JP5184817B2 - Shrink label - Google Patents

Shrink label Download PDF

Info

Publication number
JP5184817B2
JP5184817B2 JP2007136157A JP2007136157A JP5184817B2 JP 5184817 B2 JP5184817 B2 JP 5184817B2 JP 2007136157 A JP2007136157 A JP 2007136157A JP 2007136157 A JP2007136157 A JP 2007136157A JP 5184817 B2 JP5184817 B2 JP 5184817B2
Authority
JP
Japan
Prior art keywords
layer
film
shrink
resin
heat shrinkage
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP2007136157A
Other languages
Japanese (ja)
Other versions
JP2008001098A (en
Inventor
秀和 田中
收平 松本
奈緒美 穂積
那央 上▲陰▼
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fuji Seal International Inc
Original Assignee
Fuji Seal International Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fuji Seal International Inc filed Critical Fuji Seal International Inc
Priority to JP2007136157A priority Critical patent/JP5184817B2/en
Publication of JP2008001098A publication Critical patent/JP2008001098A/en
Application granted granted Critical
Publication of JP5184817B2 publication Critical patent/JP5184817B2/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、植物由来の原料であるポリ乳酸系重合体を用いたシュリンクフィルム、及び、印刷層を有するシュリンクラベル(以下、単にシュリンクフィルム、若しくはシュリンクラベルと表現しても特に断らない限りそれらはシュリンクフィルム、及び、それからなり且つ印刷層を有するシュリンクラベル両方意味する場合がある)に関する。   The present invention is a shrink film using a polylactic acid-based polymer that is a plant-derived raw material, and a shrink label having a printed layer (hereinafter simply referred to as “shrink film” or “shrink label” unless otherwise noted) It may mean both shrink film and shrink labels made of it and having a printed layer).

現在、お茶や清涼飲料水等の飲料用容器として、PETボトルなどのプラスチック製ボトルや、ボトル缶等の金属製ボトル等が広く用いられている。これらの容器には、表示や装飾性、機能性の付与のため、シュリンクラベルなどのプラスチックラベルが広く使用されている。   Currently, plastic bottles such as PET bottles and metal bottles such as bottle cans are widely used as containers for beverages such as tea and soft drinks. For these containers, plastic labels such as shrink labels are widely used for providing display, decoration, and functionality.

上記シュリンクラベルとしては、近年、環境保護の観点から、生分解性であり、且つ、植物由来の材料であるポリ乳酸を用いたフィルムが検討されている(例えば、特許文献1参照)。また、ポリ乳酸フィルムの耐衝撃性やシール強度を改善するために、ポリ乳酸系重合体およびポリエステル系樹脂を有する積層シュリンクフィルムが知られている(例えば、特許文献2、3参照)。   As the shrink label, in recent years, a film using polylactic acid which is biodegradable and plant-derived material has been studied from the viewpoint of environmental protection (for example, see Patent Document 1). Moreover, in order to improve the impact resistance and seal strength of a polylactic acid film, a laminated shrink film having a polylactic acid polymer and a polyester resin is known (see, for example, Patent Documents 2 and 3).

しかし、上記ポリ乳酸を含むシュリンクフィルムには、ポリ乳酸の固有の性質として、熱収縮の際の収縮速度がポリスチレン系フィルムやポリエステル系フィルムなどの既存のシュリンクフィルムに対して非常に大きく、熱収縮が急激に起こるため、熱収縮加工を行う際の収縮挙動の制御が困難で、熱収縮後のラベルの外観を損なう場合が多く問題であった。特に、飲料用ボトル用途の場合など、部位によって熱収縮率が大きく異なる場合には、「しわ」が発生したり、熱収縮が不均一となりラベルとしての意匠性が低下したりするなどの問題が生じていた。   However, in the shrink film containing polylactic acid, the shrinkage rate at the time of thermal shrinkage is much higher than that of existing shrink film such as polystyrene film and polyester film because of the inherent property of polylactic acid. Since this occurs abruptly, it is difficult to control the shrinkage behavior at the time of heat shrinking, and the appearance of the label after heat shrinking is often impaired. In particular, when the heat shrinkage rate varies greatly depending on the site, such as in the case of beverage bottles, there are problems such as `` wrinkles '' or non-uniform heat shrinkage resulting in poor design as a label. It was happening.

このように、適切な熱収縮性を有するシュリンクフィルムが求められており、特に環境面からは、植物由来のポリ乳酸を用いた適切な熱収縮速度を有するシュリンクフィルムが求められているのが現状である。   Thus, there is a demand for a shrink film having an appropriate heat shrinkability, and in particular, from the environmental viewpoint, there is a need for a shrink film having an appropriate heat shrink rate using plant-derived polylactic acid. It is.

特開平5−212790号公報JP-A-5-212790 特開2002−234117号公報JP 2002-234117 A 特開2005−35238号公報JP-A-2005-35238

本発明の目的は、ポリ乳酸系重合体を用いた、シュリンクラベルであって、シュリンクフィルムの熱収縮速度を調整することによって、シュリンク加工性や仕上がり性を改良し、以って生産性を向上させたシュリンクラベルを提供することにある。   The object of the present invention is a shrink label using a polylactic acid-based polymer, and by improving the heat shrinkage rate of the shrink film, the shrink processability and the finish are improved, thereby improving the productivity. It is to provide a contracted shrink label.

本発明者らは、上記目的を達成するため鋭意検討した結果、ポリ乳酸系重合体を必須成分とするフィルム層を有するシュリンクフィルム及び印刷層を有するシュリンクラベルの75℃における熱収縮速度を特定の範囲に制御することによって、低温あるいは短時間で熱収縮加工が可能で、なおかつ、優れた仕上がり性を有するシュリンクラベルが得られることを見出し本発明を完成した。また、ポリ乳酸系重合体を主成分とするフィルム層とポリスチレン系樹脂または芳香族ポリエステル系樹脂を主成分とするフィルム層の積層シュリンクフィルムであって、それぞれのフィルム層の厚み比を特定の範囲に制御することによって、上記特性を有するシュリンクラベルが得られることを見出した。   As a result of intensive studies to achieve the above object, the inventors of the present invention specified a heat shrinkage rate at 75 ° C. of a shrink film having a film layer containing a polylactic acid polymer as an essential component and a shrink label having a printed layer. By controlling to the range, it was found that a shrink label capable of heat shrinking at a low temperature or in a short time and having excellent finish was obtained, and the present invention was completed. Also, a laminated shrink film of a film layer mainly composed of a polylactic acid polymer and a film layer mainly composed of a polystyrene resin or an aromatic polyester resin, wherein the thickness ratio of each film layer is within a specific range. It has been found that a shrink label having the above characteristics can be obtained by controlling to the above.

すなわち、本発明は、ポリ乳酸系重合体を必須成分とするフィルム層(A層)を少なくとも1層有するシュリンクフィルム及び印刷層を有するシュリンクラベルであって、前記シュリンクフィルムが、さらに、ポリスチレン系樹脂又は芳香族ポリエステル系樹脂であるポリ乳酸系重合体以外の樹脂を主成分とするフィルム層(B層)を少なくとも1層有する積層シュリンクフィルムであり、前記積層シュリンクフィルムの、全A層のフィルム層厚みと全B層のフィルム層厚みの比(A層厚み/B層厚み)が80/20〜20/80であり、前記A層中の前記ポリ乳酸系重合体の含有量が50重量%以上であり、前記ポリ乳酸系重合体を構成する単量体成分における、全乳酸成分に占めるD−乳酸成分の割合が4〜15重量%であり、前記B層中の前記ポリ乳酸系重合体以外の樹脂の含有量が70〜100重量%であり、75℃温水中での熱収縮開始1秒後における主配向方向の熱収縮率が3〜23%、さらに90℃、10秒における主配向方向の熱収縮率が40〜84%であることを特徴とするシュリンクラベルを提供する。 That is, the present invention is a shrink label having at least one film layer (A layer) having a polylactic acid polymer as an essential component and a printed layer, wherein the shrink film further comprises a polystyrene resin. Or it is a laminated shrink film which has at least one film layer (B layer) which has resin other than the polylactic acid-type polymer which is an aromatic polyester resin as a main component, and is a film layer of all the A layers of the laminated shrink film The ratio of the thickness to the film layer thickness of all B layers (A layer thickness / B layer thickness) is 80/20 to 20/80, and the content of the polylactic acid polymer in the A layer is 50% by weight or more. In the monomer component constituting the polylactic acid polymer, the ratio of the D-lactic acid component in the total lactic acid component is 4 to 15% by weight, and the B layer A of the content of the resin other than the polylactic acid polymer from 70 to 100 wt.%, 75 ° C. main alignment direction of the heat shrinkage rate in the heat shrinkage starting one second after the in hot water 3-23%, further 90 A shrink label having a thermal shrinkage ratio in the main alignment direction at 40 ° C. for 10 seconds at 40 ° C. is provided.

また、本発明は、ポリ乳酸系重合体を必須成分とするフィルム層(A層)を少なくとも1層有するシュリンクフィルム及び印刷層を有するシュリンクラベルであって、前記シュリンクフィルムが、さらに、ポリスチレン系樹脂又は芳香族ポリエステル系樹脂であるポリ乳酸系重合体以外の樹脂を主成分とするフィルム層(B層)を少なくとも1層有する積層シュリンクフィルムであり、前記積層シュリンクフィルムの、全A層のフィルム層厚みと全B層のフィルム層厚みの比(A層厚み/B層厚み)が80/20〜20/80であり、前記A層中の前記ポリ乳酸系重合体の含有量が50重量%以上であり、前記ポリ乳酸系重合体を構成する単量体成分における、全乳酸成分に占めるD−乳酸成分の割合が4〜15重量%であり、前記B層中の前記ポリ乳酸系重合体以外の樹脂の含有量が70〜100重量%であり、75℃温水中での主配向方向の最大熱収縮速度が7〜40%/秒であり、さらに90℃、10秒における主配向方向の熱収縮率が40〜84%であることを特徴とするシュリンクラベルを提供する。 The present invention also relates to a shrink label having at least one film layer (A layer) having a polylactic acid polymer as an essential component and a printed layer, wherein the shrink film further comprises a polystyrene resin. Or it is a laminated shrink film which has at least one film layer (B layer) which has resin other than the polylactic acid-type polymer which is an aromatic polyester resin as a main component, and is a film layer of all the A layers of the laminated shrink film The ratio of the thickness to the film layer thickness of all B layers (A layer thickness / B layer thickness) is 80/20 to 20/80, and the content of the polylactic acid polymer in the A layer is 50% by weight or more. In the monomer component constituting the polylactic acid polymer, the proportion of the D-lactic acid component in the total lactic acid component is 4 to 15% by weight, Serial content of the resin other than the polylactic acid polymer is from 70 to 100 wt%, the maximum heat shrinkage rate in the main orientation direction in 75 ° C. hot water 7-40% / sec, further 90 ° C., 10 A shrink label having a heat shrinkage rate in the main orientation direction in seconds of 40 to 84% is provided.

さらに、本発明は、シュリンクフィルムが、A層の両側にB層を、若しくはB層の両側にA層を有する積層シュリンクフィルムである前記のシュリンクラベルを提供する。   Furthermore, the present invention provides the aforementioned shrink label, wherein the shrink film is a laminated shrink film having a B layer on both sides of the A layer or an A layer on both sides of the B layer.

また、本発明は、ポリ乳酸系重合体を必須成分とするフィルム層(A層)を少なくとも1層有するシュリンクフィルム及び印刷層を有するシュリンクラベルであって、前記シュリンクフィルムが、前記A層の単層シュリンクフィルムであり、前記A層中の前記ポリ乳酸系重合体の含有量が50重量%以上であり、前記A層が、さらに、ポリスチレン系樹脂及び芳香族ポリエステル系樹脂からなる群より選ばれたポリ乳酸系重合体以外の樹脂を10〜50重量%含み、前記ポリ乳酸系重合体を構成する単量体成分における、全乳酸成分に占めるD−乳酸成分の割合が5重量%以下であり、前記芳香族ポリエステル系樹脂に用いられる全ジカルボン酸成分中における芳香族ジカルボン酸成分の含有量が60モル%以上であり、75℃温水中での熱収縮開始1秒後における主配向方向の熱収縮率が3〜23%、さらに90℃、10秒における主配向方向の熱収縮率が40〜84%であることを特徴とするシュリンクラベルを提供する。 The present invention also relates to a shrink label having at least one film layer (A layer) comprising a polylactic acid polymer as an essential component and a printed layer, wherein the shrink film is a single layer of the A layer. It is a layer shrink film, the content of the polylactic acid polymer in the layer A is 50% by weight or more, and the layer A is further selected from the group consisting of a polystyrene resin and an aromatic polyester resin. 10% to 50% by weight of a resin other than the polylactic acid polymer, and the proportion of the D-lactic acid component in the total lactic acid component in the monomer component constituting the polylactic acid polymer is 5% by weight or less. The content of the aromatic dicarboxylic acid component in the total dicarboxylic acid component used in the aromatic polyester resin is 60 mol% or more, and heat in 75 ° C. warm water There is provided a shrink label characterized in that the heat shrinkage rate in the main alignment direction at 1 second after the start of shrinkage is 3 to 23%, and further at 90 ° C., the heat shrinkage rate in the main alignment direction at 10 seconds is 40 to 84%. .

また、本発明は、ポリ乳酸系重合体を必須成分とするフィルム層(A層)を少なくとも1層有するシュリンクフィルム及び印刷層を有するシュリンクラベルであって、前記シュリンクフィルムが、前記A層の単層シュリンクフィルムであり、前記A層中の前記ポリ乳酸系重合体の含有量が50重量%以上であり、前記A層が、さらに、ポリスチレン系樹脂及び芳香族ポリエステル系樹脂からなる群より選ばれたポリ乳酸系重合体以外の樹脂を10〜50重量%含み、前記ポリ乳酸系重合体を構成する単量体成分における、全乳酸成分に占めるD−乳酸成分の割合が5重量%以下であり、前記芳香族ポリエステル系樹脂に用いられる全ジカルボン酸成分中における芳香族ジカルボン酸成分の含有量が60モル%以上であり、75℃温水中での主配向方向の最大熱収縮速度が7〜40%/秒であり、さらに90℃、10秒における主配向方向の熱収縮率が40〜84%であることを特徴とするシュリンクラベルを提供する。
The present invention also relates to a shrink label having at least one film layer (A layer) comprising a polylactic acid polymer as an essential component and a printed layer, wherein the shrink film is a single layer of the A layer. It is a layer shrink film, the content of the polylactic acid polymer in the layer A is 50% by weight or more, and the layer A is further selected from the group consisting of a polystyrene resin and an aromatic polyester resin. 10% to 50% by weight of a resin other than the polylactic acid polymer, and the proportion of the D-lactic acid component in the total lactic acid component in the monomer component constituting the polylactic acid polymer is 5% by weight or less. The content of the aromatic dicarboxylic acid component in the total dicarboxylic acid component used in the aromatic polyester resin is 60 mol% or more, The shrink label is characterized in that the maximum heat shrinkage rate in the alignment direction is 7 to 40% / second, and the heat shrinkage rate in the main alignment direction at 90 ° C. for 10 seconds is 40 to 84%.

本発明のシュリンクラベルは、植物由来原料であるポリ乳酸系重合体を必須成分として用いることにより環境負荷が少ない。また、熱収縮速度をある特定の範囲に制御することで、シュリンク加工に際して「しわ」や「印刷の歪み」などの問題を生じにくく、生産効率、仕上がり性が向上する。このため、本発明のシュリンクラベルはPETボトルなどのプラスチック容器等に用いられるラベル用途として特に有用である。   The shrink label of this invention has little environmental impact by using the polylactic acid-type polymer which is a plant-derived raw material as an essential component. Further, by controlling the heat shrinkage rate within a certain range, problems such as “wrinkles” and “printing distortion” are less likely to occur during shrink processing, and production efficiency and finish are improved. For this reason, the shrink label of the present invention is particularly useful as a label for use in plastic containers such as PET bottles.

以下に、本発明のシュリンクラベルについて、さらに詳細に説明する。   Below, the shrink label of this invention is demonstrated in detail.

本発明のシュリンクラベルは、シュリンクフィルム及び印刷層を必須の構成成分としてなる。   The shrink label of the present invention comprises a shrink film and a printing layer as essential constituent components.

本発明のシュリンクフィルムはポリ乳酸系重合体を必須の成分とするフィルム層(以下、A層という)を少なくとも1層有していれば良くA層の単層フィルムであっても良い。また、A層とポリ乳酸系重合体以外の樹脂を主成分とするフィルム層(以下、B層という)を少なくとも1層ずつ有する積層フィルムであっても良い。   The shrink film of the present invention only needs to have at least one film layer (hereinafter referred to as A layer) containing a polylactic acid polymer as an essential component, and may be a single layer film of A layer. Moreover, the laminated film which has at least 1 layer of film layers (henceforth B layer) which has resin other than A layer and polylactic acid-type polymer as a main component may be sufficient.

本発明のシュリンクフィルムが積層フィルムである場合、その積層方法としては、公知の方法を用いることが可能で特に限定されないが、例えば、共押出、接着層を介した接着、ドライラミネート、溶融押出ラミネートなどが挙げられる。中でも、熱収縮加工の仕上がり性の観点から、共押出が好ましい。積層構成としては、特に限定されないが、A/Bの2種2層構成やB/A/B、A/B/Aの2種3層構成が好ましく、熱収縮加工性、フィルムの化学的安定性(耐候性、耐加水分解性等)の観点から、特に好ましくはB/A/Bの2種3層構成である。なお、3層構成とする場合の2つのA層、若しくは2つのB層は、全く同じフィルム層であってもよいが、同種の樹脂を主成分としておれば異なる組成であってもよく、フィルム層厚みが異なっていてもよい。さらに、本発明の効果が損なわれない範囲で、これらのフィルム層は接着層を介して積層されていてもよい(例えば、B層/接着層/A層/接着層/B層の3種5層構成など)。また、A層、B層以外の他のフィルム層を有していてもよい。   When the shrink film of the present invention is a laminated film, a known method can be used as the laminating method, and for example, coextrusion, adhesion via an adhesive layer, dry lamination, melt extrusion lamination are possible. Etc. Of these, coextrusion is preferred from the viewpoint of the finish of heat shrink processing. The laminated structure is not particularly limited, but an A / B two-type two-layer structure or a B / A / B or A / B / A two-type three-layer structure is preferable, and heat shrink processability, chemical stability of the film. From the viewpoint of properties (weather resistance, hydrolysis resistance, etc.), a B / A / B type of two-layer structure is particularly preferable. The two A layers or the two B layers in the case of a three-layer structure may be the same film layer, but may have different compositions as long as the same kind of resin is a main component. The layer thickness may be different. Furthermore, as long as the effect of the present invention is not impaired, these film layers may be laminated via an adhesive layer (for example, B layer / adhesive layer / A layer / adhesive layer / B layer 3 type 5) Layer structure). Moreover, you may have other film layers other than A layer and B layer.

本発明のシュリンクフィルムは、少なくとも1方向に配向している。A層、B層を有する積層構成の場合には、フィルム中のA層、B層の少なくとも1層ずつが同方向に配向している。A層、B層のどちらか一方だけが配向している場合やフィルム中の全ての層が無配向の場合には、良好な熱収縮性を得ることができない。中でも、すべてのフィルム層が配向していることが特に好ましい。配向は1軸配向、2軸配向の何れでも良く特に限定されない。2軸配向にあっては、主にラベル用として用いられるフィルムはフィルムの長手方向又は幅方向のどちらか一方向に大きく配向しているフィルムが一般的に使用される。そのようなフィルムは、フィルム幅方向(ラベルを筒状にした場合に周方向となる方向)により強く配向しても良いし、また、フィルムの長手方向(幅方向と直行する方向)により強く配向していても良い。フィルムが筒状シュリンクラベルとして使用される時は前者の方が好ましい。   The shrink film of the present invention is oriented in at least one direction. In the case of a laminated structure having an A layer and a B layer, at least one of the A layer and the B layer in the film is oriented in the same direction. When only one of the A layer and the B layer is oriented, or when all the layers in the film are non-oriented, good heat shrinkability cannot be obtained. Among them, it is particularly preferable that all the film layers are oriented. The orientation may be either uniaxial orientation or biaxial orientation and is not particularly limited. In the biaxial orientation, the film mainly used for labeling is generally a film that is largely oriented in either the longitudinal direction or the width direction of the film. Such a film may be oriented more strongly in the film width direction (the direction that becomes the circumferential direction when the label is made cylindrical), or more strongly oriented in the longitudinal direction of the film (the direction perpendicular to the width direction). You may do it. The former is preferred when the film is used as a cylindrical shrink label.

本発明のA層は、ポリ乳酸系重合体を必須の成分とするフィルム層である。A層はポリ乳酸系重合体のみから構成されていてもよいが、他の樹脂を含む組成物であってもよく、シュリンク加工時の熱収縮速度の調整、層間の接着性向上、或いは回収原料を使用する観点から、ポリエステル系樹脂、ポリスチレン系樹脂、ポリオレフィン系樹脂などのB層の主成分として用いられる樹脂を含んでいてもよい。また、その他の添加剤を含んでいてもよい。   The A layer of the present invention is a film layer containing a polylactic acid polymer as an essential component. Layer A may be composed of only a polylactic acid polymer, but may be a composition containing other resins, adjustment of heat shrinkage rate during shrink processing, improvement of adhesion between layers, or recovered material From the viewpoint of using, a resin used as a main component of the B layer such as a polyester resin, a polystyrene resin, or a polyolefin resin may be included. Moreover, the other additive may be included.

本発明のA層に用いられるポリ乳酸系重合体は、乳酸を単量体成分とする重合体を意味するが、乳酸は光学異性体を有しポリマーを構成する光学異性体の組成比(D体とL体の含有率比)によって重合体の物性が変化する。例えば、L体に対するD体の割合を少なくすると、熱収縮速度を遅くできるが、樹脂の結晶化度が上昇し、フィルムの剛性が必要以上に高くなり、フィルムの触感が悪くなる、衝撃特性や耐寒性が低下するなどの欠点が生じてくる。市販のポリ乳酸系重合体には、例えば、全乳酸成分の内D−乳酸が1〜2重量%程度、4〜5重量%程度、或いは、10〜15重量%程度占めるものなどがあるが、本発明はそれらを区別せず総てを対象とする。中でも、本発明に用いられるシュリンクフィルムが単層である場合には、熱収縮速度を遅くする観点がより重要となるため、ポリ乳酸系重合体としては、全乳酸成分に占めるD−乳酸成分の割合が5重量%以下のものを用いることが好ましい。一方、本発明に用いられるシュリンクフィルムが積層フィルムである場合には、B層による熱収縮速度を遅くする効果が加わるため、単層の場合と比べて、剛性などの観点をより重視することが可能となる。このため、ポリ乳酸系重合体としては、上記フィルムの剛性という観点から、全乳酸成分に占めるD−乳酸成分の割合が4〜15重量%程度のものが好ましく、より好ましくは7〜15重量%、更に好ましくは10〜15重量%である。また、本発明のA層に用いられるポリ乳酸系重合体は、乳酸と他のヒドロキシカルボン酸又はラクトン類との共重合体、或いは乳酸と他のジカルボン酸類、及び/又は、ジオール類との共重合体も含まれる。他のヒドロキシカルボン酸として、例えば、グリコール酸、2−メチル乳酸、2−ヒドロキシ酪酸、3−ヒドロキシ酪酸、4−ヒドロキシ酪酸、2−ヒドロキシ−3−メチル酪酸、2−ヒドロキシ−3,3−ジメチル酪酸、2−ヒドロキシカプロン酸などが挙げられる。ラクトン類としては、例えば、γ−ブチロラクトン、δ−バレロラクトン、ε−カプロラクトンなどが例示される。また、ジカルボン酸としては、各種の脂肪族(飽和及び不飽和)ジカルボン酸、脂環式ジカルボン酸、芳香族ジカルボン酸などが挙げられる。ジオール成分としては、各種の脂肪族ジオールの他脂環式ジオールなどが例示される。   The polylactic acid polymer used in the A layer of the present invention means a polymer containing lactic acid as a monomer component, and lactic acid has an optical isomer and the composition ratio of optical isomers constituting the polymer (D The physical properties of the polymer change depending on the content ratio of the body and the L body. For example, if the ratio of D body to L body is reduced, the heat shrinkage rate can be slowed, but the crystallinity of the resin increases, the rigidity of the film becomes higher than necessary, and the tactile feeling of the film deteriorates. Disadvantages such as reduced cold resistance occur. Commercially available polylactic acid-based polymers include, for example, those in which D-lactic acid accounts for about 1-2% by weight, about 4-5% by weight, or about 10-15% by weight of the total lactic acid component. The present invention covers all of them without distinguishing them. Among these, when the shrink film used in the present invention is a single layer, the viewpoint of slowing the heat shrinkage rate becomes more important. Therefore, as a polylactic acid polymer, the D-lactic acid component occupies the total lactic acid component. It is preferable to use a ratio of 5% by weight or less. On the other hand, when the shrink film used in the present invention is a laminated film, the effect of slowing the heat shrinkage rate by the B layer is added, and therefore, it is more important to consider the viewpoint of rigidity as compared with the case of a single layer. It becomes possible. For this reason, from the viewpoint of the rigidity of the film, the polylactic acid polymer preferably has a D-lactic acid component ratio of about 4 to 15% by weight, more preferably 7 to 15% by weight, based on the total lactic acid component. More preferably, it is 10 to 15% by weight. In addition, the polylactic acid-based polymer used in the A layer of the present invention is a copolymer of lactic acid and other hydroxycarboxylic acid or lactone, or a copolymer of lactic acid with other dicarboxylic acids and / or diols. Polymers are also included. Other hydroxycarboxylic acids include, for example, glycolic acid, 2-methyllactic acid, 2-hydroxybutyric acid, 3-hydroxybutyric acid, 4-hydroxybutyric acid, 2-hydroxy-3-methylbutyric acid, 2-hydroxy-3,3-dimethyl Examples include butyric acid and 2-hydroxycaproic acid. Examples of lactones include γ-butyrolactone, δ-valerolactone, and ε-caprolactone. Examples of the dicarboxylic acid include various aliphatic (saturated and unsaturated) dicarboxylic acids, alicyclic dicarboxylic acids, and aromatic dicarboxylic acids. Examples of the diol component include various aliphatic diols and alicyclic diols.

ここで例示されたヒドロキシカルボン酸類、ラクトン類、ジカルボン酸、或いはジオール類は乳酸とモノマー状態で混合され、ランダム共重合体としてポリマー中に導かれても良いし、事前にポリエステルとして重合されたオリゴマー、或いはプレポリマーとして乳酸とブロック共重合体を形成する形でポリマー中に導かれても良い。   The hydroxycarboxylic acids, lactones, dicarboxylic acids or diols exemplified here may be mixed with lactic acid in the monomer state and introduced into the polymer as a random copolymer, or an oligomer previously polymerized as a polyester. Alternatively, it may be introduced into the polymer in the form of forming a block copolymer with lactic acid as a prepolymer.

ポリ乳酸系重合体を構成する全単量体に占める乳酸の割合は、フィルムが単独材料からなるA層単層で構成される場合は、一般に20モル%以上、好ましくは35モル%以上、更に好ましくは50モル%以上、特に生分解性の観点からすれば65モル%以上のものが好ましい。フィルムがA層とB層が組み合わされた多層フィルムの場合、A層のポリ乳酸系重合体を構成する全単量体に占める乳酸の割合は、一般に50モル%以上、好ましくは65モル%以上、さらに好ましくは80モル%以上であり、特に95モル%以上(例えば100モル%)のものが好ましい。ポリ乳酸系重合体は単独で又は2種以上を混合して用いてもよい。例えば、L−乳酸とD−乳酸との比率が異なるポリ乳酸系重合体を2種以上組み合わせて用いることができる。   The proportion of lactic acid in all monomers constituting the polylactic acid polymer is generally 20 mol% or more, preferably 35 mol% or more when the film is composed of a single layer A composed of a single material. Preferably it is 50 mol% or more, and particularly from the viewpoint of biodegradability, 65 mol% or more is preferred. When the film is a multilayer film in which the A layer and the B layer are combined, the proportion of lactic acid in the total monomers constituting the polylactic acid polymer of the A layer is generally 50 mol% or more, preferably 65 mol% or more. More preferably, it is at least 80 mol%, particularly preferably at least 95 mol% (for example, 100 mol%). Polylactic acid polymers may be used alone or in admixture of two or more. For example, two or more polylactic acid polymers having different ratios of L-lactic acid and D-lactic acid can be used in combination.

ポリ乳酸系重合体を得る方法としては、特に限定されず、縮重合法、開環重合法等の公知の方法を採用できる。例えば、縮重合法では、乳酸、又は乳酸と他の単量体成分とを直接脱水縮合することにより任意の組成を有するポリ乳酸系重合体を得ることができる。また、開環重合法では、乳酸の環状2量体であるラクチドを、適当な触媒の存在下で重合させることにより任意の組成のポリ乳酸系重合体を得ることができる。   The method for obtaining the polylactic acid polymer is not particularly limited, and known methods such as a condensation polymerization method and a ring-opening polymerization method can be employed. For example, in the polycondensation method, lactic acid or a polylactic acid polymer having an arbitrary composition can be obtained by directly dehydrating condensation of lactic acid and other monomer components. In the ring-opening polymerization method, lactide, which is a cyclic dimer of lactic acid, is polymerized in the presence of a suitable catalyst to obtain a polylactic acid polymer having an arbitrary composition.

ポリ乳酸系重合体の数平均分子量は、特に限定されないが、通常1万〜100万、好ましくは3万〜40万程度、より好ましくは5万〜20万程度である。分子量が小さすぎると引っ張り破断伸度、引き裂き強度、衝撃強度などフィルムとしての機械物性や耐候性耐熱性などの長期物性に劣り、分子量が大きすぎると成形加工性が低下する。   The number average molecular weight of the polylactic acid polymer is not particularly limited, but is usually 10,000 to 1,000,000, preferably about 30,000 to 400,000, and more preferably about 50,000 to 200,000. If the molecular weight is too small, the mechanical properties as a film, such as tensile elongation at break, tear strength, and impact strength, and long-term physical properties such as weather resistance and heat resistance are inferior. If the molecular weight is too large, molding processability decreases.

本発明のA層中におけるポリ乳酸系重合体の含有量は、熱収縮速度を本発明の範囲に制御する観点から、50〜100重量%が好ましく、より好ましくは60〜100重量%、さらに好ましくは70〜100%である。   The content of the polylactic acid polymer in the layer A of the present invention is preferably 50 to 100% by weight, more preferably 60 to 100% by weight, and still more preferably, from the viewpoint of controlling the heat shrinkage rate within the range of the present invention. Is 70 to 100%.

本発明のA層には、上記ポリ乳酸系重合体以外の樹脂が含まれていてもよい。A層に含まれるポリ乳酸系重合体以外の樹脂としては、特に限定されないが、例えば、脂肪族ポリエステル系樹脂、芳香族ポリエステル系樹脂などのポリエステル系樹脂(上記ポリ乳酸系重合体に該当するポリエステル系樹脂は除く)、ポリスチレン系樹脂が好ましく例示される。中でも、本発明に用いられるシュリンクフィルムがA層のみからなる単層フィルムの場合には、シュリンク加工時の熱収縮特性を調整する観点から、ポリスチレン系樹脂、脂肪族ポリエステル系樹脂、芳香族ポリエステル系樹脂が好ましく、圧縮強度の観点から、特に好ましくはポリスチレン系樹脂、芳香族ポリエステル系樹脂である。一方、本発明に用いられるシュリンクフィルムがB層を有する積層フィルムの場合には、透明性の観点から、脂肪族ポリエステル系樹脂が好ましい。   Resin other than the said polylactic acid-type polymer may be contained in A layer of this invention. The resin other than the polylactic acid polymer contained in the A layer is not particularly limited. For example, a polyester resin such as an aliphatic polyester resin or an aromatic polyester resin (polyester corresponding to the above polylactic acid polymer). And polystyrene resins are preferred. Among them, in the case where the shrink film used in the present invention is a single layer film composed of only the A layer, from the viewpoint of adjusting the heat shrinkage characteristics during shrink processing, a polystyrene-based resin, an aliphatic polyester-based resin, an aromatic polyester-based film Resins are preferable, and from the viewpoint of compressive strength, polystyrene resins and aromatic polyester resins are particularly preferable. On the other hand, when the shrink film used in the present invention is a laminated film having a B layer, an aliphatic polyester resin is preferable from the viewpoint of transparency.

上記脂肪族ポリエステル系樹脂は、脂肪族又は脂環式ジオール成分と脂肪族又は脂環式ジカルボン酸成分との縮重合、脂肪族又は脂環式ヒドロキシカルボン酸の縮重合、ラクトン類の開環重合、又はこれらの組み合わせにより製造される。各単量体成分は複数種組み合わせて用いることもできる。脂肪族又は脂環式ジオール成分としては、例えば、エチレングリコール、1,3−プロパンジオール、プロピレングリコール、2,2−ジメチル−1,3−プロパンジオール、1,4−ブタンジオール、1,6−ヘキサンジオールなどの脂肪族ジオール;ジエチレングリコールなどのポリアルキレングリコール;1,2−シクロヘキサンジメタノール、1,3−シクロヘキサンジメタノール、1,4−シクロヘキサンジメタノールなどの脂環式ジオールなどが例示される。脂肪族又は脂環式ジカルボン酸成分としては、例えば、コハク酸、グルタル酸、アジピン酸、ピメリン酸、スベリン酸、アゼライン酸、セバシン酸、ドデカン二酸などの脂肪族ジカルボン酸;1,4−デカヒドロナフタレンジカルボン酸、1,4−シクロヘキサンジカルボン酸、1,3−シクロヘキサンジカルボン酸などの脂環式ジカルボン酸などが挙げられる。脂肪族又は脂環式ヒドロキシカルボン酸及びラクトン類としては、前記例示のものを使用できる。   The aliphatic polyester-based resin is a polycondensation of an aliphatic or alicyclic diol component and an aliphatic or alicyclic dicarboxylic acid component, a polycondensation of an aliphatic or alicyclic hydroxycarboxylic acid, or a ring-opening polymerization of lactones. Or a combination thereof. Each monomer component can be used in combination. Examples of the aliphatic or alicyclic diol component include ethylene glycol, 1,3-propanediol, propylene glycol, 2,2-dimethyl-1,3-propanediol, 1,4-butanediol, 1,6- Examples include aliphatic diols such as hexanediol; polyalkylene glycols such as diethylene glycol; alicyclic diols such as 1,2-cyclohexanedimethanol, 1,3-cyclohexanedimethanol, and 1,4-cyclohexanedimethanol. Examples of the aliphatic or alicyclic dicarboxylic acid component include aliphatic dicarboxylic acids such as succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, and dodecanedioic acid; And alicyclic dicarboxylic acids such as hydronaphthalenedicarboxylic acid, 1,4-cyclohexanedicarboxylic acid, and 1,3-cyclohexanedicarboxylic acid. As the aliphatic or alicyclic hydroxycarboxylic acid and lactone, those exemplified above can be used.

上記の脂肪族ポリエステル系樹脂においては、脂肪族又は脂環式ジカルボン酸成分の一部(例えば0.1〜50モル%程度、好ましくは0.1〜20モル%)を芳香族ジカルボン酸成分で置き換えてもよい。このようにして得られるポリエステル(芳香族脂肪族ポリエステル)をポリ乳酸系重合体に添加して得られるフィルムは、耐衝撃性に特に優れ、熱収縮させた後にも破断しにくいという特徴を有する。前記芳香族ジカルボン酸としては、例えば、イソフタル酸、テレフタル酸、2,6−ナフタレンジカルボン酸、4,4’−ビフェニルジカルボン酸などが挙げられる。これらは単独で又は2種以上混合して使用できる。   In the above aliphatic polyester resin, a part of the aliphatic or alicyclic dicarboxylic acid component (for example, about 0.1 to 50 mol%, preferably 0.1 to 20 mol%) is an aromatic dicarboxylic acid component. It may be replaced. The film obtained by adding the polyester (aromatic aliphatic polyester) thus obtained to the polylactic acid polymer is particularly excellent in impact resistance and has a characteristic that it is not easily broken even after being thermally contracted. Examples of the aromatic dicarboxylic acid include isophthalic acid, terephthalic acid, 2,6-naphthalenedicarboxylic acid, and 4,4′-biphenyldicarboxylic acid. These can be used alone or in admixture of two or more.

前記脂肪族ポリエステル系樹脂の代表的な例として、ポリブチレンサクシネート(PBS)、ポリエチレンサクシネート(PES)、ポリブチレンサクシネートアジペート(PBSA)、ポリカプロラクトン(PCL)、ポリヒドロキシ酪酸、ポリエチレンテレフタレートサクシネート(PETS)などが挙げられる。中でも、PBS、PCL、及びこれらの混合物などが好適に利用される。   Representative examples of the aliphatic polyester resin include polybutylene succinate (PBS), polyethylene succinate (PES), polybutylene succinate adipate (PBSA), polycaprolactone (PCL), polyhydroxybutyric acid, polyethylene terephthalate succinate. Nate (PETS). Among these, PBS, PCL, and a mixture thereof are preferably used.

また、上記ポリスチレン系樹脂、芳香族ポリエステル系樹脂は、B層に用いることができる樹脂として、例示されているポリスチレン系樹脂、芳香族ポリエステル系樹脂の中から選択して用いることができる。   Moreover, the said polystyrene-type resin and aromatic polyester-type resin can be selected and used from the polystyrene-type resin and aromatic polyester-type resin which are illustrated as resin which can be used for B layer.

A層に脂肪族ポリエステル系樹脂、芳香族ポリエステル系樹脂、ポリスチレン系樹脂などのポリ乳酸系重合体以外の樹脂を含有させる場合、A層中の含有量は10〜50重量%が好ましく、より好ましくは20〜40重量%である。脂肪族ポリエステル系樹脂の含有量が50重量%を超える場合には、フィルムが柔らかくなりすぎて熱収縮仕上がり性が低下しやすく、表面がべたついて取扱性に劣る他、透明性が低下しやすい。   When the A layer contains a resin other than a polylactic acid polymer such as an aliphatic polyester resin, an aromatic polyester resin, or a polystyrene resin, the content in the A layer is preferably 10 to 50% by weight, more preferably. Is 20-40% by weight. When the content of the aliphatic polyester resin exceeds 50% by weight, the film becomes too soft and the heat shrink finish is liable to deteriorate, the surface becomes sticky and the handling property is inferior, and the transparency is liable to be lowered.

本発明のA層には、上記以外にも他の樹脂成分、例えば、脂肪族ポリエステルアミド、脂肪族ポリエステルエーテル、脂肪族ポリエステルカーボネートなどの生分解性樹脂などを少量添加してもよい。これらの樹脂は単独で又は2種以上組み合わせて使用できる。   In addition to the above, the A layer of the present invention may contain a small amount of other resin components such as biodegradable resins such as aliphatic polyesteramide, aliphatic polyester ether, and aliphatic polyester carbonate. These resins can be used alone or in combination of two or more.

また、回収原料を再利用してA層に用いる場合、回収原料の含有量は、フィルムの引張伸度特性や透明性の観点から、A層全重量に対して30重量%以下であることが好ましく、より好ましくは10〜30重量%である。なお、本発明に用いられるシュリンクフィルムが積層フィルムである場合、回収原料を添加することによって、B層に用いる樹脂がA層にも含まれることとなるため、A層とB層の層間接着強度が向上するため好ましい。   When the recovered raw material is reused and used in the A layer, the content of the recovered raw material is 30% by weight or less based on the total weight of the A layer from the viewpoint of the tensile elongation characteristics and transparency of the film. Preferably, it is 10 to 30% by weight. In addition, when the shrink film used for this invention is a laminated | multilayer film, since the resin used for B layer is also contained in A layer by adding a collection | recovery raw material, the interlayer adhesive strength of A layer and B layer Is preferable.

本発明のA層樹脂(A層に含まれる全ての樹脂の混合物)のガラス転移温度(Tg)は、加工性の観点から、40〜80℃が好ましく、より好ましくは50〜80℃である。Tgが40℃未満では延伸後のフィルムの自然熱収縮が大きく、また、80℃を超える場合はフィルムの延伸に際して十分の延伸倍率を確保することが難しくなりフィルムの生産性が低下する。   The glass transition temperature (Tg) of the A layer resin of the present invention (a mixture of all resins contained in the A layer) is preferably 40 to 80 ° C, more preferably 50 to 80 ° C, from the viewpoint of processability. When Tg is less than 40 ° C., the natural heat shrinkage of the stretched film is large, and when it exceeds 80 ° C., it is difficult to ensure a sufficient stretch ratio when stretching the film, and the productivity of the film decreases.

本発明のA層は、必要に応じてその他の添加剤、例えば、滑剤、充填剤、熱安定剤、酸化防止剤、紫外線吸収剤、帯電防止剤、難燃剤、着色剤等を含んでいてもよい。   The layer A of the present invention may contain other additives such as a lubricant, a filler, a heat stabilizer, an antioxidant, an ultraviolet absorber, an antistatic agent, a flame retardant, a colorant and the like as necessary. Good.

本発明のシュリンクフィルムが上記A層とポリ乳酸系重合体以外の樹脂を主成分とするフィルム層(B層)の積層フィルムの場合、B層に用いられる樹脂は、シュリンクフィルム全体の熱収縮速度を緩やかに制御する観点から、延伸配向後にA層よりも熱収縮速度が遅いことが好ましい。   In the case where the shrink film of the present invention is a laminated film of a film layer (B layer) whose main component is a resin other than the A layer and the polylactic acid polymer, the resin used for the B layer is the heat shrinkage rate of the entire shrink film. From the viewpoint of slowly controlling the thickness, it is preferable that the heat shrinkage rate is slower than that of the A layer after the stretching orientation.

このようなB層の主成分として用いられる樹脂としては、例えば、ポリスチレン系樹脂、ポリエステル系樹脂、ポリオレフィン系樹脂、ポリ塩化ビニル樹脂、ポリアミド樹脂、ポリイミド樹脂、ポリフェニレンスルフィド樹脂、アクリル樹脂などが挙げられる。中でも、ポリスチレン系樹脂、ポリエステル系樹脂(芳香族ポリエステル系樹脂、脂肪族ポリエステル系樹脂)、ポリオレフィン系樹脂が好ましく、特に好ましくはポリスチレン系樹脂または芳香族ポリエステル系樹脂である。   Examples of the resin used as the main component of the B layer include polystyrene resin, polyester resin, polyolefin resin, polyvinyl chloride resin, polyamide resin, polyimide resin, polyphenylene sulfide resin, and acrylic resin. . Among these, polystyrene resins, polyester resins (aromatic polyester resins, aliphatic polyester resins) and polyolefin resins are preferable, and polystyrene resins or aromatic polyester resins are particularly preferable.

本発明のB層に用いられるポリスチレン系樹脂は、構成モノマーとして、例えば、スチレン、α−メチルスチレン、m−メチルスチレン、p−メチルスチレン、p−エチルスチレン、p−イソブチルスチレン、p−t−ブチルスチレン、クロロメチルスチレン等のスチレン系単量体を1種又は2種以上含み、且つ製膜した際に熱収縮性を示す樹脂であれば特に限定されない。   For example, styrene, α-methyl styrene, m-methyl styrene, p-methyl styrene, p-ethyl styrene, p-isobutyl styrene, pt- The resin is not particularly limited as long as it contains one or more styrene monomers such as butyl styrene and chloromethyl styrene and exhibits heat shrinkability when formed into a film.

このようなポリスチレン系樹脂としては、スチレンの単独重合体である一般ポリスチレン(GPPS)、スチレン系単量体の単独又は共重合体;ポリスチレンと合成ゴム(例えば、ポリブタジエンやポリイソプレン等)の混合物、合成ゴムにスチレンをグラフト重合させた高衝撃性ポリスチレン(HIPS);スチレン−ブタジエン−スチレン(SBS)ブロック共重合体などに代表される、スチレン系単量体とブタジエンやイソプレン等の共役ジエンの共重合体(特に、ブロック共重合体)であるスチレン−共役ジエン共重合体;スチレン系単量体と(メタ)アクリル酸エステル系単量体などの共重合体であるスチレン−重合性不飽和カルボン酸エステル共重合体;スチレン−共役ジエン−重合性不飽和カルボン酸エステル共重合体;スチレン系単量体と(メタ)アクリル酸エステル系単量体との共重合体の連続相中にゴム状弾性体を分散させ、該ゴム状弾性体に前記共重合体をグラフト重合させた透明・高衝撃性ポリスチレン(グラフトTIPS)等が挙げられる。   Examples of such polystyrene resins include general polystyrene (GPPS), which is a homopolymer of styrene, a homopolymer or copolymer of styrene monomers; a mixture of polystyrene and synthetic rubber (for example, polybutadiene or polyisoprene), High impact polystyrene (HIPS) with styrene grafted on synthetic rubber; styrene monomer and conjugated dienes such as butadiene and isoprene, such as styrene-butadiene-styrene (SBS) block copolymer Styrene-conjugated diene copolymer that is a polymer (particularly a block copolymer); Styrene-polymerizable unsaturated carboxylic acid that is a copolymer of a styrene monomer and a (meth) acrylate monomer Acid ester copolymer; styrene-conjugated diene-polymerizable unsaturated carboxylic acid ester copolymer; A rubbery elastic material is dispersed in a continuous phase of a copolymer of a monomer and a (meth) acrylic acid ester monomer, and the copolymer is graft-polymerized on the rubbery elastic material. -High impact polystyrene (graft TIPS) etc. are mentioned.

上記スチレン−共役ジエン共重合体に用いられる共役ジエンとしては、例えば、1,3−ブタジエン、イソプレン(2−メチル−1,3−ブタジエン)、2,3−ジメチル−1,3−ブタジエン、1,3−ペンタジエン、1,3−ヘキサジエン、クロロプレンなどが挙げられる。中でも、特に好ましくは、共役ジエンとして1,3−ブタジエンを用いたスチレン−ブタジエン共重合体である。また、共重合の形態としては、特に限定されないが、ブロック共重合体が好ましく、スチレンブロック(S)−共役ジエンブロック(D)型、S−D−S型、D−S−D型、S−D−S−D型等が挙げられる。また、スチレン−共役ジエン共重合体において、スチレン含有量は55〜95重量%(共役ジエン含有量:5〜45重量%)程度が好ましい。   Examples of the conjugated diene used in the styrene-conjugated diene copolymer include 1,3-butadiene, isoprene (2-methyl-1,3-butadiene), 2,3-dimethyl-1,3-butadiene, and the like. , 3-pentadiene, 1,3-hexadiene, chloroprene and the like. Among these, a styrene-butadiene copolymer using 1,3-butadiene as a conjugated diene is particularly preferable. The form of copolymerization is not particularly limited, but a block copolymer is preferable, and styrene block (S) -conjugated diene block (D) type, SDS type, DSD type, S type. -DSD type etc. are mentioned. In the styrene-conjugated diene copolymer, the styrene content is preferably about 55 to 95% by weight (conjugated diene content: 5 to 45% by weight).

上記スチレン−ブタジエン共重合体としては、スチレン−ブタジエン−スチレン(SBS)ブロック共重合体が好ましい。スチレン−ブタジエンブロック共重合体において、スチレン含有量は、65〜90重量%(ブタジエン含有量:10〜35重量%)が好ましく、より好ましくは75〜88重量%(ブタジエン含有量:12〜25重量%)である。また、スチレン−ブタジエンブロック共重合体のメルトフローレート(MFR)(JIS K 7210 :温度200℃/荷重49N)は、1〜20g/10分が好ましく、より好ましくは3〜10g/10分である。スチレン−ブタジエンブロック共重合体は、旭化成ケミカルズ(株)製「アサフレックス」、フィリップス(株)製「K−レジン」等が市場で入手可能である。   As the styrene-butadiene copolymer, a styrene-butadiene-styrene (SBS) block copolymer is preferable. In the styrene-butadiene block copolymer, the styrene content is preferably 65 to 90% by weight (butadiene content: 10 to 35% by weight), more preferably 75 to 88% by weight (butadiene content: 12 to 25% by weight). %). The melt flow rate (MFR) (JIS K 7210: temperature 200 ° C./load 49 N) of the styrene-butadiene block copolymer is preferably 1 to 20 g / 10 minutes, more preferably 3 to 10 g / 10 minutes. . As the styrene-butadiene block copolymer, “Asaflex” manufactured by Asahi Kasei Chemicals Corporation, “K-resin” manufactured by Philips Co., Ltd., and the like are available on the market.

上記スチレン−重合性不飽和カルボン酸エステル共重合体に用いられる重合性不飽和カルボン酸エステルとしては、例えば、(メタ)アクリル酸メチル、(メタ)アクリル酸エチル、(メタ)アクリル酸ブチル、(メタ)アクリル酸イソブチル、(メタ)アクリル酸2−エチルヘキシル、(メタ)アクリル酸オクチルなどの(メタ)アクリル酸アルキルエステル(特に、(メタ)アクリル酸C1-10アルキルエステル);フマル酸ジメチル、フマル酸ジエチルなどのフマル酸モノ又はジエステル;マレイン酸ジメチル、マレイン酸ジエチルなどのマレイン酸モノ又はジエステル;イタコン酸ジメチル、イタコン酸ジエチルなどのイタコン酸モノ又はジエステルなどが挙げられる。これらの中でも、アクリル酸メチル及びメタクリル酸メチルは透明性に優れているため好ましく用いられる。また、アクリル酸ブチルやメタクリル酸ブチルなどの炭素数4以上(例えば、炭素数4〜10程度)のアルキル基を有する(メタ)アクリル酸アルキルエステルは自然熱収縮率(25〜35℃で保管したときの収縮率)の低減に寄与するため好ましい。これらの重合性不飽和カルボン酸エステルは単独で又は2種以上を混合して使用できる。スチレン−重合性不飽和カルボン酸エステル共重合体中のスチレン含有量は50〜98重量%が好ましい。より好ましくは60〜95重量%、更に好ましくは70〜90従量%である。なお、ここでいう「(メタ)アクリル酸」とは、「アクリル酸及び/又はメタクリル酸」をさす。 Examples of the polymerizable unsaturated carboxylic acid ester used in the styrene-polymerizable unsaturated carboxylic acid ester copolymer include methyl (meth) acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, ( (Meth) acrylic acid alkyl esters (especially (meth) acrylic acid C 1-10 alkyl esters) such as isobutyl acrylate, 2-ethylhexyl (meth) acrylate, octyl (meth) acrylate; dimethyl fumarate, Examples thereof include fumaric acid mono- or diesters such as diethyl fumarate; maleic mono- or diesters such as dimethyl maleate and diethyl maleate; itaconic mono- or diesters such as dimethyl itaconate and diethyl itaconate. Among these, methyl acrylate and methyl methacrylate are preferably used because of excellent transparency. In addition, (meth) acrylic acid alkyl ester having an alkyl group having 4 or more carbon atoms (for example, about 4 to 10 carbon atoms) such as butyl acrylate or butyl methacrylate is stored at a natural heat shrinkage (25 to 35 ° C.). Is preferable because it contributes to a reduction in the shrinkage rate. These polymerizable unsaturated carboxylic acid esters can be used alone or in admixture of two or more. The styrene content in the styrene-polymerizable unsaturated carboxylic acid ester copolymer is preferably 50 to 98% by weight. More preferably, it is 60-95 weight%, More preferably, it is 70-90 weight%. Here, “(meth) acrylic acid” refers to “acrylic acid and / or methacrylic acid”.

上記スチレン−共役ジエン−重合性不飽和カルボン酸エステル共重合体に用いられる共役ジエン、重合性不飽和カルボン酸エステル共重合体は前記の化合物が挙げられる。スチレン−共役ジエン−重合性不飽和カルボン酸エステル共重合体中の、スチレン含有量は50〜98重量%、共役ジエン含有量は1〜45重量%、重合性不飽和カルボン酸エステル共重合体含有量は1〜45重量%が好ましい。より好ましくはスチレン含有量が60〜90重量%、共役ジエン含有量が5〜35重量%、重合性不飽和カルボン酸エステル共重合体含有量5〜35重量%であり、更に好ましくはスチレン含有量が65〜80重量%、共役ジエン含有が5〜25重量%、重合性不飽和カルボン酸エステル共重合体含有量が5〜25重量%である。   Examples of the conjugated diene and polymerizable unsaturated carboxylic acid ester copolymer used in the styrene-conjugated diene-polymerizable unsaturated carboxylic acid ester copolymer include the compounds described above. In the styrene-conjugated diene-polymerizable unsaturated carboxylic acid ester copolymer, the styrene content is 50 to 98% by weight, the conjugated diene content is 1 to 45% by weight, and the polymerizable unsaturated carboxylic acid ester copolymer is contained. The amount is preferably 1 to 45% by weight. More preferably, the styrene content is 60 to 90% by weight, the conjugated diene content is 5 to 35% by weight, the polymerizable unsaturated carboxylic acid ester copolymer content is 5 to 35% by weight, and still more preferably the styrene content. Is 65 to 80% by weight, conjugated diene content is 5 to 25% by weight, and polymerizable unsaturated carboxylic acid ester copolymer content is 5 to 25% by weight.

本発明のB層に用いられるポリスチレン系樹脂としては、上記の中でも、SBSなどのスチレン−ブタジエンブロック共重合体やスチレン−ブタジエン−イソプレン共重合体(SBIS)が特に好ましい。   Among the above, the polystyrene resin used for the B layer of the present invention is particularly preferably a styrene-butadiene block copolymer such as SBS or a styrene-butadiene-isoprene copolymer (SBIS).

本発明のB層に用いられるポリエステル系樹脂は、上記ポリ乳酸重合体を除くポリエステル系樹脂である。上記に示したような脂肪族ポリエステル系樹脂であっても、芳香族ポリエステル系樹脂であってもよいが、好ましくは芳香族ポリエステル系樹脂である。   The polyester resin used in the B layer of the present invention is a polyester resin excluding the polylactic acid polymer. Although it may be an aliphatic polyester-based resin as described above or an aromatic polyester-based resin, it is preferably an aromatic polyester-based resin.

本発明のB層に用いられる芳香族ポリエステル系樹脂は、芳香環を構造単位に含むポリエステルであり、主なものとしては、芳香族ジカルボン酸を含むジカルボン酸とジオールの縮合反応による重合体、共重合体またはこれらの混合物が挙げられる。特にジカルボン酸成分のうち50モル%を超える成分が芳香族ジカルボン酸であるポリエステルが挙げられる。   The aromatic polyester-based resin used in the B layer of the present invention is a polyester containing an aromatic ring as a structural unit. Mainly, the aromatic polyester-based resin is a polymer obtained by a condensation reaction of a dicarboxylic acid containing an aromatic dicarboxylic acid and a diol, A polymer or a mixture thereof may be mentioned. In particular, polyesters in which the component exceeding 50 mol% of the dicarboxylic acid component is an aromatic dicarboxylic acid can be mentioned.

上記芳香族ジカルボン酸成分としては、テレフタル酸、イソフタル酸、フタル酸、2,5−ジメチルテレフタル酸、5−t−ブチルイソフタル酸、4,4’−ビフェニルジカルボン酸、トランス−3,3’−スチルベンジカルボン酸、トランス−4,4’−スチルベンジカルボン酸、4,4’−ジベンジルジカルボン酸、1,4−ナフタレンジカルボン酸、1,5−ナフタレンジカルボン酸、2,3−ナフタレンジカルボン酸、2,6−ナフタレンジカルボン酸、2,7−ナフタレンジカルボン酸、2,2,6,6−テトラメチルビフェニル−4,4’−ジカルボン酸、1,1,3−トリメチル−3−フェニルインデン−4,5−ジカルボン酸、1,2−ジフェノキシエタン−4,4’−ジカルボン酸、ジフェニルエーテルジカルボン酸、2,5−アントラセンジカルボン酸、2,5−ピリジンジカルボン酸及びこれらの置換体などが挙げられる。中でも、生産性、加工性、コスト等の観点から、テレフタル酸、イソフタル酸、2,7−ナフタレンジカルボン酸が好ましく、特に好ましくはテレフタル酸である。また、これら芳香族ジカルボン酸に追加して、例えば、コハク酸、グルタル酸、アジピン酸、ピメリン酸、スベリン酸、アゼライン酸、セバシン酸、ドデカン二酸などの脂肪族ジカルボン酸、また、1,4−デカヒドロナフタレンジカルボン酸、1,4−シクロヘキサンジカルボン酸、1,3−シクロヘキサンジカルボン酸などの脂環式ジカルボン酸などを共重合させても良い。これらを共重合することにより、結晶化度が低下し、分子組織の滑りが起こりやすくなるためと考えられるが、シュリンク特性が向上する。なお、上記ジカルボン酸は、それぞれ単独で又は2種以上混合して使用できる。耐熱性や熱収縮特性の観点から、芳香族ポリエステル系樹脂に用いられる全ジカルボン酸成分中における上記芳香族ジカルボン酸成分の含有量は、60モル%以上が好ましく、より好ましくは70モル%以上、更に好ましくは80モル%以上である。   Examples of the aromatic dicarboxylic acid component include terephthalic acid, isophthalic acid, phthalic acid, 2,5-dimethylterephthalic acid, 5-t-butylisophthalic acid, 4,4′-biphenyldicarboxylic acid, trans-3,3′- Stilbene dicarboxylic acid, trans-4,4′-stilbene dicarboxylic acid, 4,4′-dibenzyldicarboxylic acid, 1,4-naphthalenedicarboxylic acid, 1,5-naphthalenedicarboxylic acid, 2,3-naphthalenedicarboxylic acid, 2 , 6-Naphthalenedicarboxylic acid, 2,7-naphthalenedicarboxylic acid, 2,2,6,6-tetramethylbiphenyl-4,4′-dicarboxylic acid, 1,1,3-trimethyl-3-phenylindene-4, 5-dicarboxylic acid, 1,2-diphenoxyethane-4,4′-dicarboxylic acid, diphenyl ether dicarboxylic acid, 2 5-anthracene dicarboxylic acid, 2,5-pyridinedicarboxylic acid and substituted products thereof. Among these, terephthalic acid, isophthalic acid, and 2,7-naphthalenedicarboxylic acid are preferable from the viewpoint of productivity, processability, cost, and the like, and terephthalic acid is particularly preferable. In addition to these aromatic dicarboxylic acids, for example, aliphatic dicarboxylic acids such as succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, dodecanedioic acid, and 1,4 -An alicyclic dicarboxylic acid such as decahydronaphthalenedicarboxylic acid, 1,4-cyclohexanedicarboxylic acid, 1,3-cyclohexanedicarboxylic acid or the like may be copolymerized. By copolymerizing these, it is considered that the degree of crystallinity decreases and the slip of the molecular structure is likely to occur, but the shrink characteristics are improved. In addition, the said dicarboxylic acid can be used individually or in mixture of 2 or more types, respectively. From the viewpoint of heat resistance and heat shrinkage properties, the content of the aromatic dicarboxylic acid component in the total dicarboxylic acid component used in the aromatic polyester resin is preferably 60 mol% or more, more preferably 70 mol% or more, More preferably, it is 80 mol% or more.

上記ジオール成分としては、エチレングリコール、1,2−プロパンジオール、1,3−プロパンジオール、2,2−ジメチル−1,3−プロパンジオール(ネオペンチルグリコール)、1,3−ブタンジオール、1,4−ブタンジオール、1,5−ペンタンジオール、1,6−ヘキサンジオール、1,7−ヘプタンジオール、2−エチル−2−メチル−1,3−プロパンジオール、2,2−ジエチル−1,3−プロパンジオール、1,8−オクタンジオール、2−エチル−2−ブチル−1,3−プロパンジオール、2−エチル−2,4−ジメチル−1,3−ヘキサンジオール、1,10−デカンジオールなどの脂肪族ジオール、ジエチレングリコール、トリエチレングリコールなどのポリアルキレングリコール、1,2−シクロヘキサンジメタノール、1,3−シクロヘキサンジメタノール、1,4−シクロヘキサンジメタノール、2,2,4,4−テトラメチル−1,3−シクロブタンジオールなどの脂環式ジオール、2,2−ビス(4’−β−ヒドロキシエトキシジフェニル)プロパン、ビス(4’−β−ヒドロキシエトキシフェニル)スルホン等のビスフェノール系化合物のエチレンオキシド付加物、キシリレングリコール等の芳香族ジオールなどが挙げられる。中でも、エチレングリコール、1,4−シクロヘキサンジメタノール、1,2−シクロヘキサンジメタノールが好ましい。なお、これらは単独で又は2種以上混合して使用できる。   Examples of the diol component include ethylene glycol, 1,2-propanediol, 1,3-propanediol, 2,2-dimethyl-1,3-propanediol (neopentyl glycol), 1,3-butanediol, 1, 4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,7-heptanediol, 2-ethyl-2-methyl-1,3-propanediol, 2,2-diethyl-1,3 -Propanediol, 1,8-octanediol, 2-ethyl-2-butyl-1,3-propanediol, 2-ethyl-2,4-dimethyl-1,3-hexanediol, 1,10-decanediol, etc. Aliphatic diols, polyalkylene glycols such as diethylene glycol and triethylene glycol, 1,2-cyclohexanedi Alicyclic diols such as butanol, 1,3-cyclohexanedimethanol, 1,4-cyclohexanedimethanol, 2,2,4,4-tetramethyl-1,3-cyclobutanediol, 2,2-bis (4 ′ Examples thereof include ethylene oxide adducts of bisphenol compounds such as -β-hydroxyethoxydiphenyl) propane and bis (4'-β-hydroxyethoxyphenyl) sulfone, and aromatic diols such as xylylene glycol. Of these, ethylene glycol, 1,4-cyclohexanedimethanol, and 1,2-cyclohexanedimethanol are preferable. In addition, these can be used individually or in mixture of 2 or more types.

また、本発明の芳香族ポリエステル系樹脂には、上記以外にも、p−オキシ安息香酸、p−オキシエトキシ安息香酸等のオキシカルボン酸;安息香酸、ベンゾイル安息香酸等のモノカルボン酸;トリメリット酸等の多価カルボン酸;ポリアルキレングリコールモノメチルエーテル等の1価アルコール;グリセリン、ペンタエリスリトール、トリメチロールプロパン等の多価アルコールなどが、本発明の効果を損なわない範囲内で共重合されていてもよい。   In addition to the above, the aromatic polyester resin of the present invention includes oxycarboxylic acids such as p-oxybenzoic acid and p-oxyethoxybenzoic acid; monocarboxylic acids such as benzoic acid and benzoylbenzoic acid; Polyhydric carboxylic acids such as acids; monohydric alcohols such as polyalkylene glycol monomethyl ether; polyhydric alcohols such as glycerin, pentaerythritol, and trimethylolpropane are copolymerized within a range that does not impair the effects of the present invention. Also good.

本発明のB層に用いられる具体的な芳香族ポリエステル系樹脂としては、特に限定されないが、ジカルボン酸成分としてテレフタル酸を主成分とし、イソフタル酸、アジピン酸、琥珀酸を追加成分として用い、一方、ジオール成分としてエチレングリコールやブタンジオールを主成分として用いることが出来る。例えば、ポリエチレンテレフタレート(PET)、ポリブチレンテレフタレート(PBT)、さらに1,4−シクロヘキサンジメタノール(CHDM)を共重合成分として用いたCHDM共重合PET、その他ジオール成分としてジエチレングリコール(DEG)やネオペンチルグリコール(NPG)を加えたものが、シュリンクフィルムとした際の熱収縮挙動、コスト、生産性、A層との層間強度向上の観点で、特に好ましい。上記CHDMの共重合の割合はエチレングリコールに対して10〜40モル%が好ましく、さらに好ましくは15〜20モル%である。上記の割合でCHDMを共重合させることによって、ポリエステル系樹脂が非晶性となるため、層間の密着性が高くなるため好ましい。   The specific aromatic polyester resin used in the B layer of the present invention is not particularly limited, but terephthalic acid is the main component as the dicarboxylic acid component, and isophthalic acid, adipic acid, and succinic acid are used as additional components. As the diol component, ethylene glycol or butanediol can be used as a main component. For example, polyethylene terephthalate (PET), polybutylene terephthalate (PBT), CHDM copolymerized PET using 1,4-cyclohexanedimethanol (CHDM) as a copolymer component, and diethylene glycol (DEG) and neopentyl glycol as other diol components What added (NPG) is especially preferable from a viewpoint of the heat shrink behavior at the time of setting it as a shrink film, cost, productivity, and an interlayer strength improvement with A layer. The proportion of CHDM copolymerization is preferably 10 to 40 mol%, more preferably 15 to 20 mol%, relative to ethylene glycol. By copolymerizing CHDM at the above ratio, the polyester resin becomes amorphous, which is preferable because adhesion between layers is increased.

上記の芳香族ポリエステル系樹脂としては、既存品を用いることも可能であり、例えば、Eastman Chemical社製「Eastar Copolyester」、「EMBRACE」(以上、CHDM共重合PET);ベルポリエステルプロダクツ(株)製「ベルペット」(NPG共重合PET)等が市場で入手できる。   As the aromatic polyester-based resin, existing products can be used. For example, “Easter Polymer” manufactured by Eastman Chemical, “EMBRACE” (above, CHDM copolymerized PET); manufactured by Bell Polyester Products Co., Ltd. “Belpet” (NPG copolymerized PET) and the like are commercially available.

また、B層に脂肪族ポリエステル系樹脂を用いる場合には、ポリブチレンサクシネート(PBS)やポリブチレンサクシネートアジペート(PBSA)など、前述でA層に用いることができる樹脂として、例示されている脂肪族ポリエステル系樹脂の中から選択して用いることができる。   Moreover, when using an aliphatic polyester-type resin for B layer, it is illustrated as resin which can be used for A layer above-mentioned, such as polybutylene succinate (PBS) and polybutylene succinate adipate (PBSA). It can be selected from aliphatic polyester resins.

本発明のB層に用いられるポリオレフィン系樹脂としては、特に限定されないが、例えば、ポリエチレン(PE)、ポリプロピレン(PP)、ポリブチレン、ポリメチルペンテン(PMP)等の単独重合体;エチレン−α−オレフィンランダム共重合体、プロピレン−α−オレフィンランダム共重合体等のランダム共重合体;環状オレフィンとα−オレフィン(エチレン、プロピレン等)との共重合体又はそのグラフト変性物、環状オレフィンの開環重合体若しくはその水添物又はそれらのグラフト変性物等の非晶性環状オレフィン系重合体等が挙げられる。上記の中でも、低密度ポリエチレン(LDPE)、直鎖状低密度ポリエチレン(LLDPE)、メタロセン触媒系LLDPE(mLLDPE)などのポリエチレン、ポリプロピレン、プロピレン−α−オレフィン共重合体などのプロピレン系ランダム共重合体が好ましい。また、これらのポリオレフィン系樹脂は単独で又は2種以上混合して使用できる。   Although it does not specifically limit as polyolefin-type resin used for B layer of this invention, For example, homopolymers, such as polyethylene (PE), polypropylene (PP), polybutylene, polymethylpentene (PMP); Ethylene-alpha-olefin Random copolymers, random copolymers such as propylene-α-olefin random copolymers; copolymers of cyclic olefins and α-olefins (ethylene, propylene, etc.) or graft-modified products thereof, ring-opening weight of cyclic olefins Examples thereof include amorphous cyclic olefin polymers such as coalesced or hydrogenated products thereof or graft-modified products thereof. Among these, polyethylenes such as low density polyethylene (LDPE), linear low density polyethylene (LLDPE), metallocene catalyst system LLDPE (mLLDPE), and propylene random copolymers such as polypropylene and propylene-α-olefin copolymers. Is preferred. Moreover, these polyolefin resin can be used individually or in mixture of 2 or more types.

本発明のB層の主成分として用いられる樹脂のB層中の含有量は、樹脂の種類によっても異なり、特に限定されないが、B層の総重量に対して、40〜100重量%、より好ましくは50〜100重量%、更に好ましくは60〜100重量%である。40重量%未満では、シュリンクラベルの熱収縮特性を改善する効果が得られない場合や、透明性、寸法安定性、腰の強さ等、シュリンクラベルとして必要な特性が低下する場合がある。中でも、ポリスチレン系樹脂の場合、B層中の含有量は、50〜100重量%が好ましく、より好ましくは60〜100重量%であり、更に好ましくは70〜100重量%である。芳香族ポリエステル系樹脂の場合には50〜100重量%が好ましく、より好ましくは60〜100重量%であり、更に好ましくは70〜100重量%である。ポリオレフィン系樹脂の場合には、70〜100重量%が好ましく、より好ましくは80〜100重量%、更に好ましくは90〜100重量%である。   The content of the resin used as the main component of the B layer of the present invention in the B layer varies depending on the type of the resin and is not particularly limited, but is preferably 40 to 100% by weight, more preferably based on the total weight of the B layer. Is 50 to 100% by weight, more preferably 60 to 100% by weight. If it is less than 40% by weight, the effect of improving the shrinkage characteristics of the shrink label may not be obtained, and the characteristics required for the shrink label such as transparency, dimensional stability, and waist strength may be deteriorated. Among these, in the case of a polystyrene resin, the content in the B layer is preferably 50 to 100% by weight, more preferably 60 to 100% by weight, and still more preferably 70 to 100% by weight. In the case of an aromatic polyester resin, it is preferably 50 to 100% by weight, more preferably 60 to 100% by weight, and still more preferably 70 to 100% by weight. In the case of polyolefin resin, it is preferably 70 to 100% by weight, more preferably 80 to 100% by weight, and still more preferably 90 to 100% by weight.

本発明のB層樹脂(B層に含まれる全ての樹脂の混合物)がポリエステル系樹脂やポリスチレン系樹脂の場合、B層樹脂のガラス転移温度(Tg)は、加工性の観点から、40〜80℃が好ましく、より好ましくは50〜70℃である。Tgが上記範囲を外れる場合には、積層の場合などに、各フィルム層を十分に配向させることが困難となったり、生産性が低下する場合がある。   When the B layer resin of the present invention (a mixture of all resins contained in the B layer) is a polyester resin or a polystyrene resin, the glass transition temperature (Tg) of the B layer resin is 40 to 80 from the viewpoint of workability. ° C is preferred, more preferably 50-70 ° C. When Tg is out of the above range, it may be difficult to sufficiently orient each film layer in the case of lamination or the productivity may be lowered.

本発明のB層は、必要に応じて、その他の添加剤、例えば、滑剤、充填剤、熱安定剤、酸化防止剤、紫外線吸収剤、帯電防止剤、難燃剤、着色剤等を含んでいてもよい。   The B layer of the present invention contains other additives such as a lubricant, a filler, a heat stabilizer, an antioxidant, an ultraviolet absorber, an antistatic agent, a flame retardant, a colorant and the like as necessary. Also good.

本発明のシュリンクラベルは、少なくとも1層の印刷層を有する。印刷層は、前記シュリンクフィルムのどちらか片方の表面に設けられることが好ましい。中でも、シュリンクフィルムが積層フィルムの場合には、シュリンク加工時の印刷層の追従性や耐溶剤性を向上する観点から、B層表面に設けられることが好ましい。印刷層は、特に限定されないが、透明ラベルの場合などには、容器等に装着する場合に内側(すなわち被着体側)になる側の面に施すと、市場で流通する際の印刷層のはがれや汚れなどがなく好ましい。また、シュリンクフィルムが不透明である場合には、装飾性の観点から、外側(すなわち被着体側と反対側)に設けられることが好ましい。さらには、シュリンクフィルムの両面に設けられていてもよい。   The shrink label of the present invention has at least one printed layer. The printed layer is preferably provided on one surface of the shrink film. Especially, when a shrink film is a laminated | multilayer film, it is preferable to provide in the B layer surface from a viewpoint of improving the followable | trackability and solvent resistance of a printing layer at the time of shrink processing. The printed layer is not particularly limited. However, in the case of a transparent label or the like, if it is applied to the inner side (that is, the adherend side) when attached to a container or the like, the printed layer is peeled off when it is distributed in the market. It is preferable because there is no dirt or dirt. Moreover, when a shrink film is opaque, it is preferable to provide in the outer side (namely, the opposite side to a to-be-adhered body side) from a decorative viewpoint. Furthermore, it may be provided on both surfaces of the shrink film.

本発明の印刷層は、商品名やイラスト、取り扱い注意事項等を表示した層であり、グラビア印刷やフレキソ印刷等の慣用の印刷方法により形成することができる。印刷層の形成に用いられる印刷インキは、例えば顔料、バインダー樹脂、溶剤、その他の添加剤等からなる。上記バインダー樹脂としては、特に限定されないが、例えば、アクリル系、ウレタン系、ポリアミド系、塩化ビニル−酢酸ビニル共重合系、セルロース系、ニトロセルロース系などの樹脂を単独あるいは併用して使用できる。上記顔料としては、酸化チタン(二酸化チタン)等の白顔料、銅フタロシアニンブルー等の藍顔料、カーボンブラック、アルミフレーク、雲母(マイカ)、その他の着色顔料等が用途に合わせて選択、使用できる。また、顔料として、その他にも、光沢調製などの目的で、アルミナ、炭酸カルシウム、硫酸バリウム、シリカ、アクリルビーズ等の体質顔料も使用できる。上記溶剤としては、例えば、メチルエチルケトン、酢酸エチル、メチルアルコール、エチルアルコール、イソプロピルアルコールなどの有機溶媒や水などのグラビア、フレキソ印刷インキ等で塗工性やコーティング剤中の各成分の相溶性や分散性を改良する目的で通常用いられるものを使用できる。   The printing layer of the present invention is a layer displaying a product name, an illustration, handling precautions, and the like, and can be formed by a conventional printing method such as gravure printing or flexographic printing. The printing ink used for forming the printing layer is made of, for example, a pigment, a binder resin, a solvent, and other additives. Although it does not specifically limit as said binder resin, For example, resin, such as an acrylic type, a urethane type, a polyamide type, a vinyl chloride-vinyl acetate copolymer type, a cellulose type, a nitrocellulose type, can be used individually or in combination. As the pigment, white pigments such as titanium oxide (titanium dioxide), indigo pigments such as copper phthalocyanine blue, carbon black, aluminum flakes, mica (mica), and other colored pigments can be selected and used in accordance with the application. In addition, extender pigments such as alumina, calcium carbonate, barium sulfate, silica, and acrylic beads can also be used as pigments for the purpose of adjusting gloss. Examples of the solvent include organic solvents such as methyl ethyl ketone, ethyl acetate, methyl alcohol, ethyl alcohol, and isopropyl alcohol, gravure such as water, and flexographic printing ink, and the compatibility and dispersion of each component in the coating agent. Those usually used for the purpose of improving the properties can be used.

本発明の印刷層は、A層、B層の種類や用途などによっても異なり、特に限定されないが、可視光、紫外線、電子線などの活性エネルギー線硬化性の樹脂層であってもよい。活性エネルギー線硬化性の印刷層である場合には、印刷インキには、上記の他に、光ラジカル重合開始剤及び光カチオン重合開始剤などの光重合開始剤や増感剤等を添加することが好ましい。   The printing layer of the present invention varies depending on the type and use of the A layer and B layer, and is not particularly limited, but may be an active energy ray-curable resin layer such as visible light, ultraviolet light, or electron beam. In the case of an active energy ray-curable printing layer, in addition to the above, a photopolymerization initiator such as a photo radical polymerization initiator and a photo cationic polymerization initiator, a sensitizer, etc. should be added to the printing ink. Is preferred.

本発明のシュリンクラベルには、上記フィルム層、印刷層の他に、例えば、コーティング層、樹脂層、アンカーコート層、プライマーコート層、接着剤層、接着性樹脂層などを設けることができ、不織布、紙、金属薄膜等の層を必要に応じて設けてもよい。   The shrink label of the present invention can be provided with, for example, a coating layer, a resin layer, an anchor coat layer, a primer coat layer, an adhesive layer, an adhesive resin layer, etc. in addition to the film layer and the print layer, and a nonwoven fabric. A layer such as paper or a metal thin film may be provided as necessary.

本発明のシュリンクフィルムの厚みは、用途によって異なり特に限定されないが、10〜100μmが好ましく、より好ましくは20〜80μm、さらに好ましくは30〜60μmである。   Although the thickness of the shrink film of this invention changes with uses and is not specifically limited, 10-100 micrometers is preferable, More preferably, it is 20-80 micrometers, More preferably, it is 30-60 micrometers.

本発明のシュリンクフィルムが積層フィルムの場合、A層の厚みは、5〜60μmが好ましく、より好ましくは15〜40μmである。B層の厚みは4〜40μmが好ましく、より好ましくは10〜20μmである。また、A層(フィルム中の全てのA層厚みの総和)に対するB層(フィルム中の全てのB層厚みの総和)の厚み比(A層/B層)は、80/20〜20/80が好ましく、より好ましくは80/20〜30/70、さらに好ましくは80 /20〜40/60であり、最も好ましくは80/20〜50/50である。上記範囲に対して、A層が厚い場合には、熱収縮速度が速く加工性が低下したり、熱収縮応力が小さく印刷層の追従性が劣ったりして生産性が低下する場合がある。また、上記範囲に対して、B層が厚い場合には、熱収縮速度の低下や、加工温度の上昇により、相対的にみて生産性が低下する側に生産条件が移動する。また、環境への負荷も相対的にみて大きくなる。中でも、特に好ましい厚み構成としては、B/A/B、若しくはA/B/Aの積層構成で、厚み比が5/90/5〜1/1/1(A/B/Aの場合)、1/8/1〜1/1/1(より好ましくは1/8/1〜1/2/1)(B/A/Bの場合)である。   When the shrink film of the present invention is a laminated film, the thickness of the A layer is preferably 5 to 60 μm, more preferably 15 to 40 μm. The thickness of the B layer is preferably 4 to 40 μm, more preferably 10 to 20 μm. The thickness ratio (A layer / B layer) of B layer (sum of all B layer thicknesses in the film) to A layer (sum of all A layer thicknesses in the film) is 80/20 to 20/80. Is preferable, more preferably 80/20 to 30/70, still more preferably 80/20 to 40/60, and most preferably 80/20 to 50/50. With respect to the above range, when the A layer is thick, the heat shrinkage rate is high and the workability may be reduced, or the heat shrinkage stress may be small and the followability of the print layer may be inferior. In contrast, when the B layer is thicker than the above range, the production conditions move to a side where productivity is relatively lowered due to a decrease in heat shrinkage rate or an increase in processing temperature. In addition, the load on the environment is relatively large. Among these, as a particularly preferable thickness configuration, the thickness ratio is 5/90/5 to 1/1/1 (in the case of A / B / A) in a stacked configuration of B / A / B or A / B / A, 1/8/1 to 1/1/1 (more preferably 1/8/1 to 1/2/1) (in the case of B / A / B).

本発明の印刷層の厚みは、特に限定されないが、例えば0.1〜10μm程度である。厚みが0.1μm未満である場合には、印刷層を均一に設けることが困難である場合があり、部分的な「かすれ」が起こったりして、装飾性が損なわれたり、デザイン通りの印刷が困難となる場合がある。また、厚みが10μmを超える場合には、印刷インキを多量に消費するため、コストが高くなったり、均一に塗布することが困難となったり、印刷層がもろくなって、剥離しやすくなったりする。また、印刷層の剛性が高くなり、シュリンク加工時にフィルムの熱収縮に追従しにくくなる場合がある。   Although the thickness of the printing layer of this invention is not specifically limited, For example, it is about 0.1-10 micrometers. If the thickness is less than 0.1 μm, it may be difficult to provide a uniform printing layer, and partial “blur” may occur, resulting in a loss of decorativeness or printing as designed. May be difficult. In addition, when the thickness exceeds 10 μm, a large amount of printing ink is consumed, which increases the cost, makes it difficult to apply uniformly, makes the printed layer brittle and easily peels off. . Moreover, the rigidity of a printing layer becomes high and it may become difficult to follow the thermal contraction of a film at the time of shrink processing.

本発明のシュリンクラベル(及びシュリンクフィルム)は、所定の温度の温水中、熱収縮開始直後において、特定の熱収縮率または熱収縮速度を有する必要がある。本発明では以下の測定原理に基づいて測定された加熱条件下のサンプル(シュリンクラベルまたはシュリンクフィルム)の収縮速度を熱収縮速度と定義する。   The shrink label (and shrink film) of the present invention needs to have a specific heat shrinkage rate or heat shrinkage rate immediately after the start of heat shrinkage in warm water at a predetermined temperature. In the present invention, the shrinkage rate of a sample (shrink label or shrink film) under heating conditions measured based on the following measurement principle is defined as a heat shrinkage rate.

上記熱収縮速度の測定原理図を図1に示す。熱収縮速度は、シュリンクラベル(又はシュリンクフィルム)から採取した短冊状サンプル1を、所定の温水中に入れた際の、特定の標線A、B間の距離(標線間距離)ABの変化を検出することによって測定する。本発明においては、上記標線間距離ABは、特定の支点OとA、Bのそれぞれを結ぶ線分OA、OBがなす角度θ(開き角ともいう)を測定することによって算出する。すなわち、この角度θの変化量からサンプル1の熱収縮率を、角速度から熱収縮速度を算出する。なお、測定装置、測定条件、算出方法などは、後述の[熱収縮率、熱収縮速度の測定方法ならびに評価方法]の部分に記載する。   The measurement principle diagram of the heat shrinkage rate is shown in FIG. The heat shrinkage rate is a change in the distance between specific marked lines A and B (distance between marked lines) AB when the strip-shaped sample 1 collected from the shrink label (or shrink film) is placed in a predetermined hot water. Measure by detecting. In the present invention, the distance AB between the marked lines is calculated by measuring an angle θ (also referred to as an opening angle) formed by line segments OA and OB connecting the specific fulcrum O and each of A and B. That is, the heat shrinkage rate of the sample 1 is calculated from the change amount of the angle θ, and the heat shrinkage rate is calculated from the angular velocity. The measuring apparatus, measurement conditions, calculation method, etc. will be described in the section of [Measurement method and evaluation method of heat shrinkage rate, heat shrinkage rate] described later.

本発明のシュリンクラベルは、75℃温水中での熱収縮開始1秒後における主配向方向の熱収縮率が3〜23%であるか、又は、75℃温水中での主配向方向の最大熱収縮速度が7〜40%/秒であることが必要である。   The shrink label of the present invention has a heat shrinkage rate of 3 to 23% in the main orientation direction 1 second after the start of heat shrinkage in 75 ° C. warm water, or the maximum heat in the main orientation direction in 75 ° C. warm water. It is necessary that the shrinkage rate is 7 to 40% / second.

本発明のシュリンクラベルの75℃温水中での熱収縮開始1秒後における主配向方向の熱収縮率は3〜23%であり、好ましくは3〜21%、より好ましくは4〜21%、さらに好ましくは5〜19%である。該熱収縮率が23%を超える場合には、シュリンクラベルをシュリンク加工する際の熱収縮速度が速すぎて、制御が困難となり、「しわ」が発生したり、熱収縮が不均一となって意匠性が低下したりする。また熱収縮率が3%未満の場合には、熱収縮速度が遅く生産性が低下したり、高温で熱収縮加工を行う必要があり、耐熱性の低い容器や熱劣化しやすい内容物に使用できない場合が生じたりする。   The shrinkage rate of the shrink label of the present invention in the main orientation direction after 1 second of heat shrinkage in 75 ° C. warm water is 3 to 23%, preferably 3 to 21%, more preferably 4 to 21%, Preferably it is 5 to 19%. If the thermal shrinkage rate exceeds 23%, the thermal shrinkage rate when shrinking the shrink label is too fast, making it difficult to control, causing “wrinkles” or uneven thermal shrinkage. Designability may deteriorate. Also, if the heat shrinkage rate is less than 3%, the heat shrinkage rate is slow and the productivity must be reduced, or heat shrink processing must be performed at a high temperature, so it is used for containers with low heat resistance and contents that are susceptible to heat deterioration. Sometimes it can't be done.

本発明のシュリンクラベルの75℃温水中での主配向方向の最大熱収縮速度は7〜40%/秒であり、より好ましくは10〜38%/秒、さらに好ましくは12〜35%/秒である。一般的に、熱収縮開始時、若しくは熱収縮開始直後の熱収縮速度が最大熱収縮速度となる。該熱収縮速度が40%/秒を超える場合には、シュリンクラベルをシュリンク加工する際の熱収縮速度が速すぎて、制御が困難となり、「しわ」が発生したり、熱収縮が不均一となって意匠性が低下したりする。また該熱収縮速度が7%/秒未満の場合には、熱収縮速度が遅く生産性が低下したり、より高温で熱収縮加工を行う必要があり、耐熱性の低い容器や変質しやすい内容物の容器には使用できない場合が生じたりする。   The maximum heat shrinkage rate in the main orientation direction of the shrink label of the present invention in 75 ° C. warm water is 7 to 40% / second, more preferably 10 to 38% / second, and further preferably 12 to 35% / second. is there. Generally, the heat shrinkage rate at the start of heat shrinkage or immediately after the start of heat shrinkage is the maximum heat shrinkage rate. When the heat shrinkage rate exceeds 40% / second, the heat shrinkage rate when shrinking the shrink label is too high, and it becomes difficult to control, “wrinkles” occur, or heat shrinkage is uneven. As a result, the designability is lowered. Further, when the heat shrinkage rate is less than 7% / second, the heat shrinkage rate is slow, the productivity needs to be lowered, or heat shrinkage processing needs to be performed at a higher temperature. In some cases, the container cannot be used.

なお、上記「主配向方向」とは主に延伸処理を施した方向のことをいう。1軸延伸フィルムの場合には延伸方向(通常は長手方向または幅方向)であり、2軸延伸フィルムの場合には2つの延伸方向(通常は長手方向と幅方向)のうち、配向の大きな方向(熱収縮の大きな方向)である。製造条件などから主配向方向が判断できない場合には、例えば、フィルム中で最も熱収縮率(90℃、10秒など)の大きな方向を主配向方向とする。   The “main orientation direction” means a direction mainly subjected to stretching treatment. In the case of a uniaxially stretched film, it is the stretching direction (usually the longitudinal direction or the width direction), and in the case of a biaxially stretched film, the direction of large orientation among the two stretching directions (usually the longitudinal direction and the width direction). (In the direction of large heat shrinkage). If the main orientation direction cannot be determined from the manufacturing conditions, for example, the direction with the largest thermal shrinkage (90 ° C., 10 seconds, etc.) in the film is taken as the main orientation direction.

本発明のシュリンクラベルの75℃温水中での熱収縮開始3秒後における主配向方向の熱収縮率は、1秒後の熱収縮率が上記記載の範囲にあれば特に限定されないが、例えば、下限が10%が好ましく、より好ましくは13%、さらに好ましくは14%、最も好ましくは17%である。一方、上限は45%が好ましく、より好ましくは30%、さらに好ましくは28%、最も好ましくは25%である。   The heat shrinkage rate in the main orientation direction after 3 seconds after the start of heat shrinkage in 75 ° C. warm water of the shrink label of the present invention is not particularly limited as long as the heat shrinkage rate after 1 second is in the above range, for example, The lower limit is preferably 10%, more preferably 13%, still more preferably 14%, and most preferably 17%. On the other hand, the upper limit is preferably 45%, more preferably 30%, still more preferably 28%, and most preferably 25%.

本発明に用いられるシュリンクラベルの90℃温水中での10秒後における主配向方向の熱収縮率は、40〜84%であり、好ましくは50〜80%、さらに好ましくは55〜75%である。該熱収縮率は、サンプルの90℃の温水条件下で浸漬10秒後に測定された熱収縮率である。上記熱収縮率は、フィルムの延伸加工における延伸倍率、その他の延伸条件と関連する値であり、同時にシュリンクラベルの限界熱収縮率に関わる値である。該熱収縮率が84%を超える場合には、延伸倍率が6倍を超え、延伸加工が難しいのみならず、延伸後のフィルムの破断伸度や衝撃強度の低下を招くことがある。また熱収縮率が40%未満の場合には、シュリンク加工時の熱収縮量が不足し、容器形状に十分追従せず仕上がり性が劣る。   The thermal shrinkage rate in the main alignment direction after 10 seconds in 90 ° C. warm water of the shrink label used in the present invention is 40 to 84%, preferably 50 to 80%, more preferably 55 to 75%. . The heat shrinkage rate is a heat shrinkage rate measured after 10 seconds of immersion in a 90 ° C. hot water condition. The heat shrinkage rate is a value related to the draw ratio in the film drawing process and other drawing conditions, and at the same time is a value related to the limit heat shrinkage rate of the shrink label. When the thermal shrinkage rate exceeds 84%, the stretching ratio exceeds 6 times, and not only is the stretching process difficult, but also the elongation at break and impact strength of the film after stretching may be reduced. On the other hand, when the heat shrinkage rate is less than 40%, the amount of heat shrinkage at the time of shrink processing is insufficient, and the finish performance is inferior because the container shape does not sufficiently follow.

シュリンクラベルの熱収縮特性(75℃1秒における熱収縮率、75℃3秒における熱収縮率、90℃10秒における熱収縮率、熱収縮速度)は、シュリンクラベルに用いるシュリンクフィルムの熱収縮特性とほとんど同じであるため、シュリンクフィルムの各熱収縮率もシュリンクラベルと同様の範囲にあることが好ましい。これらの熱収縮特性は、ポリ乳酸系重合体の含有量、ポリ乳酸以外の樹脂の種類、含有量、フィルム層厚みや厚み比、シュリンクフィルムの延伸配向条件などにより制御することができる。   The thermal shrinkage characteristics of the shrink label (heat shrinkage rate at 75 ° C. for 1 second, heat shrinkage rate at 75 ° C. for 3 seconds, heat shrinkage rate at 90 ° C. for 10 seconds, heat shrinkage rate) are as follows. Therefore, it is preferable that each shrinkage rate of the shrink film is in the same range as the shrink label. These heat shrink characteristics can be controlled by the content of the polylactic acid polymer, the type and content of the resin other than polylactic acid, the thickness and thickness ratio of the film layer, the stretching orientation condition of the shrink film, and the like.

本発明の特徴は、熱収縮速度の速いポリ乳酸系重合体と熱収縮速度の緩やかなポリスチレン系樹脂や芳香族ポリエステル系樹脂などを複合(積層、混合など)して用いることによって、シュリンク加工を行う際に、高い生産性と加工性、美麗な仕上がり性が両立しうるように熱収縮速度を制御したことにある。本発明においては、シュリンクフィルムが、ポリ乳酸系重合体とそれ以外の重合体の組成物からなる単層フィルムの場合であっても、また、ポリ乳酸系重合体を主成分とするA層とそれ以外の重合体を主成分とするB層等との組み合わせからなる多層フィルムの場合であっても、ポリ乳酸系重合体はフィルムの熱収縮速度を上昇させる成分としての役割を負い、それ以外の重合体は熱収縮速度を低減させる役割を負っている。前記A層の主成分であるポリ乳酸系重合体を単独成分とするフィルムにあっては、熱収縮速度が速く、熱収縮挙動が急激であり、結果として、シュリンク加工時の収縮挙動の制御が困難となって、「しわ」や「印刷層の歪み」等の問題を引き起こしやすくなる。これとは逆に、B層の主成分(例えば、ポリスチレン系樹脂)を単独成分とするフィルムにあっては、熱収縮速度が遅く、また、環境面で劣る。環境面で優れる植物由来のポリ乳酸系重合体と、例えばポリスチレン系重合体或いはポリエステル系重合体を組成物として、或いは積層体として組み合わせることにより、環境面で優れるラベルを得ることができるとともに、得られたフィルムの熱収縮速度を調整し、シュリンク加工時の熱収縮挙動を容易に制御することができ、更に、両者の組成比や層構成を調整することで、シュリンク加工の生産効率や製品の仕上がりを向上できる。   The feature of the present invention is that shrink processing is performed by using a composite (lamination, mixing, etc.) of a polylactic acid polymer having a high heat shrinkage rate and a polystyrene resin or an aromatic polyester resin having a slow heat shrinkage rate. This is because the heat shrinkage rate is controlled so that high productivity, workability, and beautiful finish can be achieved at the same time. In the present invention, even if the shrink film is a single-layer film made of a composition of a polylactic acid polymer and another polymer, the A layer containing the polylactic acid polymer as a main component, Even in the case of a multilayer film composed of a combination with other layers such as a B layer mainly composed of a polymer, the polylactic acid-based polymer plays a role as a component for increasing the heat shrinkage rate of the film. These polymers have the role of reducing the heat shrinkage rate. In a film having a polylactic acid polymer as the main component of the A layer as a single component, the heat shrinkage rate is fast and the heat shrinkage behavior is abrupt. As a result, the shrinkage behavior during shrink processing can be controlled. It becomes difficult to easily cause problems such as “wrinkles” and “distortion of the printing layer”. On the other hand, in a film having the main component (for example, polystyrene resin) of the B layer as a single component, the heat shrinkage rate is slow and the environment is inferior. By combining an environmentally superior plant-derived polylactic acid polymer with, for example, a polystyrene polymer or a polyester polymer as a composition or a laminate, an environmentally superior label can be obtained and obtained. By adjusting the heat shrinkage rate of the film, the heat shrinkage behavior during shrink processing can be easily controlled, and by adjusting the composition ratio and layer structure of both, the production efficiency of the shrink processing and the product The finish can be improved.

これらの組み合わせは、熱収縮速度の調整のみならず、熱収縮応力の調整においてもその効力を発揮する。即ち、ポリ乳酸系重合体は熱収縮応力が小さいため、単体で用いる場合には、印刷層が厚い場合、無機顔料を多く含む場合など印刷層の剛性が高い場合には、シュリンク時に印刷層がフィルムの熱収縮にうまく追従せず、仕上がりが低下する場合がある。これに対して、B層に用いられる樹脂が芳香族ポリエステル系樹脂やポリスチレン系樹脂の場合は、A層対比熱収縮応力が大きいため、シュリンクラベルの熱収縮応力を向上させる。さらに、B層のポリスチレン系樹脂や芳香族ポリエステル系樹脂などは、ポリ乳酸系重合体に比べ、シール性(後述の溶剤によるセンターシール適性)が良好であるため、B層を表層にする場合には、シール性が良好となり好ましい。なお、A層とB層とでは、上記の通り、熱収縮特性が大きく異なるため、カール等の問題を防ぐ観点では、B/A/B型2種3層積層構成とすることが好ましい。   These combinations are effective not only in adjusting the heat shrinkage rate but also in adjusting the heat shrinkage stress. That is, since the polylactic acid-based polymer has a small heat shrinkage stress, when used alone, when the printing layer is thick, such as when the printing layer is thick or when containing a large amount of inorganic pigment, the printing layer does not shrink when shrinking. The film may not follow the heat shrinkage of the film well, and the finish may be reduced. On the other hand, when the resin used for the B layer is an aromatic polyester-based resin or a polystyrene-based resin, the heat shrinkage stress of the shrink label is improved because the heat shrinkage stress relative to the A layer is large. Furthermore, since the B-layer polystyrene-based resin and aromatic polyester-based resin have better sealing properties than the polylactic acid-based polymer (center seal suitability with a solvent described later), the B layer is used as a surface layer. Is preferable because of good sealing properties. In addition, since the heat shrinkage characteristics are greatly different between the A layer and the B layer as described above, it is preferable to adopt a B / A / B type 2 type 3 layer laminated structure from the viewpoint of preventing problems such as curling.

本発明のシュリンクラベルおよびシュリンクフィルムの主配向方向と直交する方向の熱収縮率(温水、90℃、10秒)は、シュリンク加工性等の観点から、−3〜15%が好ましく、より好ましくは−1〜10%である。   The thermal shrinkage rate (warm water, 90 ° C., 10 seconds) in the direction orthogonal to the main orientation direction of the shrink label and the shrink film of the present invention is preferably −3 to 15%, more preferably from the viewpoint of shrink workability. -1 to 10%.

本発明のシュリンクフィルムの透明性(ヘイズ値:JIS K 7136)(単位:%)は、10以下であることが好ましく、より好ましくは5以下である。ヘイズ値が10を超える場合には、シュリンクフィルムの内側(ラベルを容器に装着した時に容器側になる面側)に印刷を施し、フィルムを通して、印刷を見せるシュリンクラベルの場合、製品とした際に、印刷が曇り、装飾性が低下することがある。   The transparency (haze value: JIS K 7136) (unit:%) of the shrink film of the present invention is preferably 10 or less, more preferably 5 or less. When the haze value exceeds 10, the inside of the shrink film (the side that becomes the container side when the label is attached to the container) is printed, and in the case of a shrink label that shows printing through the film, , Printing may become cloudy and decorative properties may be reduced.

本発明に用いられるシュリンクフィルムの耐ブロッキング性(積層フィルムの場合にはB層表面)(JIS K 6854−3に準じたT型剥離試験における剥離強度、加圧条件:40℃、0.3MPa、180秒)は、0.1N/15mm以下が好ましい。剥離強度が0.1N/15mmを超える場合には、ブロッキングが生じやすく、生産性、加工性が低下する場合や、加温状態で本発明のシュリンクラベルを用いる場合に取り扱い不良が生じる場合がある。   Blocking resistance of the shrink film used in the present invention (B layer surface in the case of a laminated film) (peel strength in a T-type peel test according to JIS K 6854-3, pressure condition: 40 ° C., 0.3 MPa, 180 seconds) is preferably 0.1 N / 15 mm or less. When the peel strength exceeds 0.1 N / 15 mm, blocking is likely to occur, and productivity and workability may be reduced, or handling failure may occur when the shrink label of the present invention is used in a heated state. .

本発明のシュリンクフィルムの主配向方向の熱収縮応力(85℃)は、3〜11MPaが好ましく、より好ましくは4〜8MPaである。熱収縮応力が3MPa未満の場合には、印刷層のシュリンク加工追従性が低下し、仕上がりが低下する場合がある。11MPaを超えると容器の変形を引き起こしたり、開封時に内容物があふれたりするおそれがある。   The heat shrinkage stress (85 ° C.) in the main orientation direction of the shrink film of the present invention is preferably 3 to 11 MPa, more preferably 4 to 8 MPa. When the heat shrinkage stress is less than 3 MPa, the shrinkage followability of the printed layer is lowered, and the finish may be lowered. If it exceeds 11 MPa, the container may be deformed or the contents may overflow when opened.

本発明のシュリンクラベルは、例えば、ラベル両端を溶剤や接着剤でシールし筒状にして容器に装着されるタイプの筒状シュリンクラベルや、ラベルの一端を容器に貼り付け、ラベルを巻き回した後、他端を一端に重ね合わせて筒状にする巻き付け方式のシュリンクラベルとして好適に用いることができる。この筒状シュリンクラベルのセンターシール強度は、2.0(N/15mm)以上が好ましい。シール強度が2.0(N/15mm)未満の場合には、加工工程や製品化した後に、シール部分がはがれて、生産性を低下させたり、ラベル脱落の原因となったりする。また、筒状シュリンクラベルはシール部が白化していないことが好ましい。   The shrink label of the present invention is, for example, a cylindrical shrink label of a type in which both ends of the label are sealed with a solvent or an adhesive and attached to the container, and one end of the label is attached to the container, and the label is wound Then, it can be suitably used as a wrapping type shrink label in which the other end is overlapped with one end to form a cylinder. The center seal strength of this cylindrical shrink label is preferably 2.0 (N / 15 mm) or more. When the seal strength is less than 2.0 (N / 15 mm), the seal part is peeled off after the processing step or commercialization, and the productivity is lowered or the label is dropped. Moreover, it is preferable that the seal part of the cylindrical shrink label is not whitened.

上記の熱収縮特性を有するシュリンクラベルを達成する一つの態様は、ポリ乳酸系重合体を必須成分とするフィルム層(A層)、ポリスチレン系樹脂を主成分とするフィルム層(B1層)を少なくとも1層ずつ有する積層シュリンクフィルムであって、A層(フィルム中の全てのA層厚みの総和)とB1層(フィルム中の全てのB1層厚みの総和)の厚み比(A層厚み/B1層厚み)が80/20〜20/80、好ましくは80/20〜30/70、より好ましくは80/20〜40/60、最も好ましくは80/20〜50/50であるシュリンクフィルム及び印刷層を有するシュリンクラベルである。   One aspect of achieving the above-described shrink label having heat shrinkage characteristics is at least a film layer (A layer) containing a polylactic acid polymer as an essential component and a film layer (B1 layer) containing a polystyrene resin as a main component. A laminated shrink film having one layer at a time, the thickness ratio (A layer thickness / B1 layer) of A layer (sum of all A layer thicknesses in the film) and B1 layer (sum of all B1 layer thicknesses in the film) A shrink film and a printed layer having a thickness) of 80/20 to 20/80, preferably 80/20 to 30/70, more preferably 80/20 to 40/60, and most preferably 80/20 to 50/50. It is a shrink label.

上記のB1層に用いるポリスチレン系樹脂としては、前述のポリスチレン系樹脂を用いることが可能である。なお、A層中のポリ乳酸系重合体の含有量は50〜100重量%が好ましく、より好ましくは60〜100重量%、さらに好ましくは70〜100重量%である。B1層中のポリスチレン系樹脂の含有量は50〜100重量%が好ましく、より好ましくは60〜100重量%、さらに好ましくは70〜100重量%である。また、A層中には、前述の脂肪族ポリエステル系樹脂が1〜50重量%、より好ましくは2〜40重量%、さらに好ましくは5〜30重量%程度含まれていてもよい。   As the polystyrene resin used for the B1 layer, the above-mentioned polystyrene resin can be used. The content of the polylactic acid polymer in the A layer is preferably 50 to 100% by weight, more preferably 60 to 100% by weight, and still more preferably 70 to 100% by weight. The content of the polystyrene resin in the B1 layer is preferably 50 to 100% by weight, more preferably 60 to 100% by weight, and still more preferably 70 to 100% by weight. Moreover, in the A layer, the above-mentioned aliphatic polyester resin may be contained in an amount of 1 to 50% by weight, more preferably 2 to 40% by weight, and still more preferably about 5 to 30% by weight.

上記の熱収縮特性を有するシュリンクラベルを達成する他の一つの態様は、ポリ乳酸系重合体を必須成分とするフィルム層(A層)、芳香族ポリエステル系樹脂を主成分とするフィルム層(B2層)を少なくとも1層ずつ有する積層シュリンクフィルムであって、A層(フィルム中の全てのA層厚みの総和)とB2層(フィルム中の全てのB2層厚みの総和)の厚み比(A層厚み/B2層厚み)が80/20〜20/80、好ましくは80/20〜30/70、より好ましくは80/20〜40/60、最も好ましくは80/20〜50/50であるシュリンクフィルム及び印刷層を有するシュリンクラベルである。   Another embodiment for achieving a shrink label having the above heat shrink property is a film layer (A layer) containing a polylactic acid polymer as an essential component, and a film layer (B2) containing an aromatic polyester resin as a main component. Layer) is a laminated shrink film having at least one layer, and a thickness ratio (A layer) of A layer (total thickness of all A layers in the film) and B2 layer (total thickness of all B2 layers in the film) (Thickness / B2 layer thickness) is 80/20 to 20/80, preferably 80/20 to 30/70, more preferably 80/20 to 40/60, most preferably 80/20 to 50/50. And a shrink label having a printed layer.

上記のB2層に用いる、芳香族ポリエステル系樹脂としては、前述の芳香族ポリエステル系樹脂を用いることが可能である。なお、A層中のポリ乳酸系重合体の含有量は50〜100重量%が好ましく、より好ましくは60〜100重量%、さらに好ましくは70〜100重量%である。B2層中の芳香族ポリエステル系樹脂の含有量は50〜100重量%が好ましく、より好ましくは60〜100重量%、さらに好ましくは70〜100重量%である。また、A層中には、前述の脂肪族ポリエステル系樹脂が1〜50重量%、より好ましくは2〜40重量%、さらに好ましくは5〜30重量%程度含まれていてもよい。   As the aromatic polyester resin used for the B2 layer, the above-described aromatic polyester resin can be used. The content of the polylactic acid polymer in the A layer is preferably 50 to 100% by weight, more preferably 60 to 100% by weight, and still more preferably 70 to 100% by weight. The content of the aromatic polyester resin in the B2 layer is preferably 50 to 100% by weight, more preferably 60 to 100% by weight, and still more preferably 70 to 100% by weight. Moreover, in the A layer, the above-mentioned aliphatic polyester resin may be contained in an amount of 1 to 50% by weight, more preferably 2 to 40% by weight, and still more preferably about 5 to 30% by weight.

本発明のシュリンクラベルは、容器に装着し、ラベル付き容器として用いられる。このような容器には、例えば、PETボトルなどのソフトドリンク用ボトル、宅配用牛乳瓶、調味料などの食品用容器、アルコール飲料用ボトル、医薬品容器、洗剤、スプレーなどの化学製品の容器、カップ麺容器などが含まれる。容器の形状としても、円筒状、角形のボトルや、カップタイプなど様々な形状が含まれる。また、容器の材質としても、PETなどのプラスチック製、ガラス製、金属製などが含まれる。   The shrink label of the present invention is attached to a container and used as a labeled container. Such containers include, for example, soft drink bottles such as PET bottles, milk bottles for home delivery, food containers such as seasonings, alcoholic beverage bottles, pharmaceutical containers, containers for chemical products such as detergents and sprays, cups, etc. This includes noodle containers. The shape of the container includes various shapes such as a cylindrical shape, a square bottle, and a cup type. Further, the material of the container includes plastic such as PET, glass, metal and the like.

以下に、本発明のシュリンクラベルの製造方法及び容器に対する装着加工方法の一例を説明する。ここでは、ポリ乳酸系重合体からなるA層、ポリスチレン系樹脂からなるB層を有するB/A/B型2種3層のシュリンクラベルを例に説明するが、これに限定したものではない。なお、下記説明において、工程順に、延伸後のフィルム原反を「シュリンクフィルム」、これに印刷処理を施したものを「長尺状シュリンクラベル」、さらに長尺のまま筒状に加工したものを「長尺筒状シュリンクラベル」と記載する。   Below, an example of the manufacturing method of the shrink label of this invention, and the mounting method with respect to a container is demonstrated. Here, a B / A / B type 2 type 3 layer shrink label having an A layer made of a polylactic acid polymer and a B layer made of a polystyrene resin will be described as an example, but the present invention is not limited to this. In the following description, in the order of the process, the original film after stretching is “shrink film”, the one subjected to printing treatment is “long shrink label”, and further processed into a cylindrical shape with a long length. It is described as “long cylindrical shrink label”.

[シュリンクフィルム]
本発明のシュリンクフィルムに用いる、ポリ乳酸系重合体及びポリスチレン系樹脂は、既知の手法を用いて重合することができる。また、これらの樹脂は、市販のものを用いることができる。例えば、ポリ乳酸系重合体としては、三井化学(株)製「レイシア」、ネイチャーワークス社製「ネイチャーワークス」等を用いてもよい。また、スチレン系樹脂としては、例えば、スチレン−ブタジエン共重合体としては、旭化成株式会社製「アフサレックス」やフィルップス社製「K−レジン」、PSジャパン(株)製「SC004」等を用いることが可能である。また、必要に応じて、コストやリサイクルの観点から、回収原料を一定量添加することも可能である。
[Shrink film]
The polylactic acid polymer and polystyrene resin used for the shrink film of the present invention can be polymerized using a known technique. Moreover, these resin can use a commercially available thing. For example, as the polylactic acid polymer, “Lacia” manufactured by Mitsui Chemicals, Inc., “Nature Works” manufactured by Nature Works, etc. may be used. As the styrene resin, for example, “Afusalex” manufactured by Asahi Kasei Co., Ltd., “K-resin” manufactured by Phillips, “SC004” manufactured by PS Japan Co., Ltd., or the like can be used as the styrene-butadiene copolymer. Is possible. Moreover, it is also possible to add a certain amount of recovered raw materials as necessary from the viewpoint of cost and recycling.

次に得られた原料を用いて、積層フィルムを作成する。積層の方法としては、慣用の方法、例えば、Tダイ方式若しくはインフレーション方式の共押出法、ドライラミネート法、サンドラミネート法などを用いることが可能である。また、積層した後に延伸してもよいし、延伸したフィルム同士を積層することも可能である。中でも、生産性の観点からは、共押出法により積層未延伸フィルムを作製した後に延伸を行う方法が好ましい。以下には、共押出法(B/A/B型2種3層積層)の例を示す。   Next, a laminated film is prepared using the obtained raw material. As a lamination method, a conventional method, for example, a T-die type or inflation type co-extrusion method, a dry lamination method, a sand lamination method, or the like can be used. Moreover, after extending | stretching, you may extend | stretch and it is also possible to laminate | stack the stretched films. Among these, from the viewpoint of productivity, a method of stretching after producing a laminated unstretched film by a coextrusion method is preferable. Below, the example of the co-extrusion method (B / A / B type 2 type | mold 3 layer lamination | stacking) is shown.

所定の温度に設定した押出機aにはポリ乳酸系重合体を投入し、押出機bには、ポリスチレン系樹脂を投入し、Tダイ、サーキュラーダイなどから共押出し、冷却ドラムなどを用いて急冷し、未延伸積層フィルムを作成する。この際、3層マニホールドや合流ブロックを用いて、B/A/B型2種3層積層構成とすることが好ましい。また必要に応じて、ギアポンプを用いて供給量を調節してもよく、さらにフィルターを用いて、異物を除去するとフィルム破れが低減できるため好ましい。なお、押出温度は、用いるポリ乳酸系重合体、ポリスチレン系樹脂の種類によっても異なり、特に限定されないが、190〜250℃が好ましい。さらに、必要に応じて、滑剤、帯電防止剤、防曇剤、酸化防止剤などの他の混合剤を混合してもよい。   The extruder a set at a predetermined temperature is charged with a polylactic acid polymer, the extruder b is charged with a polystyrene resin, co-extruded from a T die, a circular die, etc., and rapidly cooled using a cooling drum or the like. And an unstretched laminated film is created. At this time, it is preferable to use a B / A / B type 2 type 3 layer laminated structure by using a 3 layer manifold or a merge block. Further, if necessary, the supply amount may be adjusted using a gear pump, and it is preferable to remove foreign substances using a filter because film tearing can be reduced. The extrusion temperature varies depending on the type of polylactic acid polymer and polystyrene resin used, and is not particularly limited, but is preferably 190 to 250 ° C. Further, if necessary, other admixtures such as a lubricant, an antistatic agent, an antifogging agent and an antioxidant may be mixed.

また、用途によっては、3台の押出機を用いて、共押出を行ってもよい。その場合には、A層の両側にそれぞれ異なる厚み、異なる樹脂からなる積層部を設けることが可能である。   Depending on the application, co-extrusion may be performed using three extruders. In that case, it is possible to provide laminated portions made of different resins and different thicknesses on both sides of the A layer.

次に、得られた未延伸積層フィルムを延伸し、長尺状のシュリンクフィルムを作製する。延伸は、長手方向(縦方向;MD方向)および幅方向(横方向;TD方向)の2軸延伸でもよいし、長手、または、幅方向の1軸延伸でもよい。また、延伸方式は、ロール方式、テンター方式、チューブ方式の何れの方式を用いてもよい。延伸処理は、70〜110℃程度の温度で、必要に応じて長手方向に例えば1.01〜1.5倍、好ましくは1.05〜1.3倍程度に延伸した後、幅方向に2〜8倍、好ましくは3〜6倍程度延伸することにより行う。   Next, the obtained unstretched laminated film is stretched to produce a long shrink film. The stretching may be biaxial stretching in the longitudinal direction (longitudinal direction; MD direction) and width direction (transverse direction; TD direction), or may be uniaxial stretching in the longitudinal direction or the width direction. The stretching method may be any of a roll method, a tenter method, and a tube method. The stretching treatment is performed at a temperature of about 70 to 110 ° C., if necessary, for example, 1.01 to 1.5 times, preferably about 1.05 to 1.3 times in the longitudinal direction, and then 2 in the width direction. It is carried out by stretching about 8 times, preferably about 3 to 6 times.

また、本発明のシュリンクフィルムの表面には、必要に応じて、コロナ放電処理やプライマー処理(アンダーコート処理)等の慣用の表面処理が施されていてもよい。   Further, the surface of the shrink film of the present invention may be subjected to a conventional surface treatment such as corona discharge treatment or primer treatment (undercoat treatment) as necessary.

[シュリンクラベル]
次に、上記のようにして得られた長尺状のシュリンクフィルムの少なくとも一方の面に印刷層を形成し、長尺状シュリンクラベルを作製する。印刷層は、顔料、バインダー樹脂、溶剤、その他の添加剤等を混合して調製した印刷インキを塗布することにより形成する。塗布の方法は、シュリンクフィルムの製造工程中(例えば、未延伸または縦1軸延伸後)に塗布を行うインラインコートでもよいし、フィルム製膜後に塗布を行うオフラインコートでもよく、特に限定されないが、生産性、加工性などの観点から、オフラインコートが好ましい。また、印刷手法としては、慣用の方法を用いることができるが、グラビア印刷またはフレキソ印刷が最も好ましい。
[Shrink label]
Next, a printing layer is formed on at least one surface of the long shrink film obtained as described above, thereby producing a long shrink label. The printing layer is formed by applying a printing ink prepared by mixing a pigment, a binder resin, a solvent, other additives, and the like. The method of application may be in-line coating applied during the shrink film manufacturing process (for example, unstretched or after longitudinal uniaxial stretching) or offline coating applied after film formation, and is not particularly limited. From the viewpoint of productivity, workability, etc., off-line coating is preferred. As a printing method, a conventional method can be used, but gravure printing or flexographic printing is most preferable.

上記のラベルは、所定の幅にスリットして、ロール状に巻回し、複数個のロール状物として、シュリンクラベル(長尺状シュリンクラベル)が得られる。   The label is slit into a predetermined width and wound into a roll shape, and a shrink label (long shrink label) is obtained as a plurality of roll-like objects.

[長尺状シュリンクラベルの加工] [Processing of long shrink labels]

以下に得られたシュリンクラベルを容器に装着する加工の一例を示すが、製造方法は、これに限定されるものではない。   Although an example of the process which mounts the obtained shrink label on a container is shown below, a manufacturing method is not limited to this.

上記ロール状物のひとつを繰り出しながら、長尺状シュリンクフィルムの幅方向が円周方向となるように円筒状に成形する。具体的には、長尺状シュリンクラベルを筒状に形成し、ラベルの一方の側縁部に、長手方向に帯状に約2〜4mm幅で、テトラヒドロフラン(THF)などの溶剤や接着剤(以下溶剤等)を内面に塗布し、筒状に丸めて、該溶剤等塗布部を、他方の側縁部から5〜10mmの位置に重ね合わせて外面に接着(センターシール)し、長尺筒状のラベル連続体とし、長尺筒状シュリンクラベルを得る。   While feeding one of the rolls, the long shrink film is formed into a cylindrical shape so that the width direction is the circumferential direction. Specifically, a long shrink label is formed into a cylindrical shape, and a solvent or adhesive (hereinafter referred to as “THF”) having a width of about 2 to 4 mm in the longitudinal direction on one side edge of the label. Solvent etc.) is applied to the inner surface, rolled up into a cylindrical shape, and the solvent applied portion is overlapped at a position of 5-10 mm from the other side edge and adhered to the outer surface (center seal). A long cylindrical shrink label is obtained.

なお、ラベル切除用のミシン目を設ける場合は、所定の長さ及びピッチのミシン目を長手方向に形成する。ミシン目は慣用の方法(例えば、周囲に切断部と非切断部とが繰り返し形成された円板状の刃物を押し当てる方法やレーザーを用いる方法等)により施すことができる。ミシン目を施す工程段階は、印刷工程の後や、筒状加工工程の前後など、適宜選択ことができる。   In the case where a perforation for label excision is provided, a perforation having a predetermined length and pitch is formed in the longitudinal direction. The perforation can be applied by a conventional method (for example, a method of pressing a disk-shaped blade having a cut portion and a non-cut portion repeatedly formed around it, a method using a laser, or the like). The process stage for perforating can be appropriately selected after the printing process and before and after the cylindrical processing process.

[ラベル付き容器]
最後に、上記で得られた長尺筒状シュリンクラベルを切断後、所定の容器に装着し、加熱処理によって、ラベルを熱収縮、容器に追従密着させることによってラベル付き容器を作製する。上記長尺筒状シュリンクラベルを、自動ラベル装着装置(シュリンクラベラー)に供給し、必要な長さに切断した後、内容物を充填した容器に外嵌し、所定温度の熱風トンネルやスチームトンネルを通過させたり、赤外線等の輻射熱で加熱して熱収縮させ、容器に密着させて、ラベル付き容器を得る。上記加熱処理としては、例えば、80〜100℃のスチームで処理する(スチームおよび湯気が充満した加熱トンネルを通過させる)ことなどが例示される。
[Container with label]
Finally, after cutting the long cylindrical shrink label obtained above, it is mounted on a predetermined container, and the container is manufactured by heat-shrinking the label to heat shrink and follow the container. The above long cylindrical shrink label is supplied to an automatic label mounting device (shrink labeler), cut to the required length, and then externally fitted into a container filled with contents, and a hot air tunnel or steam tunnel at a predetermined temperature is attached. Passed or heated with radiant heat such as infrared rays to cause heat shrinkage and adhere to the container to obtain a labeled container. Examples of the heat treatment include treatment with steam at 80 to 100 ° C. (passing through a heating tunnel filled with steam and steam).

[熱収縮率、熱収縮速度の測定方法ならびに評価方法]
以下に、前述および図1に示した測定原理に基づき、本発明における熱収縮率および熱収縮速度を測定する方法(測定装置、測定方法、算出方法)を説明する。
[Measurement method and evaluation method of heat shrinkage rate and heat shrinkage rate]
Below, based on the measurement principle shown above and shown in FIG. 1, the method (measurement apparatus, measurement method, calculation method) of measuring the heat shrinkage rate and the heat shrinkage rate in the present invention will be described.

(1)測定装置
本発明で使用する測定装置は、水平に設置された台座に、図1のOA、OBに相当する2本のアームと、支点Oの位置に回転角度を測定する回転角測定器が設置されてなる。上記アームのうち一方のアーム(OA)は台座に固定されたアームである。また、他方のアーム(OB)は、回転角測定器の回転軸に取り付けられた可動式のアームであり、支点Oを中心に自由に回動可能(回転トルクは2mN・m以下である。)である。なお、2本アームはそれぞれ、地面と水平に設置する。
アーム先端部(A、Bの点に相当する)には試料(フィルム)を固定する留め金具(クリップ)が取り付けられている。なお、必要に応じて、アーム先端部に、試料支持アームが垂直に取り付けられ、それぞれの試料支持アームの先端に試料固定用の留め金具が取り付けられた構造でもよい。それぞれの留め金具は相互に水平になるように位置決めされている。
なお、上記装置の試料部分は、測定系を保ったまま、温水中に移動可能となっている。例えば、上記台座が温調可能な水槽上に取り付けられ、上下に可動となっており、台座を上下にスライドさせることにより試料部分をすばやく所定の温度に温調された水中に浸漬できる構造である。
(1) Measuring device The measuring device used in the present invention is a rotation angle measurement that measures a rotation angle at the position of a fulcrum O and two arms corresponding to OA and OB in FIG. A vessel is installed. One of the arms (OA) is an arm fixed to the pedestal. The other arm (OB) is a movable arm attached to the rotation shaft of the rotation angle measuring device, and can freely rotate around the fulcrum O (the rotational torque is 2 mN · m or less). It is. Each of the two arms is installed horizontally with the ground.
A fastener (clip) for fixing the sample (film) is attached to the arm tip (corresponding to points A and B). If necessary, a structure in which a sample support arm is vertically attached to the arm tip and a sample fixing bracket is attached to the tip of each sample support arm may be employed. Each fastener is positioned so as to be horizontal to each other.
In addition, the sample part of the said apparatus can be moved to warm water, maintaining a measurement system. For example, the pedestal is mounted on a temperature-controllable water tank, is movable up and down, and has a structure in which the sample portion can be quickly immersed in water temperature-controlled at a predetermined temperature by sliding the pedestal up and down. .

(2)測定方法
測定対象であるシュリンクラベルを主配向方向(実施例、比較例のシュリンクラベルの場合には幅方向)に長さ100mm、幅5mmの短冊状に裁断し、これを試料フィルムとした。試料フィルムの両端に掴み代を略均等に残すようにして88.0mm間隔の標線を設けた。
この試料フィルムを上記アーム(又は試料支持アーム)の先端部に固定する。固定アーム(OA)の留め金具に一方の標線の部位を固定し、次いで可動側アーム(OB)の開き角を調整しながら、もう一方の留め金具にもう一方の標線部を固定し、両留め金具間の距離が正確に88mmになるように調節した。なお、OA、OBの長さは100mmである。
次いで、試料フィルム部分をすばやく75℃±0.5℃に温調された水槽に浸漬し、同時に試料フィルムの熱収縮によるアームOA−OB間の角度θ(開き角)の変化の測定を開始し、同開き角を測定開始後0.1秒毎に測定した。
なお、実施例、比較例の測定に用いた測定条件は以下の通りである。
(測定、装置条件)
回転角度測定器 : 株式会社緑測器製、無接触型回転角度センサー「CP−2UK−R200」
アーム : アルミ製角柱(断面:10mm×10mm)
温水温度 : 75℃±0.5℃(75℃測定の場合)
(2) Measuring method Shrink labels to be measured are cut into strips having a length of 100 mm and a width of 5 mm in the main orientation direction (width direction in the case of the shrink labels of Examples and Comparative Examples), and this is referred to as a sample film. did. Mark lines with an interval of 88.0 mm were provided so as to leave the grip allowance substantially equally at both ends of the sample film.
This sample film is fixed to the tip of the arm (or sample support arm). Fix the part of one marked line to the clamp of the fixed arm (OA), then fix the other marked line part to the other clamp while adjusting the opening angle of the movable arm (OB), The distance between both fasteners was adjusted to be exactly 88 mm. The length of OA and OB is 100 mm.
Next, the sample film part is quickly immersed in a water bath adjusted to 75 ° C. ± 0.5 ° C., and at the same time, measurement of the change in the angle θ (opening angle) between the arms OA and OB due to the thermal contraction of the sample film is started. The opening angle was measured every 0.1 second after the start of measurement.
In addition, the measurement conditions used for the measurement of an Example and a comparative example are as follows.
(Measurement, equipment conditions)
Rotation angle measuring device: Non-contact type rotation angle sensor “CP-2UK-R200” manufactured by Midorokki
Arm: Aluminum prism (cross section: 10mm x 10mm)
Hot water temperature: 75 ° C ± 0.5 ° C (when measuring 75 ° C)

(3)算出方法
(3−1)熱収縮率(st
測定された開き角から試料の標線間距離を算出(標線間距離=OA(又はOB)×sin(θ/2)×2)し、初期標線間距離(L0=88mm)とt秒後の標線間距離(Lt)からt秒後の熱収縮率st(%)を下記式1により求め、t=0から0.1秒毎のstをグラフにプロットする。
t=(L0−Lt)×100/L0 (式1)
(3) Calculation method (3-1) Thermal contraction rate (s t )
The distance between the marked lines of the sample is calculated from the measured opening angle (distance between marked lines = OA (or OB) × sin (θ / 2) × 2), and the initial distance between marked lines (L 0 = 88 mm) and t The thermal contraction rate s t (%) after t seconds is obtained from the distance between the marked lines after second (L t ) by the following formula 1, and s t from 0.1 to 0.1 seconds is plotted on the graph.
s t = (L 0 -L t ) × 100 / L 0 ( Equation 1)

(3−2)熱収縮速度(Vt)、最大熱収縮速度(Vmax
次に測定点毎に式2により熱収縮速度Vtを求める。
t=(st+0.2−st)/0.2 (式2)
上記式2の意味するところは、測定開始よりt秒後の熱収縮速度は(t+0.2)秒後の熱収縮率(st+0.2)とt秒後の熱収縮率(st)の差を0.2秒で除した数字(即ち、2点間の傾き)と定義することである。1つの試料中、0.1秒間隔の全ての測定点について求められたVtの最大値を最大熱収縮速度(Vmax)とする。
なお、測定は少なくとも熱収縮率の変化が定常に達するまで行う。
(3-2) Thermal contraction rate (V t ), maximum thermal contraction rate (V max )
Next, the thermal contraction speed V t is obtained by Equation 2 for each measurement point.
V t = (s t + 0.2 -s t) /0.2 ( Equation 2)
The meaning of the above formula 2, the heat shrinkage rate of t seconds after the start of the measurement of the (t + 0.2) sec thermal shrinkage ratio after (s t + 0.2) and the t seconds thermal shrinkage ratio after (s t) The difference is defined as a number obtained by dividing the difference by 0.2 seconds (that is, the slope between two points). The maximum value of V t obtained for all measurement points at intervals of 0.1 seconds in one sample is defined as the maximum heat shrinkage rate (V max ).
The measurement is performed at least until the change in the heat shrinkage rate reaches a steady state.

(3−3)熱収縮開始点(T0
本発明において、上記式1で得られたt秒後の熱収縮率st(縦軸)を、時間t(横軸)に対してプロットしたグラフの一例を図2に示した。グラフ中の曲線が熱収縮率の変化であり、直線は、下記の最大の傾き(上記Vmaxである)の直線(接線と近似する)である。前記試料フィルムを温水に浸漬し測定を開始した時点を原点(t=0)としている。
フィルムは原点よりやや遅れて熱収縮を開始し、収縮の立ち上がり部では熱伝導の遅れの影響を受けるため、多くの場合、該曲線はS字状の曲線となる。
その為、本発明では、熱収縮開始点(T0)を次のように定義する。上記Vmaxが得られた測定点を通り、傾きがVmaxの直線を引き、時間軸との交点を求める。この交点の時間より後のはじめての測定点の時間(サンプリング時間)を熱収縮開始点(T0)として定義する。
(3-3) Thermal contraction start point (T 0 )
In the present invention, FIG. 2 shows an example of a graph in which the thermal contraction rate s t (vertical axis) after t seconds obtained by Equation 1 is plotted against time t (horizontal axis). A curve in the graph is a change in heat shrinkage rate, and a straight line is a straight line (approximate to a tangent line) having the following maximum slope (which is V max ). The origin (t = 0) is the time when the sample film is immersed in warm water and measurement is started.
Since the film starts thermal contraction with a slight delay from the origin and is affected by the delay in heat conduction at the rising edge of the contraction, the curve is often an S-shaped curve.
Therefore, in the present invention, the thermal contraction start point (T 0 ) is defined as follows. A straight line with a slope of V max is drawn through the measurement point where V max is obtained, and the intersection with the time axis is obtained. The time (sampling time) of the first measurement point after this intersection time is defined as the thermal contraction start point (T 0 ).

(3−4)熱収縮開始1、3秒後における熱収縮率(S1、S3
図2に示すとおり、T0から1秒後(T1)における熱収縮率S1を「熱収縮開始1秒後における熱収縮率」とした。同様に、T0から3秒後(T3)の熱収縮率S3を「熱収縮開始3秒後における熱収縮率」とした。
(3-4) Thermal contraction rate at 1 and 3 seconds after start of thermal contraction (S 1 , S 3 )
As shown in FIG. 2, the heat shrinkage rate S 1 after 1 second (T 1 ) from T 0 was defined as “heat shrinkage rate 1 second after the start of heat shrinkage”. Similarly, the thermal contraction rate S 3 after 3 seconds from T 0 (T 3 ) was defined as “the thermal contraction rate 3 seconds after the start of thermal contraction”.

(4)90℃、10秒における熱収縮率(S10’)
水槽の温度を90℃±0.5℃に変更して、上記(3)同様に熱収縮率の測定を実施し、同様の算出方法を用いて、T0’から10秒後の熱収縮率S10’(熱収縮開始10秒後の熱収縮率)を求め、「90℃、10秒における熱収縮率」とした。
(4) Thermal shrinkage at 90 ° C. for 10 seconds (S 10 ′)
The temperature of the water tank was changed to 90 ° C. ± 0.5 ° C., the heat shrinkage rate was measured in the same manner as in (3) above, and the heat shrinkage rate after 10 seconds from T 0 ′ using the same calculation method. S 10 ′ (heat shrinkage rate after 10 seconds from the start of heat shrinkage) was determined and set as “heat shrinkage rate at 90 ° C. for 10 seconds”.

[その他の評価]
(1)透明性(ヘイズ値)(単位:%)
JIS K 7136に準じて測定を行う。40μm厚みに換算して、以下の基準で評価する。
5.0以下 : ラベル用途として優れた透明性である(◎)。
5.0より大、10以下 : ラベル用途として十分な透明性である(○)。
10より大 : ラベル用途として不十分な透明性である(×)。
[Other evaluations]
(1) Transparency (haze value) (unit:%)
Measurement is performed according to JIS K 7136. Converted to a thickness of 40 μm, evaluation is made according to the following criteria.
5.0 or less: Excellent transparency for label use (◎).
Greater than 5.0 and 10 or less: Transparency sufficient for label use (◯).
Greater than 10: The transparency is insufficient for label use (×).

(2)フィルム層厚み、印刷層厚み
フィルム厚みは、ダイヤルゲージを用いて測定した。印刷層厚みは、印刷層を設けた部分(塗布面)と印刷層を設けていない部分(非塗布面)の段差を、3次元顕微鏡(キーエンス(株)製VK8510)を用いて測定した。
(2) Film layer thickness, printing layer thickness The film thickness was measured using a dial gauge. The thickness of the printed layer was measured using a three-dimensional microscope (Keyence Co., Ltd. VK8510) for the level difference between the portion provided with the print layer (application surface) and the portion not provided with the print layer (non-application surface).

(3)シール強度
センターシールされた筒状シュリンクラベルを、ラベルの高さ方向に15mm幅となるように、ラベルの円周方向に切断し、幅15mmのリング状のラベル片を採取した後、前記リング状ラベル片を、センターシールが施された部分(以下、シール部分という)以外の部分で切開し、上記円周方向が長辺となる短冊状のサンプル片を作成する。
T型剥離されるように、上記のサンプル片をチャックして、引張試験機で引っ張ることにより、下記の条件で、T型剥離試験(JIS K 6854−3に準拠)を行う。なお、初期チャック間隔は40mmであり、シール部分がチャック間の中心となるようにセットして測定を行う。また、試験はサンプル片の破断まで行う。
試験で得られた最大荷重をもってシール強度(N/15mm)とし、該シール強度が2(N/15mm)以上であればセンタシール性が良好(○)と判断し、2(N/15mm)未満の場合にはシール性が不良(×)と判断する。
(なお、上記の測定に際しては、必要に応じて、伸びないフィルム片をつなぎ合わせて測定に用いてもよい。)
測定装置 : 島津製作所(株)製オートグラフ(AGS−50G:ロードセルタイプ500N)
温湿度 : 温度23±2℃、湿度50±5%RH(JIS K 7000標準温度状態2級)
初期チャック間隔 : 40mm
サンプル幅 : 15mm
試験回数 : 3回
クロスヘッド移動速度 : 200mm/分
(3) Seal strength After the center-sealed cylindrical shrink label is cut in the circumferential direction of the label so as to have a width of 15 mm in the height direction of the label, and a ring-shaped label piece having a width of 15 mm is collected, The ring-shaped label piece is cut at a portion other than a portion where a center seal is applied (hereinafter referred to as a seal portion), and a strip-shaped sample piece having a long side in the circumferential direction is created.
The sample piece is chucked and pulled by a tensile tester so as to be T-type peeled, and a T-type peel test (conforming to JIS K 6854-3) is performed under the following conditions. Note that the initial chuck interval is 40 mm, and measurement is performed with the seal portion set to be the center between the chucks. The test is conducted until the sample piece is broken.
The maximum load obtained in the test is taken as the seal strength (N / 15 mm). If the seal strength is 2 (N / 15 mm) or more, the center seal property is judged as good (◯) and less than 2 (N / 15 mm) In this case, it is determined that the sealing performance is poor (x).
(In the above measurement, if necessary, film pieces that do not stretch may be joined together and used for the measurement.)
Measuring device: Shimadzu Corporation autograph (AGS-50G: load cell type 500N)
Temperature and humidity: Temperature 23 ± 2 ° C, humidity 50 ± 5% RH (JIS K 7000 standard temperature state 2nd grade)
Initial chuck interval: 40 mm
Sample width: 15mm
Number of tests: 3 times Crosshead moving speed: 200 mm / min

(4)熱収縮応力
実施例、比較例で得られたシュリンクフィルムから、シュリンクフィルム主延伸方向(実施例、比較例では幅方向)に200mm、主延伸方向と直交する方向(実施例、比較例では長手方向)に15mmの略矩形のフィルム片を切り出しサンプルとした。
引張試験機(島津製作所(株)製「オートグラフ AGS−50G」、ロードセル500N)のチャックにチャック間距離100mmでセット(シュリンクフィルムの主延伸方向が引張試験機の引張方向)し、チャック間距離(100mm)を保持した状態で、85℃の温水に10秒浸漬した。なお、チャック間100mmのうち、80mmまでの部分を温水に浸漬した。
この際に生じた応力を検出し、最大値を熱収縮応力とした。
(4) Thermal shrinkage stress From the shrink film obtained in the examples and comparative examples, the shrink film main stretching direction (width direction in the examples and comparative examples) is 200 mm, and the direction orthogonal to the main stretching direction (examples and comparative examples). In the longitudinal direction), a substantially rectangular film piece of 15 mm was cut out and used as a sample.
Set to a chuck of a tensile tester ("Autograph AGS-50G" manufactured by Shimadzu Corporation, load cell 500N) with a chuck distance of 100 mm (the main stretch direction of the shrink film is the tensile direction of the tensile tester), and the chuck distance (100 mm) was held for 10 seconds in 85 ° C. warm water. In addition, the part to 80 mm was immersed in warm water among 100 mm between chuck | zippers.
The stress generated at this time was detected, and the maximum value was defined as the heat shrinkage stress.

以下に、実施例に基づいて、本発明をより詳細に説明するが、本発明はこれらの実施例により限定されるものではない。なお、実施例6〜8は「参考例」とする。 EXAMPLES Hereinafter, the present invention will be described in more detail based on examples, but the present invention is not limited to these examples. Examples 6 to 8 are referred to as “reference examples”.

実施例1
A層樹脂として、ポリ乳酸樹脂(三井化学(株)製「レイシア H−280」)70重量%とポリブチレンサクシネート(昭和高分子(株)製「ビオノーレ 1003」)30重量%の混合樹脂(樹脂A1)を用いた。また、B層樹脂として、SBS樹脂(旭化成ケミカルズ株式会社 「アサフレックス825」)100重量%(樹脂B1)を用いた。
210℃に加熱した押出機aに樹脂A1を投入し、225℃に加熱した押出機bには樹脂B1を投入した。上記2台の押出機を用いて溶融押出を行った。押出機aから押出される樹脂が基層部、押出機bから押出される樹脂が基層部両側の積層部となるように、合流ブロックを用いて合流させ、Tダイ(スリット間隔1mm)より押出した後、25℃に冷却したキャスティングドラム上で急冷して、積層部(B1)/基層部(A1)/積層部(B1)の2種3層積層未延伸フィルムを得た。未延伸フィルムの積層厚み比は、B1/A1/B1=1/3/1であった。
次に、該未延伸フィルムを、ロール延伸機を用いて、長さ方向に1.3倍延伸した後、幅方向に5.3倍テンター延伸することにより、主に1軸方向に熱収縮する2軸延伸フィルム(シュリンクフィルム)を得た。フィルムの総厚みは50μm(層厚み比:1/3/1)であった。
続いて、得られたシュリンクフィルムの片面にアクリル系インキ(商品名「PS−985」、サカタインクス社製)をグラビア印刷により塗布、印刷層(厚み3μm)を形成し、シュリンクラベルを得た。
得られたシュリンクラベルの、75℃温水中での熱収縮開始1秒後(T1)における主配向方向の熱収縮率(S1)は9%、熱収縮開始3秒後(T3)における主配向方向の熱収縮率(S3)は17%、90℃10秒における熱収縮率(S10’)は55%であった。また、最大熱収縮速度(Vmax)は10.1%/秒であった。
上記シュリンクラベルを、印刷面が内側となり、且つ、フィルムの幅方向が円周方向となるように筒状に丸めて、テトラヒドロフラン(THF)でセンターシールし、筒状シュリンクラベルを得た。さらに、上記筒状シュリンクラベルを容器(東洋製罐(株)製500ml耐熱角形PETボトル)に装着し、雰囲気温度90℃のスチームトンネルで加熱収縮して、ラベル付き容器96本を得た。得られたラベル付き容器には「しわ」などの不良が1本もなく、優れた仕上がりであった。
Example 1
As the A layer resin, a mixed resin (70% by weight of polylactic acid resin (“Lacia H-280” manufactured by Mitsui Chemicals, Inc.) and 30% by weight of polybutylene succinate (“Bionore 1003” manufactured by Showa Polymer Co., Ltd.) Resin A1) was used. Moreover, 100 weight% (resin B1) of SBS resin (Asahi Kasei Chemicals Corporation "Asaflex 825") was used as B layer resin.
Resin A1 was charged into the extruder a heated to 210 ° C., and the resin B1 was charged into the extruder b heated to 225 ° C. Melt extrusion was performed using the above two extruders. The resin extruded from the extruder a is merged using a merge block so that the resin extruded from the extruder b is a laminated portion on both sides of the substrate layer, and extruded from a T die (slit spacing 1 mm). Then, it rapidly cooled on the casting drum cooled at 25 degreeC, and obtained the 2 type 3 layer lamination | stacking unstretched film of a laminated part (B1) / base layer part (A1) / laminated part (B1). The lamination thickness ratio of the unstretched film was B1 / A1 / B1 = 1/3/1.
Next, the unstretched film is stretched 1.3 times in the length direction using a roll stretching machine, and then thermally contracted mainly in a uniaxial direction by being stretched 5.3 times in the width direction. A biaxially stretched film (shrink film) was obtained. The total thickness of the film was 50 μm (layer thickness ratio: 1/3/1).
Subsequently, acrylic ink (trade name “PS-985”, manufactured by Sakata Inx Co., Ltd.) was applied to one side of the obtained shrink film by gravure printing to form a printing layer (thickness 3 μm), and a shrink label was obtained.
The thermal shrinkage rate (S 1 ) in the main orientation direction after 1 second (T 1 ) of heat shrinkage in 75 ° C. warm water of the obtained shrink label was 9%, and after 3 seconds (T 3 ) of heat shrinkage start The heat shrinkage rate (S 3 ) in the main orientation direction was 17%, and the heat shrinkage rate (S 10 ′) at 90 ° C. for 10 seconds was 55%. The maximum heat shrinkage rate (V max ) was 10.1% / second.
The shrink label was rolled into a cylindrical shape so that the printing surface was inside and the width direction of the film was the circumferential direction, and center-sealed with tetrahydrofuran (THF) to obtain a cylindrical shrink label. Furthermore, the cylindrical shrink label was attached to a container (500 ml heat-resistant square PET bottle manufactured by Toyo Seikan Co., Ltd.) and heat-shrinked in a steam tunnel having an atmospheric temperature of 90 ° C. to obtain 96 labeled containers. The obtained labeled container had no defects such as “wrinkles” and was an excellent finish.

実施例2
層厚み比を、B1/A1/B1=1/5/1に変更した以外は、実施例1と同様にして総厚み50μmのシュリンクフィルム、及び、シュリンクラベルを得た。得られたシュリンクラベルの熱収縮率(S1)は19%、熱収縮率(S3)は26%、90℃10秒後の熱収縮率(S10’)は62%であった。最大熱収縮速度(Vmax)は25.8%/秒であった。
また、実施例1と同様にして、ラベル付き容器96本を得た。得られたラベル付き容器には「しわ」などの不良が1本もなく、優れた仕上がりであった。
Example 2
A shrink film having a total thickness of 50 μm and a shrink label were obtained in the same manner as in Example 1 except that the layer thickness ratio was changed to B1 / A1 / B1 = 1/5/1. The resulting shrink label had a heat shrinkage rate (S 1 ) of 19%, a heat shrinkage rate (S 3 ) of 26%, and a heat shrinkage rate (S 10 ′) after 90 seconds at 90 ° C. of 62%. The maximum heat shrinkage rate (V max ) was 25.8% / second.
Further, 96 labeled containers were obtained in the same manner as in Example 1. The obtained labeled container had no defects such as “wrinkles” and was an excellent finish.

実施例3
層厚み比を、B1/A1/B1=1/8/1に変更した以外は、実施例1と同様にして総厚み50μmのシュリンクフィルム、及び、シュリンクラベルを得た。
得られたシュリンクラベルの熱収縮率(S1)は21%、熱収縮率(S3)は27%、90℃10秒後の熱収縮率(S10’)は65%であった。最大熱収縮速度(Vmax)は39.2%/秒であった。
また、実施例1と同様にして、ラベル付き容器96本を得た。得られたラベル付き容器には「しわ」などの不良が1本もなく、優れた仕上がりであった。
Example 3
A shrink film having a total thickness of 50 μm and a shrink label were obtained in the same manner as in Example 1 except that the layer thickness ratio was changed to B1 / A1 / B1 = 1/8/1.
The resulting shrink label had a heat shrinkage rate (S 1 ) of 21%, a heat shrinkage rate (S 3 ) of 27%, and a heat shrinkage rate (S 10 ′) after 90 seconds at 90 ° C. of 65%. The maximum heat shrinkage rate (V max ) was 39.2% / second.
Further, 96 labeled containers were obtained in the same manner as in Example 1. The obtained labeled container had no defects such as “wrinkles” and was an excellent finish.

比較例1
押出機1台のみを用い、樹脂A1からなる単層フィルムを作製した。
210℃に加熱した押出機に、樹脂A1を投入して、Tダイ(スリット間隔1mm)より溶融押出した後、25℃に冷却したキャスティングドラム上で急冷して、単層未延伸フィルムを得た。さらに、実施例1と同様にして、総厚み50μmのシュリンクフィルム、及び、シュリンクラベルを得た。
得られたシュリンクラベルの熱収縮率(S1)は24%、熱収縮率(S3)は30%、90℃10秒後の熱収縮率(S10’)は70%であった。最大熱収縮速度(Vmax)は115.7%/秒であった。
また、実施例1と同様にして、ラベル付き容器96本を得た。得られたラベル付き容器の17本に対して、「しわ」が観察され、外観が劣っていた。
Comparative Example 1
Using only one extruder, a single-layer film made of resin A1 was produced.
Resin A1 was put into an extruder heated to 210 ° C., melt-extruded from a T-die (slit spacing 1 mm), and then rapidly cooled on a casting drum cooled to 25 ° C. to obtain a single-layer unstretched film. . Further, in the same manner as in Example 1, a shrink film having a total thickness of 50 μm and a shrink label were obtained.
The obtained shrink label had a heat shrinkage rate (S 1 ) of 24%, a heat shrinkage rate (S 3 ) of 30%, and a heat shrinkage rate (S 10 ′) after 10 seconds at 90 ° C. of 70%. The maximum heat shrinkage rate (V max ) was 115.7% / second.
Further, 96 labeled containers were obtained in the same manner as in Example 1. “Wrinkles” were observed on 17 of the obtained labeled containers, and the appearance was inferior.

実施例4〜8
原料として、表1に示すポリ乳酸系重合体70重量部と添加樹脂(ポリ乳酸系重合体以外の樹脂)30重量部の混合原料を用い、押出機1台のみを用い、該混合樹脂からなる単層フィルムを作製した。
190℃に加熱した押出機に、混合原料を投入して、Tダイ(スリット間隔1mm)より溶融押出した後、25℃に冷却したキャスティングドラム上で急冷して、単層未延伸フィルムを得た。さらに、表1に示す延伸条件で横1軸延伸を行い、総厚み50μmのシュリンクフィルムを得た。さらに、実施例1と同様にしてシュリンクラベルを得た。
得られたシュリンクラベルの熱収縮率(S1)、熱収縮率(S3)、90℃10秒後の熱収縮率(S10’)、最大熱収縮速度(Vmax)は表1に示したとおりである。
また、実施例1と同様にして、ラベル付き容器96本を得た。得られたラベル付き容器は表1に示すとおり、「しわ」などの不良が1本もなく、優れた仕上がりであった。
Examples 4-8
As a raw material, a mixed raw material of 70 parts by weight of a polylactic acid polymer shown in Table 1 and 30 parts by weight of an additive resin (a resin other than a polylactic acid polymer) is used, and only one extruder is used, and the mixed resin is used. A single layer film was prepared.
A mixed raw material was charged into an extruder heated to 190 ° C., melt-extruded from a T-die (slit interval 1 mm), and then rapidly cooled on a casting drum cooled to 25 ° C. to obtain a single-layer unstretched film. . Furthermore, horizontal uniaxial stretching was performed under the stretching conditions shown in Table 1 to obtain a shrink film having a total thickness of 50 μm. Further, a shrink label was obtained in the same manner as in Example 1.
Table 1 shows the thermal shrinkage rate (S 1 ), thermal shrinkage rate (S 3 ), thermal shrinkage rate after 10 seconds at 90 ° C. (S 10 ′), and maximum thermal shrinkage rate (V max ). That's right.
Further, 96 labeled containers were obtained in the same manner as in Example 1. As shown in Table 1, the obtained labeled container had no defects such as “wrinkles” and had an excellent finish.

実施例9〜15
A層樹脂(A層原料)およびB層樹脂(B層原料)として、表2に示した樹脂を用い、表2に示した配合組成で、2種3層積層フィルムを作製した。
190℃に加熱した押出機aにA層樹脂を投入し、180℃に加熱した押出機bにはB層樹脂を投入した。押出機aから押出される樹脂が基層部、押出機bから押出される樹脂が基層部両側の積層部となるように、合流ブロックを用いて合流させ、Tダイ(スリット間隔1mm)より押出した後、25℃に冷却したキャスティングドラム上で急冷して、積層部(B層)/基層部(A層)/積層部(B層)の2種3層積層未延伸フィルムを得た。さらに、表2に示す延伸条件で横1軸延伸を行い、総厚み50μmのシュリンクフィルムを得た。さらに、実施例1と同様にしてシュリンクラベルを得た。
得られたシュリンクラベルの熱収縮率(S1)、熱収縮率(S3)、90℃10秒後の熱収縮率(S10’)、最大熱収縮速度(Vmax)は表2に示したとおりである。
また、実施例2と同様にして、ラベル付き容器96本を得た。得られたラベル付き容器は表2に示すとおり、「しわ」などの不良が1本もなく、優れた仕上がりであった。
Examples 9-15
As the A-layer resin (A-layer raw material) and the B-layer resin (B-layer raw material), a resin shown in Table 2 was used, and a two-type three-layer laminated film was prepared with the composition shown in Table 2.
The layer A resin was charged into the extruder a heated to 190 ° C., and the layer B resin was charged into the extruder b heated to 180 ° C. The resin extruded from the extruder a is merged using a merge block so that the resin extruded from the extruder b is a laminated portion on both sides of the substrate layer, and extruded from a T die (slit spacing 1 mm). Then, it rapidly cooled on the casting drum cooled at 25 degreeC, and the 2 type 3 layer lamination | stacking unstretched film of a laminated part (B layer) / base layer part (A layer) / laminated part (B layer) was obtained. Furthermore, transverse uniaxial stretching was performed under the stretching conditions shown in Table 2 to obtain a shrink film having a total thickness of 50 μm. Further, a shrink label was obtained in the same manner as in Example 1.
Table 2 shows the thermal shrinkage rate (S 1 ), thermal shrinkage rate (S 3 ), thermal shrinkage rate after 10 seconds at 90 ° C. (S 10 ′), and maximum thermal shrinkage rate (V max ) of the obtained shrink label. That's right.
Further, 96 labeled containers were obtained in the same manner as in Example 2. As shown in Table 2, the obtained labeled container had no defects such as “wrinkles” and had an excellent finish.

なお、表2における「配合量」の単位は重量部であり、実施例4〜15で用いた原料樹脂の詳細は表3に示した。   The unit of “blending amount” in Table 2 is parts by weight, and details of the raw material resins used in Examples 4 to 15 are shown in Table 3.

Figure 0005184817
Figure 0005184817

Figure 0005184817
Figure 0005184817

Figure 0005184817
Figure 0005184817

本発明の熱収縮開始直後の熱収縮率および最大熱収縮速度の測定の原理図である。It is a principle figure of the measurement of the thermal contraction rate and the maximum thermal contraction rate immediately after the start of thermal contraction of the present invention. 本発明の熱収縮率測定で得られた、時間tと時間tにおける熱収縮率stの関係をプロットしたグラフの一例である。Obtained in the heat shrinkage measured present invention, an example of a graph plotting the relationship between thermal shrinkage s t at time t and time t.

符号の説明Explanation of symbols

1 試料フィルム
O 支点
A、B 標線
θ OAとOBのなす角(開き角)
1 Sample film O Support point A, B Mark line θ Angle formed by OA and OB (open angle)

Claims (5)

ポリ乳酸系重合体を必須成分とするフィルム層(A層)を少なくとも1層有するシュリンクフィルム及び印刷層を有するシュリンクラベルであって、
前記シュリンクフィルムが、さらに、ポリスチレン系樹脂又は芳香族ポリエステル系樹脂であるポリ乳酸系重合体以外の樹脂を主成分とするフィルム層(B層)を少なくとも1層有する積層シュリンクフィルムであり、
前記積層シュリンクフィルムの、全A層のフィルム層厚みと全B層のフィルム層厚みの比(A層厚み/B層厚み)が80/20〜20/80であり、
前記A層中の前記ポリ乳酸系重合体の含有量が50重量%以上であり、
前記ポリ乳酸系重合体を構成する単量体成分における、全乳酸成分に占めるD−乳酸成分の割合が4〜15重量%であり、
前記B層中の前記ポリ乳酸系重合体以外の樹脂の含有量が70〜100重量%であり、
75℃温水中での熱収縮開始1秒後における主配向方向の熱収縮率が3〜23%、さらに90℃、10秒における主配向方向の熱収縮率が40〜84%であることを特徴とするシュリンクラベル。
A shrink label having a printed film and a shrink film having at least one film layer (A layer) comprising a polylactic acid polymer as an essential component,
The shrink film is a laminated shrink film further comprising at least one film layer (B layer) mainly comprising a resin other than a polylactic acid polymer that is a polystyrene resin or an aromatic polyester resin,
The ratio of the film layer thickness of all A layers and the film layer thickness of all B layers (A layer thickness / B layer thickness) of the laminated shrink film is 80/20 to 20/80,
The content of the polylactic acid polymer in the layer A is 50% by weight or more,
The proportion of the D-lactic acid component in the total lactic acid component in the monomer component constituting the polylactic acid polymer is 4 to 15% by weight,
The content of the resin other than the polylactic acid-based polymer in the B layer is 70 to 100% by weight,
The heat shrinkage rate in the main orientation direction at 1 second after the start of heat shrinkage in 75 ° C. warm water is 3 to 23%, and the heat shrinkage rate in the main orientation direction at 90 ° C. and 10 seconds is 40 to 84%. Shrink label.
ポリ乳酸系重合体を必須成分とするフィルム層(A層)を少なくとも1層有するシュリンクフィルム及び印刷層を有するシュリンクラベルであって、
前記シュリンクフィルムが、さらに、ポリスチレン系樹脂又は芳香族ポリエステル系樹脂であるポリ乳酸系重合体以外の樹脂を主成分とするフィルム層(B層)を少なくとも1層有する積層シュリンクフィルムであり、
前記積層シュリンクフィルムの、全A層のフィルム層厚みと全B層のフィルム層厚みの比(A層厚み/B層厚み)が80/20〜20/80であり、
前記A層中の前記ポリ乳酸系重合体の含有量が50重量%以上であり、
前記ポリ乳酸系重合体を構成する単量体成分における、全乳酸成分に占めるD−乳酸成分の割合が4〜15重量%であり、
前記B層中の前記ポリ乳酸系重合体以外の樹脂の含有量が70〜100重量%であり、
75℃温水中での主配向方向の最大熱収縮速度が7〜40%/秒であり、さらに90℃、10秒における主配向方向の熱収縮率が40〜84%であることを特徴とするシュリンクラベル。
A shrink label having a printed film and a shrink film having at least one film layer (A layer) comprising a polylactic acid polymer as an essential component,
The shrink film is a laminated shrink film further comprising at least one film layer (B layer) mainly comprising a resin other than a polylactic acid polymer that is a polystyrene resin or an aromatic polyester resin,
The ratio of the film layer thickness of all A layers and the film layer thickness of all B layers (A layer thickness / B layer thickness) of the laminated shrink film is 80/20 to 20/80,
The content of the polylactic acid polymer in the layer A is 50% by weight or more,
The proportion of the D-lactic acid component in the total lactic acid component in the monomer component constituting the polylactic acid polymer is 4 to 15% by weight,
The content of the resin other than the polylactic acid-based polymer in the B layer is 70 to 100% by weight,
The maximum heat shrinkage rate in the main alignment direction in 75 ° C. warm water is 7 to 40% / second, and the heat shrinkage rate in the main alignment direction at 90 ° C. for 10 seconds is 40 to 84%. Shrink label.
前記積層シュリンクフィルムが、前記A層の両側に前記B層を、若しくは前記B層の両側に前記A層を有する積層シュリンクフィルムである請求項1または2に記載のシュリンクラベル。   The shrink label according to claim 1 or 2, wherein the laminated shrink film is a laminated shrink film having the B layer on both sides of the A layer or the A layer on both sides of the B layer. ポリ乳酸系重合体を必須成分とするフィルム層(A層)を少なくとも1層有するシュリンクフィルム及び印刷層を有するシュリンクラベルであって、
前記シュリンクフィルムが、前記A層の単層シュリンクフィルムであり、
前記A層中の前記ポリ乳酸系重合体の含有量が50重量%以上であり、
前記A層が、さらに、ポリスチレン系樹脂及び芳香族ポリエステル系樹脂からなる群より選ばれたポリ乳酸系重合体以外の樹脂を10〜50重量%含み、
前記ポリ乳酸系重合体を構成する単量体成分における、全乳酸成分に占めるD−乳酸成分の割合が5重量%以下であり、
前記芳香族ポリエステル系樹脂に用いられる全ジカルボン酸成分中における芳香族ジカルボン酸成分の含有量が60モル%以上であり、
75℃温水中での熱収縮開始1秒後における主配向方向の熱収縮率が3〜23%、さらに90℃、10秒における主配向方向の熱収縮率が40〜84%であることを特徴とするシュリンクラベル。
A shrink label having a printed film and a shrink film having at least one film layer (A layer) comprising a polylactic acid polymer as an essential component,
The shrink film is a single layer shrink film of the A layer,
The content of the polylactic acid polymer in the layer A is 50% by weight or more,
The A layer further contains 10 to 50% by weight of a resin other than a polylactic acid polymer selected from the group consisting of a polystyrene resin and an aromatic polyester resin,
In the monomer component constituting the polylactic acid polymer, the proportion of the D-lactic acid component in the total lactic acid component is 5% by weight or less,
The content of the aromatic dicarboxylic acid component in the total dicarboxylic acid component used in the aromatic polyester-based resin is 60 mol% or more,
The heat shrinkage rate in the main orientation direction at 1 second after the start of heat shrinkage in 75 ° C. warm water is 3 to 23%, and the heat shrinkage rate in the main orientation direction at 90 ° C. and 10 seconds is 40 to 84%. Shrink label.
ポリ乳酸系重合体を必須成分とするフィルム層(A層)を少なくとも1層有するシュリンクフィルム及び印刷層を有するシュリンクラベルであって、
前記シュリンクフィルムが、前記A層の単層シュリンクフィルムであり、
前記A層中の前記ポリ乳酸系重合体の含有量が50重量%以上であり、
前記A層が、さらに、ポリスチレン系樹脂及び芳香族ポリエステル系樹脂からなる群より選ばれたポリ乳酸系重合体以外の樹脂を10〜50重量%含み、
前記ポリ乳酸系重合体を構成する単量体成分における、全乳酸成分に占めるD−乳酸成分の割合が5重量%以下であり、
前記芳香族ポリエステル系樹脂に用いられる全ジカルボン酸成分中における芳香族ジカルボン酸成分の含有量が60モル%以上であり、
75℃温水中での主配向方向の最大熱収縮速度が7〜40%/秒であり、さらに90℃、10秒における主配向方向の熱収縮率が40〜84%であることを特徴とするシュリンクラベル。
A shrink label having a printed film and a shrink film having at least one film layer (A layer) comprising a polylactic acid polymer as an essential component,
The shrink film is a single layer shrink film of the A layer,
The content of the polylactic acid polymer in the layer A is 50% by weight or more,
The A layer further contains 10 to 50% by weight of a resin other than a polylactic acid polymer selected from the group consisting of a polystyrene resin and an aromatic polyester resin,
In the monomer component constituting the polylactic acid polymer, the proportion of the D-lactic acid component in the total lactic acid component is 5% by weight or less,
The content of the aromatic dicarboxylic acid component in the total dicarboxylic acid component used in the aromatic polyester-based resin is 60 mol% or more,
The maximum heat shrinkage rate in the main alignment direction in 75 ° C. warm water is 7 to 40% / second, and the heat shrinkage rate in the main alignment direction at 90 ° C. for 10 seconds is 40 to 84%. Shrink label.
JP2007136157A 2006-05-26 2007-05-23 Shrink label Expired - Fee Related JP5184817B2 (en)