JP5309832B2 - Weedproof structure including weedproof sheet and construction method thereof - Google Patents
Weedproof structure including weedproof sheet and construction method thereof Download PDFInfo
- Publication number
- JP5309832B2 JP5309832B2 JP2008242193A JP2008242193A JP5309832B2 JP 5309832 B2 JP5309832 B2 JP 5309832B2 JP 2008242193 A JP2008242193 A JP 2008242193A JP 2008242193 A JP2008242193 A JP 2008242193A JP 5309832 B2 JP5309832 B2 JP 5309832B2
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- main body
- patch
- weedproof
- construction method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
本発明は、草の成育を防止する必要がある場所、特に支柱を既に有する場所に配置する、防草シートを含む防草構造体及びその施工方法に関する。 The present invention relates to a grass protection structure including a grass protection sheet and a construction method thereof, which are disposed in a place where grass growth needs to be prevented, particularly in a place which already has a support.
道路、線路、河川、公園及び造林園など並びにこれらの周辺の地面、表面、特に法面などでは、美観が損なわれるなどの理由により、雑草などの草の成育を防止する必要があることが多い。特に、道路の路肩及びそれに隣接する法面においては、雑草が繁茂することにより、美観が損なわれるだけでなく、交通の安全が損なわれる可能性がある。そのため、それらの場所では、草の成育を防止する必要がある。 It is often necessary to prevent the growth of grasses such as weeds on roads, railways, rivers, parks, afforestation gardens, and the surrounding grounds, surfaces, and especially slopes, because of the loss of aesthetics. . In particular, on the shoulders of roads and the slopes adjacent to them, weeds may not only impair the aesthetics, but also impair traffic safety. Therefore, it is necessary to prevent grass growth in those places.
草の成育の防止のためには、例えば、特許文献１に開示されているような防草シートが用いられている。 In order to prevent grass growth, for example, a herbicidal sheet as disclosed in Patent Document 1 is used.
草の成育を防止するための構造体として、例えば、特許文献２には、法面部上端の路肩部に敷設されるコンクリートブロック部と、そのコンクリートブロック部の法面側に一端部が一体的に固定された防草シート部とからなり、コンクリートブロック部を路肩部に布設した状態で、防草シート部を法面部上に展開して法面部を被覆可能とした路肩ブロックが開示されている。 As a structure for preventing grass growth, for example, in Patent Document 2, a concrete block portion laid on a road shoulder at the upper end of a slope portion and one end portion on the slope side of the concrete block portion are integrated. There is disclosed a road shoulder block that includes a fixed grass prevention sheet portion and that can be covered with a slope portion by spreading the grass prevention sheet portion on the slope surface portion in a state where the concrete block portion is laid on the road shoulder portion.
また、特許文献３には、シート両面に多数の凸部を交互に形成した遮光性かつ遮水性の合成樹脂製エンボスシート（防草シート）を、除草すべき地面に敷設、固定したことを特徴とする防草構体が開示されている。この特許文献３には、路肩にガードレールがある場合には、ガードレール支柱と、エンボスシート（防草シート）に形成したガードレール支柱の挿通孔との隙間に、コーキング材を詰めることが開示されている。
本発明は、施工場所での火気の使用が制限されている場合にも、防草構造体を施工することができる施工方法を得ることを目的とする。特に、ガードレール、道路標識や信号等の取付物が取り付けられている支柱を有する防草区域であっても、防草区域全体にわたって草の生育を防止し、特に防草シートと支柱との隙間からの草の生育を防止するための、簡便で低コストの防草構造体の施工を、火気の使用が制限されている場合にも行うことのできる方法及び施工方法により設置する防草構造体を得ることを目的とする。 An object of this invention is to obtain the construction method which can construct a weedproof structure also when the use of the fire in a construction place is restrict | limited. In particular, even in a grass protection area having a support post to which attachments such as guardrails, road signs, signals, etc. are attached, the grass growth is prevented over the entire grass prevention area, especially from the gap between the protection sheet and the support post. The construction of a simple and low-cost herbicidal structure to prevent the growth of grass is possible even when the use of fire is restricted and the herbicidal structure installed by the construction method The purpose is to obtain.
本発明は、舗装面に隣接した防草区域に、防草シート本体含む防草構造体を設置するための施工方法であって、防草シート本体の第一端部を、舗装面端部に重なるように配置する工程（Ａ）と、防草シート本体の第一端部を、テープ接着によって舗装面端部に固定する工程（Ｂ）と、防草シート本体の第一端部を、さらに第一の釘状器具によって舗装面端部に固定する工程（Ｃ）と、防草シート本体の第一端部とは反対側の第二端部を、第二の釘状器具によって地面に固定する工程（Ｄ）とを含む、防草構造体の施工方法である。 The present invention is a construction method for installing a grass protection structure including a grass protection sheet body in a grass protection area adjacent to a pavement surface, wherein the first end portion of the grass protection sheet body is formed at the edge of the pavement surface. The step (A) of arranging the overlapping, the step (B) of fixing the first end of the weedproof sheet main body to the paved surface end by tape bonding, and the first end of the weedproof sheet main body, Step (C) of fixing to the pavement surface end with the first nail-shaped device, and fixing the second end opposite to the first end of the weedproof sheet body to the ground with the second nail-shaped device It is the construction method of the weed prevention structure including the process (D) to do.
本発明の施工方法の好ましい態様を以下に示す。本発明では、これらの態様を適宜組み合わせることができる。
（１）舗装面が、アスファルト舗装道路の舗装面であり、防草区域が、アスファルト舗装道路の法面である。
（２）防草区域が、取付物が取り付けられている支柱を有し、工程（Ａ）の前に、防草シート本体の、支柱位置に対応する防草シート本体の位置に本体開口部及び本体開口部の１点と防草シート本体の端部の１点との間に本体切断部を形成する工程と、パッチシートに、パッチ開口部及びパッチ開口部の１点とパッチシートの端部の１点との間にパッチ切断部を形成する工程と、本体切断部に支柱を通過させることによって、支柱を防草シート本体の本体開口部に貫通さる工程とをさらに含み、工程（Ａ）の後に、パッチ切断部に支柱を通過させることによって、支柱をパッチシートのパッチ開口部に貫通させ、本体切断部を全て覆いかつ本体切断部とパッチ切断部とが重ならないように、防草シート本体上にパッチシートを敷設する工程と、パッチシートを、テープ接着によって防草シート本体に固定する工程とをさらに含む。
（３）支柱貫通前の本体開口部の形状が、支柱の断面の形状と相似形状であり、かつ支柱の断面の形状の最長寸法より１〜２０ｍｍ大きい。
（４）本体切断部を、本体開口部の１点と防草シート本体の端部の１点との距離が、最短距離となるように形成する。
（５）パッチシートの形状が、正方形又は長方形であり、正方形又は長方形の一辺の長さが、支柱の断面の形状の最長寸法Ｄｐより１００〜４００ｍｍ長い。
（６）本体切断部及びパッチ切断部の形状が直線状であり、パッチシートを敷設する工程において、本体切断部とパッチ切断部との支柱中心位置を中心とした角度が、９０〜２７０度であるようにパッチシートを敷設する。
（７）本体開口部と支柱との間及び／又はパッチ開口部と支柱との間に、シリコン系シール材を充填する工程をさらに含む。
（８）支柱貫通前のパッチ開口部の形状が、支柱の断面の形状と相似形状である。（９）支柱貫通前のパッチ開口部の形状の最長寸法Ｄｈと、支柱の断面の形状の最長寸法Ｄｐとの比Ｄｈ／Ｄｐが、０．９〜１．１である。
（１０）パッチシートが、少なくとも平面方向に伸び性を有し、パッチシートの引張伸び率が、２０％以上である。
（１１）防草シート本体及び／又はパッチシートが、耐貫通型防草シートである。
（１２）取付物が、ガードレールである。
The preferable aspect of the construction method of this invention is shown below. In the present invention, these embodiments can be appropriately combined.
(1) The paved surface is a paved surface of an asphalt paved road, and the grass protection area is a slope of the asphalt paved road.
(2) The weedproof area has a support post to which an attachment is attached, and before the step (A), the main body opening and A step of forming a main body cutting portion between one point of the main body opening and one end of the weedproof sheet main body, a patch opening, one point of the patch opening and the end of the patch sheet on the patch sheet A step of forming a patch cutting part between the point and the step of passing the support through the main body cutting part to pass the support through the main body opening of the weedproof sheet main body, and the step (A) After that, by passing the strut through the patch cutting section, the strut is penetrated through the patch opening of the patch sheet, so that all the main body cutting section is covered and the main body cutting section and the patch cutting section do not overlap Laying a patch sheet on the main body and The patch sheet, further comprising a step of fixing the weed seat body by a tape adhesive.
(3) The shape of the opening of the main body before penetrating the pillar is similar to the shape of the cross section of the pillar, and is 1 to 20 mm larger than the longest dimension of the shape of the cross section of the pillar.
(4) The main body cutting portion is formed so that the distance between one point of the main body opening and one point of the end portion of the weedproof sheet main body is the shortest distance.
(5) The shape of the patch sheet is a square or a rectangle, and the length of one side of the square or the rectangle is 100 to 400 mm longer than the longest dimension Dp of the cross-sectional shape of the column.
(6) The shape of the main body cutting portion and the patch cutting portion is linear, and in the step of laying the patch sheet, the angle centered on the column center position between the main body cutting portion and the patch cutting portion is 90 to 270 degrees. Lay the patch sheet as there is.
(7) The method further includes a step of filling a silicon-based sealant between the main body opening and the column and / or between the patch opening and the column.
(8) The shape of the patch opening before penetrating is similar to the cross-sectional shape of the column. (9) The ratio Dh / Dp of the longest dimension Dh of the shape of the patch opening before penetrating the longest dimension Dp of the cross-sectional shape of the pillar is 0.9 to 1.1.
(10) The patch sheet has extensibility at least in the plane direction, and the tensile elongation of the patch sheet is 20% or more.
(11) The weedproof sheet body and / or the patch sheet is a penetration-resistant weedproof sheet.
(12) The attachment is a guard rail.
また、本発明は、上述の施工方法により施工される、防草構造体である。 Moreover, this invention is a weed prevention structure constructed | assembled by the above-mentioned construction method.
本発明によって、施工場所での火気の使用が制限されている場合にも、防草構造体を施工することができる。特に、本発明によって、ガードレール、道路標識や信号等の取付物が取り付けられている支柱を有する防草区域であっても、防草区域全体にわたって草の生育を防止し、特に防草シートと支柱との隙間からの草の生育を防止するための、簡便で低コストの防草構造体の施工を、火気の使用が制限されている場合にも行うことのできる施工方法及びその施工方法により設置する防草構造体を得ることができる。 Even when the use of fire at the construction site is restricted by the present invention, the weedproof structure can be constructed. In particular, according to the present invention, even in a grass protection area having a support column to which attachments such as guardrails, road signs and signals are attached, grass growth is prevented over the entire grass protection area, in particular, a grass protection sheet and a support column. Installation of a simple and low-cost grass-proof structure to prevent grass growth from the gap with the installation method that can be performed even when the use of fire is restricted, and its installation method Can be obtained.
本発明の防草構造体の施工方法は、施工場所での火気の使用が好ましくない場所及び施工場所での火気の使用が制限されている場所への防草構造体の施工方法に関する。特に、本発明の防草構造体の施工方法は、ガードレール、道路標識や信号等が取り付けられている支柱を有する防草区域に対して防草構造体を施工することが容易であり、かつ、高い防草効果を得ることができる施工方法であって、施工場所での火気の使用が好ましくない場合、あるいは制限されている場合にも適用できる防草構造体の施工方法に関する。本明細書では、支柱に取り付けられているガードレール、道路標識や信号等を「取付物」という。また、防草構造体を設置する区域を「防草区域」という。また、「粘着材接着法」とは、二つの物体の間の少なくとも一部に、改質アスファルトを含む目止め材などの粘着材を塗布し、二つの物体及び粘着材塗布層を加圧し、粘着することにより、二つの物体を固定する固定方法である。「テープ接着法」とは、二つの物体の間の少なくとも一部に、両面に接着性のあるアスファルトテープなどの粘着性テープ（両面粘着テープ）を挟み、二つの物体及び両面粘着テープを加圧し、粘着することにより、二つの物体を固定する固定方法である。 The construction method of the weed prevention structure of this invention is related with the construction method of the weed prevention structure to the place where the use of the fire in a construction place is unpreferable and the use of the fire in a construction place is restrict | limited. In particular, the construction method of the grass protection structure of the present invention is easy to construct the grass protection structure for the grass protection area having a support rail to which a guardrail, a road sign or a signal is attached, and The present invention relates to a construction method capable of obtaining a high herbicidal effect, which can be applied even when the use of fire at a construction site is not preferable or restricted. In this specification, a guardrail, a road sign, a signal, and the like attached to a support column are referred to as an “attachment”. In addition, the area where the weedproof structure is installed is referred to as “weedproof area”. In addition, the “adhesive material adhesion method” means that an adhesive material such as a sealing material containing modified asphalt is applied to at least a part between two objects, and the two objects and the adhesive material application layer are pressurized, This is a fixing method for fixing two objects by sticking. The “tape bonding method” means that an adhesive tape (double-sided adhesive tape) such as asphalt tape with adhesive on both sides is sandwiched between at least a part between two objects, and the two objects and the double-sided adhesive tape are pressed. This is a fixing method for fixing two objects by adhering.
一般に、草の成育を防止するために防草構造体を設置する場所（防草区域）に、支柱のみが存在する場合、図１０及び図１１に示すように、防草シート（防草シート本体１０）に開口部を設けて支柱にかぶせるという敷設方法をとることにより、本発明の防草構造体を施工することができる。この場合に、防草シート本体１０の端部を、舗装面端部２２に粘着材接着法及び／又はテープ接着法により接着することにより、施工場所での火気の使用が好ましくない場合、あるいは制限されている場合にも、防草構造体を施工することができる。 In general, in the case where only a support is present in a place (weedproof area) where a weedproof structure is installed in order to prevent grass growth, as shown in FIG. 10 and FIG. The grass protection structure of the present invention can be constructed by adopting a laying method in which an opening is provided in 10) and covered with a support. In this case, the use of fire at the construction site is not preferable or restricted by adhering the end portion of the weed prevention sheet body 10 to the paved surface end portion 22 by the adhesive material bonding method and / or the tape bonding method. Even if it is done, a weedproof structure can be constructed.
また、防草区域に、ガードレール、道路標識や信号等を取り付けた支柱が既に存在している場合がある。防草構造体をこのような場所に設置する際には、支柱にはガードレールや標識が取り付けられているため、防草シートに開口部を設けて支柱にかぶせるという敷設方法をとることはできない。この場合には、以下に述べる方法によって、本発明の防草構造体を施工することができる。 In some cases, there are already pillars with guardrails, road signs, signals, etc. in the grass protection area. When the weedproof structure is installed in such a place, since the guard rail and the sign are attached to the support, it is not possible to adopt a laying method in which an opening is provided on the support and covered with the support. In this case, the weedproof structure of the present invention can be constructed by the method described below.
＜防草構造体＞
本発明の防草構造体の上面模式図を図１に、支柱２３を含む断面模式図を図８に示す。図１及び図８に図示されている支柱２３には、ガードレール２４が取り付けられている。本発明の防草構造体は、所定の防草シート本体１０及び所定のパッチシート４０を用いることにより、本発明の防草構造体を設置した区域（防草区域）全体にわたって草の生育を防止することができる。特に、防草区域が、ガードレール、道路標識や信号等（取付物）が既に取り付けられた支柱２３を有する場合、本発明の防草構造体を設置すると、支柱２３と防草シート本体１０及びパッチシート４０との隙間を無くすことができる。そのため、本発明の防草構造体を用いることによって、支柱２３と防草シート本体１０及びパッチシート４０との間の隙間からの草の生育を、簡便で低コストの施工方法により防止することができる。また、防草シート本体１０及びパッチシート４０の接着を、粘着材接着法及び／又はテープ接着法により接着することにより、施工場所での火気の使用が好ましくない場合、あるいは制限されている場合にも、防草構造体を施工することができる。なお、図８において、粘着材接着法及び／又はテープ接着法により接着している部分を接着層４５として示す。
<Weedproof structure>
FIG. 1 is a schematic top view of a weedproof structure of the present invention, and FIG. 8 is a schematic cross-sectional view including a support 23. A guard rail 24 is attached to the column 23 shown in FIGS. 1 and 8. The grass protection structure of the present invention prevents grass growth over the entire area (the grass protection area) where the grass protection structure of the present invention is installed by using the predetermined grass protection sheet body 10 and the predetermined patch sheet 40. can do. In particular, in the case where the grass protection area has a support post 23 to which a guardrail, a road sign, a signal or the like (attachment) is already attached, when the grass prevention structure of the present invention is installed, the support 23, the grass prevention sheet main body 10 and the patch are installed. A gap with the sheet 40 can be eliminated. Therefore, by using the weedproof structure of the present invention, it is possible to prevent grass growth from the gap between the support 23, the weedproof sheet body 10 and the patch sheet 40 by a simple and low cost construction method. it can. Further, when the use of fire at the construction site is not preferable or restricted by adhering the herbicidal sheet main body 10 and the patch sheet 40 by the adhesive material bonding method and / or the tape bonding method. Can also construct a weedproof structure. In FIG. 8, a portion bonded by the adhesive material bonding method and / or the tape bonding method is shown as an adhesive layer 45.
図２に、本発明の防草構造体を設置するのに好適な場所の断面模式図を示す。図２に示す防草区域には、ガードレール２４が取り付けられている支柱２３を有する。図１及び図８に、本発明の防草構造体を、図２に示すような場所に設置した例を示す。図１には本発明の防草構造体の上面模式図を、図８にはその断面模式図を示す。これらの図には、本発明の防草構造体をアスファルト舗装道路の法面３０の防草区域に配置した例を示している。「法面」とは、道路や線路及びこれらの周辺の斜面、切り土又は盛土などでできた斜面、段差のある２つの地表面の間の斜面、２つの地表面の間の斜面及び２つの地表面の間などを意味する。図１及び図８に示すように、本発明の防草構造体は、所定の防草シート本体１０及び所定のパッチシート４０を含み、これらに対して支柱２３が貫通している。後述するように、本発明の防草構造体を設置する際には、所定の防草シート本体１０及び所定のパッチシート４０に対する支柱２３の貫通を簡単に行うことができる。 In FIG. 2, the cross-sectional schematic diagram of a suitable place for installing the weed prevention structure of this invention is shown. The grass prevention area shown in FIG. 2 has a column 23 to which a guardrail 24 is attached. 1 and 8 show an example in which the weedproof structure of the present invention is installed in a place as shown in FIG. FIG. 1 is a schematic top view of the weedproof structure of the present invention, and FIG. 8 is a schematic cross-sectional view thereof. In these drawings, an example is shown in which the grass protection structure of the present invention is arranged in the grass protection area on the slope 30 of the asphalt paved road. "Slope" refers to roads and tracks and their surrounding slopes, slopes made of cut or embankment, slopes between two stepped ground surfaces, slopes between two ground surfaces and two It means between the ground surface. As shown in FIG.1 and FIG.8, the weed prevention structure of this invention contains the predetermined weed prevention sheet main body 10 and the predetermined patch sheet 40, and the support | pillar 23 has penetrated with respect to these. As will be described later, when the grass protection structure of the present invention is installed, the column 23 can be easily penetrated into the predetermined grass protection sheet main body 10 and the predetermined patch sheet 40.
＜防草シート本体＞
図３に、所定の防草シート本体１０の一例を示す。防草シート本体１０には、支柱位置に対応する防草シート本体１０の位置に、支柱２３を貫通させるための本体開口部１１が形成されている。「支柱位置に対応する位置」とは、ある防草区域の所定の場所に防草シート本体１０を敷設する際に、その防草シート本体１０とその防草区域に配置される支柱２３とが重なる位置のことである。
<Weedproof sheet body>
In FIG. 3, an example of the predetermined weedproof sheet main body 10 is shown. The weedproof sheet main body 10 is formed with a main body opening 11 for allowing the support 23 to pass through at the position of the weedproof sheet main body 10 corresponding to the position of the support. “Position corresponding to the column position” means that when the grass protection sheet main body 10 is laid at a predetermined location in a certain grass prevention area, the grass protection sheet main body 10 and the columns 23 arranged in the grass protection area are It is the overlapping position.
防草シート本体１０は、本体開口部１１と防草シート本体１０の端部の１点との間を切断した部分である本体切断部４３を有する。そのため、防草シート本体１０の敷設の際、本体切断部４３に支柱２３を通過させることによって、図５及び図６に示すように、支柱２３を本体開口部１１に貫通した状態にすることが容易である。したがって、支柱２３にガードレール等の取付物が取り付けられている場合でも、防草シート本体１０を容易に敷設することができる。 The weedproof sheet main body 10 has a main body cutting part 43 which is a part cut between the main body opening 11 and one end of the weedproof sheet main body 10. Therefore, when the weedproof sheet main body 10 is laid, the post 23 is passed through the main body opening 11 as shown in FIGS. 5 and 6 by passing the post 23 through the main body cutting portion 43. Easy. Therefore, even when an attachment such as a guard rail is attached to the support post 23, the weedproof sheet body 10 can be easily laid.
なお、図１では、支柱２３が円柱であり、その断面形状が円形である場合について示しているが、支柱２３の断面形状は円形以外の形状、例えば、三角形、四角形などの多角形や楕円形等、任意の形状であることができる。本発明の防草構造体に用いる防草シート本体１０の本体開口部１１の形状は、支柱２３の断面の形状と相似形状であることが好ましい。 Note that FIG. 1 shows a case where the support column 23 is a cylinder and the cross-sectional shape thereof is circular, but the cross-sectional shape of the support column 23 is a shape other than a circle, for example, a polygon such as a triangle or a quadrangle, or an elliptical shape. Or any other shape. The shape of the body opening 11 of the weedproof sheet body 10 used in the weedproof structure of the present invention is preferably similar to the shape of the cross section of the column 23.
図１に示す防草構造体は、１枚の防草シート本体１０が一つの本体開口部１１を有する場合を図示したが、１枚の防草シート本体１０は、二つ以上の支柱２３を貫通させるために、二つ以上の本体開口部１１を有することができる。このような場合には、複数の支柱位置に対応する防草シート本体１０の位置に、複数の本体開口部１１を正確に形成することは困難である。そのため、本体開口部１１は、支柱２３の断面の形状の最長寸法より１〜２０ｍｍ大きいことが好ましい。「形状の最長寸法」とは、その形状の任意の２点を結ぶ直線の長さの中で最長の長さをいう。例えば、支柱２３の断面の形状が円の場合は、支柱２３の形状の最長寸法は円の直径である。また、支柱２３の形状が長方形の場合には、最長寸法は対角線の長さである。 The grass protection structure shown in FIG. 1 illustrates the case where one grass protection sheet main body 10 has one main body opening 11, but one grass protection sheet main body 10 includes two or more support columns 23. Two or more body openings 11 can be provided for penetration. In such a case, it is difficult to accurately form the plurality of main body openings 11 at the position of the weedproof sheet main body 10 corresponding to the plurality of column positions. Therefore, the main body opening 11 is preferably 1 to 20 mm larger than the longest dimension of the cross-sectional shape of the column 23. The “longest dimension of the shape” refers to the longest length of straight lines connecting two arbitrary points of the shape. For example, when the cross-sectional shape of the column 23 is a circle, the longest dimension of the column 23 is the diameter of the circle. Moreover, when the shape of the support | pillar 23 is a rectangle, the longest dimension is the length of a diagonal line.
草の生育をより確実に防止する点から、防草シート本体１０の本体切断部４３をなるべく短くすることが好ましい。したがって、図３の例で示すように、防草シート本体１０において、本体切断部４３を、本体開口部１１の１点と防草シート本体１０の端部の１点との距離が、最短距離となるような直線状に形成することが好ましい。なお、図３においては、本体開口部１１から防草シート本体１０の右辺の端部に向かって本体切断部４３を形成するように図示している。本体開口部１１の位置によっては、図３の防草シート本体１０の上辺、下辺又は左辺の端部に向かって本体切断部４３を形成することにより、本体切断部４３を最短とすることができる。 From the viewpoint of more reliably preventing grass growth, it is preferable to shorten the main body cutting portion 43 of the weedproof sheet main body 10 as much as possible. Therefore, as shown in the example of FIG. 3, in the weedproof sheet main body 10, the distance between the main body cutting portion 43 and one point of the main body opening 11 and one end of the weedproof sheet main body 10 is the shortest distance. It is preferable to form a straight line such that In addition, in FIG. 3, it has illustrated so that the main body cutting part 43 may be formed toward the edge part of the right side of the weed prevention sheet main body 10 from the main body opening part 11. As shown in FIG. Depending on the position of the main body opening 11, the main body cutting portion 43 can be made the shortest by forming the main body cutting portion 43 toward the end of the upper side, the lower side or the left side of the weedproof sheet main body 10 in FIG. 3. .
＜パッチシート＞
本発明の防草構造体は、パッチシート４０を含む。パッチシート４０の一例を、図４に示す。パッチシート４０は、パッチ開口部４２及びパッチ切断部４４を有する。パッチシート４０は、防草シート本体１０上に敷設される。パッチ開口部４２は、パッチシート４０を支柱２３に貫通させるための開口部である。
<Patch sheet>
The herbicidal structure of the present invention includes a patch sheet 40. An example of the patch sheet 40 is shown in FIG. The patch sheet 40 has a patch opening 42 and a patch cutting part 44. The patch sheet 40 is laid on the weedproof sheet body 10. The patch opening 42 is an opening for allowing the patch sheet 40 to penetrate the support post 23.
パッチシート４０は、パッチ開口部４２とパッチシート４０との端部の１点との間を切断した部分であるパッチ切断部４４を有する。パッチシート４０を防草シート本体１０上に敷設する際に、パッチ切断部４４に支柱２３を通過させることによって、図７及び図８に示すように、支柱２３がパッチ開口部４２を貫通する状態にすることができる。そのため、支柱２３にガードレール等の取付物が取り付けられている場合でも、パッチシート４０を容易に敷設することができる。 The patch sheet 40 includes a patch cutting portion 44 that is a portion obtained by cutting between the patch opening 42 and one point at the end of the patch sheet 40. When the patch sheet 40 is laid on the weedproof sheet main body 10, the strut 23 passes through the patch opening 42 as shown in FIGS. 7 and 8 by passing the strut 23 through the patch cutting portion 44. Can be. Therefore, even when an attachment such as a guard rail is attached to the column 23, the patch sheet 40 can be easily laid.
パッチシート４０を防草シート本体１０上に敷設する際には、パッチシート４０が、防草シート本体１０の本体切断部４３を全て覆うように敷設する。また、このとき、本体切断部４３とパッチ切断部４４が重ならないように、パッチシート４０を敷設する。このようにパッチシート４０を防草シート本体１０上に敷設することによって、本体切断部４３の全体がパッチシート４０のパッチ切断部４４ではない部分に覆われることになるので、防草シート本体１０の本体切断部４３からの草の生育を防止することができる。 When laying the patch sheet 40 on the weedproof sheet main body 10, the patch sheet 40 is laid so as to cover the main body cutting part 43 of the weedproof sheet main body 10. At this time, the patch sheet 40 is laid so that the main body cutting part 43 and the patch cutting part 44 do not overlap. By laying the patch sheet 40 on the weedproof sheet main body 10 in this way, the entire main body cutting portion 43 is covered with a portion other than the patch cutting portion 44 of the patch sheet 40. Grass growth from the main body cutting part 43 can be prevented.
防草シート本体１０と、防草シート本体１０上に敷設したパッチシート４０とは、粘着材接着法及び／又はテープ接着法により固定することが好ましい。 The weedproof sheet body 10 and the patch sheet 40 laid on the weedproof sheet body 10 are preferably fixed by an adhesive material bonding method and / or a tape bonding method.
粘着材接着法により固定する場合、具体的には、防草シート本体１０の表面と、パッチシート４０の裏面との間の防草シート本体１０の表面に、改質アスファルトを含む目止め材などの粘着材を塗布し、加圧し、粘着することにより接着層４５を形成し、防草シート本体１０の表面とパッチシート４０の裏面とを固定することができる。なお、防草シート本体１０の表面に無機質粒子などが配置される場合があるが、改質アスファルトを含む目止め材などの粘着材が無機質粒子間に充填されて、密実な粘着材塗布層が形成されるため無機質粒子を除去する必要はない。粘着材のみを用いた固定の場合には、粘着材が無機質粒子などと渾然とした状態になるので、明確な層状の接着層４５を形成しなくなる。しかしながら、所定の場所に粘着材が存在して被接着物同士を接着すれば良いので、接着層４５は明確な層状である必要は無い。 When fixing by the adhesive material adhesion method, specifically, a sealing material containing modified asphalt on the surface of the weedproof sheet body 10 between the surface of the weedproof sheet body 10 and the back surface of the patch sheet 40, etc. The adhesive layer 45 can be formed by applying, pressurizing, and adhering the adhesive material, and the surface of the weedproof sheet body 10 and the back surface of the patch sheet 40 can be fixed. In some cases, inorganic particles or the like may be disposed on the surface of the herbicidal sheet main body 10, but an adhesive material such as a sealing material containing modified asphalt is filled between the inorganic particles to provide a dense adhesive material coating layer. Therefore, it is not necessary to remove inorganic particles. In the case of fixing using only the pressure-sensitive adhesive material, the pressure-sensitive adhesive material is in a resolute state with inorganic particles and the like, so that a clear layered adhesive layer 45 is not formed. However, the adhesive layer 45 does not need to be a clear layer because an adhesive is present at a predetermined location and the objects to be bonded are bonded together.
テープ接着法により接着層４５を形成して固定する場合、具体的には、防草シート本体１０の表面と、パッチシート４０の裏面との間に、全体の大きさがパッチシート４０の大きさ以下である両面粘着テープを挟み、加圧し、粘着することにより、防草シート本体１０の表面とパッチシート４０の裏面とを固定することができる。なお、防草シート本体１０の表面に無機質粒子などが配置される場合があるが、両面粘着テープを挟む前に、両面粘着テープにより接着する場所に位置する無機質粒子を除去することが好ましい。 When the adhesive layer 45 is formed and fixed by the tape bonding method, specifically, the overall size is the size of the patch sheet 40 between the surface of the weedproof sheet body 10 and the back surface of the patch sheet 40. The surface of the weedproof sheet main body 10 and the back surface of the patch sheet 40 can be fixed by sandwiching, pressing and adhering the double-sided adhesive tape described below. In addition, although inorganic particles etc. may be arrange | positioned on the surface of the weed prevention sheet main body 10, before pinching a double-sided adhesive tape, it is preferable to remove the inorganic particle located in the place adhere | attached with a double-sided adhesive tape.
粘着材接着法及びテープ接着法により接着層４５を形成して固定する場合、具体的には、防草シート本体１０の表面と、パッチシート４０の裏面との間の防草シート本体１０の表面に、改質アスファルトを含む目止め材などの粘着材を塗布し、粘着材の塗布層の表面と、パッチシート４０の裏面との間に、全体の大きさがパッチシート４０の大きさ以下である両面粘着テープを挟み、加圧し、粘着することにより、防草シート本体１０の表面とパッチシート４０の裏面とを固定することができる。なお、防草シート本体１０の表面に無機質粒子などが配置される場合があるが、改質アスファルトを含む目止め材などの粘着材が無機質粒子間に充填されて、密実な粘着材塗布層が形成されるため無機質粒子を除去する必要はない。 When the adhesive layer 45 is formed and fixed by the adhesive material bonding method and the tape bonding method, specifically, the surface of the grass protection sheet body 10 between the surface of the grass protection sheet body 10 and the back surface of the patch sheet 40. In addition, an adhesive material such as a sealing material containing modified asphalt is applied, and the overall size is less than the size of the patch sheet 40 between the surface of the adhesive material coating layer and the back surface of the patch sheet 40. The surface of the weedproof sheet main body 10 and the back surface of the patch sheet 40 can be fixed by sandwiching a certain double-sided adhesive tape, applying pressure, and adhering. In some cases, inorganic particles or the like may be disposed on the surface of the herbicidal sheet main body 10, but an adhesive material such as a sealing material containing modified asphalt is filled between the inorganic particles to provide a dense adhesive material coating layer. Therefore, it is not necessary to remove inorganic particles.
粘着材接着法及び／又はテープ接着法を用いて接着層４５を形成し固定すると、加熱融着法と同等の接着強度を得ることができる。住宅地近傍への設置の場合や、設置箇所近傍に下草等の可燃物が多い場合など、火気の使用が好ましくない場合、あるいは制限されている場合に、粘着材接着法及び／又はテープ接着法を用いて防草構造体を施工することができる。 When the adhesive layer 45 is formed and fixed using the adhesive material bonding method and / or the tape bonding method, an adhesive strength equivalent to the heat fusion method can be obtained. Adhesive bonding method and / or tape bonding method when use of fire is not desirable or restricted, such as when installed near residential areas or when there are many flammables such as undergrass near the installation location Can be used to construct a weedproof structure.
パッチシート４０は、敷設したときに本体切断部４３を覆うのに十分な大きさを有する形状であることが必要である。パッチシート４０の形状は、円形、楕円形、正方形又は長方形のものを用いることができ、特に正方形又は長方形のものを用いることが好ましい。正方形又は長方形パッチシート４０の一辺の長さは、支柱２３の断面の形状の最長寸法Ｄｐより１００〜４００ｍｍ長いことが好ましい。 The patch sheet 40 needs to have a shape having a size sufficient to cover the main body cutting portion 43 when laid. The patch sheet 40 can be circular, oval, square or rectangular, and is preferably square or rectangular. The length of one side of the square or rectangular patch sheet 40 is preferably 100 to 400 mm longer than the longest dimension Dp of the cross-sectional shape of the column 23.
切断部の長さを最小限にとどめる点から、防草シート本体１０の本体切断部４３及びパッチシート４０のパッチ切断部４４の形状は、ともに直線的に切断した形状であることが好ましい。また、草の生育の防止を確実にするという点から、本体切断部４３とパッチ切断部４４との支柱中心位置を中心とした角度（図９に示す角度θ）が、９０〜２７０度であるようにパッチシート４０を防草シート本体１０上に敷設することが好ましい。 From the standpoint of minimizing the length of the cutting part, it is preferable that the main body cutting part 43 of the weedproof sheet main body 10 and the patch cutting part 44 of the patch sheet 40 are both linearly cut. Further, from the viewpoint of ensuring the prevention of grass growth, the angle (angle θ shown in FIG. 9) around the column center position of the main body cutting part 43 and the patch cutting part 44 is 90 to 270 degrees. Thus, it is preferable to lay the patch sheet 40 on the weedproof sheet body 10.
パッチシート４０は、少なくとも平面方向に伸び性を有することが好ましい。パッチシート４０が伸び性を有する場合、パッチシート４０のパッチ開口部４２の大きさは、支柱２３の断面の形状より小さいことが好ましい。「伸び性を有する」とは、ある方向に力を加えた場合に、その方向に向かって弾性的な伸びを示すことができる性質をいう。パッチシート４０が伸び性を有すると、パッチ開口部４２に支柱２３を貫通させる際、パッチ開口部４２は広がることができ、支柱貫通前のパッチ開口部４２の形状の最長寸法Ｄｈと、支柱２３の断面の形状の最長寸法Ｄｐとの比Ｄｈ／Ｄｐが、０．９≦Ｄｈ／Ｄｐ≦１である場合に、パッチ開口部４２に支柱２３が貫通した後には、支柱２３とパッチ開口部４２との間の隙間を無くすことができる。そのため、支柱２３とパッチ開口部４２との間にコーキング材を詰めなくても、その隙間からの草の生育を防止することができる。 The patch sheet 40 preferably has extensibility at least in the plane direction. In the case where the patch sheet 40 has stretchability, the size of the patch opening 42 of the patch sheet 40 is preferably smaller than the cross-sectional shape of the column 23. “Having extensibility” refers to a property that, when a force is applied in a certain direction, can exhibit elastic elongation in that direction. When the patch sheet 40 is stretchable, the patch opening 42 can be widened when the support 23 is penetrated through the patch opening 42, and the longest dimension Dh of the shape of the patch opening 42 before penetrating the strut 23 and the support 23. When the ratio Dh / Dp to the longest dimension Dp of the cross-sectional shape is 0.9 ≦ Dh / Dp ≦ 1, after the support 23 penetrates the patch opening 42, the support 23 and the patch opening 42 The gap between the two can be eliminated. Therefore, even if caulking material is not packed between the support column 23 and the patch opening 42, it is possible to prevent grass growth from the gap.
また、支柱貫通前のパッチ開口部の形状の最長寸法Ｄｈと、支柱の断面の形状の最長寸法Ｄｐとの比Ｄｈ／Ｄｐが、１＜Ｄｈ／Ｄｐ≦１．１である場合には、パッチ開口部４２に支柱２３が貫通した後には、支柱２３とパッチ開口部４２との間の隙間をほとんど無くすことができるが、防草をより確実にするために、支柱２３とパッチ開口部４２との間にシリコン系シール材等のコーキング材を配置することが好ましい。 If the ratio Dh / Dp of the longest dimension Dh of the shape of the patch opening before penetrating and the longest dimension Dp of the cross section of the pillar is 1 <Dh / Dp ≦ 1.1, the patch After the support 23 penetrates the opening 42, the gap between the support 23 and the patch opening 42 can be almost eliminated. However, in order to make the grass protection more reliable, the support 23 and the patch opening 42 It is preferable to arrange a caulking material such as a silicon-based sealing material between them.
パッチシート４０のパッチ開口部４２の形状は、本体開口部１１の場合と同様に、支柱２３の断面の形状と相似形状であることが好ましい。より確実に防草を行うという点から、支柱２３が貫通する前のパッチ開口部４２の形状の最長寸法Ｄｈと、支柱２３の断面の形状の最長寸法Ｄｐとの比Ｄｈ／Ｄｐは、好ましくは０．９〜１．１であること、より好ましくは０．９５〜１．０５であること、さらに好ましくは０．９８〜１．０２であること、特に好ましくは０．９９〜１．０１であることが好ましい。 The shape of the patch opening 42 of the patch sheet 40 is preferably similar to the shape of the cross section of the column 23, as in the case of the main body opening 11. The ratio Dh / Dp between the longest dimension Dh of the shape of the patch opening 42 before the column 23 penetrates and the longest dimension Dp of the cross-sectional shape of the column 23 is preferably 0.9 to 1.1, more preferably 0.95 to 1.05, further preferably 0.98 to 1.02, particularly preferably 0.99 to 1.01. Preferably there is.
また、さらに確実に防草を行うという点から、パッチシート４０の引張伸び率が、好ましくは２０％以上、さらに好ましくは３０％以上、より好ましくは４０％以上、特に好ましくは５０％以上であることが好ましい。前記の引張伸び率を有するパッチシート４０を用いることによって良好な防草シート施工性と優れた防草特性を得ることができる。なお、「引張伸び率」とは、ＪＩＳ・Ａ６０１３に準拠した測定値である。 In addition, from the viewpoint of more reliably preventing grass, the tensile elongation of the patch sheet 40 is preferably 20% or more, more preferably 30% or more, more preferably 40% or more, and particularly preferably 50% or more. It is preferable. By using the patch sheet 40 having the above-described tensile elongation rate, it is possible to obtain good herbicidal sheet workability and excellent herbicidal properties. The “tensile elongation” is a measured value based on JIS A6013.
＜防草シート本体及びパッチシートの材料＞
本発明の防草構造体に含まれる防草シート本体１０及びパッチシート４０は、特に限定されるものではなく、市販の防草シートから適宜選択して用いることができるが、特に、可撓性、防水性及び遮光性を有し、シート状の形状を有するものは、良好な耐久性を有することから好適に用いることができる。本発明に用いる防草シート１０及びパッチシート４０の具体例として、優れた可撓性、防水性及び遮光性を有する改質アスファルト系防草シート、例えば、特開２００２−２７２３４８号公報（特許文献１）に開示された改質アスファルト系防草シートを好ましく用いることができる。
<Material of the weedproof sheet body and patch sheet>
The weedproof sheet main body 10 and the patch sheet 40 included in the weedproof structure of the present invention are not particularly limited, and can be appropriately selected from commercially available weedproof sheets. Those having waterproofness and light-shielding properties and having a sheet-like shape can be suitably used because they have good durability. Specific examples of the herbicidal sheet 10 and the patch sheet 40 used in the present invention include a modified asphalt-based herbicidal sheet having excellent flexibility, waterproofness and light-shielding property, for example, JP-A-2002-272348 (Patent Document) The modified asphalt type herbicidal sheet disclosed in 1) can be preferably used.
「改質アスファルト系防草シート」とは、改質アスファルトを材料として含む防草シートのことをいう。改質アスファルトとしては、具体的には後述する耐貫通型防草シートの（ｂ）層及び（ｄ）層に用いることのできる改質アスファルトと同様のものを用いることができる。改質アスファルト系防草シートは、建築用防水シート（改質アスファルト系防水シート）を転用して用いることができる。 The “modified asphalt-based herbicidal sheet” refers to a herbicidal sheet containing modified asphalt as a material. Specifically, the modified asphalt may be the same as the modified asphalt that can be used for the (b) layer and the (d) layer of the penetration-resistant grass protection sheet described later. The modified asphalt-based herbicidal sheet can be used by diverting an architectural waterproof sheet (modified asphalt-based waterproof sheet).
改質アスファルト系防草シートとしては、単層の改質アスファルトと基材層とからなるシートのみならず、２層の改質アスファルト層の間に不織布等からなる基材層を含む構造のものを用いることができる。 The modified asphalt type herbicidal sheet has a structure including not only a sheet composed of a single layer of modified asphalt and a base material layer but also a base material layer composed of a nonwoven fabric or the like between two modified asphalt layers. Can be used.
また、改質アスファルト系防草シートは、さらに表面層及び裏面層を含むことができる。表面層には、後述する耐貫通型防草シートの（ａ）表面層と同様のものを用いることができる。また、裏面層には、合成樹脂フィルムを好適に用いることができる。合成樹脂フィルムとしては、具体的には、ＨＤＰＥフィルム（高密度ポリエチレン）及びＯＰＰフィルム（二軸延伸成形ポリプロピレン）などから選択したものを好適に用いることができる。また、後述する耐貫通型防草シートの（ｅ）裏面層と同様のものを用いることができる。 Moreover, the modified asphalt-based herbicidal sheet can further include a surface layer and a back surface layer. As the surface layer, the same material as the surface layer (a) of the penetration-resistant weedproof sheet described later can be used. Moreover, a synthetic resin film can be used suitably for a back surface layer. As the synthetic resin film, specifically, a film selected from an HDPE film (high density polyethylene) and an OPP film (biaxially stretched polypropylene) can be suitably used. Moreover, the same thing as the (e) back surface layer of the penetration-proof type weedproof sheet mentioned later can be used.
改質アスファルト系防草シートの構造の一例は、表面層、改質アスファルト層、基材層、改質アスファルト層及び裏面層をこの順番で有する構造であるが、これらの層の全てを含む必要はなく、また、さらなる層を含むこともできる。 An example of the structure of the modified asphalt type herbicidal sheet is a structure having a surface layer, a modified asphalt layer, a base material layer, a modified asphalt layer, and a back surface layer in this order, but it is necessary to include all of these layers. It can also include additional layers.
本発明の防草構造体に含まれる防草シート本体１０及びパッチシート４０として、改質アスファルト系防草シートの１種である、後述する耐貫通型防草シートを用いることが特に好ましい。 As the weedproof sheet main body 10 and the patch sheet 40 included in the weedproof structure of the present invention, it is particularly preferable to use a penetration-resistant weedproof sheet, which will be described later, which is one type of a modified asphalt type weedproof sheet.
上述した本発明の施工方法によって、優れた防草構造体の施工を容易に行うことができ、得られた防草構造体は、長期に渡って良好な防草効果を発揮して、良好な景観形成に寄与できる。 By the construction method of the present invention described above, it is possible to easily construct an excellent herbicidal structure, and the obtained herbicidal structure exhibits a good herbicidal effect over a long period of time. It can contribute to landscape formation.
また、本発明の防草構造体に含まれる防草シート本体１０及びパッチシート４０の少なくとも一方が、後述する耐貫通型防草シートであることが特に好ましい。 Moreover, it is particularly preferable that at least one of the weedproof sheet main body 10 and the patch sheet 40 included in the weedproof structure of the present invention is a penetration-resistant weedproof sheet described later.
＜防草構造体の態様＞
本発明の防草構造体を、道路の法面３０のような舗装面２１に隣接した防草区域に設置する場合、防草シート本体１０の一端（第一端部１２）が道路の舗装面端部２２に固定され、第一端部１２の反対側の他端（第二端部１３）は法面３０に固定される。防草シート本体１０の第一端部１２と、舗装面端部２２とが接触する部分は、粘着材接着法及び／又はテープ接着法により固定される。さらに、防草シート本体１０の第一端部１２の舗装面端部２２への固定を、第一の釘状器具１４を用いて行うことにより、固定を確実にする。また、防草シート本体１０の第二端部１３は、第二の釘状器具１５によって地面に固定される。なお、「第一端部１２」及び「第二端部１３」は、防草シート本体１０の所定の一端付近の領域であり、防草シート本体１０を所定の方法によって固定するために必要な寸法を有する領域である。
<Mode of the weed prevention structure>
When the grass protection structure of the present invention is installed in a grass protection area adjacent to a pavement surface 21 such as a road slope 30, one end (first end portion 12) of the grass protection sheet body 10 is a road pavement surface. The other end (second end portion 13) opposite to the first end portion 12 is fixed to the slope 22. The portion where the first end 12 of the weedproof sheet main body 10 and the paved surface end 22 are in contact with each other is fixed by an adhesive material bonding method and / or a tape bonding method. Furthermore, fixing is ensured by fixing the first end portion 12 of the weedproof sheet main body 10 to the paved surface end portion 22 by using the first nail-like instrument 14. Further, the second end portion 13 of the weedproof sheet main body 10 is fixed to the ground by the second nail-like instrument 15. The “first end portion 12” and the “second end portion 13” are regions in the vicinity of a predetermined end of the weedproof sheet body 10, and are necessary for fixing the weedproof sheet body 10 by a predetermined method. An area having dimensions.
防草シート本体１０の端部と舗装面２１等とは、粘着材接着法及び／又はテープ接着法により固定することができる。具体的には、防草シート本体１０の端部と、舗装面２１との間に、改質アスファルトを含む目止め材などの粘着材塗布層及び／又は両面粘着テープなどのテープ接着層４５を挟み、加圧し、粘着して固化することにより、端部を舗装面２１等に固定する。 The edge part of the weedproof sheet main body 10 and the pavement surface 21 can be fixed by an adhesive material bonding method and / or a tape bonding method. Specifically, a tape adhesive layer 45 such as a pressure-sensitive adhesive coating layer such as a sealing material containing modified asphalt and / or a double-sided pressure-sensitive adhesive tape is provided between the end portion of the weedproof sheet main body 10 and the pavement surface 21. The end is fixed to the pavement surface 21 or the like by sandwiching, pressing, sticking and solidifying.
また、防草シート本体１０の端部と舗装面２１等とは、粘着材接着法及び／又はテープ接着法により固定することができる。具体的には、改質アスファルトを含む目止め材などの粘着材塗布層及び／又は両面に接着性のあるアスファルトテープを防草シート本体１０の端部と舗装面２１等との間に設け、端部と舗装面２１等との固定を行うことができる。 Moreover, the edge part and the pavement surface 21 grade | etc., Of the weed prevention sheet main body 10 can be fixed by the adhesive material adhesion method and / or the tape adhesion method. Specifically, an adhesive material coating layer such as a sealing material containing modified asphalt and / or an asphalt tape having adhesiveness on both sides are provided between the end of the weedproof sheet body 10 and the pavement surface 21 or the like, The end and the paved surface 21 can be fixed.
防草シート本体１０の端部と舗装面２１等との固定をより確実にするという点から、粘着材接着法及び／又はテープ接着法を用いる。粘着材接着法及び／又はテープ接着法は、火気の使用が好ましくない場合、あるいは制限されている場合にも用いることができる。 From the viewpoint of securing the end portion of the weedproof sheet main body 10 and the pavement surface 21 and the like more reliably, an adhesive material bonding method and / or a tape bonding method is used. The pressure-sensitive adhesive bonding method and / or the tape bonding method can be used even when the use of fire is not preferable or restricted.
防草シート本体１０の第一端部１２の舗装面端部２２への固定のための第一の釘状器具１４としては、オールアンカー、コンクリート釘、又は測量釘などを用いることができる。オールアンカーとは、アンカー本体、打込みピン、ナット及びワッシャーがセットになったアンカーのことである。オールアンカーの一例として、直径５ｍｍ、長さ３０ｍｍのものを用いることができる。また、オールアンカーによる固定を確実にするために、さらにオールアンカー用ディスク（例えば、厚さ１．２ｍｍ、直径４５ｍｍ）を用いることができる。また、コンクリート釘による固定を効率的にかつ確実にするために、自動釘打機を用いることが好ましい。 As the first nail-like instrument 14 for fixing the first end portion 12 of the weedproof sheet main body 10 to the paved surface end portion 22, an all anchor, a concrete nail, a surveying nail, or the like can be used. The all anchor is an anchor in which an anchor body, a driving pin, a nut and a washer are set. As an example of the all anchor, one having a diameter of 5 mm and a length of 30 mm can be used. Further, in order to ensure fixing by the all anchor, an all anchor disk (for example, a thickness of 1.2 mm and a diameter of 45 mm) can be used. Moreover, it is preferable to use an automatic nailing machine in order to efficiently and reliably fix the concrete nails.
防草シート本体１０の第二端部１３を法面３０に固定するための第二の釘状器具１５としては、具体的には、Ｌ字型のピンを用いることができる。Ｌ字型のピンの寸法の一例として、鉄道軌道の法面に防草構造体を施工する場合、直径１６ｍｍ、長辺の長さ５００〜８００ｍｍのものを好適に用いることができ、道路法面に防草構造体を施工する場合、直径９ｍｍ、長辺の長さ１５０〜３００ｍｍのものを好適に用いることができる。 Specifically, an L-shaped pin can be used as the second nail-like instrument 15 for fixing the second end portion 13 of the weedproof sheet body 10 to the slope 30. As an example of the dimension of the L-shaped pin, when constructing a weedproof structure on the slope of a railroad track, one having a diameter of 16 mm and a long side length of 500 to 800 mm can be suitably used. When constructing a weedproof structure, one having a diameter of 9 mm and a long side length of 150 to 300 mm can be suitably used.
図１４及び図１５に、防草シート１０の第二端部１３を法面３０へ固定するための一態様の、法面３０付近の断面模式図を示す。この態様の場合、図１４に示すように、法面３０に法面掘削部３１を設け、第二の釘状器具１５を用いて防草シート１０を法面掘削部３１に固定する。次に、図１５に示すように、法面掘削部３１を埋め戻すことにより、第二端部１３を法面３０へ埋め込むことで、第二端部１３の固定を確実にする。防草シート１０の第二端部１３は、法面埋設部３２に埋め込まれるため、暴風などによって防草シート１０の第二端部１３が捲れることを防止することができる。 14 and 15 are schematic cross-sectional views in the vicinity of the slope 30 of one embodiment for fixing the second end 13 of the weedproof sheet 10 to the slope 30. FIG. In the case of this aspect, as shown in FIG. 14, a slope digging portion 31 is provided on the slope 30, and the grass protection sheet 10 is fixed to the slope digging portion 31 using the second nail-like instrument 15. Next, as shown in FIG. 15, the second end portion 13 is embedded in the slope 30 by refilling the slope excavation portion 31, thereby securing the second end portion 13. Since the second end portion 13 of the weedproof sheet 10 is embedded in the slope burying portion 32, it is possible to prevent the second end portion 13 of the weedproof sheet 10 from dripping due to a storm or the like.
また、図１に示すように、鉄筋１６を配置し、第二の釘状器具１５によって鉄筋１６を固定すると、防草シート本体１０の第二端部１３を埋設することなく、防草シート本体１０の法面３０への固定を確実にすることができる。鉄筋１６は、寒冷地などで融雪剤等が道路管理に用いられる場所では、融雪剤等の薬品に侵されることがないようなものを用いることが好ましい。鉄筋１６は、具体的には、亜鉛メッキやアルミニウムを含む亜鉛合金メッキを施した直径６ｍｍ程度の鋼線であることが好ましい。 Further, as shown in FIG. 1, when the reinforcing bar 16 is arranged and the reinforcing bar 16 is fixed by the second nail-like instrument 15, the second end 13 of the weedproof sheet main body 10 is not embedded and the weedproof sheet main body is embedded. The fixing to the 10 slopes 30 can be ensured. It is preferable to use a reinforcing bar 16 that is not affected by chemicals such as a snow melting agent in a cold district or the like where a snow melting agent or the like is used for road management. Specifically, the reinforcing bar 16 is preferably a steel wire having a diameter of about 6 mm subjected to zinc plating or zinc alloy plating including aluminum.
また、防草シート１０の第二端部１３を法面３０へ固定するための別の態様として、メッシュ状押さえ具２７を用いることができる。メッシュ状押さえ具２７として、具体的には、金属製メッシュや合成樹脂製メッシュ等のメッシュ状材料を帯状にしたものを用いることができる。メッシュ状押さえ具２７を用いて防草シート１０を法面３０に固定する具体例を、図１２（平面模式図）及び図１３（断面模式図に）に示す。メッシュ状押さえ具２７の幅は、０．３〜２ｍ程度であり、０．５〜１ｍであることが好ましい。図１２及び図１３に示すように、防草シート１０の第二端部１３と法面３０の一部を跨ぐように、メッシュ状押さえ具２７を敷設する。メッシュ状押さえ具２７の防草シート１０上に敷設した部分及び法面３０上に敷設した部分の両方を、上述の第二の釘状器具１５によって法面３０に固定することにより、防草シート１０の法面３０に対する固定を確実にすることができる。このようにメッシュ状押さえ具２７を用いる固定方法の場合、暴風などによって防草シート１０の第二端部１３が捲れることを防止することもできる。 Further, as another mode for fixing the second end portion 13 of the weedproof sheet 10 to the slope 30, a mesh-like presser 27 can be used. Specifically, as the mesh-like presser 27, a belt-like mesh-like material such as a metal mesh or a synthetic resin mesh can be used. Specific examples of fixing the grass prevention sheet 10 to the slope 30 using the mesh-shaped presser 27 are shown in FIG. 12 (planar schematic diagram) and FIG. 13 (cross-sectional schematic diagram). The width | variety of the mesh-shaped pressing tool 27 is about 0.3-2m, and it is preferable that it is 0.5-1m. As shown in FIG. 12 and FIG. 13, a mesh-like presser 27 is laid so as to straddle the second end portion 13 of the weedproof sheet 10 and a part of the slope 30. Both the portion laid on the grass prevention sheet 10 and the portion laid on the slope 30 of the mesh-like presser 27 are fixed to the slope 30 by the second nail-shaped instrument 15, thereby providing the grass prevention sheet. The fixing to the 10 slopes 30 can be ensured. Thus, in the case of the fixing method using the mesh-shaped presser 27, it can also prevent that the 2nd edge part 13 of the weed prevention sheet | seat 10 is curled by a storm or the like.
また、防草シート１０の法面３０に対する固定をさらに確実にするために、メッシュ状押さえ具２７の上にさらに上述の鉄筋１６を配置し、第二の釘状器具１５を用いてメッシュ状押さえ具２７及び鉄筋１６を固定することが好ましい。 Further, in order to further secure the herbicidal sheet 10 to the slope 30, the above-described reinforcing bar 16 is further arranged on the mesh-like presser 27, and the mesh-like presser is used using the second nail-like tool 15. It is preferable to fix the tool 27 and the reinforcing bar 16.
防草シート本体１０の寸法は、防草区域の寸法やその他の施工条件によって、適宜選択することができる。例えば、図１に示す例においては、複数の防草シート本体１０が、防草シート本体重ね合わせ接着部１７にて接続された構造となっている。このように、適宜選択した寸法の複数の防草シート本体１０の防草シート本体重ね合わせ接着部１７を、粘着材接着法及び／又はテープ接着法により張り合わせて用いることにより、本発明の防草構造体を任意の寸法の防草区域に設置することができる。 The dimension of the weedproof sheet body 10 can be appropriately selected depending on the dimensions of the weedproof area and other construction conditions. For example, in the example shown in FIG. 1, a plurality of weedproof sheet main bodies 10 are connected by a weedproof sheet main body overlapping bonding portion 17. In this way, the herbicidal sheet main body overlapping adhesive portions 17 of the plurality of herbicidal sheet main bodies 10 having dimensions appropriately selected are used by being bonded together by an adhesive material bonding method and / or a tape bonding method, thereby providing the herbicidal material of the present invention. The structure can be installed in a weedproof area of any size.
防草区域の幅が防草シート本体１０より狭い場合、すなわち防草区域の幅が一般的に１ｍ程度以下の場合には、一枚のテープ状の防草シートを防草シート本体１０として用いて防草構造体を設置することができる。テープ状の防草シート本体１０には、支柱２３の間隔に対応する所定の位置に複数の本体開口部１１を形成する。複数の本体開口部１１を有するテープ状の防草シート本体１０を、支柱２３が本体開口部１１を貫通するように敷設することができる。防草シート本体１０の本体開口部１１の大きさは、支柱２３の断面大きさより大きくすることにより、防草シート本体１０の複数の本体開口部１１と、対応する複数の支柱２３との位置合わせは容易になる。ただし、支柱２３の位置と、本体開口部１１との位置合わせをさらに容易にするためには、各々の防草シート本体１０が一つの本体開口部１１を有するように防草シート本体１０の寸法を選択することが好ましい。各々の支柱２３の周りの防草シート本体１０上には、パッチシート４０が敷設される。 When the width of the grass protection area is narrower than that of the grass protection sheet body 10, that is, when the width of the grass protection area is generally about 1 m or less, a single tape-shaped grass protection sheet is used as the grass protection sheet body 10. Can be installed. A plurality of main body openings 11 are formed in the tape-shaped weed-proof sheet main body 10 at predetermined positions corresponding to the intervals between the columns 23. The tape-shaped weed-proof sheet main body 10 having a plurality of main body openings 11 can be laid so that the columns 23 penetrate the main body openings 11. The size of the main body opening 11 of the weedproof sheet main body 10 is larger than the cross-sectional size of the support post 23, thereby aligning the plurality of main body opening portions 11 of the weedproof sheet main body 10 with the corresponding plurality of support posts 23. Becomes easier. However, in order to further facilitate the alignment between the position of the column 23 and the main body opening 11, the dimensions of the weedproof sheet main body 10 so that each of the weedproof sheet main bodies 10 has one main body opening 11. Is preferably selected. A patch sheet 40 is laid on the weedproof sheet body 10 around each column 23.
防草区域の横方向端部１８及び１９（図１及び図１２では上下方向で示されている）は、防草シート本体１０を、コンクリート等への粘着材接着法及び／又はテープ接着法による固定（横方向端部１８）、ピンによる固定処理（横方向端部１９）などの終端処理を行うことにより、防草効果を確実にすることができる。 The lateral ends 18 and 19 (shown in the vertical direction in FIGS. 1 and 12) of the weed prevention area are obtained by attaching the weed prevention sheet main body 10 to an adhesive material and / or a tape adhering method to concrete or the like. By performing termination processing such as fixing (lateral end portion 18) and pin fixing processing (lateral end portion 19), the weedproof effect can be ensured.
本発明の防草構造体は、道路、線路、河川、公園及び造林園など並びにこれらの周辺の地面、表面及び法面など、防草が必要な場所であれば、どのような場所にも用いることができる。とりわけ、防草区域が舗装面２１に隣接した防草区域に本発明の防草構造体を設置すると、より優れた防草効果を奏することができる。また、本発明の防草構造体は、舗装面２１が、アスファルト舗装道路の舗装面２１であり、防草区域が、アスファルト舗装道路の法面３０である場合に、さらに優れた防草効果を奏することができる。本発明の施工方法では、粘着材接着法及び／又はテープ接着法を防草シート本体１０等の固定に用いることにより、施工場所での火気の使用が好ましくない場合、あるいは制限されている場合にも、防草構造体を施工し、設置することができる The grass protection structure of the present invention is used in any place where grass protection is necessary, such as roads, railways, rivers, parks, afforestation gardens, and the surrounding ground, surfaces, and slopes. be able to. In particular, when the grass protection structure of the present invention is installed in a grass protection area where the grass protection area is adjacent to the pavement surface 21, it is possible to achieve a better grass protection effect. Further, the grass protection structure of the present invention has a further excellent herbicidal effect when the pavement surface 21 is the pavement surface 21 of the asphalt pavement and the grass prevention area is the slope 30 of the asphalt pavement. Can play. In the construction method of the present invention, when the adhesive material bonding method and / or the tape bonding method is used for fixing the grass protection sheet main body 10 or the like, the use of fire at the construction site is not preferable or limited. Can also construct and install a weedproof structure
＜防草構造体の施工方法＞
次に、本発明の防草構造体の施工方法について説明する。
<Construction method of weedproof structure>
Next, the construction method of the weedproof structure of this invention is demonstrated.
本発明の防草構造体は、図２に例示するような、取付物が取り付けられている支柱２３を有する防草区域に施工される。本発明の防草構造体の施工方法は、防草シート本体１０の、支柱位置に対応する防草シート本体１０の位置に本体開口部１１を形成する。また、防草区域に、ガードレール、道路標識や信号等を取り付けた支柱が既に存在している場合には、その本体開口部１１の１点と防草シート本体１０の端部の１点との間に本体切断部４３を形成することが好ましい。本体開口部１１及び本体切断部４３を形成することにより、図３に示すような防草シート本体１０を得ることができる。支柱貫通前の本体開口部１１の形状は、支柱２３の断面の形状と相似形状であり、かつ支柱２３の断面の形状の最長寸法より１〜２０ｍｍ大きいことが好ましい。また、本体切断部４３を、本体開口部１１の１点と防草シート本体１０の端部の１点との距離が、最短距離となるように形成することが好ましい。 The grass protection structure of the present invention is applied to a grass protection area having a post 23 to which an attachment is attached as illustrated in FIG. The construction method of the weedproof structure of the present invention forms the main body opening 11 at the position of the weedproof sheet main body 10 corresponding to the position of the support. In addition, when there is already a support post attached with a guardrail, a road sign, a signal or the like in the grass prevention area, one point of the main body opening 11 and one point of the end of the grass prevention sheet main body 10 It is preferable to form the main body cutting part 43 between them. By forming the main body opening 11 and the main body cutting part 43, the weedproof sheet main body 10 as shown in FIG. 3 can be obtained. The shape of the main body opening 11 before penetrating the column is preferably similar to the shape of the cross section of the column 23 and is 1 to 20 mm larger than the longest dimension of the cross section of the column 23. Moreover, it is preferable to form the main body cutting part 43 so that the distance between one point of the main body opening 11 and one point of the end of the weedproof sheet main body 10 is the shortest distance.
また、本発明の防草構造体の施工方法において、図４に例示するようなパッチシート４０を用いる場合には、パッチシート４０に、パッチ開口部４２を形成し、パッチ開口部４２の１点とパッチシート４０の端部の１点との間にパッチ切断部４４を形成する。これにより、図４に示すようなパッチシート４０を得ることができる。パッチシート４０の形状は、正方形又は長方形であり、正方形又は長方形の一辺の長さが、支柱２３の断面の形状の最長寸法Ｄｐより１００〜４００ｍｍ長いことが好ましい。支柱貫通前のパッチ開口部４２の形状は、支柱２３の断面の形状と相似形状であり、かつ支柱２３の断面の形状とほぼ同じであることが好ましい。また、支柱貫通前のパッチ開口部４２の形状の最長寸法Ｄｈと、支柱２３の断面の形状の最長寸法Ｄｐとの比Ｄｈ／Ｄｐが、０．９〜１．１であることが好ましい。また、パッチシート４０が、少なくとも平面方向に伸び性を有し、パッチシート４０の引張伸び率が、２０％以上であることが好ましい。 Further, in the construction method of the weedproof structure of the present invention, when the patch sheet 40 illustrated in FIG. 4 is used, a patch opening 42 is formed in the patch sheet 40, and one point of the patch opening 42 is formed. And a patch cutting portion 44 is formed between one point at the end of the patch sheet 40. Thereby, the patch sheet 40 as shown in FIG. 4 can be obtained. The shape of the patch sheet 40 is a square or a rectangle, and the length of one side of the square or the rectangle is preferably 100 to 400 mm longer than the longest dimension Dp of the cross-sectional shape of the column 23. It is preferable that the shape of the patch opening 42 before penetrating through is similar to the cross-sectional shape of the post 23 and substantially the same as the cross-sectional shape of the post 23. The ratio Dh / Dp between the longest dimension Dh of the shape of the patch opening 42 before penetrating the longest dimension Dp of the cross-sectional shape of the pillar 23 is preferably 0.9 to 1.1. Moreover, it is preferable that the patch sheet 40 has extensibility at least in a plane direction, and the tensile elongation rate of the patch sheet 40 is 20% or more.
また、本発明の防草構造体の施工方法では、防草シート本体１０の本体開口部１１に本体切断部４３を通過させることによって支柱２３を防草シート本体１０に貫通させることができる。本発明の防草構造体の施工方法は、防草シート本体１０の端部（第一端部１２）を、舗装面端部２２に重なるように配置する工程を含む。この工程により、図５及び図６に示すような構造を得ることができる。防草シート本体１０の端部（第一端部１２）は、粘着材接着法及び／又はテープ接着法によって舗装面端部２２に固定することができる。図６の例示において、粘着材及び／又はテープは、第一端部１２と舗装面端部２２との間の接着層４５として図示している。さらに、防草シート本体１０の端部（第一端部１２）を、さらに第一の釘状器具１４によって舗装面端部２２に固定することができる。 Moreover, in the construction method of the weedproof structure of this invention, the support | pillar 23 can be penetrated to the weedproof sheet main body 10 by allowing the main body cutting part 43 to pass through the main body opening part 11 of the weedproof sheet main body 10. FIG. The construction method of the weedproof structure of the present invention includes a step of arranging the end portion (first end portion 12) of the weedproof sheet body 10 so as to overlap the paved surface end portion 22. By this step, a structure as shown in FIGS. 5 and 6 can be obtained. The end portion (first end portion 12) of the weedproof sheet main body 10 can be fixed to the pavement surface end portion 22 by an adhesive material bonding method and / or a tape bonding method. In the illustration of FIG. 6, the adhesive material and / or the tape is illustrated as an adhesive layer 45 between the first end portion 12 and the paved surface end portion 22. Further, the end portion (first end portion 12) of the weedproof sheet main body 10 can be further fixed to the paved surface end portion 22 by the first nail-like instrument 14.
また、本発明の防草構造体の施工方法は、パッチ開口部４２にパッチ切断部４４を通過させることによって支柱２３をパッチシート４０に貫通させ、本体切断部４３を全て覆いかつ本体切断部４３とパッチ切断部４４が重ならないように、防草シート本体１０上にパッチシート４０を敷設する工程を含む。この工程により、図７及び図８に示すような構造を得ることができる。このとき、本体切断部４３及びパッチ切断部４４の形状が直線状であり、パッチシート４０を敷設する工程において、本体切断部４３とパッチ切断部４４との支柱中心位置を中心とした角度（図９に示す角度θ）が、９０〜２７０度であるようにパッチシート４０を敷設することが好ましい。 In the construction method of the weedproof structure according to the present invention, the patch cutting part 44 is passed through the patch opening 42 to penetrate the patch sheet 40 to cover the main body cutting part 43 and the main body cutting part 43. And a step of laying the patch sheet 40 on the weedproof sheet main body 10 so that the patch cutting part 44 does not overlap. By this step, a structure as shown in FIGS. 7 and 8 can be obtained. At this time, the main body cutting portion 43 and the patch cutting portion 44 have a straight shape, and in the step of laying the patch sheet 40, an angle centered on the column center position between the main body cutting portion 43 and the patch cutting portion 44 (see FIG. It is preferable to lay the patch sheet 40 so that the angle θ) shown in 9 is 90 to 270 degrees.
防草シート本体１０と、防草シート本体１０上に敷設したパッチシート４０とは粘着材接着法及び／又はテープ接着法により固定する。図８の例示において、粘着材及び／又はテープは、防草シート本体１０とパッチシート４０との間の接着層４５として図示している。固定をより確実にするという点から、防草シート本体１０と、パッチシート４０とは、粘着材接着法及び／又はテープ接着法により固定する。粘着材接着法及び／又はテープ接着法により、住宅地近傍への設置の場合や、設置箇所近傍に下草等の可燃物が多い場合など、火気の使用が好ましくない場合、あるいは制限されている場所においても本発明の防草構造体を施工することができる。 The weedproof sheet body 10 and the patch sheet 40 laid on the weedproof sheet body 10 are fixed by an adhesive material bonding method and / or a tape bonding method. In the illustration of FIG. 8, the adhesive material and / or tape is illustrated as an adhesive layer 45 between the weedproof sheet body 10 and the patch sheet 40. From the point of securing the fixing more securely, the weedproof sheet body 10 and the patch sheet 40 are fixed by an adhesive material bonding method and / or a tape bonding method. Places where the use of fire is not preferred or restricted due to the adhesive bonding method and / or tape bonding method, such as when installed near residential areas or when there are many flammables such as undergrass near the installation location In this case, the weedproof structure of the present invention can be applied.
また、本体開口部１１と支柱２３のとの間及び／又はパッチ開口部４２と支柱２３との間に、シリコン系シール材を充填する工程をさらに含むことが好ましい。 Moreover, it is preferable to further include a step of filling a silicon-based sealant between the main body opening 11 and the support column 23 and / or between the patch opening 42 and the support column 23.
防草区域が、道路の法面３０のように、舗装面２１に隣接した防草区域である場合には、防草シート本体１０の第一端部１２を、舗装面端部２２に重なるように配置する工程（Ａ）と、防草シート本体１０の第一端部１２を、粘着材接着法及び／又はテープ接着によって舗装面端部２２に固定する工程（Ｂ）と、防草シート本体の第一端部を、さらに第一の釘状器具１４によって舗装面端部２２に固定する工程（Ｃ）と、防草シート本体の第一端部とは反対側の第二端部１３を、第二の釘状器具１５によって地面に固定する工程（Ｄ）とを含むことができる。 When the grass protection area is a grass protection area adjacent to the pavement surface 21 like the slope 30 of the road, the first end 12 of the grass protection sheet main body 10 overlaps the pavement surface end 22. A step (A) of arranging the first weed portion 12 of the weedproof sheet main body 10 on the pavement surface end portion 22 by an adhesive material bonding method and / or tape bonding, and a weedproof sheet main body. (C) which fixes the 1st end part of this to the pavement surface edge part 22 further by the 1st nail-like instrument 14, and the 2nd end part 13 on the opposite side to the 1st end part of a weed prevention sheet main body And (D) fixing to the ground with the second nail-like instrument 15.
本発明の防草構造体の施工方法は、取付物が、ガードレールのように複数の支柱２３に連続的に取り付けられている場合に、より優れた効果を奏することができる。 The construction method of the weedproof structure according to the present invention can achieve a more excellent effect when the attachment is continuously attached to the plurality of support columns 23 like a guardrail.
防草構造体の施工方法を、舗装面２１がアスファルト舗装道路の舗装面２１であり、防草区域がアスファルト舗装道路の法面３０であるような場所に用いると、本発明のさらに優れた効果を奏する防草構造体を得ることができる。 When the construction method of the weed prevention structure is used in a place where the pavement surface 21 is the pavement surface 21 of the asphalt pavement and the grass prevention area is the slope 30 of the asphalt pavement, the further excellent effect of the present invention is achieved. Can be obtained.
また、本発明の防草構造体の施工方法は、防草区域が、取付物が取り付けられている支柱２３を有している場合には、上記工程（Ａ）の前に、防草シート本体１０の、支柱２３の位置に対応する防草シート本体１０の位置に本体開口部１１及び本体開口部１１の１点と防草シート本体１０の端部の１点との間に本体切断部４３を形成する工程と、パッチシート４０に、パッチ開口部４２及びパッチ開口部４２の１点とパッチシート４０の端部の１点との間にパッチ切断部４４を形成する工程と、本体切断部４３に支柱２３を通過させることによって、支柱２３を防草シート本体１０の本体開口部１１に貫通させる工程をさらに含むことが好ましい。また、工程（Ａ）の後に、パッチ切断部４４に支柱２３を通過させることによって、支柱２３をパッチシート４０のパッチ開口部４２に貫通させ、本体切断部４３を全て覆いかつ本体切断部４３とパッチ切断部４４とが重ならないように、防草シート本体１０上にパッチシート４０を敷設する工程と、パッチシート４０を、粘着材接着法及び／又はテープ接着によって防草シート本体１０に固定する工程とをさらに含むことが好ましい。 Moreover, the construction method of the weedproof structure of this invention is the weedproof sheet main body before the said process (A), when the weedproof area has the support | pillar 23 to which the attachment is attached. 10 at the position of the weedproof sheet main body 10 corresponding to the position of the support 23, and between the one point of the main body opening 11 and the main body opening 11 and one end of the weedproof sheet main body 10. Forming a patch cutting portion 44 between the patch opening 42 and one point of the patch opening portion 42 and one end of the patch sheet 40, and a main body cutting portion. It is preferable to further include a step of passing the support post 23 through the main body opening 11 of the weedproof sheet main body 10 by passing the support post 23 through 43. Further, after the step (A), the post 23 is passed through the patch cutting unit 44, thereby penetrating the post 23 through the patch opening 42 of the patch sheet 40, covering all the main body cutting unit 43 and the main body cutting unit 43. The step of laying the patch sheet 40 on the grass protection sheet main body 10 so that the patch cutting portion 44 does not overlap, and the patch sheet 40 is fixed to the grass protection sheet main body 10 by an adhesive material bonding method and / or tape bonding. It is preferable that a process is further included.
＜耐貫通型防草シート＞
次に、本発明の防草構造体の防草シート本体及び／又はパッチシートに用いることが特に好ましいに防草シートついて説明する。本明細書及び特許請求の範囲では、ここで説明する防草シートのことを「耐貫通型防草シート」という。耐貫通型防草シートは、硬く鋭い雑草の芽に対する貫通防止性に優れるため、本発明の防草構造体に用いることが特に好ましい。本発明の防草構造体の防草シート本体及び／又はパッチシートとして耐貫通型防草シート本体を用いることにより、際立った防草性能と優れた耐久性とを併せ持った防草構造体及びその施工方法を得ることができる。なお、耐貫通型防草シートは、改質アスファルト系防草シートの一種である。
<Penetration-proof grass protection sheet>
Next, the weedproof sheet is particularly preferably used for the weedproof sheet body and / or patch sheet of the weedproof structure of the present invention. In the present specification and claims, the weedproof sheet described here is referred to as a “penetration-resistant weedproof sheet”. The penetration-resistant weedproof sheet is particularly preferable for use in the weedproof structure of the present invention because it is excellent in penetration prevention against hard and sharp weed buds. By using a penetration-proof grass-proof sheet main body as a grass-proof sheet main body and / or patch sheet of the grass-proof structure of the present invention, a grass-proof structure having both outstanding herbicidal performance and excellent durability and its A construction method can be obtained. The penetration-resistant weedproof sheet is a kind of modified asphalt-based weedproof sheet.
＜耐貫通型防草シートの態様＞
耐貫通型防草シートは、（ａ）無機質粒子又は無機質粒子を含有する合成樹脂を含む表面層、（ｂ）改質アスファルト層、（ｃ）基材層、（ｄ）改質アスファルト層及び（ｅ）合成樹脂又は無機質粒子を含有する合成樹脂を含む裏面層の少なくとも５層をこの順で積層した耐貫通型防草シートであって、（ｃ）基材層が、織布、編み布及び不織布からなる群より選ばれる少なくとも一つである基材Ａと、スクリムを有する基材Ｂとを含み、基材Ａの織布、編み布及び不織布が、芯部と鞘部とを有する芯鞘構造の繊維を含み、芯部が融点２００℃以上の繊維及び鞘部が融点２００℃以上の樹脂であり、（ｅ）裏面層の合成樹脂が硬質合成樹脂である耐貫通型防草シートである。
<Aspects of penetration-proof grass protection sheet>
The penetration-proof grass protection sheet comprises (a) a surface layer containing inorganic particles or a synthetic resin containing inorganic particles, (b) a modified asphalt layer, (c) a base material layer, (d) a modified asphalt layer and ( e) a penetration-proof weedproof sheet in which at least 5 layers of a back surface layer containing a synthetic resin or a synthetic resin containing inorganic particles are laminated in this order, wherein (c) the base material layer comprises a woven fabric, a knitted fabric, and A core sheath comprising a base material A which is at least one selected from the group consisting of non-woven fabrics and a base material B having a scrim, wherein the woven fabric, knitted fabric and non-woven fabric of the base material A have a core portion and a sheath portion. It is a penetration-proof herbicidal sheet containing fibers having a structure, a core having a melting point of 200 ° C. or higher and a sheath having a melting point of 200 ° C. or higher, and (e) a synthetic resin for the back layer being a hard synthetic resin. .
耐貫通型防草シートの好ましい態様を以下に示す。耐貫通型防草シートでは、これらの態様を適宜組み合わせることができる。
（１）（ｅ）裏面層の硬質合成樹脂が、ポリプロピレン、ポリエステル、ポリカーボネート、ポリアミドイミド、ポリエステルイミド、ポリアミド、ポリイミド、ポリ塩化ビニル及びポリハロゲン化ポリビニルからなる群より選択される少なくとも一つの合成樹脂である。
（２）（ｅ）裏面層が、厚さ１０〜５０μｍの二軸延伸成形ポリプロピレンフィルムである。
（３）（ｃ）基材層が、基材Ａと、基材Ｂと、基材Ａとをこの順に積層し、接着された、若しくは熱融着された三層構造を有する。
（４）芯部と鞘部とが、熱融着されている。
（５）基材Ｂが、複数の互いに平行な略等間隔の高強度繊維の繊維束からなる組を２組以上有し、異なった組の繊維束は、略等角度で互いに交差しあうスクリムである。
（６）基材Ａと、基材Ｂとの接触部の少なくとも一部が、融点２００℃以上の樹脂及び／又は２００℃で熱分解しない接着剤により接着されている、若しくは熱融着されている。
（７）（ｃ）基材層が、７５〜５００ｇ／ｍ２の目付量を有する。
（８）（ａ）表面層が、天然スレート、タルク及びマイカからなる群より選ばれる少なくとも一種以上の、扁平状の無機質粒子を含む。
The preferable aspect of a penetration-proof grass prevention sheet is shown below. In the penetration-proof weedproof sheet, these modes can be combined as appropriate.
(1) (e) At least one synthetic resin in which the hard synthetic resin of the back layer is selected from the group consisting of polypropylene, polyester, polycarbonate, polyamideimide, polyesterimide, polyamide, polyimide, polyvinyl chloride, and polyhalogenated polyvinyl It is.
(2) (e) The back layer is a biaxially stretched polypropylene film having a thickness of 10 to 50 μm.
(3) (c) The base material layer has a three-layer structure in which the base material A, the base material B, and the base material A are laminated in this order and adhered or heat-sealed.
(4) The core part and the sheath part are heat-sealed.
(5) The base material B has two or more sets of fiber bundles of a plurality of high-strength fibers that are parallel to each other at approximately equal intervals, and the different sets of fiber bundles cross each other at substantially equal angles. It is.
(6) At least a part of the contact portion between the base material A and the base material B is bonded or thermally fused with a resin having a melting point of 200 ° C. or higher and / or an adhesive that does not thermally decompose at 200 ° C. Yes.
(7) (c) The base material layer has a basis weight of 75 to 500 g / m 2 .
(8) (a) The surface layer contains at least one or more flat inorganic particles selected from the group consisting of natural slate, talc and mica.
また、耐貫通型防草シートは、上記の防草シートを敷設した防草構造体に用いることができる。 Further, the penetration-proof grass protection sheet can be used for a grass protection structure in which the grass protection sheet is laid.
＜耐貫通型防草シートの効果＞
耐貫通型防草シートにより、道路、線路、河川、公園及び造林園など並びにこれらの周辺などの地面、表面、特に法面での草の成育を防止ための、遮光性を有し、耐候性、機械的特性、不透水性に優れ、さらに硬く鋭い雑草の芽の防草シートに対する貫通防止性に優れる防草シートを得ることができる。
<Effect of penetration-proof grass protection sheet>
With a penetration-proof grass protection sheet, it has light-shielding and weather resistance to prevent grass growth on the ground, surface, especially slopes, such as roads, railways, rivers, parks and afforestation gardens, and their surroundings. Thus, it is possible to obtain a herbicidal sheet excellent in mechanical properties and water impermeability, and further excellent in preventing penetration of hard and sharp weed buds against the herbicidal sheet.
＜耐貫通型防草シートの詳細＞
図１６に、耐貫通型防草シートの模式的断面図を示す。耐貫通型防草シートは、（ａ）無機質粒子又は無機質粒子を含有する合成樹脂を含む表面層１、（ｂ）改質アスファルト層２、（ｃ）基材層３、（ｄ）改質アスファルト層４及び（ｅ）合成樹脂又は無機質粒子を含有する合成樹脂である裏面層５の少なくとも５層を、この順で積層した耐貫通型防草シートである。耐貫通型防草シートは、道路、線路、河川、公園及び造林園など並びにこれらの周辺などの地面、表面、特に法面での草の成育を防止するための、遮光性を有し、耐候性、機械的特性、不透水性に優れ、さらに硬く鋭い雑草の芽の防草シートに対する貫通防止性に優れる。以下、耐貫通型防草シートを詳細に説明する。
<Details of penetration-proof grass protection sheet>
FIG. 16 shows a schematic cross-sectional view of a penetration-proof grass protection sheet. The penetration-proof grass protection sheet includes (a) a surface layer 1 containing inorganic particles or a synthetic resin containing inorganic particles, (b) a modified asphalt layer 2, (c) a base material layer 3, and (d) a modified asphalt. It is a penetration-proof weedproof sheet in which at least five layers of the layer 4 and (e) the back surface layer 5 which is a synthetic resin or a synthetic resin containing inorganic particles are laminated in this order. The penetration-proof grass protection sheet is light-shielding and weather-resistant to prevent grass growth on the ground, surfaces, especially slopes, such as roads, railways, rivers, parks and afforestation gardens, and their surroundings. It has excellent properties, mechanical properties, and imperviousness, and also has excellent penetration prevention properties against hard and sharp weed buds. Hereinafter, the penetration-resistant weedproof sheet will be described in detail.
＜（ｃ）基材層＞
（ｃ）基材層は、織布、編み布及び不織布からなる群より選ばれる少なくとも一つである基材Ａと、スクリムを有する基材Ｂとを含む。
<(C) Base material layer>
(C) A base material layer contains the base material A which is at least 1 chosen from the group which consists of a woven fabric, a knitted fabric, and a nonwoven fabric, and the base material B which has a scrim.
＜（ｃ）基材層の基材Ａ＞
基材Ａを構成する織布、編み布及び不織布は、芯部と鞘部とを有する芯鞘構造の繊維を含むものである。本明細書で「繊維」とは、単繊維、２本以上の繊維、２本以上の繊維の束（繊維束）、及び２本以上の繊維によりをかけたもの（糸）を包含する。
<(C) Base material A of base material layer>
The woven fabric, knitted fabric and non-woven fabric constituting the base material A include fibers having a core-sheath structure having a core portion and a sheath portion. In the present specification, the “fiber” includes a single fiber, two or more fibers, a bundle of two or more fibers (fiber bundle), and a yarn (thread) multiplied by two or more fibers.
基材Ａは、織布、編み布及び不織布から選ばれる基材であり、織布、編み布又は不織布を２以上組み合わせて用いることができる。基材Ａとして、芯部が融点２００℃以上の繊維と、鞘部が融点２００℃以上の樹脂からなる芯鞘構造の繊維からなる織布、編み布及び／又は不織布を用いることができる。また、基材Ａとして、その芯鞘構造の繊維からなる織布、編み布及び／又は不織布と、融点２００℃以上の繊維からなる織布、編み布及び／又は不織布を組み合わせて用いることもできる。なお、繊維の融点の上限は特に限定されない。樹脂の融点の上限も特に限定されないが、製造の容易性及びコストの点から、５００℃以下が好ましく、４００℃以下がさらに好ましい。 The base material A is a base material selected from woven fabric, knitted fabric and non-woven fabric, and can be used in combination of two or more woven fabric, knitted fabric or non-woven fabric. As the base material A, a woven fabric, a knitted fabric, and / or a non-woven fabric made of a fiber having a core-sheath structure in which a core has a melting point of 200 ° C. or higher and a sheath has a melting point of 200 ° C. or higher can be used. Further, as the base material A, a woven fabric, a knitted fabric and / or a nonwoven fabric made of fibers of the core-sheath structure and a woven fabric, a knitted fabric and / or a nonwoven fabric made of fibers having a melting point of 200 ° C. or higher can be used in combination. . The upper limit of the melting point of the fiber is not particularly limited. The upper limit of the melting point of the resin is not particularly limited, but is preferably 500 ° C. or less, and more preferably 400 ° C. or less, from the viewpoint of ease of production and cost.
＜（ｃ）基材層の基材Ａ：芯鞘構造＞
（ｃ）基材層の基材Ａとして用いることのできる芯鞘構造の繊維とは、一つの成分（鞘部）がもう一つの成分（芯部）の少なくとも一部の表面を包む状態の構造を有する繊維を意味する。芯鞘構造の繊維は、鞘部が芯部の表面を、５０％以上、さらに７０％以上、特に９０％以上包む状態の構造であることが好ましい。特に、芯鞘構造の繊維は、鞘部が芯部の表面を完全に包む状態の構造の繊維であることが最も好ましい。
<(C) Base material A of base material layer: core-sheath structure>
(C) The core-sheath structure fiber that can be used as the base material A of the base material layer is a structure in which one component (sheath part) wraps at least a part of the surface of another component (core part). Means a fiber having The fiber having a core-sheath structure preferably has a structure in which the sheath part covers the surface of the core part by 50% or more, further 70% or more, particularly 90% or more. In particular, the core-sheath structure fiber is most preferably a fiber having a structure in which the sheath part completely wraps around the surface of the core part.
芯部は、融点２００℃以上の繊維である。また、芯部は、低吸水性の合成樹脂や無機物であることが、耐貫通型防草シートを製造する過程での耐熱性や長期供用時の物性の安定性に優れるために好ましい。芯部は、吸水率（２４時間、２３℃）が好ましくは１％以下、さらに好ましくは０．９％以下、特に好ましくは０．８％未満の合成樹脂や無機物が好ましく用いることができる。具体的な芯部の材料としては、低吸水性のナイロン１１やナイロン１２、ポリエステルやガラスなどの合成樹脂や無機物からなる繊維を用いることが、吸水性及び機械的強度などの点から好ましい。 The core is a fiber having a melting point of 200 ° C. or higher. Moreover, it is preferable that the core part is a low water-absorbing synthetic resin or an inorganic substance because it is excellent in heat resistance in the process of producing a penetration-proof grassproof sheet and in stability of physical properties during long-term use. For the core, a synthetic resin or an inorganic substance having a water absorption rate (24 hours, 23 ° C.) of preferably 1% or less, more preferably 0.9% or less, and particularly preferably less than 0.8% can be preferably used. As a specific core material, it is preferable from the viewpoint of water absorption and mechanical strength to use low water-absorbing nylon 11, nylon 12, synthetic resin such as polyester and glass, or fibers made of inorganic materials.
鞘部の材料は、融点２００℃以上の樹脂であることが、耐貫通型防草シートを製造する過程での耐熱性や長期供用時の物性の安定性に優れるために好ましい。融点２００℃以上の樹脂としては、融点２００℃以上の天然や合成の樹脂ならどのようなものでも用いることができ、特に、融点２００℃以上のポリアミド、ポリカーボネート、ポリフェニレンオキシド、ポリエーテルスルホン、ポリアミドイミド、ポリエステルイミド、ポリイミド、ポリスルホン及びポリエーテルなどから選択した１種以上の樹脂を用いることができる。特に、低吸水性のナイロン１１及びナイロン１２から選択した１種以上が長期供用時の物性に優れることから好適に使用できる。また、融点２００℃以上の樹脂としては、部分架橋あるいは架橋したゴムを用いることもできる。 The material of the sheath is preferably a resin having a melting point of 200 ° C. or higher because of excellent heat resistance in the process of producing a penetration-proof grassproof sheet and stability of physical properties during long-term use. As the resin having a melting point of 200 ° C. or higher, any natural or synthetic resin having a melting point of 200 ° C. or higher can be used. Particularly, polyamide, polycarbonate, polyphenylene oxide, polyethersulfone, polyamideimide having a melting point of 200 ° C. or higher can be used. One or more resins selected from polyester imide, polyimide, polysulfone, polyether and the like can be used. In particular, one or more selected from low water-absorbing nylon 11 and nylon 12 can be suitably used because they have excellent physical properties during long-term use. Further, as the resin having a melting point of 200 ° C. or higher, partially crosslinked or crosslinked rubber can be used.
また、芯部と鞘部とは、熱融着されていることが好ましい。熱融着は、芯部の材料と鞘部の材料のうち少なくともどちらか一つの融点より高い温度を加えることによって行うことができる。芯部と鞘部とは、熱融着されていることにより、耐貫通型防草シートの製造過程で溶融状態（２００℃未満）の改質アスファルト中に浸漬されても優れた形状安定性を得ることができる。 Moreover, it is preferable that the core part and the sheath part are heat-sealed. The thermal fusion can be performed by applying a temperature higher than the melting point of at least one of the core material and the sheath material. The core part and the sheath part are heat-sealed, so that excellent shape stability can be obtained even when immersed in modified asphalt in a molten state (less than 200 ° C.) in the process of manufacturing a penetration-proof grassproof sheet. Can be obtained.
基材Ａに、融点２００℃以上の芯鞘構造の繊維からなる織布、編み布及び不織布を用いる場合には、芯鞘構造の繊維の、（ｉ）一部が融点２００℃以上の樹脂により接着されている織布、編み布、不織布など、（ｉｉ）一部が２００℃で熱分解しない接着剤及び／又は樹脂により接着されている織布、編み布、不織布など、（ｉｉｉ）一部が熱融着されている織布、編み布、不織布などを用いることが好ましい。なお、樹脂の融点及び接着剤の熱分解温度の上限は特に限定されないが、製造の容易性及びコストの点から、５００℃以下が好ましく、４００℃以下がさらに好ましい。 When a woven fabric, a knitted fabric, or a non-woven fabric made of a core-sheath fiber having a melting point of 200 ° C. or higher is used as the base material A, Adhered woven fabric, knitted fabric, non-woven fabric, etc. (ii) Partially woven fabric, knitted fabric, non-woven fabric bonded with an adhesive and / or resin that does not thermally decompose at 200 ° C. (iii) Some It is preferable to use a woven fabric, a knitted fabric, a non-woven fabric, or the like that is heat-sealed. In addition, although the upper limit of melting | fusing point of resin and the thermal decomposition temperature of an adhesive agent is not specifically limited, 500 degreeC or less is preferable from the point of the ease of manufacture and cost, and 400 degreeC or less is more preferable.
基材Ａとして、（ｉ）一部が融点２００℃以上の樹脂により接着されている織布、編み布、不織布を用いる場合には、融点２００℃以上の樹脂としては、融点２００℃以上の天然や合成の樹脂であればどのようなものでも用いることができ、特に、融点２００℃以上のポリアミド、ポリカーボネート、ポリフェニレンオキシド、ポリエーテルスルホン、ポリアミドイミド、ポリエステルイミド、ポリイミド、ポリスルホン及びポリエーテルなどから選択した１種以上の樹脂を用いることができる。特に、低吸水性のナイロン１１及びナイロン１２から選択した１種以上を好適に使用できる。融点２００℃以上の樹脂としては、部分架橋あるいは架橋したゴムを用いることもできる。 In the case of using a woven fabric, a knitted fabric or a non-woven fabric partly bonded with a resin having a melting point of 200 ° C. or higher as the substrate A, the resin having a melting point of 200 ° C. or higher is a natural material having a melting point of 200 ° C. or higher. Any synthetic resin can be used, and in particular, selected from polyamide, polycarbonate, polyphenylene oxide, polyethersulfone, polyamideimide, polyesterimide, polyimide, polysulfone and polyether having a melting point of 200 ° C. or higher. One or more types of resins can be used. In particular, one or more selected from nylon 11 and nylon 12 having low water absorption can be suitably used. As the resin having a melting point of 200 ° C. or higher, partially crosslinked or crosslinked rubber can be used.
基材Ａとして、（ｉｉ）一部が２００℃で熱分解しない接着剤及び／又は樹脂により接着されている織布、編み布、不織布を用いることができる。２００℃で熱分解しない接着剤とは、熱重量分析において、空気中、５℃／分の昇温速度の条件下で、２００℃で重量減少率が１％以下、さらに０．５％以下、特に０％の天然や合成の樹脂である。 As the substrate A, (ii) a woven fabric, a knitted fabric, or a non-woven fabric partially bonded with an adhesive and / or resin that is not thermally decomposed at 200 ° C. can be used. An adhesive that does not thermally decompose at 200 ° C. means that, in thermogravimetric analysis, the weight loss rate is 1% or less, further 0.5% or less at 200 ° C. under the condition of a heating rate of 5 ° C./min in air. Especially 0% natural or synthetic resin.
２００℃で熱分解しない接着剤としては、２００℃で熱分解しない無機系接着剤や有機系接着剤などを用いることができる。２００℃で熱分解しない接着剤としては、例えば、ウレタン系接着剤、アクリル系接着剤、ポリアミド系接着剤、エポキシ系接着剤、ポリエステル系接着剤、ナイロン／エポキシ系接着剤、エラストマー／エポキシ系接着剤、ニトリル／フェノリック系接着剤、ウレタン／エポキシ系接着剤、ポリエステル／エポキシ系接着剤、ポリイソシアネート系接着剤、ポリエチレンイミン系接着剤、メラミン系接着剤、尿素系接着剤、フェノール系接着剤、ポリクロロプレン系接着剤、ニトリルゴム系接着剤、再生ゴム系接着剤、ＳＢＲ系接着剤及び天然ゴム系接着剤などから選択した１種以上を用いることができる。 As an adhesive that does not thermally decompose at 200 ° C., an inorganic adhesive or an organic adhesive that does not thermally decompose at 200 ° C. can be used. Examples of adhesives that do not thermally decompose at 200 ° C. include urethane adhesives, acrylic adhesives, polyamide adhesives, epoxy adhesives, polyester adhesives, nylon / epoxy adhesives, and elastomer / epoxy adhesives. Agent, nitrile / phenolic adhesive, urethane / epoxy adhesive, polyester / epoxy adhesive, polyisocyanate adhesive, polyethyleneimine adhesive, melamine adhesive, urea adhesive, phenolic adhesive, One or more selected from a polychloroprene adhesive, a nitrile rubber adhesive, a recycled rubber adhesive, an SBR adhesive, a natural rubber adhesive, and the like can be used.
２００℃で熱分解しない接着剤として、エポキシ樹脂、後述する（ａ）表面層に用いることができる合成樹脂塗料などの架橋性を有する天然や合成の樹脂を用いることが好ましい。 As an adhesive that does not thermally decompose at 200 ° C., it is preferable to use a natural or synthetic resin having crosslinkability such as an epoxy resin or a synthetic resin paint that can be used for the surface layer (a) described later.
＜（ｃ）基材層の基材Ａ：芯鞘構造の繊維及び融点２００℃以上の繊維を併用＞
また、基材Ａとして、融点２００℃以上の繊維からなる織布、編み布及び／又は不織布を用いることもできる。この融点２００℃以上の繊維からなる織布、編み布及び／又は不織布は、芯部が融点２００℃以上の繊維と、鞘部が融点２００℃以上の樹脂とからなる芯鞘構造の繊維からなる織布、編み布及び／又は不織布と組み合わせて用いることが、基材Ａとして好ましい。融点２００℃以上の繊維としては、融点２００℃以上の天然、半合成及び合成樹脂の繊維や無機のガラスなどの融点２００℃以上の有機質繊維や無機質繊維などにより構成されるものを用いることができる。
<(C) Base material A of base material layer: Combined use of fibers having a core-sheath structure and fibers having a melting point of 200 ° C. or higher>
Moreover, as the base material A, a woven fabric, a knitted fabric and / or a nonwoven fabric made of fibers having a melting point of 200 ° C. or higher can also be used. The woven fabric, knitted fabric and / or non-woven fabric made of fibers having a melting point of 200 ° C. or higher is made of fibers having a core-sheath structure in which the core portion is made of fibers having a melting point of 200 ° C. or higher and the sheath portion is made of resin having a melting point of 200 ° C. or higher. The substrate A is preferably used in combination with a woven fabric, a knitted fabric and / or a non-woven fabric. As the fiber having a melting point of 200 ° C. or higher, fibers composed of organic fibers or inorganic fibers having a melting point of 200 ° C. or higher, such as natural, semi-synthetic and synthetic resin fibers having a melting point of 200 ° C. or higher, and inorganic glass can be used. .
融点２００℃以上の繊維としては、融点２００℃以上の樹脂からなる、又は、融点２００℃以上の樹脂を含む、繊維、ガラスなどの融点２００℃以上の有機質繊維や無機質繊維などを用いることができる。なお、繊維の融点の上限は特に限定されない。 As the fiber having a melting point of 200 ° C. or higher, an organic fiber or an inorganic fiber made of a resin having a melting point of 200 ° C. or higher, or containing a resin having a melting point of 200 ° C. or higher, such as fiber or glass, can be used. . The upper limit of the melting point of the fiber is not particularly limited.
基材Ａとして、融点２００℃以上の芯鞘構造の繊維と、融点２００℃以上の繊維とからなる織布、編み布及び不織布を用いる場合には、芯鞘構造の繊維及び／又は融点２００℃以上の繊維の、（ｉ）一部が融点２００℃以上の樹脂により接着されている織布、編み布、不織布など、（ｉｉ）一部が２００℃で熱分解しない接着剤及び／又は樹脂により接着されている織布、編み布、不織布など、（ｉｉｉ）一部が熱融着されている織布、編み布、不織布などを用いることが好ましい。なお、樹脂の融点及び接着剤の熱分解温度の上限は特に限定されないが、製造の容易性及びコストの点から、５００℃以下が好ましく、４００℃以下がさらに好ましい。 In the case of using a woven fabric, a knitted fabric or a non-woven fabric composed of a core-sheath fiber having a melting point of 200 ° C. or higher and a fiber having a melting point of 200 ° C. or higher as the substrate A, the core-sheath fiber and / or the melting point of 200 ° C. Of these fibers, (i) woven fabric, knitted fabric, non-woven fabric, etc. partially bonded with a resin having a melting point of 200 ° C. or higher, and (ii) an adhesive and / or resin that does not thermally decompose at 200 ° C. It is preferable to use (iii) a woven fabric, a knitted fabric, a non-woven fabric or the like partially bonded by heat, such as a bonded woven fabric, a knitted fabric, or a non-woven fabric. In addition, although the upper limit of melting | fusing point of resin and the thermal decomposition temperature of an adhesive agent is not specifically limited, 500 degreeC or less is preferable from the point of the ease of manufacture and cost, and 400 degreeC or less is more preferable.
基材Ａとして、（ｉ）一部が融点２００℃以上の樹脂により接着されている織布、編み布、不織布を用いる場合には、融点２００℃以上の樹脂としては、融点２００℃以上の天然や合成の樹脂であればどのようなものでも用いることができ、特に、融点２００℃以上のポリアミド、ポリカーボネート、ポリフェニレンオキシド、ポリエーテルスルホン、ポリアミドイミド、ポリエステルイミド、ポリイミド、ポリスルホン及びポリエーテルなどから選択した１種以上の樹脂を用いることができる。特に、低吸水性のナイロン１１及びナイロン１２から選択した１種以上を好適に使用できる。融点２００℃以上の樹脂としては、部分架橋あるいは架橋したゴムを用いることもできる。 In the case of using a woven fabric, a knitted fabric or a non-woven fabric partly bonded with a resin having a melting point of 200 ° C. or higher as the base material A, Any synthetic resin can be used, and in particular, selected from polyamide, polycarbonate, polyphenylene oxide, polyethersulfone, polyamideimide, polyesterimide, polyimide, polysulfone and polyether having a melting point of 200 ° C. or higher. One or more types of resins can be used. In particular, one or more selected from nylon 11 and nylon 12 having low water absorption can be suitably used. As the resin having a melting point of 200 ° C. or higher, partially crosslinked or crosslinked rubber can be used.
基材Ａとして、（ｉｉ）一部が２００℃で熱分解しない接着剤及び／又は樹脂により接着されている織布、編み布、不織布を用いることができる。２００℃で熱分解しない接着剤とは、熱重量分析において、空気中、５℃／分の昇温速度の条件下で、２００℃で重量減少率が１％以下、さらに０．５％以下、特に０％の天然や合成の樹脂である。 As the substrate A, (ii) a woven fabric, a knitted fabric, or a non-woven fabric partially bonded with an adhesive and / or resin that is not thermally decomposed at 200 ° C. can be used. An adhesive that does not thermally decompose at 200 ° C. means that, in thermogravimetric analysis, the weight loss rate is 1% or less, further 0.5% or less at 200 ° C. under the condition of a heating rate of 5 ° C./min in air. Especially 0% natural or synthetic resin.
２００℃で熱分解しない接着剤としては、２００℃で熱分解しない無機系接着剤や有機系接着剤などを用いることができる。２００℃で熱分解しない接着剤としては、例えば、ウレタン系接着剤、アクリル系接着剤、ポリアミド系接着剤、エポキシ系接着剤、ポリエステル系接着剤、ナイロン／エポキシ系接着剤、エラストマー／エポキシ系接着剤、ニトリル／フェノリック系接着剤、ウレタン／エポキシ系接着剤、ポリエステル／エポキシ系接着剤、ポリイソシアネート系接着剤、ポリエチレンイミン系接着剤、メラミン系接着剤、尿素系接着剤、フェノール系接着剤、ポリクロロプレン系接着剤、ニトリルゴム系接着剤、再生ゴム系接着剤、ＳＢＲ系接着剤及び天然ゴム系接着剤などから選択した１種以上を用いることができる。 As an adhesive that does not thermally decompose at 200 ° C., an inorganic adhesive or an organic adhesive that does not thermally decompose at 200 ° C. can be used. Examples of adhesives that do not thermally decompose at 200 ° C. include urethane adhesives, acrylic adhesives, polyamide adhesives, epoxy adhesives, polyester adhesives, nylon / epoxy adhesives, and elastomer / epoxy adhesives. Agent, nitrile / phenolic adhesive, urethane / epoxy adhesive, polyester / epoxy adhesive, polyisocyanate adhesive, polyethyleneimine adhesive, melamine adhesive, urea adhesive, phenolic adhesive, One or more selected from a polychloroprene adhesive, a nitrile rubber adhesive, a recycled rubber adhesive, an SBR adhesive, a natural rubber adhesive, and the like can be used.
２００℃で熱分解しない接着剤として、エポキシ樹脂、後述する（ａ）表面層に用いることができる合成樹脂塗料などの架橋性を有する天然や合成の樹脂を用いることが好ましい。 As an adhesive that does not thermally decompose at 200 ° C., it is preferable to use a natural or synthetic resin having crosslinkability such as an epoxy resin or a synthetic resin paint that can be used for the surface layer (a) described later.
＜（ｃ）基材層の基材Ｂ＞
防草シートの機械的強度を増加させるという点から、耐貫通型防草シートにおいて、（ｃ）基材層の基材Ｂは、融点２００℃以上の繊維からなるスクリムを有していることが好ましい。スクリムとは、あらい平織り又は綾織りの織布のことを意味する。すなわち、スクリムとは、複数の互いに平行な略等間隔の繊維及び／又は糸を有する組を２組以上有し、異なった組の繊維及び／又は糸は、略等角度で互いに交差しあう形状である。一例として、２組の複数の互いに平行な略等間隔の繊維及び／又は糸が、互いにほぼ直角に交差しあう形状のスクリムを用いることができる。また、３組が互いに約６０度の角度で交差しあうスクリムを用いることもできる。繊維及び／又は糸の間隔の下限は、スクリムの重量及びコストを抑制するという点から、好ましくは３ｍｍ以上、さらに好ましくは４ｍｍ以上、より好ましくは５ｍｍ以上、特に好ましくは６ｍｍ以上のスクリムが好ましい。また、繊維及び／又は糸の間隔の上限は、必要な機械的強度の点から、好ましくは３０ｍｍ以下、さらに好ましくは２０ｍｍ以下、より好ましくは１８ｍｍ以下のスクリムが好ましい。
<(C) Base material B of base material layer>
From the point of increasing the mechanical strength of the weedproof sheet, in the penetration-resistant weedproof sheet, (c) the base material B of the base material layer has a scrim made of fibers having a melting point of 200 ° C. or higher. preferable. The scrim means a plain woven or twill woven fabric. In other words, the scrim has two or more sets each having a plurality of fibers and / or yarns that are substantially equally spaced in parallel to each other, and different sets of fibers and / or yarns cross each other at substantially equal angles. It is. As an example, it is possible to use a scrim having a shape in which two sets of a plurality of parallel and equally spaced fibers and / or yarns intersect each other at substantially right angles. It is also possible to use scrims in which the three sets cross each other at an angle of about 60 degrees. The lower limit of the fiber and / or yarn spacing is preferably a scrim of 3 mm or more, more preferably 4 mm or more, more preferably 5 mm or more, particularly preferably 6 mm or more, from the viewpoint of suppressing the weight and cost of the scrim. Moreover, the upper limit of the space | interval of a fiber and / or a thread | yarn from the point of required mechanical strength becomes like this. Preferably it is 30 mm or less, More preferably, it is 20 mm or less, More preferably, it is 18 mm or less.
また、スクリムを構成する繊維及び／又は糸は、融点２００℃以上であることが好ましい。また、高強度を有するため、スクリムを構成する繊維は、２本以上の高強度繊維の束（高強度繊維束）であることが好ましい。高強度繊維束の高強度繊維は、カーボン繊維、アラミド繊維、スチール繊維、ナイロン繊維、ポリエステル繊維及びガラス繊維から選ばれる１種以上のものを好適に使用でき、価格と入手容易性の点からガラス繊維を好適に使用することができる。なお、繊維の融点の上限は特に限定されない。 Moreover, it is preferable that the fiber and / or thread | yarn which comprise a scrim have melting | fusing point 200 degreeC or more. Moreover, since it has high intensity | strength, it is preferable that the fiber which comprises a scrim is a bundle | flux (high-strength fiber bundle) of two or more high-strength fibers. As the high-strength fiber of the high-strength fiber bundle, one or more kinds selected from carbon fiber, aramid fiber, steel fiber, nylon fiber, polyester fiber and glass fiber can be suitably used. From the viewpoint of price and availability, glass can be used. Fibers can be suitably used. The upper limit of the melting point of the fiber is not particularly limited.
＜（ｃ）基材層の構造＞
（ｃ）基材層は、基材Ａと、基材Ｂと、基材Ａとをこの順に積層した三層構造を有することが好ましい。「三層構造」とは、基材Ａと、基材Ｂと、基材Ａとをこの順に並べて接着した構造のことをいう。なお、基材Ｂはスクリムを有するため、繊維及び／又は糸が存在しない部分があるが、本明細書では、そのような部分も含めて「三層構造」という。（ｃ）基材層が、三層構造を有することによって、中間に位置する基材Ｂの上面側と下面側とが均質構造となり、この（ｃ）基材層を用いた耐貫通型防草シートを敷設した場合に良好な平面性が得られ、防草シート端部の反り返りを回避することができる。
<(C) Structure of base material layer>
(C) The base material layer preferably has a three-layer structure in which the base material A, the base material B, and the base material A are laminated in this order. The “three-layer structure” refers to a structure in which the base material A, the base material B, and the base material A are arranged and bonded in this order. In addition, since the base material B has a scrim, there are portions where fibers and / or yarns are not present. In the present specification, such a portion is also referred to as a “three-layer structure”. (C) Since the base material layer has a three-layer structure, the upper surface side and the lower surface side of the base material B located in the middle have a homogeneous structure. When the sheet is laid, good flatness can be obtained, and warping of the end portion of the weedproof sheet can be avoided.
（ｃ）基材層は、基材Ａと基材Ｂとの接着、及び基材Ｂが存在しない部分では二つの基材Ａの接着を行うことにより形成される。基材の接着を確実にするという点から、（ｃ）基材層は、基材Ａと、基材Ｂとの接触部の少なくとも一部が、融点２００℃以上の樹脂及び／又は２００℃で熱分解しない接着剤により接着されていることが好ましい。又は、基材Ａと、基材Ｂとの接触部の少なくとも一部が、２００℃以上の温度で熱融着されていることが好ましい。二つの基材Ａを接着又は融着する部分についても同様である。基材Ａと基材Ｂとが、融点２００℃以上の樹脂及び／又は２００℃で熱分解しない接着剤により接着されている、又は、２００℃以上の温度で熱融着されていることにより、（ｃ）基材層を用いた耐貫通型防草シートの製造過程で、（ｃ）基材層が溶融状態（２００℃未満）の改質アスファルト中に浸漬されても（ｃ）基材層の物性は損なわれることはなく、また優れた形状安定性を得ることができる。 (C) The base material layer is formed by adhering the base material A and the base material B and by adhering two base materials A at a portion where the base material B does not exist. From the viewpoint of ensuring the adhesion of the base material, (c) the base material layer is a resin having a melting point of 200 ° C. or higher and / or 200 ° C. at least part of the contact portion between the base material A and the base material B. It is preferable to adhere by an adhesive that does not thermally decompose. Or it is preferable that at least one part of the contact part of the base material A and the base material B is heat-sealed at the temperature of 200 degreeC or more. The same applies to a portion where two substrates A are bonded or fused. The base material A and the base material B are bonded by a resin having a melting point of 200 ° C. or higher and / or an adhesive that is not thermally decomposed at 200 ° C., or by being heat-sealed at a temperature of 200 ° C. or higher. (C) Even if the (c) base material layer is immersed in the modified asphalt in a molten state (less than 200 ° C.) in the manufacturing process of the penetration-proof grassproof sheet using the base material layer, (c) the base material layer The physical properties are not impaired, and excellent shape stability can be obtained.
（ｃ）基材層の目付量（単位面積当たりの重量）の下限は、耐貫通型防草シートの強度を保つという点から、７５ｇ／ｍ２、好ましくは１００ｇ／ｍ２、さらに好ましくは１２０ｇ／ｍ２、特に好ましくは１４０ｇ／ｍ２である。また、（ｃ）基材層の目付量の上限は、耐貫通型防草シートを施工する際の良好な作業性を確保するとともに、コストを抑えるという点から、５００ｇ／ｍ２以下、好ましくは４００ｇ／ｍ２、さらに好ましくは２００ｇ／ｍ２である。スクリムを含む基材層の目付量の具体例としては、１５５ｇ／ｍ２のものを用いることができる。（ｃ）基材層の目付量が下限値（７５ｇ／ｍ２）以上であると、好ましい引張強度や引き裂き強度を得ることができ、また上限値（５００ｇ／ｍ２）以下であると耐貫通型防草シートの強度特性が適正であるとともにシート重量が大きすぎず、敷設作業性が低下することがないことから好ましい。 (C) The lower limit of the basis weight of the base material layer (weight per unit area) is 75 g / m 2 , preferably 100 g / m 2 , more preferably 120 g, from the viewpoint of maintaining the strength of the penetration-proof grass protection sheet. / M 2 , particularly preferably 140 g / m 2 . Moreover, (c) The upper limit of the basis weight of a base material layer is 500 g / m < 2 > or less from the point of ensuring favorable workability | operativity at the time of constructing a penetration-proof type weedproof sheet, and holding down cost, Preferably 400 g / m 2 , more preferably 200 g / m 2 . As a specific example of the basis weight of the base material layer including the scrim, a material having a weight of 155 g / m 2 can be used. (C) When the basis weight of the base material layer is not less than the lower limit (75 g / m 2 ), preferable tensile strength and tear strength can be obtained, and when it is not more than the upper limit (500 g / m 2 ), there is no penetration resistance. It is preferable because the strength characteristics of the mold herbicidal sheet are appropriate and the weight of the sheet is not too large, and the laying workability does not deteriorate.
＜（ａ）表面層＞
（ａ）表面層は、無機質粒子又は無機質粒子を含有する合成樹脂を含む層である。（ａ）表面層は、無機質粒子又は無機質粒子を含有する合成樹脂からなる層であることが好ましい。（ａ）表面層に用いられる無機質粒子としては、天然スレート砂、マイカ及びタルクなどの鉱物質の扁平状無機質粒子を用いることができる。無機質粒子は、一種類又は複数種を組み合わせて用いることができる。耐貫通型防草シートでは、（ａ）表面層に扁平状の無機質粒子を用いることによって、耐候性塗料の塗着に頼ることなく長期供用においても耐貫通型防草シート全面が剥離することなく、変色や退色も小さく、耐貫通型防草シートの施工直後の状態を維持することができる。
<(A) Surface layer>
(A) The surface layer is a layer containing inorganic particles or a synthetic resin containing inorganic particles. (A) The surface layer is preferably a layer made of inorganic particles or a synthetic resin containing inorganic particles. (A) As the inorganic particles used for the surface layer, flat inorganic particles of mineral substances such as natural slate sand, mica and talc can be used. The inorganic particles can be used alone or in combination. In the penetration-proof weedproof sheet, (a) by using flat inorganic particles in the surface layer, the entire penetration-proof weedproof sheet does not peel off even in long-term use without relying on the application of weather-resistant paint. Moreover, discoloration and fading are small, and the state immediately after the construction of the penetration-proof grassproof sheet can be maintained.
さらに、耐貫通型防草シートは、扁平状の無機質粒子と改質アスファルトコンパウンドとが積層された構造を有していることから、一般的な防草シートと比較し、ポイ捨てされたタバコによる穴あき等の重大な損傷が生じにくいという効果を奏する。 Furthermore, the penetration-resistant weed-proof sheet has a structure in which flat inorganic particles and modified asphalt compound are laminated. There is an effect that serious damage such as perforation hardly occurs.
無機質粒子の粒子径は、使用上問題ないものであればどのようなものでもよく、好ましくは０．１〜１０ｍｍ、より好ましくは０．３〜８ｍｍ、さらに好ましくは０．５〜６ｍｍ、特に好ましくは１〜５ｍｍの範囲が好ましい。なお、「粒子径」とは、無機質粒子が扁平状等の場合には、無機質粒子の任意の二点を結ぶ直線のうち、最も長いものの長さのことをいうものとする。 The particle size of the inorganic particles may be any as long as there is no problem in use, preferably 0.1 to 10 mm, more preferably 0.3 to 8 mm, still more preferably 0.5 to 6 mm, particularly preferably. Is preferably in the range of 1 to 5 mm. The “particle diameter” refers to the length of the longest of the straight lines connecting any two points of the inorganic particles when the inorganic particles are flat or the like.
無機質粒子が扁平状等の場合に、無機質粒子の任意の二点を結ぶ直線のうち最も長いものの長さをＸ、この直線に直交する無機質粒子の任意の二点を結ぶ直線のうち最も長いものの長さをＹ、扁平状の無機質粒子の最も厚い部分の厚さをＺとすると、Ｙ／Ｘの値が好ましくは０．２〜１の範囲であり、より好ましくは０．３〜０．９の範囲であり、さらに好ましくは０．５〜０．８の範囲のものを好適に使用できる。また、Ｚ／Ｘの値は好ましくは０．００２〜０．４の範囲であり、より好ましくは０．０１〜０．２の範囲であり、さらに好ましくは０．０２〜０．１の範囲のものを好適に使用できる。 When the inorganic particles are flat or the like, the length of the longest line among the straight lines connecting any two points of the inorganic particles is X, and the longest of the straight lines connecting any two points of the inorganic particles perpendicular to the straight line When the length is Y and the thickness of the thickest portion of the flat inorganic particles is Z, the value of Y / X is preferably in the range of 0.2 to 1, more preferably 0.3 to 0.9. More preferably, the range of 0.5 to 0.8 can be suitably used. The value of Z / X is preferably in the range of 0.002 to 0.4, more preferably in the range of 0.01 to 0.2, and still more preferably in the range of 0.02 to 0.1. A thing can be used conveniently.
（ａ）表面層において、耐貫通型防草シート表面１ｍ２当たりの無機質粒子量は、好ましくは１００〜２０００ｇ／ｍ２、より好ましくは２００〜１５００ｇ／ｍ２、さらに好ましくは４００〜１２００ｇ／ｍ２の範囲が好ましい。 (A) in the surface layer, the inorganic particles per penetration type weed sheet surface 1 m 2 is preferably 100 to 2000 g / m 2, more preferably 200~1500g / m 2, more preferably 400~1200g / m A range of 2 is preferred.
無機質粒子は、必要に応じて撥水剤、塗料、顔料、増粘剤、耐光剤及び耐候剤などから選択される１種以上を添加、吹付け、塗布又は含浸したものを用いることができる。 As the inorganic particles, those obtained by adding, spraying, applying or impregnating at least one selected from water repellents, paints, pigments, thickeners, light fasteners, weathering agents and the like can be used.
（ａ）表面層において、無機質粒子を含有する合成樹脂は、（ｂ）改質アスファルト層に例えば貼り合わせ、塗布、吹付け及び含浸などの方法により、塗膜、シート又はフィルムとして用いることができる。無機質粒子を含有する合成樹脂は、無機質粒子及び合成樹脂塗料を含むものを用いることができる。無機質粒子を含有する合成樹脂は、合成樹脂塗料１００重量部に対し、無機質粒子３〜２５０重量部、さらに５〜２００重量部、特に１０〜１８０重量部を配合したものを用いることが好ましい。無機質粒子を含有する合成樹脂は、必要に応じて撥水剤、顔料、増粘剤、耐光剤及び耐候剤などから選択される１種以上を添加することが好ましい。 (A) In the surface layer, the synthetic resin containing inorganic particles can be used as a coating film, a sheet or a film by a method such as bonding, coating, spraying and impregnation to the modified asphalt layer (b). . As the synthetic resin containing inorganic particles, those containing inorganic particles and a synthetic resin paint can be used. As the synthetic resin containing inorganic particles, it is preferable to use a compound in which 3 to 250 parts by weight of inorganic particles, further 5 to 200 parts by weight, particularly 10 to 180 parts by weight are blended with 100 parts by weight of the synthetic resin coating. The synthetic resin containing inorganic particles is preferably added with at least one selected from water repellents, pigments, thickeners, light fasteners, weathering agents, and the like as necessary.
（ａ）表面層において、合成樹脂に含まれる無機質粒子の量は、耐貫通型防草シート表面１ｍ２当たりの無機質粒子量が、好ましくは１００〜２０００ｇ／ｍ２、より好ましくは２００〜１５００ｇ／ｍ２、さらに好ましくは４００〜１２００ｇ／ｍ２の範囲となることが好ましい。 (A) In the surface layer, the amount of the inorganic particles contained in the synthetic resin is preferably 100 to 2000 g / m 2 , more preferably 200 to 1500 g / m 2 per 1 m 2 of the penetration-proof grass protection sheet surface. m 2 , more preferably 400 to 1200 g / m 2 .
（ａ）表面層の合成樹脂としては、ポリエチレン、ポリプロピレン、エチレン−酢酸ビニル共重合体、エチレン−アクリル酸誘導体などのポリオレフィン、ポリウレタン、ポリエステル、ポリカーボネート、ポリフェニレンオキシド、ポリスルホン、ポリエーテルスルホン、ポリアミドイミド、ポリエステルイミド、ポリアミド、アクリル樹脂、ポリブタジエン、スチレン−ブタジエン共重合体などの主鎖に２重結合を２以上有するオレフィン重合体、ビニル重合体及び主鎖に２重結合を２以上有するオレフィンと主鎖に２重結合を１つ有するオレフィンとの共重合体などから選択される１種以上を用いることができる。合成樹脂としては耐候性の優れたものを使用することが好ましい。合成樹脂としては耐光性の優れたものを使用することが好ましい。合成樹脂としては柔軟性の優れたものを使用することが好ましい。 (A) As a synthetic resin of the surface layer, polyethylene, polypropylene, ethylene-vinyl acetate copolymer, polyolefin such as ethylene-acrylic acid derivative, polyurethane, polyester, polycarbonate, polyphenylene oxide, polysulfone, polyethersulfone, polyamideimide, Olefin polymer having two or more double bonds in the main chain, such as polyesterimide, polyamide, acrylic resin, polybutadiene, styrene-butadiene copolymer, vinyl polymer, and olefin having two or more double bonds in the main chain and main chain One or more selected from a copolymer with an olefin having one double bond may be used. It is preferable to use a synthetic resin having excellent weather resistance. It is preferable to use a synthetic resin having excellent light resistance. As the synthetic resin, it is preferable to use a resin having excellent flexibility.
（ａ）表面層において、合成樹脂塗料としては、ポリウレタン、アクリル樹脂、エチレン−酢酸ビニル共重合体、ポリエステル、ポリアミド、ポリイミド、ポリブタジエン及びスチレン−ブタジエン共重合体などから選択される１種以上を用いることができる。合成樹脂塗料としては耐候性の優れたものを使用することが好ましい。合成樹脂塗料としては柔軟性の優れたものを使用することが好ましい。特に、合成樹脂塗料としては、アクリル酸メチル、アクリル酸エチル、アクリル酸ブチル、メタクリル酸メチル、メタクリル酸エチル、メタクリル酸ブチルなどのアクリル酸エステル及びメタクリル酸エステルから選択されるモノマーの少なくとも１種の重合体、又はモノマーの少なくとも１種とエチレンなどのα−オレフィンやスチレンなどのほかのビニル系モノマーとの共重合体が好ましい。 (A) In the surface layer, as the synthetic resin paint, one or more selected from polyurethane, acrylic resin, ethylene-vinyl acetate copolymer, polyester, polyamide, polyimide, polybutadiene, styrene-butadiene copolymer, and the like are used. be able to. It is preferable to use a synthetic resin paint having excellent weather resistance. As the synthetic resin paint, it is preferable to use an excellent flexibility. In particular, as the synthetic resin coating, at least one monomer selected from acrylic acid esters and methacrylic acid esters such as methyl acrylate, ethyl acrylate, butyl acrylate, methyl methacrylate, ethyl methacrylate, and butyl methacrylate is used. A polymer or a copolymer of at least one monomer and an α-olefin such as ethylene or another vinyl monomer such as styrene is preferable.
＜（ｂ）層及び（ｄ）層の改質アスファルト＞
（ｂ）層及び（ｄ）層の改質アスファルトとしては、アスファルト及びポリマーを含むもの、アスファルト、ポリマー及び無機充填材の３成分を含むものなどを用いることができる。（ｂ）層及び（ｄ）層の改質アスファルトとしては、アスファルト１００重量部に対し、ポリマー１０〜４０重量部、及び無機充填材０〜２０重量部を含むものを用いることが好ましい。
<Modified asphalt of (b) layer and (d) layer>
As the modified asphalt of the (b) layer and the (d) layer, those containing asphalt and polymer, those containing three components of asphalt, polymer and inorganic filler can be used. As the modified asphalt of the (b) layer and the (d) layer, it is preferable to use those containing 10 to 40 parts by weight of the polymer and 0 to 20 parts by weight of the inorganic filler with respect to 100 parts by weight of the asphalt.
改質アスファルトは、アスファルト及びポリマーを含むもの、アスファルト、ポリマー及び無機充填材の３成分を含むものなどを１２０〜２００℃で３〜３０時間加熱混合して調製したものを用いることが、防水・防湿性、伸縮性などに優れているために好ましい。 As the modified asphalt, it is possible to use one prepared by heating and mixing at 120 to 200 ° C. for 3 to 30 hours, such as one containing asphalt and polymer, one containing three components of asphalt, polymer and inorganic filler. It is preferable because it is excellent in moisture resistance, stretchability and the like.
改質アスファルトには、以上述べた成分のほかに、プロセスオイル、ワセリン、セレシン、石油樹脂など、一般に合成樹脂やゴムの配合で用いられる撥水剤、顔料、増粘剤、耐光剤、耐候剤などの無機や有機の配合剤を添加してもよい。 In addition to the components described above, modified asphalt includes process oil, petrolatum, ceresin, petroleum resin, and other water repellents, pigments, thickeners, light-proofing agents, and weathering agents that are commonly used in blending synthetic resins and rubbers. An inorganic or organic compounding agent such as may be added.
（ｂ）層及び（ｄ）層の改質アスファルトにおいて、アスファルトとしては、天然アスファルトやアスファルタイトなど天然に産するもの、ストレートアスファルト、ブローンアスファルト、カットバックアスファルト等の石油アスファルト、又はこれらのアスファルトの混合物等が好ましい。 In the modified asphalt of the (b) layer and the (d) layer, the asphalt may be natural asphalt or asphaltite, natural asphalt, blown asphalt, petroleum asphalt such as cutback asphalt, or these asphalts A mixture or the like is preferred.
（ｂ）層及び（ｄ）層の改質アスファルトにおいて、ポリマーとしては、天然ゴム、合成ゴム、天然ゴムと合成ゴムとの混合物、ポリエチレン、エチレン酢酸−ビニル共重合体、エチレンとアクリル酸誘導体との共重合体、ポリプロピレン、ポリブテン−１、ポリ４−メチルペンテン−１、ポリスチレン、アクリロニトリル・スチレン共重合体、ＡＢＳ樹脂、ポリ塩化ビニル、ポリアクリロニトリル及びスチレンとブタジエンとの重合体（例えば、ＳＢＳなど、ＳＢＲなど）等から選択される１種以上を使用することができる。特にＳＢＳなどのゴム系が好適である。 In the modified asphalt of the (b) layer and the (d) layer, polymers include natural rubber, synthetic rubber, a mixture of natural rubber and synthetic rubber, polyethylene, ethylene acetate-vinyl copolymer, ethylene and acrylic acid derivatives, and Copolymer, polypropylene, polybutene-1, poly-4-methylpentene-1, polystyrene, acrylonitrile / styrene copolymer, ABS resin, polyvinyl chloride, polyacrylonitrile, and a polymer of styrene and butadiene (for example, SBS) , SBR, etc.) can be used. A rubber system such as SBS is particularly suitable.
（ｂ）層及び（ｄ）層の改質アスファルトにおいて、無機充填材としては、炭酸カルシウム、ケイ酸マグネシウム、ケイ酸カルシウム、ケイ酸アルミニウム、無水ケイ酸、クレー、カーボンブラック、タルク、マイカ、硫酸バリウム、珪藻土及びシリカ等の粒子状無機充填材並びに石綿及びガラス繊維などの繊維状無機充填材から選択される１種以上を用いることができる。 In the modified asphalt of the (b) layer and the (d) layer, as the inorganic filler, calcium carbonate, magnesium silicate, calcium silicate, aluminum silicate, anhydrous silicic acid, clay, carbon black, talc, mica, sulfuric acid One or more selected from particulate inorganic fillers such as barium, diatomaceous earth, and silica, and fibrous inorganic fillers such as asbestos and glass fiber can be used.
（ｂ）層及び（ｄ）層の改質アスファルトは、針入度が、好ましくは１０ｄｍｍ〜２００ｄｍｍの範囲、さらに好ましくは１５ｄｍｍ〜１００ｄｍｍの範囲、より好ましくは２０ｄｍｍ〜５０ｄｍｍの範囲、特に好ましくは２５ｄｍｍ〜３５ｄｍｍの範囲が柔軟性に優れるために好ましい。 The modified asphalt of the (b) layer and the (d) layer has a penetration of preferably 10 dmm to 200 dmm, more preferably 15 dmm to 100 dmm, more preferably 20 dmm to 50 dmm, and particularly preferably 25 dmm. The range of ˜35 dmm is preferable because of excellent flexibility.
耐貫通型防草シートでは、（ｂ）層及び（ｄ）層として、上記組成の改質アスファルトを用いることにより、特に法面に配置した場合には、法面上部に不透水性に優れた層を形成することができる。そのため、雑草の生育に不可欠な水分を遮断できるのみならず、法面が盛土で構築されている場合には、法面上部（法肩）からの雨水の浸透に伴う法面自体の帯水を効果的に防止することにより、集中豪雨などに伴う法面地盤の崩壊を回避することができる。 In the penetration-proof weedproof sheet, by using the modified asphalt having the above composition as the (b) layer and the (d) layer, particularly when arranged on the slope, it has excellent water impermeability at the top of the slope. A layer can be formed. For this reason, not only can the water essential for the growth of weeds be blocked, but when the slope is constructed with embankments, the water on the slope itself can be removed with the infiltration of rainwater from the upper part of the slope (slope). By preventing it effectively, it is possible to avoid the collapse of the slope ground due to heavy rain.
＜（ｅ）裏面層＞
耐貫通型防草シートは、（ｅ）裏面層が、合成樹脂又は無機質粒子を含有する合成樹脂を含む。（ｅ）裏面層は、合成樹脂フィルム又は無機質粒子を含有する合成樹脂フィルムであることが好ましい。
<(E) Back layer>
As for a penetration-proof type weedproof sheet, (e) the back layer contains a synthetic resin containing a synthetic resin or inorganic particles. (E) The back layer is preferably a synthetic resin film or a synthetic resin film containing inorganic particles.
（ｅ）裏面層の合成樹脂は、硬質合成樹脂である。裏面層に、硬質合成樹脂を材料としたフィルムを用いることによって、チガヤなどの雑草の芽が、耐貫通型防草シートの（ｅ）裏面層を貫くことが防止できる。また、合成樹脂フィルムの表面滑性を活かして、雑草の芽の成長方向をシート裏面と平行な方向に誘導することが可能となる。 (E) The synthetic resin of the back layer is a hard synthetic resin. By using a film made of a hard synthetic resin as the back layer, it is possible to prevent weed buds such as chigaya from penetrating the (e) back layer of the penetration-proof weedproof sheet. In addition, taking advantage of the surface smoothness of the synthetic resin film, the growth direction of weed buds can be induced in a direction parallel to the back surface of the sheet.
（ｅ）裏面層の合成樹脂フィルムの合成樹脂としては、耐光性及び耐候性に優れたものを使用することが好ましい。 (E) As the synthetic resin of the synthetic resin film of the back layer, it is preferable to use a resin excellent in light resistance and weather resistance.
（ｅ）裏面層の合成樹脂としては、具体的には、ポリプロピレン、ポリエステル、ポリカーボネート、ポリアミドイミド、ポリエステルイミド、ポリアミド、ポリイミド、ポリ塩化ビニル、ポリ塩化ビニリデンなどのポリハロゲン化ポリビニルなどの硬質合成樹脂をフィルム状にしたものを好ましく用いることができる。特に、二軸延伸成形工程を経て製造されるＯＰＰフィルム（二軸延伸成形ポリプロピレンフィルム）を好適に使用することができる。 (E) Specific examples of the synthetic resin for the back surface layer include hard synthetic resins such as polypropylene, polyester, polycarbonate, polyamideimide, polyesterimide, polyamide, polyimide, polyvinyl chloride, polyvinylidene chloride, and other polyhalogenated polyvinyls. A film-like material can be preferably used. In particular, an OPP film (biaxially stretched polypropylene film) produced through a biaxial stretch molding process can be suitably used.
耐貫通型防草シートに用いる（ｅ）裏面層としては、厚さが、好ましくは１０〜５０μｍであり、より好ましくは１２〜４０μｍであり、さらに好ましくは１５〜３０μｍの硬質合成樹脂フィルムを好適に使用できる。（ｅ）裏面層である硬質合成樹脂フィルムが前記範囲（１０〜５０μｍ）の上限以下の場合、耐貫通型防草シートの柔軟性が損なわれることなく、チガヤの芽が耐貫通型防草シートを貫通するのを防止する効果は高くなる。そのため、耐貫通型防草シートを製造したのちロール状に梱包するとシート表面にシワが発生するなどの問題が生じる可能性が小さく、また施工作業においても敷設時の作業性が損なわれる可能性が小さいため好ましい。また、（ｅ）裏面層の合成樹脂フィルムが前記範囲（１０〜５０μｍ）の下限以上の場合には、硬く鋭いチガヤの芽が耐貫通型防草シートを貫通するのを防止する効果が大きくなるため好ましい。 (E) As a back surface layer used for a penetration-proof type weedproof sheet, the thickness is preferably 10 to 50 μm, more preferably 12 to 40 μm, and still more preferably 15 to 30 μm. Can be used for (E) When the hard synthetic resin film which is a back surface layer is below the upper limit of the said range (10-50 micrometers), the flexibility of a penetration-proof weedproof sheet is not impaired, and a shoot of Tigaya is a penetration-proof weedproof sheet The effect of preventing the penetration is increased. For this reason, if a through-proof type weedproof sheet is manufactured and then packed in a roll, there is little possibility of problems such as wrinkling on the surface of the sheet, and workability during laying may be impaired in construction work. It is preferable because it is small. Moreover, (e) When the synthetic resin film of a back surface layer is more than the lower limit of the said range (10-50 micrometers), the effect which prevents that the hard and sharp chigaya bud penetrates a penetration-proof type weedproof sheet becomes large. Therefore, it is preferable.
（ｅ）裏面層の合成樹脂には、ゴムを添加することができる。合成樹脂に添加できるゴムとしては、明確な降伏点を有しない熱可塑性の低結晶性エラストマー又は明確な融点及び降伏点を有しない熱可塑性の非晶性エラストマーが好ましく、常温でゴム弾性を有するエラストマーを用いることができる。スチレン系エラストマー、オレフィン系エラストマー、ポリエステル系エラストマー及びポリアミド系エラストマー等から選択される１種以上の熱可塑性エラストマーを用いることができる。 (E) Rubber can be added to the synthetic resin of the back layer. The rubber that can be added to the synthetic resin is preferably a thermoplastic low crystalline elastomer having no clear yield point or a thermoplastic amorphous elastomer having no clear melting point and yield point, and an elastomer having rubber elasticity at room temperature. Can be used. One or more thermoplastic elastomers selected from styrene elastomers, olefin elastomers, polyester elastomers, polyamide elastomers, and the like can be used.
スチレン系エラストマーとしては、スチレン−ブタジエン−スチレン共重合体（ＳＢＳなど）、水添スチレン−ブタジエン−スチレン共重合体（ＳＥＢＳなど）、水添スチレン−ブタジエン共重合体（ＨＳＢＲなど）、水添スチレン−ブタジエン−オレフィン結晶ブロック共重合体（ＳＥＢＣなど）等などのブタジエン−スチレン共重合体（ランダム共重合体、ブロック共重合体、グラフト共重合体等の全てを含む）及びその水添物、水添スチレン−イソプレン共重合体（ＳＥＰなど）、水添スチレン−ビニルイソプレン共重合体（Ｖ−ＳＥＰＳなど）、スチレン−イソプレン−スチレン共重合体（ＳＩＳなど）、水添スチレン−イソプレン−スチレン共重合体（ＳＥＰＳなど）などのイソプレン−スチレン共重合体（ランダム共重合体、ブロック共重合体、グラフト共重合体等の全てを含む）及びその水添物などから選択される１種以上を用いることができる。 Examples of styrene elastomers include styrene-butadiene-styrene copolymers (SBS, etc.), hydrogenated styrene-butadiene-styrene copolymers (SEBS, etc.), hydrogenated styrene-butadiene copolymers (HSBR, etc.), hydrogenated styrene. -Butadiene-styrene copolymers (including all random copolymers, block copolymers, graft copolymers, etc.) such as butadiene-olefin crystal block copolymers (SEBC, etc.) and their hydrogenated products, water Styrene-isoprene copolymer (SEP, etc.), hydrogenated styrene-vinylisoprene copolymer (V-SEPS, etc.), styrene-isoprene-styrene copolymer (SIS, etc.), hydrogenated styrene-isoprene-styrene copolymer Isoprene-styrene copolymers (random copolymers, Click copolymer, it may be used one or more selected from such as all inclusive) and its hydrogenated product of a graft copolymer.
ポリオレフィン系エラストマーとしては、非晶性ポリプロピレンなどの非晶性又は低結晶性α−オレフィン（共）重合体、ポリオレフィンとオレフィン系ゴムとの混合物等を用いることができる。ポリオレフィン系エラストマーとしては、エチレン−プロピレン系エラストマー（ＥＰＲなど）、エチレン・ブテン−１系エラストマー（ＥＢＭなど）を用いることができる。ポリエステル系エラストマーとしては、ポリエステル−ポリエーテル共重合体、ポリエステル−ポリエステル共重合体等からなるエラストマーを用いることができる。ポリアミド系エラストマーとしては、ポリアミド−ポリエステル共重合体、ポリアミド−ポリエーテル共重合体等からなるエラストマー等を用いることができる。上記のエラストマーを二種以上、混合して用いてもよい。 As the polyolefin-based elastomer, amorphous or low-crystalline α-olefin (co) polymer such as amorphous polypropylene, a mixture of polyolefin and olefin-based rubber, or the like can be used. As the polyolefin elastomer, ethylene-propylene elastomer (EPR, etc.) and ethylene butene-1 elastomer (EBM, etc.) can be used. As the polyester elastomer, an elastomer made of a polyester-polyether copolymer, a polyester-polyester copolymer, or the like can be used. As the polyamide-based elastomer, an elastomer made of a polyamide-polyester copolymer, a polyamide-polyether copolymer, or the like can be used. Two or more of the above elastomers may be mixed and used.
（ｅ）裏面層の合成樹脂に添加できるゴムとしては、具体的には、ポリブタジエン、スチレン−ブタジエン共重合体、ポリイソブチレン、クロロプレンゴム及びニトリルゴムなどから選択される１種以上を用いることができる。 (E) As the rubber that can be added to the synthetic resin of the back layer, specifically, one or more selected from polybutadiene, styrene-butadiene copolymer, polyisobutylene, chloroprene rubber, nitrile rubber, and the like can be used. .
（ｅ）裏面層が、無機質粒子を含有する合成樹脂を含む場合には、無機質粒子として、炭酸カルシウム、ケイ酸マグネシウム、ケイ酸カルシウム、ケイ酸アルミニウム、無水ケイ酸、クレー、カーボンブラック、タルク、マイカ、硫酸バリウム、珪藻土及びシリカ等から選択される１種以上を用いることができる。 (E) When the back layer includes a synthetic resin containing inorganic particles, as inorganic particles, calcium carbonate, magnesium silicate, calcium silicate, aluminum silicate, anhydrous silicic acid, clay, carbon black, talc, One or more selected from mica, barium sulfate, diatomaceous earth, silica and the like can be used.
＜耐貫通型防草シートの製造方法＞
次に、耐貫通型防草シートの製造方法について説明する。
<Manufacturing method of penetration-proof grass protection sheet>
Next, the manufacturing method of a penetration-proof type weedproof sheet is demonstrated.
所定の芯部の表面に、所定の鞘部を熱融着し、芯鞘構造の繊維を作製する。この芯鞘構造の繊維を用いて織布、編み布及び／又は不織布を作製することにより、基材Ａを得る。次に、所定のスクリムを有する基材Ｂを、２つの基材Ａの間に挟む。基材Ａと、基材Ｂと、基材Ａとをこの順に積層したものを、融点２００℃以上の樹脂及び／又は２００℃で熱分解しない接着剤により接着する、若しくは熱融着することにより、シート状の（ｃ）基材層を得ることができる。 A predetermined sheath portion is heat-sealed to the surface of the predetermined core portion to produce a fiber having a core-sheath structure. The base material A is obtained by producing a woven fabric, a knitted fabric and / or a non-woven fabric using the fibers of the core-sheath structure. Next, the base material B having a predetermined scrim is sandwiched between the two base materials A. By laminating the base material A, the base material B, and the base material A in this order with a resin having a melting point of 200 ° C. or higher and / or an adhesive that is not thermally decomposed at 200 ° C., or by heat-sealing. A sheet-like (c) substrate layer can be obtained.
次に、上記のように製造した（ｃ）基材層を、１７０℃以上で２００℃未満に加熱溶融混合した所定の改質アスファルト中に浸漬して通過させ、（ｃ）基材層の両面に所定の（ｂ）層及び（ｄ）層の改質アスファルト層を設けた３層シートを作製する。この３層シートの一方の面（表面）に、所定の無機質粒子又は所定の無機質粒子を含有する合成樹脂を付着することにより（ａ）表面層を形成する。また、もう一方の面（裏面）には、所定の合成樹脂又は無機質粒子を含有する合成樹脂を含むシートを貼り合わせて（ｅ）裏面層を形成することにより、耐貫通型防草シートを得ることができる。 Next, the (c) base material layer produced as described above is immersed and passed in a predetermined modified asphalt heated and mixed at 170 ° C. or higher and lower than 200 ° C., and (c) both surfaces of the base material layer. A three-layer sheet provided with a predetermined asphalt layer (b) and (d) is prepared. (A) A surface layer is formed by adhering predetermined inorganic particles or a synthetic resin containing predetermined inorganic particles to one surface (surface) of the three-layer sheet. Further, a sheet including a predetermined synthetic resin or a synthetic resin containing inorganic particles is bonded to the other surface (back surface), and (e) a back surface layer is formed to obtain a penetration-proof grassproof sheet. be able to.
＜耐貫通型防草シートの特性＞
本発明に用いる耐貫通型防草シート及びその他の防草シートは、下記の特性を有することが好ましい。
<Characteristics of penetration-proof grass protection sheet>
The penetration-resistant weedproof sheet and other weedproof sheets used in the present invention preferably have the following characteristics.
本発明に用いる防草シートの光線透過率は、好ましくは１０％以下、より好ましくは５％以下、さらに好ましくは０％であることが好ましい。光線透過率が上記範囲内では、雑草の生育を有効に防止することができるため好ましい。 The light transmittance of the herbicidal sheet used in the present invention is preferably 10% or less, more preferably 5% or less, and still more preferably 0%. When the light transmittance is within the above range, it is preferable because weed growth can be effectively prevented.
本発明に用いる防草シートの貫通抵抗力は、好ましくは１００Ｎ以上、より好ましくは１５０Ｎ以上、さらに好ましくは２００Ｎ以上、特に好ましくは２５０Ｎ以上が好ましい。貫通抵抗力が上記範囲では、雑草の生育を有効に防止・抑制することができるため好ましい。「貫通抵抗」とは、ＡＳＴＭ・Ｄ４８３３に準拠した測定値である。 The penetration resistance of the weedproof sheet used in the present invention is preferably 100 N or more, more preferably 150 N or more, still more preferably 200 N or more, and particularly preferably 250 N or more. The penetration resistance is preferably in the above range because weed growth can be effectively prevented and suppressed. “Penetration resistance” is a measured value based on ASTM D 4833.
本発明に用いる防草シートの引張強度は、好ましくは５０Ｎ／ｃｍ以上、より好ましくは８０Ｎ／ｃｍ以上、さらに好ましくは１２０Ｎ／ｃｍ以上、特に好ましくは１３５Ｎ／ｃｍ以上であることが好ましい。「引張強度」とは、ＪＩＳ・Ａ６０１３に準拠した測定値である。防草シートが上記範囲の引張強度を有することにより、防草シートの製造過程では良好な連続生産性が得られ、防草シートの施工過程では優れた取扱性が得られ、施工後の供用においては優れた耐久性を得ることができる。 The tensile strength of the herbicidal sheet used in the present invention is preferably 50 N / cm or more, more preferably 80 N / cm or more, still more preferably 120 N / cm or more, and particularly preferably 135 N / cm or more. “Tensile strength” is a measured value based on JIS A6013. When the weedproof sheet has a tensile strength in the above range, good continuous productivity is obtained in the process of manufacturing the weedproof sheet, and excellent handling is obtained in the construction process of the weedproof sheet. Can obtain excellent durability.
本発明に用いる防草シートの引張伸び率は、好ましくは１５％以上、より好ましくは３０％以上、さらに好ましくは４０％以上が好ましい。「引張伸び率」とは、ＪＩＳ・Ａ６０１３に準拠した測定値である。上記範囲では、適度の柔軟性により下地の不陸になじむため、施工時の取扱性に優れ、耐久性に優れる。また、防草シートを製造する過程での連続生産性に優れるために好ましい。 The tensile elongation of the herbicidal sheet used in the present invention is preferably 15% or more, more preferably 30% or more, and still more preferably 40% or more. “Tensile elongation” is a measured value based on JIS A6013. In the above-mentioned range, because it is suitable for unevenness of the ground due to moderate flexibility, it is excellent in handling at the time of construction and excellent in durability. Moreover, since it is excellent in continuous productivity in the process of manufacturing a herbicidal sheet, it is preferable.
本発明に用いる防草シートの引裂強度は、好ましくは５０Ｎ以上、より好ましくは７０Ｎ以上、さらに好ましくは９０Ｎ／ｃｍ以上、特に好ましくは１１０Ｎ／ｃｍ以上であることが好ましい。「引裂強度」とは、ＪＩＳ・Ａ６０１３に準拠した測定値である。防草シートが上記範囲の引裂強度を有することにより、防草シートの製造過程では良好な連続生産性が得られ、防草シートの施工過程では優れた取扱性が得られ、施工後の供用においては優れた耐久性を得ることができる。また、防草シートの引裂強度が前記範囲であれば、防草シートの端部を、固定ピンを用いて固定した場合にも、固定箇所（応力が集中する箇所）の耐久性を充分に確保することができる。 The tear strength of the herbicidal sheet used in the present invention is preferably 50 N or more, more preferably 70 N or more, still more preferably 90 N / cm or more, and particularly preferably 110 N / cm or more. “Tear strength” is a measured value based on JIS A6013. When the weedproof sheet has a tear strength in the above range, good continuous productivity is obtained in the process of manufacturing the weedproof sheet, and excellent handling is obtained in the construction process of the weedproof sheet. Can obtain excellent durability. In addition, if the tear strength of the weedproof sheet is within the above range, even when the end of the weedproof sheet is fixed using a fixing pin, the durability of the fixed location (location where stress is concentrated) is sufficiently secured. can do.
本発明に用いる防草シートは、（ａ）表面層から（ｅ）裏面層までの５層全体の厚みが、好ましくは１ｍｍ〜１０ｍｍの範囲、より好ましくは１．５ｍｍ〜８ｍｍの範囲、さらに好ましくは２ｍｍ〜６ｍｍの範囲、特に好ましくは３ｍｍ〜５ｍｍの範囲であることが、施工時の取り扱い易さや、隣り合う防草シートの熱融着部分の品質を充分に安定して確保できることから好ましい。 In the weedproof sheet used in the present invention, the total thickness of the five layers from the (a) surface layer to the (e) back layer is preferably in the range of 1 mm to 10 mm, more preferably in the range of 1.5 mm to 8 mm, and still more preferably. Is preferably in the range of 2 mm to 6 mm, particularly preferably in the range of 3 mm to 5 mm, since the handling at the time of construction and the quality of the heat-sealed portion of the adjacent herbicidal sheet can be secured sufficiently stably.
本発明に用いる防草シートは、引張強度の縦方向と横方向との比が、好ましくは０．６０〜１．６０の範囲、より好ましくは０．７２〜１．４０の範囲、さらに好ましくは０．７４〜１．３５の範囲、特に好ましくは０．７５〜１．３０の範囲であることが、引張強度や引裂強度などの物性がシートの方向性に依存せず、安定した耐久性が得られることから好ましい。 In the weedproof sheet used in the present invention, the ratio between the longitudinal direction and the transverse direction of the tensile strength is preferably in the range of 0.60 to 1.60, more preferably in the range of 0.72 to 1.40, and still more preferably. The range of 0.74 to 1.35, particularly preferably the range of 0.75 to 1.30, the physical properties such as tensile strength and tear strength do not depend on the orientation of the sheet, and stable durability is achieved. Since it is obtained, it is preferable.
本発明に用いる防草シートは、引裂強度の縦方向と横方向との比が、好ましくは０．５０〜２．００の範囲、より好ましくは０．８０〜１．２０の範囲、さらに好ましくは０．８３〜１．１８の範囲、特に好ましくは０．８６〜１．１６の範囲であることが、引張強度や引裂強度などの物性がシートの方向性に依存せず、安定した耐久性が得られることから好ましい。 In the weedproof sheet used in the present invention, the ratio between the longitudinal direction and the transverse direction of the tear strength is preferably in the range of 0.50 to 2.00, more preferably in the range of 0.80 to 1.20, and still more preferably. The range of 0.83 to 1.18, particularly preferably the range of 0.86 to 1.16, the physical properties such as tensile strength and tear strength do not depend on the orientation of the sheet, and stable durability is achieved. Since it is obtained, it is preferable.
機械的強度の一例として、（ｅ）裏面層として厚さ２０μｍの二軸延伸成形ポリプロピレンフィルム及び目付量１５５ｇ／ｍ２の基材層を用い、全体の厚さを３ｍｍとした耐貫通型防草シートの場合には、引張強度１１０〜１９０Ｎ／ｃｍ程度、引張伸び率５０〜７０％程度、引裂強度８５〜１４０Ｎ／ｃｍ程度の値を得ることできる。 As an example of the mechanical strength, (e) a through-proof type herbicide using a biaxially stretched polypropylene film having a thickness of 20 μm and a base material layer having a basis weight of 155 g / m 2 as a back layer and having a total thickness of 3 mm In the case of a sheet, values of a tensile strength of about 110 to 190 N / cm, a tensile elongation of about 50 to 70%, and a tear strength of about 85 to 140 N / cm can be obtained.
以上述べたように、耐貫通型防草シートでは、織布、編み布及び不織布から選ばれる少なくとも一つである基材Ａと、スクリムを有する基材Ｂとを含む基材層を用い、さらに裏面層に特定の樹脂フィルムを選択して用いるため、引裂強度及び引張強度に優れ、寸法安定性が優れる耐貫通型防草シートを得ることができる。また、耐貫通型防草シートを用いれば、道路、線路、河川、公園及び造林園など並びにこれらの周辺などの地面、表面、特に法面での草の成育を防止する遮光性と、非透水性とを有するとともに、集中豪雨などによる法面の帯水を防止でき、特に、硬く鋭い雑草の芽の防草シートに対する貫通防止性に優れる防草構造体を得ることができる。
＜参考実施例＞
As described above, in the penetration-proof weedproof sheet, a base material layer including at least one base material A selected from a woven fabric, a knitted fabric and a non-woven fabric and a base material B having a scrim is used, Since a specific resin film is selected and used for the back surface layer, a penetration-resistant weedproof sheet having excellent tear strength and tensile strength and excellent dimensional stability can be obtained. In addition, the use of a penetration-proof grass protection sheet prevents the growth of grass on roads, railways, rivers, parks, afforestation, etc. In addition, it is possible to obtain a weed-proof structure that can prevent water from being sloped by concentrated heavy rain and the like, and is particularly excellent in preventing penetration of hard and sharp weed buds to a herbicidal sheet.
<Reference Example>
以下に参考実施例として実験例を挙げて耐貫通型防草シートを説明するが、本発明に用いる耐貫通型防草シートはこれにより何ら限定されるものではない。 The penetration-resistant weedproof sheet will be described below with reference to experimental examples as reference examples, but the penetration-resistant weedproof sheet used in the present invention is not limited thereto.
＜評価方法＞
１．引張強度、引張伸び率、引裂強度：ＪＩＳ・Ａ６０１３に準拠して、万能材料試験機［オリエンテック（株）製ＵＴＭ−１０Ｔ］を用い、引張速度１００ｍｍ／分、サンプル幅５０ｍｍ、チャック間１００ｍｍ、試験温度２２℃の条件下で一軸引張強度を測定した。
<Evaluation method>
1. Tensile strength, tensile elongation, tear strength: In accordance with JIS A6013, using universal material testing machine [UTM-10T manufactured by Orientec Co., Ltd.], tensile speed 100 mm / min, sample width 50 mm, chuck interval 100 mm, Uniaxial tensile strength was measured under the test temperature of 22 ° C.
２．貫通抵抗：ＡＳＴＭ・Ｄ４８３３に準拠して行った。具体的には、防草シートの貫通抵抗力は、図１９（Ａ）及び図１９（Ｂ）に示されているように、下端に先端部７を有する測定用治具６を用い、図１９（Ｃ）のように展張、固定された試験用防草シート８を測定用治具６が貫通する際の抵抗力を、貫通速度３００ｍｍ／分、試験温度２２℃の条件下で測定した。 2. Penetration resistance: performed in accordance with ASTM D 4833. Specifically, as shown in FIGS. 19A and 19B, the penetration resistance of the weedproof sheet is measured using a measuring jig 6 having a tip 7 at the lower end, as shown in FIG. The resistance force when the measuring jig 6 penetrates the test herbicidal sheet 8 that was stretched and fixed as in (C) was measured under the conditions of a penetration speed of 300 mm / min and a test temperature of 22 ° C.
＜実験１〜３＞
雑草を刈り取った地面の表面に、下記の合成樹脂フィルムを敷設して２ヵ月後に防草効果を確認した。
１）合成樹脂フィルム
・合成樹脂フィルムａ ： ＰＥフィルム（ポリエチレンフィルム）、厚さ＝３０μｍ、１ｍ×１ｍ。
・合成樹脂フィルムｂ ： ＯＰＰフィルム（二軸延伸成形ポリプロピレンフィルム）、厚さ＝２０μｍ、１ｍ×１ｍ。
・合成樹脂フィルムｃ ： ＯＰＰフィルム（二軸延伸成形ポリプロピレンフィルム）、厚さ＝６０μｍ、１ｍ×１ｍ。
<Experiments 1-3>
The following synthetic resin film was laid on the surface of the ground from which weeds were cut, and the weed control effect was confirmed after 2 months.
1) Synthetic resin film • Synthetic resin film a: PE film (polyethylene film), thickness = 30 μm, 1 m × 1 m.
Synthetic resin film b: OPP film (biaxially stretched polypropylene film), thickness = 20 μm, 1 m × 1 m.
Synthetic resin film c: OPP film (biaxially stretched polypropylene film), thickness = 60 μm, 1 m × 1 m.
表１及び図１７に、実験１〜３のチガヤの芽の貫通状態を観察した結果を示す。 In Table 1 and FIG. 17, the result of having observed the penetration state of the bud of Chigaya of Experiments 1-3 is shown.
厚さ＝３０μｍのＰＥフィルム（ポリエチレンフィルム）を敷設した実験３の場合、チガヤの芽がフィルムを貫通して２０ｍｍ以上に成長している箇所が１５箇所観察された。一方、厚さ＝２０μｍのＯＰＰフィルム（二軸延伸成形ポリプロピレンフィルム）を敷設した実験１の場合、チガヤの芽がフィルムを貫通して２０ｍｍ以上に成長している箇所は１箇所のみであり、厚さ＝６０μｍのＯＰＰフィルム（二軸延伸成形ポリプロピレンフィルム）を敷設した実験２の場合、チガヤの芽は全くフィルムを貫通していなかった。 In the case of Experiment 3 in which a PE film (polyethylene film) having a thickness of 30 μm was laid, fifteen spots where Tigaya sprouts penetrated the film and grew to 20 mm or more were observed. On the other hand, in the case of Experiment 1 in which an OPP film having a thickness of 20 μm (biaxially stretched polypropylene film) was laid, there was only one place where the buds of chigaya had grown through the film to 20 mm or more. In the case of Experiment 2 in which an OPP film (biaxially stretched polypropylene film) having a thickness of 60 μm was laid, no chigaya buds penetrated the film.
上記の結果から、ＰＥフィルム（ポリエチレンフィルム）を用いた場合には防草効果を奏するといえる。また、ＯＰＰフィルム（二軸延伸成形ポリプロピレンフィルム）を用いた場合には、より優れた防草効果を奏することができるといえる。 From the above results, it can be said that when a PE film (polyethylene film) is used, a herbicidal effect is exhibited. Moreover, when an OPP film (biaxially stretched polypropylene film) is used, it can be said that a more excellent herbicidal effect can be achieved.
＜実験例１〜７＞
以下の手順にしたがって、表２に示す条件で防草シートを製造した。なお、実験例３〜７は、耐貫通型防草シートに該当する。
<Experimental Examples 1-7>
According to the following procedures, a herbicidal sheet was produced under the conditions shown in Table 2. In addition, Experimental Examples 3-7 correspond to a penetration-proof type weedproof sheet.
複合不織布を、１９０℃に加熱溶融混合した改質アスファルト中を通過させ、複合不織布の両面に改質アスファルトの層を設けた３層シートを作製した。 The composite nonwoven fabric was passed through modified asphalt that was heated and melted and mixed at 190 ° C. to prepare a three-layer sheet in which layers of modified asphalt were provided on both sides of the composite nonwoven fabric.
複合不織布（基材層）として、以下の３種類のものを用いた。
２）複合不織布
・複合不織布Ａ ： ＡＫＺＯ・ＮＯＢＥＬ社製、製品名：ｃｏｌｂａｃｋ；品種：ＳＮＳ１５５（不織布−スクリム−不織布の三層構造）、上層及び下層の不織布：芯鞘構造、鞘部：ナイロン、芯部：ポリエステル、中間層：ガラス繊維束のスクリム（シートの長さ方向と、長さ方向の垂直方向に２方向補強）、目付量＝１５５ｇ／ｍ２、１ｍ×６ｍ。
・複合不織布Ｂ ： ＡＫＺＯ・ＮＯＢＥＬ社製、製品名：ｃｏｌｂａｃｋ；品種：ＳＮＳ１２５（不織布−スクリム−不織布の三層構造）、上層及び下層の不織布：芯鞘構造、鞘部：ナイロン、芯部：ポリエステル、中間層：ガラス繊維束のスクリム（シートの長さ方向と、長さ方向の垂直方向に２方向補強）、目付量＝１２５ｇ／ｍ２、１ｍ×６ｍ。
・複合不織布Ｃ ： フロイデンベルグ社製、製品名：ＴＥＲＢＯＮＤ・Ｒ１５０（不織布−ガラス繊維束の２層構造）、上層の不織布：芯鞘構造、鞘部：ナイロン、芯部：ポリエステル、下層：ガラス繊維束（シートの長さ方向に１方向補強）、目付量＝１５０ｇ／ｍ２、１ｍ×６ｍ。
The following three types of composite nonwoven fabric (base material layer) were used.
2) Composite nonwoven fabric-Composite nonwoven fabric A: manufactured by AKZO NOBEL, product name: colback; varieties: SNS155 (non-woven fabric-scrim-nonwoven fabric three-layer structure), upper layer and lower layer nonwoven fabric: core-sheath structure, sheath: nylon, Core: polyester, intermediate layer: scrim of glass fiber bundle (reinforcement in two directions in the length direction of the sheet and in the direction perpendicular to the length direction), basis weight = 155 g / m 2 , 1 m × 6 m.
Composite nonwoven fabric B: manufactured by AKZO NOBEL, product name: colback; product type: SNS125 (non-woven fabric-scrim-nonwoven fabric three-layer structure), upper layer and lower layer nonwoven fabric: core sheath structure, sheath portion: nylon, core portion: polyester Intermediate layer: scrim of glass fiber bundle (two-way reinforcement in the length direction of the sheet and in the direction perpendicular to the length direction), basis weight = 125 g / m 2 , 1 m × 6 m.
Composite nonwoven fabric C: manufactured by Freudenberg, product name: TERBOND • R150 (nonwoven fabric-glass fiber bundle two-layer structure), upper layer nonwoven fabric: core-sheath structure, sheath: nylon, core: polyester, lower layer: glass fiber Bundle (reinforced in one direction in the length direction of the sheet), basis weight = 150 g / m 2 , 1 m × 6 m.
ここで、製品名：ｃｏｌｂａｃｋ−品種：ＳＮＳ１５５、及び、製品名：ｃｏｌｂａｃｋ−品種：ＳＮＳ１２５は、芯鞘構造（鞘部：ナイロン、芯部：ポリエステル；ＰＥＴ）の繊維からなる不織布とガラス繊維のスクリムとを、不織布−スクリム−不織布の順に積層して、不織布の鞘部のナイロンの熱融着により一体に成形したものである。 Here, the product name: colback-variety: SNS155 and the product name: colback-variety: SNS125 are non-woven fabric and glass fiber scrim made of fibers of a core-sheath structure (sheath part: nylon, core part: polyester; PET). Are laminated in the order of non-woven fabric-scrim-non-woven fabric, and are integrally formed by heat-sealing nylon of the sheath portion of the non-woven fabric.
改質アスファルトは、ＳＢＳ改質タイプの針入度３０ｄｍｍ、又は、ＡＰＰ改質タイプの針入度２９ｄｍｍのものを用いた。 As the modified asphalt, an SBS modified type penetration of 30 dmm or an APP modified type of penetration of 29 dmm was used.
３層シートの改質アスファルト層の片面（表面側）には、扁平状のスレートチップを５００ｇ／ｍ２〜１０００ｇ／ｍ２の範囲で付着させた。 The three-layer sheet of reforming one side of the asphalt layer (surface side), and the flat slate chips deposited in the range of 500g / m 2 ~1000g / m 2 .
他方の面（裏面側）には、下記の合成樹脂フィルムを貼り合わせ、厚さ３．２ｍｍの５層シートを作製し、ボール紙の芯材にロール状に巻き付けて防草シートを製造した。
３）合成樹脂フィルム
・合成樹脂フィルムｄ ： ＨＤＰＥフィルム（高密度ポリエチレン）、厚さ＝２０μｍ。
・合成樹脂フィルムｅ ： ＯＰＰフィルム（二軸延伸成形ポリプロピレン）、厚さ＝２０μｍ。
The following synthetic resin film was bonded to the other surface (rear surface side) to produce a 5-layer sheet having a thickness of 3.2 mm, and wound around a core of cardboard in a roll shape to produce a herbicidal sheet.
3) Synthetic resin film Synthetic resin film d: HDPE film (high density polyethylene), thickness = 20 μm.
Synthetic resin film e: OPP film (biaxially stretched molded polypropylene), thickness = 20 μm.
防草シートは、連続して生産することができた。また、いずれの防草シートの光線透過率も０％で、光を透過しなかった。 The herbicidal sheet could be produced continuously. Moreover, the light transmittance of any of the herbicidal sheets was 0% and did not transmit light.
得られた防草シートについて、引張強度など物性評価を行った結果を表３に示す。雑草を刈り取った地面の表面に、得られた防草シートを敷設して２ヵ月後に防草効果を評価した。また、図１８に、チガヤの芽の貫通状態を観察した結果を示す。なお、表３中の「施工性」とは、シートの重量、柔軟性やシワの発生状況等、防草シートの施工作業おける取扱性及び容易性を総合的に判断したものである。 Table 3 shows the results of physical properties such as tensile strength of the obtained herbicidal sheet. The obtained weedproof sheet was laid on the surface of the ground from which weeds were cut, and the weedproof effect was evaluated two months later. Moreover, the result of having observed the penetration state of the bud of Chigaya is shown in FIG. In addition, “workability” in Table 3 is a comprehensive judgment of the ease of handling and ease of construction work of the herbicidal sheet, such as the weight of the sheet, flexibility, and the state of occurrence of wrinkles.
これらの結果から明らかなように、実験例１〜７のいずれの防草シートにおいても良好な防草効果が得られたが、特に、裏面層として、硬質合成樹脂の一種である二軸延伸成形ポリプロピレンを用いた場合には、高密度ポリエチレンを用いた場合と比較して、チガヤの芽の貫通数を低減し、より高い防草効果を得ることができた。 As is clear from these results, a good herbicidal effect was obtained in any of the herbicidal sheets of Experimental Examples 1 to 7, but in particular, as the back layer, biaxially stretched molding which is a kind of hard synthetic resin When polypropylene was used, the number of penetrating shoots of chigaya was reduced, and a higher herbicidal effect could be obtained as compared with the case of using high-density polyethylene.
また、二軸延伸成形ポリプロピレンを用いるとともに、基材層として目付量が１５５ｇ／ｍ２の複合不織布を使用した場合には、チガヤの芽が全く貫通しない（実験例６）、又は、チガヤの芽が貫通したとしてもその貫通数は極僅かであり（実験例４、実験例５及び実験例７）、貫通した目の長さも２０ｍｍ未満であった。貫通したチガヤの芽が、裏面の合成樹脂フィルムを貫通したのち、２０ｍｍ以上にさらに大きく成長できなかったのは、目付量の大きい複合不織布の繊維構造と、複合不織布に含浸した改質アスファルト層とが、芽の成長にとって大きな障害となったことによるものと推考される。 In addition, when biaxially stretched polypropylene is used and a composite nonwoven fabric having a basis weight of 155 g / m 2 is used as the base material layer, no chigaya buds penetrate (Experimental Example 6) or However, the number of penetrations was very small (Experimental Example 4, Experimental Example 5 and Experimental Example 7), and the length of the penetrated eye was less than 20 mm. After the penetrated chigaya bud penetrated the synthetic resin film on the back side, it could not grow larger than 20 mm. The fiber structure of the composite nonwoven fabric with a large basis weight and the modified asphalt layer impregnated in the composite nonwoven fabric This is thought to be due to a major obstacle to the growth of buds.
１ ： 表面層（無機質粒子）
２ ： 改質アスファルト層
３ ： 基材層
４ ： 改質アスファルト層
５ ： 裏面層
６ ： 測定用治具
７ ： 測定用治具の先端部
８ ： 防草シート
１０ ： 防草シート本体
１１ ： 本体開口部
１２ ： 第一端部
１３ ： 第二端部
１４ ： 第一の釘状器具
１５ ： 第二の釘状器具
１６ ： 鉄筋
１７ ： 防草シート本体重ね合わせ接着部（粘着材接着処理及び／又はテープ接着処理）
１８ ： 横方向端部（粘着材接着処理及び／又はテープ接着処理）
１９ ： 横方向端部（ピン固定処理）
２１ ： 舗装面
２２ ： 舗装面端部
２３ ： 支柱
２４ ： ガードレール
２５ ： ガードレール取付具
２６ ： 支柱中心位置
２７ ： メッシュ状押さえ具 ３０ ： 法面
３１ ： 法面掘削部
３２ ： 法面埋設部
４０ ： パッチシート
４２ ： パッチ開口部
４３ ： 本体切断部
４４ ： パッチ切断部
４５ ： 接着層（粘着材接着層及び／又はテープ接着層）
Ｄｈ ： 支柱貫通前の本体開口部の形状の最長寸法
Ｄｐ ： 支柱の断面の形状の最長寸法
Ｌ１ ： 防草シート本体の長さ
Ｌ２ ： 防草シート本体接着部の長さ
θ ： 本体切断部とパッチ切断部との支柱中心位置を中心とした角度
1: Surface layer (inorganic particles)
2: Modified asphalt layer 3: Base material layer 4: Modified asphalt layer 5: Back surface layer 6: Measuring jig 7: Tip portion of measuring jig 8: Weedproof sheet 10: Weedproof sheet main body 11: Main body Opening portion 12: First end portion 13: Second end portion 14: First nail-like device 15: Second nail-like device 16: Reinforcing bar 17: Weed prevention sheet main body overlapping adhesion portion (adhesive material adhesion treatment and / or (Or tape adhesive treatment)
18: End in the horizontal direction (adhesive material adhesion treatment and / or tape adhesion treatment)
19: Lateral end (pin fixing process)
21: Pavement surface 22: End portion of pavement surface 23: Support column 24: Guard rail 25: Guard rail mounting tool 26: Support column center position 27: Mesh presser 30: Slope 31: Slope digging unit 32: Slope embedded unit 40: Patch sheet 42: Patch opening 43: Main body cutting part 44: Patch cutting part 45: Adhesive layer (adhesive adhesive layer and / or tape adhesive layer)
Dh: The longest dimension of the shape of the main body opening before penetrating through the pillar Dp: The longest dimension of the shape of the cross section of the pillar L1: The length of the weedproof sheet main body L2: The length of the weedproof sheet main body bonding portion θ: Angle around the center of the column with the patch cutting part
Claims (14)
防草シート本体の第一端部を、舗装面端部に重なるように配置する工程（Ａ）と、
防草シート本体の第一端部を、粘着材接着及び／又はテープ接着によって舗装面端部に固定する工程（Ｂ）と、
防草シート本体の第一端部を、さらに第一の釘状器具によって舗装面端部に固定する工程（Ｃ）と、
防草シート本体の第一端部とは反対側の第二端部を、第二の釘状器具によって地面に固定する工程（Ｄ）とを含み、
工程（Ａ）の前に、
防草シート本体の、支柱位置に対応する防草シート本体の位置に本体開口部及び本体開口部の１点と防草シート本体の端部の１点との間に本体切断部を形成する工程と、
パッチシートに、パッチ開口部及びパッチ開口部の１点とパッチシートの端部の１点との間にパッチ切断部を形成する工程と、
本体切断部に支柱を通過させることによって、支柱を防草シート本体の本体開口部に貫通させる工程とを含み、
工程（Ａ）の後に、
パッチ切断部に支柱を通過させることによって、支柱をパッチシートのパッチ開口部に貫通させ、本体切断部を全て覆いかつ本体切断部とパッチ切断部とが重ならないように、防草シート本体上にパッチシートを敷設する工程と、
パッチシートを、粘着材接着及び／又はテープ接着によって防草シート本体に固定する工程とを含む、防草構造体の施工方法。 Adjacent to the pavement, the weed areas with struts fitment is attached to a construction method for installing a weed structure containing weed seat body,
The step (A) of arranging the first end of the weedproof sheet main body so as to overlap the paved surface end,
A step (B) of fixing the first end of the weedproof sheet main body to the pavement surface end by adhesive bonding and / or tape bonding;
A step (C) of fixing the first end of the weedproof sheet main body to the end of the pavement surface with a first nail-like tool;
A second end opposite the first end portion of the weed seat body, seen including a step (D) to be secured to the ground by the second nail instrument,
Before step (A)
A step of forming a main body cutting portion at one position of the main body opening and one of the main body opening and one end of the weedproof sheet main body at the position of the main body of the weedproof sheet corresponding to the position of the support. When,
Forming a patch cutting portion between the patch opening and one point of the patch opening and one point of the end of the patch sheet on the patch sheet;
Passing the column through the body opening of the weedproof sheet body by passing the column through the body cutting part,
After step (A)
By passing the strut through the patch cutting part, the strut is penetrated through the patch opening of the patch sheet, covering all the main body cutting part and so that the main body cutting part and the patch cutting part do not overlap each other on the grass prevention sheet main body Laying a patch sheet;
Fixing the patch sheet to the weedproof sheet main body by adhesive bonding and / or tape bonding .
施工方法が、パッチシートを、粘着材接着によって防草シート本体に固定する工程を含み、粘着材が、改質アスファルトを含む目止め材である、請求項１〜１１のいずれか１項記載の施工方法。 The construction method according to any one of claims 1 to 11, wherein the construction method includes a step of fixing the patch sheet to the herbicidal sheet main body by adhesive material adhesion, and the adhesive material is a sealing material containing modified asphalt. Construction method.