JP4693125B2 - Sheet member with liquid crystal and method for producing the same - Google Patents

Sheet member with liquid crystal and method for producing the same Download PDF

Info

Publication number
JP4693125B2
JP4693125B2 JP2006277224A JP2006277224A JP4693125B2 JP 4693125 B2 JP4693125 B2 JP 4693125B2 JP 2006277224 A JP2006277224 A JP 2006277224A JP 2006277224 A JP2006277224 A JP 2006277224A JP 4693125 B2 JP4693125 B2 JP 4693125B2
Authority
JP
Japan
Prior art keywords
liquid crystal
layer
sheet
sheet member
surface side
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2006277224A
Other languages
Japanese (ja)
Other versions
JP2008093920A (en
Inventor
操 中村
信一 小野
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Osaka Sealing Printing Co Ltd
Original Assignee
Osaka Sealing Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Osaka Sealing Printing Co Ltd filed Critical Osaka Sealing Printing Co Ltd
Priority to JP2006277224A priority Critical patent/JP4693125B2/en
Publication of JP2008093920A publication Critical patent/JP2008093920A/en
Application granted granted Critical
Publication of JP4693125B2 publication Critical patent/JP4693125B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、コレステリック液晶組成物が含有された液晶層が基材シートに形成された液晶付きシート部材及びその製造方法に係り、特に、上記の液晶層において本来の特性の発現が損なわれるのを抑制し、識別性に優れて偽造が困難になると共に、その製造も容易に行えて、製造コストも低減されるようにした点に特徴を有するものである。   The present invention relates to a sheet member with a liquid crystal in which a liquid crystal layer containing a cholesteric liquid crystal composition is formed on a base sheet and a method for producing the same, and particularly, the above-mentioned liquid crystal layer impairs the expression of original characteristics. It is characterized in that it is suppressed, has excellent discrimination, makes counterfeiting difficult, makes it easy to manufacture, and reduces manufacturing costs.

従来から、カード、証書、金券類等の偽造防止用識別媒体として、ホログラムが用いられているが、最近においてはホログラムの制作が容易になり、特に目視用のホログラムについては、本物と区別がつかないほどの偽造品が製造されるようになっている。   Conventionally, holograms have been used as anti-counterfeiting identification media for cards, certificates, vouchers, etc., but recently it has become easier to produce holograms, especially for visual holograms, which can be distinguished from the real ones. There are so many counterfeit products.

このため、近年においては、偽造防止用識別媒体として、基材シートにコレステリック液晶組成物が含有された液晶層を形成した液晶付きシート部材を用い、その反射光を目視又は光学機器により検出するようにしたものが数多く提案されている。   Therefore, in recent years, as an identification medium for preventing counterfeiting, a sheet member with a liquid crystal in which a liquid crystal layer containing a cholesteric liquid crystal composition is formed on a base sheet is used, and the reflected light is detected visually or by an optical instrument. Many things have been proposed.

そして、このような液晶付きシート部材としては、基材シートの片面にコレステリック液晶組成物が含有された液晶層を形成し、この液晶層の上に直接或いは背景層を介して接着剤や粘着剤の層を設け、この接着剤や粘着剤の層を対象物に接着させるようにしたものが提案されている。（例えば、特許文献１，２参照。）   And as such a sheet member with a liquid crystal, a liquid crystal layer containing a cholesteric liquid crystal composition is formed on one side of a base sheet, and an adhesive or a pressure-sensitive adhesive is directly or via a background layer on the liquid crystal layer. A layer is proposed in which the adhesive layer and the adhesive layer are adhered to an object. (For example, see Patent Documents 1 and 2.)

ここで、上記の液晶付きシート部材を上記のようにして対象物に接着させた場合、基材シートが表面側に位置するようになり、この基材シートに一般に使用されているポリエチレンテレフタレート等のポリエステル樹脂からなる材料を用いた場合には、円偏光フィルタを用いた識別が困難になる等、上記のコレステリック液晶組成物の含有された液晶層において本来の特性の発現が損なわれという問題があった。   Here, when the above-mentioned sheet member with a liquid crystal is adhered to an object as described above, the base sheet comes to be positioned on the surface side, such as polyethylene terephthalate generally used for this base sheet. When a material made of polyester resin is used, there is a problem in that the original characteristics are impaired in the liquid crystal layer containing the cholesteric liquid crystal composition, such as difficulty in identification using a circular polarizing filter. It was.

また、上記のような液晶付きシート部材として、基材シートの表面にコレステリック液晶組成物が含有された液晶層を直接形成するようにしたものや、基材シートの表面側に、感熱記録層を介してコレステリック液晶組成物が含有された液晶層を形成するようにしたものも提案されている。（例えば、特許文献３参照。）   In addition, as a sheet member with a liquid crystal as described above, a liquid crystal layer containing a cholesteric liquid crystal composition is directly formed on the surface of the base sheet, or a thermosensitive recording layer is provided on the surface side of the base sheet. Also proposed is a liquid crystal layer containing a cholesteric liquid crystal composition. (For example, refer to Patent Document 3.)

しかし、このように基材シートの表面に上記の液晶層を直接形成する場合や、上記の感熱記録層の上に上記の液晶層を直接形成するようにした場合、基材シートや基材シートの上に設けられた感熱記録層に対する液晶層の接着力が弱く、液晶層が簡単に剥がれてしまうという問題があった。   However, when the liquid crystal layer is directly formed on the surface of the base sheet, or when the liquid crystal layer is directly formed on the thermosensitive recording layer, the base sheet or the base sheet The adhesion of the liquid crystal layer to the heat-sensitive recording layer provided thereon is weak and the liquid crystal layer is easily peeled off.

また、上記のように感熱記録層の上に上記の液晶層を直接形成する場合や、また上記の液晶層の接着力を高めるために、基材シートや感熱記録層の上に接着剤層により上記の液晶層を直接接着して形成するようにした場合には、上記の感熱記録層や接着剤層における凹凸や、これらの層に用いる材料によって、液晶層に用いた上記のコレステリック液晶組成物の配向特性が低下し、色彩がまだらに現れたり、円偏光フィルタを用いた識別が困難になる等の問題があった。   In addition, when the liquid crystal layer is directly formed on the thermosensitive recording layer as described above, or in order to increase the adhesive force of the liquid crystal layer, an adhesive layer is provided on the base sheet or the thermosensitive recording layer. When the liquid crystal layer is formed by directly adhering, the cholesteric liquid crystal composition used in the liquid crystal layer depends on the unevenness in the heat-sensitive recording layer and the adhesive layer and the material used for these layers. The orientation characteristics of the film deteriorated, and the colors appear mottled, making it difficult to identify using a circularly polarizing filter.

さらに、従来の液晶付きシート部材においては、一般に基材シートの全面に上記のような液晶層を形成し、このように形成した液晶層に対してエッチング加工やレーザ加工等によりパターニングを行うようにしており、液晶付きシート部材の製造が面倒であると共に、液晶層の無駄も多くなり、製造コストが高くつく等の問題もあった。
特開２００２−１２７６４７号公報 国際公開ＷＯ２００４／０３２０９９号公報 特開２００２−６７５０２号公報 Furthermore, in the conventional sheet member with liquid crystal, the liquid crystal layer as described above is generally formed on the entire surface of the base sheet, and the liquid crystal layer thus formed is patterned by etching or laser processing. In addition, the manufacture of the sheet member with a liquid crystal is troublesome, the liquid crystal layer is wasted, and the manufacturing cost is high.
JP 2002-127647 A International Publication WO2004 / 032099 JP 2002-67502 A

本発明は、コレステリック液晶組成物が含有された液晶層が基材シートに形成された液晶付きシート部材における上記のような様々な問題を解決することを課題とするものであり、上記の液晶層において本来の特性の発現が損なわれるのを抑制し、識別性に優れて偽造が困難になると共に、その製造が容易に行えて、製造コストも低減される液晶付きシート部材及びその製造方法を提供することを課題とするものである。   An object of the present invention is to solve the above-mentioned various problems in a sheet member with a liquid crystal in which a liquid crystal layer containing a cholesteric liquid crystal composition is formed on a base material sheet. Providing a sheet member with a liquid crystal and a manufacturing method thereof that suppresses the deterioration of the original characteristics of the sheet, makes it easy to forge, and makes it easy to manufacture and reduce manufacturing costs It is an object to do.

本発明における液晶付きシート部材においては、上記のような課題を解決するため、基材シートの表面側に接着剤層を介して樹脂層を設けると共に、この樹脂層の表面側にコレステリック液晶組成物が含有された複数の液晶層を分離して設けるようにしている。   In the sheet member with a liquid crystal according to the present invention, in order to solve the above-described problems, a resin layer is provided on the surface side of the base sheet via an adhesive layer, and the cholesteric liquid crystal composition is provided on the surface side of the resin layer. A plurality of liquid crystal layers containing bismuth are provided separately.

そして、本発明における液晶付きシート部材においては、上記の液晶層の光輝性等を向上させるために、上記の基材シートの表面側又は裏面側に背景層を形成することが好ましい。なお、この背景層の色彩が液晶層に反映されるようにするため、この背景層を基材シートの表面側に形成する場合には、上記の接着剤層及び樹脂層を透明又は半透明の透光性材料で構成するようにし、また上記の接着剤層及び樹脂層と共に上記の基材シートを透明又は半透明の透光性材料で構成すると、上記の背景層を基材シートの表面側又は裏面側の何れに設けるようにすることも可能になる。   And in the sheet | seat member with a liquid crystal in this invention, in order to improve the brightness etc. of said liquid crystal layer, it is preferable to form a background layer in the surface side or back surface side of said base material sheet. In order to reflect the color of the background layer on the liquid crystal layer, when the background layer is formed on the surface side of the base material sheet, the adhesive layer and the resin layer are transparent or translucent. When the base sheet is made of a transparent or translucent light-transmitting material together with the adhesive layer and the resin layer, the background layer is formed on the surface side of the base sheet. Alternatively, it can be provided on any of the back side.

また、本発明における液晶付きシート部材においては、上記の樹脂層の表面側に設けられた液晶層を紫外線や熱等から保護するために、樹脂層の表面側に液晶層を覆うようにして透光性の表面保護層を設けることが好ましく、またこの表面保護層を耐熱性樹脂で構成すると共に、この表面保護層に紫外線吸収剤を添加させることが好ましい。   Further, in the sheet member with a liquid crystal according to the present invention, in order to protect the liquid crystal layer provided on the surface side of the resin layer from ultraviolet rays, heat, etc., the liquid crystal layer is covered so as to cover the surface side of the resin layer. It is preferable to provide a light-sensitive surface protective layer, and it is preferable that the surface protective layer is made of a heat-resistant resin and an ultraviolet absorber is added to the surface protective layer.

また、本発明における液晶付きシート部材を対象物に貼着させるラベルとして使用する場合には、上記の基材シートの裏面側の最下層に粘着剤層を設けるようする。   Moreover, when using the sheet | seat member with a liquid crystal in this invention as a label which sticks to a target object, an adhesive layer is provided in the lowest layer of the back surface side of said base material sheet.

また、本発明における液晶付きシート部材の製造方法においては、上記のような液晶付きシート部材を製造するにあたり、剥離性シートにコレステリック液晶組成物が含有された複数の液晶層を分離して形成する工程と、上記の液晶層を被覆するようにしてこの剥離性シートの面に前記液晶層に対する接着性が強い一方、上記の剥離性シートに対する接着性が弱い材料で形成された樹脂層を形成する工程と、基材シートの表面側に設けられた接着剤層に上記の剥離性シートに形成された樹脂層を接着させる工程と、上記の剥離性シートを上記の液晶層及び樹脂層から剥離させる工程とを行うようにする。 Further, in the method for producing a sheet member with a liquid crystal according to the present invention, in producing the sheet member with a liquid crystal as described above, a plurality of liquid crystal layers containing a cholesteric liquid crystal composition are separated and formed on a peelable sheet. And a resin layer formed of a material having a strong adhesiveness to the liquid crystal layer on the surface of the peelable sheet and a weak adhesiveness to the peelable sheet so as to cover the liquid crystal layer. A step, a step of bonding the resin layer formed on the peelable sheet to an adhesive layer provided on the surface side of the base sheet, and a peeling of the peelable sheet from the liquid crystal layer and the resin layer. Process.

本発明における液晶付きシート部材においては、基材シートの表面側に接着剤層を介して樹脂層を設けると共に、この樹脂層の表面側にコレステリック液晶組成物が含有された複数の液晶層を分離して設けるようにしたため、液晶層が基材シートの表面側に位置するようになり、上記の液晶層を基材シートの裏面側に設けた従来の液晶付きシート部材のように、基材シートによって液晶層における本来の特性の発現が損なわれるということがなく、円偏光フィルタを用いた識別等が適切に行えるようになる。   In the sheet member with a liquid crystal according to the present invention, a resin layer is provided on the surface side of the base sheet via an adhesive layer, and a plurality of liquid crystal layers containing a cholesteric liquid crystal composition are separated on the surface side of the resin layer. Since the liquid crystal layer is positioned on the surface side of the base sheet, the base sheet is like the conventional sheet member with liquid crystal provided with the liquid crystal layer on the back side of the base sheet. Thus, the original characteristics of the liquid crystal layer are not impaired, and identification using a circularly polarizing filter can be performed appropriately.

また、この液晶付きシート部材においては、上記の液晶層が樹脂層を介して接着剤層により基材シートに十分に接着されるようになり、液晶層が簡単に剥がれるのも防止されるようになる。   In the sheet member with liquid crystal, the liquid crystal layer is sufficiently adhered to the base sheet by the adhesive layer via the resin layer, and the liquid crystal layer is prevented from being easily peeled off. Become.

また、本発明においては、上記のような液晶付きシート部材を製造するにあたり、剥離性シートにコレステリック液晶組成物が含有された複数の液晶層を分離して形成する工程と、上記の液晶層を被覆するようにしてこの剥離性シートの面に樹脂層を形成する工程と、基材シートの表面側に設けられた接着剤層に上記の剥離性シートに形成された樹脂層を接着させる工程と、上記の剥離性シートを上記の液晶層及び樹脂層から剥離させる工程とを行うようにしたため、基材シート等の上に上記の液晶層を直接形成する従来技術の課題が解決されるようになる。すなわち、液晶層に凹凸が生じるのが抑制されると共に、液晶層に用いた上記のコレステリック液晶組成物の配向特性が低下するということもなく、色彩がまだらに現れたり、円偏光フィルタを用いた識別が困難になったりするのが防止される。   Further, in the present invention, in producing the sheet member with a liquid crystal as described above, a step of separating and forming a plurality of liquid crystal layers containing a cholesteric liquid crystal composition in a releasable sheet; A step of forming a resin layer on the surface of the peelable sheet so as to cover; a step of bonding the resin layer formed on the peelable sheet to an adhesive layer provided on the surface side of the base sheet; and In order to solve the problems of the prior art in which the liquid crystal layer is directly formed on the base sheet or the like, since the above-described peelable sheet is peeled off from the liquid crystal layer and the resin layer. Become. That is, the occurrence of unevenness in the liquid crystal layer is suppressed, and the cholesteric liquid crystal composition used in the liquid crystal layer does not deteriorate in the alignment characteristics, and the colors appear mottled or a circular polarizing filter is used. It is prevented that the identification becomes difficult.

また、本発明においては、上記のように剥離性シートにコレステリック液晶組成物が含有された複数の液晶層を分離して形成するようにしたため、基材シートの全面に液晶層を形成し、このように形成した液晶層に対してエッチング加工やレーザ加工等によりパターニングを行う従来の場合に比べて、その製造が容易に行えるようになると共に、液晶層の無駄も少なくなって、製造コストが低減される。   In the present invention, as described above, since the plurality of liquid crystal layers containing the cholesteric liquid crystal composition are separated and formed on the peelable sheet, a liquid crystal layer is formed on the entire surface of the base sheet. Compared to the conventional case where the liquid crystal layer thus formed is patterned by etching, laser processing, etc., it can be manufactured more easily, and the liquid crystal layer is less wasted and the manufacturing cost is reduced. Is done.

以下、この発明の実施形態に係る液晶付きシート部材及びその製造方法を添付図面に基づいて具体的に説明する。なお、この発明に係る液晶付きシート部材及びその製造方法は、特に下記の実施形態に示したものに限定されるものではなく、その要旨を変更しない範囲において適宜変更して実施できるものである。   Hereinafter, a sheet member with a liquid crystal and a manufacturing method thereof according to an embodiment of the present invention will be specifically described with reference to the accompanying drawings. In addition, the sheet member with a liquid crystal and the manufacturing method thereof according to the present invention are not particularly limited to those shown in the following embodiments, and can be appropriately changed and implemented within a range not changing the gist thereof.

この実施形態における液晶付きシート部材１０においては、図１に示すように、透光性の基材シート１１の裏面側に背景層１２を形成する一方、この基材シート１１の表面側に透光性の接着剤層１３を設け、表面側にコレステリック液晶組成物が含有された複数の液晶層１５が分離して設けられた透光性の樹脂層１４をこの接着剤層１３の表面側に接着させ、この樹脂層１４の表面に上記の液晶層１５の表面を覆うようにして透光性の表面保護層１６を設けている。   In the sheet member 10 with a liquid crystal in this embodiment, as shown in FIG. 1, the background layer 12 is formed on the back side of the translucent base sheet 11, while the translucent side is on the front side of the base sheet 11. A transparent adhesive layer 13 is provided, and a translucent resin layer 14 in which a plurality of liquid crystal layers 15 containing a cholesteric liquid crystal composition is separated on the surface side is adhered to the surface side of the adhesive layer 13. A light-transmitting surface protective layer 16 is provided on the surface of the resin layer 14 so as to cover the surface of the liquid crystal layer 15.

そして、このような液晶付きシート部材１０を製造するにあたっては、図２に示すように、上記の液晶層１５に対する剥離性が高い剥離性シート２１を用い、この剥離性シート２１にコレステリック液晶組成物が含有された複数の液晶層１５を分離して形成する。   And in manufacturing such a sheet member 10 with a liquid crystal, as shown in FIG. 2, a peelable sheet 21 having a high peelability with respect to the liquid crystal layer 15 is used, and a cholesteric liquid crystal composition is used for the peelable sheet 21. Are formed separately from each other.

ここで、上記の液晶層１５に用いるコレステリック液晶組成物としては、公知の螺旋構造のコレステリック相を示す材料、或いはネマチック相を示す化合物にキラル分子を添加して得られるコレステリック相と類似の螺旋構造を有するキラルネマチック相を示す材料を用いることができる（本願発明においては、キラルネマチック相も含めてコレステリック相という。）。   Here, as the cholesteric liquid crystal composition used for the liquid crystal layer 15, a helical structure similar to a cholesteric phase obtained by adding a chiral molecule to a material showing a cholesteric phase having a known helical structure or a compound showing a nematic phase. A material exhibiting a chiral nematic phase having the above can be used (in the present invention, including a chiral nematic phase is referred to as a cholesteric phase).

そして、このようなコレステリック液晶組成物を用いて液晶層１５を形成するにあたっては、コレステリック相を固定化させるように形成することが好ましく、例えば、両末端にアクリル基を導入させた液晶分子を含む液晶層形成用塗液を上記の剥離性シート２１に塗工し、これを加熱させてコレステリック相を形成し、さらにこれに紫外線を照射させて架橋させ、このコレステリック相を固定させるようにすることができる。このようにすると、温度等の環境条件が変化しても、コレステリック相は安定して存在するようになる。   In forming the liquid crystal layer 15 using such a cholesteric liquid crystal composition, the liquid crystal layer 15 is preferably formed so as to fix the cholesteric phase, and includes, for example, liquid crystal molecules in which acrylic groups are introduced at both ends. The liquid crystal layer-forming coating solution is applied to the above-described peelable sheet 21 and heated to form a cholesteric phase, which is further irradiated with ultraviolet rays to be crosslinked to fix the cholesteric phase. Can do. In this way, the cholesteric phase is stably present even when environmental conditions such as temperature change.

また、上記の液晶分子と一般に使用されるバインダーとを含む液晶層形成用塗液を剥離性シート２１に塗工し、これを加熱させてコレステリック相を形成した後、これを乾燥させて、バインダーによりコレステリック相を固定させるようにすることもできる。   In addition, a liquid crystal layer forming coating solution containing the above liquid crystal molecules and a commonly used binder is applied to the peelable sheet 21 and heated to form a cholesteric phase, and then dried to form a binder. Thus, the cholesteric phase can be fixed.

また、上記の液晶層形成用塗液は、溶剤系と非溶剤系の何れであってもよい。   The liquid crystal layer forming coating solution may be either solvent-based or non-solvent-based.

そして、溶剤系の液晶層形成用塗液においては、溶剤としてＭＥＫ，ＭＩＢＫ等のケトン類、トルエン、酢酸エチル等を用いることができ、また固形分濃度は、特に制限はないが、２５〜６７ｗｔ％の範囲であることが好ましい。これは、固形分濃度が２５ｗｔ％を下回ると、液晶層１５の端部を鮮明に形成することができなくなるおそれがあると共に、乾燥に要する時間が長くなる。一方、固形分濃度が６７％を超えると、塗液を加熱しないと固体が析出するおそれがある。そして、特に好ましい固形分濃度の範囲は５０〜６５ｗｔ％である。   In the solvent-based coating liquid for forming a liquid crystal layer, ketones such as MEK and MIBK, toluene, ethyl acetate and the like can be used as the solvent, and the solid content concentration is not particularly limited, but is 25 to 67 wt. % Is preferable. This is because if the solid content concentration is less than 25 wt%, the end portion of the liquid crystal layer 15 may not be formed clearly, and the time required for drying becomes longer. On the other hand, when the solid content concentration exceeds 67%, solids may be deposited unless the coating liquid is heated. And the range of especially preferable solid content concentration is 50 to 65 wt%.

また、非溶剤系の液晶層形成用塗液においては、コレステリック相を形成する最低温度以上、好ましくはコレステリック相を形成する温度領域の温度に加熱しながら塗工を行う。   In the non-solvent-based liquid crystal layer forming coating solution, the coating is performed while heating to a temperature not lower than the minimum temperature for forming a cholesteric phase, preferably in a temperature region for forming a cholesteric phase.

また、上記の溶剤系及び非溶剤系の何れの液晶層形成用塗液においても、コレステリック相の固定を行うため、コレステリック相を形成する温度範囲に保ったまま架橋等を行う。このようにすると、コレステリック相は、温度環境等が変わっても安定に維持される。   Further, in any of the solvent-based and non-solvent-based liquid crystal layer-forming coating solutions, the cholesteric phase is fixed, and thus crosslinking and the like are performed while maintaining the temperature range in which the cholesteric phase is formed. In this way, the cholesteric phase is stably maintained even when the temperature environment changes.

そして、上記のようにして剥離性シート２１にコレステリック液晶組成物が含有された複数の液晶層１５を分離して形成した後は、図３に示すように、液晶層１５を被覆するようにして、剥離性シート２１の面に透光性の樹脂層１４を形成する。   Then, after the plurality of liquid crystal layers 15 containing the cholesteric liquid crystal composition are separated and formed on the peelable sheet 21 as described above, the liquid crystal layer 15 is covered as shown in FIG. The translucent resin layer 14 is formed on the surface of the peelable sheet 21.

ここで、上記の樹脂層１４の材料としては、透明又は半透明であって、上記の液晶層１５に対する接着性が強い一方、上記の剥離性シート２１に対する接着性が弱い材料を用いるようにし、例えば、溶剤系やエマルジョン系のアクリル系樹脂や、紫外線硬化型のアクリル系樹脂等を用いることができる。   Here, as the material of the resin layer 14, a material that is transparent or translucent and has high adhesion to the liquid crystal layer 15, while having low adhesion to the peelable sheet 21, is used. For example, a solvent-based or emulsion-based acrylic resin, an ultraviolet curable acrylic resin, or the like can be used.

そして、上記のように裏面側に背景層１２が形成されると共に表面側に接着剤層１３が設けられた基材シート１１を用い、図４に示すように、上記の剥離性シート２１に形成された樹脂層１４を、基材シート１１の表面側に設けられた接着剤層１３に接着させた後、図５に示すように、上記の剥離性シート２１を液晶層１５及び樹脂層１４から剥離させるようにする。   Then, as shown in FIG. 4, the base sheet 11 having the background layer 12 formed on the back side and the adhesive layer 13 provided on the front side is formed on the peelable sheet 21 as described above. The adhered resin layer 14 is adhered to the adhesive layer 13 provided on the surface side of the base sheet 11, and then the peelable sheet 21 is separated from the liquid crystal layer 15 and the resin layer 14 as shown in FIG. 5. Try to peel.

ここで、上記の基材シート１１としては、その裏面側に形成した背景層１２の色彩が液晶層１５に有効に反映されるようにするため、透明又は半透明の透光性を有する材料で構成されたものを用いるようにし、例えば、一般に使用されているポリエチレンテレフタレート等の透明又は半透明の合成樹脂等を用いるようにする。   Here, as said base material sheet 11, in order to reflect the color of the background layer 12 formed in the back surface side effectively in the liquid-crystal layer 15, it is a transparent or translucent material which has translucency. For example, a transparent or translucent synthetic resin such as polyethylene terephthalate that is generally used is used.

また、上記の接着剤層１３の材料としては、透明又は半透明の透光性を有するものを用いるようにし、例えば、溶剤系やエマルジョン系のアクリル系接着剤、エステル系接着剤、エーテル系接着剤等を用いることができる。   Further, as the material of the adhesive layer 13, a transparent or translucent material having translucency is used, for example, a solvent-based or emulsion-based acrylic adhesive, an ester-based adhesive, an ether-based adhesive. An agent or the like can be used.

そして、上記の基材シート１１の裏面側における背景層１２は、基材シート１１の裏面側に適当な色彩のインキ等を印刷や塗工により形成することができる。ここで、この背景層１２は、上記の液晶層１５の光輝性等を際立たせるためのものであり、液晶層１５の光輝性等を際立たせる点からは、墨インキ等を用いて黒色の背景層１２を形成することが好ましい。   And the background layer 12 in the back surface side of said base material sheet 11 can form the ink etc. of a suitable color on the back surface side of the base material sheet 11 by printing or coating. Here, the background layer 12 is for making the above-mentioned glitter of the liquid crystal layer 15 stand out. From the standpoint of making the glitter of the liquid crystal layer 15 stand out, a black background using black ink or the like is used. Layer 12 is preferably formed.

また、この背景層１２の色彩によって、液晶層１５の目視による色調が変化するため、背景層１２を形成するインキの組成や色が重要である。例えば、背景層１２の色が黒のときは、液晶層１５がグリーンからブルーの光輝性を示し、背景層１２が赤のときは、液晶層１５がオレンジから紫の光輝性を示し、背景層１２が白に近い着色のときには、液晶層１５が乳白色やパール調の光輝性を示すようになる。そして、この背景層１２を２色以上で区分けして形成すると、液晶層１５の目視による色調が、背景層１２の色彩の変化に対応した彩り鮮やかな色調になる。   In addition, since the color tone of the liquid crystal layer 15 is changed by the color of the background layer 12, the composition and color of the ink forming the background layer 12 are important. For example, when the color of the background layer 12 is black, the liquid crystal layer 15 exhibits green to blue glitter, and when the background layer 12 is red, the liquid crystal layer 15 exhibits orange to purple glitter. When 12 is colored close to white, the liquid crystal layer 15 shows milky white or pearly luster. When the background layer 12 is formed by dividing it into two or more colors, the color tone of the liquid crystal layer 15 visually becomes a colorful tone corresponding to the color change of the background layer 12.

そして、上記のように剥離性シート２１を液晶層１５及び樹脂層１４から剥離させた後、上記の樹脂層１４の表面に、上記の液晶層１５を覆うようにして透光性の表面保護層１６を形成する。   Then, after the peelable sheet 21 is peeled from the liquid crystal layer 15 and the resin layer 14 as described above, a light-transmitting surface protective layer is formed on the surface of the resin layer 14 so as to cover the liquid crystal layer 15. 16 is formed.

ここで、上記の表面保護層１６の材料としては、上記の液晶層１５の特性を損なうことがなく、またこの液晶層１５を熱や衝撃等から保護するため、耐熱性や耐衝撃性に優れたものを用いることが好ましく、例えば、アクリル系樹脂、ウレタン系樹脂、エポキシ系樹脂、シリコーン系樹脂、ＥＶＡ系樹脂、ポリアミド系樹脂、ポリエステル系樹脂、ポリスチレン系樹脂、セルロース系樹脂、及びこれらの混合物などを用いることができる。   Here, the material of the surface protective layer 16 is excellent in heat resistance and impact resistance because it does not impair the characteristics of the liquid crystal layer 15 and protects the liquid crystal layer 15 from heat and impact. For example, acrylic resins, urethane resins, epoxy resins, silicone resins, EVA resins, polyamide resins, polyester resins, polystyrene resins, cellulose resins, and mixtures thereof Etc. can be used.

また、上記の液晶層１５を紫外線から保護するため、この表面保護層１６に紫外線吸収剤を添加させることが好ましく、例えば、ベンゾフェノン系、サリチレート系、ベンゾトリアゾール系、アクリロニトリル系等の各種紫外線吸収剤及びこれらの混合物等を用いることができる。   In order to protect the liquid crystal layer 15 from ultraviolet rays, it is preferable to add an ultraviolet absorber to the surface protective layer 16, for example, various ultraviolet absorbers such as benzophenone, salicylate, benzotriazole, and acrylonitrile. And a mixture thereof.

そして、この実施形態においては、液晶付きシート部材１０を上記のようにして製造したため、上記の液晶層１５に凹凸が生じるのが抑制されて、色彩がまだらに現れることがなく、優れた光輝性を有するようになると共に、液晶層１５に用いた上記のコレステリック液晶組成物の配向特性が低下するということもなく、円偏光フィルタを用いた識別が適切に行えるようになる。   And in this embodiment, since the sheet member 10 with a liquid crystal was manufactured as described above, the liquid crystal layer 15 was suppressed from being uneven, and the color did not appear mottled and had excellent glitter. In addition, the orientation characteristics of the cholesteric liquid crystal composition used for the liquid crystal layer 15 are not deteriorated, and the discrimination using the circularly polarizing filter can be performed appropriately.

なお、この実施形態の液晶付きシート部材１０に形成する上記の液晶層１５の平面形状は特に限定されず、文字、絵柄、模様等の様々な平面形状にすることができる。   In addition, the planar shape of the liquid crystal layer 15 formed on the liquid crystal sheet member 10 of this embodiment is not particularly limited, and can be various planar shapes such as characters, patterns, patterns, and the like.

そして、この実施形態の液晶付きシート部材１０において、上記の液晶層１５におけるコレステリック液晶組成物に右円偏光を反射するものを用い、例えば図６に示すように、このような液晶組成物を用いた液晶層１５を円形状に形成すると共に、上記の背景層１２を黒色に塗りつぶした場合において、この液晶層１５の部分を図７に示すような右円偏光フィルタ３１と左円偏光フィルタ３２とが設けられた円偏光フィルタ３０を用いて観察した。   In the sheet member with a liquid crystal 10 of this embodiment, the cholesteric liquid crystal composition in the liquid crystal layer 15 that reflects right circularly polarized light is used. For example, as shown in FIG. When the liquid crystal layer 15 is formed in a circular shape and the background layer 12 is painted black, the liquid crystal layer 15 is divided into a right circular polarizing filter 31 and a left circular polarizing filter 32 as shown in FIG. Observation was performed using a circular polarizing filter 30 provided with.

この結果、図８に示すように、円偏光フィルタ３０の右円偏光フィルタ３１の部分においては、液晶層１５に用いた上記のコレステリック液晶組成物により反射された右円偏光の光がこの右円偏光フィルタ３１を通して導かれ液晶層１５の平面形状が見える一方、左円偏光フィルタ３２の部分においては、上記のコレステリック液晶組成物により反射された右円偏光の光がカットされて、液晶層１５の平面形状が見えずに、背景層１２の黒色のみが見えるようになる。   As a result, as shown in FIG. 8, in the right circular polarizing filter 31 portion of the circular polarizing filter 30, the right circularly polarized light reflected by the cholesteric liquid crystal composition used for the liquid crystal layer 15 is the right circular circle. While the planar shape of the liquid crystal layer 15 is guided through the polarizing filter 31, the right circularly polarized light reflected by the cholesteric liquid crystal composition is cut in the left circular polarizing filter 32, and the liquid crystal layer 15 Only the black color of the background layer 12 can be seen without seeing the planar shape.

なお、この実施形態の液晶付きシート部材１０を対象物に接着させるラベルとして使用する場合には、例えば、図９に示すように、上記の背景層１２が形成された基材シート１１の裏面側に粘着剤層１７を設け、この粘着剤層１７に剥離紙２２を剥離可能に貼着させるようにする。   In addition, when using the sheet | seat member 10 with a liquid crystal of this embodiment as a label which adhere | attaches to a target object, as shown in FIG. 9, for example, the back surface side of the base material sheet 11 on which the background layer 12 is formed is shown. An adhesive layer 17 is provided on the adhesive layer 17, and the release paper 22 is detachably attached to the adhesive layer 17.

また、この実施形態の液晶付きシート部材１０においては、上記の背景層１２を基材シート１１の裏面側に設けるようにしたが、図１０に示すように、背景層１２を基材シート１１の表面側に設け、この背景層１２の上に接着剤層１３を設けるようにすることも可能である。なお、この場合には、上記の基材シート１１を透明又は半透明の透光性を有する材料で構成する必要はない。   Further, in the sheet member with a liquid crystal 10 of this embodiment, the background layer 12 is provided on the back surface side of the base sheet 11, but the background layer 12 is provided on the base sheet 11 as shown in FIG. It is also possible to provide the adhesive layer 13 on the background layer 12 on the surface side. In this case, the base sheet 11 does not need to be made of a transparent or translucent material having translucency.

また、この実施形態の液晶付きシート部材１０においては、背景層１２を特定の色彩に塗りつぶすようにして形成したが、図示していないが、この背景層１２を様々な模様や文字にすることも可能であり、さらにこのような背景層１２を設けないようにしたり、また上記の基材シート１１として、その表面に各種の表面処理や表面加工を行ったものを用いるようにすることも可能である。   Further, in the sheet member 10 with a liquid crystal according to this embodiment, the background layer 12 is formed so as to be painted in a specific color. However, although not illustrated, the background layer 12 may be formed in various patterns and characters. Further, it is possible not to provide such a background layer 12, or it is possible to use the base sheet 11 that has been subjected to various surface treatments or surface treatments on the surface thereof. is there.

また、この実施形態においては、上記の背景層１２を基材シート１１の表面側又は裏面側に直接形成するようにしたが、この背景層１２を接着剤層等の他の層を介して形成することも可能である。   In this embodiment, the background layer 12 is directly formed on the front surface side or the back surface side of the base sheet 11. However, the background layer 12 is formed via another layer such as an adhesive layer. It is also possible to do.

この発明の一実施形態に係る液晶付きシート部材を示した断面説明図である。It is a section explanatory view showing a sheet member with a liquid crystal concerning one embodiment of this invention. 上記の実施形態に係る液晶付きシート部材の製造において、剥離性シートに複数の液晶層を分離して形成した状態を示した断面説明図である。In manufacture of the sheet member with a liquid crystal concerning the above-mentioned embodiment, it is a section explanatory view showing the state where a plurality of liquid crystal layers were separated and formed in a releasable sheet. 図２に示すようにして形成した液晶層を被覆するようにして、剥離性シートの面に透光性の樹脂層を形成した状態を示した断面説明図である。FIG. 3 is a cross-sectional explanatory view showing a state in which a translucent resin layer is formed on the surface of a peelable sheet so as to cover the liquid crystal layer formed as shown in FIG. 2. 図３に示すようにして剥離性シートに形成した樹脂層を基材シートの表面側に設けられた接着剤層に接着させた状態を示した断面説明図である。It is sectional explanatory drawing which showed the state which made the resin layer formed in the peelable sheet as shown in FIG. 3 adhere to the adhesive bond layer provided in the surface side of the base material sheet. 図４に示すように樹脂層を基材シートの表面側に設けられた接着剤層に接着させた後、剥離性シートを液晶層及び樹脂層から剥離させた状態を示した断面説明図である。FIG. 5 is a cross-sectional explanatory view showing a state in which the peelable sheet is peeled off from the liquid crystal layer and the resin layer after the resin layer is bonded to the adhesive layer provided on the surface side of the base sheet as shown in FIG. 4. . 上記の実施形態に係る液晶付きシート部材において、液晶層を円形状に形成すると共に、背景層を黒色に塗りつぶした状態を示した概略平面図である。In the sheet member with a liquid crystal according to the above embodiment, the liquid crystal layer is formed in a circular shape, and the schematic plan view showing a state in which the background layer is painted black. 上記の実施形態に係る液晶付きシート部材の液晶層の部分を観察するのに用いた円偏光フィルタの平面図である。It is a top view of the circularly polarizing filter used in observing the part of the liquid crystal layer of the sheet member with a liquid crystal concerning the above-mentioned embodiment. 上記の実施形態に係る液晶付きシート部材の液晶層の部分を円偏光フィルタで観察した状態を示した概略平面図である。It is the schematic plan view which showed the state which observed the part of the liquid-crystal layer of the sheet | seat member with a liquid crystal which concerns on said embodiment with the circularly-polarizing filter. 上記の実施形態に係る液晶付きシート部材を対象物に接着させるラベルとして使用する例を示した断面説明図である。It is sectional explanatory drawing which showed the example used as a label which adhere | attaches the sheet | seat member with a liquid crystal which concerns on said embodiment to a target object. 上記の実施形態に係る液晶付きシート部材の変更例において、背景層を基材シート表面側に設けた例を示した断面説明図である。In the example of a change of the sheet member with a liquid crystal concerning the above-mentioned embodiment, it is a section explanatory view showing the example which provided the background layer in the substrate sheet surface side.

符号の説明Explanation of symbols

１０ 液晶付きシート部材
１１ 基材シート
１２ 背景層
１３ 接着剤層
１４ 樹脂層
１５ 液晶層
１６ 表面保護層
１７ 粘着剤層
２１ 剥離性シート
２２ 剥離紙
３０ 円偏光フィルタ
３１ 右円偏光フィルタ
３２ 左円偏光フィルタ DESCRIPTION OF SYMBOLS 10 Sheet member with liquid crystal 11 Base material sheet 12 Background layer 13 Adhesive layer 14 Resin layer 15 Liquid crystal layer 16 Surface protective layer 17 Adhesive layer 21 Release sheet 22 Release paper 30 Circular polarization filter 31 Right circular polarization filter 32 Left circular polarization filter

Claims (6)

基材シートの表面側に接着剤層を介して樹脂層が設けられると共に、この樹脂層の表面側にコレステリック液晶組成物が含有された複数の液晶層が分離して設けられている液晶付きシート部材において、
前記接着剤層および前記樹脂層が透光性材料で構成されると共に、前記基材シートの表面側に背景層が形成されていることを特徴とする液晶付きシート部材。 On the surface side of the substrate sheet through an adhesive layer with a resin layer is provided, the cholesteric liquid crystal composition with a liquid crystal plurality of liquid crystal layers that have been provided separately, which is contained in the surface side of the resin layer In the sheet member ,
A sheet member with a liquid crystal, wherein the adhesive layer and the resin layer are made of a translucent material, and a background layer is formed on the surface side of the base sheet. 基材シートの表面側に接着剤層を介して樹脂層が設けられると共に、この樹脂層の表面側にコレステリック液晶組成物が含有された複数の液晶層が分離して設けられている液晶付きシート部材において、
前記樹脂層が前記液晶層に対する接着性が強い材料で形成され、
前記基材シートと前記接着剤層と前記樹脂層とが透光性材料で構成されると共に、該基材シートの表面側または裏面側に背景層が形成されていることを特徴とする液晶付きシート部材。 On the surface side of the substrate sheet through an adhesive layer with a resin layer is provided, the cholesteric liquid crystal composition with a liquid crystal plurality of liquid crystal layers that have been provided separately, which is contained in the surface side of the resin layer In the sheet member ,
The resin layer is formed of a material having strong adhesion to the liquid crystal layer;
The substrate sheet, the adhesive layer, and the resin layer are made of a translucent material, and a background layer is formed on the front side or the back side of the base sheet. Sheet member. 請求項１または請求項２の何れかに記載の液晶付きシート部材において、前記樹脂層の表面側に設けられた前記液晶層を覆うようにして透光性の表面保護層が形成されていることを特徴とする液晶付きシート部材。 In the liquid crystal with the sheet member according to claim 1 or claim 2, the light-transmitting surface protective layer is formed so as to cover the liquid crystal layer provided on the surface side of the resin layer A sheet member with a liquid crystal. 請求項３に記載の液晶付きシート部材において、前記表面保護層が耐熱性樹脂で構成されると共に、該表面保護層に紫外線吸収剤が添加されていることを特徴とする液晶付きシート部材。 In the liquid crystal with the sheet member according to claim 3, the liquid crystal with a sheet member in which the surface protective layer with formed of heat-resistant resin, wherein the ultraviolet absorber is added to the surface protective layer. 請求項１〜請求項４の何れか１項に記載の液晶付きシート部材において、前記基材シートの裏面側の最下層に粘着剤層が形成されていることを特徴とする液晶付きシート部材。 The sheet member with a liquid crystal according to any one of claims 1 to 4 , wherein a pressure-sensitive adhesive layer is formed on the lowermost layer on the back surface side of the base sheet. 剥離性シートにコレステリック液晶組成物が含有された複数の液晶層を分離して形成する工程と、
前記液晶層を被覆するようにして前記剥離性シートの面に該液晶層に対する接着性が強い一方、該剥離性シートに対する接着性が弱い材料で形成された樹脂層を形成する工程と、
基材シートの表面側に設けられた接着剤層に前記剥離性シートに形成された前記樹脂層を接着させる工程と、
前記剥離性シートを前記液晶層及び前記樹脂層から剥離させる工程とを有することを特徴とする液晶付きシート部材の製造方法。 Separating and forming a plurality of liquid crystal layers containing a cholesteric liquid crystal composition in a peelable sheet ;
While a strong adhesion to the liquid crystal layer so as to cover the surface of the release sheet the liquid crystal layer, and forming a resin layer adhesive is formed by a weak material for the release sheet,
A step of bonding the resin layer formed on the release sheet to the adhesive layer provided on the surface side of the substrate sheet,
Method of manufacturing a liquid crystal with a sheet member, characterized in that it comprises a step of peeling off the release sheet from said liquid crystal layer and the resin layer.
JP2006277224A 2006-10-11 2006-10-11 Sheet member with liquid crystal and method for producing the same Active JP4693125B2 (en)