JP4971686B2 - Wrinkle composition and eyelash cosmetics and hair cosmetics using the same - Google Patents
Wrinkle composition and eyelash cosmetics and hair cosmetics using the same Download PDFInfo
- Publication number
- JP4971686B2 JP4971686B2 JP2006145216A JP2006145216A JP4971686B2 JP 4971686 B2 JP4971686 B2 JP 4971686B2 JP 2006145216 A JP2006145216 A JP 2006145216A JP 2006145216 A JP2006145216 A JP 2006145216A JP 4971686 B2 JP4971686 B2 JP 4971686B2
- Authority
- JP
- Japan
- Prior art keywords
- cosmetics
- oil
- eyelashes
- cosmetic
- eyelash
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は曳糸性組成物およびそれを用いた睫毛用化粧料、毛髪用化粧料、特にアミノ酸誘導体変性シリコーンを含む曳糸性組成物およびそれを用いた睫毛用、毛髪用化粧料に関するものである。 TECHNICAL FIELD The present invention relates to a cocoon composition, an eyelash cosmetic using the same, and a hair cosmetic, in particular, an cocoon composition containing an amino acid derivative-modified silicone, and an eyelash and hair cosmetic using the same. is there.
成形性、作業性の観点から、化粧品、医薬部外品のみならず、塗料、樹脂などの各種分野で曳糸性を有する組成物の研究が行われている。曳糸性とは、例えば、棒状物の先端を曳糸性組成物中に浸した後、上方へ持ち上げた場合に糸を引くように伸ばすことができる特性である。これを各種用途に適用させるためには、目的に応じた曳糸性および適度な粘稠性が要求される。 From the viewpoint of moldability and workability, not only cosmetics and quasi-drugs, but also compositions having spinnability have been studied in various fields such as paints and resins. The spinnability is a characteristic that, for example, when the tip of a rod-like object is immersed in the spinnable composition and then lifted upward, it can be stretched to pull the thread. In order to apply this to various uses, a spinnability and an appropriate consistency according to the purpose are required.
例えば曳糸性組成物の用途として睫毛用化粧料が挙げられる。この睫毛用化粧料は、睫毛を太く長くみせることで目元をはっきりさせる効果を有するものであり、その目的のために曳糸性成分を配合し、睫毛にボリューム感やロングラッシュ効果を付与することが図られる。具体的には曳糸性の水溶性高分子である高重合度ポリエチレングリコールを睫毛用化粧料に配合して睫毛のボリュームアップを図り、かつ長くみせようとする技術がある（例えば、特許文献１を参照）。
一方で、睫毛用化粧料に繊維を粘着性被膜形成剤と共に配合し、繊維を睫毛に塗布させて睫毛をボリュームアップさせる技術も種々開発されている（例えば、特許文献２を参照）。
On the other hand, various techniques have been developed for blending fibers with eyelash cosmetics together with an adhesive film-forming agent and applying the fibers to the eyelashes to increase the volume of the eyelashes (see, for example, Patent Document 2).
しかしながら、前記曳糸性の水溶性高分子を配合した睫毛用化粧料は、ある程度のボリューム感が得られるものの、曳糸性は十分でなくロングラッシュ効果は十分満足できるものではなかった。また、効果の向上のために配合量を高めてしまうと、他の油性成分との相溶性が悪くなることに起因して透明感が低下し、その結果、美的効果が劣るものとなってしまう。
繊維を配合した睫毛用化粧料は、ロングラッシュ効果は高いものの、繊維が睫毛に過剰に塗布されると不自然な仕上がりになり、さらに繊維による光の散乱のためにツヤのある外観が得られない。また、被膜剤が固過ぎてしまうことによって繊維が目の下に粉状に落ちてしまう場合がある。
本発明は前述の事情に鑑みなされたものであり、その目的は、透明性に優れた曳糸性組成物、さらにそれを睫毛用化粧料に用いた場合には、繊維を配合しなくても睫毛を長く見せる効果に優れ、自然な仕上がり感を付与することが可能な睫毛用化粧料、そして毛髪用化粧料に用いた場合には、自由な形に髪をセットすることができ、髪型がくずれにくい毛髪用化粧料を提供することにある。
However, the eyelash cosmetics containing the above-mentioned spinnable water-soluble polymer can provide a certain level of volume, but the spinnability is not sufficient and the long lash effect is not fully satisfactory. Further, if the blending amount is increased in order to improve the effect, the transparency is lowered due to the poor compatibility with other oil components, and as a result, the aesthetic effect becomes inferior. .
Although the long lash effect is high, the cosmetics for eyelashes with fibers have an unnatural finish when the fibers are excessively applied to the eyelashes, and a glossy appearance is obtained due to light scattering by the fibers. Absent. Further, when the coating agent is too hard, the fibers may fall into powder under the eyes.
The present invention has been made in view of the above-mentioned circumstances, and the purpose thereof is a stringent composition excellent in transparency, and when it is used in eyelash cosmetics, it is not necessary to add fibers. When used in eyelash cosmetics, which have an excellent effect of making eyelashes look long and can give a natural finish, and when used in hair cosmetics, the hair can be set freely. The object is to provide a cosmetic for hair that is difficult to break.
前記目的を達成するために、本発明者らが鋭意研究を行った結果、特定のリジン誘導体変性シリコーンとシリコーン化プルランを含む組成物において、透明性に優れた曳糸性粗組成物が得られ、それを睫毛用化粧料に用いた場合には、ロングラッシュ効果および自然な仕上がり感に優れることを見出し、本発明を完成するに至った。
すなわち、本発明の曳糸性組成物は、
（ａ）下記一般式（I）〜（III）のいずれかで表されるリジン誘導体変性シリコーンと、
（ｂ）下記一般式（V）で表されるシリコーン化プルランとを含有することを特徴とする。
That is, the spinnable composition of the present invention is
(A) a lysine derivative-modified silicone represented by any one of the following general formulas (I) to (III);
(B) It contains siliconized pullulan represented by the following general formula (V).
前記本発明にかかる曳糸性組成物において、（ａ）上記一般式（I）〜（III）のいずれかで表されるリジン誘導体変性シリコーンと（ｂ）上記一般式（V）で表されるシリコーン化プルランの配合量比（（ａ）／（ｂ））が２／５〜２／１であることが好適である。 In the spinnable composition according to the present invention, (a) a lysine derivative-modified silicone represented by any one of the general formulas (I) to (III) and (b) represented by the general formula (V). It is preferable that the blending ratio ((a) / (b)) of the siliconized pullulan is 2/5 to 2/1.
前記本発明にかかる曳糸性組成物において、さらに（ｃ）油分を含むことを特徴とする。
また、前記（ｃ）油分の総重量の２０質量％以上がシリコーン油であることが好適である。
The spinnable composition according to the present invention further includes (c) an oil component.
In addition, it is preferable that 20% by mass or more of the total weight of the (c) oil is silicone oil.
また、本発明は前記曳糸性組成物を用いた睫毛用化粧料を提供するものである。
また、本発明は前記曳糸性組成物を用いた毛髪用化粧料を提供するものである。
Moreover, this invention provides the cosmetics for eyelashes using the said spinnable composition.
Moreover, this invention provides the cosmetics for hair using the said spinnable composition.
本発明によれば、特定のリジン誘導体変性シリコーンおよび特定のシリコーン化プルランを含む曳糸性組成物において、極めて優れた透明性を有し、それを睫毛用化粧料に用いた場合には、繊維を配合せずとも睫毛を長く見せる効果に優れ、自然な仕上がり感を付与することが可能である睫毛用化粧料、および髪を自由な形にセットすることができ、髪型がくずれにくい毛髪用化粧料を得ることができる。 According to the present invention, in a spine composition containing a specific lysine derivative-modified silicone and a specific silicone-modified pullulan, the fiber composition has extremely excellent transparency, and when used in cosmetics for eyelashes, It is excellent in the effect of making the eyelashes look long without blending, and the cosmetics for eyelashes that can give a natural feeling of finish, and the hair makeup that can set the hair in a free shape and the hairstyle is difficult to break You can get a fee.
以下、本発明の実施の形態について詳細に説明する。本発明はこれにより何ら限定されるものではない。
本発明にかかる曳糸性組成物における「曳糸性」とは、棒状物の先端を該曳糸性組成物中に浸した後、上方へ持ち上げた場合に糸を引くように伸ばすことができる特性であり、目視で確認可能なものとする。
Hereinafter, embodiments of the present invention will be described in detail. The present invention is not limited thereby.
“Spinnability” in the spinnable composition according to the present invention means that the rod-like object can be stretched so as to pull the thread when it is lifted upward after being dipped in the spinnable composition. It is a characteristic and shall be visually confirmed.
（ａ）リジン誘導体変性シリコーン
本発明におけるリジン誘導体変性シリコーンは、下記一般式（I）〜（III）のいずれかで表される。
上記化合物のうち、特に好ましい化合物は一般式（I）および（II）の構造において、ｘが５０〜２００、ｎおよびｍが１０、Ｒ３がエチル基もしくはイソブチル基である化合物である。
具体的には、下記式（VI）〜（IX）で表される構造を有する化合物である。
Specifically, it is a compound having a structure represented by the following formulas (VI) to (IX).
本発明にかかる曳糸性組成物を睫毛用化粧料または毛髪用化粧料に用いる場合、上記一般式（I）〜（III）で表されるリジン誘導体変性シリコーンの好適な配合量（実分）は、化粧料全体において１〜２０質量％、より好ましくは３〜１０質量％である。配合量が１質量％未満であると、十分な曳糸性が得られない場合がある。また、２０質量％を超えると、のびが悪く、自然な仕上がり感に劣る場合がある。 When the spinnable composition according to the present invention is used in eyelash cosmetics or hair cosmetics, a suitable blending amount (actual amount) of lysine derivative-modified silicones represented by the above general formulas (I) to (III) Is 1 to 20% by mass, more preferably 3 to 10% by mass in the whole cosmetic. If the blending amount is less than 1% by mass, sufficient spinnability may not be obtained. On the other hand, if it exceeds 20% by mass, the spread may be poor and the natural finish may be inferior.
（ｂ）シリコーン化プルラン
本発明にかかる曳糸性組成物に含まれるシリコーン化プルランは、下記一般式（Ｖ）で表される。
本発明にかかる曳糸性組成物において、上記シリコーン化プルランは、公知の製法により製造したものを用いることができる（例えば、特開平１０−２９９１０号公報）。
(B) Siliconized pullulan The siliconeized pullulan contained in the spinnable composition according to the present invention is represented by the following general formula (V).
In the spinnable composition according to the present invention, the siliconized pullulan can be produced by a known production method (for example, JP-A-10-29910).
本発明にかかる曳糸性組成物を睫毛用化粧料または毛髪用化粧料に用いる場合、上記シリコーン化プルランの好適な配合量（実分）は、化粧料全体において１〜２０質量％、より好ましくは３〜１０質量％である。配合量が１質量％未満であると、十分な曳糸性が得られない場合がある。また、２０質量％を超えると、のびが悪く、自然な仕上がり感に劣る場合がある。 When using the cocoon composition according to the present invention for eyelash cosmetics or hair cosmetics, the preferred blending amount (actual amount) of the above siliconeized pullulan is preferably 1 to 20% by mass, more preferably the whole cosmetics. Is 3-10 mass%. If the blending amount is less than 1% by mass, sufficient spinnability may not be obtained. On the other hand, if it exceeds 20% by mass, the spread may be poor and the natural finish may be inferior.
さらに、本発明にかかる曳糸性組成物において、前記（ａ）リジン誘導体変性シリコーンおよび（ｂ）シリコーン化プルランの配合量比（（ａ）／（ｂ））は２／５〜２／１であることが好ましい。このような配合量比であるときに、曳糸性組成物に適度な稠度を持った曳糸性および優れた透明性が得られる。また該曳糸性組成物を睫毛用化粧料に用いた場合には、のびが良く、かつロングラッシュ効果に優れたものとなる。 Furthermore, in the spinnable composition according to the present invention, the blending ratio ((a) / (b)) of (a) lysine derivative-modified silicone and (b) siliconeized pullulan is 2/5 to 2/1. Preferably there is. When the blending ratio is such, the spinnability having an appropriate consistency in the spinnable composition and excellent transparency can be obtained. In addition, when the cocoon composition is used in a cosmetic for eyelashes, it has a good stretch and an excellent long lash effect.
（ｃ）油分
本発明で用いる油分として、シリコーン油、炭化水素油、エステル油、脂肪酸類、高級アルコール、ロウ類、ワックス類、フッ素系油脂、動植物油脂類などの常温で液状の油分、ないし常温で固体、半固体の油分が適宜用いられる。具体的には、メチルポリシロキサン、メチルフェニルポリシロキサン等のシリコーン油、流動パラフィン、イソパラフィン、スクワラン、スクワレン等の炭化水素油、ミリスチン酸イソプロピル、ミリスチン酸２−オクチルデシル、ミリスチン酸２−オクチルドデシル、２−エチルヘキサン酸セチル、２−エチルヘキサン酸２−エチルヘキシル、２−エチルヘキサン酸イソノニル、パルミチン酸２−エチルヘキシル、ステアリン酸２−ヘキシルデシル、イソステアリン酸エチル、イソステアリン酸イソプロピル、サリチル酸２−エチルヘキシル等のエステル油、パラフィンワックス、ポリエチレンワックス、マイクロクリスタリンワックス等のワックス類、オリーブ油、ツバキ油、マカデミアナッツ油、ヒマシ油等の油脂等が挙げられる。
本発明においては、上記油分の1種または２種以上を用いてもよい。
本発明にかかる曳糸性組成物に油分を配合する場合、好適な配合量は６０質量％以上である。配合量が６０質量％未満であると、適度な稠度、すなわち曳糸性が維持できず本発明においては好ましくない。
(C) Oil content Oils used in the present invention include oils that are liquid at room temperature such as silicone oils, hydrocarbon oils, ester oils, fatty acids, higher alcohols, waxes, waxes, fluorinated oils and fats, animal and vegetable oils, and room temperature. Solid and semi-solid oils are used as appropriate. Specifically, silicone oil such as methylpolysiloxane and methylphenylpolysiloxane, hydrocarbon oil such as liquid paraffin, isoparaffin, squalane and squalene, isopropyl myristate, 2-octyldecyl myristate, 2-octyldecyl myristate, Such as cetyl 2-ethylhexanoate, 2-ethylhexyl 2-ethylhexanoate, isononyl 2-ethylhexanoate, 2-ethylhexyl palmitate, 2-hexyldecyl stearate, ethyl isostearate, isopropyl isostearate, 2-ethylhexyl salicylate, etc. Examples thereof include waxes such as ester oil, paraffin wax, polyethylene wax and microcrystalline wax, and fats and oils such as olive oil, camellia oil, macadamia nut oil and castor oil.
In the present invention, one or more of the above oils may be used.
When the oil component is blended in the spinnable composition according to the present invention, the preferred blending amount is 60% by mass or more. When the blending amount is less than 60% by mass, an appropriate consistency, that is, the spinnability cannot be maintained, which is not preferable in the present invention.
さらに、上記油分の総重量のうち、シリコーン油が２０質量％以上をしめることが好適である。シリコーン油を含むことにより、前記成分（ａ）リジン誘導体変性シリコーンおよび（ｂ）シリコーン化プルランを含む曳糸性組成物において、油分との相溶性が良好になるため好ましい。さらに該曳糸性組成物を睫毛用化粧料に用いた場合には、揮発性のシリコーン油であると、睫毛に塗布した後に油分の大部分が揮発することによって流動性が低下し、ロングラッシュ効果が長時間維持されるため好ましい。
また、ここでいう「油分の総重量」とは、曳糸性組成物における油分の総重量、または曳糸性組成物を用いた睫毛用化粧料および毛髪用化粧料の全体における油分の総重量のことを意味する。
Furthermore, it is preferable that silicone oil accounts for 20% by mass or more of the total weight of the oil. Including a silicone oil is preferable because the spinnable composition containing the component (a) lysine derivative-modified silicone and (b) siliconeized pullulan has good compatibility with the oil. Further, when the cocoon composition is used in a cosmetic for eyelashes, if it is a volatile silicone oil, the liquidity is lowered by the volatilization of most of the oil after being applied to the eyelashes, resulting in a long lash. This is preferable because the effect is maintained for a long time.
In addition, the “total weight of oil” as used herein refers to the total weight of oil in the spinnable composition, or the total weight of oil in the eyelash cosmetics and hair cosmetics using the spinnable composition. Means that.
ここで「揮発性」とは、常圧における沸点が６０〜２６０℃の範囲である成分を意味するものとする。本発明で用いられる揮発性のシリコーン油としては、例えば、ジメチルポリシロキサン、メチルフェニルポリシロキサン、メチルハイドロジェンポリシロキサン等の鎖状ポリシロキサン、オクタメチルシクロテトラシロキサン、デカメチルシクロペンタシロキサン、ドデカメチルシクロヘキサシロキサン、テトラメチルテトラハイドロジェンシクロテトラシロキサン等の環状ポリシロキサン等が挙げられる。また、これらの商品例を挙げるとすると、例えば、ＫＦ９６Ｌ−０．６５、ＫＦ９６Ｌ−１、ＫＦ９６Ｌ−１．５、ＫＦ９９５、（信越化学工業）、ＳＨ２００−１ｃｓ、ＳＨ２００−１．５ｃｓ、ＳＨ２００−２ｃｓ（東レダウコーニングシリコーン）、ＴＳＦ４０４、ＴＳＦ４０５、ＴＳＦ４０４５（東芝シリコーン）等である。 Here, “volatile” means a component having a boiling point in the range of 60 to 260 ° C. at normal pressure. Examples of the volatile silicone oil used in the present invention include linear polysiloxanes such as dimethylpolysiloxane, methylphenylpolysiloxane, and methylhydrogenpolysiloxane, octamethylcyclotetrasiloxane, decamethylcyclopentasiloxane, and dodecamethyl. And cyclic polysiloxanes such as cyclohexasiloxane and tetramethyltetrahydrogencyclotetrasiloxane. Moreover, if these product examples are given, for example, KF96L-0.65, KF96L-1, KF96L-1.5, KF995 (Shin-Etsu Chemical Co., Ltd.), SH200-1cs, SH200-1.5cs, SH200-2cs (Toray Dow Corning Silicone), TSF404, TSF405, TSF4045 (Toshiba Silicone) and the like.
本発明において、前述の曳糸性組成物を睫毛用化粧料および毛髪用化粧料に用いることが可能である。特に睫毛用化粧料に用いた場合には、該化粧料に繊維を配合せずとも睫毛を長く太く見せる効果に優れたものとなる。該曳糸性組成物の特性を生かして、透明性に優れた自然な仕上がり感が得られる。
また、毛髪化粧料に用いた場合には、髪に「つや」「みずみずしさ」を与え、本発明にかかる曳糸性組成物の持つ滑らかで腰のある整髪性に優れたものが得られる。
本発明にかかる曳糸性組成物は、前記化粧料の他、塗料、表面処理剤等の各種製品の増粘剤としても用いることが可能である。
In the present invention, the above-described threadable composition can be used in eyelash cosmetics and hair cosmetics. In particular, when used in eyelash cosmetics, the effect of making eyelashes appear long and thick without adding fibers to the cosmetics is excellent. Taking advantage of the properties of the spinnable composition, a natural finish with excellent transparency can be obtained.
Further, when used in hair cosmetics, it is possible to give the hair “luster” and “freshness” and to obtain the smooth and waist-like hair-styling property of the spinnable composition according to the present invention.
The spinnable composition according to the present invention can be used as a thickener for various products such as paints and surface treatment agents in addition to the cosmetics.
本発明にかかる睫毛化粧料および毛髪化粧料には色材を配合することが可能である。色材は、一般にメーキャップ化粧料に用いられるものであれば特に制限されない。例えばタルク、マイカ、カオリン、シリカ、炭酸カルシウム、亜鉛華、二酸化チタン、赤酸化鉄、黄酸化鉄、黒酸化鉄、群青、紺青、カーボンブラック、低次酸化チタン、コバルトバイオレット、酸化クロム、水酸化クロム、チタン酸コバルト、オキシ塩化ビスマス、チタン−マイカ系パール顔料などの無機顔料；赤色２０１号、赤色２０２号、赤色２０４号、赤色２０５号、赤色２２０号、赤色２２６号、赤色２２８号、赤色４０５号、橙色２０３号、黄色２０５号、黄色４号、黄色５号、青色１号、青色４０４号、緑色３号などのジルコニウム、バリウム又はアルミニウムレーキなどの有機顔料；クロロフィル、β−カロチンなどの天然色素；染料等が挙げられる。これらの色材は１種又は２種以上を用いることができる。 It is possible to mix | blend a coloring material with the eyelash cosmetics and hair cosmetics concerning this invention. The color material is not particularly limited as long as it is generally used for makeup cosmetics. For example, talc, mica, kaolin, silica, calcium carbonate, zinc white, titanium dioxide, red iron oxide, yellow iron oxide, black iron oxide, ultramarine, bitumen, carbon black, low-order titanium oxide, cobalt violet, chromium oxide, hydroxide Inorganic pigments such as chromium, cobalt titanate, bismuth oxychloride, titanium-mica pearl pigments; red 201, red 202, red 204, red 205, red 220, red 226, red 228, red Organic pigments such as zirconium, barium or aluminum lakes such as 405, orange 203, yellow 205, yellow 4, yellow 5, blue 1, blue 404, green 3, etc .; chlorophyll, β-carotene, etc. Natural pigments; dyes and the like. These color materials can be used alone or in combination of two or more.
色材の配合量は適宜調整される。好ましくは０．１〜３０質量％であり、さらに好ましくは３〜２０質量％である。３０質量％を超えて配合すると、付着性の点で好ましくない。０．１質量％未満では色材の効果が不十分となる場合がある。 The blending amount of the color material is adjusted as appropriate. Preferably it is 0.1-30 mass%, More preferably, it is 3-20 mass%. When it exceeds 30 mass%, it is not preferable in terms of adhesion. If it is less than 0.1% by mass, the effect of the coloring material may be insufficient.
また、本発明にかかる睫毛化粧料および毛髪化粧料には前記必須成分以外の被膜形成樹脂を配合してもよい。具体的には、ポリビニルアルコール、ポリビニルピロリドン、ポリ酢酸ビニル、ポリアクリル酸アルキルなどのラテックス類、デキストリン、アルキルセルロースやニトロセルロースなどのセルロース誘導体、トリメチルシロキシケイ酸などが用いられる。これの樹脂は１種又は２種以上が選択して用いられる。 Moreover, you may mix | blend film forming resin other than the said essential component with the eyelash cosmetics and hair cosmetics concerning this invention. Specifically, latexes such as polyvinyl alcohol, polyvinyl pyrrolidone, polyvinyl acetate, and polyalkyl acrylate, dextrin, cellulose derivatives such as alkyl cellulose and nitrocellulose, trimethylsiloxysilicic acid, and the like are used. One or more of these resins are selected and used.
また、本発明にかかる睫毛化粧料および毛髪化粧料には前記必須成分以外の多糖類および水溶性高分子を配合してもよい。水溶性高分子としては、多糖類、水溶性の天然高分子、半合成高分子、無機高分子等が挙げられる。
具体的には、多糖類としては、セルロース、デンプン、グリコーゲン、ヒアルロン酸、コンドロイチン、グアガム、ローカストビンガム、クインスシード、ガラクタン、アラビアガム、トラガントガム、キサンタンガム、デキストラン、サクシノグルカン、コンドロイチン硫酸、ムコイチン硫酸等が挙げられる。
Moreover, you may mix | blend polysaccharides and water-soluble polymers other than the said essential component with the eyelash cosmetics and hair cosmetics concerning this invention. Examples of the water-soluble polymer include polysaccharides, water-soluble natural polymers, semi-synthetic polymers, and inorganic polymers.
Specifically, as polysaccharides, cellulose, starch, glycogen, hyaluronic acid, chondroitin, guar gum, locust bin gum, quince seed, galactan, gum arabic, tragacanth gum, xanthan gum, dextran, succinoglucan, chondroitin sulfate, mucoitin sulfate, etc. Is mentioned.
水溶性天然高分子としては、カラギーナン、グリチルリチン酸、キャロブガム、ペクチン、カラヤガム、アルゲコロイド（カッソウエキス）等の植物系高分子、デキストラン、ブルラン等の微生物系高分子、コラーゲン、アルブミン等の動物系高分子等が挙げられる。
水溶性の半合成高分子としては、カルボキシメチルデンプン、メチルヒドロキシプロピルデンプン等のデンプン系、メチルセルロース、エチルセルロース、ヒドロキシエチルセルロース、ヒドロキシプロピルセルロース、結晶セルロース、メチルヒドロキシプロピルセルロース、セルロース硫酸Ｎａ、カルボキシメチルセスロースＮａ（ＣＭＣ）、セルロース末等のセルロース系、アルギン酸Ｎａ、アルギン酸プロピレングリコールエステル等のアルギン酸系が挙げられる。
水溶性の合成高分子としては、ポリビニルアルコール、ポリビニルピロリドン、カルボキシビニルポリマー、ポリビニルメチルエーテル等のビニル系、ポリエチレングリコール等のポリオキシエチレン系、ポリオキシエチレン・ポリオキシプロピレン共重合体等の共重合系、ポリアクリル酸ナトリウム、ポリアクリルアミド、ポリエチルアクリレート等のアクリル系、ポリエチレンイミン、カチオンポリマー等が挙げられる。
水溶性の無機高分子としては、ベントナイト、ラポナイト、無水ケイ酸等が挙げられる。 これらの多糖類、水溶性高分子は１種又は２種以上が選択して用いられる。
Examples of water-soluble natural polymers include plant polymers such as carrageenan, glycyrrhizic acid, carob gum, pectin, karaya gum, and alge colloid (casso extract), microbial polymers such as dextran and bullulan, and animal polymers such as collagen and albumin. Etc.
Water-soluble semi-synthetic polymers include starch systems such as carboxymethyl starch and methylhydroxypropyl starch, methylcellulose, ethylcellulose, hydroxyethylcellulose, hydroxypropylcellulose, crystalline cellulose, methylhydroxypropylcellulose, cellulose sulfate Na, carboxymethylsesulose Examples thereof include celluloses such as Na (CMC) and cellulose powder, and alginic acids such as sodium alginate and propylene glycol alginate.
Examples of water-soluble synthetic polymers include polyvinyl alcohol, polyvinyl pyrrolidone, carboxy vinyl polymer, vinyl type such as polyvinyl methyl ether, polyoxyethylene type such as polyethylene glycol, copolymer such as polyoxyethylene / polyoxypropylene copolymer, etc. And acrylics such as poly (sodium acrylate), polyacrylamide and polyethyl acrylate, polyethyleneimine, and cationic polymers.
Examples of the water-soluble inorganic polymer include bentonite, laponite, and silicic anhydride. One or two or more of these polysaccharides and water-soluble polymers are selected and used.
本発明にかかる睫毛用化粧料および毛髪用化粧料には、上記成分に加えて、本発明の効果を損なわない範囲で通常化粧料、医薬部外品等に用いられる成分を配合することができる。このような成分としては、例えば、保湿剤、分散剤、防腐剤、香料、薬剤、紫外線吸収剤、増粘剤などが挙げられる。
本発明にかかる睫毛用化粧料および毛髪用化粧料の形態は、Ｗ／Ｏ乳化または油性の形態を好ましくとるが、この限りではない。
以下、実施例を挙げて本発明を更に詳しく説明する。本発明はこれらの実施例により限定されるものではない。配合量については特に断りのない限り質量％を示す。
In addition to the above components, the eyelash cosmetic and hair cosmetic according to the present invention can be blended with components that are usually used in cosmetics, quasi-drugs and the like within a range that does not impair the effects of the present invention. . Examples of such components include humectants, dispersants, preservatives, fragrances, drugs, ultraviolet absorbers, thickeners, and the like.
The form of the eyelash cosmetic and the hair cosmetic according to the present invention preferably takes a W / O emulsified or oily form, but is not limited thereto.
Hereinafter, the present invention will be described in more detail with reference to examples. The present invention is not limited to these examples. Unless otherwise specified, the blending amount indicates mass%.
［製造例１］Ｎε−ラウロイル−Ｌ−リジンイソブチルエステル誘導体変性シリコーン
（１）２０．１ｇのＮε−ラウロイル−Ｌ−リジンを２０５ｍｌのエタノ−ルに懸濁させた。反応溶液を氷冷後、乾燥塩化水素ガスを飽和になるまで導入し、６時間撹拌した。
次にエタノ−ルを留去後、２５０ｍｌのジイソブチルエーテルを加え、吸引濾過後、精製水３００ｍｌを加えた。この溶液に精製水７０ｍｌに溶かしたモルホリン５５ｇを撹拌しながらゆっくりと加え、析出した白色粉末をろ別した。得られた白色粉末は、ｎ−ヘキサンから再結晶を行い、Ｎε−ラウロイル−Ｌ−リジンイソブチルエステル２０．１ｇを得た。
（２）アジ化ナトリウム４５．５ｇに精製水１５０ｇを加え、氷水中で冷却しながら、撹拌して完全に均一な溶液とした。ここに１０−ウンデセノイルクロライド１０１．４ｇとアセトン１５０ｍｌを混合した溶液を少しずつ、溶液の温度が１０〜１５℃の範囲になるように滴下した。添加終了後、１２℃付近で１時間撹拌した。
次に溶液を分液ロートに移し、水層と有機層を分けた。有機層を６０℃に維持した５００ｍｌのトルエンにゆっくりと加え、温度５０〜６０℃の範囲で３時間撹拌を行ったートルエンを留去後、減圧蒸留することで１０−ウンデセノイルイソシアネート７３．２ｇを得た。
（３）次式
次に得られた固体を細かく砕き、２５℃のヘキサンでよく洗いながら吸引ろ過を行った後、減圧乾燥することで上記式（VI）で表される粉末状のリジン誘導体変成シリコーン（Ｎε−ラウロイル−Ｌ−リジンイソブチルエステル誘導体変性シリコーン）２０．３ｇを得た。
[Production Example 1] N epsilon - lauroyl -L- lysine isobutyl ester derivative-modified silicone (1) 20.1 g of N epsilon - lauroyl -L- lysine in 205ml ethanol - were suspended in Le. After cooling the reaction solution with ice, dry hydrogen chloride gas was introduced until saturation, and the mixture was stirred for 6 hours.
Next, ethanol was distilled off, 250 ml of diisobutyl ether was added, and after suction filtration, 300 ml of purified water was added. To this solution, 55 g of morpholine dissolved in 70 ml of purified water was slowly added with stirring, and the precipitated white powder was filtered off. The obtained white powder was recrystallized from n-hexane to obtain 20.1 g of N ε -lauroyl-L-lysine isobutyl ester.
(2) 150 g of purified water was added to 45.5 g of sodium azide, and the mixture was stirred to obtain a completely homogeneous solution while cooling in ice water. A solution obtained by mixing 101.4 g of 10-undecenoyl chloride and 150 ml of acetone was added dropwise little by little so that the temperature of the solution was in the range of 10 to 15 ° C. After completion of the addition, the mixture was stirred at around 12 ° C. for 1 hour.
The solution was then transferred to a separatory funnel and the aqueous and organic layers were separated. The organic layer was slowly added to 500 ml of toluene maintained at 60 ° C., and stirred for 3 hours at a temperature in the range of 50 to 60 ° C. After distilling off the toluene and distilling under reduced pressure, 73.2 g of 10-undecenoyl isocyanate Got.
(3) The following formula
Next, the obtained solid is finely pulverized, suction filtered while thoroughly washing with hexane at 25 ° C., and then dried under reduced pressure, whereby powdered lysine derivative-modified silicone (N ε −) represented by the above formula (VI) is obtained. 20.3 g of lauroyl-L-lysine isobutyl ester derivative-modified silicone) was obtained.
続いて、本発明者らは、上記合成例に準じて各種リジン誘導体変性シリコーンを合成し、当該リジン誘導体変性シリコーンを配合した曳糸性組成物の評価を行った。各試験例の曳糸性組成物の配合組成と評価結果とを下記に併せて示す。
（ｂ）成分として、シリコーン化プルラン（３−[トリス（トリメチルシロキサン）シリル]プロピルカルバド酸プルラン混合物、商品名：ＴＳＰＬ−３０−Ｄ５、信越化学工業株式会社製。３−[トリス（トリメチルシロキサン）シリル]プロピルカルバド酸プルラン混合物を３０％含有する。）を使用した。また（ｃ）成分としてデカメチルシクロペンタシロキサン、ジメチルポリシロキサン、イソノナン酸イソノニルを使用した。
Subsequently, the present inventors synthesized various lysine derivative-modified silicones according to the above synthesis examples, and evaluated the spinnable composition containing the lysine derivative-modified silicones. The blending composition and evaluation results of the spinnable composition of each test example are also shown below.
As component (b), silicone-treated pullulan (3- [tris (trimethylsiloxane) silyl] propylcarbadoic acid pullulan mixture, trade name: TSPL-30-D5, manufactured by Shin-Etsu Chemical Co., Ltd. 3- [tris (trimethylsiloxane) Containing 30% silyl] propylcarbadoic acid pullulan mixture). Further, decamethylcyclopentasiloxane, dimethylpolysiloxane, and isonononyl isononanoate were used as the component (c).
評価基準は以下の通りである。
（１）官能評価：曳糸性
あらかじめ石鹸で洗浄した手の甲に、上記成分を含む試料を各１ｇ塗布し、指を試料に押し付けた後に指を上方に引き離したときの曳糸性を、専門パネル（２０名）の目視により評価した。評価基準は、きわめてよく伸びると感じた場合は３点、適度に伸びると感じた場合は２点、若干伸びると感じた場合は1点、伸びないと感じた場合は０点とし、その合計点を算出した。
◎：合計点が４６点以上。
○：合計点が３６点〜４５点。
△：合計点が２６点〜３５点。
×：合計点が２５点以下。
The evaluation criteria are as follows.
(1) Sensory evaluation: Spinnability 1 g of each sample containing the above components was applied to the back of the hand that had been washed with soap beforehand, and the fingernail when the finger was pulled upward after pressing the finger against the sample It was evaluated by visual observation of (20 persons). The evaluation criteria are 3 points if you feel very well, 2 points if you feel moderately stretched, 1 point if you feel slightly stretched, and 0 points if you feel you are not stretched. Was calculated.
A: The total score is 46 or more.
A: The total score is 36 to 45 points.
Δ: Total score of 26 to 35 points.
X: A total score is 25 or less.
（２）官能評価：透明性
サンプルを５ｍｍ厚になるように透明樹脂容器に流し込み、２５℃にて容器下に置いたフォント８８のＴｉｍｅｓ Ｎｅｗ Ｒｏｍａｎの文字の見える鮮明さを、専門パネル（２０名）により評価した。
５点：非常に文字がハッキリと見え、鮮明度が非常に高い。
４点：文字がハッキリと見え、鮮明度が高い。
３点：文字が見えるが、鮮明度がやや劣る。
２点：かろうじて文字が見えるが、鮮明度に劣る。
１点：文字が読めず、不透明である。
これらの合計点を算出した。
◎：合計点が９１点以上。
○：合計点が７１〜９０点。
△：合計点が４１〜７０点。
×：合計点が４０点以下。
(2) Sensory evaluation: Transparency The sample was poured into a transparent resin container so as to have a thickness of 5 mm, and the clearness of the characters of Times New Roman font 88 placed under the container at 25 ° C. ).
5 points: The characters look very clear and the sharpness is very high.
4 points: Characters are clearly visible and sharpness is high.
3 points: Characters can be seen, but sharpness is slightly inferior.
2 points: Characters are barely visible, but inferior in clarity.
1 point: Characters cannot be read and are opaque.
These total points were calculated.
A: The total score is 91 points or more.
A: The total score is 71 to 90 points.
(Triangle | delta): A total score is 41-70 points.
X: The total score is 40 or less.
本発明にかかる曳糸性組成物を用い睫毛用化粧料に関しては以下の項目についても評価した。
（３）塗布性
専門パネル（２０名）により、睫毛に各試料（マスカラ）を塗布したときの、マスカラの塗布のしやすさを官能評価した。評価基準は極めて塗布しやすいと感じた場合には３点、適度に塗布しやすいと感じた場合には２点、塗布しにくいと感じた場合には１点、極めてぬりのばしにくく塗布しにくいと感じた場合には０点とし、その合計点を算出した。
○：合計点が４１点以上。
△：合計点が２６〜４０点。
×：合計点が２５点以下。
The following items were also evaluated for the eyelash cosmetics using the cocoon composition according to the present invention.
(3) Application property A special panel (20 persons) performed sensory evaluation on the ease of application of mascara when each sample (mascara) was applied to the eyelashes. The evaluation criteria are 3 points if you feel that it is very easy to apply, 2 points if you feel it is easy to apply moderately, 1 point if you feel that it is difficult to apply, When it felt, it was set as 0 points, and the total score was calculated.
○: The total score is 41 points or more.
(Triangle | delta): A total score is 26-40 points.
X: A total score is 25 or less.
（４）ロングラッシュ効果
専門パネル（２０名）により、睫毛に各試料（マスカラ）を１０回塗布し、塗布前後の睫毛の長さを目視により観察し、官能でロングラッシュ効果を評価した。評価基準は、睫毛が極めて長くなったと感じた場合には３点、適度に長くなったと感じた場合には２点、若干長くなったと感じた場合には１点、塗布前と変化を感じなかった場合には０点とし、その合計点を算出した。
○：合計点が４１点以上。
△：合計点が２６〜４０点。
×：合計点が２５点以下。
(4) Long lash effect Each sample (mascara) was applied 10 times to the eyelashes by a professional panel (20 persons), and the length of the eyelashes before and after the application was visually observed to evaluate the long lash effect with a sense. The evaluation criteria are 3 points when the eyelashes feel extremely long, 2 points when it feels moderately long, 1 point when it feels slightly longer, no change from before application In this case, the score was 0, and the total score was calculated.
○: The total score is 41 points or more.
(Triangle | delta): A total score is 26-40 points.
X: A total score is 25 or less.
（５）自然な仕上がり感
専門パネル（２０名）により、睫毛に各試料（マスカラ）を１０回塗布し、目視により自然な仕上がり感を評価した。評価基準は優れた自然な仕上がり感があると感じた場合には３点、適度な仕上がり感であると感じた場合には２点、あまり自然な仕上がり感ではないと感じた場合には１点、極めて不自然な仕上がり感であると感じた場合には０点とし、その合計点を算出した。
○：合計点が４１点以上。
△：合計点が２６〜４０点。
×：合計点が２５点以下。
(5) Natural finish feeling Each sample (mascara) was applied 10 times to the eyelashes by a professional panel (20 persons), and the natural finish feeling was visually evaluated. The evaluation criteria are 3 points if you feel that there is an excellent natural finish, 2 points if you feel that the finish is moderate, and 1 point if you feel that the finish is not very natural. When it was felt that the finish was extremely unnatural, the score was 0, and the total score was calculated.
○: The total score is 41 points or more.
(Triangle | delta): A total score is 26-40 points.
X: A total score is 25 or less.
＜リジン誘導体変性シリコーンの種類＞
リジン誘導体変性シリコーンの適正について検討するために下記に示す各種リジン誘導体変性シリコーンを前述の製造例１に準じて合成し、それらを配合した組成物の評価を行った。その結果を下記表１に示す。
合成リジン誘導体変性シリコーンの構造
In order to examine the suitability of lysine derivative-modified silicones, the following various lysine derivative-modified silicones were synthesized in accordance with the above-mentioned Production Example 1, and compositions containing them were evaluated. The results are shown in Table 1 below.
Structure of synthetic lysine derivative-modified silicone
（製法）上記成分（１）〜（９）を９０℃に加熱し、攪拌混合した後冷却し、各々の試料を得た。
上記表１の結果から明らかなように、各種リジン誘導体変性シリコーンをシリコーン化プルランと組み合わせた試験例１〜４において、優れた曳糸性および透明性を有する組成物が得られた。
一方、試験例５のようにシリコーン化プルランを配合しないと、所望とする曳糸性は得られず、固いゲルの組成物であった。また、リジン誘導体変性シリコーンに変わり、増粘剤であるパルミチン酸デキストリンを配合すると（試験例６）、やや粘稠なゲルとなり、また透明性に欠くものであった。
次に、リジン誘導体変性シリコーンと従来の油性被膜形成剤とを組み合わせた組成物の評価を行った。その結果を下記表２に示す。
As is clear from the results in Table 1 above, compositions having excellent spinnability and transparency were obtained in Test Examples 1 to 4 in which various lysine derivative-modified silicones were combined with silicone-modified pullulan.
On the other hand, if the siliconeized pullulan was not blended as in Test Example 5, the desired spinnability could not be obtained, and the composition was a hard gel. Moreover, when it replaced with the lysine derivative modified silicone and the palmitic acid dextrin which is a thickener was mix | blended (Test Example 6), it became a somewhat viscous gel and lacked transparency.
Next, the composition which combined the lysine derivative modified silicone and the conventional oil-based film formation agent was evaluated. The results are shown in Table 2 below.
上記表２の結果から明らかなように、リジン誘導体変性シリコーンと従来の油性被膜形成剤とを組み合わせた試験例７〜９において、透明性が劣るものであり、また所望とする曳糸性が十分でなく、固いゲルが形成される結果となった。曳糸性を有する油性被膜剤であるイソステアリン酸アルミニウムを油分とを混合した試験例１０においては、曳糸性はあるものの、本発明にかかる曳糸性組成物にみられる透明感に優れる曳糸性とは異なり、ややべたつき感の強いものであった。また極性油分であるエステル油との共存により、イソステアリン酸アルミニウムのゲル構造の破壊による安定性の低下が危惧されるため、曳糸性組成物を化粧料に用いた場合に、共に配合する成分が制限されるという欠点が存在する。 As is clear from the results of Table 2 above, in Test Examples 7 to 9 in which a lysine derivative-modified silicone and a conventional oily film forming agent are combined, the transparency is inferior and the desired spinnability is sufficient. Instead, a hard gel was formed. In Test Example 10 in which aluminum isostearate, which is an oil-based film agent having spinnability, was mixed with an oil component, there was spinnability, but the silky yarn excellent in transparency seen in the spinnable composition according to the present invention Unlike sex, it was somewhat sticky. In addition, coexistence with ester oil, which is a polar oil component, may lead to a decrease in stability due to the destruction of the gel structure of aluminum isostearate. There is a drawback of being.
以上の結果から、リジン誘導体変性シリコーンとシリコーン化プルランとの組み合わせにおいて、極めて優れた曳糸性および透明性を見出した本発明者らは、上記２成分の好適な配合量比の検討を実施した。その結果を下記表３に示す。
＜リジン誘導体変性シリコーンとシリコーン化プルランの配合比＞
<Combination ratio of lysine derivative-modified silicone and siliconized pullulan>
上記表３より明らかなように、前記（ａ）リジン誘導体変性シリコーン（VI）と（ｂ）シリコーン化プルランの１種である３−[トリス（トリメチルシロキサン）シリル]プロピルカルバド酸プルラン混合物の配合量比は２／５〜２／１であるときに、曳糸性組成物の曳糸性が優れていることがわかる。この範囲を逸脱する試験例１１は、適度な曳糸性にかけ非常に極めて高い流動性のため成形性が十分ではなく、一方試験例１５は粘度が固くなりすぎて、糸を引くような滑らかな感触に欠けるものであった。
次に、本発明にかかる曳糸性組成物を利用した睫毛用化粧料において、共に配合する各種成分についての検討を行った。最初に成分（ａ）リジン誘導体変性シリコーンの好適な配合量の検討結果を下記表４に示す。
As is apparent from Table 3 above, the blending amount of 3- (tris (trimethylsiloxane) silyl] propylcarbadoic acid pullulan mixture which is one of (a) lysine derivative-modified silicone (VI) and (b) siliconeized pullulan It can be seen that the spinnability of the spinnable composition is excellent when the ratio is 2/5 to 2/1. Test Example 1 1 outside this range, moderate spinnability sieved not have sufficient formability for the very extremely high fluidity, whereas Test Example 1 5 too hard the viscosity, such as pulling the yarn It lacked a smooth feel.
Next, various components to be blended together in the eyelash cosmetic using the spinnable composition according to the present invention were examined. First, Table 4 below shows the results of studying suitable blending amounts of component (a) lysine derivative-modified silicone.
＜（ａ）リジン誘導体変性シリコーンの好適な配合量＞
※３：商品名 エマレックスＲＷＩＳ−３２０、日本エマルジョン株式会社製
（製法）成分（１）、（２）を含む油相部を９０℃に加熱し攪拌して均一にする。水相部も９０℃に加熱し、前記油相部に添加して乳化した後、室温まで冷却して各試料を得た。
<Preferred blending amount of (a) lysine derivative-modified silicone>
上記表４より明らかなように、試験例１６ではリジン誘導体変性シリコーンの配合量が１質量％と少ないため、粘性が高く睫毛に塗布しにくいものである。また自然な仕上がり感に欠けるものである。さらに、試験例２０はリジン誘導体変性シリコーンの配合量が多いために固いゲルとなってしまい睫毛用化粧料としては不適なものであった。
以上の結果から、本発明にかかる曳糸性組成物を睫毛用化粧料に用いた場合には、成分（ａ）リジン誘導体変性シリコーンの好適な配合量は３〜１０質量％であることが分かる。
続いて、本発明にかかる曳糸性組成物を利用した睫毛用化粧料における、成分（ｂ）シリコーン化プルランの好適な配合量の検討を行った。その結果を下記表５に示す。
As apparent from Table 4 above, in Test Example 16, since the blending amount of the lysine derivative-modified silicone is as small as 1% by mass, the viscosity is high and it is difficult to apply to the eyelashes. It also lacks a natural finish. Furthermore, since Test Example 20 contained a large amount of lysine derivative-modified silicone, it became a hard gel and was unsuitable as a cosmetic for eyelashes.
From the above results, it can be seen that when the spinnable composition according to the present invention is used in a cosmetic for eyelashes, the preferred amount of component (a) lysine derivative-modified silicone is 3 to 10% by mass. .
Then, the suitable compounding quantity of the component (b) silicone-ized pullulan in the cosmetics for eyelashes using the spinnable composition concerning this invention was examined. The results are shown in Table 5 below.
＜（ｂ）シリコーン化プルランの好適な配合量＞
上記表５より明らかなように、試験例２１ではシリコーン化プルランの配合量が１質量％と少ないため、曳糸性組成物が得られず、睫毛に塗布したときのロングラッシュ効果がみられない。さらに、試験例２５はシリコーン化プルランが多いために粘性が高く睫毛に塗布しにくいものであり、睫毛用化粧料としては不適なものであった。
以上の結果から、本発明にかかる曳糸性組成物を睫毛用化粧料に用いた場合には、成分（ｂ）シリコーン化プルランの好適な配合量は３〜１０質量％であることが分かる。
次に、本発明にかかる曳糸性組成物を利用した睫毛用化粧料における油分の検討を行った。その結果を下記表６に示す。
As is apparent from Table 5 above, in Test Example 21, since the blended amount of siliconeized pullulan is as small as 1% by mass, a spinnable composition cannot be obtained, and no long lash effect is observed when applied to eyelashes. . Furthermore, since Test Example 25 has a lot of siliconeized pullulan, it has a high viscosity and is difficult to apply to eyelashes, and was unsuitable as a cosmetic for eyelashes.
From the above results, it can be seen that when the spinnable composition according to the present invention is used in a cosmetic for eyelashes, the preferred amount of component (b) siliconeized pullulan is 3 to 10% by mass.
Next, the oil content in the eyelash cosmetic using the spinnable composition according to the present invention was examined. The results are shown in Table 6 below.
＜油分の種類＞
（製法）上記成分（１）〜（１２）を９０℃に加熱し、攪拌混合した後冷却し、各々の試料を得た。
<Oil content>
上記表６の結果から明らかなように、本発明にかかる睫毛用化粧料において油分として揮発性シリコーン油が配合されていないと、透明感のある自然な仕上がりに欠けるものであった。また、睫毛に塗布した後に、該化粧料の固化が十分になされず、睫毛をこすると化粧持ちの点で問題が残るものであった。
また、揮発性シリコーン油が配合されていても、油分全体に占める揮発性シリコーン油の割合が低いと（試験例３０）、前述と同様に化粧落ちの点で若干問題があった。
以上の結果から、本発明にかかる曳糸性組成物を用いた睫毛用化粧料においては、油分として揮発性シリコーン油を含むことが好ましく、油分の総量において揮発性シリコーン油が６０％以上を占めることがより好ましいことが明らかである。
さらに、本発明者らは本発明にかかる睫毛用化粧料と、従来からロングラッシュ効果のために繊維を配合した睫毛用化粧料とを比較検討した。その結果を下記表７に示す。
As is apparent from the results in Table 6 above, if the volatile silicone oil is not blended as an oil component in the eyelash cosmetic according to the present invention, the transparent natural finish is lacking. In addition, after the application to the eyelashes, the cosmetic material was not sufficiently solidified, and when the eyelashes were rubbed, there was a problem in terms of durability.
Even when volatile silicone oil is blended, if the proportion of volatile silicone oil in the total oil content is low (Test Example 30), there was a slight problem in terms of makeup removal as described above.
From the above results, the eyelash cosmetic using the spinnable composition according to the present invention preferably contains volatile silicone oil as the oil, and the volatile silicone oil accounts for 60% or more in the total amount of oil. It is clear that this is more preferable.
Furthermore, the present inventors compared and examined the eyelash cosmetic according to the present invention and the eyelash cosmetic conventionally blended with fibers for a long lash effect. The results are shown in Table 7 below.
上記表７の結果から明らかなように、本発明にかかる睫毛用化粧料は繊維を配合せずともロングラッシュ効果に優れていることが分かる。繊維を配合した試験例３２にでは、自然な仕上がり感および塗布性が劣るものである。また、繊維配合の化粧料を塗布すると、時間の経過とともに、繊維落ちにより目の下の汚れが気になり、目の中へ入り込む可能性も危惧されるという問題がある。
以上の結果より、本発明にかかる曳糸性組成物を用いた睫毛用化粧料は、繊維を配合しなくても睫毛を長く見せる効果に優れ、塗布性、自然な仕上がり感も良好であることが明らかである。
As is apparent from the results in Table 7 above, it can be seen that the eyelash cosmetic according to the present invention is excellent in the long lash effect without blending fibers. In Test Example 32 in which fibers were blended, the natural feeling of finish and applicability were poor. In addition, when a fiber-blended cosmetic is applied, there is a problem that with the passage of time, the stains under the eyes are worrisome due to fiber dropping and the possibility of entering into the eyes is feared.
From the above results, the eyelash cosmetics using the cocoon composition according to the present invention are excellent in the effect of making the eyelashes look long without blending fibers, and have good applicability and a natural finish. Is clear.
以下、本発明にかかる曳糸性組成物を用いた化粧料の実施例を挙げて、本発明を更に詳細に説明するが、本発明はこれらに限定されるものではない。
実施例３−１：Ｗ／Ｏマスカラ
（１）リジン誘導体変性シリコーン（VII） ６．０ 質量％
（２）３−[トリス（トリメチルシロキサン）シリル] ６．０
プロピルカルバド酸プルラン混合物
（３）ジメチルポリシロキサン（６ｍＰａ・ｓ） ２．０
（４）デカメチルシクロペンタシロキサン １０．０
（５）軽質イソパラフィン ７．０
（６）トリメチルシロキシケイ酸 １０．０
（７）メチルポリシロキサンエマルション 適量
（商品名：BY22-080 cosmetic emulsion、東レダウコーニング株式会社製）
（８）ジオレイン酸ポリエチレングリコール ２．０
（９）ジイソステアリン酸ジグリセリル ２．０
（１０）１，３−ブチレングリコール ４．０
（１１）炭酸水素ナトリウム ０．２
（１２）酢酸ＤＬ−α−トコフェロール ０．１
（１３）パラオキシ安息香酸エステル 適量
（１４）デヒドロ酢酸ナトリウム 適量
（１５）黒酸化鉄 ７．０
（１６）海藻エキス ０．１
（１７）ベントナイト １．０
（１８）ジメチルジステアリルアンモニウムヘクトナイト ６．０
（１９）ポリ酢酸ビニルエマルション ３０．０
（商品名：ビニブラン Ｓ−４０、日信化学工業株式会社製）
（２０）精製水 残部
（製法）（製法）成分（１）、（２）を含む油相部を９０℃に加熱し攪拌して均一にする。水相部も９０℃に加熱し、前記油相部に添加して乳化した後、室温まで冷却してマスカラ容器に充填した。
EXAMPLES Hereinafter, although the Example of the cosmetics using the spinnable composition concerning this invention is given and this invention is demonstrated further in detail, this invention is not limited to these.
Example 3-1 W / O mascara (1) Lysine derivative-modified silicone (VII) 6.0% by mass
(2) 3- [Tris (trimethylsiloxane) silyl] 6.0
Propylcarbadoic acid pullulan mixture (3) Dimethylpolysiloxane (6 mPa · s)
(4) Decamethylcyclopentasiloxane 10.0
(5) Light isoparaffin 7.0
(6) Trimethylsiloxysilicic acid 10.0
(7) Methyl polysiloxane emulsion appropriate amount (Brand name: BY22-080 cosmetic emulsion, manufactured by Toray Dow Corning Co., Ltd.)
(8) Polyethylene glycol dioleate 2.0
(9) Diglyceryl diisostearate 2.0
(10) 1,3-butylene glycol 4.0
(11) Sodium bicarbonate 0.2
(12) DL-α-tocopherol acetate 0.1
(13) Paraoxybenzoic acid ester appropriate amount (14) sodium dehydroacetate appropriate amount (15) black iron oxide 7.0
(16) Seaweed extract 0.1
(17) Bentonite 1.0
(18) Dimethyl distearyl ammonium hectorite 6.0
(19) Polyvinyl acetate emulsion 30.0
(Product name: Viniblanc S-40, manufactured by Nissin Chemical Industry Co., Ltd.)
(20) Purified water The oil phase portion containing the remainder (manufacturing method) (manufacturing method) components (1) and (2) is heated to 90 ° C. and stirred to make it uniform. The aqueous phase was also heated to 90 ° C., added to the oil phase and emulsified, then cooled to room temperature and filled into a mascara container.
実施例３−２：油性マスカラ
（１）リジン誘導体変性シリコーン（VII） ５．０ 質量％
（２）３−[トリス（トリメチルシロキサン）シリル] ５．０
プロピルカルバド酸プルラン混合物
（３）メチルハイドロジェンポリシロキサン １．０
（４）デカメチルシクロペンタシロキサン ４０．０
（５）軽質イソパラフィン 残量
（６）トリメチルシロキシケイ酸 １５．０
（７）ポリ（オキシエチレン・オキシプロピレン）
メチルポリシロキサン共重合体 ２．０
（下記一般式（1）において、ｍ＝４００、ｎ＝１０、ｘ＝３、ｙ＝１９、ｚ＝１９、Ｒ８＝Ｈ分子量約５５，０００のもの。）
（９）キャンデリラロウ ５．０
（１０）イソステアリン酸 ３．０
（１１）オレイン酸 １．０
（１２）トリ２−エチルヘキサン酸グリセリル ２．０
（１３）ムクロジエキス ０．１
（１３）カラスムギエキス ０．１
（１４）テトラデセン ０．１
（１５）ポリエチレン ５．０
（１６）マイクロクリスタリンワックス ５．０
（製法）上記成分（１）〜（１６）を９０℃に加熱し、攪拌混合した後冷却し、マスカラ容器に充填した。
Example 3-2: Oily mascara (1) Lysine derivative-modified silicone (VII) 5.0 mass%
(2) 3- [Tris (trimethylsiloxane) silyl] 5.0
Propylcarbadoic acid pullulan mixture (3) methyl hydrogen polysiloxane 1.0
(4) Decamethylcyclopentasiloxane 40.0
(5) Light isoparaffin remaining amount (6) Trimethylsiloxysilicic acid 15.0
(7) Poly (oxyethylene / oxypropylene)
Methylpolysiloxane copolymer 2.0
(In the following general formula (1), m = 400, n = 10, x = 3, y = 19, z = 19, R 8 = H having a molecular weight of about 55,000.)
(9) Candelilla wax 5.0
(10) Isostearic acid 3.0
(11) Oleic acid 1.0
(12) Glyceryl tri-2-ethylhexanoate 2.0
(13) Mukuroji extract 0.1
(13) Oat extract 0.1
(14) Tetradecene 0.1
(15) Polyethylene 5.0
(16) Microcrystalline wax 5.0
(Production Method) The above components (1) to (16) were heated to 90 ° C., stirred and mixed, cooled, and filled into a mascara container.
実施例３−３：毛髪用化粧料（ヘアワックス）
（１）リジン誘導体変性シリコーン（VII） ５．０ 質量％
（２）３−[トリス（トリメチルシロキサン）シリル］ ５．０
プロピルカルバド酸プルラン混合物
（３）ジメチルポリシロキサン（６ｍＰａ・ｓ） １０．０
（４）メチルフェニルポリシロキサン ５．０
（５）高重合メチルポリシロキサン １０．０
（６）ポリオキシプロピレン（４０）ブチルエーテル 残余
（７）サラシミツロウ １０．０
（８）モクロウ ５．０
（９）カルナウバロウ １．０
（１０）親油型モノステアリン酸グリセリン ８．０
（１１）自己乳化型モノステアリン酸グリセリン １０．０
（１２）香料 適量
（製法）上記成分（１）〜（１２）を９０℃に加熱し、攪拌混合した後冷却して目的の毛髪用化粧料を得た。
Example 3-3: Hair cosmetic (hair wax)
(1) Lysine derivative-modified silicone (VII) 5.0 mass%
(2) 3- [Tris (trimethylsiloxane) silyl] 5.0
Propylcarbadoic acid pullulan mixture (3) Dimethylpolysiloxane (6 mPa · s) 10.0
(4) Methylphenylpolysiloxane 5.0
(5) Highly polymerized methylpolysiloxane 10.0
(6) Polyoxypropylene (40) Butyl ether Residue (7) White beeswax 10.0
(8) Mowl 5.0
(9) Carnauba wax 1.0
(10) Lipophilic glyceryl monostearate 8.0
(11) Self-emulsifying glyceryl monostearate 10.0
(12) Fragrance Appropriate amount (Manufacturing method) The above components (1) to (12) were heated to 90 ° C., stirred and mixed, and then cooled to obtain the desired cosmetic for hair.
Claims (3)
（ｂ）下記一般式（V）で表されるシリコーン化プルランと、
（ｃ）油分
を含有し、
（ａ）及び（ｂ）の配合量がそれぞれ３〜１０質量％であり、
（ａ）の（ｂ）に対する配合量の比（（ａ）／（ｂ））が２／５〜２／１であり、
（ｃ）油分の総重量の２０質量％以上がシリコーン油であること、
を特徴とする曳糸性組成物。
(B) a siliconized pullulan represented by the following general formula (V) :
(C) contains an oil component ,
The blending amounts of (a) and (b) are 3 to 10% by mass,
The ratio of the blending amount of (a) to (b) ((a) / (b)) is 2/5 to 2/1,
(C) 20% by mass or more of the total weight of the oil is silicone oil,
A spinnable composition characterized by the above.
A cosmetic for hair containing the spinnable composition according to claim 1 as a base.