JP5337424B2 - ゴムホースの製法 - Google Patents
ゴムホースの製法 Download PDFInfo
- Publication number
- JP5337424B2 JP5337424B2 JP2008196261A JP2008196261A JP5337424B2 JP 5337424 B2 JP5337424 B2 JP 5337424B2 JP 2008196261 A JP2008196261 A JP 2008196261A JP 2008196261 A JP2008196261 A JP 2008196261A JP 5337424 B2 JP5337424 B2 JP 5337424B2
- Authority
- JP
- Japan
- Prior art keywords
- rubber hose
- mandrel
- water
- aqueous liquid
- silicone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
(X)下記(A)と(B)との混合液からなり、粘度が2000〜5000mPa・sの範囲に調整された水性液。
(A)水分量が40〜94重量%の範囲のシリコーン系エマルジョン。
(B)水溶性増粘剤。
(X)下記(A)と(B)との混合液からなり、粘度が2000〜5000mPa・sの範囲に調整された水性液。
(A)水分量が40〜94重量%の範囲のシリコーン系エマルジョン。
(B)水溶性増粘剤。
ジメチルシリコーンエマルジョン(東レ・ダウコーニング社製、シリコーンエマルジョンDKQ−2、シリコーン成分量60重量%、水分量40重量%、粘度400mPa・s)。
上記ジメチルシリコーンエマルジョンAを、水で希釈して、シリコーン成分量6重量%、水分量94重量%、粘度11mPa・sに調製した。
上記ジメチルシリコーンエマルジョン(東レ・ダウコーニング社製、シリコーンエマルジョンDKQ−2)を濃縮した、ジメチルシリコーンエマルジョン(シリコーン成分量65重量%、水分量35重量%、粘度600mPa・s)。
上記ジメチルシリコーンエマルジョンAを、水で希釈して、シリコーン成分量3重量%、水分量97重量%、粘度5mPa・sに調製した。
セルロース系増粘剤(CMC)(第一工業社製、セロゲン4H)
ポリアクリル酸系増粘剤(ポリアクリル酸)(日本触媒社製、アクアリックAS58)
下記の表1に示すように、シリコーン系エマルジョンA100部に、水溶性増粘剤A1.2部(シリコーン系エマルジョンA中の水分量100部に対して、水溶性増粘剤A3部)を添加して、粘度2000mPa・sの水性液を調製した。なお、上記水性液の粘度は、室温(25℃)にてB型粘度計(東京計器社製、No.3)を使用して測定した。
下記の表1および表2に示すように、配合成分および配合量を変更する以外は、水性液Aの調製に準じて、各水性液を調製した。
(ホース材料の調製)
NBR−PVC〔NBR/PVC=70/30(重量比)、AN量:33.5〕(日本ゼオン社製、ニポール1203JNS)100部と、ステアリン酸(花王社製、ルナックS30)1部と、MgO(協和化学社製、協和マグ♯150)10部と、DBUナフトエ酸塩(ダイソー社製、DA−500)2部と、SRF級カーボンブラック(東海カーボン社製、シーストS)30部と、エーテルエステル系可塑剤(旭電化社製、アデカサイザーRS107)25部と、硫黄(鶴見化学工業社製、金華印粉砕硫黄)1部と、チアゾール系加硫促進剤(OBS)としてN−オキシジエチレン−2−ベンゾチアゾリルスルフェンアミド(OBS)(大内新興化学工業社製、ノクセラーMSA−G)1部とを配合し、これらをバンバリー、ロールを用いて混練することにより、ホース材料(NBR−PVC材料)を調製した。
押し出し成形により、未加硫ゴムホース(直径35mm、厚み5mm、長さ300mm)を作製した。つぎに、この未加硫ゴムホースを、上記水性液A中に1分間浸漬した。つづいて、この水性液に浸漬した未加硫ゴムホースを、マンドレル(金属製、直径35mm)に挿入し、その状態でスチーム加硫缶(関西ロール社製)にて160℃×35分加硫処理を行った。その後、加硫ゴムホースから上記マンドレルを抜き取り、ゴムホース(加硫ゴムホース)を作製した。
下記の表3および表4に示すように、未加硫ゴムホースを浸漬する際の水性液の種類を変更する以外は、実施例1に準じて、ゴムホース(加硫ゴムホース)を作製した。
各ゴムホースを切断し、外観を肉眼で観察した。評価は、アバタ(エアー溜まり)が発生したものを×、アバタが発生しなかったものを○とした。
マンドレルの差し込み性や抜き取り性、水性液の洗浄性の各項目について評価を行った。
(差し込み性)
マンドレルを差し込む際に、現行法より力がいるものを×、力がいらないものを○とした。
マンドレルを抜き取る際に、現行法より力がいるものを×、力がいらないものを○とした。
40℃のお湯にてゴムホースを30分間洗浄した。その後、指先をホース内に入れて、ヌメリ(シリコーン系エマルジョンの残渣)があったものを×、ヌメリがないものを○とした。
Claims (3)
- マンドレルに未加硫ゴムホースを嵌挿するに際し、マンドレルの外周面および未加硫ゴムホースの内周面の少なくとも一方に予め下記(X)の水性液を塗布する工程と、上記マンドレルに未加硫ゴムホースを嵌挿した状態で未加硫ゴムホースをスチーム加硫する工程と、上記加硫工程を経た後で加硫されたゴムホースからマンドレルを引き抜く工程とを備えたことを特徴とするゴムホースの製法。
(X)下記(A)と(B)との混合液からなり、粘度が2000〜5000mPa・sの範囲に調整された水性液。
(A)水分量が40〜94重量%の範囲のシリコーン系エマルジョン。
(B)水溶性増粘剤。 - 上記(B)の水溶性増粘剤が、セルロース系増粘剤である請求項1記載のゴムホースの製法。
- 上記セルロース系増粘剤が、カルボキシメチルセルロース、メチルセルロース、カルボキシメチルセルロースナトリウムである請求項2記載のゴムホースの製法。