴ−１２について、ＤＳＣ（示差型走査熱分析）で相転移温度を測定した結果、相転移温度が「Ｃｒｙｓｔ（結晶相）５０．３℃ ＳｍＡ（スメクティックＡ相）７９．２℃ Ｎ（ネマティック相）８６．４℃ Ｉｓｏ（等方相）を示す液晶材料である（降温下５℃／ｍｉｎで測定）。As a result of measuring the phase transition temperature of the synthesized 5O-PBT-12 by DSC (differential scanning thermal analysis), the phase transition temperature was “Cryst (crystalline phase) 50.3 ° C. SmA (smectic A phase) 79.2 ° C. It is a liquid crystal material exhibiting N (nematic phase) 86.4 ° C. Iso (isotropic phase) (measured at a temperature drop of 5 ° C./min).
各相間の温度は、相転移温度を示している。液晶相の同定はＸ線回折で行なった。The temperature between the phases indicates the phase transition temperature. The liquid crystal phase was identified by X-ray diffraction.
液晶セルとしては、真空成膜によりＩＴＯ電極（表面抵抗１００〜２００Ω／□）を設けたセルギャップ９μｍのガラス基板を用いた。試料の精製は、カラムクロマトグラフィー、再結晶を組み合わせて、２〜３回行なった。試料の液晶セルへの注入は、ホットプレート上で加熱した液晶セルに等方相にまで昇温した試料を毛細管現象を利用してセルにしみ込ませた。移動度の測定は、光源３３７ｎｍの窒素レーザーを使用して液晶相でＴｉｍｅ ｏｆ Ｆｌｉｇｈｔ法による測定を行なった。このとき、Ｎ相での正孔の移動度は１．０×１０−４ｃｍ２／Ｖ・ｓ以上であった。As the liquid crystal cell, a glass substrate having a cell gap of 9 μm provided with an ITO electrode (surface resistance of 100 to 200Ω / □) by vacuum film formation was used. The sample was purified 2-3 times in combination with column chromatography and recrystallization. In the injection of the sample into the liquid crystal cell, the sample heated to the isotropic phase in the liquid crystal cell heated on the hot plate was impregnated into the cell using the capillary phenomenon. The mobility was measured by the Time of Flight method in a liquid crystal phase using a nitrogen laser with a light source of 337 nm. At this time, the mobility of holes in the N phase was 1.0 × 10 −4 cm 2 / V · s or more.
＜２−（４′−オクチルフェニル）−６−エトキシナフタレン（以下、８−ＰＮＰ−Ｏ２と略記する）の液晶相における電荷輸送特性＞ <Charge Transport Properties in Liquid Crystal Phase of 2- (4′-Octylphenyl) -6-ethoxynaphthalene (hereinafter abbreviated as 8-PNP-O2)>
合成した８−ＰＮＰ−Ｏ２について、ＤＳＣ（示差型走査熱分析）で相転移温度を測定した結果、相転移温度が「Ｃｒｙｓｔ２（結晶相２）３５℃ Ｃｒｙｓｔ１（結晶相１）６９．７℃ ＳｍＥ（スメクティックＥ相）１１５．３℃ Ｎ（ネマティック相）１２９．３℃ Ｉｓｏ（等方相）を示す液晶材料である（降温下５℃／ｍｉｎで測定）。As a result of measuring the phase transition temperature of the synthesized 8-PNP-O2 by DSC (differential scanning thermal analysis), the phase transition temperature was found to be “Cryst2 (crystal phase 2) 35 ° C. Cryst1 (crystal phase 1) 69.7 ° C. SmE. (Smectic E phase) 115.3 ° C. N (nematic phase) 129.3 ° C. It is a liquid crystal material exhibiting Iso (isotropic phase) (measured at 5 ° C./min under cooling temperature).
各相間の温度は、相転移温度を示している。液晶相の同定はＸ線回折で行なった。The temperature between the phases indicates the phase transition temperature. The liquid crystal phase was identified by X-ray diffraction.
液晶セルとしては、真空成膜によりＩＴＯ電極（表面抵抗１００〜２００Ω／□）を設けたセルギャップ９μｍのガラス基板を用いた。試料の精製は、カラムクロマトグラフィー、再結晶を組み合わせて、２〜３回行なった。試料の液晶セルへの注入は、ホットプレート上で加熱した液晶セルに等方相にまで昇温した試料を毛細管現象を利用してセルにしみ込ませた。移動度の測定は、光源３３７ｎｍの窒素レーザーを使用して液晶相でＴｉｍｅ ｏｆ Ｆｌｉｇｈｔ法による測定を行なった。このとき、Ｎ相での正孔の移動度は１．１×１０−４ｃｍ２／Ｖ・ｓ以上であった。As the liquid crystal cell, a glass substrate having a cell gap of 9 μm provided with an ITO electrode (surface resistance of 100 to 200Ω / □) by vacuum film formation was used. The sample was purified 2-3 times in combination with column chromatography and recrystallization. In the injection of the sample into the liquid crystal cell, the sample heated to the isotropic phase in the liquid crystal cell heated on the hot plate was impregnated into the cell using the capillary phenomenon. The mobility was measured by the Time of Flight method in a liquid crystal phase using a nitrogen laser with a light source of 337 nm. At this time, the mobility of holes in the N phase was 1.1 × 10 −4 cm 2 / V · s or more.
＜２−（４′−ヘキシルオキシフェニル）−６−メトキシフェニルナフタレン（以下、６−ＰＮＰ−Ｏ２と略記する）の液晶相における電荷輸送特性＞ <Charge Transport Properties of 2- (4′-Hexyloxyphenyl) -6-methoxyphenylnaphthalene (hereinafter abbreviated as 6-PNP-O2) in liquid crystal phase>
合成した６−ＰＮＰ−Ｏ２について、ＤＳＣ（示差型走査熱分析）で相転移温度を測定した結果、相転移温度が「Ｃｒｙｓｔ（結晶相）６６．３℃ ＳｍＸ（スメクティックＸ相）１２１．４℃ Ｎ（ネマティック相）１３３．５℃ Ｉｓｏ（等方相）を示す液晶材料である（降温下５℃／ｍｉｎで測定）。As a result of measuring the phase transition temperature of the synthesized 6-PNP-O2 by DSC (differential scanning calorimetry), the phase transition temperature was “Cryst (crystalline phase) 66.3 ° C. SmX (smectic X phase) 121.4 ° C. N (nematic phase) 133.5 ° C. This is a liquid crystal material exhibiting Iso (isotropic phase) (measured at 5 ° C./min under temperature drop).
各相間の温度は、相転移温度を示している。液晶相の同定はＸ線回折で行なった。The temperature between the phases indicates the phase transition temperature. The liquid crystal phase was identified by X-ray diffraction.
液晶セルとしては、真空成膜によりＩＴＯ電極（表面抵抗１００〜２００Ω／□）を設けたセルギャップ９μｍのガラス基板を用いた。試料の精製は、カラムクロマトグラフィー、再結晶を組み合わせて、２〜３回行なった。試料の液晶セルへの注入は、ホットプレート上で加熱した液晶セルに等方相にまで昇温した試料を毛細管現象を利用してセルにしみ込ませた。移動度の測定は、光源３３７ｎｍの窒素レーザーを使用して液晶相でＴｉｍｅ ｏｆ Ｆｌｉｇｈｔ法による測定を行なった。このとき、Ｎ相での正孔の移動度は１．１×１０−４ｃｍ２／Ｖ・ｓ以上であった。As the liquid crystal cell, a glass substrate having a cell gap of 9 μm provided with an ITO electrode (surface resistance of 100 to 200Ω / □) by vacuum film formation was used. The sample was purified 2-3 times in combination with column chromatography and recrystallization. In the injection of the sample into the liquid crystal cell, the sample heated to the isotropic phase in the liquid crystal cell heated on the hot plate was impregnated into the cell using the capillary phenomenon. The mobility was measured by the Time of Flight method in a liquid crystal phase using a nitrogen laser with a light source of 337 nm. At this time, the mobility of holes in the N phase was 1.1 × 10 −4 cm 2 / V · s or more.
＜２−（４′−オクチルオキシフェニル）−６−ブトキシベンゾチアゾール（以下、８Ｏ−ＰＢＴ−Ｏ４と略記する）の液晶相における電荷輸送特性＞ <Charge Transport Characteristics in Liquid Crystal Phase of 2- (4′-Octyloxyphenyl) -6-butoxybenzothiazole (hereinafter referred to as 8O-PBT-O4)>
合成した８Ｏ−ＰＢＴ−Ｏ４について、ＤＳＣ（示差型走査熱分析）で相転移温度を測定した結果、相転移温度が「Ｃｒｙｓｔ２（結晶相２）４２．７℃ Ｃｒｙｓｔ１（結晶相１）６７．３℃ ＳｍＣ（スメクティックＣ相）１０１℃ Ｎ（ネマティック相）１２３．８℃ Ｉｓｏ（等方相）を示す液晶材料である（降温下５℃／ｍｉｎで測定）。As a result of measuring the phase transition temperature of the synthesized 8O-PBT-O4 by DSC (differential scanning calorimetry), the phase transition temperature was “Cryst2 (crystal phase 2) 42.7 ° C. Cryst1 (crystal phase 1) 67.3. C. SmC (smectic C phase) 101.degree. C. N (nematic phase) 123.8.degree. C. Liquid crystal material showing Iso (isotropic phase) (measured at 5.degree. C./min under cooling temperature).
各相間の温度は、相転移温度を示している。液晶相の同定はＸ線回折で行なった。 The temperature between the phases indicates the phase transition temperature. The liquid crystal phase was identified by X-ray diffraction.
液晶セルとしては、真空成膜によりＩＴＯ電極（表面抵抗１００〜２００Ω／□）を設けたセルギャップ９μｍのガラス基板を用いた。試料の精製は、試料の精製は、カラムクロマトグラフィーで行った。試料の液晶セルへの注入は、ホットプレート上で加熱した液晶セルに等方相にまで昇温した試料を毛細管現象を利用してセルにしみ込ませた。移動度の測定は、光源３３７ｎｍの窒素レーザーを使用して液晶相でＴｉｍｅ ｏｆ Ｆｌｉｇｈｔ法による測定を行なった。このとき、Ｎ相での正孔の移動度は３．０×１０−５ｃｍ２／Ｖ・ｓ以下であった。As the liquid crystal cell, a glass substrate having a cell gap of 9 μm provided with an ITO electrode (surface resistance of 100 to 200Ω / □) by vacuum film formation was used. The sample was purified by column chromatography. In the injection of the sample into the liquid crystal cell, the sample heated to the isotropic phase in the liquid crystal cell heated on the hot plate was impregnated into the cell using the capillary phenomenon. The mobility was measured by the Time of Flight method in a liquid crystal phase using a nitrogen laser with a light source of 337 nm. At this time, the mobility of holes in the N phase was 3.0 × 10 −5 cm 2 / V · s or less.
＜２−（４′−オクチルフェニル）−６−ブトキシベンゾチアゾール（以下、８−ＰＢＴ−Ｏ４と略記する）の液晶相における電荷輸送特性＞ <Charge Transport Properties in Liquid Crystal Phase of 2- (4′-Octylphenyl) -6-butoxybenzothiazole (hereinafter referred to as 8-PBT-O4)>
合成した８−ＰＢＴ−Ｏ４について、ＤＳＣ（示差型走査熱分析）で相転移温度を測定した結果、相転移温度が「Ｃｒｙｓｔ（結晶相）２０．３℃ Ｎ（ネマティック相）８４．８℃ Ｉｓｏ（等方相）を示す液晶材料である（降温下５℃／ｍｉｎで測定）。
各相間の温度は、相転移温度を示している。液晶相の同定はＸ線回折で行なった。As a result of measuring the phase transition temperature of the synthesized 8-PBT-O4 by DSC (differential scanning thermal analysis), the phase transition temperature was “Cryst (crystalline phase) 20.3 ° C. N (nematic phase) 84.8 ° C. Iso. It is a liquid crystal material exhibiting (isotropic phase) (measured at 5 ° C./min under temperature drop).
The temperature between the phases indicates the phase transition temperature. The liquid crystal phase was identified by X-ray diffraction.
液晶セルとしては、真空成膜によりＩＴＯ電極（表面抵抗１００〜２００Ω／□）を設けたセルギャップ９μｍのガラス基板を用いた。試料の精製は、試料の精製は、カラムクロマトグラフィーで行った。試料の液晶セルへの注入は、ホットプレート上で加熱した液晶セルに等方相にまで昇温した試料を毛細管現象を利用してセルにしみ込ませた。移動度の測定は、光源３３７ｎｍの窒素レーザーを使用して液晶相でＴａｍｅ ｏｆ Ｆｌｉｇｈｔ法による測定を行なった。このとき、Ｎ相での正孔の移動度は５．０×１０−５ｃｍ２／Ｖ・ｓ以下であった。As the liquid crystal cell, a glass substrate having a cell gap of 9 μm provided with an ITO electrode (surface resistance of 100 to 200Ω / □) by vacuum film formation was used. The sample was purified by column chromatography. In the injection of the sample into the liquid crystal cell, the sample heated to the isotropic phase in the liquid crystal cell heated on the hot plate was impregnated into the cell using the capillary phenomenon. The mobility was measured by the Time of Flight method in a liquid crystal phase using a nitrogen laser with a light source of 337 nm. At this time, the mobility of holes in the N phase was 5.0 × 10 −5 cm 2 / V · s or less.
＜２−（４′−オクチルフェニル）−６−メトキシベンゾチアゾール（以下、８−ＰＢＴ−Ｏ１と略記する）の液晶相における電荷輸送特性＞<Charge Transport Properties in Liquid Crystal Phase of 2- (4′-Octylphenyl) -6-methoxybenzothiazole (hereinafter referred to as 8-PBT-O1)>
合成した８−ＰＢＴ−Ｏ１について、ＤＳＣ（示差型走査熱分析）で相転移温度を測定した結果、相転移温度が「Ｃｒｙｓｔ（結晶相）５２．７℃ Ｎ（ネマティック相）７３．４℃ Ｉｓｏ（等方相）を示す液晶材料である（降温下５℃／ｍｉｎで測定）。As a result of measuring the phase transition temperature of the synthesized 8-PBT-O1 by DSC (differential scanning thermal analysis), the phase transition temperature was “Cryst (crystalline phase) 52.7 ° C. N (nematic phase) 73.4 ° C. Iso. It is a liquid crystal material exhibiting (isotropic phase) (measured at 5 ° C./min under temperature drop).
各相間の温度は、相転移温度を示している。液晶相の同定はＸ線回折で行なった。The temperature between the phases indicates the phase transition temperature. The liquid crystal phase was identified by X-ray diffraction.
液晶セルとしては、真空成膜によりＩＴＯ電極（表面抵抗１００〜２００Ω／□）を設けたセルギャップ９μｍのガラス基板を用いた。試料の精製は、試料の精製は、カラムクロマトグラフィーで行った。試料の液晶セルへの注入は、ホットプレート上で加熱した液晶セルに等方相にまで昇温した試料を毛細管現象を利用してセルにしみ込ませた。移動度の測定は、光源３３７ｎｍの窒素レーザーを使用して液晶相でＴｉｍｅ ｏｆ Ｆｌｉｇｈｔ法による測定を行なった。このとき、Ｎ相での正孔の移動度は４．０×１０−５ｃｍ２／Ｖ・ｓ以下であった。As the liquid crystal cell, a glass substrate having a cell gap of 9 μm provided with an ITO electrode (surface resistance of 100 to 200Ω / □) by vacuum film formation was used. The sample was purified by column chromatography. In the injection of the sample into the liquid crystal cell, the sample heated to the isotropic phase in the liquid crystal cell heated on the hot plate was impregnated into the cell using the capillary phenomenon. The mobility was measured by the Time of Flight method in a liquid crystal phase using a nitrogen laser with a light source of 337 nm. At this time, the mobility of holes in the N phase was 4.0 × 10 −5 cm 2 / V · s or less.
＜２−（４′−ペンチルオキシフェニル）−６−ドデシルベンゾチアゾール（以下、５Ｏ−ＰＢＴ−１２と略記する）の液晶相における電荷輸送特性＞ <Charge Transport Properties of 2- (4′-pentyloxyphenyl) -6-dodecylbenzothiazole (hereinafter abbreviated as 5O-PBT-12) in liquid crystal phase>
合成した５Ｏ−ＰＢＴ−１２について、ＤＳＣ（示差型走査熱分析）で相転移温度を測定した結果、相転移温度が「Ｃｒｙｓｔ（結晶相）５０．３℃ ＳｍＡ（スメクティックＡ相）７９．２℃ Ｎ（ネマティック相）８６．４℃ Ｉｓｏ（等方相）を示す液晶材料である（降温下５℃／ｍｉｎで測定）。
各相間の温度は、相転移温度を示している。液晶相の同定はＸ線回折で行なった。As a result of measuring the phase transition temperature of the synthesized 5O-PBT-12 by DSC (differential scanning thermal analysis), the phase transition temperature was “Cryst (crystalline phase) 50.3 ° C. SmA (smectic A phase) 79.2 ° C. It is a liquid crystal material exhibiting N (nematic phase) 86.4 ° C. Iso (isotropic phase) (measured at a temperature drop of 5 ° C./min).
The temperature between the phases indicates the phase transition temperature. The liquid crystal phase was identified by X-ray diffraction.
液晶セルとしては、真空成膜によりＩＴＯ電極（表面抵抗１００〜２００Ω／□）を設けたセルギャップ９μｍのガラス基板を用いた。試料の精製は、試料の精製は、カラムクロマトグラフィーで行った。試料の液晶セルへの注入は、ホットプレート上で加熱した液晶セルに等方相にまで昇温した試料を毛細管現象を利用してセルにしみ込ませた。移動度の測定は、光源３３７ｎｍの窒素レーザーを使用して液晶相でＴｉｍｅ ｏｆ Ｆｌｉｇｈｔ法による測定を行なった。このとき、Ｎ相での正孔の移動度は５．０×１０−５ｃｍ２／Ｖ・ｓ以下であった。As the liquid crystal cell, a glass substrate having a cell gap of 9 μm provided with an ITO electrode (surface resistance of 100 to 200Ω / □) by vacuum film formation was used. The sample was purified by column chromatography. In the injection of the sample into the liquid crystal cell, the sample heated to the isotropic phase in the liquid crystal cell heated on the hot plate was impregnated into the cell using the capillary phenomenon. The mobility was measured by the Time of Flight method in a liquid crystal phase using a nitrogen laser with a light source of 337 nm. At this time, the mobility of holes in the N phase was 5.0 × 10 −5 cm 2 / V · s or less.
＜２−（４′−オクチルフェニル）−６−エトキシナフタレン（以下、８−ＰＮＰ−Ｏ２と略記する）の液晶相における電荷輸送特性＞ <Charge Transport Properties in Liquid Crystal Phase of 2- (4′-Octylphenyl) -6-ethoxynaphthalene (hereinafter abbreviated as 8-PNP-O2)>
合成した８−ＰＮＰ−Ｏ２について、ＤＳＣ（示差型走査熱分析）で相転移温度を測定した結果、相転移温度が「Ｃｒｙｓｔ２（結晶相２）３５℃ Ｃｒｙｓｔ１（結晶相１）６９．７℃ ＳｍＥ（スメクティックＥ相）１１５．３℃ Ｎ（ネマティック相）１２９．３℃ Ｉｓｏ（等方相）を示す液晶材料である（降温下５℃／ｍｉｎで測定）。The synthesized 8-PNP-O2 was measured for phase transition temperature by DSC (Differential Scanning Thermal Analysis). As a result, the phase transition temperature was found to be “Cryst2 (Crystal Phase 2) 35 ° C. (Smectic E phase) 115.3 ° C. N (nematic phase) 129.3 ° C. It is a liquid crystal material exhibiting Iso (isotropic phase) (measured at 5 ° C./min under cooling temperature).
各相間の温度は、相転移温度を示している。液晶相の同定はＸ線回折で行なった。The temperature between the phases indicates the phase transition temperature. The liquid crystal phase was identified by X-ray diffraction.
液晶セルとしては、真空成膜によりＩＴＯ電極（表面抵抗１００〜２００Ω／□）を設けたセルギャップ９μｍのガラス基板を用いた。試料の精製は、試料の精製は、カラムクロマトグラフィーで行った。試料の液晶セルへの注入は、ホットプレート上で加熱した液晶セルに等方相にまで昇温した試料を毛細管現象を利用してセルにしみ込ませた。移動度の測定は、光源３３７ｎｍの窒素レーザーを使用して液晶相でＴｉｍｅ ｏｆ Ｆｌｉｇｈｔ法による測定を行なった。このとき、Ｎ相での正孔の移動度は５．０×１０−５ｃｍ２／Ｖ・ｓ以下であった。As the liquid crystal cell, a glass substrate having a cell gap of 9 μm provided with an ITO electrode (surface resistance of 100 to 200Ω / □) by vacuum film formation was used. The sample was purified by column chromatography. In the injection of the sample into the liquid crystal cell, the sample heated to the isotropic phase in the liquid crystal cell heated on the hot plate was impregnated into the cell using the capillary phenomenon. The mobility was measured by the Time of Flight method in a liquid crystal phase using a nitrogen laser with a light source of 337 nm. At this time, the mobility of holes in the N phase was 5.0 × 10 −5 cm 2 / V · s or less.
＜２−（４′−ヘキシルオキシフェニル）−６−メトキシフェニルナフタレン（以下、６−ＰＮＰ−Ｏ２と略記する）の液晶相における電荷輸送特性＞ <Charge Transport Properties of 2- (4′-Hexyloxyphenyl) -6-methoxyphenylnaphthalene (hereinafter abbreviated as 6-PNP-O2) in liquid crystal phase>
合成した６−ＰＮＰ−Ｏ２について、ＤＳＣ（示差型走査熱分析）で相転移温度を測定した結果、相転移温度が「Ｃｒｙｓｔ（結晶相）６６．３℃ ＳｍＸ（スメクティックＸ相）１２１．４℃ Ｎ（ネマティック相）１３３．５℃ Ｉｓｏ（等方相）を示す液晶材料である（降温下５℃／ｍｉｎで測定）。As a result of measuring the phase transition temperature of the synthesized 6-PNP-O2 by DSC (differential scanning calorimetry), the phase transition temperature was “Cryst (crystalline phase) 66.3 ° C. SmX (smectic X phase) 121.4 ° C. N (nematic phase) 133.5 ° C. This is a liquid crystal material exhibiting Iso (isotropic phase) (measured at 5 ° C./min under temperature drop).
各相間の温度は、相転移温度を示している。液晶相の同定はＸ線回折で行なった。 The temperature between the phases indicates the phase transition temperature. The liquid crystal phase was identified by X-ray diffraction.
液晶セルとしては、真空成膜によりＩＴＯ電極（表面抵抗１００〜２００Ω／□）を設けたセルギャップ９μｍのガラス基板を用いた。試料の精製は、試料の精製は、カラムクロマトグラフィーで行った。試料の液晶セルへの注入は、ホットプレート上で加熱した液晶セルに等方相にまで昇温した試料を毛細管現象を利用してセルにしみ込ませた。移動度の測定は、光源３３７ｎｍの窒素レーザーを使用して液晶相でＴｉｍｅ ｏｆ Ｆｌｉｇｈｔ法による測定を行なった。このとき、Ｎ相での正孔の移動度は４．０×１０−５ｃｍ２／Ｖ・ｓ以下であった。As the liquid crystal cell, a glass substrate having a cell gap of 9 μm provided with an ITO electrode (surface resistance of 100 to 200Ω / □) by vacuum film formation was used. The sample was purified by column chromatography. In the injection of the sample into the liquid crystal cell, the sample heated to the isotropic phase in the liquid crystal cell heated on the hot plate was impregnated into the cell using the capillary phenomenon. The mobility was measured by the Time of Flight method in a liquid crystal phase using a nitrogen laser with a light source of 337 nm. At this time, the mobility of holes in the N phase was 4.0 × 10 −5 cm 2 / V · s or less.
（評価方法）
上記の実施例１〜６及び比較例１〜６で合成したサンプルについて、下記に示す評価項目について試験を行い、そのデータを測定した。(Evaluation method)
About the sample synthesize | combined in said Examples 1-6 and Comparative Examples 1-6, it tested about the evaluation item shown below and measured the data.
相転移温度の測定には、ＤＳＣ（示差型走査熱分析、セイコー電子工業ＤＳＣ２２０Ｃ）を用いた。液晶相の同定には、ホットステージ付きＸ線回折装置（ＲＩＧＡＫＵ ＲＡＤ−Ｂ，理学電気製）を用いた。電荷移動度の測定は、図３に示す装置を用い、励起光として窒素パルスレーザー（Ｌａｓｅｒ ｐｈｏｔｏｎｉｃｓＬＮ２０３Ｃ）を用い、Ｔｉｍｅ ｏｆ ｆｌｉｇｈｔ法による測定を各液晶相で行った。 For the measurement of the phase transition temperature, DSC (Differential Scanning Thermal Analysis, Seiko Electronics DSC220C) was used. For identification of the liquid crystal phase, an X-ray diffractometer with a hot stage (RIGAKU RAD-B, manufactured by Rigaku Corporation) was used. The charge mobility was measured using the apparatus shown in FIG. 3, using a nitrogen pulse laser (Laser photonics LN203C) as excitation light, and measuring by the time of flight method for each liquid crystal phase.
［図５］
精製を十分に行なった実施例１で示した８０−ＰＢＴ−０４の希釈前後でのネマティック相における過渡光電流波形に見られる変化を示す。印下電圧は１００Ｖとした。液晶セルとしては、真空成膜によりＩＴＯ電極（表面抵抗１００〜２００Ω／□）を設けたセルギャップ９μｍのガラス基板を用いた。７２．６ｓｅｃ付近に見られる肩は、電荷が対向電極に到達したことを表しており、移動度は１．１×１０−４ｃｍ２／Ｖｓに対応する。ｎ−テトラデカン１０モル％希釈した物では、１０３μｓｅｃ付近に見られる肩は遅い時間領域に移動しており、移動度が減少したことを示している。これは、電子伝導に特徴的な特性である。[Fig. 5]
The change seen in the transient photocurrent waveform in the nematic phase before and after dilution of 80-PBT-04 shown in Example 1 which has been sufficiently purified is shown. The under voltage was 100V. As the liquid crystal cell, a glass substrate having a cell gap of 9 μm provided with an ITO electrode (surface resistance of 100 to 200Ω / □) by vacuum film formation was used. The shoulder seen in the vicinity of 72.6 sec represents that the charge has reached the counter electrode, and the mobility corresponds to 1.1 × 10 −4 cm 2 / Vs. In a product diluted with 10 mol% of n-tetradecane, the shoulder seen in the vicinity of 103 μsec moved to a slow time region, indicating that the mobility was reduced. This is a characteristic characteristic of electron conduction.
［図６］
精製の不十分な８０−ＰＢＴ−０４例に、比較例１で示した８０−ＰＢＴ−０４の希釈前後でのネマティック相における過渡光電流波形に見られる変化を示す。印下電圧は１００Ｖとした。液晶セルとしては、真空成膜によりＩＴＯ電極（表面抵抗１００〜２００Ω／□）を設けたセルギャップ９μｍのガラス基板を用いた。５９６μｓｅｃ付近に見られる肩は、電荷が対向電極に到達したことを表しており、移動度は１．３６×１０−５ｃｍ２／Ｖｓに対応する。ｎ−テトラデカンで１０ｍｏｌ％希釈した物では、５７４μｓｅｃ付近に見られる肩は速い時間領域に移動しており、移動度が増加したことを示している。これは、イオン伝導に特徴的な特性である。[Fig. 6]
The 80-PBT-04 example with insufficient purification shows the change seen in the transient photocurrent waveform in the nematic phase before and after dilution of 80-PBT-04 shown in Comparative Example 1. The under voltage was 100V. As the liquid crystal cell, a glass substrate having a cell gap of 9 μm provided with an ITO electrode (surface resistance of 100 to 200Ω / □) by vacuum film formation was used. The shoulder seen in the vicinity of 596 μsec represents that the charge has reached the counter electrode, and the mobility corresponds to 1.36 × 10 −5 cm 2 / Vs. In a product diluted by 10 mol% with n-tetradecane, the shoulder seen in the vicinity of 574 μsec moved to a fast time region, indicating that the mobility increased. This is a characteristic characteristic of ionic conduction.
本発明は、ネマティック液晶物質が、その純度の保証をされれば、通常の固体系の有機半導体材料と同様に、種々の有機電子デバイスに適用可能である。具体的には、光センサ、有機ＥＬ素子、有機トランジスタ、太陽電池、有機電子メモリー素子などに利用できる。特に、分子配向の制御が容易であることから、偏光の受光発光素子として、特徴ある光学的にアクティブな光電子デバイスへの応用が本材料を活かすことになる。
また、光学活性なネマティック液晶物質を用いれば、同様に、円偏光の受光、発光素子にも適用できる。The present invention can be applied to various organic electronic devices in the same manner as ordinary solid organic semiconductor materials as long as the purity of the nematic liquid crystal substance is guaranteed. Specifically, it can be used for optical sensors, organic EL elements, organic transistors, solar cells, organic electronic memory elements, and the like. In particular, since the control of molecular orientation is easy, the material can be utilized for application to a characteristic optically active optoelectronic device as a light receiving and emitting element of polarized light.
Further, if an optically active nematic liquid crystal substance is used, it can be similarly applied to circularly polarized light receiving and light emitting elements.
１０ 有機半導体装置
１１ 基板
１２ ゲート電極
１３ ゲート絶縁層
１４ 有機半導体層
１５ ドレイン電極
１６ ソース電極
１７ 有機半導体装置
１８ 基板
１９ 電極
２０ 電極
２１ スペーサー
２２ 液晶性有機半導体材料
２０１ Ｎ２パルスレーザー
３０１ 試料
４０１ デジタルオシロスコープ
２３ 精製を十分に行なった８０−ＰＢＴ−Ｏ４でのネマティック相における過渡光電流波形である
２４ 精製を十分に行なった８０−ＰＢＴ−Ｏ４に対してｎ−テトラデカンを１０ｍｏｌ％で希釈した時のネマティック相における過渡光電流波形である
２５ 精製が不十分な８０−ＰＢＴ−Ｏ４でのネマティック相における過渡光電流波形である
２６ 精製が不十分な８０−ＰＢＴ−Ｏ４に対してｎ−テトラデカンを１０ｍｏｌ％で希釈した時のネマティック相における過渡光電流波形であるDESCRIPTION OF
Claims (6)
該有機化合物の熱分解温度以下の作動温度において、少なくとも一種類のネマティック液晶相状態を有し、
Ｔｉｍｅ−ｏｆ−ｆｌｉｇｈｔ（ＴＯＦ）法による過渡光電流測定に基づく電荷の走行時間から求めた、該有機化合物の移動度の値が１０−４ｃｍ２／Ｖｓ以上であり、
３〜１５ｍｏｌ％の炭化水素化合物で希釈した試料の移動度が、希釈前の試料の移動度より小さく観測されることを特徴とする有機半導体材料。 L 6π-electron aromatic rings, M 10π-electron aromatic rings, and N 14π-electron aromatic rings (where L, M, and N each represent an integer of 0 to 4, L + M + N = 1 to 4 . to) skeletal structure (Z1) containing, and have a terminal structure that express liquid crystallinity at the end of the skeletal structure, and an organic semiconductor materials of the rod-like molecules having the following structural formula;
Having an at least one nematic liquid crystal phase state at an operating temperature below the thermal decomposition temperature of the organic compound ;
The mobility value of the organic compound determined from the transit time of the electric charge based on the transient photocurrent measurement by Time-of-flight (TOF) method is 10 −4 cm 2 / Vs or more,
An organic semiconductor material characterized in that mobility of a sample diluted with 3 to 15 mol% of a hydrocarbon compound is observed to be smaller than mobility of a sample before dilution .
該有機化合物の熱分解温度以下の作動温度において、少なくとも一種類のネマティック液晶相状態を有し、
Ｔｉｍｅ−ｏｆ−ｆｌｉｇｈｔ（ＴＯＦ）法による過渡光電流測定に基づく電荷の走行時間から求めた、該有機化合物の移動度の値が１０ −４ ｃｍ ２ ／Ｖｓ以上であり、
、且つ
３〜１５ｍｏｌ％の炭化水素化合物で希釈した試料の移動度が、希釈前の試料の移動度より小さく観測されることを特徴とする有機半導体材料。 L 6π-electron aromatic rings, M 10π-electron aromatic rings, and N 14π-electron aromatic rings (where L, M, and N each represent an integer of 0 to 4, L + M + N = 1 to 4 An organic semiconductor material of a rod-like molecule having a skeleton structure (Z1, Z2) including a terminal structure that has liquid crystallinity at the terminal of the skeleton structure and having the following structural formula;
Having an at least one nematic liquid crystal phase state at an operating temperature below the thermal decomposition temperature of the organic compound;
The mobility value of the organic compound determined from the transit time of the electric charge based on the transient photocurrent measurement by Time-of-flight (TOF) method is 10 −4 cm 2 / Vs or more,
,and
An organic semiconductor material characterized in that mobility of a sample diluted with 3 to 15 mol% of a hydrocarbon compound is observed to be smaller than mobility of a sample before dilution .