JP5202570B2 - 絶縁電線 - Google Patents
絶縁電線 Download PDFInfo
- Publication number
- JP5202570B2 JP5202570B2 JP2010104981A JP2010104981A JP5202570B2 JP 5202570 B2 JP5202570 B2 JP 5202570B2 JP 2010104981 A JP2010104981 A JP 2010104981A JP 2010104981 A JP2010104981 A JP 2010104981A JP 5202570 B2 JP5202570 B2 JP 5202570B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- parts
- component
- insulated wire
- halogen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(1)ハロゲンフリー難燃性樹脂組成物からなる絶縁体2の、JIS C 3005に準拠して測定される引張強さが12MPa以上、同伸びが500%以上である。
(2)電線全体として、傾斜燃焼試験(JIS C 3005)に合格する難燃性を有する。
低密度ポリエチレン(LDPE;住友化学社製 商品名 スミカセンEP;密度0.927g/cm3)60部、エチレン・酢酸ビニル共重合体(EVR;三井・デュポンポリケミカル社製 商品名 エバフレックスV5274)30部、マレイン酸変性水添スチレン系熱可塑性エラストマ(旭化成ケミカルズ社製 商品名 タフテックM1943)10部、水酸化アルミニウム(昭和電工社製 商品名 ハイジライトH42M)30部、水酸化マグネシウム(神島化学工業社製 商品名 マグシーズV6−F)30部、およびフェノール・リン系酸化防止剤(住友化学社製 商品名 スミライザーGP)0.2部を加圧ニーダにより均一に混練して難燃性樹脂組成物を得た。
組成を表1〜表3に示すように変えた以外は実施例1と同様にして各成分を均一に混合して難燃性樹脂組成物を得、さらに、得られた組成物を用いて実施例1と同様にして絶縁電線を製造した。実施例1で用いた成分以外の配合成分は以下の通りである。
脂肪酸誘導体滑剤:川研ファインケミカル社製 商品名 LE−5
低分子量ポリエチレン:三井化学社製 商品名 ハイワックス400P
シリコーン・アクリル複合ゴム:三菱レイヨン社製 商品名 メタブレンSX−005
[引張強さおよび引張伸び]
JIS C 3005に基づく引張試験(引張速度200mm/分)を行い、測定した。
[耐傷付き性]
金属製エッジ治具上を荷重300g、速度100mm/分の条件で絶縁電線を長さ約150mmに亘って移動させ、電線表面の傷の発生の有無を目視にて観察し、下記の基準で評価した。
合格:傷が観察されない
不合格:傷が観察される
[耐ピンキング性]
絶縁電線をNOx雰囲気下に1週間暴露し、表面の変色の有無を目視にて観察し、下記の基準で評価した。
合格:変色なし
不合格:変色あり
[難燃性]
JIS C 3005に規定する60°傾斜燃焼試験を行い、評価した。
Claims (5)
- (A)低密度ポリエチレン、直鎖状低密度ポリエチレンおよび超低密度ポリエチレンから選ばれる少なくとも1種30〜70質量%、(B)エチレン・酢酸ビニル共重合体20〜60質量%、および(C)スチレン・ブタジエン・スチレンブロック共重合体のポリブタジエンブロックを水素添加して得られる水添型共重合体を無水マレイン酸で変性してなる酸価(滴定法)8mgCH 3 ONa/g以上、スチレン/エチレン・ブチレン比10/90〜20/80のマレイン酸変性水添スチレン系熱可塑性エラストマ5〜20質量%からなるベースポリマー100質量部に対し、(D)水酸化アルミニウム、および/または水酸化マグネシウム40〜80質量部、並びに(E)6−[3−(3−t−ブチル−4−ヒドロキシ−5メチルフェニル−)プロポキシ]−2,4,8,10−テトラ−t−ブチルジベンズ[d,f][1,3,2]−ジオキサホスフェピン0.2〜0.5質量部を含有するハロゲンフリー難燃性樹脂組成物を、導体上に被覆したことを特徴とする絶縁電線。
- 前記ハロゲンフリー難燃性樹脂組成物は、(A)成分40〜60質量%、(B)成分30〜40質量%、および(C)成分10〜15質量%からなるベースポリマー100質量部に対し、(D)成分40〜80質量部、および(E)成分0.2〜0.5質量部を含有することを特徴とする請求項1記載の絶縁電線。
- 前記ハロゲンフリー難燃性樹脂組成物は、前記ベースポリマー100質量部に対し、(F)脂肪酸誘導体滑剤1〜5質量部、(G)低分子量ポリエチレン3〜5質量部、および(H)シリコーン・アクリル複合ゴム1〜3質量部をさらに含有することを特徴とする請求項1または2記載の絶縁電線。
- 前記ハロゲンフリー難燃性樹脂組成物からなる被覆は、引張強さが12MPa以上、伸びが500%以上であることを特徴とする請求項1乃至3のいずれか1項記載の絶縁電線。
- 電線全体として、傾斜燃焼試験(JIS C 3005)に合格する難燃性を有することを特徴とする請求項1乃至4のいずれか1項記載の絶縁電線。