JP5329806B2 - Absorbent article surface sheet - Google Patents
Absorbent article surface sheet Download PDFInfo
- Publication number
- JP5329806B2 JP5329806B2 JP2007339651A JP2007339651A JP5329806B2 JP 5329806 B2 JP5329806 B2 JP 5329806B2 JP 2007339651 A JP2007339651 A JP 2007339651A JP 2007339651 A JP2007339651 A JP 2007339651A JP 5329806 B2 JP5329806 B2 JP 5329806B2
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- convex
- roll
- absorbent article
- layer sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
本発明は、吸収性物品の表面シートに関する。特に、着用者の肌に直接当てて用いられる吸収性物品の表面シートに関する。 The present invention relates to a surface sheet of an absorbent article. In particular, it is related with the surface sheet of the absorbent article used directly on a wearer's skin.
使い捨ておむつ、生理用ナプキン、パンティーライナー、及び使い捨ておむつといった吸収性物品は通常着用者の肌に当接して、液体の吸収保持等に用いられる。特に肌荒れのしやすいところに用いられることが多く、しかも長時間にわたって着用されることがある。そのため柔らかく肌あたりのやさしいものが望まれる。他方、吸収性物品には液吸収性及び液保持性が要求される。 Absorbent articles such as disposable diapers, sanitary napkins, panty liners, and disposable diapers are usually in contact with the wearer's skin and used for absorbing and holding liquids. In particular, it is often used in places that are prone to rough skin, and may be worn for a long time. For this reason, a soft and gentle skin is desired. On the other hand, the absorbent article is required to have liquid absorbability and liquid retention.
上記のような機能性でありかつ触感のよい表面シートの開発が試みられている。例えば特許文献１には、２層の不織シートを複数の間欠的に設けたピンエンボスにより接合し、下層のシートを熱乾燥により選択的に収縮させて、上層のシートを波打つように離間させた表面シートが開示されている。特許文献２には、上層シート及び下層シートからなる表面シートであって、内部が空洞になっている多数の凸部を有する表面シートが開示されている。この特許文献２に記載の表面シートの凸部の底部は矩形であり、該凸部は全体として直方体又は截頭四角錐体状にされている。
しかしながら、特許文献１に記載の表面シートでは、凹部における接合部によってシート同士が固定されているが、それ以外の部位ではシートとシートの間が離間しており、外部からの圧力に弱く、構造が維持し難い。また、特許文献２に記載の表面シートで例示されている構造では、形状維持性は高いが、凸部が柔軟に動き難く、違和感や硬い印象を持たれる場合がある。
An attempt has been made to develop a surface sheet having the above-described functionality and good tactile sensation. For example, in Patent Document 1, two layers of non-woven sheets are joined by a plurality of intermittent pin embosses, the lower layer sheet is selectively shrunk by heat drying, and the upper layer sheet is separated so as to wave. A surface sheet is disclosed. Patent Document 2 discloses a surface sheet that is composed of an upper layer sheet and a lower layer sheet and has a large number of convex portions that are hollow inside. The bottom part of the convex part of the surface sheet described in Patent Document 2 is rectangular, and the convex part as a whole has a rectangular parallelepiped or truncated quadrangular pyramid shape.
However, in the surface sheet described in Patent Document 1, the sheets are fixed to each other by the joint portion in the recess, but the sheet is separated from the sheet in other portions, and the structure is weak against external pressure. Is difficult to maintain. Moreover, in the structure illustrated with the surface sheet of patent document 2, although shape maintenance property is high, a convex part cannot move flexibly and there may be a sense of incongruity and a hard impression.
本発明は、吸収性物品の高い液吸収性及び液保持性を実現し、表面の液残りが抑制され、しかもクッション性に富み肌当たりがやさしく柔らかい吸収性物品の表面シートの提供を目的とする。また本発明は特に、なめらかでソフトな触感、表面の液残りの抑制、高粘性液の良好な透過処理性、ドレープ性に優れ、凸部の構造に柔軟性を有するため着用者に違和感を与え難い吸収性物品の表面シートを提供する。さらには体圧がかかり表面シートが潰されたときであっても液戻りしにくく、また、一度潰されてもシートの厚みを回復しやすい、着用後にもソフトな触感が長時間持続され、シート面と平行な方向の通気性の良い吸収性物品の表面シートの提供を目的とする。 An object of the present invention is to provide a surface sheet of an absorbent article that achieves high liquid absorbency and liquid retention of the absorbent article, suppresses liquid residue on the surface, is rich in cushioning properties, and soft to the skin. . In addition, the present invention is particularly smooth and soft to the touch, suppressed liquid residue on the surface, good permeation of high-viscosity liquid, excellent drapeability, and the convex structure is flexible, giving the wearer an uncomfortable feeling. Provided is a top sheet of a difficult absorbent article. Furthermore, even when the body pressure is applied and the surface sheet is crushed, it is difficult for the liquid to return, and even if crushed once, the thickness of the sheet is easy to recover. An object of the present invention is to provide a top sheet of an absorbent article having good air permeability in a direction parallel to the surface.
上記の課題は、凸部が略千鳥状に配設された、繊維からなる表面シートであって、前記凸部は内部に空間を保持し、該凸部はこれより細幅の尾根部により互いに連結されて凸部列をなし、該凸部列はこの間に配される溝部が折れ線状になるよう並列し、前記折れ線状の溝部は前記尾根部の両側において谷部を有する吸収性物品の表面シートによって解決された。 The above-mentioned problem is a surface sheet made of fibers in which convex portions are arranged in a substantially staggered pattern, wherein the convex portions hold a space inside, and the convex portions are mutually connected by narrower ridges. Connected to form a row of convex portions, and the rows of convex portions are arranged in parallel so that the groove portions arranged between them are in the form of a polygonal line, and the polygonal line-like groove portions have a valley portion on both sides of the ridge portion. Solved by the sheet.
本発明の吸収性物品の表面シートは、吸収性物品の高い液吸収性及び液保持性を示すとともに表面の液残りを抑制し、しかもクッション性に富み、肌当たりが柔らかく、やさしい風合いを有する。また本発明の表面シートは、なめらかでソフトな触感、表面の液残りの抑制、高粘性液の良好な透過処理性、ドレープ性に優れ、凸部の構造に柔軟性を有するため着用者に違和感を与え難い。さらには体圧がかかり表面シートが潰されたときであっても液戻りしにくく、また、一度潰されてもシートの厚みを回復しやすく、着用後にもソフトでサラッとした触感が長時間持続されるという優れた作用効果を奏し、シート面と平行な方向の通気性の良いシートが得られる。 The surface sheet of the absorbent article of the present invention exhibits a high liquid absorbability and liquid retention of the absorbent article, suppresses liquid residue on the surface, is rich in cushioning properties, has a soft touch, and has a gentle texture. In addition, the surface sheet of the present invention is smooth and soft to the touch, suppresses liquid residue on the surface, excellent permeation of high-viscosity liquid, is excellent in drapeability, and has a convex structure so that it is uncomfortable for the wearer. Is hard to give. Furthermore, even when the body sheet is crushed and the top sheet is crushed, it is difficult for the liquid to return, and even if crushed once, the thickness of the sheet is easy to recover, and the soft and smooth feel after wearing lasts for a long time. Thus, a sheet having good air permeability in the direction parallel to the sheet surface can be obtained.
以下、本発明を、その好ましい実施形態を示す図面を参照しながら詳細に説明する。
図１は本発明の吸収性物品の表面シートの一実施形態の要部を模式的に示す部分斜視図であり、図２は図１における領域ＩＩの部分を多少異なる角度からみて拡大して示す斜視図である。本実施形態の表面シート１０は上層シート１及び下層シート２を有する。この表面シート１０は例えば生理用ナプキンや使い捨ておむつなどの吸収性物品に適用することが好ましく、下層シート２の下面に吸収体を配し、上層シート１を着用者の肌に直接当てて使用することができる。
Hereinafter, the present invention will be described in detail with reference to the drawings showing preferred embodiments thereof.
FIG. 1 is a partial perspective view schematically showing a main part of one embodiment of a surface sheet of an absorbent article of the present invention, and FIG. 2 is an enlarged view showing a portion of region II in FIG. 1 from a slightly different angle. It is a perspective view. The topsheet 10 of this embodiment has an upper layer sheet 1 and a lower layer sheet 2. The top sheet 10 is preferably applied to an absorbent article such as a sanitary napkin or a disposable diaper, for example, and an absorber is disposed on the bottom surface of the lower layer sheet 2 so that the upper layer sheet 1 is directly applied to the skin of the wearer. be able to.
本実施形態の吸収性物品の表面シート１０の上層シート１側、すなわち着用者の肌に当接する側に、多数の凸部３が略千鳥状に設けられている。凸部３は上層シート１の凹凸賦型により形成されたドーム形状の空間６を内部に保持しており、極めて柔らかく肌当たりの良いやさしい触感が得られる。すなわち、凸部３がエアクッションとして作用し、着用者の肌の起伏があるところであっても、柔らかくフィットしてソフトな感触を与えることができる。また溝部に沿って空気が移動しやすいことに加えて、凸部内部のドーム状空間６が空気を保持し、これが出入りしうる。また、軟便等の高粘性の液体や半固形物の***があっても、まず谷部にストックし、続いて粘性が低い液体を凸部内部の空間６や表面シートの下層シートへ移動させて隠蔽して吸収するため、着用者に不快感を与えない。特に乳幼児に対しては、軟便や下痢便等がそのまま肌に触れ続けることが避けられ、肌を清潔に保ち、肌荒れやかぶれの抑制に効果的である。 A large number of convex portions 3 are provided in a substantially staggered pattern on the upper sheet 1 side of the topsheet 10 of the absorbent article of the present embodiment, that is, on the side in contact with the skin of the wearer. The convex portion 3 holds a dome-shaped space 6 formed by the concave-convex shaping of the upper layer sheet 1, and an extremely soft and soft touch-sensitive touch is obtained. That is, even if the convex part 3 acts as an air cushion and a wearer's skin has undulations, it can fit softly and give a soft touch. Further, in addition to air easily moving along the groove portion, the dome-shaped space 6 inside the convex portion holds air, which can enter and exit. In addition, even if there is excretion of high-viscosity liquid such as loose stool or semi-solid, first stock it in the valley, then move the low-viscosity liquid to the space 6 inside the convex part or the lower layer sheet of the top sheet Because it is concealed and absorbed, it does not cause discomfort to the wearer. Especially for infants, it is possible to avoid loose stool or diarrhea stool from touching the skin as it is, and to keep the skin clean and effective in suppressing rough skin and rash.
本実施形態の表面シートにおいて上記の略千鳥状に配置された凸部３は、尾根部により連結され凸部列１１（１１ａ、１１ｂ、１１ｃ、１１ｄ・・・）をなしている。図２においては、凸部列１１ａ、凸部列１１ｂ、及び凸部列１１ｃの３列の凸部列を示している。そして、各凸部列１１ａ，１１ｂ，１１ｃは並列し、隣在する凸部列の間には、尾根部５の両側に配された谷部４を繋ぐようにして形成された折れ線状の溝部８が配されている。この溝部８の底面は平面ではなく、谷部４の間に小山をなすように小凸部９が交互に配され、起伏のある底面形状とされている。また、尾根部５の内部にはトンネル状空間７（図３、図４参照）が設けられ、隣在するドーム状の凸部内部の空間６が互いに連繋されている。 The convex portions 3 arranged in a substantially staggered manner in the top sheet of the present embodiment are connected by a ridge portion to form a convex portion row 11 (11a, 11b, 11c, 11d...). In FIG. 2, the three convex part rows of the convex part row | line | column 11a, the convex part row | line | column 11b, and the convex part row | line | column 11c are shown. And each convex part row | line | column 11a, 11b, 11c is parallel, and the polygonal groove part formed so that the trough part 4 distribute | arranged to the both sides of the ridge part 5 might be connected between adjacent convex part rows | lines. 8 is arranged. The bottom surface of the groove portion 8 is not a flat surface, but small convex portions 9 are alternately arranged so as to form a small mountain between the valley portions 4 to form a undulating bottom surface shape. Further, a tunnel-like space 7 (see FIGS. 3 and 4) is provided inside the ridge portion 5, and the spaces 6 inside the adjacent dome-shaped convex portions are connected to each other.
上述のようにして、本実施形態の表面シートは、凸部が連結されてなす山脈状の凸部列が、緩やかに曲がった渓谷状の溝部を挟んで並設された、特有の外表面形状を有する。そして、凸部内部のドーム状空間６はトンネル状空間７により繋がれており、この特有の内部空間と上記特有の外表面形状とが立体的ネットワークを形成する。このネットワーク構造がなす吸収性物品における表面シートの個別の作用は後に詳しく述べるが、これにより本実施形態の表面シートはドレープ性（複雑な起伏を有する肌表面に対しても柔らかく変形して座屈することなくフィットし、着用者の動き等により肌の起伏形状が変わっても追従しうる性質）を有する。例えば股間部のように複雑に起伏し動きのある部分に当接して用いるときに特に高い効果が発揮され、表面シートと肌との間に過度の隙間を与えることなく当接し、その良好なフィット性が維持される。さらに、表面シート全体としては低目付であっても十分な厚みが実現されクッション性に富み、しかも凸部等が一度体圧等で潰されても形状が復元して、ソフトな触感を失うことなく持続される。また、液体や軟便等の吸収性においては、上記特有の外表面形状と内部構造とのネットワークにより、液体等を吸収体に移行させる、あるいは隠蔽する作用が高い。これにより、液体や軟便等の***があった後でも不快感を与えず、また軟便等の逆戻りによる付着などを抑え清潔な肌状態を維持する。 As described above, the surface sheet according to the present embodiment has a unique outer surface shape in which the mountain-shaped convex portion rows formed by connecting the convex portions are arranged side by side with the gently curved valley-shaped groove portion interposed therebetween. Have And the dome-shaped space 6 inside the convex part is connected by the tunnel-shaped space 7, and this specific internal space and the above-mentioned specific outer surface shape form a three-dimensional network. The individual action of the topsheet in the absorbent article formed by this network structure will be described in detail later, whereby the topsheet of this embodiment is draped (bently deformed and buckled even on the skin surface having complex undulations). It fits without any change and has the property of being able to follow even if the undulation shape of the skin changes due to the movement of the wearer. For example, it is particularly effective when used in contact with a part that moves up and down in a complicated manner such as the crotch part, and it makes contact without giving an excessive gap between the top sheet and the skin, and its good fit Sex is maintained. Furthermore, even if the surface sheet as a whole is low in weight, it has a sufficient thickness and is cushioning, and even if the convex part etc. is crushed by body pressure etc. once, the shape is restored and the soft feel is lost. It will last without. Moreover, in the absorptivity of a liquid, a loose stool, etc., the effect | action which transfers or conceals a liquid etc. to an absorber with the network of the said specific outer surface shape and internal structure is high. Thereby, even after excretion of liquid or loose stool, no discomfort is given, and adhesion due to reversal of loose stool or the like is suppressed and a clean skin state is maintained.
図３は図１のＩＩＩ−ＩＩＩ線断面を示す断面図である。この断面においては凸部３が尾根部５により連結され、かつドーム状の凸部内部の空間６がトンネル状空間７で空間的に連続するようにされている。これにより、軟便等を空間６及び空間７がなす内部空間ネットワークに、効果的に隠蔽する。この軟便等の透過処理作用について以下のように説明することができる。軟便等の***があると、表面シートの外表面においては、まずこれが溝部８の底の方に移行して留まり、その後、あるいはそれと同時に表面シートの繊維間を通過し軟便等が内部空間６に保持される。ここで内部空間６に収納された軟便等は次第に表面シートの下側に配される吸収体等によって水分を吸われ乾燥していき、逆戻りしない状態になり着用者に対する良好な触感が維持される。そして、本実施形態の表面シートはドーム状の凸部内部の空間６が尾根部内部のトンネル状空間７により連繋されている。このため、表面シートに例えば大きな体圧がかかったときにも、尾根部等による変形抑制により肌当接面側への逆戻りを抑制・防止することが可能となる。また、空間６内に収納された軟便等を、トンネル状空間７を通じて表面シートの面方向に拡散させて、肌当接面側への逆戻りを抑制・防止する。これにより、軟便や下り物に含まれる高粘性の液体や半固形物の***があっても、極めて良好な着用感及び肌の清潔な状態が長時間にわたって保たれる。 3 is a cross-sectional view showing a cross section taken along line III-III in FIG. In this cross section, the convex portion 3 is connected by the ridge portion 5, and the space 6 inside the dome-shaped convex portion is spatially continuous in the tunnel-shaped space 7. Thereby, soft stool or the like is effectively concealed in the internal space network formed by the space 6 and the space 7. The permeabilizing action of soft stool or the like can be explained as follows. If there is excretion of loose stool or the like, on the outer surface of the top sheet, it first moves toward the bottom of the groove 8 and then passes between the fibers of the top sheet. Retained. Here, the soft stool or the like stored in the internal space 6 is gradually dampened by moisture absorbed by an absorbent body or the like disposed on the lower side of the top sheet, and is not reversed, maintaining good tactile sensation for the wearer. . And the surface sheet of this embodiment has the space 6 inside the dome-shaped convex part connected by the tunnel-like space 7 inside the ridge part. For this reason, even when a large body pressure is applied to the top sheet, for example, it is possible to suppress / prevent back return to the skin contact surface side by suppressing deformation by the ridge portion or the like. In addition, soft stool or the like stored in the space 6 is diffused in the surface direction of the surface sheet through the tunnel-like space 7 to suppress / prevent back-return to the skin contact surface side. Thereby, even if there is excretion of high-viscosity liquid or semi-solid matter contained in loose stool or falling goods, a very good wearing feeling and a clean state of the skin can be maintained for a long time.
本実施形態の表面シートにおいては凸部３の高さｈｔは特に限定されないが、０．７〜７ｍｍであることが好ましく、より好ましくは１〜２．５ｍｍである。また本実施形態においては凸部の高さｈｔより尾根部５の高さｈｏが低くなるようにされており、凸部３と尾根部５の高さの比（ｈｏ／ｈｔ）は０．１５〜０．８が好ましい。なお、本実施形態における尾根部５の高さｈｏより小凸部９の高さｈｓ（図５参照）との関係をここでいうと、該小凸部９は尾根部より低くなるようにされており、尾根部５と小凸部９の高さの比（ｈｓ／ｈｏ）は０．１〜０．９であることが好ましい。凸部の頂点のＭＤ方向の間隔については、特に限定されないが、１．５〜１０ｍｍであることが好ましく、より好ましくは２ｍｍ〜６ｍｍである。ここでＭＤ方向とは不織布等のシート材が製造時に流れる方向をいい、「Ｍａｃｈｉｎｅ Ｄｉｒｅｃｔｉｏｎ」の略語であり、単にＭＤと表記してその方向を示すことがある。これに対して、ＣＤ方向とは上記ＭＤ方向に直交する方向であり、「Ｃｒｏｓｓ Ｄｉｒｅｃｔｉｏｎ」の略語であり、単にＣＤと表記してその方向を示すことがある。 The height h t of the protrusions 3 in the topsheet of the present embodiment is not particularly limited, but is preferably 0.7～7Mm, more preferably 1 to 2.5 mm. Further and in this embodiment it is as the height h o of the ridge portions 5 than the height h t of the protrusions is lower, the ratio of the height of the protrusions 3 and the ridge 5 (h o / h t) Is preferably 0.15 to 0.8. Incidentally, speaking of the relationship between the height h s of the height h o from the small protrusions 9 of the ridge section 5 in the present embodiment (see FIG. 5) where the small protrusion 9 so as to be lower than ridges it is the height ratio of the ridge portion 5 small protrusions 9 (h s / h o) is preferably from 0.1 to 0.9. Although it does not specifically limit about the space | interval of the MD direction of the vertex of a convex part, It is preferable that it is 1.5-10 mm, More preferably, it is 2 mm-6 mm. Here, the MD direction refers to a direction in which a sheet material such as a nonwoven fabric flows during manufacture, and is an abbreviation of “Machine Direction”, which is sometimes simply expressed as MD to indicate the direction. On the other hand, the CD direction is a direction orthogonal to the MD direction, which is an abbreviation of “Cross Direction”, and may be simply expressed as CD to indicate the direction.
本発明において凸部ないし尾根部の内部の空間とは表面シートを構成する所定のシート（本実施形態においては上層シート１）の所定の面側（通常は肌当接面側）に突出した凸形状の賦形部に対応してこの裏面側（通常は非肌当接面側）に形成された凹形状の賦形部をいう。このように凸部が内部空間を有することを凸部の中空構造ということもある。上記所定のシートの裏面（通常は非肌当接面）を別の所定の平面（例えば下層シート２ないしは吸収体の表面）に積層したときに、上記内部空間においては、両面の間に０．１ｍｍ以上の間隔があることが好ましい。この間隔は、凸部内部のドーム状空間６における最も広い部分における間隔ｈｄ（図３参照）で０．１５〜６．５ｍｍであることが好ましく、より好ましくは０．２ｍｍ〜１．２ｍｍである。尾根部内部のトンネル状空間７における最も広い部分におる間隔ｈｎで０．１〜５ｍｍであることが好ましく、より好ましくは０．１ｍｍ〜１ｍｍである。 In the present invention, the convex portion or the space inside the ridge portion is a convex portion protruding to a predetermined surface side (usually the skin contact surface side) of a predetermined sheet (upper sheet 1 in this embodiment) constituting the surface sheet. It refers to a concave shaped portion formed on the back side (usually the non-skin contact surface side) corresponding to the shaped shaped portion. Such a convex portion having an internal space is sometimes referred to as a hollow structure of the convex portion. When the back surface (usually the non-skin contact surface) of the predetermined sheet is laminated on another predetermined plane (for example, the lower layer sheet 2 or the surface of the absorber), in the internal space, 0. It is preferable that there is an interval of 1 mm or more. This interval is preferably 0.15 to 6.5 mm, more preferably 0.2 mm to 1.2 mm in the interval h d (see FIG. 3) in the widest portion of the dome-shaped space 6 inside the convex portion. is there. Is preferably 0.1~5mm at intervals h n that dwell in the widest portion of the ridge inside the tunnel-like spaces 7, and more preferably from 0.1 mm to 1 mm.
図４は図１のＩＶ−ＩＶ線断面を示す断面図である。この断面においては、尾根部５の両側に溝部を構成する谷部４が配され、さらにその両側に凸部３が配されている。同図でも分かるように、尾根部５はトンネル構造にされている。ここで凸部３の形状について詳しくいうと、凸部３は機能的に頂部３ａ、肩部３ｂ、側壁部３ｃに区分することができる。本実施形態の凸部３は頂部３ａから肩部３ｂを通り側壁部３ｃにかけて丸みを帯びた略山形の形状であり、内部に中空空間６を有する。このように、丸みを帯びた凸部とすることにより、着用者の運動等により吸収性物品が多少ずれたときにも、擦れる感じが抑えられなめらかな触感が得られる。 4 is a cross-sectional view showing a cross section taken along line IV-IV in FIG. In this cross section, trough portions 4 constituting the groove portions are disposed on both sides of the ridge portion 5, and convex portions 3 are disposed on both sides thereof. As can be seen from the figure, the ridge portion 5 has a tunnel structure. If it says in detail about the shape of the convex part 3 here, the convex part 3 can be functionally divided into the top part 3a, the shoulder part 3b, and the side wall part 3c. The convex portion 3 of the present embodiment has a substantially mountain shape that is rounded from the top portion 3a through the shoulder portion 3b to the side wall portion 3c, and has a hollow space 6 therein. Thus, by using the rounded convex part, even when the absorbent article is slightly displaced due to the wearer's movement or the like, the feeling of rubbing is suppressed and a smooth tactile sensation is obtained.
さらに本実施形態の表面シートにおいては、凸部３が上述のとおり丸みを帯びたこぶ状にされている。このようにすることで、表面シートの柔らかでなめらかな触感とともに、見た目にも柔らかく、なめらかで、しかも優美な印象を与える。また、特に凸部の肩部３ｂから頂部３ａにかけて山形に緩やかに突起した形状を有するため、着用者の肌との接触面積が小さい。このように表面シートと着用者との接触面積を減少させることにより、液体を一度吸収したシートが面接触してベタつく感じを大幅に低減し、サラッとした状態を実現する。このような表面シートの、柔らかさ、なめらかさ、サラッとした触感、ないしはそのような印象を与える見た目の良さは、凸部を矩形基調の直方体状又は截頭四角錐体状としたのでは得がたい。 Furthermore, in the surface sheet of this embodiment, the convex part 3 is made into the rounded hump shape as above-mentioned. By doing in this way, the surface sheet has a soft and smooth tactile sensation, and also looks soft, smooth and graceful. Moreover, since it has the shape which protruded in the mountain shape from the shoulder part 3b of the convex part to the top part 3a especially, a contact area with a wearer's skin is small. By reducing the contact area between the top sheet and the wearer in this way, the sheet that once absorbed the liquid is brought into surface contact and the sticky feeling is greatly reduced, and a smooth state is realized. The softness, smoothness, smooth tactile sensation, or good appearance that gives such an impression is difficult to obtain if the convex part is a rectangular solid rectangular parallelepiped or truncated quadrangular pyramid. .
本実施形態において凸部３の側壁部３ｃは、繊維が疎になって形成された細孔（図せず）ないし薄部（図示せず）を有する。これは典型的には、後述する歯を有するロールの噛み合わせによるシート成形において、単一厚みの不織布シートが凹凸賦形されることにより、不織布シートは全体的に引伸ばされながらもＭＤ方向に繊維が配列する傾向を有するため、繊維が集まる部分と繊維が少なくなる部分が形成されやすいことによる。他方、製造工程中に局部的に繊維が集中する部分が形成される。 In this embodiment, the side wall part 3c of the convex part 3 has pores (not shown) or thin parts (not shown) formed by sparse fibers. Typically, in sheet forming by meshing rolls having teeth, which will be described later, a nonwoven fabric sheet having a single thickness is unevenly shaped, so that the nonwoven fabric sheet is stretched in the MD direction as a whole. This is because the fibers tend to be arranged, so that a portion where the fibers gather and a portion where the fibers are reduced are easily formed. On the other hand, a portion where the fibers concentrate locally during the manufacturing process is formed.
ここで凸部側壁部３ｃは、凸部の高さｈｔ（図３参照）の略中間点より下方（非肌当接面側）にあたる部分に配されている。そして凸部側壁部３ｃは谷部４につながる凸部３の裾野にあたる位置にあり、かつ谷部４を配した溝部８は折れ線状に蛇行しているため溝部における***物の流動が抑えられ、谷部４に軟便等の粘性のある液体ないし半固形物が一時溜まる。 Here, the convex portion side wall portion 3c is disposed in a portion corresponding to a lower portion (on the non-skin contact surface side) than a substantially middle point of the convex portion height h t (see FIG. 3). And the convex part side wall part 3c exists in the position which hits the base of the convex part 3 connected to the trough part 4, and since the groove part 8 which arranged the trough part 4 meanders in the shape of a broken line, the flow of excrement in a groove part is suppressed, A viscous liquid such as loose stool or semi-solid is temporarily stored in the valley 4.
本実施形態の表面シートにおいては谷部４において上層シート１と下層シート２とがヒートエンボスにより接合されている。ただし、この接合方法は特に限定されず。超音波エンボスやホットメルトによる接着方法でもよい。谷部の幅ｗｂ（図４参照）は特に限定されないが、０．５〜３ｍｍであることが通常の吸収性物品の寸法との関係を考慮したときに実際的である。 In the top sheet of the present embodiment, the upper layer sheet 1 and the lower layer sheet 2 are joined by heat embossing at the valleys 4. However, this joining method is not particularly limited. An adhesion method using ultrasonic embossing or hot melt may be used. The width w b of the valley (see FIG. 4) is not particularly limited, but it is practical that the width is 0.5 to 3 mm in consideration of the relationship with the dimensions of a normal absorbent article.
本実施形態の表面シートにおいて、尾根部５の幅ｗｏは凸部３の幅ｗｔより細いものとされている。これらの具体的な幅は特に限定されないが、例えば尾根部５の幅ｗｏと凸部３の幅ｗｔとの比（ｗｏ／ｗｔ）を０．１〜０．６の範囲とすることが好ましい。 In the topsheet of this embodiment, the width w o of the ridge portions 5 is intended narrower than the width w t of the protrusions 3. Although these specific widths are not particularly limited, for example, the ratio (w o / w t ) between the width w o of the ridge portion 5 and the width w t of the convex portion 3 is in the range of 0.1 to 0.6. It is preferable.
図５は図１におけるＶ−Ｖ線断面を拡大して示した断面図である。同図に示した断面においては、各凸部が溝部８を挟んで連設されているが、この溝部には小凸部９が配されている。本実施形態において、この小凸部９は、尾根部５より低くされており、一方谷部４の底部（最も低い非肌当接面側となる部分）より高さの有る状態にされている。この小凸部９により、溝部８の底面が平坦なＵ字溝状にならず、上述したように機能的な凹凸面とされている。また、本実施形態において、この小凸部９は下層シート２と接しているが、谷部４のようにエンボス接合はされていない。このように、略千鳥格子状の凸部３と谷部４の配列中に、高さや、幅、接合状態の異なる尾根部５と小凸部９とが配設されていることにより、単に線状シールで溝状部を形成したのではなし得ないドレープ性等の機能を示す。 5 is an enlarged cross-sectional view taken along the line VV in FIG. In the cross section shown in the same figure, each convex part is connected with the groove part 8 interposed therebetween, and a small convex part 9 is arranged in this groove part. In this embodiment, this small convex part 9 is made lower than the ridge part 5, and has a height higher than the bottom part of the valley part 4 (the part on the lowest non-skin contact surface side). . Due to the small convex portions 9, the bottom surface of the groove portion 8 does not have a flat U-shaped groove shape, but has a functional uneven surface as described above. Moreover, in this embodiment, although this small convex part 9 is in contact with the lower layer sheet 2, it is not embossed like the trough part 4. FIG. As described above, the ridges 5 and the small protrusions 9 having different heights, widths, and joining states are arranged in the arrangement of the substantially staggered protrusions 3 and the valleys 4. It shows functions such as drape that cannot be achieved by forming a groove-like portion with a linear seal.
凸部内部に単に空間を形成したのでは大きな圧力に対しては潰れやすくなるが、本実施形態の表面シートにおいては、凸部３が細幅の尾根部５により連結され山脈状に連なった形状とされたため、良好なクッション性を維持しながら、凸部３が強く押圧されたときには変形されすぎない。すなわち、内部に空間６を保持することによる凸部３の変形性と、尾根部５や小凸部９による変形の抑制がおこなわれ、凸部が潰されすぎず極めて良好なクッション性が実現される。尾根部５や小凸部９は上層シート及び下層シートが接合または接着により形成された谷部４に挟まれており、曲率が凸部３より小さいため変形を起こし難く、凸部３の変形に対して尾根部５や小凸部９各々のもつ高さにより段階的に変形を抑制することができる。したがって、本実施形態の表面シートを吸収性物品に適用しこれを肌に当接して用いたときには、小さな圧力に対しては凸部３の頂部周辺が小さく変形してソフト感を与え、大きな圧力に対しては凸部３だけではなく尾根部５及び小凸部９が弾力的に支える。その結果、着用者の動きや体重がかかることにより多様な圧力が表面シートにかかるときにも、機能的に応答して適度な反発力を示し、柔軟でやさしい肌当たりとなる。 If a space is simply formed inside the convex part, it will be easily crushed against a large pressure. However, in the topsheet of this embodiment, the convex part 3 is connected by a narrow ridge part 5 and connected in a mountain range. Therefore, it is not deformed too much when the convex portion 3 is strongly pressed while maintaining a good cushioning property. That is, the deformability of the convex portion 3 by holding the space 6 inside and the deformation by the ridge portion 5 and the small convex portion 9 are suppressed, and the convex portion is not crushed so that a very good cushioning property is realized. The The ridge portion 5 and the small convex portion 9 are sandwiched between the valley portions 4 formed by joining or bonding the upper layer sheet and the lower layer sheet, and since the curvature is smaller than the convex portion 3, it is difficult to cause the deformation. On the other hand, deformation can be suppressed in a stepwise manner depending on the height of each of the ridge portion 5 and the small convex portion 9. Therefore, when the top sheet of the present embodiment is applied to an absorbent article and used in contact with the skin, the periphery of the top of the convex portion 3 is deformed to give a soft feeling to a small pressure, and a large pressure is applied. In contrast, not only the convex portion 3 but also the ridge portion 5 and the small convex portion 9 are elastically supported. As a result, even when various pressures are applied to the surface sheet due to the movement and weight of the wearer, the surface sheet responds functionally and exhibits an appropriate repulsive force, resulting in a soft and gentle skin contact.
また、凸部３が孤立せず、弾力のある尾根部５で連結されたため、シートが折り曲げられたときにも、凸部３が不可逆的な変形状態となりにくい。これにより、シートが肌の起伏や激しい動きにより大きな屈曲変形をうけても、脱力された後には凸部３及び尾根部５との連結構造が復元され元の厚みのあるソフトな表面シートの状態に回復する。さらには、上述のように適度な高さで凸部３の変形が押さえられることにより、空間６内部に収納された粘性の液体等が押し出されにくく、肌当接面側への逆戻りが抑制され、サラッとして清潔な着用状態が維持される。 Moreover, since the convex part 3 is not isolated but connected by the elastic ridge part 5, even when the sheet is bent, the convex part 3 is unlikely to be irreversibly deformed. Thus, even if the sheet is subjected to a large bending deformation due to the undulation or intense movement of the skin, the connection structure with the convex portion 3 and the ridge portion 5 is restored after being weakened, and the state of the soft topsheet with the original thickness is restored. To recover. Further, as described above, the deformation of the convex portion 3 is suppressed at an appropriate height, so that the viscous liquid stored in the space 6 is not easily pushed out, and the return to the skin contact surface side is suppressed. A smooth and clean wearing condition is maintained.
本発明の吸収性物品の表面シートにおいては、上記の実施形態において示したように、凸部３を略千鳥状に配置することが好ましい。ここで千鳥状とは、各例の凸部３が等間隔に配置され、隣在する列どうしで互いに凸部が（好ましくは半ピッチ）ずらされている状態をいう。さらに詳述すれば、各列の凸部３をこの列に直交する方向に投影したときに、特定の列の各凸部３の投影像の間に（好ましくは中間に）、これと隣在する列の凸部の投影像が配置される状態をいう。そして略千鳥状というときには、上記千鳥状の配置において、製造上不可避的なずれなど、わずかに上記の配列がずれている場合も含む意味である。このように凸部３を略千鳥格子状に配列することにより、着用者の肌に当接する圧力が均一に分散され良好なクッション性が実現される。また液体の吸収保持においても均一にシート全体においてその作用が発揮されるため好ましい。 In the surface sheet of the absorbent article of the present invention, it is preferable to arrange the convex portions 3 in a substantially staggered manner as shown in the above embodiment. Here, the staggered pattern refers to a state in which the convex portions 3 in each example are arranged at equal intervals, and the convex portions are shifted from each other between adjacent rows (preferably a half pitch). More specifically, when the projections 3 of each row are projected in a direction orthogonal to the row, the projections 3 of the projections 3 of a specific row are located between the projection images (preferably in the middle) and adjacent to this. This is a state in which the projected images of the convex portions of the row to be arranged are arranged. The term “staggered” means that the arrangement is slightly shifted in the staggered arrangement, such as an inevitable shift in manufacturing. Thus, by arranging the convex portions 3 in a substantially staggered pattern, the pressure that comes into contact with the wearer's skin is uniformly dispersed, and a good cushioning property is realized. Further, it is also preferable in absorbing and holding liquid because the action is uniformly exerted on the entire sheet.
本実施形態の表面シート１０は上層シート１及び下層シート２の２層構造とされているが（図１等参照）、上層シート１のみにより構成された表面シート（図示せず）としてもよい。その場合の使用態様としては、例えば上層シート１からなる表面シートを、その非肌当接面側（谷部４を形成している側）の裏面が接するように吸収体上面に積層して用いることが挙げられる。このとき、上層シート１からなる表面シートの裏面と吸収体上面とを接合してもよい。このようにすることで、肌当接面側に配された凸部３及びこれに対応する空間６、さらにはこれらが尾根部５により連結されたことによる弾力性や柔軟性は上述の２層構造のものと同様に発揮される。また、液体や軟便等の透過処理機能についても、ドーム状空間６及びこれがトンネル状空間７により連繋されてなす作用は、吸収体等との組み合わせにより発揮される。このとき、特に空間６の内部に隠蔽された軟便等が直接吸収体に接しているため水分が吸収体に移行しやすく、速やかに軟便等が乾燥していく点で好ましい。また、繊維密度が高められた尾根部５や谷部４に移行した液が下層シート２を介さずに、直接吸収体に吸収保持される点でも好ましい。なお本実施形態の表面シートを１層構造のものとして製造する好ましい製造方法については後述する。 Although the top sheet 10 of this embodiment has a two-layer structure of the upper layer sheet 1 and the lower layer sheet 2 (see FIG. 1 and the like), it may be a top sheet (not shown) constituted only by the upper layer sheet 1. As a usage mode in that case, for example, a top sheet made of the upper layer sheet 1 is used by being laminated on the upper surface of the absorber so that the back surface of the non-skin contact surface side (side on which the valley portion 4 is formed) is in contact. Can be mentioned. At this time, you may join the back surface of the surface sheet which consists of the upper layer sheet | seat 1, and an absorber upper surface. By doing in this way, the elasticity and flexibility by the convex part 3 distribute | arranged to the skin contact surface side and the space 6 corresponding to this, and also these being connected by the ridge part 5 are the above-mentioned two layers. It is demonstrated in the same way as the structure. Moreover, also about the permeation | transmission processing functions, such as a liquid and a loose stool, the effect | action which the dome-shaped space 6 and this connect with the tunnel-shaped space 7 is exhibited by the combination with an absorber. At this time, in particular, soft stool or the like concealed inside the space 6 is in direct contact with the absorbent body, which is preferable in that moisture easily moves to the absorbent body and the soft stool or the like is quickly dried. Moreover, it is preferable also in the point which the liquid which moved to the ridge part 5 and the trough part 4 with which the fiber density was raised is directly absorbed and held by the absorbent body without the lower layer sheet 2 being interposed. In addition, the preferable manufacturing method which manufactures the surface sheet of this embodiment as a thing of 1 layer structure is mentioned later.
図６は本実施形態の表面シートにおける６点エンボスパターンを模式化して示したパターン図である。同図においては１２行×１２列のマス目によりエンボスパターンが示されており、６点を１組としたエンボスパターンの各構成要素として示すと下記のとおりとなる。エンボス（１，２），（１，４），（３，１），（３，５），（５，２），（５，４）の６点で第１の６点パターン要素（第１要素）が構成されている。ここで（ ）内の数値は、（行番号，列番号）を表す。そして右隣りの第２要素は、エンボス（１，８），（１，１０），（３，７），（３，１１），（５，８），（５，１０）の６点で構成されている。さらに第１要素の下方の第３要素は、第１要素の下部の２点（５，２），（５，４）を共有するようにして、（７，１），（７，５），（９，２），（９，４）とともに６点で構成されている。さらにこの右の第４要素は、エンボス（３，５），（３，７），（５，４），（７，５），（５，８）を第１〜３要素のいずれかと共有し、エンボス（７，７）と合わせた６点で構成されている。このようにして各要素の一部（少なくとも２点）を互いに共有しつつ、６点パターンが広く繰り返され構成されている。 FIG. 6 is a pattern diagram schematically showing a six-point emboss pattern in the top sheet of the present embodiment. In the figure, an emboss pattern is shown by squares of 12 rows × 12 columns, and the following is shown as each component of the emboss pattern with 6 points as one set. Emboss (1, 2), (1, 4), (3, 1), (3, 5), (5, 2), (5, 4) at the first 6-point pattern element (first Element). Here, the numerical value in () represents (row number, column number). The second element on the right is composed of 6 points of emboss (1, 8), (1, 10), (3, 7), (3, 11), (5, 8), (5, 10). Has been. Further, the third element below the first element shares two points (5, 2), (5, 4) at the bottom of the first element, so that (7, 1), (7, 5), It is composed of 6 points together with (9, 2) and (9, 4). Further, the fourth element on the right shares the emboss (3, 5), (3, 7), (5, 4), (7, 5), (5, 8) with any of the first to third elements. , And 6 points including emboss (7, 7). In this way, a six-point pattern is widely repeated while sharing a part (at least two points) of each element.
このように、エンボス部分（谷部）を間欠的にパターン化して設けたことにより、連続シールによるものとは異なり、賦形部が折れても形状が維持復元され、肌の起伏に対する良好な密着状態が維持される効果が高まる。また、上述のようなエンボスの局部的な賦形により谷部をなしたため、これに対応して形成された凸部は低繊維密度に保たれ、触感及び液吸収性能に優れる。さらに、上記のような凸部の配置形態とすることで、高い液漏れ防止作用を発揮する。詳しくは、吸収性物品の表面シート１０を例えば使い捨ておむつ、特に高粘度の***物である軟便を***する低月齢児用のおむつの表面シートとして用いた場合に、次のような作用を奏する。軟便は高粘度であることから、一般に表面シートを速やかに透過しづらくシート上に滞留して横流れを起こしやすい。これに対して、本実施形態の吸収性物品の表面シート１０によれば、折れ線状に蛇行する溝部８の中で、しかも凸部３によって取り囲まれて形成され略すり鉢状とされた谷部４（図１、図２参照）に軟便が捕捉される。それにより横流れを起こしづらくなり、軟便に含まれる液体分の吸収体方向への移動が促進される。その結果、軟便からの液漏れを効果的に防止することができる。そして、凸部３の内部には空間６があり、そこに軟便を収納して隠蔽することができる。この隠蔽作用は凸部３を略千鳥格子状に配列することにより均一化され、シート表面全域にわたり清潔な状態を維持することができる。上記作用について軟便を例に説明したが、それと同様に下り物等に含まれる高粘度の***物を吸収するための生理用ナプキンの表面シートとして用いたときにも同様の作用を奏する。 Thus, by providing the embossed part (valley part) in an intermittent pattern, unlike the case of continuous sealing, the shape is maintained and restored even if the shaped part is broken, and it has good adhesion to the skin roughness The effect that a state is maintained increases. Moreover, since the valley part was made by the local shaping of the emboss as described above, the convex part formed corresponding to this is kept at a low fiber density, and is excellent in tactile sensation and liquid absorption performance. Furthermore, a high liquid leakage prevention effect is exhibited by adopting the arrangement of the convex portions as described above. Specifically, when the topsheet 10 of the absorbent article is used as a topsheet for disposable diapers, for example, diapers for low-age children who excrete loose stool, which is a highly viscous excrement, the following effects are exhibited. Since soft stool has a high viscosity, it is generally difficult to permeate the surface sheet quickly and stays on the sheet and tends to cause a lateral flow. On the other hand, according to the surface sheet 10 of the absorbent article of the present embodiment, the valley portion 4 is formed in the groove portion 8 meandering in the shape of a polygonal line and surrounded by the convex portion 3 and has a substantially mortar shape. Soft stool is captured in (see FIGS. 1 and 2). Thereby, it becomes difficult to cause a lateral flow, and the movement of the liquid component contained in the soft stool toward the absorber is promoted. As a result, liquid leakage from soft stool can be effectively prevented. And inside the convex part 3, there is a space 6, in which soft stool can be stored and concealed. This hiding action is made uniform by arranging the convex portions 3 in a substantially staggered pattern, and a clean state can be maintained over the entire sheet surface. Although the above-described action has been described by taking loose stool as an example, the same action can be obtained when it is used as a top sheet of a sanitary napkin for absorbing high-viscosity excreta contained in descending goods and the like.
本実施形態の吸収性物品の表面シート１０において、上層シート１もしくは下層シート２を構成する繊維は特に限定されず、例えば繊度１〜８ｄｔｅｘのものを用いることが好ましい。本実施形態においては上層シート１及び下層シート２をそれぞれ１層構造のものとして示したが、２層以上にしてもよく、また各層の間及び／又は外側に他の機能性の層を設けてもよい。上層シート１及び下層シート２の坪量は特に限定されないが、通常の吸収性物品に適用することを考慮すると上層シート１及び下層シート２の坪量がそれぞれ８〜８０ｇ／ｍ２の範囲にあることが実際的である。 In the surface sheet 10 of the absorbent article of the present embodiment, the fibers constituting the upper layer sheet 1 or the lower layer sheet 2 are not particularly limited, and for example, those having a fineness of 1 to 8 dtex are preferably used. In the present embodiment, the upper layer sheet 1 and the lower layer sheet 2 are each shown as having a single layer structure, but may be two or more layers, and other functional layers may be provided between and / or outside each layer. Also good. The basis weight of the upper layer sheet 1 and the lower layer sheet 2 is not particularly limited, but the basis weight of the upper layer sheet 1 and the lower layer sheet 2 is in the range of 8 to 80 g / m 2 in consideration of application to a normal absorbent article. That is practical.
上層シート１及び下層シート２として不織布を用いることが好ましい。この不織布としてはカード法により製造されたエアースルー不織布やヒートボンド不織布、その他にスパンボンド不織布、メルトブローン不織布、スパンレース不織布、及びニードルパンチ不織布等の種々の不織布が挙げられる。また、上層シート１と下層シート２とを後述するように熱融着によって接合する場合には、前記不織布に熱融着繊維が含まれることが好ましい。熱融着繊維としては、ＰＥＴ／ＰＥ、ＰＰ／ＰＥなどの芯鞘構造のものが好ましい。また、前記不織布には、界面活性剤等を用いた親水化処理を施すことが好ましい。上層シート１及び下層シート２の構成繊維の種類のうち、好ましい組み合わせはＰＥＴ／ＰＥ繊維どうしの組み合わせである。中でも、本発明においては所定方向における破断伸度（脱力状態にある不織布の元の長さをＬ１とし、伸長した時の長さをＬ２としたとき、特定の方向に不織布を伸長して破断させたときの伸長率（（Ｌ２−Ｌ１）／Ｌ１））が５０％以上である不織布を用いることが好ましい。このような不織布を用いることにより、賦形形状が均一な表面シートが得られる。 It is preferable to use a nonwoven fabric as the upper layer sheet 1 and the lower layer sheet 2. Examples of the nonwoven fabric include air-through nonwoven fabric and heat bond nonwoven fabric manufactured by the card method, and various nonwoven fabrics such as spunbond nonwoven fabric, meltblown nonwoven fabric, spunlace nonwoven fabric, and needle punched nonwoven fabric. Moreover, when joining the upper layer sheet | seat 1 and the lower layer sheet | seat 2 by thermal fusion so that it may mention later, it is preferable that a thermal fusion fiber is contained in the said nonwoven fabric. As the heat-fusible fiber, those having a core-sheath structure such as PET / PE and PP / PE are preferable. The nonwoven fabric is preferably subjected to a hydrophilic treatment using a surfactant or the like. Among the types of constituent fibers of the upper layer sheet 1 and the lower layer sheet 2, a preferable combination is a combination of PET / PE fibers. Among them, in the present invention, the elongation at break in a predetermined direction (when the original length of the nonwoven fabric in a weak state is L1, and the length when stretched is L2, the nonwoven fabric is stretched and broken in a specific direction. It is preferable to use a nonwoven fabric having an elongation ratio ((L2-L1) / L1)) of 50% or more. By using such a nonwoven fabric, a surface sheet having a uniform shaped shape can be obtained.
次に、本実施形態の吸収性物品の表面シート１０の好ましい製造方法を図面を参照しながら説明する。図７は本実施形態の吸収性物品の表面シートを製造する一実施態様を模式的に示す工程説明図である。同図に示すように、まず上層シート１を原反ロール（図示せず）から繰り出す。これとは別に、下層シート２を原反ロール（図示せず）から繰り出す。上層シート１及び下層シート２はそれぞれ、そのＭＤ方向（方向ｄ１及びｄ２）に沿って繰り出される。 Next, the preferable manufacturing method of the surface sheet 10 of the absorbent article of this embodiment is demonstrated, referring drawings. FIG. 7 is a process explanatory view schematically showing one embodiment for producing the top sheet of the absorbent article of the present embodiment. As shown in the figure, first, the upper layer sheet 1 is fed out from a raw fabric roll (not shown). Separately from this, the lower layer sheet 2 is fed out from a raw fabric roll (not shown). The upper layer sheet 1 and the lower layer sheet 2 are respectively fed out along the MD direction (directions d 1 and d 2 ).
繰り出された上層シート１を、周面が凹凸形状となっている第１ロール５１と、その凹凸形状と噛み合い形状となっている凹凸形状を周面に有する第２ロール５２との噛み合わせ部Ｐ１に噛み込ませて上層シート１を凹凸賦形する。第１ロール５１における各歯車の歯溝部には吸引孔（図示せず）が形成されていることが好ましい。この歯溝部は、第１ロール５１の周面における凹凸形状のうちの凹部に相当するものである。吸引孔は、ブロワや真空ポンプなどの吸引源（図示せず）に通じ、第１ロール５１（回転方向：矢印ｄ５）と第２ロール５２（回転方向：矢印ｄ７）との噛み合い部Ｐ１から上層シート１と下層シート２とを接合した表面シートを送り出す部分Ｐ３に至るまで吸引されるように制御されていることが好ましい。これにより、第１ロールと第２ロールとの噛み合いによって凹凸賦形された上層シート１は、吸引孔による吸引力によって第１ロール５１周面に密着したまま、その凹凸賦形された状態が保持される。 The meshed portion P of the fed upper layer sheet 1 between the first roll 51 having a concavo-convex shape on the peripheral surface and the second roll 52 having a concavo-convex shape meshing with the concavo-convex shape on the peripheral surface. 1 , the upper sheet 1 is unevenly shaped. It is preferable that a suction hole (not shown) is formed in the tooth groove portion of each gear in the first roll 51. The tooth groove portion corresponds to a recess in the uneven shape on the peripheral surface of the first roll 51. The suction hole communicates with a suction source (not shown) such as a blower or a vacuum pump, and a meshing portion P between the first roll 51 (rotation direction: arrow d 5 ) and the second roll 52 (rotation direction: arrow d 7 ). it is preferably controlled so as to be sucked from 1 up to the portion P 3 for feeding the top sheet joined to the upper layer sheet 1 and lower layer sheet 2. Accordingly, the upper layer sheet 1 formed with the unevenness by the meshing of the first roll and the second roll is kept in the state where the unevenness is formed while being in close contact with the peripheral surface of the first roll 51 by the suction force by the suction holes. Is done.
合流部Ｐ２では、上層シート１を第１ロール５１の周面に吸引密着させた状態で、別に供給されている下層シート２と積層する。ここで両シートを第１ロール５１と第３ロール５３とで挟圧することが好ましくい。第３ロール５３としては凹凸を有しないアンビルロールを用いることが好ましく、第３ロール５３のみを所定温度に加熱しておくことが好ましい。これによって、第１ロール５１の歯車の凸部先端に位置する上層シート１と下層シート２とが熱融着によって接合される。この押圧接合により表面シートとしたときに谷部４（図１、図２参照）が形成される。一方、歯車の凹部においては上層シート１及び下層シート２は挟圧されず、熱融着が起こらず凸部３（図１、図２参照）が形成される。すなわち、本実施態様においては第１ロール５１と第２ロール５２とによるシート賦形において圧熱加工はしていないため、凸部３の頂部において柔らかさが保たれる。したがって表面シートとして用いたときに、谷部４となる部分においては加熱狭圧され不織布繊維が熱溶融し多少硬化していても、凸部３は柔らかく突出しているため、硬い部分が直接肌に当接することなく良好な触感が実現される。なお尾根部５の形成については後述する。 The merging portion P 2, the upper layer sheet 1 while being sucked in close contact with the peripheral surface of the first roll 51 is laminated with the lower layer sheet 2 being fed separately. Here, it is preferable to sandwich both sheets between the first roll 51 and the third roll 53. As the third roll 53, an anvil roll having no irregularities is preferably used, and it is preferable to heat only the third roll 53 to a predetermined temperature. Thereby, the upper layer sheet 1 and the lower layer sheet 2 located at the tip of the convex portion of the gear of the first roll 51 are joined by thermal fusion. A valley 4 (see FIGS. 1 and 2) is formed when the surface sheet is formed by this pressure bonding. On the other hand, the upper layer sheet 1 and the lower layer sheet 2 are not pinched in the concave portion of the gear, and heat fusion does not occur, and the convex portion 3 (see FIGS. 1 and 2) is formed. That is, in the present embodiment, since the heat treatment is not performed in the sheet shaping by the first roll 51 and the second roll 52, the softness is maintained at the top of the convex portion 3. Therefore, when it is used as a top sheet, even if the nonwoven fabric fibers are heat-melted and hardened somewhat in the part that becomes the valley part 4, the convex part 3 protrudes softly, so that the hard part directly touches the skin. A good tactile sensation is realized without contact. The formation of the ridge portion 5 will be described later.
本実施態様の製造方法においては、上層シート１と下層シート２とが貼り合わされた複合シートが、第１ロール５１及び第４ロール５４によって挟まれた部分Ｐ３で加熱挟圧される。このとき第４ロール５４は第３ロール５３と同様に外周に凹凸を有さないアンビルロールであることが好ましく、所定の温度に加熱されていることが好ましい。このようにして、しっかりと固定された接合部が形成され、凸部の形状安定性が維持される。 In the manufacturing method of the present embodiment, the composite sheet in which the upper layer sheet 1 and the lower layer sheet 2 are bonded together is heated and pressed at the portion P 3 sandwiched between the first roll 51 and the fourth roll 54. At this time, like the third roll 53, the fourth roll 54 is preferably an anvil roll having no irregularities on the outer periphery, and is preferably heated to a predetermined temperature. In this way, a firmly fixed joint is formed, and the shape stability of the convex portion is maintained.
図８は本実施形態の吸収性物の表面シートを製造する別の実施態様を模式的に示す工程説明図である。同図に示すように、第１〜第４のロール（５１，５２，５３，５４）を用いる点で上記の図７に示した実施態様と共通する。しかし、図８に示した実施態様においては下層シート２を用いず、上層シート１のみが用いられており、この上層シート１に凸部３と谷部４となる凹凸が賦形されている。したがって、谷部４において他のシートと接合されていないが、第１ロール５１と第３ロール５３もしくは第４ロール５４とで加熱狭圧され、不織布繊維が熱溶融され硬化した状態にされている。このようにして単に凹凸形状に屈曲させられているだけでなく、上述した表面シートとしたときに特定の機能を示す凸部３及び谷部４となるよう賦形される。その他、第１ロール５１と第２ロール５２との歯の噛み込みによるシート賦形及び第１ロール５１によるＰ１〜Ｐ３にかけての吸引は、図７に示した実施態様と同様である。 FIG. 8 is a process explanatory view schematically showing another embodiment for producing the top sheet of the absorbent material of the present embodiment. As shown in the figure, it is common to the embodiment shown in FIG. 7 in that the first to fourth rolls (51, 52, 53, 54) are used. However, in the embodiment shown in FIG. 8, only the upper layer sheet 1 is used without using the lower layer sheet 2, and the upper and lower sheets 1 have irregularities that form the convex portions 3 and the valley portions 4. Therefore, although it is not joined to another sheet in the valley portion 4, it is heated and compressed by the first roll 51 and the third roll 53 or the fourth roll 54, and the nonwoven fabric fiber is thermally melted and cured. . In this way, it is not only simply bent into a concavo-convex shape, but is shaped so as to be a convex portion 3 and a trough portion 4 exhibiting a specific function when the above-described topsheet is used. In addition, the sheet shaping by the biting of the teeth of the first roll 51 and the second roll 52 and the suction from P 1 to P 3 by the first roll 51 are the same as in the embodiment shown in FIG.
図９は図７に示した実施態様の製造方法において第１ロール及び第２ロールの歯が互いに噛み込む状態を模式的に示したパターン図である。図９においては、第１ロール及び第２ロールの歯が噛み込んでいる点Ｐ１における両ロールの歯の先端を図７の矢印ＩＸの方向から投影した状態で示しており、実線が第２ロール５２の歯（歯の先端）５２ａを示し、点線が第１ロール５１の歯（歯の先端）５１ａを示している。ただし、実際の両ロールは正面図（図７参照）において円形であり互いに１列の歯でのみ噛み合うが、図９においては、これを対向する平板上の歯が面で噛み合うようにみたてて（あるいは点Ｐ１における噛み合い状態を時間的に連続してＭＤ方向に送って）パターン図化して示している。 FIG. 9 is a pattern diagram schematically showing a state in which the teeth of the first roll and the second roll are engaged with each other in the manufacturing method of the embodiment shown in FIG. 9 shows a state projected from the direction of the first roll and the arrow IX in Figure 7 the tips of the both rolls teeth in the point P 1 teeth are bite of the second roll, the solid line second The tooth (tip of tooth) 52a of the roll 52 is shown, and the dotted line shows the tooth (tip of tooth) 51a of the first roll 51. However, both actual rolls are circular in the front view (see FIG. 7) and mesh with each other only with one row of teeth. In FIG. 9, this is viewed as if the teeth on the opposing flat plates mesh with each other. (or sent to the MD direction of the meshing state at point P 1 sequentially in time) are shown patterned plotter.
以下に上記両ロールの歯の噛み合い状態についてさらに詳しく説明する。図９に示したパターン図においては、図７において方向ＩＸから見た状態であるから、歯の先端５２ａが紙面奥側の方向に没入する方向に、歯の先端５１ａが紙面手前側に突出してくる方向に動作し、両者が噛み合うといえる。すなわち、歯の先端５２ａが紙面奥側に没入しながら上層シート１（図７では示されていない。）を押し込み、表面シートとしたときに凸部３（図１参照）をなす局部的な屈曲形状を多数賦形する。一方、歯の先端５１ａが上層シートを紙面手前側に押し上げるようにして、表面シートとしたときに谷部４をなす局部的な屈曲形状を多数賦形する。このように凹凸賦形された上層シートが第１ロールとの密着状態を維持され第３ロールの方へと送られ、先に述べたように別途送られてきた下層シート２と積層される（図７参照）。そして、第１ロール５１の歯の先端５１ａと第３ロール５３ないし第４ロール５４の周面とで両シートが加熱狭圧され、歯の先端５１ａの部分で熱溶融接合されたヒートエンボスが形成される。 Hereinafter, the meshing state of the teeth of both rolls will be described in more detail. In the pattern diagram shown in FIG. 9, since it is the state seen from the direction IX in FIG. 7, the tooth tip 51a protrudes toward the front side of the paper in a direction in which the tooth tip 52a is immersed in the back side of the paper. It can be said that it moves in the coming direction and the two mesh. In other words, the upper end sheet 1 (not shown in FIG. 7) is pushed in while the front end 52a of the tooth is immersed in the back side of the paper, and is locally bent to form the convex portion 3 (see FIG. 1) when the top sheet is used. Form many shapes. On the other hand, the tip 51a of the tooth pushes up the upper layer sheet toward the front side of the page, and a number of local bent shapes forming the valley 4 are formed when the surface sheet is formed. The upper layer sheet thus formed with unevenness is maintained in close contact with the first roll and sent to the third roll, and is laminated with the lower layer sheet 2 sent separately as described above ( (See FIG. 7). Then, both the sheets are heated and compressed by the tooth tip 51a of the first roll 51 and the peripheral surface of the third roll 53 to the fourth roll 54, and heat embossing is formed at the tooth tip 51a portion. Is done.
ここで、図９における歯の先端５１ａのうちＴ１〜Ｔ６を取り出していうと、歯の先端Ｔ１〜Ｔ６がそれぞれ谷部４となる部分を形成する。このとき、歯の先端５１ａ，５２ａで押し出されるあるいは押し込まれる部分の不織布は引き伸ばしないしは圧縮により、局部的に移動しながら、例えば先端部に位置する繊維が両ロールの歯の隙間入り込もうとする。このとき、通常上層シート１に対しＭＤ方向にテンションがかけられているため、これが影響して、上層シートをなす不織布の繊維の流動において特有の動きを与える。具体的には、先に述べた歯の先端Ｔ１〜Ｔ６のそれぞれの歯の間に繊維が入り込もうとするとき、ＭＤ方向にかけられたシートテンションとの関係で、ＭＤ方向及びＣＤ方向のそれぞれにおいて繊維の流動状態が異なる。すなわち、歯の先端Ｔ１とＴ４との間及び歯の先端Ｔ３とＴ６との間をなす領域９１では、その他の領域９２より入り込んでくる繊維の量が多くなり、表面シートとしたときに尾根部５となる部分が形成される。そして、領域９１の部分は歯の先端５２ａにより加熱狭圧されないので、その部分には下層シート２と接合されず、表面シートにおけるトンネル状空間７が形成される。なお、図９におけるＭＤ方向は、図１及び図２に示した実施形態の表面シートにおいてＸ方向に相当する。 Here, when T 1 to T 6 are taken out of the tooth tip 51 a in FIG. 9, the tooth tips T 1 to T 6 each form a valley 4. At this time, the non-woven fabric of the portion pushed out or pushed in by the tooth tips 51a and 52a moves locally by stretching or compression, and for example, fibers located at the tips try to enter the gaps between the teeth of both rolls. At this time, since tension is normally applied to the upper layer sheet 1 in the MD direction, this influences and gives a specific movement in the flow of the nonwoven fabric fibers forming the upper layer sheet. Specifically, when the fiber is going to enter between the teeth of the tooth tips T 1 to T 6 described above, each of the MD direction and the CD direction is related to the sheet tension applied in the MD direction. The flow state of the fibers is different. That is, in the region 91 formed between the tooth tips T 1 and T 4 and between the tooth tips T 3 and T 6 , the amount of fibers entering from the other regions 92 increases, and the surface sheet is obtained. Sometimes a portion that becomes the ridge 5 is formed. And since the part of the area | region 91 is not heat-narrowed by the front-end | tip 52a of a tooth | gear, it is not joined to the lower layer sheet | seat 2 in that part, but the tunnel-shaped space 7 in a surface sheet is formed. In addition, MD direction in FIG. 9 is corresponded to X direction in the surface sheet of embodiment shown in FIG.1 and FIG.2.
これに対して、領域９２においては入り込んでくる繊維量が比較的少なく、結果として表面シートにしたときに小凸部９（図５参照）をなす程度となる。こうして、歯の先端５１ａにより狭圧された部分がなす谷部４と上記小凸部９とが連続して折れ線状の溝部をなすこととなる。図示したもので具体的に溝部となったときの形態を示すと、Ｔ１、Ｔ２、及びＴ３がなす列、並びにＴ４、Ｔ５、及びＴ６がなす列がそれぞれＭＤ方向に沿って１つの折れ線状に連続した溝部８を形成することとなる。したがって、表面シートにおける凸部と尾根部とが図１及び図２におけるＸ方向に連結された山脈状の凸部列１１が、本実施態様の製造方法においてはＭＤ方向（図９参照）に沿って形成される。これに対し、図１及び図２のＹ方向に延びる図４に示した断面形状は、図９に示したＣＤ方向に沿って形成される。 On the other hand, in the region 92, the amount of entering fibers is relatively small, and as a result, when the surface sheet is formed, a small convex portion 9 (see FIG. 5) is formed. In this way, the valley portion 4 formed by the portion narrowed by the tooth tip 51a and the small convex portion 9 continuously form a polygonal groove portion. The form when the groove portion is specifically shown in the figure is shown. The rows formed by T 1 , T 2 , and T 3 , and the rows formed by T 4 , T 5 , and T 6 are each along the MD direction. Thus, a continuous groove portion 8 is formed. Therefore, the mountain-shaped convex part row | line | column 11 by which the convex part and ridge part in the surface sheet were connected to the X direction in FIG.1 and FIG.2 is along MD direction (refer FIG. 9) in the manufacturing method of this embodiment. Formed. On the other hand, the cross-sectional shape shown in FIG. 4 extending in the Y direction of FIGS. 1 and 2 is formed along the CD direction shown in FIG.
ここで、第１ロールの歯（先端面）５１ａのＴ１〜Ｔ６の中心を結んだ六角形の面積を基本面積Ａとする。第１ロールの歯５１ａのＴ１〜Ｔ６の中心を結んだ六角形内に含まれる面積を面積Ｂとし、面積Ｂの基本面積Ａに対する比（Ｂ／Ａ）は０．１０〜０．２５が好ましい。この比（Ｂ／Ａ）の値が小さくなりすぎると凸部３と尾根部５の差が無くなり、一つの凸部になってしまい尾根部５が成型できなくなるため潰れやすくなる。この比（Ｂ／Ａ）の値が大きくなりすぎると尾根部５の空間が無くなり空間の連続性が損なわれる。また、基本面積Ａ内の第２ロールの歯（先端面）５２ａの面積Ｃの基本面積Ａに対する比（Ｃ／Ａ）は０．１０〜０．２５が好ましい。この比（Ｃ／Ａ）の値が小さくなりすぎると賦形部３の形状が安定せず凸部の成型が難しい。この比（Ｃ／Ａ）の値が大きすぎると凸部が直方体形状になり、硬くなってしまい柔らかな感触が低下する。第１ロールの歯の間隔９７を第２ロールの歯のＣＤ寸法９８で割った値は０．２５〜０．８３が好ましい。この値の設定範囲において最も安定した略山形形状の凸部３と尾根部５を得られる。
第１ロールの歯のＭＤ寸法１０１は特に限定されないが、例えば０．５〜３．５ｍｍであることが好ましく、より好ましくは０．６〜２ｍｍである。また、ＣＤ寸法１００は特に限定されないが、例えば０．５〜３．５ｍｍであることが好ましく、より好ましくは０．６〜２ｍｍである。また、第１ロールの歯の間９７は特に限定されないが、例えば０．８〜５ｍｍであることが好ましく、より好ましくは１〜２ｍｍである。第２ロールの歯のＭＤ寸法９９は特に限定されないが、例えば０．５〜３．５ｍｍであることが好ましく、より好ましくは０．６〜２ｍｍである。また、ＣＤ寸法９８は特に限定されないが、例えば０．５〜６ｍｍであることが好ましく、より好ましくは０．６〜４ｍｍである。第１ロール及び第２ロールの歯の間隔９４は適宜に定めることができるが、例えば１．５〜１０ｍｍとすることが好ましく、より好ましくは２〜６ｍｍである。第１ロールのＭＤ方向の歯の間隔１０２は特に限定されないが、例えば０．４〜４ｍｍであることが好ましい。第２ロールのＭＤ方向の歯の間隔１０３についても特に限定されないが、第１ロールのＭＤ方向の歯の間隔１０２と同じ寸法が好ましく、例えば０．４〜４ｍｍであることが好ましい。また、ＣＤ方向の歯の間隔１０４についても特に限定されないが、例えば１．２〜７．５ｍｍであることが好ましい。
さらに第１ロール及び第２ロールの歯の高さや形状は、目的とする表面シートの形態によって適宜に定めることができるが、例えば０．８〜９ｍｍであることが好ましい。なお、図９については第１ロール及び第２ロールの歯の噛み込みによるシートの賦形について図７に示した実施態様の製造方法との関係で説明したが、このことは図８に示した実施態様の製造方法においても同様である。
また、ＭＤの破断伸長率が１００％以上の不織布が好ましく、本願発明の好ましい賦形形状の表面シートが加工できる。
Here, an area of a hexagon connecting the centers of T 1 to T 6 of the teeth (tip surface) 51a of the first roll is defined as a basic area A. The area included in the hexagon connecting the centers of T 1 to T 6 of the teeth 51a of the first roll is defined as area B, and the ratio of area B to basic area A (B / A) is 0.10 to 0.25. Is preferred. If the value of this ratio (B / A) becomes too small, there will be no difference between the convex part 3 and the ridge part 5, and it will become one convex part, and the ridge part 5 cannot be molded, so it will be easily crushed. If the value of this ratio (B / A) becomes too large, the space of the ridge portion 5 is lost and the continuity of the space is impaired. Further, the ratio (C / A) of the area C of the tooth (tip surface) 52a of the second roll within the basic area A to the basic area A is preferably 0.10 to 0.25. If the value of this ratio (C / A) becomes too small, the shape of the shaped part 3 is not stable and it is difficult to mold the convex part. When the value of this ratio (C / A) is too large, the convex portion becomes a rectangular parallelepiped shape, becomes hard and the soft feeling is lowered. The value obtained by dividing the tooth interval 97 of the first roll by the CD dimension 98 of the second roll tooth is preferably 0.25 to 0.83. In the setting range of this value, the most stable convex portion 3 and ridge portion 5 having a substantially chevron shape can be obtained.
Although MD dimension 101 of the tooth | gear of a 1st roll is not specifically limited, For example, it is preferable that it is 0.5-3.5 mm, More preferably, it is 0.6-2 mm. Further, the CD dimension 100 is not particularly limited, but is preferably 0.5 to 3.5 mm, and more preferably 0.6 to 2 mm. Moreover, although 97 between the teeth of a 1st roll is not specifically limited, For example, it is preferable that it is 0.8-5 mm, More preferably, it is 1-2 mm. Although MD dimension 99 of the tooth | gear of a 2nd roll is not specifically limited, For example, it is preferable that it is 0.5-3.5 mm, More preferably, it is 0.6-2 mm. The CD dimension 98 is not particularly limited, but is preferably 0.5 to 6 mm, and more preferably 0.6 to 4 mm. Although the interval 94 between the teeth of the first roll and the second roll can be determined as appropriate, it is preferably 1.5 to 10 mm, and more preferably 2 to 6 mm. The tooth interval 102 in the MD direction of the first roll is not particularly limited, but is preferably 0.4 to 4 mm, for example. Although it does not specifically limit about the space | interval 103 of the tooth | gear of MD direction of a 2nd roll, The same dimension as the space | interval 102 of the tooth | gear of the MD direction of a 1st roll is preferable, for example, it is preferable that it is 0.4-4 mm. Moreover, although it does not specifically limit about the space | interval 104 of the tooth | gear of CD direction, For example, it is preferable that it is 1.2-7.5 mm.
Furthermore, although the height and shape of the teeth of the first roll and the second roll can be appropriately determined depending on the form of the target surface sheet, it is preferably, for example, 0.8 to 9 mm. In addition, about FIG. 9, although the shaping | molding of the sheet | seat by the biting of the teeth of a 1st roll and a 2nd roll was demonstrated in relation to the manufacturing method of the embodiment shown in FIG. 7, this was shown in FIG. The same applies to the manufacturing method of the embodiment.
Moreover, the nonwoven fabric whose break elongation rate of MD is 100% or more is preferable, and the surface sheet of the preferable shaping shape of this invention can be processed.
図１０は本発明の吸収性物品の表面シートを用いた使い捨ておむつを一部切欠して模式的に示す斜視図である。同図に示した使い捨ておむつ８０は、同物品において一般的な形態を有しており外包体８１と吸収体８８とを組み合わせて形成されている。 FIG. 10 is a perspective view schematically showing a disposable diaper using the top sheet of the absorbent article of the present invention with a part cut away. The disposable diaper 80 shown in the figure has a general form in the article, and is formed by combining an outer package 81 and an absorber 88.
外包体８１は１枚のシートからなるものであっても、複数のシートからなるものであってもよい。外包体８１には横漏れ防止ギャザー８４が設けられており、乳幼児の運動による液漏れの防止に効果を奏する。本実施形態のおむつにおいては、さらに機能的な構造部やシート材等を設けてもよい。
さらに本実施形態のおむつはテープ型のおむつとして示しており、背側ｒのフラップ部にはテープ８５が設けられている。このテープを腹側ｆのフラップ部に設けたテープ貼付部（図示せず）に貼付して装着固定することができる。このとき、おむつ中央ｃを緩やかに内側に折り曲げて、吸収体８８が乳幼児の臀部から下腹部にわたって沿わされるように着用する。これにより***物が的確に吸収体８８に吸収保持される。
The outer package 81 may be composed of a single sheet or a plurality of sheets. The outer package 81 is provided with a lateral leakage prevention gather 84, which is effective in preventing liquid leakage due to the movement of the infant. In the diaper of this embodiment, a functional structure part, a sheet material, etc. may be provided.
Furthermore, the diaper of this embodiment is shown as a tape-type diaper, and a tape 85 is provided on the flap portion on the back side r. This tape can be attached and fixed to a tape applying portion (not shown) provided on the flap portion of the ventral side f. At this time, the diaper center c is gently bent inward, and the absorbent body 88 is worn so as to be stretched from the buttocks to the lower abdomen. As a result, excreta is accurately absorbed and held by the absorber 88.
吸収体８８には、厚みのある吸収材８３の表面に本実施形態の表面シート１０が配設されている。通常吸収材自体は肌当りがあまり良くなく、液体を一度吸収した後にはベタついた感じを与えてしまうが、上記のように本実施形態の表面シートを乳幼児の肌に当接するように配設したことで肌触りが良化し、サラッとした触感となる。特に空間を保持した凸部と、谷部、及び特別の形状を有する尾根部とがネットワーク構造により、上述した多様な作用を発揮し、大幅に吸収性物品の着用感、フィット性、液体吸収性能等が向上する。しかも柔らかい肌あたりで運動などにより多少おむつの位置がずれたときにも違和感を与えない。さらには、丸みを帯びた凸部が多数表面に連設されているため、外観においても柔らかさを感じさせ、看者に対し肌にやさしい印象を与える。 In the absorbent body 88, the top sheet 10 of the present embodiment is disposed on the surface of a thick absorbent material 83. Usually, the absorbent material itself does not have very good contact with the skin and gives a sticky feeling after absorbing the liquid once. However, as described above, the surface sheet of this embodiment is disposed so as to contact the skin of the infant. As a result, the touch is improved and the feel is smooth. In particular, the convex portion that holds the space, the valley portion, and the ridge portion having a special shape exert the above-described various effects due to the network structure, and the wear feeling, fit property, and liquid absorption performance of the absorbent article are greatly improved. Etc. are improved. Moreover, it does not give a sense of incongruity when the diaper is slightly out of position due to exercise, etc. around soft skin. Furthermore, since many rounded convex portions are continuously provided on the surface, the external appearance is soft and gives the viewer a gentle impression on the skin.
本実施形態のおむつ８０において、外包体８１、テープ８５、ギャザー８４、吸収材８３等に用いられる材料は通常おむつに用いられるものを用いることができ、特に限定されるものではない。本発明の吸収性物品の表面シートは、上記使い捨ておむつに限らず、ナプキン及びパンティーライナー等の各種の吸収性物品にも好適に用いることがきる。 In the diaper 80 of the present embodiment, materials used for the outer package 81, the tape 85, the gathers 84, the absorbent material 83, and the like can be those normally used for diapers, and are not particularly limited. The surface sheet of the absorbent article of the present invention is not limited to the disposable diaper, and can be suitably used for various absorbent articles such as napkins and panty liners.
以下、実施例に基づき本発明を更に詳細に説明するが、本発明はこれらの実施例により限定して解釈されるものではない。 EXAMPLES Hereinafter, although this invention is demonstrated further in detail based on an Example, this invention is limited and interpreted by these Examples.
（実施例１）
上層シートを構成する不織布として、芯がポリエチレンテレフタレートで鞘がポリエチレンからなる２．２ｄｔｅｘ×５１ｍｍの芯鞘型複合繊維６ｇ／ｍ２と４．４ｄｔｅｘ×５１ｍｍの芯鞘型複合繊維１２ｇ／ｍ２を積層した坪量１８ｇ／ｍ２のエアースルー不織布を用いた。上層シートは賦形加工により、ＭＤ方向に折り曲げられ目付が上がるため賦形後は２２ｇ／ｍ２になる（上層の繰出し速度は、下層シート繰出し速度の約２０％増であった）。下層シートを構成する不織布として、芯がポリエチレンテレフタレートで鞘がポリエチレンからなる２．２ｄｔｅｘ×５１ｍｍの芯鞘型複合繊維を構成繊維とする坪量１８ｇ／ｍ２のエアースルー不織布を用いた。これらのシートを用い、図７に示す装置を用いて、図９に示す歯の噛み込みパターン（間隔９４は３．２ｍｍ、間隔９７は１ｍｍ、幅９８は２ｍｍ、長さ９９は０．８ｍｍ、幅１００は１ｍｍ、長さ１０１は０．８ｍｍ）となる第１ロール及び第２ロールにより、図６に示す６点エンボスパターンの表面シート（試験材１）を作製した。得られた表面シート（試験材１）は図１〜図５に示した特有のシート形状を有し、凸部の高さｈｔはおよそ１．７〜２．１ｍｍであり、尾根部の高さｈｏはおよそ０．６〜１．０ｍｍであった。この表面シート（試験材１）の上層シート側の表面形状を表面形状解析顕微鏡（キーエンス社製、ＶＨＸ−９００（商品名））で測定し斜視図として画像化した表面形状解析図を図１１に示す。同図中、「ｔ」が凸部、「ｂ」が谷部、「ｏ」が尾根部、「ｓ」が小凸部をそれぞれ示す。なお、図中における寸法の単位は「ｕｍ」と表記されているが「μｍ」の意味である。
Example 1
As the nonwoven fabric constituting the upper layer sheet, 2.2 dtex × 51 mm core-sheath type composite fiber 6 g / m 2 and 4.4 dtex × 51 mm core-sheath type composite fiber 12 g / m 2 having a core made of polyethylene terephthalate and a sheath made of polyethylene are used. A laminated air-through nonwoven fabric having a basis weight of 18 g / m 2 was used. The upper layer sheet is bent in the MD direction by the shaping process, so that the basis weight is increased, so that after shaping, the upper layer sheet is 22 g / m 2 (the upper layer feeding speed was about 20% higher than the lower sheet feeding speed). As a nonwoven fabric constituting the lower layer sheet, an air-through nonwoven fabric having a basis weight of 18 g / m 2 having a core-sheath type composite fiber of 2.2 dtex × 51 mm whose core is polyethylene terephthalate and whose sheath is made of polyethylene was used. Using these sheets and using the apparatus shown in FIG. 7, the tooth biting pattern shown in FIG. 9 (interval 94 is 3.2 mm, interval 97 is 1 mm, width 98 is 2 mm, length 99 is 0.8 mm, A top sheet (test material 1) having a 6-point emboss pattern shown in FIG. 6 was produced by a first roll and a second roll having a width 100 of 1 mm and a length 101 of 0.8 mm. The resulting topsheet (test material 1) had a distinctive sheet configuration as shown in FIGS. 1 to 5, the height h t of the protrusions is approximately 1.7～2.1Mm, the ridges high is h o was approximately 0.6~1.0mm. FIG. 11 shows a surface shape analysis diagram obtained by measuring the surface shape on the upper layer sheet side of this surface sheet (test material 1) with a surface shape analysis microscope (manufactured by Keyence Corporation, VHX-900 (trade name)) and imaging it as a perspective view. Show. In the figure, “t” indicates a convex portion, “b” indicates a valley portion, “o” indicates a ridge portion, and “s” indicates a small convex portion. The unit of dimension in the figure is expressed as “um”, but means “μm”.
（実施例２）
上層シート及び下層シートを構成する不織布として、芯がポリエチレンテレフタレートで鞘がポリエチレンからなる２．２ｄｔｅｘ×５１ｍｍの芯鞘型複合繊維１８ｇ／ｍ２のエアースルー不織布を用いた。上層シートは賦形加工により、ＭＤ方向に折り曲げられ目付が上がるため賦形後は２２ｇ／ｍ２になる。（上層の繰出し速度は、下層シート繰出し速度の約２０％増であった）これらのシートを用い、図７に示す装置を用いて、図９に示す歯の噛み込みパターン（間隔９４は３．２ｍｍ、間隔９７は１ｍｍ、幅９８は２ｍｍ、長さ９９は０．８ｍｍ、幅１００は１ｍｍ、長さ１０１は０．８ｍｍ）となる第１ロール及び第２ロールにより、図６に示す６点エンボスパターンの表面シート（試験材２）を作製した。得られた表面シート（試験材２）は図１〜図５に示した特有のシート形状を有し、凸部の高さｈｔはおよそ１．３〜１．７ｍｍであり、尾根部の高さｈｏはおよそ０．４〜０．７ｍｍであった。
(Example 2)
As a nonwoven fabric constituting the upper layer sheet and the lower layer sheet, an air-through nonwoven fabric of core / sheath type composite fiber 18 g / m 2 of 2.2 dtex × 51 mm whose core is polyethylene terephthalate and whose sheath is made of polyethylene was used. Since the upper layer sheet is bent in the MD direction by the shaping process and the basis weight is increased, it becomes 22 g / m 2 after the shaping. (The feeding speed of the upper layer was about 20% higher than the feeding speed of the lower layer sheet) Using these sheets, the tooth biting pattern shown in FIG. 6 points shown in FIG. 6 by the first roll and the second roll, which are 2 mm, the interval 97 is 1 mm, the width 98 is 2 mm, the length 99 is 0.8 mm, the width 100 is 1 mm, and the length 101 is 0.8 mm. An embossed pattern surface sheet (test material 2) was prepared. The resulting topsheet (test material 2) had a specific sheet shape shown in FIGS. 1 to 5, the height h t of the protrusions is approximately 1.3～1.7Mm, the ridges high is h o was approximately 0.4~0.7mm.
（比較例１）
上層シートを構成する繊維ウェブとして、芯がポリエチレンテレフタレートで鞘がポリエチレンからなる７．７ｄｔｅｘ×５１ｍｍの芯鞘型複合繊維を構成繊維とする坪量１６ｇ／ｍ２に、下層シートを構成する繊維ウェブとして、芯がポリエチレンテレフタレートで鞘がポリエチレンからなる３．３ｄｔｅｘ×５１ｍｍの芯鞘型複合繊維を坪量２４ｇ／ｍ２を積層したエアースルー不織布を用いた。これらのシートを積層させ接合し、比較のための表面シート（試験材３）を得た。表面シート（試験材３）の厚みはおよそ１ｍｍであった。
（比較例２）
上層シートと下層シートを構成する不織布として、芯がポリエチレンテレフタレートで鞘がポリエチレンからなる２．２ｄｔｅｘ×５１ｍｍの芯鞘型複合繊維を構成繊維とする坪量２０ｇ／ｍ２のエアースルー不織布を２枚重ね超音波により接合したものを用い、表面シート（試験材４）を得た。表面シート（試験材４）の厚みはおよそ１ｍｍであった。
(Comparative Example 1)
As a fiber web constituting the upper layer sheet, a fiber web constituting the lower layer sheet with a basis weight of 16 g / m 2 comprising a core-sheath type composite fiber of 7.7 dtex × 51 mm whose core is made of polyethylene terephthalate and whose sheath is made of polyethylene. As an air-through nonwoven fabric, a core-sheath type composite fiber of 3.3 dtex × 51 mm whose core is made of polyethylene terephthalate and whose sheath is made of polyethylene is laminated with a basis weight of 24 g / m 2 . These sheets were laminated and joined to obtain a surface sheet (test material 3) for comparison. The thickness of the top sheet (test material 3) was about 1 mm.
(Comparative Example 2)
Two sheets of air-through nonwoven fabric with a basis weight of 20 g / m 2 comprising 2.2 dtex × 51 mm core-sheath type composite fiber having a core made of polyethylene terephthalate and a sheath made of polyethylene as the nonwoven fabric constituting the upper layer sheet and the lower layer sheet The surface sheet (test material 4) was obtained using what was joined by the superposition | stacking ultrasonic wave. The thickness of the top sheet (test material 4) was approximately 1 mm.
〔表層液戻り試験〕
重量を測定した表面シート（試験材）を吸収材（フラッフパルプと高吸収性ポリマーとの積繊体であり、パルプの坪量及びポリマーの坪量をいずれも２５７ｇ／ｍ２としたものを用いた。）の上に載置した。次に、表面シートの中心部より定量ポンプを使い８０ｇの人工尿を注入する。注入後、１０分間放置する。その後、表面シートの重量を測定し評価前の重量を差し引いた。その値を不織布の表層液残り量とした。この液残り量が３００ｍｇ以下であれば実用上の要求を満足し、１５０ｍｇ以下であれば実用上の要求を高いレベルで満足しうる。
[Surface liquid return test]
The weight measured surface sheet (test material) is an absorbent material (a pile of fluff pulp and superabsorbent polymer, and the basis weight of the pulp and the basis weight of the polymer are both 257 g / m 2 . ). Next, 80 g of artificial urine is injected from the center of the topsheet using a metering pump. Leave for 10 minutes after injection. Then, the weight of the surface sheet was measured and the weight before evaluation was subtracted. The value was made into the surface layer liquid remaining amount of a nonwoven fabric. If the remaining amount of the liquid is 300 mg or less, the practical requirement can be satisfied, and if it is 150 mg or less, the practical requirement can be satisfied at a high level.
〔横通気試験〕
表面シート（各試験材）について、３５ｇ／ｃｍ２圧力下でのシート面と平行な方向への空気通過容量は以下の方法で測定した。
先ず、ＫＥＳ圧縮試験機（カトーテック（株）社製、ＫＥＳ ＦＢ−３ ＡＵＴＯ−Ａ（商品名）、接触部円形（面積２ｃｍ２）を用い、３５ｇ／ｃｍ２の荷重を加えたときの表面シートの厚みＴｈ１を測定した。
厚みを測定した表面シートを、中央に一辺１０ｍｍの正方形状の開口部を有する正方形状の第１アクリル板（寸法：５０ｍｍ×５０ｍｍ×３ｍｍ）と、開口部を有しない以外は第１アクリル板と同じ第２アクリル板との間に、該表面シートの着用者の肌側に向けられる面を第１アクリル板側にして挟んだ。これを、ＪＩＳ Ｐ ８１１７の「ガーレー試験機法」に規定されるガーレー試験機（Ｂ型）のガスケット下に第１アクリル板側を上に向けてセットし、表面シートが上記厚みＴｈ１となるまで圧縮する。
次いで、厚みＴｈ１を維持した表面シートの中央部に、上記開口部を介して空気を導入して３００ｍＬの空気を導入するのに要した時間を計測する。
そして、開口部の単位面積（１ｃｍ２）×１秒当たりの空気導入量（ｃｃ）を算出した。この横通気試験の結果は表面シートにおける空気の移動しやすさ、つまりムレにくさを示し、横通気量が３０ｃｃ／ｓｅｃ以上であれば実用上の要求を満足し、７０ｃｃ／ｓｅｃ以上であれば実用上の要求を高いレベルで満足しうる。
(Lateral ventilation test)
About the surface sheet (each test material), the air passage capacity in the direction parallel to the sheet surface under 35 g / cm 2 pressure was measured by the following method.
First, the surface when applying a load of 35 g / cm 2 using a KES compression tester (Kato Tech Co., Ltd., KES FB-3 AUTO-A (trade name), circular contact area (area 2 cm 2 )) The thickness Th1 of the sheet was measured.
The top sheet whose thickness was measured was a square-shaped first acrylic plate (dimension: 50 mm × 50 mm × 3 mm) having a square-shaped opening with a side of 10 mm in the center, and the first acrylic plate except that it did not have an opening. Between the same 2nd acrylic board, the surface turned to the wearer's skin side of this surface sheet was pinched | interposed into the 1st acrylic board side. This is set under the gasket of the Gurley tester (B type) prescribed in “Gurley tester method” of JIS P 8117, with the first acrylic plate side facing up, until the top sheet reaches the thickness Th1. Compress.
Next, the time required to introduce 300 mL of air through the opening is measured at the center of the topsheet that maintains the thickness Th1.
Then, the unit area (1 cm 2 ) of the opening × the air introduction amount (cc) per second was calculated. The result of this lateral ventilation test shows the ease of air movement in the top sheet, that is, the squeeze, and if the lateral ventilation amount is 30 cc / sec or more, it satisfies the practical requirement, and if it is 70 cc / sec or more. It can satisfy practical requirements at a high level.
〔ＫＥＳ厚み〕
各表面シート（各試験材）について、ＫＥＳ圧縮試験機（カトーテック（株）社製、ＫＥＳ ＦＢ−３ ＡＵＴＯ−Ａ（商品名）、接触部円形（面積２ｃｍ２）を用い、０．５ｇ／ｃｍ２及び５０ｇ／ｃｍ２の荷重をそれぞれ加えたときの厚み（凸部の高さｈｔ（図３参照）に下層シートの厚さを加えたサンプル厚さ）を測定した。この厚さの値が大きいほど、おむつを実際に着用して使用したときに良好なクッション性が維持される。具体的に、上記０．５ｇ／ｃｍ２の荷重条件でＫＥＳ厚みが１．２以上であり、２０ｇ／ｃｍ２の荷重条件でＫＥＳ厚みが０．８以上で、５０ｇ／ｃｍ２の荷重条件でＫＥＳ厚みが０．５以上であるとき、実用上の要求を満足しうる。
[KES thickness]
About each surface sheet (each test material), using a KES compression tester (Kato Tech Co., Ltd., KES FB-3 AUTO-A (trade name), circular contact area (area 2 cm 2 ), 0.5 g / The thickness (sample thickness obtained by adding the thickness of the lower layer sheet to the height h t of the protrusion (see FIG. 3)) when a load of cm 2 and 50 g / cm 2 was applied was measured. The larger the value, the better the cushioning property is maintained when the diaper is actually worn and used, specifically, the KES thickness is 1.2 or more under the load condition of 0.5 g / cm 2 , When the KES thickness is 0.8 or more under a load condition of 20 g / cm 2 and the KES thickness is 0.5 or more under a load condition of 50 g / cm 2 , a practical requirement can be satisfied.
〔圧縮硬さ（ＫＥＳ）試験〕
各表面シート（各試験材）について、５０ｇ／ｃｍ２荷重下での圧縮硬さの測定を行った。
表面シートをＫＥＳ圧縮試験機（カトーテック（株）社製、ＫＥＳ ＦＢ−３ ＡＵＴＯ−Ａ（商品名）、接触部円形（面積２ｃｍ２）を用い、５０ｇ／ｃｍ２荷重まで加圧を行い圧縮特性を測定した。上記圧縮硬さ（ＫＥＳ）試験において、ＬＣの値は小さい力での圧縮性を意味し、０．７５以下であれば実用上の要求を満足しうる。ＷＣの値はふんわり感を意味し、０．５ｇｆ・ｃｍ／ｃｍ２以上であれば実用上の要求を満足し、１．０ｇｆ・ｃｍ／ｃｍ２以上であれば実用上の要求を高いレベルで満足する。ＲＣの値は圧縮回復性を意味し、３０％以上であれば実用上の要求を高いレベルで満足する。
[Compression hardness (KES) test]
For each surface sheet (each test material) was measured for compressive hardness under a 50 g / cm 2 load.
Using a KES compression tester (manufactured by Kato Tech Co., Ltd., KES FB-3 AUTO-A (trade name), circular contact area (area 2 cm 2 ), compress the top sheet to 50 g / cm 2 load. In the above compression hardness (KES) test, the LC value means compressibility with a small force, and if it is 0.75 or less, the practical requirement can be satisfied. means sensitive to satisfy the practical requirements of long 0.5gf · cm / cm 2 or more, to satisfy the practical requirements of long 1.0gf · cm / cm 2 or more at a high level .RC The value means compression recovery, and if it is 30% or more, the practical requirement is satisfied at a high level.
〔ドレープ性、ＫＥＳ曲げ特性Ｂ’試験〕
各表面シート（各試験材）について、一定曲率（±２．５ｃｍ−１）をあたえた時の曲げモーメントの測定を行った。
表面シートを２０ｃｍ×１０ｃｍ（ＭＤ×ＣＤ）の形状に裁断し試験片とした。得られた試験片を、ＫＥＳ純曲げ試験機（カトーテック（株）社製、ＫＥＳ ＦＢ−２ ＡＵＴＯ−Ａ（商品名）を用い、ＭＤ方向とＣＤ方向のそれぞれで一定曲率（±２．５ｃｍ−１）をあたえた時の曲げモーメントを測定した。曲率±２．５ｃｍ−１の曲げモーメントの値をＢ‘としている。
上記ドレープ性、ＫＥＳ曲げ特性Ｂ’試験において、値が小さいほど曲がり易いことを意味し、一方向（ＭＤ方向）において０．３５ｇｆ・ｃｍ２／ｃｍ以下であれば実用上の要求を満足し、０．２ｇｆ・ｃｍ２／ｃｍ以下であれば実用上の要求を高いレベルで満足する。他の方向（ＣＤ方向）において０．２０ｇｆ・ｃｍ２／ｃｍ以下であれば実用上の要求を満足する。
[Drapability, KES bending characteristics B 'test]
About each surface sheet (each test material), the bending moment was measured when a constant curvature (± 2.5 cm −1 ) was given.
The surface sheet was cut into a shape of 20 cm × 10 cm (MD × CD) to obtain a test piece. Using the KES pure bending test machine (Kato Tech Co., Ltd., KES FB-2 AUTO-A (trade name)), the obtained test piece was fixed with a constant curvature (± 2.5 cm) in each of the MD direction and the CD direction. -1 ) was measured, and the value of the bending moment with a curvature of ± 2.5 cm −1 was defined as B ′.
In the drapability and KES bending characteristics B ′ test, it means that the smaller the value, the easier it is to bend, and if it is 0.35 gf · cm 2 / cm or less in one direction (MD direction), the practical requirement is satisfied, If it is 0.2 gf · cm 2 / cm or less, the practical requirement is satisfied at a high level. If it is 0.20 gf · cm 2 / cm or less in the other direction (CD direction), the practical requirement is satisfied.
〔座屈有無（ＭＤ２つ折り部）試験〕
各表面シート（各試験材）について、定規を置き基点として二つ折り（ＭＤ方向）にし、開いた時の折れ目の状態を確認した。この評価において○以上であれば実用上の要求を満足し、◎以上であれば実用上の要求を高いレベルで満足する。
×： 折れ目が多数付いてシワや角ができ、折れ目の硬さを感じる。
△： 折れ目が付いて複数のシワが残り、折れ目の硬さを少し感じる。
○： 折れ目は付くがシワは付かない。折れ目の硬さは殆ど感じられない。
◎： 折れ目が付かず元の状態のまま。折れ目の硬さは全く感じない。
[Buckling test (folded part of MD) test]
Each surface sheet (each test material) was folded in two (MD direction) using a ruler as a base point, and the state of the fold when opened was confirmed. In this evaluation, if it is ◯ or more, the practical requirement is satisfied, and if it is ◎ or more, the practical requirement is satisfied at a high level.
×: Many folds are formed, wrinkles and corners are formed, and the hardness of the folds is felt.
Δ: A crease is formed, a plurality of wrinkles remain, and the hardness of the crease is felt a little.
○: There are creases but no wrinkles. The hardness of the fold is hardly felt.
◎: No creases and the original state. I do not feel the hardness of the crease at all.
〔手触り感触試験〕
上記の表層液残り量測定試験を行ったおむつの表面シートを手のひらで直接触って触感を確認した。おむつに組み込む前の表面シートの表面（上層の表面）を手のひらで直接触れ、その感触を以下の基準に従って判定した。判定は３人以上で行い、最も支持の多い意見を判定の結果とした。判定が１人ずつに分かれた場合は、それらの中間となる意見を判定結果とした。この評価において○以上であれば実用上の要求を満足し、◎以上であれば実用上の要求を高いレベルで満足する。
×：硬い。抵抗感（ざらざら感）がある。
△：やや硬い。抵抗感（ざらざら感）が少しある。
○：やや柔らかい。なめらかな感じが少しある。
◎：柔らかく、なめらかな感じがある。
[Hand feeling test]
The tactile sensation was confirmed by directly contacting the surface sheet of the diaper subjected to the above-described surface layer liquid remaining amount measurement test with the palm of the hand. The surface of the topsheet (upper surface) before being incorporated into a diaper was directly touched with the palm of the hand, and the touch was determined according to the following criteria. Judgment was made by three or more people, and the opinion with the most support was taken as the result of the judgment. When the judgment was divided into one person, the opinion that was in between them was taken as the judgment result. In this evaluation, if it is ◯ or more, the practical requirement is satisfied, and if it is ◎ or more, the practical requirement is satisfied at a high level.
X: Hard. There is a sense of resistance.
Δ: Slightly hard There is a little resistance (rough feeling).
○: Slightly soft. There is a little smooth feeling.
A: Soft and smooth feeling.
上記の結果より、本発明による表面シート（試験材１、２）は、比較例のものに対して、高い表面液戻り性及び横通気性を示すことが分かる。また、本発明の表面シート（試験材１、２）は、上記表面シートの各特性評価（ＫＥＳ厚み試験、圧縮硬さ試験、ドレープ性試験、座屈有無試験、及び手触り感触試験）において比較例のものに対して優れた結果を示し、肌の起伏に追従しやすく柔らかくなめらかな風合いを有するものであることが分かる。 From the above results, it can be seen that the surface sheets (test materials 1 and 2) according to the present invention exhibit high surface liquid return and lateral air permeability as compared with the comparative example. Moreover, the surface sheet (test materials 1 and 2) of the present invention is a comparative example in each characteristic evaluation of the above surface sheet (KES thickness test, compression hardness test, drape test, buckling presence test, and hand touch test). Excellent results are shown, and it is easy to follow the undulations of the skin, and it is understood that it has a soft and smooth texture.
１ 上層シート
２ 下層シート
３ 凸部
３ａ 凸部頂部
３ｂ 凸部肩部
３ｃ 凸部側壁部
４ 谷部
５ 尾根部
６ 凸部内部の空間
７ トンネル状空間
８ 溝部
９ 小凸部
１０ 表面シート
１１、１１ａ、１１ｂ、１１ｃ、１１ｄ 凸部列
５１ 第１ロール
５１ａ 第１ロールの歯（歯の先端）
５２ 第２ロール
５２ａ 第２ロールの歯（歯の先端）
５３ 第３ロール
５４ 第４ロール
８０ 使い捨ておむつ
８１ 外包体
８３ 吸収材
８４ 横漏れ防止ギャザー
８５ テープ
８８ 吸収体
９１ 尾根部をなす上層シート賦形領域
９２ 小凸部をなす上層シート賦形領域
９４ ロールの歯の間隔
９７ 第１ロールの歯のＣＤ方向の間隔
９８ 第２ロールの歯のＣＤ方向の幅
DESCRIPTION OF SYMBOLS 1 Upper layer sheet 2 Lower layer sheet 3 Convex part 3a Convex part top part 3b Convex part shoulder part 3c Convex part side wall part 4 Valley part 5 Ridge part 6 Space inside convex part 7 Tunnel-shaped space 8 Groove part 9 Small convex part 10 Top sheet 11, 11a, 11b, 11c, 11d Convex part row 51 First roll 51a First roll tooth (tooth tip)
52 Second Roll 52a Second Roll Teeth (Tooth Tip)
53 3rd roll 54 4th roll 80 Disposable diaper 81 Outer package 83 Absorbent material 84 Side leakage prevention gather 85 Tape 88 Absorber 91 Upper layer sheet forming area 92 forming ridge part Upper layer sheet forming area 94 forming small convex part 94 roll Tooth spacing 97 The first roll teeth CD spacing 98 The second roll teeth CD width
Claims (5)