JP4467268B2 - 蒸着用プロピレン系重合体積層フィルム及び蒸着積層フィルム - Google Patents
蒸着用プロピレン系重合体積層フィルム及び蒸着積層フィルム Download PDFInfo
- Publication number
- JP4467268B2 JP4467268B2 JP2003294216A JP2003294216A JP4467268B2 JP 4467268 B2 JP4467268 B2 JP 4467268B2 JP 2003294216 A JP2003294216 A JP 2003294216A JP 2003294216 A JP2003294216 A JP 2003294216A JP 4467268 B2 JP4467268 B2 JP 4467268B2
- Authority
- JP
- Japan
- Prior art keywords
- propylene
- vapor deposition
- film
- weight
- vapor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
又、蒸着用プロピレン系重合体積層フィルムに無機化合物を蒸着してなるフィルムは、上記特性に加え、低温ヒートシール性、耐ブロッキング性が良好である。
本発明に係わるプロピレン・α−オレフィン共重合体(A)は、DSCに基づく結晶融解曲線から求められたピーク温度(Tp)が110〜140℃、好ましくは115〜130℃、融解開始温度(Ts)と融解終了温度(Te)との差(Te−Ts)が45℃未満、好ましくは30〜40℃の範囲にあり、好ましくは融解開始温度(Ts)とピーク温度(Tp)との差(Tp−Ts)が35℃未満、より好ましくは25〜34℃の範囲にある。プロピレン・α−オレフィン共重合体(A)のα―オレフィンの含有量は上記熱融解特性を有する限りとくに制限はされないが、通常はα―オレフィンの含有量は1.0〜20重量%、より好ましくは1.5〜15重量%の範囲にある。α―オレフィンとしては、エチレン、1−ブテン、1−ヘキセン、4−メチル・1−ペンテン、1−オクテン等が例示できる。これらの中では、エチレン及び/又は1−ブテンとのランダム共重合体が好ましい。又、MFR(メルトフローレート;ASTM D−1238 荷重2160g、温度230℃)はフィルムとすることができる限り特に限定はされないが、通常0.5〜20g/10分、好ましくは2〜10g/10分の範囲にある。本発明に係わるプロピレン・α−オレフィン共重合体(A)は通常、分子量分布(重量平均分子量Mwと数平均分子量Mnとの比で表される)が2〜3の範囲にある。本発明に係わるプロピレン・α―オレフィン共重合体(A)は、蒸着用プロピレン系重合体積層フィルムの被蒸着層と熱融着層の原料となる。
本発明に係わるプロピレン・α−オレフィン共重合体(A)の上記ピーク温度(Tp)、融解開始温度(Ts)及び融解終了温度(Te)は以下の方法で測定した。プロピレン・α−オレフィン共重合体(A)約5mgを秤量し、セイコ−電子工業株式会社製の示差走査熱量計(タイプDSC220モジュ−ル)を用いて、昇温速度;10℃/分で200℃まで昇温し、200℃で5分間保持した後、降温速度;100℃/分で0℃まで冷却し、再度、昇温速度;10℃/分で0℃〜200℃まで昇温したときの融解曲線を測定し、かかる融解曲線から、ASTM D3418−99の方法に習い、融解曲線からピ−ク温度(Tp)、融解開始温度(Ts)、融解終了温度(Te)を求めた。尚、本発明では、ASTM D3418−99に記載の(Tpm1)を(Tp)、(Teim)を(Ts)及び(Tefm)を(Te)とした。
本発明に係わるプロピレン重合体(B)は、プロピレンの単独重合体、またはプロピレンと10重量%以下、好ましくは5重量%以下のα−オレフィンとの共重合体、あるいは単独重合体と共重合体との組成物である。α−オレフィンは、プロピレン以外の通常炭素数2〜10のα−オレフィンであって、例えば、エチレン、1−ブテン、3−メチル−1−ブテン、1―ペンテン、3―メチル―1―ペンテン、4−メチル−1−ペンテン、1―へキセン、1―オクテン等を挙げることができる。これらプロピレン重合体(B)の中でも、得られる熱融着性プロピレン系重合体積層フィルムの耐熱性、剛性の面からプロピレン単独重合体が好ましい。かかるプロピレン重合体(B)は、フィルムとして成形できる限り、特に限定はされないが、MFR(メルトフローレート;ASTM D−1238 荷重2160g、温度230℃)が、通常0.1〜100g/10分、好ましくは1〜50g/10分の範囲にある。
本発明に係わるプロピレン重合体(B)は、蒸着用プロピレン系重合体積層フィルムの中間層の原料となる。
本発明に係わるエチレン系重合体(C)は、通常、密度が0.900〜0.970g/cm3、好ましくは0.910〜0.968g/cm3、MFR(ASTM D1238 荷重2160g、温度190℃)が1〜50g/10分、好ましくは5〜30g/10分の、エチレンの単独重合体、若しくはエチレンと少量の炭素数が3〜10のα−オレフィン、例えばプロピレン、ブテン−1、ヘプテン−1、ヘキセン−1、オクテン−1、4−メチル−ペンテン−1とのランダム共重合体で、いわゆる、高圧法低密度ポリエチレン(HP−LDPE)、線状低密度ポリエチレン(直鎖状低密度ポリエチレンとも呼ぶ)(LLDPE)、中密度ポリエチレン(MDPE)、高密度ポリエチレン(HDPE)と呼ばれているエチレンを主体とした重合体である。これらエチレン系重合体(C)は、単一の重合体であっても、二種以上のエチレン系重合体との組成物(混合物)であってもよい。
本発明に係わる線状低密度ポリエチレン(E)は、前記エチレン系重合体(C)の範疇に含まれる重合体で、密度が0.900〜0.935g/cm3、好ましくは0.910〜0.930g/cm3、MFR(ASTM D1238 荷重2160g、温度190℃)が1〜50g/10分、好ましくは5〜30g/10分の、エチレンと少量の炭素数が3〜10のα−オレフィン、例えばプロピレン、ブテン−1、ヘプテン−1、ヘキセン−1、オクテン−1、4−メチル−ペンテン−1とのランダム共重合体である。さらにかかる線状低密度ポリエチレンとしては、分子量分布(重量平均分子量:Mw、と数平均分子量:Mn、との比:Mw/Mnで表示)が通常1.5〜4.0、好ましくは1.8〜3.5の範囲にある。このMw/Mnはゲル透過クロマトグラフィー(GPC)によって測定できる。
又、線状低密度ポリエチレン(E)は、示差走査熱量計(DSC)の昇温速度10℃/分で測定した吸熱曲線から求めた鋭いピークが1個ないし複数個あり、該ピークの最高温度、すなわち融点が通常70〜130℃、好ましくは80〜120℃の範囲にある。
なお、このようなメタロセン化合物を含むオレフィン重合用触媒、および触媒を用いた線状低密度ポリエチレン(E)の調整方法は、たとえば特開平8−269270号公報に記載されている。
本発明に係わる不飽和カルボン酸変性プロピレン系重合体(F)は、プロピレンの単独重合体、またはプロピレンと10重量%以下、好ましくは5重量%以下のα−オレフィンとの共重合体、あるいは単独重合体と共重合体との組成物等のプロピレン系重合体を不飽和カルボン酸もしくはその誘導体でグラフト変性したものである。プロピレンと共重合されるα−オレフィンは、プロピレン以外の通常炭素数2〜10のα−オレフィンであって、例えば、エチレン、1−ブテン、3−メチル−1−ブテン、1―ペンテン、3―メチル―1―ペンテン、4−メチル−1−ペンテン、1―へキセン、1―オクテン等を挙げることができる。
不飽和カルボン酸もしくはその誘導体としては、例えばアクリル酸、マレイン酸、フマール酸、テトラヒドロフタル酸、イタコン酸、シトラコン酸、クロトン酸、イソクロトン酸、ナジック酸(エンドシス−ビシクロ[2.2.1]ヘプト−5−エン−2,3−ジカルボン酸)等の不飽和カルボン酸;またはその誘導体、例えば酸ハライド、アミド、イミド、無水物、エステル等が挙げられる。かかる誘導体の具体例としては、例えば塩化マレニル、マレイミド、無水マレイン酸、無水シトラコン酸、マレイン酸モノメチル、マレイン酸ジメチル、グリシジルマレエート等が挙げられる。これらの中では、不飽和ジカルボン酸またはその酸無水物が好適であり、特にマレイン酸、ナジック酸またはこれらの酸無水物が好ましく用いられる。
変性前のプロピレン系重合体としては、前記記載のプロピレン系重合体に限られず、前記記載のプロピレン・α−オレフィン共重合体(A)であってもよい。
又、不飽和カルボン酸変性プロピレン系重合体(F)は、不飽和カルボン酸もしくはその誘導体でグラフト量が前記範囲内にある限り、不飽和カルボン酸もしくはその誘導体でグラフト変性されたプロピレン系重合体と未変性のプロピレン系重合体との組成物であってもよい。
本発明に係わるプロピレン・α−オレフィン共重合体(A)及びプロピレン重合体(B)は種々公知の方法、例えば、典型的には固体状チタン触媒成分と有機金属化合物触媒成分から形成される触媒、あるいはこれら両成分および電子供与体から形成される触媒を用いて製造することができる。
有機金属化合物触媒成分としては、有機アルミニウム化合物が好適であり、具体的には、トリアルキルアルミニウム、ジアルキルアルミニウムハライド、アルキルアルミニウムセスキハライド、アルキルアルミニウムジハライドなどが挙げられる。これらの化合物のうち、好適な有機金属化合物触媒成分は、使用する上記チタン触媒成分の種類によって異なる。
電子供与体は、窒素、リン、イオウ、酸素、ケイ素、ホウ素などを含む有機化合物であり、好適な具体例としては、これらの元素を有する有機エステル、有機エーテルなどを挙げることができる。
担体付触媒成分を用いた重合体の製造方法に関しては、たとえば特開昭50−108385号、特開昭50−126590号、特開昭51−20297号、特開昭51−28189号、特開昭52−151691号などの各公報に開示されている。
前記メタロセン系遷移金属化合物としては、例えば特開平5−209014号、特開平6−100579号、特開平1−301704号、特開平3−193796号、特開平5−148284号、特開2000−20431号等に記載された化合物などがあげられる。
有機アルミニウム化合物としては、アルキルアルミニウム、または鎖状あるいは環状アルミノキサン等があげられる。上記鎖状あるいは環状アルミノキサンは、アルキルアルミニウムと水とを接触させることにより生成される。例えば重合時にアルキルアルミニウムを加えておいて、後で水を添加するか、あるいは錯塩の結晶水または有機、無機化合物の吸着水とアルキルアルミニウムとを反応させることにより得られる。
前記メタロセン系遷移金属化合物と反応してイオン対を形成する化合物は、例えば特表平1−501950号、特開平3−207704号、特開2002−20431号等に記載された化合物などがあげられる。シングルサイト触媒を担持させる前記無機物としては、シリカゲル、ゼオライト、珪藻土等があげられる。
重合方法としては、塊状重合、溶液重合、懸濁重合、気相重合等があげられる。これらの重合はバッチ法であっても連続法であっても良い。重合条件は通常、重合温度;−100〜+250℃、重合時間;5分〜10時間、反応圧力;常圧〜300Kg/cm2(ゲージ圧)である。
本発明の蒸着用プロピレン系重合体積層フィルムは、DSCに基づく結晶融解曲線から求められたピーク温度(Tp)が110〜140℃及び融解開始温度(Ts)と融解終了温度(Te)との差(Te−Ts)が45℃未満のプロピレン・α―オレフィン共重合体(A)から得られる被蒸着層の片面に、プロピレン系重合体(B)から得られる中間層を介して前記プロピレン・α―オレフィン共重合体(A)から得られる熱融着層からなる三層フィルムある。
本発明の蒸着用プロピレン系重合体積層フィルムは被蒸着層を構成するプロピレン・α―オレフィン共重合体(A)に、エチレン系重合体(C)を35重量%以下、より好ましくは5〜35重量%、さらに好ましくは15〜30重量%含ませておくと、被蒸着層に無機化合物を蒸着した際に密着性をより強くすることができる。
又、エチレン系重合体(C)として高密度ポリエチレン(D)を0.5〜5重量%、より好ましくは1〜4重量%加えておくと、得られる蒸着用プロピレン系重合体フィルムの剛性、耐熱性が向上し蒸着加工時、更には蒸着されたフィルムのブロッキング性やロ−ル状に巻いた場合の巻き絞まり等がより改良され、製品としての品質がより改良される。
又、エチレン系重合体(C)として線状低密度ポリエチレン(E)を3〜30重量%、より好ましくは15〜25重量%加えておくと、無機化合物を蒸着した際の常温時の密着性がより強く改良される。
更に、プロピレン・α―オレフィン共重合体(A)に不飽和カルボン酸変性プロピレン系重合体(F)を50重量%以下、より好ましくは10〜45重量%、さらに好ましくは25〜45重量%加えておくと、得られる蒸着用プロピレン系重合体フィルムを包装材料として用いた場合に、ヒ−トシ−ル等によりフィルムに熱が加わった場合に無機化合物との密着性が向上し、包装体になった場合のヒ−トシ−ル強度、バリア性等の性質がより改良される。
被蒸着層と熱融着層に用いるプロピレン・α―オレフィン共重合体(A)は上記範囲にある限り同一の物性を有するプロピレン・α―オレフィン共重合体(A)であっても異なる物性を有するプロピレン・α―オレフィン共重合体(A)であってもよい。
本発明の蒸着用プロピレン系重合体積層フィルムの厚さは、種々用途により適宜選択され得るが、通常被蒸着層が1〜100μm、好ましくは1〜20μm、中間層が8〜498μm、好ましくは18〜98μm、熱融着層が1〜100μm、好ましくは1〜20μm、三層フィルムの総厚が10〜500μm、好ましくは20〜100μmの範囲にある。
本発明の蒸着用プロピレン系重合体積層フィルムは被蒸着層面に無機化合物との接着性を改良するためにコロナ処理、火炎処理、プラズマ処理、プライマーコート処理等の表面処理を行っておいてもよい。
本発明のプロピレン系重合体蒸着積層フィルムは、前記蒸着用プロピレン系重合体積層フィルムの被蒸着層面に、無機化合物を蒸着してなるフィルムである。かかる無機化合物としては、アルミニウム及び亜鉛等の金属、クロム、亜鉛、コバルト、アルミニウム、錫及び珪素等の無機酸化物、窒化物、酸化インジウム錫、チタン酸鉛等が挙げられる。
無機化合物の薄膜を蒸着用プロピレン系重合体フィルムもしくは蒸着用プロピレン系重合体積層フィルムに形成させる方法としては、化学蒸着(CVD)、低圧CVD及びプラズマCVD等の化学蒸着法、真空蒸着(反応性真空蒸着)、スパッタリング(反応性スパッタリング)及びイオンプレーティング(反応性イオンプレーティング)等の物理蒸着法(PVD)、低圧プラズマスプレイ及びプラズマスプレイ等のプラズマスプレイ法とが例示できる。
形成される無機化合物の薄膜の厚さは、通常50〜5000Å、好ましくは100〜2000Åの範囲である。5000Åを越えると耐屈曲性が低下するとなる虞があり、一方、50Å未満では充分な耐ガスバリア性が得られない虞がある。
かかるフィルム基材としては、熱可塑性樹脂からなるシート状またはフィルム状の基材が挙げられる。かかる熱可塑性樹脂としては、種々公知の熱可塑性樹脂、例えば、ポリオレフィン(ポリエチレン、ポリプロピレン、ポリ4−メチル・1−ペンテン、ポリブテン等)、ポリエステル(ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート等)、ポリアミド(ナイロン−6、ナイロン−66、ポリメタキシレンアジパミド等)、ポリ塩化ビニル、ポリイミド、エチレン・酢酸ビニル共重合体、ポリアクリロニトリル、ポリカーボネート、ポリスチレン、アイオノマー、あるいはこれらの混合物等を例示することができる。これらのうちでは、ポリプロピレン、ポリエチレンテレフタレート、ポリアミド等、延伸性、透明性が良好な熱可塑性樹脂が好ましい。
又、かかる熱可塑性樹脂フィルムからなる基材は、無延伸フィルムであっても、延伸フィルムであっても良いし、1種或いは2種以上の共押し出し品、押出しラミ品、ドライラミ品等の積層体であっても良い。中でも、ニ軸延伸フィルムが剛性、透明性等に優れているので好ましい。
又、フィルム基材の片面あるいは両面に、無機化合物蒸着層との接着性を改良するために例えば、コロナ処理、火炎処理、プラズマ処理、アンダーコート処理、プライマーコート処理、フレーム処理等の表面活性化処理を行っておいてもよい。フィルム基材の厚さは、通常5〜1000μm、好ましくは7〜200μmの範囲にある。フィルム基材は必要に応じて印刷を施しておいてもよい。
なお、ヒートシール強度、アルミニウム密着強度評価を行なう前に、実施例及び比較例で得られた蒸着積層フィルムの蒸着面に、エステル系接着剤を用いて厚さ25μmの二軸延伸ポリプロピレンフィルムをドライラミネ−ションにより積層し、40℃×48時間エ−ジングして、測定用の積層フィルムを用意した。
(1)ヒートシール強度(N/15mm)
測定用の積層フィルムの熱融着層面を重ね合せ、所定の温度で、幅10mmのシールバーにより、0.2MPaの圧力で0.5秒間、上部シ−ルバ−温度を所定の温度、下部シ−ルバ−温度は70℃一定状態で、フィルムの流れ方向に対して直角方向にヒートシールした後放冷した。これから15mm幅の試験片を切り取りクロスヘッド速度300mm/分でヒートシール部を剥離し、その強度をヒートシール強度とした。
(2)アルミニウム密着強度(N/15mm)
測定用の積層フィルムの熱融着層に二軸延伸ポリプロピレンフィルムからなるテ−プを貼り、所定の温度で、幅10mmのシールバーにより、0.2MPaの圧力で0.5秒間、上部シ−ルバ−温度を所定の温度、下部シ−ルバ−温度は70℃一定状態で、フィルムの流れ方向に対して直角方向にヒートシールバ−を用いて熱を加えた後放冷した。これから15mm幅の試験片を切り取り、T型剥離法によりクロスヘッド速度300mm/分で、熱を加えた部分のアルミニウム蒸着層と積層フイルムとの間を剥離したときの強度を測定し、アルミニウム密着強度とした。
(3)ブロッキング性
ブロッキング性を測定する前に、フィルムを38℃のオ−ブン中で15時間エ−ジングした後放冷した。蒸着加工を施さないフィルムから20mm×100mm幅の短冊状の試験片を切り取り、熱融着性面を重ね合せたものを5個ずつ作製し、試験片の中央付近で十字方向に直角に市販のプレパラ−トではさむ。試験片とプレパラ−トが重なった5.2cm2の面積部分に4kgの荷重を掛け、所定の温度条件で2日間エ−ジングした後、放冷する。その後熱融着層面を重ね合せたものをクロスヘッド速度300mm/分で剪断剥離を行い、最大強度をブロッキング力とした。ブロッキング力をn=5で評価し、平均値をブロッキング力(N/5.2cm2)とした。
(1) プロピレン・エチレンランダム共重合体(1)(PER)
エチレン含有量:3.1重量%、Ts:94.0℃、Tp:126.6℃、Te:131.4℃、Te−Ts:37.4℃、Tp−Ts:32.6℃、Mw/Mn:2.7及びMFR:7g/10分。
(2) プロピレン・エチレン・1−ブテンランダム共重合体(PEBR)
エチレン含有量:2.2重量%、1−ブテン含有量:2.0重量%、Ts:95.4℃、Tp:139.3℃、Te:150.3℃、Te−Ts:54.9℃、Tp−Ts:43.9℃、Mw/Mn:3.9及びMFR:7g/10分。
(3)高密度ポリエチレン(HDPE)
密度:0.965g/cm3、Tm:135℃、MFR:17.0g/10分(190℃)。
(4)線状低密度ポリエチレン(LL)
密度:0.920g/cm3、Tm:120℃、MFR:8.0g/10分(190℃)。
(5)無水マレイン酸グラフト変性プロピレン系重合体(MAH−PP)
密度:0.903g/cm3、Tm:139℃、MFR:13.0g/10分(230℃)。
(6) プロピレン単独重合体(PP)
Tm:160℃、MFR:7.0g/10分(230℃)。
熱融着層として、PER:97.6重量%及びHDPE:2.4重量%とをドライブレンドしたプロピレン系重合体組成物を、中間層として、PP:100重量%を、被蒸着層としてPER:39.2重量%及びHDPE:2.0重量%、LL:19.6重量%、MAH−PP:39.2重量%、を夫々用意して別個の押出機に供給し、Tダイ法によって熱融着層/中間層/被蒸着層からなる三層共押出積層フイルムを得た後、被蒸着層面を直後で40dyn/cm以上になるようにコロナ処理して、蒸着用プロピレン系重合体積層フィルムを得た。得られた積層フィルムの総厚は20μmで、各層の厚みは熱融着層:中間層:被蒸着層=2.8μm:14.8μm:2.4μmであった。
抵抗加熱方式ベルジャー型蒸着装置(真空機工社製、小型真空蒸着装置VPC−260)を用い、得られた蒸着用プロピレン系重合体積層フィルムの被蒸着層上にアルミニウムの厚みが約450Åになるように蒸着し、プロピレン系重合体蒸着積層フィルムを得た。
得られた蒸着用プロピレン系重合体積層フィルム及び蒸着積層フイルムを前記記載の方法で評価した。結果を表1に示す。
熱融着層としてPEBR:97.6重量%及びHDPE:2.4重量%とをドライブレンドしたプロピレン系重合体組成物を、中間層としてPP:100重量%を、被蒸着層としてPEBR:39.2重量%及びHDPE:2.0重量%、LL:19.6重量%、MAH−PP:39.2重量%をドライブレンドしたプロピレン系重合体組成物を用いる以外は実施例1と同様に行い、蒸着用プロピレン系重合体積層フィルム及び蒸着積層フィルムを得た。評価結果を表1に示す。
菓子類、チルド食品、冷凍食品、パン・麺等の食品、或いはキャラクタ−カ−ドなどの玩具、衣料品、日用品等あらゆる分野の製品の包装材料として広く使用出来る。
Claims (2)
- 密度が0.940〜0.970g/cm 3 の高密度ポリエチレン(D)を0.5〜5重量%、密度が0.910〜0.930g/cm 3 の線状低密度ポリエチレン(E)を3〜30重量%及び不飽和カルボン酸変性プロピレン系重合体(F)を10〜45重量%含む、DSCに基づく結晶融解曲線から求められたピーク温度(Tp)が110〜140℃及び融解開始温度(Ts)と融解終了温度(Te)との差(Te−Ts)が45℃未満のプロピレン・α―オレフィン共重合体(A)〔但し、(D)+(E)+(F)+(A)=100重量%〕から得られる被蒸着層の片面に、プロピレン単独重合体から得られる中間層を介して、密度が0.940〜0.970g/cm 3 の高密度ポリエチレン(D)を0.5〜5重量%含む、DSCに基づく結晶融解曲線から求められたピーク温度(Tp)が110〜140℃及び融解開始温度(Ts)と融解終了温度(Te)との差(Te−Ts)が45℃未満のプロピレン・α―オレフィン共重合体(A)〔但し、(D)+(A)=100重量%〕から得られる熱融着層が積層されてなることを特徴とする蒸着用プロピレン系重合体積層フィルム。
- 請求項1に記載の蒸着用プロピレン系重合体積層フィルムの被蒸着層に無機化合物が蒸着されてなる蒸着積層フィルム。