JP4651275B2 - エチレン系共重合体樹脂組成物とその用途 - Google Patents
エチレン系共重合体樹脂組成物とその用途 Download PDFInfo
- Publication number
- JP4651275B2 JP4651275B2 JP2003373894A JP2003373894A JP4651275B2 JP 4651275 B2 JP4651275 B2 JP 4651275B2 JP 2003373894 A JP2003373894 A JP 2003373894A JP 2003373894 A JP2003373894 A JP 2003373894A JP 4651275 B2 JP4651275 B2 JP 4651275B2
- Authority
- JP
- Japan
- Prior art keywords
- ethylene
- mfr
- copolymer
- olefin
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
Mw/Mn+4.7≦MFR10/MFR2
Mw/Mn+4.7≦MFR10/MFR2
以下、本発明に係るエチレン系共重合体組成物およびその用途について具体的に説明する。本発明に係るエチレン系共重合体組成物は、エチレン・α−オレフィン共重合体(A)とエチレン・α−オレフィン共重合体(B)とからなっている。
本発明に係るエチレン系共重合体組成物を構成するエチレン・α−オレフィン共重合体(A)は、エチレンと炭素数3〜20のα−オレフィンとのランダム共重合体である。エチレンとの共重合に用いられる炭素数3〜20のα−オレフィンとしては、プロピレン、1−ブテン、1−ペンテン、1−ヘキセン、4−メチル−1−ペンテン、1−オクテン、1−デセン、1−ドデセン、1−テトラデセン、1−ヘキサデセン、1−オクタデセン、1−エイコセンなどが挙げられる。これらのうちでも、炭素原子数3〜10のα−オレフィンが好ましく、特にプロピレン、1−ブテン、1−ヘキセン、1−オクテンが好ましい。これらのα− オレフィンは、単独で、あるいは2種以上組み合わせて用いられる。また、エチレン・α− オレフィン共重合体(A)は、これらの単位の他に、本発明の目的を損なわない範囲で、他の重合性モノマーから導かれる単位を含有していてもよい。
エチレン・α−オレフィン共重合体(A)としては、具体的には、エチレン・プロピレン共重合体、エチレン・1−ブテン共重合体、エチレン・プロピレン・1−ブテン共重合体、エチレン・プロピレン・エチリデンノルボルネン共重合体、エチレン・1−ヘキセン共重合体、エチレン・1−オクテン共重合体などが挙げられる。これらの内でも、エチレン・プロピレン共重合体、エチレン・1−ブテン共重合体、エチレン・1−ヘキセン共重合体、エチレン・1−オクテン共重合体などが好ましく用いられ、特にエチレン・1−ブテン共重合体が好ましく用いられる。これらの共重合体は、ランダムあるいはブロック共重合体であるが、特にランダム共重合体であることが好ましい。
本発明のエチレン・α−オレフィン共重合体(A)は13C-NMRスペクトルにおけるTααに対するTαβの強度比(Tαβ/Tαα)が0.5以下、好ましくは0.4以下であると物性強度の面で好ましい。
B値=[POE]/(2・[PE][PO]) …(1)
本発明に係るエチレン系共重合体組成物を構成するエチレン・α−オレフィン共重合体(B)は、エチレンと炭素数3〜20のα−オレフィンとのランダム共重合体である。エチレンとの共重合に用いられる炭素数3〜20のα−オレフィンとしては、プロピレン、1−ブテン、1−ペンテン、1−ヘキセン、4−メチル−1−ペンテン、1−オクテン、1−デセン、1−ドデセン、1−テトラデセン、1−ヘキサデセン、1−オクタデセン、1−エイコセンなどが挙げられる。これらのうちでも、炭素原子数3〜10の α−オレフィンが好ましく、特にプロピレン、1−ブテン、1−ヘキセン、1−オクテンが好ましい。これらのα−オレフィンは、単独で、あるいは2種以上組み合わせて用いられる。
上記のような本発明で用いられるエチレン・α−オレフィン共重合体は、上記条件を満足するように公知の方法で製造可能である。また、少なくともどちらか一方が、式 Mw/Mn+4.7≦MFR10/MFR2を満足するエチレン・α−オレフィン共重合体は、例えば特開平6−136196、特開平12−191862に記載されている触媒としてメタロセン系触媒などを用いる従来公知の方法により製造することができる。メタロセン系触媒の存在下にエチレンと炭素数3〜10のα−オレフィンとを共重合させることによって製造することができる。
また有機アルミニウム化合物を用いる場合には、通常約0〜5ミリモル/リットル(重合容積)、好ましくは約0〜2ミリモル/リットルとなるような量で用いられる。
共重合反応は、通常、反応温度が−20〜+150℃、好ましくは0〜120℃、さらに好ましくは0〜100℃で、圧力が0を超えて7.8MPa(80kgf/cm2、ゲージ圧)以下、好ましくは0を超えて4.9MPa(50kgf/cm2、ゲージ圧)以下の条件下に行われる。
エチレン系共重合体組成物は、上記エチレン・α−オレフィン共重合体(A)および、エチレン・α−オレフィン共重合体(B)とからなる。該組成物中の(A)/(B)の割合は、重量%で5/95〜95/5であり、好ましくは60/40〜95/5である。この範囲にあると破断強度、残留歪みなどの機械的特性に優れ、押出し特性などの成形性に優れている。
Mw/Mn +4.7≦MFR10/MFR2の関係を満たしていると、流動性に優れた組成物が得られる。
(1)エチレン・α−オレフィン共重合体(A)と、エチレン・α−オレフィン共重合体(B)、および所望により添加される他成分を、押出機、ニーダー等を用いて機械的にブレンドする方法。
(2)エチレン・α−オレフィン共重合体(A)と、エチレン・α−オレフィン共重合体(B)、および所望により添加される他成分を適当な良溶媒(例えば;ヘキサン、ヘプタン、デカン、シクロヘキサン、ベンゼン、トルエンおよびキシレン等の炭化水素溶媒)に溶解し、次いで溶媒を除去する方法。
(3)エチレン・α−オレフィン共重合体(A)と、エチレン・α−オレフィン共重合体(B)、および所望により添加される他成分を適当な良溶媒にそれぞれ別個に溶解した溶液を調製した後混合し、次いで溶媒を除去する方法。
(4)上記(1)〜(3)の方法を組み合わせて行う方法等がある。
本発明のエチレン系共重合体組成物は、使い捨ておむつ、使い捨て下着、生理用ナプキンなどの使い捨て着用物品として、ずり落ち防止に用いられる伸縮性および成形加工性に優れた成形体にも使用される。この成形体に求められる特性として、漏れ防止性を向上させるためにフィット性、即ち、応力保持性を高めることである。
本発明に係るエチレン系重合体組成物は、押出成形、射出成形、インフレーション成形、カレンダー成形などの成形方法により、フィルム、シートなどの各種成形品に成形することができる。
本発明のエチレン系共重合体組成物は、通常の空冷インフレーション成形、空冷2段冷却インフレーション成形、高速インフレーション成形、T−ダイフィルム成形、水冷インフレーション成形等で加工することにより、フィルムを得ることができる。このようにして成形されたフィルムは、機械的強度に優れている。本発明のフィルムの厚みは15〜200μmの範囲であることが好ましい。また、熱針加工、パーフォレーション加工等により通気性を向上させることが好ましい。
また、本発明の組成物に架橋助剤(C)を添加して得られたフィルムを電離性放射線で架橋することにより、更に機械物性および残留歪みが向上したフィルムが得られる。
本発明に係る積層体は、少なくとも1層の伸長性不織布層と、少なくとも1層のフィルムとからなり、少なくとも一方の表面層が伸長性不織布層である積層体である。
本発明で用いられる伸長性不織布は、横方向の伸長率が100%以上、好ましくは200%以上である不織布である。また、伸長性不織布は、加工適性を損なわないために、縦方向において低伸長であって、ある程度の強度を有することが好ましく、5%伸長時の引張荷重が500g/50mm以上、好ましくは1000g/50mm以上である。
本発明の積層体の厚さは、用途、要求される品質、貼り合わせ等に応じて適宜選択することができる。
なお、実施例において各種物性の測定は、以下のようにして行った。
50mm幅の試験片を23℃雰囲気下で万能引張試験機(インストロン社製)にセットし、スパン間隔をI0とする。20mm/分のスピードで150%まで伸長させた後、直ちに同一スピードで出発点まで戻し、直ちに同一スピードで伸張させ、荷重がゼロ以上に生じたときのスパン間隔Iを読み、次式で求めた。
残留歪み=I/I0×100(%)
本実施例では、I0を30mmとして測定した。
(3)MFR10(190℃):ASTM D1238に準拠し、190℃、10kg荷重にて測定した。
(4)密度:密度:ASTM D1505に準拠して測定した。
(5)破断点応力・伸び:JIS K6781に準拠し、200mm/minの引張り速度にて測定した。
ゲル分率(ゲル含量;キシレン不溶解分)は、次のようにして測定される。試料を秤量して細かく裁断し、次いで得られた細片を、密閉容器中にキシレンと共に入れ、3時間還流させる。 次に、この試料をろ紙上に取出し、絶乾させ、この乾燥残渣の重量からポリマー成分以外のキシレン不溶性成分(たとえばフィラー、充填剤、顔料等)の重量を減じた値を、「補正された最終重量(Y)」とする。
一方、試料の重量からポリマー成分以外のキシレン可溶性成分(たとえば安定剤等)の重量およびポリマー成分以外のキシレン不溶性成分(たとえばフィラー、充填剤、顔料等)の重量を減じた値を、「補正された初期重量(X)」とする。
ここに、ゲル含量(キシレン不溶解分)は、次式により求められる。
ゲル含量[重量%]=[補正された最終重量(Y)]÷[補正された初期重量(X)]
×100
特開2003−073494号公報実施例に準じた方法でメタロセン触媒を用いて、MFR2(190℃)が0.5g/10min、MFR10(190℃)が3.4g/10分、密度が0.861g/cm3、GPCにより求めた分子量分布(Mw/Mn)が2.1、1−ブテンから導かれる構成単位含有量が19モル%であるエチレン・1−ブテン共重合体(A−1)90重量部、およびMFR2(190℃)が70g/10min、MFR10(190℃)が490g/10分、密度が0.893g/cm3、GPCにより求めた分子量分布(Mw/Mn)が1.9、1−ブテンから導かれる構成単位含有量が11モル%であるエチレン・1−ブテン共重合体(B−1)10重量部を40mmφの単軸押出機で溶融混練後、ペレットを作成した。このペレットを50mmφの押出機を備えた幅300mmのT−ダイ成形機にて、シリンダー温度、ダイス温度230℃、チルロール温度30℃の条件で、厚み約100μmのフィルムを得た。得られたフィルムを、照射装置[日新ハイボルテージ(株)製]を用いて種々の線量で電子線照射し、物性測定をした。その結果を表1に示す。
実施例1において、(A−1)を75重量部、(B−1)を25重量部とするほかは同様にしてフィルムを作成し、電子線照射して物性測定をした。その結果を表2に示す。
実施例2において、架橋助剤トリアリルイソシアヌレート(TAIC)[商品名 M−60(TAIC含有量60%)、日本化成(株)製] 3重量部(TAIC含量として)、を添加し同様の測定をした。その結果を表2に示す。
MFR2(190℃)が1.2g/10分、MFR10(190℃)が11.8g/10分、密度が0.870g/cm3、GPCにより求めた分子量分布(Mw/Mn)が2.1、1−ブテンから導かれる構成単位含有量が15モル%であるエチレン・1−ブテン共重合体(D−1)100重量部を使用した以外は実施例1と同様にしてフィルムを作成し、同様な測定をした。その結果を表2に示す。
得られたエチレン・1−ブテン共重合体の性状を表1にまとめる。
Claims (4)
- (A)密度が0.857〜0.880g/cm3 の範囲であり、190℃、2.16kg荷重で測定したメルトフローレート(MFR2)が0.01〜10g/10分の範囲にあるエチレン・α-オレフィン共重合体5〜95重量%と、(B)密度が0.883〜0.910g/cm3の範囲であり、メルトフローレート(MFR2)が10〜100g/10分の範囲にあるエチレン・α-オレフィン共重合体5〜95重量%とからなるエチレン系共重合体組成物からなり、衛生材用伸縮部材であることを特徴とする成形体。
- 前記(A)および(B)の少なくとも一方が、190℃、10kg荷重で測定したメルトフローレート(MFR10)と190℃、2.16kg荷重で測定したメルトフローレート(MFR2)との比:MFR10/MFR2と、GPCにより求めた分子量分布Mw/Mnが下記式の関係を満たす請求項1に記載の成形体。
Mw/Mn+4.7≦MFR10/MFR2 - 前記成形体が、前記エチレン系共重合体組成物100重量部に対して、架橋助剤(C)を0.01〜20重量部含有させた該組成物の成形体を電離性放射線により架橋して得られる架橋成形体であることを特徴とする請求項1または2に記載の成形体。
- 成形体がフィルムであることを特徴とする請求項1〜3のいずれかに記載の成形体。