JP5061997B2 - Hydraulic transfer film and hydraulic transfer body - Google Patents
Hydraulic transfer film and hydraulic transfer body Download PDFInfo
- Publication number
- JP5061997B2 JP5061997B2 JP2008086278A JP2008086278A JP5061997B2 JP 5061997 B2 JP5061997 B2 JP 5061997B2 JP 2008086278 A JP2008086278 A JP 2008086278A JP 2008086278 A JP2008086278 A JP 2008086278A JP 5061997 B2 JP5061997 B2 JP 5061997B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- film
- hydraulic transfer
- curable resin
- transfer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、深み感や色あいなどにおいて天然材料を再現できるような、意匠性の高い水圧転写フィルムに関する。 The present invention relates to a hydraulic transfer film having high designability that can reproduce a natural material in a sense of depth and color.
水圧転写法は、水溶性もしくは水膨潤性の樹脂からなる支持体フィルムと意匠性を付与する転写層を有する水圧転写フィルムを、支持体フィルムを下方にして水面に浮かべ、通常活性化剤と呼ばれる有機溶剤を噴霧して転写層を柔軟化させた後、被転写体をその上方から押し付けながら水中に沈めることにより、転写層を被転写体に転写する方法である。
水圧転写法は、意匠性を付与する転写層の柄を選択することにより、金属、あるいはプラスチック等からなる複雑な三次元立体形状を有する成型品に、任意の絵柄を均一に綺麗に付与することができる。
最近では、トップコート層となる硬化性樹脂層と装飾層とが一体となった転写層を有する水圧転写フィルムも開発されており(例えば、特許文献1参照。)、1回の転写工程で、被転写体にトップコート層と装飾層とを付与することができる。
In the hydraulic transfer method, a hydraulic transfer film having a support film made of a water-soluble or water-swellable resin and a transfer layer imparting designability is floated on the water surface with the support film facing downward, and is usually called an activator. In this method, the organic layer is sprayed to soften the transfer layer, and then the transfer layer is transferred to the transfer target by being submerged in water while pressing the transfer target from above.
In the hydraulic transfer method, any pattern can be uniformly and neatly imparted to a molded product having a complicated three-dimensional shape made of metal or plastic by selecting the pattern of the transfer layer that imparts design properties. Can do.
Recently, a hydraulic transfer film having a transfer layer in which a curable resin layer serving as a topcoat layer and a decorative layer are integrated has also been developed (see, for example, Patent Document 1). A topcoat layer and a decorative layer can be provided on the transfer object.
一方、木目柄意匠等の天然材料柄は従来より好まれる意匠であり、これらの意匠を付与できる水圧転写フィルムや水圧転写法が知られている。
例えば、被転写体の表面に濃色系パターンから成る第一の転写層を有し、この第一の転写層の上に木目模様のパターンから成る第二の転写層を有し、且つ第二の転写層には真珠光沢顔料が分散しており、該真珠光沢顔料が第一の転写層のインクや素地の色と互いに干渉して発色し、また深み感、照り感を生じて第二の転写層の転写パターンの質感を向上させた水圧転写体が知られている。(例えば特許文献2参照)
また、光輝性顔料が練り込まれた樹脂基材から成形された成形品本体と前記成型品本体の表面に施された石目模様、木目模様、砂目模様、カーボン調模様又は抽象模様の液圧転写層とから成っており、天然材料に近く、且つ高度の立体感や光輝感をもたせた樹脂成型品が知られている(例えば特許文献3参照)
しかし特許文献2に記載の方法は、転写工程を少なくとも2回必要とするため、製造過程が煩雑であった。また、特許文献3に記載の方法は、樹脂基材に直接光輝性顔料を練り込んだ特定の樹脂から製造された被転写体しか使用することができず、汎用的ではないといった問題があった。
On the other hand, natural material patterns such as wood grain pattern designs are designs that have been favored in the past, and hydraulic transfer films and hydraulic transfer methods that can impart these designs are known.
For example, a first transfer layer having a dark color pattern is provided on the surface of a transfer target, a second transfer layer having a woodgrain pattern is provided on the first transfer layer, and a second transfer layer is provided. A pearlescent pigment is dispersed in the transfer layer, and the pearlescent pigment is colored by interfering with the color of the ink and the base of the first transfer layer, and also produces a feeling of depth and shine. There is known a hydraulic transfer body in which the texture of the transfer pattern of the transfer layer is improved. (For example, see Patent Document 2)
Further, a molded product body molded from a resin base material in which a glitter pigment is kneaded, and a liquid of a grain pattern, a wood grain pattern, a grain pattern, a carbon tone pattern or an abstract pattern applied to the surface of the molded article body There is known a resin molded product which is composed of a pressure transfer layer and is close to a natural material and has a high degree of three-dimensional feeling and glitter (for example, see Patent Document 3).
However, since the method described in Patent Document 2 requires a transfer process at least twice, the manufacturing process is complicated. In addition, the method described in Patent Document 3 has a problem that it can only be used for a transfer object manufactured from a specific resin in which a bright pigment is directly kneaded into a resin base material, and is not versatile. .
本発明が解決しようとする課題は、深み感や色あいなどの視認性において天然材料、特に木目柄を再現できるような、意匠性の高い水圧転写フィルムを提供することにある。 The problem to be solved by the present invention is to provide a hydraulic transfer film having a high design property capable of reproducing a natural material, in particular, a wood grain pattern, in terms of visibility such as a sense of depth and hue.
本発明者らは、装飾層に使用するインキとして光輝性顔料を含むインキを使用し、複数色使用する各々のインキに含まれる光輝性顔料の反射色を各々変えることで、深み感や色あいなどにおいて天然材料を再現することができ、本発明の課題を解決した。
木目柄で特に珍重される本杢は、独特の「照り感」を有する。この「照り感」は、光を受けた細胞内部からの反射や散乱によって生まれるため、「深み」を感じ、さらに、見る角度によって変化して見えるものであり、天然木だけに見られる現象である。
この「照り感」と「深み感」があることにより、人の目には、天然材料により近い意匠であると感じることから、従来、「照り感」を表現するために、パール顔料などの光輝性顔料を用いた印刷版を、転写後、木目柄の下になるように印刷するなどして、「深み感」を表現してきた。
本発明者らは、これを水圧転写体で再現するために、異なる反射色の光輝性顔料を、転写層の深さ方向に異なる位置で各々存在、あるいは重ね合わせることで、「照り感」を再現し、見る角度を変えると、あたかも「照り感」が変化したように感じる天然材料に近い視認性を有する水圧転写体が得られることを見出した。
The present inventors use an ink containing a bright pigment as the ink used for the decoration layer, and change the reflection color of the bright pigment contained in each ink used in a plurality of colors, thereby providing a sense of depth, hue, etc. The natural material can be reproduced in the above, and the problem of the present invention has been solved.
Honkan, which is especially prized for its wood grain pattern, has a unique “shine”. This “shine” is born by reflection and scattering from the inside of cells that receive light, so it feels “deep” and changes depending on the viewing angle, and is a phenomenon seen only in natural wood. .
Because of this “shine” and “deepness”, human eyes feel that the design is closer to natural materials, and so far, radiance such as pearl pigments has been used to express “shine”. A printing plate using a conductive pigment has been printed so as to be under a wood grain pattern after transfer, etc., to express a “feel of depth”.
In order to reproduce this with a hydraulic transfer body, the present inventors have different reflection colors of luster pigments at different positions in the depth direction of the transfer layer, or by superimposing each other, thereby providing a “shine feeling”. It was found that when the reproduction angle was changed and the viewing angle was changed, a hydraulic transfer body having visibility close to that of a natural material that felt as if the “light feeling” had changed was obtained.
即ち本発明は、水溶性もしくは水膨潤性の樹脂からなる支持体フィルムと、前記支持体フィルム上に設けた有機溶剤に溶解可能な転写層を有し、前記転写層が少なくとも、単層もしくは複数層からなる印刷層と、活性エネルギー線照射と加熱のどちらか一方またはその両方で硬化可能な硬化性樹脂層とを有する水圧転写用フィルムであって、前記単層もしくは複数層からなる印刷層の少なくとも1層及び前記硬化性樹脂層に光輝性顔料を含み、且つ該光輝性顔料を含む少なくとも2層の反射色が異なる水圧転写用フィルムを提供する。 That is, the present invention has a support film made of a water-soluble or water-swellable resin and a transfer layer that can be dissolved in an organic solvent provided on the support film, and the transfer layer is at least a single layer or a plurality of layers. A hydraulic transfer film having a printing layer comprising a layer and a curable resin layer curable by active energy ray irradiation and / or heating, wherein the printing layer comprises a single layer or a plurality of layers. Provided is a hydraulic transfer film comprising a glitter pigment in at least one layer and the curable resin layer, and at least two layers including the glitter pigment having different reflection colors.
また本発明は、前記記載の水圧転写用フィルムを、前記支持体フィルムを下にして水に浮かべ、活性化剤により前記転写層を活性化し、前記転写層を被転写体に転写し、前記支持体フィルムを除去し、転写層を乾燥し、前記転写層を活性エネルギー線照射と加熱の少なくとも一種で硬化させた水圧転写体を提供する。 The present invention also provides the hydraulic transfer film described above, wherein the support film is floated on water, the transfer layer is activated by an activator, the transfer layer is transferred to a transfer target, and the support is transferred. A hydraulic transfer body in which the body film is removed, the transfer layer is dried, and the transfer layer is cured by at least one of irradiation with active energy rays and heating is provided.
本発明により、深み感や色あいなどの視認性において本物を再現できるような、意匠性の高い水圧転写フィルムを提供することができる。 According to the present invention, it is possible to provide a hydraulic transfer film with high designability that can reproduce the real thing in visibility such as a sense of depth and hue.
(水圧転写フィルム) (Hydraulic transfer film)
(支持体フィルム)
本発明で使用する水圧転写用フィルムに用いる支持体フィルムは、水溶性もしくは水膨潤性の樹脂から成るフィルムである。
水溶性もしくは水膨潤性の樹脂から成る樹脂としては、例えば、ポリビニルアルコール(PVA)、ポリビニルピロリドン、アセチルセルロース、ポリアクリルアミド、アセチルブチルセルロース、ゼラチン、にかわ、アルギン酸ナトリウム、ヒドロキシエチルセルロース、カルボキシメチルセルロース等が使用できる。なかでも一般に水圧転写用フィルムとして用いられているPVAフィルムが水に溶解し易く、入手が容易で、硬化性樹脂層の印刷にも適しており、特に好ましい。これらの樹脂層は単層でも多層でも良く、層厚みは10〜200μm程度が好ましい。
(Support film)
The support film used for the hydraulic transfer film used in the present invention is a film made of a water-soluble or water-swellable resin.
Examples of resins comprising water-soluble or water-swellable resins include polyvinyl alcohol (PVA), polyvinyl pyrrolidone, acetyl cellulose, polyacrylamide, acetyl butyl cellulose, gelatin, glue, sodium alginate, hydroxyethyl cellulose, carboxymethyl cellulose, etc. it can. Among them, a PVA film generally used as a hydraulic transfer film is particularly preferable because it is easily dissolved in water, easily available, and suitable for printing a curable resin layer. These resin layers may be a single layer or multiple layers, and the layer thickness is preferably about 10 to 200 μm.
(光輝性顔料)
本発明で使用する光輝性顔料は、後述の印刷層及び後述の硬化性樹脂層の少なくとも2層に添加される。使用する光輝性顔料としては、市販の、光輝性を有する顔料であれば特に限定なく使用することが可能である。例えば、メルク社製のIriodin100、200、300、500、7000シリーズ、colorstreamシリーズ、xirallicシリーズ、miravalシリーズ等;日本光研社製のPEARL−GLAZEシリーズ、ULTIMICAシリーズ、PROMINENCEシリーズ等;BASF社製のDESERT REFLECTIONSシリーズ、TIMICAシリーズ、FLAMENCOシリーズ、CLOISONNEシリーズ、DUOCROMEシリーズ、GEMTONEシリーズ、CELLINIシリーズ、MEARLMAIDシリーズ、REFLECKSシリーズ、CHROMA−LITEシリーズ、COSMICAシリーズ等があげられる。
該光輝性顔料は、通常インキとして印刷できる程度の粒径であればよく、例えばグラビア印刷法で行う場合には粒径が200μm以下であればよく、グラビア印刷の版の大きさから、100μm以下が好ましい。
これらの光輝性顔料は、単独で使用してもよいし、複数を混合して使用してもよい。本発明は、前記印刷層及び前記硬化性樹脂層の少なくとも2層が光輝性顔料を含み、且つ該光輝性顔料を含む少なくとも2層の反射色が異なることが特徴であるが、このときの反射色を調整するために、複数の光輝性顔料を混合し調色することは好ましい。例えば、ゴールド色の光輝性顔料とシルバー色の光輝性顔料を混合し、中間色を調整することも可能である。
(Bright pigment)
The glitter pigment used in the present invention is added to at least two layers of a printing layer described later and a curable resin layer described later. As the glitter pigment to be used, any commercially available pigment having glitter can be used without particular limitation. For example, Iriodin100, 200, 300, 500, 7000 series, colorstream series, xiallic series, miraval series, etc. manufactured by Merck & Co .; PEARL-GLAZE series, ULTIMICA series, PROMINENCE series, etc. manufactured by Nihon Koken; DESRT manufactured by BASF Examples include the REFLECTIONS series, TIMICA series, FLAMENCO series, CLOISONE series, DUOCROME series, GEMTONE series, CELLINI series, MEARLMID series, REFLECKS series, CHROMA-LITE series, COSMICA series, and the like.
The glitter pigment only needs to have a particle size that can be printed as a normal ink. For example, when the gravure printing method is used, the particle size may be 200 μm or less, and 100 μm or less from the size of the gravure printing plate. Is preferred.
These glitter pigments may be used alone or in combination. The present invention is characterized in that at least two layers of the printed layer and the curable resin layer contain a bright pigment, and the reflection color of at least two layers containing the bright pigment is different. In order to adjust the color, it is preferable to mix a plurality of bright pigments and perform toning. For example, a neutral color can be adjusted by mixing a gold-colored glitter pigment and a silver-colored glitter pigment.
(反射色)
本発明において反射色は、前記光輝性顔料を含む印刷層または硬化性樹脂層を、測色計にて測定し、表色系CIE L*a*b*で表した。(但しL*はCIE1976明度を表し、a*、b*はクロマティクネス指数(色相と彩度を示す色度)を表す。)
またその反射色の差はΔE*abで表した。
本発明においては、測色値の測定をコニカミノルタ社製の分光測色計CM3500dを使用し、視野設定10度、D65光源の条件で反射測定(正反射光除去)を行なった。
(Reflective color)
In the present invention, the reflected color is represented by the color system CIE L * a * b * by measuring the printed layer or curable resin layer containing the glitter pigment with a colorimeter. (However, L * represents CIE 1976 brightness, and a * and b * represent chromaticness index (chromaticity indicating hue and saturation).)
The difference in reflected color is represented by ΔE * ab.
In the present invention, the colorimetric value was measured using a spectrocolorimeter CM3500d manufactured by Konica Minolta, Inc., and reflection measurement (regular reflection light removal) was performed under the conditions of a visual field setting of 10 degrees and a D65 light source.
(転写層 装飾層)
本発明で使用する水圧転写用フィルムが有する転写層において、前記装飾層は、少なくとも1層の前記光輝性顔料を含む印刷層からなる。なおここでいう「1層の印刷層」とは、1つのインキを1つの版により刷って得られる単色層を指す。例えば装飾層が4色のインキで構成された多色刷りで得られる場合、(本発明でいうところの)印刷層は4層であると表現される。
(Transfer layer decoration layer)
In the transfer layer of the hydraulic transfer film used in the present invention, the decorative layer is composed of a printed layer containing at least one glittering pigment. Here, “one printed layer” refers to a single color layer obtained by printing one ink on one plate. For example, when the decorative layer is obtained by multicolor printing composed of four colors of ink, the printing layer (as referred to in the present invention) is expressed as four layers.
本発明においては、光輝性顔料を含む印刷層の印刷順序等に特に制限はない。例えば、最も被転写体に近い印刷層を、全面を光輝性顔料入りのインキで全面(網点ならば100%)を印刷したベタ版とし、最も被転写体に遠い印刷層を光輝性顔料入りの柄版とし、各々の印刷層の間は顔料入りの柄版とした少なくとも3層の印刷層からなる装飾層としてもよいし、また、最も被転写体に近い印刷層に光輝性顔料を含むインキでベタ版を印刷し、次に光輝性顔料を含むインキで木目柄を重ねて印刷した後、汎用の顔料を含むインキを複数柄印刷した後、最も硬化性樹脂層に近い印刷層となる層に、光輝性顔料を含むインキで柄印刷して、4〜5層の印刷層としてもよい。特に柄が木目柄の場合は、本杢感を出すために、多色刷りの5層のうち少なくとも3層が各々反射色の異なる光輝性顔料を含むことが望ましい。
1層の印刷層が含有する光輝性顔料は、特に限定はなく通常インキとして使用する量でよい。具体的には例えば、対塗膜固形分比として5〜40%が好ましく使用される。
In the present invention, there is no particular limitation on the printing order of the printing layer containing the glitter pigment. For example, the printed layer closest to the transfer target is a solid plate with the entire surface printed with ink containing a glitter pigment (100% if halftone dot), and the print layer farthest from the transfer target is filled with a bright pigment. It may be a decorative layer consisting of at least three printed layers in the form of a pigmented pattern plate between each printed layer, and the printed layer closest to the transfer material contains a bright pigment. After printing a solid plate with ink, and then printing with multiple patterns of ink containing general-purpose pigments after printing with a grain pattern overlaid with ink containing glittering pigment, it becomes the printed layer closest to the curable resin layer A pattern may be printed on the layer with ink containing a luster pigment to form a printed layer of 4 to 5 layers. In particular, when the pattern is a wood grain pattern, it is desirable that at least three of the five layers of multicolor printing contain glitter pigments having different reflection colors in order to give a real feeling.
The glitter pigment contained in one printing layer is not particularly limited and may be used in an amount usually used as ink. Specifically, for example, 5 to 40% is preferably used as the coating film solid content ratio.
装飾層においては、前記光輝性顔料の他、汎用の無機、有機顔料を使用することができる。無機顔料としては例えば、白色顔料の亜鉛華(酸化亜鉛)、鉛白、リトポン、酸化チタン等、体質顔料の沈降性硫酸バリウム、バライト粉等、赤色顔料の鉛丹、弁柄等、黄色顔料の黄鉛(クロムイエロー)、亜鉛黄(ジンククロメート、ジンクイエロー)、カドミウムイエロー、ニッケルチタンイエロー、ストロンチウムクロメート等、緑色顔料のヴィリジアン、オキサイド・オブ・クロミウム等、青色顔料の群青(ウルトラマリン)、紺青(プルシアンブルー)、コバルトブルー等、黒色顔料のカーボンブラック等、金色や銀色に使われるアルミニウム粉等の合成無機顔料、褐色顔料のアンバーやシェンナ等、白または無色の炭酸カルシウム、無色のカオリン(粘土)等、パール顔料の白色雲母(マイカ)等の天然鉱物顔料、灰色顔料のジルコングレー等、黄色顔料のプラセオジムイエロー、クロムチタンイエロー等、緑色顔料のクロムグリーン、ピーコック、ビクトリアグリーン等、青色顔料の紺青、ターコイズブルー等、桃色顔料のクロムスズピンク、陶試紅、サーモンピンク等のセラミック顔料等が挙げられる。
また、有機顔料としては、たとえば、キナクリドン系顔料、フタロシアニン系顔料、スレン系顔料、ペリレン系顔料、フタロン系顔料、ジオキサジン系顔料、イソインドリノン系顔料、メチン・アゾメチン系顔料、ジケトピロロピロール系顔料、アゾレーキ顔料系顔料、不溶性アゾ系顔料、縮合アゾ系顔料等が挙げられる。
これらの汎用の顔料は、インキとして印刷できる程度の粒径であればよく、例えばグラビア印刷法で行う場合には1μm以下が一般的である。
1層の印刷層が含有する汎用の顔料は、特に限定はなく通常インキとして使用する量でよい。具体的には例えば、対塗膜固形分比として3〜30%が好ましく使用される。
また、前記汎用の顔料は、色合いを調整する目的で前記光輝性顔料と適宜混合することも可能である。
In the decorative layer, general-purpose inorganic and organic pigments can be used in addition to the glitter pigment. Examples of inorganic pigments include white pigments such as zinc white (zinc oxide), lead white, lithopone, and titanium oxide, body pigments such as precipitated barium sulfate and barite powder, red pigments such as red lead and petals, and yellow pigments. Yellow lead (chrome yellow), zinc yellow (zinc chromate, zinc yellow), cadmium yellow, nickel titanium yellow, strontium chromate, etc., green pigment viridian, oxide of chromium, etc. Blue pigment ultramarine, bitumen (Prussian blue), cobalt blue, etc., black pigment carbon black, etc., synthetic inorganic pigments such as aluminum powder used in gold and silver, brown pigment amber and senna, white or colorless calcium carbonate, colorless kaolin (clay ), Natural mineral pigments such as white mica (pearl mica), gray pigment di Ceramics such as congray, yellow pigments praseodymium yellow, chrome titanium yellow, green pigments chrome green, peacock, victoria green, blue pigments bitumen, turquoise blue, pink pigments chrome tin pink, ceramic red, and salmon pink And pigments.
Examples of organic pigments include quinacridone pigments, phthalocyanine pigments, selenium pigments, perylene pigments, phthalone pigments, dioxazine pigments, isoindolinone pigments, methine / azomethine pigments, and diketopyrrolopyrrole pigments. Examples thereof include pigments, azo lake pigments, insoluble azo pigments, and condensed azo pigments.
These general-purpose pigments only have to have a particle size that can be printed as ink. For example, when the gravure printing method is used, the particle size is generally 1 μm or less.
The general-purpose pigment contained in one printing layer is not particularly limited, and may be an amount used as a normal ink. Specifically, for example, 3 to 30% is preferably used as the solid content ratio to the coating film.
The general-purpose pigment can be appropriately mixed with the glitter pigment for the purpose of adjusting the hue.
また、インキに含有されるワニス用樹脂は、例えば、アクリル樹脂系、ポリウレタン樹脂系、ポリエステル樹脂系、ビニル樹脂系(塩ビ、酢ビ、塩ビ−酢ビ共重合樹脂)、塩素化オレフィン樹脂系、エチレン−アクリル樹脂系、石油系樹脂系、セルロース誘導体樹脂系などの公知のインキを用いることができる。これらの中でもポリウレタン樹脂、ポリエステル樹脂、塩ビ−酢ビ共重合樹脂が、セルロース誘導体樹脂系は有機溶剤への溶解性、流動性、顔料分散性、転写性に優れることから好ましく用いられ、ポリウレタン樹脂系、ポリエステル樹脂系、及び、セルロース誘導体樹脂系が好ましく、ポリウレタン樹脂系、及び、セルロース誘導体樹脂系が特に好ましい。
られる。
The varnish resin contained in the ink is, for example, an acrylic resin system, a polyurethane resin system, a polyester resin system, a vinyl resin system (vinyl chloride, vinyl acetate, vinyl chloride-vinyl acetate copolymer resin), a chlorinated olefin resin system, Known inks such as ethylene-acrylic resin, petroleum resin, and cellulose derivative resin can be used. Among these, polyurethane resins, polyester resins, vinyl chloride-vinyl acetate copolymer resins, cellulose derivative resin systems are preferably used because they are excellent in solubility in organic solvents, fluidity, pigment dispersibility, and transferability. Polyester resin system and cellulose derivative resin system are preferable, and polyurethane resin system and cellulose derivative resin system are particularly preferable.
It is done.
前記印刷層の印刷方法については特に限定はなく、例えば、グラビア印刷、オフセット印刷、スクリーン印刷、インクジェット印刷、ロールコーティング、コンマコーティング、ロッドグラビアコーティング、マイクログラビアコーティングなどの方法で印刷又はコーティングして作製することができる。印刷層は、全面を同じインキで全面(網点ならば100%)を印刷または塗工したベタ版としてもよいし、絵柄を成すように部分的にインキを印刷することもできる。印刷は、前記支持体フィルムや後述の硬化性樹脂層に直接印刷してもよいし、また、別途剥離性を有するポリプロピレン等のフィルムに印刷した後、支持体フィルムあるいは硬化性樹脂層とラミネートさせることもできる。 The printing method of the printing layer is not particularly limited. For example, the printing layer is printed or coated by a method such as gravure printing, offset printing, screen printing, ink jet printing, roll coating, comma coating, rod gravure coating, or micro gravure coating. can do. The printing layer may be a solid plate in which the entire surface is printed or coated with the same ink (100% in the case of halftone dots), or the ink may be partially printed so as to form a pattern. The printing may be performed directly on the support film or the curable resin layer described later, or after printing on a film such as polypropylene having a separate peelability and then laminating with the support film or the curable resin layer. You can also.
(転写層 硬化性樹脂層)
本発明で使用する硬化性樹脂層は、活性エネルギー線照射又は加熱により硬化可能な樹脂を含む樹脂層である。また、活性エネルギー線硬化と加熱硬化とを併用させてもよい。該硬化性樹脂層は、得られる水圧転写体の装飾層の意匠性が良く発現できることから透明であることが好ましいが、転写体の要求特性や意匠性により。基本的に得られる水圧転写体の装飾層の色や柄が透けて見えれば良く、完全に透明であることは要しない。即ち、透明から半透明なものまでを含む。また、着色されていてもよい。
(Transfer layer curable resin layer)
The curable resin layer used in the present invention is a resin layer containing a resin that can be cured by irradiation with active energy rays or heating. Active energy ray curing and heat curing may be used in combination. The curable resin layer is preferably transparent since the design of the decorative layer of the resulting hydraulic transfer body can be expressed well, but depending on the required properties and design characteristics of the transfer body. Basically, it is sufficient that the color and pattern of the decorative layer of the hydraulic transfer body obtained can be seen through, and it is not necessary to be completely transparent. That is, from transparent to translucent ones are included. Moreover, it may be colored.
(硬化性樹脂層中の光輝性顔料)
硬化性樹脂層に添加される光輝性顔料の添加量は0.5〜5質量%の範囲が好ましい。添加量が多すぎるとギラギラした感じを与え天然材料とは異なる視認性を与える場合がある。また該硬化性樹脂層中で光輝性顔料が平行配列(リーフィング)してしまい、やはり天然材料とは異なる視認性を与える。一方光輝性顔料が少なすぎる量では目に見える効果が得にくい。
(Bright pigment in the curable resin layer)
The addition amount of the luster pigment added to the curable resin layer is preferably in the range of 0.5 to 5% by mass. If the amount added is too large, it may give a glaring feeling and may give visibility different from that of natural materials. In addition, the glittering pigment is arranged in parallel (leafing) in the curable resin layer, which also gives visibility different from that of natural materials. On the other hand, if the amount of the glitter pigment is too small, it is difficult to obtain a visible effect.
また、硬化性樹脂層の膜厚はある程度厚いことが好ましく、具体的には3μm以上であることが好ましい。該膜厚が薄すぎると、光輝性顔料は平行配列してしまい、天然材料とは異なる視認性を与える場合がある。該膜厚が10μm以上であると、得られる水圧転写体の保護効果も備えることができより好ましい。一方該膜厚が200μmを超えると、有機溶剤による硬化性樹脂層の活性化が十分なされにくい。従って好ましい膜厚は10〜200μmであり、活性化速度をより速めたい場合は10〜70μmの範囲が好ましい。 Further, the thickness of the curable resin layer is preferably thick to some extent, and specifically, it is preferably 3 μm or more. If the film thickness is too thin, the glittering pigments are arranged in parallel and may give visibility different from that of natural materials. It is more preferable that the film thickness is 10 μm or more because the protective effect of the obtained hydraulic transfer body can be provided. On the other hand, if the film thickness exceeds 200 μm, it is difficult to sufficiently activate the curable resin layer with an organic solvent. Accordingly, the preferable film thickness is 10 to 200 μm, and when it is desired to increase the activation rate, the range of 10 to 70 μm is preferable.
硬化性樹脂層が光輝性顔料を含むことにより得られる意匠の特に深み感に寄与する。ノンリーフィングタイプの光輝性顔料を含む塗膜は一般に光を乱反射することと、硬化性樹脂層が光輝性顔料を含むことにより、その下に光輝性顔料を含む印刷層があるために、各々の層に存在する光輝性顔料の複雑な光反射や光散乱が生じ(これは、光の反射位置が異なることに起因する反射や散乱と、反射色が異なることに起因する反射や散乱が複雑に絡んでいるものと推定している)、これが深み感に寄与すると考えられる。従って装飾層を木目調にした場合は、本杢の「照り感」までも再現することが可能となる。 The curable resin layer contributes to a particularly deep feeling of the design obtained by including the glitter pigment. A coating film containing a non-leafing type bright pigment generally reflects light irregularly, and since the curable resin layer contains a bright pigment, there is a printing layer containing the bright pigment underneath, so that each The complex pigment reflection and light scattering of the glitter pigment in the layer occurs (this is because the reflection and scattering due to different reflection positions of light and the reflection and scattering due to different reflection colors are complicated This is thought to contribute to a sense of depth. Therefore, when the decoration layer is made of wood grain, it is possible to reproduce even the “shiny feeling” of the main frame.
このように、本発明においては、前記単層もしくは複数層からなる印刷層の少なくとも1層及び前記硬化性樹脂層に光輝性顔料を含み、且つ該光輝性顔料を含む少なくとも2層の反射色が異なることが特徴であるが、その反射色の差(前述の通りΔE*abで表される)は3以上であることが好ましい。3以上であると、各々の層の中、及び、各々の層間で光の反射や散乱が好適に生じ、例えば意匠が木目柄であった場合、天然材料により近い深み感や照り感を有する意匠を有する水圧転写体が得られる。4.5以上であるとより好ましい。 As described above, in the present invention, at least one of the single layer or the plurality of printed layers and the curable resin layer contain a glitter pigment, and at least two layers of reflected colors including the glitter pigment have a reflected color. Although it is different, it is preferable that the difference in reflected color (expressed by ΔE * ab as described above) is 3 or more. When it is 3 or more, light reflection and scattering are suitably generated in each layer and between each layer. For example, when the design is a wood grain pattern, the design has a sense of depth and shine closer to natural materials. A hydraulic transfer body having the following is obtained. More preferably, it is 4.5 or more.
また、光輝性顔料を含む少なくとも2層の位置は、反射色の差が小さい場合(例えば3〜5)は、なるべく離れていることが好ましい。反射色の差が小さい各々の層が隣接すると、十分な反射や散乱効果が得られない場合がある。 Further, it is preferable that the positions of at least two layers containing the glitter pigment are separated as much as possible when the difference in reflected color is small (for example, 3 to 5). If each layer having a small difference in reflection color is adjacent, sufficient reflection or scattering effects may not be obtained.
また、該光輝性顔料を含む層の光沢値も、視認性に影響を与える。一般に塗膜の20度光沢値が高いと輝度が高くキラキラした印象を受け、低いと輝度が低く穏やかな印象となる。本発明においては、前記印刷層のうち少なくとも2層が光輝性顔料を含む場合、各々の印刷層の20度光沢値(本発明においては、日本電色工業社製のハンディー光沢計PG−1Mにより20度光沢値を測定した)に差があるほうが、より視認的に天然材料により近い深み感を与えることが判った。
この場合、各々の層のL*、a*、b*で表される色座標が近い場合であっても、視認的に異なる意匠性を与える場合がある。ここでいう「視認的に異なる意匠性」とは、例えば「キラキラした」や「穏やかな」あるいは「隠蔽力のある」等の、視認される感覚的な意匠性を指す。20度光沢値が例えば5以上離れると、このような意匠性に対して変化を与えることが可能である。
Further, the gloss value of the layer containing the glitter pigment also affects visibility. Generally, when the 20 ° gloss value of the coating film is high, the image has a high brightness and a glittering impression, and when it is low, the image has a low brightness and a gentle impression. In the present invention, when at least two of the printed layers contain a bright pigment, the 20-degree gloss value of each printed layer (in the present invention, a handy gloss meter PG-1M manufactured by Nippon Denshoku Industries Co., Ltd.). It was found that the difference in the 20-degree gloss value) gave a deeper feeling closer to the natural material more visually.
In this case, even if the color coordinates represented by L *, a *, and b * of each layer are close, visually different design properties may be given. Here, “visually different design properties” refer to visually perceptible design properties such as “brilliant”, “gentle”, or “with concealing power”. When the 20 degree gloss value is 5 or more, for example, it is possible to change the design properties.
反射色の差と、光沢値の差との関係は定かではないが、例えば、該光輝性顔料を含む2層の印刷層のΔE*abが大きく(例えば10以上)且つ20度光沢値の差が大きい(例えば20以上)場合、各々の層が互いに隣接していても視認性において天然材料に近い意匠が得られるが、ΔE*abの値が3〜5であり且つ20度光沢値の差が小さい(5〜10である)場合、互いに隣接していると複雑な干渉を与えることが出来ず、あたかも一層の版のように見えてしまうことがある。 Although the relationship between the difference in reflected color and the difference in gloss value is not clear, for example, ΔE * ab of the two printed layers containing the glitter pigment is large (for example, 10 or more) and the difference in the gloss value at 20 degrees Is large (for example, 20 or more), even if each layer is adjacent to each other, a design close to that of a natural material can be obtained in terms of visibility. Is small (5 to 10), if they are adjacent to each other, complicated interference cannot be given, and it may appear as if it is a further plate.
(活性エネルギー線硬化性樹脂又は加熱により硬化可能な樹脂)
本発明における硬化性樹脂層は、前記光輝性顔料を含む以外は特に限定されず、公知の活性エネルギー線照射又は加熱により硬化可能な樹脂を含む樹脂層であればよい。
(Active energy ray curable resin or resin curable by heating)
The curable resin layer in the present invention is not particularly limited as long as it contains the glitter pigment, and may be a resin layer containing a resin curable by known active energy ray irradiation or heating.
(活性エネルギー線硬化性樹脂)
活性エネルギー線照射により硬化可能な樹脂を含む樹脂層には、例えば、公知のラジカル重合性化合物、及び必要に応じて光重合開始剤を含む。ラジカル重合性化合物としては、1分子中に3つ以上の(メタ)アクリロイル基を有するオリゴマーまたはポリマーが好ましく、1分子中に3つ以上の(メタ)アクリロイル基を有する質量平均分子量が300〜1万、より好ましくは300〜5000の活性エネルギー線硬化性のオリゴマーまたはポリマーが好ましく用いられる。また、粘度を調製する目的で(メタ)アクリロイル基を有する反応性モノマーを含有することや、硬化性樹脂層の粘着性低減、ガラス転移温度(Tg)の向上、あるいは硬化性樹脂層の凝集破壊強度の向上等の目的で、熱可塑性樹脂を含有させてよい。
(Active energy ray curable resin)
The resin layer containing a resin curable by active energy ray irradiation includes, for example, a known radical polymerizable compound and, if necessary, a photopolymerization initiator. As the radically polymerizable compound, an oligomer or polymer having three or more (meth) acryloyl groups in one molecule is preferable, and a mass average molecular weight having three or more (meth) acryloyl groups in one molecule is 300 to 1. Ten thousand, more preferably 300 to 5,000 active energy ray-curable oligomers or polymers are preferably used. Also, it contains a reactive monomer having a (meth) acryloyl group for the purpose of adjusting the viscosity, reduces the tackiness of the curable resin layer, improves the glass transition temperature (Tg), or cohesive failure of the curable resin layer For the purpose of improving the strength, a thermoplastic resin may be contained.
(メタ)アクリロイル基を有するオリゴマーまたはポリマーの例としては、例えば、ポリウレタン(メタ)アクリレート、ポリエステル(メタ)アクリレート、ポリアクリル(メタ)アクリレート、エポキシ(メタ)アクリレート、ポリアルキレングリコールポリ(メタ)アクリレート、ポリエーテル(メタ)アクリレート等が挙げられ、中でもポリウレタン(メタ)アクリレート、ポリエステル(メタ)アクリレートおよびエポキシ(メタ)アクリレートが好ましく用いられる。 Examples of the oligomer or polymer having a (meth) acryloyl group include, for example, polyurethane (meth) acrylate, polyester (meth) acrylate, polyacryl (meth) acrylate, epoxy (meth) acrylate, and polyalkylene glycol poly (meth) acrylate. , Polyether (meth) acrylate, etc., among which polyurethane (meth) acrylate, polyester (meth) acrylate and epoxy (meth) acrylate are preferably used.
(メタ)アクリロイル基を有する反応性モノマーの例としては、例えば、メチルアクリレート、メチルメタクリレート(以下、合わせてメチル(メタ)アクリレートのように表記する)、エチル(メタ)アクリレート、n−ブチル(メタ)アクリレート、ヘキシル(メタ)アクリレート、2−エチルヘキシル(メタ)アクリレート、ラウリル(メタ)アクリレート、イソボニル(メタ)アクリレート、ジシクロペンテニル(メタ)アクリレート、ジシクロペンテニロキシエチル(メタ)アクリレート、フェニル(メタ)アクリレート、フェニルセロソルブ(メタ)アクリレート、2−メトキシエチル(メタ)アクリレート、ヒドロキシエチル(メタ)アクリレート、ヒドロキシプロピル(メタ)アクリレート、2−アクリロイルオキシエチルハイドロゲンフタレート、ジメチルアミノエチル(メタ)アクリレート、トリフルオロエチル(メタ)アクリレート、トリメチルシロキシエチルメタクリレート、N−ビニルピロリドン、スチレン等の単官能モノマー、ジエチレングリコールジ(メタ)アクリレート、ネオペンチルグリコールジ(メタ)アクリレート、1,6−ヘキサンジオールジ(メタ)アクリレート、ポリエチレングリコールジ(メタ)アクリレート、2,2‘−ビス(4−(メタ)アクリロイルオキシポリエチレンオキシフェニル)プロパン、2,2’−ビス(4−(メタ)アクリロイルオキシポリプロピレンオキシフェニル)プロパン等の2官能モノマー、トリメチロールプロパントリ(メタ)アクリレート、トリメチロールエタントリ(メタ)アクリレート等の3官能モノマー、ペンタエリスリトールテトラ(メタ)アクリレート等の4官能モノマー、ジペンタエリスリトールヘキサアクリレート等の6官能モノマー等が挙げられる。また、トリブチレングリコールビス(マレイミド酢酸エステル)のようなマレイミド化合物を使用することもできる。もちろん、これらのモノマーを2種類以上混合して用いることも可能である。 Examples of the reactive monomer having a (meth) acryloyl group include, for example, methyl acrylate, methyl methacrylate (hereinafter collectively referred to as methyl (meth) acrylate), ethyl (meth) acrylate, n-butyl (meta ) Acrylate, hexyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, lauryl (meth) acrylate, isobornyl (meth) acrylate, dicyclopentenyl (meth) acrylate, dicyclopentenyloxyethyl (meth) acrylate, phenyl ( (Meth) acrylate, phenyl cellosolve (meth) acrylate, 2-methoxyethyl (meth) acrylate, hydroxyethyl (meth) acrylate, hydroxypropyl (meth) acrylate, 2-acryloyloxyethyl Monofunctional monomers such as idrogen phthalate, dimethylaminoethyl (meth) acrylate, trifluoroethyl (meth) acrylate, trimethylsiloxyethyl methacrylate, N-vinylpyrrolidone, styrene, diethylene glycol di (meth) acrylate, neopentyl glycol di (meth) ) Acrylate, 1,6-hexanediol di (meth) acrylate, polyethylene glycol di (meth) acrylate, 2,2′-bis (4- (meth) acryloyloxypolyethyleneoxyphenyl) propane, 2,2′-bis ( 3-functional monomers such as 4- (meth) acryloyloxypolypropyleneoxyphenyl) propane, 3 such as trimethylolpropane tri (meth) acrylate, trimethylolethane tri (meth) acrylate, etc. Ability monomers, tetrafunctional monomers such as pentaerythritol tetra (meth) acrylate, hexafunctional monomers such as dipentaerythritol hexaacrylate. A maleimide compound such as butylene glycol bis (maleimide acetate) can also be used. Of course, it is also possible to use a mixture of two or more of these monomers.
光重合開始剤の例としては、例えば、ジエトキシアセトフェノン、1−ヒドロキシシクロヘキシル−フェニルケトンの如きアセトフェノン系化合物;ベンゾイン、ベンゾインイソプロピルエーテルの如きベンゾイン系化合物;2,4,6−トリメチルベンゾインジフェニルホスフィンオキシドの如きアシルホスフィンオキシド系化合物;ベンゾフェノン、o−ベンゾイル安息香酸メチル−4−フェニルベンゾフェノンの如きベンゾフェノン系化合物;2,4−ジメチルチオキサントンの如きチオキサントン系化合物;4,4′−ジエチルアミノベンゾフェノンの如きアミノベンゾフェノン系化合物;ポリエーテル系マレイミドカルボン酸エステル化合物などが挙げられ、これらは併用して使用することもできる。光重合開始剤の使用量は用いる活性エネルギー線硬化性樹脂に対して、通常、0.1〜15質量%、好ましくは0.5〜8質量%である。光増感剤としては、例えば、トリエタノールアミン、4−ジメチルアミノ安息香酸エチルの如きアミン類が挙げられる。さらに、ベンジルスルホニウム塩やベンジルピリジニウム塩、アリールスルホニウム塩などのオニウム塩は、光カチオン開始剤として知られており、これらの開始剤を用いることも可能であり、上記の光重合開始剤と併用することもできる。 Examples of photopolymerization initiators include, for example, acetophenone compounds such as diethoxyacetophenone and 1-hydroxycyclohexyl-phenyl ketone; benzoin compounds such as benzoin and benzoin isopropyl ether; 2,4,6-trimethylbenzoin diphenylphosphine oxide Acyl phosphine oxide compounds such as benzophenone, benzophenone compounds such as methyl-4-phenylbenzophenone o-benzoylbenzoate; thioxanthone compounds such as 2,4-dimethylthioxanthone; aminobenzophenones such as 4,4'-diethylaminobenzophenone Compounds such as polyether-based maleimide carboxylic acid ester compounds, and the like, which can be used in combination. The usage-amount of a photoinitiator is 0.1-15 mass% normally with respect to the active energy ray curable resin to be used, Preferably it is 0.5-8 mass%. Examples of the photosensitizer include amines such as triethanolamine and ethyl 4-dimethylaminobenzoate. Furthermore, onium salts such as benzylsulfonium salt, benzylpyridinium salt, and arylsulfonium salt are known as photocationic initiators, and these initiators can also be used, and are used in combination with the above photopolymerization initiators. You can also.
使用する熱可塑性樹脂は、活性エネルギー線硬化性樹脂に相溶できるものが好ましく、具体例としては、ポリメタアクリレート、ポリスチレン、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリ酢酸ビニル、ポリエステルなどが挙げられる。これらはホモポリマーまたは複数のモノマーが共重合したものであって良い。熱可塑性樹脂は、非重合性であることが好ましい。
なかでも、ポリスチレンおよびポリメタアクリレートは、Tgが高く硬化性樹脂層の粘着性低減に適しているために好ましく、特にポリメチルメタアクリレートを主成分としたポリメタアクリレートが透明性、耐溶剤性および耐擦傷性に優れる点で好ましい。
The thermoplastic resin used is preferably compatible with the active energy ray curable resin, and specific examples include polymethacrylate, polystyrene, polyvinyl chloride, polyvinylidene chloride, polyvinyl acetate, and polyester. These may be a homopolymer or a copolymer of a plurality of monomers. The thermoplastic resin is preferably non-polymerizable.
Among them, polystyrene and polymethacrylate are preferable because they have high Tg and are suitable for reducing the adhesiveness of the curable resin layer, and in particular, polymethacrylate mainly composed of polymethyl methacrylate is transparent, solvent resistant, and It is preferable at the point which is excellent in abrasion resistance.
また、熱可塑性樹脂の分子量とTgは塗膜形成能に大きな影響を与える。硬化性樹脂の流動性を抑制し、かつ硬化性樹脂層の活性化を容易にするために、熱可塑性樹脂の質量平均分子量は好ましくは3,000〜40万、より好ましくは1万〜20万であり、Tgは好ましくは35℃〜200℃、より好ましくは35℃〜150℃である。Tgが35℃付近の比較的低いTgを有する熱可塑性樹脂を用いる場合は、熱可塑性樹脂の質量平均分子量は10万以上であることが好ましい。
熱可塑性樹脂は、あまり多いと硬化性樹脂の硬化反応を阻害するので、硬化性樹脂層の全樹脂量100質量部に対して熱可塑性樹脂は70質量部を超えない範囲で添加することが好ましい。
Further, the molecular weight and Tg of the thermoplastic resin have a great influence on the film-forming ability. In order to suppress fluidity of the curable resin and facilitate activation of the curable resin layer, the mass average molecular weight of the thermoplastic resin is preferably 3,000 to 400,000, more preferably 10,000 to 200,000. Tg is preferably 35 ° C to 200 ° C, more preferably 35 ° C to 150 ° C. When using a thermoplastic resin having a relatively low Tg of around 35 ° C., the mass average molecular weight of the thermoplastic resin is preferably 100,000 or more.
If the amount of the thermoplastic resin is too large, the curing reaction of the curable resin is inhibited. Therefore, the thermoplastic resin is preferably added in a range not exceeding 70 parts by mass with respect to 100 parts by mass of the total resin amount of the curable resin layer. .
活性エネルギー線硬化性樹脂と非重合性の熱可塑性樹脂を含む硬化性樹脂層としては、これらのなかでも、1分子中に3つ以上の(メタ)アクリロイル基を有する質量平均分子量300〜1万、より好ましくは300〜5000である活性エネルギー線硬化性樹脂と、この活性エネルギー線硬化性樹脂に相溶するTgが35℃〜200℃、好ましくは35℃〜150℃で、質量平均分子量が3000〜40万、好ましくは1万〜20万である非重合性の熱可塑性樹脂を含有する硬化性樹脂層が好ましい。さらに、前記活性エネルギー線硬化性樹脂が、1分子中に3つ以上の(メタ)アクリロイル基を有するポリウレタン(メタ)アクリレートであり、非重合性の熱可塑性樹脂がポリメタアクリレート、特にポリメチルメタアクリレートである硬化性樹脂層がとりわけ好ましい。 Among these, the curable resin layer containing the active energy ray-curable resin and the non-polymerizable thermoplastic resin has a mass average molecular weight of 300 to 10,000 having three or more (meth) acryloyl groups in one molecule. More preferably, the active energy ray-curable resin is 300 to 5,000, and the Tg compatible with the active energy ray curable resin is 35 ° C to 200 ° C, preferably 35 ° C to 150 ° C, and the mass average molecular weight is 3000. A curable resin layer containing a non-polymerizable thermoplastic resin of ˜400,000, preferably 10,000 to 200,000 is preferred. Further, the active energy ray-curable resin is a polyurethane (meth) acrylate having three or more (meth) acryloyl groups in one molecule, and the non-polymerizable thermoplastic resin is a polymethacrylate, particularly polymethylmethacrylate. A curable resin layer that is an acrylate is particularly preferred.
(熱硬化性樹脂)
加熱により硬化可能な樹脂を含む樹脂層には、熱または触媒の作用により重合する官能基を分子中に有する化合物であるか、または主剤となる熱硬化性化合物に硬化剤となる熱反応性化合物を含む。また、前記活性エネルギー線硬化性樹脂と同様、、硬化性樹脂層の粘着性低減、ガラス転移温度(Tg)の向上、あるいは硬化性樹脂層の凝集破壊強度の向上等の目的で、前記熱可塑性樹脂を含有させてよい。
(Thermosetting resin)
The resin layer containing a resin curable by heating is a compound having a functional group that polymerizes by the action of heat or a catalyst in the molecule, or a thermoreactive compound that becomes a curing agent to a thermosetting compound that becomes a main agent including. Further, like the active energy ray curable resin, the thermoplastic resin is used for the purpose of reducing the adhesiveness of the curable resin layer, improving the glass transition temperature (Tg), or improving the cohesive failure strength of the curable resin layer. A resin may be included.
熱重合開始剤としては特に限定はないが、被転写体が耐熱温度の低いプラスチック等の場合には、開始温度のなるべく低い熱重合開始剤を使用するのが好ましく、100℃を超えない温度の開始温度を有する熱重合開始剤を使用するのが好ましい。
また、熱硬化性化合物としては公知のものを使用でき、例えば、熱または触媒の作用により重合する官能基を有する、例えば、N−メチロール基、N−アルコキシメチル基、エポキシ基、メチロール基、酸無水物、炭素−炭素二重結合などを有する化合物や樹脂等を使用できる。
The thermal polymerization initiator is not particularly limited. However, when the transfer object is a plastic having a low heat resistant temperature, it is preferable to use a thermal polymerization initiator having a starting temperature as low as possible. It is preferred to use a thermal polymerization initiator having an initiation temperature.
Moreover, a well-known thing can be used as a thermosetting compound, for example, it has a functional group which superposes | polymerizes by the effect | action of a heat | fever or a catalyst, for example, N-methylol group, N-alkoxymethyl group, an epoxy group, a methylol group, an acid. A compound or resin having an anhydride, a carbon-carbon double bond, or the like can be used.
硬化性樹脂層は、無機・金属化合物、または、有機処理を施された無機・金属化合物を添加することもできる。
これら添加可能な化合物に何ら制限はなく、例えば、シリガゲル、シリカゾル、モンモリロナイト、マイカ、アルミナ、酸化チタン、ガラスビーズ等の無機・金属化合物、オルガノシリカゾル、アクリル変性シリカ、クロイサイト等の有機処理を施された無機・金属化合物を用いることができる。
In the curable resin layer, an inorganic / metal compound or an inorganic / metal compound subjected to organic treatment can be added.
There are no restrictions on these compounds that can be added, and for example, organic treatments such as silica gel, silica sol, montmorillonite, mica, alumina, titanium oxide, glass beads, and other inorganic / metal compounds, organosilica sol, acrylic-modified silica, and closite are performed. Inorganic / metal compounds prepared can be used.
(その他の層)
本発明においては、前記支持体フィルム、前記転写層である印刷層と硬化性樹脂層の他に、例えば、前記支持体フィルムと印刷層の層間に印刷インキ受理層、膨潤抑制層等が積層されていても良い。
前記印刷インキ受理層は、例えば印刷層をインクジェット印刷法で得る場合に、支持体フィルムとして汎用されるポリビニルアルコール樹脂や、印刷基材として用いられるポリプロピレン樹脂とインキとの相性が悪い場合に使用する。また、膨潤抑制層は、主に、活性化時の装飾層や硬化性樹脂層の過度の柄伸びを抑制する目的で使用する。具体的には、例えば体質顔料として、沈降性硫酸バリウムやシリカ等を添加することができる。
(Other layers)
In the present invention, in addition to the support film, the printing layer that is the transfer layer, and the curable resin layer, for example, a printing ink receiving layer, a swelling suppression layer, and the like are laminated between the support film and the printing layer. May be.
The printing ink receiving layer is used, for example, when the printing layer is obtained by an ink jet printing method, when the compatibility between the polyvinyl alcohol resin widely used as a support film or the polypropylene resin used as a printing substrate and the ink is poor. . The swelling suppression layer is mainly used for the purpose of suppressing excessive pattern elongation of the decorative layer and the curable resin layer at the time of activation. Specifically, for example, precipitated barium sulfate and silica can be added as extender pigments.
(水圧転写体の製造方法)
本発明の水圧転写体は、本発明の水圧転写用フィルムを使用する以外は、特に限定はなく公知の転写方法にて製造することができる。
具体的には、例えば、使用する水圧転写用フィルムを、必要に応じて剥離性フィルムを剥離した後、転写層を上にして、支持体を下にして水に浮かべ、活性化剤により硬化性樹脂層、もしくは装飾層と硬化性樹脂層からなる転写層を活性化し(活性化は水に浮かべる前に行っても良い)、転写層を被転写体に転写し、支持体を除去し、次いで転写層の硬化性樹脂層を活性エネルギー線照射と加熱の少なくとも一種で硬化させる。概略は、以下に示す通りである。
(Method for producing hydraulic transfer body)
The hydraulic transfer body of the present invention is not particularly limited except that the hydraulic transfer film of the present invention is used, and can be produced by a known transfer method.
Specifically, for example, the hydraulic transfer film to be used is peeled off from the peelable film as necessary, then floated in water with the transfer layer up, the support down, and curable by an activator. Activate the resin layer or the transfer layer composed of the decorative layer and the curable resin layer (activation may be performed before floating in water), transfer the transfer layer to the transfer target, remove the support, The curable resin layer of the transfer layer is cured by at least one of active energy ray irradiation and heating. The outline is as shown below.
(1)剥離性フィルムを剥離した水圧転写用フィルムを支持体フィルムを下にして水槽中の水に浮かべ、支持体フィルムを水で溶解もしくは膨潤させる。
(2)転写層に活性化剤を塗布または噴霧することにより硬化性樹脂層と装飾層とから成る転写層を活性化させる。なお活性化は、フィルムを水に浮かべる前に行っても良い。
(3)転写層に被転写体を押し付けながら、被転写体と水圧転写用フィルムを水中に沈めて行き、水圧によって転写層を被転写体に密着させて転写する。
(4)水から出した被転写体から支持体フィルムを除去し、被転写体に転写された転写層の硬化性樹脂層を活性エネルギー線照射と加熱の少なくとも一種により硬化させて、硬化した樹脂層と装飾層とを有する水圧転写体を得る。
(1) The hydraulic transfer film from which the peelable film has been peeled is floated on water in a water tank with the support film facing down, and the support film is dissolved or swollen with water.
(2) The transfer layer composed of the curable resin layer and the decorative layer is activated by applying or spraying an activator to the transfer layer. The activation may be performed before the film is floated on water.
(3) While the transfer medium is pressed against the transfer layer, the transfer object and the hydraulic transfer film are submerged in water, and the transfer layer is brought into close contact with the transfer object by water pressure and transferred.
(4) The cured resin obtained by removing the support film from the transfer medium taken out of water and curing the curable resin layer of the transfer layer transferred to the transfer medium by at least one of irradiation with active energy rays and heating. A hydraulic transfer body having a layer and a decorative layer is obtained.
(水)
水圧転写における水槽の水は、転写層を転写する際に水圧転写用フィルムの硬化性樹脂層と装飾層とを被転写体の三次元曲面に密着させる水圧媒体として働く他、支持体フィルムを膨潤または溶解させるものであり、具体的には、水道水、蒸留水、イオン交換水などの水で良く、また用いる支持体フィルムによっては、水にホウ酸等の無機塩類を10%以下、またはアルコール類を50%以下溶解させてもよい。
(water)
The water in the water tank in hydraulic transfer functions as a hydraulic medium that closely adheres the curable resin layer and decorative layer of the hydraulic transfer film to the three-dimensional curved surface of the transfer target when transferring the transfer layer, and also swells the support film. Or, specifically, water such as tap water, distilled water, ion-exchanged water, etc., and depending on the support film used, 10% or less of inorganic salts such as boric acid in the water or alcohol 50% or less may be dissolved.
(活性化剤)
活性化剤は公知のものを使用できる。具体的には、硬化性樹脂層と装飾層とを可溶化させ、柔軟性を付与する有機溶剤、あるいは、低粘度のラジカル重合性組成物を使用することができる。中でも、取り扱いが容易であることから、有機溶剤を使用することが好ましい。
具体的には、有機溶剤としては、トルエン、キシレン、エチルベンゼン、ヘキサン、シクロヘキサン、メチルエチルケトン、メチルイソブチルケトン、メチルイソアミルケトン、酢酸エチル、酢酸ブチル、酢酸プロピル、酢酸イソブチル、酢酸イソアミル、1−プロパノール、2−プロパノール、1−ブタノール、2−ブタノール、イソブタノール、エチルセロソルブ、セロソルブアセテート、ブチルセロソルブ、カルビトール、カルビトールアセテート、ブチルカルビトールアセテート、ソルフィットアセテート、D−リモネン及びそれらの混合物が挙げられる。
低粘度のラジカル重合性組成物は、光重合性プレポリマー、光重合性モノマー、及び光重合開始剤を必須成分とするもので、公知のものを使用することができる。また、粘度を調製する目的で有機溶剤を適宜添加しても構わない。
(Activator)
A known activator can be used. Specifically, an organic solvent that solubilizes the curable resin layer and the decorative layer and imparts flexibility, or a low-viscosity radically polymerizable composition can be used. Among these, it is preferable to use an organic solvent because it is easy to handle.
Specifically, examples of the organic solvent include toluene, xylene, ethylbenzene, hexane, cyclohexane, methyl ethyl ketone, methyl isobutyl ketone, methyl isoamyl ketone, ethyl acetate, butyl acetate, propyl acetate, isobutyl acetate, isoamyl acetate, 1-propanol, 2 -Propanol, 1-butanol, 2-butanol, isobutanol, ethyl cellosolve, cellosolve acetate, butyl cellosolve, carbitol, carbitol acetate, butyl carbitol acetate, sorbite acetate, D-limonene and mixtures thereof.
The low-viscosity radical polymerizable composition contains a photopolymerizable prepolymer, a photopolymerizable monomer, and a photopolymerization initiator as essential components, and known ones can be used. Moreover, you may add an organic solvent suitably for the purpose of adjusting a viscosity.
この活性化剤中に印刷インキ又は塗料と成形品との密着性を高めるために、若干の樹脂成分を含ませてもよい。例えば、ポリウレタン、アクリル樹脂、エポキシ樹脂といった、インキのバインダーに類似の構造のものを1〜10%含ませることによって密着性が高まることがある。 In order to improve the adhesion between the printing ink or paint and the molded product, this activator may contain some resin components. For example, adhesion may be increased by including 1 to 10% of an ink binder having a similar structure such as polyurethane, acrylic resin, or epoxy resin.
(活性化剤の適用方法)
活性化工程における本発明の活性化剤の適用方法としては、塗布または噴霧する方法が挙げられる。具体的には、活性化剤をフィルムに適用することができる方法であれば、何ら制限はなく、ロールコーター、ダイコーター、カーテンコーター、スプレーノズル、インクジェット式ノズル等を用いることができる。活性化剤の塗布量は特に限定はないが、水圧転写フィルム1m2に対し、10g/m2〜60g/m2の範囲が好ましく、20g/m2〜40g/m2の範囲がなお好ましい。
(Application method of activator)
Examples of a method for applying the activator of the present invention in the activation step include a method of applying or spraying. Specifically, there is no limitation as long as the activator can be applied to the film, and a roll coater, a die coater, a curtain coater, a spray nozzle, an inkjet nozzle, or the like can be used. Although the coating amount of the activator is not particularly limited with respect to the water pressure transfer film 1 m 2, preferably in a range of 10g / m 2 ~60g / m 2 , the range of 20g / m 2 ~40g / m 2 is further preferable.
活性化後の転写層を被転写体に転写する。具体的には、水圧転写用フィルムの転写層に被転写体を押しつけながら、被転写体と水圧転写用フィルムを水中に沈めて行き、水圧によって転写層を前記被転写体に密着させて転写する。 The activated transfer layer is transferred to a transfer target. Specifically, while the transfer target is pressed against the transfer layer of the hydraulic transfer film, the transfer target and the hydraulic transfer film are submerged in water, and the transfer layer is brought into close contact with the transfer target by water pressure and transferred. .
転写後の被転写体から、前記支持体フィルムを除去する。具体的には、水から出した被転写体から支持体フィルムを除去し、乾燥させる。
被転写体からの支持体フィルムの除去は、従来の水圧転写方法と同様に水流で支持体フィルムを溶解もしくは剥離して除去する。
乾燥工程は、加熱乾燥であると、乾燥を短時間で行うことができ好ましい。この時の乾燥温度は、被転写体が耐熱温度の低いプラスチック等の場合には、被転写体の熱変形を引き起こさないように、基材の耐熱温度を超えない温度で行うのが好ましい。オーブンや乾燥炉を使用することができる。
The support film is removed from the transfer target after transfer. Specifically, the support film is removed from the transfer medium taken out of water and dried.
The support film is removed from the transfer target by dissolving or peeling the support film with a water flow in the same manner as in the conventional hydraulic transfer method.
The drying step is preferably heat drying because it can be performed in a short time. The drying temperature at this time is preferably a temperature that does not exceed the heat resistance temperature of the substrate so that the material to be transferred is a plastic or the like having a low heat resistance temperature so as not to cause thermal deformation of the material to be transferred. An oven or a drying furnace can be used.
使用する水圧転写フィルムが、硬化性樹脂層を有する場合は、活性エネルギー線又は熱により硬化性樹脂層を硬化させる。使用する活性エネルギー線は、通常は可視光や紫外線を使用するのが好ましい。特に紫外線が好適である。紫外線源としては、太陽光線、低圧水銀灯、高圧水銀灯、超高圧水銀灯、カーボンアーク灯、メタルハライドランプ、キセノンランプ等が用いられる。また加熱源としては、熱風、近赤外線など公知の熱源が適用可能である。 When the hydraulic transfer film to be used has a curable resin layer, the curable resin layer is cured by active energy rays or heat. As the active energy ray to be used, it is usually preferable to use visible light or ultraviolet light. In particular, ultraviolet rays are suitable. As the ultraviolet light source, sunlight, a low-pressure mercury lamp, a high-pressure mercury lamp, an ultrahigh-pressure mercury lamp, a carbon arc lamp, a metal halide lamp, a xenon lamp, or the like is used. Moreover, as a heat source, well-known heat sources, such as a hot air and a near infrared ray, are applicable.
(プライマー層)
被転写体は、その表面に硬化性樹脂層や装飾層が十分密着することが好ましく必要に応じて被転写体表面にプライマー層を設ける。プライマー層を形成する樹脂は、プライマー層として慣用の樹脂を特に制限なく用いることができ、ウレタン樹脂、エポキシ樹脂、アクリル樹脂などが挙げられる。また、密着性の良好なABS樹脂やSBSゴムなどの溶剤吸収性の高い樹脂成分からなる被転写体にはプライマー処理は不要である。被転写体の材質は、必要に応じて防水加工を施すことにより水中に沈めても形状が崩れない防水性があれば、金属、プラスチック、木材、パルプモールド、ガラス等のいずれであっても良く特に限定されない。
(Primer layer)
It is preferable that the curable resin layer and the decoration layer are sufficiently adhered to the surface of the transferred body, and a primer layer is provided on the surface of the transferred body as necessary. As the resin forming the primer layer, a conventional resin can be used as the primer layer without particular limitation, and examples thereof include a urethane resin, an epoxy resin, and an acrylic resin. In addition, primer treatment is not required for a transfer medium comprising a resin component having high solvent absorbability such as ABS resin or SBS rubber having good adhesion. The material of the transferred material may be any of metal, plastic, wood, pulp mold, glass, etc., as long as it has a waterproof property so that its shape does not collapse even if it is submerged in water by applying a waterproof process. There is no particular limitation.
以下に具体例をもって本発明を説明するが、本発明はこれらに限定されるものではない。なお%は全て質量基準とする。 Hereinafter, the present invention will be described with specific examples, but the present invention is not limited thereto. All percentages are based on mass.
本発明の水圧転写体は、以下の項目に従い評価を行った。
(「深み感」評価方法)
後述の方法により得られた水圧転写体の装飾層を、標準光源(D65)下、転写面に対して垂直方向から目視にて観察し、硬化性樹脂層及び印刷層に含まれる異なる色及び質感の光輝性顔料のそれぞれが重ね合うことによって、互いに反射や散乱することにより本杢に近い深み感を有すると判断したものを、「深み感あり」と判断した。
The hydraulic transfer body of the present invention was evaluated according to the following items.
("Deep feeling" evaluation method)
The decorative layer of the hydraulic transfer body obtained by the method described later is visually observed from the direction perpendicular to the transfer surface under the standard light source (D65), and different colors and textures contained in the curable resin layer and the printing layer. When the glitter pigments were overlapped with each other, they were judged to have a sense of depth close to that of the main shell by being reflected or scattered from each other, and were judged to have “feel of depth”.
(「照り感」評価方法)
後述の方法により得られた水圧転写品の装飾層を、標準光源(D65)下、転写面に対して90度からの目視観察を基準として、60度、30度の順に目視にて観察し、目視角度に依存して照りが変化し、即ち本杢に近い照り感を有すると判断したものを「木質的照り感あり」と判断した。
(Evaluation method for “shine”)
The decorative layer of the hydraulic transfer product obtained by the method described later is visually observed in the order of 60 degrees and 30 degrees with reference to the visual observation from 90 degrees with respect to the transfer surface under the standard light source (D65). The shininess changed depending on the viewing angle, that is, the one judged to have a shining sensation close to that of the main sword was judged as “woody sensation”.
(硬化性樹脂A1の製造例)
ペンタエリスリトール2モル当量とヘキサメチレンジイソシアネート7モル当量とヒドロキシエチルメタクリレート6モル当量を60℃で反応して得られる平均6官能ウレタンアクリレート(UA1)60部(重量平均分子量890)とロームアンドハース社製アクリル樹脂パラロイドA−11(Tg100℃、重量平均分子量125,000)40部と、酢酸エチルとメチルエチルケトンの混合溶剤(混合比1/1)とで固形分50%の硬化性樹脂A1を製造した。
(Production example of curable resin A1)
60 parts of an average hexafunctional urethane acrylate (UA1) (weight average molecular weight 890) obtained by reacting 2 mole equivalents of pentaerythritol, 7 mole equivalents of hexamethylene diisocyanate and 6 mole equivalents of hydroxyethyl methacrylate at 60 ° C., manufactured by Rohm and Haas A curable resin A1 having a solid content of 50% was produced with 40 parts of acrylic resin paraloid A-11 (Tg 100 ° C., weight average molecular weight 125,000) and a mixed solvent of ethyl acetate and methyl ethyl ketone (mixing ratio 1/1).
(硬化性樹脂A2の製造例)
上記A1の硬化性樹脂層に対し、0.5%の割合で、光輝性顔料としてメルク社製の「Xirallic T60-20WNT」(以下光輝性顔料P1とする)を添加し、硬化性樹脂A2を製造した。
(Production example of curable resin A2)
“Xirallic T60-20WNT” (hereinafter referred to as glitter pigment P1) manufactured by Merck is added as a glitter pigment at a ratio of 0.5% to the curable resin layer of A1, and the curable resin A2 is added. Manufactured.
(硬化性樹脂A3の製造例)
上記A1の硬化性樹脂層に対し、10%の割合で、光輝性顔料としてP1を添加し、硬化性樹脂A3を製造した。
(Production example of curable resin A3)
P1 was added as a luster pigment at a ratio of 10% to the curable resin layer of A1 to produce a curable resin A3.
(光輝性顔料を使用したインキ組成)
インキB1:
インキ用ビヒクル:荒川化学社製「ポリウレタン2569」:20部
顔料:P1:10部
酢酸エチル・トルエン(1/1):60部
ワックス等添加剤:10部
インキB2:
インキ用ビヒクル:荒川化学社製「ポリウレタン2569」:20部
顔料:メルク社製Iriodin302(以下光輝性顔料P2と略す):10部
酢酸エチル・トルエン(1/1):60部
ワックス等添加剤:10部
インキB3:
インキ用ビヒクル:荒川化学社製「ポリウレタン2569」:20部
顔料:メルク社製Iriodin120(以下光輝性顔料P3と略す):10部
酢酸エチル・トルエン(1/1):60部
ワックス等添加剤:10部
インキB4:
インキ用ビヒクル:荒川化学社製「ポリウレタン2569」:20部
顔料:メルク社製Iriodin300(以下光輝性顔料P4と略す):10部
酢酸エチル・トルエン(1/1):60部
ワックス等添加剤:10部
(Ink composition using glitter pigment)
Ink B1:
Ink vehicle: “Polyurethane 2569” manufactured by Arakawa Chemical Co., Ltd .: 20 parts Pigment: P1: 10 parts
Ethyl acetate / toluene (1/1): 60 parts
Additives such as wax: 10 parts ink B2:
Ink vehicle: “Polyurethane 2569” manufactured by Arakawa Chemical Co., Ltd .: 20 parts Pigment: Iriodin 302 manufactured by Merck Co., Ltd. (hereinafter abbreviated as bright pigment P2): 10 parts
Ethyl acetate / toluene (1/1): 60 parts
Additives such as wax: 10 parts ink B3:
Ink vehicle: “Polyurethane 2569” manufactured by Arakawa Chemical Co., Ltd .: 20 parts Pigment: Iriodin 120 manufactured by Merck Co., Ltd. (hereinafter abbreviated as bright pigment P3): 10 parts
Ethyl acetate / toluene (1/1): 60 parts
Additives such as wax: 10 parts ink B4:
Ink vehicle: “Polyurethane 2569” manufactured by Arakawa Chemical Co., Ltd .: 20 parts Pigment: Iriodin 300 manufactured by Merck Co., Ltd. (hereinafter abbreviated as bright pigment P4): 10 parts
Ethyl acetate / toluene (1/1): 60 parts
Additives such as wax: 10 parts
(インキ製造例)
(顔料を使用したインキ組成)
インキB5、B6:
インキ用ビヒクル:荒川化学社製「ポリウレタン2569」:20部
顔料: 白、黒、黄、紅、藍):10部
酢酸エチル・トルエン(1/1):60部
ワックス等添加剤:10部
使用する顔料は、以下の物を組み合わせて使用し、B5、B6を調色した。
白:酸化チタン
黒:カーボンブラック
黄:ジスアゾイエロー
紅:クロモフタルレッド
藍:フタロシアニンブルー
(Example of ink production)
(Ink composition using pigment)
Inks B5 and B6:
Ink vehicle: Arakawa Chemical "Polyurethane 2569": 20 parts Pigment: White, black, yellow, red, indigo): 10 parts
Ethyl acetate / toluene (1/1): 60 parts
Additives such as wax: 10 parts of pigments were used in combination of the following, and B5 and B6 were toned.
White: Titanium oxide
Black: Carbon black
Yellow: Disazo yellow
Red: Chromophthal red
Indigo: phthalocyanine blue
(20度光沢値測定方法)
前記硬化性樹脂A2、A3及びインキB1〜B4の20度光沢値測定は、以下のように行った。
硬化性樹脂またはインキを、白色ABS基板上に、乾燥後膜厚が30μmとなるように塗工し乾燥させ塗膜とした。該塗膜の光沢値を、日本電色工業社製のハンディー光沢計PG−1Mを用い、20度、60度、85度光沢値を読み取った。
表1に示す。
(20 degree gloss value measurement method)
The 20-degree gloss values of the curable resins A2 and A3 and the inks B1 to B4 were measured as follows.
A curable resin or ink was applied onto a white ABS substrate so that the film thickness after drying was 30 μm and dried to form a coating film. The gloss value of the coating film was read at 20 °, 60 °, and 85 ° using a handy gloss meter PG-1M manufactured by Nippon Denshoku Industries Co., Ltd.
Table 1 shows.
(反射色の測定方法)
前記光沢値測定方法で使用した塗膜について、測色を行い、反射色及びその差を測定した。
測色値の測定はコニカミノルタ社製の分光測色計CM3500dを用い、視野設定10度、D65光源の条件で反射測定(正反射光除去)を行ない、表色系CIE L*a*b*で表した。
(但しL*はCIE1976明度を表し、a*、b*はクロマティクネス指数と呼ばれ、色相と彩度を示す色度を表し、ΔE*abは各々の色差値を表す)。インキB1を基準とし、インキB1に対する色差値を「反射色の差」とした。
結果を表1に示す。
(Measurement method of reflected color)
The coating film used in the gloss value measuring method was measured for color, and the reflected color and the difference were measured.
The colorimetric value is measured using a spectrocolorimeter CM3500d manufactured by Konica Minolta, Inc., and reflection measurement (regular reflection light removal) is performed under the conditions of a visual field setting of 10 degrees and a D65 light source, and the color system CIE L * a * b *. Expressed in
(However, L * represents CIE 1976 brightness, a * and b * are called chromaticness indices, and represent chromaticity indicating hue and saturation, and ΔE * ab represents each color difference value). Based on ink B1, the color difference value with respect to ink B1 was defined as “difference in reflected color”.
The results are shown in Table 1.
(印刷層の製造例)
(印刷模様層を有するフィルム(C)C1の製造)
剥離性フィルムとして、東洋紡社製の厚さ50μmの無延伸ポリプロピレンフィルム(以下、PPフィルムと略す)を用い、該フィルムにグラビア印刷機にて、インキB2でベタ層を印刷した(版1)後、インキB3で木目柄を印刷し(版2)、さらにインキB5及びB6で2版の木目柄を印刷した(版3、版4)上に、インキB4で木目柄を印刷して(版5)、装飾フィルム(C)C1を製造した。ここで版2〜版5それぞれが、木目柄を構成しているものとする。
(Example of printed layer production)
(Production of film (C) C1 having printed pattern layer)
As a peelable film, a 50 μm thick unstretched polypropylene film (hereinafter abbreviated as PP film) manufactured by Toyobo Co., Ltd. was used, and after printing a solid layer with ink B2 on the film with a gravure printer (plate 1) A wood grain pattern was printed with ink B3 (plate 2), and a two-grain wood grain pattern was printed with inks B5 and B6 (plate 3, plate 4), and a wood grain pattern was printed with ink B4 (plate 5). ), A decorative film (C) C1 was produced. Here, it is assumed that each of the plates 2 to 5 constitutes a wood grain pattern.
(印刷模様層を有するフィルム(C)C2の製造)
前記PPフィルムにグラビア印刷機にて、インキB2でベタ層を印刷した(版1)後、インキB3で木目柄を印刷し(版2)、さらにインキB5及びB6で2版の木目柄を印刷して(版3、版4)、装飾フィルム(C)C2を製造した。
(Production of film (C) C2 having printed pattern layer)
On the PP film, a solid layer was printed with ink B2 on the gravure printer (plate 1), then a wood grain pattern was printed with ink B3 (plate 2), and a two-grain wood grain pattern was printed with inks B5 and B6. Thus, the decorative film (C) C2 was manufactured (plate 3, plate 4).
(印刷模様層を有するフィルム(C)C3の製造)
前記PPフィルムにグラビア印刷機にて、インキB2でベタ層を印刷した(版1)後、インキB5及びB6で2版の木目柄を印刷した(版3、版4)上に、インキB4で木目柄を印刷して、装飾フィルム(C)C3を製造した。
(Production of film (C) C3 having printed pattern layer)
On the PP film, a solid layer was printed with an ink B2 on a gravure printing machine (plate 1), and then a two-grain grain pattern was printed with inks B5 and B6 (plate 3, plate 4) with an ink B4. A wood grain pattern was printed to produce a decorative film (C) C3.
(印刷模様層を有するフィルム(C)C4の製造)
前記PPフィルムにグラビア印刷機にて、インキB2で木目柄を印刷し(版2)、さらにインキB5及びB6で2版の木目柄を印刷した(版3、版4)上に、インキB4で木目柄を印刷して(版5)、装飾フィルム(C)C4を製造した。
(Production of film (C) C4 having printed pattern layer)
On the PP film, a gravure printing machine was used to print a wood grain pattern with ink B2 (plate 2), and further onto a two-layer wood grain pattern printed with inks B5 and B6 (plate 3, plate 4), with ink B4 A wood grain pattern was printed (plate 5) to produce a decorative film (C) C4.
(印刷模様層を有するフィルム(C)C5の製造)
前記PPフィルムにグラビア印刷機にて、インキB2でベタ層を印刷した(版1)後、インキB5及びB6で2版の木目柄を印刷して(版3、版4)、装飾フィルム(C)C5を製造した。
(Production of film (C) C5 having printed pattern layer)
After printing a solid layer with the ink B2 on the PP film with a gravure printing machine (version 1), printing a two-grain grain pattern with the inks B5 and B6 (version 3 and version 4), the decorative film (C ) C5 was produced.
(印刷模様層を有するフィルム(C)C6の製造)
前記PPフィルムにグラビア印刷機にて、インキB1でベタ層を印刷した(版1)後、インキB1で木目柄を印刷し(版2)、さらにインキB5及びB6で2版の木目柄を印刷した(版3、版4)上に、インキB1で木目柄を印刷して(版5)、装飾フィルム(C)C6を製造した。
(Production of film (C) C6 having printed pattern layer)
On the PP film, a solid layer was printed with ink B1 on a gravure printing machine (plate 1), then a wood grain pattern was printed with ink B1 (plate 2), and a two-grain wood grain pattern was printed with inks B5 and B6. A wood grain pattern was printed with ink B1 on (Plate 3, Plate 4) (Plate 5) to produce a decorative film (C) C6.
(印刷模様層を有するフィルム(C)C7の製造)
前記PPフィルムにグラビア印刷機にてインキB3で木目柄を印刷し(版2)、装飾フィルム(C)C7を製造した。
表2に、フィルム(C)C1〜C7の印刷層構成を示す。
(Production of film (C) C7 having printed pattern layer)
A wood grain pattern was printed on the PP film with an ink B3 using a gravure printer (plate 2) to produce a decorative film (C) C7.
Table 2 shows the print layer configuration of the films (C) C1 to C7.
(製造例3−1)水圧転写フィルムD1の製造
支持体フィルムとしてアイセロ化学社製のPVA(膜厚30μm、幅360mm)の光沢面に、硬化性樹脂A2をコンマコーターで固形分膜厚20μmになるように塗工し、次いで60℃で2分間乾燥して、フィルム(A2)を製造した。このフィルム(A2)の硬化性樹脂層と、印刷模様層を有するフィルム(C)C1のインキ層とを相対するように、60℃でラミネートし、ラミネートしたフィルムをそのまま巻き取って水圧転写用フィルムD1を製造した。
(Production Example 3-1) Manufacture of hydraulic transfer film D1 As a support film, on the glossy surface of PVA (film thickness 30 μm, width 360 mm) manufactured by Aicero Chemical Co., Ltd., curable resin A2 with a comma coater to a solid film thickness of 20 μm And then dried at 60 ° C. for 2 minutes to produce a film (A2). The film (A2) curable resin layer and the printed pattern layer (C) C1 ink layer are laminated so as to face each other at 60 ° C., and the laminated film is wound up as it is and the film for hydraulic transfer. D1 was produced.
(製造例3−2)水圧転写フィルムD2の製造
水圧転写フィルムD1と同様に、PVAに硬化性樹脂A3をコンマコーターで固形分膜厚20μmになるように塗工し、フィルム(A3)を製造した。このフィルム(A3)の硬化性樹脂層と、印刷模様層を有するフィルム(C)C1のインキ層とラミネートし、水圧転写用フィルムD2を製造した。
(Production Example 3-2) Manufacture of hydraulic transfer film D2 Similarly to the hydraulic transfer film D1, curable resin A3 is applied to PVA with a comma coater so as to have a solid film thickness of 20 μm, and a film (A3) is manufactured. did. The curable resin layer of this film (A3) and the ink layer of film (C) C1 having a printed pattern layer were laminated to produce a hydraulic transfer film D2.
(製造例3−3)水圧転写フィルムD3の製造
水圧転写フィルムD1と同様に、PVAに硬化性樹脂A2をコンマコーターで固形分膜厚20μmになるように塗工し、フィルム(A2)を製造した。このフィルム(A2)の硬化性樹脂層と、印刷模様層を有するフィルム(C)C2のインキ層とラミネートし、水圧転写用フィルムD3を製造した。
(Production Example 3-3) Manufacture of hydraulic transfer film D3 As with the hydraulic transfer film D1, a curable resin A2 is applied to PVA with a comma coater so that the solid content film thickness is 20 μm, and a film (A2) is manufactured. did. The curable resin layer of this film (A2) and the ink layer of the film (C) C2 having a printed pattern layer were laminated to produce a hydraulic transfer film D3.
(製造例3−4)水圧転写フィルムD4の製造
水圧転写フィルムD1と同様に、PVAに硬化性樹脂A2をコンマコーターで固形分膜厚20μmになるように塗工し、フィルム(A2)を製造した。このフィルム(A2)の硬化性樹脂層と、印刷模様層を有するフィルム(C)C3のインキ層とラミネートし、水圧転写用フィルムD4を製造した。
(Manufacture example 3-4) Manufacture of hydraulic transfer film D4 Similarly to hydraulic transfer film D1, curable resin A2 is applied to PVA with a comma coater so as to have a solid film thickness of 20 μm to manufacture film (A2). did. The curable resin layer of this film (A2) and the ink layer of the film (C) C3 having a printed pattern layer were laminated to produce a hydraulic transfer film D4.
(製造例3−5)水圧転写フィルムD5の製造
水圧転写フィルムD1と同様に、PVAに硬化性樹脂A2をコンマコーターで固形分膜厚20μmになるように塗工し、フィルム(A2)を製造した。このフィルム(A2)の硬化性樹脂層と、印刷模様層を有するフィルム(C)C4のインキ層とラミネートし、水圧転写用フィルムD5を製造した。
(Manufacturing example 3-5) Manufacture of hydraulic transfer film D5 Similarly to the hydraulic transfer film D1, curable resin A2 is applied to PVA with a comma coater so as to have a solid film thickness of 20 μm to manufacture a film (A2). did. The curable resin layer of this film (A2) and the ink layer of the film (C) C4 having a printed pattern layer were laminated to produce a hydraulic transfer film D5.
(製造例3−6)水圧転写フィルムD6の製造
水圧転写フィルムD1と同様に、PVAに硬化性樹脂A2をコンマコーターで固形分膜厚20μmになるように塗工し、フィルム(A2)を製造した。このフィルム(A2)の硬化性樹脂層と、印刷模様層を有するフィルム(C)C5のインキ層とラミネートし、水圧転写用フィルムD6を製造した。
(Manufacture example 3-6) Manufacture of hydraulic transfer film D6 Similarly to hydraulic transfer film D1, curable resin A2 is applied to PVA with a comma coater so as to have a solid film thickness of 20 μm, and film (A2) is manufactured. did. The curable resin layer of this film (A2) and the ink layer of film (C) C5 having a printed pattern layer were laminated to produce a hydraulic transfer film D6.
(製造例3−7)水圧転写フィルムD7の製造
水圧転写フィルムD1と同様に、PVAに硬化性樹脂A2をコンマコーターで固形分膜厚20μmになるように塗工し、フィルム(A2)を製造した。このフィルム(A2)の硬化性樹脂層と、印刷模様層を有するフィルム(C)C7のインキ層とラミネートし、水圧転写用フィルムD7を製造した。
(Manufacture example 3-7) Manufacture of hydraulic transfer film D7 Similarly to hydraulic transfer film D1, curable resin A2 is applied to PVA with a comma coater so as to have a solid film thickness of 20 μm, and film (A2) is manufactured. did. The curable resin layer of this film (A2) and the ink layer of the film (C) C7 having a printed pattern layer were laminated to produce a hydraulic transfer film D7.
(水圧転写フィルムの製造例)
(製造例3−H1)水圧転写フィルムHD1の製造
水圧転写フィルムD1と同様に、PVAに硬化性樹脂A1をコンマコーターで固形分膜厚20μmになるように塗工し、次いで60℃で2分間乾燥して、フィルム(A1)を製造した。このフィルム(A1)の硬化性樹脂層と、印刷模様層を有するフィルム(C)C1のインキ層とを相対するように、60℃でラミネートし、ラミネートしたフィルムをそのまま巻き取って水圧転写用フィルムHD1を製造した。
(Production example of hydraulic transfer film)
(Production Example 3-H1) Production of hydraulic transfer film HD1 Similar to the hydraulic transfer film D1, curable resin A1 was applied to PVA with a comma coater to a solid content film thickness of 20 μm, and then at 60 ° C. for 2 minutes. It dried and the film (A1) was manufactured. The film (A1) curable resin layer and the printed pattern layer (C) C1 ink layer are laminated at 60 ° C. so as to face each other. HD1 was produced.
(製造例3−H2)水圧転写フィルムHD2の製造
水圧転写フィルムD1と同様に、PVAに硬化性樹脂A1をコンマコーターで固形分膜厚20μmになるように塗工し、フィルム(A1)を製造した。このフィルム(A1)の硬化性樹脂層と、印刷模様層を有するフィルム(C)C2のインキ層とラミネートし、水圧転写用フィルムHD2を製造した。
(Production Example 3-H2) Production of hydraulic transfer film HD2 Similar to the hydraulic transfer film D1, a curable resin A1 is applied to PVA with a comma coater so as to have a solid film thickness of 20 μm to produce a film (A1). did. The curable resin layer of this film (A1) and the ink layer of the film (C) C2 having a printed pattern layer were laminated to produce a hydraulic transfer film HD2.
(製造例3−H3)水圧転写フィルムHD3の製造
水圧転写フィルムD1と同様に、PVAに硬化性樹脂A2をコンマコーターで固形分膜厚20μmになるように塗工し、フィルム(A1)を製造した。このフィルム(A2)の硬化性樹脂層と、印刷模様層を有するフィルム(C)C6のインキ層とラミネートし、水圧転写用フィルムHD3を製造した。
(Production Example 3-H3) Manufacture of hydraulic transfer film HD3 In the same manner as hydraulic transfer film D1, curable resin A2 is applied to PVA with a comma coater so as to have a solid content film thickness of 20 μm to manufacture film (A1). did. The curable resin layer of this film (A2) and the ink layer of the film (C) C6 having a printed pattern layer were laminated to produce a hydraulic transfer film HD3.
(製造例3−H4)水圧転写フィルムHD4の製造
水圧転写フィルムD1と同様に、PVAに硬化性樹脂A1をコンマコーターで固形分膜厚20μmになるように塗工し、フィルム(A1)を製造した。このフィルム(A1)の硬化性樹脂層と、印刷模様層を有するフィルム(C)C5のインキ層とラミネートし、水圧転写用フィルムHD4を製造した。
(Manufacture example 3-H4) Manufacture of hydraulic transfer film HD4 Similarly to hydraulic transfer film D1, curable resin A1 is applied to PVA with a comma coater so as to have a solid film thickness of 20 μm to manufacture film (A1). did. The curable resin layer of this film (A1) and the ink layer of the film (C) C5 having a printed pattern layer were laminated to produce a hydraulic transfer film HD4.
前記製造例3−1〜3−7,3−H1〜3−H4により得られた水圧転写フィルムD1〜D7、HD1〜HD4のフィルム仕様と製造条件を表3及び表4にまとめた。 Tables 3 and 4 summarize the film specifications and production conditions of the hydraulic transfer films D1 to D7 and HD1 to HD4 obtained by Production Examples 3-1 to 3-7 and 3-H1 to 3-H4.
(実施例1)
水槽に25℃の水を入れ、剥離性フィルムを剥離した水圧転写用フィルムD1のPVA側を下にして水面に浮かべた。活性化剤(イソブタノール/メチルイソアミルケトン/D−リモネン/酢酸イソアミル=45/30/20/5)を25g/m2噴霧し、15秒後、ベージュ色のABS成型体(210mm×75mmの柄見本用プレート)を水圧転写フィルムから水中に向かって挿入し水圧転写した。
PVAを日伸精機株式会社製ジェットウォッシャーJW−350Bを用い、28Hz、45℃、2分間の条件で水洗除去した後、80℃で30分間乾燥させた。次にGSユアサ株式会社製のUV照射装置及びGSユアサ株式会社製の高圧水銀灯(主波長は254nm、313nm、365nm、405nm、436nm、546nm、577nm)を用いて、照射量1000mJ/cm2、ピーク強度200mW/cm2のUV光を照射することにより、硬化性樹脂層を硬化させることで、良好な深み感、及び良好な木質的照り感を有する水圧転写体を得た。
Example 1
Water at 25 ° C. was placed in a water tank and floated on the water surface with the PVA side of the hydraulic transfer film D1 from which the peelable film was peeled down. An activator (isobutanol / methylisoamyl ketone / D-limonene / isoamyl acetate = 45/30/20/5) was sprayed at 25 g / m 2 , and after 15 seconds, a beige ABS molded body (210 mm × 75 mm handle) The sample plate was inserted into the water from the hydraulic transfer film and transferred hydraulically.
The PVA was washed with water using a jet washer JW-350B manufactured by Nisshin Seiki Co., Ltd. under conditions of 28 Hz, 45 ° C. and 2 minutes, and then dried at 80 ° C. for 30 minutes. Next, using a UV irradiation apparatus manufactured by GS Yuasa Co., Ltd. and a high-pressure mercury lamp manufactured by GS Yuasa Co., Ltd. (main wavelengths are 254 nm, 313 nm, 365 nm, 405 nm, 436 nm, 546 nm, 576 nm), the irradiation amount is 1000 mJ / cm 2 , peak By irradiating with UV light having an intensity of 200 mW / cm 2 , the curable resin layer was cured to obtain a hydraulic transfer body having a good depth feeling and a good woody feeling.
(実施例2)
実施例1と同様に、水圧転写用フィルムD2を用いて転写した結果、深み感、及び良好な木質的照り感を有する水圧転写体を得た。
(Example 2)
As in Example 1, as a result of the transfer using the hydraulic transfer film D2, a hydraulic transfer body having a sense of depth and good woody feeling was obtained.
(実施例3)
実施例2と同様に、水圧転写用フィルムD3を用いて転写した結果、良好な深み感、及び良好な木質的照り感を有する水圧転写体を得た。
(Example 3)
As in Example 2, as a result of the transfer using the hydraulic transfer film D3, a hydraulic transfer body having a good depth feeling and a good woody feeling was obtained.
(実施例4)
実施例2と同様に、水圧転写用フィルムD4を用いて転写した結果、良好な深み感、及び良好な木質的照り感を有する水圧転写体を得た。
Example 4
As in Example 2, as a result of the transfer using the hydraulic transfer film D4, a hydraulic transfer body having a good depth feeling and a good woody feeling was obtained.
(実施例5)
実施例2と同様に、水圧転写用フィルムD5を用いて転写した結果、良好な深み感、及び良好な木質的照り感を有する水圧転写体を得た。
(Example 5)
As in Example 2, as a result of the transfer using the hydraulic transfer film D5, a hydraulic transfer body having a good depth feeling and a good woody feeling was obtained.
(実施例6)
実施例2と同様に、水圧転写用フィルムD6を用いて転写した結果、良好な深み感、及び良好な木質的照り感を有する水圧転写体を得た。
(Example 6)
As in Example 2, as a result of the transfer using the hydraulic transfer film D6, a hydraulic transfer body having a good depth feeling and a good woody feeling was obtained.
(実施例7)
実施例2と同様に、水圧転写用フィルムD7を用いて転写した結果、良好な深み感、及び良好な木質的照り感を有する水圧転写体を得た。
(Example 7)
As in Example 2, as a result of the transfer using the hydraulic transfer film D7, a hydraulic transfer body having a good depth feeling and a good woody feeling was obtained.
(比較例1)
実施例1と同様に、水圧転写用フィルムHD1を用いて転写した結果、良好な深み感はるものの木質的照り感のない水圧転写体を得た。
(Comparative Example 1)
As in Example 1, as a result of transfer using the hydraulic transfer film HD1, a hydraulic transfer body having a good depth feeling but no woody feeling was obtained.
(比較例2)
実施例2と同様に、水圧転写用フィルムHD2を用いて転写した結果、良好な深み感はるものの木質的照り感のない水圧転写体を得た。
(Comparative Example 2)
As in Example 2, as a result of the transfer using the hydraulic transfer film HD2, a hydraulic transfer body having a good depth feeling but no woody feeling was obtained.
(比較例3)
実施例2と同様に、水圧転写用フィルムHD3を用いて転写した結果、良好な木質的照り感はあるものの、深み感のない水圧転写体を得た。
(Comparative Example 3)
As in Example 2, as a result of the transfer using the hydraulic transfer film HD3, a hydraulic transfer body having a good woody feeling but no depth was obtained.
(比較例4)
実施例2と同様に、水圧転写用フィルムHD4を用いて転写した結果、深み感、及び木質的照り感が共にない水圧転写体を得た。
(Comparative Example 4)
As in Example 2, as a result of the transfer using the hydraulic transfer film HD4, a hydraulic transfer body having neither a sense of depth nor a woody feeling was obtained.
以上の結果より、水圧転写フィルムとしてD1〜D7を使用した実施例1〜7は、深み感及び照り感を持つものが得られた。実施例2は、硬化性樹脂層として光輝性顔料が10%入った例であるが、標準光源(D65)下では、ややギラギラした視認性を有したため、深み感を△とした。ただし、自動車の内装等、やや遮光された中では、この程度の方が好ましい場合もある。 From the above results, Examples 1 to 7 using D1 to D7 as the hydraulic transfer film had a feeling of depth and shine. Example 2 is an example in which 10% of a glitter pigment is contained as a curable resin layer. However, under the standard light source (D65), it had a slightly glaring visibility, and thus the depth feeling was Δ. However, this level may be preferable when the vehicle interior is slightly shielded from light.
本発明の製造方法で得られる水圧転写体は、テレビ、ビデオ、エアコン、ラジオカセット、携帯電話、冷蔵庫等の家庭電化製品;パーソナルコンピューター、ファックスやプリンター等のOA機器;ファンヒーターやカメラなどの家庭製品のハウジング部分;テーブル、タンス、柱などの家具部材;バスタブ、システムキッチン、扉、窓枠などの建築部材;電卓、電子手帳などの雑貨;自動車内装パネル、自動車やオートバイの外板、ホイールキャップ、スキーキャリヤ、自動車用キャリアバッグなどの車内外装品;ゴルフクラブ、スキー板、スノーボード、ヘルメット、ゴーグルなどのスポーツ用品;広告用立体像、看板、モニュメントなどが挙げられ、曲面を有しかつ意匠性を必要とする成形品に特に有用に用いられ、極めて広い分野で使用可能である。 The hydraulic transfer body obtained by the production method of the present invention includes home appliances such as televisions, videos, air conditioners, radio cassettes, mobile phones and refrigerators; OA equipment such as personal computers, fax machines and printers; homes such as fan heaters and cameras. Housing parts of products; furniture parts such as tables, chests and pillars; building parts such as bathtubs, system kitchens, doors and window frames; miscellaneous goods such as calculators and electronic notebooks; automobile interior panels, automobile and motorcycle skins, wheel caps Car interiors and accessories such as ski carriers and automobile carrier bags; sports equipment such as golf clubs, skis, snowboards, helmets and goggles; 3D images for advertising, signboards, monuments, etc. Is particularly useful for molded products that require It is possible to use.
Claims (5)