JP5097537B2 - ガラス生産を意図した暗灰色のソーダ石灰シリカガラス組成物 - Google Patents
ガラス生産を意図した暗灰色のソーダ石灰シリカガラス組成物 Download PDFInfo
- Publication number
- JP5097537B2 JP5097537B2 JP2007503382A JP2007503382A JP5097537B2 JP 5097537 B2 JP5097537 B2 JP 5097537B2 JP 2007503382 A JP2007503382 A JP 2007503382A JP 2007503382 A JP2007503382 A JP 2007503382A JP 5097537 B2 JP5097537 B2 JP 5097537B2
- Authority
- JP
- Japan
- Prior art keywords
- glass
- less
- composition according
- composition
- range
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
Fe2O3(全鉄) 0.7ないし0.95%
CoO 50ないし80ppm
NiO 400ないし700ppm
又は
Fe2O3(全鉄) 0.7ないし0.95%
CoO 200ないし300ppm
NiO 1500ないし1900ppm
から本質的になる着色剤を含むガラス組成物によって達成され、該組成物はセレニウムを含まず、0.40以下のレドックスを有し、及び前記ガラスは50%以下の光源Aの下での光透過係数(TLA)及び45%未満の総エネルギー透過係数(TE)を有し、これらは3.85mmの厚さで測定される。
L* について30から80までの範囲内であり、
a* について−15から0までの範囲内であり、及び
b* について−20から+25までの範囲内である。
Fe2O3(全鉄) 0.80ないし0.95%
CoO 50ないし80ppm
NiO 400ないし700ppm
レドックス 0.20ないし0.30
から本質的になる着色剤が含まれる。
Fe2O3(全鉄) 0.80ないし0.95%
CoO 200ないし300ppm
NiO 1500ないし1900ppm
レドックス 0.20ないし0.30
から本質的になる着色剤が含まれる。
SiO2 64ないし75%
Al2O3 0ないし5%
B2O3 0ないし5%
CaO 5ないし15%
MgO 0ないし10%
Na2O 10ないし18%
K2O 0ないし5%
BaO 0ないし5%
を含むガラスマトリクスからなるいずれかのガラス組成物に関する。
T(logη=3.5)−Tliq>20℃
を満たし、なおよりよくは
T(logη=3.5)−Tliq>50℃
を満たす。
R=[300Fe2O3+NiO}/[1200FeO+5CoO]
のように定義され、前記Fe2O3及びFeO含有量が重量%として表され、前記NiO及びCoO含有量がppmで表されれば(Fe2O3はこの式では三価の鉄イオン含有量を表す。)、前記比Rが約2.2よりも大きいとき、青銅色の色合いを有するガラスを得ることができ、前記比が0.6よりも小さいとき、青色の色合いを有するガラスを得ることができる。Rの値がこれらの制限の間にあるとき、好ましくは0.8ないし1.5のとき、前記ガラスは特に有利な中性の色合いを有する。
光源D65の下での色座標L*、a*及びb*、光源Aの下での総体的な光透過係数(TLA)共に380ないし780nmで積分。CIE1931比色定量測定基準オブザーバーによりこれらの計算を実施する。
SiO2 71%
Al2O3 0.70%
CaO 8.90%
MgO 3.80%
Na2O 14.10%
K2O 0.10%
から調製し、その含有量を重量%で表し、これを、添加される着色料の総含有量に符合するためにシリカに関して補正する。
Claims (17)
- 灰色のソーダ石灰ケイ酸塩ガラス組成物であって、
以下の重量範囲内の含有量で以下の化合物、
Fe2O3(全鉄) 0.7ないし0.95%
CoO 50ないし80ppm
NiO 550ppmを超えかつ700ppm以下
又は
Fe2O3(全鉄) 0.7ないし0.95%
CoO 200ないし300ppm
NiO 1500ないし1900ppm
から本質的になる着色剤を含み、
前記組成物はセレニウムを含まず、0.40以下のレドックスを有し、並びに
前記ガラスは、光源Aの下、3.85mmの厚さで測定して、50%以下の光透過係数(TLA)及び45%未満の総エネルギー透過係数(TE)を有する
ことを特徴とする、前記組成物。 - レドックスが0.30を超過しないことを特徴とする、請求項1に記載の組成物。
- 光源Aの下での光透過係数TLAが5%を超過することを特徴とする、請求項1又は2のいずれかに記載の組成物。
- 総エネルギー透過係数TEが30%未満であることを特徴とする、請求項1ないし3のうちの一項に記載の組成物。
- 酸化銅、酸化クロム、酸化チタン、酸化バナジウム及びこれらの混合物から選択される着色料の1%未満をさらに含むことを特徴とする、請求項1ないし4のうちの一項に記載の組成物。
- 酸化銅、酸化クロム、酸化チタン、酸化バナジウム及びこれらの混合物から選択される着色料の0.5%未満をさらに含むことを特徴とする、請求項5に記載の組成物。
- 酸化チタン含有量が0.5%未満であることを特徴とする、請求項5または6に記載の組成物。
- 酸化チタン含有量が0.3%未満であることを特徴とする、請求項7に記載の組成物。
- 着色料として、
Fe2O3(全鉄) 0.80ないし0.95%
CoO 50ないし80ppm
NiO 550ppmを超えかつ700ppm以下
レドックス 0.20ないし0.30
を含み、
ガラスが30ないし45%の光源Aの下での光透過係数(TLA)を有することを特徴とする、請求項1ないし8のうちの一項に記載の組成物。 - 着色料として、
Fe2O3(全鉄) 0.80ないし0.95%
CoO 200ないし300ppm
NiO 1500ないし1900ppm
レドックス 0.20ないし0.30
を含み、
ガラスが6ないし12%の光源Aの下での光透過係数(TLA)を有することを特徴とする、請求項1ないし8のうちの一項に記載の組成物。 - (重量%で)以下の構成成分:
SiO2 64ないし75%
Al2O3 0ないし5%
B2O3 0ないし5%
CaO 5ないし15%
MgO 0ないし10%
Na2O 10ないし18%
K2O 0ないし5%
BaO 0ないし5%
を含むガラスマトリクスからなることを特徴とする、請求項1ないし10のうちの一項に記載の組成物。 - 溶融金属浴でのフロート法により、請求項1ないし11のうちのいずれか一項によって定義される化学組成物を使用して形成されるガラスシート。
- 3.85mmの厚さで光源D65の下に測定される以下の色座標、
L*について30から80までの範囲内、
a*について−15から0までの範囲内、
b*について−20から25までの範囲内
を有することを特徴とする、請求項12に記載のガラスシート。 - 請求項1ないし11のうちのいずれか1つに記載の組成物を使用し、及び3.85mmの厚さで光源D65の下に測定される以下の色座標、
a*について−10から0の範囲内、
b*について−20から+15までの範囲内
を有する、熱的に強化されたガラスシート。 - 前記色座標においてb*について−5から+5までの範囲内である、請求項14に記載の熱的に強化されたガラスシート。
- 赤外線照射を反射するために少なくとも1つの金属酸化物の少なくとも1つの層をさらに含むことを特徴とする、請求項12ないし15のうちの一項に記載のガラスシート。
- 請求項12ないし16のうちの一項に記載の少なくとも1つのガラスシートを含むことを特徴とする窓。