JP5034937B2 - 摺動部材用樹脂組成物及びこれを使用した摺動部材 - Google Patents
摺動部材用樹脂組成物及びこれを使用した摺動部材 Download PDFInfo
- Publication number
- JP5034937B2 JP5034937B2 JP2007340520A JP2007340520A JP5034937B2 JP 5034937 B2 JP5034937 B2 JP 5034937B2 JP 2007340520 A JP2007340520 A JP 2007340520A JP 2007340520 A JP2007340520 A JP 2007340520A JP 5034937 B2 JP5034937 B2 JP 5034937B2
- Authority
- JP
- Japan
- Prior art keywords
- sliding member
- resin composition
- resin
- metal
- friction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
滑り速度 20m/min
荷重 20kgf/cm2
試験時間 8時間
潤滑 無潤滑
相手材 機械構造用炭素鋼(S45C)
滑り速度 10m/min
荷重 100kgf/cm2
試験時間 8時間
潤滑 無潤滑
相手材 機械構造用炭素鋼(S45C)
滑り速度 5m/min
荷重 50kgf/cm2
試験時間 8時間
潤滑 潤滑油(出光興産社製ATF−DII)
相手材 機械構造用炭素鋼(S45C)
滑り速度 5m/min
荷重 100kgf/cm2
試験時間 8時間
潤滑 潤滑油(出光興産社製ATF−DII)
相手材 機械構造用炭素鋼(S45C)
実 施 例
1 2 3 4
PTFE 73 72.5 72.5 69.5
硫酸バリウム 15 15 15 18
沈降性
簸 性 ○ ○ ○ ○
リン酸塩 10 10 10 10
ピロリン酸カルシウム ○ ○ ○
リン酸水素カルシウム ○
ポリイミド樹脂 2 2 2 2
芳香族
熱硬化 ○ ○ ○ ○
固体潤滑剤 − 0.5 0.5 0.5
黒鉛 ○ ○ ○
二硫化モリブデン
スラスト試験(1)
摩擦係数(×10−2) 11.5 11 13 12
摩耗量(μm) 5 4 8 5
スラスト試験(2)
摩擦係数(×10−2) 7 7 8.5 7.5
摩耗量(μm) 14 12 16 12
実 施 例
5 6 7 8
PTFE 69 69 72 71.5
硫酸バリウム 18 18 20 20
沈降性 ○
簸 性 ○ ○ ○
リン酸塩 10 10 5 5
ピロリン酸カルシウム ○ ○ ○
リン酸水素カルシウム ○
ポリイミド樹脂 2.5 2.5 3 3
芳香族
熱硬化 ○ ○ ○ ○
固体潤滑剤 0.5 0.5 − 0.5
黒鉛 ○ ○
二硫化モリブデン ○
スラスト試験(1)
摩擦係数(×10−2) 14 15 15 13
摩耗量(μm) 5 6 4 4
スラスト試験(2)
摩擦係数(×10−2) 7.5 8 9 8
摩耗量(μm) 12 14 17 13
実 施 例
9 10 11 12
PTFE 68 67.5 67.5 65
硫酸バリウム 20 20 20 20
沈降性
簸 性 ○ ○ ○ ○
リン酸塩 10 10 10 10
ピロリン酸カルシウム ○ ○ ○
リン酸水素カルシウム ○
ポリイミド樹脂 2 2 2 4
芳香族 ○ ○
熱硬化 ○ ○
固体潤滑剤 − 0.5 0.5 1
黒鉛 ○ ○
二硫化モリブデン ○
スラスト試験(1)
摩擦係数(×10−2) 14 12 13 14
摩耗量(μm) 3 5 6 4
スラスト試験(2)
摩擦係数(×10−2) 7.5 7.5 8 7.5
摩耗量(μm) 13 13 15 10
実 施 例
13 14 15
PTFE 67 66 62
硫酸バリウム 25 25 25
沈降性
簸 性 ○ ○ ○
リン酸塩 5 5 10
ピロリン酸カルシウム ○ ○ ○
リン酸水素カルシウム
ポリイミド樹脂 3 3 3
芳香族
熱硬化 ○ ○ ○
固体潤滑剤 − 1 −
黒鉛 ○
二硫化モリブデン
スラスト試験(1)
摩擦係数(×10−2) 14 16 15
摩耗量(μm) 3 6 2
スラスト試験(2)
摩擦係数(×10−2) 8.5 8 9
摩耗量(μm) 16 14 9
実 施 例
16 17 18 19 20
PTFE 70 69 68 67.5 70.5
硫酸バリウム 15 15 18 18 15
沈降性
簸 性 ○ ○ ○ ○ ○
リン酸塩 10 10 10 10 10
ピロリン酸カルシウム ○ ○ ○ ○ ○
リン酸水素カルシウム
ポリイミド樹脂 − − − − 2
芳香族
熱硬化 ○
焼成フェノール樹脂 5 5 − − −
ポリフェンレンスルホン樹脂− − 4 4 2
固体潤滑剤 − 1 − 0.5 0.5
黒鉛 ○ ○ ○
二硫化モリブデン
スラスト試験(1)
摩擦係数(×10−2) 12 12 13 12 13
摩耗量(μm) 3 3 4 3 4
スラスト試験(2)
摩擦係数(×10−2) 7 7 8 7 9
摩耗量(μm) 17 16 13 12 13
比 較 例
1 2 3
PTFE 50 70 80
硫酸バリウム − − −
沈降性
簸 性
リン酸塩 − 10 −
ピロリン酸カルシウム ○
リン酸水素カルシウム
ポリイミド樹脂 − − 20
芳香族 ○
熱硬化
鉛 50 20 −
スラスト試験(1)
摩擦係数(×10−2) 14 16 19
摩耗量(μm) 31 8 12
スラスト試験(2)
摩擦係数(×10−2) * 11 10
摩耗量(μm) * 85 20
(注)*は試験開始後2時間で摩擦係数が急激に上昇し試験を中止したため、測
定できなかった。
実 施 例
1 2 4 7 8
往復動試験(3)
摩擦係数(×10−3) 26 24 20 26 25
摩耗量(μm) 6 5 2 4 3
往復動試験(4)
摩擦係数(×10−3) 36 35 26 30 28
摩耗量(μm) 8 5 4 6 5
実 施 例
9 10 12 13 14
往復動試験(3)
摩擦係数(×10−3) 21 23 25 28 26
摩耗量(μm) 2 3 5 5 4
往復動試験(4)
摩擦係数(×10−3) 29 28 30 33 30
摩耗量(μm) 4 4 6 6 5
実 施 例
16 17 18 19 20
往復動試験(3)
摩擦係数(×10−3) 31 29 27 28 27
摩耗量(μm) 4 4 3 4 3
往復動試験(4)
摩擦係数(×10−3) 35 38 30 33 32
摩耗量(μm) 6 6 5 3 5
比 較 例
2 3
往復動試験(3)
摩擦係数(×10−3) 100 28
摩耗量(μm) 48 7
往復動試験(4)
摩擦係数(×10−3) * 51
摩耗量(μm) * 18
(注)*は試験開始後30分で摩擦係数が急激に上昇したため試験を中止した。
実 施 例
21 22 23 24
PTFE 73 73 69.5 69.5
硫酸バリウム 15 15 18 18
沈降性
簸 性 ○ ○ ○ ○
リン酸塩 10 10 10 10
ピロリン酸カルシウム ○ ○ ○ ○
リン酸水素カルシウム
ポリイミド樹脂 2 2 2 2
芳香族
熱硬化 ○ ○ ○ ○
固体潤滑剤 − − 0.5 0.5
黒鉛 ○ ○
二硫化モリブデン
基材種類 A B A B
スラスト試験(2)
摩擦係数(×10−2) 7 7 7 8
摩耗量(μm) 12 13 11 12
実 施 例
25 26 27 28
PTFE 68 67.5 66 62
硫酸バリウム 20 20 20 25
沈降性
簸 性 ○ ○ ○ ○
リン酸塩 10 10 10 10
ピロリン酸カルシウム ○ ○ ○ ○
リン酸水素カルシウム
ポリイミド樹脂 2 2 4 3
芳香族
熱硬化 ○ ○ ○ ○
固体潤滑剤 − 0.5 − −
黒鉛 ○
二硫化モリブデン
基材種類 A A A B
スラスト試験(2)
摩擦係数(×10−2) 8 8 9 8
摩耗量(μm) 13 11 10 11
実 施 例
29 30 31 32 33
PTFE 70 69 68 67.5 70.5
硫酸バリウム 15 15 18 18 15
沈降性
簸 性 ○ ○ ○ ○ ○
リン酸塩 10 10 10 10 10
ピロリン酸カルシウム ○ ○ ○ ○ ○
リン酸水素カルシウム
ポリイミド樹脂 − − − − 2
芳香族
熱硬化 ○
焼成フェノール樹脂 5 5 − − −
ポリフェニレンスルホン樹脂− − 4 4 2
固体潤滑剤 − 1 − 0.5 0.5
黒鉛 ○ ○ ○
二硫化モリブデン
基材種類 A B B A A
スラスト試験(2)
摩擦係数(×10−2) 7 7 8 7 9
摩耗量(μm) 15 14 13 13 13
比 較 例
4 5 6
PTFE 70 70 80
硫酸バリウム − − −
沈降性
簸 性
リン酸塩 10 10 −
ピロリン酸カルシウム ○ ○
リン酸水素カルシウム
ポリイミド樹脂 − − 20
芳香族
熱硬化 ○
鉛 20 20 −
基材種類 A B A
スラスト試験(2)
摩擦係数(×10−2) 12 13 11
摩耗量(μm) 90 96 25
2 多孔質金属焼結層
3 被覆層
4 エキスパンドメタル
5 辺
6 網目
7 被覆層
8 織組ワイヤーメッシュ
9 被覆層
Claims (3)
- 鋼裏金と、該鋼裏金上に形成された多孔質金属焼結層と、該多孔質金属層の孔隙および表面に充填被覆された樹脂組成物の被覆層とを備えた複層摺動部材であって、該被覆層を形成する樹脂組成物が、硫酸バリウム5〜40重量%、リン酸塩1〜30重量%、芳香族ポリイミド樹脂および熱硬化性ポリイミド樹脂から選択されるポリイミド樹脂1〜10重量%および残部が四ふっ化エチレン樹脂から成ることを特徴とする複層摺動部材。
- リン酸塩は、リン酸三リチウム、リン酸水素リチウム、ピロリン酸リチウム、リン酸三カルシウム、リン酸水素カルシウムおよびピロリン酸カルシウムから選択される請求項1に記載の複層摺動部材。
- 樹脂組成物は、さらに黒鉛または二硫化モリブデンを5重量%以下の割合で含有する請求項1又は2に記載の複層摺動部材。