JP5081536B2 - Planographic printing plate precursor and method for producing the same - Google Patents
Planographic printing plate precursor and method for producing the same Download PDFInfo
- Publication number
- JP5081536B2 JP5081536B2 JP2007220024A JP2007220024A JP5081536B2 JP 5081536 B2 JP5081536 B2 JP 5081536B2 JP 2007220024 A JP2007220024 A JP 2007220024A JP 2007220024 A JP2007220024 A JP 2007220024A JP 5081536 B2 JP5081536 B2 JP 5081536B2
- Authority
- JP
- Japan
- Prior art keywords
- group
- printing plate
- alkyl
- lithographic printing
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は平版印刷版原版およびその作製方法に関する。 The present invention relates to a lithographic printing plate precursor and a method for producing the same.
一般に平版印刷版は、親油性の画像部と親水性の非画像部からなる表面を有する。平版印刷は、この版表面に湿し水と油性インキとを交互に与え、水と油が互いに反発する性質を利用して、親水性の非画像部を湿し水受容部(インキ非受容部)とし、親油性の画像部のみにインキを受容させた後、紙等の被印刷体にインキを転写して印刷する方法である。
この平版印刷版を作製するため、従来、親水性の支持体上に親油性の感光層(画像記録層)を設けてなる平版印刷版原版(PS版)が広く用いられている。通常は、平版印刷版原版を、リスフィルム等の原画を通した露光を行った後、画像部となる画像記録層を残存させ、それ以外の不要な画像記録層をアルカリ性現像液または有機溶剤によって溶解して除去することで親水性の支持体の表面を露出させて非画像部を形成する方法により製版を行って、平版印刷版を得ている。
In general, a lithographic printing plate has a surface composed of an oleophilic image portion and a hydrophilic non-image portion. In lithographic printing, dampening water and oil-based ink are alternately applied to the plate surface, and the hydrophilic non-image area is dampened with a dampening water receiving area (ink non-receiving area) by utilizing the property that water and oil repel each other. ), After the ink is received only in the oleophilic image area, the ink is transferred to a printing medium such as paper and printed.
In order to produce this lithographic printing plate, a lithographic printing plate precursor (PS plate) in which an oleophilic photosensitive layer (image recording layer) is provided on a hydrophilic support has been widely used. Usually, after exposing the lithographic printing plate precursor through an original image such as a lithographic film, the image recording layer to be an image portion is left, and the other unnecessary image recording layer is removed with an alkaline developer or an organic solvent. The lithographic printing plate is obtained by carrying out plate making by a method in which the surface of the hydrophilic support is exposed by dissolving and removing to form a non-image portion.
従来の平版印刷版原版の製版工程においては、露光の後、不要な画像記録層を現像液等によって溶解除去する工程が必要であるが、このような付加的に行われる湿式処理を簡易化することが課題の一つとして挙げられている。簡易化の一つとして、中性に近い水溶液または単なる水で現像できることが望まれている。 In the conventional plate making process of a lithographic printing plate precursor, a step of dissolving and removing unnecessary image recording layers with a developer or the like is necessary after exposure, but simplifies such additional wet processing. This is one of the issues. As one of simplification, it is desired that development can be performed with an aqueous solution close to neutrality or simple water.
一方、近年、画像情報を、コンピュータを用いて電子的に処理し、蓄積し、出力する、デジタル化技術が広く普及してきており、このようなデジタル化技術に対応した新しい画像出力方式が種々実用されるようになってきている。これに伴い、レーザー光のような高収斂性の輻射線にデジタル化された画像情報を担持させて、その光で平版印刷版原版を走査露光し、リスフィルムを介することなく、直接平版印刷版を製造するコンピュータ・トゥ・プレート技術が注目されてきている。従って、このような技術に適応した平版印刷版原版を得ることが重要な技術課題の一つとなっている。 On the other hand, in recent years, digitization technology that electronically processes, stores, and outputs image information using a computer has become widespread, and various new image output methods corresponding to such digitization technology have been put into practical use. It has come to be. Along with this, digitized image information is carried by high-convergence radiation such as laser light, and the lithographic printing plate precursor is scanned and exposed with that light, directly without using a lithographic film. Computer-to-plate technology for manufacturing is attracting attention. Accordingly, obtaining a lithographic printing plate precursor adapted to such a technique is one of the important technical issues.
上述のような背景から、現在、製版作業の簡易化とデジタル化の両面への適合が、従来にも増して、強く望まれるようになってきている。 From the background as described above, it is now more strongly desired than ever to adapt both the simplification of the plate making operation and the digitization.
これに対して、例えば、特許文献1には、親水性支持体上に、疎水性前駆体、親水性樹脂、光熱変換剤を含有する画像形成層を有する平版印刷版原版の画像形成層中に、さらにエチレンオキシド鎖を有する化合物を含有することによって、機上現像のほかに、露光、水または適当な水溶液を現像液とする液体現像処理を施して印刷に用いることが可能であると記載されている。 On the other hand, for example, in Patent Document 1, in an image forming layer of a lithographic printing plate precursor having an image forming layer containing a hydrophobic precursor, a hydrophilic resin, and a photothermal conversion agent on a hydrophilic support. In addition to the on-press development, it is further described that by using a compound having an ethylene oxide chain, it can be used for printing after being subjected to exposure, liquid development processing using water or a suitable aqueous solution as a developer. Yes.
また、特許文献2には、(i)親水性支持体、および(ii)ラジカル重合性エチレン状不飽和モノマー、ラジカル重合開始剤および赤外吸収染料を含有し、赤外レーザー露光により硬化し、しかも60質量%以上の水を含有し、pH2.0〜10.0の水性現像液で現像可能な親油性感熱層からなる平版印刷版原版を用意し、赤外レーザーで画像様に露光し、水性現像液で該感熱層の未硬化領域を除くことからなる平版印刷版原版の処理方法が記載されている。 Patent Document 2 contains (i) a hydrophilic support, and (ii) a radical polymerizable ethylenically unsaturated monomer, a radical polymerization initiator and an infrared absorbing dye, and is cured by infrared laser exposure. Moreover, a lithographic printing plate precursor comprising an oleophilic heat-sensitive layer containing 60% by mass or more of water and developable with an aqueous developer having a pH of 2.0 to 10.0 is prepared and exposed imagewise with an infrared laser. A processing method for a lithographic printing plate precursor comprising removing an uncured region of the heat-sensitive layer with an aqueous developer is described.
また、特許文献3には、支持体上に存在する、重合開始剤、重合性化合物、水またはアルカリ水溶液に可溶あるいは膨潤するバインダーを含有する画像記録層またはその他の層に、エチレン性不飽和結合、支持体表面と相互作用する官能基を有するバインダーを含有
することにより、アルカリ現像液使用条件下において高感度、高耐刷で非画像部の汚れ性に優れる平版印刷版原版が得られると記載されている。また特許文献4には、支持体上に画像記録層を有する平版印刷版原板を画像露光した後、擦り部材を備えた現像処理部において、pHが2〜10の現像液の存在下で前記平版印刷版用原板の記録面を前記擦り部材により擦って非露光部の画像記録層を除去する現像工程を含む平版印刷版の作製方法が記載されている。また特許文献5には、親水性支持体上に光重合層を設け露光した後、ガム液によって未露光部を除去する工程を含む印刷版の作成方法が記載されている。
しかしながら、pH2〜10の水性現像液に対する現像性を維持するために、感光層は親水性または高水浸透性であることが必要であるが、露光により硬化した感光層は耐水性や皮膜強度が不十分であり、支持体との接着性が低く、その結果耐刷性がいまだ不十分であった。また、耐刷性を向上させるために未露光膜の親水性を落としたり支持体との密着性を上げると、現像性が低下したり非画像部の汚れが悪化したりするという問題があった。本発明はこれらの点を改良するものである。
すなわち、本発明の目的は、とくにpH2〜10の水性現像液で現像可能であり、非画像部の汚れを防止し、耐刷性に優れる平版印刷版原版およびその作製方法を提供することである。
However, in order to maintain developability with respect to an aqueous developer having a pH of 2 to 10, the photosensitive layer needs to be hydrophilic or highly water-permeable, but the photosensitive layer cured by exposure has water resistance and film strength. Insufficient and poor adhesion to the support, resulting in still insufficient printing durability. In addition, if the hydrophilicity of the unexposed film is reduced or the adhesion to the support is increased in order to improve the printing durability, there is a problem that the developability is deteriorated or the stain of the non-image area is deteriorated. . The present invention improves these points.
That is, an object of the present invention is to provide a lithographic printing plate precursor that can be developed with an aqueous developer having a pH of 2 to 10 in particular, prevents non-image areas from being stained, and has excellent printing durability, and a method for producing the same. .
本発明者らは、感光層またはその他の層に特定の共重合体を含有させることによって上
記課題を解決できることを見出した。すなわち、本発明は以下のとおりである。
<1> 支持体上に、少なくとも(A)開始剤化合物、(B)重合性化合物および(C)バインダーを含有する感光層を設けてなる平版印刷版原版であって、
前記支持体と接する前記感光層またはその他の層が、前記(C)成分とは異なる(D)成分として、下記一般式(D1)で示される繰り返し単位を有する共重合体を含有する平版印刷版原版。
式(D1)中、A 1 は下記式(A1)で示される繰り返し単位を表し、A 2 は下記式(A2)で示される繰り返し単位を表し、A 3 は下記式(A3)で示される繰り返し単位を表し、x、y、zは共重合比を表し、xは1〜80モル%、yは1〜80モル%、zは10〜95モル%である。
式(A1)中、R 101 、R 102 は水素原子、メチル基またはエチル基を表し、R 103 は水素原子、メチル基、−CH 2 −OHまたは−CH 2 −O−CO−(C1〜4アルキル)を表し、R 104 は水素原子、メチル基、−CH 2 −OH、−CH 2 −O−CO−(C1〜4アルキル)、−CO−O−(C1〜4アルキル)または−CO−NH−(C1〜4アルキル)を表し、R 105 、R 106 は水素原子、メチル基またはエチル基を表し、R 107 はメチル基、エチル基またはベンジル基を表し、L 101 は、−CO−O−L0−、−CO−NH−L0−、−二価の芳香族基−または−二価の芳香族基−L0−を表し、L0は二価の脂肪族基、二価の芳香族基またはこれらの組み合わせを表し、L 102 は、以下のLa〜Lqのいずれかを表し、
La:−L0−O−CO−
Lb:−L0−NH−CO−
Lc:−L0−O−
Ld:−L0−CO−O−
Le:−L0−O−CO−O−
Lf:−L0−O−CH 2 −
Lg:−L0−CO−O−CH 2 −
Lh:−L0−O−CO−O−CH 2 −
Li:−L0−O−CO−NH−L0−O−CO−
Lj:−L0−O−CO−L0−O−CO−
Lk:−L0−O−CO−L0−NH−CO−
Ll:−L0−CO−O−L0−O−CO−
Lm:−L0−CO−O−L0−NH−CO−
Ln:−L0−二価の芳香族基−
Lo:−O−CO−二価の芳香族基−
Lp:−O−CO−L0−二価の芳香族基−
Lq:−CO−O−二価の芳香族基−
Lr:−CO−O−L0−二価の芳香族基−
m 101 は0〜3の整数を表し、m 102 は1〜3の整数を表し、m 101 +m 102 =3を満たし、m 101 が2以上のとき、複数のR 107 は同じでも異なっていても良く、m 102 が2以上のとき、複数のR 104 〜R 106 、L 102 はそれぞれ同じでも異なっていても良く、m 102 ×n 101 の値は1〜6であり、X 101 −は−CO 2 −、−PO 3 H−、−O−PO 3 H−または−SO 3 −を表し、Y 101 はn 101 価の炭化水素残基であり、脂肪族、芳香族どちらの構造を含んでも良く、直鎖状、分岐状、環状のどの構造を含んでも良く、環状の場合は単環、多環いずれでも良く、また、炭化水素を構成する炭素−炭素原子に−CO−、−O−、−S−、−N(R 109 )−、−SO 2 −およびそれらの組み合わせからなる構造で中断されていても良く、R 109 は水素原子、メチル基、エチル基、n−プロピル基、i−プロピル基、n−ブチル基またはフェニル基を表す。
<2> 前記その他の層が、前記支持体と前記感光層との間に設けられる下塗り層であることを特徴とする前記<1>に記載の平版印刷版原版。
<3> 前記式(A1)中のL 102 が、La:−L0−O−CO−、Lb:−L0−NH−CO−、Ln:−L0−二価の芳香族基−、Lo:−O−CO−二価の芳香族基−、Lp:−O−CO−L0−二価の芳香族基−、Lq:−CO−O−二価の芳香族基−、Lr:−CO−O−L0−二価の芳香族基−、Lf:−L0−O−CH 2 −、Lg:−L0−CO−O−CH 2 −またはLh:−L0−O−CO−O−CH 2 −であることを特徴とする前記<1>または<2>に記載の平版印刷版原版。
<4> 前記式(A2)中のQで表される支持体表面と相互作用する官能基のうち少なくとも1つが、スルホン酸基若しくはその塩、リン酸エステル基若しくはその塩、または、ホスホン酸基若しくはその塩であることを特徴とする前記<1>〜<3>のいずれか1項に記載の平版印刷版原版。
<5> 前記感光層がさらに、(E)350〜450nmの波長域に極大吸収を有する増感色素を含有することを特徴とする前記<1>〜<4>のいずれか1項に記載の平版印刷版原版。
<6> 前記(C)バインダーの酸価が、0.3meq/g以下であることを特徴とする前記<1>〜<5>のいずれか1項に記載の平版印刷版原版。
<7> 前記<6>に記載の平版印刷版原版を、350nm〜450nmの範囲に発振波長を有する光源を搭載した露光装置を用いて露光した後、擦り部材を備えた自動処理機により、pHが2〜10の現像液の存在下、擦り部材で版面を擦ることにより、非露光部の感光層を除去することを特徴とする平版印刷版の作製方法。
本発明は、上記<1>〜<6>記載の平版印刷版原版及び上記<7>記載の平版印刷版の作製方法に関するものであるが、その他の事項についても参考のために記載する。
(1)支持体上に、少なくとも(A)開始剤化合物、(B)重合性化合物および(C)
バインダーを含有する感光層を設けてなる平版印刷版原版であって、
前記支持体と接する該感光層またはその他の層が、前記(C)成分とは異なる(D)成
分として、(a1)少なくとも1つのエチレン性不飽和結合がイオン対を介して導入され
ている繰り返し単位と、(a2)前記支持体表面と相互作用する官能基を少なくとも1つ
有する繰り返し単位とを有する共重合体を含有する平版印刷版原版。
(2)前記その他の層が、前記支持体と感光層との間に設けられる下塗り層であること
を特徴とする前記(1)に記載の平版印刷版原版。
(3)前記(a1)中のエチレン性不飽和結合を含む構造の少なくとも1つが、(メタ
)アクリル酸エステル、(メタ)アクリル酸アミド、芳香族ビニルまたはアリル基である
ことを特徴とする前記(1)または(2)に記載の平版印刷版原版。
(4) 前記(a2)中の支持体表面と相互作用する官能基のうち少なくとも1つが、
スルホン酸基若しくはその塩、リン酸エステル基若しくはその塩、または、ホスホン酸基
若しくはその塩であることを特徴とする前記(1)〜(3)のいずれかに記載の平版印刷
版原版。
(5)前記(a1)中のイオン対のうち少なくとも1つが、スルホン酸基、リン酸基お
よびホスホン酸基から選択される基のアニオンと、アンモニウムカチオンとの組み合わせ
であることを特徴とする前記(1)〜(4)のいずれかに記載の平版印刷版原版。
(6)前記(D)がさらに、(a3)前記(a1)以外の親水性基を少なくとも1つ有
する繰り返し単位を含有することを特徴とする前記(1)〜(5)のいずれかに記載の平
版印刷版原版。
(7)前記感光層がさらに、(E)350〜450nmの波長域に極大吸収を有する増
感色素を含有することを特徴とする前記(1)〜(6)のいずれかに記載の平版印刷版原
版。
(8)前記(C)バインダーの酸価が、0.3meq/g以下であることを特徴とする
前記(1)〜(6)のいずれかに記載の平版印刷版原版。
(9)前記(8)に記載の平版印刷版原版を、350nm〜450nmの範囲に発振波
長を有する光源を搭載した露光装置を用いて露光した後、擦り部材を備えた自動処理機に
より、pHが2〜10の現像液の存在下、擦り部材で版面を擦ることにより、非露光部の
感光層を除去することを特徴とする平版印刷版の作製方法。
The present inventors have found that the above problem can be solved by including a specific copolymer in the photosensitive layer or other layers. That is, the present invention is as follows.
<1> A lithographic printing plate precursor comprising a photosensitive layer containing at least (A) an initiator compound, (B) a polymerizable compound, and (C) a binder on a support,
The lithographic printing plate wherein the photosensitive layer or other layer in contact with the support contains a copolymer having a repeating unit represented by the following general formula (D1) as a component (D) different from the component (C) Original edition.
Wherein (D1), A 1 represents a repeating unit represented by the following formula (A1), A 2 represents a repeating unit represented by the following formula (A2), repeat A 3 is represented by the following formula (A3) A unit is represented, x, y, z represents a copolymerization ratio, x is 1-80 mol%, y is 1-80 mol%, z is 10-95 mol%.
In formula (A1), R 101 and R 102 represent a hydrogen atom, a methyl group or an ethyl group, and R 103 represents a hydrogen atom, a methyl group, —CH 2 —OH or —CH 2 —O—CO— (C 1 to 4 Alkyl), R 104 represents a hydrogen atom, a methyl group, —CH 2 —OH, —CH 2 —O—CO— (C1-4 alkyl), —CO—O— (C1-4 alkyl) or —CO—. NH— (C1-4 alkyl) is represented, R 105 and R 106 represent a hydrogen atom, a methyl group or an ethyl group, R 107 represents a methyl group, an ethyl group or a benzyl group, and L 101 represents —CO—O. -L0-, -CO-NH-L0-, -divalent aromatic group- or -divalent aromatic group -L0-, wherein L0 is a divalent aliphatic group, divalent aromatic group or represent combinations thereof, L 102 represents one of the following La~Lq,
La: -L0-O-CO-
Lb: -L0-NH-CO-
Lc: -L0-O-
Ld: -L0-CO-O-
Le: -L0-O-CO-O-
Lf: -L0-O-CH 2 -
Lg: -L0-CO-O- CH 2 -
Lh: -L0-O-CO- O-CH 2 -
Li: -L0-O-CO-NH-L0-O-CO-
Lj: -L0-O-CO-L0-O-CO-
Lk: -L0-O-CO-L0-NH-CO-
Ll: -L0-CO-O-L0-O-CO-
Lm: -L0-CO-O-L0-NH-CO-
Ln: -L0-divalent aromatic group-
Lo: —O—CO—divalent aromatic group—
Lp: -O-CO-L0-divalent aromatic group-
Lq: —CO—O—divalent aromatic group—
Lr: -CO-O-L0-divalent aromatic group-
m 101 represents an integer of 0 to 3, m 102 represents an integer of 1 to 3, satisfying m 101 + m 102 = 3, and when m 101 is 2 or more, a plurality of R 107 may be the same or different. well, when m 102 is 2 or more, plural R 104 ~R 106, L 102 may be the same or different from each value of m 102 × n 101 is 1 to 6, X 101 - is -CO 2 -, - PO 3 H - , - O-PO 3 H- or -SO 3 - represents, Y 101 is a hydrocarbon residue of 101 valence n, it may include aliphatic, aromatic either structure , May include any of linear, branched, and cyclic structures, and in the case of a cyclic structure, it may be monocyclic or polycyclic, and the carbon-carbon atom constituting the hydrocarbon may be —CO—, —O—, -S -, - N (R 109 ) -, - SO 2 - and may be interrupted by a structure consisting of combinations, R 109 is a hydrogen atom Methyl group, ethyl group, n- propyl group, an i- propyl, n- butyl group or a phenyl group.
<2> The lithographic printing plate precursor as described in <1>, wherein the other layer is an undercoat layer provided between the support and the photosensitive layer.
<3> L 102 in the formula (A1) is, La: -L0-O-CO- , Lb: -L0-NH-CO-, Ln: -L0- divalent aromatic group -, Lo: - O—CO—Divalent aromatic group—, Lp: —O—CO—L 0 —Divalent aromatic group—, Lq: —CO—O—Divalent aromatic group—, Lr: —CO—O -L0- divalent aromatic group -, Lf: -L0-O- CH 2 -, Lg: -L0-CO-O-CH 2 - or Lh: -L0-O-CO- O-CH 2 - with The lithographic printing plate precursor as described in <1> or <2> above, wherein
<4> At least one of the functional groups that interact with the support surface represented by Q in the formula (A2) is a sulfonic acid group or a salt thereof, a phosphate ester group or a salt thereof, or a phosphonic acid group. Alternatively, the lithographic printing plate precursor as described in any one of <1> to <3> above, which is a salt thereof.
<5> The photosensitive layer according to any one of <1> to <4>, wherein the photosensitive layer further contains (E) a sensitizing dye having a maximum absorption in a wavelength region of 350 to 450 nm. A lithographic printing plate precursor.
<6> The lithographic printing plate precursor as described in any one of <1> to <5> above, wherein the acid value of the (C) binder is 0.3 meq / g or less.
<7> After exposing the lithographic printing plate precursor as described in <6> above using an exposure apparatus equipped with a light source having an oscillation wavelength in the range of 350 nm to 450 nm, the pH is adjusted by an automatic processor equipped with a rubbing member. A method for preparing a lithographic printing plate, comprising removing a photosensitive layer in a non-exposed portion by rubbing the plate surface with a rubbing member in the presence of a developer of 2-10.
The present invention relates to the lithographic printing plate precursor as described in <1> to <6> above and the method for preparing the lithographic printing plate as described in <7> above, but other matters are also described for reference.
(1) On the support, at least (A) an initiator compound, (B) a polymerizable compound, and (C)
A lithographic printing plate precursor provided with a photosensitive layer containing a binder,
The photosensitive layer or other layer in contact with the support is a component (D) different from the component (C), and (a1) at least one ethylenically unsaturated bond is introduced through an ion pair. A lithographic printing plate precursor comprising a copolymer having a unit and (a2) a repeating unit having at least one functional group that interacts with the support surface.
(2) The lithographic printing plate precursor as described in (1) above, wherein the other layer is an undercoat layer provided between the support and the photosensitive layer.
(3) At least one of the structures containing an ethylenically unsaturated bond in (a1) is a (meth) acrylic acid ester, a (meth) acrylic acid amide, an aromatic vinyl or an allyl group, The lithographic printing plate precursor as described in (1) or (2).
(4) At least one of the functional groups that interact with the support surface in (a2) is
The lithographic printing plate precursor as described in any one of (1) to (3) above, which is a sulfonic acid group or a salt thereof, a phosphate ester group or a salt thereof, or a phosphonic acid group or a salt thereof.
(5) At least one of the ion pairs in (a1) is a combination of an anion of a group selected from a sulfonic acid group, a phosphoric acid group and a phosphonic acid group, and an ammonium cation. The lithographic printing plate precursor as described in any one of (1) to (4).
(6) The above (D) further contains (a3) a repeating unit having at least one hydrophilic group other than the above (a1), according to any one of the above (1) to (5), Lithographic printing plate precursor.
(7) The lithographic printing according to any one of (1) to (6), wherein the photosensitive layer further contains (E) a sensitizing dye having a maximum absorption in a wavelength region of 350 to 450 nm. Version original edition.
(8) The lithographic printing plate precursor as described in any one of (1) to (6) above, wherein the acid value of the binder (C) is 0.3 meq / g or less.
(9) The lithographic printing plate precursor as described in (8) above is exposed using an exposure apparatus equipped with a light source having an oscillation wavelength in the range of 350 nm to 450 nm, and then pH is adjusted by an automatic processor equipped with a rubbing member. A method for preparing a lithographic printing plate, comprising removing a photosensitive layer in a non-exposed portion by rubbing the plate surface with a rubbing member in the presence of a developer of 2-10.
また本発明では下記の形態も好ましい。
(10)前記(a2)中の支持体表面と相互作用する官能基のうち少なくとも1つが、アンモニウム基、スルホン酸基またはその塩、リン酸エステル基またはその塩、ホスホン酸基またはその塩、ホウ酸基またはβ−ジケトン基であることを特徴とする前記(1)〜(8)いずれかに記載の平版印刷版原版。
(11)前記(a1)中のアンモニウムカチオンの窒素原子に直接置換している原子が、全て水素原子ではないことを特徴とする前記(5)に記載の平版印刷版原版。
(12)前記(C)バインダーが、側鎖に架橋性基を有する(メタ)アクリル共重合体および側鎖に架橋性基を有するポリウレタン樹脂から選択される少なくとも1種であることを特徴とする、前記(1)〜(8)のいずれかに記載の平版印刷版原版。
(13)前記現像液のpHが、3〜8であることを特徴とする、前記(9)記載の平版印刷版の作製方法。
In the present invention, the following modes are also preferable.
(10) At least one of the functional groups interacting with the support surface in (a2) is an ammonium group, a sulfonic acid group or a salt thereof, a phosphate ester group or a salt thereof, a phosphonic acid group or a salt thereof, The lithographic printing plate precursor as described in any one of (1) to (8) above, which is an acid group or a β-diketone group.
(11) The lithographic printing plate precursor as described in (5) above, wherein the atoms directly substituted with nitrogen atoms of the ammonium cation in (a1) are not all hydrogen atoms.
(12) The (C) binder is at least one selected from a (meth) acrylic copolymer having a crosslinkable group in the side chain and a polyurethane resin having a crosslinkable group in the side chain. The lithographic printing plate precursor as described in any one of (1) to (8) above.
(13) The method of preparing a lithographic printing plate as described in (9) above, wherein the developer has a pH of 3 to 8.
本発明によれば、とくにpH2.0〜10.0の水性現像液で現像可能であり、非画像部の汚れを防止し、耐刷性に優れる平版印刷版原版およびその作製方法を提供することができる。 According to the present invention, a lithographic printing plate precursor that can be developed with an aqueous developer having a pH of 2.0 to 10.0, prevents non-image areas from being stained, and has excellent printing durability, and a method for producing the same. Can do.
〔平版印刷版原版〕
<感光層>
本発明に係る平版印刷版原版の感光層は、(A)開始剤化合物、(B)重合性化合物、(C)バインダー、前記(C)成分とは異なる成分として、(D)(a1)少なくとも1つのエチレン性不飽和結合がイオン対を介して導入されている繰り返し単位と、(a2)前記支持体表面と相互作用する官能基を少なくとも1つ有する繰り返し単位とを有する共重合体を含有する。なお、前記支持体と感光層との間に、その他の層として例えば後述する下塗り層を設ける場合には、感光層は上記(D)成分を含まずに、上記(D)成分を該下塗り層に含有させてもよい。また、本発明の感光層は、必要に応じて、さらにその他の成分を含有することができる。以下、感光層の構成成分について詳細に説明する。
[Lithographic printing plate precursor]
<Photosensitive layer>
The photosensitive layer of the lithographic printing plate precursor according to the invention comprises (A) an initiator compound, (B) a polymerizable compound, (C) a binder, (D) (a1) at least as a component different from the component (C). A copolymer having a repeating unit in which one ethylenically unsaturated bond is introduced through an ion pair, and (a2) a repeating unit having at least one functional group that interacts with the surface of the support. . In the case where, for example, an undercoat layer described later is provided as another layer between the support and the photosensitive layer, the photosensitive layer does not contain the component (D), and the component (D) is added to the primer layer. You may make it contain. Further, the photosensitive layer of the present invention can further contain other components as required. Hereinafter, the components of the photosensitive layer will be described in detail.
(A)開始剤化合物
本発明に用いられる開始剤化合物(重合開始剤)は、光または熱エネルギーによりラジカルを発生し、重合性不飽和基を有する化合物の重合を開始、促進する化合物である。このようなラジカル発生剤としては、公知の重合開始剤や結合解離エネルギーの小さな結合を有する化合物などから、適宜、選択して用いることができる。
(A) Initiator Compound The initiator compound (polymerization initiator) used in the present invention is a compound that initiates and accelerates polymerization of a compound having a polymerizable unsaturated group by generating radicals by light or heat energy. As such a radical generator, a known polymerization initiator or a compound having a bond having a small bond dissociation energy can be appropriately selected and used.
上記のラジカルを発生する化合物としては、例えば、有機ハロゲン化合物、カルボニル化合物、有機過酸化物、アゾ系重合開始剤、アジド化合物、メタロセン化合物、ヘキサアリールビイミダゾール化合物、有機ホウ素化合物、ジスルホン化合物、オキシムエステル化合物、オニウム塩化合物、が挙げられる。 Examples of the compounds that generate radicals include organic halogen compounds, carbonyl compounds, organic peroxides, azo polymerization initiators, azide compounds, metallocene compounds, hexaarylbiimidazole compounds, organic boron compounds, disulfone compounds, and oximes. Examples thereof include ester compounds and onium salt compounds.
上記有機ハロゲン化合物としては、具体的には、若林等、「Bull Chem.Soc Japan」42、2924(1969)、米国特許第3,905,815号明細書、特公昭46−4605号、特開昭48−36281号、特開53−133428号、特開昭55−32070号、特開昭60−239736号、特開昭61−169835号、特開昭61−169837号、特開昭62−58241号、特開昭62−212401号、特開昭63−70243号、特開昭63−298339号の公報、M.P.Hutt,"Journal of Heterocyclic Chemistry",1(No.3)(1970)に記載の化合物が挙げられる。中でも、トリハロメチル基が置換したオキサゾール化合物およびS−トリアジン化合物が好適である。 Specific examples of the organic halogen compound include Wakabayashi et al., “Bull Chem. Soc Japan” 42, 2924 (1969), US Pat. No. 3,905,815, Japanese Patent Publication No. 46-4605, JP 48-36281, JP 53-133428, JP 55-3070, JP 60-239736, JP 61-169835, JP 61-169837, JP 62- 58241, JP-A 62-212401, JP-A 63-70243, JP-A 63-298339, P. The compound as described in Hutt, "Journal of Heterocyclic Chemistry", 1 (No. 3) (1970) is mentioned. Of these, oxazole compounds and S-triazine compounds substituted with a trihalomethyl group are preferred.
より好適には、すくなくとも一つのモノ、ジ、またはトリハロゲン置換メチル基が、s−トリアジン環に結合したs−トリアジン誘導体およびオキサジアゾール環に結合したオキサジアゾール誘導体が挙げられる。具体的には、例えば、2,4,6−トリス(モノクロロメチル)−s−トリアジン、2,4,6−トリス(ジクロロメチル)−s−トリアジン、2,4,6−トリス(トリクロロメチル)−s−トリアジン、2−メチル−4,6−ビス(トリクロロメチル)−s−トリアジン、2―n−プロピル−4,6−ビス(トリクロロメチル)−s−トリアジン、2−(α,α,β−トリクロロエチル)−4,6−ビス(トリクロロメチル)−s−トリアジン、2−(3,4−エポキシフェニル)−4、6−ビス(トリクロロメチル)−s−トリアジン、2−〔1−(p−メトキシフェニル)−2,4−ブタジエニル〕−4,6−ビス(トリクロロメチル)−s−トリアジン、2−スチリル−4,6−ビス(トリクロロメチル)−s−トリアジン、2−(p−メトキシスチリル)−4,6−ビス(トリクロロメチル)−s−トリアジン、2−(p−i−プロピルオキシスチリル)−4、6−ビス(トリクロロメチル)−s−トリアジン、2−(p−トリル)−4,6−ビス(トリクロロメチル)−s−トリアジン、2−(4−メトキシナフチル)−4,6−ビス(トリクロロメチル)−s−トリアジン、2−フェニルチオ−4,6−ビス(トリクロロメチル)−s−トリアジン、2−ベンジルチオ−4,6−ビス(トリクロロメチル)−s−トリアジン、2,4,6−トリス(ジブロモメチル)−s−トリアジン、2,4,6−トリス(トリブロモメチル)−s−トリアジン、2−メチル−4,6−ビス(トリブロモメチル)−s−トリアジン、2−メトキシ−4,6−ビス(トリブロモメチル)−s−トリアジンや下記化合物等が挙げられる。 More preferable examples include s-triazine derivatives in which at least one mono, di, or trihalogen-substituted methyl group is bonded to the s-triazine ring, and oxadiazole derivatives in which the oxadiazole ring is bonded. Specifically, for example, 2,4,6-tris (monochloromethyl) -s-triazine, 2,4,6-tris (dichloromethyl) -s-triazine, 2,4,6-tris (trichloromethyl) -S-triazine, 2-methyl-4,6-bis (trichloromethyl) -s-triazine, 2-n-propyl-4,6-bis (trichloromethyl) -s-triazine, 2- (α, α, β-trichloroethyl) -4,6-bis (trichloromethyl) -s-triazine, 2- (3,4-epoxyphenyl) -4,6-bis (trichloromethyl) -s-triazine, 2- [1- (P-methoxyphenyl) -2,4-butadienyl] -4,6-bis (trichloromethyl) -s-triazine, 2-styryl-4,6-bis (trichloromethyl) -s-triazine, 2- ( -Methoxystyryl) -4,6-bis (trichloromethyl) -s-triazine, 2- (pi-propyloxystyryl) -4,6-bis (trichloromethyl) -s-triazine, 2- (p- Tolyl) -4,6-bis (trichloromethyl) -s-triazine, 2- (4-methoxynaphthyl) -4,6-bis (trichloromethyl) -s-triazine, 2-phenylthio-4,6-bis ( Trichloromethyl) -s-triazine, 2-benzylthio-4,6-bis (trichloromethyl) -s-triazine, 2,4,6-tris (dibromomethyl) -s-triazine, 2,4,6-tris ( Tribromomethyl) -s-triazine, 2-methyl-4,6-bis (tribromomethyl) -s-triazine, 2-methoxy-4,6-bis (tribromomethyl) Etc. -s- triazine and the following compounds.
上記カルボニル化合物としては、ベンゾフェノン、ミヒラーケトン、2−メチルベンゾフェノン、3−メチルベンゾフェノン、4−メチルベンゾフェノン、2−クロロベンゾフェノン、4−ブロモベンゾフェノン、2−カルボキシベンゾフェノン等のベンゾフェノン誘導体、2,2−ジメトキシ−2−フェニルアセトフェノン、2,2−ジエトキシアセトフェノン、1−ヒドロキシシクロヘキシルフェニルケトン、α−ヒドトキシ−2−メチルフェニルプロパノン、1−ヒドロキシ−1−メチルエチル−(p−イソプロピルフェニル)ケトン、1−ヒドロキシ−1−(p−ドデシルフェニル)ケトン、2−メチル−(4'−(メチルチオ)フェニル)−2−モルホリノ−1−プロパノン、1,1,1−トリクロロメチル−(p−ブチルフェニル)ケトン等のアセトフェノン誘導体、チオキサントン、2−エチルチオキサントン、2−イソプロピルチオキサントン、2−クロロチオキサントン、2,4−ジメチルチオキサントン、2,4−ジエチルチオキサントン、2,4−ジイソプロピルチオキサントン等のチオキサントン誘導体、p−ジメチルアミノ安息香酸エチル、p−ジエチルアミノ安息香酸エチル等の安息香酸エステル誘導体等を挙げることができる。 Examples of the carbonyl compound include benzophenone, Michler ketone, 2-methylbenzophenone, 3-methylbenzophenone, 4-methylbenzophenone, 2-chlorobenzophenone, 4-bromobenzophenone, 2-carboxybenzophenone and other benzophenone derivatives, 2,2-dimethoxy- 2-phenylacetophenone, 2,2-diethoxyacetophenone, 1-hydroxycyclohexyl phenyl ketone, α-hydroxy-2-methylphenylpropanone, 1-hydroxy-1-methylethyl- (p-isopropylphenyl) ketone, 1- Hydroxy-1- (p-dodecylphenyl) ketone, 2-methyl- (4 ′-(methylthio) phenyl) -2-morpholino-1-propanone, 1,1,1-trichloromethyl- (p-butylphenyl) Acetophenone derivatives such as ketones, thioxanthone derivatives such as thioxanthone, 2-ethylthioxanthone, 2-isopropylthioxanthone, 2-chlorothioxanthone, 2,4-dimethylthioxanthone, 2,4-diethylthioxanthone, 2,4-diisopropylthioxanthone, p- Examples thereof include benzoic acid ester derivatives such as ethyl dimethylaminobenzoate and ethyl p-diethylaminobenzoate.
上記アゾ化合物としては例えば、特開平8−108621号公報に記載のアゾ化合物等を使用することができる。 As the azo compound, for example, an azo compound described in JP-A-8-108621 can be used.
上記有機過酸化物としては、例えば、トリメチルシクロヘキサノンパーオキサイド、アセチルアセトンパーオキサイド、1,1−ビス(tert−ブチルパーオキシ)−3,3,5−トリメチルシクロヘキサン、1,1−ビス(tert−ブチルパーオキシ)シクロヘキサン、2,2−ビス(tert−ブチルパーオキシ)ブタン、tert−ブチルハイ
ドロパーオキサイド、クメンハイドロパーオキサイド、ジイソプロピルベンゼンハイドロパーオキサイド、2,5−ジメチルヘキサン−2,5−ジハイドロパーオキサイド、1,1,3,3−テトラメチルブチルハイドロパーオキサイド、tert−ブチルクミルパーオキサイド、ジクミルパーオキサイド、2,5−ジメチル−2,5−ジ(tert−ブチルパーオキシ)ヘキサン、2,5−オキサノイルパーオキサイド、過酸化こはく酸、過酸化ベンゾイル、2,4−ジクロロベンゾイルパーオキサイド、ジイソプロピルパーオキシジカーボネート、ジ−2−エチルヘキシルパーオキシジカーボネート、ジ−2−エトキシエチルパーオキシジカーボネート、ジメトキシイソプロピルパーオキシカーボネート、ジ(3−メチル−3−メトキシブチル)パーオキシジカーボネート、tert−ブチルパーオキシアセテート、tert−ブチルパーオキシピバレート、tert−ブチルパーオキシネオデカノエート、tert−ブチルパーオキシオクタノエート、tert−ブチルパーオキシラウレート、ターシルカーボネート、3,3',4,4'−テトラ−(t−ブチルパーオキシカルボニル)ベンゾフェノン、3,3',4,4'−テトラ−(t−ヘキシルパーオキシカルボニル)ベンゾフェノン、3,3',4,4'−テトラ−(p−イソプロピルクミルパーオキシカルボニル)ベンゾフェノン、カルボニルジ(t−ブチルパーオキシ二水素二フタレート)、カルボニルジ(t−ヘキシルパーオキシ二水素二フタレート)等が挙げられる。
Examples of the organic peroxide include trimethylcyclohexanone peroxide, acetylacetone peroxide, 1,1-bis (tert-butylperoxy) -3,3,5-trimethylcyclohexane, 1,1-bis (tert-butyl). Peroxy) cyclohexane, 2,2-bis (tert-butylperoxy) butane, tert-butyl hydroperoxide, cumene hydroperoxide, diisopropylbenzene hydroperoxide, 2,5-dimethylhexane-2,5-dihydro Peroxide, 1,1,3,3-tetramethylbutyl hydroperoxide, tert-butylcumyl peroxide, dicumyl peroxide, 2,5-dimethyl-2,5-di (tert-butylperoxy) hexane, 2, -Oxanoyl peroxide, succinic peroxide, benzoyl peroxide, 2,4-dichlorobenzoyl peroxide, diisopropyl peroxydicarbonate, di-2-ethylhexyl peroxydicarbonate, di-2-ethoxyethyl peroxydicarbonate , Dimethoxyisopropyl peroxycarbonate, di (3-methyl-3-methoxybutyl) peroxydicarbonate, tert-butyl peroxyacetate, tert-butyl peroxypivalate, tert-butyl peroxyneodecanoate, tert- Butyl peroxyoctanoate, tert-butyl peroxylaurate, tersyl carbonate, 3,3 ′, 4,4′-tetra- (t-butylperoxycarbonyl) benzophenone, 3,3 ′, 4,4 ′ − Tra- (t-hexylperoxycarbonyl) benzophenone, 3,3 ′, 4,4′-tetra- (p-isopropylcumylperoxycarbonyl) benzophenone, carbonyldi (t-butylperoxydihydrogen diphthalate), carbonyl And di (t-hexylperoxydihydrogen diphthalate).
上記メタロセン化合物としては、特開昭59−152396号公報、特開昭61−151197号公報、特開昭63−41484号公報、特開平2−249号公報、特開平2−4705号公報、特開平5−83588号公報記載の種々のチタノセン化合物、例えば、ジ−シクロペンタジエニル−Ti−ビス−フェニル、ジ−シクロペンタジエニル−Ti−ビス−2,6−ジフルオロフェニ−1−イル、ジ−シクロペンタジエニル−Ti−ビス−2,4−ジ−フルオロフェニ−1−イル、ジ−シクロペンタジエニル−Ti−ビス−2,4,6−トリフルオロフェニ−1−イル、ジ−シクロペンタジエニル−Ti−ビス−2,3,5,6−テトラフルオロフェニ−1−イル、ジ−シクロペンタジエニル−Ti−ビス−2,3,4,5,6−ペンタフルオロフェニ−1−イル、ジ−メチルシクロペンタジエニル−Ti−ビス−2,6−ジフルオロフェニ−1−イル、ジ−メチルシクロペンタジエニル−Ti−ビス−2,4,6−トリフルオロフェニ−1−イル、ジ−メチルシクロペンタジエニル−Ti−ビス−2,3,5,6−テトラフルオロフェニ−1−イル、ジ−メチルシクロペンタジエニル−Ti−ビス−2,3,4,5,6−ペンタフルオロフェニ−1−イル、ビス(シクロペンタジエニル)−ビス(2,6−ジフルオロ−3−(ピル−1−イル)フェニル)チタニウム、特開平1−304453号公報、特開平1−152109号公報記載の鉄−アレーン錯体等が挙げられる。 Examples of the metallocene compound include JP-A-59-152396, JP-A-61-151197, JP-A-63-41484, JP-A-2-249, JP-A-2-4705, Various titanocene compounds described in JP-A-5-83588, such as di-cyclopentadienyl-Ti-bis-phenyl, di-cyclopentadienyl-Ti-bis-2,6-difluorophen-1-yl, Di-cyclopentadienyl-Ti-bis-2,4-di-fluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2,4,6-trifluorophen-1-yl, di- -Cyclopentadienyl-Ti-bis-2,3,5,6-tetrafluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2,3,4,5,6-penta Fluorophen-1-yl, di-methylcyclopentadienyl-Ti-bis-2,6-difluorophen-1-yl, di-methylcyclopentadienyl-Ti-bis-2,4,6-trifluoropheny -1-yl, di-methylcyclopentadienyl-Ti-bis-2,3,5,6-tetrafluorophen-1-yl, di-methylcyclopentadienyl-Ti-bis-2,3,4 , 5,6-pentafluorophen-1-yl, bis (cyclopentadienyl) -bis (2,6-difluoro-3- (pyr-1-yl) phenyl) titanium, JP-A-1-304453, Examples thereof include iron-arene complexes described in JP-A-1-152109.
上記ヘキサアリールビイミダゾール化合物としては、例えば、特公平6−29285号公報、米国特許第3,479,185号、同第4,311,783号、同第4,622,286号の明細書等に記載の種々の化合物、具体的には、2,2'−ビス(o−クロロフ
ェニル)−4,4',5,5'−テトラフェニルビイミダゾール、2,2'−ビス(o−ブ
ロモフェニル))4,4',5,5'−テトラフェニルビイミダゾール、2,2'−ビス(
o,p−ジクロロフェニル)−4,4',5,5'−テトラフェニルビイミダゾール、2,2'−ビス(o−クロロフェニル)−4,4',5,5'−テトラ(m−メトキシフェニル
)ビイジダゾール、2,2'−ビス(o,o'−ジクロロフェニル)−4,4',5,5'−テトラフェニルビイミダゾール、2,2'−ビス(o−ニトロフェニル)−4,4',5,5'−テトラフェニルビイミダゾール、2,2'−ビス(o−メチルフェニル)−4,4'
,5,5'−テトラフェニルビイミダゾール、2,2'−ビス(o−トリフルオロフェニル)−4,4',5,5'−テトラフェニルビイミダゾール等が挙げられる。
Examples of the hexaarylbiimidazole compound include, for example, Japanese Patent Publication No. 6-29285, U.S. Pat. Nos. 3,479,185, 4,311,783, and 4,622,286. And, specifically, 2,2′-bis (o-chlorophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole, 2,2′-bis (o-bromophenyl) )) 4,4 ′, 5,5′-tetraphenylbiimidazole, 2,2′-bis (
o, p-dichlorophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole, 2,2′-bis (o-chlorophenyl) -4,4 ′, 5,5′-tetra (m-methoxyphenyl) ) Bididazole, 2,2′-bis (o, o′-dichlorophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole, 2,2′-bis (o-nitrophenyl) -4,4 ′ , 5,5'-tetraphenylbiimidazole, 2,2'-bis (o-methylphenyl) -4,4 '
, 5,5′-tetraphenylbiimidazole, 2,2′-bis (o-trifluorophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole, and the like.
上記有機ホウ素化合物としては、例えば、特開昭62−143044号、特開昭62−150242号、特開平9−188685号、特開平9−188686号、特開平9−1
88710号、特開2000−131837号、特開2002−107916号の公報、特許第2764769号明細書、特開2002−116539号公報、および、Kunz,Martin"Rad Tech'98.Proceeding April 19−22,1998,Chicago"等に記載される有機ホウ酸塩、特開平6−157623
号公報、特開平6−175564号公報、特開平6−175561号公報に記載の有機ホウ素スルホニウム錯体あるいは有機ホウ素オキソスルホニウム錯体、特開平6−175554号公報、特開平6−175553号公報に記載の有機ホウ素ヨードニウム錯体、特開平9−188710号公報に記載の有機ホウ素ホスホニウム錯体、特開平6−348011号公報、特開平7−128785号公報、特開平7−140589号公報、特開平7−306527号公報、特開平7−292014号公報等の有機ホウ素遷移金属配位錯体等が挙げられる。
Examples of the organic boron compound include, for example, JP-A-62-143044, JP-A-62-1050242, JP-A-9-188865, JP-A-9-188686, and JP-A-9-1.
88710, JP 2000-131837, JP 2002-107916, JP 2764769, JP 2002-116539, and Kunz, Martin "Rad Tech '98. Proceeding April 19-22. , 1998, Chicago ", etc., JP-A-6-157623
Organoboron sulfonium complexes or organoboron oxosulfonium complexes described in JP-A-6-175564, JP-A-6-175561, JP-A-6-175554, and JP-A-6-175553. Organoboron iodonium complexes, organoboron phosphonium complexes described in JP-A-9-188710, JP-A-6-348011, JP-A-7-128785, JP-A-7-140589, JP-A-7-306527 Examples thereof include organoboron transition metal coordination complexes described in JP-A-7-292014.
上記ジスルホン化合物としては、特開昭61−166544号公報、特開2003−328465号公報等記載される化合物が挙げられる。 Examples of the disulfone compound include compounds described in JP-A Nos. 61-166544 and 2003-328465.
上記オキシムエステル化合物としては、J.C.S. Perkin II (1979 )1653-1660)、J.C.S.Perkin II (1979)156-162、Journal of Photopolymer Science and Technology(1995)202-232、特開2000−66385号公報記載の化合物、特開2000−80068号公報記載の化合物が挙げられる。具体例としては、下記の構造式で示される化合物が挙げられる。 Examples of the oxime ester compound include JCS Perkin II (1979) 1653-1660), JCSPerkin II (1979) 156-162, Journal of Photopolymer Science and Technology (1995) 202-232, and JP-A 2000-66385. And compounds described in JP 2000-80068 A. Specific examples include compounds represented by the following structural formula.
上記オニウム塩化合物としては、例えば、S.I.Schlesinger,Photogr.Sci.Eng.,18,387(1974)、T.S.Bal et al,Polymer,21,423(1980)に記載のジアゾニウム塩、米国特許第4,069,055号明細書、特開平4−365049号公報等に記載のアンモニウム塩、米国特許第4,069,055号、同第4,069,056号の明細書に記載のホスホニウム塩、欧州特許第104、143号、米国特許第339,049号、同第410,201号の明細書、特開平2−150848号、特開平2−296514号の公報に記載のヨードニウム塩、欧州特許第370,693号、同第390,214号、同第233,567号、同第297,443号、同第297,442号、米国特許第4,933,377号、同第161,811号、同第410,201号、同第339,049号、同第4,760,013号、同第4,734,444号、同第2,833,827号、独国特許第2,904,626号、同第3,604,580号、同第3,604,581号の明細書に記載のスルホニウム塩、J.V.Crivello et al,Macromolecules,10(6),1307(1977)、J.V.Crivello et al,J.Polymer Sci.,Polymer Chem.Ed.,17,1047(1979)に記載のセレノニウム塩、C.S.Wen et al,Teh,Proc.Conf.Rad.Curing ASIA,p478 Tokyo,Oct(1988)に記載のアルソニウム塩等のオニウム塩等が挙げられる。 Examples of the onium salt compound include S.I. I. Schlesinger, Photogr. Sci. Eng. 18, 387 (1974), T .; S. Diazonium salts described in Bal et al, Polymer, 21, 423 (1980), ammonium salts described in US Pat. No. 4,069,055, JP-A-4-365049, etc., US Pat. No. 4,069 , 055, 4,069,056, phosphonium salts described in European Patent Nos. 104,143, US Pat. Nos. 339,049, 410,201, JP -150848, JP-A-2-296514, iodonium salts, European Patent Nos. 370,693, 390,214, 233,567, 297,443, and 297 442, U.S. Pat. Nos. 4,933,377, 161,811, 410,201, 339,049, 4,760,013 No. 4,734,444, No. 2,833,827, German Patent No. 2,904,626, No. 3,604,580, No. 3,604,581 Or a sulfonium salt described in J. V. Crivello et al, Macromolecules, 10 (6), 1307 (1977), J. MoI. V. Crivello et al, J.A. Polymer Sci. , Polymer Chem. Ed. , 17, 1047 (1979), a selenonium salt described in C.I. S. Wen et al, Teh, Proc. Conf. Rad. Curing ASIA, p478 Tokyo, Oct (1988), and onium salts such as arsonium salts.
本発明において、これらのオニウム塩は酸発生剤ではなく、イオン性のラジカル重合開始剤として機能する。
本発明において好適に用いられるオニウム塩は、下記一般式(RI−I)〜(RI−II
I)で表されるオニウム塩である。
In the present invention, these onium salts function not as acid generators but as ionic radical polymerization initiators.
The onium salts preferably used in the present invention are represented by the following general formulas (RI-I) to (RI-II).
An onium salt represented by I).
式(RI−I)中、Ar11は置換基を1〜6個有していてもよい炭素数20以下のアリール基を表し、好ましい置換基としては炭素数1〜12のアルキル基、炭素数1〜12のアルケニル基、炭素数1〜12のアルキニル基、炭素数1〜12のアリール基、炭素数1〜12のアルコキシ基、炭素数1〜12のアリーロキシ基、ハロゲン原子、炭素数1〜12のアルキルアミノ基、炭素数1〜12のジアルキルアミノ基、炭素数1〜12のアルキルアミド基またはアリールアミド基、カルボニル基、カルボキシル基、シアノ基、スルホニル基、炭素数1〜12のチオアルキル基、炭素数1〜12のチオアリール基が挙げられる。Z11 -は1価の陰イオンを表し、具体的には、ハロゲンイオン、過塩素酸イオン、ヘキサフルオロホスフェートイオン、テトラフルオロボレートイオン、スルホン酸イオン、スルフィン酸イオン、チオスルホン酸イオン、硫酸イオンが挙げられる。中でも安定性の面から、過塩素酸イオン、ヘキサフルオロホスフェートイオン、テトラフルオロボレートイオン、スルホン酸イオンおよびスルフィン酸イオンが好ましい。 In the formula (RI-I), Ar 11 represents an aryl group having 20 or less carbon atoms which may have 1 to 6 substituents, and preferred substituents include an alkyl group having 1 to 12 carbon atoms and a carbon number. 1-12 alkenyl group, C1-C12 alkynyl group, C1-C12 aryl group, C1-C12 alkoxy group, C1-C12 aryloxy group, halogen atom, C1-C1 12 alkylamino groups, C1-C12 dialkylamino groups, C1-C12 alkylamide groups or arylamide groups, carbonyl groups, carboxyl groups, cyano groups, sulfonyl groups, C1-C12 thioalkyl groups And a thioaryl group having 1 to 12 carbon atoms. Z 11 - represents a monovalent anion, specifically a halogen ion, perchlorate ion, hexafluorophosphate ion, tetrafluoroborate ion, sulfonate ion, sulfinate ion, thiosulfonate ion, a sulfate ion Can be mentioned. Among these, perchlorate ion, hexafluorophosphate ion, tetrafluoroborate ion, sulfonate ion and sulfinate ion are preferable from the viewpoint of stability.
式(RI−II)中、Ar21およびAr22は、各々独立に置換基を1〜6個有していてもよい炭素数20以下のアリール基を表し、好ましい置換基としては炭素数1〜12のアル
キル基、炭素数1〜12のアルケニル基、炭素数1〜12のアルキニル基、炭素数1〜12のアリール基、炭素数1〜12のアルコキシ基、炭素数1〜12のアリーロキシ基、ハロゲン原子、炭素数1〜12のアルキルアミノ基、炭素数1〜12のジアルキルアミノ基、炭素数1〜12のアルキルアミド基またはアリールアミド基、カルボニル基、カルボキシル基、シアノ基、スルホニル基、炭素数1〜12のチオアルキル基、炭素数1〜12のチオアリール基が挙げられる。Z21 -は1価の陰イオンを表す。具体的には、ハロゲンイオン、過塩素酸イオン、ヘキサフルオロホスフェートイオン、テトラフルオロボレートイオン、スルホン酸イオン、スルフィン酸イオン、チオスルホン酸イオン、硫酸イオンが挙げられる。中でも、安定性、反応性の面から過塩素酸イオン、ヘキサフルオロホスフェートイオン、テトラフルオロボレートイオン、スルホン酸イオン、スルフィン酸イオン、カルボン酸イオンが好ましい。
In the formula (RI-II), Ar 21 and Ar 22 each independently represent an aryl group having 20 or less carbon atoms which may have 1 to 6 substituents, and preferred substituents include 1 to 1 carbon atoms. 12 alkyl groups, an alkenyl group having 1 to 12 carbon atoms, an alkynyl group having 1 to 12 carbon atoms, an aryl group having 1 to 12 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, an aryloxy group having 1 to 12 carbon atoms, Halogen atom, C1-C12 alkylamino group, C1-C12 dialkylamino group, C1-C12 alkylamide group or arylamide group, carbonyl group, carboxyl group, cyano group, sulfonyl group, carbon Examples thereof include a thioalkyl group having 1 to 12 carbon atoms and a thioaryl group having 1 to 12 carbon atoms. Z 21 - represents a monovalent anion. Specific examples include halogen ions, perchlorate ions, hexafluorophosphate ions, tetrafluoroborate ions, sulfonate ions, sulfinate ions, thiosulfonate ions, and sulfate ions. Among these, perchlorate ion, hexafluorophosphate ion, tetrafluoroborate ion, sulfonate ion, sulfinate ion, and carboxylate ion are preferable from the viewpoint of stability and reactivity.
式(RI−III)中、R31、R32およびR33は、各々独立に置換基を1〜6個有していてもよい炭素数20以下のアリール基、アルキル基、アルケニル基、またはアルキニル基を表す。中でも反応性、安定性の面から好ましいのは、アリール基である。置換基としては、炭素数1〜12のアルキル基、炭素数1〜12のアルケニル基、炭素数1〜12のアルキニル基、炭素数1〜12のアリール基、炭素数1〜12のアルコキシ基、炭素数1〜12のアリーロキシ基、ハロゲン原子、炭素数1〜12のアルキルアミノ基、炭素数1〜12のジアルキルアミノ基、炭素数1〜12のアルキルアミド基またはアリールアミド基、カルボニル基、カルボキシル基、シアノ基、スルホニル基、炭素数1〜12のチオアルキル基、炭素数1〜12のチオアリール基が挙げられる。Z31 -は1価の陰イオンを表
す。具体例としては、ハロゲンイオン、過塩素酸イオン、ヘキサフルオロホスフェートイオン、テトラフルオロボレートイオン、スルホン酸イオン、スルフィン酸イオン、チオスルホン酸イオン、硫酸イオンが挙げられる。中でも安定性、反応性の面から、過塩素酸イオン、ヘキサフルオロホスフェートイオン、テトラフルオロボレートイオン、スルホン酸イオン、スルフィン酸イオン、カルボン酸イオンが好ましい。より好ましいものとして特開2001−343742号公報記載のカルボン酸イオン、特に好ましいものとして特開2002−148790号公報記載のカルボン酸イオンが挙げられる。
In the formula (RI-III), R 31 , R 32 and R 33 are each independently an aryl group, alkyl group, alkenyl group or alkynyl having 20 or less carbon atoms, which may have 1 to 6 substituents. Represents a group. Among them, an aryl group is preferable from the viewpoint of reactivity and stability. Examples of the substituent include an alkyl group having 1 to 12 carbon atoms, an alkenyl group having 1 to 12 carbon atoms, an alkynyl group having 1 to 12 carbon atoms, an aryl group having 1 to 12 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, Aryloxy group having 1 to 12 carbon atoms, halogen atom, alkylamino group having 1 to 12 carbon atoms, dialkylamino group having 1 to 12 carbon atoms, alkylamide group or arylamide group having 1 to 12 carbon atoms, carbonyl group, carboxyl Group, a cyano group, a sulfonyl group, a thioalkyl group having 1 to 12 carbon atoms, and a thioaryl group having 1 to 12 carbon atoms. Z 31 - represents a monovalent anion. Specific examples include halogen ions, perchlorate ions, hexafluorophosphate ions, tetrafluoroborate ions, sulfonate ions, sulfinate ions, thiosulfonate ions, and sulfate ions. Among these, perchlorate ion, hexafluorophosphate ion, tetrafluoroborate ion, sulfonate ion, sulfinate ion, and carboxylate ion are preferable from the viewpoints of stability and reactivity. More preferred are the carboxylate ions described in JP-A No. 2001-343742, and particularly preferred are the carboxylate ions described in JP-A No. 2002-148790.
重合開始剤としては、上記に限定されないが、特に反応性、安定性の面から、トリアジン系開始剤、有機ハロゲン化合物、オキシムエステル化合物、メタロセン化合物、ヘキサアリールビイミダゾール化合物、有機ホウ素化合物、ジアゾニウム塩、ヨードニウム塩、スルホニウム塩がより好ましい。 The polymerization initiator is not limited to the above, but particularly from the viewpoint of reactivity and stability, a triazine-based initiator, an organic halogen compound, an oxime ester compound, a metallocene compound, a hexaarylbiimidazole compound, an organic boron compound, a diazonium salt. More preferred are iodonium salts and sulfonium salts.
これらの重合開始剤は、1種のみを用いてもよいし、2種以上を併用してもよい。また、これらの重合開始剤は他の成分と同一の層に添加してもよいし、別の層を設けそこに添加してもよい。これらの重合開始剤は、感光層を構成する全固形分に対し0.1〜50質量%が好ましく、より好ましくは0.5〜30質量%、特に好ましくは0.8〜20質量%の割合で添加することができる。 These polymerization initiators may be used alone or in combination of two or more. Moreover, these polymerization initiators may be added to the same layer as other components, or another layer may be provided and added thereto. These polymerization initiators are preferably from 0.1 to 50% by mass, more preferably from 0.5 to 30% by mass, particularly preferably from 0.8 to 20% by mass, based on the total solid content constituting the photosensitive layer. Can be added.
(B)重合性化合物
本発明における感光層に用いる重合性化合物は、少なくとも一個のエチレン性不飽和二重結合を有する付加重合性化合物であり、末端エチレン性不飽和結合を少なくとも1個、好ましくは2個以上有する化合物から選ばれる。このような化合物群は当該産業分野において広く知られるものであり、本発明においてはこれらを特に限定無く用いることができる。これらは、例えばモノマー、プレポリマー、すなわち2量体、3量体およびオリゴマー、またはそれらの共重合体、またはそれらの混合物などの化学的形態をもつ。モノマーの例としては、不飽和カルボン酸(例えば、アクリル酸、メタクリル酸、イタコン酸、クロトン酸、イソクロトン酸、マレイン酸など)や、そのエステル類、アミド類が挙げられ、好ましくは、不飽和カルボン酸と脂肪族多価アルコール化合物とのエステル、不飽和カルボン酸と脂肪族多価アミン化合物とのアミド類が用いられる。また、ヒドロキシル基やアミノ基、メルカプト基等の求核性置換基を有する不飽和カルボン酸エステル或いはアミド類と単官能もしくは多官能イソシアネート類或いはエポキシ類との付加反応物、および単官能もしくは、多官能のカルボン酸との脱水縮合反応物等も好適に使用される。また、イソシアネート基や、エポキシ基等の親電子性置換基を有する不飽和カルボン酸エステル或いはアミド類と単官能もしくは多官能のアルコール類、アミン類、チオール類との付加反応物、更にハロゲン基や、トシルオキシ基等の脱離性置換基を有する不飽和カルボン酸エステル或いはアミド類と単官能もしくは多官能のアルコール類、アミン類、チオール類との置換反応物も好適である。また、別の例として、上記の不飽和カルボン酸の代わりに、不飽和ホスホン酸、スチレン、ビニルエーテル等に置き換えた化合物群を使用することも可能である。
(B) Polymerizable compound The polymerizable compound used in the photosensitive layer in the invention is an addition polymerizable compound having at least one ethylenically unsaturated double bond, and preferably has at least one terminal ethylenically unsaturated bond, preferably It is selected from compounds having two or more. Such a compound group is widely known in the industrial field, and can be used without any particular limitation in the present invention. These have chemical forms such as monomers, prepolymers, i.e. dimers, trimers and oligomers, or copolymers thereof, or mixtures thereof. Examples of monomers include unsaturated carboxylic acids (for example, acrylic acid, methacrylic acid, itaconic acid, crotonic acid, isocrotonic acid, maleic acid, etc.), esters and amides thereof, preferably unsaturated carboxylic acids. An ester of an acid and an aliphatic polyhydric alcohol compound and an amide of an unsaturated carboxylic acid and an aliphatic polyamine compound are used. In addition, an addition reaction product of an unsaturated carboxylic acid ester or amide having a nucleophilic substituent such as a hydroxyl group, amino group or mercapto group with a monofunctional or polyfunctional isocyanate or epoxy, and monofunctional or polyfunctional A dehydration condensation reaction product with a functional carboxylic acid is also preferably used. Further, an addition reaction product of an unsaturated carboxylic acid ester or amide having an electrophilic substituent such as an epoxy group or an epoxy group with a monofunctional or polyfunctional alcohol, amine or thiol, a halogen group or In addition, a substitution reaction product of an unsaturated carboxylic acid ester or amide having a leaving substituent such as a tosyloxy group and a monofunctional or polyfunctional alcohol, amine or thiol is also suitable. As another example, it is also possible to use a group of compounds substituted with unsaturated phosphonic acid, styrene, vinyl ether or the like instead of the unsaturated carboxylic acid.
脂肪族多価アルコール化合物と不飽和カルボン酸とのエステルのモノマーの具体例としては、アクリル酸エステルとして、エチレングリコールジアクリレート、トリエチレングリコールジアクリレート、1,3−ブタンジオールジアクリレート、テトラメチレングリコールジアクリレート、プロピレングリコールジアクリレート、ネオペンチルグリコールジアクリレート、トリメチロールプロパントリアクリレート、トリメチロールプロパントリ(アクリロイルオキシプロピル)エーテル、トリメチロールエタントリアクリレート、ヘキサンジオールジアクリレート、1,4−シクロヘキサンジオールジアクリレート、テトラエチレングリコールジアクリレート、ペンタエリスリトールジアクリレート、ペンタエリスリトールトリアクリレート、ペンタエリスリトールテトラアクリレート、ジペンタエリスリトールジアクリレート、ジペンタエリスリトールヘキサアクリレート、ソルビトールトリアクリレート、ソルビトールテトラアクリレート、ソルビトールペンタアクリレート、ソルビトールヘキサアクリレート、トリ(アクリロイルオキシエチル)イソシアヌレート、イソシアヌール酸エチレンオキシド(EO)変性トリアクリレート、ポリエステルアクリレートオリゴマー等がある。 Specific examples of the monomer of an ester of an aliphatic polyhydric alcohol compound and an unsaturated carboxylic acid include acrylic acid esters such as ethylene glycol diacrylate, triethylene glycol diacrylate, 1,3-butanediol diacrylate, and tetramethylene glycol. Diacrylate, propylene glycol diacrylate, neopentyl glycol diacrylate, trimethylolpropane triacrylate, trimethylolpropane tri (acryloyloxypropyl) ether, trimethylolethane triacrylate, hexanediol diacrylate, 1,4-cyclohexanediol diacrylate , Tetraethylene glycol diacrylate, pentaerythritol diacrylate, pentaerythritol triacrylate , Pentaerythritol tetraacrylate, dipentaerythritol diacrylate, dipentaerythritol hexaacrylate, sorbitol triacrylate, sorbitol tetraacrylate, sorbitol pentaacrylate, sorbitol hexaacrylate, tri (acryloyloxyethyl) isocyanurate, isocyanuric acid ethylene oxide (EO) Examples include modified triacrylates and polyester acrylate oligomers.
メタクリル酸エステルとしては、テトラメチレングリコールジメタクリレート、トリエチレングリコールジメタクリレート、ネオペンチルグリコールジメタクリレート、トリメチロールプロパントリメタクリレート、トリメチロールエタントリメタクリレート、エチレングリコールジメタクリレート、1,3−ブタンジオールジメタクリレート、ヘキサンジオールジメタクリレート、ペンタエリスリトールジメタクリレート、ペンタエリスリトールトリメタクリレート、ペンタエリスリトールテトラメタクリレート、ジペンタエリスリトールジメタクリレート、ジペンタエリスリトールヘキサメタクリレート、ソルビトールトリメタクリレート、ソルビトールテトラメタクリレート、ビス〔p−(3−メタクリルオキシ−2−ヒドロキシプロポキシ)フェニル〕ジメチルメタン、ビス−〔p−(メタクリルオキシエトキシ)フェニル〕ジメチルメタン等がある。 Methacrylic acid esters include tetramethylene glycol dimethacrylate, triethylene glycol dimethacrylate, neopentyl glycol dimethacrylate, trimethylolpropane trimethacrylate, trimethylolethane trimethacrylate, ethylene glycol dimethacrylate, 1,3-butanediol dimethacrylate, Hexanediol dimethacrylate, pentaerythritol dimethacrylate, pentaerythritol trimethacrylate, pentaerythritol tetramethacrylate, dipentaerythritol dimethacrylate, dipentaerythritol hexamethacrylate, sorbitol trimethacrylate, sorbitol tetramethacrylate, bis [p- (3-methacryloxy- 2-hydroxypro ) Phenyl] dimethyl methane, bis - [p- (methacryloxyethoxy) phenyl] dimethyl methane.
イタコン酸エステルとしては、エチレングリコールジイタコネート、プロピレングリコールジイタコネート、1,3−ブタンジオールジイタコネート、1,4−ブタンジオールジイタコネート、テトラメチレングリコールジイタコネート、ペンタエリスリトールジイタコネート、ソルビトールテトライタコネート等がある。クロトン酸エステルとしては、エチレングリコールジクロトネート、テトラメチレングリコールジクロトネート、ペンタエリスリトールジクロトネート、ソルビトールテトラジクロトネート等がある。イソクロトン酸エステルとしては、エチレングリコールジイソクロトネート、ペンタエリスリトールジイソクロトネート、ソルビトールテトライソクロトネート等がある。マレイン酸エステルとしては、エチレングリコールジマレート、トリエチレングリコールジマレート、ペンタエリスリトールジマレート、ソルビトールテトラマレート等がある。 Itaconic acid esters include ethylene glycol diitaconate, propylene glycol diitaconate, 1,3-butanediol diitaconate, 1,4-butanediol diitaconate, tetramethylene glycol diitaconate, pentaerythritol diitaconate And sorbitol tetritaconate. Examples of crotonic acid esters include ethylene glycol dicrotonate, tetramethylene glycol dicrotonate, pentaerythritol dicrotonate, and sorbitol tetradicrotonate. Examples of isocrotonic acid esters include ethylene glycol diisocrotonate, pentaerythritol diisocrotonate, and sorbitol tetraisocrotonate. Examples of maleic acid esters include ethylene glycol dimaleate, triethylene glycol dimaleate, pentaerythritol dimaleate, and sorbitol tetramaleate.
その他のエステルの例として、例えば、特公昭51−47334号、特開昭57−196231号の各公報に記載の脂肪族アルコール系エステル類や、特開昭59−5240号、特開昭59−5241号、特開平2−226149号の各公報に記載の芳香族系骨格を有するもの、特開平1−165613号公報記載のアミノ基を含有するもの等も好適に用いられる。
更に、前述のエステルモノマーは混合物としても使用することができる。
Examples of other esters include aliphatic alcohol esters described in JP-B-51-47334 and JP-A-57-196231, JP-A-59-5240, JP-A-59- Those having an aromatic skeleton described in JP-A No. 5241 and JP-A-2-226149 and those containing an amino group described in JP-A-1-165613 are also preferably used.
Furthermore, the ester monomers described above can also be used as a mixture.
また、脂肪族多価アミン化合物と不飽和カルボン酸とのアミドのモノマーの具体例としては、メチレンビス−アクリルアミド、メチレンビス−メタクリルアミド、1,6−ヘキサメチレンビス−アクリルアミド、1,6−ヘキサメチレンビス−メタクリルアミド、ジエチレントリアミントリスアクリルアミド、キシリレンビスアクリルアミド、キシリレンビスメタクリルアミド等がある。その他の好ましいアミド系モノマーの例としては、特公昭54−21726号公報記載のシクロへキシレン構造を有すものを挙げることができる。 Specific examples of amide monomers of aliphatic polyvalent amine compounds and unsaturated carboxylic acids include methylene bis-acrylamide, methylene bis-methacrylamide, 1,6-hexamethylene bis-acrylamide, 1,6-hexamethylene bis. -Methacrylamide, diethylenetriamine trisacrylamide, xylylene bisacrylamide, xylylene bismethacrylamide and the like. Examples of other preferable amide monomers include those having a cyclohexylene structure described in JP-B No. 54-21726.
また、イソシアネートと水酸基の付加反応を用いて製造されるウレタン系付加重合性化合物も好適であり、そのような具体例としては、例えば、特公昭48−41708号公報に記載されている1分子に2個以上のイソシアネート基を有するポリイソシアネート化合物に、下記一般式(A)で示される水酸基を含有するビニルモノマーを付加させた1分子中に2個以上の重合性ビニル基を含有するビニルウレタン化合物等が挙げられる。 Further, urethane-based addition polymerizable compounds produced by using an addition reaction of isocyanate and hydroxyl group are also suitable. Specific examples thereof include, for example, one molecule described in JP-B-48-41708. A vinylurethane compound containing two or more polymerizable vinyl groups in one molecule obtained by adding a vinyl monomer containing a hydroxyl group represented by the following general formula (A) to a polyisocyanate compound having two or more isocyanate groups Etc.
CH2=C(R4)COOCH2CH(R5)OH (A)
(ただし、R4およびR5は、HまたはCH3を示す。)
CH 2 = C (R 4) COOCH 2 CH (R 5) OH (A)
(However, R 4 and R 5 represent H or CH 3. )
また、特開昭51−37193号公報、特公平2−32293号公報、特公平2−16765号公報に記載されているようなウレタンアクリレート類や、特公昭58−49860号公報、特公昭56−17654号公報、特公昭62−39417号公報、特公昭62−39418号公報記載のエチレンオキサイド系骨格を有するウレタン化合物類も好適である。更に、特開昭63−277653号公報、特開昭63−260909号公報、特開平1−105238号公報に記載される、分子内にアミノ構造やスルフィド構造を有する付加重合性化合物類を用いることによっては、非常に感光スピードに優れた光重合性組成物を得ることができる。 Also, urethane acrylates such as those described in JP-A-51-37193, JP-B-2-32293, JP-B-2-16765, JP-B-58-49860, JP-B-56- Urethane compounds having an ethylene oxide skeleton described in Japanese Patent No. 17654, Japanese Patent Publication No. 62-39417, and Japanese Patent Publication No. 62-39418 are also suitable. Furthermore, addition polymerizable compounds having an amino structure or a sulfide structure in the molecule described in JP-A-63-277653, JP-A-63-260909, and JP-A-1-105238 are used. Depending on the case, it is possible to obtain a photopolymerizable composition excellent in the photosensitive speed.
その他の例としては、特開昭48−64183号、特公昭49−43191号、特公昭52−30490号、各公報に記載されているようなポリエステルアクリレート類、エポキシ樹脂と(メタ)アクリル酸を反応させたエポキシアクリレート類等の多官能のアクリレートやメタクリレートを挙げることができる。また、特公昭46−43946号、特公平1−40337号、特公平1−40336号各公報に記載の特定の不飽和化合物や、特開平2−25493号公報記載のビニルホスホン酸系化合物等も挙げることができる。また、ある場合には、特開昭61−22048号公報記載のペルフルオロアルキル基を含有する構造が好適に使用される。更に日本接着協会誌vol.20、No.7、300〜308ページ(1984年)に光硬化性モノマーおよびオリゴマーとして紹介されているものも使用することができる。 Other examples include polyester acrylates, epoxy resins and (meth) acrylic acid as described in JP-A-48-64183, JP-B-49-43191, JP-B-52-30490, and JP-A-52-30490. Mention may be made of polyfunctional acrylates and methacrylates such as reacted epoxy acrylates. In addition, specific unsaturated compounds described in JP-B-46-43946, JP-B-1-40337, JP-B-1-40336, and vinylphosphonic acid compounds described in JP-A-2-25493 are also included. Can be mentioned. In some cases, a structure containing a perfluoroalkyl group described in JP-A-61-22048 is preferably used. Furthermore, Journal of Japan Adhesion Association vol. 20, no. 7, pages 300 to 308 (1984), which are introduced as photocurable monomers and oligomers, can also be used.
これらの重合性化合物について、その構造、単独使用か併用か、添加量等の使用方法の詳細は、最終的な平版印刷版原版の性能設計にあわせて任意に設定できる。例えば、次のような観点から選択される。
感度の点では1分子あたりの不飽和基含量が多い構造が好ましく、多くの場合、2官能以上が好ましい。また、画像部すなわち硬化膜の強度を高くするためには、3官能以上のものがよく、更に、異なる官能数・異なる重合性基(例えばアクリル酸エステル、メタクリル酸エステル、スチレン系化合物、ビニルエーテル系化合物)のものを併用することで、感度と強度の両方を調節する方法も有効である。
また、感光層中の他の成分(例えばバインダーポリマー、重合開始剤、着色剤等)との相溶性、分散性に対しても、重合性化合物の選択・使用法は重要な要因であり、例えば、低純度化合物の使用や、2種以上の併用により相溶性を向上させうることがある。また、支持体や後述の保護層等との密着性を向上せしめる目的で特定の構造を選択することもあり得る。そのほか、重合性化合物の使用法は、酸素に対する重合阻害の大小、解像度、か
ぶり性、屈折率変化、表面粘着性等の観点から適切な構造、配合、添加量を任意に選択でき、更に場合によっては下塗り、上塗りといった層構成・塗布方法も考慮され得る。
About these polymerizable compounds, the details of usage such as the structure, single use or combination, addition amount, etc. can be arbitrarily set according to the performance design of the final lithographic printing plate precursor. For example, it is selected from the following viewpoints.
From the viewpoint of sensitivity, a structure having a large unsaturated group content per molecule is preferable, and in many cases, a bifunctional or higher functionality is preferable. Further, in order to increase the strength of the image area, that is, the cured film, those having three or more functionalities are preferable. A method of adjusting both sensitivity and strength by using a compound) is also effective.
In addition, the compatibility and dispersibility with other components in the photosensitive layer (for example, binder polymer, polymerization initiator, colorant, etc.), the selection and use method of the polymerizable compound is an important factor. In some cases, the compatibility can be improved by using a low-purity compound or by using two or more kinds in combination. In addition, a specific structure may be selected for the purpose of improving adhesion to a support or a protective layer described later. In addition, the usage of the polymerizable compound can be arbitrarily selected from the viewpoint of polymerization inhibition with respect to oxygen, resolution, fogging, refractive index change, surface adhesiveness, etc. The layer construction and coating method such as undercoating and overcoating can be considered.
上記の重合性化合物は、感光層の全固形分に対して、好ましくは5〜75質量%、更に好ましくは25〜70質量%、特に好ましくは30〜60質量%の範囲で使用される。 The polymerizable compound is preferably used in the range of 5 to 75% by mass, more preferably 25 to 70% by mass, and particularly preferably 30 to 60% by mass with respect to the total solid content of the photosensitive layer.
(C)バインダー
本発明の感光層に用いられるバインダーは、とくに限定されないが、酸価(ポリマー1gあたりの酸含率を化学当量数で表したもの)が、0.3meq/g以下であることが好ましい。バインダーの酸価は、好ましくは、0.1meq/g以下である。酸価が0.3meq/gを超えると現像性の悪化(残膜の発生)や、親水性の上昇による耐刷性の低下などの問題が発生する場合がある。
(C) Binder The binder used in the photosensitive layer of the invention is not particularly limited, but the acid value (the acid content per 1 g of polymer expressed in terms of the number of chemical equivalents) is 0.3 meq / g or less. Is preferred. The acid value of the binder is preferably 0.1 meq / g or less. When the acid value exceeds 0.3 meq / g, problems such as deterioration in developability (generation of residual film) and reduction in printing durability due to increase in hydrophilicity may occur.
また、本発明に用いられるバインダーは、水およびpH10以上の水溶液に対し実質的に不溶であることが好ましい。バインダーの水に対する溶解度(飽和溶解時のポリマー濃度)は、1.0質量%以下であることが好ましい。なお、上記溶解度の測定温度は、製版現像時の通常の温度である25℃である。
このようなバインダーを用いることによって、水性現像液に対する良好な現像性を維持しつつ、感光層の膜強度、耐水性および着肉性が向上して、耐刷性の向上が得られる。
Moreover, it is preferable that the binder used for this invention is substantially insoluble with respect to water and aqueous solution of pH 10 or more. The solubility of the binder in water (polymer concentration at the time of saturated dissolution) is preferably 1.0% by mass or less. The solubility measurement temperature is 25 ° C., which is a normal temperature during plate-making development.
By using such a binder, it is possible to improve the printing durability by improving the film strength, water resistance and inking property of the photosensitive layer while maintaining good developability with respect to an aqueous developer.
バインダーとしては、本発明の平版印刷版原版の性能を損なわない限り、上記範囲であれば、従来公知のものを制限なく使用でき、皮膜性を有する線状有機ポリマーが好ましい。
このようなバインダーの例としては、アクリル樹脂、メタクリル樹脂、スチレン系樹脂、ポリビニルアセタール樹脂、ポリウレタン樹脂、ポリアミド樹脂、エポキシ樹脂、ポリエステル樹脂から選ばれる高分子が好ましい。なかでも、アクリル樹脂、メタクリル樹脂、スチレン系樹脂等のビニル共重合体が好ましい。
As the binder, as long as the performance of the lithographic printing plate precursor according to the present invention is not impaired, a conventionally known one can be used without limitation within the above range, and a linear organic polymer having film properties is preferable.
Examples of such binders are preferably polymers selected from acrylic resins, methacrylic resins, styrene resins, polyvinyl acetal resins, polyurethane resins, polyamide resins, epoxy resins, and polyester resins. Especially, vinyl copolymers, such as an acrylic resin, a methacryl resin, and a styrene resin, are preferable.
このようなビニル共重合体は、公知のビニル単量体を用いて、上記特性(酸価、溶解性等)を有するように単量体の種類、量比を調整して得ることができる。ビニル単量体としては、例えば(メタ)アクリル酸エステル類、クロトン酸エステル類、ビニルエステル類、マレイン酸ジエステル類、フマル酸ジエステル類、イタコン酸ジエステル類、、(メタ)アクリルアミド類、ビニルエーテル類、スチレン類、や(メタ)アクリロニトリル等が好ましい。この様な化合物の具体例としては例えば以下の様な化合物が挙げられる。 Such a vinyl copolymer can be obtained by using a known vinyl monomer and adjusting the type and amount ratio of the monomer so as to have the above properties (acid value, solubility, etc.). Examples of vinyl monomers include (meth) acrylic acid esters, crotonic acid esters, vinyl esters, maleic acid diesters, fumaric acid diesters, itaconic acid diesters, (meth) acrylamides, vinyl ethers, Styrenes and (meth) acrylonitrile are preferred. Specific examples of such compounds include the following compounds.
(メタ)アクリル酸エステル類としては、メチル(メタ)アクリレート、エチル(メタ)アクリレート、n−プロピル(メタ)アクリレート、イソプロピル(メタ)アクリレート、n−ブチル(メタ)アクリレート、イソブチル(メタ)アクリレート、tert−ブチル(メタ)アクリレート、n−ヘキシル(メタ)アクリレート、2−エチルヘキシル(メタ)アクリレート、アセトキシエチル(メタ)アクリレート、フェニル(メタ)アクリレート、2−ヒドロキシエチル(メタ)アクリレート、2−ヒドロキシプロピル(メタ)アクリレート、4−ヒドロキシブチル(メタ)アクリレート、2−メトキシエチル(メタ)アクリレート、2−エトキシエチル(メタ)アクリレート、2−(2−メトキシエトキシ)エチル(メタ)アクリレート、シクロヘキシル(メタ)アクリレート、ベンジル(メタ)アクリレート、ジエチレングリコールモノメチルエーテル(メタ)アクリレート、ジエチレングリコールモノエチルエーテル(メタ)アクリレート、ジエチレングリコールモノフェニルエーテル(メタ)アクリレート、トリエチレングリコールモノメチルエーテル(メタ)アクリレート、トリエチレングリコールモノエチルエーテル(メタ)アクリレート、ジプロピレングリコールモノメチルエーテル(メタ)アクリレート、ポリエチレングリコールモノメチルエーテル(メタ)アクリレート、ポリプロピレングリコールモノメチルエーテル(メタ)アクリレート、エチレングリコールとプロピレングリコールとの共重合体のモノメチルエーテル(メタ)アクリレート、N,N−ジメチルアミノエチル(メタ)アクリレート、N,N−ジエチルアミノエチル(メタ)アクリレート、N,N−ジメチルアミノプロピル(メタ)アクリレート等が挙げられる。 Examples of (meth) acrylic acid esters include methyl (meth) acrylate, ethyl (meth) acrylate, n-propyl (meth) acrylate, isopropyl (meth) acrylate, n-butyl (meth) acrylate, isobutyl (meth) acrylate, tert-butyl (meth) acrylate, n-hexyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, acetoxyethyl (meth) acrylate, phenyl (meth) acrylate, 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (Meth) acrylate, 4-hydroxybutyl (meth) acrylate, 2-methoxyethyl (meth) acrylate, 2-ethoxyethyl (meth) acrylate, 2- (2-methoxyethoxy) ethyl (meth) acrylate , Cyclohexyl (meth) acrylate, benzyl (meth) acrylate, diethylene glycol monomethyl ether (meth) acrylate, diethylene glycol monoethyl ether (meth) acrylate, diethylene glycol monophenyl ether (meth) acrylate, triethylene glycol monomethyl ether (meth) acrylate, tri Ethylene glycol monoethyl ether (meth) acrylate, dipropylene glycol monomethyl ether (meth) acrylate, polyethylene glycol monomethyl ether (meth) acrylate, polypropylene glycol monomethyl ether (meth) acrylate, monomethyl copolymer of ethylene glycol and propylene glycol Ether (meth) acrylate, N, N-di Chill aminoethyl (meth) acrylate, N, N-diethylaminoethyl (meth) acrylate, N, N-dimethylaminopropyl (meth) acrylate.
クロトン酸エステル類としては、クロトン酸ブチル、クロトン酸ヘキシル等が挙げられる。ビニルエステル類としては、ビニルアセテート、ビニルプロピオネート、ビニルブチレート、ビニルメトキシアセテート、安息香酸ビニルなどが挙げられる。
マレイン酸ジエステル類としては、マレイン酸ジメチル、マレイン酸ジエチル、マレイン酸ジブチルなどが挙げられる。フマル酸ジエステル類としては、フマル酸ジメチル、フマル酸ジエチル、フマル酸ジブチルなどが挙げられる。イタコン酸ジエステル類としては、イタコン酸ジメチル、イタコン酸ジエチル、イタコン酸ジブチルなどが挙げられる。
Examples of the crotonic acid esters include butyl crotonic acid and hexyl crotonic acid. Examples of vinyl esters include vinyl acetate, vinyl propionate, vinyl butyrate, vinyl methoxyacetate, vinyl benzoate and the like.
Examples of maleic acid diesters include dimethyl maleate, diethyl maleate, and dibutyl maleate. Examples of the fumaric acid diesters include dimethyl fumarate, diethyl fumarate, dibutyl fumarate and the like. Examples of the itaconic acid diesters include dimethyl itaconate, diethyl itaconate, and dibutyl itaconate.
(メタ)アクリルアミド類としては、(メタ)アクリルアミド、N−メチル(メタ)アクリルアミド、N−エチル(メタ)アクリルアミド、N−プロピル(メタ)アクリルアミド、N−nブチルアクリル(メタ)アミド、N−tertブチル(メタ)アクリルアミド
、N−シクロヘキシル(メタ)アクリルアミド、N−(2−メトキシエチル)(メタ)アクリルアミド、N,N−ジ゛メチル(メタ)アクリルアミド、N,N−ジエチル(メタ)アクリルアミド、N−フェニル(メタ)アクリルアミド、N−ベンジル(メタ)アクリルアミド、(メタ)アクリロイルモルフォリンなどが挙げられる。
ビニルエーテル類としては、メチルビニルエーテル、ブチルビニルエーテル、ヘキシルビニルエーテル、メトキシエチルビニルエーテルなどが挙げられる。
(Meth) acrylamides include (meth) acrylamide, N-methyl (meth) acrylamide, N-ethyl (meth) acrylamide, N-propyl (meth) acrylamide, Nn butylacryl (meth) amide, N-tert Butyl (meth) acrylamide, N-cyclohexyl (meth) acrylamide, N- (2-methoxyethyl) (meth) acrylamide, N, N-dimethyl (meth) acrylamide, N, N-diethyl (meth) acrylamide, N -Phenyl (meth) acrylamide, N-benzyl (meth) acrylamide, (meth) acryloylmorpholine, etc. are mentioned.
Examples of vinyl ethers include methyl vinyl ether, butyl vinyl ether, hexyl vinyl ether, and methoxyethyl vinyl ether.
スチレン類としては、スチレン、メチルスチレン、ジメチルスチレン、トリメチルスチレン、エチルスチレン、イソプロピルスチレン、ブチルスチレン、ヒドロキシスチレン、メトキシスチレン、ブトキシスチレン、アセトキシスチレン、クロロスチレン、ジクロロスチレン、ブロモスチレン、クロロメチルスチレン、ビニル安息香酸メチル、αメチルスチレンなどが挙げられる。
この他ビニルピリジン、ビニルピロリドン、ビニルカルバゾール、(メタ)アクリロニトリル等も使用できる。
またウレタン基やウレア基を有するビニル単量体も使用することができる。この様な化合物としては例えば下記のような化合物が挙げられる。
Styrenes include styrene, methyl styrene, dimethyl styrene, trimethyl styrene, ethyl styrene, isopropyl styrene, butyl styrene, hydroxy styrene, methoxy styrene, butoxy styrene, acetoxy styrene, chloro styrene, dichloro styrene, bromo styrene, chloromethyl styrene, Examples include methyl vinylbenzoate and α-methylstyrene.
In addition, vinyl pyridine, vinyl pyrrolidone, vinyl carbazole, (meth) acrylonitrile and the like can also be used.
A vinyl monomer having a urethane group or a urea group can also be used. Examples of such a compound include the following compounds.
酸価が0.3meq/g以下のバインダーを用いて、pHが2〜10の現像液で画像形成を行うためには、非酸性の親水性基を有するビニル単量体を、バインダーの成分の一部に用いることが好ましい。
親水性基としては、例えば、ヒドロキシ基、カルボキシレート基、ヒドロキシエチル基、エチレンオキシ基、ヒドロキシプロピル基、アミノ基、アミノエチル基、アミノプロピル基、アンモニウム基、アミド基、カルボキシメチル基等や、ポリエーテル基(ジエチレンオキシド、トリエチレンオキシド、ポリエチレンオキシド、ジプロピレンオキシド、トリプロピレンオキシド、ポリプロピレンオキシド、ジテトラメチレンオキシド、トリテトラメチレンオキシド、ポリテトラメチレンオキシドやこれらの組合せ等)等が挙げられ、このような親水性基を有するビニル単量体を用いることが好ましい。
より具体的には、(メタ)アクリル酸エステル類のエステル残基(−COOR)のRに−CH2CH2O−単位、−CH2CH(CH3)O−単位または−CH2CH2NH−単位を含む(メタ)アクリル酸エステル類、水酸基含有(メタ)アクリル酸エステル類、(メタ)アクリルアミド類などの少なくとも1種を含む共重合体が特に好ましい。また本発明のバインダー中における親水性基を有するビニル単量体の割合は5〜70モル%が好ましく、10〜60モル%がより好ましく、15〜50モル%が特に好ましい。親水性基を有するビニル単量体の割合が5モル%未満では現像性が低下する場合があり、70モル%を超えると耐刷性が低下する場合がある。
In order to form an image with a developer having a pH of 2 to 10 using a binder having an acid value of 0.3 meq / g or less, a vinyl monomer having a non-acidic hydrophilic group is used as a component of the binder. It is preferable to use some.
Examples of hydrophilic groups include hydroxy groups, carboxylate groups, hydroxyethyl groups, ethyleneoxy groups, hydroxypropyl groups, amino groups, aminoethyl groups, aminopropyl groups, ammonium groups, amide groups, carboxymethyl groups, and the like. Polyether groups (diethylene oxide, triethylene oxide, polyethylene oxide, dipropylene oxide, tripropylene oxide, polypropylene oxide, ditetramethylene oxide, tritetramethylene oxide, polytetramethylene oxide, combinations thereof, etc.) It is preferable to use a vinyl monomer having such a hydrophilic group.
More specifically, R of the ester residue (—COOR) of (meth) acrylic acid ester is —CH 2 CH 2 O— unit, —CH 2 CH (CH 3 ) O— unit or —CH 2 CH 2. Copolymers containing at least one kind such as (meth) acrylic acid esters containing NH units, hydroxyl group-containing (meth) acrylic acid esters, (meth) acrylamides and the like are particularly preferred. Moreover, 5-70 mol% is preferable, as for the ratio of the vinyl monomer which has a hydrophilic group in the binder of this invention, 10-60 mol% is more preferable, and 15-50 mol% is especially preferable. If the ratio of the vinyl monomer having a hydrophilic group is less than 5 mol%, the developability may be lowered, and if it exceeds 70 mol%, the printing durability may be lowered.
また、感光層のバインダーとしては、ポリウレタン樹脂も好ましく利用できる。ポリウレタン樹脂は、公知のジイソシアネート化合物とジオール化合物との重付加反応によって得られるが、前述の特性(酸価、溶解性等)を有するようにジイソシアネート化合物とジオール化合物の種類、量比を適宜調整して得ることができる。 A polyurethane resin can also be preferably used as the binder for the photosensitive layer. The polyurethane resin is obtained by a polyaddition reaction between a known diisocyanate compound and a diol compound. The type and amount ratio of the diisocyanate compound and the diol compound are appropriately adjusted so as to have the above-mentioned characteristics (acid value, solubility, etc.). Can be obtained.
1)ジイソシアネート化合物
ジイソシアネート化合物としては下記のものを挙げることできる。好ましいものは、下記一般式(6)で表されるジイソシアネート化合物である。
1) Diisocyanate compound Examples of the diisocyanate compound include the following. Preferred is a diisocyanate compound represented by the following general formula (6).
OCN−L1−NCO (6) OCN-L 1 -NCO (6)
一般式(6)中、L1は置換基を有していてもよい2価の脂肪族または芳香族炭化水素
基を表す。必要に応じ、L1中はイソシアネート基と反応しない他の官能基、例えばエス
テル、ウレタン、アミド、ウレイド基を有していてもよい。
In General Formula (6), L 1 represents a divalent aliphatic or aromatic hydrocarbon group which may have a substituent. If necessary, L 1 may have another functional group that does not react with an isocyanate group, such as an ester, urethane, amide, or ureido group.
上記一般式(6)で表されるジイソシアネート化合物としては、具体的には以下に示すものが含まれる。
すなわち、2,4−トリレンジイソシアネート、2,4−トリレンジイソシアネートの二量体、2,6−トリレンジレンジイソシアネート、p−キシリレンジイソシアネート、m−キシリレンジイソシアネート、4,4’−ジフェニルメタンジイソシアネート、1,5−ナフチレンジイソシアネート、3,3’−ジメチルビフェニル−4,4’−ジイソシアネート等のような芳香族ジイソシアネート化合物;
ヘキサメチレンジイソシアネート、トリメチルヘキサメチレンジイソシアネート、リジンジイソシアネート、ダイマー酸ジイソシアネート等のような脂肪族ジイソシアネート化合物;
イソホロンジイソシアネート、4,4’−メチレンビス(シクロヘキシルイソシアネート)、メチルシクロヘキサン−2,4(または2,6)ジイソシアネート、1,3−(イソシアネートメチル)シクロヘキサン等のような脂環族ジイソシアネート化合物;
1,3−ブチレングリコール1モルとトリレンジイソシアネート2モルとの付加体等のようなジオールとジイソシアネートとの反応物であるジイソシアネート化合物;等が挙げられる。
Specific examples of the diisocyanate compound represented by the general formula (6) include those shown below.
That is, 2,4-tolylene diisocyanate, dimer of 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, p-xylylene diisocyanate, m-xylylene diisocyanate, 4,4′-diphenylmethane diisocyanate Aromatic diisocyanate compounds such as 1,5-naphthylene diisocyanate, 3,3′-dimethylbiphenyl-4,4′-diisocyanate;
Aliphatic diisocyanate compounds such as hexamethylene diisocyanate, trimethylhexamethylene diisocyanate, lysine diisocyanate, dimer acid diisocyanate and the like;
Alicyclic diisocyanate compounds such as isophorone diisocyanate, 4,4′-methylenebis (cyclohexyl isocyanate), methylcyclohexane-2,4 (or 2,6) diisocyanate, 1,3- (isocyanatomethyl) cyclohexane;
And a diisocyanate compound which is a reaction product of a diol and a diisocyanate such as an adduct of 1 mol of 1,3-butylene glycol and 2 mol of tolylene diisocyanate.
2)ジオール化合物
ジオール化合物としては、例えば、ポリエーテルジオール化合物、ポリエステルジオール化合物、ポリカーボネートジオール化合物を挙げることできる。
2) Examples of the diol compound diol compound include a polyether diol compound, a polyester diol compound, and a polycarbonate diol compound.
ポリエーテルジオール化合物としては、下記式(7)、(8)、(9)、(10)、(11)で表される化合物、および、末端に水酸基を有するエチレンオキシドとプロピレンオキシドとのランダム共重合体が挙げられる。 Examples of the polyether diol compound include compounds represented by the following formulas (7), (8), (9), (10) and (11), and random copolymerization of ethylene oxide and propylene oxide having a hydroxyl group at the terminal. Coalescence is mentioned.
式(7)〜(11)中、R14は水素原子またはメチル基を表し、X1は、以下の基を表
す。また、a、b、c、d、e、f、gはそれぞれ2以上の整数を表し、好ましくは2〜
100の整数である。
In formulas (7) to (11), R 14 represents a hydrogen atom or a methyl group, and X 1 represents the following group. A, b, c, d, e, f, and g each represents an integer of 2 or more, preferably 2 to 2.
It is an integer of 100.
上記式(7)、(8)で表されるポリエーテルジオール化合物としては具体的には以下に示すものが挙げられる。
すなわち、ジエチレングリコール、トリエチレングリコール、テトラエチレングリコール、ペンタエチレングリコール、ヘキサエチレングリコール、ヘプタエチレングリコール、オクタエチレングリコール、ジ−1,2−プロピレングリコール、トリ−1,2−プロピレングリコール、テトラ−1,2−プロピレングリコール、ヘキサ−1,2−プロピレングリコール、ジ−1,3−プロピレングリコール、トリ−1,3−プロピレングリコール、テトラ−1,3−プロピレングリコール、ジ−1,3−ブチレングリコール、トリ−1,3−ブチレングリコール、ヘキサ−1,3−ブチレングリコール、重量平均分子量1000のポリエチレングリコール、重量平均分子量1500のポリエチレングリコール、重量平均分子量2000のポリエチレングリコール、重量平均分子量3000のポリエチレングリコール、重量平均分子量7500のポリエチレングリコール、重量平均分子量400のポリプロピレングリコール、重量平均分子量700のポリプロピレングリコール、重量平均分子量1000のポリプロピレングリコール、重量平均分子量2000のポリプロピレングリコール、重量平均分子量3000のポリプロピレングリコール、重量平均分子量4000のポリプロピレングリコール等である。
Specific examples of the polyether diol compound represented by the above formulas (7) and (8) include the following.
That is, diethylene glycol, triethylene glycol, tetraethylene glycol, pentaethylene glycol, hexaethylene glycol, heptaethylene glycol, octaethylene glycol, di-1,2-propylene glycol, tri-1,2-propylene glycol, tetra-1, 2-propylene glycol, hexa-1,2-propylene glycol, di-1,3-propylene glycol, tri-1,3-propylene glycol, tetra-1,3-propylene glycol, di-1,3-butylene glycol, Tri-1,3-butylene glycol, hexa-1,3-butylene glycol, polyethylene glycol having a weight average molecular weight of 1000, polyethylene glycol having a weight average molecular weight of 1500, poly having a weight average molecular weight of 2000 Tylene glycol, polyethylene glycol with a weight average molecular weight of 3000, polyethylene glycol with a weight average molecular weight of 7500, polypropylene glycol with a weight average molecular weight of 400, polypropylene glycol with a weight average molecular weight of 700, polypropylene glycol with a weight average molecular weight of 1000, polypropylene glycol with a weight average molecular weight of 2000 , Polypropylene glycol having a weight average molecular weight of 3000, polypropylene glycol having a weight average molecular weight of 4000, and the like.
上記式(9)で表されるポリエーテルジオール化合物としては、具体的には以下に示すものが挙げられる。
すなわち、三洋化成工業(株)製、(商品名)PTMG650、PTMG1000、PTMG2000、PTMG3000等である。
Specific examples of the polyether diol compound represented by the formula (9) include those shown below.
That is, Sanyo Chemical Industries, Ltd. (trade name) PTMG650, PTMG1000, PTMG2000, PTMG3000, and the like.
上記式(10)で表されるポリエーテルジオール化合物としては、具体的には以下に示すものが挙げられる。
すなわち、三洋化成工業(株)製、(商品名)ニューポールPE−61、ニューポールPE−62、ニューポールPE−64、ニューポールPE−68、ニューポールPE−71、ニューポールPE−74、ニューポールPE−75、ニューポールPE−78、ニューポールPE−108、ニューポールPE−128、ニューポールPE−61等である。
Specific examples of the polyether diol compound represented by the formula (10) include those shown below.
That is, Sanyo Chemical Industries, Ltd. (trade name) New Pole PE-61, New Pole PE-62, New Pole PE-64, New Pole PE-68, New Pole PE-71, New Pole PE-74, New Pole PE-75, New Pole PE-78, New Pole PE-108, New Pole PE-128, New Pole PE-61, and the like.
上記式(11)で表されるポリエーテルジオール化合物としては、具体的には以下に示すものが挙げられる。
すなわち、三洋化成工業(株)製、(商品名)ニューポールBPE−20、ニューポールBPE−20F、ニューポールBPE−20NK、ニューポールBPE−20T、ニューポールBPE−20G、ニューポールBPE−40、ニューポールBPE−60、ニューポールBPE−100、ニューポールBPE−180、ニューポールBPE−2P、ニューポールBPE−23P、ニューポールBPE−3P、ニューポールBPE−5P等である。
Specific examples of the polyether diol compound represented by the formula (11) include those shown below.
That is, Sanyo Chemical Industries, Ltd. (trade name) New Pole BPE-20, New Pole BPE-20F, New Pole BPE-20NK, New Pole BPE-20T, New Pole BPE-20G, New Pole BPE-40, New Pole BPE-60, New Pole BPE-100, New Pole BPE-180, New Pole BPE-2P, New Pole BPE-23P, New Pole BPE-3P, New Pole BPE-5P, and the like.
末端に水酸基を有するエチレンオキシドとプロピレンオキシドとのランダム共重合体としては、具体的には以下に示すものが挙げられる。
すなわち、三洋化成工業(株)製、(商品名)ニューポール50HB−100、ニューポール50HB−260、ニューポール50HB−400、ニューポール50HB−660、ニューポール50HB−2000、ニューポール50HB−5100等である。
Specific examples of the random copolymer of ethylene oxide and propylene oxide having a hydroxyl group at the terminal include the following.
That is, Sanyo Chemical Industries, Ltd. (trade name) New Pole 50HB-100, New Pole 50HB-260, New Pole 50HB-400, New Pole 50HB-660, New Pole 50HB-2000, New Pole 50HB-5100, etc. It is.
ポリエステルジオール化合物としては、式(12)、(13)で表される化合物が挙げられる。 Examples of the polyester diol compound include compounds represented by formulas (12) and (13).
式(12)、(13)中、L2、L3およびL4ではそれぞれ同一でも相違してもよく2
価の脂肪族または芳香族炭化水素基を表し、L5は2価の脂肪族炭化水素基を表す。好ま
しくは、L2〜L4は、それぞれアルキレン基、アルケニレン基、アルキニレン基、アリレン基を表し、L5はアルキレン基を表す。またL2〜L5中にはイソシアネート基と反応し
ない他の官能基、例えばエーテル、カルボニル、エステル、シアノ、オレフィン、ウレタン、アミド、ウレイド基またはハロゲン原子等が存在していてもよい。n1、n2はそれぞれ2以上の整数であり、好ましくは2〜100の整数を表す。
ポリカーボネートジオール化合物としては、式(14)で表される化合物がある。
In formulas (12) and (13), L 2 , L 3 and L 4 may be the same or different.
Represents a divalent aliphatic or aromatic hydrocarbon group, and L 5 represents a divalent aliphatic hydrocarbon group. Preferably, L 2 to L 4 each represent an alkylene group, an alkenylene group, an alkynylene group, or an arylene group, and L 5 represents an alkylene group. In addition, other functional groups that do not react with the isocyanate group, such as ether, carbonyl, ester, cyano, olefin, urethane, amide, ureido group or halogen atom may be present in L 2 to L 5 . n1 and n2 are each an integer of 2 or more, preferably an integer of 2 to 100.
As the polycarbonate diol compound, there is a compound represented by the formula (14).
式(14)中、L6はそれぞれ同一でも相違してもよく2価の脂肪族または芳香族炭化
水素基を表す。好ましくは、L6はアルキレン基、アルケニレン基、アルキニレン基、ア
リーレン基を表す。またL6中にはイソシアネート基と反応しない他の官能基、例えばエ
ーテル、カルボニル、エステル、シアノ、オレフィン、ウレタン、アミド、ウレイド基またはハロゲン原子等が存在していてもよい。n3は2以上の整数であり、好ましくは2〜100の整数を表す。
In formula (14), L 6 may be the same or different and represents a divalent aliphatic or aromatic hydrocarbon group. Preferably, L 6 represents an alkylene group, an alkenylene group, an alkynylene group or an arylene group. In addition, other functional groups that do not react with the isocyanate group, such as ether, carbonyl, ester, cyano, olefin, urethane, amide, ureido group or halogen atom may be present in L 6 . n3 is an integer of 2 or more, and preferably represents an integer of 2 to 100.
上記式(12)、(13)または(14)で表されるジオール化合物としては具体的には以下に示す(例示化合物No.1)〜(例示化合物No.18)が含まれる。具体例中のnは2以上の整数を表す。 Specific examples of the diol compound represented by the above formula (12), (13) or (14) include (Exemplary Compound No. 1) to (Exemplary Compound No. 18) shown below. N in the specific examples represents an integer of 2 or more.
また、特定ポリウレタン樹脂の合成には、上記ジオール化合物の他に、イソシアネート基と反応しない置換基を有するジオール化合物を併用することもできる。このようなジオール化合物としては、例えば、以下に示すものが含まれる。 Moreover, in the synthesis | combination of specific polyurethane resin, the diol compound which has a substituent which does not react with an isocyanate group other than the said diol compound can also be used together. Examples of such diol compounds include those shown below.
HO−L7−O−CO−L8−CO−O−L7−OH (15)
HO−L8−CO−O−L7−OH (16)
HO-L 7 -O-CO- L 8 -CO-O-L 7 -OH (15)
HO-L 8 -CO-O- L 7 -OH (16)
式(15)、(16)中、L7、L8はそれぞれ同一でも相違していてもよく、置換基(例えば、アルキル基、アラルキル基、アリール基、アルコキシ基、アリーロキシ基、−F、−Cl、−Br、−I等のハロゲン原子などの各基が含まれる。)を有していてもよい2価の脂肪族炭化水素基、芳香族炭化水素基または複素環基を表す。必要に応じ、L7、
L8中にイソシアネート基と反応しない他の官能基、例えば、カルボニル基、エステル基
、ウレタン基、アミド基、ウレイド基などを有していてもよい。なおL7、L8で環を形成してもよい。
In the formulas (15) and (16), L 7 and L 8 may be the same or different, and each may have a substituent (for example, an alkyl group, an aralkyl group, an aryl group, an alkoxy group, an aryloxy group, —F, — And a divalent aliphatic hydrocarbon group, an aromatic hydrocarbon group or a heterocyclic group, which may have a halogen atom such as Cl, -Br, and -I. L 7 , if necessary
L 8 may have another functional group that does not react with an isocyanate group, such as a carbonyl group, an ester group, a urethane group, an amide group, or a ureido group. Note that L 7 and L 8 may form a ring.
更にバインダーには、画像部の皮膜強度を向上させるために、架橋性をもたせることができる。
バインダーポリマーに架橋性を持たせるためには、エチレン性不飽和結合等の架橋性官能基を高分子の主鎖中または側鎖中に導入すればよい。架橋性官能基は、共重合により導入してもよいし、高分子反応によって導入してもよい。
Further, the binder can be provided with a crosslinking property in order to improve the film strength of the image area.
In order to impart crosslinkability to the binder polymer, a crosslinkable functional group such as an ethylenically unsaturated bond may be introduced into the main chain or side chain of the polymer. The crosslinkable functional group may be introduced by copolymerization or may be introduced by a polymer reaction.
ここで架橋性基とは、平版印刷版原版を露光した際に感光層中で起こるラジカル重合反応の過程で高分子バインダーを架橋させる基のことである。このような機能の基であれば特に限定されないが、例えば、付加重合反応し得る官能基としてエチレン性不飽和結合基
、アミノ基、エポキシ基等が挙げられる。また光照射によりラジカルになり得る官能基であってもよく、そのような架橋性基としては、例えば、チオール基、ハロゲン基、オニウム塩構造等が挙げられる。なかでも、エチレン性不飽和結合基が好ましく、下記一般式(1)〜(3)で表される官能基が特に好ましい。
Here, the crosslinkable group is a group that crosslinks the polymer binder in the process of radical polymerization reaction that occurs in the photosensitive layer when the lithographic printing plate precursor is exposed. Although it will not specifically limit if it is a group of such a function, For example, an ethylenically unsaturated bond group, an amino group, an epoxy group etc. are mentioned as a functional group which can be addition-polymerized. Moreover, the functional group which can become a radical by light irradiation may be sufficient, and as such a crosslinkable group, a thiol group, a halogen group, an onium salt structure etc. are mentioned, for example. Especially, an ethylenically unsaturated bond group is preferable and the functional group represented by the following general formula (1)-(3) is especially preferable.
上記一般式(1)において、Rl〜R3はそれぞれ独立に、水素原子または1価の有機基を表すが、R1としては、好ましくは、水素原子または置換基を有してもよいアルキル基
などが挙げられ、なかでも、水素原子、メチル基がラジカル反応性が高いことから好ましい。また、R2、R3は、それぞれ独立に、水素原子、ハロゲン原子、アミノ基、カルボキシル基、アルコキシカルボニル基、スルホ基、ニトロ基、シアノ基、置換基を有してもよいアルキル基、置換基を有してもよいアリール基、置換基を有してもよいアルコキシ基、置換基を有してもよいアリールオキシ基、置換基を有してもよいアルキルアミノ基、置換基を有してもよいアリールアミノ基、置換基を有してもよいアルキルスルホニル基、置換基を有してもよいアリールスルホニル基などが挙げられ、なかでも、水素原子、カルボキシル基、アルコキシカルボニル基、置換基を有してもよいアルキル基、置換基を有してもよいアリール基がラジカル反応性が高いことから好ましい。
In the general formula (1), R 1 to R 3 each independently represents a hydrogen atom or a monovalent organic group, and R 1 is preferably a hydrogen atom or an alkyl which may have a substituent. A hydrogen atom or a methyl group is preferable because of high radical reactivity. R 2 and R 3 are each independently a hydrogen atom, a halogen atom, an amino group, a carboxyl group, an alkoxycarbonyl group, a sulfo group, a nitro group, a cyano group, an optionally substituted alkyl group, or a substituted group. An aryl group that may have a group, an alkoxy group that may have a substituent, an aryloxy group that may have a substituent, an alkylamino group that may have a substituent, and a substituent An arylamino group which may have a substituent, an alkylsulfonyl group which may have a substituent, an arylsulfonyl group which may have a substituent, and the like. Among them, a hydrogen atom, a carboxyl group, an alkoxycarbonyl group, a substituent An alkyl group which may have a substituent and an aryl group which may have a substituent are preferable because of high radical reactivity.
Xは、酸素原子、硫黄原子、または−N(R12)−を表し、ここで、R12は、水素原子または1価の有機基を表す。1価の有機基としては置換基を有してもよいアルキル基などが挙げられる。R12は、水素原子、メチル基、エチル基、イソプロピル基がラジカル反応性が高いことから好ましい。 X represents an oxygen atom, a sulfur atom, or —N (R 12 ) —, wherein R 12 represents a hydrogen atom or a monovalent organic group. Examples of the monovalent organic group include an alkyl group which may have a substituent. R 12 is preferably a hydrogen atom, a methyl group, an ethyl group or an isopropyl group because of high radical reactivity.
ここで、導入し得る置換基としては、アルキル基、アルケニル基、アルキニル基、アリール基、アルコキシ基、アリーロキシ基、ハロゲン原子、アミノ基、アルキルアミノ基、アリールアミノ基、カルボキシル基、アルコキシカルボニル基、スルホ基、ニトロ基、シアノ基、アミド基、アルキルスルホニル基、アリールスルホニル基などが挙げられる。 Here, examples of the substituent that can be introduced include an alkyl group, an alkenyl group, an alkynyl group, an aryl group, an alkoxy group, an aryloxy group, a halogen atom, an amino group, an alkylamino group, an arylamino group, a carboxyl group, an alkoxycarbonyl group, A sulfo group, a nitro group, a cyano group, an amide group, an alkylsulfonyl group, an arylsulfonyl group and the like can be mentioned.
上記一般式(2)において、R4〜R8は、それぞれ独立に水素原子または1価の有機基を表すが、R4〜R8は、好ましくは、水素原子、ハロゲン原子、アミノ基、ジアルキルアミノ基、カルボキシル基、アルコキシカルボニル基、スルホ基、ニトロ基、シアノ基、置換基を有してもよいアルキル基、置換基を有してもよいアリール基、置換基を有してもよいアルコキシ基、置換基を有してもよいアリールオキシ基、置換基を有してもよいアルキルアミノ基、置換基を有してもよいアリールアミノ基、置換基を有してもよいアルキルスルホニル基、置換基を有してもよいアリールスルホニル基などが挙げられ、なかでも、水素原子、カルボキシル基、アルコキシカルボニル基、置換基を有してもよいアルキル基、置換基を有してもよいアリール基が好ましい。 In the general formula (2), R 4 to R 8 each independently represents a hydrogen atom or a monovalent organic group, and R 4 to R 8 are preferably a hydrogen atom, a halogen atom, an amino group, or a dialkyl. Amino group, carboxyl group, alkoxycarbonyl group, sulfo group, nitro group, cyano group, alkyl group which may have a substituent, aryl group which may have a substituent, alkoxy which may have a substituent A group, an aryloxy group which may have a substituent, an alkylamino group which may have a substituent, an arylamino group which may have a substituent, an alkylsulfonyl group which may have a substituent, Examples include an arylsulfonyl group which may have a substituent. Among them, a hydrogen atom, a carboxyl group, an alkoxycarbonyl group, an alkyl group which may have a substituent, and an aryl which may have a substituent The ru group is preferred.
導入し得る置換基としては、一般式(1)と同様のものが例示される。また、Yは、酸
素原子、硫黄原子、またはN(R12)−を表す。R12は、一般式(1)のR12の場合と同義であり、好ましい例も同様である。
Examples of the substituent that can be introduced are the same as those in the general formula (1). Y represents an oxygen atom, a sulfur atom, or N (R 12 ) —. R 12 has the same meaning as R 12 in general formula (1), and preferred examples are also the same.
上記一般式(3)において、R9としては、水素原子または1価の有機基を表し、好ま
しくは、水素原子または置換基を有してもよいアルキル基などが挙げられ、なかでも、水素原子、メチル基がラジカル反応性が高いことから好ましい。R10、R11は、それぞれ独立に、水素原子、ハロゲン原子、アミノ基、ジアルキルアミノ基、カルボキシル基、アルコキシカルボニル基、スルホ基、ニトロ基、シアノ基、置換基を有してもよいアルキル基、置換基を有してもよいアリール基、置換基を有してもよいアルコキシ基、置換基を有してもよいアリールオキシ基、置換基を有してもよいアルキルアミノ基、置換基を有してもよいアリールアミノ基、置換基を有してもよいアルキルスルホニル基、置換基を有してもよいアリールスルホニル基などが挙げられ、なかでも、水素原子、カルボキシル基、アルコキシカルボニル基、置換基を有してもよいアルキル基、置換基を有してもよいアリール基がラジカル反応性が高いことから好ましい。
In the general formula (3), R 9 represents a hydrogen atom or a monovalent organic group, and preferably includes a hydrogen atom or an alkyl group which may have a substituent. A methyl group is preferred because of high radical reactivity. R 10 and R 11 are each independently a hydrogen atom, a halogen atom, an amino group, a dialkylamino group, a carboxyl group, an alkoxycarbonyl group, a sulfo group, a nitro group, a cyano group, or an alkyl group which may have a substituent. An aryl group which may have a substituent, an alkoxy group which may have a substituent, an aryloxy group which may have a substituent, an alkylamino group which may have a substituent, a substituent An arylamino group that may have, an alkylsulfonyl group that may have a substituent, an arylsulfonyl group that may have a substituent, and the like, among them, a hydrogen atom, a carboxyl group, an alkoxycarbonyl group, An alkyl group which may have a substituent and an aryl group which may have a substituent are preferable because of high radical reactivity.
ここで、導入し得る置換基としては、一般式(1)と同様のものが例示される。また、Zは、酸素原子、硫黄原子、−N(R13)−、または置換基を有してもよいフェニレン基を表す。R13としては、置換基を有してもよいアルキル基などが挙げられ、なかでも、メチル基、エチル基、イソプロピル基がラジカル反応性が高いことから好ましい。 Here, examples of the substituent that can be introduced are the same as those in the general formula (1). Further, Z is an oxygen atom, a sulfur atom, -N (R 13) -, or a phenylene group which may have a substituent. Examples of R 13 include an alkyl group which may have a substituent. Among them, a methyl group, an ethyl group, and an isopropyl group are preferable because of high radical reactivity.
上記の中でも、側鎖に架橋性基を有する(メタ)アクリル共重合体及び側鎖に架橋性基を有するポ
リウレタン樹脂がより好ましい。
Among these, a (meth) acrylic copolymer having a crosslinkable group in the side chain and a polyurethane resin having a crosslinkable group in the side chain are more preferable.
架橋性を有するバインダーは、例えば、その架橋性官能基にフリーラジカル(重合開始ラジカルまたは重合性化合物の重合過程の生長ラジカル)が付加し、バインダー間で直接にまたは重合性化合物の重合連鎖を介して付加重合して、バインダー分子間に架橋が形成されて硬化する。または、バインダー中の原子(例えば、官能性架橋基に隣接する炭素原子上の水素原子)がフリーラジカルにより引き抜かれてポリマーラジカルが生成し、それが互いに結合することによって、バインダー分子間に架橋が形成されて硬化する。
バインダー中の架橋性基の含有量(ヨウ素滴定によるラジカル重合可能な不飽和二重結合の含有量)は、バインダー1g当たり、好ましくは0.1〜10.0mmol、より好ましくは1.0〜7.0mmol、最も好ましくは2.0〜5.5mmolである。
本発明に係るバインダーのガラス転移温度(Tg)は0〜150℃が好ましく、20〜120℃がより好ましく、30〜100℃が特に好ましい。ガラス転移温度が0℃未満では耐刷性が悪化する場合があり、ガラス転移温度が150℃を超えると現像性が悪化する場合がある。
In the binder having crosslinkability, for example, free radicals (polymerization initiating radicals or growth radicals in the polymerization process of the polymerizable compound) are added to the crosslinkable functional group, and the binder is directly or via a polymerization chain of the polymerizable compound. Then, addition polymerization is performed, and a crosslink is formed between the binder molecules to be cured. Alternatively, atoms in the binder (for example, hydrogen atoms on carbon atoms adjacent to the functional bridging group) are extracted by free radicals to form polymer radicals that are bonded to each other, thereby causing cross-linking between the binder molecules. Forms and cures.
The content of the crosslinkable group in the binder (content of unsaturated double bond capable of radical polymerization by iodometric titration) is preferably 0.1 to 10.0 mmol, more preferably 1.0 to 7 per gram of binder. 0.0 mmol, most preferably 2.0-5.5 mmol.
The glass transition temperature (Tg) of the binder according to the present invention is preferably 0 to 150 ° C, more preferably 20 to 120 ° C, and particularly preferably 30 to 100 ° C. When the glass transition temperature is less than 0 ° C., the printing durability may be deteriorated, and when the glass transition temperature exceeds 150 ° C., the developability may be deteriorated.
バインダーは、質量平均分子量が5000以上であるのが好ましく、1万〜30万であるのがより好ましく、また、数平均分子量が1000以上であるのが好ましく、2000〜25万であるのがより好ましい。多分散度(質量平均分子量/数平均分子量)は、1.1〜10であるのが好ましい。
バインダーは、ランダムポリマー、ブロックポリマー、グラフトポリマー等のいずれでもよい。
バインダーは単独で用いても2種以上を混合して用いてもよい。
バインダーの含有量は、良好な画像部強度と画像形成性の観点から、感光層の全固形分に対して、5〜75質量%が好ましく、10〜60質量%がより好ましく、20〜50質量%が特に好ましい。
The binder preferably has a mass average molecular weight of 5,000 or more, more preferably 10,000 to 300,000, more preferably a number average molecular weight of 1,000 or more, and more preferably 2000 to 250,000. preferable. The polydispersity (mass average molecular weight / number average molecular weight) is preferably 1.1 to 10.
The binder may be any of random polymer, block polymer, graft polymer and the like.
A binder may be used independently or may mix and use 2 or more types.
The content of the binder is preferably from 5 to 75 mass%, more preferably from 10 to 60 mass%, more preferably from 20 to 50 mass%, based on the total solid content of the photosensitive layer, from the viewpoints of good image area strength and image formability. % Is particularly preferred.
(D)共重合体
本発明においては、支持体と接する該感光層または下塗り層のようなその他の層に、(a1)少なくとも1つのエチレン性不飽和結合がイオン対を介して導入されている繰り返し単位と、(a2)前記支持体表面と相互作用する官能基を少なくとも1つ有する繰り返し単位とを有する共重合体を含有する。(D)成分を感光層または下塗り層に含有することで良好な非画像部の汚れ、耐刷性を示す。
上記共重合体としては、下記式(D1)で表される繰り返し単位を含有するものが好ましい。
式(D1)
(D) Copolymer In the present invention, (a1) at least one ethylenically unsaturated bond is introduced via an ion pair into the other layer such as the photosensitive layer or the undercoat layer in contact with the support. A copolymer having a repeating unit and (a2) a repeating unit having at least one functional group that interacts with the support surface is contained. By including the component (D) in the photosensitive layer or the undercoat layer, good non-image area stains and printing durability are exhibited.
As said copolymer, what contains the repeating unit represented by a following formula (D1) is preferable.
Formula (D1)
式(D1)中、A1は少なくとも1つのエチレン性不飽和結合がイオン対を介して導入されている繰り返し単位(a1)を表し、A2は支持体表面と相互作用する官能基を少なくとも1つ有する繰り返し単位(a2)を表し、A3は(a1)以外の親水性基を少なくとも1つ含有する繰り返し単位(a3)を表す。x、y、zは共重合比を表す。 In formula (D1), A 1 represents a repeating unit (a1) in which at least one ethylenically unsaturated bond is introduced via an ion pair, and A 2 represents at least one functional group that interacts with the support surface. represents a repeating unit (a2) having one, a 3 represents a repeating unit (a3) containing at least one hydrophilic group other than (a1). x, y, z represents a copolymerization ratio.
A1で表される、少なくとも1つのエチレン性不飽和結合がイオン対を介して導入されている繰り返し単位(a1)は、好ましくは下記式(A1)で表される。
式(A1)
The repeating unit (a1) represented by A 1 and having at least one ethylenically unsaturated bond introduced through an ion pair is preferably represented by the following formula (A1).
Formula (A1)
式(A1)中、
R101〜R103はそれぞれ独立に、水素原子、炭素数1〜6のアルキル基、―CH2―OH、―CH2―OR112、―CH2−O−CO−R112またはハロゲン原子を表す。
R104〜R106はそれぞれ独立に、水素原子、炭素数1〜6のアルキル基、ハロゲン原子、―CH2―OH、―CH2―OR108、―CH2−O−CO−R108、―CO−R108、
―O―CO―R108、―CO―O−R108または―CO―N(R109)―R108を表す。またR104とR105、またはR105とR106で環を形成してもよい。
R107は水素原子、炭素数1〜10のアルキル基、炭素数6〜10のアリール基または
炭素数7〜20のアラルキル基を表す。
R108は炭素数1〜10のアルキル基または炭素数6〜10のアリール基を表す。
R109は水素原子、炭素数1〜10のアルキル基または炭素数6〜10のアリール基を
表す。
R112は炭素数1〜10のアルキル基、炭素数6〜10のアリール基または炭素数7〜20のアラルキル基を表す。
L101は−CO−、−O−、―S―、−N(R109)−、―SO2―、二価の脂肪族基、二価の芳香族基およびそれらの組み合わせからなる群より選ばれる二価の連結基を表す。
L102は−CO−、−O−、−N(R109)−、二価の脂肪族基、二価の芳香族基およびそれらの組み合わせからなる群より選ばれる二価の連結基を表す。
m101は0〜3の整数である。
m102は1〜3の整数である。m101+m102=3を満たす。
m101が2以上のとき、複数のR107は同じでも異なっていても良い。m102が2以上の
とき、複数のR104〜R106、L102はそれぞれ同じでも異なっていても良い。
X101 −は、―CO2 −、―PO3H−、―O−PO3H−、―SO3 −または―O−
SO3 −を表す。
Y101はn101価の連結基を表す。
n101は1〜10の整数である。
m102×n101の値はゼロではない。
In formula (A1),
R 101 to R 103 each independently represents a hydrogen atom, an alkyl group having 1 to 6 carbon atoms, —CH 2 —OH, —CH 2 —OR 112 , —CH 2 —O—CO—R 112 or a halogen atom. .
R 104 to R 106 are each independently a hydrogen atom, an alkyl group having 1 to 6 carbon atoms, a halogen atom, —CH 2 —OH, —CH 2 —OR 108 , —CH 2 —O—CO—R 108 , — CO-R 108 ,
—O—CO—R 108 , —CO—O—R 108 or —CO—N (R 109 ) —R 108 is represented. R 104 and R 105 , or R 105 and R 106 may form a ring.
R107 represents a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, an aryl group having 6 to 10 carbon atoms, or an aralkyl group having 7 to 20 carbon atoms.
R 108 represents an alkyl group or an aryl group having 6 to 10 carbon atoms having 1 to 10 carbon atoms.
R 109 represents a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, or an aryl group having 6 to 10 carbon atoms.
R 112 represents an alkyl group having 1 to 10 carbon atoms, an aryl group having 6 to 10 carbon atoms, or an aralkyl group having 7 to 20 carbon atoms.
L 101 is selected from the group consisting of —CO—, —O—, —S— , —N (R 109 ) —, —SO 2 —, a divalent aliphatic group, a divalent aromatic group, and combinations thereof. Represents a divalent linking group.
L 102 is -CO -, - O -, - N (R 109) -, a divalent aliphatic group, a divalent aromatic group and the divalent linking group selected from the group consisting of.
m 101 is an integer of 0 to 3.
m102 is an integer of 1-3. m 101 + m 102 = 3 is satisfied.
When m 101 is 2 or more, the plurality of R 107 may be the same or different. When m 102 is 2 or more, plural R 104 ~R 106, L 102 may be the same or different.
X 101 — represents —CO 2 — , —PO 3 H − , —O—PO 3 H − , —SO 3 — or —O—.
SO 3 - represents a.
Y 101 represents an n 101- valent linking group.
n101 is an integer of 1-10.
The value of m 102 × n 101 is not zero.
式(A1)のさらに好ましい形態を以下に示す。
R101、R102は水素原子、メチル基、エチル基が好ましく、水素原子がより好ましい。
R103は水素原子、メチル基、―CH2―OHまたは―CH2−O−CO−(C1〜4
アルキル)が好ましく、水素原子、メチル基、―CH2―OHまたは―CH2−O−CO−CH3がより好ましい。
R104は水素原子、メチル基、―CH2―OH、―CH2−O−CO−(C1〜4アル
キル)、―CO―O−(C1〜4アルキル)、―CO―NH―(C1〜4アルキル)が好ましく、水素原子、メチル基、―CH2―OH、―CH2−O−CO−CH3、―CO―O−(C1〜2アルキル)、―CO―NH―(C1〜2アルキル)がより好ましい。
R105、R106は水素原子、メチル基、エチル基が好ましく、水素原子がより好ましい。
R107は水素原子、C1〜4アルキル基、ベンジル基、(C1〜4アルキル置換)フェ
ニルメチル基、(C1〜4アルコキシ置換)フェニルメチル基、(C1〜4アシルオキシ置換)フェニルメチル基、(C1〜4アルコキシカルボニル置換)フェニルメチル基が好ましく、メチル、エチル、ベンジルがより好ましい。
R108は、メチル、エチル、nプロピル、iプロピル、nブチル、フェニルが好ましく
、メチル、エチル、nプロピルがより好ましい。
R109は、水素原子、メチル、エチル、nプロピル、iプロピル、nブチル、フェニル
が好ましく、水素原子、メチル、エチル、nプロピルがより好ましい。
L101は、―CO―O―L0―、―CO―NH―L0−、―CO―NH―L0−、―二価の芳香族基−、―二価の芳香族基−L0−が好ましく、―CO―O―L0―、―CO―NH―L0−がより好ましい。
ここでL0は、二価の脂肪族基、二価の芳香族基またはこれらの組み合わせを表す。
L102は、以下のLa〜Lqが好ましく、La、Lb、Lf、Lg、Lh、Li、Lo、
Lp、Lrがより好ましい。(L0は前記と同義)
La:−L0−O−CO−
Lb:−L0−NH−CO−
Lc:−L0−O−
Ld:−L0−CO−O−
Le:−L0−O−CO−O−
Lf:−L0−O−CH2−
Lg:−L0−CO−O−CH2−
Lh:−L0−O−CO−O−CH2−
Li:−L0−O−CO−NH−L0−O−CO−
Lj:−L0−O−CO−L0−O−CO−
Lk:−L0−O−CO−L0−NH−CO−
Ll:−L0−CO−O−L0−O−CO−
Lm:−L0−CO−O−L0−NH−CO−
Ln:−L0−二価の芳香族基−
Lo:−O−CO−二価の芳香族基−
Lp:−O−CO−L0−二価の芳香族基−
Lq:−CO−O−二価の芳香族基−
Lr:−CO−O−L0−二価の芳香族基−
A more preferable form of the formula (A1) is shown below.
R 101 and R 102 are preferably a hydrogen atom, a methyl group or an ethyl group, more preferably a hydrogen atom.
R 103 represents a hydrogen atom, a methyl group, —CH 2 —OH or —CH 2 —O—CO— (C1-4
Alkyl) is preferable, and a hydrogen atom, a methyl group, —CH 2 —OH or —CH 2 —O—CO—CH 3 is more preferable.
R 104 is a hydrogen atom, a methyl group, —CH 2 —OH, —CH 2 —O—CO— (C1-4 alkyl), —CO—O— (C1-4 alkyl), —CO—NH— (C1— 4 alkyl), preferably a hydrogen atom, a methyl group, —CH 2 —OH, —CH 2 —O—CO—CH 3 , —CO—O— (C 1 -2 alkyl), —CO—NH— (C 1-2). Alkyl) is more preferred.
R 105 and R 106 are preferably a hydrogen atom, a methyl group or an ethyl group, more preferably a hydrogen atom.
R 107 is a hydrogen atom, C1 -4 alkyl group, a benzyl group, (C1 -4 alkyl-substituted) phenylmethyl group, (C1 -4 alkoxy-substituted) phenylmethyl group, (C1 -4 acyloxy-substituted) phenylmethyl group, (C1 ˜4 alkoxycarbonyl-substituted) phenylmethyl group is preferred, and methyl, ethyl, and benzyl are more preferred.
R 108 are methyl, ethyl, n-propyl, i-propyl, n-butyl, phenyl are preferred, methyl, ethyl, n-propyl is more preferable.
R 109 is preferably a hydrogen atom, methyl, ethyl, npropyl, ipropyl, nbutyl, or phenyl, and more preferably a hydrogen atom, methyl, ethyl, or npropyl.
L 101 is preferably -CO-O-L0-, -CO-NH-L0-, -CO-NH-L0-, -divalent aromatic group-, -divalent aromatic group -L0-, -CO-O-L0- and -CO-NH-L0- are more preferable.
Here, L0 represents a divalent aliphatic group, a divalent aromatic group, or a combination thereof.
L 102 is preferably La to Lq below, La, Lb, Lf, Lg, Lh, Li, Lo,
Lp and Lr are more preferable. (L0 is as defined above)
La: -L0-O-CO-
Lb: -L0-NH-CO-
Lc: -L0-O-
Ld: -L0-CO-O-
Le: -L0-O-CO-O-
Lf: -L0-O-CH 2 -
Lg: -L0-CO-O- CH 2 -
Lh: -L0-O-CO- O-CH 2 -
Li: -L0-O-CO-NH-L0-O-CO-
Lj: -L0-O-CO-L0-O-CO-
Lk: -L0-O-CO-L0-NH-CO-
Ll: -L0-CO-O-L0-O-CO-
Lm: -L0-CO-O-L0-NH-CO-
Ln: -L0-divalent aromatic group-
Lo: —O—CO—divalent aromatic group—
Lp: -O-CO-L0-divalent aromatic group-
Lq: —CO—O—divalent aromatic group—
Lr: -CO-O-L0-divalent aromatic group-
m101、m102、n101は特に限定されないが、m102×n101の値が1〜6になることが好
ましく、1〜4になることがより好ましい。
X101 −は、―CO2 −、―PO3H−、―O−PO3H−、―SO3 −が好ましく、
―CO2 −、―O−PO3H−、―SO3 −がより好ましい。
Y101は一般に、n101価の炭化水素残基であり、脂肪族、芳香族どちらの構造を含んでも良く、直鎖状、分岐状、環状のどの構造を含んでも良い。環状の場合は単環、多環いずれでも良い。また、炭化水素を構成する炭素−炭素原子に−CO−、―O―、―S―、−N(R109)−、―SO2―およびそれらの組み合わせからなる構造で中断されていても
良い。
m 101 , m 102 , and n 101 are not particularly limited, but the value of m 102 × n 101 is preferably 1 to 6, and more preferably 1 to 4.
X 101 - is, -CO 2 -, -PO 3 H -, -O-PO 3 H -, -SO 3 - are preferred,
-CO 2 -, -O-PO 3 H -, -SO 3 - is more preferred.
Y 101 is generally an n 101 valent hydrocarbon residue, which may include any of aliphatic and aromatic structures, and may include any of linear, branched, and cyclic structures. In the case of a ring, it may be monocyclic or polycyclic. Further, the carbon-carbon atom constituting the hydrocarbon may be interrupted by a structure comprising —CO—, —O—, —S— , —N (R 109 ) —, —SO 2 —, and combinations thereof. .
上記において、(a1)中のエチレン性不飽和結合を含む構造の少なくとも1つが、(メタ)アクリル酸エステル、(メタ)アクリル酸アミド、芳香族ビニルまたはアリル基であることが最も好ましい。 In the above, at least one of the structures containing an ethylenically unsaturated bond in (a1) is most preferably a (meth) acrylic acid ester, a (meth) acrylic acid amide, an aromatic vinyl or an allyl group.
上記A2で表される、支持体表面と相互作用する官能基を少なくとも1つ有する繰り返し単位(a2)は、具体的には下記式(A2)で表される。 Represented by A 2, the repeating unit having at least one functional group capable of interacting with a surface of the support (a2) is specifically represented by the following formula (A2).
式中、R1〜R3は、式(A1)におけるR101〜R103と同様に定義される。
Lは−CO−、−O−、−NH−、二価の脂肪族基、二価の芳香族基およびそれらの組合せからなる群より選ばれる二価の連結基を表す。
In the formula, R 1 to R 3 are defined in the same manner as R 101 to R 103 in the formula (A1).
L represents a divalent linking group selected from the group consisting of —CO—, —O—, —NH—, a divalent aliphatic group, a divalent aromatic group, and combinations thereof.
Lの具体例を以下に挙げる。なお、下記例において左側が主鎖に結合する。
L1:−CO−O−二価の脂肪族基−O−
L2:−CO−O−二価の脂肪族基−NH−
L3:−CO−O−二価の脂肪族基−
L4:−CO−O−二価の芳香族基−O−
L5:−CO−O−二価の芳香族基−NH−
L6:−CO−O−二価の芳香族基−
L7:−二価の芳香族基−O−
L8:−二価の芳香族基−NH−
L9:−CO−二価の脂肪族基−CO−O−二価の脂肪族基−O−
L10:−CO−二価の脂肪族基−O−CO−二価の脂肪族基−O−
L11:−CO−二価の芳香族基−CO−O−二価の脂肪族基−O−
L12:−CO−二価の芳香族基−O−CO−二価の脂肪族基−O−
L13:−CO−二価の脂肪族基−CO−O−二価の芳香族基−O−
L14:−CO−二価の脂肪族基−O−CO−二価の芳香族基−O−
L15:−CO−二価の芳香族基−CO−O−二価の芳香族基−O−
L16:−CO−二価の芳香族基−O−CO−二価の芳香族基−O−
L17:−CO−O−二価の芳香族基−O−CO−NH−二価の脂肪族基−O−
L18:−CO−O−二価の脂肪族基−O−CO−NH−二価の脂肪族基−O−
L19: −CO−NH−
L20: −CO−O−
L21: −二価の芳香族基−
Specific examples of L are given below. In the following examples, the left side is bonded to the main chain.
L1: -CO-O-divalent aliphatic group -O-
L2: —CO—O—divalent aliphatic group —NH—
L3: —CO—O—divalent aliphatic group—
L4: -CO-O-divalent aromatic group -O-
L5: -CO-O-divalent aromatic group -NH-
L6: -CO-O-divalent aromatic group-
L7: -Divalent aromatic group -O-
L8: -Divalent aromatic group -NH-
L9: -CO-divalent aliphatic group-CO-O-divalent aliphatic group-O-
L10: -CO-divalent aliphatic group-O-CO-divalent aliphatic group-O-
L11: —CO—Divalent aromatic group—CO—O—Divalent aliphatic group —O—
L12: —CO—Divalent aromatic group —O—CO—Divalent aliphatic group —O—
L13: -CO-divalent aliphatic group-CO-O-divalent aromatic group-O-
L14: -CO-divalent aliphatic group-O-CO-divalent aromatic group-O-
L15: -CO-divalent aromatic group-CO-O-divalent aromatic group-O-
L16: -CO-Divalent aromatic group -O-CO-Divalent aromatic group -O-
L17: -CO-O-divalent aromatic group -O-CO-NH-divalent aliphatic group -O-
L18: -CO-O-divalent aliphatic group -O-CO-NH-divalent aliphatic group -O-
L19: -CO-NH-
L20: —CO—O—
L21: -Divalent aromatic group-
二価の脂肪族基とは、アルキレン基、置換アルキレン基、アルケニレン基、置換アルケニレン基、アルキニレン基、置換アルキニレン基またはポリアルキレンオキシ基を意味する。なかでもアルキレン基、置換アルキレン基、アルケニレン基、および置換アルケニレン基が好ましく、アルキレン基および置換アルキレン基がさらに好ましい。
二価の脂肪族基は、環状構造よりも鎖状構造の方が好ましく、さらに分岐を有する鎖状構造よりも直鎖状構造の方が好ましい。
二価の脂肪族基の炭素原子数は、1乃至20であることが好ましく、1乃至15であることがより好ましく、1乃至12であることがさらに好ましく、1乃至10であることがさらにまた好ましく、1乃至8であることが最も好ましい。
二価の脂肪族基の置換基の例としては、ハロゲン原子(F、Cl、Br、I)、ヒドロキシル基、カルボキシル基、アミノ基、シアノ基、アリール基、アルコキシ基、アリールオキシ基、アシル基、アルコキシカルボニル基、アリールオキシカルボニル基、アシルオキシ基、モノアルキルアミノ基、ジアルキルアミノ基、アリールアミノ基およびジアリールアミノ基等が挙げられる。
二価の芳香族基とは、アリレン基または置換アリレン基を意味する。好ましくは、フェニレン、置換フェニレン基、ナフチレンおよび置換ナフチレン基である。
二価の芳香族基の置換基の例としては、上記二価の脂肪族基の置換基の例に加えて、アルキル基が挙げられる。
The divalent aliphatic group means an alkylene group, a substituted alkylene group, an alkenylene group, a substituted alkenylene group, an alkynylene group, a substituted alkynylene group or a polyalkyleneoxy group. Of these, an alkylene group, a substituted alkylene group, an alkenylene group, and a substituted alkenylene group are preferable, and an alkylene group and a substituted alkylene group are more preferable.
The divalent aliphatic group is preferably a chain structure rather than a cyclic structure, and more preferably a linear structure than a branched chain structure.
The number of carbon atoms in the divalent aliphatic group is preferably 1 to 20, more preferably 1 to 15, further preferably 1 to 12, and further preferably 1 to 10. It is preferably 1 to 8, and most preferably.
Examples of the substituent of the divalent aliphatic group include a halogen atom (F, Cl, Br, I), a hydroxyl group, a carboxyl group, an amino group, a cyano group, an aryl group, an alkoxy group, an aryloxy group, and an acyl group. , Alkoxycarbonyl group, aryloxycarbonyl group, acyloxy group, monoalkylamino group, dialkylamino group, arylamino group and diarylamino group.
The divalent aromatic group means an arylene group or a substituted arylene group. Preferable are phenylene, substituted phenylene group, naphthylene and substituted naphthylene group.
Examples of the substituent for the divalent aromatic group include an alkyl group in addition to the examples of the substituent for the divalent aliphatic group.
前記L1〜L21の中では、L1、L2、L9、およびL10が好ましい。 Among L1 to L21, L1, L2, L9, and L10 are preferable.
Qは支持体表面と相互作用する官能基(以下、「特定官能基」と略記する場合がある。)を表す。 特定官能基としては、例えば、陽極酸化処理または親水化処理を施した支持体上に存在する金属、金属酸化物、水酸基などと共有結合、イオン結合、水素結合、極性相互作用、ファンデルワールス相互作用などの相互作用が可能な基が挙げられる。
特定官能基の具体例を以下に挙げる。
Q represents a functional group that interacts with the support surface (hereinafter sometimes abbreviated as “specific functional group”). Specific functional groups include, for example, covalent bonds, ionic bonds, hydrogen bonds, polar interactions, van der Waals interactions with metals, metal oxides, hydroxyl groups, etc. present on an anodized or hydrophilized support. Examples include groups capable of interaction such as action.
Specific examples of the specific functional group are listed below.
(上記式中、R11〜R13はそれぞれ独立に、水素原子、アルキル基、アリール基、アルキニル基、またはアルケニル基を表し、M1およびM2はそれぞれ独立に、水素原子、金属原子、またはアンモニウム基を表し、X-はカウンターアニオンを表す。)
これらのなかでも特定官能基としては、アンモニウム基、スルホン酸基若しくはその塩、リン酸エステル若しくはその塩、ホスホン酸基若しくはその塩、ホウ酸基、アセチルアセトン基などのβ−ジケトン基、ピリジニウム基等のオニウム塩基、などが好適である。
さらに好ましくは、スルホン酸基若しくはその塩、リン酸エステル基若しくはその塩、または、ホスホン酸基若しくはその塩である。
(In the above formula, R 11 to R 13 each independently represents a hydrogen atom, an alkyl group, an aryl group, an alkynyl group, or an alkenyl group, and M 1 and M 2 each independently represent a hydrogen atom, a metal atom, or Represents an ammonium group, and X − represents a counter anion.)
Among these, specific functional groups include ammonium groups, sulfonic acid groups or salts thereof, phosphate esters or salts thereof, phosphonic acid groups or salts thereof, β-diketone groups such as boric acid groups and acetylacetone groups, pyridinium groups, etc. Of these, onium bases are preferred.
More preferred are a sulfonic acid group or a salt thereof, a phosphate ester group or a salt thereof, or a phosphonic acid group or a salt thereof.
A3で表される、(a1)以外の親水性基を少なくとも1つ含有する繰り返し単位(a3)は、好ましくは下記式(A3)で表される。 Represented by A 3, (a1) other hydrophilic groups at least one containing repeated unit (a3) is preferably represented by the following formula (A3).
式中、R1〜R3およびLは前記式(A2)で表されるものと同義である。Wは下記基を表す。 In formula, R < 1 > -R < 3 > and L are synonymous with what is represented by said Formula (A2). W represents the following group.
ただし、M1は前記式(A2)の説明で表されるものと同義である。
R7およびR8はそれぞれ独立に、水素原子、あるいは炭素数1〜6の直鎖または分岐のアルキル基を表す。
R9は炭素数1〜6の直鎖または分岐のアルキレン基を表し、エチレン基が好ましい。
R10は水素原子または炭素数1〜12のアルキル基を表す。
nは1〜100の整数を表し、1〜30が好ましい。
However, M 1 is the same meanings as those represented in the description of the formula (A2).
R 7 and R 8 each independently represents a hydrogen atom or a linear or branched alkyl group having 1 to 6 carbon atoms.
R 9 represents a linear or branched alkylene group having 1 to 6 carbon atoms, preferably an ethylene group.
R 10 represents a hydrogen atom or an alkyl group having 1 to 12 carbon atoms.
n represents an integer of 1 to 100, and preferably 1 to 30.
前記Wとしては、カルボン酸(塩)基、スルホン酸(塩)基を含むものが好ましく、特にスルホン酸(塩)基を含むものが汚れ防止性の観点から好ましい。 As W, those containing a carboxylic acid (salt) group and a sulfonic acid (salt) group are preferred, and those containing a sulfonic acid (salt) group are particularly preferred from the viewpoint of stain resistance.
本発明における(D)共重合体は上記A1、A2、A3で表される繰り返し単位以外に本
発明の効果を損なわない限りにおいて、以下に説明するその他のモノマーから選ばれた1
種以上との共重合体であっても良い。
The copolymer (D) in the present invention is selected from the other monomers described below as long as the effects of the present invention are not impaired other than the repeating units represented by A 1 , A 2 and A 3.
It may be a copolymer with more than one species.
(その他のモノマー)
(1)2−ヒドロキシエチルアクリレートまたは2−ヒドロキシエチルメタクリレート等の脂肪族水酸基を有するアクリル酸エステル類、およびメタクリル酸エステル類。
(2)アクリル酸メチル、アクリル酸エチル、アクリル酸プロピル、アクリル酸アミル、アクリル酸ベンジル、アクリル酸−2−クロロエチル、グリシジルアクリレート、N−ジメチルアミノエチルアクリレート、ポリエチレングリコールモノアクリレート、ポリプロピレングリコールモノアルキレート等のアクリレート。
(3)メタクリル酸メチル、メタクリル酸エチル、メタクリル酸プロピル、メタクリル酸アミル、メタクリル酸シクロヘキシル、メタクリル酸ベンジル、メタクリル酸−2−クロロエチル、グリシジルメタクリレート、N−ジメチルアミノエチルメタクリレート、ポリエチレングリコールモノメタクリレート、ポリプロピレングリコールモノメタクリレート等のメタクリレート。
(Other monomers)
(1) Acrylic acid esters and methacrylic acid esters having an aliphatic hydroxyl group such as 2-hydroxyethyl acrylate or 2-hydroxyethyl methacrylate.
(2) Methyl acrylate, ethyl acrylate, propyl acrylate, amyl acrylate, benzyl acrylate, 2-chloroethyl acrylate, glycidyl acrylate, N-dimethylaminoethyl acrylate, polyethylene glycol monoacrylate, polypropylene glycol monoalkylate Acrylates and the like.
(3) Methyl methacrylate, ethyl methacrylate, propyl methacrylate, amyl methacrylate, cyclohexyl methacrylate, benzyl methacrylate, 2-chloroethyl methacrylate, glycidyl methacrylate, N-dimethylaminoethyl methacrylate, polyethylene glycol monomethacrylate, polypropylene Methacrylates such as glycol monomethacrylate.
(4)アクリルアミド、メタクリルアミド、N−メチロールアクリルアミド、N−エチルアクリルアミド、N−ヘキシルメタクリルアミド、N−シクロヘキシルアクリルアミド、N−ヒドロキシエチルアクリルアミド、N−フェニルアクリルアミド、N−ニトロフェニルアクリルアミド、N−エチル−N−フェニルアクリルアミド等のアクリルアミドまたはメタクリルアミド。
(5)エチルビニルエーテル、2−クロロエチルビニルエーテル、ヒドロキシエチルビニルエーテル、プロピルビニルエーテル、ブチルビニルエーテル、フェニルビニルエーテル等のビニルエーテル類。
(6)ビニルアセテート、ビニルクロロアセテート、ビニルブチレート、安息香酸ビニル等のビニルエステル類。
(4) Acrylamide, methacrylamide, N-methylolacrylamide, N-ethylacrylamide, N-hexylmethacrylamide, N-cyclohexylacrylamide, N-hydroxyethylacrylamide, N-phenylacrylamide, N-nitrophenylacrylamide, N-ethyl- Acrylamide or methacrylamide such as N-phenylacrylamide.
(5) Vinyl ethers such as ethyl vinyl ether, 2-chloroethyl vinyl ether, hydroxyethyl vinyl ether, propyl vinyl ether, butyl vinyl ether, and phenyl vinyl ether.
(6) Vinyl esters such as vinyl acetate, vinyl chloroacetate, vinyl butyrate and vinyl benzoate.
(7)スチレン、α−メチルスチレン、メチルスチレン、クロロメチルスチレン等のスチレン類。
(8)メチルビニルケトン、エチルビニルケトン、プロピルビニルケトン、フェニルビ
ニルケトン等のビニルケトン類。
(9)エチレン、プロピレン、イソブチレン、ブタジエン、イソプレン等のオレフィン類。
(10)N−ビニルピロリドン、N−ビニルカルバゾール、4−ビニルピリジン、アクリロニトリル、メタクリロニトリル等。
(11)マレイミド、N−アクリロイルアクリルアミド、N−アセチルメタクリルアミド、N−プロピオニルメタクリルアミド、N−(p−クロロベンゾイル)メタクリルアミド等の不飽和イミド。
(7) Styrenes such as styrene, α-methylstyrene, methylstyrene, and chloromethylstyrene.
(8) Vinyl ketones such as methyl vinyl ketone, ethyl vinyl ketone, propyl vinyl ketone, and phenyl vinyl ketone.
(9) Olefins such as ethylene, propylene, isobutylene, butadiene, and isoprene.
(10) N-vinylpyrrolidone, N-vinylcarbazole, 4-vinylpyridine, acrylonitrile, methacrylonitrile and the like.
(11) Unsaturated imides such as maleimide, N-acryloylacrylamide, N-acetylmethacrylamide, N-propionylmethacrylamide, N- (p-chlorobenzoyl) methacrylamide.
前記(D)共重合体の分子量としては、質量平均分子量で500〜100,000の範囲が好ましく、700〜50,000の範囲がより好ましい。また、(A1)は全共重合モノマーに対して1〜80モル%が好ましく、2〜50モル%が好ましい。(A2)は全共重合モノマーに対して1〜80モル%が好ましく、2〜40モル%が好ましい。(A3)は全共重合モノマーに対して10〜95モル%が好ましく、20〜90モル%が好ましい。 The molecular weight of the copolymer (D) is preferably in the range of 500 to 100,000, more preferably in the range of 700 to 50,000 in terms of mass average molecular weight. Further, (A 1 ) is preferably from 1 to 80 mol%, more preferably from 2 to 50 mol%, based on all copolymerized monomers. (A 2) is 1 to 80 mol% are preferred with respect to the total copolymerizable monomer, preferably 2 to 40 mol%. (A 3) is preferably 10 to 95 mol% based on the total copolymerization monomers, preferably 20 to 90 mol%.
(D)共重合体の具体例を下記に示すが、本発明は、下記例に限定されない。 Specific examples of the copolymer (D) are shown below, but the present invention is not limited to the following examples.
(D)共重合体の製造方法は、とくに限定されるものではないが、例えば、通常のラジカル重合でポリマーを得た後、エチレン性不飽和結合を含有するアミン化合物、もしくはエチレン性不飽和結合を含有するアンモニウム塩を加えることで合成できる。加えるアンモニウム塩に含まれるアニオンの構造は、ポリマー中の酸基よりも酸性度の低い化合物のアニオン、例えばヒドロキシアニオン(OH−)やカルボキシレートアニオン(CH3CO2 −)であることが好ましい。 (D) Although the manufacturing method of a copolymer is not specifically limited, For example, after obtaining a polymer by normal radical polymerization, an amine compound containing an ethylenically unsaturated bond, or an ethylenically unsaturated bond It can be synthesized by adding an ammonium salt containing. The structure of the anion contained in the ammonium salt to be added is preferably an anion of a compound having a lower acidity than the acid group in the polymer, such as a hydroxy anion (OH − ) or a carboxylate anion (CH 3 CO 2 − ).
(D)共重合体の使用形態としては、感光層中に含有させることも、またはその他の層に含有させることもできる。その他の層としては、支持体に隣接する層である。なかでも支持体と感光層との間に設けられる下塗り層(中間層)に用いるのが本発明の効果が十分に発揮されるため特に好ましい。下塗り層に用いることにより、露光部の支持体と感光層とのより強固な接着性が得られ、未露光部においては、感光層の支持体からの剥離を生じやすくさせるため、現像性、汚れ性が向上する。 (D) As a usage form of the copolymer, it can be contained in the photosensitive layer, or can be contained in other layers. The other layer is a layer adjacent to the support. Of these, use for an undercoat layer (intermediate layer) provided between the support and the photosensitive layer is particularly preferable because the effects of the present invention are sufficiently exhibited. By using it as an undercoat layer, stronger adhesion between the support in the exposed area and the photosensitive layer can be obtained, and in the unexposed area, peeling from the support of the photosensitive layer is likely to occur. Improves.
本発明において(D)共重合体を下塗り層に用いる場合には、通常該共重合体を溶剤で希釈して用いる。溶媒としては、水や、メタノール、エタノール、プロパノール、イソプロパノール、エチレングリコール、ヘキシレングリコール、テトラヒドロフラン、ジメチルホルムアミド、1−メトキシ−2−プロパノール、ジメチルアセトアミド、ジメチルスルホキシド等の有機溶媒が挙げられ、特に水、アルコール類が好ましい。これらの有機溶媒は混合して用いることもできる。 In the present invention, when the (D) copolymer is used for the undercoat layer, the copolymer is usually diluted with a solvent. Examples of the solvent include water and organic solvents such as methanol, ethanol, propanol, isopropanol, ethylene glycol, hexylene glycol, tetrahydrofuran, dimethylformamide, 1-methoxy-2-propanol, dimethylacetamide, and dimethyl sulfoxide. Alcohols are preferred. These organic solvents can also be mixed and used.
下塗り層塗布液の濃度としては、0.001〜10質量%が好ましく、より好ましくは0.01〜5質量%であり、さらに好ましくは0.05〜1質量%である。下塗り層には、必要に応じて後述する界面活性剤を添加してもよい。下塗り層塗布液を支持体に塗布する方法としては、公知の種々の方法を用いることができる。例えば、バーコーター塗布、回転塗布、スプレー塗布、カーテン塗布、ディップ塗布、エアナイフ塗布、ブレード塗布、ロール塗布等を挙げることができる。 As a density | concentration of undercoat layer coating liquid, 0.001-10 mass% is preferable, More preferably, it is 0.01-5 mass%, More preferably, it is 0.05-1 mass%. A surfactant described later may be added to the undercoat layer as necessary. Various known methods can be used as a method of applying the undercoat layer coating solution to the support. Examples thereof include bar coater coating, spin coating, spray coating, curtain coating, dip coating, air knife coating, blade coating, and roll coating.
下塗り層の塗布量(固形分)は0.1〜200mg/m2であるのが好ましく、1〜5
0mg/m2であるのがより好ましい。
The coating amount (solid content) of the undercoat layer is preferably 0.1 to 200 mg / m 2 , and 1 to 5
More preferably, it is 0 mg / m 2 .
(E)増感色素
本発明の感光層には、露光光源の波長に対応した、350〜450nmの波長域に極大吸収を有する増感色素を含有するのが好ましい。
この様な増感色素としては、例えば、下記一般式(V)に示されるメロシアニン色素類、下記一般式(VI)で示されるベンゾピラン類、クマリン類、下記一般式(VII)で表される芳香族ケトン類、下記一般式(VIII)で表されるアントラセン類、等を挙げることができる。
(E) Sensitizing dye The photosensitive layer of the present invention preferably contains a sensitizing dye having a maximum absorption in a wavelength region of 350 to 450 nm corresponding to the wavelength of the exposure light source.
Examples of such a sensitizing dye include merocyanine dyes represented by the following general formula (V), benzopyrans and coumarins represented by the following general formula (VI), and fragrances represented by the following general formula (VII). And anthracenes represented by the following general formula (VIII).
(式中、AはS原子もしくは、NR6を表し、R6は一価の非金属原子団を表し、Yは隣接するAおよび、隣接炭素原子と共同して色素の塩基性核を形成する非金属原子団を表し、X1、X2はそれぞれ独立に、一価の非金属原子団を表し、X1、X2は互いに結合して色素の酸性核を形成してもよい。) (In the formula, A represents an S atom or NR 6 , R 6 represents a monovalent non-metallic atomic group, Y represents a basic nucleus of the dye in cooperation with the adjacent A and the adjacent carbon atom. A non-metallic atomic group, X 1 and X 2 each independently represent a monovalent non-metallic atomic group, and X 1 and X 2 may combine with each other to form an acidic nucleus of the dye.)
(式中、=Zは、オキソ基、チオキソ基、イミノ基または上記部分構造式(1’)で表されるアルキリデン基を表し、X1、X2は一般式(V)と同義であり、R7〜R12はそれ
ぞれ独立に一価の非金属原子団を表す。)
(In the formula, = Z represents an oxo group, a thioxo group, an imino group or an alkylidene group represented by the partial structural formula (1 ′), and X 1 and X 2 have the same meanings as those in the general formula (V); R 7 to R 12 each independently represents a monovalent nonmetallic atomic group.)
(式中Ar3は、置換基を有していてもよい芳香族基またはヘテロ芳香族基を表し、R13は一価の非金属原子団を表す。より好ましいR13は、芳香族基またはヘテロ芳香族基で
あって、Ar3とR13が互いに結合して環を形成してもよい。)
(In the formula, Ar 3 represents an aromatic group or a heteroaromatic group which may have a substituent, and R 13 represents a monovalent nonmetallic atomic group. More preferred R 13 represents an aromatic group or It is a heteroaromatic group, and Ar 3 and R 13 may be bonded to each other to form a ring.)
(式中、X3、X4、R14〜R21はそれぞれ独立に、一価の非金属原子団を表し、より好ましいX3、X4はハメットの置換基定数が負の電子供与性基である。) (In the formula, X 3 , X 4 and R 14 to R 21 each independently represents a monovalent non-metallic atomic group, and more preferable X 3 and X 4 are electron donating groups having a negative Hammett's substituent constant. .)
一般式(V)から(VIII)における、X1からX4、R6からR21で表される一価の
非金属原子団の好ましい例としては、水素原子、アルキル基(例えば、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、ヘプチル基、オクチル基、ノニル
基、デシル基、ウンデシル基、ドデシル基、トリデシル基、ヘキサデシル基、オクタデシル基、エイコシル基、イソプロピル基、イソブチル基、s−ブチル基、t−ブチル基、イソペンチル基、ネオペンチル基、1−メチルブチル基、イソヘキシル基、2−エチルヘキシル基、2−メチルヘキシル基、シクロヘキシル基、シクロペンチル基、2−ノルボルニル基、クロロメチル基、ブロモメチル基、2−クロロエチル基、トリフルオロメチル基、メトキシメチル基、メトキシエトキシエチル基、アリルオキシメチル基、フェノキシメチル基、メチルチオメチル基、トリルチオメチル基、エチルアミノエチル基、ジエチルアミノプロピル基、モルホリノプロピル基、アセチルオキシメチル基、ベンゾイルオキシメチル基、N−シクロヘキシルカルバモイルオキシエチル基、N−フェニルカルバモイルオキシエチル基、アセチルアミノエチル基、N−メチルベンゾイルアミノプロピル基、2−オキソエチル基、2−オキソプロピル基、カルボキシプロピル基、メトキシカルボニルエチル基、アリルオキシカルボニルブチル基、クロロフェノキシカルボニルメチル基、カルバモイルメチル基、N−メチルカルバモイルエチル基、N,N−ジプロピルカルバモイルメチル基、N−(メトキシフェニル)カルバモイルエチル基、N−メチル−N−(スルホフェニル)カルバモイルメチル基、スルホブチル基、スルホナトブチル基、スルファモイルブチル基、N−エチルスルファモイルメチル基、N,N−ジプロピルスルファモイルプロピル基、N−トリルスルファモイルプロピル基、N−メチル−N−(ホスフォノフェニル)スルファモイルオクチル基、ホスフォノブチル基、ホスフォナトヘキシル基、ジエチルホスフォノブチル基、ジフェニルホスフォノプロピル基、メチルホスフォノブチル基、メチルホスフォナトブチル基、トリルホスフォノヘキシル基、トリルホスフォナトヘキシル基、ホスフォノオキシプロピル基、ホスフォナトオキシブチル基、ベンジル基、フェネチル基、α−メチルベンジル基、1−メチル−1−フェニルエチル基、p−メチルベンジル基、シンナミル基、アリル基、1−プロペニルメチル基、2−ブテニル基、2−メチルアリル基、2−メチルプロペニルメチル基、2−プロピニル基、2−ブチニル基、3−ブチニル基等)、アリール基(例えば、フェニル基、ビフェニル基、ナフチル基、トリル基、キシリル基、メシチル基、クメニル基、クロロフェニル基、ブロモフェニル基、クロロメチルフェニル基、ヒドロキシフェニル基、メトキシフェニル基、エトキシフェニル基、フェノキシフェニル基、アセトキシフェニル基、ベンゾイロキシフェニル基、メチルチオフェニル基、フェニルチオフェニル基、メチルアミノフェニル基、ジメチルアミノフェニル基、アセチルアミノフェニル基、カルボキシフェニル基、メトキシカルボニルフェニル基、エトキシフェニルカルボニル基、フェノキシカルボニルフェニル基、N−フェニルカルバモイルフェニル基、フェニル基、シアノフェニル基、スルホフェニル基、スルホナトフェニル基、ホスフォノフェニル基、ホスフォナトフェニル基等)、ヘテロアリール基(例えば、チオフェン、チアスレン、フラン、ピラン、イソベンゾフラン、クロメン、キサンテン、フェノキサジン、ピロール、ピラゾール、イソチアゾール、イソオキサゾール、ピラジン、ピリミジン、ピリダジン、インドリジン、イソインドリジン、インドイール、インダゾール、プリン、キノリジン、イソキノリン、フタラジン、ナフチリジン、キナゾリン、シノリン、プテリジン、カルバゾール、カルボリン、フェナンスリン、アクリジン、ペリミジン、フェナンスロリン、フタラジン、フェナルザジン、フェノキサジン、フラザン、フェノキサジン等)、アルケニル基(例えばビニル基、1−プロペニル基、1−ブテニル基、シンナミル基、2−クロロ−1−エテニル基、等)、アルキニル基(例えば、エチニル基、1−プロピニル基、1−ブチニル基、トリメチルシリルエチニル基等)、ハロゲン原子(−F、−Br、−Cl、−I)、ヒドロキシル基、アルコキシ基、アリーロキシ基、メルカプト基、アルキルチオ基、アリールチオ基、アルキルジチオ基、アリールジチオ基、アミノ基、N−アルキルアミノ基、N,N−ジアルキルアミノ基、N−アリールアミノ基、N,N−ジアリールアミノ基、N−アルキル−N−アリールアミノ基、アシルオキシ基、カルバモイルオキシ基、N−アルキルカルバモイルオキシ基、N−アリールカルバモイルオキシ基、N,N−ジアルキルカルバモイルオキシ基、N,N−ジアリールカルバモイルオキシ基、N−アルキル−N−アリールカルバモイルオキシ基、アルキルスルホキシ基、アリールスルホキシ基、アシルチオ基、アシルアミノ基、N−アルキルアシルアミノ基、N−アリールアシルアミノ基、ウレイド基、N′−アルキルウレイド基、N′,N′−ジアルキルウレイド基、N′−アリールウレイド基、N′,N′−ジアリールウレイド基、N′−アルキル−N′−アリールウレイド基、N−アルキルウレイド基、N−アリールウレイド基、N′−アルキル−N−アルキルウレイド基、N′−アルキル−N−アリールウレイド基、N′,N′−ジアルキル−N−アルキルウレイド基、N′,N′−ジアルキル−N−アリールウレイド基、N′−アリール−N−アルキルウレイド基、N′−アリール−N−アリールウレイド基、N′,N′−ジアリール−N−アルキルウレイド基、N′,N′−ジアリール−N−アリールウレイド基、N′−アルキル−N′−アリール−N−アルキルウレイド基、N′−アルキル−N′−アリール−N−アリールウレイド基、アルコキシカルボニルアミノ基、アリーロキシカルボニルアミノ基、N−アルキル−N−アルコキシカルボニルアミノ基、N−アルキル−N−アリーロキシカルボニルアミノ基、N−アリール−N−アルコキシカルボニルアミノ基、N−アリール−N−アリーロキシカルボニルアミノ基、アシル基、カルボキシル基、アルコキシカルボニル基、アリーロキシカルボニル基、カルバモイル基、N−アルキルカルバモイル基、N,N−ジアルキルカルバモイル基、N−アリールカルバモイル基、N,N−ジアリールカルバモイル基、N−アルキル−N−アリールカルバモイル基、アルキルスルフィニル基、アリールスルフィニル基、アルキルスルホニル基、アリールスルホニル基、スルホ基(−SO3H)およびその共役塩基基(以下、スルホナト基と称す)、アルコキシスルホニル基、アリーロキシスルホニル基、スルフィナモイル基、N−アルキルスルフィナモイル基、N,N−ジアルキルスルフィナモイル基、N−アリールスルフィナモイル基、N,N−ジアリールスルフィナモイル基、N−アルキル−N−アリールスルフィナモイル基、スルファモイル基、N−アルキルスルファモイル基、N,N−ジアルキルスルファモイル基、N−アリールスルファモイル基、N,N−ジアリールスルファモイル基、N−アルキル−N−アリールスルファモイル基、ホスフォノ基(−PO3H2)およびその共役塩基基(以下、ホスフォナト基と称す)、ジアルキルホスフォノ基(−PO3(alkyl)2)、ジアリールホスフォノ基(−PO3(aryl)2)、アルキルアリールホスフォノ基(−PO3(alkyl)(aryl))、モノアルキルホスフォノ基(−PO3H(alkyl))およびその共役塩基基(以後、アルキルホスフォナト基と称す)、モノアリールホスフォノ基(−PO3H(aryl))およびその共役塩基基(以後、アリールホスフォナト基と称す)、ホスフォノオキシ基(−OPO3H2)およびその共役塩基基(以後、ホスフォナトオキシ基と称す)、ジアルキルホスフォノオキシ基(−OPO3(alkyl)2)、ジアリールホスフォノオキシ基(−OPO3(aryl)2)、アルキルアリールホスフォノオキシ基(−OPO3(alkyl)(aryl))、モノアルキルホスフォノオキシ基(−OPO3H(alkyl))およびその共役塩基基(以後、アルキルホスフォナトオキシ基と称す)、モノアリールホスフォノオキシ基(−OPO3H(aryl))およびその共役塩基基(以後、アリールフォスホナトオキシ基と称す)、シアノ基、ニトロ基、等が挙げられ、以上の置換基のうち、水素原子、アルキル基、アリール基、ハロゲン原子、アルコキシ基、アシル基が特に好ましい。
In the general formulas (V) to (VIII), preferred examples of the monovalent nonmetallic atomic group represented by X 1 to X 4 and R 6 to R 21 include a hydrogen atom, an alkyl group (for example, a methyl group, Ethyl group, propyl group, butyl group, pentyl group, hexyl group, heptyl group, octyl group, nonyl group, decyl group, undecyl group, dodecyl group, tridecyl group, hexadecyl group, octadecyl group, eicosyl group, isopropyl group, isobutyl group , S-butyl group, t-butyl group, isopentyl group, neopentyl group, 1-methylbutyl group, isohexyl group, 2-ethylhexyl group, 2-methylhexyl group, cyclohexyl group, cyclopentyl group, 2-norbornyl group, chloromethyl group , Bromomethyl group, 2-chloroethyl group, trifluoromethyl group, methoxymethyl group, methoxy ester Toxiethyl group, allyloxymethyl group, phenoxymethyl group, methylthiomethyl group, tolylthiomethyl group, ethylaminoethyl group, diethylaminopropyl group, morpholinopropyl group, acetyloxymethyl group, benzoyloxymethyl group, N-cyclohexylcarbamoyloxyethyl Group, N-phenylcarbamoyloxyethyl group, acetylaminoethyl group, N-methylbenzoylaminopropyl group, 2-oxoethyl group, 2-oxopropyl group, carboxypropyl group, methoxycarbonylethyl group, allyloxycarbonylbutyl group, chloro Phenoxycarbonylmethyl group, carbamoylmethyl group, N-methylcarbamoylethyl group, N, N-dipropylcarbamoylmethyl group, N- (methoxyphenyl) carbamoylethyl group, -Methyl-N- (sulfophenyl) carbamoylmethyl group, sulfobutyl group, sulfonatobutyl group, sulfamoylbutyl group, N-ethylsulfamoylmethyl group, N, N-dipropylsulfamoylpropyl group, N-tolylsulfa Moylpropyl group, N-methyl-N- (phosphonophenyl) sulfamoyloctyl group, phosphonobutyl group, phosphonatohexyl group, diethylphosphonobutyl group, diphenylphosphonopropyl group, methylphosphonobutyl group, methyl Phosphonatobutyl group, tolylphosphonohexyl group, tolylphosphonatohexyl group, phosphonooxypropyl group, phosphonatoxybutyl group, benzyl group, phenethyl group, α-methylbenzyl group, 1-methyl-1-phenylethyl group P-methylbenzyl group , Cinnamyl group, allyl group, 1-propenylmethyl group, 2-butenyl group, 2-methylallyl group, 2-methylpropenylmethyl group, 2-propynyl group, 2-butynyl group, 3-butynyl group, etc.), aryl group ( For example, phenyl group, biphenyl group, naphthyl group, tolyl group, xylyl group, mesityl group, cumenyl group, chlorophenyl group, bromophenyl group, chloromethylphenyl group, hydroxyphenyl group, methoxyphenyl group, ethoxyphenyl group, phenoxyphenyl group , Acetoxyphenyl group, benzoyloxyphenyl group, methylthiophenyl group, phenylthiophenyl group, methylaminophenyl group, dimethylaminophenyl group, acetylaminophenyl group, carboxyphenyl group, methoxycarbonylphenyl group, ethoxyphenylcarbonyl Phenoxycarbonylphenyl group, N-phenylcarbamoylphenyl group, phenyl group, cyanophenyl group, sulfophenyl group, sulfonatophenyl group, phosphonophenyl group, phosphonatophenyl group, etc.), heteroaryl group (for example, thiophene, thiathrene) , Furan, pyran, isobenzofuran, chromene, xanthene, phenoxazine, pyrrole, pyrazole, isothiazole, isoxazole, pyrazine, pyrimidine, pyridazine, indolizine, isoindolizine, indoyl, indazole, purine, quinolidine, isoquinoline, phthalazine , Naphthyridine, quinazoline, cynoline, pteridine, carbazole, carboline, phenanthrine, acridine, perimidine, phenanthroline, phthalazine, phenalzadi , Phenoxazine, furazane, phenoxazine, etc.), alkenyl group (eg, vinyl group, 1-propenyl group, 1-butenyl group, cinnamyl group, 2-chloro-1-ethenyl group, etc.), alkynyl group (eg, ethynyl group) 1-propynyl group, 1-butynyl group, trimethylsilylethynyl group, etc.), halogen atom (-F, -Br, -Cl, -I), hydroxyl group, alkoxy group, aryloxy group, mercapto group, alkylthio group, arylthio group Alkyldithio group, aryldithio group, amino group, N-alkylamino group, N, N-dialkylamino group, N-arylamino group, N, N-diarylamino group, N-alkyl-N-arylamino group, Acyloxy group, carbamoyloxy group, N-alkylcarbamoyloxy group, N-arylcal Vamoyloxy group, N, N-dialkylcarbamoyloxy group, N, N-diarylcarbamoyloxy group, N-alkyl-N-arylcarbamoyloxy group, alkylsulfoxy group, arylsulfoxy group, acylthio group, acylamino group, N- Alkylacylamino group, N-arylacylamino group, ureido group, N′-alkylureido group, N ′, N′-dialkylureido group, N′-arylureido group, N ′, N′-diarylureido group, N '-Alkyl-N'-arylureido group, N-alkylureido group, N-arylureido group, N'-alkyl-N-alkylureido group, N'-alkyl-N-arylureido group, N', N ' -Dialkyl-N-alkylureido groups, N ', N'-dialkyl-N-arylurees Group, N′-aryl-N-alkylureido group, N′-aryl-N-arylureido group, N ′, N′-diaryl-N-alkylureido group, N ′, N′-diaryl-N-aryl Ureido group, N′-alkyl-N′-aryl-N-alkylureido group, N′-alkyl-N′-aryl-N-arylureido group, alkoxycarbonylamino group, aryloxycarbonylamino group, N-alkyl- N-alkoxycarbonylamino group, N-alkyl-N-aryloxycarbonylamino group, N-aryl-N-alkoxycarbonylamino group, N-aryl-N-aryloxycarbonylamino group, acyl group, carboxyl group, alkoxycarbonyl Group, aryloxycarbonyl group, carbamoyl group, N-alkylcarbamo Group, N, N-dialkylcarbamoyl group, N-arylcarbamoyl group, N, N-diarylcarbamoyl group, N-alkyl-N-arylcarbamoyl group, alkylsulfinyl group, arylsulfinyl group, alkylsulfonyl group, arylsulfonyl group , Sulfo group (—SO 3 H) and its conjugate base group (hereinafter referred to as sulfonate group), alkoxysulfonyl group, aryloxysulfonyl group, sulfinamoyl group, N-alkylsulfinamoyl group, N, N-dialkylsulfina Moyl group, N-arylsulfinamoyl group, N, N-diarylsulfinamoyl group, N-alkyl-N-arylsulfinamoyl group, sulfamoyl group, N-alkylsulfamoyl group, N, N-dialkylsulfur group Famoyl group, N-arylsulfur Amoyl group, N, N-diarylsulfamoyl group, N-alkyl-N-arylsulfamoyl group, phosphono group (—PO 3 H 2 ) and its conjugate base group (hereinafter referred to as phosphonate group), dialkylphosphine Phono group (—PO 3 (alkyl) 2 ), diaryl phosphono group (—PO 3 (aryl) 2 ), alkylaryl phosphono group (—PO 3 (alkyl) (aryl)), monoalkyl phosphono group (— PO 3 H (alkyl)) and its conjugate base group (hereinafter referred to as alkyl phosphonate group), monoaryl phosphono group (—PO 3 H (ary)) and its conjugate base group (hereinafter referred to as aryl phosphonate group) referred), phosphonooxy group (-OPO 3 H 2) and its conjugated base group (hereinafter referred to as phosphonophenyl group), dialkyl Phosphonooxy group (-OPO 3 (alkyl) 2) , diaryl phosphonooxy group (-OPO 3 (aryl) 2) , alkylaryl phosphonooxy group (-OPO 3 (alkyl) (aryl )), monoalkyl phosphate A phonooxy group (—OPO 3 H (alkyl)) and its conjugate base group (hereinafter referred to as an alkylphosphonatooxy group), a monoarylphosphonooxy group (—OPO 3 H (aryl)) and its conjugate base group ( Hereinafter, it is referred to as an arylphosphonatooxy group), a cyano group, a nitro group, and the like. Among these substituents, a hydrogen atom, an alkyl group, an aryl group, a halogen atom, an alkoxy group, and an acyl group are particularly preferable.
一般式(V)に於けるYが隣接するAおよび、隣接炭素原子と共同して形成する色素の塩基性核としては、5、6、7員の含窒素、あるいは含硫黄複素環が挙げられ、好ましくは5、6員の複素環がよい。 Examples of the basic nucleus of the dye formed together with A adjacent to Y in the general formula (V) and the adjacent carbon atom include 5-, 6-, and 7-membered nitrogen-containing or sulfur-containing heterocycles. A 5- or 6-membered heterocyclic ring is preferable.
含窒素複素環の例としては例えば、L.G.Brooker et al.,J.Am.Chem.Soc.,73,5326−5358(1951)および参考文献に記載されるメロシアニン色素類における塩基性核を構成するものとして知られるものをいずれも好適に用いることができる。具体例としては、チアゾール類(例えば、チアゾール、4−メチルチアゾール、4ーフェニルチアゾール、5−メチルチアゾール、5−フェニルチアゾール、4,5−ジメチルチアゾール、4,5−ジフェニルチアゾール、4,5−ジ(p−メトキシフェニルチアゾール)、4−(2−チエニル)チアゾール、等)、ベンゾチアゾール類(例えば、ベンゾチアゾール、4−クロロベンゾチアゾール、5−クロロベンゾチアゾール、6−クロロベンゾチアゾール、7−クロロベンゾチアゾール、4−メチルベンゾチアゾール、5−メチルベンゾチアゾール、6−メチルベンゾチアゾール、5−ブロモベンゾチアゾール、4−フェニルベンゾチアゾール、5−フェニルベンゾチアゾール、4−メトキシベンゾチアゾール、5−メトキシベンゾチアゾール、6−メトキシベンゾチアゾール、5−ヨードベンゾチアゾール、6−ヨードベンゾチアゾール、4−エトキシベンゾチアゾール、5−エトキシベンゾチアゾール、テトラヒドロベンゾチアゾール、5,6−ジメトキシベンゾチアゾール、5,6−ジオキシメチレンベンゾチアゾール、5−ヒドロキシベンゾチアゾール、6−ヒドロキシベンゾチアゾール、6ージメチルアミノベンゾチアゾール、5−エトキシカルボニルベンゾチアゾール等)、ナフトチアゾール類(例えば、ナフト[1,2]チアゾール、ナフト[2,1]チアゾール、5−メトキシナフト[2,1]チアゾール、5−エトキシナフト[2,1]チアゾール、8−メトキシナフト[1,2]チアゾール、7−メトキシナフト[1,2]チアゾール等)、チアナフテノ−7’,6’,4,5−チアゾール類(例えば、4’−メトキシチアナフテノ−7’,6’,4,5−チアゾール等)、オキサゾール類(例えば、4−メチルオキサゾール、5−メチルオキサゾール、4−フェニルオキサゾール、4,5−ジフェニルオキサゾール、4−エチルオキサゾール、4,5−ジメチルオキサゾール、5−フェニルオキサゾール等)、ベンゾオキサゾール類(ベンゾオキサゾール、5−クロロベンゾオキサゾール、5−メチルベンゾオキサゾール、5−フェニルベンゾオキサゾール、6−メチルベンゾオキサゾール、5,6−ジメチルベンゾオキサゾール、4,6−ジメチルベンゾオキサゾール、6−メトキシベンゾオキサゾール、5−メトキシベンゾオキサゾール、4−エトキシベンゾオキサゾール、5−クロロベンゾオキサゾール、6−メトキシベンゾオキサゾール、5−ヒドロキシベンゾオキサゾール、6−ヒドロキシベンゾオキサゾール等)、ナフトオキサゾール類(例えば、ナフト[1,2]オキサゾール、ナフト[2,1]オキサゾール等)、セレナゾール類(例えば、4−メチルセレナゾール、4−フェニルセレナゾール等)、ベンゾセレナゾール類(例えば、ベンゾセレナゾール、5−クロロベンゾセレナゾール、5−メトキシベンゾセレナゾール、5−ヒドロキシベンゾセレナゾール、テトラヒドロベンゾセレナゾール等)、ナフトセレナゾール類(例えば、ナフト[1,2]セレナゾール、ナフト[2,1]セレナゾール等)、チアゾリン類(例えば、チアゾリン、4−メチルチアゾリン等)、キノリン類(例えば、キノリン、3−メチルキノリン、5−メチルキノリン、7−メチルキノリン、8−メチルキノリン、6−クロロキノリン、8−クロロキノリン、6−メトキシキノリン、6−エトキシキノリン、6−ヒドロキシキノリン、8−ヒドロキシキノリン等)、イソキノリン類(例えば、イソキノリン、3,4−ジヒドロイソキノリン、等)、ベンズイミダゾール類(例えば、1,3−ジエチルベンズイミダゾール、1−エチル−3−フェニルベンズイミダゾール等)、3,3−ジアルキルインドレニン類(例えば、3,3−ジメチルインドレニン、3,3,5,−トリメチルインドレニン、3,3,7,−トリメチルインドレニン等)、ピリジン類(例えば、ピリジン、5−メチルピリジン等)等を挙げることができる。 Examples of nitrogen-containing heterocycles include L. G. Brooker et al. , J .; Am. Chem. Soc. 73, 5326-5358 (1951) and those known to constitute basic nuclei in the merocyanine dyes described in References can be suitably used. Specific examples include thiazoles (for example, thiazole, 4-methylthiazole, 4-phenylthiazole, 5-methylthiazole, 5-phenylthiazole, 4,5-dimethylthiazole, 4,5-diphenylthiazole, 4,5- Di (p-methoxyphenylthiazole), 4- (2-thienyl) thiazole, etc.), benzothiazoles (for example, benzothiazole, 4-chlorobenzothiazole, 5-chlorobenzothiazole, 6-chlorobenzothiazole, 7- Chlorobenzothiazole, 4-methylbenzothiazole, 5-methylbenzothiazole, 6-methylbenzothiazole, 5-bromobenzothiazole, 4-phenylbenzothiazole, 5-phenylbenzothiazole, 4-methoxybenzothiazole, 5-methoxybenzo Cheer , 6-methoxybenzothiazole, 5-iodobenzothiazole, 6-iodobenzothiazole, 4-ethoxybenzothiazole, 5-ethoxybenzothiazole, tetrahydrobenzothiazole, 5,6-dimethoxybenzothiazole, 5,6-di Oxymethylenebenzothiazole, 5-hydroxybenzothiazole, 6-hydroxybenzothiazole, 6-dimethylaminobenzothiazole, 5-ethoxycarbonylbenzothiazole, etc.), naphthothiazoles (for example, naphtho [1,2] thiazole, naphtho [2 , 1] thiazole, 5-methoxynaphtho [2,1] thiazole, 5-ethoxynaphtho [2,1] thiazole, 8-methoxynaphtho [1,2] thiazole, 7-methoxynaphtho [1,2] thiazole, etc.) , Chianafuteno 7 ′, 6 ′, 4,5-thiazole (for example, 4′-methoxythianaphtheno-7 ′, 6 ′, 4,5-thiazole, etc.), oxazole (for example, 4-methyloxazole, 5-methyloxazole) 4-phenyloxazole, 4,5-diphenyloxazole, 4-ethyloxazole, 4,5-dimethyloxazole, 5-phenyloxazole, etc.), benzoxazoles (benzoxazole, 5-chlorobenzoxazole, 5-methylbenzoxazole) 5-phenylbenzoxazole, 6-methylbenzoxazole, 5,6-dimethylbenzoxazole, 4,6-dimethylbenzoxazole, 6-methoxybenzoxazole, 5-methoxybenzoxazole, 4-ethoxybenzoxazole, 5-chloroben Zoxazole, 6-methoxybenzoxazole, 5-hydroxybenzoxazole, 6-hydroxybenzoxazole, etc.), naphthoxazoles (eg, naphtho [1,2] oxazole, naphtho [2,1] oxazole, etc.), selenazoles ( For example, 4-methylselenazole, 4-phenylselenazole, etc.), benzoselenazoles (for example, benzoselenazole, 5-chlorobenzoselenazole, 5-methoxybenzoselenazole, 5-hydroxybenzoselenazole, tetrahydrobenzo Selenazole etc.), naphthoselenazoles (eg naphtho [1,2] selenazole, naphtho [2,1] selenazole etc.), thiazolines (eg thiazoline, 4-methylthiazoline etc.), quinolines (eg quinoline) , 3-methyl Quinoline, 5-methylquinoline, 7-methylquinoline, 8-methylquinoline, 6-chloroquinoline, 8-chloroquinoline, 6-methoxyquinoline, 6-ethoxyquinoline, 6-hydroxyquinoline, 8-hydroxyquinoline, etc.), isoquinoline (Eg, isoquinoline, 3,4-dihydroisoquinoline, etc.), benzimidazoles (eg, 1,3-diethylbenzimidazole, 1-ethyl-3-phenylbenzimidazole, etc.), 3,3-dialkylindolenines (For example, 3,3-dimethylindolenine, 3,3,5, -trimethylindolenine, 3,3,7, -trimethylindolenine, etc.), pyridines (for example, pyridine, 5-methylpyridine, etc.) and the like. Can be mentioned.
また、含硫黄複素環の例としては、例えば、特開平3−296759号公報記載の色素類におけるジチオール部分構造をあげることができる。
具体例としては、ベンゾジチオール類(例えば、ベンゾジチオール、5−t−ブチルベンゾジチオール、5−メチルベンゾジチオール等)、ナフトジチオール類(例えば、ナフト[1,2]ジチオール、ナフト[2,1]ジチオール等)、ジチオール類(例えば、4,5−ジメチルジチオール類、4−フェニルジチオール類、4−メトキシカルボニルジチオール類、4,5−ジメトキシカルボニルベンゾジチオール類、4,5−ジトリフルオロメチルジチオール、4,5−ジシアノジチオール、4−メトキシカルボニルメチルジチオール、4−カルボキシメチルジチオール等を挙げることができる。
Examples of the sulfur-containing heterocycle include a dithiol partial structure in dyes described in JP-A-3-296759.
Specific examples include benzodithiols (for example, benzodithiol, 5-t-butylbenzodithiol, 5-methylbenzodithiol, etc.), naphthodithiols (for example, naphtho [1,2] dithiol, naphtho [2,1] Dithiols, etc.), dithiols (for example, 4,5-dimethyldithiols, 4-phenyldithiols, 4-methoxycarbonyldithiols, 4,5-dimethoxycarbonylbenzodithiols, 4,5-ditrifluoromethyldithiols, 4 , 5-dicyanodithiol, 4-methoxycarbonylmethyldithiol, 4-carboxymethyldithiol and the like.
以上、述べた複素環に関する説明に用いた記述は、便宜上、慣例上、複素環母骨格の名
称を用いたが、増感色素の塩基性骨格部分構造をなす場合は例えばベンゾチアゾール骨格の場合は3−置換−2(3H)−ベンゾチアゾリリデン基のように、不飽和度を一つ下げたアルキリデン型の置換基形で導入される。
As mentioned above, the description used for the description of the heterocyclic ring described above has conventionally used the name of the heterocyclic mother skeleton for the sake of convenience. It is introduced in the form of an alkylidene-type substituent with one degree of unsaturation, such as a 3-substituted-2 (3H) -benzothiazolidene group.
350nmから450nmの波長域に吸収極大を持つ増感色素のうち、高感度の観点からより好ましい色素は下記一般式(IX)で表される色素である。 Among the sensitizing dyes having an absorption maximum in the wavelength range of 350 nm to 450 nm, a dye more preferable from the viewpoint of high sensitivity is a dye represented by the following general formula (IX).
(一般式(IX)中、Aは置換基を有してもよい芳香族環基またはヘテロ環基を表し、Xは酸素原子、硫黄原子またはN−(R3)をあらわす。R1、R2およびR3は、それぞれ独立に、一価の非金属原子団を表し、AとR1およびR2とR3はそれぞれ互いに結合して
、脂肪族性または芳香族性の環を形成してもよい。)
(In the general formula (IX), A represents an aromatic ring group or a heterocyclic group which may have a substituent, and X represents an oxygen atom, a sulfur atom or N- (R 3 ). R 1 , R 2 and R 3 each independently represent a monovalent nonmetallic atomic group, and A and R 1 and R 2 and R 3 are bonded to each other to form an aliphatic or aromatic ring. May be.)
一般式(IX)について更に詳しく説明する。
R1、R2およびR3は、それぞれ独立に、一価の非金属原子団であり、好ましくは、置
換もしくは非置換のアルキル基、置換もしくは非置換のアルケニル基、置換もしくは非置換のアリール基、置換もしくは非置換の芳香族複素環残基、置換もしくは非置換のアルコキシ基、置換もしくは非置換のアルキルチオ基、ヒドロキシル基、ハロゲン原子を表す。
General formula (IX) will be described in more detail.
R 1 , R 2 and R 3 are each independently a monovalent nonmetallic atomic group, preferably a substituted or unsubstituted alkyl group, a substituted or unsubstituted alkenyl group, a substituted or unsubstituted aryl group. Represents a substituted or unsubstituted aromatic heterocyclic residue, a substituted or unsubstituted alkoxy group, a substituted or unsubstituted alkylthio group, a hydroxyl group, or a halogen atom.
R1、R2およびR3の好ましい例について具体的に述べる。好ましいアルキル基の例と
しては、炭素原子数が1から20までの直鎖状、分岐状、および環状のアルキル基を挙げることができ、その具体例としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、ヘプチル基、オクチル基、ノニル基、デシル基、ウンデシル基、ドデシル基、トリデシル基、ヘキサデシル基、オクタデシル基、エイコシル基、イソプロピル基、イソブチル基、s−ブチル基、t−ブチル基、イソペンチル基、ネオペンチル基、1−メチルブチル基、イソヘキシル基、2−エチルヘキシル基、2−メチルヘキシル基、シクロヘキシル基、シクロペンチル基、2−ノルボルニル基を挙げることができる。これらの中では、炭素原子数1から12までの直鎖状、炭素原子数3から12までの分岐状、ならびに炭素原子数5から10までの環状のアルキル基がより好ましい。
Preferable examples of R 1 , R 2 and R 3 will be specifically described. Examples of preferable alkyl groups include linear, branched, and cyclic alkyl groups having 1 to 20 carbon atoms. Specific examples thereof include a methyl group, an ethyl group, a propyl group, Butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, hexadecyl, octadecyl, eicosyl, isopropyl, isobutyl, s-butyl, Examples thereof include t-butyl group, isopentyl group, neopentyl group, 1-methylbutyl group, isohexyl group, 2-ethylhexyl group, 2-methylhexyl group, cyclohexyl group, cyclopentyl group and 2-norbornyl group. Of these, linear alkyl groups having 1 to 12 carbon atoms, branched alkyl groups having 3 to 12 carbon atoms, and cyclic alkyl groups having 5 to 10 carbon atoms are more preferable.
置換アルキル基の置換基としては、水素を除く一価の非金属原子団が用いられ、好ましい例としては、ハロゲン原子(−F、−Br、−Cl、−I)、ヒドロキシル基、アルコキシ基、アリーロキシ基、メルカプト基、アルキルチオ基、アリールチオ基、アルキルジチオ基、アリールジチオ基、アミノ基、N−アルキルアミノ基、N,N−ジアルキルアミノ基、N−アリールアミノ基、N,N−ジアリールアミノ基、N−アルキル−N−アリールアミノ基、アシルオキシ基、カルバモイルオキシ基、N−アルキルカルバモイルオキシ基、N−アリールカルバモイルオキシ基、N,N−ジアルキルカルバモイルオキシ基、N,N−ジアリールカルバモイルオキシ基、N−アルキル−N−アリールカルバモイルオキシ基、アルキルスルホキシ基、アリールスルホキシ基、アシルチオ基、アシルアミノ基、N−アルキルアシルアミノ基、N−アリールアシルアミノ基、ウレイド基、N′−アルキルウレイド基、N′,N′−ジアルキルウレイド基、N′−アリールウレイド基、N′,N′−ジアリールウレイド基、N′−アルキル−N′−アリールウレイド基、N−アルキルウレイド基、N−アリールウレイド基、N′−アルキル−N−アルキルウレイド基、N′−アルキル−N−アリールウレイド基、N′,N′−ジアルキル−N−アルキルウレイド基、N′,N′−ジアルキル−N−アリールウレイド基、N′−アリール−N−アルキルウレイド基、N′−アリール−N−アリールウレイド基、N′,N′−ジアリール−N−アルキルウレイド基、N′,N′−ジアリール−N−アリールウレイド基、N′−アルキル−N′−アリール−N−アルキルウレイド基、N′−アルキル−N′−アリール−N−アリールウレイド基、アルコキシカルボニルアミノ基、アリーロキシカルボニルアミノ基、N−アルキル−N−アルコキシカルボニルアミノ基、N−アルキル−N−アリーロキシカルボニルアミノ基、N−アリール−N−アルコキシカルボニルアミノ基、N−アリール−N−アリーロキシカルボニルアミノ基、アシル基、カルボキシル基、アルコキシカルボニル基、アリーロキシカルボニル基、カルバモイル基、N−アルキルカルバモイル基、N,N−ジアルキルカルバモイル基、N−アリールカルバモイル基、N,N−ジアリールカルバモイル基、N−アルキル−N−アリールカルバモイル基、アルキルスルフィニル基、アリールスルフィニル基、アルキルスルホニル基、アリールスルホニル基、スルホ基(−SO3H)およびその共役塩基基(以下、スルホナト基と称す)、アルコキシスルホニル基、アリーロキシスルホニル基、スルフィナモイル基、N−アルキルスルフィナモイル基、N,N−ジアルキルスルフィナモイル基、N−アリールスルフィナモイル基、N,N−ジアリールスルフィナモイル基、N−アルキル−N−アリールスルフィナモイル基、スルファモイル基、N−アルキルスルファモイル基、N,N−ジアルキルスルファモイル基、N−アリールスルファモイル基、N,N−ジアリールスルファモイル基、N−アルキル−N−アリールスルファモイル基、ホスフォノ基(−PO3H2)およびその共役塩基基(以下、ホスフォナト基と称す)、ジアルキルホスフォノ基(−PO3(alkyl)2)、ジアリールホスフォノ基(−PO3(aryl)2)、アルキルアリールホスフォノ基(−PO3(alkyl)(aryl))、モノアルキルホスフォノ基(−PO3H(alkyl))およびその共役塩基基(以後、アルキルホスフォナト基と称す)、モノアリールホスフォノ基(−PO3H(aryl))およびその共役塩基基(以後、アリールホスフォナト基と称す)、ホスフォノオキシ基(−OPO3H2)およびその共役塩基基(以後、ホスフォナトオキシ基と称す)、ジアルキルホスフォノオキシ基(−OPO3(alkyl)2)、ジアリールホスフォノオキシ基(−OPO3(aryl)2)、アルキルアリールホスフォノオキシ基(−OPO3(alkyl)(aryl))、モノアルキルホスフォノオキシ基(−OPO3H(alkyl))およびその共役塩基基(以後、アルキルホスフォナトオキシ基と称す)、モノアリールホスフォノオキシ基(−OPO3H(aryl))およびその共役塩基基(以後、アリールフォスホナトオキシ基と称す)、シアノ基、ニトロ基、アリール基、ヘテロアリール基、アルケニル基、アルキニル基が挙げられる。 As the substituent of the substituted alkyl group, a monovalent nonmetallic atomic group excluding hydrogen is used, and preferred examples include a halogen atom (—F, —Br, —Cl, —I), a hydroxyl group, an alkoxy group, Aryloxy group, mercapto group, alkylthio group, arylthio group, alkyldithio group, aryldithio group, amino group, N-alkylamino group, N, N-dialkylamino group, N-arylamino group, N, N-diarylamino group N-alkyl-N-arylamino group, acyloxy group, carbamoyloxy group, N-alkylcarbamoyloxy group, N-arylcarbamoyloxy group, N, N-dialkylcarbamoyloxy group, N, N-diarylcarbamoyloxy group, N-alkyl-N-arylcarbamoyloxy group, alkylsulfoxy group, Reelsulfoxy group, acylthio group, acylamino group, N-alkylacylamino group, N-arylacylamino group, ureido group, N'-alkylureido group, N ', N'-dialkylureido group, N'-arylureido Group, N ′, N′-diarylureido group, N′-alkyl-N′-arylureido group, N-alkylureido group, N-arylureido group, N′-alkyl-N-alkylureido group, N′- Alkyl-N-arylureido group, N ', N'-dialkyl-N-alkylureido group, N', N'-dialkyl-N-arylureido group, N'-aryl-N-alkylureido group, N'- Aryl-N-arylureido group, N ′, N′-diaryl-N-alkylureido group, N ′, N′-diaryl-N-ary Luureido group, N′-alkyl-N′-aryl-N-alkylureido group, N′-alkyl-N′-aryl-N-arylureido group, alkoxycarbonylamino group, aryloxycarbonylamino group, N-alkyl- N-alkoxycarbonylamino group, N-alkyl-N-aryloxycarbonylamino group, N-aryl-N-alkoxycarbonylamino group, N-aryl-N-aryloxycarbonylamino group, acyl group, carboxyl group, alkoxycarbonyl Group, aryloxycarbonyl group, carbamoyl group, N-alkylcarbamoyl group, N, N-dialkylcarbamoyl group, N-arylcarbamoyl group, N, N-diarylcarbamoyl group, N-alkyl-N-arylcarbamoyl group, alkylsulfinyl Group, Arylsulfinyl group, alkylsulfonyl group, arylsulfonyl group, sulfo group (—SO 3 H) and its conjugate base group (hereinafter referred to as sulfonate group), alkoxysulfonyl group, aryloxysulfonyl group, sulfinamoyl group, N-alkyls Rufinamoyl group, N, N-dialkylsulfinamoyl group, N-arylsulfinamoyl group, N, N-diarylsulfinamoyl group, N-alkyl-N-arylsulfinamoyl group, sulfamoyl group, N-alkyl Sulfamoyl group, N, N-dialkylsulfamoyl group, N-arylsulfamoyl group, N, N-diarylsulfamoyl group, N-alkyl-N-arylsulfamoyl group, phosphono group (-PO 3 H 2) and its conjugated base group (hereinafter referred to as phosphonato group , Dialkyl phosphono group (-PO 3 (alkyl) 2) , diaryl phosphono group (-PO 3 (aryl) 2) , alkyl aryl phosphono group (-PO 3 (alkyl) (aryl )), monoalkyl phosphono Group (—PO 3 H (alkyl)) and its conjugate base group (hereinafter referred to as alkylphosphonate group), monoarylphosphono group (—PO 3 H (aryl)) and its conjugate base group (hereinafter referred to as arylphosphine group). A phosphonooxy group (—OPO 3 H 2 ) and its conjugate base group (hereinafter referred to as a phosphonatooxy group), a dialkylphosphonooxy group (—OPO 3 (alkyl) 2 ), a diarylphosphine Fonookishi group (-OPO 3 (aryl) 2) , alkylaryl phosphonooxy group (-OPO 3 (alkyl (Aryl)), monoalkyl phosphonooxy group (-OPO 3 H (alkyl)) and its conjugated base group (hereinafter referred to as alkyl phosphonophenyl group), monoaryl phosphonooxy group (-OPO 3 H (aryl )) And conjugated base groups thereof (hereinafter referred to as arylphosphonatooxy groups), cyano groups, nitro groups, aryl groups, heteroaryl groups, alkenyl groups, and alkynyl groups.
これらの置換基における、アルキル基の具体例としては、前述のアルキル基が挙げられ、アリール基の具体例としては、フェニル基、ビフェニル基、ナフチル基、トリル基、キシリル基、メシチル基、クメニル基、クロロフェニル基、ブロモフェニル基、クロロメチルフェニル基、ヒドロキシフェニル基、メトキシフェニル基、エトキシフェニル基、フェノキシフェニル基、アセトキシフェニル基、ベンゾイロキシフェニル基、メチルチオフェニル基、フェニルチオフェニル基、メチルアミノフェニル基、ジメチルアミノフェニル基、アセチルアミノフェニル基、カルボキシフェニル基、メトキシカルボニルフェニル基、エトキシフェニルカルボニル基、フェノキシカルボニルフェニル基、N−フェニルカルバモイルフェニル基、フェニル基、シアノフェニル基、スルホフェニル基、スルホナトフェニル基、ホスフォノフェニル基、ホスフォナトフェニル基等を挙げることができる。 Specific examples of the alkyl group in these substituents include the above-described alkyl groups, and specific examples of the aryl group include a phenyl group, a biphenyl group, a naphthyl group, a tolyl group, a xylyl group, a mesityl group, and a cumenyl group. , Chlorophenyl group, bromophenyl group, chloromethylphenyl group, hydroxyphenyl group, methoxyphenyl group, ethoxyphenyl group, phenoxyphenyl group, acetoxyphenyl group, benzoyloxyphenyl group, methylthiophenyl group, phenylthiophenyl group, methylamino Phenyl group, dimethylaminophenyl group, acetylaminophenyl group, carboxyphenyl group, methoxycarbonylphenyl group, ethoxyphenylcarbonyl group, phenoxycarbonylphenyl group, N-phenylcarbamoylphenyl group, phenyl group Cyanophenyl group, sulfophenyl group, sulfonatophenyl group, phosphonophenyl phenyl group, phosphonophenyl phenyl group and the like.
R1、R2およびR3として好ましいヘテロアリール基としては、窒素、酸素、硫黄原子
の少なくとも一つを含有する単環、もしくは多環芳香族環が用いられ、特に好ましいヘテロアリール基の例としては、例えば、チオフェン、チアスレン、フラン、ピラン、イソベンゾフラン、クロメン、キサンテン、フェノキサジン、ピロール、ピラゾール、イソチアゾール、イソオキサゾール、ピラジン、ピリミジン、ピリダジン、インドリジン、イソインドリジン、インドイール、インダゾール、プリン、キノリジン、イソキノリン、フタラ
ジン、ナフチリジン、キナゾリン、シノリン、プテリジン、カルバゾール、カルボリン、フェナンスリン、アクリジン、ペリミジン、フェナンスロリン、フタラジン、フェナルザジン、フェノキサジン、フラザン、フェノキサジンや等があげられ、これらは、さらにベンゾ縮環してもよく、また置換基を有していてもよい。
As the preferred heteroaryl group as R 1 , R 2 and R 3 , a monocyclic or polycyclic aromatic ring containing at least one of nitrogen, oxygen and sulfur atoms is used. Examples of particularly preferred heteroaryl groups Is, for example, thiophene, thiathrene, furan, pyran, isobenzofuran, chromene, xanthene, phenoxazine, pyrrole, pyrazole, isothiazole, isoxazole, pyrazine, pyrimidine, pyridazine, indolizine, isoindolizine, indolizine, indazole, indazole, Purine, quinolidine, isoquinoline, phthalazine, naphthyridine, quinazoline, sinoline, pteridine, carbazole, carboline, phenanthrine, acridine, perimidine, phenanthrolin, phthalazine, phenalazine, phenoxazine, flaza And phenoxazine and the like. These may be further benzo-fused and may have a substituent.
また、R1、R2およびR3として好ましいアルケニル基の例としては、ビニル基、1−
プロペニル基、1−ブテニル基、シンナミル基、2−クロロ−1−エテニル基、等が挙げられ、アルキニル基の例としては、エチニル基、1−プロピニル基、1−ブチニル基、トリメチルシリルエチニル基等が挙げられる。アシル基(G1CO−)におけるG1としては、水素、ならびに上記のアルキル基、アリール基を挙げることができる。これら置換基の内、更により好ましいものとしてはハロゲン原子(−F、−Br、−Cl、−I)、アルコキシ基、アリーロキシ基、アルキルチオ基、アリールチオ基、N−アルキルアミノ基、N,N−ジアルキルアミノ基、アシルオキシ基、N−アルキルカルバモイルオキシ基、N−アリールカルバモイルオキシ基、アシルアミノ基、アシル基、カルボキシル基、アルコキシカルボニル基、アリーロキシカルボニル基、カルバモイル基、N−アルキルカルバモイル基、N,N−ジアルキルカルバモイル基、N−アリールカルバモイル基、N−アルキル−N−アリールカルバモイル基、スルホ基、スルホナト基、スルファモイル基、N−アルキルスルファモイル基、N,N−ジアルキルスルファモイル基、N−アリールスルファモイル基、N−アルキル−N−アリールスルファモイル基、ホスフォノ基、ホスフォナト基、ジアルキルホスフォノ基、ジアリールホスフォノ基、モノアルキルホスフォノ基、アルキルホスフォナト基、モノアリールホスフォノ基、アリールホスフォナト基、ホスフォノオキシ基、ホスフォナトオキシ基、アリール基、アルケニル基が挙げられる。
Examples of preferred alkenyl groups for R 1 , R 2 and R 3 include vinyl groups, 1-
A propenyl group, a 1-butenyl group, a cinnamyl group, a 2-chloro-1-ethenyl group, and the like. Examples of the alkynyl group include an ethynyl group, a 1-propynyl group, a 1-butynyl group, and a trimethylsilylethynyl group. Can be mentioned. Examples of G 1 in the acyl group (G 1 CO—) include hydrogen and the above alkyl groups and aryl groups. Among these substituents, even more preferred are halogen atoms (—F, —Br, —Cl, —I), alkoxy groups, aryloxy groups, alkylthio groups, arylthio groups, N-alkylamino groups, N, N— Dialkylamino group, acyloxy group, N-alkylcarbamoyloxy group, N-arylcarbamoyloxy group, acylamino group, acyl group, carboxyl group, alkoxycarbonyl group, aryloxycarbonyl group, carbamoyl group, N-alkylcarbamoyl group, N, N-dialkylcarbamoyl group, N-arylcarbamoyl group, N-alkyl-N-arylcarbamoyl group, sulfo group, sulfonate group, sulfamoyl group, N-alkylsulfamoyl group, N, N-dialkylsulfamoyl group, N An arylsulfamoyl group, N Alkyl-N-arylsulfamoyl group, phosphono group, phosphonate group, dialkyl phosphono group, diaryl phosphono group, monoalkyl phosphono group, alkyl phosphonate group, monoaryl phosphono group, aryl phosphonate group, phosphono Examples thereof include an oxy group, a phosphonatooxy group, an aryl group, and an alkenyl group.
一方、置換アルキル基におけるアルキレン基としては前述の炭素数1から20までのアルキル基上の水素原子のいずれか1つを除し、2価の有機残基としたものを挙げることができ、好ましくは炭素原子数1から12までの直鎖状、炭素原子数3から12までの分岐状ならびに炭素原子数5から10までの環状のアルキレン基を挙げることができる。 On the other hand, examples of the alkylene group in the substituted alkyl group include divalent organic residues obtained by removing any one of the hydrogen atoms on the alkyl group having 1 to 20 carbon atoms. Can include linear alkylene groups having 1 to 12 carbon atoms, branched chains having 3 to 12 carbon atoms, and cyclic alkylene groups having 5 to 10 carbon atoms.
該置換基とアルキレン基を組み合わせることにより得られるR1、R2およびR3として
好ましい置換アルキル基の、具体例としては、クロロメチル基、ブロモメチル基、2−クロロエチル基、トリフルオロメチル基、メトキシメチル基、メトキシエトキシエチル基、アリルオキシメチル基、フェノキシメチル基、メチルチオメチル基、トリルチオメチル基、エチルアミノエチル基、ジエチルアミノプロピル基、モルホリノプロピル基、アセチルオキシメチル基、ベンゾイルオキシメチル基、N−シクロヘキシルカルバモイルオキシエチル基、N−フェニルカルバモイルオキシエチル基、アセチルアミノエチル基、N−メチルベンゾイルアミノプロピル基、2−オキソエチル基、2−オキソプロピル基、カルボキシプロピル基、メトキシカルボニルエチル基、アリルオキシカルボニルブチル基、クロロフェノキシカルボニルメチル基、カルバモイルメチル基、N−メチルカルバモイルエチル基、N,N−ジプロピルカルバモイルメチル基、N−(メトキシフェニル)カルバモイルエチル基、N−メチル−N−(スルホフェニル)カルバモイルメチル基、スルホブチル基、スルホナトブチル基、スルファモイルブチル基、N−エチルスルファモイルメチル基、N,N−ジプロピルスルファモイルプロピル基、N−トリルスルファモイルプロピル基、N−メチル−N−(ホスフォノフェニル)スルファモイルオクチル基、ホスフォノブチル基、ホスフォナトヘキシル基、ジエチルホスフォノブチル基、ジフェニルホスフォノプロピル基、メチルホスフォノブチル基、メチルホスフォナトブチル基、トリルホスフォノヘキシル基、トリルホスフォナトヘキシル基、ホスフォノオキシプロピル基、ホスフォナトオキシブチル基、ベンジル基、フェネチル基、α−メチルベンジル基、1−メチル−1−フェニルエチル基、p−メチルベンジル基、シンナミル基、アリル基、1−プロペニルメチル基、2−ブテニル基、2−メチルアリル基、2−メチルプロペニルメチル基、2−プロピニル基、2−ブチニル基、3−ブチニル基、等を挙げることができる。
Specific examples of preferable substituted alkyl groups as R 1 , R 2 and R 3 obtained by combining the substituent and the alkylene group include chloromethyl group, bromomethyl group, 2-chloroethyl group, trifluoromethyl group, methoxy Methyl group, methoxyethoxyethyl group, allyloxymethyl group, phenoxymethyl group, methylthiomethyl group, tolylthiomethyl group, ethylaminoethyl group, diethylaminopropyl group, morpholinopropyl group, acetyloxymethyl group, benzoyloxymethyl group, N -Cyclohexylcarbamoyloxyethyl group, N-phenylcarbamoyloxyethyl group, acetylaminoethyl group, N-methylbenzoylaminopropyl group, 2-oxoethyl group, 2-oxopropyl group, carboxypropyl group, methoxycarbo Nylethyl group, allyloxycarbonylbutyl group, chlorophenoxycarbonylmethyl group, carbamoylmethyl group, N-methylcarbamoylethyl group, N, N-dipropylcarbamoylmethyl group, N- (methoxyphenyl) carbamoylethyl group, N-methyl- N- (sulfophenyl) carbamoylmethyl group, sulfobutyl group, sulfonatobutyl group, sulfamoylbutyl group, N-ethylsulfamoylmethyl group, N, N-dipropylsulfamoylpropyl group, N-tolylsulfamoylpropyl group N-methyl-N- (phosphonophenyl) sulfamoyloctyl group, phosphonobutyl group, phosphonatohexyl group, diethylphosphonobutyl group, diphenylphosphonopropyl group, methylphosphonobutyl group, methylphosphonatobu Group, tolylphosphonohexyl group, tolylphosphonatohexyl group, phosphonooxypropyl group, phosphonateoxybutyl group, benzyl group, phenethyl group, α-methylbenzyl group, 1-methyl-1-phenylethyl group, p -Methylbenzyl group, cinnamyl group, allyl group, 1-propenylmethyl group, 2-butenyl group, 2-methylallyl group, 2-methylpropenylmethyl group, 2-propynyl group, 2-butynyl group, 3-butynyl group, etc. Can be mentioned.
R1、R2およびR3として好ましいアリール基の具体例としては、1個から3個のベン
ゼン環が縮合環を形成したもの、ベンゼン環と5員不飽和環が縮合環を形成したものを挙げることができ、具体例としては、フェニル基、ナフチル基、アントリル基、フェナントリル基、インデニル基、アセナフテニル基、フルオレニル基、を挙げることができ、これらのなかでは、フェニル基、ナフチル基がより好ましい。
Specific examples of preferred aryl groups as R 1 , R 2 and R 3 include those in which 1 to 3 benzene rings form a condensed ring, and those in which a benzene ring and a 5-membered unsaturated ring form a condensed ring. Specific examples include a phenyl group, a naphthyl group, an anthryl group, a phenanthryl group, an indenyl group, an acenaphthenyl group, and a fluorenyl group. Among these, a phenyl group and a naphthyl group are more preferable. .
R1、R2およびR3として好ましい置換アリール基の具体例としては、前述のアリール
基の環形成炭素原子上に置換基として、水素を除く一価の非金属原子団を有するものが用いられる。好ましい置換基の例としては前述のアルキル基、置換アルキル基、ならびに、先に置換アルキル基における置換基として示したものを挙げることができる。この様な、置換アリール基の好ましい具体例としては、ビフェニル基、トリル基、キシリル基、メシチル基、クメニル基、クロロフェニル基、ブロモフェニル基、フルオロフェニル基、クロロメチルフェニル基、トリフルオロメチルフェニル基、ヒドロキシフェニル基、メトキシフェニル基、メトキシエトキシフェニル基、アリルオキシフェニル基、フェノキシフェニル基、メチルチオフェニル基、トリルチオフェニル基、エチルアミノフェニル基、ジエチルアミノフェニル基、モルホリノフェニル基、アセチルオキシフェニル基、ベンゾイルオキシフェニル基、N−シクロヘキシルカルバモイルオキシフェニル基、N−フェニルカルバモイルオキシフェニル基、アセチルアミノフェニル基、N−メチルベンゾイルアミノフェニル基、カルボキシフェニル基、メトキシカルボニルフェニル基、アリルオキシカルボニルフェニル基、クロロフェノキシカルボニルフェニル基、カルバモイルフェニル基、N−メチルカルバモイルフェニル基、N,N−ジプロピルカルバモイルフェニル基、N−(メトキシフェニル)カルバモイルフェニル基、N−メチル−N−(スルホフェニル)カルバモイルフェニル基、スルホフェニル基、スルホナトフェニル基、スルファモイルフェニル基、N−エチルスルファモイルフェニル基、N,N−ジプロピルスルファモイルフェニル基、N−トリルスルファモイルフェニル基、N−メチル−N−(ホスフォノフェニル)スルファモイルフェニル基、ホスフォノフェニル基、ホスフォナトフェニル基、ジエチルホスフォノフェニル基、ジフェニルホスフォノフェニル基、メチルホスフォノフェニル基、メチルホスフォナトフェニル基、トリルホスフォノフェニル基、トリルホスフォナトフェニル基、アリルフェニル基、1−プロペニルメチルフェニル基、2−ブテニルフェニル基、2−メチルアリルフェニル基、2−メチルプロペニルフェニル基、2−プロピニルフェニル基、2−ブチニルフェニル基、3−ブチニルフェニル基、等を挙げることができる。
Specific examples of preferred substituted aryl groups as R 1 , R 2 and R 3 include those having a monovalent non-metallic atomic group excluding hydrogen as a substituent on the ring-forming carbon atom of the aryl group described above. . Examples of preferred substituents include the alkyl groups, substituted alkyl groups, and those previously shown as substituents in the substituted alkyl group. Preferred examples of such a substituted aryl group include biphenyl group, tolyl group, xylyl group, mesityl group, cumenyl group, chlorophenyl group, bromophenyl group, fluorophenyl group, chloromethylphenyl group, trifluoromethylphenyl group. Hydroxyphenyl group, methoxyphenyl group, methoxyethoxyphenyl group, allyloxyphenyl group, phenoxyphenyl group, methylthiophenyl group, tolylthiophenyl group, ethylaminophenyl group, diethylaminophenyl group, morpholinophenyl group, acetyloxyphenyl group, Benzoyloxyphenyl group, N-cyclohexylcarbamoyloxyphenyl group, N-phenylcarbamoyloxyphenyl group, acetylaminophenyl group, N-methylbenzoylaminophenyl group, carbo Cyphenyl group, methoxycarbonylphenyl group, allyloxycarbonylphenyl group, chlorophenoxycarbonylphenyl group, carbamoylphenyl group, N-methylcarbamoylphenyl group, N, N-dipropylcarbamoylphenyl group, N- (methoxyphenyl) carbamoylphenyl group N-methyl-N- (sulfophenyl) carbamoylphenyl group, sulfophenyl group, sulfonatophenyl group, sulfamoylphenyl group, N-ethylsulfamoylphenyl group, N, N-dipropylsulfamoylphenyl group, N-tolylsulfamoylphenyl group, N-methyl-N- (phosphonophenyl) sulfamoylphenyl group, phosphonophenyl group, phosphonatophenyl group, diethylphosphonophenyl group, diphenylphosphono Enyl group, methylphosphonophenyl group, methylphosphonatophenyl group, tolylphosphonophenyl group, tolylphosphonatephenyl group, allylphenyl group, 1-propenylmethylphenyl group, 2-butenylphenyl group, 2-methylallylphenyl group Group, 2-methylpropenylphenyl group, 2-propynylphenyl group, 2-butynylphenyl group, 3-butynylphenyl group, and the like.
次に、一般式(IX)におけるAについて説明する。Aは置換基を有してもよい芳香族環基またはヘテロ環基を表し、置換基を有してもよい芳香族環またはヘテロ環の具体例としては、一般式(IX)中のR1、R2およびR3で記載したものと同様のものが挙げられ
る。
Next, A in the general formula (IX) will be described. A represents an aromatic ring group or a heterocyclic group which may have a substituent. Specific examples of the aromatic ring or heterocyclic ring which may have a substituent include R 1 in the general formula (IX). , R 2 and R 3 are the same.
本発明の一般式(IX)で表される増感色素は、上に示したような酸性核や、活性メチレン基を有する酸性核と、置換、もしくは非置換の、芳香族環またはヘテロ環との縮合反応によって得られるが、これらは特公昭59−28329号公報を参照して合成することができる。 The sensitizing dye represented by the general formula (IX) of the present invention includes an acidic nucleus as shown above, an acidic nucleus having an active methylene group, a substituted or unsubstituted aromatic ring or heterocyclic ring, These can be synthesized by referring to Japanese Patent Publication No. 59-28329.
以下に一般式(IX)で表される化合物の好ましい具体例(D1)から(D75)を示す。また、酸性核と塩基性核を結ぶ2重結合による異性体については、どちらかの異性体に限定されるものではない。 Preferred specific examples (D1) to (D75) of the compound represented by the general formula (IX) are shown below. In addition, an isomer with a double bond connecting an acidic nucleus and a basic nucleus is not limited to either isomer.
これらの増感色素のどの構造を用いるか、単独で使用するか2種以上併用するか、添加量はどうか、といった使用法の詳細は、平版印刷版原版の性能設計にあわせて適宜設定できる。
例えば、増感色素を2種以上併用することで、感光層への相溶性を高めることができる。増感色素の選択は、感光性の他、使用する光源の発光波長でのモル吸光係数が重要な因
子である。モル吸光係数の大きな色素を使用する事により、色素の添加量は比較的少なくできるので、経済的であり、かつ平版印刷版原版に用いた場合、その感光層の膜物性の点からも有利である。該感光層の感光性、解像度や、露光膜の物性は光源波長での吸光度に大きな影響を受けるので、これらを考慮して増感色素の添加量を適宜選択する。
Details of the usage such as which structure of these sensitizing dyes are used, whether they are used alone or in combination of two or more, and the addition amount can be appropriately set according to the performance design of the lithographic printing plate precursor.
For example, the compatibility with the photosensitive layer can be increased by using two or more sensitizing dyes in combination. In selecting the sensitizing dye, in addition to the photosensitivity, the molar extinction coefficient at the emission wavelength of the light source used is an important factor. By using a dye having a large molar extinction coefficient, the amount of the dye added can be made relatively small, which is economical and advantageous when used for a lithographic printing plate precursor in terms of film physical properties of the photosensitive layer. is there. The photosensitivity of the photosensitive layer, the resolution, and the physical properties of the exposed film are greatly affected by the absorbance at the light source wavelength. Therefore, the addition amount of the sensitizing dye is appropriately selected in consideration of these factors.
但し、例えば5μm以上の厚い膜を硬化せしめる目的に対しては、低い吸光度の方がかえって硬化度をあげられる場合もある。比較的薄い膜厚で使用する平版印刷版原版としての使用に際しては、増感色素の添加量は、本発明の感光層の吸光度が0.1から1.5の範囲、好ましくは0.25から1の範囲となるように設定するのが好ましい。通常、感光層の全固形分100質量部に対し、好ましくは0.05〜30質量部、更に好ましくは0.1〜20質量部、最も好ましくは0.2〜10質量部の範囲である。 However, for example, for the purpose of curing a thick film having a thickness of 5 μm or more, the degree of curing may be increased by lower absorbance. When used as a lithographic printing plate precursor used in a relatively thin film thickness, the addition amount of the sensitizing dye is such that the absorbance of the photosensitive layer of the present invention is in the range of 0.1 to 1.5, preferably from 0.25. It is preferable to set so as to be in the range of 1. Usually, the amount is preferably 0.05 to 30 parts by mass, more preferably 0.1 to 20 parts by mass, and most preferably 0.2 to 10 parts by mass with respect to 100 parts by mass of the total solid content of the photosensitive layer.
<マイクロカプセル>
本発明においては、上記の感光層構成成分および後述のその他の構成成分を感光層に含有させる方法として、例えば、特開2001−277740号公報、特開2001−277742号公報に記載のごとく、該構成成分の一部をマイクロカプセルに内包させて感光層に添加することができる。その場合、各構成成分はマイクロカプセル内および外に、任意の比率で含有させることが可能である。
<Microcapsule>
In the present invention, as a method for causing the photosensitive layer to contain the above-described photosensitive layer constituents and other constituents described later, for example, as described in JP-A Nos. 2001-277740 and 2001-277742, A part of the components can be encapsulated in microcapsules and added to the photosensitive layer. In that case, each component can be contained in any ratio in and out of the microcapsule.
感光層構成成分をマイクロカプセル化する方法としては、公知の方法が適用できる。例えばマイクロカプセルの製造方法としては、米国特許第2800457号、同第2800458号明細書にみられるコアセルベーションを利用した方法、米国特許第3287154号の各明細書、特公昭38−19574号、同42−446号の各公報にみられる界面重合法による方法、米国特許第3418250号、同第3660304号明細書にみられるポリマーの析出による方法、米国特許第3796669号明細書に見られるイソシアナートポリオール壁材料を用いる方法、米国特許第3914511号明細書に見られるイソシアナート壁材料を用いる方法、米国特許第4001140号、同第4087376号、同第4089802号の各明細書にみられる尿素―ホルムアルデヒド系または尿素ホルムアルデヒド−レゾルシノール系壁形成材料を用いる方法、米国特許第4025445号明細書にみられるメラミン−ホルムアルデヒド樹脂、ヒドロキシセルロース等の壁材を用いる方法、特公昭36−9163号、同51−9079号の各公報にみられるモノマー重合によるin situ法、英国特許第930422号、米国特許第3111407号明細書にみられるスプレードライング法、英国特許第952807号、同第967074号の各明細書にみられる電解分散冷却法などがあるが、これらに限定されるものではない。 As a method for microencapsulating the photosensitive layer constituent components, known methods can be applied. For example, as a method for producing microcapsules, a method using coacervation found in U.S. Pat. Nos. 2,800,547 and 2,800,498, U.S. Pat. No. 3,287,154, JP-B-38-19574, 42-446 by the interfacial polymerization method, US Pat. No. 3,418,250, US Pat. No. 3,660,304 by polymer precipitation method, US Pat. No. 3,796,669, isocyanate polyol A method using a wall material, a method using an isocyanate wall material found in US Pat. No. 3,914,511, and a urea-formaldehyde system found in US Pat. Nos. 4,001,140, 4,087,376 and 4,089,802. Or urea formaldehyde-resorcino A method using a wall forming material, a method using a wall material such as melamine-formaldehyde resin and hydroxycellulose, as shown in US Pat. No. 4,025,445, and Japanese Patent Publication Nos. 36-9163 and 51-9079. In situ method using monomer polymerization, spray drying method found in British Patent No. 930422, US Pat. No. 3,111,407, electrolytic dispersion cooling method seen in British Patent Nos. 952807 and 967074, etc. However, it is not limited to these.
本発明に用いられる好ましいマイクロカプセル壁は、3次元架橋を有し、溶剤によって膨潤する性質を有するものである。このような観点から、マイクロカプセルの壁材は、ポリウレア、ポリウレタン、ポリエステル、ポリカーボネート、ポリアミド、およびこれらの混合物が好ましく、特に、ポリウレアおよびポリウレタンが好ましい。また、マイクロカプセル壁に、上記の非水溶性高分子に導入可能なエチレン性不飽和結合等の架橋性官能基を有する化合物を導入してもよい。 A preferable microcapsule wall used in the present invention has a three-dimensional cross-linking and has a property of swelling with a solvent. From such a viewpoint, the wall material of the microcapsule is preferably polyurea, polyurethane, polyester, polycarbonate, polyamide, and a mixture thereof, and particularly preferably polyurea and polyurethane. Moreover, you may introduce | transduce into the microcapsule wall the compound which has crosslinkable functional groups, such as an ethylenically unsaturated bond which can be introduce | transduced into said water-insoluble polymer.
上記のマイクロカプセルの平均粒径は、0.01〜3.0μmが好ましい。0.05〜2.0μmがさらに好ましく、0.10〜1.0μmが特に好ましい。この範囲内で良好な解像度と経時安定性が得られる。 The average particle size of the microcapsules is preferably 0.01 to 3.0 μm. 0.05-2.0 micrometers is further more preferable, and 0.10-1.0 micrometer is especially preferable. Within this range, good resolution and stability over time can be obtained.
<その他の感光層成分>
本発明の感光層には、さらに、必要に応じて種々の添加剤を含有させることができる。以下、それらについて説明する。
<Other photosensitive layer components>
The photosensitive layer of the present invention can further contain various additives as required. These will be described below.
<界面活性剤>
本発明において、感光層には、現像性の促進および塗布面状を向上させるために界面活性剤を用いるのが好ましい。界面活性剤としては、ノニオン界面活性剤、アニオン界面活性剤、カチオン界面活性剤、両性界面活性剤、フッ素系界面活性剤等が挙げられる。界面活性剤は、単独で用いてもよく、2種以上を組み合わせて用いてもよい。
<Surfactant>
In the present invention, it is preferable to use a surfactant in the photosensitive layer in order to promote developability and improve the coated surface state. Examples of the surfactant include nonionic surfactants, anionic surfactants, cationic surfactants, amphoteric surfactants, and fluorosurfactants. Surfactant may be used independently and may be used in combination of 2 or more type.
本発明の感光層に用いられるノニオン界面活性剤は、特に限定されず、従来公知のものを用いることができる。例えば、ポリオキシエチレンアルキルエーテル類、ポリオキシエチレンアルキルフェニルエーテル類、ポリオキシエチレンポリスチリルフェニルエーテル類、ポリオキシエチレンポリオキシプロピレンアルキルエーテル類、グリセリン脂肪酸部分エステル類、ソルビタン脂肪酸部分エステル類、ペンタエリスリトール脂肪酸部分エステル類、プロピレングリコールモノ脂肪酸エステル類、ショ糖脂肪酸部分エステル類、ポリオキシエチレンソルビタン脂肪酸部分エステル類、ポリオキシエチレンソルビトール脂肪酸部分エステル類、ポリエチレングリコール脂肪酸エステル類、ポリグリセリン脂肪酸部分エステル類、ポリオキシエチレン化ひまし油類、ポリオキシエチレングリセリン脂肪酸部分エステル類、脂肪酸ジエタノールアミド類、N,N−ビス−2−ヒドロキシアルキルアミン類、ポリオキシエチレンアルキルアミン、トリエタノールアミン脂肪酸エステル、トリアルキルアミンオキシド、ポリエチレングリコール、ポリエチレングリコールとポリプロピレングリコールの共重合体が挙げられる。 The nonionic surfactant used in the photosensitive layer of the invention is not particularly limited, and conventionally known nonionic surfactants can be used. For example, polyoxyethylene alkyl ethers, polyoxyethylene alkyl phenyl ethers, polyoxyethylene polystyryl phenyl ethers, polyoxyethylene polyoxypropylene alkyl ethers, glycerin fatty acid partial esters, sorbitan fatty acid partial esters, pentaerythritol Fatty acid partial esters, propylene glycol monofatty acid esters, sucrose fatty acid partial esters, polyoxyethylene sorbitan fatty acid partial esters, polyoxyethylene sorbitol fatty acid partial esters, polyethylene glycol fatty acid esters, polyglycerin fatty acid partial esters, Polyoxyethylenated castor oil, polyoxyethylene glycerin fatty acid partial esters, fatty acid diethanolamides, N N- bis-2-hydroxyalkylamines, polyoxyethylene alkylamines, triethanolamine fatty acid ester, trialkylamine oxide, polyethylene glycol, copolymers of polyethylene glycol and polypropylene glycol.
本発明の感光層に用いられるアニオン界面活性剤は、特に限定されず、従来公知のものを用いることができる。例えば、脂肪酸塩類、アビエチン酸塩類、ヒドロキシアルカンスルホン酸塩類、アルカンスルホン酸塩類、ジアルキルスルホ琥珀酸エステル塩類、直鎖アルキルベンゼンスルホン酸塩類、分岐鎖アルキルベンゼンスルホン酸塩類、アルキルナフタレンスルホン酸塩類、アルキルフェノキシポリオキシエチレンプロピルスルホン酸塩類、ポリオキシエチレンアルキルスルホフェニルエーテル塩類、N−メチル−N−オレイルタウリンナトリウム塩、N−アルキルスルホコハク酸モノアミド二ナトリウム塩、石油スルホン酸塩類、硫酸化牛脂油、脂肪酸アルキルエステルの硫酸エステル塩類、アルキル硫酸エステル塩類、ポリオキシエチレンアルキルエーテル硫酸エステル塩類、脂肪酸モノグリセリド硫酸エステル塩類、ポリオキシエチレンアルキルフェニルエーテル硫酸エステル塩類、ポリオキシエチレンスチリルフェニルエーテル硫酸エステル塩類、アルキルリン酸エステル塩類、ポリオキシエチレンアルキルエーテルリン酸エステル塩類、ポリオキシエチレンアルキルフェニルエーテルリン酸エステル塩類、スチレン/無水マレイン酸共重合物の部分けん化物類、オレフィン/無水マレイン酸共重合物の部分けん化物類、ナフタレンスルホン酸塩ホルマリン縮合物類が挙げられる。 The anionic surfactant used in the photosensitive layer of the invention is not particularly limited, and conventionally known anionic surfactants can be used. For example, fatty acid salts, abietic acid salts, hydroxyalkane sulfonates, alkane sulfonates, dialkyl sulfosuccinate esters, linear alkyl benzene sulfonates, branched alkyl benzene sulfonates, alkyl naphthalene sulfonates, alkyl phenoxy poly Oxyethylene propyl sulfonates, polyoxyethylene alkyl sulfophenyl ether salts, N-methyl-N-oleyl taurine sodium salt, N-alkyl sulfosuccinic acid monoamide disodium salt, petroleum sulfonates, sulfated beef oil, fatty acid alkyl esters Sulfates, alkyl sulfates, polyoxyethylene alkyl ether sulfates, fatty acid monoglyceride sulfates, polyoxyethylene alcohol Ruphenyl ether sulfates, polyoxyethylene styryl phenyl ether sulfates, alkyl phosphates, polyoxyethylene alkyl ether phosphates, polyoxyethylene alkyl phenyl ether phosphates, styrene / maleic anhydride Examples thereof include partial saponification products of polymers, partial saponification products of olefin / maleic anhydride copolymers, and naphthalene sulfonate formalin condensates.
本発明の感光層に用いられるカチオン界面活性剤は、特に限定されず、従来公知のものを用いることができる。例えば、アルキルアミン塩類、第四級アンモニウム塩類、ポリオキシエチレンアルキルアミン塩類、ポリエチレンポリアミン誘導体が挙げられる。
本発明の感光層に用いられる両性界面活性剤は、特に限定されず、従来公知のものを用いることができる。例えば、カルボキシベタイン類、アミノカルボン酸類、スルホベタイン類、アミノ硫酸エステル類、イミタゾリン類が挙げられる。
The cationic surfactant used in the photosensitive layer of the present invention is not particularly limited, and conventionally known cationic surfactants can be used. Examples thereof include alkylamine salts, quaternary ammonium salts, polyoxyethylene alkylamine salts, and polyethylene polyamine derivatives.
The amphoteric surfactant used in the photosensitive layer of the present invention is not particularly limited, and conventionally known ones can be used. Examples thereof include carboxybetaines, aminocarboxylic acids, sulfobetaines, aminosulfuric esters, and imidazolines.
なお、上記界面活性剤の中で、「ポリオキシエチレン」とあるものは、ポリオキシメチレン、ポリオキシプロピレン、ポリオキシブチレン等の「ポリオキシアルキレン」に読み替えることもでき、本発明においては、それらの界面活性剤も用いることができる。 Of the above surfactants, the term “polyoxyethylene” can be read as “polyoxyalkylene” such as polyoxymethylene, polyoxypropylene, polyoxybutylene, etc. These surfactants can also be used.
更に好ましい界面活性剤としては、分子内にパーフルオロアルキル基を含有するフッ素系界面活性剤が挙げられる。このようなフッ素系界面活性剤としては、例えば、パーフルオロアルキルカルボン酸塩、パーフルオロアルキルスルホン酸塩、パーフルオロアルキル
リン酸エステル等のアニオン型;パーフルオロアルキルベタイン等の両性型;パーフルオロアルキルトリメチルアンモニウム塩等のカチオン型;パーフルオロアルキルアミンオキサイド、パーフルオロアルキルエチレンオキシド付加物、パーフルオロアルキル基および親水性基を含有するオリゴマー、パーフルオロアルキル基および親油性基を含有するオリゴマー、パーフルオロアルキル基、親水性基および親油性基を含有するオリゴマー、パーフルオロアルキル基および親油性基を含有するウレタン等のノニオン型が挙げられる。また、特開昭62−170950号、同62−226143号および同60−168144号の公報に記載されているフッ素系界面活性剤も好適に挙げられる。
More preferable surfactants include fluorine-based surfactants containing a perfluoroalkyl group in the molecule. Examples of such fluorosurfactants include anionic types such as perfluoroalkyl carboxylates, perfluoroalkyl sulfonates, and perfluoroalkyl phosphates; amphoteric types such as perfluoroalkyl betaines; Cation type such as trimethylammonium salt; perfluoroalkylamine oxide, perfluoroalkylethylene oxide adduct, oligomer containing perfluoroalkyl group and hydrophilic group, oligomer containing perfluoroalkyl group and lipophilic group, perfluoroalkyl Nonionic types such as an oligomer containing a group, a hydrophilic group and a lipophilic group, and a urethane containing a perfluoroalkyl group and a lipophilic group. Also preferred are the fluorosurfactants described in JP-A-62-170950, JP-A-62-226143 and JP-A-60-168144.
界面活性剤の中で、アニオン界面活性剤及びカチオン界面活性剤が、現像性の観点から好ましい。
界面活性剤の含有量は、感光層の全固形分に対して、0.001〜10質量%であるのが好ましく、0.01〜7質量%であるのがより好ましい。
Among the surfactants, anionic surfactants and cationic surfactants are preferable from the viewpoint of developability.
The content of the surfactant is preferably 0.001 to 10% by mass and more preferably 0.01 to 7% by mass with respect to the total solid content of the photosensitive layer.
<親水性ポリマー>
本発明においては、現像性の向上、マイクロカプセルの分散安定性向上などのため、親水性ポリマーを含有させることができる。
親水性ポリマーとしては、例えば、ヒドロキシ基、カルボキシル基、カルボキシレート基、ヒドロキシエチル基、ポリオキシエチル基、ヒドロキシプロピル基、ポリオキシプロピル基、アミノ基、アミノエチル基、アミノプロピル基、アンモニウム基、アミド基、カルボキシメチル基、スルホン酸基、リン酸基等の親水性基を有するものが好適に挙げられる。
<Hydrophilic polymer>
In the present invention, a hydrophilic polymer can be contained in order to improve the developability and the microcapsule dispersion stability.
Examples of the hydrophilic polymer include hydroxy group, carboxyl group, carboxylate group, hydroxyethyl group, polyoxyethyl group, hydroxypropyl group, polyoxypropyl group, amino group, aminoethyl group, aminopropyl group, ammonium group, Preferred examples include those having a hydrophilic group such as an amide group, carboxymethyl group, sulfonic acid group, and phosphoric acid group.
具体例として、アラビアゴム、カゼイン、ゼラチン、デンプン誘導体、カルボキシメチルセルロースおよびそのナトリウム塩、セルロースアセテート、アルギン酸ナトリウム、酢酸ビニル−マレイン酸コポリマー類、スチレン−マレイン酸コポリマー類、ポリアクリル酸類およびそれらの塩、ポリメタクリル酸類およびそれらの塩、ヒドロキシエチルメタクリレートのホモポリマーおよびコポリマー、ヒドロキシエチルアクリレートのホモポリマーおよびコポリマー、ヒドロキシピロピルメタクリレートのホモポリマーおよびコポリマー、ヒドロキシプロピルアクリレートのホモポリマーおよびコポリマー、ヒドロキシブチルメタクリレートのホモポリマーおよびコポリマー、ヒドロキシブチルアクリレートのホモポリマーおよびコポリマー、ポリエチレングリコール類、ヒドロキシプロピレンポリマー類、ポリビニルアルコール類、加水分解度が60モル%以上、好ましくは80モル%以上である加水分解ポリビニルアセテート、ポリビニルホルマール、ポリビニルブチラール、ポリビニルピロリドン、アクリルアミドのホモポリマーおよびコポリマー、メタクリルアミドのホモポリマーおよびポリマー、N−メチロールアクリルアミドのホモポリマーおよびコポリマー、ポリビニルピロリドン、アルコール可溶性ナイロン、2,2−ビス−(4−ヒドロキシフェニル)−プロパンとエピクロロヒドリンとのポリエーテル等が挙げられる。 Specific examples include gum arabic, casein, gelatin, starch derivatives, carboxymethylcellulose and its sodium salt, cellulose acetate, sodium alginate, vinyl acetate-maleic acid copolymers, styrene-maleic acid copolymers, polyacrylic acids and their salts, Polymethacrylic acids and their salts, homopolymers and copolymers of hydroxyethyl methacrylate, homopolymers and copolymers of hydroxyethyl acrylate, homopolymers and copolymers of hydroxypropyl methacrylate, homopolymers and copolymers of hydroxypropyl acrylate, homopolymers of hydroxybutyl methacrylate Polymers and copolymers, homopolymers and copolymers of hydroxybutyl acrylate Polyethylene glycols, hydroxypropylene polymers, polyvinyl alcohols, hydrolyzed polyvinyl acetate, polyvinyl formal, polyvinyl butyral, polyvinyl pyrrolidone, acrylamide homopolymers and copolymers having a hydrolysis degree of 60 mol% or more, preferably 80 mol% or more , Homopolymers and polymers of methacrylamide, homopolymers and copolymers of N-methylolacrylamide, polyvinylpyrrolidone, alcohol-soluble nylon, polyether of 2,2-bis- (4-hydroxyphenyl) -propane and epichlorohydrin, etc. Is mentioned.
親水性ポリマーは、質量平均分子量が5000以上であるのが好ましく、1万〜30万であるのがより好ましい。親水性ポリマーは、ランダムポリマー、ブロックポリマー、グラフトポリマー等のいずれでもよい。
親水性ポリマーの感光層への含有量は、感光層全固形分の20質量%以下が好ましく、10質量%以下がより好ましい。
The hydrophilic polymer preferably has a mass average molecular weight of 5000 or more, more preferably 10,000 to 300,000. The hydrophilic polymer may be any of a random polymer, a block polymer, a graft polymer, and the like.
The content of the hydrophilic polymer in the photosensitive layer is preferably 20% by mass or less, more preferably 10% by mass or less, based on the total solid content of the photosensitive layer.
<着色剤>
本発明では、可視光域に大きな吸収を持つ染料を画像の着色剤として使用することができる。具体的には、オイルイエロー#101、オイルイエロー#103、オイルピンク#312、オイルグリーンBG、オイルブルーBOS、オイルブルー#603、オイルブラ
ックBY、オイルブラックBS、オイルブラックT−505(以上オリエント化学工業(株)製)、ビクトリアピュアブルー、クリスタルバイオレット(CI42555)、メチルバイオレット(CI42535)、エチルバイオレット、ローダミンB(CI145170B)、マラカイトグリーン(CI42000)、メチレンブルー(CI52015)等、および特開昭62−293247号公報に記載されている染料を挙げることができる。また、フタロシアニン系顔料、アゾ系顔料、カーボンブラック、酸化チタン等の顔料も好適に用いることができる。
<Colorant>
In the present invention, a dye having a large absorption in the visible light region can be used as an image colorant. Specifically, Oil Yellow # 101, Oil Yellow # 103, Oil Pink # 312, Oil Green BG, Oil Blue BOS, Oil Blue # 603, Oil Black BY, Oil Black BS, Oil Black T-505 (orientated chemistry) Kogyo Co., Ltd.), Victoria Pure Blue, Crystal Violet (CI42555), Methyl Violet (CI42535), Ethyl Violet, Rhodamine B (CI145170B), Malachite Green (CI42000), Methylene Blue (CI522015), etc. And dyes described in Japanese Patent No. 293247. Also, pigments such as phthalocyanine pigments, azo pigments, carbon black, titanium oxide, etc. can be suitably used.
これらの着色剤は、画像形成後、画像部と非画像部の区別がつきやすいので、添加する方が好ましい。なお、添加量は、画像記録材料全固形分に対し、0.01〜10質量%の割合が好ましい。 These colorants are preferably added since it is easy to distinguish an image area from a non-image area after image formation. The amount added is preferably 0.01 to 10% by mass with respect to the total solid content of the image recording material.
<焼き出し剤>
本発明の感光層には、焼き出し画像生成のため、酸またはラジカルによって変色する化合物を添加することができる。このような化合物としては、例えばジフェニルメタン系、トリフェニルメタン系、チアジン系、オキサジン系、キサンテン系、アンスラキノン系、イミノキノン系、アゾ系、アゾメチン系等の各種色素が有効に用いられる。
<Bakeout agent>
In the photosensitive layer of the present invention, a compound that changes color by an acid or a radical can be added in order to form a printout image. As such a compound, various dyes such as diphenylmethane, triphenylmethane, thiazine, oxazine, xanthene, anthraquinone, iminoquinone, azo, and azomethine are effectively used.
具体例としては、ブリリアントグリーン、エチルバイオレット、メチルグリーン、クリスタルバイオレット、ベイシックフクシン、メチルバイオレット2B、キナルジンレッド、ローズベンガル、メタニルイエロー、チモールスルホフタレイン、キシレノールブルー、メチルオレンジ、パラメチルレッド、コンゴーフレッド、ベンゾプルプリン4B、α−ナフチルレッド、ナイルブルー2B、ナイルブルーA、メチルバイオレット、マラカイドグリーン、パラフクシン、ビクトリアピュアブルーBOH[保土ケ谷化学(株)製]、オイルブルー#603[オリエント化学工業(株)製]、オイルピンク#312[オリエント化学工業(株)製]、オイルレッド5B[オリエント化学工業(株)製]、オイルスカーレット#308[オリエント化学工業(株)製]、オイルレッドOG[オリエント化学工業(株)製]、オイルレッドRR[オリエント化学工業(株)製]、オイルグリーン#502[オリエント化学工業(株)製]、スピロンレッドBEHスペシャル[保土ケ谷化学工業(株)製]、m−クレゾールパープル、クレゾールレッド、ローダミンB、ローダミン6G、スルホローダミンB、オーラミン、4−p−ジエチルアミノフェニルイミノナフトキノン、2−カルボキシアニリノ−4−p−ジエチルアミノフェニルイミノナフトキノン、2−カルボキシステアリルアミノ−4−p−N,N−ビス(ヒドロキシエチル)アミノ−フェニルイミノナフトキノン、1−フェニル−3−メチル−4−p−ジエチルアミノフェニルイミノ−5−ピラゾロン、1−β−ナフチル−4−p−ジエチルアミノフェニルイミノ−5−ピラゾロン等の染料やp,p',p"−ヘキサメチルトリアミノトリフェニルメタン(ロイコクリスタルバイオレット)、Pergascript Blue SRB(チバガイギー社製)等のロイコ染料が挙げられる。 Specific examples include brilliant green, ethyl violet, methyl green, crystal violet, basic fuchsin, methyl violet 2B, quinaldine red, rose bengal, methanyl yellow, thymol sulfophthalein, xylenol blue, methyl orange, paramethyl red, Congo Fred, Benzopurpurin 4B, α-Naphthyl Red, Nile Blue 2B, Nile Blue A, Methyl Violet, Malachide Green, Parafuchsin, Victoria Pure Blue BOH [manufactured by Hodogaya Chemical Co., Ltd.], Oil Blue # 603 [Orient Chemical Kogyo Co., Ltd.], Oil Pink # 312 [Orient Chemical Co., Ltd.], Oil Red 5B [Orient Chemical Co., Ltd.], Oil Scarlet # 308 [Orient Gaku Kogyo Co., Ltd.], Oil Red OG [Orient Chemical Co., Ltd.], Oil Red RR [Orient Chemical Co., Ltd.], Oil Green # 502 [Orient Chemical Co., Ltd.], Spiron Red BEH Special [made by Hodogaya Chemical Co., Ltd.], m-cresol purple, cresol red, rhodamine B, rhodamine 6G, sulforhodamine B, auramine, 4-p-diethylaminophenyliminonaphthoquinone, 2-carboxyanilino-4-p- Diethylaminophenyliminonaphthoquinone, 2-carboxystearylamino-4-pN, N-bis (hydroxyethyl) amino-phenyliminonaphthoquinone, 1-phenyl-3-methyl-4-p-diethylaminophenylimino-5-pyrazolone, 1-β-naphthyl-4- - dyes and p of diethylamino phenyl imino-5-pyrazolone, p ', p "- hexamethyl triamnotriphenylmethane (leuco crystal violet), and a leuco dye such as Pergascript Blue SRB (manufactured by Ciba-Geigy).
上記の他に、感熱紙や感圧紙用の素材として知られているロイコ染料も好適なものとして挙げられる。具体例としては、クリスタルバイオレットラクトン、マラカイトグリーンラクトン、ベンゾイルロイコメチレンブルー、2−(N−フェニル−N−メチルアミノ)−6−(N−p−トリル−N−エチル)アミノ−フルオラン、2−アニリノ−3−メチル−6−(N−エチル−p−トルイジノ)フルオラン、3,6−ジメトキシフルオラン、3−(N,N−ジエチルアミノ)−5−メチル−7−(N,N−ジベンジルアミノ)−フルオラン、3−(N−シクロヘキシル−N−メチルアミノ)−6−メチル−7−アニリノフルオラン、3−(N,N−ジエチルアミノ)−6−メチル−7−アニリノフルオラン、3−(N,N−ジエチルアミノ)−6−メチル−7−キシリジノフルオラン、3−(N,N−ジエチルアミノ)−6−メチルー7−クロロフルオラン、3−(N,N−ジエチルアミノ)−6−メトキシ−7−アミノフルオラン、3−(N,N−ジエチルアミノ)−7−(
4−クロロアニリノ)フルオラン、3−(N,N−ジエチルアミノ)−7−クロロフルオラン、3−(N,N−ジエチルアミノ)−7−ベンジルアミノフルオラン、3−(N,N−ジエチルアミノ)−7,8−ベンゾフルオラン、3−(N,N−ジブチルアミノ)−6−メチル−7−アニリノフルオラン、3−(N,N−ジブチルアミノ)−6−メチル−7−キシリジノフルオラン、3−ピペリジノ−6−メチル−7−アニリノフルオラン、3−ピロリジノ−6−メチル−7−アニリノフルオラン、3,3−ビス(1−エチル−2−メチルインドール−3−イル)フタリド、3,3−ビス(1−n−ブチル−2−メチルインドール−3−イル)フタリド、3,3−ビス(p−ジメチルアミノフェニル)−6−ジメチルアミノフタリド、3−(4−ジエチルアミノ−2−エトキシフェニル)−3−(1−エチル−2−メチルインドール−3−イル)−4−ザフタリド、3−(4−ジエチルアミノフェニル)−3−(1−エチル−2−メチルインドール−3−イル)フタリド、などが挙げられる。
In addition to the above, a leuco dye known as a material for thermal paper or pressure-sensitive paper is also suitable. Specific examples include crystal violet lactone, malachite green lactone, benzoylleucomethylene blue, 2- (N-phenyl-N-methylamino) -6- (Np-tolyl-N-ethyl) amino-fluorane, 2-anilino. -3-methyl-6- (N-ethyl-p-toluidino) fluorane, 3,6-dimethoxyfluorane, 3- (N, N-diethylamino) -5-methyl-7- (N, N-dibenzylamino) ) -Fluorane, 3- (N-cyclohexyl-N-methylamino) -6-methyl-7-anilinofluorane, 3- (N, N-diethylamino) -6-methyl-7-anilinofluorane, 3 -(N, N-diethylamino) -6-methyl-7-xylidinofluorane, 3- (N, N-diethylamino) -6-methyl-7-chloro Fluoran, 3- (N, N-diethylamino) -6-methoxy-7- aminofluoran, 3- (N, N-diethylamino) -7- (
4-chloroanilino) fluorane, 3- (N, N-diethylamino) -7-chlorofluorane, 3- (N, N-diethylamino) -7-benzylaminofluorane, 3- (N, N-diethylamino) -7 , 8-Benzofluorane, 3- (N, N-dibutylamino) -6-methyl-7-anilinofluorane, 3- (N, N-dibutylamino) -6-methyl-7-xylidinofluorane 3-piperidino-6-methyl-7-anilinofluorane, 3-pyrrolidino-6-methyl-7-anilinofluorane, 3,3-bis (1-ethyl-2-methylindol-3-yl) Phthalide, 3,3-bis (1-n-butyl-2-methylindol-3-yl) phthalide, 3,3-bis (p-dimethylaminophenyl) -6-dimethylaminophthalide, 3- ( -Diethylamino-2-ethoxyphenyl) -3- (1-ethyl-2-methylindol-3-yl) -4-zaphthalide, 3- (4-diethylaminophenyl) -3- (1-ethyl-2-methylindole) -3-yl) phthalide, and the like.
酸またはラジカルによって変色する染料の好適な添加量は、それぞれ、感光層固形分に対して0.01〜15質量%の割合である。 A suitable addition amount of the dye that changes color by acid or radical is 0.01 to 15% by mass relative to the solid content of the photosensitive layer.
<重合禁止剤>
本発明の感光層には、感光層の製造中または保存中において、ラジカル重合性化合物の不要な熱重合を防止するために、少量の熱重合防止剤を添加するのが好ましい。
熱重合防止剤としては、例えば、ハイドロキノン、p−メトキシフェノール、ジ−t−ブチル−p−クレゾール、ピロガロール、t−ブチルカテコール、ベンゾキノン、4,4′−チオビス(3−メチル−6−t−ブチルフェノール)、2,2′−メチレンビス(4−メチル−6−t−ブチルフェノール)、N−ニトロソ−N−フェニルヒドロキシルアミンアルミニウム塩が好適に挙げられる。
熱重合防止剤の添加量は、感光層の全固形分に対して、約0.01〜約5質量%であるのが好ましい。
<Polymerization inhibitor>
In order to prevent unnecessary thermal polymerization of the radical polymerizable compound during the production or storage of the photosensitive layer, it is preferable to add a small amount of a thermal polymerization inhibitor to the photosensitive layer of the present invention.
Examples of the thermal polymerization inhibitor include hydroquinone, p-methoxyphenol, di-t-butyl-p-cresol, pyrogallol, t-butylcatechol, benzoquinone, 4,4'-thiobis (3-methyl-6-t- (Butylphenol), 2,2'-methylenebis (4-methyl-6-tert-butylphenol), N-nitroso-N-phenylhydroxylamine aluminum salt are preferred.
The addition amount of the thermal polymerization inhibitor is preferably about 0.01 to about 5% by mass with respect to the total solid content of the photosensitive layer.
<高級脂肪酸誘導体等>
本発明の感光層には、酸素による重合阻害を防止するために、ベヘン酸やベヘン酸アミドのような高級脂肪酸誘導体等を添加して、塗布後の乾燥の過程で感光層の表面に偏在させてもよい。高級脂肪酸誘導体の添加量は、感光層の全固形分に対して、約0.1〜約10質量%であるのが好ましい。
<Higher fatty acid derivatives, etc.>
In order to prevent polymerization inhibition by oxygen, a higher fatty acid derivative such as behenic acid or behenamide is added to the photosensitive layer of the present invention so that it is unevenly distributed on the surface of the photosensitive layer during the drying process after coating. May be. The amount of the higher fatty acid derivative added is preferably from about 0.1 to about 10% by weight based on the total solid content of the photosensitive layer.
<可塑剤>
本発明の感光層は可塑剤を含有してもよい。可塑剤としては、例えば、ジメチルフタレート、ジエチルフタレート、ジブチルフタレート、ジイソブチルフタレート、ジオクチルフタレート、オクチルカプリルフタレート、ジシクロヘキシルフタレート、ジトリデシルフタレート、ブチルベンジルフタレート、ジイソデシルフタレート、ジアリルフタレート等のフタル酸エステル類;ジメチルグリコールフタレート、エチルフタリルエチルグリコレート、メチルフタリルエチルグリコレート、ブチルフタリルブチルグリコレート、トリエチレングリコールジカプリル酸エステル等のグリコールエステル類;トリクレジルホスフェート、トリフェニルホスフェート等のリン酸エステル類;ジイソブチルアジペート、ジオクチルアジペート、ジメチルセバケート、ジブチルセバケート、ジオクチルアゼレート、ジブチルマレエート等の脂肪族二塩基酸エステル類;ポリグリシジルメタクリレート、クエン酸トリエチル、グリセリントリアセチルエステル、ラウリン酸ブチル等が好適に挙げられる。可塑剤の含有量は、感光層の全固形分に対して、約30質量%以下であるのが好ましい。
<Plasticizer>
The photosensitive layer of the present invention may contain a plasticizer. Examples of the plasticizer include phthalates such as dimethyl phthalate, diethyl phthalate, dibutyl phthalate, diisobutyl phthalate, dioctyl phthalate, octyl capryl phthalate, dicyclohexyl phthalate, ditridecyl phthalate, butyl benzyl phthalate, diisodecyl phthalate, diallyl phthalate; Glycol esters such as glycol phthalate, ethyl phthalyl ethyl glycolate, methyl phthalyl ethyl glycolate, butyl phthalyl butyl glycolate, triethylene glycol dicaprylate; Phosphate esters such as tricresyl phosphate and triphenyl phosphate Diisobutyl adipate, dioctyl adipate, dimethyl sebacate, dibutyl sebacate, dioct Ruazereto, aliphatic dibasic acid esters such as dibutyl maleate; polyglycidyl methacrylate, triethyl citrate, glycerin triacetyl ester, butyl laurate in. The plasticizer content is preferably about 30% by mass or less based on the total solid content of the photosensitive layer.
<無機微粒子>
本発明の感光層は、画像部の硬化皮膜強度向上のために、無機微粒子を含有してもよい
。無機微粒子としては、例えば、シリカ、アルミナ、酸化マグネシウム、酸化チタン、炭酸マグネシウム、アルギン酸カルシウムまたはこれらの混合物が好適に挙げられる。これらは光熱変換性でなくても、皮膜の強化、表面粗面化による界面接着性の強化等に用いることができる。無機微粒子は、平均粒径が5nm〜10μmであるのが好ましく、0.5〜3μmであるのがより好ましい。上記範囲内であると、感光層中に安定に分散して、感光層の膜強度を十分に保持し、印刷時の汚れを生じにくい親水性に優れる非画像部を形成することができる。
上述したような無機微粒子は、コロイダルシリカ分散物等の市販品として容易に入手することができる。
無機微粒子の含有量は、感光層の全固形分に対して、20質量%以下であるのが好ましく、10質量%以下であるのがより好ましい。
<Inorganic fine particles>
The photosensitive layer of the present invention may contain inorganic fine particles in order to improve the cured film strength of the image area. As the inorganic fine particles, for example, silica, alumina, magnesium oxide, titanium oxide, magnesium carbonate, calcium alginate or a mixture thereof can be preferably mentioned. Even if they are not photothermally convertible, they can be used for strengthening the film, enhancing interfacial adhesion by surface roughening, and the like. The inorganic fine particles preferably have an average particle size of 5 nm to 10 μm, and more preferably 0.5 to 3 μm. Within the above range, it is possible to form a non-image portion excellent in hydrophilicity that is stably dispersed in the photosensitive layer, sufficiently retains the film strength of the photosensitive layer, and does not easily cause stains during printing.
The inorganic fine particles as described above can be easily obtained as a commercial product such as a colloidal silica dispersion.
The content of the inorganic fine particles is preferably 20% by mass or less, and more preferably 10% by mass or less, based on the total solid content of the photosensitive layer.
<低分子親水性化合物>
本発明の感光層は、現像性向上のため、親水性低分子化合物を含有することができる。親水性低分子化合物としては、例えば、水溶性有機化合物としては、エチレングリコール、ジエチレングリコール、トリエチレングリコール、プロピレングリコール、ジプロピレングリコール、トリプロピレングリコール等のグリコール類およびそのエーテルまたはエステル誘導体類、グリセリン、ペンタエリスリトール等のポリヒドロキシ類、トリエタノールアミン、ジエタノールアミンモノエタノールアミン等の有機アミン類およびその塩、トルエンスルホン酸、ベンゼンスルホン酸等の有機スルホン酸類およびその塩、フェニルホスホン酸等の有機ホスホン酸類およびその塩、酒石酸、シュウ酸、クエン酸、リンゴ酸、乳酸、グルコン酸、アミノ酸類等の有機カルボン酸類およびその塩や、テトラエチルアミン塩酸塩等の有機4級アンモニウム塩等が挙げられる。
<Low molecular hydrophilic compound>
The photosensitive layer of the present invention can contain a hydrophilic low molecular weight compound for improving developability. Examples of the hydrophilic low-molecular compound include water-soluble organic compounds such as ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol, tripropylene glycol and the like, and ether or ester derivatives thereof, glycerin, Polyhydroxys such as pentaerythritol, organic amines such as triethanolamine and diethanolamine monoethanolamine and salts thereof, organic sulfonic acids such as toluenesulfonic acid and benzenesulfonic acid and salts thereof, organic phosphonic acids such as phenylphosphonic acid and the like Organic carboxylic acids such as salts, tartaric acid, oxalic acid, citric acid, malic acid, lactic acid, gluconic acid, amino acids and their salts, and organic quaternary amines such as tetraethylamine hydrochloride Salt, and the like.
<共増感剤>
ある種の添加剤を用いることで、該感光層の感度をさらに向上させることができる。そのような化合物を、本発明では共増感剤という。これらの作用機構は、明確ではないが、多くは次のような化学プロセスに基づくものと考えられる。すなわち、先述の光重合開始系の光吸収により開始される光反応、と、それに引き続く付加重合反応の過程で生じる様々な中間活性種(ラジカル、過酸化物、酸化剤、還元剤等)と、共増感剤が反応し、新たな活性ラジカルを生成するものと推定される。これらは、大きくは、(a)還元されて活性ラジカルを生成しうるもの、(b)酸化されて活性ラジカルを生成しうるもの、(c)活性の低いラジカルと反応し、より活性の高いラジカルに変換するか、もしくは連鎖移動剤として作用するもの、に分類できるが、個々の化合物がこれらのどれに属するかに関しては、通説がない場合も多い。
<Co-sensitizer>
The sensitivity of the photosensitive layer can be further improved by using certain additives. Such a compound is referred to as a co-sensitizer in the present invention. These mechanisms of action are not clear, but many are thought to be based on the following chemical processes. That is, a photoreaction initiated by light absorption of the above-described photopolymerization initiation system, and various intermediate active species (radicals, peroxides, oxidizing agents, reducing agents, etc.) generated in the course of the subsequent addition polymerization reaction, It is presumed that the co-sensitizer reacts to generate a new active radical. These can be broadly divided into (a) those that can be reduced to generate active radicals, (b) those that can be oxidized to generate active radicals, and (c) radicals that are more active by reacting with less active radicals. Can be classified into those that act as chain transfer agents, but there is often no generality as to which of these individual compounds belong.
(a)還元されて活性ラジカルを生成する化合物
炭素−ハロゲン結合を有する化合物:還元的に炭素−ハロゲン結合が解裂し、活性ラジカルを発生すると考えられる。具体的には、例えば、トリハロメチル−s−トリアジン類や、トリハロメチルオキサジアゾール類等が好適に使用できる。
窒素−窒素結合を有する化合物:還元的に窒素−窒素結合が解裂し、活性ラジカルを発生すると考えられる。具体的にはヘキサアリールビイミダゾール類等が好適に使用される。
酸素−酸素結合を有する化合物:還元的に酸素−酸素結合が解裂し、活性ラジカルを発生すると考えられる。具体的には、例えば、有機過酸化物類等が好適に使用される。
オニウム化合物:還元的に炭素−ヘテロ結合や、酸素−窒素結合が解裂し、活性ラジカルを発生すると考えられる。具体的には例えば、ジアリールヨードニウム塩類、トリアリールスルホニウム塩類、N−アルコキシピリジニウム(アジニウム)塩類等が好適に使用される。
フェロセン、鉄アレーン錯体類:還元的に活性ラジカルを生成しうる。
(A) Compound that is reduced to produce an active radical Compound having a carbon-halogen bond: It is considered that an active radical is generated by reductive cleavage of the carbon-halogen bond. Specifically, for example, trihalomethyl-s-triazines and trihalomethyloxadiazoles can be preferably used.
Compound having nitrogen-nitrogen bond: It is considered that the nitrogen-nitrogen bond is reductively cleaved to generate an active radical. Specifically, hexaarylbiimidazoles and the like are preferably used.
Compound having oxygen-oxygen bond: It is considered that the oxygen-oxygen bond is reductively cleaved to generate an active radical. Specifically, for example, organic peroxides are preferably used.
Onium compounds: It is considered that carbon-hetero bonds and oxygen-nitrogen bonds are reductively cleaved to generate active radicals. Specifically, for example, diaryliodonium salts, triarylsulfonium salts, N-alkoxypyridinium (azinium) salts and the like are preferably used.
Ferrocene and iron arene complexes: An active radical can be reductively generated.
(b)酸化されて活性ラジカルを生成する化合物
アルキルアート錯体:酸化的に炭素−ヘテロ結合が解裂し、活性ラジカルを生成すると考えられる。具体的には例えば、トリアリールアルキルボレート類が好適に使用される。
アルキルアミン化合物:酸化により窒素に隣接した炭素上のC−X結合が解裂し、活性ラジカルを生成するものと考えられる。Xとしては、水素原子、カルボキシル基、トリメチルシリル基、ベンジル基等が好適である。具体的には、例えば、エタノールアミン類、N−フェニルグリシン類、N−トリメチルシリルメチルアニリン類等が挙げられる。
含硫黄、含錫化合物:上述のアミン類の窒素原子を硫黄原子、錫原子に置き換えたものが、同様の作用により活性ラジカルを生成しうる。また、S−S結合を有する化合物もS−S解裂による増感が知られる。
(B) Compound which is oxidized to generate an active radical Alkylate complex: It is considered that a carbon-hetero bond is oxidatively cleaved to generate an active radical. Specifically, for example, triarylalkyl borates are preferably used.
Alkylamine compound: It is considered that the C—X bond on carbon adjacent to nitrogen is cleaved by oxidation to generate an active radical. X is preferably a hydrogen atom, a carboxyl group, a trimethylsilyl group, a benzyl group or the like. Specific examples include ethanolamines, N-phenylglycines, N-trimethylsilylmethylanilines, and the like.
Sulfur-containing and tin-containing compounds: those in which the nitrogen atoms of the above-described amines are replaced by sulfur atoms and tin atoms can generate active radicals by the same action. Further, a compound having an SS bond is also known to be sensitized by SS cleavage.
α−置換メチルカルボニル化合物:酸化により、カルボニル−α炭素間の結合解裂により、活性ラジカルを生成しうる。また、カルボニルをオキシムエーテルに変換したものも同様の作用を示す。具体的には、2−アルキル−1−[4−(アルキルチオ)フェニル]−2−モルフォリノプロノン−1類、並びに、これらと、ヒドロキシアミン類とを反応したのち、N−OHをエーテル化したオキシムエーテル類をあげることができる。
スルフィン酸塩類:還元的に活性ラジカルを生成しうる。具体的は、アリールスルフィン酸ナトリウム等を挙げることができる。
α-Substituted methylcarbonyl compound: An active radical can be generated by oxidative cleavage of the carbonyl-α carbon bond. Moreover, what converted carbonyl into the oxime ether also shows the same effect | action. Specifically, 2-alkyl-1- [4- (alkylthio) phenyl] -2-morpholinopronone-1 and these and a hydroxylamine were reacted, and then N—OH was etherified. Examples include oxime ethers.
Sulfinic acid salts: An active radical can be reductively generated. Specific examples include sodium arylsulfinate.
(c)ラジカルと反応し高活性ラジカルに変換、もしくは連鎖移動剤として作用する化合物
ラジカルと反応し高活性ラジカルに変換、もしくは連鎖移動剤として作用する化合物としては、例えば、分子内にSH、PH、SiH、GeHを有する化合物群が用いられる。これらは、低活性のラジカル種に水素供与して、ラジカルを生成するか、もしくは、酸化された後、脱プロトンすることによりラジカルを生成しうる。具体的には、例えば、2−メルカプトベンズイミダゾール類等が挙げられる。
(C) Compounds that react with radicals to convert to highly active radicals or act as chain transfer agents Compounds that react with radicals to convert to highly active radicals or act as chain transfer agents include, for example, SH, PH in the molecule , SiH, and GeH are used. These can donate hydrogen to low-activity radical species to generate radicals, or can be oxidized and then deprotonated to generate radicals. Specifically, 2-mercaptobenzimidazoles etc. are mentioned, for example.
これらの共増感剤のより具体的な例は、例えば、特開平9−236913号公報中に、感度向上を目的とした添加剤として、多く記載されている。以下に、その一部を例示するが、本発明はこれらに限定されるものはない。 Many more specific examples of these co-sensitizers are described, for example, in JP-A-9-236913 as additives for the purpose of improving sensitivity. Some examples are shown below, but the present invention is not limited thereto.
これらの共増感剤に関しても、先の増感色素と同様、さらに、平版印刷版原版の感光層の特性を改良するための様々な化学修飾を行うことも可能である。例えば、増感色素やチ
タノセン、付加重合性不飽和化合物その他のラジカル発生パートとの結合、親水性部位の導入、相溶性向上、結晶析出抑制のための置換基導入、密着性を向上させる置換基導入、ポリマー化等の方法が利用できる。これらの共増感剤は、単独でまたは2種以上併用して用いることができる。使用量はエチレン性不飽和二重結合を有する化合物100質量部に対し0.05〜100質量部、好ましくは1〜80質量部、さらに好ましくは3〜50質量部の範囲が適当である。
These co-sensitizers can also be subjected to various chemical modifications for improving the characteristics of the photosensitive layer of the lithographic printing plate precursor as in the case of the sensitizing dye. For example, bonds with sensitizing dyes, titanocene, addition polymerizable unsaturated compounds and other radical generating parts, introduction of hydrophilic sites, improved compatibility, introduction of substituents for suppressing crystal precipitation, substituents for improving adhesion Methods such as introduction and polymerization can be used. These co-sensitizers can be used alone or in combination of two or more. The amount used is 0.05 to 100 parts by mass, preferably 1 to 80 parts by mass, and more preferably 3 to 50 parts by mass with respect to 100 parts by mass of the compound having an ethylenically unsaturated double bond.
<感光層の形成>
本発明の感光層は、必要な上記各成分を溶剤に分散または溶解して塗布液を調製し、塗布して形成される。ここで使用する溶剤としては、エチレンジクロリド、シクロヘキサノン、メチルエチルケトン、メタノール、エタノール、プロパノール、エチレングリコールモノメチルエーテル、1−メトキシ−2−プロパノール、2−メトキシエチルアセテート、1−メトキシ−2−プロピルアセテート、ジメトキシエタン、乳酸メチル、乳酸エチル、N,N−ジメチルアセトアミド、N,N−ジメチルホルムアミド、テトラメチルウレア、N−メチルピロリドン、ジメチルスルホキシド、スルホラン、γ−ブチルラクトン、トルエン、水等を挙げることができるが、これに限定されるものではない。これらの溶剤は、単独または混合して使用される。塗布液の固形分濃度は、好ましくは1〜50質量%である。
本発明の感光層は、同一または異なる上記各成分を同一または異なる溶剤に分散、または溶かした塗布液を複数調製し、複数回の塗布、乾燥を繰り返して形成することも可能である。
<Formation of photosensitive layer>
The photosensitive layer of the present invention is formed by preparing or applying a coating solution by dispersing or dissolving the necessary components described above in a solvent. Solvents used here include ethylene dichloride, cyclohexanone, methyl ethyl ketone, methanol, ethanol, propanol, ethylene glycol monomethyl ether, 1-methoxy-2-propanol, 2-methoxyethyl acetate, 1-methoxy-2-propyl acetate, dimethoxy Examples include ethane, methyl lactate, ethyl lactate, N, N-dimethylacetamide, N, N-dimethylformamide, tetramethylurea, N-methylpyrrolidone, dimethyl sulfoxide, sulfolane, γ-butyllactone, toluene, water, and the like. However, the present invention is not limited to this. These solvents are used alone or in combination. The solid content concentration of the coating solution is preferably 1 to 50% by mass.
The photosensitive layer of the present invention can be formed by preparing a plurality of coating solutions in which the same or different components are dispersed or dissolved in the same or different solvents, and repeatedly applying and drying a plurality of times.
また塗布、乾燥後に得られる支持体上の感光層塗布量(固形分)は、用途によって異なるが、一般的に0.3〜3.0g/m2が好ましい。この範囲内で、良好な感度と感光層
の良好な皮膜特性が得られる。
塗布する方法としては、種々の方法を用いることができる。例えば、バーコーター塗布、回転塗布、スプレー塗布、カーテン塗布、ディップ塗布、エアーナイフ塗布、ブレード塗布、ロール塗布等を挙げられる。
The coating, the photosensitive layer coating amount on the support obtained after drying (solid content) may be varied according to the intended purpose, generally 0.3 to 3.0 g / m 2 is preferred. Within this range, good sensitivity and good film properties of the photosensitive layer can be obtained.
Various methods can be used as a coating method. Examples thereof include bar coater coating, spin coating, spray coating, curtain coating, dip coating, air knife coating, blade coating, and roll coating.
<保護層>
本発明の平版印刷版原版には、露光時の重合反応を妨害する酸素の拡散侵入を遮断するため、感光層上に保護層(酸素遮断層)が設けられる。本発明に用いられる保護層は25℃、1気圧下における酸素透過性Aが1.0≦A≦20(mL/m2・day)であることが好ましい。酸素透過性Aが1.0(mL/m2・day)未満で極端に低い場合は、製造時・生保存時に不要な重合反応が生じたり、また画像露光時に、不要なカブリ、画線の太りが生じたりという問題を生じる。逆に、酸素透過性Aが20(mL/ m2・day)を超えて高すぎる場合は感度の低下を招く。酸素透過性Aは、より好ましくは1.5≦A≦12(mL/m2・day)、更に好ましくは2.0≦A≦10.0(mL/m2・day)の範囲である。また、保護層に望まれる特性としては、上記酸素透過性以外に、さらに、露光に用いる光の透過は実質阻害せず、感光層との密着性に優れ、かつ、露光後の現像工程で容易に除去できる事が望ましい。この様な保護層に関する工夫が従来なされており、米国特許第3,458,311号明細書、特公昭55−49729号公報に詳しく記載されている。
<Protective layer>
In the lithographic printing plate precursor according to the invention, a protective layer (oxygen blocking layer) is provided on the photosensitive layer in order to block diffusion and penetration of oxygen that hinders the polymerization reaction during exposure. The protective layer used in the present invention preferably has an oxygen permeability A at 25 ° C. and 1 atm of 1.0 ≦ A ≦ 20 (mL / m 2 · day). When the oxygen permeability A is extremely low at less than 1.0 (mL / m 2 · day), unnecessary polymerization reaction occurs at the time of production and raw storage, and unnecessary fogging and image streaking occur during image exposure. The problem that fatness arises arises. Conversely, when the oxygen permeability A exceeds 20 (mL / m 2 · day) and is too high, the sensitivity is lowered. The oxygen permeability A is more preferably in the range of 1.5 ≦ A ≦ 12 (mL / m 2 · day), further preferably 2.0 ≦ A ≦ 10.0 (mL / m 2 · day). In addition to the oxygen permeability described above, the properties desired for the protective layer further do not substantially inhibit the transmission of light used for exposure, have excellent adhesion to the photosensitive layer, and are easy in the development process after exposure. It is desirable that it can be removed. The device concerning such a protective layer has been conventionally made, and is described in detail in US Pat. No. 3,458,311 and JP-B-55-49729.
保護層に使用できる材料としては例えば、比較的結晶性に優れた水溶性高分子化合物を用いることが好ましく、具体的には、ポリビニルアルコール、ビニルアルコール/フタル酸ビニル共重合体、酢酸ビニル/ビニルアルコール/フタル酸ビニル共重合体、酢酸ビニル/クロトン酸共重合体、ポリビニルピロリドン、酸性セルロース類、ゼラチン、アラビアゴム、ポリアクリル酸、ポリアクリルアミドなどのような水溶性ポリマーが挙げられ、これらは単独または混合して使用できる。これらの内、ポリビニルアルコールを主成分と
して用いる事が、酸素遮断性、現像除去性といった基本特性的にもっとも良好な結果を与える。
As a material that can be used for the protective layer, for example, a water-soluble polymer compound having relatively excellent crystallinity is preferably used. Specifically, polyvinyl alcohol, vinyl alcohol / vinyl phthalate copolymer, vinyl acetate / vinyl are used. Examples include water-soluble polymers such as alcohol / vinyl phthalate copolymer, vinyl acetate / crotonic acid copolymer, polyvinyl pyrrolidone, acidic celluloses, gelatin, gum arabic, polyacrylic acid, and polyacrylamide. Or they can be mixed. Of these, the use of polyvinyl alcohol as the main component gives the best results in terms of basic properties such as oxygen barrier properties and development removability.
保護層に使用するポリビニルアルコールは、必要な酸素遮断性と水溶性を有するための、未置換ビニルアルコール単位を含有する限り、一部がエステル、エーテル、およびアセタールで置換されていても良い。また、同様に一部が他の共重合成分を有していても良い。ポリビニルアルコールの具体例としては71〜100モル%加水分解され、重合繰り返し単位が300から2400の範囲のものをあげる事ができる。具体的には、株式会社クラレ製のPVA−105、PVA−110、PVA−117、PVA−117H、PVA−120、PVA−124、PVA−124H、PVA−CS、PVA−CST、PVA−HC、PVA−203、PVA−204、PVA−205、PVA−210、PVA−217、PVA−220、PVA−224、PVA−217EE、PVA−217E、PVA−220E、PVA−224E、PVA−405、PVA−420、PVA−613、L−8等が挙げられ、これらは単独または混合して使用できる。好ましい態様としてはポリビニルアルコールの保護層中の含有率が20〜95質量%、より好ましくは、30〜90質量%である。 The polyvinyl alcohol used for the protective layer may be partially substituted with an ester, an ether, and an acetal as long as it contains an unsubstituted vinyl alcohol unit for having necessary oxygen barrier properties and water solubility. Similarly, some of them may have other copolymer components. Specific examples of polyvinyl alcohol include those that are hydrolyzed by 71 to 100 mol% and have a polymerization repeating unit in the range of 300 to 2400. Specifically, Kuraray Co., Ltd. PVA-105, PVA-110, PVA-117, PVA-117H, PVA-120, PVA-124, PVA-124H, PVA-CS, PVA-CST, PVA-HC, PVA-203, PVA-204, PVA-205, PVA-210, PVA-217, PVA-220, PVA-224, PVA-217EE, PVA-217E, PVA-220E, PVA-224E, PVA-405, PVA- 420, PVA-613, L-8 and the like, and these can be used alone or in combination. In a preferred embodiment, the content of polyvinyl alcohol in the protective layer is 20 to 95% by mass, and more preferably 30 to 90% by mass.
また、公知の変性ポリビニルアルコールも好ましく用いることができる。例えば、カルボキシル基、スルホ基等のアニオンで変性されたアニオン変性部位、アミノ基、アンモニウム基等のカチオンで変性されたカチオン変性部位、シラノール変性部位、チオール変性部位等種々の親水性変性部位をランダムに有す各種重合度のポリビニルアルコール、前記のアニオン変性部位、前記のカチオン変性部位、シラノール変性部位、チオール変性部位、更にはアルコキシル変性部位、スルフィド変性部位、ビニルアルコールと各種有機酸とのエステル変性部位、前記アニオン変性部位とアルコール類等とのエステル変性部位、エポキシ変性部位等種々の変性部位をポリマー鎖末端に有す各種重合度のポリビニルアルコール等が挙げられる。 Moreover, well-known modified polyvinyl alcohol can also be used preferably. For example, various hydrophilic modification sites such as anion modification sites modified with anions such as carboxyl groups and sulfo groups, cation modification sites modified with cations such as amino groups and ammonium groups, silanol modification sites, and thiol modification sites are randomly selected. Polyvinyl alcohol having various degrees of polymerization, the anion-modified site, the cation-modified site, the silanol-modified site, the thiol-modified site, the alkoxyl-modified site, the sulfide-modified site, and the ester modification of vinyl alcohol and various organic acids. Examples thereof include polyvinyl alcohol having various polymerization degrees having various modified sites such as a site, an ester-modified site of the anion-modified site and alcohols, an epoxy-modified site, and the like.
ポリビニルアルコールと混合して使用する成分としてはポリビニルピロリドンまたはその変性物が酸素遮断性、現像除去性といった観点から好ましく、保護層中の含有率が3.5〜80質量%、好ましくは10〜60質量%、さらに好ましくは15〜30質量%である。 As a component used by mixing with polyvinyl alcohol, polyvinyl pyrrolidone or a modified product thereof is preferable from the viewpoint of oxygen barrier properties and development removability, and the content in the protective layer is 3.5 to 80% by mass, preferably 10 to 60%. It is 15 mass%, More preferably, it is 15-30 mass%.
保護層の成分(PVAの選択、添加剤の使用)、塗布量等は、酸素遮断性・現像除去性の他、カブリ性や密着性・耐傷性を考慮して選択される。一般には使用するPVAの加水分解率が高い程(保護層中の未置換ビニルアルコール単位含率が高い程)、膜厚が厚い程酸素遮断性が高くなり、感度の点で有利である。上記ポリビニルアルコール(PVA)等の(共)重合体の分子量は、2000〜1000万の範囲のものが使用でき、好ましくは2万〜300万範囲のものが適当である。 Components of the protective layer (selection of PVA, use of additives), coating amount, and the like are selected in consideration of fogging, adhesion, and scratch resistance in addition to oxygen barrier properties and development removability. In general, the higher the hydrolysis rate of the PVA used (the higher the content of the unsubstituted vinyl alcohol unit in the protective layer), the thicker the film thickness, the higher the oxygen barrier property, which is advantageous in terms of sensitivity. The molecular weight of the (co) polymer such as polyvinyl alcohol (PVA) can be in the range of 2000 to 10 million, preferably in the range of 20,000 to 3 million.
保護層の他の組成物として、グリセリン、ジプロピレングリコール等を(共)重合体に対して数質量%相当量添加して可撓性を付与することができ、また、アルキル硫酸ナトリウム、アルキルスルホン酸ナトリウム等のアニオン界面活性剤;アルキルアミノカルボン酸塩、アルキルアミノジカルボン酸塩等の両性界面活性剤;ポリオキシエチレンアルキルフェニルエーテル等の非イオン界面活性剤を(共)重合体に対して数質量%添加することができる。 As another composition of the protective layer, glycerin, dipropylene glycol and the like can be added in an amount corresponding to several mass% with respect to the (co) polymer to provide flexibility. Anionic surfactants such as sodium acid salts; amphoteric surfactants such as alkylaminocarboxylates and alkylaminodicarboxylates; nonionic surfactants such as polyoxyethylene alkylphenyl ethers to the (co) polymer Mass% can be added.
また、画像部との密着性や、耐傷性も版の取り扱い上極めて重要である。すなわち、水溶性ポリマーからなる親水性の層を親油性の感光層に積層すると、接着力不足による膜剥離が発生しやすく、剥離部分が酸素の重合阻害により膜硬化不良などの欠陥を引き起こす。これに対し、これら2層間の接着性を改良すべく種々の提案がなされている。例えば米国特許出願番号第292,501号、米国特許出願番号第44,563号には、主にポリビニルアルコールからなる親水性ポリマー中に、アクリル系エマルジョンまたは水不溶性ビニルピロリドン−ビニルアセテート共重合体などを20〜60質量%混合し、感光層の上に積層することにより、十分な接着性が得られることが記載されている。本発明における保護層に対しては、これらの公知の技術をいずれも適用することができる。このような保護層の塗布方法については、例えば米国特許第3,458,311号明細書、特公昭55−49729号公報に詳しく記載されている。 In addition, adhesion to the image area and scratch resistance are extremely important in handling the plate. That is, when a hydrophilic layer made of a water-soluble polymer is laminated on an oleophilic photosensitive layer, film peeling due to insufficient adhesion tends to occur, and the peeled part causes defects such as poor film hardening due to inhibition of oxygen polymerization. On the other hand, various proposals have been made to improve the adhesion between these two layers. For example, in U.S. Patent Application No. 292,501 and U.S. Patent Application No. 44,563, an acrylic emulsion or a water-insoluble vinyl pyrrolidone-vinyl acetate copolymer is contained in a hydrophilic polymer mainly composed of polyvinyl alcohol. It is described that sufficient adhesiveness can be obtained by mixing 20 to 60% by mass and laminating on a photosensitive layer. Any of these known techniques can be applied to the protective layer in the present invention. Such a coating method for the protective layer is described in detail in, for example, US Pat. No. 3,458,311 and Japanese Patent Publication No. 55-49729.
さらに、本発明の平版印刷版原版における保護層には、酸素遮断性や感光層表面保護性を向上させる目的で、無機質の層状化合物を含有させることも好ましい。
ここで無機質の層状化合物とは、薄い平板状の形状を有する粒子であり、例えば、下記一般式
A(B,C)2-5 D4 O10(OH,F,O)2
〔ただし、AはK,Na,Caの何れか、BおよびCはFe(II),Fe(III),Mn,Al,Mg,Vの何れかであり、DはSiまたはAlである。〕で表される天然雲母、合成雲母等の雲母群、式3MgO・4SiO・H2Oで表されるタルク、テニオライ
ト、モンモリロナイト、サポナイト、ヘクトライト、りん酸ジルコニウムなどが挙げられる。
Furthermore, the protective layer in the lithographic printing plate precursor according to the invention preferably contains an inorganic stratiform compound for the purpose of improving oxygen barrier properties and photosensitive layer surface protection.
Here, the inorganic layered compound is a particle having a thin flat plate shape. For example, the following general formula A (B, C) 2-5 D 4 O 10 (OH, F, O) 2
[However, A is any one of K, Na, and Ca, B and C are any of Fe (II), Fe (III), Mn, Al, Mg, and V, and D is Si or Al. And mica groups such as natural mica and synthetic mica, talc, teniolite, montmorillonite, saponite, hectorite, zirconium phosphate and the like represented by the formula 3MgO.4SiO.H 2 O.
上記雲母群においては、天然雲母としては白雲母、ソーダ雲母、金雲母、黒雲母および鱗雲母が挙げられる。また、合成雲母としては、フッ素金雲母KMg3 (AlSi3O10
)F2、カリ四ケイ素雲母KMg2.5 Si4 O10)F2等の非膨潤性雲母、およびNaテトラシリリックマイカNaMg2.5 (Si4O10)F2、NaまたはLiテニオライト(Na,Li)Mg2 Li(Si4 O10)F2、モンモリロナイト系のNaまたはLiヘクトラ
イト(Na,Li)1/8 Mg2 /5Li1/8 (Si4O10)F2等の膨潤性雲母等が挙げられる。更に合成スメクタイトも有用である。
In the mica group, examples of natural mica include muscovite, soda mica, phlogopite, biotite and sericite. As the synthetic mica, fluorine phlogopite KMg 3 (AlSi 3 O 10
) F 2 , Potassium tetrasilicon mica KMg 2.5 Si 4 O 10 ) Non-swelling mica such as F 2 , and Na tetrasilicic mica NaMg 2.5 (Si 4 O 10 ) F 2 , Na or Li teniolite (Na, Li) Swelling mica such as Mg 2 Li (Si 4 O 10 ) F 2 , montmorillonite Na or Li hectorite (Na, Li) 1/8 Mg 2 / 5Li 1/8 (Si 4 O 10 ) F 2 Is mentioned. Synthetic smectite is also useful.
本発明においては、上記の無機質の層状化合物の中でも、合成の無機質の層状化合物であるフッ素系の膨潤性雲母が特に有用である。すなわち、この膨潤性合成雲母や、モンモリロナイト、サポナイト、ヘクトライト、ベントナイト等の膨潤性粘度鉱物類等は、10〜15A程度の厚さの単位結晶格子層からなる積層構造を有し、格子内金属原子置換が他の粘度鉱物より著しく大きい。その結果、格子層は正電荷不足を生じ、それを補償するために層間にNa+、Ca2+、Mg2+等の陽イオンを吸着している。これらの層間に介在し
ている陽イオンは交換性陽イオンと呼ばれ、いろいろな陽イオンと交換する。特に層間の陽イオンがLi+ 、Na+ の場合、イオン半径が小さいため層状結晶格子間の結合が弱く、水により大きく膨潤する。その状態でシェアーをかけると容易に劈開し、水中で安定したゾルを形成する。ベントナイトおよび膨潤性合成雲母はこの傾向が強く、本発明において有用であり、特に膨潤性合成雲母が好ましく用いられる。
In the present invention, among the inorganic layered compounds, fluorine-based swellable mica, which is a synthetic inorganic layered compound, is particularly useful. That is, this swellable synthetic mica and swellable viscosity minerals such as montmorillonite, saponite, hectorite, bentonite, etc. have a laminated structure composed of unit crystal lattice layers with a thickness of about 10-15A, Atomic substitution is significantly greater than other viscous minerals. As a result, the lattice layer is deficient in positive charges, and cations such as Na + , Ca 2+ and Mg 2+ are adsorbed between the layers in order to compensate for this. The cations present between these layers are called exchangeable cations and exchange with various cations. In particular, when the cation between the layers is Li + or Na + , the bond between the layered crystal lattices is weak because the ionic radius is small, and the layer swells greatly with water. If shear is applied in this state, it will easily cleave and form a stable sol in water. Bentonite and swellable synthetic mica have this tendency and are useful in the present invention, and swellable synthetic mica is particularly preferably used.
本発明で使用する無機質の層状化合物の形状としては、拡散制御の観点からは、厚さは薄ければ薄いほどよく、平面サイズは塗布面の平滑性や活性光線の透過性を阻害しない限りにおいて大きいほどよい。従って、アスペクト比は20以上であり、好ましくは100以上、特に好ましくは200以上である。なお、アスペクト比は粒子の長径に対する厚さの比であり、たとえば、粒子の顕微鏡写真による投影図から測定することができる。アスペクト比が大きい程、得られる効果が大きい。 As the shape of the inorganic layered compound used in the present invention, from the viewpoint of diffusion control, the smaller the thickness, the better. The plane size is as long as it does not hinder the smoothness of the coated surface or the transmittance of actinic rays. Larger is better. Accordingly, the aspect ratio is 20 or more, preferably 100 or more, particularly preferably 200 or more. The aspect ratio is the ratio of the thickness to the major axis of the particle, and can be measured, for example, from a projected view of the particle by a micrograph. The larger the aspect ratio, the greater the effect that can be obtained.
本発明で使用する無機質の層状化合物の粒子径は、その平均長径が0.3〜20μm、好ましくは0.5〜10μm、特に好ましくは1〜5μmである。また、該粒子の平均の厚さは、0.1μm以下、好ましくは、0.05μm以下、特に好ましくは、0.01μm以下である。例えば、無機質の層状化合物のうち、代表的化合物である膨潤性合成雲母
のサイズは厚さが1〜50nm、面サイズが1〜20μm程度である。
As for the particle diameter of the inorganic stratiform compound used in the present invention, the average major axis is 0.3 to 20 μm, preferably 0.5 to 10 μm, particularly preferably 1 to 5 μm. The average thickness of the particles is 0.1 μm or less, preferably 0.05 μm or less, particularly preferably 0.01 μm or less. For example, among inorganic layered compounds, the size of the swellable synthetic mica that is a representative compound is about 1 to 50 nm in thickness and about 1 to 20 μm in surface size.
このようにアスペクト比が大きい無機質の層状化合物の粒子を保護層に含有させると、塗膜強度が向上し、また、酸素や水分の透過を効果的に防止しうるため、変形などによる保護層の劣化を防止し、高湿条件下において長期間保存しても、湿度の変化による平版印刷版原版における画像形成性の低下もなく保存安定性に優れる。 When the inorganic layered compound particles having such a large aspect ratio are contained in the protective layer, the coating film strength is improved, and the permeation of oxygen and moisture can be effectively prevented. Deterioration is prevented, and even when stored for a long time under high-humidity conditions, the storage stability of the planographic printing plate precursor does not deteriorate due to changes in humidity, and the storage stability is excellent.
保護層中の無機質層状化合物の含有量は、保護層に使用されるバインダーの量に対し、質量比で5/1〜1/100であることが好ましい。複数種の無機質の層状化合物を併用した場合でも、これら無機質の層状化合物の合計量が上記の質量比であることが好ましい。 It is preferable that content of the inorganic stratiform compound in a protective layer is 5/1-1/100 by mass ratio with respect to the quantity of the binder used for a protective layer. Even when a plurality of types of inorganic layered compounds are used in combination, the total amount of these inorganic layered compounds is preferably the above-described mass ratio.
次に、保護層に用いる無機質層状化合物の一般的な分散方法の例について述べる。まず、水100質量部に先に無機質層状化合物の好ましいものとして挙げた膨潤性の層状化合物を5〜10質量部添加し、充分水になじませ、膨潤させた後、分散機にかけて分散する。ここで用いる分散機としては、機械的に直接力を加えて分散する各種ミル、大きな剪断力を有する高速攪拌型分散機、高強度の超音波エネルギーを与える分散機等が挙げられる。具体的には、ボールミル、サンドグラインダーミル、ビスコミル、コロイドミル、ホモジナイザー、ティゾルバー、ポリトロン、ホモミキサー、ホモブレンダー、ケディミル、ジェットアジター、毛細管式乳化装置、液体サイレン、電磁歪式超音波発生機、ポールマン笛を有する乳化装置等が挙げられる。上記の方法で分散した無機質層状化合物の5〜10質量%の分散物は高粘度あるいはゲル状であり、保存安定性は極めて良好である。この分散物を用いて保護層塗布液を調製する際には、水で希釈し、充分攪拌した後、バインダー溶液と配合して調製するのが好ましい。 Next, an example of a general dispersion method of the inorganic stratiform compound used for the protective layer will be described. First, 5 to 10 parts by mass of the swellable layered compound mentioned above as a preferred inorganic layered compound is added to 100 parts by mass of water, and the mixture is thoroughly swelled and swollen, and then dispersed by a disperser. Examples of the disperser used here include various mills that disperse mechanically by applying a direct force, a high-speed stirring disperser having a large shearing force, and a disperser that provides high-intensity ultrasonic energy. Specifically, ball mill, sand grinder mill, visco mill, colloid mill, homogenizer, tisol bar, polytron, homomixer, homo blender, ketdy mill, jet agitator, capillary emulsifier, liquid siren, electrostrictive ultrasonic generator, An emulsifying device having a Paulman whistle can be used. A dispersion of 5 to 10% by mass of the inorganic stratiform compound dispersed by the above method is highly viscous or gelled and has very good storage stability. When preparing a protective layer coating solution using this dispersion, it is preferably prepared by diluting with water and stirring sufficiently, and then blending with a binder solution.
この保護層塗布液には、上記無機質層状化合物の他に、塗布性を向上させための界面活性剤や皮膜の物性改良のための水溶性可塑剤などの公知の添加剤を加えることができる。水溶性の可塑剤としては、例えば、プロピオンアミド、シクロヘキサンジオール、グリセリン、ソルビトール等が挙げられる。また、水溶性の(メタ)アクリル系ポリマーを加えることもできる。さらに、この塗布液には、感光層との密着性、塗布液の経時安定性を向上するための公知の添加剤を加えてもよい。 In addition to the inorganic layered compound, known additives such as a surfactant for improving the coating property and a water-soluble plasticizer for improving the physical properties of the film can be added to the protective layer coating solution. Examples of the water-soluble plasticizer include propionamide, cyclohexanediol, glycerin, sorbitol and the like. A water-soluble (meth) acrylic polymer can also be added. Furthermore, known additives for improving the adhesion to the photosensitive layer and the temporal stability of the coating solution may be added to the coating solution.
このように調製された保護層塗布液を、支持体上に備えられた感光層の上に塗布し、乾燥して保護層を形成する。塗布溶剤はバインダーとの関連において適宜選択することができるが、水溶性ポリマーを用いる場合には、蒸留水、精製水を用いることが好ましい。保護層の塗布方法は、特に制限されるものではなく、米国特許第3,458,311号明細書または特公昭55−49729号公報に記載されている方法など公知の方法を適用することができる。具体的には、例えば、保護層は、ブレード塗布法、エアナイフ塗布法、グラビア塗布法、ロールコーティング塗布法、スプレー塗布法、ディップ塗布法、バー塗布法等が挙げられる。 The protective layer coating solution thus prepared is applied onto the photosensitive layer provided on the support and dried to form a protective layer. The coating solvent can be appropriately selected in relation to the binder, but when a water-soluble polymer is used, it is preferable to use distilled water or purified water. The method for applying the protective layer is not particularly limited, and a known method such as the method described in US Pat. No. 3,458,311 or Japanese Patent Publication No. 55-49729 can be applied. . Specific examples of the protective layer include blade coating, air knife coating, gravure coating, roll coating coating, spray coating, dip coating, and bar coating.
保護層の塗布量としては、乾燥後の塗布量で、0.05〜10g/m2 の範囲であることが好ましく、無機質の層状化合物を含有する場合には、0.1〜0.5g/m2の範囲
であることがさらに好ましく、無機質の層状化合物を含有しない場合には、0.5〜5g/m2の範囲であることがさらに好ましい。
The coating amount of the protective layer is preferably in the range of 0.05 to 10 g / m 2 in terms of the coating amount after drying. When the inorganic layered compound is contained, 0.1 to 0.5 g / The range of m 2 is more preferable, and when the inorganic layered compound is not contained, the range of 0.5 to 5 g / m 2 is more preferable.
〔支持体〕
本発明の平版印刷版原版に用いられる支持体は、特に限定されず、寸度的に安定な板状な親水性支持体であればよい。例えば、紙、プラスチック(例えば、ポリエチレン、ポリプロピレン、ポリスチレン等)がラミネートされた紙、金属板(例えば、アルミニウム、
亜鉛、銅等)、プラスチックフィルム(例えば、二酢酸セルロース、三酢酸セルロース、プロピオン酸セルロース、酪酸セルロース、酢酸酪酸セルロース、硝酸セルロース、ポリエチレンテレフタレート、ポリエチレン、ポリスチレン、ポリプロピレン、ポリカーボネート、ポリビニルアセタール等)、上述した金属がラミネートされまたは蒸着された紙またはプラスチックフィルム等が挙げられる。好ましい支持体としては、ポリエステルフィルムおよびアルミニウム板が挙げられる。中でも、寸法安定性がよく、比較的安価であるアルミニウム板が好ましい。
[Support]
The support used in the lithographic printing plate precursor according to the invention is not particularly limited as long as it is a dimensionally stable plate-like hydrophilic support. For example, paper, paper laminated with plastic (eg, polyethylene, polypropylene, polystyrene, etc.), metal plate (eg, aluminum,
Zinc, copper, etc.), plastic films (eg, cellulose diacetate, cellulose triacetate, cellulose propionate, cellulose butyrate, cellulose acetate butyrate, cellulose nitrate, polyethylene terephthalate, polyethylene, polystyrene, polypropylene, polycarbonate, polyvinyl acetal, etc.), as described above Examples thereof include a paper or plastic film on which the above-mentioned metal is laminated or vapor-deposited. Preferable supports include a polyester film and an aluminum plate. Among these, an aluminum plate that has good dimensional stability and is relatively inexpensive is preferable.
アルミニウム板は、純アルミニウム板、アルミニウムを主成分とし、微量の異元素を含む合金板、または、アルミニウムもしくはアルミニウム合金の薄膜にプラスチックがラミネートされているものである。アルミニウム合金に含まれる異元素には、ケイ素、鉄、マンガン、銅、マグネシウム、クロム、亜鉛、ビスマス、ニッケル、チタン等がある。合金中の異元素の含有量は10質量%以下であるのが好ましい。本発明においては、純アルミニウム板が好ましいが、完全に純粋なアルミニウムは精錬技術上製造が困難であるので、わずかに異元素を含有するものでもよい。アルミニウム板は、その組成が特定されるものではなく、公知公用の素材のものを適宜利用することができる。 The aluminum plate is a pure aluminum plate, an alloy plate containing aluminum as a main component and containing a trace amount of different elements, or a plastic laminated on a thin film of aluminum or an aluminum alloy. Examples of foreign elements contained in the aluminum alloy include silicon, iron, manganese, copper, magnesium, chromium, zinc, bismuth, nickel, and titanium. The content of foreign elements in the alloy is preferably 10% by mass or less. In the present invention, a pure aluminum plate is preferable, but completely pure aluminum is difficult to manufacture in terms of refining technology, and therefore may contain a slightly different element. The composition of the aluminum plate is not specified, and a publicly known material can be used as appropriate.
支持体の厚さは0.1〜0.6mmであるのが好ましく、0.15〜0.4mmであるのがより好ましく、0.2〜0.3mmであるのが更に好ましい。 The thickness of the support is preferably from 0.1 to 0.6 mm, more preferably from 0.15 to 0.4 mm, and even more preferably from 0.2 to 0.3 mm.
アルミニウム板を使用するに先立ち、粗面化処理、陽極酸化処理等の表面処理を施すのが好ましい。表面処理により、親水性の向上および感光層と支持体との密着性の確保が容易になる。アルミニウム板を粗面化処理するに先立ち、所望により、表面の圧延油を除去するための界面活性剤、有機溶剤、アルカリ性水溶液等による脱脂処理が行われる。 Prior to using the aluminum plate, it is preferable to perform a surface treatment such as roughening treatment or anodizing treatment. By the surface treatment, it becomes easy to improve hydrophilicity and secure adhesion between the photosensitive layer and the support. Prior to roughening the aluminum plate, a degreasing treatment with a surfactant, an organic solvent, an alkaline aqueous solution or the like for removing rolling oil on the surface is performed as desired.
アルミニウム板表面の粗面化処理は、種々の方法により行われるが、例えば、機械的粗面化処理、電気化学的粗面化処理(電気化学的に表面を溶解させる粗面化処理)、化学的粗面化処理(化学的に表面を選択溶解させる粗面化処理)が挙げられる。
機械的粗面化処理の方法としては、ボール研磨法、ブラシ研磨法、ブラスト研磨法、バフ研磨法等の公知の方法を用いることができる。
電気化学的粗面化処理の方法としては、例えば、塩酸、硝酸等の酸を含有する電解液中で交流または直流により行う方法が挙げられる。また、特開昭54−63902号公報に記載されているような混合酸を用いる方法も挙げられる。
The surface roughening treatment of the aluminum plate is performed by various methods. For example, mechanical surface roughening treatment, electrochemical surface roughening treatment (surface roughening treatment for dissolving the surface electrochemically), chemical treatment, etc. Surface roughening treatment (roughening treatment that chemically selectively dissolves the surface).
As a method for the mechanical surface roughening treatment, a known method such as a ball polishing method, a brush polishing method, a blast polishing method, or a buff polishing method can be used.
Examples of the electrochemical surface roughening treatment include a method in which an alternating current or a direct current is used in an electrolytic solution containing an acid such as hydrochloric acid or nitric acid. Another example is a method using a mixed acid as described in JP-A-54-63902.
粗面化処理されたアルミニウム板は、必要に応じて、水酸化カリウム、水酸化ナトリウム等の水溶液を用いてアルカリエッチング処理を施され、更に、中和処理された後、所望により、耐摩耗性を高めるために陽極酸化処理を施される。 The surface-roughened aluminum plate is subjected to an alkali etching treatment using an aqueous solution of potassium hydroxide, sodium hydroxide or the like, if necessary, further neutralized, and if desired, wear resistant. In order to increase the anodic oxidation treatment.
アルミニウム板の陽極酸化処理に用いられる電解質としては、多孔質酸化皮膜を形成させる種々の電解質の使用が可能である。一般的には、硫酸、塩酸、シュウ酸、クロム酸またはそれらの混酸が用いられる。それらの電解質の濃度は電解質の種類によって適宜決められる。
陽極酸化処理の条件は、用いられる電解質により種々変わるので一概に特定することはできないが、一般的には、電解質濃度1〜80質量%溶液、液温度5〜70℃、電流密度5〜60A/dm2 、電圧1〜100V、電解時間10秒〜5分であるのが好ましい。形
成される陽極酸化皮膜の量は、1.0〜5.0g/m2 であるのが好ましく、1.5〜4.0g/m2 であるのがより好ましい。この範囲内で、良好な耐刷性と平版印刷版の非画像部の良好な耐傷性が得られる。
As the electrolyte used for the anodizing treatment of the aluminum plate, various electrolytes that form a porous oxide film can be used. In general, sulfuric acid, hydrochloric acid, oxalic acid, chromic acid or a mixed acid thereof is used. The concentration of these electrolytes is appropriately determined depending on the type of electrolyte.
The conditions for anodizing treatment vary depending on the electrolyte used, and thus cannot be specified in general. In general, however, an electrolyte concentration of 1 to 80% by mass solution, a liquid temperature of 5 to 70 ° C., a current density of 5 to 60 A / dm 2 , voltage 1 to 100 V, and electrolysis time 10 seconds to 5 minutes are preferable. The amount of the anodized film formed is preferably from 1.0 to 5.0 g / m 2, and more preferably 1.5 to 4.0 g / m 2. Within this range, good printing durability and good scratch resistance of the non-image area of the lithographic printing plate can be obtained.
本発明で用いられる支持体としては、上記のような表面処理をされ陽極酸化皮膜を有す
る基板そのままでもよいが、上層との接着性、親水性、汚れ難さ、断熱性などの一層改良のため、必要に応じて、特開2001−253181号や特開2001−322365号の公報に記載されている陽極酸化皮膜のマイクロポアの拡大処理、マイクロポアの封孔処理、および親水性化合物を含有する水溶液に浸漬する表面親水化処理などを適宜選択して行うことができる。もちろんこれら拡大処理、封孔処理は、これらに記載のものに限られたものではなく従来公知の何れの方法も行うことができる。
As the support used in the present invention, the substrate having the above-mentioned surface treatment and having an anodized film may be used as it is, but for further improvement in adhesion to the upper layer, hydrophilicity, resistance to contamination, heat insulation and the like. If necessary, it contains a micropore enlargement treatment, a micropore sealing treatment, and a hydrophilic compound described in Japanese Patent Application Laid-Open Nos. 2001-253181 and 2001-322365. A surface hydrophilization treatment immersed in an aqueous solution can be selected as appropriate. Of course, these enlargement processing and sealing processing are not limited to those described above, and any conventionally known method can be performed.
封孔処理としては、蒸気封孔のほかフッ化ジルコン酸の単独処理、フッ化ナトリウムによる処理など無機フッ素化合物を含有する水溶液による封孔処理、塩化リチウムを添加した蒸気封孔、熱水による封孔処理でも可能である。
なかでも、無機フッ素化合物を含有する水溶液による封孔処理、水蒸気による封孔処理および熱水による封孔処理が好ましい。
Sealing treatment includes vapor sealing, single treatment with zirconic fluoride, treatment with an aqueous solution containing an inorganic fluorine compound such as treatment with sodium fluoride, vapor sealing with addition of lithium chloride, sealing with hot water. Hole processing is also possible.
Of these, sealing treatment with an aqueous solution containing an inorganic fluorine compound, sealing treatment with water vapor, and sealing treatment with hot water are preferable.
親水化処理としては、米国特許第2,714,066号、同第3,181,461号、同第3,280,734号および同第3,902,734号の明細書に記載されているようなアルカリ金属シリケート法がある。この方法においては、支持体をケイ酸ナトリウム等の水溶液で浸漬処理し、または電解処理する。そのほかに、特公昭36−22063号公報に記載されているフッ化ジルコン酸カリウムで処理する方法、米国特許第3,276,868号、同第4,153,461号および同第4,689,272号の明細書に記載されているようなポリビニルホスホン酸で処理する方法等が挙げられる。 The hydrophilization treatment is described in the specifications of US Pat. Nos. 2,714,066, 3,181,461, 3,280,734, and 3,902,734. There are such alkali metal silicate methods. In this method, the support is immersed in an aqueous solution such as sodium silicate or electrolytically treated. In addition, the treatment with potassium zirconate fluoride described in JP-B 36-22063, U.S. Pat. Nos. 3,276,868, 4,153,461 and 4,689, And a method of treating with polyvinylphosphonic acid as described in the specification of No. 272.
本発明の支持体としてポリエステルフィルムなど表面の親水性が不十分な支持体を用いる場合は、親水層を塗布して表面を親水性にすることが望ましい。親水層としては、特開2001−199175号公報に記載の、ベリリウム、マグネシウム、アルミニウム、珪素、チタン、硼素、ゲルマニウム、スズ、ジルコニウム、鉄、バナジウム、アンチモンおよび遷移金属から選択される少なくとも一つの元素の酸化物または水酸化物のコロイドを含有する塗布液を塗布してなる親水層や、特開2002−79772号公報に記載の、有機親水性ポリマーを架橋あるいは疑似架橋することにより得られる有機親水性マトリックスを有する親水層や、ポリアルコキシシラン、チタネート、ジルコネートまたはアルミネートの加水分解、縮合反応からなるゾル−ゲル変換により得られる無機親水性マトリックスを有する親水層、あるいは、金属酸化物を含有する表面を有する無機薄膜からなる親水層が好ましい。中でも、珪素の酸化物または水酸化物のコロイドを含有する塗布液を塗布してなる親水層が好ましい。 When using a support with insufficient surface hydrophilicity such as a polyester film as the support of the present invention, it is desirable to apply a hydrophilic layer to make the surface hydrophilic. As the hydrophilic layer, at least one element selected from beryllium, magnesium, aluminum, silicon, titanium, boron, germanium, tin, zirconium, iron, vanadium, antimony, and a transition metal described in JP-A-2001-199175 A hydrophilic layer formed by coating a coating solution containing a colloid of oxide or hydroxide, or organic hydrophilicity obtained by crosslinking or pseudo-crosslinking an organic hydrophilic polymer described in JP-A-2002-79772 A hydrophilic layer having a hydrophilic matrix, a hydrophilic layer having an inorganic hydrophilic matrix obtained by sol-gel conversion comprising hydrolysis, condensation reaction of polyalkoxysilane, titanate, zirconate or aluminate, or a metal oxide A hydrophilic layer made of an inorganic thin film having a surface is preferred. Arbitrariness. Of these, a hydrophilic layer formed by applying a coating solution containing a colloid of silicon oxide or hydroxide is preferable.
また、本発明の支持体としてポリエステルフィルム等を用いる場合には、支持体の親水性層側または反対側、あるいは両側に、帯電防止層を設けるのが好ましい。帯電防止層を支持体と親水性層との間に設けた場合には、親水性層との密着性向上にも寄与する。帯電防止層としては、特開2002−79772号公報に記載の、金属酸化物微粒子やマット剤を分散したポリマー層等が使用できる。 Moreover, when using a polyester film etc. as a support body of this invention, it is preferable to provide an antistatic layer in the hydrophilic layer side of a support body, the opposite side, or both sides. In the case where the antistatic layer is provided between the support and the hydrophilic layer, it also contributes to improving the adhesion with the hydrophilic layer. As the antistatic layer, a polymer layer in which metal oxide fine particles or a matting agent are dispersed as described in JP-A-2002-79772 can be used.
支持体は、中心線平均粗さが0.10〜1.2μmであるのが好ましい。この範囲内で、感光層との良好な密着性、良好な耐刷性と良好な汚れ難さが得られる。
また、支持体の色濃度としては、反射濃度値として0.15〜0.65であるのが好ましい。この範囲内で、画像露光時のハレーション防止による良好な画像形成性と現像後の良好な検版性が得られる。
The support preferably has a center line average roughness of 0.10 to 1.2 μm. Within this range, good adhesion to the photosensitive layer, good printing durability and good stain resistance can be obtained.
The color density of the support is preferably 0.15 to 0.65 as the reflection density value. Within this range, good image formability by preventing halation during image exposure and good plate inspection after development can be obtained.
〔バックコート層〕
支持体に表面処理を施した後または下塗り層を形成させた後、必要に応じて、支持体の裏面にバックコートを設けることができる。
バックコートとしては、例えば、特開平5−45885号公報に記載されている有機高
分子化合物、特開平6−35174号公報に記載されている有機金属化合物または無機金属化合物を加水分解および重縮合させて得られる金属酸化物からなる被覆層が好適に挙げられる。中でも、Si(OCH3 )4 、Si(OC2 H5 )4 、Si(OC3 H7 )4 、Si(OC4 H9 )4 等のケイ素のアルコキシ化合物を用いるのが、原料が安価で入手しやすい点で好ましい。
[Back coat layer]
After the surface treatment is performed on the support or after the undercoat layer is formed, a back coat can be provided on the back surface of the support, if necessary.
Examples of the back coat include hydrolysis and polycondensation of organic polymer compounds described in JP-A-5-45885, organometallic compounds or inorganic metal compounds described in JP-A-6-35174. A coating layer made of a metal oxide obtained in this manner is preferred. Among them, it is inexpensive to use a silicon alkoxy compound such as Si (OCH 3 ) 4 , Si (OC 2 H 5 ) 4 , Si (OC 3 H 7 ) 4 , Si (OC 4 H 9 ) 4. It is preferable in terms of easy availability.
〔製版方法〕
本発明における平版印刷版原版を、350nm〜450nmの光源で画像露光した後、自動現像機により、(C)バインダーの酸価が、0.3meq/g以下である場合は、pHが2〜10の現像液の存在下、擦り部材で版面を擦ることにより、非露光部の感光層を除去し、アルミニウム板支持体表面に画像を形成することができる。
すなわち、保護層がある場合は保護層および非露光部の感光層を一括除去した後、直ちに印刷機にセットして印刷することができる。
また、このような自動現像機での処理は、機上現像の場合に生ずる保護層/感光層に由来の現像カスへの対応から開放されるという優位性がある。
[Plate making method]
After the lithographic printing plate precursor according to the invention is subjected to image exposure with a light source of 350 nm to 450 nm, the pH is 2 to 10 when the acid value of the binder (C) is 0.3 meq / g or less by an automatic processor. By rubbing the plate surface with a rubbing member in the presence of the developer, the photosensitive layer in the non-exposed area can be removed and an image can be formed on the surface of the aluminum plate support.
That is, when there is a protective layer, the protective layer and the photosensitive layer in the non-exposed area can be removed and then immediately set in a printing press for printing.
In addition, such processing in an automatic developing machine has an advantage that it is freed from dealing with development residue derived from the protective layer / photosensitive layer that occurs in the case of on-press development.
本発明において用いられる現像液は、pHが2〜10の水溶液である。例えば、水単独または水を主成分(水を60質量%以上含有)とする水溶液が好ましく、特に、一般的に公知な湿し水と同様組成の水溶液、界面活性剤(アニオン系、ノニオン系、カチオン系等)を含有する水溶液や、水溶性高分子化合物を含有する水溶液が好ましい。特に、界面活性剤と水溶性高分子化合物の両方を含有する水溶液が好ましい。該現像液のpHは、より好ましくは3〜8、さらに好ましくは4〜7である。
尚、酸性〜中性の現像液を用いる場合は、有機酸或いは無機酸のいずれかを含有することが好ましい。有機酸或いは無機酸を含有させることにより、製版時には現像性を向上させることができ、また製版された印刷版の非画像部に汚れが発生するのを抑制することができる。
The developer used in the present invention is an aqueous solution having a pH of 2 to 10. For example, water alone or an aqueous solution containing water as a main component (containing 60% by mass or more of water) is preferable. An aqueous solution containing a cationic system or the like, or an aqueous solution containing a water-soluble polymer compound is preferable. In particular, an aqueous solution containing both a surfactant and a water-soluble polymer compound is preferable. The pH of the developer is more preferably 3-8, and even more preferably 4-7.
When an acidic to neutral developer is used, it is preferable to contain either an organic acid or an inorganic acid. By containing an organic acid or an inorganic acid, developability can be improved during plate making, and it is possible to suppress the occurrence of stains in the non-image area of the plate that has been made.
本発明の現像液に用いられるアニオン系界面活性剤としては、脂肪酸塩類、アビエチン酸塩類、ヒドロキシアルカンスルホン酸塩類、アルカンスルホン酸塩類、ジアルキルスルホコハク酸塩類、直鎖アルキルベンゼンスルホン酸塩類、分岐鎖アルキルベンゼンスルホン酸塩類、アルキルナフタレンスルホン酸塩類、アルキルフェノキシポリオキシエチレンプロピルスルホン酸塩類、ポリオキシエチレンアルキルスルホフェニルエーテル塩類、N−メチル−N−オレイルタウリンナトリウム類、N−アルキルスルホコハク酸モノアミド二ナトリウム塩類、石油スルホン酸塩類、硫酸化ヒマシ油、硫酸化牛脂油、脂肪酸アルキルエステルの硫酸エステル塩類、アルキル硫酸エステル塩類、ポリオキシエチレンアルキルエーテル硫酸エステル塩類、脂肪酸モノグリセリド硫酸エステル塩類、ポリオキシエチレンアルキルフェニルエーテル硫酸エステル塩類、ポリオキシエチレンスチリルフェニルエーテル硫酸エステル塩類、アルキル燐酸エステル塩類、ポリオキシエチレンアルキルエーテル燐酸エステル塩類、ポリオキシエチレンアルキルフェニルエーテル燐酸エステル塩類、スチレン−無水マレイン酸共重合物の部分ケン化物類、オレフィン−無水マレイン酸共重合物の部分ケン化物類、ナフタレンスルホン酸塩ホルマリン縮合物類等が挙げられる。これらの中でもジアルキルスルホコハク酸塩類、アルキル硫酸エステル塩類およびアルキルナフタレンスルホン酸塩類が特に好ましく用いられる。 Examples of the anionic surfactant used in the developer of the present invention include fatty acid salts, abietic acid salts, hydroxyalkane sulfonic acid salts, alkane sulfonic acid salts, dialkyl sulfosuccinic acid salts, linear alkyl benzene sulfonic acid salts, and branched alkyl benzene sulfonic acid. Acid salts, alkylnaphthalene sulfonates, alkylphenoxy polyoxyethylene propyl sulfonates, polyoxyethylene alkyl sulfophenyl ether salts, N-methyl-N-oleyl taurine sodium, N-alkyl sulfosuccinic acid monoamide disodium salts, petroleum Sulfonates, sulfated castor oil, sulfated beef tallow oil, sulfate esters of fatty acid alkyl esters, alkyl sulfate esters, polyoxyethylene alkyl ether sulfate esters, Fatty acid monoglyceride sulfates, polyoxyethylene alkylphenyl ether sulfates, polyoxyethylene styryl phenyl ether sulfates, alkyl phosphates, polyoxyethylene alkyl ether phosphates, polyoxyethylene alkylphenyl ether phosphates , Partially saponified products of styrene-maleic anhydride copolymer, partially saponified products of olefin-maleic anhydride copolymer, naphthalene sulfonate formalin condensate and the like. Among these, dialkyl sulfosuccinates, alkyl sulfate esters and alkyl naphthalene sulfonates are particularly preferably used.
本発明の現像液に用いられるカチオン系界面活性剤としては、特に限定されず、従来公知のものを用いることができる。例えば、アルキルアミン塩類、第四級アンモニウム塩類、ポリオキシエチレンアルキルアミン塩類、ポリエチレンポリアミン誘導体が挙げられる。 The cationic surfactant used in the developer of the present invention is not particularly limited, and conventionally known ones can be used. Examples thereof include alkylamine salts, quaternary ammonium salts, polyoxyethylene alkylamine salts, and polyethylene polyamine derivatives.
本発明の現像液に用いられるノニオン系界面活性剤としては、ポリエチレングリコール
型の高級アルコールエチレンオキサイド付加物、アルキルフェノールエチレンオキサイド付加物、脂肪酸エチレンオキサイド付加物、多価アルコール脂肪酸エステルエチレンオキサイド付加物、高級アルキルアミンエチレンオキサイド付加物、脂肪酸アミドエチレンオキサイド付加物、油脂のエチレンオキサイド付加物、ポリプロピレングリコールエチレンオキサイド付加物、ジメチルシロキサン−エチレンオキサイドブロックコポリマー、ジメチルシロキサン−(プロピレンオキサイド−エチレンオキサイド)ブロックコポリマー等や、多価アルコール型のグリセロールの脂肪酸エステル、ペンタエリスリトールの脂肪酸エステル、ソルビトールおよびソルビタンの脂肪酸エステル、ショ糖の脂肪酸エステル、多価アルコールのアルキルエーテル、アルカノールアミン類の脂肪酸アミド等が挙げられる。
これらノニオン性界面活系剤は、単独でも、2種以上を混合して用いても良い。本発明においては、ソルビトールおよび/またはソルビタン脂肪酸エステルのエチレンオキサイド付加物、ポリプロピレングリコールエチレンオキサイド付加物、ジメチルシロキサン−エチレンオキサイドブロックコポリマー、ジメチルシロキサン−(プロピレンオキサイド−エチレンオキサイド)ブロックコポリマー、多価アルコールの脂肪酸エステルがより好ましい。
Nonionic surfactants used in the developer of the present invention include polyethylene glycol type higher alcohol ethylene oxide adduct, alkylphenol ethylene oxide adduct, fatty acid ethylene oxide adduct, polyhydric alcohol fatty acid ester ethylene oxide adduct, higher Alkylamine ethylene oxide adduct, fatty acid amide ethylene oxide adduct, oil and fat ethylene oxide adduct, polypropylene glycol ethylene oxide adduct, dimethylsiloxane-ethylene oxide block copolymer, dimethylsiloxane- (propylene oxide-ethylene oxide) block copolymer, etc. , Fatty acid ester of glycerol of polyhydric alcohol type, fatty acid ester of pentaerythritol, sorbitol and Fatty acid esters of Rubitan, fatty acid esters of sucrose, alkyl ethers of polyhydric alcohols, fatty acid amides of alkanolamines.
These nonionic surfactants may be used alone or in admixture of two or more. In the present invention, ethylene oxide adduct of sorbitol and / or sorbitan fatty acid ester, polypropylene glycol ethylene oxide adduct, dimethylsiloxane-ethylene oxide block copolymer, dimethylsiloxane- (propylene oxide-ethylene oxide) block copolymer, polyhydric alcohol Fatty acid esters are more preferred.
また、水に対する安定な溶解性あるいは混濁性の観点から、本発明の現像液に使用するノニオン系界面活性剤としては、HLB(Hydorophile−Lipophile
Balance)値が、6以上であることが好ましく、8以上であることがより好ましい。さらに、現像液中に含有するノニオン性界面活性剤の比率は、0.01〜10質量%が好ましく、0.01〜5質量%がより好ましい。
またアセチレングリコール系とアセチレンアルコール系のオキシエチレン付加物、フッ素系、シリコン系等の界面活性剤も同様に使用することができる。
本発明の現像液に使用する界面活性剤としては、抑泡性の観点から、ノニオン性界面活性剤が特に好適である。
Further, from the viewpoint of stable solubility or turbidity in water, the nonionic surfactant used in the developer of the present invention is HLB (Hydrophile-Lipophile).
The (Balance) value is preferably 6 or more, and more preferably 8 or more. Furthermore, the ratio of the nonionic surfactant contained in the developer is preferably 0.01 to 10% by mass, and more preferably 0.01 to 5% by mass.
Also, acetylene glycol-based and acetylene alcohol-based oxyethylene adducts, fluorine-based and silicon-based surfactants can be used in the same manner.
As the surfactant used in the developer of the present invention, a nonionic surfactant is particularly suitable from the viewpoint of foam suppression.
また、本発明の現像液に用いられる水溶性高分子化合物としては、大豆多糖類、変性澱粉、アラビアガム、デキストリン、繊維素誘導体(例えばカルボキシメチルセルロース、カルボキシエチルセルロース、メチルセルロース等)およびその変性体、プルラン、ポリビニルアルコールおよびその誘導体、ポリビニルピロリドン、ポリアクリルアミドおよびアクリルアミド共重合体、ビニルメチルエーテル/無水マレイン酸共重合体、酢酸ビニル/無水マレイン酸共重合体、スチレン/無水マレイン酸共重合体などが挙げられる。 Examples of the water-soluble polymer compound used in the developer of the present invention include soybean polysaccharide, modified starch, gum arabic, dextrin, fibrin derivatives (eg, carboxymethylcellulose, carboxyethylcellulose, methylcellulose, etc.) and modified products thereof, pullulan. , Polyvinyl alcohol and its derivatives, polyvinyl pyrrolidone, polyacrylamide and acrylamide copolymer, vinyl methyl ether / maleic anhydride copolymer, vinyl acetate / maleic anhydride copolymer, styrene / maleic anhydride copolymer, etc. It is done.
上記大豆多糖類は、公知のものが使用でき、例えば市販品として商品名ソヤファイブ(不二製油(株)製)があり、各種グレードのものを使用することができる。好ましく使用できるものは、10質量%水溶液の粘度が10〜100mPa/secの範囲にあるものである。 A well-known thing can be used for the said soybean polysaccharide, for example, there exists a brand name Soya Five (made by Fuji Oil Co., Ltd.) as a commercial item, and the thing of various grades can be used. What can be preferably used is one in which the viscosity of a 10% by mass aqueous solution is in the range of 10 to 100 mPa / sec.
上記変性澱粉も、公知のものが使用でき、トウモロコシ、じゃがいも、タピオカ、米、小麦等の澱粉を酸または酵素等で1分子当たりグルコース残基数5〜30の範囲で分解し、更にアルカリ中でオキシプロピレンを付加する方法等で作ることができる。 As the modified starch, known ones can be used, and starch such as corn, potato, tapioca, rice and wheat is decomposed with acid or enzyme in the range of 5 to 30 glucose residues per molecule, and further in an alkali. It can be made by a method of adding oxypropylene or the like.
水溶性高分子化合物は2種以上を併用することもできる。水溶性高分子化合物の現像液中における含有量は、0.1〜20質量%が好ましく、より好ましくは0.5〜10質量
%である。
Two or more water-soluble polymer compounds can be used in combination. The content of the water-soluble polymer compound in the developer is preferably from 0.1 to 20% by mass, and more preferably from 0.5 to 10% by mass.
また、本発明の現像液には、有機溶剤を含有しても良い。含有可能な有機溶剤としては、例えば、脂肪族炭化水素類(ヘキサン、ヘプタン、”アイソパーE、H、G”(エッソ化学(株)製)あるいはガソリン、灯油等)、芳香族炭化水素類(トルエン、キシレン等)、あるいはハロゲン化炭化水素(メチレンジクロライド、エチレンジクロライド、トリクレン、モノクロルベンゼン等)や、極性溶剤が挙げられる。 Further, the developer of the present invention may contain an organic solvent. Examples of the organic solvent that can be contained include aliphatic hydrocarbons (hexane, heptane, “Isopar E, H, G” (manufactured by Esso Chemical Co., Ltd.) or gasoline, kerosene, etc.), and aromatic hydrocarbons (toluene). , Xylene, etc.), halogenated hydrocarbons (methylene dichloride, ethylene dichloride, tricrene, monochlorobenzene, etc.) and polar solvents.
極性溶剤としては、アルコール類(メタノール、エタノール、プロパノール、イソプロパノール、ベンジルアルコール、エチレングリコールモノメチルエーテル、2−エトキシエタノール、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノヘキシルエーテル、トリエチレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル、プロピレングリコールモノメチルエーテル、ポリエチレングリコールモノメチルエーテル、ポリプロピレングリコール、テトラエチレングリコール、エチレングリコールモノブチルエーテル、エチレングリコールモノベンジルエーテル、エチレングリコールモノフェニルエーテル、メチルフェニルカルビノール、n−アミルアルコール、メチルアミルアルコール等)、ケトン類(アセトン、メチルエチルケトン、エチルブチルケトン、メチルイソブチルケトン、シクロヘキサノン等)、エステル類(酢酸エチル、酢酸プロピル、酢酸ブチル、酢酸アミル、酢酸ベンジル、乳酸メチル、乳酸ブチル、エチレングリコールモノブチルアセテート、プロピレングリコールモノメチルエーテルアセテート、ジエチレングリコールアセテート、ジエチルフタレート、レブリン酸ブチル等)、その他(トリエチルフォスフェート、トリクレジルフォスフェート、N−フェニルエタノールアミン、N−フェニルジエタノールアミン等)等が挙げられる。 Polar solvents include alcohols (methanol, ethanol, propanol, isopropanol, benzyl alcohol, ethylene glycol monomethyl ether, 2-ethoxyethanol, diethylene glycol monoethyl ether, diethylene glycol monohexyl ether, triethylene glycol monomethyl ether, propylene glycol monoethyl ether , Propylene glycol monomethyl ether, polyethylene glycol monomethyl ether, polypropylene glycol, tetraethylene glycol, ethylene glycol monobutyl ether, ethylene glycol monobenzyl ether, ethylene glycol monophenyl ether, methylphenyl carbinol, n-amyl alcohol, methyl amyl alcohol, etc.) , (Acetone, methyl ethyl ketone, ethyl butyl ketone, methyl isobutyl ketone, cyclohexanone, etc.), esters (ethyl acetate, propyl acetate, butyl acetate, amyl acetate, benzyl acetate, methyl lactate, butyl lactate, ethylene glycol monobutyl acetate, propylene Glycol monomethyl ether acetate, diethylene glycol acetate, diethyl phthalate, butyl levulinate, etc.) and others (triethyl phosphate, tricresyl phosphate, N-phenylethanolamine, N-phenyldiethanolamine, etc.).
また、上記有機溶剤が水に不溶な場合は、界面活性剤等を用いて水に可溶化して使用することも可能であり、現像液に、有機溶剤を含有する場合は、安全性、引火性の観点から、溶剤の濃度は40質量%未満が望ましい。 If the organic solvent is insoluble in water, it can be used after being solubilized in water using a surfactant or the like. If the developer contains an organic solvent, safety, ignition, From the viewpoint of property, the concentration of the solvent is preferably less than 40% by mass.
本発明の現像液には上記の他に、防腐剤、キレート化合物、消泡剤、有機酸、無機酸、無機塩などを含有することができる。 In addition to the above, the developer of the present invention may contain a preservative, a chelate compound, an antifoaming agent, an organic acid, an inorganic acid, an inorganic salt, and the like.
防腐剤としては、フェノールまたはその誘導体、ホルマリン、イミダゾール誘導体、デヒドロ酢酸ナトリウム、4−イソチアゾリン−3−オン誘導体、ベンゾイソチアゾリン−3−オン、ベンズトリアゾール誘導体、アミジングアニジン誘導体、四級アンモニウム塩類、ピリジン、キノリン、グアニジン等の誘導体、ダイアジン、トリアゾール誘導体、オキサゾール、オキサジン誘導体、ニトロブロモアルコール系の2−ブロモ−2−ニトロプロパン−1,3ジオール、1,1−ジブロモ−1−ニトロ−2−エタノール、1,1−ジブロモ−1−ニトロ−2−プロパノール等が好ましく使用できる。 Preservatives include phenol or derivatives thereof, formalin, imidazole derivatives, sodium dehydroacetate, 4-isothiazolin-3-one derivatives, benzisothiazolin-3-one, benztriazole derivatives, amiding anidine derivatives, quaternary ammonium salts, pyridine, Derivatives such as quinoline and guanidine, diazine, triazole derivatives, oxazole, oxazine derivatives, nitrobromoalcohol-based 2-bromo-2-nitropropane-1,3diol, 1,1-dibromo-1-nitro-2-ethanol, 1,1-dibromo-1-nitro-2-propanol and the like can be preferably used.
キレート化合物としては、例えば、エチレンジアミンテトラ酢酸、そのカリウム塩、そのナトリウム塩;ジエチレントリアミンペンタ酢酸、そのカリウム塩、そのナトリウム塩;トリエチレンテトラミンヘキサ酢酸、そのカリウム塩、そのナトリウム塩、ヒドロキシエチルエチレンジアミントリ酢酸、そのカリウム塩、そのナトリウム塩;ニトリロトリ酢酸、そのナトリウム塩;1−ヒドロキシエタン−1,1−ジホスホン酸、そのカリウム塩、そのナトリウム塩;アミノトリ(メチレンホスホン酸)、そのカリウム塩、そのナトリウム塩などのような有機ホスホン酸類あるいはホスホノアルカントリカルボン酸類を挙げることができる。上記キレート剤のナトリウム塩、カリウム塩の代りに有機アミンの塩も有効である。 Examples of the chelate compound include ethylenediaminetetraacetic acid, potassium salt thereof, sodium salt thereof; diethylenetriaminepentaacetic acid, potassium salt thereof, sodium salt thereof; triethylenetetraminehexaacetic acid, potassium salt thereof, sodium salt thereof, hydroxyethylethylenediaminetriacetic acid Nitrilotriacetic acid, sodium salt; 1-hydroxyethane-1,1-diphosphonic acid, potassium salt, sodium salt; aminotri (methylenephosphonic acid), potassium salt, sodium salt And organic phosphonic acids and phosphonoalkanetricarboxylic acids. Organic amine salts are also effective in place of the sodium and potassium salts of the chelating agents.
消泡剤としては一般的なシリコン系の自己乳化タイプ、乳化タイプ、ノニオン系界面活性剤のHLBが5以下等の化合物を使用することができる。シリコン消泡剤が好ましい。
その中で乳化分散型および可溶化等がいずれも使用できる。
As the antifoaming agent, a general silicon-based self-emulsifying type, emulsifying type, or nonionic surfactant having a HLB of 5 or less can be used. Silicon antifoaming agents are preferred.
Among them, emulsification dispersion type and solubilization can be used.
有機酸としては、クエン酸、酢酸、蓚酸、マロン酸、サリチル酸、カプリル酸、酒石酸、リンゴ酸、乳酸、レブリン酸、p−トルエンスルホン酸、キシレンスルホン酸、フィチン酸、有機ホスホン酸などが挙げられる。有機酸は、そのアルカリ金属塩またはアンモニウム塩の形で用いることもできる。 Examples of organic acids include citric acid, acetic acid, succinic acid, malonic acid, salicylic acid, caprylic acid, tartaric acid, malic acid, lactic acid, levulinic acid, p-toluenesulfonic acid, xylenesulfonic acid, phytic acid, and organic phosphonic acid. . The organic acid can also be used in the form of its alkali metal salt or ammonium salt.
無機酸および無機塩としては、リン酸、メタリン酸、第一リン酸アンモニウム、第二リン酸アンモニウム、第一リン酸ナトリウム、第二リン酸ナトリウム、第一リン酸カリウム、第二リン酸カリウム、トリポリリン酸ナトリウム、ピロリン酸カリウム、ヘキサメタリン酸ナトリウム、硝酸マグネシウム、硝酸ナトリウム、硝酸カリウム、硝酸アンモニウム、硫酸ナトリウム、硫酸カリウム、硫酸アンモニウム、亜硫酸ナトリウム、亜硫酸アンモニウム、硫酸水素ナトリウム、硫酸ニッケルなどが挙げられる。 Examples of inorganic acids and inorganic salts include phosphoric acid, metaphosphoric acid, primary ammonium phosphate, secondary ammonium phosphate, primary sodium phosphate, secondary sodium phosphate, primary potassium phosphate, secondary potassium phosphate, Examples include sodium tripolyphosphate, potassium pyrophosphate, sodium hexametaphosphate, magnesium nitrate, sodium nitrate, potassium nitrate, ammonium nitrate, sodium sulfate, potassium sulfate, ammonium sulfate, sodium sulfite, ammonium sulfite, sodium hydrogen sulfate, nickel sulfate and the like.
上記の現像液は、露光されたネガ型平版印刷版原版の現像液および現像補充液として用いることができ、後述の自動処理機に適用することが好ましい。自動処理機を用いて現像する場合、処理量に応じて現像液が疲労してくるので、補充液または新鮮な現像液を用いて処理能力を回復させてもよい。本発明の平版印刷版の製版方法においてもこの補充方式が好ましく適用される。 The developer described above can be used as a developer and developer replenisher for the exposed negative lithographic printing plate precursor, and is preferably applied to an automatic processor described later. When developing using an automatic processor, the developing solution becomes fatigued according to the amount of processing, so the processing capability may be restored using a replenisher or a fresh developer. This replenishing method is also preferably applied to the lithographic printing plate making method of the present invention.
本発明におけるpH2〜10の水溶液による現像処理は、現像液の供給手段および擦り部材を備えた自動処理機により好適に実施することができる。自動処理機としては、例えば、画像記録後の平版印刷版原版を搬送しながら擦り処理を行う、特開平2−220061号、特開昭60−59351号各公報に記載の自動処理機や、シリンダー上にセットされた画像記録後の平版印刷版原版をシリンダーを回転させながら擦り処理を行う、米国特許5148746号、同5568768号、英国特許2297719号に記載の自動処理機等が挙げられる。なかでも、擦り部材として、回転ブラシロールを用いる自動処理機が特に好ましい。 The development treatment with an aqueous solution having a pH of 2 to 10 in the present invention can be preferably carried out by an automatic processor equipped with a developer supply means and a rubbing member. As an automatic processor, for example, an automatic processor described in JP-A-2-220061 and JP-A-60-59351, which performs a rubbing process while transporting a lithographic printing plate precursor after image recording, or a cylinder Examples thereof include an automatic processor described in US Pat. Nos. 5,148,746, 5,568,768 and British Patent 2,297,719, which rub the lithographic printing plate precursor after image recording set thereon while rotating a cylinder. Among these, an automatic processor using a rotating brush roll as the rubbing member is particularly preferable.
本発明に好ましく使用できる回転ブラシロールは、画像部の傷つき難さ、さらには、平版印刷版原版の支持体の腰の強さ等を考慮して適宜選択することができる。上記回転ブラシロールとしては、ブラシ素材をプラスチックまたは金属のロールに植え付けて形成された公知のものが使用できる。例えば、特開昭58−159533号公報や、特開平3−100554号公報記載のものや、実公昭62−167253号公報に記載されているような、ブラシ素材を列状に植え込んだ金属またはプラスチックの溝型材を芯となるプラスチックまたは金属のロールに隙間なく放射状に巻き付けたブラシロールが使用できる。
また、ブラシ素材としては、プラスチック繊維(例えば、ポリエチレンテレフタレート、ポリブチレンテレフタレート等のポリエステル系、ナイロン6.6、ナイロン6.10等のポリアミド系、ポリアクリロニトリル、ポリ(メタ)アクリル酸アルキル等のポリアクリル系、および、ポリプロピレン、ポリスチレン等のポリオレフィン系の合成繊維)を使用することができ、例えば、繊維の毛の直径は、20〜400μm、毛の長さは、5〜30mmのものが好適に使用できる。
さらに、回転ブラシロールの外径は、30〜200mmが好ましく、版面を擦るブラシの先端の周速は、0.1〜5m/secが好ましい。
また、回転ブラシロールは、2本以上の複数本用いることが好ましい。
The rotating brush roll that can be preferably used in the present invention can be appropriately selected in consideration of the difficulty of scratching the image area and the stiffness of the support of the lithographic printing plate precursor. As the rotating brush roll, a known one formed by planting a brush material on a plastic or metal roll can be used. For example, as described in Japanese Patent Application Laid-Open No. 58-159533, Japanese Patent Application Laid-Open No. 3-100554, or Japanese Utility Model Publication No. 62-167253, metal or plastic in which brush materials are implanted in rows. A brush roll can be used in which the groove mold material is radially wound around a plastic or metal roll as a core without a gap.
The brush material includes plastic fibers (for example, polyesters such as polyethylene terephthalate and polybutylene terephthalate, polyamides such as nylon 6.6 and nylon 6.10, polyacrylonitrile, poly (meth) acrylate, etc. Acrylic and polyolefin synthetic fibers such as polypropylene and polystyrene) can be used. For example, the fiber has a hair diameter of 20 to 400 μm and a hair length of 5 to 30 mm. Can be used.
Furthermore, the outer diameter of the rotating brush roll is preferably 30 to 200 mm, and the peripheral speed at the tip of the brush rubbing the plate surface is preferably 0.1 to 5 m / sec.
Moreover, it is preferable to use two or more rotating brush rolls.
本発明に用いる回転ブラシロールの回転方向は、本発明の平版印刷版原版の搬送方向に対し、同一方向であっても、逆方向であってもよいが、図1に例示した自動処理機のように、2本以上の回転ブラシロールを使用する場合は、少なくとも1本の回転ブラシロールが、同一方向に回転し、少なくとも1本の回転ブラシロールが、逆方向に回転することが好ましい。これにより、非画像部の感熱層の除去が、さらに確実となる。さらに、回転ブラシロールを、ブラシロールの回転軸方向に揺動させることも効果的である。 The rotating direction of the rotating brush roll used in the present invention may be the same or opposite to the conveying direction of the planographic printing plate precursor of the present invention. Thus, when two or more rotating brush rolls are used, it is preferable that at least one rotating brush roll rotates in the same direction and at least one rotating brush roll rotates in the opposite direction. This further ensures the removal of the heat sensitive layer in the non-image area. Furthermore, it is also effective to swing the rotating brush roll in the direction of the rotation axis of the brush roll.
上記現像液の温度は、任意の温度で使用できるが、好ましくは10℃〜50℃である。 Although the temperature of the developer can be used at any temperature, it is preferably 10 ° C to 50 ° C.
なお、本発明において、擦り処理後の平版印刷版を、引き続いて、水洗、乾燥処理、不感脂化処理することも任意に可能である。不感脂化処理では、公知の不感脂化液を用いることができる。 In the present invention, the lithographic printing plate after the rubbing treatment can be optionally washed with water, dried and desensitized. In the desensitizing treatment, a known desensitizing solution can be used.
その他、本発明の平版印刷版原版からの平版印刷版の製版プロセスとしては、必要に応じ、露光前、露光中、露光から現像までの間に、全面を加熱してもよい。この様な加熱により、該感光層中の画像形成反応が促進され、感度や耐刷性の向上や感度の安定化といった利点が生じ得る。さらに、画像強度・耐刷性の向上を目的として、現像後の画像に対し、全面後加熱もしくは全面露光を行う事も有効である。通常現像前の加熱は150℃以下の穏和な条件で行う事が好ましい。温度が高すぎると、非画像部迄がかぶってしまう等の問題を生じる。現像後の加熱には非常に強い条件を利用する。通常は100〜500℃の範囲である。温度が低いと十分な画像強化作用が得られず、高すぎる場合には支持体の劣化、画像部の熱分解といった問題を生じる。 In addition, as the plate-making process of the lithographic printing plate from the lithographic printing plate precursor according to the present invention, the entire surface may be heated before exposure, during exposure, and between exposure and development, if necessary. By such heating, the image forming reaction in the photosensitive layer is promoted, and advantages such as improvement in sensitivity and printing durability and stabilization of sensitivity may occur. Further, for the purpose of improving the image strength and printing durability, it is also effective to subject the developed image to full post heating or full exposure. Usually, the heating before development is preferably performed under a mild condition of 150 ° C. or less. If the temperature is too high, problems such as covering up to the non-image area occur. Very strong conditions are used for heating after development. Usually, it is the range of 100-500 degreeC. If the temperature is low, sufficient image strengthening action cannot be obtained. If the temperature is too high, problems such as deterioration of the support and thermal decomposition of the image area occur.
上記の現像処理に先立って、平版印刷版原版は、線画像、網点画像等を有する透明原画を通してレーザー露光するかデジタルデータによるレーザー光走査等で画像様に露光される。
望ましい光源の波長は350nmから450nmであり、具体的にはInGaN系半導体レーザーが好適である。露光機構は、内面ドラム方式、外面ドラム方式、フラットベッド方式等の何れでもよい。
Prior to the above development processing, the lithographic printing plate precursor is exposed imagewise by laser exposure through a transparent original image having a line image, a halftone dot image or the like, or by laser beam scanning by digital data.
A desirable wavelength of the light source is 350 nm to 450 nm, and specifically, an InGaN semiconductor laser is suitable. The exposure mechanism may be any of an internal drum system, an external drum system, a flat bed system, and the like.
350nm〜450nmの入手可能なレーザー光源としては以下のものを利用することができる。
ガスレーザとして、Arイオンレーザ(364nm、351nm、10mW〜1W)、Krイオンレーザ(356nm、351nm、10mW〜1W)、He−Cdレーザー(441nm、325nm、1mW〜100mW)、固体レーザーとして、Nd:YAG(YVO4)とSHG結晶×2回の組み合わせ(355nm、5mW〜1W)、Cr:LiSAFとSHG結晶の組み合わせ(430nm、10mW)、半導体レーザー系として、KNbO3リング共振器(430nm、30mW)、導波型波長変換素子とAlGaAs、InGaAs半導体の組み合わせ(380nm〜450nm、5mW〜100mW)、導波型波長変換素子とAlGaInP、AlGaAs半導体の組み合わせ(300nm〜350nm、5mW〜100mW)、AlGaInN(350nm〜450nm、5mW〜30mW)、その他、パルスレーザとしてN2レーザ(337nm、パルス0.1〜10mJ)、XeF(351nm、パルス10〜250mJ)。特にこの中でAlGaInN半導体レーザー(市販InGaN系半導体レーザー400〜410nm、5〜30mW)が波長特性、コストの面で好適である。
As available laser light sources of 350 nm to 450 nm, the following can be used.
As a gas laser, an Ar ion laser (364 nm, 351 nm, 10 mW to 1 W), a Kr ion laser (356 nm, 351 nm, 10 mW to 1 W), a He-Cd laser (441 nm, 325 nm, 1 mW to 100 mW), and a solid laser as Nd: YAG (YVO 4 ) and SHG crystal × 2 combinations (355 nm, 5 mW to 1 W), Cr: LiSAF and SHG crystal combination (430 nm, 10 mW), as a semiconductor laser system, KNbO 3 ring resonator (430 nm, 30 mW), Combination of waveguide type wavelength conversion element and AlGaAs / InGaAs semiconductor (380 nm to 450 nm, 5 mW to 100 mW), combination of waveguide type wavelength conversion element and AlGaInP, AlGaAs semiconductor (300 nm to 350 nm, 5 mW to 100 mW) ), AlGaInN (350 nm to 450 nm, 5 mW to 30 mW), N 2 laser (337 nm, pulse 0.1 to 10 mJ), XeF (351 nm, pulse 10 to 250 mJ) as a pulse laser. In particular, an AlGaInN semiconductor laser (commercially available InGaN-based semiconductor laser 400 to 410 nm, 5 to 30 mW) is preferable in terms of wavelength characteristics and cost.
また走査露光方式の平版印刷版露光装置としては、露光機構として内面ドラム方式、外面ドラム方式、フラットベッド方式があり、光源としては上記光源の中で連続発振可能なものが好ましく利用することができる。現実的には感材感度と製版時間の関係で、以下の露光装置が特に好ましい。
・内面ドラム方式で総出力20mW以上の半導体レーザーとなる様に、ガスレーザあるいは固体レーザー光源を1個以上使用するシングルビーム〜トリプルビームの露光装置
・フラットベッド方式で総出力20mW以上となる様に、半導体レーザー、ガスレーザあるいは固体レーザーを1個以上使用したマルチビーム(1〜10本)の露光装置
・外面ドラム方式で総出力20mW以上となる様に、半導体レーザー、ガスレーザあるいは固体レーザーを1個以上使用したマルチビーム(1〜9本)の露光装置
・外面ドラム方式で総出力20mW以上となる様に、半導体レーザーあるいは固体レーザーを1個以上使用したマルチビーム(10本以上)の露光装置
以上のようなレーザー直描型の平版印刷版においては、一般に感材感度X(J/cm2
)、感材の露光面積S(cm2)、レーザー光源1個のパワーq(W)、レーザー本数n
、全露光時間t(s)との間に式(eq 1)が成立する。
Further, as the lithographic printing plate exposure apparatus of the scanning exposure method, there are an inner drum method, an outer drum method, and a flat bed method as an exposure mechanism, and a light source that can continuously oscillate among the light sources can be preferably used. . Practically, the following exposure apparatus is particularly preferable in terms of the relationship between the photosensitive material sensitivity and the plate making time.
・ Single beam to triple beam exposure equipment that uses one or more gas lasers or solid-state laser light sources so that it becomes a semiconductor laser with a total output of 20 mW or more with an internal drum system. ・ A total output of 20 mW or more with a flat bed system. Multi-beam (1 to 10) exposure equipment that uses one or more semiconductor lasers, gas lasers, or solid-state lasers • Use one or more semiconductor lasers, gas lasers, or solid-state lasers to achieve a total output of 20 mW or more with the external drum system Multi-beam (1 to 9) exposure apparatus ・ Multi-beam (10 or more) exposure apparatus using one or more semiconductor lasers or solid-state lasers so that the total output is 20 mW or more by the external drum method In general, laser sensitive drawing type lithographic printing plates generally use photosensitive material sensitivity X (J / c m 2
), Exposure area S (cm 2 ) of photosensitive material, power q (W) of one laser light source, number of lasers n
The equation (eq 1) is established between the total exposure time t (s).
X・S=n・q・t (eq 1) X · S = n · q · t (eq 1)
i)内面ドラム(シングルビーム)方式の場合
レーザー回転数f(ラジアン/s)、感材の副走査長Lx(cm)、解像度Z(ドット/cm)、全露光時間t(s)の間には一般的に式(eq 2)が成立する。
i) In the case of the internal drum (single beam) system, the laser rotation speed f (radians / s), the sub-scanning length Lx (cm) of the photosensitive material, the resolution Z (dots / cm), and the total exposure time t (s) In general, equation (eq 2) holds.
f・Z・t=Lx (eq 2) f · Z · t = Lx (eq 2)
ii)外面ドラム(マルチビーム)方式の場合
ドラム回転数F(ラジアン/s)、感材の副走査長Lx(cm)、解像度Z(ドット/cm)、全露光時間t(s)、ビーム数(n)の間には一般的に式(eq 3)が成立する。
ii) External drum (multi-beam) system Drum rotation speed F (radians / s), photosensitive material sub-scanning length Lx (cm), resolution Z (dots / cm), total exposure time t (s), number of beams In general, formula (eq 3) is established during (n).
F・Z・n・t=Lx (eq 3) F.Z.n.t = Lx (eq 3)
iii)フラットヘッド(マルチビーム)方式の場合
ポリゴンミラーの回転数H(ラジアン/s)、感材の副走査長Lx(cm)、解像度Z(ドット/cm)、全露光時間t(s)、ビーム数(n)の間には一般的に式(eq 4)が成立する。
iii) Flat head (multi-beam) system Polygon mirror rotation speed H (radians / s), photosensitive material sub-scanning length Lx (cm), resolution Z (dots / cm), total exposure time t (s), Equation (eq 4) is generally established between the number of beams (n).
F・Z・n・t=Lx (eq 4) F.Z.n.t = Lx (eq 4)
実際の印刷版に要求される解像度(2560dpi)、版サイズ(A1/B1、副走査長42inch)、20枚/1時間程度の露光条件と本発明の平版印刷版原版の感光特性(感光波長、感度:約0.1mJ/cm2)を上記式に代入することで、本発明の平版印
刷版原版においては総出力20mW以上のレーザーを用いたマルチビーム露光方式との組み合わせが特に好ましいことが理解できる。さらに操作性、コスト等を掛け合わせることにより外面ドラム方式の半導体レーザーマルチビーム(10本以上)露光装置との組み合わせが最も好ましいことになる。
Resolution (2560 dpi) required for the actual printing plate, plate size (A1 / B1, sub-scan length 42 inch), exposure conditions of about 20 sheets / hour and photosensitive characteristics of the planographic printing plate precursor of the present invention (photosensitive wavelength, By substituting (sensitivity: about 0.1 mJ / cm 2 ) into the above formula, it is understood that a combination with a multi-beam exposure method using a laser having a total output of 20 mW or more is particularly preferable in the planographic printing plate precursor of the present invention. it can. Further, by combining operability, cost, etc., a combination with an external drum type semiconductor laser multi-beam (10 or more) exposure apparatus is most preferable.
以下、実施例により本発明を詳細に説明するが、本発明はこれらに限定されるものではない。 EXAMPLES Hereinafter, although an Example demonstrates this invention in detail, this invention is not limited to these.
〔支持体の作製〕
厚み0.3mmのアルミニウム板(材質1050)の表面の圧延油を除去するため、10質量%アルミン酸ソーダ水溶液を用いて50℃で30秒間、脱脂処理を施した後、毛径0.3mmの束植ナイロンブラシ3本とメジアン径25μmのパミス−水懸濁液(比重1.1g/cm3)を用いアルミニウム表面を砂目立てして、水でよく洗浄した。この板を45℃の25質量%水酸化ナトリウム水溶液に9秒間浸漬してエッチングを行い、水洗後、さらに60℃で20質量%硝酸水溶液に20秒間浸漬し、水洗した。この時の砂目立て表面のエッチング量は約3g/m2であった。
(Production of support)
In order to remove rolling oil on the surface of an aluminum plate (material 1050) having a thickness of 0.3 mm, a degreasing treatment was performed at 50 ° C. for 30 seconds using a 10 mass% sodium aluminate aqueous solution, and then the hair diameter was 0.3 mm. The aluminum surface was grained using three bundle-planted nylon brushes and a pumice-water suspension (specific gravity 1.1 g / cm 3 ) having a median diameter of 25 μm and washed thoroughly with water. This plate was etched by being immersed in a 25 mass% sodium hydroxide aqueous solution at 45 ° C for 9 seconds, washed with water, further immersed in a 20 mass% nitric acid aqueous solution at 60 ° C for 20 seconds, and washed with water. The etching amount of the grained surface at this time was about 3 g / m 2 .
次に、60Hzの交流電圧を用いて連続的に電気化学的な粗面化処理を行った。このときの電解液は、硝酸1質量%水溶液(アルミニウムイオンを0.5質量%含む)、液温50℃であった。交流電源波形は、電流値がゼロからピークに達するまでの時間TPが0.8msec、duty比1:1、台形の矩形波交流を用いて、カーボン電極を対極として電気化学的な粗面化処理を行った。補助アノードにはフェライトを用いた。電流密度は電流のピーク値で30A/dm2、補助陽極には電源から流れる電流の5%を分流させた。
硝酸電解における電気量はアルミニウム板が陽極時の電気量175C/dm2であった。
その後、スプレーによる水洗を行った。
Next, an electrochemical roughening treatment was performed continuously using an alternating voltage of 60 Hz. The electrolytic solution at this time was a 1% by mass nitric acid aqueous solution (containing 0.5% by mass of aluminum ions) and a liquid temperature of 50 ° C. The AC power source waveform is electrochemical roughening treatment using a trapezoidal rectangular wave alternating current with a time ratio TP of 0.8 msec until the current value reaches a peak from zero, a duty ratio of 1: 1, and a trapezoidal rectangular wave alternating current. Went. Ferrite was used for the auxiliary anode. The current density was 30 A / dm 2 at the peak current value, and 5% of the current flowing from the power source was shunted to the auxiliary anode.
The amount of electricity in the nitric acid electrolysis was 175 C / dm 2 when the aluminum plate was the anode.
Then, water washing by spraying was performed.
次に、塩酸0.5質量%水溶液(アルミニウムイオンを0.5質量%含む)、液温50℃の電解液にて、アルミニウム板が陽極時の電気量50C/dm2の条件で、硝酸電解と同様の方法で、電気化学的な粗面化処理を行い、その後、スプレーによる水洗を行った。この板を15質量%硫酸水溶液(アルミニウムイオンを0.5質量%含む)を電解液として電流密度15A/dm2で2.5g/m2の直流陽極酸化皮膜を設けた後、水洗、乾燥した。
このようにして得た支持体表面の中心線平均粗さRa(JIS B0601)を直径2μmの針を用いて測定したところ、0.51μmであった。
Next, a 0.5% by mass hydrochloric acid aqueous solution (containing 0.5% by mass of aluminum ions) and an electrolytic solution having a liquid temperature of 50 ° C. and nitric acid electrolysis under the condition of an electric quantity of 50 C / dm 2 when the aluminum plate is an anode. In the same manner as above, an electrochemical surface roughening treatment was performed, followed by washing with water by spraying. The plate was provided with a DC anodized film of 2.5 g / m 2 at a current density of 15 A / dm 2 using a 15% by mass sulfuric acid aqueous solution (containing 0.5% by mass of aluminum ions) as an electrolyte, then washed with water and dried. .
The centerline average roughness Ra (JIS B0601) of the surface of the support thus obtained was measured using a needle having a diameter of 2 μm and found to be 0.51 μm.
更に、下記下塗り液(1)をバー塗布した後、80℃、10秒オーブン乾燥し、乾燥塗布量が10mg/m2の下塗り層を有する支持体を作製した。 Further, the following undercoat liquid (1) was bar-coated and then oven-dried at 80 ° C. for 10 seconds to prepare a support having an undercoat layer having a dry coating amount of 10 mg / m 2 .
<下塗り液(1)>
・下塗り化合物(1) 0.017g
・メタノール 9.00g
・水 1.00g
<Undercoat liquid (1)>
・ Undercoat compound (1) 0.017 g
・ Methanol 9.00 g
・ Water 1.00g
下塗り化合物(1)組成比(モル比)=上記繰り返し単位の左:30、中央:30、右:40。質量平均分子量=40000 Undercoat compound (1) Composition ratio (molar ratio) = left of the above repeating unit: 30, center: 30, right: 40. Mass average molecular weight = 40000
〔平版印刷版原版(1)の作製〕
上記の下塗り層を付与した支持体上に、下記組成の感光層塗布液(1)をバー塗布した後、70℃、60秒でオーブン乾燥し、乾燥塗布量1.1g/m2の感光層を形成し、この上に下記組成よりなる保護層塗布液(1)を、乾燥塗布量が0.75g/m2となるよう
にバーを用いて塗布した後、125℃、70秒間乾燥して平版印刷版原版(1)を得た。
[Preparation of lithographic printing plate precursor (1)]
A photosensitive layer coating solution (1) having the following composition was bar coated on the support provided with the undercoat layer, followed by oven drying at 70 ° C. for 60 seconds, and a photosensitive layer having a dry coating amount of 1.1 g / m 2 . A protective layer coating solution (1) having the following composition is applied on the substrate using a bar so that the dry coating amount is 0.75 g / m 2, and then dried at 125 ° C. for 70 seconds. A lithographic printing plate precursor (1) was obtained.
<感光層塗布液(1)>
・下記バインダーポリマー(1)(平均分子量8万、酸価0meq/g)
0.54g
・重合性化合物 0.40g
イソシアヌール酸EO変性トリアクリレート
(東亜合成(株)製、アロニックスM−315)
・重合性化合物
エトキシ化トリメチロールプロパントリアクリレート 0.08g
(日本化薬(株)製、SR9035、EO付加モル数15、分子量1000)
・下記増感色素(1) 0.06g
・下記重合開始剤(1) 0.18g
・下記連鎖移動剤(1) 0.07g
・ε―フタロシアニン顔料の分散物 0.40g
(顔料:15質量部、分散剤 バインダーポリマー(1):10質量部、溶剤 シクロヘキサノン/メトキシプロピルアセテート/1−メトキシ−2−プロパノール=15質量部/20質量部/40質量部)
・熱重合禁止剤 0.01g
N−ニトロソフェニルヒドロキシルアミンアルミニウム塩
・下記水溶性フッ素系界面活性剤(1) 0.001g
・ポリオキシエチレン−ポリオキシプロピレン縮合物 0.04g
(旭電化工業(株)製、プルロニックL44)
・テトラエチルアミン塩酸塩 0.01g
・1−メトキシ−2−プロパノール 3.5g
・メチルエチルケトン 8.0g
<Photosensitive layer coating solution (1)>
・ The following binder polymer (1) (average molecular weight 80,000, acid value 0 meq / g)
0.54g
・ Polymerizable compound 0.40g
Isocyanuric acid EO-modified triacrylate (manufactured by Toa Gosei Co., Ltd., Aronix M-315)
・ Polymerizable compound Ethoxylated trimethylolpropane triacrylate 0.08 g
(Nippon Kayaku Co., Ltd., SR9035, EO addition mole number 15, molecular weight 1000)
・ The following sensitizing dye (1) 0.06 g
・ The following polymerization initiator (1) 0.18 g
・ The following chain transfer agent (1) 0.07 g
・ 0.40 g of ε-phthalocyanine pigment dispersion
(Pigment: 15 parts by mass, dispersant Binder polymer (1): 10 parts by mass, solvent cyclohexanone / methoxypropyl acetate / 1-methoxy-2-propanol = 15 parts by mass / 20 parts by mass / 40 parts by mass)
・ Thermal polymerization inhibitor 0.01g
N-nitrosophenylhydroxylamine aluminum salt ・ The following water-soluble fluorosurfactant (1) 0.001 g
・ Polyoxyethylene-polyoxypropylene condensate 0.04g
(Asahi Denka Kogyo Co., Ltd., Pluronic L44)
・ Tetraethylamine hydrochloride 0.01g
・ 3.5 g of 1-methoxy-2-propanol
・ Methyl ethyl ketone 8.0g
保護層塗布液(1)
ポリビニルアルコール(ケン化度98モル%、重合度500) 40g
ポリビニルピロリドン(分子量5万) 5g
ポリ(ビニルピロリドン/酢酸ビニル(1/1))分子量7万 0.5g
界面活性剤(エマレックス710、日本エマルジョン(株)製) 0.5g
水 950g
Protective layer coating solution (1)
Polyvinyl alcohol (saponification degree 98 mol%, polymerization degree 500) 40 g
Polyvinylpyrrolidone (molecular weight 50,000) 5g
Poly (vinyl pyrrolidone / vinyl acetate (1/1)) molecular weight 70,000 0.5g
Surfactant (Emalex 710, manufactured by Nippon Emulsion Co., Ltd.) 0.5g
950g of water
〔平版印刷版原版(2)〜(14)の作製〕
平版印刷版原版(1)の下塗り液(1)における下塗り化合物(1)を、上記(D)共重合体の説明の欄で例示した(D)共重合体2)〜14)に各々代える以外は、平版印刷版原版(1)と同様にして、平版印刷版原版(2)〜(14)を得た。
[Preparation of lithographic printing plate precursors (2) to (14)]
Except for substituting the undercoat compound (1) in the undercoat liquid (1) of the lithographic printing plate precursor (1) with the (D) copolymers 2) to 14) exemplified in the above description of the (D) copolymer. Obtained lithographic printing plate precursors (2) to (14) in the same manner as lithographic printing plate precursor (1).
共重合体2)〜14)における各繰り返し単位のモル比、重量平均分子量は、表1に示すとおりである。 The molar ratio and weight average molecular weight of each repeating unit in the copolymers 2) to 14) are as shown in Table 1.
〔比較用平版印刷版原版(1)の作製〕
平版印刷版原版(1)の下塗り液(1)における下塗り化合物(1)を、下記比較用下塗り化合物(1)に代える以外は、平版印刷版原版(1)と同様にして、比較用平版印刷版原版(1)を得た。
[Preparation of comparative planographic printing plate precursor (1)]
Comparative lithographic printing is performed in the same manner as the lithographic printing plate precursor (1) except that the undercoat compound (1) in the undercoat liquid (1) of the lithographic printing plate precursor (1) is replaced with the following comparative undercoat compound (1). An original plate (1) was obtained.
〔実施例1〜14及び比較例1〕
(1)露光、現像および印刷
上記平版印刷版原版(1)〜(14)及び比較用平版印刷版原版(1)各々について、出力100mWの405nm半導体レーザーを用いて、エネルギー密度を変えて画像様露
光を行った。
その後、下記組成の現像液(1)をリン酸と水酸化ナトリウムを用いてpH5.5に調整し、図1に示す構造の自動現像処理機にて、現像処理を実施した。自動現像処理機は、回転ブラシロールを2本有する自動処理機であり、回転ブラシロールとしては、1本目のブラシロールに、ポリブチレンテレフタレート製の繊維(毛の直径200μm、毛の長さ17mm)を植え込んだ外径90mmのブラシロールを用い、搬送方向と同一方向に毎分200回転(ブラシの先端の周速0.94m/sec)させ、2本目のブラシロールには、ポリブチレンテレフタレート製の繊維(毛の直径200μm、毛の長さ17mm)を植え込んだ外径60mmのブラシロールを用い、搬送方向と反対方向に毎分200回転(ブラシの先端の周速0.63m/sec)させた。平版印刷版原版の搬送は、搬送速度100cm/minで行った。
現像液は、循環ポンプによりスプレーパイプからシャワーリングして、版面に供給した。現像液のタンク容量は、10リットルであった。
[Examples 1 to 14 and Comparative Example 1]
(1) Exposure, development, and printing For each of the above lithographic printing plate precursors (1) to (14) and the comparative lithographic printing plate precursor (1), using a 405 nm semiconductor laser with an output of 100 mW, changing the energy density to form an image Exposure was performed.
Thereafter, the developer (1) having the following composition was adjusted to pH 5.5 using phosphoric acid and sodium hydroxide, and developed with an automatic developing processor having a structure shown in FIG. The automatic processor is an automatic processor having two rotating brush rolls. As the rotating brush roll, the first brush roll and the polybutylene terephthalate fiber (hair diameter 200 μm, hair length 17 mm). Using a brush roll with an outer diameter of 90 mm implanted with 200 mm / min in the same direction as the conveying direction (peripheral speed 0.94 m / sec at the tip of the brush), the second brush roll is made of polybutylene terephthalate Using a brush roll having an outer diameter of 60 mm in which fibers (hair diameter: 200 μm, hair length: 17 mm) were planted, it was rotated 200 times per minute in the direction opposite to the conveying direction (peripheral speed of the brush tip: 0.63 m / sec). . The planographic printing plate precursor was transported at a transport speed of 100 cm / min.
The developer was showered from the spray pipe with a circulation pump and supplied to the plate surface. The tank capacity of the developer was 10 liters.
現像液(1)
・水 100g
・アルキルナフタレンスルホン酸ナトリウム 5g
(花王(株)製ペレックスNB−L)
・アラビアガム 1g
・第1リン酸アンモニウム 0.05g
・2−ヒドロキシプロピルスターチ 1g
・クエン酸 0.05g
・エチレンジアミンテトラアセテート4ナトリウム塩 0.05g
Developer (1)
・ Water 100g
・ Sodium alkylnaphthalenesulfonate 5g
(Perox NB-L manufactured by Kao Corporation)
・ 1g gum arabic
・ Primary ammonium phosphate 0.05g
・ 2-hydroxypropyl starch 1g
・ Citric acid 0.05g
・ Ethylenediaminetetraacetate tetrasodium salt 0.05g
次いで、現像後の平版印刷版を、ハイデルベルグ社製印刷機SOR−Mに取り付け、湿し水(EU−3(富士写真フイルム(株)製エッチ液)/水/イソプロピルアルコール=1/89/10(容量比))とTRANS−G(N)墨インキ(大日本インキ化学工業(株)製)とを用い、毎時6000枚の印刷速度で印刷を行った。 Subsequently, the developed lithographic printing plate is attached to a printing machine SOR-M manufactured by Heidelberg, and dampening water (EU-3 (Etchi solution manufactured by Fuji Photo Film Co., Ltd.) / Water / isopropyl alcohol = 1/89/10. (Capacity ratio)) and TRANS-G (N) black ink (manufactured by Dainippon Ink & Chemicals, Inc.) were used for printing at a printing speed of 6000 sheets per hour.
(2)評価
上記平版印刷版原版について、平版印刷版の現像性、汚れ防止性、放置汚れ防止性、耐刷性を下記のように評価した。
(2) Evaluation With respect to the above lithographic printing plate precursor, the developability, stain resistance, neglected stain resistance and printing durability of the planographic printing plate were evaluated as follows.
<現像性>
平版印刷版原版を上記の通り露光、現像し、得られた平版印刷版の非画像部を目視確認し、感光層の残存の有無を下記の基準で評価した。
○:残膜なし
△:わずかに残膜
×:残膜あり
<Developability>
The lithographic printing plate precursor was exposed and developed as described above, the non-image area of the obtained lithographic printing plate was visually confirmed, and the presence or absence of the remaining photosensitive layer was evaluated according to the following criteria.
○: No remaining film △: Slightly remaining film ×: With remaining film
<汚れ性・耐刷性>
上記の通り印刷を行ったところ、印刷枚数の増加と共に徐々に画像部が磨耗しインキ受容性が低下するため、印刷用紙におけるインキ濃度が低下した。インキ濃度(反射濃度)が印刷開始よりも0.1低下したときの印刷枚数により、耐刷性を評価した。またこの際、非画像部の汚れの有無を目視にて評価した。
◎:汚れが全く見られない
○:汚れがほとんど見られない
△:わずかに汚れが見られる
×:汚れがはっきりと見られる
<Stain and printing durability>
When printing was performed as described above, as the number of printed sheets increased, the image area was gradually worn out and the ink receptivity was lowered, so that the ink density in the printing paper was lowered. Printing durability was evaluated based on the number of printed sheets when the ink density (reflection density) was reduced by 0.1 from the start of printing. At this time, the presence or absence of dirt on the non-image area was visually evaluated.
◎: No dirt is seen at all ○: Little dirt is seen △: Slight dirt is seen ×: The dirt is clearly seen
<放置汚れ防止性>
1万枚印刷した後、版を1時間放置し、その後、再度印刷を開始して、非画像部のブランケットの汚れを目視で評価した。放置汚れ防止性をブランケットの汚れの程度が少ない方から、◎、○、△、×の4段階で評価した。結果を表2に示す。
◎:汚れが全く見られない
○:汚れがほとんど見られない
△:わずかに汚れが見られる
×:汚れがはっきりと見られる
<Leaving dirt prevention>
After printing 10,000 sheets, the plate was allowed to stand for 1 hour, after which printing was started again, and the blanket in the non-image area was visually evaluated. The ability to prevent neglected stains was evaluated in four grades, ◎, ○, Δ, and ×, starting from the one with less dirt on the blanket. The results are shown in Table 2.
◎: No dirt is seen at all ○: Little dirt is seen △: Slight dirt is seen ×: The dirt is clearly seen
表2に示す結果から明らかなように、本発明における特定の(D)共重合体を用いる平版印刷版原版は、比較例に比べて、現像性、汚れ性、耐刷性、放置汚れ防止性に優れていることが明らかである。 As is clear from the results shown in Table 2, the lithographic printing plate precursor using the specific (D) copolymer in the present invention has developability, stain resistance, printing durability, and anti-stain properties as compared with the comparative examples. It is clear that this is superior.
1:回転ブラシロール
2:受けロール
3:搬送ロール
4:搬送ガイド板
5:スプレーパイプ
6:管路
7:フィルター
8:給版台
9:排版台
10:現像液タンク
11:循環ポンプ
12:版
1: rotating brush roll 2: receiving roll 3: transport roll 4: transport guide plate 5: spray pipe 6: pipeline 7: filter 8: plate supply table 9: plate discharge table 10: developer tank 11: circulation pump 12: plate
Claims (7)
前記支持体と接する前記感光層またはその他の層が、前記(C)成分とは異なる(D)成分として、下記一般式(D1)で示される繰り返し単位を有する共重合体を含有する平版印刷版原版。
式(D1)中、A 1 は下記式(A1)で示される繰り返し単位を表し、A 2 は下記式(A2)で示される繰り返し単位を表し、A 3 は下記式(A3)で示される繰り返し単位を表し、x、y、zは共重合比を表し、xは1〜80モル%、yは1〜80モル%、zは10〜95モル%である。
式(A1)中、R 101 、R 102 は水素原子、メチル基またはエチル基を表し、R 103 は水素原子、メチル基、−CH 2 −OHまたは−CH 2 −O−CO−(C1〜4アルキル)を表し、R 104 は水素原子、メチル基、−CH 2 −OH、−CH 2 −O−CO−(C1〜4アルキル)、−CO−O−(C1〜4アルキル)または−CO−NH−(C1〜4アルキル)を表し、R 105 、R 106 は水素原子、メチル基またはエチル基を表し、R 107 はメチル基、エチル基またはベンジル基を表し、L 101 は、−CO−O−L0−、−CO−NH−L0−、−二価の芳香族基−または−二価の芳香族基−L0−を表し、L0は二価の脂肪族基、二価の芳香族基またはこれらの組み合わせを表し、L 102 は、以下のLa〜Lqのいずれかを表し、
La:−L0−O−CO−
Lb:−L0−NH−CO−
Lc:−L0−O−
Ld:−L0−CO−O−
Le:−L0−O−CO−O−
Lf:−L0−O−CH 2 −
Lg:−L0−CO−O−CH 2 −
Lh:−L0−O−CO−O−CH 2 −
Li:−L0−O−CO−NH−L0−O−CO−
Lj:−L0−O−CO−L0−O−CO−
Lk:−L0−O−CO−L0−NH−CO−
Ll:−L0−CO−O−L0−O−CO−
Lm:−L0−CO−O−L0−NH−CO−
Ln:−L0−二価の芳香族基−
Lo:−O−CO−二価の芳香族基−
Lp:−O−CO−L0−二価の芳香族基−
Lq:−CO−O−二価の芳香族基−
Lr:−CO−O−L0−二価の芳香族基−
m 101 は0〜3の整数を表し、m 102 は1〜3の整数を表し、m 101 +m 102 =3を満たし、m 101 が2以上のとき、複数のR 107 は同じでも異なっていても良く、m 102 が2以上のとき、複数のR 104 〜R 106 、L 102 はそれぞれ同じでも異なっていても良く、m 102 ×n 101 の値は1〜6であり、X 101 −は−CO 2 −、−PO 3 H−、−O−PO 3 H−または−SO 3 −を表し、Y 101 はn 101 価の炭化水素残基であり、脂肪族、芳香族どちらの構造を含んでも良く、直鎖状、分岐状、環状のどの構造を含んでも良く、環状の場合は単環、多環いずれでも良く、また、炭化水素を構成する炭素−炭素原子に−CO−、−O−、−S−、−N(R 109 )−、−SO 2 −およびそれらの組み合わせからなる構造で中断されていても良く、R 109 は水素原子、メチル基、エチル基、n−プロピル基、i−プロピル基、n−ブチル基またはフェニル基を表す。
The lithographic printing plate wherein the photosensitive layer or other layer in contact with the support contains a copolymer having a repeating unit represented by the following general formula (D1) as a component (D) different from the component (C) Original edition.
Wherein (D1), A 1 represents a repeating unit represented by the following formula (A1), A 2 represents a repeating unit represented by the following formula (A2), repeat A 3 is represented by the following formula (A3) A unit is represented, x, y, z represents a copolymerization ratio, x is 1-80 mol%, y is 1-80 mol%, z is 10-95 mol%.
In formula (A1), R 101 and R 102 represent a hydrogen atom, a methyl group or an ethyl group, and R 103 represents a hydrogen atom, a methyl group, —CH 2 —OH or —CH 2 —O—CO— (C 1 to 4 Alkyl), R 104 represents a hydrogen atom, a methyl group, —CH 2 —OH, —CH 2 —O—CO— (C1-4 alkyl), —CO—O— (C1-4 alkyl) or —CO—. NH— (C1-4 alkyl) is represented, R 105 and R 106 represent a hydrogen atom, a methyl group or an ethyl group, R 107 represents a methyl group, an ethyl group or a benzyl group, and L 101 represents —CO—O. -L0-, -CO-NH-L0-, -divalent aromatic group- or -divalent aromatic group -L0-, wherein L0 is a divalent aliphatic group, divalent aromatic group or represent combinations thereof, L 102 represents one of the following La~Lq,
La: -L0-O-CO-
Lb: -L0-NH-CO-
Lc: -L0-O-
Ld: -L0-CO-O-
Le: -L0-O-CO-O-
Lf: -L0-O-CH 2 -
Lg: -L0-CO-O- CH 2 -
Lh: -L0-O-CO- O-CH 2 -
Li: -L0-O-CO-NH-L0-O-CO-
Lj: -L0-O-CO-L0-O-CO-
Lk: -L0-O-CO-L0-NH-CO-
Ll: -L0-CO-O-L0-O-CO-
Lm: -L0-CO-O-L0-NH-CO-
Ln: -L0-divalent aromatic group-
Lo: —O—CO—divalent aromatic group—
Lp: -O-CO-L0-divalent aromatic group-
Lq: —CO—O—divalent aromatic group—
Lr: -CO-O-L0-divalent aromatic group-
m 101 represents an integer of 0 to 3, m 102 represents an integer of 1 to 3, satisfying m 101 + m 102 = 3, and when m 101 is 2 or more, a plurality of R 107 may be the same or different. well, when m 102 is 2 or more, plural R 104 ~R 106, L 102 may be the same or different from each value of m 102 × n 101 is 1 to 6, X 101 - is -CO 2 -, - PO 3 H - , - O-PO 3 H- or -SO 3 - represents, Y 101 is a hydrocarbon residue of 101 valence n, it may include aliphatic, aromatic either structure , May include any of linear, branched, and cyclic structures, and in the case of a cyclic structure, it may be monocyclic or polycyclic, and the carbon-carbon atom constituting the hydrocarbon may be —CO—, —O—, -S -, - N (R 109 ) -, - SO 2 - and may be interrupted by a structure consisting of combinations, R 109 is a hydrogen atom Methyl group, ethyl group, n- propyl group, an i- propyl, n- butyl group or a phenyl group.