JP4950072B2 - 無溶媒の水性ポリウレタン分散液およびそれからの造形品 - Google Patents
無溶媒の水性ポリウレタン分散液およびそれからの造形品 Download PDFInfo
- Publication number
- JP4950072B2 JP4950072B2 JP2007555284A JP2007555284A JP4950072B2 JP 4950072 B2 JP4950072 B2 JP 4950072B2 JP 2007555284 A JP2007555284 A JP 2007555284A JP 2007555284 A JP2007555284 A JP 2007555284A JP 4950072 B2 JP4950072 B2 JP 4950072B2
- Authority
- JP
- Japan
- Prior art keywords
- article
- dispersion
- substrate
- mdi
- prepolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本出願は現在係属中の、2005年10月19日出願の米国特許出願第11/253927号、2005年2月11日出願の米国特許出願第11/056067号、および2005年12月13日出願の米国特許出願第11/300229号の優先権を主張するものである。
約600〜約3,500の数平均分子量を有する少なくとも1つのポリエーテル(コポリエーテルを含む)、ポリカーボネートまたはポリエステルポリオール成分、例えば、約1,400〜約2,400の数平均分子量を有するポリ(テトラメチレンエーテル)グリコール、
約65:35〜約35:65の4,4’−MDI対2,4’−MDI異性体の比の、4,4’−および2,4’−メチレンビス(フェニルイソシアネート)(MDI)異性体の混合物であるポリイソシアネート、ならびに
(i)成分b)のMDI異性体の混合物と反応することができるヒドロキシ基と(ii)成分b)のMDI異性体の混合物と反応することができない、中和時に塩を形成することができる少なくとも1つのカルボン酸基とを有する少なくとも1つのジオール化合物
を含む水性ポリウレタン分散液での使用のためのプレポリマーを含んでもよい。
約600〜約3,500の数平均分子量を有する少なくとも1つのポリエーテル(コポリエーテルを含む)、ポリカーボネートまたはポリエステルポリオール成分、好ましくは、約600〜約3,500の数平均分子量を有するポリ(テトラメチレンエーテル)グリコール、
約65:35〜約35:65の4,4’−MDI対2,4’−MDI異性体の比の、4,4’−および2,4’−メチレンビス(フェニルイソシアネート)(MDI)異性体の混合物であるポリイソシアネート、ならびに
(i)成分b)のMDI異性体の混合物と反応することができるヒドロキシ基と(ii)成分b)のMDI異性体の混合物と反応することができない、中和時に塩を形成することができる少なくとも1つのカルボン酸基とを有する少なくとも1つのジオール化合物
を含み、
そして成分a)、b)、およびc)を実質的に無溶媒の系で組み合わせる工程を含む方法を含んでもよい。
該水性ポリウレタン分散液は実質的に無溶媒の系であり、
成分c)とイオン性塩を形成するための少なくとも1つの中和剤、
イソシアネート基のためのブロッキング剤としての少なくとも1つの単官能性ジアルキルアミン化合物、
場合により、少なくとも1つのジアミン鎖延長成分、ならびに
場合により、ポリマーのモル当たり少なくとも3つ以上の第一級および/または第二級アミノ基を有する、500より大きい分子量を有する少なくとも1つのポリマー成分
をさらに含む水性ポリウレタン分散液を含んでもよい。
水性ポリウレタン分散液がプレポリマーを含み、水性ポリウレタン分散液が、
成分c)とイオン性塩を形成するための少なくとも1つの中和剤、
イソシアネート基のためのブロッキング剤としての少なくとも1つの単官能性ジアルキルアミン化合物
をさらに含む実質的に無溶媒の系であり、
およびプレポリマーを水性媒体に分散させる工程を含み、少なくとも1つの中和剤がプレポリマーを水性媒体に分散させる前にプレポリマーか水性媒体かのどちらかに加えられ、そして少なくとも1つのブロッキング剤がプレポリマーを水性媒体に分散させる間にかまたはその後かのどちらかに水性媒体に加えられる方法を含んでもよい。
約34%〜約89%の成分a)、
約59%〜約10%の成分b)、および
約7.0%〜約1.0%の成分c)。
a)テラセイン(登録商標)1800ポリエーテルグリコール:約61%〜約80%、
b)モンデュール(登録商標)MLジイソシアネート:約35%〜約18%、および
c)2,2−ジメチロールプロピオン酸(DMPA):約4.0%〜約2.0%。
−約0〜10%、例えば約0〜5%、典型的には約0%〜約3%の伸長後残留歪、
−約400〜約800%の伸び、および
−約0.5〜約3Mpaのテナシティ。
−強度の少なくとも50%が洗濯前のそれから維持されている50回洗濯後の剥離強度、
−少なくとも約0〜約0.5cfmの通気度、および
−24時間にわたって少なくとも約0〜約300g/m2の水蒸気透過度。
以下の実施例では、次の分析方法を用いた。
その全開示が参照により本明細書に援用される、ASTM(米国材料試験協会)D903−93をフィルム積層布の試験のために修正した。試験に使用したサンプルサイズは1インチ×6インチ(2.5cm×15cm)であった。分離速度は2インチ毎分(5センチメートル毎分)であった。データは、表2および4に示すように、サンプル幅のインチ当たりのポンドの力(ミリメートル当たりのキログラム)として報告する。
その全開示が参照により本明細書に援用される、AATCC(米国繊維化学者・色彩技術者協会)試験方法150−2001を成形ブラカップの洗濯のために用いた。機械サイクルは(I)標準/木綿スターディ(sturdy)であった。洗濯温度は(III)41℃であった。乾燥手順は、(A)(i)10分冷却時間で66℃30分間のタンブル木綿スターディであった。
その全開示が参照により本明細書に援用される、ASTM E96−00を物品の水蒸気輸送性を試験するために用いた。データは、表7に示すように、24時間期間の平方メートル当たりのグラムとして報告する。
その全開示が参照により本明細書に援用される、ASTM D−737を物品の通気性を試験するために用いた。データは、表7に示すように、布の平方フィート当たり分当たりの空気の立方フィート(cfm、布の平方センチメートル当たり秒当たりの空気の立方センチメートル(ccs))として報告する。
伸びおよびテナシティ特性は、動的引張試験機インストロン(Instron)を用いてフィルムについて測定した。サンプルサイズは、長い寸法に沿って測定されて1×3インチ(1.5cm×7.6cm)であった。サンプルをクランプに入れ、最大伸びに達するまで200%伸び毎分の歪み速度で引き伸ばした。テナシティおよび伸びは、フィルムが破壊する直前に測定した。同様に、残留歪%は、フィルムの1×3インチ・サンプル(1.5cm×7.6cm)を200%毎分の歪み速度で5サイクルの間0〜50%伸びに引き伸ばすことによって測定した。残留歪%は第5サイクル後に測定した。
テラセイン(登録商標)1800は、1,800の数平均分子量の、線状ポリテトラメチレングリコール(PTMEG)(カンザス州ウィッチタおよびデラウェア州ウィルミントンのインビスタ社(Invista,S.a.r.L.,of Wichita,KS and Wilmington,DE)から市販されている)であり、
プルラコール(Pluracol)(登録商標)HP4000Dは、400の数平均分子量の、線状の第一級ヒドロキシル末端ポリプロピレンエーテルグリコール(バスフ、ベルギー国ブリュッセル(Bruxelles,Belgium)から市販されている)であり、
モンデュール(登録商標)MLは、50〜60%の2,4’−MDI異性体および50〜40%の4,4’−MDI異性体を含有するジフェニルメタンジイソシアネート(MDI)の異性体混合物(バイエル、テキサス州ベイタウン(Baytown,TX)から市販されている)であり、
ルプラネート(登録商標)MIは、45〜55%の2,4’−MDI異性体および55〜45%の4,4’−MDI異性体を含有するジフェニルメタンジイソシアネート(MDI)の異性体混合物(バスフ、ミシガン州ワイアンドット(Wyandotte,Michigan)から市販されている)であり、
アイソネート(登録商標)125MDRは、98%の4,4’−MDI異性体および2%の2,4’−MDI異性体を含有するジフェニルメタンジイソシアネート(MDI)の純混合物(ダウ・カンパニー、ミシガン州ミッドランド(Dow Company,Midland,Michigan)から市販されている)であり、そして
DMPAは2,2−ジメチロールプロピオン酸である。
プレポリマーの製造を窒素雰囲気のグローブボックス中で行った。圧力駆動撹拌機、加熱マントル、および熱電対温度測定を備えている2000mlパイレックス(Pyrex)(登録商標)ガラス反応ケトルに、382.5グラムのテラセイン(登録商標)1800グリコールおよび約12.5グラムのDMPAを装入した。この混合物を撹拌しながら約50℃に加熱し、それに約105グラムのルプラネート(登録商標)MIジイソシアネートの添加が続いた。反応混合物を次に連続的に撹拌しながら約90℃に加熱し、90℃に約120分間保持し、その時間後に、混合物の%NCOがイソシアネート末端基を有するプレポリマーの計算値(1.914の%NCO照準)にマッチする安定値に低下したので、反応を完了させた。プレポリマーの粘度を、約40℃で操作される、モデル(Model)DV−8落球粘度計(Falling Ball Viscometer)(デュラテック・コープ、バージニア州ウェーンズバロ(Duratech Corp.,Waynesboro,VA.)によって販売される)を用いてASTM D1343−69の一般法に従って測定した。キャップドグリコールプレポリマーの、NCO基の重量パーセントの観点からの、全イソシアネート部分含有率を、その全開示が参照により本明細書に援用される、(非特許文献2)の方法によって測定した。
製造手順は、下記原料を反応混合物に使用したことを除いては、実施例1と同じものであった:
テラセイン(登録商標)1800: 約361グラム、
DMPA: 約19グラム、および
モンデュール(登録商標)ML: 約120グラム。
製造手順は、下記原料を反応混合物に使用したことを除いては、実施例1と同じものであった:
テラセイン(登録商標)1800: 約349グラム、
DMPA: 約21グラム、および
モンデュール(登録商標)ML: 約130グラム。
製造手順は、下記原料を反応混合物に使用したことを除いては、実施例1と同じものであった:
テラセイン(登録商標)1800: 約329グラム、
プルラコール(登録商標)HP4000D:約30グラム、
DMPA: 約21グラム、および
モンデュール(登録商標)ML: 約120グラム。
製造手順は、下記原料を反応混合物に使用したことを除いては、実施例1と同じものであった:
テラセイン(登録商標)1800: 約331グラム、
プルラコール(登録商標)HP4000D:約30グラム、
DMPA: 約19グラム、および
モンデュール(登録商標)ML: 約120グラム。
下記プレポリマーサンプルにおいて、製造手順ならびに原料タイプおよび量は、MDIイソシアネートを除いては同じものに保った。比較のために、アイソネート(登録商標)125MDRを、下に示すような反応混合物にルプラネート(登録商標)MIまたはモンデュール(登録商標)MLの代わりに同じ量で使用した。
テラセイン(登録商標)1800: 約382.5グラム、
DMPA: 約12.5グラム、および
アイソネート(登録商標)125MDR:約105グラム。
テラセイン(登録商標)1800: 約361グラム、
DMPA: 約19グラム、および
アイソネート(登録商標)125MDR:約120グラム。
テラセイン(登録商標)1800: 約349グラム、
DMPA: 約21グラム、および
アイソネート(登録商標)125MDR:約130グラム。
テラセイン(登録商標)1800: 約329グラム、
プルラコール(登録商標)HP4000D:約30グラム、
DMPA: 約21グラム、および
アイソネート(登録商標)125MDR: 約120グラム。
テラセイン(登録商標)1800: 約331グラム、
プルラコール(登録商標)HP4000D:約30グラム、
DMPA: 約19グラム、および
アイソネート(登録商標)125MDR: 約120グラム。
実施例1に記載した手順および組成に従って製造されるような、無溶媒のプレポリマーを、本発明のポリウレタンウレア水性分散液を製造するために使用した。
実施例1に記載した手順および組成に従って製造されるような、無溶媒のプレポリマーを、本発明のポリウレタンウレア水性分散液を製造するために使用した。
実施例1に記載した手順および組成に従って製造されるような、無溶媒のプレポリマーを、本発明のポリウレタンウレア水性分散液を製造するために使用した。
製造手順は、プレポリマーを混合した後にDEAを分散液へ加えなかったことを除いては、実施例11と同じものであった。最初は、分散液は実施例11と全く異ならないように見えた。しかしながら、分散液を室温で1週間以上エージングしたときに、この分散液からキャストしたフィルムは脆く、接着または積層に好適ではなかった。
実施例11で製造したような濾過した水性分散液を、連続の12インチ(30cm)実験室リバースロール・コーターで、シリコーンコーテッド剥離紙上にフィルムをコートするために使用した。コーターは、それぞれ、約60℃、75℃および120℃の温度設定の、3ゾーン乾燥オーブンを備えていた。乾燥の全滞留時間は約6分であった。約3ミル厚さの乾燥フィルムを約2メートル毎分のスピードで巻き取った。エラストマーフィルム12は容易に剥離紙から剥離することができ、積層のために使用した。
実施例11で製造したような濾過した水性分散液を、シリコーンコーテッド剥離紙上にフィルムをコートしてエラストマーフィルム12を形成するために使用した。実験室サンプルを、両面シリコーン剥離紙(プリント・マウント社(Print Mount Co.,Inc)製のカバーマウント(Covermount)DS 401−232−0096)の12インチ×12インチ(30cm×30cm)シートをマスキングテープで作業表面に固定することによって手動で製造した。水性分散液を剥離紙上へ注ぎ、5ミルの厚さの6インチ(15cm)幅のギャップを有する、図8および9に示すような、金属ナイフブレード工具を用いて剥離紙の全域に分散液を広げることによって均一な厚さへキャストした。過剰の溶液を紙タオルで拭き取った。キャスティングをフード下で一晩風乾させた。生じたフィルム12は、さらなる使用のために剥離紙から剥離するのが容易であった。
実施例15からの剥離紙12上のフィルムを、12インチ×12インチ(30cm×30cm)縦編スパンデックス14とのナイロン布の裏面上へ置いた。布/フィルム/剥離紙サンドイッチを羽島HP−400Cベルトオーブン積層機(Hashima HP−400C Belt Oven Laminator)(羽島株式会社(Hashima Co.,Ltd)、日本国岐阜市)、058−245−4501)へフィードし、図1のバス11aで示されるように、20秒の滞留時間およびP=1の圧力設定で、165℃で積層した16。剥離紙を取り除き、フィルム/布ラミネート・ストレッチ品18aを残した。
積層ストレッチ品18aを縦編ナイロン・スパンデックス布の別の12インチ×12インチ(30cm×30cm)片でカバーした。布/フィルム/布サンドイッチを羽島積層機へフィードし、20秒の滞留時間およびP=1の圧力設定で、165℃で積層してストレッチ品24aを与えた。実施例18についての剥離強度は2.56ポンド/インチであった。表2を参照されたい。
実施例15のフィルム12を、積層温度が120℃であったことを除いては、実施例17と同じ条件下に布に積層した。剥離紙を取り除き、フィルム/布ラミネート・ストレッチ品18aを残した。物品18aのフィルム側を縦編ナイロン・スパンデックス布の別の12インチ×12インチ(30cm×30cm)層でカバーした。布/フィルム/布サンドイッチを羽島積層機へフィードし、20秒の滞留時間およびP=1の圧力設定で、165℃で積層してストレッチ品24aを与えた。実施例19についての剥離強度は1.71ポンド/インチであった。表2を参照されたい。
本実施例では、2つの18aのストレッチ品を、フィルム側が互いに面した状態で層状化させた。布/フィルム/フィルム/布サンドイッチを羽島積層機へフィードし、20秒の滞留時間およびP=1の圧力設定で、165℃で積層してストレッチ品を与えた。実施例20についての剥離強度は4.25ポンド/インチであった。表2を参照されたい。
実施例15のフィルム12を剥離紙から注意深く取り外し、12インチ×12インチ(30cm×30cm)縦編スパンデックスとのナイロン布上へ置いた14。縦編ナイロン・スパンデックス布の別の12インチ×12インチ(30cm×30cm)層をキャストフィルム上へ置いた20。布/フィルム/布サンドイッチ20を羽島積層機へフィードし、20秒の滞留時間およびP=1の圧力設定で、165℃で積層して22ストレッチ品24aを与えた。実施例21についての剥離強度は1.72ポンド/インチであった。表2を参照されたい。
第2フィルムを剥離紙から注意深く取り除き、布/フィルム/布サンドイッチ24a上に置いて物品を形成した26。縦編ナイロン・スパンデックス布の第2の12インチ×12インチ(30cm×30cm)層をキャストフィルムの第2層上へ置いた28。布/フィルム/布/フィルム/布サンドイッチを羽島積層機へフィードし、30におけるように20秒の滞留時間およびP=1の圧力設定で、165℃で積層してストレッチ品32aを与えた。
本実施例では、縦編ナイロン・スパンデックス布の一片(1インチ×12インチ(2.5cm×30cm))を実施例11からの高粘度水性分散液10b中へ浸漬し、取り出し、次に過剰を、手袋をした指間で圧搾除去した。過剰を、手袋をした指間で2回圧搾除去して浸漬品34を与えた。コートしたストリップを吊し、フード下に一晩風乾させてストレッチ品38a、図2のパス21aを与えた。
横方向に変形可能な、軽量不織布の一片を、実施例12の方法によって製造した、低粘度の水性分散液10b(40重量%固形分および28センチポアズ)中へ浸漬する。浸漬品34を、滴らせて過剰の分散液を除去し、次に一晩ドラフト中で乾燥させるために吊して36ストレッチ品38a、図2のバス21aを与える。
本実施例では、実施例23からのストレッチ品38aを縦編ナイロン・スパンデックス布(6インチ×12インチ(15cm×30cm))でカバーした40。層状品40を羽島積層機へフィードし、42、図2のパス21bにおけるように20秒の滞留時間およびP=1の圧力設定で、165℃で積層してストレッチ品44aを与えた。実施例25についての剥離強度は6.17ポンド/インチであった。表2を参照されたい。
本実施例では、ストレッチ品44aを縦編ナイロン・スパンデックス布(6インチ×12インチ(15cm×30cm))でカバーした、46、図2のバス21c。層状品46を羽島積層機へフィードし、48におけるように20秒の滞留時間およびP=1の圧力設定で、165℃で積層してストレッチ品50aを与えた。実施例26についての剥離強度は5.26ポンド/インチであった。表2を参照されたい。
本実施例では、実施例12で製造したような水性分散液の濾過した溶液を、典型的なスプレーボトルへ注ぎ入れる。図3に示すように、濾過した水性分散液10cを、スプレーボトルを用いて両ストレッチ木綿/スパンデックス綾織布に直接塗布する52。布を風乾させて54、ストレッチ品56aを形成する、図3のパス31a。
ストレッチデニム生地の一片を、凝固剤としての20重量%硝酸カルシウム四水和物の水溶液を含有する浴中へ浸漬することによって前処理し、オーブン中100℃で30分間乾燥させる。実施例12の方法によって製造した、水性分散液10c(40重量%固形分および28センチポアズ)を、前処理した生地の裏面上へ5ミルギャップ厚さを有する、図8および9に示すような、ブレードで均一にコートする。分散液を、しみ込むことなく生地の表面上で凝固させる。この布を次にオーブン中80℃で60分間乾燥させて54ストレッチ品56a、図3のパス31aを与える。
ストレッチデニム生地の一片を、実施例11の高粘度分散液10c(43%固形分および25,000センチポアズ)でコートする。この増加した粘度は、分散液が生地にしみ込むことなく生地の一面上にコートされるのを可能にする52。布をオーブン中80℃で60分間乾燥させて54ストレッチ品56a、図3のパス31aを与える。
12インチ×12インチ(30cm×30cm)縦編ナイロン・スパンデックス布片を、マスキングテープを用いて作業表面に固定した(布がたて方向にわずかな張力下に保持されるのを可能にする)。実施例11の濾過した水性分散液10c(43重量%固形分および25,000センチポアズ)を布上へ注いだ52。この増加した粘度は、分散液が布にしみ込むことなく布の一面上にコートされるのを可能にする52。均一な厚さのフィルムを、10ミル厚さの6インチ幅ギャップを有する、図8および9に示す、金属工具を用いて布の全域に分散液を広げることによって製造した。過剰の溶液を紙タオルで拭き取った。コーテッド布をフード下で一晩風乾させた。物品52を羽島積層機へフィードし、54におけるように20秒の滞留時間およびP=1の圧力設定で、165℃で積層してストレッチ品56a、図3のパス31aを形成した。
12インチ×12インチ(30cm×30cm)縦編ナイロン・スパンデックス布片を、マスキングテープを用いて作業表面に固定した(布がたて方向にわずかな張力下に保持されるのを可能にする)。実施例11の濾過した水性分散液10c(43重量%固形分および25,000センチポアズ)を布上へ注いだ52。均一な厚さのフィルムを、10ミル厚さの6インチ幅ギャップを有する、図8および9に示す、金属工具を用いて布の全域に分散液を広げることによって製造した。過剰の溶液を紙タオルで拭き取った。別の12インチ×12インチ(30cm×30cm)縦編ナイロン・スパンデックス布を、分散液上に置き、軽くプレスして接着を促進した58、図3のパス31b。コーテッド布サンドイッチをフード下で一晩風乾させた。層状品58を羽島積層機へフィードし、60におけるように20秒の滞留時間およびP=1の圧力設定で、165℃で積層してストレッチ品62aを与えた。実施例31についての剥離強度は4.06ポンド/インチであった。表2を参照されたい。
ストレッチ品24a、図1を、100%木綿丸編布をトップ布およびボトム布として使用したことを除いては実施例21に従って製造した。木綿ベースのストレッチ品24aの12インチ×12インチ(30cm×30cm)片を、8.5cm深さの円形ビュレット金型を備えたテキシルフォールムング・ウィリ・レーマン社の成形機タイプ2030NT(Texilformung Willi Lehman GmbH Molding Machine Type 2030 NT)を用いてブラカップに成形した。ビュレットおよび円錐金型ベースを195℃に加熱し、一方、リングクランプを185℃に加熱した。布を標準慣行に従って45秒間成形した。カップ高さを成形直後およびAATCC試験方法150−2001に従った洗濯および乾燥サイクル後に再び測定した。積層および成形した木綿のカップは7.4cmの高さを有した。洗濯後に、実施例32のカップは4.2cmの高さを有した。
100%木綿丸編の12インチ×12インチ(30cm×30cm)片を実施例32と同じやり方で成形した。カップ高さを成形直後およびAATCC試験方法150−2001に従った洗濯および乾燥サイクル後に再び測定した。100%木綿丸編成形カップは7.3cmの高さを有した。洗濯後に、比較例33Cのカップは1.9cmの高さを有した。
ストレッチ品24a、図1を、実施例21に従って、トップ布およびボトム布として縦編ナイロン・スパンデックス布を使って製造した。縦編ナイロン・スパンデックスベースのストレッチ品24aの12インチ×12インチ(30cm×30cm)片を、実施例32と同じやり方で成形した。カップ高さを成形直後およびAATCC試験方法150−2001に従った洗濯および乾燥サイクル後に再び測定した。積層および成形したカップは6.7cmの高さを有した。洗濯後に、実施例34のカップは6.4cmの高さを有した。
100%縦編ナイロンの12インチ×12インチ(30cm×30cm)片を、実施例32と同じやり方で成形した。カップ高さを成形直後およびAATCC試験方法150−2001に従った洗濯および乾燥サイクル後に再び測定した。積層および成形したカップは6.8cmの高さを有した。洗濯後に、比較例35Cのカップは5.9cmの高さを有した。
4つのスパンデックス糸(ライクラ(Lycra)(登録商標)70デニール)をパッケージから110cm長さへカットし、サイド−バイ−サイドに置いた。糸を、フラット束でサイド−バイ−サイドにレイダウンし、実施例11、図14のキャストフィルムから形成したテープへプレスした。糸テープ複合材料を縦編布と共に接合機(ソー・システムズ、英国レスター(Sew Systems,Leicester,England)から市販されている)へフィードして布上に折り重ねたへりを形成した。へりの折り重ねは180℃で実施し、接着テープで一緒に保持され、そしてスパンデックス糸で強化された滑らかなへりをもたらした、図16。
本実施例では、へりの折り重ねを実施例36と同様に行ったが、スパンデックス糸を延伸し(引き伸ばし)、そしてテープは、それが接合機へフィードされつつある間ずっと延伸もまたは張力もほとんどないし全く持たなかった。これは、実施例36のへりに似ているへりをもたらしたが、本実施例でのへりは集結した。
本実施例では、実施例36の布を実施例30におけるような分散液の溶液でコートする。ストレッチ糸を布に付け、布を、実施例36におけるような接合機を用いてへりを折り返す。ストレッチ糸で強化されたフラット接合へりが形成される。
本実施例では、スパンデックス糸を実施例11の分散液でコートする。コーテッド糸を布のエッジに付ける。布のエッジを折り重ねてへりを作る。折り重ねたへりを、実施例36におけるように接合機を用いて接合する。布を接合するためにストレッチ糸を使用するフラット接合へりが形成される。
実施例17からと同様に製造した積層品を剥離強度について試験した。サンプルを5、10、20、30、40、および50回洗濯した。本実施例についてのデータを表4に与える。
積層品を、フィルムを除いては実施例40に従って製造した。本実施例のために使用したフィルムは1ミル・ストレッチフィルム#3410(マサチューセッツ州シャーリーのベミス・アソシエイツ社(Bemis Associates,Inc.of Shirley,Massachusetts)から市販されている)であった。ラミネートを剥離強度について試験した。サンプルを5、10、20、30、40、および50回洗濯した。本実施例についてのデータを表4および5に与える。
本実施例では、実施例12の分散液を実施例15に従って使用して2ミル・フィルムを製造した。フィルムの第2層を、ポリプロピレンシート上の4.5ミル・フィルムへ実施例12の分散液のキャスティングによって製造した。このフィルムの2つの層を一緒に、熱油加熱された100℃の金属ロールおよび15psiの圧力下のゴムロールによって積層して6.5ミル厚さのフィルムを形成した。本実施例でのフィルムを、テナシティ、伸びおよび残留歪をはじめとする引張特性について試験した、表6。
本実施例では、実施例13の分散液を実施例15に従って使用して3ミル・フィルムを製造した。本実施例でのフィルムを、テナシティ、伸びおよび残留歪をはじめとする引張特性について試験した、表6。
本実施例では、フィルムを、ポリプロピレンシート上の4.5ミル・フィルムへの実施例12の分散液のキャスティングによって製造した。このフィルムの2つの層を一緒に、熱油加熱された100℃の金属ロールおよび15psiの圧力下のゴムロールによって積層して9ミル厚さのフィルムを形成した。本実施例でのフィルムを、テナシティ、伸びおよび残留歪をはじめとする引張特性について試験した、表6。
本実施例では、実施例18のラミネートを上に与えた方法に従って水蒸気輸送について試験した。データを表7に与える。
本実施例では、実施例17のラミネートを上に与えた方法に従って水蒸気輸送について試験した。データを表7に与える。
本実施例では、実施例18のラミネートを上に与えた方法に従って通気性について試験した。データを表7に与える。
本実施例では、実施例17のラミネートを上に与えた方法に従って通気性について試験した。データを表7に与える。
以下に、本発明の好ましい態様を示す。
1. a)600〜3,500の数平均分子量を有する、少なくとも1つのポリエーテル、ポリエステル、またはポリカーボネートポリオール、
b)4,4’−MDI対2,4’−MDI異性体の比が65:35〜35:65の範囲である、4,4’−および2,4’−メチレンビス(フェニルイソシアネート)(MDI)異性体の混合物、ならびに
c)(i)成分b)のMDI異性体の混合物と反応することができるヒドロキシ基と、(ii)成分b)のMDI異性体の混合物と反応することができない、中和時に塩を形成することができる少なくとも1つのカルボン酸基とを含む少なくとも1つのジオール化合物
を含む水性ポリウレタン分散液での使用のためのプレポリマーであって、
実質的に無溶媒であることを特徴とするプレポリマー。
2. 成分a)の少なくとも1つのポリエーテル、ポリエステル、またはポリカーボネートポリオールが1,400〜2,400の数平均分子量を有するポリ(テトラメチレンエーテル)グリコールであることを特徴とする1.に記載のプレポリマー。
3. 4,4’−MDI対2,4’−MDI異性体の比が55:45〜45:55の範囲であることを特徴とする1.に記載のプレポリマー。
4. 少なくとも1つのジオール化合物が2,2−ジメチロールプロピオン酸(DMPA)、2,2−ジメチロールブタン酸、および2,2−ジメチロール吉草酸からなる群から選択されることを特徴とする1.に記載のプレポリマー。
5. 4,4’−MDI対2,4’−MDI異性体の比が55:45〜45:55の範囲であり、そして少なくとも1つのジオール化合物が2,2−ジメチロールプロピオン酸(DMPA)であることを特徴とする2.に記載のプレポリマー。
6. 成分(a)がプレポリマーの総重量を基準にして34%〜89%の範囲の重量百分率で存在し、成分b)がプレポリマーの総重量を基準にして59%〜10%の範囲の重量百分率で存在し、そして成分c)がプレポリマーの総重量を基準にして7.0%〜1.0%の範囲の重量百分率で存在することを特徴とする1.に記載のプレポリマー。
7. 落球法によって40℃で測定された、500〜6,000ポアズのバルク粘度を有することを特徴とする1.に記載のプレポリマー。
8. 落球法によって40℃で測定された、500〜4,500ポアズのバルク粘度を有することを特徴とする7.に記載のプレポリマー。
9. 酸化防止剤、UV安定剤、着色剤、顔料、架橋剤、相変化物質、抗菌剤、鉱物、マイクロカプセル化健康添加剤、ナノ粒子、炭酸カルシウム、難燃剤、粘着防止添加剤、耐塩素性添加剤、染色助剤、接着促進剤、帯電防止剤、クレーター形成防止剤、クローリング防止剤、蛍光増白剤、融合助剤、導電性添加剤、ルミネセンス添加剤、フロー剤および均染剤、凍結融解安定剤、滑剤、有機および無機充填剤、防腐剤、テクスチャー加工剤、熱変色添加剤、昆虫忌避剤、ならびに湿潤剤からなる群から選択される少なくとも1つの追加成分をさらに含むことを特徴とする1.に記載のプレポリマー。
10. 成分a)の少なくとも1つのポリエーテル、ポリエステル、またはポリカーボネートポリオールが2つのグリコール末端または3つのグリコール末端を有することを特徴とする1.に記載のプレポリマー。
11. 水性ポリウレタン分散液がポリウレタンウレアであることを特徴とする1.に記載のプレポリマー。
12. 水性ポリウレタン分散液での使用のためのプレポリマーの製造方法であって、プレポリマーが、
a)600〜3,500の数平均分子量を有する、少なくとも1つのポリエーテル、ポリエステル、またはポリカーボネートポリオール、
b)4,4’−MDI対2,4’−MDI異性体の比が65:35〜35:65の範囲である、4,4’−および2,4’−メチレンビス(フェニルイソシアネート)(MDI)異性体の混合物、ならびに
c)(i)成分b)のMDI異性体の混合物と反応することができるヒドロキシ基と、(ii)成分b)のMDI異性体の混合物と反応することができない、中和時に塩を形成することができる少なくとも1つのカルボン酸基とを含む少なくとも1つのジオール化合物
を含み、
そして該方法が成分a)、b)、およびc)を実質的に無溶媒の系で組み合わせる工程を含むことを特徴とする方法。
13. 成分a)、b)、およびc)が混合され、そして50℃〜100℃の範囲の温度で反応させてもよいことを特徴とする12.に記載の方法。
14. 成分a)、b)、およびc)が1つの工程で一緒に組み合わせられることを特徴とする12.に記載の方法。
15. 成分a)およびb)が第1工程で反応させられ、それに成分c)との混合が続くことを特徴とする12.に記載の方法。
16. 触媒をさらに含むことを特徴とする12.に記載の方法。
17. a)600〜3,500の数平均分子量を有する、少なくとも1つのポリエーテル、ポリエステル、またはポリカーボネートポリオール、
b)4,4’−MDI対2,4’−MDI異性体の比が65:35〜35:65の範囲である、4,4’−および2,4’−メチレンビス(フェニルイソシアネート)(MDI)異性体の混合物、ならびに
c)(i)成分b)のMDI異性体の混合物と反応することができるヒドロキシ基と(ii)成分b)のMDI異性体の混合物と反応することができない、中和時に塩を形成することができる少なくとも1つのカルボン酸基とを含む少なくとも1つのジオール化合物
を含むプレポリマーを含む水性ポリウレタン分散液であって、
該水性ポリウレタン分散液は実質的に無溶媒の系であり、
d)少なくとも1つのジオール化合物とイオン性塩を形成するための少なくとも1つの中和剤、および
e)イソシアネート基のためのブロッキング剤としての少なくとも1つの単官能性ジアルキルアミン化合物
をさらに含むことを特徴とする水性ポリウレタン分散液。
18. 少なくとも1つの界面活性剤および少なくとも1つの消泡剤をさらに含むことを特徴とする17.に記載の水性ポリウレタン分散液。
19. 少なくとも1つのレオロジー調整剤をさらに含むことを特徴とする18.に記載の水性ポリウレタン分散液。
20. f)少なくとも1つのジアミン鎖延長成分、および
g)ポリマーのモル当たり少なくとも3つ以上の第一級および/または第二級アミノ基を有する、500より大きい分子量を有する少なくとも1つのポリマー成分
をさらに含むことを特徴とする19.に記載の水性ポリウレタン分散液。
21. 少なくとも1つの中和剤が第三級アミンおよびアルカリ金属水酸化物からなる群から選択され、そして少なくとも1つのブロッキング剤がN,N−ジエチルアミン、N−エチル−N−プロピルアミン、N,N−ジイソプロピルアミン、N−tert−ブチル−N−メチルアミン、N−tert−ブチル−N−ベンジルアミン、N,N−ジシクロヘキシルアミン、N−エチル−N−イソプロピルアミン、N−tert−ブチル−N−イソプロピルアミン、N−イソプロピル−N−シクロヘキシルアミン、N−エチル−N−シクロヘキシルアミン、N,N−ジエタノールアミン、および2,2,6,6−テトラメチルピペリジンからなる群から選択されることを特徴とする17.に記載の水性ポリウレタン分散液。
22. 少なくとも1つの界面活性剤がドデシル硫酸ナトリウム、ドデシルベンゼンスルホン酸ナトリウム、エトキシル化ノニルフェノール、および臭化ラウリルピリジニウムからなる群から選択されることを特徴とする18.に記載の水性ポリウレタン分散液。
23. 少なくとも1つのレオロジー調整剤が疎水性改質エトキシレートウレタン(HEUR)、疎水性改質アルカリ膨潤性エマルジョン(HASE)、および疎水性改質ヒドロキシエチルセルロース(HMHEC)からなる群から選択されることを特徴とする19.に記載の水性ポリウレタン分散液。
24. 少なくとも1つのジアミン鎖延長成分が1,2−エチレンジアミン、1,4−ブタンジアミン、1,6−ヘキサメチレンジアミン、1,12−ドデカンジアミン、1,2−プロパンジアミン、2−メチル−1,5−ペンタンジアミン、1,2−シクロヘキサンジアミン、1,4−シクロヘキサンジアミン、4,4’−メチレン−ビス(シクロヘキシルアミン)、イソホロンジアミン、2,2−ジメチル−1,3−プロパンジアミン、およびm−テトラメチルキシレンジアミンからなる群から選択され、そして500より大きい分子量を有する少なくとも1つのポリマー成分がポリエチレンイミンデンドリマー、ポリ(ビニルアミン)デンドリマー、ポリ(アリルアミン)デンドリマー、およびポリ(アミドアミン)デンドリマーからなる群から選択されることを特徴とする20.に記載の水性ポリウレタン分散液。
25. 成分a)の少なくとも1つのポリエーテル、ポリエステル、またはポリカーボネートポリオールが1,700〜2,100の数平均分子量を有するポリ(テトラメチレンエーテル)グリコールであり、4,4’−MDI対2,4’−MDI異性体の比が55:45〜45:55の範囲であり、そして少なくとも1つのジオール化合物が2,2−ジメチロールプロピオン酸(DMPA)であることを特徴とする17.に記載の水性ポリウレタン分散液。
26. 酸化防止剤、UV安定剤、着色剤、顔料、架橋剤、相変化物質、抗菌剤、鉱物、マイクロカプセル化健康添加剤、ナノ粒子、炭酸カルシウム、難燃剤、粘着防止添加剤、耐塩素分解性添加剤、染色助剤、湿潤剤、および均染剤、接着促進剤、帯電防止剤、クレーター形成防止剤、クローリング防止剤、蛍光増白剤、融合助剤、導電性添加剤、ルミネセンス添加剤、フロー剤および均染剤、凍結融解安定剤、滑剤、有機および無機充填剤、防腐剤、テクスチャー加工剤、熱変色添加剤、ならびに湿潤剤からなる群から選択される少なくとも1つの追加成分をさらに含むことを特徴とする20.に記載の水性ポリウレタン分散液。
27. バルク粘度が落球法によって40℃で測定した際に10〜100,000センチポアズであることを特徴とする20.に記載の水性ポリウレタン分散液。
28. バルク粘度が落球法によって40℃で測定した際に500〜30,000センチポアズであることを特徴とする27.に記載の水性ポリウレタン分散液。
29. 水性ポリウレタン分散液の製造方法であって、
水性ポリウレタン分散液がプレポリマーを含み、水性ポリウレタン分散液が、
d)少なくとも1つのジオール化合物とイオン性塩を形成するための少なくとも1つの中和剤、および
e)イソシアネート基のためのブロッキング剤としての少なくとも1つの単官能性ジアルキルアミン化合物
をさらに含む実質的に無溶媒の系であり、
およびプレポリマーを水性媒体に分散させる工程を含み、少なくとも1つの中和剤がプレポリマーを水性媒体に分散させる前にプレポリマーか水性媒体かのどちらかに加えられ、そして少なくとも1つのブロッキング剤がプレポリマーを水性媒体に分散させる間にかまたはその後かのどちらかに水性媒体に加えられることを特徴とする方法。
30. 少なくとも1つのブロッキング剤がプレポリマーを水性媒体に分散させた直後に水性媒体に加えられることを特徴とする29.に記載の方法。
31. 少なくとも1つの中和剤がプレポリマーを水性媒体に分散させる前に水性媒体に加えられることを特徴とする30.に記載の方法。
32. 少なくとも1つの中和剤がプレポリマーを水性媒体に分散させる前にプレポリマーに加えられることを特徴とする30.に記載の方法。
33. 実質的に無溶媒の水性ポリウレタン分散液から誘導されることを特徴とする造形品。
34. 実質的に非粘着性であることを特徴とする33.に記載の造形品。
35. 成形されていることを特徴とする33.に記載の造形品。
36. 35.に記載の造形品を含むことを特徴とする物品。
37. 33.に記載の造形品を含むことを特徴とする物品。
38. 36.に記載の物品を含むことを特徴とする衣類。
39. ブラであることを特徴とする38.に記載の衣類。
40. 少なくとも1つの造形品と前記造形品が付けられる基材とを含むことを特徴とする物品。
41. 基材が編織布であることを特徴とする40.に記載の物品。
42. 衣類であることを特徴とする40.に記載の物品。
43. 造形品が剥離紙からの剥離と同時に基材に付けられることを特徴とする40.に記載の物品。
44. 造形品が基材に接合されまたは接着され、前記基材が編織布を含むことを特徴とする43.に記載の物品。
45. 造形品が編織布上の継ぎ目または支持区域に接合されるかまたは接着されることを特徴とする44.に記載の物品。
46. 衣類であることを特徴とする44.に記載の物品。
47. 衣類が下着、ブラジャー、パンティー、ランジェリー、水着、シェーパー、キャミソール、靴下、寝間着、エプロン、ウェットスーツ、タイ、手術着、宇宙服、制服、帽子、ガーター、汗止めバンド、ベルト、スポーツウェア、上着、雨着、冷気候ジャケット、パンツ、シャツ地、ドレス、ブラウス、男女トップス、セーター、コルセット、チョッキ、ニッカー、ソックス、ハイソックス、ドレス、ブラウス、エプロン、タキシード、ビシュト、アバーヤ、ヒジャーブ、ジルバーブ、サウブ、ブルカ、ケープ、コスチューム、潜水服、キルト、着物、ジャージ、ガウン、防護服、サリー、サロン、スカート、スパッツ、ストラ、スーツ、拘束衣、トーガ、タイツ、タオル、制服、ベール、ウェットスーツ、医療圧迫帯、包帯、スーツ芯材、ウエストバンド、およびそれらにおけるすべての構成材からなる群から選択されることを特徴とする42.に記載の物品。
48. 基材が前処理されることを特徴とする40.に記載の物品。
49. 基材が前記基材上のヒドロキシル官能性を増加させるために前処理されることを特徴とする40.に記載の物品。
50. 成形されていることを特徴とする40.に記載の物品。
51. 50.に記載の物品を含むことを特徴とする衣類。
52. ブラであることを特徴とする51.に記載の衣類。
53. 水性分散液でコートされた基材を含むことを特徴とする物品。
54. 分散液をスプレーする、コートする、塗装する、プリントする、型押しする、浸漬する、および含浸させるための手段を用いて分散液を基材に提供する工程を含むことを特徴とする53.に記載の物品の形成方法。
55. 成形されていることを特徴とする53.に記載の物品。
56. 衣類であることを特徴とする53.に記載の物品。
57. 55.に記載の物品を含むことを特徴とする衣類。
58. ブラであることを特徴とする57.に記載の衣類。
59. 手袋、コンドーム、ビーズ、繊維、およびフィルムのシートを含むことを特徴とする33.に記載の造形品。
60. フィルムまたはテープの2つ以上の層が付けられることを特徴とする33.に記載の造形品。
61. 水性ポリウレタン分散液の少なくとも1つの層をさらに含むことを特徴とする33.に記載の造形品。
62. プリントされていることを特徴とする33.に記載の造形品。
63. 0.1ミル〜250ミルの厚さを有することを特徴とする33.に記載の造形品。
64. 0.5ミル〜25ミルの厚さを有することを特徴とする63.に記載の造形品。
65. 1〜6ミルの厚さを有することを特徴とする64.に記載の造形品。
66. 水性分散液コーティングが2.5g/m2〜6.40kg/m2の坪量を有することを特徴とする53.に記載の物品。
67. 水性分散液コーティングが12.7g/m2〜635g/m2の坪量を有することを特徴とする66.に記載の物品。
68. 水性分散液コーティングが25.4g/m2〜152.4g/m2の坪量を有すことを特徴とする67.に記載の物品。
69. 接着剤がストレッチ部材を基材に折ったへり配置で貼り付けるために使用されることを特徴とする接着剤、ストレッチ部材、および基材を含む物品。
70. 接着剤がテープであることを特徴とする69.に記載の物品。
71. 接着剤が水性ポリウレタン分散液であることを特徴とする69.に記載の物品。
72. ストレッチ部材がスパンデックスであることを特徴とする69.に記載の物品。
73. ストレッチ部材がゴムであることを特徴とする69.に記載の物品。
74. ストレッチ部材が狭い弾性ストリップであることを特徴とする69.に記載の物品。
75. 接着剤およびストレッチ部材が第1工程で接合されて接着剤ストレッチ部材を製造し、そして接着剤ストレッチ部材が第2工程で基材に付けられることを特徴とする69.に記載の物品の製造方法。
76. 接着剤およびストレッチ部材が1つの工程で基材に加えられることを特徴とする69.に記載の物品の製造方法。
77. 69.に記載の物品を含むことを特徴とする衣類。
78. ブラジャーであることを特徴とする77.に記載の衣類。
79. 下着であることを特徴とする77.に記載の衣類。
80. 水着であることを特徴とする77.に記載の衣類。
81. 残留歪の%が0〜10%であることを特徴とする33.に記載の物品。
82. %残留歪が0〜5%であることを特徴とする33.に記載の物品。
83. %残留歪が0〜3%であることを特徴とする33.に記載の物品。
84. 最大伸びが400%〜800%であることを特徴とする33.に記載の物品。
85. テナシティが0.5〜3Mpaであることを特徴とする33.に記載の物品。
86. ラミネートの剥離強度が、AATCC−150−2001に従う50回洗濯の後のASTM D093−93に従って、元の剥離強度値の50%まで下がらないことを特徴とする物品および基材を含むラミネート。
87. ラミネートの水蒸気輸送がASTM E96−00に従って24時間にわたって0〜300g/m2であることを特徴とする物品および基材を含むラミネート。
88. ラミネートの通気度がASTM D737−96に従って0〜0.5cfmであることを特徴とする物品および基材を含むラミネート。
89. 造形品および基材が貼り付けられてラミネートを形成し、それによってラミネートの摩擦係数が基材の摩擦係数より高いことを特徴とする33.に記載の造形品および基材を含む物品。
90. 造形品を含む物品であって、物品が弾性率および長さを有し、前記弾性率が物品の長さに沿って変わることを特徴とする物品。
Claims (14)
- a)600〜3,500の数平均分子量を有する、少なくとも1つのポリエーテル、ポリエステル、またはポリカーボネートポリオール、
b)4,4’−MDI対2,4’−MDI異性体の比が65:35〜35:65の範囲である、4,4’−および2,4’−メチレンビス(フェニルイソシアネート)(MDI)異性体の混合物、ならびに
c)(i)成分b)のMDI異性体の混合物と反応することができるヒドロキシ基と(ii)成分b)のMDI異性体の混合物と反応することができない、中和時に塩を形成することができる少なくとも1つのカルボン酸基とを含む少なくとも1つのジオール化合物
を含むプレポリマーを含む無溶媒の水性ポリウレタン分散液から誘導されることを特徴とする造形品。 - 請求項1に記載の造形品を含むことを特徴とする物品。
- 請求項2に記載の物品を含むことを特徴とする衣類。
- 少なくとも1つの請求項1に記載の造形品と前記造形品が付けられる基材とを含むことを特徴とする物品。
- 請求項4に記載の物品を含むことを特徴とする衣類。
- 接着剤がストレッチ部材を基材に折ったへり配置で貼り付けるために使用されることを特徴とする接着剤、ストレッチ部材、および基材を含む物品であって、
前記接着剤がa)600〜3,500の数平均分子量を有する、少なくとも1つのポリエーテル、ポリエステル、またはポリカーボネートポリオール、
b)4,4’−MDI対2,4’−MDI異性体の比が65:35〜35:65の範囲である、4,4’−および2,4’−メチレンビス(フェニルイソシアネート)(MDI)異性体の混合物、ならびに
c)(i)成分b)のMDI異性体の混合物と反応することができるヒドロキシ基と(ii)成分b)のMDI異性体の混合物と反応することができない、中和時に塩を形成することができる少なくとも1つのカルボン酸基とを含む少なくとも1つのジオール化合物
を含むプレポリマーを含む無溶媒の水性ポリウレタン分散液から製造されることを特徴とする物品。 - 接着剤およびストレッチ部材が第1工程で接合されて接着剤ストレッチ部材を製造し、そして接着剤ストレッチ部材が第2工程で基材に付けられることを特徴とする請求項6に記載の物品の製造方法。
- 接着剤およびストレッチ部材が1つの工程で基材に加えられることを特徴とする請求項6に記載の物品の製造方法。
- 請求項5に記載の物品を含むことを特徴とする衣類。
- 請求項1に記載の造形品および基材を含むラミネートであって、前記ラミネートの剥離強度が、AATCC−150−2001に従う50回洗濯の後のASTM D093−93に従って、元の剥離強度値の50%まで下がらないことを特徴とするラミネート。
- 請求項1に記載の造形品および基材を含むラミネートであって、前記ラミネートの水蒸気輸送がASTM E96−00に従って24時間にわたって0〜300g/m2であることを特徴とするラミネート。
- 請求項1に記載の造形品および基材を含むラミネートであって、前記ラミネートの通気度がASTM D737−96に従って0〜0.5cfmであることを特徴とするラミネート。
- 造形品および基材が貼り付けられてラミネートを形成し、それによってラミネートの摩擦係数が基材の摩擦係数より高いことを特徴とする請求項1に記載の造形品および基材を含む物品。
- 請求項1に記載の造形品を含む物品であって、物品が弾性率および長さを有し、前記弾性率が物品の長さに沿って変わることを特徴とする物品。