JP4466466B2 - Weather resistance test method and weather resistance test apparatus - Google Patents
Weather resistance test method and weather resistance test apparatus Download PDFInfo
- Publication number
- JP4466466B2 JP4466466B2 JP2005141026A JP2005141026A JP4466466B2 JP 4466466 B2 JP4466466 B2 JP 4466466B2 JP 2005141026 A JP2005141026 A JP 2005141026A JP 2005141026 A JP2005141026 A JP 2005141026A JP 4466466 B2 JP4466466 B2 JP 4466466B2
- Authority
- JP
- Japan
- Prior art keywords
- sample
- weather resistance
- resistance test
- test
- heater
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、屋根材や外装材等の耐候性を人工的環境下で試験する耐候性試験方法に関し、特に試料の表面に結露を生じさせる過程に特徴を有する耐候性試験方法に関する。 The present invention relates to a weather resistance test method for testing the weather resistance of roofing materials, exterior materials, and the like in an artificial environment, and more particularly to a weather resistance test method characterized by a process in which condensation occurs on the surface of a sample.
建物の屋根材や外壁材として利用される各種の金属材料、無機質材料、有機質材料等(以下、これらを「外装材料」と総称する。)の耐候性試験方法として、温湿度の制御可能な試験槽内に上記外装材料の試料を定置し、さまざまな温湿度条件下で、メタルハライドランプや紫外線ランプその他の光源による光の照射や、シャワーによる散水等を繰り返し、試料を人工的に劣化させて耐候性を評価する方法がよく知られている。 As a weather resistance test method for various metal materials, inorganic materials, organic materials, etc. (hereinafter collectively referred to as “exterior materials”) used as building roofing materials and exterior wall materials, tests with controllable temperature and humidity A sample of the above exterior material is placed in the tank, and under various temperature and humidity conditions, the sample is artificially deteriorated and weathered by repeatedly irradiating light from a metal halide lamp, ultraviolet lamp or other light source, or spraying water from a shower. Methods for evaluating sex are well known.
かかる耐候性試験においては、外装材料の表面塗膜を劣化させたり、金属材料を腐食させたりする因子として、結露の影響も重要視される。かかる観点から、試料の表面に人工的に結露を発生させる方法も提案されているが、試験槽内を高温多湿に保ちつつ、試料台に設けた冷却装置を用いて試料を裏面から冷却することにより、試料の表面に結露を生じさせる方法が一般的である(例えば特許文献1〜4等)。
上記のように試料を裏面から冷却する方法を採る場合、金属板のような熱伝導率の高い外装材料であれば、その表面にも容易に結露するが、試料が断熱材を積層した複合材や多孔質材料など熱伝動率の低い外装材料であったり、試料の厚みが大きくなったりすると、上記のような方法では試料の表面温度がなかなか低下しないので、結露が生じにくい。 When the method of cooling the sample from the back side as described above is adopted, if the exterior material has a high thermal conductivity such as a metal plate, it will easily condense on its surface, but the sample is a composite material in which a heat insulating material is laminated. In the case of an exterior material having a low thermal conductivity, such as a porous material or a porous material, or when the thickness of the sample is increased, the surface temperature of the sample is not easily lowered by the above-described method, so that condensation does not easily occur.
また、実際の屋根材や外壁材では、それらの裏面が冷却されて結露するのではなく、朝方、気温が上昇して絶対湿度が上がりはじめたときに、夜間に冷やされていた屋根材や外壁材の表面温度の上昇速度が気温の上昇速度よりも遅れ、屋根材や外壁材の表面が露点温度以下になって結露する。したがって、上記のような試験方法において、例えば試験槽内の気温50度、湿度98%といった高温多湿の環境下で結露を発生させることは、実際の状況とは結露発生原理が大きく相違することなる。 Also, in actual roofing materials and outer wall materials, the back side of the roofing materials and outer walls are not cooled and condensation occurs, but when the absolute humidity begins to rise in the morning and the temperature rises in the morning, The rising speed of the surface temperature of the material is slower than the rising speed of the air temperature, and the surface of the roofing material and the outer wall material becomes below the dew point temperature to cause condensation. Therefore, in the test method as described above, for example, generating dew condensation in a high temperature and high humidity environment such as a temperature of 50 ° C. and a humidity of 98% in the test tank is greatly different from the actual situation in terms of dew generation. .
本発明は、かかる問題点に着目してなされたもので、熱伝導率の低い外装材料であっても、より実際に近い状況で、自然な結露を発生させることのできる耐候性試験方法と、該試験方法に適した耐候性試験装置を提供するものである。 The present invention was made paying attention to such a problem, and even in an exterior material with low thermal conductivity, a weather resistance test method capable of generating natural dew condensation in a more realistic situation, A weather resistance test apparatus suitable for the test method is provided.
上記した目的を達成するため、本発明の耐候性試験方法は、加湿ヒータの加熱によって水蒸気を発生させる加湿手段と、攪拌ファンの運転によって試験槽内の空気を循環させる空気攪拌手段とが収容された試験槽内に外装材料の試料を定置し、試験槽内を一定時間、低温高湿状態に保持して、試料全体を表裏均一に冷却した後、攪拌ファンを停止した状態で加湿ヒータを加熱して、試験槽内を加湿しつつ、室温を上昇させ、試験槽内の湿度及び温度が上昇しはじめて所定時間経過してから攪拌ファンを運転することにより、試料表面の温度上昇を室温上昇よりも遅らせて試料の表面に結露を発生させることを特徴とする。 In order to achieve the above object, the weather resistance test method of the present invention includes a humidifying means for generating water vapor by heating a humidifying heater and an air agitating means for circulating air in the test tank by operating a stirring fan. A sample of the exterior material is placed in the test chamber, the interior of the test chamber is kept at a low temperature and high humidity for a certain period of time, the entire sample is cooled uniformly on both sides, and the humidifier heater is heated with the stirring fan stopped. Then, the room temperature is raised while humidifying the inside of the test chamber, and the temperature rise on the sample surface is increased from the room temperature rise by operating the stirring fan after a predetermined time has passed since the humidity and temperature in the test chamber began to rise. Is also characterized by causing condensation on the surface of the sample.
この試験方法において、低温高湿状態とは、室温が概ね15℃以下、湿度が概ね90%以上の状態とし、この低温高湿状態を保持する時間は、試料の材質にもよるが、概ね1時間以上とする。また、加熱ヒータを加熱しはじめてから攪拌ファンを運転するまでの時間差は、試験槽の容量にもよるが、概ね5分ないし10分とする。攪拌ファンの運転開始が早すぎると、加湿ヒータが十分に温まって湿度が上昇しはじめるまでに試料の表面温度も上昇することとなり、反対に攪拌ファンの運転開始が遅すぎると、試験槽内が必要以上に高温多湿となるからである。 In this test method, the low temperature and high humidity state is a state where the room temperature is approximately 15 ° C. or less and the humidity is approximately 90% or more. The time for maintaining this low temperature and high humidity state is approximately 1 although it depends on the material of the sample. Over time. The time difference from the start of heating the heater to the operation of the stirring fan is approximately 5 to 10 minutes, depending on the capacity of the test tank. If the stirring fan starts too early, the surface temperature of the sample also rises until the humidifying heater becomes sufficiently warm and the humidity begins to rise. Conversely, if the stirring fan starts too late, the inside of the test chamber It is because it becomes hot and humid more than necessary.
この試験方法によれば、加湿ヒータの加熱運転によって試験槽内の絶対湿度が上昇する状況で、試験槽内の室温よりも試料表面の温度上昇が遅れるため、試料表面が露点温度以下になって結露する。このようにして生じる結露は、試料の小口や周縁部よりも比較的、温度上昇が遅い中間部に発生しやすく、この点でも実際の自然環境下で生じる結露と酷似したものとなる。 According to this test method, in the situation where the absolute humidity in the test chamber rises due to the heating operation of the humidifying heater, the temperature rise of the sample surface is delayed from the room temperature in the test chamber, so the sample surface becomes below the dew point temperature. Condensation. Condensation generated in this way is more likely to occur in the middle part where the temperature rise is relatively slower than the edge and peripheral edge of the sample, and this is also very similar to the condensation that occurs in the actual natural environment.
また、本発明の耐候性試験装置は、外装材料の試料を定置させうる試験槽内に、光源と、加湿ヒータの加熱によって水蒸気を発生させる加湿手段と、攪拌ファンの運転によって試験槽内の空気を循環させる空気攪拌手段とが収容された耐候性試験装置において、加湿ヒータの加熱運転開始後、攪拌ファンの運転を所定時間だけ停止させうる制御モードが設けられたことを特徴とする。 Further, the weather resistance test apparatus of the present invention includes a test chamber in which a sample of the exterior material can be placed, a humidifier that generates water vapor by heating of a humidifier heater, and air in the test chamber by operating a stirring fan. In the weather resistance test apparatus in which the air agitating means for circulating the air is accommodated, a control mode is provided in which the operation of the agitating fan can be stopped for a predetermined time after the heating operation of the humidifying heater is started.
この試験装置によって、上記試験方法を好適に実施することができる。なお、ここで、光源とは、メタルハライドランプ、紫外線ランプ、キセノンランプ、カーボンアーク等の、耐候性試験において用いられる一般的な光源を包括するものであり、特にその種類は限定しない。また、試験槽内には、上記以外に散水装置等の付加設備が設けられていてもよい。 With this test apparatus, the above test method can be suitably carried out. Here, the light source includes general light sources used in a weather resistance test, such as a metal halide lamp, an ultraviolet lamp, a xenon lamp, and a carbon arc, and the type thereof is not particularly limited. In addition to the above, additional equipment such as a watering device may be provided in the test tank.
上述のように構成される本発明の耐候性試験方法によれば、試料の厚みが大きかったり、熱伝導率が低かったりする場合でも、実際に近い状況で、表面に自然な結露を発生させることのことができる。したがって、自然環境下での実際の劣化に近似した劣化状態を再現することができる。 According to the weather resistance test method of the present invention configured as described above, even when the thickness of the sample is large or the thermal conductivity is low, natural condensation is generated on the surface in a situation close to the actual situation. Can be. Therefore, it is possible to reproduce a deterioration state that approximates actual deterioration in a natural environment.
以下、本発明の実施の形態について図を参照して説明する。 Hereinafter, embodiments of the present invention will be described with reference to the drawings.
図1〜図3は、本発明の耐候性試験に使用する試験装置の構成例を示す。 1 to 3 show a configuration example of a test apparatus used for the weather resistance test of the present invention.
符号1は試験槽で、前面側が開閉可能になっている。試験槽1内の前方寄りには、試料の載置角度を調整しうる試料台2が設けられている。試料台2の上方には光源3と、散水用のシャワーノズル4が取り付けられている。試験槽1内の奥寄りには、加湿ヒータ5、冷却コイル6、左右2個の攪拌ファン7が設置されている。2個の攪拌ファン7は、図3に示すように、回転方向が互いに逆向きになるように取り付けられている。符号8は攪拌ファン7を駆動させるためのモータであり、符号9は電気部品盤である。
試験装置の前面には、ディスプレイ付き操作パネル10と記録装置11が取り付けられている。また、試験装置の下方には、冷凍機12、光源用電源装置13が設置され、側方には水タンク14が設置されている。また、背後には排熱ブロア15が設けられている。
An
これらの機器・装置類の種類や配置は一例であって、特にこの形態に限定されるものではないが、本発明に係る耐候性試験装置の要部は、試験槽1内に加湿ヒータ5と攪拌ファン7が設置され、少なくとも攪拌ファン7が、加湿ヒータ5と連動しないで運転しうるように設定されている点にある。
The types and arrangements of these devices / equipment are examples, and are not particularly limited to this form. However, the essential part of the weather resistance test apparatus according to the present invention is the
次に、このような耐候性試験装置を使用して試料に結露を生じさせた試験結果について説明する。 Next, a test result in which dew condensation is caused on the sample using such a weather resistance test apparatus will be described.
実施例1として、表面にアクリルエマルジョン塗装を施したサイディングボード(厚さ16mm)に対する耐候性試験を行った。試験装置の光源にはメタルハライドランプを用いた。 As Example 1, a weather resistance test was performed on a siding board (thickness 16 mm) having an acrylic emulsion coating on the surface. A metal halide lamp was used as the light source of the test apparatus.
まず、照射モードとして、4時間の光源照射を実施した。この照射モードにおける試験槽内の室温は63℃、相対湿度は50%に保持した。 First, as an irradiation mode, light source irradiation for 4 hours was performed. In this irradiation mode, the room temperature in the test chamber was kept at 63 ° C. and the relative humidity was kept at 50%.
続いて、光源照射を切り、冷却モードに移行した。冷却モードでは、室温15℃。相対湿度95%の状態を1時間保持した。 Subsequently, the light source irradiation was turned off, and the cooling mode was entered. In the cooling mode, the room temperature is 15 ° C. A state where the relative humidity was 95% was maintained for 1 hour.
続いて、結露モードに移行した。結露モードでは、攪拌ファンを停止したままの状態で加湿ヒータを加熱し、加熱開始から5分後に攪拌ファンを運転して、相対湿度を95%に保持しままま、室温を30℃まで上昇させた。 Then, it shifted to the dew condensation mode. In the dew condensation mode, the humidifying heater was heated with the stirring fan stopped, and the stirring fan was operated 5 minutes after the start of heating, and the room temperature was raised to 30 ° C. while maintaining the relative humidity at 95%. .
この結果、結露モードに切り替えてから約4分後に、試料の小口近傍を除く表面ほぼ全体にわたって、細かい結露が確認された。さらに、結露モードに切り替えてから10分後には、試料の表面ほぼ全体にわたって結露の粒径の増大が確認された。
[比較例1]
実施例1との比較のため、実施例1と同じ試料に対し、同じ試験装置を用いて、同じ照射モードを保持した。
As a result, about 4 minutes after switching to the dew condensation mode, fine dew condensation was confirmed over almost the entire surface except the vicinity of the edge of the sample. Further, 10 minutes after switching to the dew condensation mode, an increase in the particle size of dew condensation was confirmed over almost the entire surface of the sample.
[Comparative Example 1]
For comparison with Example 1, the same irradiation mode was maintained using the same test apparatus for the same sample as in Example 1.
続いて、光源照射を切り、冷却モードを経ずに結露モードに移行した。この結露モードでは、加熱ヒータを加熱しはじめると同時に攪拌ファンを運転して、相対湿度を95%に保持しままま、室温を30℃まで上昇させた。 Subsequently, the light source irradiation was turned off, and the mode shifted to the dew condensation mode without passing through the cooling mode. In this dew condensation mode, the stirrer fan was operated simultaneously with starting to heat the heater, and the room temperature was raised to 30 ° C. while maintaining the relative humidity at 95%.
この結果、試料台には結露が生じたが、試料の表面には結露が生じなかった。
[比較例2]
実施例1と同じ試料に対し、同じ試験装置を用いて、同じ照射モードを保持した。
As a result, condensation occurred on the sample stage, but no condensation occurred on the surface of the sample.
[Comparative Example 2]
The same irradiation mode was maintained for the same sample as in Example 1 using the same test apparatus.
続いて、光源照射を切り、冷却モードに移行した。冷却モードでは、室温15℃。相対湿度95%の状態を1時間保持した。 Subsequently, the light source irradiation was turned off, and the cooling mode was entered. In the cooling mode, the room temperature is 15 ° C. A state where the relative humidity was 95% was maintained for 1 hour.
続いて、結露モードに移行した。この結露モードでも、加熱ヒータを加熱しはじめると同時に攪拌ファンを運転して、相対湿度を95%に保持しままま、室温を30℃まで上昇させた。 Then, it shifted to the dew condensation mode. Even in this dew condensation mode, the stirring fan was operated at the same time as the heater started to be heated, and the room temperature was raised to 30 ° C. while maintaining the relative humidity at 95%.
この結果、試料台には結露が生じたが、試料の表面には結露が生じなかった。 As a result, condensation occurred on the sample stage, but no condensation occurred on the surface of the sample.
実施例2として、耐候性試験装置における攪拌ファンの運転をタイマー制御しうるように設定し、実施例1と同じ試料に対して、反復的な耐候性試験を行った。試験装置の光源にはメタルハライドランプを用いた。 In Example 2, the operation of the stirring fan in the weather resistance test apparatus was set so that the timer could be controlled, and the same sample as in Example 1 was subjected to repeated weather resistance tests. A metal halide lamp was used as the light source of the test apparatus.
反復サイクルは、照射モード4時間、冷却モード1時間、結露モード3時間の順とした。照射モードは室温63℃、相対湿度50%とし、冷却モードは、室温15℃。相対湿度95%とした。結露モードでは、攪拌ファンを停止したままの状態で加湿ヒータを加熱し、加熱開始から7分後に攪拌ファンを運転して、相対湿度を95%に保持しままま、室温を30℃まで上昇させた。
The repetition cycle was in the order of
この反復サイクルを通算400時間継続し、200時間経過時及び400時間経過時の試料表面における光沢保持率、色差を調べた。
[比較例3]
実施例2に対する比較例として、同じ試料及び試験装置を使用し、反復サイクルの異なる耐候性試験を行った。反復サイクルは、照射モード4時間、結露モード4時間の順とした。照射モードは室温63℃、相対湿度50%とし、結露モードは、加熱ヒータを加熱しはじめると同時に攪拌ファンを運転して、相対湿度を95%に保持しままま、室温を30℃まで上昇させた。
This repeated cycle was continued for 400 hours, and the gloss retention and color difference on the sample surface after 200 hours and 400 hours were examined.
[Comparative Example 3]
As a comparative example with respect to Example 2, the same sample and test apparatus were used, and different weathering tests with repeated cycles were performed. The repetition cycle was in the order of
この反復サイクルを、実施例2と同様に通算400時間継続し、200時間経過時及び400時間経過時の試料表面における光沢保持率、色差を調べた。 This repeated cycle was continued for 400 hours in the same manner as in Example 2, and the gloss retention and color difference on the sample surface after 200 hours and after 400 hours were examined.
実施例2及び比較例3の結果を表1に示す。
The results of Example 2 and Comparative Example 3 are shown in Table 1.
1 試験槽
2 試料台
3 光源
5 加湿ヒータ
7 攪拌ファン
1
7 Stirrer fan
Claims (2)
試験槽内を一定時間、低温高湿状態に保持して、試料全体を表裏均一に冷却した後、
攪拌ファンを停止した状態で加湿ヒータを加熱して、試験槽内を加湿しつつ、室温を上昇させ、
試験槽内の湿度及び温度が上昇しはじめて所定時間経過してから攪拌ファンを運転することにより、試料表面の温度上昇を室温上昇よりも遅らせて試料の表面に結露を発生させることを特徴とする耐候性試験方法。 A sample of the exterior material is placed in a test chamber in which humidification means for generating water vapor by heating of the humidification heater and air agitation means for circulating air in the test tank by operation of the agitation fan are housed,
After keeping the inside of the test chamber at a low temperature and high humidity for a certain period of time,
While heating the humidification heater with the stirring fan stopped, the room temperature is raised while humidifying the inside of the test chamber,
By operating the stirring fan after a certain period of time has passed since the humidity and temperature in the test chamber have started to rise, the temperature rise on the sample surface is delayed from the room temperature rise, causing condensation on the sample surface. Weather resistance test method.