JP5230987B2 - 表皮材一体発泡成形品用の軟質ポリウレタン発泡体 - Google Patents
表皮材一体発泡成形品用の軟質ポリウレタン発泡体 Download PDFInfo
- Publication number
- JP5230987B2 JP5230987B2 JP2007256095A JP2007256095A JP5230987B2 JP 5230987 B2 JP5230987 B2 JP 5230987B2 JP 2007256095 A JP2007256095 A JP 2007256095A JP 2007256095 A JP2007256095 A JP 2007256095A JP 5230987 B2 JP5230987 B2 JP 5230987B2
- Authority
- JP
- Japan
- Prior art keywords
- foam
- polyol
- polyurethane foam
- skin material
- flexible polyurethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
請求項3の発明は、請求項1又は請求項2に係る発明において、前記発泡体原料には、ジオール又はトリオールよりなる架橋剤を含有することを特徴とする。
請求項1に係る表皮材一体発泡成形品用の軟質ポリウレタン発泡体では、ポリオールとしてポリエーテルポリオールとポリイソシアネートとの反応により得られる水酸基含有ウレタンプレポリマーがポリオール中に30質量%以上含まれるものを用いることから、発泡体原料の粘度を高くすることができる。このため、得られる発泡体中のセルの合体が抑えられ、微細なセルが形成される。その結果、軟質ポリウレタン発泡体のセル数が50〜80個/25mm及び通気量が0.3〜10cc/cm2/secに設定される。
自動車部品としてのヘッドレストやアームレストは、表皮材一体発泡成形品で構成されている。すなわち、表皮材は軟質ポリウレタン発泡体の外面に織物、合成皮革等で形成された表面材がラミネートされて構成されている。さらに、この表皮材の内面にポリウレタンの発泡原液がモールド一体発泡成形されることにより、表皮材一体発泡成形品が形成される。軟質ポリウレタン発泡体(以下、単にポリウレタン発泡体又は発泡体ともいう)は、係る表皮材一体発泡成形品用として使用されるものである。
・ 本実施形態の軟質ポリウレタン発泡体では、前記水酸基含有ウレタンプレポリマーがポリオール中に30質量%以上含まれるものを用いることから、発泡体原料の粘度を高くすることができ、発泡体中のセルの合体が抑えられ、微細なセルを形成することができる。このため、発泡体のセル数が50〜80個/25mm及び通気量が0.3〜10cc/cm2/secに設定される。
(実施例1〜7及び比較例1〜5)
ポリオール、ポリイソシアネート、発泡剤、整泡剤、触媒及び難燃剤を含有する軟質ポリウレタン発泡体の原料を、表1及び表2に示す組成にて調製した。表1及び表2における発泡体原料の数値は質量部を表す。そして、発泡体原料を常温で混合し、常法に従って反応及び発泡(スラブ発泡)させることにより軟質ポリウレタン発泡体を製造した。
水酸基含有プレポリマーA:ポリエーテルポリオール(三洋化成工業(株)製、GP3050)96質量部とポリイソシアネート(日本ポリウレタン工業(株)製、コロネートT−80)4質量部とを反応させて得られたもので、粘度は27000mPa・s)
水酸基含有プレポリマーB:ポリエーテルポリオール(三洋化成工業(株)製、GP3050)97質量部とポリイソシアネート(日本ポリウレタン工業(株)製、コロネートT−80)3質量部とを反応させて得られたもので、粘度は7000mPa・s)
水酸基含有プレポリマーC:ポリエーテルポリオール(三洋化成工業(株)製、GP3050)95.5質量部とポリイソシアネート(日本ポリウレタン工業(株)製、コロネートT−80)4.5質量部とを反応させて得られたもので、粘度は40000mPa・s)
ポリオールA:ポリエーテルポリオール、水酸基価56.1mgKOH/g、三洋化成工業(株)製、GP3050
ポリオールB:ポリエステル変性ポリエーテルポリオール、水酸基価56.1、三井化学(株)製、L−50
ポリオールC:コポリマーポリオール(ポリエーテルポリオールにスチレン(約40質量%)等がグラフト共重合されたポリオール)、旭硝子(株)製、EX941
ポリオールD:ポリエステルポリオール、日本ポリウレタン工業(株)製、N2200
整泡剤A:ポリジメチルシロキサン(繰返し単位数50〜100)−ポリオキシアルキレン(繰返し単位数5〜20)グラフト共重合体、ポリオキシアルキレン鎖の末端は水素、エーテル系ウレタン用高活性タイプ、デグサジャパン(株)製、B8110
整泡剤B:ポリジメチルシロキサン(繰返し単位数5〜30)−ポリオキシアルキレン(繰返し単位数2〜15)グラフト共重合体、ポリオキシアルキレン鎖の末端は水素、エステル系ウレタン用中活性タイプ、デグサジャパン(株)製、B8300
整泡剤C:ポリジメチルシロキサン(繰返し単位数50〜100)−ポリオキシアルキレン(繰返し単位数5〜20)グラフト共重合体、ポリオキシアルキレン鎖の末端は水酸基、エーテル系ウレタン用反応型タイプ、東レ・ダウコーニング(株)製、SZ−1919
整泡剤D:ポリジメチルシロキサン(繰返し単位数50〜100)−ポリオキシアルキレン(繰返し単位数5〜20)グラフト共重合体、ポリオキシアルキレン鎖の末端は水素、エーテル系ウレタン用高活性タイプ、東レ・ダウコーニング(株)製、SH−192
アミン触媒:トリエチレンジアミン、エアープロダクツジャパン(株)製、33LV
金属触媒:オクチル酸スズ、城北化学工業(株)製、MRH−110
ポリイソシアネート(T−80):2,4-トルエンジイソシアネート80質量%と2,6-トルエンジイソシアネート20質量%との混合物、日本ポリウレタン工業(株)製、コロネートT−80
ポリイソシアネート(T−65):2,4-トルエンジイソシアネート65質量%と2,6-トルエンジイソシアネート35質量%との混合物、日本ポリウレタン工業(株)製、コロネートT−65
架橋剤(ジオール):ポリエチレングリコール、三洋化成工業(株)製、PEG−200
架橋剤(トリオール):ポリエチレングリコール、エアープロダクツジャパン(株)製、Dabco2035
難燃剤A:含塩素リン酸エステル、トリス(クロロプロピル)ホスフェートの縮合タイプ、リン含有量11質量%、塩素含有量23質量%
そして、得られた軟質ポリウレタン発泡体について、見掛け密度、平均セル数、通気量、スチレンモノマー量、燃焼試験、剥離強度、ウレタン発泡原液透過量及び湿熱老化性を下記に示す方法によって測定した。それらの結果を表1及び表2に示した。
平均セル数(個/25mm):JIS K 6400−1:2004の付属書1(参考)に準拠して測定した値である。
スチレンモノマー量(ppm):軟質ポリウレタン発泡体中に含まれるスチレンモノマー量を測定した。
・ 前記水酸基含有ウレタンプレポリマーとして、種類の異なるもの、水酸基価の異なるもの、分子量の異なるもの等を複数使用して発泡体原料の粘度などを調整するように構成することもできる。
さらに、前記実施形態より把握できる技術的思想について以下に記載する。
Claims (4)
- ポリオール、ポリイソシアネート、発泡剤、整泡剤、触媒及び難燃剤を含有する発泡体原料を反応及び発泡させてなる軟質ポリウレタン発泡体の外面に表面材がラミネートされて表皮材が形成され、その内面にポリウレタンの発泡原液がモールド一体発泡成形されて構成される表皮材一体発泡成形品用の軟質ポリウレタン発泡体において、
前記ポリオールは、ポリエーテルポリオールとポリイソシアネートとの反応により得られる水酸基含有ウレタンプレポリマーがポリオール中に30質量%以上含まれるものであると共に、前記整泡剤は、ポリジメチルシロキサンとポリオキシアルキレンとのグラフト共重合体であって、ポリオキシアルキレン鎖の末端が水酸基のものと、水素のものとの混合物であり、軟質ポリウレタン発泡体のセル数が50〜80個/25mm及び通気量が0.3〜10cc/cm2/secであることを特徴とする表皮材一体発泡成形品用の軟質ポリウレタン発泡体。 - 前記ポリオールは、ポリエステル変性ポリエーテルポリオールを含有するものであることを特徴とする請求項1に記載の表皮材一体発泡成形品用の軟質ポリウレタン発泡体。
- 前記発泡体原料には、ジオール又はトリオールよりなる架橋剤を含有することを特徴とする請求項1又は請求項2に記載の表皮材一体発泡成形品用の軟質ポリウレタン発泡体。
- 前記ラミネートは、フレームラミネート法によるものであることを特徴とする請求項1から請求項3のいずれか1項に記載の表皮材一体発泡成形品用の軟質ポリウレタン発泡体。