JP4869673B2

JP4869673B2 - Brush piece of washing brush for car wash machine, washing brush for car wash machine and car wash machine

Info

Publication number: JP4869673B2
Application number: JP2005294158A
Authority: JP
Inventors: 健司白勢
Original assignee: Kowa Co Ltd
Current assignee: Kowa Co Ltd
Priority date: 2005-09-07
Filing date: 2005-09-07
Publication date: 2012-02-08
Anticipated expiration: 2025-09-07
Also published as: JP2007068954A

Description

本発明は、自動車あるいは車両の外面の被洗浄面に付着した汚れ等を洗浄する為の洗車機に使用する洗浄ブラシのブラシ片、及びそれを用いた洗車機用洗浄ブラシ、及びその洗車機用洗浄ブラシを用いた洗車機に関するものである。 The present invention relates to a brush piece of a cleaning brush used in a car wash machine for cleaning dirt or the like attached to a surface to be cleaned of an automobile or a vehicle, a washing brush for a car wash machine using the same, and a car wash machine therefor The present invention relates to a car wash machine using a cleaning brush.

自動車あるいは車両の外面の被洗浄面に付着した汚れ等を洗浄する為の洗車機に使用する洗浄ブラシのブラシ片に関しては、使用目的に応じて、さまざまな改良がなされ、材質については、合成樹脂繊維、布、フィルム状樹脂組成物、独立気泡発泡体等を使用したブラシ片が提案されてある。ところで、合成樹脂繊維は洗い残しが少なく、洗浄性が良好で、水を含まない為、凍結しにくいが、被洗浄面に傷を付けやすいという特徴を持っている。布は被洗浄面に柔らかく接触する為、被洗浄面に傷を付けにくいが、水を含む為、凍結しやすく、弾性変形しないことから、破れ、ほつれ、切れが発生し、耐久性が劣るという特徴を持っている。フィルムは洗浄時の音が小さく、被洗浄面に傷を付けにくいが、毛腰が弱く、耐久性が低いという特徴を有している。独立気泡発泡体は耐久性が良好で、被洗浄面に傷を付けにくいが、洗浄性が低いという特徴を有している。 Various improvements have been made to the brush pieces of cleaning brushes used in car wash machines for cleaning dirt, etc. adhering to the surface to be cleaned of automobiles or vehicles, depending on the purpose of use. Brush pieces using fibers, fabrics, film-like resin compositions, closed cell foams, and the like have been proposed. By the way, the synthetic resin fiber has a feature that it is hardly left unwashed, has good cleanability, does not contain water, and therefore is difficult to freeze, but it is easy to damage the surface to be cleaned. Because the cloth is softly in contact with the surface to be cleaned, it is difficult to scratch the surface to be cleaned, but because it contains water, it freezes easily and does not elastically deform, resulting in tearing, fraying, cutting, and poor durability. Has characteristics. The film has the characteristics that the sound at the time of cleaning is small and the surface to be cleaned is not easily scratched, but the fluff is weak and the durability is low. The closed-cell foam has good durability and is difficult to damage the surface to be cleaned, but has a characteristic of low cleaning properties.

従来の洗車機用洗浄ブラシのブラシ片は、上記の如くの特徴を有しているが、合成樹脂繊維においては、例えば、剛性度が１２００ｋｇ／ｃｍ^２〜５０００ｋｇ／ｃｍ^２の熱可塑性樹脂で構成された分岐形状の断面をなす発泡糸で、発泡倍率が１．１〜１．７倍であることを特徴とする回転ブラシ用発泡糸が、特公平６−２１３７１号公報に開示されてある。前記回転ブラシ用発泡糸は、熱可塑性樹脂に発泡剤を添加して、低発泡で発泡化することにより、腰の強さ、強度等を保ちつつ、柔軟性の高いブラシ用毛材を実現しているという特徴を有している。The brush strips of the conventional car wash cleaning brush, has the features of the above as, in the synthetic resin fibers, for example, stiffness is constituted by a thermoplastic resin 1200kg ^/ cm ² ~5000kg ^/ cm 2 Japanese Patent Publication No. 6-21371 discloses a foamed yarn for a rotating brush, which is a foamed yarn having a cross-section having a branched shape and having a foaming ratio of 1.1 to 1.7 times. The foamed yarn for rotating brush is made by adding a foaming agent to thermoplastic resin and foaming with low foaming, realizing a highly flexible bristle material for the brush while maintaining the strength and strength of the waist. It has the feature of being.

また、布においては、例えば、見掛け密度が０．２〜１ｇ／ｃｍ^３で、熱圧着面積が４〜４５％で部分熱圧着され、かつ撥水度が５０以上である合成長繊維不織布からなることを特徴とする洗車用ブラシが、特許第３１９１５３４号に開示されてある。前記洗車用ブラシは、自動車の塗装面を傷つけない合成長繊維不織布からなり、洗浄中に自動車の塗装面を痛めることが無いという特徴を有している。Moreover, in the cloth, for example, it is composed of a synthetic long-fiber nonwoven fabric having an apparent density of 0.2 to 1 g / cm ³ , a partial thermocompression bonding with a thermocompression bonding area of 4 to 45%, and a water repellency of 50 or more. A car wash brush characterized by this is disclosed in Japanese Patent No. 3191534. The car wash brush is made of a synthetic long-fiber nonwoven fabric that does not damage the painted surface of the automobile, and has a feature that the painted surface of the automobile is not damaged during washing.

また、極細繊維を用いた洗車ブラシに関しては、例えば、ブラシ用布帛が通水可能な貫通孔を複数個有することを特徴とする洗車用ブラシが特開２００４−１２３０９１号公報に開示されてある。前記洗車用ブラシは、布帛が複数の通水可能な貫通孔を有すると共に、極細繊維が用いられていることから、排水性に優れ、洗浄性ならびに拭き取り作業性に優れる上に、柔軟で軽量性を維持することができるという特徴を有している。 Moreover, regarding a car wash brush using ultrafine fibers, for example, JP 2004-123091 A discloses a car wash brush having a plurality of through-holes through which a brush fabric can pass water. The car wash brush has a plurality of through-holes through which water can flow and ultrafine fibers are used, so it has excellent drainage, cleaning and wiping workability, and is flexible and lightweight. Is maintained.

特公平６−２１３７１号公報 Japanese Examined Patent Publication No. 6-21371 特許第３１９１５３４号 Japanese Patent No. 3191534 特開２００４−１２３０９１号公報 JP 2004-123091 A

従来の洗車機用洗浄ブラシのブラシ片は、例えば、上記の如くの各種の特徴を有する技術が開示されてあるが、特公平６−２１３７１号公報に開示されてある技術においては、上記の如く、熱可塑性樹脂に発泡剤を添加して、低発泡で発泡化しているものの、被洗浄面に傷を付けやすいという課題を有している。また、特許第３１９１５３４号に開示されてある技術においては、ブラシ片が弾性変形しない為、切れ、破れ、ほつれ、座屈等による耐久性の低さという課題を有している。さらに、特開２００４−１２３０９１号公報に開示されてある技術においては、自動車、及び車両の装備品であるワイパーやアンテナ等が貫通孔に引っ掛かり、装備品の破損につながるという課題を有している。 For example, a conventional brush piece of a washing brush for a car wash machine has disclosed a technique having various characteristics as described above. However, in the technique disclosed in Japanese Patent Publication No. 6-21371, as described above. Although the foaming agent is added to the thermoplastic resin and foamed with low foaming, the surface to be cleaned is easily damaged. Further, in the technique disclosed in Japanese Patent No. 3191534, since the brush piece does not elastically deform, there is a problem of low durability due to cutting, tearing, fraying, buckling, and the like. Furthermore, the technique disclosed in Japanese Patent Application Laid-Open No. 2004-123091 has a problem that a wiper, an antenna, or the like, which is an automobile and vehicle equipment, is caught in the through-hole, resulting in equipment damage. .

本発明は、上記のような課題を解決するためになされたもので、高い洗浄性を有すると共に、被洗浄面に傷を付けることが無く、自動車、及び車両の装備品の破損が無く、且つ高い耐久性を有する洗車機用洗浄ブラシのブラシ片を提供することを目的としている。 The present invention has been made to solve the above problems, has high cleaning properties, does not damage the surface to be cleaned, does not damage automobiles and vehicle equipment, and An object of the present invention is to provide a brush piece of a car brush washing brush having high durability.

本発明にかかる洗車機用洗浄ブラシのブラシ片は、次のように構成したものである。
（１）自動車洗浄用あるいは車両洗浄用の洗車機に使用する洗浄ブラシのブラシ片において、前記洗浄ブラシのブラシ片は、複数のフィラメントからなる不織布にて形成されてあり、該不織布にたいして高分子弾性体が、コーティング、バインダー固着、あるいは練り込まれてあるものであって、前記フィラメントの少なくとも一部にはスリットが形成されてあり、且つ外周面の長手方向に沿って、前記スリットにより発生した角部が少なくとも二箇所以上形成されてあることを特徴としている。 The brush piece of the washing brush for a car wash machine according to the present invention is configured as follows.
(1) In a brush piece of a cleaning brush used in a car washing machine for car washing or vehicle washing, the brush piece of the washing brush is formed of a nonwoven fabric composed of a plurality of filaments, and has high polymer elasticity with respect to the nonwoven fabric. The body is coated, binder-bonded, or kneaded, and at least a part of the filament has a slit, and an angle generated by the slit along the longitudinal direction of the outer peripheral surface. It is characterized in that at least two or more parts are formed.

（２）上記（１）記載の洗車機用洗浄ブラシのブラシ片において、前記不織布にたいして撥水剤がコーティングされてあるものである。 ( 2 ) In the brush piece of the washing brush for a car wash machine described in the above (1), a water repellent is coated on the nonwoven fabric.

（３）上記（１）又は（２）に記載の前記洗車機用洗浄ブラシのブラシ片が使用されてある洗車機用洗浄ブラシである。 ( 3 ) A washing brush for a car wash machine in which the brush piece of the washing brush for a car wash machine described in (1) or (2 ) above is used.

（４）駆動源と、被洗浄面に散布する洗浄剤、及び水を噴出させるノズルと、洗浄後の被洗浄面を乾燥させる乾燥手段を備えると共に、上記（３）に記載の前記洗車機用洗浄ブラシが搭載されてある洗車機である。 ( 4 ) A driving source, a cleaning agent sprayed on the surface to be cleaned, a nozzle for ejecting water, and a drying means for drying the surface to be cleaned after cleaning, and for the car wash machine according to ( 3 ) above It is a car wash machine equipped with a cleaning brush.

本発明の洗車機用洗浄ブラシのブラシ片は、次に示すような効果を得ることができる。なお、説明にあたっては、請求項の番号と同じ番号を付して説明する。 The brush piece of the washing brush for a car wash machine of the present invention can obtain the following effects. In the description, the same reference numerals as those in the claims are attached.

（１）ブラシ片は、複数のフィラメントからなる不織布にて形成されてあり、該不織布にたいして高分子弾性体が、コーティング、バインダー固着、あるいは練り込まれてあるものであって、前記フィラメントの少なくとも一部にはスリットが形成されてあり、且つ外周面の長手方向に沿って、スリットにより発生した角部が少なくとも二箇所以上形成されてある。その為、ブラシ片は、フィラメントの有する角部による汚れの掻き出し、及びブラッシング効果に優れており、高い洗浄性を発現させることができる。また、スリットに水等が溜まりやすく、洗車時における保水性に優れていると共に、洗車後は、ブラシの空運転によるブラシ片からの水引きが速く、速乾性を有していることから、高い凍結防止性を有することができる。 (1) The brush piece is formed of a nonwoven fabric composed of a plurality of filaments, and a polymer elastic body is coated, bonded to a binder, or kneaded to the nonwoven fabric , and at least one of the filaments. A slit is formed in the portion, and at least two corner portions generated by the slit are formed along the longitudinal direction of the outer peripheral surface. Therefore, the brush piece is excellent in the scraping of dirt by the corners of the filament and the brushing effect, and can exhibit high detergency. In addition, water is likely to accumulate in the slits and has excellent water retention at the time of washing the car. It can have anti-freezing properties.

（１）また、不織布にたいして、高分子弾性体が、コーティング、バインダー固着、あるいは練り込まれてある為、ブラシ片は、不織布が有する高い洗浄性を保持しつつ、高分子弾性体が弾性を有していることから、被労屈折等による座屈、あるいは破れ、ほつれ等が無く、高い耐久性を有することができる。また、高分子弾性体は、柔軟性を有している為、洗車中に被洗浄体である自動車、あるいは車両の車体に傷を付けることが無い。また、高分子弾性体がフィラメントにたいして部分的に付着されてある場合においては、高分子弾性体が付着している部分、及び付着していない部分とで異なる強度により、車体にブラシ片を接触させることができる。 ( 1 ) Also, since the polymer elastic body is coated, bonded to a binder, or kneaded with the nonwoven fabric, the brush piece retains the high detergency of the nonwoven fabric while the polymer elastic body has elasticity. Therefore, there is no buckling due to labor refraction or the like, and there is no breakage, fraying, etc., and high durability can be achieved. In addition, since the polymer elastic body has flexibility, it does not damage the automobile to be cleaned or the vehicle body during the car wash. Further, when the polymer elastic body is partially attached to the filament, the brush piece is brought into contact with the vehicle body with different strengths between the portion where the polymer elastic body is attached and the portion where the polymer elastic body is not attached. be able to.

（２）前記不織布にたいして、撥水剤がコーティングされてある。その為、ブラシ片は、撥水剤がコーティングされてあることから、洗車中に水等を極めて含み難く、水等で重くなることが無く、ブラシの洗車時における回転バランスが崩れることが無く、被洗浄体である自動車、あるいは車両の装備品を破損させることが無い。 ( 2 ) The nonwoven fabric is coated with a water repellent. Therefore, the brush piece is coated with a water repellent, so it is very difficult to contain water etc. during the car wash, it does not become heavy with water etc., and the rotation balance at the time of car wash of the brush is not lost, The car to be cleaned or the equipment of the vehicle will not be damaged.

（３）洗車機用洗浄ブラシは、上記（１）又は（２）に記載の前記洗車機用洗浄ブラシのブラシ片が使用されてある。その為、洗車機用洗浄ブラシは、前記洗車機用洗浄ブラシのブラシ片が有する高い洗浄性を保持しつつ、チャンネルブラシの間隔、及びチャンネルブラシの傾き角度等を調整することにより、被洗浄面に均一にブラシ片を当てることができ、被洗浄面の洗い残しを無くすことができる。 (3) car wash machine wash brush, the (1) or brush strip of the car wash cleaning brush according to (2) are used. Therefore, the washing brush for a car wash machine maintains the high detergency of the brush piece of the washing brush for the car wash machine, while adjusting the interval between the channel brushes, the inclination angle of the channel brush, etc. It is possible to apply the brush piece uniformly to the surface to be cleaned, and it is possible to eliminate the unwashed surface of the surface to be cleaned.

前記洗車機用洗浄ブラシのブラシ片の使用枚数、及び台座上の溝部の間隔等を調整することにより、ブラシ片を被洗浄面に連続的に当てることができ、洗車時における被洗浄面にたいするブラシ片の接触音を低減させることができる。 The brush piece can be continuously applied to the surface to be cleaned by adjusting the number of brush pieces used in the washing brush for the car wash machine and the interval between the grooves on the pedestal, and the brush for the surface to be cleaned at the time of car washing. The contact sound of the piece can be reduced.

（４）駆動源と、被洗浄面に散布する洗浄剤、及び水を噴出させるノズルと、洗浄後の被洗浄面を乾燥させる乾燥手段を備えると共に、上記（３）に記載の前記洗車機用洗浄ブラシが搭載されてある。その為、前記洗車機用洗浄ブラシに使用されてある洗車機用洗浄ブラシのブラシ片は、上記の如く、高い凍結防止性を有していることから、前記洗車機用洗浄ブラシの重量は水分等で重くなることが無く、駆動源にたいする負荷が軽減されると共に、洗車機用洗浄ブラシにたいするメンテナンスの軽減を図ることができる。 ( 4 ) A driving source, a cleaning agent sprayed on the surface to be cleaned, a nozzle for ejecting water, and a drying means for drying the surface to be cleaned after cleaning, and for the car wash machine according to ( 3 ) above A cleaning brush is installed. Therefore, since the brush piece of the washing brush for car washing machine used in the washing brush for car washing machine has high anti-freezing property as described above, the weight of the washing brush for car washing machine is moisture. Therefore, the load on the driving source is reduced, and the maintenance on the washing brush for the car wash machine can be reduced.

高い洗浄性を有すると共に、被洗浄面に傷を付けることが無く、自動車、及び車両の装備品の破損が無く、且つ高い耐久性を有する洗車機用洗浄ブラシのブラシ片を提供するという目的を、前記洗浄ブラシのブラシ片は、複数のフィラメントからなる不織布にて形成されてあり、前記フィラメントの一部は、外周面の長手方向に沿って、スリットにより発生した角部が少なくとも二箇所以上形成されてあるという構成において実現した。 An object of the present invention is to provide a brush piece for a washing brush for a car wash machine that has high cleaning properties, does not damage the surface to be cleaned, does not damage automobiles and vehicle equipment, and has high durability. The brush piece of the cleaning brush is formed of a nonwoven fabric composed of a plurality of filaments, and a part of the filament is formed along at least two corners generated by the slit along the longitudinal direction of the outer peripheral surface. Realized in a configuration that has been.

図１から図２にて実施例１を示す。図１は、本発明の洗車機用洗浄ブラシのブラシ片を前面側から見た斜視図である。図１において、１はブラシ片、２は不織布、３はフィラメントである。図２は、図１の部分拡大図である。図２において、４はスリット、５は角部である。 Example 1 is shown in FIGS. FIG. 1 is a perspective view of a brush piece of a washing brush for a car wash machine according to the present invention as seen from the front side. In FIG. 1, 1 is a brush piece, 2 is a nonwoven fabric, and 3 is a filament. FIG. 2 is a partially enlarged view of FIG. In FIG. 2, 4 is a slit and 5 is a corner.

洗車機用洗浄ブラシのブラシ片１は、図１の如く、平板状に形成されてあると共に、複数のフィラメント３からなる不織布２にて形成されてある。また、図２（Ａ）から（Ｃ）の如く、不織布２を構成するフィラメント３の一部は、外周面の長手方向に沿って、スリット４により発生した角部５が少なくとも二箇所以上形成されてある。図２（Ａ）は、フィラメント３の一部分がスリット４により裂けた形状であり、図２（Ａ１）の如く、スリット４、及び二箇所の角部５を有する断面形状をなす。また、図２（Ｂ）は、フィラメント３の先端部から中途部までがスリット４により裂けた形状であり、図２（Ｂ１）の如く、スリット４、及び二箇所の角部５を有する断面形状をなす。また、図２（Ｃ）は、フィラメント３の先端部から末端部までがスリット４により裂けた形状であり、図２（Ｃ１）の如く、複数のスリット４、及び二箇所以上の角部５を有する断面形状をなす。なお、フィラメント３の断面形状は、上記の如くの形状に限定されるものでは無く、フィラメント３の外周面の長手方向に沿って、スリット４により発生した角部５が少なくとも二箇所以上形成されてあれば良い。フィラメント３は、例えば、ポリエチレンテレフタレート、ポリブチレンテレフタレート等のポリエステル、ポリアミド６、ポリアミド６６等のナイロン、ポリエチレン、ポリプロピレン等のポリオレフィンなどの材質が、少なくとも１種類以上使用されてある。 As shown in FIG. 1, a brush piece 1 of a washing brush for a car wash machine is formed in a flat plate shape and is formed of a nonwoven fabric 2 composed of a plurality of filaments 3. Further, as shown in FIGS. 2A to 2C, at least two corner portions 5 generated by the slits 4 are formed in a part of the filament 3 constituting the nonwoven fabric 2 along the longitudinal direction of the outer peripheral surface. It is. FIG. 2A shows a shape in which a part of the filament 3 is torn by the slit 4 and has a cross-sectional shape having the slit 4 and the two corners 5 as shown in FIG. 2A1. FIG. 2B shows a shape in which the tip 3 to the middle of the filament 3 is torn by the slit 4, and a cross-sectional shape having the slit 4 and the two corners 5 as shown in FIG. 2B1. Make. Further, FIG. 2C shows a shape in which the end portion to the end portion of the filament 3 are torn by the slit 4, and as shown in FIG. 2C1, a plurality of slits 4 and two or more corner portions 5 are formed. It has a cross-sectional shape. The cross-sectional shape of the filament 3 is not limited to the shape as described above, and at least two corners 5 generated by the slit 4 are formed along the longitudinal direction of the outer peripheral surface of the filament 3. I just need it. The filament 3 is made of, for example, at least one material such as polyester such as polyethylene terephthalate and polybutylene terephthalate, nylon such as polyamide 6 and polyamide 66, and polyolefin such as polyethylene and polypropylene.

次に、ブラシ片１の製造手順について説明する。最初に、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリアミド６、ポリアミド６６、ポリエチレン、ポリプロピレン等の熱可塑性樹脂を溶融紡糸して、フィラメント３を得る。得られたフィラメント３に、特殊な針を突き刺して、前記フィラメント３を立体的に絡合する。前記の如く、立体的に絡合させる製造方法は、一般的には、ニードルパンチングと呼ばれており、立体的に絡合されたフィラメント３はウエブと呼ばれている。次いで、前記ウエブにたいして、１００ｋｇ〜１５０ｋｇ程度の高圧水流を当てて、フィラメント３を結合させると共に、前記フィラメント３は、高圧水流が当たることにより、外周面の長手方向に沿って、スリット４が発生すると共に、細分割されて極細繊維を形成する。前記の如く、高圧水流を当てて、フィラメント３を結合させ、不織布２を得る製造方法は、一般的には、水流絡合方式と呼ばれている。また、極細繊維とは、繊度が１デシテックス未満の繊維のことであり、１デシテックスとは、糸長１００００ｍ当たり１ｇの重量の繊維のことをいう。 Next, the manufacturing procedure of the brush piece 1 will be described. First, a filament 3 is obtained by melt spinning a thermoplastic resin such as polyethylene terephthalate, polybutylene terephthalate, polyamide 6, polyamide 66, polyethylene, and polypropylene. A special needle is inserted into the obtained filament 3 to entangle the filament 3 three-dimensionally. As described above, the manufacturing method for three-dimensionally intertwining is generally called needle punching, and the three-dimensionally intertwined filament 3 is called a web. Next, a high-pressure water flow of about 100 kg to 150 kg is applied to the web to bind the filaments 3, and the filaments 3 generate slits along the longitudinal direction of the outer peripheral surface when hit with the high-pressure water flow. At the same time, it is subdivided to form ultrafine fibers. As described above, the production method for obtaining the nonwoven fabric 2 by applying the high-pressure water flow to bond the filaments 3 is generally called a water-entanglement method. The ultrafine fiber is a fiber having a fineness of less than 1 dtex, and 1 dtex means a fiber having a weight of 1 g per 10,000 m of yarn length.

次に、本発明の洗車機用洗浄ブラシのブラシ片１の洗浄性について試験した。表１に試験に用いた試験片の組成を示す。下記に示した要領で測定し、その結果を表２に示した。なお、比較例として、フィラメントを熱ロールで加圧し、フィラメント間を結合させるスパンボンド方式により製造された不織布を用いた。 Next, the washability of the brush piece 1 of the washing brush for a car wash machine of the present invention was tested. Table 1 shows the composition of the test piece used in the test. The measurement was performed as shown below, and the results are shown in Table 2. In addition, as a comparative example, a nonwoven fabric manufactured by a spunbond method in which filaments were pressed with a hot roll and bonded between filaments was used.

断面が長方形である幅５０ｍｍ×厚み０．５ｍｍ×長さ２２６ｍｍの帯状試験片を四本切り出した。 Four strip-shaped test pieces having a rectangular cross section of 50 mm in width, 0.5 mm in thickness, and 226 mm in length were cut out.

そして、直径が１１４ｍｍで且つ長さが３６０ｍｍの円柱状回転体の外周面における長さ方向の中央部に、各試験片をその長さ方向の中央部分から二つ折りした上で、幅方向が回転体の長さ方向に合致し且つ試験片の屈曲部外面が回転体の外周面に当接した状態にして、回転体の周方向に等間隔毎に取り付けた。 Then, each test piece is folded in half from the central portion in the length direction on the outer peripheral surface of a cylindrical rotating body having a diameter of 114 mm and a length of 360 mm, and the width direction rotates. The test piece was attached at regular intervals in the circumferential direction of the rotating body so that the outer surface of the bent portion of the test piece was in contact with the outer circumferential surface of the rotating body.

次に、上記回転体を２４０ｒｐｍの一定の回転速度で回転させる一方、一面に人工汚れを塗布した白色ソリッド塗装鋼板を用意し、上記回転速度で回転している回転体の外周面に取り付けた各試験片の先端が描く仮想円上から３０ｍｍだけ回転体の回転軸方向に近接した位置に上記白色ソリッド塗装鋼板を、その汚れ面が回転体に対向した状態に配設して１０分間に亘って鋼板の汚れ面に試験片を順次、摺接させることによって鋼板の汚れを除去した。 Next, while rotating the rotating body at a constant rotational speed of 240 rpm, a white solid coated steel sheet coated with artificial dirt on one surface was prepared, and each attached to the outer peripheral surface of the rotating body rotating at the rotational speed The white solid-coated steel plate is disposed at a position close to the rotation axis direction of the rotating body by 30 mm from the virtual circle drawn by the tip of the test piece, and the dirt surface thereof faces the rotating body for 10 minutes. The stain on the steel plate was removed by sequentially sliding the test piece on the stain surface of the steel plate.

そして、鋼板の汚れ面における試験片によって汚れを除去した部分の明度を色差計で測定して、下記基準により判断した。
○・・・＋３以上
△・・・＋２
×・・・＋１以下And the brightness of the part which removed the stain | pollution | contamination with the test piece in the stain | pollution | contamination surface of a steel plate was measured with the color difference meter, and it judged by the following reference | standard.
○ ・・・ +3 or more △ ・・・ +2
× ・・・ +1 or less

上記の如くの試験の結果、洗浄性においては、実施例１は＋３以上であった。 As a result of the test as described above, Example 1 was +3 or more in terms of detergency.

実施例１のブラシ片１は、上記の如くの構成となっているので、前記洗浄ブラシのブラシ片１は、複数のフィラメント３からなる不織布２にて形成されてあり、前記フィラメント３の一部は、外周面の長手方向に沿って、スリット４により発生した角部５が少なくとも二箇所以上形成されてある。その為、ブラシ片１は、フィラメント３の有する角部５による汚れの掻き出し、及びブラッシング効果に優れており、高い洗浄性を発現させることができる。また、スリット４に水等が溜まりやすく、洗車時における保水性に優れていると共に、洗車後は、ブラシの空運転によるブラシ片１からの水引きが速く、速乾性を有していることから、高い凍結防止性を有することができる。 Since the brush piece 1 of Example 1 is configured as described above, the brush piece 1 of the cleaning brush is formed of a nonwoven fabric 2 composed of a plurality of filaments 3 and a part of the filament 3. Is formed with at least two corners 5 generated by the slits 4 along the longitudinal direction of the outer peripheral surface. Therefore, the brush piece 1 is excellent in the scraping of dirt by the corner portion 5 of the filament 3 and the brushing effect, and can exhibit high detergency. In addition, water or the like easily accumulates in the slit 4 and is excellent in water retention at the time of car washing, and after car washing, water is quickly drawn from the brush piece 1 due to the idle operation of the brush, and has quick drying properties. High anti-freezing property can be obtained.

図３にて実施例２を示す。図３は、本発明の洗車機用洗浄ブラシのブラシ片を前面側から見た斜視図、及ひ部分拡大図である。図３において、１１はブラシ片、１２は不織布、１３はフィラメント、１６は高分子弾性体である。 Example 2 is shown in FIG. FIG. 3 is a perspective view and a partially enlarged view of the brush piece of the washing brush for a car wash machine according to the present invention as seen from the front side. In FIG. 3, 11 is a brush piece, 12 is a non-woven fabric, 13 is a filament, and 16 is a polymer elastic body.

洗車機用洗浄ブラシのブラシ片１１は、図３の如く、平板状に形成されてあると共に、複数のフィラメント１３からなる不織布１２にて形成されてある。また、前記不織布１２にたいして、高分子弾性体１６が付着して形成されてある。図３（Ａ２）から（Ｃ２）は、フィラメント１３にたいして高分子弾性体１６が付着されてある断面図である。前記高分子弾性体１６は、不織布１２を構成するフィラメント１３にたいして、図３（Ａ２）から（Ｃ２）の如く、全面的に付着していても良いし、部分的に付着していても良い。前記高分子弾性体１６は、例えば、ウレタンゴム、アクリルゴム、スチレンゴム、ニトリルゴム、シリコーンゴム、フッ素ゴム等の材質が、少なくとも１種類以上使用されてある。 As shown in FIG. 3, the brush piece 11 of the washing brush for a car wash machine is formed in a flat plate shape and is formed of a nonwoven fabric 12 including a plurality of filaments 13. A polymer elastic body 16 is attached to the nonwoven fabric 12. 3A2 to 3C2 are cross-sectional views in which the polymer elastic body 16 is attached to the filament 13. As shown in FIGS. 3A2 to 3C2, the polymer elastic body 16 may be adhered to the filament 13 constituting the nonwoven fabric 12 or may be partially adhered. The polymer elastic body 16 is made of, for example, at least one material such as urethane rubber, acrylic rubber, styrene rubber, nitrile rubber, silicone rubber, and fluorine rubber.

次に、ブラシ片１１の製造手順について説明する。最初に、上記水流絡合方式により、不織布１２を得る。次いで、前記不織布１２にたいして、高分子弾性体１６を、コーティング、バインダー固着、あるいは練り込み等の方法により付着させる。 Next, the manufacturing procedure of the brush piece 11 will be described. First, the nonwoven fabric 12 is obtained by the above-described hydroentanglement method. Next, the polymer elastic body 16 is attached to the nonwoven fabric 12 by a method such as coating, binder fixing, or kneading.

次に、本発明の洗車機用洗浄ブラシのブラシ片１１の耐摩耗性について試験した。表３に、試験に用いた試験片の組成を示す。下記に示した要領で測定し、その結果を表４に示した。なお、比較例として、上記スパンボンド方式により製造された不織布を用いた。 Next, the wear resistance of the brush piece 11 of the washing brush for a car wash machine of the present invention was tested. Table 3 shows the composition of the test piece used in the test. The measurement was performed in the manner shown below, and the results are shown in Table 4. In addition, the nonwoven fabric manufactured by the said spun bond system was used as a comparative example.

断面が長方形である幅５０ｍｍ×厚み０．５ｍｍ×長さ２２６ｍｍの帯状試験片を四本切り出し、各試験片の重量を測定してこれら試験片の平均重量をＷ_１とした。Four strip-shaped test pieces having a rectangular cross section of width 50 mm × thickness 0.5 mm × length 226 mm were cut out, the weight of each test piece was measured, and the average weight of these test pieces was defined as W ₁ .

次に、上記回転体を２４０ｒｐｍの一定の回転速度で回転させる一方、表面粗さ１００の金属板を用意し、上記回転速度で回転している回転体の外周面に取り付けた各試験片の先端が描く仮想円上から３０ｍｍだけ回転体の回転軸方向に近接した位置に上記金属板を、その表面粗さ１００とされた面を対向した状態に配設して２４時間に亘って金属板の表面に試験片を順次、摺接させた。 Next, while rotating the rotating body at a constant rotational speed of 240 rpm, a metal plate having a surface roughness of 100 is prepared, and the tip of each test piece attached to the outer peripheral surface of the rotating body rotating at the rotational speed. The metal plate is disposed at a position close to the rotation axis direction of the rotating body by 30 mm from the virtual circle drawn by the surface of the metal plate with the surface having a surface roughness of 100 facing each other for 24 hours. Test pieces were sequentially brought into sliding contact with the surface.

そして、金属板の表面に上述のようにして擦り付けた後の各試験片の重量を測定して、これら試験片の平均重量をＷ_２とし、下記式によって試験前後のブラシ片の重量変化を算出し、下記基準により耐摩耗性を判断した。
重量変化率（％）＝１００×（Ｗ_１−Ｗ_２）／Ｗ_１ Then, by measuring the weight of each test piece after rubbed as described above to the surface of the metal plate, the average weight of these specimens and W _2, calculating the weight change of the brush pieces before and after the test according to the following formula The wear resistance was judged according to the following criteria.
Weight change rate (%) = 100 × (W ₁ −W ₂ ) / W ₁

○・・・重量変化率が０．５％未満であった。
△・・・重量変化率が０．５〜１．０％であった。
×・・・重量変化率が１．０％を超えていた。○ The weight change rate was less than 0.5%.
Δ: The weight change rate was 0.5 to 1.0%.
X: The weight change rate exceeded 1.0%.

上記の如くの試験の結果、耐摩耗性においては、実施例２は、重量変化率が０．５％未満であった。 As a result of the test as described above, in terms of wear resistance, the weight change rate of Example 2 was less than 0.5%.

実施例２のブラシ片１１は、上記の如くの構成となっているので、前記不織布１２にたいして、高分子弾性体１６が、コーティング、バインダー固着、あるいは練り込まれてある。その為、ブラシ片１１は、不織布１２が有する高い洗浄性を保持しつつ、高分子弾性体１６が弾性を有していることから、被労屈折等による座屈、あるいは破れ、ほつれ等が無く、高い耐久性を有することができる。また、高分子弾性体１６は、柔軟性を有している為、洗車中に被洗浄体である自動車、あるいは車両の車体に傷を付けることが無い。また、高分子弾性体１６がフィラメント１３にたいして部分的に付着されてある場合においては、高分子弾性体１６が付着している部分、及び付着していない部分とで異なる強度により、車体にブラシ片１１を接触させることができる。 Since the brush piece 11 of Example 2 is configured as described above, the polymer elastic body 16 is coated, bonded to a binder, or kneaded to the nonwoven fabric 12. Therefore, the brush piece 11 does not have buckling due to work refraction or the like, or breakage, fraying, etc., since the polymer elastic body 16 has elasticity while maintaining the high detergency that the nonwoven fabric 12 has. , Can have high durability. In addition, since the polymer elastic body 16 has flexibility, it does not damage the automobile to be cleaned or the vehicle body during the car wash. When the polymer elastic body 16 is partially attached to the filament 13, the brush piece is attached to the vehicle body due to different strengths between the part to which the polymer elastic body 16 is attached and the part to which the polymer elastic body 16 is not attached. 11 can be brought into contact.

図４にて実施例３を示す。図４は、本発明の洗車機用洗浄ブラシのブラシ片を前面側から見た斜視図、及び部分拡大図である。図４において、２１はブラシ片、２２は不織布、２３はフィラメント、２６は撥水剤である。 Example 3 is shown in FIG. FIG. 4 is a perspective view and a partially enlarged view of a brush piece of a washing brush for a car wash machine according to the present invention as seen from the front side. In FIG. 4, 21 is a brush piece, 22 is a non-woven fabric, 23 is a filament, and 26 is a water repellent.

洗車機用洗浄ブラシのブラシ片２１は、図４の如く、平板状に形成されてあると共に、不織布２２にて形成されてある。また、前記不織布２２にたいして、撥水剤２６がコーティングして付着されてある。図４（Ａ３）から（Ｃ３）は、フィラメント２３にたいして撥水剤２６が付着されてある断面図である。また、図４（Ａ３）から（Ｃ３）の如く、前記撥水剤２６は、不織布２２を構成するフィラメント２３にたいして、全面的に付着している。前記撥水剤２６は、例えば、シリコーン、フッ素、メラミン等の撥水性能を有する材質が少なくとも１種類以上使用されてあり、含浸、浸漬、スプレー等の方法により、前記不織布２２にたいして、コーティングされてある。 As shown in FIG. 4, the brush piece 21 of the washing brush for a car wash machine is formed in a flat plate shape and is formed of a nonwoven fabric 22. Further, a water repellent 26 is coated and attached to the nonwoven fabric 22. 4A3 to 4C3 are cross-sectional views in which the water repellent 26 is attached to the filament 23. FIG. Further, as shown in FIGS. 4A3 to 4C3, the water repellent 26 is attached to the entire surface of the filament 23 constituting the nonwoven fabric 22. The water repellent 26 is made of, for example, at least one material having water repellency such as silicone, fluorine, melamine, etc., and is coated on the non-woven fabric 22 by a method such as impregnation, dipping or spraying. is there.

実施例３のブラシ片２１は、上記の如くの構成となっているので、前記不織布２２にたいして、撥水剤２６がコーティングされてある。その為、ブラシ片２１は、撥水剤２６がコーティングされてあることから、洗車中に水等を極めて含み難く、水等で重くなることが無く、ブラシの洗車時における回転バランスが崩れることが無く、被洗浄体である自動車、あるいは車両の装備品を破損させることが無い。 Since the brush piece 21 of Example 3 is configured as described above, the nonwoven fabric 22 is coated with a water repellent 26. Therefore, since the brush piece 21 is coated with the water repellent 26, it is very difficult to contain water or the like during the car wash, and does not become heavy due to water or the like, and the rotation balance of the brush during the car wash may be lost. In addition, there is no possibility of damaging the automobile or vehicle equipment that is the object to be cleaned.

図５にて実施例４を示す。図５は、本発明の洗車機用洗浄ブラシのブラシ片が使用されてある洗車機用洗浄ブラシを前面側から見た斜視図である。図５において、３１は洗車機用洗浄ブラシ、３２は台座、３３はチャンネルブラシ、３４は止め金具である。 Example 4 is shown in FIG. FIG. 5: is the perspective view which looked at the washing brush for car wash machines in which the brush piece of the washing brush for car wash machines of this invention is used from the front side. In FIG. 5, 31 is a washing brush for a car wash machine, 32 is a base, 33 is a channel brush, and 34 is a stopper.

洗車機用洗浄ブラシ３１は、図５の如く、ブラシ片１、台座３２、チャンネルブラシ３３、及び止め金具３４より構成されてある。台座３２は、略円筒形状からなり、外周の両端部には、止め金具３４が組み付けられて形成されてある。チャンネルブラシ３３は、ブラシ片１を芯線、及び概Ｕ字断面を有する帯状体にて挟み付けて折り込んだ後、台座３２の外周の周りに捩りを加えて螺旋状に形成されてあり、止め金具３４にて固定されてある。 As shown in FIG. 5, the car brush washing brush 31 includes a brush piece 1, a pedestal 32, a channel brush 33, and a stopper 34. The pedestal 32 has a substantially cylindrical shape, and is formed by assembling stoppers 34 at both ends of the outer periphery. The channel brush 33 is formed in a spiral shape by twisting the outer periphery of the pedestal 32 after the brush piece 1 is sandwiched and folded between the core wire and a belt-like body having a substantially U-shaped cross section. It is fixed at 34.

実施例４の洗車機用洗浄ブラシ３１は、上記の如くの構成となっているので、実施例１から３のいずれか１項に記載の前記洗車機用洗浄ブラシのブラシ片１が使用されてある。その為、洗車機用洗浄ブラシ３１は、前記洗車機用洗浄ブラシのブラシ片１が有する高い洗浄性を保持しつつ、チャンネルブラシ３３の間隔、及びチャンネルブラシ３３の傾き角度等を調整することにより、被洗浄面に均一にブラシ片１を当てることができ、被洗浄面の洗い残しを無くすことができる。 Since the car wash machine cleaning brush 31 according to the fourth embodiment is configured as described above, the brush piece 1 of the car wash machine cleaning brush according to any one of the first to third embodiments is used. is there. Therefore, the washing brush 31 for the car wash machine adjusts the interval between the channel brushes 33 and the inclination angle of the channel brush 33 while maintaining the high detergency of the brush piece 1 of the washing brush for car wash machine. Further, the brush piece 1 can be uniformly applied to the surface to be cleaned, and the uncleaned surface of the surface to be cleaned can be eliminated.

次に、図６にて、本発明の実施例４の洗車機用洗浄ブラシの他の実施の形態を示す。図６は、本発明の洗車機用洗浄ブラシのブラシ片が使用されてある他の形態の洗車機用洗浄ブラシを前面側から見た斜視図である。図６において、４１は洗車機用洗浄ブラシ、４２は台座、４４は止め金具、４５は溝部である。 Next, FIG. 6 shows another embodiment of the washing brush for a car wash machine according to the fourth embodiment of the present invention. FIG. 6 is a perspective view of another embodiment of the washing brush for a car wash machine in which the brush piece of the washing brush for a car wash machine of the present invention is used as seen from the front side. In FIG. 6, 41 is a washing brush for a car wash machine, 42 is a base, 44 is a stopper, and 45 is a groove.

洗車機用洗浄ブラシ４１は、図６の如く、ブラシ片１、台座４２、止め金具４４、溝部４５より構成されてある。台座４２は、略円筒形状からなり、外周の両端部には、止め金具４４が組み付けられてあると共に、溝部４５が形成されてある。ブラシ片１は、概Ｕ字断面を有する帯状体にて溝部４５に勘合挿入されてあり、止め金具４４にて固定されてある。 As shown in FIG. 6, the washing brush 41 for a car wash machine includes a brush piece 1, a pedestal 42, a fastener 44, and a groove 45. The pedestal 42 is formed in a substantially cylindrical shape, and stoppers 44 are assembled to both ends of the outer periphery, and a groove 45 is formed. The brush piece 1 is fitted and inserted into the groove 45 with a belt-like body having a substantially U-shaped cross section, and is fixed by a stopper 44.

実施例４の他の実施の形態の洗車機用洗浄ブラシ４１は、上記の如くの構成となっているので、前記洗車機用洗浄ブラシのブラシ片１の使用枚数、及び台座４２上の溝部４５の間隔等を調整することにより、ブラシ片１を被洗浄面に連続的に当てることができ、洗車時における被洗浄面にたいするブラシ片１の接触音を低減させることができる。 Since the washing brush 41 for a car wash machine according to another embodiment of Example 4 is configured as described above, the number of brush pieces 1 used for the washing brush for the car wash machine and the groove 45 on the pedestal 42 are as follows. By adjusting the interval, etc., the brush piece 1 can be continuously applied to the surface to be cleaned, and the contact noise of the brush piece 1 against the surface to be cleaned during car washing can be reduced.

なお、ブラシ構造に関しては、特に限定されるものでは無く、上記の如くの構造以外にも、使用目的に応じて、適時、設定することができる。 The brush structure is not particularly limited, and can be set in a timely manner according to the purpose of use other than the structure as described above.

図７にて実施例５を示す。図７は、本発明の洗車機用洗浄ブラシのブラシ片が使用されてある洗車機用洗浄ブラシが搭載されてある洗車機の正面図である。図７において、５０は洗車機、５１は洗車機用洗浄ブラシ、５２は駆動源、５３はノズル、５４は乾燥機である。 Example 5 is shown in FIG. FIG. 7 is a front view of a car wash machine equipped with a car brush washing brush in which a brush piece of the car wash machine brush of the present invention is used. In FIG. 7, 50 is a car wash machine, 51 is a car brush washing brush, 52 is a driving source, 53 is a nozzle, and 54 is a dryer.

洗車機５０は、洗車機用洗浄ブラシ５１が搭載されてあり、前記洗車機用洗浄ブラシ５１は駆動源５２により回転される。ノズル５３からは、被洗浄面にたいして、洗浄剤、及び水が散布され、前記洗車機用洗浄ブラシ５１により洗浄され、洗浄後は、乾燥機５４等の乾燥手段により被洗浄面が乾燥される。 The car wash machine 50 is equipped with a car wash machine cleaning brush 51, and the car wash machine cleaning brush 51 is rotated by a drive source 52. From the nozzle 53, a cleaning agent and water are sprayed on the surface to be cleaned, and the surface is cleaned by the car brush washing brush 51. After the cleaning, the surface to be cleaned is dried by a drying means such as a dryer 54.

実施例５の洗車機５０は、上記の如くの構成となっているので、駆動源５２と、被洗浄面に散布する洗浄剤、及び水を噴出させるノズル５３と、洗浄後の被洗浄面を乾燥させる乾燥機５４等の乾燥手段を備えると共に、上記実施例４に記載の前記洗車機用洗浄ブラシ５１が搭載されてある。その為、前記洗車機用洗浄ブラシ５１に使用されてある洗車機用洗浄ブラシのブラシ片は、上記の如く、高い凍結防止性を有していることから、前記洗車機用洗浄ブラシ５１の重量は水分等で重くなることが無く、駆動源５２にたいする負荷が軽減されると共に、洗車機用洗浄ブラシ５１にたいするメンテナンスの軽減を図ることができる。 Since the car wash machine 50 according to the fifth embodiment is configured as described above, the drive source 52, the cleaning agent sprayed on the surface to be cleaned, the nozzle 53 for ejecting water, and the surface to be cleaned after cleaning are provided. While equipped with drying means such as a dryer 54 for drying, the washing brush 51 for the car wash machine described in the fourth embodiment is mounted. Therefore, since the brush piece of the washing brush for car washing machine used for the washing brush 51 for car washing machine has high anti-freezing property as described above, the weight of the washing brush 51 for car washing machine is high. Therefore, the load on the driving source 52 is reduced and the maintenance on the washing brush 51 for the car wash machine can be reduced.

本発明の洗車機用洗車ブラシのブラシ片は、主に、自動車あるいは車両の外面の被洗浄面に付着した汚れ等を洗浄する為の洗車機に搭載する洗浄ブラシのブラシ片として使用する。 The brush piece of the car wash brush for the car wash machine of the present invention is mainly used as a brush piece of a wash brush mounted on a car wash machine for cleaning dirt or the like adhering to the surface to be cleaned of an automobile or a vehicle.

本発明の洗車機用洗浄ブラシのブラシ片を前面側から見た斜視図である。 It is the perspective view which looked at the brush piece of the washing brush for car wash machines of the present invention from the front side. 図１の部分拡大図である。 It is the elements on larger scale of FIG. 本発明の洗車機用洗浄ブラシのブラシ片を前面側から見た斜視図、及び部分拡大図である。 It is the perspective view which looked at the brush piece of the washing brush for car wash machines of this invention from the front side, and the elements on larger scale. 本発明の洗車機用洗浄ブラシのブラシ片を前面側から見た斜視図、及び部分拡大図である。 It is the perspective view which looked at the brush piece of the washing brush for car wash machines of this invention from the front side, and the elements on larger scale. 本発明の洗車機用洗浄ブラシのブラシ片が使用されてある洗車機用洗浄ブラシを前面側から見た斜視図である。 It is the perspective view which looked at the washing brush for car wash machines in which the brush piece of the washing brush for car wash machines of the present invention is used from the front side. 本発明の洗車機用洗浄ブラシのブラシ片が使用されてある他の形態の洗車機用洗浄ブラシを前面側から見た斜視図である。 It is the perspective view which looked at the washing brush for car washing machines of other forms in which the brush piece of the washing brush for car washing machines of the present invention is used from the front side. 本発明の洗車機用洗浄ブラシのブラシ片が使用されてある洗車機用洗浄ブラシが搭載されてある洗車機の正面図である。 It is a front view of the car wash machine in which the washing brush for car wash machines in which the brush piece of the washing brush for car wash machines of the present invention is used is carried.

符号の説明Explanation of symbols

１、１１、２１ブラシ片
２、１２、２２不織布
３、１３、２３フィラメント
４スリット
５角部
１６高分子弾性体
２６撥水剤
３１、４１、５１洗車機用洗浄ブラシ
３２、４２台座
３３チャンネルブラシ
３４、４４止め金具
４５溝部
５０洗車機
５２駆動源
５３ノズル
５４乾燥機1, 11, 21 Brush pieces 2, 12, 22 Non-woven fabric 3, 13, 23 Filament 4 Slit 5 Corner 16 Polymer elastic body 26 Water repellent 31, 41, 51 Washing brush 32, 42 for washing machine Base 33 Channel brush 34, 44 Fastener 45 Groove 50 Car wash machine 52 Drive source 53 Nozzle 54 Dryer

Claims

自動車洗浄用あるいは車両洗浄用の洗車機に使用する洗浄ブラシのブラシ片において、前記洗浄ブラシのブラシ片は、複数のフィラメントからなる不織布にて形成されてあり、該不織布にたいして高分子弾性体が、コーティング、バインダー固着、あるいは練り込まれてあるものであって、前記フィラメントの少なくとも一部にはスリットが形成されてあり、且つ外周面の長手方向に沿って、前記スリットにより発生した角部が少なくとも二箇所以上形成されてあることを特徴とする洗車機用洗浄ブラシのブラシ片。 In a brush piece of a cleaning brush used in a car washing machine for washing an automobile or a vehicle, the brush piece of the washing brush is formed of a nonwoven fabric composed of a plurality of filaments, and a polymer elastic body is formed on the nonwoven fabric. Coating, binder fixing, or kneading, wherein a slit is formed in at least a part of the filament, and at least a corner portion generated by the slit along the longitudinal direction of the outer peripheral surface. A brush piece of a washing brush for a car wash machine, wherein two or more places are formed.

請求項１記載の構成よりなる洗車機用洗浄ブラシのブラシ片において、前記不織布にたいして撥水剤がコーティングされてあることを特徴とする洗車機用洗浄ブラシのブラシ片。 The brush piece of the washing brush for car wash machines which consists of a structure of Claim 1 WHEREIN: The water-repellent agent is coated with respect to the said nonwoven fabric, The brush piece of the washing brush for car wash machines characterized by the above-mentioned.

請求項１又は２に記載の前記洗車機用洗浄ブラシのブラシ片が使用されてある洗車機用洗浄ブラシ。 The washing brush for car wash machines in which the brush piece of the washing brush for car wash machines according to claim 1 or 2 is used.

駆動源と、被洗浄面に散布する洗浄剤、及び水を噴出させるノズルと、洗浄後の被洗浄面を乾燥させる乾燥手段を備えると共に、請求項３に記載の前記洗車機用洗浄ブラシが搭載されてある洗車機。 A driving source, a cleaning agent sprayed on the surface to be cleaned, a nozzle for ejecting water, and a drying means for drying the surface to be cleaned after cleaning, and equipped with the cleaning brush for a car wash machine according to claim 3 Car wash machine.