JP5331167B2 - Wetting detection sheet - Google Patents
Wetting detection sheet Download PDFInfo
- Publication number
- JP5331167B2 JP5331167B2 JP2011142769A JP2011142769A JP5331167B2 JP 5331167 B2 JP5331167 B2 JP 5331167B2 JP 2011142769 A JP2011142769 A JP 2011142769A JP 2011142769 A JP2011142769 A JP 2011142769A JP 5331167 B2 JP5331167 B2 JP 5331167B2
- Authority
- JP
- Japan
- Prior art keywords
- water
- soluble
- insoluble
- detection sheet
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、水濡れを検知する水濡れ検知シートに関する。 The present invention relates to a water wetting detection sheet for detecting water wetting.
一般的に、携帯電話機などの電子機器は、故障した場合に修理することが保証されている。故障の原因としては、物理的な破損、経時的な劣化、電子機器内部の水濡れ(水没)などが挙げられる。物理的な破損、または経時的な劣化の場合は、外観を視認することで、容易に故障の原因を判断することができる。一方、電子機器内部の水濡れの場合は、経時的に水が蒸発して痕跡がなくなってしまうため、故障の原因を判断することは容易ではない。 In general, electronic devices such as mobile phones are guaranteed to be repaired if they fail. The cause of the failure includes physical damage, deterioration with time, water wetting inside the electronic device (submersion), and the like. In the case of physical damage or deterioration over time, the cause of the failure can be easily determined by visually recognizing the appearance. On the other hand, when the inside of the electronic device is wet, water evaporates over time and the trace disappears, so it is not easy to determine the cause of the failure.
そこで、携帯電話機などの電子機器には、水濡れを検出するための水濡れ検知シートが設けられている。たとえば、水濡れ検知シートとして、吸水性紙の上に水溶性インクを所定のパターンに印刷したものが提案されている(例えば、特許文献1参照)。 Therefore, an electronic device such as a mobile phone is provided with a water wetting detection sheet for detecting water wetting. For example, a water wetness detection sheet in which water-soluble ink is printed on a water-absorbing paper in a predetermined pattern has been proposed (see, for example, Patent Document 1).
特許文献1には、水溶性インクが所定のパターンに印刷された第1の吸水性紙と、第1の吸水性紙の印刷面側に積層された遮水性透明シートと、第1の吸水性紙の反対側の面に積層された第2の吸水性紙とを有する水濡れ検知シート(水没判定ラベル)が開示されている。この水濡れ検知シートでは、第2の吸水性紙側から水が浸入すると、水溶性インク中に含まれていた色素が溶解して、第1の吸水性紙中に拡散する。したがって、水溶性インクのパターンの変化から、水濡れを検知することができる。 Patent Document 1 discloses a first water-absorbing paper on which water-soluble ink is printed in a predetermined pattern, a water-impervious transparent sheet laminated on the printing surface side of the first water-absorbing paper, and a first water-absorbing paper. A water wetting detection sheet (submergence determination label) having a second water-absorbing paper laminated on the opposite surface of the paper is disclosed. In this water wetting detection sheet, when water enters from the second water-absorbing paper side, the pigment contained in the water-soluble ink is dissolved and diffused into the first water-absorbing paper. Therefore, the wetness of water can be detected from the change in the pattern of the water-soluble ink.
特許文献1の水濡れ検知シートでは、少量の水が浸入した場合に、水溶性インクが第1の吸水性紙中を拡散することで、水濡れを検知することができる。しかしながら、大量の水が浸入した場合、または大量の水が長時間存在した場合は、水溶性インクが第1の吸水性紙から流失してしまい、水濡れが生じたことを示す痕跡がなくなってしまう。その結果、電子機器内部が水に濡れたかどうかの判断が困難になることがある。 In the water wetness detection sheet of Patent Document 1, when a small amount of water permeates, water wetness can be detected by diffusing the water-soluble ink in the first water absorbent paper. However, when a large amount of water has infiltrated or a large amount of water has existed for a long time, the water-soluble ink has been washed away from the first water-absorbent paper, and there is no trace of the occurrence of water wetting. End up. As a result, it may be difficult to determine whether the inside of the electronic device is wet.
本発明は、かかる点に鑑みてなされたものであり、大量の水と接触した場合、または少量の水と長時間接触した場合であっても、水濡れを確実に検知することができる水濡れ検知シートを提供することを目的とする。 The present invention has been made in view of such a point, and even when contacted with a large amount of water or when contacted with a small amount of water for a long period of time, water wetting can be reliably detected. An object is to provide a detection sheet.
本発明の水濡れ検知シートは、少なくとも一部の領域が非水溶性色素で着色されている非水溶性基材フィルムと、非水溶性基材フィルムの上に配置されている水溶性基材層とを有する。 The water-wetting detection sheet of the present invention includes a water-insoluble base film in which at least a partial region is colored with a water-insoluble dye, and a water-soluble base layer disposed on the water-insoluble base film. And have.
本発明によれば、大量の水と接触した場合、または少量の水と長時間接触した場合であっても、水濡れを確実に検知することができる。 According to the present invention, wetting can be reliably detected even when a large amount of water is contacted or even when a small amount of water is contacted for a long time.
本発明の水濡れ検知シートは、非水溶性色素で着色されている非水溶性基材フィルムと、非水溶性基材フィルムの上に配置されている水溶性基材層とを有する。 The water-wetting detection sheet of the present invention has a water-insoluble substrate film colored with a water-insoluble dye, and a water-soluble substrate layer disposed on the water-insoluble substrate film.
以下、本発明の水濡れ検知シートの各構成要素について説明する。 Hereinafter, each component of the water wetness detection sheet | seat of this invention is demonstrated.
[非水溶性基材フィルム]
非水溶性基材フィルムは、水溶性基材層を支持する支持部材である。また、非水溶性基材フィルムは、非水溶性色素で着色されており、水溶性基材層が水に溶解した場合に、水濡れ検知シートが水に濡れたことを示す表示部材でもある。
[Water-insoluble substrate film]
The water-insoluble substrate film is a support member that supports the water-soluble substrate layer. Further, the water-insoluble substrate film is colored with a water-insoluble pigment, and is also a display member that indicates that the water-wetting detection sheet has been wetted with water when the water-soluble substrate layer is dissolved in water.
非水溶性基材フィルムの種類は、水に対して溶解しないものであれば、特に限定されない。たとえば、非水溶性基材フィルムは、樹脂フィルムである。非水溶性基材フィルムの素材の例には、ポリエチレンテレフタレート(PET)、ポリプロピレン(PP)、ポリエチレン(PE)が含まれる。非水溶性基材フィルムの膜厚は、特に限定されないが、通常10〜250μmの範囲内である。 The type of the water-insoluble substrate film is not particularly limited as long as it does not dissolve in water. For example, the water-insoluble substrate film is a resin film. Examples of the material of the water-insoluble substrate film include polyethylene terephthalate (PET), polypropylene (PP), and polyethylene (PE). Although the film thickness of a water-insoluble base film is not specifically limited, Usually, it exists in the range of 10-250 micrometers.
非水溶性基材フィルムは、非水溶性色素で着色されている。非水溶性色素は、水に対して溶解しないものであれば、特に限定されない。非水溶性色素の例には、有機顔料、無機顔料、分散染料、油溶性色素が含まれる。これらの非水溶性色素は、単独で使用してもよいし、2種以上を組み合わせて使用してもよい。 The water-insoluble substrate film is colored with a water-insoluble pigment. The water-insoluble dye is not particularly limited as long as it does not dissolve in water. Examples of water-insoluble dyes include organic pigments, inorganic pigments, disperse dyes, and oil-soluble dyes. These water-insoluble dyes may be used alone or in combination of two or more.
非水溶性基材フィルムへの着色方法は、特に限定されない。着色方法の例には、予め非水溶性色素を添加した樹脂材料から非水溶性基材フィルムを形成する方法や、非水溶性色素を含むインクを非水溶性色素フィルムに印刷または塗布する方法などが含まれる。非水溶性色素を含むインクの例には、紫外線硬化インク、熱硬化インクが含まれる。これらの中では、有機溶剤を必要とせず、かつ硬化速度が速い観点から、紫外線硬化インクが特に好ましい。 The coloring method to a water-insoluble base film is not specifically limited. Examples of coloring methods include a method of forming a water-insoluble substrate film from a resin material to which a water-insoluble pigment has been added in advance, a method of printing or applying an ink containing a water-insoluble pigment on a water-insoluble pigment film, etc. Is included. Examples of the ink containing a water-insoluble pigment include ultraviolet curable ink and thermosetting ink. Among these, an ultraviolet curable ink is particularly preferable from the viewpoint of not requiring an organic solvent and having a high curing speed.
非水溶性基材フィルムの着色パターンは、特に限定されない。着色パターンの例には、ドット模様、水玉模様、ストライプ模様、格子模様、各種文字、各種記号が含まれる。また、非水溶性基材フィルムの全体が、非水溶性色素により着色されていてもよい。着色パターンの位置は、水溶性基材層が水に溶解した場合に、水溶性基材層側から視認することができれば、特に限定されない。たとえば、着色パターンは、非水溶性基材フィルムの表面または裏面に形成されていてもよいし、非水溶性基材フィルムの内部に形成されていてもよい。 The coloring pattern of the water-insoluble substrate film is not particularly limited. Examples of the coloring pattern include a dot pattern, a polka dot pattern, a stripe pattern, a lattice pattern, various characters, and various symbols. Further, the entire water-insoluble substrate film may be colored with a water-insoluble pigment. The position of the coloring pattern is not particularly limited as long as it can be visually recognized from the water-soluble substrate layer side when the water-soluble substrate layer is dissolved in water. For example, the coloring pattern may be formed on the front or back surface of the water-insoluble substrate film, or may be formed inside the water-insoluble substrate film.
本発明の水濡れ検知シートを被着物へ貼付する場合には、非水溶性基材フィルムの裏面(水溶性基材層が配置されていない側の面)に接着層を形成してもよい。接着層を構成する接着剤の種類は、使用中の剥離を防止する観点から、水に対して溶解しないものが好ましい。そのような接着剤の例には、ホットメルト系接着剤、合成ゴム系接着剤、エポキシ樹脂系接着剤、ウレタン系接着剤、アクリル系接着剤が含まれる。なお、接着層は、粘着剤により構成されていてもよい。 When the wetness detection sheet of the present invention is attached to an adherend, an adhesive layer may be formed on the back surface of the water-insoluble substrate film (the surface on which the water-soluble substrate layer is not disposed). The type of the adhesive constituting the adhesive layer is preferably one that does not dissolve in water from the viewpoint of preventing peeling during use. Examples of such adhesives include hot melt adhesives, synthetic rubber adhesives, epoxy resin adhesives, urethane adhesives, and acrylic adhesives. In addition, the contact bonding layer may be comprised with the adhesive.
[水溶性基材層]
水溶性基材層は、非水溶性基材フィルムの着色パターンを隠蔽する遮蔽部材である。水溶性基材層は、本発明の水濡れ検知シートが大量の水と接触した場合、または少量の水と長時間接触した場合、水に溶解する。
[Water-soluble substrate layer]
The water-soluble substrate layer is a shielding member that hides the coloring pattern of the water-insoluble substrate film. The water-soluble substrate layer dissolves in water when the wetness detection sheet of the present invention comes into contact with a large amount of water or when it contacts with a small amount of water for a long time.
水溶性基材層の素材は、前述の機能を実現できるものであれば、特に限定されない。水溶性基材層の素材の例には、水解紙などの水溶性の紙材、メチルセルロース、エチルセルロース、ヒドロキシエチルセルロース、ポリビニルアルコールなどの水溶性樹脂、水溶性インク、着色した澱粉などの水溶性化合物が含まれる。水溶性基材層の膜厚は、特に限定されないが、通常10〜300μmの範囲内である。 The material of the water-soluble substrate layer is not particularly limited as long as it can realize the above-described function. Examples of the material of the water-soluble substrate layer include water-soluble paper materials such as hydrolyzed paper, water-soluble resins such as methyl cellulose, ethyl cellulose, hydroxyethyl cellulose, and polyvinyl alcohol, water-soluble inks, and water-soluble compounds such as colored starch. included. Although the film thickness of a water-soluble base material layer is not specifically limited, Usually, it exists in the range of 10-300 micrometers.
水溶性基材層は、非水溶性基材フィルムの上に配置されている。非水溶性基材フィルムの上に水溶性基材層を配置する方法は、特に限定されない。たとえば、水溶性基材層が水溶性の紙材、フィルム形状の水溶性樹脂の場合、接着剤を用いて非水溶性基材フィルムと水溶性基材層とを接着すればよい。また、非水溶性基材フィルムの上に水溶性樹脂または水溶性化合物を含む液体を塗布し、乾燥させて、非水溶性基材フィルムの上に水溶性基材層を形成してもよい。 The water-soluble substrate layer is disposed on the water-insoluble substrate film. The method for disposing the water-soluble substrate layer on the water-insoluble substrate film is not particularly limited. For example, when the water-soluble substrate layer is a water-soluble paper material or a film-shaped water-soluble resin, the water-insoluble substrate film and the water-soluble substrate layer may be bonded using an adhesive. Alternatively, a liquid containing a water-soluble resin or a water-soluble compound may be applied on the water-insoluble substrate film and dried to form a water-soluble substrate layer on the water-insoluble substrate film.
非水溶性基材フィルムと水溶性基材層とを接着剤を用いて接着する場合、接着剤の種類は、特に限定されない。たとえば、水溶性のアクリル系溶剤型の接着剤を使用できる。また、透明であれば、水溶性の接着剤ではなく、非水溶性の接着剤を使用してもよい。 When bonding a water-insoluble base film and a water-soluble base material layer using an adhesive agent, the kind of adhesive agent is not specifically limited. For example, a water-soluble acrylic solvent type adhesive can be used. Moreover, if it is transparent, you may use a water-insoluble adhesive instead of a water-soluble adhesive.
以上の構成によれば、本発明の水濡れ検知シートが大量の水に接触した場合、または本発明の水濡れ検知シートが少量の水と長時間接触した場合、水溶性基材層が溶解して、非水溶性基材フィルムの着色パターンが出現する。したがって、ユーザーは、本発明の水濡れ検知シートが大量の水に接触した、または少量の水と長時間接触したことを確認することができる。 According to the above configuration, when the water wetting detection sheet of the present invention is in contact with a large amount of water, or when the water wetting detection sheet of the present invention is in contact with a small amount of water for a long time, the water-soluble substrate layer is dissolved. Thus, a coloring pattern of the water-insoluble substrate film appears. Therefore, the user can confirm that the water wetness detection sheet of the present invention has been in contact with a large amount of water or has been in contact with a small amount of water for a long time.
本発明の水濡れ検知シートは、水溶性基材層の表面または内部に配置されている水溶性色素をさらに有していてもよい。 The water wetting detection sheet of the present invention may further have a water-soluble dye disposed on the surface or inside of the water-soluble substrate layer.
[水溶性色素]
水溶性色素は、水溶性基材層の表面または内部に所定のパターンで配置されている。本発明の水濡れ検知シートが水に接触する前は、水溶性色素は、水溶性基材層に保持されている。本発明の水濡れ検知シートが水に接触した場合、水溶性色素は、水に溶解または分散して、毛細管現象により、水溶性基材層の表面または内部を移動する。その結果、水溶性色素の着色パターンが変化するため、ユーザーは、本発明の水濡れ検知シートが水に接触したかどうかを確認することができる。
[Water-soluble dye]
The water-soluble dye is arranged in a predetermined pattern on the surface or inside of the water-soluble substrate layer. Before the water-wetting detection sheet of the present invention comes into contact with water, the water-soluble dye is held on the water-soluble substrate layer. When the water-wetting detection sheet of the present invention comes into contact with water, the water-soluble dye is dissolved or dispersed in water and moves on the surface or inside of the water-soluble substrate layer by capillary action. As a result, since the coloring pattern of the water-soluble dye changes, the user can confirm whether or not the water wetness detection sheet of the present invention has contacted water.
水溶性色素の種類は、水に対して溶解または分散しうるものであれば、特に限定されない。水溶性色素の例には、食紅、水溶性タール色素、植物系色素が含まれる。これらの水溶性色素は、単独で使用してもよいし、2種以上を組み合わせて使用してもよい。 The type of water-soluble dye is not particularly limited as long as it can be dissolved or dispersed in water. Examples of water-soluble pigments include food colors, water-soluble tar pigments, and plant pigments. These water-soluble dyes may be used alone or in combination of two or more.
水溶性色素の位置は、本発明の水濡れ検知シートが水に接触した場合に、水溶性色素の着色パターンの変化をユーザーが外部から視認できれば、特に限定されない。たとえば、水溶性色素は、水溶性基材層の表面に配置されていてもよいし、裏面に配置されていてもよいし、内部に配置されていてもよい。また、水溶性色素の着色パターンは、水溶性基材層の表面全体を覆っていなければ特に限定されないが、非水溶性基材フィルムの着色パターンと異なっていることが好ましい。着色パターンの例には、ドット模様、水玉模様、ストライプ模様、格子模様、各種文字、各種記号が含まれる。 The position of the water-soluble dye is not particularly limited as long as the user can visually recognize the change in the coloring pattern of the water-soluble dye from the outside when the water wetness detection sheet of the present invention comes into contact with water. For example, the water-soluble dye may be disposed on the surface of the water-soluble substrate layer, may be disposed on the back surface, or may be disposed inside. The coloring pattern of the water-soluble pigment is not particularly limited as long as it does not cover the entire surface of the water-soluble substrate layer, but is preferably different from the coloring pattern of the water-insoluble substrate film. Examples of the coloring pattern include a dot pattern, a polka dot pattern, a stripe pattern, a lattice pattern, various characters, and various symbols.
水溶性色素を水溶性基材層の表面、裏面または内部に配置する方法は、特に限定されない。たとえば、水溶性色素を含む水溶性インクを水溶性基材層に印刷または塗布すればよい。水溶性インクに含まれる溶媒の種類は、水溶性色素の種類に応じて適宜選択される。溶媒の例には、メチルエチルケトン、エタノール、アセトン、水が含まれる。 The method for disposing the water-soluble dye on the front surface, back surface or inside of the water-soluble substrate layer is not particularly limited. For example, a water-soluble ink containing a water-soluble pigment may be printed or applied to the water-soluble substrate layer. The type of solvent contained in the water-soluble ink is appropriately selected according to the type of water-soluble dye. Examples of the solvent include methyl ethyl ketone, ethanol, acetone, and water.
なお、本発明の水濡れ検知シートが水溶性色素を有する場合、水溶性基材層の表面は、水溶性色素を保持する観点、および毛細管現象により水溶性色素が溶解または分散した水を移動させる観点から、粗面化または多孔質化されていることが好ましい。たとえば、水溶性基材層が水溶性樹脂からなる場合、水溶性基材層の表面に粗面化処理または多孔質化処理を行うことが好ましい。粗面化処理の例には、エンボス加工法、サンドブラスト法、水溶性基材層の表面を薬液処理する方法が含まれる。 In addition, when the water-wetting detection sheet of the present invention has a water-soluble dye, the surface of the water-soluble substrate layer moves water in which the water-soluble dye is dissolved or dispersed by the viewpoint of retaining the water-soluble dye and capillary action. From the viewpoint, it is preferable that the surface is roughened or made porous. For example, when the water-soluble substrate layer is made of a water-soluble resin, it is preferable to perform a roughening treatment or a porous treatment on the surface of the water-soluble substrate layer. Examples of the roughening treatment include an embossing method, a sand blasting method, and a method for chemical treatment of the surface of the water-soluble substrate layer.
以上の構成によれば、本発明の水濡れ検知シートが少量の水と接触した場合、水溶性色素が水に溶解または分散して水溶性基材層の表面または内部を移動する。その結果、水溶性色素の着色パターンが変化するため、ユーザーは、本発明の水濡れ検知シートが水に接触したかどうかを確認できる。また、本発明の水濡れ検知シートが大量の水に接触した場合、または本発明の水濡れ検知シートが少量の水と長時間接触した場合、水溶性基材層が溶解して、非水溶性基材フィルムの着色パターンが出現する。したがって、ユーザーは、本発明の水濡れ検知シートが大量の水に接触した、または少量の水と長時間接触したことを確認することができる。 According to the above configuration, when the water wetting detection sheet of the present invention comes into contact with a small amount of water, the water-soluble dye is dissolved or dispersed in water and moves on the surface or inside of the water-soluble substrate layer. As a result, since the coloring pattern of the water-soluble dye changes, the user can confirm whether or not the water wetness detection sheet of the present invention has contacted water. In addition, when the water wetness detection sheet of the present invention is in contact with a large amount of water, or when the water wettability detection sheet of the present invention is in contact with a small amount of water for a long time, the water-soluble substrate layer dissolves and becomes insoluble in water. A coloring pattern of the base film appears. Therefore, the user can confirm that the water wetness detection sheet of the present invention has been in contact with a large amount of water or has been in contact with a small amount of water for a long time.
また、本発明の水濡れ検知シートは、水溶性色素が配置された水溶性基材層の上に不透水性透明フィルムをさらに有していてもよい。 Moreover, the water wetness detection sheet | seat of this invention may further have a water-impermeable transparent film on the water-soluble base material layer by which the water-soluble pigment | dye is arrange | positioned.
[不透水性透明フィルム]
不透水性透明フィルムは、空気中の水分による誤検知を防止する。すなわち、空気中の水分が水溶性基材層に吸収された場合、水溶性色素が吸収された水に溶解または分散して、水溶性色素の着色パターンが変化してしまうことがある。このように、本発明の水濡れ検知シートが液体の水に接触していないにも関わらず、水溶性色素の着色パターンが変化してしまうことは好ましくない。そこで、不透水性透明フィルムは、空気中の水分が水溶性基材層に吸収されることを妨げることで、空気中の水分による誤検知を防止する。液体の水は、水溶性基材層の側面(断面)から水溶性基材層内部に浸入するため、本発明の水濡れ検知シートが液体の水に接触した場合は、水溶性色素の着色パターンが変化する。
[Impermeable transparent film]
The impermeable transparent film prevents false detection due to moisture in the air. That is, when water in the air is absorbed by the water-soluble substrate layer, the water-soluble dye may be dissolved or dispersed in the absorbed water, and the coloring pattern of the water-soluble dye may change. As described above, it is not preferable that the coloring pattern of the water-soluble dye changes even though the water-wetting detection sheet of the present invention is not in contact with liquid water. Therefore, the water-impermeable transparent film prevents erroneous detection due to moisture in the air by preventing moisture in the air from being absorbed by the water-soluble base material layer. Since liquid water permeates into the water-soluble substrate layer from the side surface (cross section) of the water-soluble substrate layer, when the water wetness detection sheet of the present invention comes into contact with liquid water, the coloring pattern of the water-soluble dye Changes.
不透水性透明フィルムの種類は、水を透過させず、かつ水溶性基材層を外部から視認できるものであれば、特に限定されない。たとえば、不透水性透明フィルムは、樹脂フィルムである。不透水性透明フィルムの素材の例には、ポリエチレンテレフタレート(PET)、ポリ塩化ビニル(PVC)が含まれる。 The type of the water-impermeable transparent film is not particularly limited as long as it does not allow water to permeate and the water-soluble substrate layer can be visually recognized from the outside. For example, the water-impermeable transparent film is a resin film. Examples of the material of the water-impermeable transparent film include polyethylene terephthalate (PET) and polyvinyl chloride (PVC).
以上の構成によれば、本発明の水濡れ検知シートが高湿度下に置かれた場合であっても、空気中の水分による誤検知を防止し、液体の水に接触したかどうかを正確に検知することができる。 According to the above configuration, even when the water wetting detection sheet of the present invention is placed under high humidity, it is possible to prevent erroneous detection due to moisture in the air and accurately determine whether it has come into contact with liquid water. Can be detected.
本発明の水濡れ検知シートを製造する方法は、特に限定されない。たとえば、本発明の水濡れ検知シートは、1)着色した非水溶性基材を準備する第1の工程と、2)非水溶性基材の上に水溶性基材層を配置する第2の工程とにより製造されうる。本発明の水濡れ検知シートが水溶性色素を有する場合は、上記1)および2)の工程の間または後に、3)水溶性基材層を水溶性色素で着色する第3の工程を行う。また、本発明の水濡れ検知シートが不透水性透明フィルムを有する場合は、上記1)〜3)の工程の間または後に、4)水溶性基材層の上に不透水性透明フィルムを配置する第4の工程を行う。 The method for producing the water wetness detection sheet of the present invention is not particularly limited. For example, the water wetness detection sheet of the present invention includes 1) a first step of preparing a colored water-insoluble substrate, and 2) a second step of disposing a water-soluble substrate layer on the water-insoluble substrate. It can be manufactured by a process. When the water wetness detection sheet | seat of this invention has a water-soluble pigment | dye, 3) The 3rd process of coloring a water-soluble base material layer with a water-soluble pigment | dye is performed during or after the process of said 1) and 2). Moreover, when the water-wetting detection sheet | seat of this invention has a water-impermeable transparent film, it arrange | positions a water-impermeable transparent film on the water-soluble base material layer between or after the process of said 1) -3). A fourth step is performed.
第1の工程では、非水溶性色素で所望のパターンに着色された非水溶性基材フィルムを準備する。たとえば、非水溶性基材フィルムを部分的に着色する場合には、非水溶性色素を含むインクを所望の着色パターンとなるように塗布し、乾燥または硬化させればよい。また、非水溶性基材フィルム全体を着色する場合には、予め非水溶性色素を含有させた樹脂材料を用いて、非水溶性基材フィルムを形成すればよい。 In the first step, a water-insoluble substrate film colored in a desired pattern with a water-insoluble dye is prepared. For example, when a water-insoluble substrate film is partially colored, an ink containing a water-insoluble dye may be applied so as to have a desired coloring pattern, and dried or cured. Moreover, what is necessary is just to form a water-insoluble base film using the resin material which previously contained the water-insoluble pigment | dye, when coloring the whole water-insoluble base film.
第2の工程では、第1の工程で準備した非水溶性基材フィルムの上に水溶性基材層を配置する。たとえば、水溶性基材層が水溶性の紙材またはフィルム形状の水溶性樹脂の場合、非水溶性基材フィルムと水溶性基材層とを接着剤を用いて接着すればよい。また、水溶性樹脂または水溶性化合物を含む液体から水溶性基材層を形成する場合、非水溶性基材フィルムの上に水溶性樹脂または水溶性化合物を含む液体を塗布し、乾燥させればよい。 In the second step, a water-soluble substrate layer is disposed on the water-insoluble substrate film prepared in the first step. For example, when the water-soluble substrate layer is a water-soluble paper material or a water-soluble resin in the form of a film, the water-insoluble substrate film and the water-soluble substrate layer may be bonded using an adhesive. Also, when forming a water-soluble substrate layer from a liquid containing a water-soluble resin or a water-soluble compound, if a liquid containing a water-soluble resin or a water-soluble compound is applied on a water-insoluble substrate film and dried, Good.
任意に行われる第3の工程では、水溶性基材層を水溶性色素で着色する。たとえば、水溶性基材層の表面または裏面に水溶性色素を含むインクを塗布すればよい。 In the optional third step, the water-soluble substrate layer is colored with a water-soluble dye. For example, an ink containing a water-soluble dye may be applied to the front or back surface of the water-soluble substrate layer.
なお、第2の工程に先立ち、第3の工程を行ってもよい。すなわち、水溶性基材層が紙材やフィルム形状の水溶性樹脂である場合、水溶性色素で水溶性基材層を着色した後に、着色された水溶性基材層を非水溶性基材フィルム上に積層してもよい。 Note that the third step may be performed prior to the second step. That is, when the water-soluble substrate layer is a water-soluble resin in the form of paper or film, after coloring the water-soluble substrate layer with a water-soluble dye, the colored water-soluble substrate layer is converted into a water-insoluble substrate film. It may be laminated on top.
任意に行われる第4の工程では、水溶性基材層の上に不透水性透明フィルムを配置する。たとえば、水溶性基材層の上に不透水性透明フィルムを積層すればよい。また、水溶性基材層の上に液体状の不透水性透明フィルムの材料を塗布し、硬化させてもよい。 In the 4th process performed arbitrarily, a water-impermeable transparent film is arrange | positioned on a water-soluble base material layer. For example, an impermeable transparent film may be laminated on the water-soluble substrate layer. Alternatively, a liquid impermeable transparent film material may be applied on the water-soluble substrate layer and cured.
以下、添付した図面を参照して本発明の実施の形態について説明する。 Hereinafter, embodiments of the present invention will be described with reference to the accompanying drawings.
(実施の形態1)
図1は、実施の形態1に係る水濡れ検知シート100の模式的な断面図である。図1に示すように、水濡れ検知シート100は、非水溶性樹脂フィルム110(非水溶性基材フィルム)と、非水溶性樹脂フィルム110の上に積層された白色の水解紙120(水溶性基材層)とを有している。
(Embodiment 1)
FIG. 1 is a schematic cross-sectional view of a water wetness detection sheet 100 according to the first embodiment. As shown in FIG. 1, the water wetness detection sheet 100 includes a water-insoluble resin film 110 (water-insoluble substrate film) and a white water-degrading paper 120 (water-soluble) laminated on the water-insoluble resin film 110. Base material layer).
非水溶性樹脂フィルム110は、例えばポリエチレンテレフタレート(PET)フィルムである。非水溶性樹脂フィルム110は、非水溶性色素によって全体が青色に着色されている。また、非水溶性樹脂フィルム110と水解紙120は、水溶性の接着剤130で接着されている。 The water-insoluble resin film 110 is, for example, a polyethylene terephthalate (PET) film. The entire water-insoluble resin film 110 is colored blue with a water-insoluble pigment. In addition, the water-insoluble resin film 110 and the hydrolytic paper 120 are bonded with a water-soluble adhesive 130.
水濡れ検知シート100は、非水溶性の接着剤140を介して被着物150に接着されうる。 The water wetness detection sheet 100 can be adhered to the adherend 150 via a water-insoluble adhesive 140.
以上の構成によれば、水に接触する前の水濡れ検知シート100の外観は、白色の無地である。一方、水濡れ検知シート100が大量の水に接触した場合、または少量の水と長時間接触した場合は、水解紙120が水に溶解してしまうため、水濡れ検知シート100の外観は、全体が青色となる。 According to the above configuration, the appearance of the water wetting detection sheet 100 before coming into contact with water is white and plain. On the other hand, when the water wetting detection sheet 100 comes into contact with a large amount of water, or when it comes into contact with a small amount of water for a long time, the water-disintegrating paper 120 is dissolved in water. Turns blue.
以上のように、本実施の形態にかかる水濡れ検知シートによれば、大量の水と接触した場合、または少量の水と長時間接触した場合であっても、水濡れを確実に検知することができる。 As described above, according to the water wetting detection sheet according to the present embodiment, even when it comes into contact with a large amount of water or when it has been in contact with a small amount of water for a long time, it can reliably detect water wetting. Can do.
(実施の形態2)
図2は、実施の形態2に係る水濡れ検知シート200の模式的な断面図である。なお、図1に示される実施の形態1の水濡れ検知シート100と同一の構成要素については、同一の符号を付してその説明を省略する。
(Embodiment 2)
FIG. 2 is a schematic cross-sectional view of a water wetness detection sheet 200 according to the second embodiment. In addition, about the component same as the water-wetting detection sheet | seat 100 of Embodiment 1 shown by FIG. 1, the same code | symbol is attached | subjected and the description is abbreviate | omitted.
図2に示すように、水濡れ検知シート200は、非水溶性樹脂フィルム110(非水溶性基材フィルム)と、水解紙120(水溶性基材層)と、水解紙120内に配置された水溶性色素210とを有している。水解紙120には、水溶性色素210によって赤色のドット模様が形成されている。 As shown in FIG. 2, the water wetness detection sheet 200 is disposed in the water-disintegrating paper 120, the water-insoluble resin film 110 (water-insoluble base film), the water-disintegrating paper 120 (water-soluble base material layer). And a water-soluble dye 210. A red dot pattern is formed on the water-disintegrating paper 120 by the water-soluble dye 210.
以上の構成によれば、水に接触する前の水濡れ検知シート200の外観は、赤色のドット模様である。一方、水濡れ検知シート200が少量の水に接触した場合、水溶性色素210が溶解または分散した水が水解紙120内を毛細管現象により移動するため、水濡れ検知シート200の外観は、全体が赤色となるか、赤色のドット模様が滲んだ状態となる。さらに、水濡れ検知シート200が大量の水に接触した場合、または少量の水と長時間接触した場合は、水解紙120が水に溶解してしまうため、水濡れ検知シート200の外観は、全体が青色となる。 According to the above configuration, the appearance of the water wetting detection sheet 200 before coming into contact with water is a red dot pattern. On the other hand, when the water wetting detection sheet 200 comes into contact with a small amount of water, the water in which the water-soluble dye 210 is dissolved or dispersed moves in the water-disintegrating paper 120 by capillary action. It becomes red or a red dot pattern is blurred. Furthermore, when the water wetting detection sheet 200 is in contact with a large amount of water or when it is in contact with a small amount of water for a long time, the water disintegration paper 120 is dissolved in water. Turns blue.
以上のように、本実施の形態に係る水濡れ検知シートによれば、水濡れ検知シートが接触する水の量および水との接触時間に関わらず、水濡れを確実に検知することができる。 As described above, according to the water wetting detection sheet according to the present embodiment, it is possible to reliably detect water wetting regardless of the amount of water and the contact time with water.
(実施の形態3)
図3は、実施の形態3に係る水濡れ検知シート300の模式的な断面図である。なお、図2に示される実施の形態2の水濡れ検知シート200と同一の構成要素については、同一の符号を付してその説明を省略する。
(Embodiment 3)
FIG. 3 is a schematic cross-sectional view of a water wetting detection sheet 300 according to the third embodiment. In addition, about the same component as the water-wetting detection sheet | seat 200 of Embodiment 2 shown by FIG. 2, the same code | symbol is attached | subjected and the description is abbreviate | omitted.
図3に示すように、水濡れ検知シート300は、非水溶性樹脂フィルム110(非水溶性基材フィルム)と、水解紙120(水溶性基材層)と、水解紙120内に配置された水溶性色素210と、水解紙120の上に配置された不透水性透明樹脂フィルム310とを有している。 As shown in FIG. 3, the water wetting detection sheet 300 is disposed in the water-disintegrating paper 120, the water-insoluble resin film 110 (water-insoluble base film), the water-disintegrating paper 120 (water-soluble base material layer), and the water-dissolving paper 120. It has a water-soluble dye 210 and a water-impermeable transparent resin film 310 disposed on the hydrolyzed paper 120.
不透水性透明樹脂フィルム310は、例えばポリエチレンテレフタレート(PET)フィルムである。不透水性透明樹脂フィルム310は、水解紙120の上にラミネートされている。 The impermeable transparent resin film 310 is, for example, a polyethylene terephthalate (PET) film. The impermeable transparent resin film 310 is laminated on the hydrolytic paper 120.
本実施の形態に係る水濡れ検知シートによれば、高湿度下に置かれた場合であっても、空気中の水分による誤検知を防止し、液体の水との接触を正確に検知することができる。 According to the water wetting detection sheet according to the present embodiment, even when placed under high humidity, it prevents false detection due to moisture in the air and accurately detects contact with liquid water. Can do.
以下、本発明を実施例を参照して詳細に説明するが、本発明はこれらの実施例により限定されない。 EXAMPLES Hereinafter, although this invention is demonstrated in detail with reference to an Example, this invention is not limited by these Examples.
1.水濡れ検知シートの作製
[実施例]
紫外線硬化インク(UV161シリーズ;株式会社T&K TOKA)を塗布して全体を青色に着色したポリエチレンテレフタレートフィルムの上に、接着剤を用いて水解紙(水溶性タック紙;リンテック株式会社)を接着した。その後、水解紙にドット模様となるように赤色の水溶性色素を含むインク(WS−7;東洋インキ株式会社)を塗布し、実施例の水濡れ検知シートを作製した。
1. Preparation of water wetting detection sheet [Example]
On the polyethylene terephthalate film, which was coated with ultraviolet curable ink (UV161 series; T & K TOKA Co., Ltd.) and colored blue as a whole, hydrolyzed paper (water-soluble tack paper; Lintec Corporation) was adhered using an adhesive. Thereafter, an ink (WS-7; Toyo Ink Co., Ltd.) containing a red water-soluble pigment was applied to the water-dissolving paper so as to form a dot pattern, and a water-wetting detection sheet of the example was produced.
[比較例1]
上質紙(片艶クラフト紙;城山製紙株式会社)に上述の赤色の水溶性色素を含むインクをドット模様となるように塗布し、比較例1の水濡れ検知シートを作製した。
[Comparative Example 1]
The ink containing the above-mentioned red water-soluble pigment was applied to high-quality paper (single gloss kraft paper; Shiroyama Paper Co., Ltd.) so as to form a dot pattern, and a water wetness detection sheet of Comparative Example 1 was produced.
[比較例2]
油分を除去した上質紙(片艶クラフト紙;城山製紙株式会社)に上述の赤色の水溶性色素を含むインクをドット模様となるように塗布し、比較例2の水濡れ検知シートを作製した。
[Comparative Example 2]
The ink containing the above-mentioned red water-soluble pigment was applied in a dot pattern to high-quality paper from which oil was removed (single gloss kraft paper; Shiroyama Paper Co., Ltd.) to prepare a water wetness detection sheet of Comparative Example 2.
2.水濡れ痕跡試験
作製した各水濡れ検知シート(実施例、比較例1または比較例2)から、5mm角の試験片を9枚ずつ切り出した。そして、各試験片を100mLの水道水に浸漬した。次いで、試験片を水道水に浸漬してから1秒後、10分後、20分後、30分後、60分(1時間)後、120分(2時間)後、720分(12時間)後および1440分(24時間)後に試験片をそれぞれ採取した。採取した試験片を乾燥させて、水濡れの痕跡を観察した。本試験は、水濡れ検知シートが大量の水に長時間接触した場合を再現したものである。
2. Water Wetting Trace Test Nine 5 mm square test pieces were cut out from each prepared water wetting detection sheet (Example, Comparative Example 1 or Comparative Example 2). And each test piece was immersed in 100 mL tap water. Next, 1 second, 10 minutes, 20 minutes, 30 minutes, 60 minutes (1 hour), 120 minutes (2 hours), and 720 minutes (12 hours) after the test piece is immersed in tap water. Specimens were collected after and after 1440 minutes (24 hours). The collected test piece was dried, and traces of water wetting were observed. This test reproduces the case where the water wetness detection sheet is in contact with a large amount of water for a long time.
図4は、水濡れ痕跡試験の試験結果を示した写真である。図4に示されるように、水に浸漬する前は、実施例、比較例1および比較例2のすべての試験片において、赤色のドット模様が観察された。水道水に浸漬して1秒経過後、すべての試験片において、赤色の水溶性色素が面方向に移動して、赤色のドットが拡大した(滲んだ)。比較例1の試験片では、赤色の水溶性色素が周囲の水道水に溶出し始めた。 FIG. 4 is a photograph showing the test result of the water wetting trace test. As shown in FIG. 4, before dipping in water, red dot patterns were observed in all the test pieces of Examples, Comparative Examples 1 and 2. After 1 second from immersion in tap water, the red water-soluble pigment moved in the surface direction in all the test pieces, and the red dots expanded (bleeded). In the test piece of Comparative Example 1, the red water-soluble pigment began to elute into the surrounding tap water.
比較例1および比較例2の試験片では、水道水に浸漬する時間が長くなるにつれて、赤色の水溶性色素による色彩が薄くなった。これは、赤色の水溶性色素が周囲の水道水に溶出したためと考えられる。その結果、比較例1および比較例2の試験片では、水濡れの痕跡が消失してしまい、水濡れが生じたか否かを判別することが困難になった。 In the test pieces of Comparative Example 1 and Comparative Example 2, the color due to the red water-soluble pigment became lighter as the time of immersion in tap water became longer. This is presumably because the red water-soluble pigment was eluted in the surrounding tap water. As a result, in the test pieces of Comparative Example 1 and Comparative Example 2, traces of water wetting disappeared, making it difficult to determine whether water wetting occurred.
一方、実施例の試験片でも、水道水に浸漬する時間が長くなるにつれて、赤色の水溶性色素による色彩が薄くなったが、その代わりに青色の非水溶性色素による色彩が濃くなった。これは、水解紙が水道水に溶解し、青色に着色されたポリエチレンテレフタレートフィルムを視認できるようになったためと考えられる。このように、実施例の試験片では、水道水に長時間浸漬しても、水濡れが生じたことを示す痕跡が残っていた。 On the other hand, in the test pieces of the examples, as the time of immersion in tap water became longer, the color due to the red water-soluble pigment became lighter, but instead the color due to the blue water-insoluble pigment became darker. This is presumably because the water-disintegrating paper was dissolved in tap water, and the blue-colored polyethylene terephthalate film became visible. As described above, in the test piece of the example, even when immersed in tap water for a long time, a trace indicating that the water was wet remained.
以上の結果から、本発明の水濡れ検知シートは、水濡れ検知シートが大量の水に長時間接触した場合であっても、水濡れ検知シートが水に接触したか否かを確実に検知できることがわかる。 From the above results, the water wetting detection sheet of the present invention can reliably detect whether or not the water wetting detection sheet has been in contact with water even when the water wetting detection sheet has been in contact with a large amount of water for a long time. I understand.
本発明の水濡れ検知シートは、例えば、携帯電話機や携帯ゲーム機などの電子機器における水没ラベル、自動車や電動歯ブラシなどの防水試験、家庭用の石油タンク内などに流入した水分の検査に有用である。 The water wetness detection sheet of the present invention is useful for, for example, submerging labels in electronic devices such as mobile phones and portable game machines, waterproof tests for automobiles, electric toothbrushes, etc., and inspection of moisture that has flowed into household oil tanks. is there.
100,200,300 水濡れ検知シート
110 非水溶性樹脂フィルム
120 水解紙
130,140 接着剤
150 被着物
210 水溶性色素
310 不透水性透明樹脂フィルム
100, 200, 300 Water wetting detection sheet 110 Water-insoluble resin film 120 Water-degrading paper 130, 140 Adhesive 150 Adherent 210 Water-soluble dye 310 Water-impermeable transparent resin film
Claims (3)
前記非水溶性基材フィルムの上に配置され、表面または内部に所定のパターンで水溶性色素が配置されている水溶性基材層と、
前記水溶性基材層の上に配置された不透水性透明フィルムと、
を有し、
前記非水溶性基材フィルムの着色パターンは、前記水溶性色素の配置パターンと異なる、
水濡れ検知シート。 A water-insoluble substrate film in which at least a part of the region is colored with a water-insoluble pigment;
A water-soluble substrate layer that is disposed on the water -insoluble substrate film, and a water-soluble pigment is disposed on the surface or in a predetermined pattern ; and
An impermeable transparent film disposed on the water-soluble substrate layer;
I have a,
The coloring pattern of the water-insoluble substrate film is different from the arrangement pattern of the water-soluble pigment.
Water wetness detection sheet.
前記水溶性基材層は、水解紙である、
請求項1に記載の水濡れ検知シート。 The water-insoluble substrate film is a resin film,
The water-soluble substrate layer is hydrolytic paper.
The water wetness detection sheet according to claim 1.