JP4766268B2 - 感放射線性樹脂組成物、層間絶縁膜およびマイクロレンズ、ならびにそれらの製造方法 - Google Patents
感放射線性樹脂組成物、層間絶縁膜およびマイクロレンズ、ならびにそれらの製造方法 Download PDFInfo
- Publication number
- JP4766268B2 JP4766268B2 JP2007051833A JP2007051833A JP4766268B2 JP 4766268 B2 JP4766268 B2 JP 4766268B2 JP 2007051833 A JP2007051833 A JP 2007051833A JP 2007051833 A JP2007051833 A JP 2007051833A JP 4766268 B2 JP4766268 B2 JP 4766268B2
- Authority
- JP
- Japan
- Prior art keywords
- weight
- naphthoquinonediazide
- sulfonic acid
- acid ester
- radiation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
上記電子部品のうち、例えばTFT型液晶表示素子は、上記の層間絶縁膜の上に、透明電極膜を形成し、さらにその上に液晶配向膜を形成する工程を経て製造されるため、層間絶縁膜は、透明電極膜の形成工程において高温条件に曝されたり、電極のパターン形成に使用されるレジストの剥離液に曝されることとなるため、これらに対する十分な耐性が必要となる。
また近年、TFT型液晶表示素子においては、大画面化、高輝度化、高精細化、高速応答化、薄型化等の動向にあり、それに用いられる層間絶縁膜形成用組成物としては高感度であり、形成される層間絶縁膜には低誘電率、高透過率等において、従来にも増して高性能が要求されている。
マイクロレンズまたはマイクロレンズアレイの形成には、レンズに相当するレジストパターンを形成した後、加熱処理することによってメルトフローさせ、そのままレンズとして利用する方法や、メルトフローさせたレンズパターンをマスクにしてドライエッチングにより下地にレンズ形状を転写させる方法等が知られている。前記レンズパターンの形成には、感放射線性樹脂組成物が幅広く使用されている(特許文献3および特許文献4参照)。
このようなマイクロレンズを形成するために用いられる感放射線性樹脂組成物は、高感度であり、また、それから形成されるマイクロレンズが所望の曲率半径を有するものであり、高耐熱性、高透過率であること等が要求される。
また、このようにして得られる層間絶縁膜やマイクロレンズは、これらを形成する際の現像工程において、現像時間が最適時間よりわずかでも過剰となると、パターンと基板との間に現像液が浸透して剥がれが生じやすくなるため、現像時間を厳密に制御する必要があり、製品の歩留まりの点で問題があった。
本発明のさらに他の目的は、本発明の方法により形成された層間絶縁膜およびマイクロレンズを提供することにある。
本発明のさらに他の目的および利点は、以下の説明から明らかになろう。
[A](a1)不飽和カルボン酸および不飽和カルボン酸無水物の群から選ばれる少なくとも1種(以下、「化合物(a1)」ということがある。)、
(a2)エポキシ基含有不飽和化合物(以下、「化合物(a2−1)」ということがある。)およびオキセタニル基含有不飽和化合物(以下、「化合物(a2−2)」ということがある。)の群から選ばれる少なくとも1種、ならびに
(a3)(a1)、(a2)以外の不飽和化合物(以下、「化合物(a3)」ということがある。)の共重合体(以下、「共重合体[A]」ということがある。)、ならびに
[B]1,2−キノンジアジド化合物(以下、「[B]成分」ということがある。)、ならびに
[C]下記式(1)で表されるシロキサンオリゴマー(以下、「[C]成分」ということがある。)
を含有することを特徴とする感放射線性樹脂組成物によって達成される。
以下の工程を以下に記載の順序で含むことを特徴とする層間絶縁膜またはマイクロレンズの形成方法によって達成される。
(1)上記の感放射線性組成物の塗膜を基板上に形成する工程、
(2)該塗膜の少なくとも一部に放射線を照射する工程、
(3)現像工程、および
(4)加熱工程。
上記方法によって形成された層間絶縁膜またはマイクロレンズによって達成される。
上記組成物から形成された本発明の層間絶縁膜は、基板への密着性が良好であり、耐溶剤性および耐熱性に優れ、高い透過率を有し、誘電率が低いものであり、電子部品の層間絶縁膜として好適に使用できる。
また、上位組成物から形成された本発明のマイクロレンズは、基板への密着性が良好であり、耐溶剤性および耐熱性に優れ、かつ高い透過率と良好なメルト形状を有するものであり、固体撮像素子のマイクロレンズとして好適に使用できる。
共重合体[A]
共重合体[A]は、化合物(a1)、化合物(a2−1)、化合物(a2−2)および化合物(a3)を溶媒中、重合開始剤の存在下でラジカル重合することによって製造することができる。
化合物(a1)はラジカル重合性を有する不飽和カルボン酸および不飽和カルボン酸無水物の群から選ばれる少なくとも1種であり、例えばモノカルボン酸、ジカルボン酸、ジカルボン酸の無水物、多価カルボン酸のモノ〔(メタ)アクリロイロキシアルキル〕エステル、両末端にカルボキシル基と水酸基とを有するポリマーのモノ(メタ)アクリレート、カルボキシル基を有する多環式化合物およびその無水物などを挙げることができる。
ジカルボン酸として、例えばマレイン酸、フマル酸、シトラコン酸、メサコン酸、イタコン酸など;
ジカルボン酸の無水物として、例えば上記ジカルボン酸として例示した化合物の無水物など;
多価カルボン酸のモノ〔(メタ)アクリロイロキシアルキル〕エステルとして、例えばコハク酸モノ〔2−(メタ)アクリロイロキシエチル〕、フタル酸モノ〔2−(メタ)アクリロイロキシエチル〕など;
両末端にカルボキシル基と水酸基とを有するポリマーのモノ(メタ)アクリレートとして、例えばω−カルボキシポリカプロラクトンモノ(メタ)アクリレートなど;
カルボキシル基を有する多環式化合物およびその無水物として、例えば5−カルボキシビシクロ[2.2.1]ヘプト−2−エン、5,6−ジカルボキシビシクロ[2.2.1]ヘプト−2−エン、5−カルボキシ−5−メチルビシクロ[2.2.1]ヘプト−2−エン、5−カルボキシ−5−エチルビシクロ[2.2.1]ヘプト−2−エン、5−カルボキシ−6−メチルビシクロ[2.2.1]ヘプト−2−エン、5−カルボキシ−6−エチルビシクロ[2.2.1]ヘプト−2−エン、5,6−ジカルボキシビシクロ[2.2.1]ヘプト−2−エン無水物などがそれぞれ挙げられる。
これらのうち、モノカルボン酸、ジカルボン酸の無水物が好ましく使用され、特にアクリル酸、メタクリル酸、無水マレイン酸が共重合反応性、アルカリ水溶液に対する溶解性および入手が容易である点から好ましく用いられる。これらの化合物(a1)は、単独であるいは組み合わせて用いられる。
3−(アクリロイルオキシメチル)オキセタン、3−(アクリロイルオキシメチル)−3−エチルオキセタン、3−(アクリロイルオキシメチル)−2−メチルオキセタン、3−(アクリロイルオキシメチル)−2−トリフロロメチルオキセタン、3−(アクリロイルオキシメチル)−2−ペンタフロロエチルオキセタン、3−(アクリロイルオキシメチル)−2−フェニルオキセタン、3−(アクリロイルオキシメチル)−2,2−ジフロロオキセタン、3−(アクリロイルオキシメチル)−2,2,4−トリフロロオキセタン、3−(アクリロイルオキシメチル)−2,2,4,4−テトラフロロオキセタン、3−(アクリロイルオキシエチル)オキセタン、3−(アクリロイルオキシエチル)−3−エチルオキセタン、2−エチル−3−(アクリロイルオキシエチル)オキセタン、3−(アクリロイルオキシエチル)−2−トリフロロメチルオキセタン、3−(アクリロイルオキシエチル)−2−ペンタフロロエチルオキセタン、3−(アクリロイルオキシエチル)−2−フェニルオキセタン、2,2−ジフロロ−3−(アクリロイルオキシエチル)オキセタン、3−(アクリロイルオキシエチル)−2,2,4−トリフロロオキセタン、3−(アクリロイルオキシエチル)−2,2,4,4−テトラフロロオキセタン等のアクリル酸エステルが挙げられる。
これらのうち、3−(メタクリロイルオキシメチル)オキセタン、3−(メタクリロイルオキシメチル)−2−トリフロロメチルオキセタン、3−(メタクリロイルオキシメチル)−2−フェニルオキセタン、2−(メタクリロイルオキシメチル)オキセタン、2−(メタクリロイルオキシメチル)−4−トリフロロメチルオキセタン、3−エチル−3−メタクリロイルオキシメチルオキセタンなどが得られる感光性樹脂組成物のプロセスマージンが広く、かつ、得られる層間絶縁膜、マイクロレンズの耐薬品性を高める点から好ましく用いられる。これらは、単独であるいは組み合わせて用いられる。
化合物(a3)はラジカル重合性を有する不飽和化合物であれば特に制限されるものではない。例えば、メタクリル酸アルキルエステル、メタクリル酸環状アルキルエステル、アクリル酸アルキルエステル、アクリル酸環状アルキルエステル、メタクリル酸アリールエステル、アクリル酸アリールエステル、不飽和ジカルボン酸ジエステル、ヒドロキシメタクリル酸エステル、ヒドロキシアクリル酸エステル、ビシクロ不飽和化合物、マレイミド化合物、不飽和芳香族化合物、共役ジエン、テトラヒドロフラン骨格、フラン骨格、テトラヒドロピラン骨格、ピラン骨格をもつ不飽和化合物およびその他の不飽和化合物を挙げることができる。
ビシクロ不飽和化合物として、例えば、ビシクロ[2.2.1]ヘプト−2−エン、5−メチルビシクロ[2.2.1]ヘプト−2−エン、5−エチルビシクロ[2.2.1]ヘプト−2−エン、5−ヒドロキシビシクロ[2.2.1]ヘプト−2−エン、5−カルボキシビシクロ[2.2.1]ヘプト−2−エン、5−ヒドロキシメチルビシクロ[2.2.1]ヘプト−2−エン、5−(2−ヒドロキシエチル)ビシクロ[2.2.1]ヘプト−2−エン、5−メトキシビシクロ[2.2.1]ヘプト−2−エン、5−エトキシビシクロ[2.2.1]ヘプト−2−エン、5,6−ジヒドロキシビシクロ[2.2.1]ヘプト−2−エン、5,6−ジカルボキシビシクロ[2.2.1]ヘプト−2−エン、5,6−ジ(ヒドロキシメチル)ビシクロ[2.2.1]ヘプト−2−エン、5,6−ジ(2−ヒドロキシエチル)ビシクロ[2.2.1]ヘプト−2−エン、5,6−ジメトキシビシクロ[2.2.1]ヘプト−2−エン、5,6−ジエトキシビシクロ[2.2.1]ヘプト−2−エン、5−ヒドロキシ−5−メチルビシクロ[2.2.1]ヘプト−2−エン、5−ヒドロキシ−5−エチルビシクロ[2.2.1]ヘプト−2−エン、5−カルボキシ−5−メチルビシクロ[2.2.1]ヘプト−2−エン、5−カルボキシ−5−エチルビシクロ[2.2.1]ヘプト−2−エン、5−ヒドロキシメチル−5−メチルビシクロ[2.2.1]ヘプト−2−エン、5−カルボキシ−6−メチルビシクロ[2.2.1]ヘプト−2−エン、5−カルボキシ−6−エチルビシクロ[2.2.1]ヘプト−2−エン、5,6−ジカルボキシビシクロ[2.2.1]ヘプト−2−エン無水物(ハイミック酸無水物)、5−t−ブトキシカルボニルビシクロ[2.2.1]ヘプト−2−エン、5−シクロヘキシルオキシカルボニルビシクロ[2.2.1]ヘプト−2−エン、5−フェノキシカルボニルビシクロ[2.2.1]ヘプト−2−エン、5,6−ジ(t−ブトキシカルボニル)ビシクロ[2.2.1]ヘプト−2−エン、5,6−ジ(シクロヘキシルオキシカルボニル)ビシクロ[2.2.1]ヘプト−2−エンなど;
不飽和芳香族化合物として、例えば、スチレン、α−メチルスチレン、m−メチルスチレン、p−メチルスチレン、ビニルトルエン、p−メトキシスチレンなど;共役ジエンとして、例えば、1,3−ブタジエン、イソプレン、2,3−ジメチル−1,3−ブタジエンなど;テトラヒドロフラン骨格を含有する不飽和化合物として、例えば、テトラヒドロフルフリル(メタ)アクリレート、2−メタクリロイルオキシ−プロピオン酸テトラヒドロフルフリルエステル、3−(メタ)アクリロイルオキシテトラヒドロフラン−2−オンなど;フラン骨格を含有する不飽和化合物として、例えば、2−メチル−5−(3−フリル)−1−ペンテン−3−オン、フルフリル(メタ)アクリレート、1−フラン−2−ブチル−3−エン−2−オン、1−フラン−2−ブチル−3−メトキシ−3−エン−2−オン、6−(2−フリル)−2−メチル−1−ヘキセン−3−オン、6−フラン−2−イル−ヘキシ−1−エン−3−オン、アクリル酸2−フラン−2−イル−1−メチル−エチルエステル、6−(2−フリル)−6−メチル−1−ヘプテン−3−オンなど;テトラヒドロピラン骨格を含有する不飽和化合物として、例えば(テトラヒドロピラン−2−イル)メチルメタクリレート、2,6−ジメチル−8−(テトラヒドロピラン−2−イルオキシ)−オクト−1−エン−3−オン、2−メタクリル酸テトラヒドロピラン−2−イルエステル、1−(テトラヒドロピラン−2−オキシ)−ブチル−3−エン−2−オンなど;ピラン骨格を含有する不飽和化合物として、例えば、4−(1,4−ジオキサ−5−オキソ−6−ヘプテニル)−6−メチル−2−ピロン、4−(1,5−ジオキサ−6−オキソ−7−オクテニル)−6−メチル−2−ピロンなど;その他の不飽和化合物として、例えばアクリロニトリル、メタクリロニトリル、塩化ビニル、塩化ビニリデン、アクリルアミド、メタクリルアミド、酢酸ビニルをそれぞれ挙げることができる。
前記重合に用いられる溶媒としては、例えば、アルコール、エーテル、グリコールエーテル、エチレングリコールアルキルエーテルアセテート、ジエチレングリコール、プロピレングリコールモノアルキルエーテル、プロピレングリコールアルキルエーテルアセテート、プロピレングリコールアルキルエーテルプロピオネート、芳香族炭化水素、ケトン、エステルなどを挙げることができる。
プロピレングリコールエーテルとして、プロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル、プロピレングリコールモノ−n−プロピルエーテル、プロピレングリコールモノ−n−ブチルエーテルなど;プロピレングリコールアルキルエーテルアセテートとして、プロピレングリコールメチルエーテルアセテート、プロピレングリコールエチルエーテルアセテート、プロピレングリコールn−プロピルエーテルアセテート、プロピレングリコールn−ブチルエーテルアセテートなど;プロピレングリコールアルキルエーテルプロピオネートとして、プロピレングリコールメチルエーテルプロピオネート、プロピレングリコールエチルエーテルプロピオネート、プロピレングリコールn−プロピルエーテルプロピオネート、プロピレングリコールn−ブチルエーテルプロピオネートなど;芳香族炭化水素として、トルエン、キシレンなど;ケトンとして、メチルエチルケトン、シクロヘキサノン、4−ヒドロキシ−4−メチル−2−ペンタノンなど;
本発明で用いられる[B]成分である1,2−キノンジアジド化合物としては、例えば1,2−ベンゾキノンジアジドスルホン酸エステル、1,2−ナフトキノンジアジドスルホン酸エステル、1,2−ベンゾキノンジアジドスルホン酸アミド、1,2−ナフトキノンジアジドスルホン酸アミド等を挙げることができる。
2,2’,4,4’−テトラヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−4−スルホン酸エステル、2,2’,4,4’−テトラヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−5−スルホン酸エステル、2,2’,4,4’−テトラヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−6−スルホン酸エステル、2,2’,4,4’−テトラヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−7−スルホン酸エステル、2,2’,4,4’−テトラヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−8−スルホン酸エステル、2,3,4,3’−テトラヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−4−スルホン酸エステル、2,3,4,3’−テトラヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−5−スルホン酸エステル、2,3,4,3’−テトラヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−6−スルホン酸エステル、2,3,4,3’−テトラヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−7−スルホン酸エステル、2,3,4,3’−テトラヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−8−スルホン酸エステル、2,3,4,4’−テトラヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−4−スルホン酸エステル、2,3,4,4’−テトラヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−5−スルホン酸エステル、2,3,4,4’−テトラヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−6−スルホン酸エステル、2,3,4,4’−テトラヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−7−スルホン酸エステル、2,3,4,4’−テトラヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−8−スルホン酸エステル、2,3,4,2’−テトラヒドロキシ−4’−メチルベンゾフェノン−1,2−ナフトキノンジアジド−4−スルホン酸エステル、2,3,4,2’−テトラヒドロキシ−4’−メチルベンゾフェノン−1,2−ナフトキノンジアジド−5−スルホン酸エステル、2,3,4,2’−テトラヒドロキシ−4’−メチルベンゾフェノン−1,2−ナフトキノンジアジド−6−スルホン酸エステル、2,3,4,2’−テトラヒドロキシ−4’−メチルベンゾフェノン−1,2−ナフトキノンジアジド−7−スルホン酸エステル、2,3,4,2’−テトラヒドロキシ−4’−メチルベンゾフェノン−1,2−ナフトキノンジアジド−8−スルホン酸エステル、2,3,4,4’−テトラヒドロキシ−3’−メトキシベンゾフェノン−1,2−ナフトキノンジアジド−4−スルホン酸エステル、2,3,4,4’−テトラヒドロキシ−3’−メトキシベンゾフェノン−1,2−ナフトキノンジアジド−5−スルホン酸エステル、2,3,4,4’−テトラヒドロキシ−3’−メトキシベンゾフェノン−1,2−ナフトキノンジアジド−6−スルホン酸エステル、2,3,4,4’−テトラヒドロキシ−3’−メトキシベンゾフェノン−1,2−ナフトキノンジアジド−7−スルホン酸エステル、2,3,4,4’−テトラヒドロキシ−3’−メトキシベンゾフェノン−1,2−ナフトキノンジアジド−8−スルホン酸エステル等のテトラヒドロキシベンゾフェノンの1,2−ナフトキノンジアジドスルホン酸エステル;
2,3,4,2’,6’−ペンタヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−4−スルホン酸エステル、2,3,4,2’,6’−ペンタヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−5−スルホン酸エステル、2,3,4,2’,6’−ペンタヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−6−スルホン酸エステル、2,3,4,2’,6’−ペンタヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−7−スルホン酸エステル、2,3,4,2’,6’−ペンタヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−8−スルホン酸エステル等のペンタヒドロキシベンゾフェノンの1,2−ナフトキノンジアジドスルホン酸エステル;
2,4,6,3’,4’,5’−ヘキサヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−4−スルホン酸エステル、2,4,6,3’,4’,5’−ヘキサヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−5−スルホン酸エステル、2,4,6,3’,4’,5’−ヘキサヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−6−スルホン酸エステル、2,4,6,3’,4’,5’−ヘキサヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−7−スルホン酸エステル、2,4,6,3’,4’,5’−ヘキサヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−8−スルホン酸エステル、3,4,5,3’,4’,5’−ヘキサヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−4−スルホン酸エステル、3,4,5,3’,4’,5’−ヘキサヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−5−スルホン酸エステル、3,4,5,3’,4’,5’−ヘキサヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−6−スルホン酸エステル、3,4,5,3’,4’,5’−ヘキサヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−7−スルホン酸エステル、3,4,5,3’,4’,5’−ヘキサヒドロキシベンゾフェノン−1,2−ナフトキノンジアジド−8−スルホン酸エステル等のヘキサヒドロキシベンゾフェノンの1,2−ナフトキノンジアジドスルホン酸エステル;
1,1,1−トリ(p−ヒドロキシフェニル)エタン−1,2−ナフトキノンジアジド−4−スルホン酸エステル、1,1,1−トリ(p−ヒドロキシフェニル)エタン−1,2−ナフトキノンジアジド−5−スルホン酸エステル、1,1,1−トリ(p−ヒドロキシフェニル)エタン−1,2−ナフトキノンジアジド−6−スルホン酸エステル、1,1,1−トリ(p−ヒドロキシフェニル)エタン−1,2−ナフトキノンジアジド−7−スルホン酸エステル、1,1,1−トリ(p−ヒドロキシフェニル)エタン−1,2−ナフトキノンジアジド−8−スルホン酸エステル、ビス(2,3,4−トリヒドロキシフェニル)メタン−1,2−ナフトキノンジアジド−4−スルホン酸エステル、ビス(2,3,4−トリヒドロキシフェニル)メタン−1,2−ナフトキノンジアジド−5−スルホン酸エステル、ビス(2,3,4−トリヒドロキシフェニル)メタン−1,2−ナフトキノンジアジド−6−スルホン酸エステル、ビス(2,3,4−トリヒドロキシフェニル)メタン−1,2−ナフトキノンジアジド−7−スルホン酸エステル、ビス(2,3,4−トリヒドロキシフェニル)メタン−1,2−ナフトキノンジアジド−8−スルホン酸エステル、2,2−ビス(2,3,4−トリヒドロキシフェニル)プロパン−1,2−ナフトキノンジアジド−4−スルホン酸エステル、2,2−ビス(2,3,4−トリヒドロキシフェニル)プロパン−1,2−ナフトキノンジアジド−5−スルホン酸エステル、2,2−ビス(2,3,4−トリヒドロキシフェニル)プロパン−1,2−ナフトキノンジアジド−6−スルホン酸エステル、2,2−ビス(2,3,4−トリヒドロキシフェニル)プロパン−1,2−ナフトキノンジアジド−7−スルホン酸エステル、2,2−ビス(2,3,4−トリヒドロキシフェニル)プロパン−1,2−ナフトキノンジアジド−8−スルホン酸エステル、
1,1,3−トリス(2,5−ジメチル−4−ヒドロキシフェニル)−3−フェニルプロパン−1,2−ナフトキノンジアジド−4−スルホン酸エステル、1,1,3−トリス(2,5−ジメチル−4−ヒドロキシフェニル)−3−フェニルプロパン−1,2−ナフトキノンジアジド−5−スルホン酸エステル、1,1,3−トリス(2,5−ジメチル−4−ヒドロキシフェニル)−3−フェニルプロパン−1,2−ナフトキノンジアジド−6−スルホン酸エステル、1,1,3−トリス(2,5−ジメチル−4−ヒドロキシフェニル)−3−フェニルプロパン−1,2−ナフトキノンジアジド−7−スルホン酸エステル、1,1,3−トリス(2,5−ジメチル−4−ヒドロキシフェニル)−3−フェニルプロパン−1,2−ナフトキノンジアジド−8−スルホン酸エステル、4,4’−〔1−〔4−〔1−〔4−ヒドロキシフェニル〕−1−メチルエチル〕フェニル〕エチリデン〕ビスフェノール−1,2−ナフトキノンジアジド−4−スルホン酸エステル、4,4’−〔1−〔4−〔1−〔4−ヒドロキシフェニル〕−1−メチルエチル〕フェニル〕エチリデン〕ビスフェノール−1,2−ナフトキノンジアジド−5−スルホン酸エステル、4,4’−〔1−〔4−〔1−〔4−ヒドロキシフェニル〕−1−メチルエチル〕フェニル〕エチリデン〕ビスフェノール−1,2−ナフトキノンジアジド−6−スルホン酸エステル、4,4’−〔1−〔4−〔1−〔4−ヒドロキシフェニル〕−1−メチルエチル〕フェニル〕エチリデン〕ビスフェノール−1,2−ナフトキノンジアジド−7−スルホン酸エステル、4,4’−〔1−〔4−〔1−〔4−ヒドロキシフェニル〕−1−メチルエチル〕フェニル〕エチリデン〕ビスフェノール−1,2−ナフトキノンジアジド−8−スルホン酸エステル、
これらの1,2−キノンジアジド化合物は単独でまたは2種類以上を組み合わせて用いることができる。
本発明で用いられる[C]成分は、オキセタニルシリケートの縮合物であり、下記式(1)で表わされるシロキサンオリゴマーである。
これらのシロキサンオリゴマーは、下記構造式(3)および(4)で示されるアルコキシシランを加水分解することで製造することができる。
Si(R10)l(OR11)m ・・・(3)
ここでR10はオキセタニル基を含有する置換基を表わし、R11は水素原子または1価の有機基を表わし、lは1〜3の整数であり、mはそれぞれ0〜3の整数である。但し、l+m=4である。
Si(R12)x(OR13)4−x ・・・(4)
ここでR12、R13はオキセタニル基を含有しない置換基を表わし、同一でも異なっていてもよく、それぞれ水素原子または1価の有機基であり、xは0〜3の整数である。但し、x+y=4である。
本発明の感放射線性樹脂組成物は、上記の共重合体[A]、[B]および[C]成分を必須成分として含有するが、その他必要に応じて[D]感熱性酸生成化合物、[E]少なくとも1個のエチレン性不飽和二重結合を有する重合性化合物、[F]共重合体[A]以外のエポキシ樹脂、[G]界面活性剤あるいは[H]接着助剤を含有することができる。
上記[D]感熱性酸生成化合物は、耐熱性や硬度を向上させるために用いることができる。その具体例としては、スルホニウム塩、ベンゾチアゾニウム塩、アンモニウム塩、ホスホニウム塩などのオニウム塩が挙げられる。
これらの具体例としては、アルキルスルホニウム塩として、例えば4−アセトフェニルジメチルスルホニウムヘキサフルオロアンチモネート、4−アセトキシフェニルジメチルスルホニウムヘキサフルオロアルセネート、ジメチル−4−(ベンジルオキシカルボニルオキシ)フェニルスルホニウムヘキサフルオロアンチモネート、ジメチル−4−(ベンゾイルオキシ)フェニルスルホニウムヘキサフルオロアンチモネート、ジメチル−4−(ベンゾイルオキシ)フェニルスルホニウムヘキサフルオロアルセネート、ジメチル−3−クロロ−4−アセトキシフェニルスルホニウムヘキサフルオロアンチモネートなど;
ベンジルスルホニウム塩として、例えばベンジル−4−ヒドロキシフェニルメチルスルホニウムヘキサフルオロアンチモネート、ベンジル−4−ヒドロキシフェニルメチルスルホニウムヘキサフルオロホスフェート、4−アセトキシフェニルベンジルメチルスルホニウムヘキサフルオロアンチモネート、ベンジル−4−メトキシフェニルメチルスルホニウムヘキサフルオロアンチモネート、ベンジル−2−メチル−4−ヒドロキシフェニルメチルスルホニウムヘキサフルオロアンチモネート、ベンジル−3−クロロ−4−ヒドロキシフェニルメチルスルホニウムヘキサフルオロアルセネート、4−メトキシベンジル−4−ヒドロキシフェニルメチルスルホニウム ヘキサフルオロホスフェートなど;
置換ベンジルスルホニウム塩として、例えばp−クロロベンジル−4−ヒドロキシフェニルメチルスルホニウムヘキサフルオロアンチモネート、p−ニトロベンジル−4−ヒドロキシフェニルメチルスルホニウムヘキサフルオロアンチモネート、p−クロロベンジル−4−ヒドロキシフェニルメチルスルホニウム ヘキサフルオロホスフェート、p−ニトロベンジル−3−メチル−4−ヒドロキシフェニルメチルスルホニウムヘキサフルオロアンチモネート、3,5−ジクロロベンジル−4−ヒドロキシフェニルメチルスルホニウムヘキサフルオロアンチモネート、o−クロロベンジル−3−クロロ−4−ヒドロキシフェニルメチルスルホニウムヘキサフルオロアンチモネートなどをそれぞれ挙げることができる。
これらの市販品としては、サンエイドSI−L85、同SI−L110、同SI−L145、同SI−L150、同SI−L160(三新化学工業(株)製)などが挙げられる。
これらのうち、3官能以上の(メタ)アクリレートが好ましく用いられ、そのうちでもトリメチロールプロパントリ(メタ)アクリレート、ペンタエリスリトールテトラ(メタ)アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレートが特に好ましい。
これらの単官能、2官能または3官能以上の(メタ)アクリレートは、単独であるいは組み合わせて用いられる。[E]成分の使用割合は、共重合体[A]100重量部に対して、好ましくは50重量部以下、より好ましくは30重量部以下である。
[F]成分の使用割合は、共重合体[A]100重量部に対して、好ましくは30重量部以下である。このような割合で[F]成分が含有されることにより、本発明の感放射線性樹脂組成物から得られる保護膜または絶縁膜の耐熱性および表面硬度等をさらに向上させることができる。この割合が30重量部を超えると、基板上に感放射線性樹脂組成物の塗膜を形成する際、塗膜の膜厚均一性が不十分となる場合がある。
なお、共重合体[A]も「エポキシ樹脂」といい得るが、アルカリ可溶性を有する点で[F]成分とは異なる。[F]成分はアルカリ不溶性である。
これらの界面活性剤は単独でまたは2種以上を組み合わせて使用することができる。
本発明の感放射線性樹脂組成物は、上記の共重合体[A]、[B]および[C]成分ならびに上記の如き任意的に添加するその他の成分を均一に混合することによって調製される。通常、本発明の感放射線性樹脂組成物は、好ましくは適当な溶媒に溶解されて溶液状態で用いられる。例えば共重合体[A]、[B]および[C]成分ならびに任意的に添加されるその他の成分を、所定の割合で混合することにより、溶液状態の感放射線性樹脂組成物を調製することができる。
このような溶媒としては、上述した共重合体[A]を製造するために使用できる溶媒として例示したものと同様のものを挙げることができる。
このようにして調製された組成物溶液は、孔径0.2μm程度のミリポアフィルタなどを用いて濾過した後、使用に供することもできる。
次に本発明の感放射線性樹脂組成物を用いて、本発明の層間絶縁膜、マイクロレンズを形成する方法について述べる。本発明の層間絶縁膜またはマイクロレンズの形成方法は、以下の工程を以下に記載の順序で含む。
(1)本発明の感放射線性組成物の塗膜を基板上に形成する工程、
(2)該塗膜の少なくとも一部に放射線を照射する工程、
(3)現像工程、および
(4)加熱工程。
上記(1)の工程においては、本発明の組成物溶液を基板表面に塗布し、好ましくはプレベークを行うことにより溶媒を除去して、感放射線性樹脂組成物の塗膜を形成する。
使用できる基板の種類としては、例えばガラス基板、シリコンウエハーおよびこれらの表面に各種金属が形成された基板を挙げることができる。
組成物溶液の塗布方法としては、特に限定されず、例えばスプレー法、ロールコート法、回転塗布法(スピンコート法)、スリットダイ塗布法、バー塗布法、インクジェット法等の適宜の方法を採用することができ、特にスピンコート法、スリットダイ塗布法が好ましい。プレベークの条件としては、各成分の種類、使用割合等によっても異なる。例えば、60〜110℃で30秒間〜15分間程度とすることができる。
形成される塗膜の膜厚としては、プレベーク後の値として、層間絶縁膜を形成する場合にあっては例えば3〜6μm、マイクロレンズを形成する場合にあっては例えば0.5〜3μmが好ましい。
上記(2)の工程においては、形成された塗膜に所定のパターンを有するマスクを介して、放射線を照射した後、現像液を用いて現像処理して放射線の照射部分を除去することによりパターニングを行う。このとき用いられる放射線としては、例えば紫外線、遠紫外線、X線、荷電粒子線等が挙げられる。
上記紫外線としては例えばg線(波長436nm)、i線(波長365nm)等が挙げられる。遠紫外線としては例えばKrFエキシマレーザー等が挙げられる。X線としては例えばシンクロトロン放射線等が挙げられる。荷電粒子線として例えば電子線等を挙げることができる。
これらのうち、紫外線が好ましく、なかでもg線および/またはi線を含む放射線が特に好ましい。
露光量としては、層間絶縁膜を形成する場合にあっては50〜1,500J/m2、マイクロレンズを形成する場合にあっては50〜2,000J/m2とすることが好ましい。
現像処理に用いられる現像液としては、例えば水酸化ナトリウム、水酸化カリウム、炭酸ナトリウム、ケイ酸ナトリウム、メタケイ酸ナトリウム、アンモニア、エチルアミン、n−プロピルアミン、ジエチルアミン、ジエチルアミノエタノール、ジ−n−プロピルアミン、トリエチルアミン、メチルジエチルアミン、ジメチルエタノールアミン、トリエタノールアミン、テトラメチルアンモニウムヒドロキシド、テトラエチルアンモニウムヒドロキシド、ピロール、ピペリジン、1,8−ジアザビシクロ〔5,4,0〕−7−ウンデセン、1,5−ジアザビシクロ〔4,3,0〕−5−ノナン等のアルカリ(塩基性化合物)の水溶液を用いることができる。また、上記のアルカリの水溶液にメタノール、エタノール等の水溶性有機溶媒や界面活性剤を適当量添加した水溶液、または本発明の組成物を溶解する各種有機溶媒を現像液として使用することができる。さらに、現像方法としては、例えば液盛り法、ディッピング法、揺動浸漬法、シャワー法等の適宜の方法を利用することができる。このときの現像時間は、組成物の組成によって異なるが、例えば30〜120秒間とすることができる。
なお、従来知られている感放射線性樹脂組成物は、現像時間が最適値から20〜25秒程度超過すると形成したパターンに剥がれが生じるため現像時間を厳密に制御する必要があったが、本発明の感放射線性樹脂組成物の場合、最適現像時間からの超過時間が30秒以上となっても良好なパターン形成が可能であり、製品歩留まり上の利点がある。
上記のように実施した(3)現像工程後に、パターニングされた薄膜に対して、好ましくは例えば流水洗浄によるリンス処理を行い、さらに、好ましくは高圧水銀灯などによる放射線を全面に照射(後露光)することにより、当該薄膜中に残存する1,2−キノンジアジト化合物の分解処理を行った後、この薄膜を、ホットプレート、オーブン等の加熱装置により加熱処理(ポストベーク処理)することにより、当該薄膜の硬化処理を行う。上記後露光工程における露光量は、好ましくは2,000〜5,000J/m2程度である。また、この硬化処理における焼成温度は、例えば120〜250℃である。加熱時間は、加熱機器の種類により異なるが、例えばホットプレート上で加熱処理を行う場合には5〜30分間、オーブン中で加熱処理を行う場合には30〜90分間とすることができる。この際に、2回以上の加熱工程を行うステップベーク法等を用いることもできる。
このようにして、目的とする層間絶縁膜またはマイクロレンズに対応する、パターン状薄膜を基板の表面上に形成することができる。
上記のようにして形成された層間絶縁膜およびマイクロレンズは、後述の実施例から明らかにされるように、密着性、耐熱性、耐溶剤性、および透明性等に優れるものである。
上記のようにして形成された本発明の層間絶縁膜は、基板への密着性が良好であり、耐溶剤性および耐熱性に優れ、高い透過率を有し、誘電率が低いものであり、電子部品の層間絶縁膜として好適に使用できる。
上記のようにして形成された本発明のマイクロレンズは、基板への密着性が良好であり、耐溶剤性および耐熱性に優れ、かつ高い透過率と良好なメルト形状を有するものであり、固体撮像素子のマイクロレンズとして好適に使用できる。
なお、本発明のマイクロレンズの形状は、図1(a)に示したように、半凸レンズ形状となる。
冷却管、攪拌機を備えたフラスコに、2,2’−アゾビス(2,4−ジメチルバレロニトリル)7重量部、プロピレングリコールモノメチルエーテルアセテート220重量部を仕込んだ。引き続きメタクリル酸22重量部、グリシジルメタクリレート40重量部、ジシクロペンタニルメタクリレート28重量部、3−エチル−3−メタクリロイルオキシメチルオキセタン10重量部、α−メチルスチレンダイマー3重量部を仕込み、窒素置換しながらゆるやかに撹拌を始めた。溶液の温度を70℃に上昇させ、この温度にて4時間加熱し共重合体[A−1]を含む重合体溶液を得た。得られた重合体溶液の固形分濃度は31.8重量%であり、重合体の重量平均分子量は17,900で分子量分布(重量平均分子量/数平均分子量の比)は1.8であった。なお、重量平均分子量および数平均分子量は、GPC(ゲルパーミエイションクロマトグラフィー(東ソー(株)製HLC−8020)を用いて測定したポリスチレン換算平均分子量である。
冷却管、攪拌機を備えたフラスコに、2,2’−アゾビス(2,4−ジメチルバレロニトリル)7重量部、ジエチレングリコールエチルメチルエーテル220重量部を仕込んだ。引き続きスチレン5重量部、メタクリル酸22重量部、グリシジルメタクリレート40重量部、3−エチル−3−メタクリロイルオキシメチルオキセタン5重量部、ジシクロペンタニルメタクリレート28重量部を仕込み窒素置換しながらゆるやかに撹拌を始めた。溶液の温度を70℃に上昇させ、この温度にて4時間加熱し共重合体[A−2]を含む重合体溶液を得た。得られた重合体溶液の固形分濃度は31.9重量%であり、重合体の重量平均分子量は20,200で分子量分布は1.9であった。
冷却管、攪拌機を備えたフラスコに、2,2’−アゾビス(2,4−ジメチルバレロニトリル)7重量部、ジエチレングリコールエチルメチルエーテル200重量部を仕込んだ。引き続きメタクリル酸12重量部、シクロヘキシルマレイイミド12重量部、α−メチル−p−ヒドロキシスチレン9重量部、グリシジルメタクリレート50重量部、3−エチル−3−メタクリロイルオキシメチルオキセタン10重量部、テトラヒドロフルフリルメタクリレート7重量部、α−メチルスチレンダイマー3重量部を仕込み、窒素置換しながらゆるやかに撹拌を始めた。溶液の温度を70℃に上昇させ、この温度にて5時間加熱し共重合体[A−3]を含む重合体溶液を得た。得られた重合体溶液の固形分濃度は32.7重量%であり、重合体の重量平均分子量は21,500で分子量分布は2.2であった。
冷却管、攪拌機を備えたフラスコに、2,2’−アゾビス(2,4−ジメチルバレロニトリル)8重量部、ジエチレングリコールエチルメチルエーテル220重量部を仕込んだ。引き続きスチレン20重量部、メタクリル酸30重量部、3−エチル−3−メタクリロイルオキシメチルオキセタン20重量部、グリシジルメタクリレート30重量部、α−メチルスチレンダイマー4.0部を仕込み窒素置換しながらゆるやかに撹拌を始めた。溶液の温度を70℃に上昇させ、この温度にて5時間加熱し共重合体[A−4]を含む重合体溶液を得た。得られた重合体溶液の固形分濃度は31.0重量%であり、重合体の重量平均分子量は19,000で分子量分布は1.7であった。
冷却管、攪拌機を備えたフラスコに、2,2’−アゾビス(2,4−ジメチルバレロニトリル)7重量部、ジエチレングリコールメチルエチルエーテル220重量部を仕込んだ。引き続きメタクリル酸23重量部、ジシクロペンタニルメタクリレート47部、メタクリル酸グリシジル20重量部、α−メチルスチレンダイマー2.0部を仕込み窒素置換しながらゆるやかに撹拌を始めた。溶液の温度を70℃に上昇させ、この温度を5時間保持し共重合体[A−1R]を含む重合体溶液を得た。得られた重合体溶液の固形分濃度は32.8重量%であり、重合体の重量平均分子量は24,000で分子量分布は2.3であった。
冷却管、攪拌機を備えたフラスコに、2,2’−アゾビス(2,4−ジメチルバレロニトリル)7重量部、ジエチレングリコールメチルエチルエーテル220重量部を仕込んだ。引き続きメタクリル酸25重量部、ジシクロペンタニルメタクリレート35部、2−ヒドロキシエチルメタクリレート40重量部、α−メチルスチレンダイマー2.0部を仕込み窒素置換しながらゆるやかに撹拌を始めた。溶液の温度を70℃に上昇させ、この温度を5時間保持し共重合体[A−2R]を含む重合体溶液を得た。得られた重合体溶液の固形分濃度は32.8重量%であり、重合体の重量平均分子量は25,000で分子量分布は2.4であった。
感放射線性樹脂組成物の調製
合成例1で得られた共重合体[A−1]を含む重合体溶液(共重合体[A−1]100重量部(固形分)に相当)と、
成分[B]として4,4’−[1−[4−[1−[4−ヒドロキシフェニル]−1−メチルエチル]フェニル]エチリデン]ビスフェノール(1モル)と1,2−ナフトキノンジアジド−5−スルホン酸クロリド(2モル)との縮合物(4,4’−[1−[4−[1−[4−ヒドロキシフェニル]−1−メチルエチル]フェニル]エチリデン]ビスフェノール−1,2−ナフトキノンジアジド−5−スルホン酸エステル)20重量部、テトラ[(3−エチルオキセタン−3−イル)メチル]シリケートの縮合物2重量部およびγ−メタクリロキシプロピルトリメトキシシラン5重量部を混合し、固形分濃度が30重量%になるようにプロピレングリコールモノメチルエーテルアセテートに溶解させた後、孔径0.5μmのミリポアフィルタで濾過して感放射線性樹脂組成物の溶液(S−1)を調製した。
(I)パターン状薄膜の形成
ガラス基板上にスピンナーを用いて、上記組成物溶液(S−1)を塗布した後、80℃で3分間ホットプレート上でプレベークして塗膜を形成した。
上記で得られた塗膜に所定パターンマスクを用いて、365nmでの強度が10mW/cm2である紫外線を15秒間照射した。次いでテトラメチルアンモニウムヒドロキシド0.5重量%水溶液で25℃で1分間現像した後、純水で1分間リンスした。これらの操作により、不要な部分を除去した。
上記で形成されたパターンに365nmでの強度が10mW/cm2である紫外線を30秒間照射した後、オーブン中で220℃で60分間加熱し硬化させ膜厚3μmのパターン状薄膜を得た。
また、プレベーク温度を90℃、100℃とした他は、上記と同様の操作を行い、プレベーク温度の異なる3種類のパターン状薄膜を形成した。
上記(I)で得られたパターン状薄膜において抜きパターン(5μm×5μmホール)が解像できている場合を○、解像できていない場合を×とした。結果を表1に示す。
(III)耐熱寸法安定性の評価
上記(I)において、プレベーク温度80℃にて形成した薄膜パターンをオーブン中、220℃で60分加熱した。加熱前後における膜厚の変化率を表2に示した。この時の寸法変化率が加熱前後で5%以内の時、耐熱寸法安定性は良好、寸法変化率が5%を越える時、不良といえる。
(IV)透明性の評価
上記(I)において、プレベーク温度80℃にて形成したパターン状薄膜の400nmの透過率を分光光度計(150−20型ダブルビーム(日立製作所(株)製))を用いて測定し、透明性の評価を行った。この結果を表2に示す。このとき透過率が90%以上の場合、透明性は良好、90%未満の場合不良といえる。
(V)耐熱変色性の評価
上記(I)において、プレベーク温度80℃にて形成したパターン状薄膜を有する基板を250℃のオーブンで1時間加熱し、加熱前後におけるパターン状薄膜の透過率の変化により耐熱変色性を評価した。このときの評価結果を表2に示す。変化率が5%未満である場合、耐熱変色性は良好、5%を超えた場合不良といえる。なお透過率は(VI)透明性の評価と同様にして求めた。
(VI)密着性の評価
上記(I)において、プレベーク温度80℃にて形成したパターン状薄膜の密着性をプレッシャークッカー試験(120℃、湿度100%、4時間)後の碁盤目剥離試験により評価した。このときの評価結果を表2に示す。評価結果は碁盤目100個中、残った碁盤目の数で表した。
(VII)保存安定性の評価
上記組成物溶液を40℃のオーブンで1週間加熱し、加熱前後における粘度の変化により保存安定性を評価した。このときの粘度変化率を表1に示す。変化率が5%未満である場合を保存安定性が良好、5%以上の場合を保存安定性が不良といえる。
(I)マイクロレンズの形成
6インチシリコン基板に上記組成物溶液(S−1)を2.5μmの膜厚になるようにスピンコートし70℃で3分間ホットプレート上でプレベークし、塗膜を形成した。
上記で得られた塗膜に所定パターンマスクを用いて、436nmでの強度が10mW/cm2である紫外線を照射した。次いでテトラメチルアンモニウムヒドロキシド2.38重量%水溶液で25℃で1分間現像した後、純水で1分間リンスした。これらの操作により、不要な部分を除去し、パターンを形成した。
上記で形成されたパターンに436nmでの強度が10mW/cm2である紫外線を200mJ/cm2照射した後、160℃で10分間加熱後さらに230℃で10分間加熱してパターンをメルトフローさせマイクロレンズを形成した。
(II)感度の評価
上記(I)で得られたメルトフロー後のマイクロレンズパターンの、0.8μmライン・アンド・スペ−スパタ−ン(10対1)のスペース線幅を解像できる最低照射量を表3に示した。この値が100mJ/cm2以下の場合、解像度良好、感度が100mJ/cm2を越える場合、解像度不良といえる。
(III)透明性の評価
ガラス基板上に上記(I)と同様にしてパターン状薄膜を形成した。
メルトフロー後のマイクロレンズパターンを形成したガラス基板について、400nmの透過率を分光光度計(150−20型ダブルビーム(日立製作所(株)製))を用いて測定し、透明性の評価を行った。このときの400nmにおける透過率を表3に示す。透過率が90〜100%のとき透過率は良好、90%未満の場合、透過率は不良といえる。
上記(III)において形成したパターン状薄膜を有するガラス基板を250℃のオーブンで1時間加熱し、加熱前後におけるパターン状薄膜の透過率の変化により耐熱透明性を評価した。このときの透過率の変化率を表3に示す。変化率が5%未満である場合耐熱透明性は良好、5%を超えた場合、不良といえる。なお透過率は(III)透明性の評価と同様にして求めた。
(V)密着性の評価
上記(I)において形成したパターン状薄膜の密着性をプレッシャークッカー試験(120℃、湿度100%、4時間)後の碁盤目剥離試験により評価した。このときの評価結果を表3に示す。評価結果は碁盤目100個中、残った碁盤目の数で表した。
(VII)耐溶剤性の評価
上記(III)と同様にして形成したパターン状薄膜を有するガラス基板を50℃中のイソプロピルアルコール中に10分間浸せきし、膜厚変化を評価した。このときの変化率を表3に示す。変化率が0〜5%のとき耐溶剤性は良好、5%を超えたときおよび溶解により膜厚が低下した場合、耐溶剤性は不良といえる。
合成例2で得られた共重合体[A−2]を含む重合体溶液(共重合体[A−2]100重量部(固形分)に相当)と、
成分[B]として4,4’−[1−[4−[1−[4−ヒドロキシフェニル]−1−メチルエチル]フェニル]エチリデン]ビスフェノール(1モル)と1,2−ナフトキノンジアジド−5−スルホン酸クロリド(2モル)との縮合物(4,4’−[1−[4−[1−[4−ヒドロキシフェニル]−1−メチルエチル]フェニル]エチリデン]ビスフェノール−1,2−ナフトキノンジアジド−5−スルホン酸エステル)20重量部、テトラ[(3−エチルオキセタン−3−イル)メチル]シリケートの縮合物2重量部およびγ−メタクリロキシプロピルトリメトキシシラン5重量部を混合し、固形分濃度が31重量%になるようにプロピレングリコールモノメチルエーテルアセテートに溶解させた後、孔径0.5μmのミリポアフィルタで濾過して感放射線性樹脂組成物の溶液(S−2)を調製し、評価した。結果を表1〜3に示す。
合成例3で得られた共重合体[A−3]を含む重合体溶液(共重合体[A−3]100重量部(固形分)に相当)と、
成分[B]として4,4’−[1−[4−[1−[4−ヒドロキシフェニル]−1−メチルエチル]フェニル]エチリデン]ビスフェノール(1モル)と1,2−ナフトキノンジアジド−5−スルホン酸クロリド(2モル)との縮合物(4,4’−[1−[4−[1−[4−ヒドロキシフェニル]−1−メチルエチル]フェニル]エチリデン]ビスフェノール−1,2−ナフトキノンジアジド−5−スルホン酸エステル)18重量部、テトラ[(3−エチルオキセタン−3−イル)メチル]シリケートの縮合物2重量部およびγ−メタクリロキシプロピルトリメトキシシラン5重量部を混合し、固形分濃度が30重量%になるようにプロピレングリコールモノメチルエーテルアセテートに溶解させた後、孔径0.5μmのミリポアフィルタで濾過して感放射線性樹脂組成物の溶液(S−3)を調製し、評価した。結果を表1〜3に示す。
合成例4で得られた共重合体[A−4]を含む重合体溶液(共重合体[A−4]100重量部(固形分)に相当)と、
成分[B]として4,4’−[1−[4−[1−[4−ヒドロキシフェニル]−1−メチルエチル]フェニル]エチリデン]ビスフェノール(1モル)と1,2−ナフトキノンジアジド−5−スルホン酸クロリド(2モル)との縮合物(4,4’−[1−[4−[1−[4−ヒドロキシフェニル]−1−メチルエチル]フェニル]エチリデン]ビスフェノール−1,2−ナフトキノンジアジド−5−スルホン酸エステル)30重量部、テトラ[(3−エチルオキセタン−3−イル)メチル]シリケートの縮合物2重量部およびγ−メタクリロキシプロピルトリメトキシシラン5重量部を混合し、固形分濃度が31重量%になるようにプロピレングリコールモノメチルエーテルアセテートに溶解させた後、孔径0.5μmのミリポアフィルタで濾過して感放射線性樹脂組成物の溶液(S−4)を調製し、評価した。結果を表1〜3に示す。
比較合成例1で得られた共重合体[A−1R]を含む重合体溶液(共重合体[A−1R]100重量部(固形分)に相当)と、
成分[B]として4,4’−[1−[4−[1−[4−ヒドロキシフェニル]−1−メチルエチル]フェニル]エチリデン]ビスフェノール(1モル)と1,2−ナフトキノンジアジド−5−スルホン酸クロリド(2モル)との縮合物(4,4’−[1−[4−[1−[4−ヒドロキシフェニル]−1−メチルエチル]フェニル]エチリデン]ビスフェノール−1,2−ナフトキノンジアジド−5−スルホン酸エステル)30重量部およびγ−メタクリロキシプロピルトリメトキシシラン5重量部を混合し、固形分濃度が31重量%になるようにプロピレングリコールモノメチルエーテルアセテートに溶解させた後、孔径0.5μmのミリポアフィルタで濾過して感放射線性樹脂組成物の溶液(S−1R)を調製し、評価した。結果を表1〜3に示す。
比較合成例1で得られた共重合体[A−2R]を含む重合体溶液(共重合体[A−2R]100重量部(固形分)に相当)と、
成分[B]として4,4’−[1−[4−[1−[4−ヒドロキシフェニル]−1−メチルエチル]フェニル]エチリデン]ビスフェノール(1モル)と1,2−ナフトキノンジアジド−5−スルホン酸クロリド(2モル)との縮合物(4,4’−[1−[4−[1−[4−ヒドロキシフェニル]−1−メチルエチル]フェニル]エチリデン]ビスフェノール−1,2−ナフトキノンジアジド−5−スルホン酸エステル)18重量部およびγ−メタクリロキシプロピルトリメトキシシラン5重量部を混合し、固形分濃度が31重量%になるようにプロピレングリコールモノメチルエーテルアセテートに溶解させた後、孔径0.5μmのミリポアフィルタで濾過して感放射線性樹脂組成物の溶液(S−2R)を調製し、評価した。結果を表1〜3に示す。
Claims (7)
- [A](a1)不飽和カルボン酸および不飽和カルボン酸無水物の群から選ばれる少なくとも1種、
(a2)エポキシ基含有不飽和化合物およびオキセタニル基含有不飽和化合物の群から選ばれる少なくとも1種、ならびに
(a3)(a1)、(a2)以外の不飽和化合物、の共重合体、
[B]1,2−キノンジアジド化合物、ならびに
[C]下記式(1)で表されるシロキサンオリゴマー
を含有することを特徴とする感放射線性樹脂組成物。 - 層間絶縁膜形成用である請求項1に記載の感放射線性樹脂組成物。
- 以下の工程を以下に記載の順序で含むことを特徴とする層間絶縁膜の形成方法。
(1)請求項1に記載の感放射線性組成物の塗膜を基板上に形成する工程、
(2)該塗膜の少なくとも一部に放射線を照射する工程、
(3)現像工程、および
(4)加熱工程。 - 請求項3の方法により形成された層間絶縁膜。
- マイクロレンズ形成用である請求項1に記載の感放射線性樹脂組成物。
- 以下の工程を以下に記載順で含むことを特徴とするマイクロレンズの形成方法。
(1)請求項1に記載の感放射線性組成物の塗膜を基板上に形成する工程、
(2)該塗膜の少なくとも一部に放射線を照射する工程、
(3)現像工程、および
(4)加熱工程。 - 請求項6の方法により形成されたマイクロレンズ。