JP4689999B2 - Curable termite control composition - Google Patents
Curable termite control composition Download PDFInfo
- Publication number
- JP4689999B2 JP4689999B2 JP2004283341A JP2004283341A JP4689999B2 JP 4689999 B2 JP4689999 B2 JP 4689999B2 JP 2004283341 A JP2004283341 A JP 2004283341A JP 2004283341 A JP2004283341 A JP 2004283341A JP 4689999 B2 JP4689999 B2 JP 4689999B2
- Authority
- JP
- Japan
- Prior art keywords
- termite control
- curable
- control composition
- sand
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、木造建築物などに生ずるシロアリの被害を有効に防除できる硬化性シロアリ防除組成物及びそれを用いたシロアリ防除方法に関する。 The present invention relates to a curable termite control composition capable of effectively controlling termite damage occurring in a wooden building and the like, and a termite control method using the same.
シロアリは、木造建築物などの木造物や地下埋設されたケーブル類などを食害して、これらを破壊する。このようなシロアリによる木造建築物の食害を防除する方法として、特開昭60−230451号公報(特許文献1)には、建築物の床下地盤面を防蟻剤で処理したのち、水硬性セメントに減水剤、保水剤、骨材及び水を配合した自己流動性水硬性組成物を自然流動させて舗設する床下防湿工法が開示されている。この文献には、床下の湿気を低減することにより、シロアリの発生を低減すること、流動性の高い水硬性流動性組成物を用いることにより作業効率を高めることなどが記載されている。 Termites damage and destroy wooden structures such as wooden buildings and cables buried underground. Japanese Unexamined Patent Publication No. 60-230451 (Patent Document 1) discloses a method for controlling the damage caused by termites on a wooden building by treating the floor foundation board surface of the building with an anti-anticide and then hydraulic cement. Discloses an underfloor moisture-proof construction method in which a self-flowing hydraulic composition containing a water reducing agent, a water retention agent, an aggregate and water is naturally flowed and paved. This document describes reducing the generation of termites by reducing the moisture under the floor and increasing the working efficiency by using a hydraulic fluid composition having high fluidity.
しかし、水を配合した自己流動性水硬性組成物は、輸送性に欠けるだけでなく、硬化するため、取り扱い性に欠ける。さらに、床下地盤面を防蟻剤で処理しても、時間の経過とともに防蟻剤が流出又は拡散するため、防蟻剤の持続性に劣る。 However, a self-flowing hydraulic composition containing water not only lacks transportability but also cures and thus lacks handleability. Furthermore, even if the floor base board surface is treated with an ant-repellent agent, the ant-repellent agent flows out or diffuses over time, so that the sustainability of the ant-repellent agent is poor.
また、特開平8−154564号公報(特許文献2)には、床下の土壌部分に土間セメントモルタル又は土間コンクリートを施し、該土間セメントモルタル又は土間コンクリート上面に亜鉛引鋼板を敷設し、該亜鉛引鋼板の目地および外周を亜鉛溶射被膜で被覆する木質建築物のシロアリ食害防止方法が開示されている。 Japanese Patent Laid-Open No. 8-154564 (Patent Document 2) discloses that a soil cement mortar or soil concrete is applied to the soil portion under the floor, a galvanized steel sheet is laid on the soil cement mortar or the soil concrete top surface, The termite damage prevention method of the wooden building which coat | covers the joint and outer periphery of a steel plate with a zinc sprayed coating is disclosed.
しかし、この方法では、亜鉛鋼板をセメントモルタル又はコンクリート上に敷設するだけでなく、亜鉛引鋼板の目地および外周を亜鉛溶射被膜で被覆する必要があるため、作業効率が低下し、簡便かつ有効に食害を防止できない。さらに、亜鉛鋼板を必要とするため、適用域が制約を受け、景観を損なう場所には、適用できない。
従って、本発明の目的は、輸送性及び取扱い性に優れるだけでなく、作業効率を大幅に向上でき、シロアリを効果的に防除できる硬化性シロアリ防除組成物及びそれを用いたシロアリ防除方法を提供することにある。 Accordingly, an object of the present invention is to provide a curable termite control composition that can not only excel in transportability and handleability but also can greatly improve work efficiency and effectively control termites, and a termite control method using the same. There is to do.
本発明の別の目的は、水硬化性物質と組み合わせて、緻密なシロアリ防除層を形成して、シロアリを有効に防除できる硬化性シロアリ防除組成物及びそれを用いたシロアリ防除方法を提供することにある。 Another object of the present invention is to provide a curable termite control composition capable of effectively controlling termites by forming a dense termite control layer in combination with a water curable material, and a termite control method using the same. It is in.
本発明のさらに別の目的は、土成分(例えば、粘土、シルト)を含んでもシロアリ防除層を形成でき、公園や霊園における景観性を保持できる硬化性シロアリ防除組成物及びそれを用いたシロアリ防除方法を提供することにある。 Still another object of the present invention is to provide a termite control layer that can contain a soil component (eg, clay, silt), and to maintain a landscape in a park or a cemetery, and a termite control using the same. It is to provide a method.
本発明者らは、前記課題を達成するため鋭意検討した結果、水硬化性物質と土砂及び/又はシロアリ防除剤とで構成された粉粒状の硬化性組成物を用いると、輸送性及び取扱い性に優れるとともに、簡便にシロアリ防除層を形成でき、シロアリを有効且つ簡便に防除できることを見いだし、本発明を完成した。 As a result of intensive studies to achieve the above-mentioned problems, the present inventors have found that when a granular curable composition composed of a water-curable substance and earth and / or termite control agent is used, transportability and handling properties are improved. It was found that the termite control layer can be easily formed and the termites can be effectively and easily controlled, and the present invention has been completed.
すなわち、本発明の硬化性シロアリ防除組成物(以下、単に、防除組成物、硬化性組成物、組成物などということがある)は、粉粒状であり、水硬化性物質と、土砂および/又はシロアリ防除剤とで構成される。具体的には、本発明の硬化性シロアリ防除組成物は、以下の組成物(i)〜(iii)のいずれかである。 That is, the curable termite control composition of the present invention (hereinafter sometimes simply referred to as a control composition, a curable composition, a composition, etc.) is in the form of a powder, a water-curable substance, earth and sand, and / or Consists of termite control agents. Specifically, the curable termite control composition of the present invention is any one of the following compositions (i) to (iii).
(i)水硬化性物質と土砂とで構成された粉粒状の硬化性シロアリ防除組成物
(ii)水硬化性物質とシロアリ防除剤とで構成された粉粒状の硬化性シロアリ防除組成物
(iii)水硬化性物質と土砂とシロアリ防除剤とで構成された粉粒状の硬化性シロアリ防除組成物。
(I) A granular curable termite control composition composed of a water curable substance and earth and sand (ii) A granular curable termite control composition composed of a water curable substance and a termite control agent (iii) ) A granular curable termite control composition comprising a water curable substance, earth and sand, and a termite control agent.
前記硬化性シロアリ防除組成物は、通常、水を混和することなく調製されている。土砂は、礫成分と細粒成分とで構成してもよく、礫成分と細粒成分との割合(重量比)は、前者/後者=99.9/0.1〜5/95程度であってもよい。また、細粒成分は、砂成分と土成分とで構成してもよく、砂成分と土成分との割合(重量比)は、前者/後者=99/1〜10/90程度であってもよい。前記土砂は、無機系廃物の破砕物を含んでいてもよい。さらに、土砂と水硬化性物質との割合(重量比)は、前者/後者=95/5〜70/30程度であってもよい。 The curable termite control composition is usually prepared without mixing water. The earth and sand may be composed of a gravel component and a fine-grain component, and the ratio (weight ratio) of the gravel component and the fine-grain component is about the former / the latter = 99.9 / 0.1-5 / 95. May be. The fine-grain component may be composed of a sand component and a soil component, and the ratio (weight ratio) between the sand component and the soil component may be about the former / the latter = 99/1 to 10/90. Good. The earth and sand may contain crushed inorganic waste. Furthermore, the ratio (weight ratio) between the earth and sand and the water curable substance may be about the former / the latter = 95/5 to 70/30.
本発明の一態様では、シロアリ防除方法は、少なくとも、硬化性シロアリ防除組成物を被処理域に敷設する工程(A)で構成できる。さらに、前記シロアリ防除方法は、硬化性シロアリ防除組成物を被処理域に敷設する工程(A)と、敷設された硬化性シロアリ防除組成物に少なくとも水分を適用する工程(B)とで構成してもよい。前記工程(B)は、敷設された硬化性シロアリ防除組成物に少なくとも水を含む液体を適用する工程(B1)で構成してもよく、敷設された硬化性シロアリ防除組成物の上に少なくとも水を含むコンクリート又は土砂を敷設する工程(B2)で構成してもよい。なお、工程(B1)の液体(水性液体)又は工程(B2)のコンクリート又は土砂は、シロアリ防除剤を含んでいてもよい。 In one aspect of the present invention, the termite control method can be configured at least in the step (A) of laying a curable termite control composition in a treatment area. Further, the termite control method includes a step (A) of laying a curable termite control composition in a treatment area and a step (B) of applying at least moisture to the laid termite control composition. May be. The step (B) may comprise a step (B 1 ) of applying a liquid containing at least water to the laid termite control composition laid, and at least on the curable termite control composition laid. water may be formed in the step of laying the concrete or soil containing (B 2). The liquid (aqueous liquid) in the step (B 1 ) or the concrete or earth and sand in the step (B 2 ) may contain a termite control agent.
また、本発明の別の態様では、シロアリ防除方法は、硬化性シロアリ防除組成物と少なくとも水とを混和する工程(C)と、前記混和物を被処理域に敷設する工程(D)とで構成されている。なお、前記工程(C)では、硬化性シロアリ防除組成物と水とシロアリ防除剤とを混和してもよい。 In another aspect of the present invention, the termite control method includes a step (C) of mixing a curable termite control composition and at least water, and a step (D) of laying the mixture in a treatment area. It is configured. In the step (C), a curable termite control composition, water, and a termite control agent may be mixed.
本発明のシロアリ防除方法における被処理域は、例えば、シロアリの侵入域、生息域又は発生域を含んでもよい。 The treated area in the termite control method of the present invention may include, for example, a termite intrusion area, a habitat area, or a generation area.
本発明では、硬化性シロアリ防除組成物が粉粒状であるため、輸送性及び取扱い性に優れるだけでなく、作業効率を大幅に向上できる。また、水硬化性物質と組み合わせて、緻密なシロアリ防除層を形成でき、シロアリを有効に防除できる。さらに、本発明では、土成分(例えば、粘土、シルト)を含んでもシロアリ防除層を形成できるため、公園や霊園などの屋外での景観性を損なうことがない。さらに、土砂として無機系廃物の破砕物を使用することにより、資源の有効活用ができる。また、消臭成分を含むことにより、床下のかび臭を低減できる。また、調湿成分を含むことにより、湿度雰囲気によらずシロアリ防除性を向上できる。 In the present invention, since the curable termite control composition is granular, not only is it excellent in transportability and handleability, but also the working efficiency can be greatly improved. Further, in combination with a water curable substance, a dense termite control layer can be formed, and termites can be effectively controlled. Furthermore, in the present invention, the termite control layer can be formed even if soil components (for example, clay and silt) are included, so that the scenery in the outdoors such as a park or a cemetery is not impaired. Furthermore, resources can be effectively used by using crushed inorganic waste as earth and sand. Moreover, by containing a deodorizing component, the musty odor under the floor can be reduced. Moreover, the termite controllability can be improved regardless of the humidity atmosphere by including the humidity control component.
[硬化性シロアリ防除組成物]
硬化性シロアリ防除組成物は、粉粒状であり、水硬化性物質と、土砂および/又はシロアリ防除剤とで構成され、通常、水と混和することなく調製される。硬化性シロアリ防除組成物は、水硬化性物質と、土砂及びシロアリ防除剤のうち少なくとも一方の成分とを含んでいればよく、水硬化性物質と土砂とシロアリ防除剤とを含んでいてもよい。
[Curable termite control composition]
The curable termite control composition is in the form of a powder and is composed of a water curable substance and earth and sand and / or a termite control agent, and is usually prepared without being mixed with water. The curable termite control composition only needs to contain a water curable substance and at least one of earth and sand and a termite control agent, and may contain a water curable substance, earth and sand, and a termite control agent. .
(水硬化性物質)
水硬化性物質は、土砂および/又はシロアリ防除剤と組み合わせて粉粒状の硬化性組成物を形成できる限り特に制限されず、水硬化性物質としては、例えば、気硬性セメント[例えば、気硬性単味セメント(例えば、焼セッコウ、無水セッコウプラスターなどのセッコウ類;消石灰、ドロマイトプラスターなどの石灰類など)、気硬性混合セメント(例えば、マグネシアセメントなど)]、水硬性セメント[例えば、水硬性単味セメント(例えば、ポルトランドセメント、早強ポルトランドセメントなどのポルトランドセメント類;アルミナセメント、石灰アルミナセメントなどのアルミナセメント類など)、水硬性混合セメント(例えば、石灰スラグセメント、石灰火山灰セメントなどの石灰混合セメント類;高炉セメント、シリカセメント、ポゾランセメント、フライアッシュセメントなどの混合ポルトランドセメント類;高硫酸塩スラグセメント類など)など]などが挙げられる。これらの水硬化性物質は単独で又は二種以上組み合わせて使用できる。
(Water curable substance)
The water curable substance is not particularly limited as long as it can be combined with earth and sand and / or a termite control agent to form a granular curable composition. Examples of the water curable substance include a pneumatic cement [for example, a pneumatic cement simple substance. Taste cement (eg gypsum such as baked gypsum and anhydrous gypsum plaster; lime such as slaked lime and dolomite plaster), air-mixed cement (eg magnesia cement)], hydraulic cement [eg hydraulic plain Cement (for example, Portland cement such as Portland cement and early-strength Portland cement; alumina cement such as alumina cement and lime alumina cement), hydraulic mixed cement (for example, lime mixed cement such as lime slag cement and lime volcanic ash cement) , Blast furnace cement, silica cement , Pozzolanic cement, mixed Portland cement such as fly ash cement; and high sulfate slag cements)], and others. These water-curable materials can be used alone or in combination of two or more.
好ましい水硬化性物質には、例えば、ポルトランドセメントなどのポルトランドセメント類;高炉セメント、シリカセメント、ポゾランセメント、フライアッシュセメントなどの混合ポルトランドセメント類などが含まれる。 Preferred water curable materials include, for example, Portland cements such as Portland cement; mixed Portland cements such as blast furnace cement, silica cement, pozzolanic cement and fly ash cement.
(土砂)
本発明の硬化性シロアリ防除組成物において、土砂を含んでいる場合における土砂は、粉粒状の硬化性シロアリ防除組成物を形成できる限り特に制限されず、例えば、少なくとも礫成分を含んでいてもよい。
(Earth and sand)
In the curable termite control composition of the present invention, the earth and sand in the case of containing earth and sand is not particularly limited as long as it can form a granular curable termite control composition, for example, may contain at least a gravel component. .
礫成分は、粒径2mm以上の土又は岩石粒子であればよく、礫成分の粒径は、例えば、2〜8mm(9メッシュ〜2 1/2メッシュ程度)程度、好ましくは2〜5mm程度(9メッシュ〜3 1/2メッシュ程度)、さらに好ましくは2〜3.5mm程度(9メッシュ〜6メッシュ程度)であってもよい(メッシュ単位はタイラー表記による)。土砂中に礫成分が存在すると、シロアリが前記防除層に侵入又は通過するのを有効に防除できる。 The gravel component may be soil or rock particles having a particle size of 2 mm or more, and the particle size of the gravel component is, for example, about 2 to 8 mm (about 9 to 21/2 mesh), preferably about 2 to 5 mm ( 9 mesh to about 3 1/2 mesh), more preferably about 2 to 3.5 mm (about 9 mesh to 6 mesh) (the mesh unit is expressed by Tyler). If gravel components are present in the earth and sand, termites can be effectively prevented from entering or passing through the control layer.
さらに、本発明の土砂は、礫成分と細粒成分とを含んでいてもよい。細粒成分は、少なくとも砂成分を含めばよく、砂成分は、粒径0.2〜2mm程度の粗砂及び粒径0.02〜0.2mm程度の細砂から選択された少なくとも一種で構成される。また、細粒成分は、さらに土成分を含んでもよく、土成分は、粘土(例えば、粒径0.002mm以下、好ましくは0.00001〜0.002mm程度)及びシルト(例えば、粒径0.002〜0.02mm程度)から選択された少なくとも一種で構成される。土砂中に細粒成分(特に、土成分)が含まれると、公園や霊園などの屋外で硬化性シロアリ防除組成物が用いられても、自然の土の風合いを有するため、周囲の景観性を損なわない。 Furthermore, the earth and sand of the present invention may contain a gravel component and a fine particle component. The fine grain component may include at least a sand component, and the sand component is composed of at least one selected from coarse sand having a particle size of about 0.2 to 2 mm and fine sand having a particle size of about 0.02 to 0.2 mm. Is done. The fine grain component may further contain a soil component, and the soil component is made of clay (for example, a particle size of 0.002 mm or less, preferably about 0.00001 to 0.002 mm) and silt (for example, a particle size of 0.002 mm). At least one selected from 002 to 0.02 mm). If the earth and sand contain fine-grained components (especially soil components), even if curable termite control compositions are used outdoors in parks and cemeteries, they have a natural soil texture, No damage.
礫成分と細粒成分との割合(重量比)は、例えば、前者/後者=99.9/0.1〜5/95程度(例えば、99/1〜25/75程度)、好ましくは99/1〜50/50程度、さらに好ましくは95/5〜75/25程度であってもよい。 The ratio (weight ratio) between the gravel component and the fine-grain component is, for example, the former / the latter = about 99.9 / 0.1 to 5/95 (for example, about 99/1 to 25/75), preferably 99 / It may be about 1-50 / 50, more preferably about 95 / 5-75 / 25.
砂成分と土成分との割合(重量比)は、粉粒状の硬化性シロアリ防除組成物を構成できる限り特に制限されず、例えば、前者/後者=99/1〜10/90、好ましくは95/5〜50/50、さらに好ましくは90/10〜60/40程度の土砂であっても利用できる。本発明では、このような土成分含有率の高い土砂をそのまま利用できるため、従来骨材にするために必要であった洗い流し作業が不要である。そのため、安価で簡便に硬化性シロアリ防除組成物を提供できるとともに、洗い流し作業に伴う環境汚染なども生じない。 The ratio (weight ratio) between the sand component and the soil component is not particularly limited as long as it can constitute a granular curable termite control composition. For example, the former / the latter = 99/1 to 10/90, preferably 95 / Even earth and sand of about 5-50 / 50, more preferably about 90 / 10-60 / 40 can be used. In the present invention, since the earth and sand having such a high soil component content can be used as it is, the washing work which has been conventionally required to obtain an aggregate is unnecessary. Therefore, it is possible to provide a curable termite control composition at a low cost and in a simple manner, and there is no environmental contamination associated with a washing operation.
本発明の土砂は、粘土、シルト、砂成分の割合に基づき、例えば、砂土類(例えば、壌質砂土、砂土);壌土類(例えば、壌土、砂壌土、微砂質壌土);埴壌土類(例えば、埴壌土、砂質埴壌土、微砂質埴壌土);埴土類(例えば、軽埴土、砂質埴土、微砂質埴土、重埴土)に分類できる。なお、これらの土砂の区分は、国際土壌学会法の土性区分に従う。これらの土砂は、単独で又は二種以上組み合わせて使用できる。 The earth and sand of the present invention is based on the ratio of clay, silt and sand components, for example, sandy earth (for example, loamy sand, sandy earth); loam (for example, loam, sandy loam, fine sandy loam); It can be classified into loam (for example, loam soil, sandy loam soil, fine sandy loam soil); dredged soil (for example, light soil, sandy soil, fine sandy soil, heavy sand soil). The classification of these sediments follows the soil classification of the International Soil Society Law. These earth and sand can be used individually or in combination of 2 or more types.
具体的には、土砂としては、例えば、珪砂、川砂、海砂、浜砂、山砂などの砂類;土類[例えば、花崗岩の風化により形成した真砂土;赤土、黒土、しらすなどの火山灰土;河川などの堆積土など]などの他、各種園芸用土(例えば、赤玉土、鹿沼土、荒木田土、腐葉土、桐生砂など)、火成岩(安山岩、花崗岩、流紋岩など)、変成岩(珪岩、晶質石灰岩など)、堆積岩(泥岩、砂岩など)などが例示できる。なお、上記砂類は一般に砂土に分類され、真砂土は、一般に壌質砂土又は壌土類に分類され、火山灰土は、一般に埴壌土類又は埴土類に分類される。これらの土砂の中で、取扱い性およびコスト面から、壌質砂土(例えば、真砂土)などの砂土類;壌土、砂壌土、微砂質壌土などの壌土類(例えば、真砂土)などが好ましく用いられる。 Specifically, as earth and sand, for example, sand such as quartz sand, river sand, sea sand, beach sand and mountain sand; earth [e.g., pure sand earth formed by granite weathering; volcanic ash earth such as red earth, black earth and white sand Sedimentary soils such as rivers], various horticultural soils (eg, Akadama soil, Kanuma soil, Arakida soil, humus soil, Kiryu sand), igneous rocks (such as andesite, granite, rhyolite), metamorphic rocks (silica rock, Examples thereof include crystalline limestone) and sedimentary rock (mudstone, sandstone, etc.). The sands are generally classified into sandy soils, true sandy soils are generally classified as loamy sandy soils or loamy soils, and volcanic ash soils are generally classified as dredged soils or dredged soils. Among these sediments, sandy soils such as loamy sand (for example, pure sandy soil); loams such as loam, sandy loam, and fine sandy loam (for example, pure sandy soil) are available from the viewpoint of handling and cost. Preferably used.
本発明の土砂は、無機系廃物の破砕物で構成されていてもよく、無機系廃物の破砕物と、前記礫成分や細粒成分との組み合わせで構成されていてもよい。無機系廃物には、人工及び天然物の廃物が含まれる。人工物としては、例えば、人工の建造又は構造物(レンガ、瓦、コンクリート建材、モルタル建材、コンクリートブロック、コンクリート道路、アスファルト道路、窓ガラスなど)、日用品(植木鉢、コップ、陶器など)などが挙げられる。天然物としては、例えば、貝殻(アサリ、シジミ、ハマグリ、ホタテの貝殻など)、骨類(ウシ、ブタ、ニワトリの骨など)などが挙げられる。これらの廃物を土砂として利用すると、資源の有効利用となる。これら廃物は、所望の粒径に破砕されていればよく、例えば、目的に応じて、前記礫成分、砂成分、土成分の粒径と同様の粒径に破砕できる。これら破砕物の粒径は、簡便性などの点から、通常、10mm以下程度の範囲から選択でき、例えば、8mm以下(0.01〜8mm)、好ましくは5mm以下(0.05〜5mm)、さらに好ましくは3mm以下(0.1〜3mm)程度である。これらの破砕物は、単独で又は二種以上組み合わせて使用できる。 The earth and sand of the present invention may be composed of a crushed product of inorganic waste, or may be composed of a combination of a crushed product of inorganic waste and the gravel component or fine particle component. Inorganic waste includes man-made and natural waste. Examples of the artificial objects include artificial constructions or structures (brick, tile, concrete building material, mortar building material, concrete block, concrete road, asphalt road, window glass, etc.), daily necessities (flower pots, cups, pottery, etc.), and the like. It is done. Examples of natural products include shells (such as clams, swordfish, clams, scallop shells), bones (such as cattle, pigs, and chicken bones). If these wastes are used as earth and sand, it will be an effective use of resources. These wastes only have to be crushed to a desired particle size, and can be crushed to a particle size similar to that of the gravel component, sand component, and soil component, for example, depending on the purpose. The particle size of these crushed materials can usually be selected from a range of about 10 mm or less from the viewpoint of simplicity, for example, 8 mm or less (0.01 to 8 mm), preferably 5 mm or less (0.05 to 5 mm), More preferably, it is about 3 mm or less (0.1-3 mm). These crushed materials can be used alone or in combination of two or more.
硬化性シロアリ防除組成物において、土砂と水硬化性物質との割合(重量比)は、前記シロアリ防除組成物の硬化性などを損わない範囲で適当に選択でき、例えば、前者/後者=95/5〜70/30、好ましくは95/5〜85/15程度である。 In the curable termite control composition, the ratio (weight ratio) between the earth and sand and the water curable substance can be appropriately selected within a range that does not impair the curability of the termite control composition. For example, the former / the latter = 95 / 5 to 70/30, preferably about 95/5 to 85/15.
本発明では、均一なシロアリ防除層を形成するため、公知又は慣用の方法により土砂と水硬化性物質とが均一に混和(又は混合)した硬化性シロアリ防除組成物を調製するのが好ましい。 In the present invention, in order to form a uniform termite control layer, it is preferable to prepare a curable termite control composition in which earth and sand and a water curable substance are uniformly mixed (or mixed) by a known or conventional method.
(シロアリ防除剤)
本発明の硬化性シロアリ防除組成物は、シロアリ防除剤を含んでいてもよい。シロアリ防除剤を含むことにより、硬化性シロアリ防除組成物は、シロアリの侵入を有効に阻害できるシロアリ防除層を形成できるだけでなく、殺シロアリ性を有するシロアリ防除層を形成できる。シロアリ防除剤としては、例えば、合成系化合物[例えば、ホキシム、クロルピリホス、フェニトロチオン、ピリダフェンチオン、イソフェンホスなどの有機リン系化合物;バッサ、プロポキサーなどのカルバメート系化合物;シフルトリン、ペルメトリン、トラロメトリン、フェンパレレート、エトフェンプロックス、ビフェントリン、シフェノトリン、シラフルオフェン、ピレトリン、プラレトリンなどのピレスロイド系化合物;ニテンピラム、アセタミプリド、(E)−1−(2−クロロチアゾール−5−イルメチル)−3−メチル−2−ニトログアニジン(一般名:クロチアニジン)、N−アセチル−N−(2−クロロチアゾール−5−イル)メチル−N’−メチル−N”−ニトログアニジン、N−(2−クロロチアゾール−5−イル)メチル−N−メトキシカルボニル−N’−メチル−N”−ニトログアニジン、1−(6−クロロ−3−ピリジルメチル)−N−ニトロイミダゾリン−2−イリデンアミン(一般名:イミダクロプリド)、3−(2−クロロ−チアゾール−5−イルメチル)−5−[1,3,5]オキサジアジナン−4−イルインデン−N−ニトロアミン(一般名:チアメトキサム)などのネオニコチノイド系化合物;フィプロニールなどのフェニルピラゾール系化合物;クロルフェナピルなどのピロール系化合物;ベンスルタップなどのネライストキシン系化合物;ヒドラメチルノンなどのアミジノヒドラゾン系化合物;α−(α,α,α−トリフルオロ−m−トルオイル)−p−トルニトリル4−(p−トリフルオロメトキシフェニル)セミカルバゾンなどのセミカルバゾン系化合物;トリデカノール、ヘキサデカノールなどの高級アルコール類(例えば、C10-20アルキルアルコール類);オルトホウ酸などのホウ酸;ルフェヌロン、ヘキサフルムロン、ジフルベンズロン、フルフェノクスロンなどのキチン合成阻害剤;メトプレン、ハイドロプレンなどの幼若ホルモン様化合物など]、天然系化合物[例えば、ヒバ油、ヒバ中性油、デカン酸、オクタン酸などの脂肪酸;モリンガ属、マラー属をはじめとした植物又はその抽出物など(特開平3−41011号公報、特開平6−329514号公報、特開2001−158008号公報、特開2001−158009号公報、特開2001−172115号公報、特開2000−63220号公報、特開2001−170908号公報など)など]などが例示できる。これらのシロアリ防除剤は、単独で又は二種以上組み合わせて使用できる。シロアリに対する阻害性の観点から、これらのシロアリ防除剤のうち、ネオニコチノイド系化合物などのシロアリ防除剤が好ましく、特にクロチアニジンが好ましい。
(Termite control agent)
The curable termite control composition of the present invention may contain a termite control agent. By including the termite control agent, the curable termite control composition can not only form a termite control layer that can effectively inhibit the entry of termites, but can also form a termite control layer having termite killing properties. Examples of termite control agents include synthetic compounds [for example, organophosphorus compounds such as phoxime, chlorpyrifos, fenitrothion, pyridafenthion, and isofenphos; carbamate compounds such as bassa and propoxer; Pyrethroid compounds such as fenprox, bifenthrin, ciphenothrin, silafluorene, pyrethrin, praretrin; nitenpyram, acetamiprid, (E) -1- (2-chlorothiazol-5-ylmethyl) -3-methyl-2-nitroguanidine (general Name: clothianidin), N-acetyl-N- (2-chlorothiazol-5-yl) methyl-N′-methyl-N ″ -nitroguanidine, N- (2-chlorothiazol-5-yl) ) Methyl-N-methoxycarbonyl-N′-methyl-N ″ -nitroguanidine, 1- (6-chloro-3-pyridylmethyl) -N-nitroimidazoline-2-ylideneamine (generic name: imidacloprid), 3- ( 2-chloro-thiazol-5-ylmethyl) -5- [1,3,5] oxadiazinan-4-ylindene-N-nitroamine (generic name: thiamethoxam) and other neonicotinoid compounds; phenylpyrazole compounds such as fipronil Pyrrole compounds such as chlorfenapyr; nereistoxin compounds such as bensultap; amidinohydrazone compounds such as hydramethylnon; α- (α, α, α-trifluoro-m-toluoyl) -p-tolunitrile 4- ( p-trifluoromethoxyphenyl) semicarbazone Mikarubazon compounds; tridecanol, higher alcohols such as hexadecanol (e.g., C 10-20 alkyl alcohols); boric acids such as orthoboric acid, lufenuron, hexaflumuron, diflubenzuron, a chitin synthesis inhibitors such as flufenoxuron Young juvenile hormone-like compounds such as metoprene, hydroprene, etc.], natural compounds [eg fatty acids such as Hiba oil, Hiba neutral oil, decanoic acid, octanoic acid; plants such as Moringa spp. Extracts and the like (JP-A-3-41011, JP-A-6-329514, JP-A-2001-158008, JP-A-2001-158809, JP-A-2001-172115, JP-A-2000-63220) Gazette, JP 2001-170908 A, etc.)] Etc. can be exemplified. These termite control agents can be used alone or in combination of two or more. Of these termite control agents, termite control agents such as neonicotinoid compounds are preferable, and clothianidin is particularly preferable.
また、これらのシロアリ防除剤は、任意の剤形で用いることができ、例えば、溶液剤、水和剤、懸濁剤、分散剤、乳剤、油剤、ローションなどの液剤;粉剤、粒剤、マイクロカプセル剤、マイクロスフェア、フロアブル剤、発泡剤などの固形剤などの形態で用いることができる。また、水硬化性物質と組み合わせて用いるためには、耐アルカリ性に優れるシロアリ防除剤、例えば、マイクロカプセル剤などであってもよい。なお、マイクロカプセル剤は、固形剤の形態で用いてもよく、マイクロカプセル剤を溶媒中に分散させた分散剤又は懸濁剤などの液剤の形態で用いてもよい。 In addition, these termite control agents can be used in any dosage form, for example, liquid agents such as solutions, wettable powders, suspensions, dispersants, emulsions, oils, lotions, etc .; powders, granules, microbes It can be used in the form of solid agents such as capsules, microspheres, flowable agents, and foaming agents. Moreover, in order to use in combination with a water curable substance, the termite control agent which is excellent in alkali resistance, for example, a microcapsule agent etc., may be sufficient. The microcapsule may be used in the form of a solid agent, or may be used in the form of a liquid agent such as a dispersant or a suspension obtained by dispersing the microcapsule in a solvent.
シロアリ防除剤の割合は特に限定されず、例えば、水硬化性物質100重量部に対して、例えば、0.01〜1000重量部、好ましくは0.05〜300重量部、さらに好ましくは0.1〜200重量部程度であってもよい。また、硬化性シロアリ防除組成物が土砂と水硬化性物質とシロアリ防除剤とを含む場合、シロアリ防除剤は、土砂と水硬化性物質との総量100重量部に対して、例えば、0.001〜30重量部、好ましくは0.005〜20重量部、さらに好ましくは0.01〜10重量部程度であってもよい。 The ratio of the termite control agent is not particularly limited, and is, for example, 0.01 to 1000 parts by weight, preferably 0.05 to 300 parts by weight, and more preferably 0.1 to 100 parts by weight of the water curable substance. About 200 parts by weight may be used. Further, when the curable termite control composition includes earth and sand, a water curable substance, and a termite control agent, the termite control agent is, for example, 0.001 with respect to 100 parts by weight of the total amount of earth and sand and the water curable substance. ˜30 parts by weight, preferably 0.005 to 20 parts by weight, more preferably about 0.01 to 10 parts by weight.
(抗菌成分)
さらに、本発明の硬化性シロアリ防除組成物は、防腐防カビ剤(又は抗菌成分)などを含んでいてもよい。防腐防カビ剤(又は抗菌成分)としては、例えば、3−ブロモ−2,3−ジヨード−2−プロペニルエチルカーボネート、3−ヨード−2−プロピニルブチルカーバメート、2,3,3−トリヨードアリルアルコール、パラクロロフェニル−3−ヨードプロパルギルホルマールなどの有機ヨード系化合物;2−(4−チアゾリル)ベンズイミダゾール、2−チオシアノメチルチオベンゾチアゾールなどのベンズイミダゾールおよびベンゾチアゾール系化合物;1−(2−(2′,4′−ジクロロフェニル)−1,3−ジオキソラン−2−イルメチル)−1H−1,2,4−トリアゾール、1−(2−(2′,4′−ジクロロフェニル)−4−プロピル−1,3−ジオキソラン−2−イルメチル)−1H−1,2,4−トリアゾール、α−(2−(4−クロロフェニル)エチル)−α−(1,1−ジメチルエチル)−1H−1,2,4−トリアゾール−1−エタノールなどのトリアゾール系化合物;4−イソプロピルトロポロン(ヒノキチオール)、ホウ砂などの天然系化合物;抗菌性金属[例えば、銀化合物(例えば、金属銀;AgCl,AgF,AgF2などのハロゲン化銀;Ag2O,AgOなどの酸化物;Ag2Sなどの硫化物;Ag2SO4,Ag2CrO4,Ag3PO4,Ag2CO3,Ag2SiO3などの酸素酸塩など)、銅化合物、亜鉛化合物など]などが挙げられる。これらの防腐防カビ剤(又は抗菌成分)は、単独で又は二種以上組み合わせて使用できる。これらの防腐防カビ剤(又は抗菌成分)も、シロアリ防除剤で例示した各種液剤、各種固形剤などの任意の剤形で用いることができる。
(Antimicrobial component)
Furthermore, the curable termite control composition of the present invention may contain antiseptic and fungicidal agents (or antibacterial components) and the like. Examples of antiseptic and antifungal agents (or antibacterial components) include, for example, 3-bromo-2,3-diiodo-2-propenylethyl carbonate, 3-iodo-2-propynylbutylcarbamate, 2,3,3-triiodoallyl alcohol Organic iodine compounds such as parachlorophenyl-3-iodopropargyl formal; benzimidazole and benzothiazole compounds such as 2- (4-thiazolyl) benzimidazole and 2-thiocyanomethylthiobenzothiazole; 1- (2- (2 ', 4'-dichlorophenyl) -1,3-dioxolan-2-ylmethyl) -1H-1,2,4-triazole, 1- (2- (2', 4'-dichlorophenyl) -4-propyl-1, 3-dioxolan-2-ylmethyl) -1H-1,2,4-triazole, α- (2 Triazole compounds such as (4-chlorophenyl) ethyl) -α- (1,1-dimethylethyl) -1H-1,2,4-triazole-1-ethanol; 4-isopropyltropolone (hinokitiol), borax, etc. Natural compounds; antibacterial metals [for example, silver compounds (for example, metallic silver; silver halides such as AgCl, AgF and AgF 2 ; oxides such as Ag 2 O and AgO; sulfides such as Ag 2 S; Ag 2 SO 4 , Ag 2 CrO 4 , Ag 3 PO 4 , Ag 2 CO 3 , Ag 2 SiO 3 , etc.), copper compounds, zinc compounds, etc.]. These antiseptic / antifungal agents (or antibacterial components) can be used alone or in combination of two or more. These antiseptic and fungicidal agents (or antibacterial components) can also be used in any dosage form such as various liquid agents and various solid agents exemplified as termite control agents.
これらの防腐防カビ剤(又は抗菌成分)の割合は特に限定されず、例えば、水硬化性物質100重量部に対して、0.01〜1000重量部、好ましくは0.05〜300重量部、さらに好ましくは0.1〜200重量部程度であってもよい。また、硬化性シロアリ防除組成物が土砂と水硬化性物質とシロアリ防除剤とを含む場合、防腐防カビ剤(又は抗菌成分)は、土砂と水硬化性物質との総量100重量部に対して、0.001〜30重量部、好ましくは0.005〜20重量部、さらに好ましくは0.01〜10重量部程度であってもよい。 The proportion of these antiseptic / antifungal agents (or antibacterial components) is not particularly limited, and is, for example, 0.01 to 1000 parts by weight, preferably 0.05 to 300 parts by weight, with respect to 100 parts by weight of the water curable substance. More preferably, it may be about 0.1 to 200 parts by weight. Further, when the curable termite control composition includes earth and sand, a water curable substance, and a termite control agent, the antiseptic and fungicide (or antibacterial component) is based on 100 parts by weight of the total amount of the earth and sand and the water curable substance. 0.001 to 30 parts by weight, preferably 0.005 to 20 parts by weight, and more preferably about 0.01 to 10 parts by weight.
(消臭成分)
本発明の硬化性シロアリ防除組成物は、さらに、消臭成分などを含んでいてもよい。消臭成分としては、例えば、触媒(又は光触媒)又は吸着剤[例えば、金属酸化物(例えば、酸化マグネシウム、酸化チタン(TiO2)、酸化ジルコニウム、酸化バナジウム、酸化タングステン(WO3など)、酸化鉄、酸化銅、酸化銀、酸化亜鉛、酸化カドミウム、酸化インジウム、酸化スズなどの酸化物半導体)、金属硫化物(例えば、硫化カドミウム、硫化亜鉛などの硫化物半導体)、金属カルコゲナイト(CdSe、In2Se3、WSe3など)、金属無機酸塩(リン酸チタン、リン酸ジルコニウム、リン酸スズなどの金属リン酸塩など)などの金属化合物;炭素化合物(活性炭など);ケイ素化合物(シリカゲル、シリカ−アルミナなど);天然鉱物(ベントナイト、カオリンなど)など]などが挙げられる。
(Deodorant component)
The curable termite control composition of the present invention may further contain a deodorizing component and the like. Examples of the deodorant component include a catalyst (or photocatalyst) or an adsorbent [for example, metal oxide (for example, magnesium oxide, titanium oxide (TiO 2 ), zirconium oxide, vanadium oxide, tungsten oxide (WO 3 etc.), oxidation) Iron, copper oxide, silver oxide, zinc oxide, cadmium oxide, indium oxide, tin oxide and other oxide semiconductors), metal sulfides (eg, sulfide semiconductors such as cadmium sulfide and zinc sulfide), metal chalcogenites (CdSe, In 2 Se 3 , WSe 3 etc.), metal compounds such as metal inorganic acid salts (metal phosphates such as titanium phosphate, zirconium phosphate, tin phosphate etc.); carbon compounds (activated carbon etc.); silicon compounds (silica gel, Silica-alumina, etc.); natural minerals (bentonite, kaolin, etc.)] and the like.
消臭成分として、特開平8−229409号公報に記載の触媒組成物、すなわち、四価金属のリン酸塩と二価金属の水酸化物と光触媒とで構成された触媒組成物を使用してもよい。前記触媒組成物において、リン酸塩としては、周期表第4族又は第4B族金属リン酸塩、特に、リン酸チタン、リン酸ジルコニウム、リン酸スズなどが挙げられる。リン酸塩を構成するリン酸は、オルトリン酸、メタリン酸、ピロリン酸、三リン酸、四リン酸などであってもよい。リン酸塩は、単独で又は2種以上組み合わせてもよい。 As a deodorant component, a catalyst composition described in JP-A-8-229409, that is, a catalyst composition composed of a tetravalent metal phosphate, a divalent metal hydroxide and a photocatalyst is used. Also good. In the catalyst composition, examples of the phosphate include Group 4 or Group 4B metal phosphates, particularly titanium phosphate, zirconium phosphate, and tin phosphate. The phosphoric acid constituting the phosphate may be orthophosphoric acid, metaphosphoric acid, pyrophosphoric acid, triphosphoric acid, tetraphosphoric acid, or the like. The phosphates may be used alone or in combination of two or more.
また、二価金属の水酸化物は、特に限定されず、周期表第1B族金属(銅など)、周期表第2A族金属(マグネシウム、カルシウムなど)、周期表第2B族金属(亜鉛、カドミウムなど)、周期表第7A族金属(マンガンなど)、周期表第8族金属(鉄、ルテニウム、コバルト、ロジウム、ニッケル、パラジウムなど)などの典型金属又は遷移金属の水酸化物であってもよい。特に好ましい二価金属には、銅、亜鉛などが含まれ、鉄、コバルト、ニッケルも好ましい。二価金属の水酸化物は、単独で又は二種以上組み合わせてもよい。これらの二価金属の水酸化物は、通常、弱酸性ないし弱アルカリ性領域(pH4〜10程度)で水不溶性または難溶性である。なお、四価金属のリン酸塩と二価金属の水酸化物とで構成された組成物は、混合ゲルなどのように、共沈などにより複合化していてもよい。 Moreover, the hydroxide of a bivalent metal is not specifically limited, Periodic table 1B group metals (copper etc.), Periodic table 2A group metals (magnesium, calcium etc.), Periodic table 2B group metals (zinc, cadmium) Etc.), periodic table group 7A metals (such as manganese), periodic table group 8 metals (iron, ruthenium, cobalt, rhodium, nickel, palladium, etc.) or transition metal hydroxides. . Particularly preferred divalent metals include copper and zinc, and iron, cobalt and nickel are also preferred. Divalent metal hydroxides may be used alone or in combination of two or more. These divalent metal hydroxides are usually insoluble or hardly soluble in a weakly acidic to weakly alkaline region (about pH 4 to 10). The composition composed of a tetravalent metal phosphate and a divalent metal hydroxide may be combined by coprecipitation, such as a mixed gel.
光触媒としては、前記例示の光触媒、金属硫化物(又は硫化物半導体)、金属酸化物(又は酸化物半導体)などが挙げられる。好ましい光触媒は、酸化物半導体、例えば、酸化チタンなどが含まれる。光触媒は、単独で又は二種以上組み合わせてもよい。 Examples of the photocatalyst include the photocatalysts exemplified above, metal sulfides (or sulfide semiconductors), metal oxides (or oxide semiconductors), and the like. Preferred photocatalysts include oxide semiconductors such as titanium oxide. The photocatalysts may be used alone or in combination of two or more.
前記リン酸塩と前記水酸化物との割合は、例えば、金属原子比(二価金属/四価金属)=0.1〜10、好ましくは0.2〜7、さらに好ましくは0.2〜5程度である。また、光触媒の使用量は、前記リン酸塩および前記水酸化物の総量100重量部に対して1〜1000重量部、好ましくは10〜750重量部、さらに好ましくは20〜500重量部程度である。 The ratio of the phosphate to the hydroxide is, for example, metal atomic ratio (divalent metal / tetravalent metal) = 0.1 to 10, preferably 0.2 to 7, and more preferably 0.2 to About 5. Moreover, the usage-amount of a photocatalyst is 1-1000 weight part with respect to 100 weight part of total amounts of the said phosphate and the said hydroxide, Preferably it is 10-750 weight part, More preferably, it is about 20-500 weight part. .
なお、本発明では、前記触媒組成物は、さらに抗菌性金属成分(特に、前記銀化合物など)を含んでいてもよい。前記四価金属のリン酸塩と二価金属の水酸化物と光触媒と、前記例示の抗菌性金属成分(特に、前記銀化合物などの抗菌性金属成分)とを組み合わせることにより、効率よく消臭および抗菌できる。前記抗菌性金属成分の割合は、前記触媒組成物および前記抗菌性金属成分の総量に対して、金属換算(例えば、金属銀換算)で0.1〜10重量部%、好ましくは0.5〜8重量%、さらに好ましくは0.5〜7重量%程度であってもよい。 In the present invention, the catalyst composition may further contain an antibacterial metal component (in particular, the silver compound or the like). By combining the tetravalent metal phosphate, the divalent metal hydroxide, the photocatalyst, and the exemplified antibacterial metal component (particularly, the antibacterial metal component such as the silver compound), the deodorization can be efficiently performed. And antibacterial. The ratio of the antibacterial metal component is 0.1 to 10 parts by weight in terms of metal (for example, in terms of metal silver), preferably 0.5 to the total amount of the catalyst composition and the antibacterial metal component. It may be about 8% by weight, more preferably about 0.5 to 7% by weight.
このような触媒組成物は、消臭性に優れており、好適に用いることができる。なお、このような触媒組成物は、日本エンバイロケミカルズ(株)から「セブントールN−PC」、「セブントールN−FP」などとして入手可能である。 Such a catalyst composition has excellent deodorizing properties and can be suitably used. Such a catalyst composition is available as “Seven Toll N-PC”, “Seven Toll N-FP”, etc. from Nippon Enviro Chemicals.
なお、前記触媒組成物が、消臭性及び/又は抗菌性を有している場合、前記触媒組成物を、消臭成分及び/又は抗菌成分として機能させることができる。特に、前記触媒組成物が、消臭性及び/又は抗菌性を有している場合、硬化性シロアリ防除組成物の取扱い性を向上できる。また、活性炭などの炭素化合物、ケイ素化合物、天然鉱物などは、通常、消臭性だけでなく調湿性も有しているため、消臭成分及び/又は調湿成分として機能させることができる。そのため、取扱い性を向上できるとともに、湿度雰囲気によらずシロアリ防除性を向上できる。 In addition, when the said catalyst composition has deodorizing property and / or antibacterial property, the said catalyst composition can be functioned as a deodorizing component and / or an antibacterial component. In particular, when the catalyst composition has a deodorizing property and / or an antibacterial property, the handleability of the curable termite control composition can be improved. In addition, carbon compounds such as activated carbon, silicon compounds, natural minerals and the like usually have not only deodorizing properties but also humidity conditioning properties, and thus can function as deodorizing components and / or humidity conditioning components. Therefore, handling property can be improved and termite controllability can be improved regardless of the humidity atmosphere.
これらの消臭成分は、単独で又は二種以上組み合わせて使用できる。これらの消臭成分のうち、複数の性質を付与できる観点から、触媒組成物(特に抗菌性金属を含む触媒組成物)、炭素化合物(特に活性炭)などが好ましい。これらの消臭成分の割合は特に制限されず、例えば、水硬化性物質100重量部に対して、0.1〜1000重量部、好ましくは0.5〜300重量部、さらに好ましくは1〜200重量部程度であってもよい。 These deodorizing components can be used alone or in combination of two or more. Of these deodorant components, a catalyst composition (particularly a catalyst composition containing an antibacterial metal), a carbon compound (particularly activated carbon), and the like are preferable from the viewpoint of imparting a plurality of properties. The ratio of these deodorant components is not particularly limited, and is, for example, 0.1 to 1000 parts by weight, preferably 0.5 to 300 parts by weight, more preferably 1 to 200 parts per 100 parts by weight of the water-curable material. It may be about parts by weight.
(調湿成分)
本発明の硬化性シロアリ防除組成物は、さらに、調湿成分を含んでいてもよい。調湿成分としては、例えば、粘土鉱物[例えば、ゼオライト、セピオライト、アタパルジャイト(パリゴルスカイト)など]、合成ゼオライト、炭(木炭、竹炭など)などの調湿成分(又は調湿剤)などが例示できる。これらの調湿成分は、単独で又は二種以上組み合わせて使用できる。
(Humidity control component)
The curable termite control composition of the present invention may further contain a humidity control component. Examples of the humidity control component include clay minerals [for example, zeolite, sepiolite, attapulgite (palygorskite), etc.], synthetic zeolite, humidity control components (or humidity control agents) such as charcoal (charcoal, bamboo charcoal, etc.), and the like. These humidity control components can be used alone or in combination of two or more.
これらの調湿成分の割合は特に制限されず、例えば、水硬化性物質100重量部に対して、0.1〜1000重量部、好ましくは10〜700重量部、さらに好ましくは20〜600重量部程度であってもよい。 The ratio of these humidity control components is not particularly limited, and is, for example, 0.1 to 1000 parts by weight, preferably 10 to 700 parts by weight, and more preferably 20 to 600 parts by weight with respect to 100 parts by weight of the water curable substance. It may be a degree.
硬化性シロアリ防除組成物には、種々の添加剤を添加してもよい。添加剤には、ナフタレンスルホン酸ナトリウムなどの減水剤;塩化カルシウムなどの硬化促進剤;有機酸塩、無機酸塩などの凝結遅延剤;起泡剤;流動化剤;染料、顔料などの着色剤;補強材などが含まれる。さらに必要であれば、骨材(細骨材や粗骨材)を添加してもよい。 Various additives may be added to the curable termite control composition. Additives include water reducing agents such as sodium naphthalene sulfonate; curing accelerators such as calcium chloride; setting retarders such as organic acid salts and inorganic acid salts; foaming agents; fluidizing agents; colorants such as dyes and pigments. ; Reinforcing materials are included. If necessary, an aggregate (fine aggregate or coarse aggregate) may be added.
シロアリ防除剤、抗菌成分、消臭成分、各種添加剤などを、液状(又は液剤)の形態で用いる場合、例えば、前記液剤と適当な固体希釈剤(又は固体担体)とを予め混合した後乾燥させ、液剤と固体担体との混合物として用いることができる。また、硬化性シロアリ防除組成物が土砂を含む場合、液剤と土砂とを予め混合した後乾燥させ、液剤と土砂との混合物として用いてもよい。これらの混合物を、水硬化性物質、および必要に応じて加える土砂又は固体担体と、適宜混和して、本発明の硬化性シロアリ防除組成物を調製できる。 When using termite control agents, antibacterial components, deodorant components, various additives, etc. in liquid (or liquid) form, for example, the liquid agent and an appropriate solid diluent (or solid carrier) are mixed in advance and then dried. Can be used as a mixture of a liquid agent and a solid carrier. Moreover, when the curable termite control composition contains earth and sand, the liquid agent and earth and sand may be mixed in advance and then dried to be used as a mixture of the liquid agent and earth and sand. The curable termite-controlling composition of the present invention can be prepared by appropriately mixing these mixtures with a water curable substance and, if necessary, earth or sand or a solid carrier.
なお、前記固体担体は、液剤と混合可能な固体成分であれば特に制限されず、固体担体としては、例えば、前記調湿成分;滑石粉、ロウ石粉などのタルク類;微粉末クレイなどのクレイ類;流紋岩系天然ガラス、パーライトなどの軽石類;バーミキュライト、炭酸カルシウムなどの鉱物性粉粒物;硫黄粉末;尿素粉末;ピートモス、木粉、澱粉などの植物性粉粒物;農薬、園芸用製剤などに繁用される各種担体などが挙げられる。これらの固形希釈剤や担体は、増量材として使用される場合も多い。これらの固体担体は、単独または二種以上の混合物として用いることができる。 The solid carrier is not particularly limited as long as it is a solid component that can be mixed with a liquid agent. Examples of the solid carrier include the humidity control component; talc such as talc powder and wax stone powder; and clay such as fine powder clay. Class: Pumice such as rhyolite natural glass, perlite; Mineral powder such as vermiculite, calcium carbonate; Sulfur powder; Urea powder; Plant powder such as peat moss, wood powder, starch; Pesticide, Horticulture And various carriers frequently used in pharmaceutical preparations. These solid diluents and carriers are often used as extenders. These solid carriers can be used alone or as a mixture of two or more.
シロアリ防除剤、抗菌成分、消臭成分、各種添加剤などを、固体(又は固形剤)の形態で用いる場合、前記固形剤と水硬化性物質とを適宜混和して硬化性シロアリ防除組成物を調製してもよく、固形剤と土砂と水硬化性物質とを適宜混和して硬化性シロアリ防除組成物を調製してもよい。なお、これらの硬化性シロアリ防除組成物には、増量剤として前記固体担体を適宜利用できる。 When the termite control agent, antibacterial component, deodorant component, various additives, etc. are used in the form of a solid (or solid agent), the solid agent and a water curable substance are mixed appropriately to obtain a curable termite control composition. The curable termite control composition may be prepared by appropriately mixing a solid agent, earth and sand, and a water curable substance. In these curable termite control compositions, the solid carrier can be appropriately used as a bulking agent.
なお、均一なシロアリ防除層を形成するため、水硬化性物質と、土砂および/又はシロアリ防除剤と、必要に応じて添加される抗菌成分、調湿成分、および消臭成分などとは、硬化性シロアリ防除組成物において、均一に混合しているのが好ましい。 In order to form a uniform termite control layer, the water-curing substance, earth and sand and / or termite control agent, antibacterial component, humidity control component, and deodorant component added as necessary are cured. In the sex termite control composition, it is preferable to mix uniformly.
[シロアリ防除方法]
本発明のシロアリ防除方法は、硬化性シロアリ防除組成物を硬化させてシロアリ防除層を形成する限り、特に制限されない。本発明のシロアリ防除方法では、シロアリ防除層が硬化して一体化しているため、シロアリによる前記シロアリ防除層の破壊を防止できる。しかも、礫成分を含むため、シロアリの侵入又は通過を有効に防止する。したがって、シロアリ防除層の崩壊を防止しつつ、シロアリの被害を有効に阻止できる。
[Termite control method]
The termite control method of the present invention is not particularly limited as long as the curable termite control composition is cured to form a termite control layer. In the termite control method of the present invention, since the termite control layer is cured and integrated, the termite control layer can be prevented from being destroyed by the termites. In addition, since it contains gravel components, termite entry or passage is effectively prevented. Therefore, it is possible to effectively prevent termite damage while preventing the decay of the termite control layer.
本発明のシロアリ防除方法は、硬化性シロアリ防除組成物を被処理域に敷設する工程(A)で構成してもよい。敷設された硬化性シロアリ防除組成物は、水分により硬化し、シロアリ防除層を形成できる。水分は、被処理域由来の水分(例えば、被処理域の土壌中の水分、被処理域の空中の水分、好ましくは被処理域の土壌中の水分など)であってもよく、外部から適用された水分であってもよい。 The termite control method of the present invention may be constituted by a step (A) of laying a curable termite control composition in a treatment area. The laid termite control composition laid can be cured by moisture to form a termite control layer. The moisture may be moisture derived from the treated area (eg, moisture in the soil of the treated area, moisture in the air of the treated area, preferably moisture in the soil of the treated area), and is applied from the outside. It may also be moisture.
例えば、被処理域が、水分含有率(含水率)5〜200重量%程度、好ましくは7〜100重量%程度の土壌である場合、被処理域由来の水分により、硬化性シロアリ防除組成物を硬化でき、シロアリ防除層を形成できる。 For example, when the area to be treated is soil having a moisture content (moisture content) of about 5 to 200% by weight, preferably about 7 to 100% by weight, the curable termite control composition is obtained by the moisture derived from the area to be treated. It can be cured and a termite control layer can be formed.
敷設工程(A)では、例えば、散布、流下、掻取りなどの種々の方法で硬化性シロアリ防除組成物を敷設できる。硬化性シロアリ防除組成物は、粉粒状であるため、輸送性及び取扱い性に優れ、敷設が容易である。敷設においては、シロアリが進入する隙間が形成されるのを避けるため、硬化性シロアリ防除組成物は、被処理域に、一定の厚みで均一に(又は余すところなく)敷設されるのが好ましい。前記硬化性シロアリ防除組成物の敷設厚み(敷設厚)は、防除層を効果的に形成できる範囲で適当に選択でき、例えば、5〜200mm程度(例えば、10〜200mm程度)、好ましくは15〜100mm程度(例えば、20〜100mm程度)、さらに好ましくは30〜50mm程度であってもよく、通常10〜50mm(例えば、20〜50mm)程度であってもよい。 In the laying step (A), for example, the curable termite control composition can be laid by various methods such as spraying, flowing down, and scraping. Since the curable termite control composition is in the form of a powder, it is excellent in transportability and handleability and easy to lay. In laying, in order to avoid the formation of gaps for termites to enter, it is preferable that the curable termite control composition is laid uniformly (or without any excess) in the treatment area at a constant thickness. The laying thickness (laying thickness) of the curable termite control composition can be appropriately selected within a range in which the control layer can be effectively formed, for example, about 5 to 200 mm (for example, about 10 to 200 mm), preferably 15 to It may be about 100 mm (for example, about 20 to 100 mm), more preferably about 30 to 50 mm, and usually about 10 to 50 mm (for example, 20 to 50 mm).
また、シロアリ防除層がシロアリ防除剤を含む場合、前記シロアリ防除層に殺シロアリ性を付与できるため、硬化性シロアリ防除組成物の敷設厚み(敷設厚)は、シロアリ防除層がシロアリ防除剤を含まない場合よりも薄くできる。この場合、敷設厚は、例えば、5〜50mm、好ましくは10〜30mm程度であってもよい。 Moreover, when the termite control layer contains a termite control agent, the termite control layer can be provided with termite-killing properties, so the laying thickness (laying thickness) of the curable termite control composition includes the termite control layer. It can be thinner than if it is not. In this case, the laying thickness may be, for example, about 5 to 50 mm, preferably about 10 to 30 mm.
とくに敷設された硬化性シロアリ防除組成物が、被処理域由来の水分により硬化する場合、シロアリ防除層中にシロアリ防除剤が含まれると、簡便な作業で有効なシロアリ防除層を形成できる。 In particular, when the curable termite control composition laid is cured by moisture derived from the treated area, an effective termite control layer can be formed by a simple operation when a termite control agent is included in the termite control layer.
工程(B)では、敷設された硬化性シロアリ防除組成物に少なくとも水分を適用すればよく、前記水分の適用により、硬化性シロアリ防除組成物は硬化してシロアリ防除層を形成する。具体的には、前記工程(B)としては、例えば、敷設された硬化性シロアリ防除組成物に、少なくとも水を含む液体(水性液体)を適用する工程(B1)、敷設された硬化性シロアリ防除組成物の上に少なくとも水を含むコンクリート又は土砂を敷設する工程(B2)などが挙げられる。 In the step (B), at least moisture may be applied to the laid termite control composition laid, and by applying the moisture, the curable termite control composition is cured to form a termite control layer. Specifically, as the step (B), for example, a step (B 1 ) of applying a liquid (aqueous liquid) containing at least water to a laid termite control composition laid, a curable termite laid Examples include a step (B 2 ) of laying concrete or earth and sand containing at least water on the control composition.
工程(B1)では、敷設された硬化性シロアリ防除組成物に、少なくとも水を含む液体(例えば水)を適用すればよい。また、前記水性液体は、シロアリ防除剤を含んだ液体(例えば、シロアリ防除剤を含む水溶液又は水分散液)であってもよい。なお、シロアリ防除剤としては、前記硬化性シロアリ防除組成物の項で記載した化合物が例示でき、これらのシロアリ防除剤は、単独で又は二種以上組み合わせて使用できる。シロアリ防除剤の適用により、シロアリの侵入を有効に阻害できるだけでなく、シロアリ防除層に殺シロアリ性を付与できる。 In the step (B 1 ), a liquid (for example, water) containing at least water may be applied to the laid termite control composition laid. The aqueous liquid may be a liquid containing a termite control agent (for example, an aqueous solution or a water dispersion containing a termite control agent). In addition, as a termite control agent, the compound described in the term of the said curable termite control composition can be illustrated, and these termite control agents can be used individually or in combination of 2 or more types. By applying the termite control agent, not only the termite penetration can be effectively inhibited, but also the termite-killing property can be imparted to the termite control layer.
シロアリ防除剤の割合は特に限定されず、例えば、敷設された硬化性シロアリ防除組成物100重量部に対して、0.001〜30重量部程度、好ましくは0.005〜20重量部程度、さらに好ましくは0.01〜10重量部程度であってもよい。 The ratio of the termite control agent is not particularly limited, and is, for example, about 0.001 to 30 parts by weight, preferably about 0.005 to 20 parts by weight, with respect to 100 parts by weight of the laid termite control composition. Preferably, it may be about 0.01 to 10 parts by weight.
前記水性液体は、さらに前記硬化性シロアリ防除組成物の項で記載した抗菌成分などを含んでいてもよい。抗菌成分は、敷設された硬化性シロアリ防除組成物100重量部に対して、例えば、0.001〜30重量部程度、好ましくは0.005〜20重量部程度、さらに好ましくは0.01〜10重量部程度であってもよい。 The aqueous liquid may further contain the antibacterial component described in the section of the curable termite control composition. The antibacterial component is, for example, about 0.001 to 30 parts by weight, preferably about 0.005 to 20 parts by weight, more preferably 0.01 to 10 parts by weight based on 100 parts by weight of the curable termite control composition laid. It may be about parts by weight.
水性液体を適用(又は散水)する方法としては、シロアリ防除層を形成できる限り、前記液体を、1回で適用してもよく、複数回に分けて適用してもよい。敷設した硬化性シロアリ防除組成物の敷設形態を保持するために、液体は複数回(例えば、2〜5回、好ましくは2〜4回、さらに好ましくは2〜3回)に分けて適用するのが好ましい。特に、第1回目(又は初回)に、敷設した硬化性シロアリ防除組成物の表面を硬化できる程度に液体を適用するのが好ましい。第1回目の液体の適用量としては、硬化性シロアリ防除組成物中の水硬化性物質やシロアリ防除剤が流出しない量であればよく、例えば、0.1〜5L/m2、好ましくは0.5〜5L/m2、さらに好ましくは1〜2L/m2程度であってもよい。後続する適用工程(例えば、2回目、3回目、4回目など)では、敷設した硬化性シロアリ防除組成物全体を硬化できる程度に適宜液体を適用すればよい。例えば、後続する適用工程(例えば、2回目、3回目など)での液体の適用量は、総量として、初回の適用量の1.5〜30重量倍、好ましくは3〜20重量倍、さらに好ましくは5〜15重量倍程度であってもよい。 As a method of applying (or sprinkling) an aqueous liquid, the liquid may be applied once or may be applied in multiple times as long as a termite control layer can be formed. In order to maintain the laying form of the laid termite control composition, the liquid is applied in a plurality of times (for example, 2 to 5 times, preferably 2 to 4 times, more preferably 2 to 3 times). Is preferred. In particular, in the first time (or the first time), it is preferable to apply the liquid to such an extent that the surface of the curable termite control composition laid can be cured. The application amount of the first liquid may be an amount that does not allow the water curable substance or termite control agent in the curable termite control composition to flow out, for example, 0.1 to 5 L / m 2 , preferably 0. It may be about 5 to 5 L / m 2 , more preferably about 1 to 2 L / m 2 . In subsequent application steps (for example, the second time, the third time, the fourth time, etc.), the liquid may be appropriately applied to such an extent that the entire curable termite control composition laid can be cured. For example, the application amount of the liquid in the subsequent application process (for example, the second time, the third time, etc.) is 1.5 to 30 times by weight, preferably 3 to 20 times by weight, more preferably the initial application amount as a total amount. May be about 5 to 15 times by weight.
また、複数回に分けて液体を適用する場合、それぞれの適用工程において、同種又は異種の液体を適用してもよい。例えば、最初に水を適用し、それ以降の適用工程(例えば、2回目)でシロアリ防除剤を含む水溶液又は水分散液を適用してもよい。また、最初にシロアリ防除剤を含む水溶液又は水分散液を適用し、それ以降の適用工程(例えば、2回目)で水を適用してもよい。さらにまた、敷設した硬化性シロアリ防除組成物を硬化させた後に、シロアリ防除剤を含む水溶液又は水分散液を適用してもよい。例えば、複数回にわたり(例えば、1回、2回など)水を適用して硬化性シロアリ防除組成物を硬化させ、さらにシロアリ防除剤を含む水溶液又は水分散液を適用して、シロアリ防除層を形成してもよい。 Moreover, when applying a liquid in multiple times, you may apply the same kind or a different kind of liquid in each application process. For example, water may be applied first, and an aqueous solution or aqueous dispersion containing a termite control agent may be applied in the subsequent application process (for example, the second time). Alternatively, an aqueous solution or aqueous dispersion containing a termite control agent may be applied first, and water may be applied in subsequent application steps (for example, the second time). Furthermore, an aqueous solution or aqueous dispersion containing a termite control agent may be applied after the curable termite control composition is laid. For example, the termite control layer is formed by applying water multiple times (eg, once, twice, etc.) to cure the curable termite control composition, and further applying an aqueous solution or aqueous dispersion containing a termite control agent. It may be formed.
工程(B2)では、敷設された硬化性シロアリ防除組成物に、少なくとも水を含むコンクリート又は土砂を敷設すればよい。水を含むコンクリート又は土砂を敷設することにより、コンクリート又は土砂からの水分で、水硬化性物質を硬化でき、シロアリ防除層を形成できる。 In the step (B 2 ), concrete or soil containing at least water may be laid on the curable termite control composition that has been laid. By laying concrete or earth and sand containing water, the water-curable substance can be cured with moisture from the concrete or earth and sand, and a termite control layer can be formed.
コンクリートは、例えば、セメント成分、水、骨材(例えば、細骨材、粗骨材など)などで構成されている。なお、コンクリートを構成するセメント成分としては、前記硬化性シロアリ防除組成物の項において記載した水硬性物質などが例示できる。 Concrete is composed of, for example, a cement component, water, aggregate (for example, fine aggregate, coarse aggregate, etc.) and the like. In addition, as a cement component which comprises concrete, the hydraulic substance etc. which were described in the term of the said curable termite prevention composition can be illustrated.
コンクリート中の水の割合は、被処理域の水分含有量などに応じて、コンクリートの強度を保持できるとともに、滲出する水分で硬化性シロアリ防除組成物を硬化できる範囲から適当に選択でき、例えば、セメント100重量部に対して、10〜150重量部(例えば、30〜100重量部)、好ましくは20〜100重量部(例えば、40〜100重量部)程度であってもよい。 The proportion of water in the concrete can be appropriately selected from the range in which the strength of the concrete can be maintained according to the moisture content of the area to be treated, and the curable termite control composition can be cured with the exuding moisture. It may be about 10 to 150 parts by weight (for example, 30 to 100 parts by weight), preferably about 20 to 100 parts by weight (for example, 40 to 100 parts by weight) with respect to 100 parts by weight of cement.
土砂は、被処理域において掘り起こした土であってもよく、他所から持ち運んだ土砂(市販の土砂を含む)であってもよい。他所から持ち運んだ土砂としては、例えば、前記硬化性シロアリ防除組成物で例示した土砂が利用でき、砂土類、壌土類、埴壌土類、埴土類のいずれでもよい。また、土砂には礫成分が存在していてもよい。これらの土砂の中で、取扱い性及びコスト面から砂土類、壌土類、埴壌土類が好ましい。土砂を敷設することにより、周囲との景観を損なうことなく、シロアリ防除層を形成できる。 The earth and sand may be earth excavated in the treated area, or earth and sand carried from another place (including commercially available earth and sand). As the earth and sand carried from other places, for example, the earth and sand exemplified in the curable termite control composition can be used, and any of earth and sand, loam, loam and earth can be used. Moreover, gravel components may exist in the earth and sand. Among these earth and sand, sand earth, loam earth, and loam earth are preferable from the viewpoint of handling and cost. By laying earth and sand, a termite control layer can be formed without damaging the surrounding landscape.
土砂中の水の割合は、硬化性シロアリ防除組成物を硬化できる割合であれば、特に限定されず、例えば、土砂100重量部に対して、5〜200重量部、好ましくは7〜100重量部程度であってもよい。 The proportion of water in the earth and sand is not particularly limited as long as it can cure the curable termite control composition, and for example, 5 to 200 parts by weight, preferably 7 to 100 parts by weight with respect to 100 parts by weight of earth and sand. It may be a degree.
また、工程(B2)では、敷設された硬化性シロアリ防除組成物に、水とシロアリ防除剤とを含むコンクリート又は土砂を敷設してもよい。例えば、コンクリートが水とともにシロアリ防除剤を含む場合、シロアリ防除剤の割合は、セメント成分及び骨材の総量100重量部に対して、例えば、0.001〜30重量部、好ましくは0.005〜20重量部、さらに好ましくは0.01〜10重量部程度であってもよい。 In the step (B 2 ), concrete or earth and sand containing water and a termite control agent may be laid on the curable termite control composition. For example, when concrete contains a termite control agent together with water, the proportion of the termite control agent is, for example, 0.001 to 30 parts by weight, preferably 0.005 to 100 parts by weight of the total amount of the cement component and the aggregate. It may be about 20 parts by weight, more preferably about 0.01 to 10 parts by weight.
また、土砂が水とともにシロアリ防除剤を含む場合、シロアリ防除剤の割合は、土砂100重量部に対して、上記と同様の割合であってもよい。なお、シロアリ防除剤としては、前記硬化性シロアリ防除組成物の項で記載した化合物が例示でき、これらのシロアリ防除剤は、単独で又は二種以上組み合わせて使用できる。シロアリ防除剤の適用により、シロアリの侵入を有効に阻害できるだけでなく、シロアリ防除層(シロアリ防除剤を含む硬化コンクリート層又は土砂層を含む)に対して殺シロアリ性を付与できる。 Moreover, when earth and sand contain a termite control agent with water, the ratio similar to the above may be sufficient with respect to 100 weight part of earth and sand. In addition, as a termite control agent, the compound described in the term of the said curable termite control composition can be illustrated, and these termite control agents can be used individually or in combination of 2 or more types. By applying the termite control agent, not only the termite intrusion can be effectively inhibited, but also termite-killing properties can be imparted to the termite control layer (including the hardened concrete layer or earth and sand layer containing the termite control agent).
工程(B2)の敷設物には、さらに前記硬化性シロアリ防除組成物の項で記載した抗菌成分などを含んでいてもよい。抗菌成分は、セメント成分及び骨材の総量100重量部に対して、0.001〜30重量部程度、好ましくは0.005〜20重量部程度、さらに好ましくは0.01〜10重量部程度であってもよい。 The laid product in the step (B 2 ) may further contain the antibacterial component described in the section of the curable termite control composition. The antibacterial component is about 0.001 to 30 parts by weight, preferably about 0.005 to 20 parts by weight, more preferably about 0.01 to 10 parts by weight with respect to 100 parts by weight of the total amount of the cement component and the aggregate. There may be.
また、本発明のシロアリ防除方法は、硬化性シロアリ防除組成物と少なくとも水とを混和する工程(C)と、前記混和物を被処理域に敷設する工程(D)とで構成されてもよい。 Moreover, the termite control method of the present invention may be composed of a step (C) of mixing the curable termite control composition and at least water, and a step (D) of laying the mixture in the treatment area. .
工程(C)では、硬化性シロアリ防除組成物と少なくとも水とを混合機などで混和してもよく、硬化性シロアリ防除組成物と水と前記と同様の1種又は2種以上のシロアリ防除剤とを混和してもよい。シロアリ防除剤を混和することにより、シロアリの侵入を有効に阻害できるだけでなく、シロアリ防除層に殺シロアリ性を付与できる。 In the step (C), the curable termite control composition and at least water may be mixed with a mixer or the like, and the curable termite control composition, water and one or more termite control agents similar to those described above. And may be mixed. By mixing the termite control agent, not only the termite intrusion can be effectively inhibited, but also the termite-killing property can be imparted to the termite control layer.
硬化性シロアリ防除組成物と水との割合は、シロアリ防除層を形成できる限り特に限定されず、例えば、水の割合は、水硬化性物質100重量部に対して、20〜65重量部、好ましくは25〜60重量部、さらに好ましくは30〜55重量部程度であってもよい。 The ratio of the curable termite control composition and water is not particularly limited as long as the termite control layer can be formed. For example, the ratio of water is 20 to 65 parts by weight, preferably 100 parts by weight of the water curable substance. May be about 25 to 60 parts by weight, more preferably about 30 to 55 parts by weight.
工程(D)で、前記混和物は、公知又は慣用の方法で被処理域に敷設できる。シロアリ防除に有効なシロアリ防除層を形成するため、敷設された混和物の厚み(敷設厚)は、例えば、10〜200mm程度、好ましくは20〜100mm程度、さらに好ましくは30〜50mm程度であってもよい。 In the step (D), the admixture can be laid in the treatment area by a known or conventional method. In order to form a termite control layer effective for termite control, the thickness (laying thickness) of the laid mixture is, for example, about 10 to 200 mm, preferably about 20 to 100 mm, and more preferably about 30 to 50 mm. Also good.
また、硬化性シロアリ防除組成物がシロアリ防除剤を含む場合や、硬化性シロアリ防除組成物と水とシロアリ防除剤とを混和する場合、シロアリ防除層に殺シロアリ性を付与できるため、混和物の敷設厚は、シロアリ防除層がシロアリ防除剤を含まない場合よりも薄くできる。敷設厚は、前記工程(A)における硬化性シロアリ防除組成物の敷設厚と同程度であってもよい。 In addition, when the curable termite control composition contains a termite control agent, or when the curable termite control composition is mixed with water and a termite control agent, the termite control layer can be imparted with termiticide, The laying thickness can be made thinner than when the termite control layer does not contain a termite control agent. The laying thickness may be the same as the laying thickness of the curable termite control composition in the step (A).
前記工程(A)及び(D)において、被処理域は、シロアリによる食害を防止できるところであればよく、シロアリの侵入域、生息域又は発生域を含むことが多い。例えば、前記シロアリの侵入域、生息域又は発生域としては、木造物や地下埋設物(例えば、電線ケーブル、光ファイバーケーブルなどのケーブル類;水道管、ガス管などの配管類)などが存在する場所又はその近傍が挙げられる。具体的には、被処理域としては、宅地域(例えば、木造建築物などの建築物床下、前記建築物周辺、玄関又は玄関口など)、造園地域(例えば、庭(又は庭園)、公園、霊園(又は墓地)など)、地下埋設物周辺などが挙げられる。なお、建築物には、木造建築物以外に、材木置き場なども含まれ、床下には、前記建築物と地面とが接する部分も含まれる。 In the said process (A) and (D), the to-be-processed area should just be a place which can prevent the damage by a termite, and often includes the intrusion area, the habitat area, or the generation area of a termite. For example, the termite intrusion area, habitat area, or generation area is a place where wooden structures or underground buried objects (for example, cables such as electric cables and optical fiber cables; pipes such as water pipes and gas pipes) exist Or its vicinity is mentioned. Specifically, the area to be treated includes a residential area (for example, a floor under a building such as a wooden building, the periphery of the building, a front door, a front door, or the like), a landscape area (for example, a garden (or garden), a park, Cemetery (or cemetery)), surroundings of underground objects, etc. In addition to the wooden building, the building includes a timber storage place and the floor includes a portion where the building is in contact with the ground.
とくに、硬化性シロアリ防除組成物が土成分を含む場合、自然の土と同じ風合いを有するため、公園、庭(又は庭園)、霊園などで用いても景観を損なうことがない。そのため、例えば、庭や公園で用いる場合、周囲と調和しつつ、庭で用いられるウッドデッキ、ウッドバルコニー、木製ガーデニング用品などの木製品や、公園で用いられる木製遊具(例えば、木製アスレチック、木製滑り台、木製ブランコなど)、木製ベンチ、木製歩道などの木製品をシロアリの食害から有効に防ぐことができる。 In particular, when the curable termite control composition contains a soil component, it has the same texture as natural soil, so that it does not impair the landscape even when used in parks, gardens (or gardens), cemeteries and the like. Therefore, for example, when used in a garden or park, the wooden products used in the garden, such as wooden decks, wooden balconies and wooden gardening equipment, and wooden playground equipment used in the park (for example, wooden athletics, wooden slides, wooden) Wood products such as swings), wooden benches and wooden sidewalks can be effectively prevented from termite damage.
本発明は、木造建築物床下などにおいてシロアリ防除層を形成することにより、シロアリを防除するのに有用である。 The present invention is useful for controlling termites by forming a termite control layer under a wooden building floor or the like.
以下に、実施例に基づいて本発明をより詳細に説明するが、本発明はこれらの実施例によって限定されるものではない。 Hereinafter, the present invention will be described in more detail based on examples, but the present invention is not limited to these examples.
(硬化性シロアリ防除組成物の調製)
硬化性シロアリ防除組成物(A−1)
乾燥真砂土[礫成分(粒径2〜5mm)の割合12.6重量%、砂成分の割合71.8重量%、土成分の割合15.6重量%]90重量部と、高炉セメント10重量部(太平洋セメント(株)製、高炉セメントB種)とを混合機を用いて混合し、前記真砂土と高炉セメントとが均一に分散した硬化性シロアリ防除組成物(A−1)を得た。
(Preparation of curable termite control composition)
Curable termite control composition (A-1)
90 parts by weight of dry sandy sand [the proportion of gravel components (particle size 2-5 mm) 12.6 wt%, the proportion of sand components 71.8 wt%, the proportion of soil components 15.6 wt%], and 10 wt. Part (produced by Taiheiyo Cement Co., Ltd., type B blast furnace cement) was mixed using a mixer to obtain a curable termite control composition (A-1) in which the sand and blast furnace cement were uniformly dispersed. .
硬化性シロアリ防除組成物(B−1)
乾燥真砂土[礫成分(粒径2〜5mm)の割合12.6重量%、砂成分の割合71.8重量%、土成分の割合15.6重量%]100重量部に対して、特開2000−247821号公報の実施例5で作製したシロアリ防除剤(有効成分クロチアニジン、マイクロカプセル剤;以下シロアリ防除剤Tと称す)を7.5重量倍で水により希釈したものを10重量部加え、混合機を用いて混合し、前記真砂土とシロアリ防除剤とが均一に分散した混合物を作製し、その後、前記混合物を乾燥した。次に、乾燥した混合物と、高炉セメント10重量部(太平洋セメント(株)製、高炉セメントB種)とを混合機を用いて混合し、前記真砂土と高炉セメントとシロアリ防除剤とが均一に分散した硬化性シロアリ防除組成物(B−1)を得た。
Curable termite control composition (B-1)
With respect to 100 parts by weight of dry pure sand [a gravel component (particle size 2 to 5 mm) ratio 12.6 wt%, a sand component ratio 71.8 wt%, a soil component ratio 15.6 wt%] 10 parts by weight of a termite control agent (active ingredient clothianidin, microcapsule agent; hereinafter referred to as termite control agent T) prepared in Example 5 of 2000-247821 diluted with water at 7.5 times by weight, The mixture was mixed using a mixer to prepare a mixture in which the true sand soil and termite control agent were uniformly dispersed, and then the mixture was dried. Next, the dried mixture and 10 parts by weight of blast furnace cement (manufactured by Taiheiyo Cement Co., Ltd., blast furnace cement B type) are mixed using a mixer, so that the sand sand, blast furnace cement, and termite control agent are evenly mixed. A dispersed curable termite control composition (B-1) was obtained.
硬化性シロアリ防除組成物(B−2)
シロアリ防除剤Tの7.5重量倍水希釈物に代えて、シロアリ防除剤「バックトップMC」(有効成分バッサ、住友化学(株)製)の8重量倍水希釈物を用いる以外は、前記硬化性シロアリ防除組成物(B−1)と同様にして、硬化性シロアリ防除組成物(B−2)を調製した。
Curable termite control composition (B-2)
Instead of using a 7.5 weight-fold water dilution of the termite control agent T, the termite control agent “Backtop MC” (active ingredient Bassa, manufactured by Sumitomo Chemical Co., Ltd.) was used except that an 8 weight-fold water dilution was used. A curable termite control composition (B-2) was prepared in the same manner as the curable termite control composition (B-1).
硬化性シロアリ防除組成物(B−3)
シロアリ防除剤Tの7.5重量倍水希釈物に代えて、シロアリ防除剤「グレネードMC」(有効成分フィプロニール,プラレトリン、住友化学(株)製)の15重量倍水希釈物を用いる以外は、前記硬化性シロアリ防除組成物(B−1)と同様にして、硬化性シロアリ防除組成物(B−3)を調製した。
Curable termite control composition (B-3)
Instead of using a 7.5-fold water dilution of the termite control agent T, a 15-fold water dilution of the termite control agent “Grenade MC” (active ingredient fipronil, praretrin, manufactured by Sumitomo Chemical Co., Ltd.) was used. The curable termite control composition (B-3) was prepared in the same manner as the curable termite control composition (B-1).
硬化性シロアリ防除組成物(B−4)
シロアリ防除剤Tの7.5重量倍水希釈物に代えて、シロアリ防除剤「ララップMC」(有効成分シフェノトリン、住友化学(株)製)の10重量倍水希釈物を用いる以外は、前記硬化性シロアリ防除組成物(B−1)と同様にして、硬化性シロアリ防除組成物(B−4)を調製した。
Curable termite control composition (B-4)
Except for using a 10-fold water dilution of the termite-controlling agent “Larup MC” (active ingredient ciphenothrin, manufactured by Sumitomo Chemical Co., Ltd.) instead of the 7.5-fold water dilution of the termite control agent T, A curable termite control composition (B-4) was prepared in the same manner as the curable termite control composition (B-1).
硬化性シロアリ防除組成物(B−5)
シロアリ防除剤Tの7.5重量倍水希釈物に代えて、シロアリ防除剤「ステルスSC」(有効成分クロルフェナピル、BASFアグロ(株)製)の20重量倍水希釈物を用いる以外は、前記硬化性シロアリ防除組成物(B−1)と同様にして、硬化性シロアリ防除組成物(B−5)を調製した。
Curable termite control composition (B-5)
The above-mentioned curing is performed except that a 20-fold water dilution of the termite-controlling agent “Stealth SC” (active ingredient chlorfenapyr, manufactured by BASF Agro Co., Ltd.) is used instead of the 7.5-fold water dilution of the termite control agent T. The curable termite control composition (B-5) was prepared in the same manner as the sexual termite control composition (B-1).
硬化性シロアリ防除組成物(B−6)
シロアリ防除剤Tの7.5重量倍水希釈物に代えて、シロアリ防除剤「アリデン乳剤−E」(有効成分エトフェンプロックス、三共ライフテック(株)製)の4重量倍水希釈物を用いる以外は、前記硬化性シロアリ防除組成物(B−1)と同様にして、硬化性シロアリ防除組成物(B−6)を調製した。
Curable termite control composition (B-6)
Instead of the 7.5-fold water dilution of the termite control agent T, a 4-fold water dilution of the termite control agent “Ariden Emulsion-E” (active ingredient etofenprox, Sankyo Lifetech Co., Ltd.) is used. Except for the above, a curable termite control composition (B-6) was prepared in the same manner as the curable termite control composition (B-1).
硬化性シロアリ防除組成物(B−7)
シロアリ防除剤Tの7.5重量倍水希釈物に代えて、シロアリ防除剤「シントー天然ピレトリンMC」(有効成分ピレトリン、シントーファイン(株)製)の10重量倍水希釈物を用いる以外は、前記硬化性シロアリ防除組成物(B−1)と同様にして、硬化性シロアリ防除組成物(B−7)を調製した。
Curable termite control composition (B-7)
Instead of using a 7.5 weight-fold water dilution of the termite-controlling agent T, a 10-fold water dilution of the termite-controlling agent “Sinto natural pyrethrin MC” (active ingredient pyrethrin, manufactured by Shinto Fine Co., Ltd.) The curable termite control composition (B-7) was prepared in the same manner as the curable termite control composition (B-1).
硬化性シロアリ防除組成物(B−8)
シロアリ防除剤Tの7.5重量倍水希釈物に代えて、シロアリ防除剤「シロネン乳剤」(有効成分シラフルオフェン、大日本除虫菊(株)製)の5重量倍水希釈物を用いる以外は、前記硬化性シロアリ防除組成物(B−1)と同様にして、硬化性シロアリ防除組成物(B−8)を調製した。
Curable termite control composition (B-8)
In place of the 7.5 weight-fold water dilution of the termite control agent T, except that the 5 weight-fold water dilution of the termite control agent “silonene emulsion” (active ingredient silafluophene, manufactured by Dainippon Insect Chrysanthemum Co., Ltd.) is used. In the same manner as the curable termite control composition (B-1), a curable termite control composition (B-8) was prepared.
硬化性シロアリ防除組成物(B−9)
シロアリ防除剤Tの7.5重量倍水希釈物に代えて、シロアリ防除剤「アリピレス乳剤」(有効成分ビフェントリン、日本農薬(株)製)の10重量倍水希釈物を用いる以外は、前記硬化性シロアリ防除組成物(B−1)と同様にして、硬化性シロアリ防除組成物(B−9)を調製した。
Curable termite control composition (B-9)
In place of the 7.5 weight-fold water dilution of the termite control agent T, the above-mentioned curing was performed except that a 10-fold water dilution of the termite control agent “Aripyres emulsion” (active ingredient bifenthrin, manufactured by Nippon Agricultural Chemicals Co., Ltd.) was used. The curable termite control composition (B-9) was prepared in the same manner as the sexual termite control composition (B-1).
硬化性シロアリ防除組成物(B−10)
シロアリ防除剤Tの7.5重量倍水希釈物に代えて、シロアリ防除剤「ハチクサンFL」(有効成分イミダクロプリド、バイエルクロップサイエンス(株)製)の15重量倍水希釈物を用いる以外は、前記硬化性シロアリ防除組成物(B−1)と同様にして、硬化性シロアリ防除組成物(B−10)を調製した。
Curable termite control composition (B-10)
Except for using a 15-fold water dilution of the termite-controlling agent “Hachikusan FL” (active ingredient imidacloprid, manufactured by Bayer Crop Science Co., Ltd.) instead of the 7.5-fold water dilution of the termite-controlling agent T, A curable termite control composition (B-10) was prepared in the same manner as the curable termite control composition (B-1).
硬化性シロアリ防除組成物(B−11)
シロアリ防除剤Tの7.5重量倍水希釈物に代えて、ペルメトリンの5重量%メタノール溶液を用いる以外は、前記硬化性シロアリ防除組成物(B−1)と同様にして、硬化性シロアリ防除組成物(B−11)を調製した。
Curable termite control composition (B-11)
The curable termite control was carried out in the same manner as the curable termite control composition (B-1) except that a 5 wt% methanol solution of permethrin was used instead of the 7.5 weight-fold water dilution of the termite control agent T. A composition (B-11) was prepared.
硬化性シロアリ防除組成物(C−1)
シロアリ防除剤Tの7.5重量倍水希釈物10重量部に代えて、ヒノキチオール(大阪有機化学工業(株)製)の5重量%メタノール溶液20重量部を用いる以外は、前記硬化性シロアリ防除組成物(B−1)と同様にして、硬化性シロアリ防除組成物(C−1)を調製した。
Curable termite control composition (C-1)
The curable termite control is used except that 20 parts by weight of a 5% by weight methanol solution of hinokitiol (manufactured by Osaka Organic Chemical Industry Co., Ltd.) is used instead of 10 parts by weight of a 7.5 weight-fold water dilution of the termite control agent T. In the same manner as in the composition (B-1), a curable termite control composition (C-1) was prepared.
硬化性シロアリ防除組成物(BS−1)
乾燥真砂土[礫成分(粒径2〜5mm)の割合12.6重量%、砂成分の割合71.8重量%、土成分の割合15.6重量%]100重量部に対してシロアリ防除剤「コロニーバスター」(有効成分α−(α,α,α−トリフルオロ−m−トルオイル)−p−トルニトリル4−(p−トリフルオロメトキシフェニル)セミカルバゾン、日本農薬(株)製)を10重量部加え、混合機を用いて混合し、前記真砂土とシロアリ防除剤とが均一に分散した混合物を作製した。次に、前記混合物と、高炉セメント10重量部(太平洋セメント(株)製、高炉セメントB種)とを混合機を用いて混合し、前記真砂土と高炉セメントとシロアリ防除剤とが均一に分散した硬化性シロアリ防除組成物(BS−1)を得た。
Curable termite control composition (BS-1)
Termite control agent with respect to 100 parts by weight of dry pure sand [a gravel component (particle size 2 to 5 mm) ratio 12.6 wt%, sand component ratio 71.8 wt%, soil component ratio 15.6 wt%] 10 parts by weight of “colony buster” (active ingredient α- (α, α, α-trifluoro-m-toluoyl) -p-tolunitrile 4- (p-trifluoromethoxyphenyl) semicarbazone, manufactured by Nippon Agricultural Chemicals Co., Ltd.) In addition, the mixture was mixed using a mixer to prepare a mixture in which the sand sand and termite control agent were uniformly dispersed. Next, the mixture and 10 parts by weight of blast furnace cement (produced by Taiheiyo Cement Co., Ltd., type B blast furnace cement) are mixed using a mixer, and the sandy sand, blast furnace cement, and termite control agent are uniformly dispersed. The obtained curable termite control composition (BS-1) was obtained.
硬化性シロアリ防除組成物(BC−1)
シロアリ防除剤「コロニーバスター」に代えて、ホウ酸およびホウ砂(ともに和光純薬(株)製)をそれぞれ5重量部ずつ加える以外は、前記硬化性シロアリ防除組成物(BS−1)と同様にして、硬化性シロアリ防除組成物(BC−1)を調製した。
Curable termite control composition (BC-1)
The same as the curable termite control composition (BS-1) except that 5 parts by weight of boric acid and borax (both manufactured by Wako Pure Chemical Industries, Ltd.) were added instead of the termite control agent “Colony Buster”. Thus, a curable termite control composition (BC-1) was prepared.
硬化性シロアリ防除組成物(BO−1)
シロアリ防除剤T10重量部をタルク(ネオライト興産(株)製)100重量部に加え、混合機を用いて混合し、前記シロアリ防除剤とタルクとが均一に分散した混合物を作製し、その後、前記混合物を乾燥した。次に、乾燥した混合物と、高炉セメント10重量部(太平洋セメント(株)製、高炉セメントB種)とを混合機を用いて混合し、前記シロアリ防除剤と高炉セメントとが均一に分散した硬化性シロアリ防除組成物(BO−1)を得た。
Curable termite control composition (BO-1)
Add 10 parts by weight of termite control agent T to 100 parts by weight of talc (manufactured by Neolite Kosan Co., Ltd.) and mix using a mixer to prepare a mixture in which the termite control agent and talc are uniformly dispersed. The mixture was dried. Next, the dried mixture and 10 parts by weight of blast furnace cement (manufactured by Taiheiyo Cement Co., Ltd., blast furnace cement B type) are mixed using a mixer, and the termite control agent and the blast furnace cement are uniformly dispersed. Sex termite control composition (BO-1) was obtained.
硬化性シロアリ防除組成物(B−12)
硬化性シロアリ防除組成物(BO−1)10重量部に対し、乾燥真砂土[礫成分(粒径2〜5mm)の割合12.6重量%、砂成分の割合71.8重量%、土成分の割合15.6重量%]100重量部、高炉セメント(太平洋セメント(株)製、高炉セメントB種)10重量部を加え、混合機を用いて混合し、シロアリ防除剤と高炉セメントと真砂土とが均一に分散した硬化性シロアリ防除組成物(B−12)を得た。
Curable termite control composition (B-12)
10 parts by weight of the curable termite control composition (BO-1), dry dry sand [the proportion of gravel component (particle size 2 to 5 mm) 12.6% by weight, the proportion of sand component 71.8% by weight, soil component 15.6 wt%] 100 parts by weight and 10 parts by weight of blast furnace cement (produced by Taiheiyo Cement Co., Ltd., Blast Furnace Cement B) are mixed using a mixer, and then a termite control agent, blast furnace cement, and sand sand. A curable termite-controlling composition (B-12) in which was uniformly dispersed was obtained.
硬化性シロアリ防除組成物(B−13)
シロアリ防除剤T10重量部を軽石「カガライト4M号」(カガライト工業(株)製)100重量部に加え、混合機を用いて混合し、前記シロアリ防除剤と軽石とが均一に分散した混合物を作製し、その後、前記混合物を乾燥した。次に、乾燥した混合物10重量部と、乾燥真砂土[礫成分(粒径2〜5mm)の割合12.6重量%、砂成分の割合71.8重量%、土成分の割合15.6重量%]100重量部と、高炉セメント10重量部(太平洋セメント(株)製、高炉セメントB種)とを混合機を用いて混合し、前記シロアリ防除剤と高炉セメントと真砂土とが均一に分散した硬化性シロアリ防除組成物(B−13)を得た。
Curable termite control composition (B-13)
10 parts by weight of termite control agent T is added to 100 parts by weight of pumice “Kagalite 4M” (manufactured by Kagalite Industry Co., Ltd.) and mixed using a mixer to produce a mixture in which the termite control agent and pumice are uniformly dispersed. Then, the mixture was dried. Next, 10 parts by weight of the dried mixture, dry sand sand [gravel component (particle size 2 to 5 mm) ratio 12.6 wt%, sand component ratio 71.8 wt%, soil component ratio 15.6 wt% %] 100 parts by weight and 10 parts by weight of blast furnace cement (manufactured by Taiheiyo Cement Co., Ltd., type B blast furnace cement) are mixed using a mixer to uniformly disperse the termite control agent, blast furnace cement and pure sand soil. The obtained curable termite control composition (B-13) was obtained.
硬化性シロアリ防除組成物(BD−1)
硬化性シロアリ防除組成物(B−13)90重量部に対し、防菌消臭効果をもつ触媒組成物「セブントールNP−C」(日本エンバイロケミカルズ(株)製)10重量部を加え、混合機を用いて混合し、シロアリ防除剤と高炉セメントと真砂土と触媒組成物とが均一に分散し、殺シロアリ性とともに防菌消臭性も併せ持つ硬化性シロアリ防除組成物(BD−1)を得た。
Curable termite control composition (BD-1)
To 90 parts by weight of the curable termite control composition (B-13), 10 parts by weight of a catalyst composition “Seventhol NP-C” (manufactured by Nippon Environmental Chemicals Co., Ltd.) having an antibacterial and deodorizing effect is added and mixed. A curable termite control composition (BD-1) having a termite-controlling agent, a blast furnace cement, a pure sand soil, and a catalyst composition uniformly dispersed, and having both termite-killing properties and bactericidal and deodorizing properties. Obtained.
硬化性シロアリ防除組成物(BD−2)
硬化性シロアリ防除組成物(B−13)80重量部に対し、調湿消臭効果をもつ活性炭「白鷺M」(日本エンバイロケミカルズ(株)製)20重量部を加え、混合機を用いて混合し、シロアリ防除剤と高炉セメントと真砂土と活性炭とが均一に分散し、殺シロアリ性とともに調湿消臭性も併せ持つ硬化性シロアリ防除組成物(BD−2)を得た。
Curable termite control composition (BD-2)
To 80 parts by weight of the curable termite control composition (B-13), 20 parts by weight of activated carbon “Shirakaba M” (manufactured by Nippon Environmental Chemicals Co., Ltd.) having a humidity control and deodorizing effect is added and mixed using a mixer. Thus, a curable termite control composition (BD-2) was obtained in which the termite control agent, blast furnace cement, pure sand and activated carbon were uniformly dispersed to have both termite killing properties and moisture conditioning and deodorizing properties.
硬化性シロアリ防除組成物(BH−1)
シロアリ防除剤T3重量部を調湿効果を持つ粉末セピオライト(水沢化学(株)製)100重量部に加え、混合機を用いて混合し、前記シロアリ防除剤とセピオライトとが均一に分散した混合物を作製し、その後、前記混合物を乾燥した。次に、乾燥した混合物50重量部と、乾燥真砂土[礫成分(粒径2〜5mm)の割合12.6重量%、砂成分の割合71.8重量%、土成分の割合15.6重量%]40重量部と、高炉セメント10重量部(太平洋セメント(株)製、高炉セメントB種)とを混合機を用いて混合し、前記シロアリ防除剤とセピオライトと高炉セメントと真砂土とが均一に分散し、殺シロアリ性とともに調湿性も併せ持つ硬化性シロアリ防除組成物(BH−1)を得た。
Curable termite control composition (BH-1)
Add 3 parts by weight of the termite control agent T to 100 parts by weight of powdered sepiolite (manufactured by Mizusawa Chemical Co., Ltd.) having a humidity control effect, and mix using a mixer to obtain a mixture in which the termite control agent and sepiolite are uniformly dispersed. After that, the mixture was dried. Next, 50 parts by weight of the dried mixture, dried sand sand [gravel component (particle size 2 to 5 mm) ratio 12.6 wt%, sand component ratio 71.8 wt%, soil component ratio 15.6 wt% %] 40 parts by weight and 10 parts by weight of blast furnace cement (manufactured by Taiheiyo Cement Co., Ltd., blast furnace cement type B) are mixed using a mixer, and the termite control agent, sepiolite, blast furnace cement, and pure sand soil are uniform. And a curable termite control composition (BH-1) having both termite killing properties and humidity control properties was obtained.
硬化性シロアリ防除組成物(A−2)
礫成分(粒径2〜5mm)の割合70重量%、砂成分の割合15重量%、土成分の割合15重量%で各成分を混合機を用いて均一に混合し、礫成分、砂成分および土成分が均一に混合した土砂を得た。次いで、前記土砂100重量部と高炉セメント10重量部(太平洋セメント(株)製、高炉セメントB種)とを混合機を用いて混合し、前記土砂と高炉セメントとが均一に分散した硬化性シロアリ防除組成物(A−2)を得た。
Curable termite control composition (A-2)
Each component is uniformly mixed using a mixer at a gravel component (particle size 2 to 5 mm) ratio of 70% by weight, a sand component ratio of 15% by weight, and a soil component ratio of 15% by weight. Sediment in which soil components were uniformly mixed was obtained. Next, 100 parts by weight of the earth and sand and 10 parts by weight of blast furnace cement (manufactured by Taiheiyo Cement Co., Ltd., type B blast furnace cement) are mixed using a mixer, so that the earth and sand and the blast furnace cement are uniformly dispersed. A control composition (A-2) was obtained.
硬化性シロアリ防除組成物(B−14)
シロアリ防除性を有するトリデカノール(協和発酵(株)製)10重量部を軽石「カガライト4M号」(カガライト工業(株)製)100重量部に加え、混合機を用いて混合し、前記シロアリ防除剤と軽石とが均一に分散した混合物を作製し、その後、前記混合物を乾燥した。次に、乾燥した混合物10重量部と、乾燥真砂土[礫成分(粒径2〜5mm)の割合12.6重量%、砂成分の割合71.8重量%、土成分の割合15.6重量%]100重量部と、高炉セメント15重量部(太平洋セメント(株)製、高炉セメントB種)とを混合機を用いて混合し、前記シロアリ防除剤と高炉セメントと真砂土とが均一に分散した硬化性シロアリ防除組成物(B−14)を得た。
Curable termite control composition (B-14)
10 parts by weight of tridecanol having a termite-controlling property (manufactured by Kyowa Hakko Co., Ltd.) is added to 100 parts by weight of pumice “Kagalite 4M” (manufactured by Kagalite Kogyo Co., Ltd.) and mixed using a mixer. And pumice were uniformly dispersed, and then the mixture was dried. Next, 10 parts by weight of the dried mixture, dry sand sand [gravel component (particle size 2 to 5 mm) ratio 12.6 wt%, sand component ratio 71.8 wt%, soil component ratio 15.6 wt% %] 100 parts by weight and 15 parts by weight of blast furnace cement (manufactured by Taiheiyo Cement Co., Ltd., type B blast furnace cement) are mixed using a mixer, and the termite control agent, blast furnace cement and pure sand soil are uniformly dispersed. The obtained curable termite control composition (B-14) was obtained.
硬化性シロアリ防除組成物(D−1)
シロアリ防除剤T 10重量部を軽石「カガライト4M号」(カガライト工業(株)製)100重量部に加え、混合機を用いて混合し、前記シロアリ防除剤と軽石とが均一に分散した混合物を作製し、その後、前記混合物を乾燥した。次に、乾燥した混合物10重量部と、レンガ破砕物(粒径分布 2〜3mm:40重量%、0.2mm以上2mm未満:30重量%、0.2mm未満:30重量%、以下同様)100重量部と、高炉セメント15重量部(太平洋セメント(株)製、高炉セメントB種)とを混合機を用いて混合し、前記レンガ破砕物と高炉セメントとシロアリ防除剤とが均一に分散した硬化性シロアリ防除組成物(D−1)を得た。
Curable termite control composition (D-1)
Add 10 parts by weight of termite control agent T to 100 parts by weight of pumice “Kagalite 4M” (manufactured by Kagalite Kogyo Co., Ltd.) and mix using a mixer to obtain a mixture in which the termite control agent and pumice are uniformly dispersed. After that, the mixture was dried. Next, 10 parts by weight of the dried mixture and a crushed brick (particle size distribution 2-3 mm: 40% by weight, 0.2 mm or more and less than 2 mm: 30% by weight, less than 0.2 mm: 30% by weight, and so on) 100 Part by weight and 15 parts by weight of blast furnace cement (manufactured by Taiheiyo Cement Co., Ltd., type B blast furnace cement) are mixed using a mixer, and the brick crushed material, blast furnace cement, and termite control agent are uniformly dispersed. Sex termite control composition (D-1) was obtained.
硬化性シロアリ防除組成物(D−2)
レンガ破砕物に代えて、素焼き植木鉢破砕物(粒径分布 2〜3mm:20重量%、0.2mm以上2mm未満:60重量%、0.2mm未満:20重量%、以下同様)を用いる以外は、前記硬化性シロアリ防除組成物(D−1)と同様にして、硬化性シロアリ防除組成物(D−2)を調製した。
Curable termite control composition (D-2)
Instead of using crushed bricks, crushed clay pots (particle size distribution 2-3 mm: 20% by weight, 0.2 mm or more and less than 2 mm: 60% by weight, less than 0.2 mm: 20% by weight, the same applies below) The curable termite control composition (D-2) was prepared in the same manner as the curable termite control composition (D-1).
硬化性シロアリ防除組成物(D−3)
レンガ破砕物に代えて、瓦破砕物(粒径分布 2〜3mm:60重量%、0.2mm以上2mm未満:25重量%、0.2mm未満:15重量%、以下同様)を用いる以外は、前記硬化性シロアリ防除組成物(D−1)と同様にして、硬化性シロアリ防除組成物(D−3)を調製した。
Curable termite control composition (D-3)
Instead of using a brick crushed material, a tile crushed material (particle size distribution: 2-3 mm: 60% by weight, 0.2 mm or more and less than 2 mm: 25% by weight, less than 0.2 mm: 15% by weight, the same applies below), The curable termite control composition (D-3) was prepared in the same manner as the curable termite control composition (D-1).
硬化性シロアリ防除組成物(D−4)
レンガ破砕物に代えて、コンクリートブロック破砕物(粒径分布 2〜3mm:45重量%、0.2mm以上2mm未満:45重量%、0.2mm未満:10重量%、以下同様)を用いる以外は、前記硬化性シロアリ防除組成物(D−1)と同様にして、硬化性シロアリ防除組成物(D−4)を調製した。
Curable termite control composition (D-4)
Instead of using brick crushed material, concrete block crushed material (particle size distribution: 2-3 mm: 45% by weight, 0.2 mm or more and less than 2 mm: 45% by weight, less than 0.2 mm: 10% by weight, the same applies below) The curable termite control composition (D-4) was prepared in the same manner as the curable termite control composition (D-1).
硬化性シロアリ防除組成物(D−5)
レンガ破砕物に代えて、ガラス破砕物(粒径分布 2〜3mm:40重量%、0.2mm以上2mm未満:55重量%、0.2mm未満:5重量%、以下同様)を用い、かつ高炉セメントの使用量を25重量部とする以外は、前記硬化性シロアリ防除組成物(D−1)と同様にして、硬化性シロアリ防除組成物(D−5)を調製した。
Curable termite control composition (D-5)
In place of the crushed brick, a crushed glass (particle size distribution: 2-3 mm: 40% by weight, 0.2 mm or more and less than 2 mm: 55% by weight, less than 0.2 mm: 5% by weight, the same applies below) and a blast furnace A curable termite control composition (D-5) was prepared in the same manner as the curable termite control composition (D-1) except that the amount of cement used was 25 parts by weight.
硬化性シロアリ防除組成物(D−6)
ガラス破砕物に代えて、陶器(茶碗)破砕物(粒径分布 2〜3mm:45重量%、0.2mm以上2mm未満:50重量%、0.2mm未満:5重量%、以下同様)を用いる以外は、前記硬化性シロアリ防除組成物(D−5)と同様にして、硬化性シロアリ防除組成物(D−6)を調製した。
Curable termite control composition (D-6)
Instead of crushed glass, crushed pottery (tea bowl) (particle size distribution: 2-3 mm: 45% by weight, 0.2 mm or more and less than 2 mm: 50% by weight, less than 0.2 mm: 5% by weight, and so on) Except for the above, a curable termite control composition (D-6) was prepared in the same manner as the curable termite control composition (D-5).
硬化性シロアリ防除組成物(D−7)
ガラス破砕物に代えて、アサリ貝殻破砕物(粒径分布 2〜5mm:50重量%、0.2mm以上2mm未満:45重量%、0.2mm未満:5重量%、以下同様)を用いる以外は、前記硬化性シロアリ防除組成物(D−5)と同様にして、硬化性シロアリ防除組成物(D−7)を調製した。
Curable termite control composition (D-7)
Instead of using a crushed glass, a clam crushed material (particle size distribution: 2 to 5 mm: 50 wt%, 0.2 mm or more and less than 2 mm: 45 wt%, less than 0.2 mm: 5 wt%, the same applies hereinafter) The curable termite control composition (D-7) was prepared in the same manner as the curable termite control composition (D-5).
硬化性シロアリ防除組成物(E−1)
レンガ破砕物100重量部に代えて、レンガ破砕物50重量部及び乾燥真砂土[礫成分(粒径2〜5mm)の割合12.6重量%、砂成分の割合71.8重量%、土成分の割合15.6重量%]50重量部を用いる以外は、前記硬化性シロアリ防除組成物(D−1)と同様にして、硬化性シロアリ防除組成物(E−1)を調製した。
Curable termite control composition (E-1)
Instead of 100 parts by weight of crushed bricks, 50 parts by weight of crushed bricks and dry true sand [the proportion of gravel components (particle size 2-5 mm) 12.6% by weight, the proportion of sand components 71.8% by weight, soil components The curable termite control composition (E-1) was prepared in the same manner as the curable termite control composition (D-1) except that 50 parts by weight] was used.
硬化性シロアリ防除組成物(E−2)
レンガ破砕物に代えて、素焼き植木鉢破砕物を用いる以外は、前記硬化性シロアリ防除組成物(E−1)と同様にして、硬化性シロアリ防除組成物(E−2)を調製した。
Curable termite control composition (E-2)
A curable termite control composition (E-2) was prepared in the same manner as the curable termite control composition (E-1) except that a crushed clay pot was used instead of the crushed brick.
硬化性シロアリ防除組成物(E−3)
レンガ破砕物に代えて、瓦破砕物を用いる以外は、前記硬化性シロアリ防除組成物(E−1)と同様にして、硬化性シロアリ防除組成物(E−3)を調製した。
Curable termite control composition (E-3)
A curable termite control composition (E-3) was prepared in the same manner as the curable termite control composition (E-1) except that the tile crushed material was used instead of the brick crushed material.
硬化性シロアリ防除組成物(E−4)
レンガ破砕物に代えて、コンクリートブロック破砕物を用いる以外は、前記硬化性シロアリ防除組成物(E−1)と同様にして、硬化性シロアリ防除組成物(E−4)を調製した。
Curable termite control composition (E-4)
A curable termite control composition (E-4) was prepared in the same manner as the curable termite control composition (E-1) except that a concrete block crushed material was used instead of the brick crushed material.
硬化性シロアリ防除組成物(E−5)
レンガ破砕物に代えて、ガラス破砕物を用いる以外は、前記硬化性シロアリ防除組成物(E−1)と同様にして、硬化性シロアリ防除組成物(E−5)を調製した。
Curable termite control composition (E-5)
A curable termite control composition (E-5) was prepared in the same manner as the curable termite control composition (E-1) except that a glass crushed material was used instead of the brick crushed material.
硬化性シロアリ防除組成物(E−6)
レンガ破砕物に代えて、陶器(茶碗)破砕物を用いる以外は、前記硬化性シロアリ防除組成物(E−1)と同様にして、硬化性シロアリ防除組成物(E−6)を調製した。
Curable termite control composition (E-6)
A curable termite control composition (E-6) was prepared in the same manner as the curable termite control composition (E-1) except that a ceramic (tea bowl) crushed material was used instead of the brick crushed material.
硬化性シロアリ防除組成物(E−7)
レンガ破砕物に代えて、アサリ貝殻破砕物を用いる以外は、前記硬化性シロアリ防除組成物(E−1)と同様にして、硬化性シロアリ防除組成物(E−7)を調製した。
Curable termite control composition (E-7)
A curable termite control composition (E-7) was prepared in the same manner as the curable termite control composition (E-1) except that a clam shell crushed material was used instead of the brick crushed material.
実施例1
120メッシュの櫛を通過したケイ砂に、水分を付着させ、含水率10重量%とした。底面をプラスチックカバーで被覆した内径約3.5cmのプラスチック製円筒中に、含水ケイ砂を厚さ3cmで敷き詰め、続いてその上に前記硬化性シロアリ防除組成物(A−1)を3cm厚に散布した。そして、組成物(A−1)に対して水を約1.5L/m2散水(第一散水)した。1時間放置した後、さらに組成物(A−1)に対して水を約5L/m2散水(第二散水)したところ、24時間後に組成物(A−1)の固化が認められた。固化から7日後、前記含水ケイ砂を厚さ1cmで敷き詰めたシャーレ(直径9cm)の中心部に、前記円筒の底面のカバーを剥がして円筒を設置した。固化した組成物(A−1)の上に、木口1cm×1cm、長さ2cmのマツの餌木を設置した。そして、シャーレの含水ケイ砂上に、イエシロアリ職蟻150頭、兵蟻15頭を放虫し、餌木への食害状況及びシロアリの存否を調査した。その結果、放虫後3週間目においても、餌木への食害は確認されなかった。
Example 1
Moisture was attached to the silica sand that passed through the 120 mesh comb to a moisture content of 10% by weight. In a plastic cylinder having an inner diameter of about 3.5 cm, the bottom surface of which is covered with a plastic cover, hydrated silica sand is spread in a thickness of 3 cm, and then the curable termite control composition (A-1) is 3 cm thick thereon. Scattered. And about 1.5 L / m < 2 > water sprinkling (1st watering) was carried out with respect to the composition (A-1). After standing for 1 hour, about 5 L / m 2 of water was sprayed on the composition (A-1), and the composition (A-1) was solidified after 24 hours. Seven days after solidification, the bottom cover of the cylinder was peeled off at the center of a petri dish (diameter 9 cm) in which the hydrous silica sand was spread with a thickness of 1 cm, and a cylinder was installed. On the solidified composition (A-1), a pine feed tree having a tip of 1 cm × 1 cm and a length of 2 cm was placed. Then, 150 termite ants and 15 soldier ants were released on the water-containing silica sand of the petri dish, and the state of feeding damage to the feeding trees and the existence of termites were investigated. As a result, feeding damage to the feeding tree was not confirmed even 3 weeks after the release.
比較例1
底面をプラスチックカバーで被覆した内径約3.5cmのプラスチック製円筒中に、実施例1と同様に調製した含水ケイ砂(含水率10重量%)を厚さ3cmで敷き詰めた後、含水ケイ砂を厚さ1cmで敷き詰めたシャーレ(直径9cm)の中心部に、前記円筒の底面のカバーを剥がして円筒を設置した。円筒内の含水ケイ砂の上に木口1cm×1cm、長さ2cmのマツの餌木を設置した。そして、シャーレの含水ケイ砂上に、イエシロアリ職蟻150頭、兵蟻15頭を放虫し、餌木への食害状況及びシロアリの存否を調査した。その結果、放虫後一日目に、餌木に対して食害の跡が確認された。
Comparative Example 1
In a plastic cylinder having an inner diameter of about 3.5 cm covered with a plastic cover on the bottom, water-containing silica sand (water content 10% by weight) prepared in the same manner as in Example 1 was laid down to a thickness of 3 cm, At the center of a petri dish (diameter 9 cm) spread with a thickness of 1 cm, the cover on the bottom surface of the cylinder was peeled off to install a cylinder. On a hydrous silica sand in a cylinder, a pine feeding tree with a lip of 1 cm × 1 cm and a length of 2 cm was installed. Then, 150 termite ants and 15 soldier ants were released on the water-containing silica sand of the petri dish, and the state of feeding damage to the feeding trees and the existence of termites were investigated. As a result, on the first day after the release, traces of feeding damage were confirmed on the feeding trees.
実施例2
第一散水の水に代えて、シロアリ防除剤Tを50重量倍で希釈した水希釈液を散水する以外は実施例1と同様にした。その結果、放虫後7日目までにイエシロアリは全て死亡した。また、餌木への食害は確認されなかった。
Example 2
It replaced with the water of the 1st watering, and it carried out similarly to Example 1 except watering the water dilution liquid which diluted the termite control agent T by 50 weight times. As a result, all the termites died by the seventh day after the release. In addition, no food damage to the prey was confirmed.
実施例3
第二散水の水に代えて、シロアリ防除剤Tの500重量倍水希釈液を散水する以外は実施例1と同様にした。その結果、放虫後7日目までにイエシロアリは全て死亡した。また、餌木への食害は確認されなかった。
Example 3
It replaced with the water of the 2nd watering, and it carried out similarly to Example 1 except watering the 500 weight times water dilution liquid of the termite control agent T. As a result, all the termites died by the seventh day after the release. In addition, no food damage to the prey was confirmed.
実施例4
第一散水及び第二散水で用いられた水に代えて、シロアリ防除剤Tの100重量倍水希釈液及び1000重量倍水希釈液をそれぞれ散水する以外は、実施例1と同様にした。その結果、放虫後7日目までにイエシロアリは全て死亡した。また、餌木への食害は確認されなかった。
Example 4
It replaced with the water used by the 1st watering and the 2nd watering, and it carried out similarly to Example 1 except watering the 100 weight times water dilution liquid and 1000 weight times water dilution liquid of the termite control agent T, respectively. As a result, all the termites died by the seventh day after the release. In addition, no food damage to the prey was confirmed.
実施例5
第二散水から24時間後、さらにシロアリ防除剤Tの100重量倍水希釈液を3ml散水する以外は、実施例1と同様とした。その結果、放虫後7日目までにイエシロアリは全て死亡した。また、餌木への食害は確認されなかった。
Example 5
24 hours after the second watering, the same procedure as in Example 1 was performed except that 3 ml of a 100-fold water-diluted termite control agent T was sprayed. As a result, all the termites died by the seventh day after the release. In addition, no food damage to the prey was confirmed.
実施例6
硬化性シロアリ防除組成物(A−1)に代えて、硬化性シロアリ防除組成物(B−1)を用いる以外、実施例1と同様とした。その結果、放虫後7日目までにイエシロアリは全て死亡した。また、餌木への食害は確認されなかった。
Example 6
It replaced with the curable termite control composition (A-1), and it carried out similarly to Example 1 except using a curable termite control composition (B-1). As a result, all the termites died by the seventh day after the release. In addition, no food damage to the prey was confirmed.
実施例7
底面をプラスチックカバーで被覆した内径約3.5cmのプラスチック製円筒中に、実施例1と同様に調製した含水ケイ砂(含水率10重量%)を厚さ3cmで敷き詰めた。次に、硬化性シロアリ防除組成物(B−1)を1cm厚に敷設した。トーヨーインスタントセメント(トーヨーマテラン(株)製)100g当たり水22.5mLを加え、練合したものを、厚さ3cmで前記敷設物の上に敷設した。組成物(B−1)の敷設から7日後、前記含水ケイ砂を厚さ1cmで敷き詰めたシャーレ(直径9cm)の中心部に、前記円筒の底面のカバーを剥がして円筒を設置した。固化したインスタントセメントの上に、木口1cm×1cm、長さ2cmのマツの餌木を設置した。そして、シャーレの含水ケイ砂上に、イエシロアリ職蟻150頭、兵蟻15頭を放虫し、餌木への食害状況及びシロアリの存否を調査した。その結果、放虫後7日目までにイエシロアリは全て死亡した。また、餌木への食害は確認されなかった。なお、前記組成物(B−1)は、円筒内で完全に固化していた。
Example 7
In a plastic cylinder having an inner diameter of about 3.5 cm whose bottom surface was covered with a plastic cover, hydrous silica sand (water content 10 wt%) prepared in the same manner as in Example 1 was laid down to a thickness of 3 cm. Next, the curable termite control composition (B-1) was laid to a thickness of 1 cm. 22.5 mL of water was added per 100 g of Toyo Instant Cement (manufactured by Toyo Materan Co., Ltd.), and the kneaded mixture was laid on the laid product with a thickness of 3 cm. Seven days after the laying of the composition (B-1), the bottom cover of the cylinder was peeled off and the cylinder was installed at the center of a petri dish (diameter 9 cm) in which the hydrous silica sand was spread in a thickness of 1 cm. On the solidified instant cement, a pine feeding tree with a lip of 1 cm × 1 cm and a length of 2 cm was placed. Then, 150 termite ants and 15 soldier ants were released on the water-containing silica sand of the petri dish, and the state of feeding damage to the feeding trees and the existence of termites were investigated. As a result, all the termites died by the seventh day after the release. In addition, no food damage to the prey was confirmed. The composition (B-1) was completely solidified in the cylinder.
実施例8
底面をプラスチックカバーで被覆した内径約3.5cmのプラスチック製円筒中に、実施例1と同様に調製した含水ケイ砂(含水率10重量%)を厚さ3cmで敷き詰めた。次に、硬化性シロアリ防除組成物(B−1)を1cm厚に散布した。組成物(B−1)の散布から3日後、組成物の表面が固化していることを確認し、前記含水ケイ砂を厚さ1cmで敷き詰めたシャーレ(直径9cm)の中心部に、前記円筒の底面のカバーを剥がして円筒を設置した。表面が固化した組成物(B−1)の上に、木口1cm×1cm、長さ2cmのマツの餌木を設置した。そして、シャーレの含水ケイ砂上に、イエシロアリ職蟻150頭、兵蟻15頭を放虫し、餌木への食害状況及びシロアリの存否を調査した。その結果、放虫後7日目までにイエシロアリは全て死亡した。また、餌木への食害は確認されなかった。
Example 8
In a plastic cylinder having an inner diameter of about 3.5 cm whose bottom surface was covered with a plastic cover, hydrous silica sand (water content 10 wt%) prepared in the same manner as in Example 1 was laid down to a thickness of 3 cm. Next, the curable termite control composition (B-1) was sprayed to a thickness of 1 cm. Three days after the application of the composition (B-1), it was confirmed that the surface of the composition was solidified, and the cylinder was placed in the center of a petri dish (diameter 9 cm) in which the hydrous silica sand was spread with a thickness of 1 cm. The bottom cover was removed and a cylinder was installed. On the composition (B-1) whose surface was solidified, a pine feed tree with a lip of 1 cm × 1 cm and a length of 2 cm was installed. Then, 150 termite ants and 15 soldier ants were released on the water-containing silica sand of the petri dish, and the state of feeding damage to the feeding trees and the existence of termites were investigated. As a result, all the termites died by the seventh day after the release. In addition, no food damage to the prey was confirmed.
実施例9
底面をプラスチックカバーで被覆した内径約3.5cmのプラスチック製円筒中に、実施例1と同様に調製した含水ケイ砂(含水率10重量%)を厚さ3cmで敷き詰めた。硬化性シロアリ防除組成物(A−1)30gに対して、水3gを加え、均一に混合した混合物の一部を、前記含水ケイ砂上に厚さ3cmで敷設した。敷設から24時間後に組成物(A−1)の固化を確認した。固化から7日後、前記含水ケイ砂を厚さ1cmで敷き詰めたシャーレ(直径9cm)の中心部に、前記円筒の底面のカバーを剥がして円筒を設置した。固化した組成物(A−1)の上に、木口1cm×1cm、長さ2cmのマツの餌木を設置した。そして、シャーレの含水ケイ砂上に、イエシロアリ職蟻150頭、兵蟻15頭を放虫し、餌木への食害状況及びシロアリの存否を調査した。その結果、放虫後3週間目においても、餌木への食害は確認されなかった。
Example 9
In a plastic cylinder having an inner diameter of about 3.5 cm whose bottom surface was covered with a plastic cover, hydrous silica sand (water content 10 wt%) prepared in the same manner as in Example 1 was laid down to a thickness of 3 cm. 3 g of water was added to 30 g of the curable termite control composition (A-1), and a part of the uniformly mixed mixture was laid at a thickness of 3 cm on the hydrous silica sand. Solidification of the composition (A-1) was confirmed 24 hours after laying. Seven days after solidification, the bottom cover of the cylinder was peeled off at the center of a petri dish (diameter 9 cm) in which the hydrous silica sand was spread with a thickness of 1 cm, and a cylinder was installed. On the solidified composition (A-1), a pine feed tree having a tip of 1 cm × 1 cm and a length of 2 cm was placed. Then, 150 termite ants and 15 soldier ants were released on the water-containing silica sand of the petri dish, and the state of feeding damage to the feeding trees and the existence of termites were investigated. As a result, feeding damage to the feeding tree was not confirmed even 3 weeks after the release.
実施例10
水に代えて、シロアリ防除剤Tの15重量倍水希釈液3gを硬化性シロアリ防除組成物(A−1)30gに対して混合する以外は実施例9と同様にした。その結果、放虫後7日目までにイエシロアリは全て死亡した。また、餌木への食害は確認されなかった。
Example 10
It replaced with water and it carried out similarly to Example 9 except mixing 3 g of 15 weight times water dilution liquid of the termite control agent T with respect to curable termite control composition (A-1) 30g. As a result, all the termites died by the seventh day after the release. In addition, no food damage to the prey was confirmed.
実施例11〜20
実施例11〜20において、実施例1〜10で用いられたイエシロアリに代えて、それぞれの実施例でヤマトシロアリを用いた。実施例1〜10に対応する各実施例(11〜20)において、ヤマトシロアリについても、イエシロアリと同様の結果が得られた。
Examples 11-20
In Examples 11 to 20, instead of the termites used in Examples 1 to 10, Yamato termites were used in the respective examples. In each Example (11-20) corresponding to Examples 1-10, the same result as the termite was obtained also about Yamato termite.
実施例21〜30
硬化性シロアリ防除組成物(A−1)に代えて、表1に示す硬化性シロアリ防除組成物を用いる以外、実施例1と同様とした。結果を表1に示す。なお、表中、餌木への食害に関する記号は、○:全く食害されていない、△:わずかに食害が見られる、×:食害が見られることを意味する。
Examples 21-30
It replaced with the curable termite control composition (A-1), and it was the same as that of Example 1 except using the curable termite control composition shown in Table 1. The results are shown in Table 1. In the table, symbols relating to feeding damage to feeding trees mean that ◯: no feeding damage, Δ: slight feeding damage is observed, and X: eating damage is seen.
実施例31〜40
硬化性シロアリ防除組成物(A−1)に代えて、表1に示す硬化性シロアリ防除組成物を用いる以外、実施例1と同様とした。結果を表2に示す。なお、表中、餌木への食害に関する記号は、表1と同様の意味である。
Examples 31-40
It replaced with the curable termite control composition (A-1), and it was the same as that of Example 1 except using the curable termite control composition shown in Table 1. The results are shown in Table 2. In addition, the symbol regarding the feeding damage to a feeding tree in a table | surface has the same meaning as Table 1.
実施例41
実施例1における含水ケイ砂に代えて、乾燥ケイ砂を用いるとともに、硬化性シロアリ防除組成物(A−1)に代えて、乾燥真砂土を用い、この上から、硬化性シロアリ防除組成物(BO−1)5L/m2を散布した以外は実施例1と同様にして、1週間後に固化した防蟻層を得た。そして、実施例1と同様にして食害状況およびシロアリの存否を調査したところ、放虫後、3週間目においても、餌木への食害は確認されなかった。
Example 41
In place of the hydrous silica sand in Example 1, dry silica sand is used, and in place of the curable termite control composition (A-1), dry diatomaceous earth is used. From this, the curable termite control composition ( BO-1) An ant barrier layer solidified after one week was obtained in the same manner as in Example 1 except that 5 L / m 2 was sprayed. And when the state of feeding damage and the presence or absence of termites were investigated in the same manner as in Example 1, no feeding damage to feeding trees was confirmed even in the third week after insect release.
実施例42
硬化性シロアリ防除組成物(B−1)を大阪府下の民家和室床下一面に3cm厚で均一に散布し、その後3L/m2の割合で散水し固化させ、シロアリ防除層を形成した。施工から1ヵ月後、未施工場所の床下では湿度95%であるのに対し、シロアリ防除層を形成した床下では湿度85%であり、シロアリ防除層の形成による優れた調湿効果が認められた。
Example 42
The curable termite-controlling composition (B-1) was uniformly sprayed at a thickness of 3 cm on the lower surface of a private Japanese-style room under Osaka Prefecture, and then watered and solidified at a rate of 3 L / m 2 to form a termite-controlling layer. One month after the installation, the humidity is 95% under the floor of the unconstructed place, whereas the humidity under the floor where the termite control layer is formed is 85%, and an excellent humidity control effect due to the formation of the termite control layer was recognized. .
実施例43
硬化性シロアリ防除組成物(D−1)〜(D−7)及び(E−1)〜(E−7)のそれぞれ100重量部に水15重量部を加えて混合した後、べた基礎の床下の基礎立ち上がり部分に厚さ2cm、巾5cmで均一に散布し、1週間後に固化した防蟻層を得た。そして、実施例1と同様にして食害状況およびシロアリの存否を調査したところ、放虫後、3週間目においても、餌木への食害は確認されなかった。
Example 43
After adding and mixing 15 parts by weight of water to 100 parts by weight of each of the curable termite control compositions (D-1) to (D-7) and (E-1) to (E-7), the floor under a solid foundation The base rising portion was uniformly sprayed with a thickness of 2 cm and a width of 5 cm to obtain an ant barrier layer solidified after one week. And when the state of feeding damage and the presence or absence of termites were investigated in the same manner as in Example 1, no feeding damage to feeding trees was confirmed even in the third week after insect release.
Claims (16)