JP5187675B2 - Method for producing hydroxyketone from trivalent or higher alcohol and catalyst used therefor - Google Patents
Method for producing hydroxyketone from trivalent or higher alcohol and catalyst used therefor Download PDFInfo
- Publication number
- JP5187675B2 JP5187675B2 JP2007155147A JP2007155147A JP5187675B2 JP 5187675 B2 JP5187675 B2 JP 5187675B2 JP 2007155147 A JP2007155147 A JP 2007155147A JP 2007155147 A JP2007155147 A JP 2007155147A JP 5187675 B2 JP5187675 B2 JP 5187675B2
- Authority
- JP
- Japan
- Prior art keywords
- catalyst
- copper
- hydroxyketone
- reaction
- trivalent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、隣接する水酸基を持つ３価以上のアルコールを原料とし、担持銅触媒を用いてヒドロキシケトンを製造する方法に関する。 The present invention relates to a method for producing a hydroxyketone using a supported copper catalyst using a trivalent or higher-valent alcohol having an adjacent hydroxyl group as a raw material.
アセトールに代表されるヒドロキシケトン類は化成品中間体、医薬品中間体などとして用いられ化学工業上重要な物質であるが、これまで効率的な製造方法が見つけられていなかった。従来、このようなヒドロキシケトンは、ジオールの酸化的脱水素（特許文献１）あるいは、ヒドロキシカルボン酸の水添により合成されていた。これらの反応はいずれも生成物にケトンという官能基を有するが故に、過剰な酸化分解あるいは過剰な還元という本質的な問題を有していた。
近年ではフォルムアルデヒド、一酸化炭素及び水素からアセトールを製造するという方法（特許文献２）があるが、当該方法は反応圧力が高く、反応装置が耐圧装置である必要があること、触媒にロジウム化合物という貴金属を用いること、さらには反応に溶媒を用いること等、設備投資、ランニングコストおよび反応効率という観点から問題のある反応であった。
また、脱水反応に着目し、公知の触媒である酸化アルミニウム等の酸触媒を用いて反応を行っても、後述する比較例に示すように、目的生成物であるヒドロキシケトンの選択率は低く効率的な触媒ではなかった。
更に近年公開された方法では、触媒としてシリカに担持した銅及びまたは酸化銅を用いて、グリセリンを気相接触反応させてモノヒドロキシアセトンを製造する方法が知られている（特許文献３）。該出願では、クロムを触媒成分として用いないことを特徴としているが、目的生成物であるジヒドロキシアセトンの収率が十分ではなく、更に希釈ガスとして窒素及び水素を加えることから空時収率が小さいという欠点を有している。
Hydroxy ketones represented by acetol are used as chemical intermediates and pharmaceutical intermediates and are important substances in the chemical industry, but no efficient production method has been found so far. Conventionally, such a hydroxyketone has been synthesized by oxidative dehydrogenation of a diol (Patent Document 1) or hydrogenation of a hydroxycarboxylic acid. All of these reactions have an essential problem of excessive oxidative decomposition or excessive reduction because the product has a functional group called ketone.
In recent years, there is a method of producing acetol from formaldehyde, carbon monoxide and hydrogen (Patent Document 2). However, this method requires a high reaction pressure, the reaction device needs to be a pressure device, and a rhodium compound as a catalyst. From the viewpoints of capital investment, running cost, and reaction efficiency, such as using a noble metal and using a solvent for the reaction, the reaction was problematic.
Further, even if the reaction is carried out using an acid catalyst such as aluminum oxide, which is a known catalyst, focusing on the dehydration reaction, the selectivity of the target product, hydroxyketone, is low and efficient, as shown in a comparative example described later. It was not a typical catalyst.
Furthermore, among methods disclosed in recent years, there is known a method of producing monohydroxyacetone by gas phase contact reaction of glycerin using copper and / or copper oxide supported on silica as a catalyst (Patent Document 3). The application is characterized in that chromium is not used as a catalyst component, but the yield of the target product, dihydroxyacetone, is not sufficient, and the addition of nitrogen and hydrogen as diluent gases results in a low space-time yield. Has the disadvantages.
本発明の目的は、上記従来の技術課題を解決することにあり、特に、ヒドロキシケトンの製造に適した触媒を採択することにより、３価以上のアルコールからヒドロキシケトンを高い選択率で効率よく製造する方法を提供することにある。 The object of the present invention is to solve the above-mentioned conventional technical problems, and in particular, by adopting a catalyst suitable for production of hydroxyketone, it is possible to efficiently produce hydroxyketone from trihydric or higher alcohols with high selectivity. It is to provide a way to do.
本発明者らは鋭意検討の結果、触媒として、銅を特定の担体に担持させた触媒担体複合体を用いることにより、３価以上のアルコールの脱水反応により隣接する水酸基を持つ水酸基の一級水酸基を脱水し、エノール体となったものが反応系内で互変異性によりケトン体を生成することを見いだし、本発明を完成するに至った。 As a result of diligent study, the present inventors have used a catalyst carrier composite in which copper is supported on a specific carrier as a catalyst, so that a primary hydroxyl group having a hydroxyl group adjacent thereto by dehydration reaction of a trivalent or higher alcohol can be obtained. It has been found that what has been dehydrated to form an enol form forms a ketone form by tautomerism in the reaction system, and the present invention has been completed.
つまり、本発明の重要な特徴は、触媒として、銅含有量が１ないし１０重量％の、銅を酸化アルミニウムおよび酸化ジルコニウムから選ばれるいずれか一種類以上の担体に担持させた触媒担体複合体を採択したこと、ならびにこれと３価以上のアルコールの脱水反応を組み合わせた点に重要な技術的意義があり、これによって、はじめて、隣接する水酸基を持つ水酸基の一級水酸基を脱水し、エノール体となったものが反応系内で互変異性によりケトン体を生成することができる。 That is, an important feature of the present invention is that a catalyst carrier composite having a copper content of 1 to 10% by weight and having copper supported on one or more kinds of carriers selected from aluminum oxide and zirconium oxide is used as a catalyst. There is an important technical significance in the fact that it has been adopted and in combination with the dehydration reaction of trihydric or higher alcohols. With this, for the first time, the primary hydroxyl group with a neighboring hydroxyl group is dehydrated to form an enol form. Can form ketone bodies by tautomerism in the reaction system.
すなわち、本発明によれば、隣接する水酸基を持つ３価以上のアルコールからヒドロキシケトンを製造するに当たり、反応総体として脱水反応で進行するとともに、触媒として、銅含有量が１ないし１０重量％の、銅を酸化アルミニウムおよび酸化ジルコニウムから選ばれる担体に担持した触媒担体複合体を用いることを特徴とするヒドロキシケトンの製造方法が提供される。 That is, according to the present invention, in producing hydroxyketone from a trihydric or higher alcohol having an adjacent hydroxyl group, the reaction as a whole proceeds with a dehydration reaction, and as a catalyst , the copper content is 1 to 10% by weight, There is provided a method for producing a hydroxyketone using a catalyst carrier composite in which copper is supported on a carrier selected from aluminum oxide and zirconium oxide.
また、本発明によれば、触媒担体が、酸化アルミニウムを含む触媒担体である上記製造方法が提供される。 In addition, according to the present invention, there is provided the above production method, wherein the catalyst carrier is a catalyst carrier containing aluminum oxide.
また、本発明によれば、触媒担体が、酸化ジルコニウムを含む触媒担体である上記製造方法が提供される。 In addition, according to the present invention, there is provided the above production method, wherein the catalyst carrier is a catalyst carrier containing zirconium oxide.
また、本発明によれば、３価以上のアルコールがグリセリンであり、ヒドロキシケトンが１−ヒドロキシアセトンである上記製造方法が提供される。 Moreover, according to this invention, the trivalent or more alcohol is glycerol, The said manufacturing method whose hydroxyketone is 1-hydroxyacetone is provided.
また、本発明によれば、触媒担体が酸化アルミニウムを含む触媒担体であり、３価以上のアルコールがグリセリンであり、ヒドロキシケトンが１−ヒドロキシアセトンである上記製造方法が提供される。 In addition, according to the present invention, there is provided the above production method wherein the catalyst carrier is a catalyst carrier containing aluminum oxide, the trivalent or higher alcohol is glycerin, and the hydroxyketone is 1-hydroxyacetone.
また、本発明によれば、触媒担体が酸化ジルコニウムを含む触媒担体であり、３価以上のアルコールがグリセリンであり、ヒドロキシケトンが１−ヒドロキシアセトンである上記製造方法が提供される。 According to the present invention, there is also provided the above production method wherein the catalyst carrier is a catalyst carrier containing zirconium oxide, the trivalent or higher alcohol is glycerin, and the hydroxyketone is 1-hydroxyacetone.
また、本発明によれば、隣接する水酸基を持つ３価以上のアルコールからヒドロキシケトンを製造するに当たり、反応総体として脱水反応で進行するとともに、触媒として、銅を酸化アルミニウムおよび酸化ジルコニウムから選ばれる担体に担持した銅−触媒担体複合体からなるヒドロキシケトン製造用触媒が提供される。 In addition, according to the present invention, in producing hydroxyketone from a trivalent or higher-valent alcohol having an adjacent hydroxyl group, the reaction proceeds as a whole by a dehydration reaction, and copper is selected from aluminum oxide and zirconium oxide as a catalyst. There is provided a catalyst for producing hydroxyketone comprising a copper-catalyst support composite supported on a catalyst.
また、本発明によれば、触媒担体が、酸化アルミニウムを含む触媒担体である上記触媒が提供される。 Moreover, according to this invention, the said catalyst whose catalyst carrier is a catalyst carrier containing an aluminum oxide is provided.
また、本発明によれば、触媒担体が、酸化ジルコニウムを含む触媒担体である上記触媒が提供される。 According to the present invention, there is also provided the above catalyst, wherein the catalyst carrier is a catalyst carrier containing zirconium oxide.
また、本発明によれば、３価以上のアルコールがグリセリンであり、ヒドロキシケトンが１−ヒドロキシアセトンである上記触媒が提供される。 Moreover, according to this invention, the trivalent or more alcohol is glycerol, The said catalyst whose hydroxyketone is 1-hydroxyacetone is provided.
本発明によれば、銅を酸化アルミニウムおよび酸化ジルコニウムから選ばれる特定の担体に担持した銅−触媒担体複合体を用い、かつ、反応総体として脱水反応で進行することにより、隣接する水酸基を持つ３価以上のアルコールからヒドロキシケトンを高い選択率で効率的に製造することができる。 According to the present invention, copper supported on a particular carrier selected copper from aluminum oxide and zirconium oxide - using a catalyst carrier complex, and, by proceeding in the dehydration reaction as a reaction whole, 3 with adjacent hydroxyl groups A hydroxyketone can be efficiently produced from a higher- valent alcohol with a high selectivity.
本発明は、隣接する水酸基を持つ３価以上のアルコールから高い選択率でヒドロキシケトンを製造する方法及び、その製造方法に用いられる特定のヒドロキシケトン製造用触媒からなるものであり、その要件は前述したとおりである。
本発明の触媒である銅−触媒担体複合体は、銅を酸化アルミニウムおよび酸化ジルコニウムから選ばれる１種類以上の触媒担体に担持した銅−触媒担体複合体である。
The present invention comprises a method for producing a hydroxyketone with a high selectivity from a trihydric or higher alcohol having an adjacent hydroxyl group, and a specific hydroxyketone production catalyst used in the production method. As you did.
The copper-catalyst support composite which is the catalyst of the present invention is a copper-catalyst support composite in which copper is supported on one or more kinds of catalyst supports selected from aluminum oxide and zirconium oxide.
本発明の反応総体の特徴である脱水反応とは、通常の脱水反応と比較して用いる触媒が大きく異なることを特徴とする。通常、アルコールの脱水反応を行なう場合は酸触媒の使用が広く普及しており、当該反応によりオレフィンあるいはエーテルが得られる。本発明における脱水反応も直接の生成物はオレフィンであると予想されるが、とりわけ、グリセリンの反応においては脱水に関わる水酸基が１位及び２位に存在し、１位の水酸基を選択的に脱水することによって、エノールアルコールとし、それが異性化することによってヒドロキシアセトンを生成する。
本反応が特に特徴的であるのは通常の酸触媒とされるアルミナやシリカ−アルミナの様な固体酸での脱水反応ではなく、通常は酸触媒に分類されない銅を触媒成分とすることである。
The catalyst used is significantly different from the dehydration reaction, which is a feature of the overall reaction of the present invention, as compared with a normal dehydration reaction. In general, when an alcohol dehydration reaction is performed, the use of an acid catalyst is widely used, and an olefin or an ether is obtained by the reaction. In the dehydration reaction in the present invention, the direct product is expected to be an olefin. In particular, in the glycerin reaction, hydroxyl groups related to dehydration are present at the 1- and 2-positions, and the hydroxyl group at the 1-position is selectively dehydrated. To produce enol alcohol, which isomerizes to produce hydroxyacetone.
This reaction is particularly characteristic in that it is not a dehydration reaction with a solid acid such as alumina or silica-alumina, which is usually used as an acid catalyst, but usually uses copper that is not classified as an acid catalyst as a catalyst component. .
本発明のヒドロキシケトン製造用触媒における銅は市販品、市販品を還元したもの、銅の酸化物、水酸化物、炭酸塩、硝酸塩、酢酸塩などを熱分解したもの、あるいは熱分解後に公知の方法にて還元したもの等、いずれの形態でも触媒として使用することが可能である。同様に銅−触媒担体複合体についても市販品、市販品を還元したもの、当該金属の水酸化物、炭酸塩、硝酸塩、酢酸塩などを触媒担体に担持させ熱分解したもの、あるいは熱分解後に公知の方法にて還元したもの等、いずれの形態でも触媒として使用することが可能である。 Copper in the catalyst for producing hydroxyketone according to the present invention is a commercially available product, a product obtained by reducing a commercially available product, a product obtained by thermally decomposing copper oxide, hydroxide, carbonate, nitrate, acetate or the like, or known after pyrolysis. Any form such as those reduced by the method can be used as the catalyst. Similarly, for a copper-catalyst carrier composite, a commercially available product, a product obtained by reducing a commercially available product, a product obtained by thermally decomposing a metal hydroxide, carbonate, nitrate, acetate, etc. on a catalyst support, or after pyrolysis Any form such as those reduced by a known method can be used as a catalyst.
銅−触媒担体複合体における触媒担体への銅の担持方法は含浸法、共沈法等公知の方法を用いることが可能である。
例えば、銅の硝酸塩を触媒担体成分の前駆体である硝酸アルミニウム等と共に水に溶解し、そこにアルカリ水溶液を加えることによって得られる沈殿を乾燥、焼成、還元して得られる複合体が触媒として使用可能である。
銅−触媒担体複合体における、銅：触媒担体の含有比は、銅の重量％で１．００％以上の範囲で選択可能である。銅：触媒担体中の銅の含有比が１．００に満たない場合は十分な触媒活性を得ることができない。また銅触媒は担体を用いなくても使用可能である。
As a method for supporting copper on the catalyst carrier in the copper-catalyst carrier composite, a known method such as an impregnation method or a coprecipitation method can be used.
For example, a composite obtained by drying, firing, and reducing a precipitate obtained by dissolving copper nitrate in water together with aluminum nitrate, which is a precursor of the catalyst carrier component, and adding an alkaline aqueous solution thereto is used as a catalyst. Is possible.
The content ratio of copper: catalyst support in the copper-catalyst support composite can be selected within a range of 1.00% or more by weight% of copper. If the copper: copper content ratio in the catalyst support is less than 1.00, sufficient catalytic activity cannot be obtained. Further, the copper catalyst can be used without using a support.
本発明のヒドロキシケトン製造方法においては、隣接する水酸基を持つ多価アルコールを銅あるいは、銅および触媒担体複合体を触媒として用い、反応総体として脱水反応で進行することが重要な特徴である。 In the method for producing hydroxyketone according to the present invention, it is an important feature that a polyhydric alcohol having an adjacent hydroxyl group is used as copper or copper and a catalyst carrier complex as a catalyst, and the reaction as a whole proceeds by a dehydration reaction.
本発明のヒドロキシケトンの製造で使用される反応装置は特に限定されない。たとえば、気相流通反応装置に所定量の触媒前駆体を入れ、これを公知の方法で還元することにより活性な触媒層を気相流通反応装置内に形成させる。ここに、原料の多価アルコールを供給することによりヒドロキシケトンを製造することが可能である。 The reaction apparatus used in the production of the hydroxyketone of the present invention is not particularly limited. For example, a predetermined amount of catalyst precursor is put into a gas phase flow reaction apparatus and reduced by a known method to form an active catalyst layer in the gas phase flow reaction apparatus. It is possible to produce a hydroxyketone by supplying a raw material polyhydric alcohol.
原料となる３価以上のアルコールとしては、隣接する水酸基を持つ多価アルコールが用いられる。隣接する水酸基を持つ３価以上のアルコールの具体例は、グリセリン、１，２，３−ブタントリオールなどが挙げられる。 As the trihydric or higher alcohol as a raw material, a polyhydric alcohol having an adjacent hydroxyl group is used. Specific examples of the trivalent or higher alcohol having an adjacent hydroxyl group include glycerin and 1,2,3-butanetriol.
また、これらの原料から得られるヒドロキシケトンとしては、ヒドロキシアセトン、２−ヒドロキシ−３−ブタノン及び１−ヒドロキシ−２−ブタノンなどがあげられる。 Examples of hydroxy ketones obtained from these raw materials include hydroxy acetone, 2-hydroxy-3-butanone, and 1-hydroxy-2-butanone.
本発明のヒドロキシケトン製造方法は、隣接する水酸基を持つ３価以上のアルコールからヒドロキシケトンを製造するのに好ましく用いられる。具体的には、グリセリンからヒドロキシアセトンの製造、１，２，３−ブタントリオールから２−ヒドロキシ−３−ブタノン及び１−ヒドロキシ−２−ブタノンの製造に用いられる。
また、原料の３価以上のアルコールは混合物であっても、同時に対応するヒドロキシケトンを製造することができる。
The method for producing hydroxyketone of the present invention is preferably used for producing hydroxyketone from a trivalent or higher alcohol having an adjacent hydroxyl group. Specifically, it is used for production of hydroxyacetone from glycerin and production of 2-hydroxy-3-butanone and 1-hydroxy-2-butanone from 1,2,3-butanetriol.
Moreover, even if the raw material trihydric or higher alcohol is a mixture, the corresponding hydroxyketone can be produced at the same time.
本発明のヒドロキシケトン製造方法の反応温度は、１５０℃から４００℃の範囲で適用可能であり、２００℃から３５０℃の温度範囲が好適である。反応を十分に進行させるためには２００℃以上が好ましく、２２５℃以上が特に好ましい。また、生成物選択率を良好に保つためには３５０℃以下が好ましく、更に好ましい反応温度は、２２５℃から３００℃の範囲である。 The reaction temperature of the method for producing hydroxyketone of the present invention can be applied in the range of 150 ° C. to 400 ° C., and the temperature range of 200 ° C. to 350 ° C. is suitable. In order to allow the reaction to proceed sufficiently, it is preferably 200 ° C. or higher, particularly preferably 225 ° C. or higher. Further, in order to keep the product selectivity good, 350 ° C. or lower is preferable, and a more preferable reaction temperature is in the range of 225 ° C. to 300 ° C.
原料の３価以上のアルコール中の水分は、０〜９８重量％の範囲で用いることが可能で、好ましくは３０〜７０重量％の範囲である。３価以上のアルコールの水分が３０〜７０重量％の範囲が反応効率が著しく優れており、目的生成物であるヒドロキシケトンを高い選択率で得ることができる。 The water in the trihydric or higher alcohol as a raw material can be used in the range of 0 to 98% by weight, and preferably in the range of 30 to 70% by weight. When the water content of the trihydric or higher alcohol is in the range of 30 to 70% by weight, the reaction efficiency is remarkably excellent, and the target product hydroxyketone can be obtained with high selectivity.
以下、実施例に基づいて本発明の効果を具体的に説明するが、本発明はこれらに限定されるものではない。
実施例、比較例に用いた固定床常圧気相流通反応装置は、内径１０ｍｍ、全長３００ｍｍの反応器であり、その上端にキャリアガス導入口と原料流入口があり、下端にガス抜け口を有する反応粗液捕集容器（冷却）を有するものである。
実施例、比較例に用いた触媒重量は、すべて０．５ｇであった。触媒である銅−酸化アルミニウムの触媒原料は、全て市販の試薬（和光純薬製、特級グレード）を用いた。
捕集容器に捕集された反応粗液は、ガスクロマトグラフィーにて測定し、検量線補正後、ヒドロキシアセトンなどの収量、グリセリンなどの原料の残量を決定し、この値から転化率（モル％）、選択率（モル％）を求めた。
Hereinafter, although the effect of the present invention is explained concretely based on an example, the present invention is not limited to these.
The fixed bed atmospheric pressure gas flow reactor used in Examples and Comparative Examples is a reactor having an inner diameter of 10 mm and a total length of 300 mm, having a carrier gas inlet and a raw material inlet at the upper end and a gas outlet at the lower end. It has a reaction crude liquid collection container (cooling).
The catalyst weight used in Examples and Comparative Examples was all 0.5 g. Commercially available reagents (manufactured by Wako Pure Chemicals, special grade) were used as catalyst raw materials for copper-aluminum oxide as a catalyst.
The reaction crude liquid collected in the collection container is measured by gas chromatography. After calibration curve correction, the yield of hydroxyacetone and the remaining amount of raw materials such as glycerin are determined, and the conversion rate (moles) is determined from this value. %) And selectivity (mol%).
＜実施例１＞
（銅−酸化アルミニウム触媒の製造）
硝酸銅（和光純薬製、特級試薬）２１２．８ｇ及び硝酸アルミニウム（和光純薬製、特級試薬）２２０．３ｇを水５Ｌに溶解させた溶液に、水酸化ナトリウム（和光純薬製、特級試薬）１５４．１ｇを水１Ｌに溶解させた溶液を加えた際に生成する沈殿を乾燥、焼成し触媒前駆体とする。該触媒前駆体を固定床常圧気相流通反応装置に設置し、水素気流中で還元し銅−酸化アルミニウム触媒とする。
<Example 1>
(Production of copper-aluminum oxide catalyst)
Sodium hydroxide (manufactured by Wako Pure Chemicals, special grade reagent) was added to a solution of 212.8 g of copper nitrate (Wako Pure Chemicals, special grade reagent) and aluminum nitrate (Wako Pure Chemicals, special grade reagent) 220.3 g in 5 L of water. ) A precipitate formed when 154.1 g of a solution dissolved in 1 L of water is added is dried and fired to obtain a catalyst precursor. The catalyst precursor is placed in a fixed bed atmospheric pressure gas flow reactor and reduced in a hydrogen stream to form a copper-aluminum oxide catalyst.
＜実施例２＞
（ヒドロキシケトンの製造）
上記、銅−酸化アルミニウム触媒層の設定された固定床常圧気相流通反応装置の上部からキャリアガスとして窒素を１０ｍｌ／ｍｉｎ．の流速で流した。この原料である３０ｗｔ％グリセリン水溶液は１．８ｍｌ／ｈの速度で触媒層へ供給し反応を行った。反応温度の相違によるグリセリン転化率、ヒドロキシアセトン選択率を表１に示す。
表１は、銅−酸化アルミニウム触媒によるグリセリンの脱水反応を示すものである。
<Example 2>
(Production of hydroxyketone)
From the upper part of the fixed bed atmospheric pressure gas flow reactor where the copper-aluminum oxide catalyst layer is set, nitrogen is added as a carrier gas at 10 ml / min. The flow rate was. The 30 wt% glycerin aqueous solution as the raw material was supplied to the catalyst layer at a rate of 1.8 ml / h for reaction. Table 1 shows the glycerin conversion rate and hydroxyacetone selectivity depending on the reaction temperature.
Table 1 shows the dehydration reaction of glycerol with a copper-aluminum oxide catalyst.
＜実施例３＞
（銅含有量を変えた銅−酸化アルミニウム触媒の製造）
実施例１に準じて銅と酸化アルミニウムの含有比を変えた銅−酸化アルミニウム触媒を調製し、ヒドロキシアセトン製造反応に供した。その他の条件は実施例２に準じた。
表２は、銅含有量を変えた銅−酸化アルミニウム触媒によるグリセリン脱水反応を示すものである。
結果を表２に示す。
<Example 3>
(Production of copper-aluminum oxide catalyst with varying copper content)
A copper-aluminum oxide catalyst in which the content ratio of copper and aluminum oxide was changed in accordance with Example 1 was prepared and subjected to a hydroxyacetone production reaction. Other conditions were the same as in Example 2.
Table 2 shows the glycerin dehydration reaction with the copper-aluminum oxide catalyst with different copper contents.
The results are shown in Table 2.
＜参考例＞
（銅触媒の製造）
硝酸銅（和光純薬製、特級試薬）３０３．８ｇを水５Ｌに溶解させた溶液に、水酸化ナトリウム（和光純薬製、特級試薬）１１０．０ｇを水１Ｌに溶解させた溶液を加えた際に生成する沈殿を乾燥、焼成し触媒前駆体とする。該触媒前駆体を固定床常圧気相流通反応装置に０．５ｇ設置し、水素気流中で還元し銅触媒とした。
< Reference example >
(Manufacture of copper catalyst)
To a solution in which 303.8 g of copper nitrate (manufactured by Wako Pure Chemicals, special grade reagent) was dissolved in 5 L of water, a solution in which 110.0 g of sodium hydroxide (made by Wako Pure Chemical Industries, special grade reagent) was dissolved in 1 L of water was added. The precipitate formed at this time is dried and calcined to obtain a catalyst precursor. 0.5 g of the catalyst precursor was placed in a fixed bed atmospheric pressure gas flow reactor and reduced in a hydrogen stream to obtain a copper catalyst.
＜実施例４＞
（銅−酸化ジルコニウム触媒の製造）
硝酸銅（和光純薬製、特級試薬）２００．３ｇ及び硝酸ジルコニル２水和物（和光純薬製、特級試薬）７３．９ｇを水５Ｌに溶解させた溶液に、水酸化ナトリウム（和光純薬製、特級試薬）１２０．９ｇを水１Ｌに溶解させた溶液を加えた際に生成する沈殿を乾燥、焼成し触媒前駆体とする。該触媒前駆体を固定床常圧気相流通反応装置に０．５ｇ設置し、水素気流中で還元し銅−酸化ジルコニウム触媒とした。
<Example 4 >
(Production of copper-zirconium oxide catalyst)
Sodium hydroxide (Wako Pure Chemical Industries, Ltd.) was added to a solution obtained by dissolving 200.3 g of copper nitrate (Wako Pure Chemical Industries, special grade reagent) and zirconyl nitrate dihydrate (Wako Pure Chemical Industries, special grade reagent) 73.9 g in 5 L of water. Manufactured, special grade reagent) The precipitate formed when 120.9 g of a solution dissolved in 1 L of water is added is dried and fired to obtain a catalyst precursor. 0.5 g of the catalyst precursor was placed in a fixed bed atmospheric pressure gas flow reactor and reduced in a hydrogen stream to obtain a copper-zirconium oxide catalyst.
＜実施例５＞
（銅−酸化ジルコニウム−酸化アルミニウム触媒の製造）
硝酸銅（和光純薬製、特級試薬）１５６．３ｇ、硝酸アルミニウム９水和物（和光純薬製、特級試薬）１６１．８ｇ、及び硝酸ジルコニル２水和物（和光純薬製、特級試薬）５７．６ｇを水５Ｌに溶解させた溶液に、水酸化ナトリウム（和光純薬製、特級試薬）１５０．９ｇを水１Ｌに溶解させた溶液を加えた際に生成する沈殿を乾燥、焼成し触媒前駆体とする。
該触媒前駆体を固定床常圧気相流通反応装置に０．５ｇ設置し、水素気流中で還元し銅−酸化ジルコニウム−酸化アルミニウム触媒とした。
<Example 5 >
(Production of copper-zirconium oxide-aluminum oxide catalyst)
Copper nitrate (Wako Pure Chemicals, special grade reagent) 156.3 g, Aluminum nitrate 9 hydrate (Wako Pure Chemicals, special grade reagent) 161.8 g, and zirconyl nitrate dihydrate (Wako Pure Chemicals, special grade reagent) The precipitate formed when 57.6 g of water dissolved in 5 L of water and 150.9 g of sodium hydroxide (made by Wako Pure Chemicals, special grade reagent) dissolved in 1 L of water was added, dried and calcined to form a catalyst. Let it be a precursor.
0.5 g of the catalyst precursor was placed in a fixed bed atmospheric pressure gas flow reactor and reduced in a hydrogen stream to obtain a copper-zirconium oxide-aluminum oxide catalyst.
＜実施例６＞
反応温度を２５０℃に固定し、実施例１、４及び５に記載の触媒を用いて実験を行った。その他の条件は実施例２に準じた。
表３は、触媒担体の相違によるグリセリンの脱水反応への影響を示すものである。
結果を表３に示す。
<Example 6 >
The experiment was conducted using the catalysts described in Examples 1, 4 and 5 with the reaction temperature fixed at 250 ° C. Other conditions were the same as in Example 2.
Table 3 shows the influence on the dehydration reaction of glycerin due to the difference in the catalyst carrier.
The results are shown in Table 3.
表２及び表３の結果から、担体のない銅触媒のみでも反応は進行するが、酸化アルミニウム、酸化ジルコニウムを触媒担体としたときには、銅触媒のみの場合よりも、グリセリン転化率、ヒドロキシアセトン選択率が高く、効率の良い反応が進行していることがわかる。更に酸化アルミニウムおよび酸化ジルコニウムの複合担体でも反応が進行している。
From the results in Tables 2 and 3, the reaction proceeds even with a copper catalyst without a carrier alone, but when aluminum oxide and zirconium oxide are used as a catalyst carrier, the glycerin conversion rate, hydroxyacetone is higher than that with a copper catalyst alone. It can be seen that the selectivity is high and an efficient reaction proceeds. Further, the reaction proceeds with a composite carrier of aluminum oxide and zirconium oxide.
＜実施例７＞
触媒に市販の触媒（Ｎ−２０１日揮化学製、銅−酸化クロム；Ｎ−２４２日揮化学製、
銅−酸化アルミニウム；Ｇ−２２ズードケミー触媒製、銅−酸化クロム；Ｔ−３１７日産ガードラー製、銅−酸化アルミニウム）を用いて実験を行った。その他の条件は実施例７
に準じた。表４は、市販担持銅触媒によるグリセリン脱水反応の結果を示すものである。 結果を表４に示す。
<Example 7 >
A commercially available catalyst (N-201 JGC Chemical, copper-chromium oxide; N-242 JGC Chemical,
An experiment was conducted using copper-aluminum oxide; G-22 Zudd Chemie Catalyst, copper-chromium oxide; T-317 Nissan Gardler, copper-aluminum oxide). Other conditions were as in Example 7.
According to Table 4 shows the results of glycerin dehydration reaction using a commercially available supported copper catalyst. The results are shown in Table 4.
＜実施例８＞
触媒に市販の触媒（Ｎ−２０１、日揮化学製、銅−酸化クロム）を用いてグリセリン濃度の異なる原料を用いて実験を行った。その他の条件は実施例７に準じた。
表５は、グリセリン脱水反応への原料中水分の影響を示すものである。
結果を表５に示す。
<Example 8 >
Experiments were conducted using raw materials having different glycerin concentrations using commercially available catalysts (N-201, JGC Chemicals, copper-chromium oxide). Other conditions were the same as in Example 7.
Table 5 shows the influence of moisture in the raw material on the glycerin dehydration reaction.
The results are shown in Table 5.
＜実施例９＞
実施例１に記載の銅−アルミニウム触媒を用い、１，２，３−ブタントリオールの脱水反応を行った。原料である１，２，３−ブタントリオールは３０ｗｔ％水溶液として反応装置に供給した。その他の条件は実施例７に準じた。
表６は、１，２，３−ブタントリオールの脱水反応を示すものである。
結果を表６に示す。
<Example 9 >
Using the copper-aluminum catalyst described in Example 1, 1,2,3-butanetriol was dehydrated. The raw material 1,2,3-butanetriol was supplied to the reactor as a 30 wt% aqueous solution. Other conditions were the same as in Example 7.
Table 6 shows the dehydration reaction of 1,2,3-butanetriol.
The results are shown in Table 6.
＜比較例１＞
触媒に銅を用いずに酸化アルミニウム担体のみを用い反応を行った。その他の条件は実施例７に準じた。
結果を表７に示す。
<Comparative Example 1>
The reaction was carried out using only the aluminum oxide support without using copper as the catalyst. Other conditions were the same as in Example 7.
The results are shown in Table 7.
＜比較例２＞
触媒に他の触媒担体を用いた銅触媒（銅−酸化セリウム、銅−酸化マグネシウム、銅−酸化亜鉛）を用いて実験を行った。その他の条件は実施例７に準じた。
結果を表８に示す。
<Comparative example 2>
An experiment was conducted using a copper catalyst (copper-cerium oxide, copper-magnesium oxide, copper-zinc oxide) using another catalyst carrier as a catalyst. Other conditions were the same as in Example 7.
The results are shown in Table 8.
本発明によれば、銅を酸化アルミニウムおよび酸化ジルコニウムから選ばれる特定の担体に担持した触媒担体複合体からなる触媒を用い、かつ、反応総体として脱水反応で進行することによって、高い選択率で、隣接する水酸基を持つ３価以上のアルコールからヒドロキシケトンを好適に製造することができ、従来の触媒を用いたのではなし得なかった工業的に優位なヒドロキシケトンの製造技術を提供することが出来る。
According to the present invention, by using a catalyst comprising a catalyst carrier complex in which copper is supported on a specific carrier selected from aluminum oxide and zirconium oxide, and by proceeding in a dehydration reaction as a reaction total, with high selectivity, A hydroxyketone can be suitably produced from a trihydric or higher alcohol having an adjacent hydroxyl group, and an industrially superior hydroxyketone production technique that cannot be achieved by using a conventional catalyst can be provided.
Claims (10)