JP4367847B2 - Original polyester multifilament yarn for carpet, production method thereof, and carpet - Google Patents

Description

本発明は、特に柔らかな風合いを持ち、人が直接素肌で接しても肌触りがよく、プードル犬の体毛のようにカールしたパイルを植設したカーペットおよびそのカーペット用糸の製造技術に関するものである。   TECHNICAL FIELD The present invention relates to a carpet having a soft texture and having a good touch even when a person touches it directly with bare skin, and a technique in which a carpet piled like a poodle dog's hair is planted, and a technique for producing the yarn for the carpet. .

カーペットに求められる性能はその用途によって様々で、防音性、防汚性、抗菌性、防ダニ性、吸音性、断熱性、消臭性、防滑性、クッション性等の機能性を要求されたり、カーペット本来の特性である色や柄、風合いやタッチ感、ボリューム感、踏み心地といった人の感性に及ぶ要求まで様々な要求がなされている。   The performance required for carpets varies depending on the application, and functions such as soundproofing, antifouling, antibacterial, mite-proofing, sound-absorbing, heat-insulating, deodorant, anti-slip, and cushioning are required, Various demands have been made, including color and patterns that are the original characteristics of carpets, textures, touch, touch, volume, and treading.

特に家庭用カーペットに要求される性能としては、人がカーペットの上に横になったり、裸足で歩いたりすることが多いことから、肌触りがよく柔らかな風合いのカーペットが好まれている。   In particular, the performance required for household carpets is that carpets that are soft and soft are preferred because people often lie on the carpet or walk barefoot.

従来からある技術としては、カーペット用糸の繊維を細くして柔らかな風合いにしたり、繊維断面を扁平にしたり、後加工としてポリシャー加工のようにカーペットパイルに熱を加えながら繊維を引き伸ばし、艶を出しながら柔らかな風合いに仕上る技術等数多くの提案がなされてきている。   Conventional techniques include thinning the carpet yarn fibers to make them soft, flattening the cross section of the fibers, and post-processing to stretch the fibers while applying heat to the carpet pile as in the polisher process. Numerous proposals have been made, such as techniques for producing a soft texture while out.

特許文献１においては、単繊維繊度が３．５〜８．０デニール、単繊維の扁平度が３．０〜５．０、沸騰水処理後の捲縮伸長率が５．０〜２０％のポリアミドマルチフィラメントを使ったカーペットが開示されている。この方法は、柔らかな風合いで肌触りもよく、腰が強いと共に耐久性に優れたカーペットとして、特に素肌に直接接触して使用する家庭用ラグマットとして好適なカーペットを提供するものである。   In Patent Document 1, the single fiber fineness is 3.5 to 8.0 denier, the flatness of the single fiber is 3.0 to 5.0, and the crimp elongation after boiling water treatment is 5.0 to 20%. A carpet using polyamide multifilaments is disclosed. This method provides a carpet suitable for use as a carpet having a soft texture, good touch, strong waist and excellent durability, and particularly as a household rug mat used in direct contact with bare skin.

しかしながら、本発明のように、糸を細くしても少ない糸量でカバーリング性が良く、特に柔らかな風合いで、人が直接素肌で接しても肌触りがよく、プードル犬の体毛を触るような感覚のカールしたパイル糸を植設したカーペットを製造する技術は未だ開示されていない。
特開２０００−２２００５０ However, as in the present invention, even if the thread is thin, the covering property is good with a small amount of thread, especially with a soft texture, and even when touched directly by human skin, it feels good and touches the poodle dog's body hair. A technique for producing a carpet in which a sensed curled pile yarn is implanted has not yet been disclosed.
JP2000-222005

本発明は、かかる技術的背景に鑑みてなされたものであって、特に柔らかな風合いを持ち、人が直接素肌で接しても肌触りがよく、プードル犬の体毛のようにカールしたパイル糸を植設し、細い糸でもカバーリング性が良く、従来にない風合いのカーペットを提供することを目的とする。   The present invention has been made in view of such a technical background, and has a particularly soft texture and feels good even when a person directly touches the bare skin, and planted pile yarn curled like the hair of a poodle dog. The purpose of the present invention is to provide a carpet with an unprecedented texture that has good covering ability even with thin threads.

本発明者らは、捲縮を付与したフィラメント糸を編上げ、熱セット後に解編して、屈曲のある糸とし、この糸をカーペットのパイル糸とすることにより、細い糸でもカバーリング性が良く、従来にない風合いのカーペットを得ることができる本発明に到達した。上記目的を達成するために、本発明は以下の手段を提供する。
［１］カーペット用原着ポリエステルマルチフィラメント糸の製造方法であって、単繊維繊度が１〜１０デシテックス、単繊維の異形度が１．２〜３．５、捲縮伸長率が５．０〜３５％の原着ポリエステルマルチフィラメントからなる無撚もしくは有撚の繊維糸条で編地を作成する工程と、該編地を熱セットする工程と、該編地を熱セット後に解編する工程とを包含することを特徴とするカーペット用原着ポリエステルマルチフィラメント糸の製造方法。
The present inventors have knitted a filament yarn that has been crimped, knitted after heat setting to form a bent yarn, and this yarn is used as a carpet pile yarn. Thus, the present invention has been achieved, which can provide a carpet with a texture that has never been seen before. In order to achieve the above object, the present invention provides the following means.
[1] A method for producing a polyester multifilament yarn for carpet, wherein the single fiber fineness is 1 to 10 dtex, the single fiber irregularity is 1.2 to 3.5, and the crimp elongation is 5.0 to A step of creating a knitted fabric with untwisted or twisted fiber yarns made of 35% original polyester multifilament, a step of heat-setting the knitted fabric, and a step of knitting the knitted fabric after heat-setting. A process for producing an original polyester multifilament yarn for carpets.

［２］前記編地を熱セットする時、無緊張状態で熱セットすることを特徴とする前項１記載のカーペット用原着ポリエステルマルチフィラメント糸の製造方法。
[2] The method for producing a polyester multifilament yarn for a carpet as described in the preceding item 1, wherein when the knitted fabric is heat-set, the knitted fabric is heat-set in an unstrained state.

［３］前項１または２のいずれかの項に記載の製造方法で製造されたカーペット用原着ポリエステルマルチフィラメント糸。
[3] An original polyester multifilament yarn for carpets produced by the production method according to any one of items 1 and 2.

［４］前記カーペット用原着ポリエステルマルチフィラメント糸が、総繊度が６００〜３５００デシテックス、撚数が４０〜１５０回／ｍあることを特徴とする前項３に記載のカーペット用原着ポリエステルマルチフィラメント糸
[4] the carpet dyed polyester multifilament yarn, the total fineness of 600 to 3500 dtex, carpet dyed polyester multifilament yarn according to item 3 twist number is equal to or in 40-150 times / m

［５］前項３または４に記載のカーペット用原着ポリエステルマルチフィラメント糸をパイル糸として少なくとも一部または全てに用いて構成されたカーペット。
[5] A carpet constructed using at least part or all of the polyester multifilament yarn for carpet as described in the above item 3 or 4 as pile yarn.

［６］前項３または４に記載のカーペット用原着ポリエステルマルチフィラメント糸をパイル糸として用いて構成されたカットパイルである前項５に記載のカーペット。
[6] The carpet according to item 5 above, wherein the carpet is a cut pile formed using the polyester multifilament yarn for carpet as described in item 3 or 4 as a pile yarn.

［７］前項３または４に記載のカーペット用原着ポリエステルマルチフィラメント糸をパイル糸として用いて構成されたカーペットであって、パイル糸が捲縮による屈曲と、編地の熱セットによる屈曲を形成していることを特徴とする前項５又は６に記載のカーペット。

[7] A carpet configured using the polyester multifilament yarn for carpet as described in the above item 3 or 4 as a pile yarn, wherein the pile yarn forms a bend due to crimping and a bend due to heat setting of the knitted fabric. 7. The carpet according to item 5 or 6 above, wherein

［８］前記編地の熱セットによる屈曲が、１パイルに一回以上屈曲していることを特徴とする前項７に記載のカーペット。   [8] The carpet according to item 7 above, wherein the knitted fabric is bent by heat setting at least once per pile.

［１］の発明では、無撚もしくは有撚の繊維糸条で編地を作成する工程と、該編地を熱セットする工程と、該編地を熱セット後に解編する工程とからカーペット用糸が製造されるので、編み上げた形に糸が熱セットされているため、解編するとカールされたような屈曲した糸形状の糸が得られる。また、単繊維繊度が１〜１０デシテックス、単繊維の異形度が１．２〜３．５、捲縮伸長率が５．０〜３５％のマルチフィラメントからなるので繊度が細く、異形度のあるフィラメントからなるので、カーペットとした場合に柔らかく、品位のある風合いで、カバーリング性の良いカーペットとなることができる。   In the invention of [1], for a carpet, a step of creating a knitted fabric with untwisted or twisted fiber yarns, a step of heat setting the knitted fabric, and a step of knitting the knitted fabric after heat setting. Since the yarn is manufactured, the yarn is heat-set in a knitted shape, so that when bent, a bent yarn shape that is curled is obtained. Moreover, since the single fiber fineness is 1 to 10 dtex, the single fiber has an irregularity of 1.2 to 3.5, and the crimped elongation is 5.0 to 35%, the fineness is thin and the irregularity is present. Since it consists of filaments, when it is made into a carpet, it can be made into a carpet that is soft, has a fine texture, and has good covering properties.

［２］の発明では、編地を熱セットする時、無緊張状態で熱セットするので、緊張状態で熱セットするよりもボリューム感あるカバーリング性の良いカーペット用糸を得ることができる。   In the invention of [2], when the knitted fabric is heat-set, it is heat-set in a non-tensioned state, so that it is possible to obtain a carpet yarn with a good volume and covering ability compared to heat setting in a tensioned state.

［３］の発明では、カールされたような屈曲した糸形状で、柔らかく、ボリューム感あるカーペット用糸が提供される。   In the invention of [3], a carpet yarn that is soft and voluminous in a bent yarn shape that is curled is provided.

［４］の発明では、前記マルチフィラメントが熱可塑性樹脂繊維からなり、総繊度が６００〜３５００デシテックス、撚数が４０〜１５０回／ｍあるので、解編時にもカールされたような屈曲が残り、熱セットされてもパイル糸としてカバーリング性がよく、カーペットとなった時、適度に解撚する柔らなカーペット用糸が提供される。   In the invention of [4], the multifilament is made of thermoplastic resin fibers, and has a total fineness of 600 to 3500 dtex and a twist number of 40 to 150 times / m. Even when heat-set, there is good covering property as a pile yarn, and a soft carpet yarn that can be untwisted moderately when it becomes a carpet is provided.

［５］の発明では、前項３〜５に記載のカーペット用糸をパイル糸として少なくとも一部または全てに用いて構成されているので十分な捲縮を備え、カールされた糸形状を保ったままの柔らかい風合いのカーペットを得ることができる。   In the invention of [5], the carpet yarn according to any one of the preceding items 3 to 5 is used as at least a part or all of the pile yarn, so that it has sufficient crimps and maintains the curled yarn shape. You can get a soft texture carpet.

［６］の発明では、カットパイルのカーペットであるため、ループパイルの場合よりもカールされた糸形状の特徴を表現しやすく、プードル犬の体毛のようにカールされた屈曲のある糸形状を保ったままの柔らかい風合いのカーペットを得ることができる。また、パイルの先端が適度に解撚して開き、しかも屈曲していることから、カバーリング性のよい柔らかい風合いのカーペットを得ることができる。   In the invention of [6], since it is a cut-pile carpet, it is easier to express the characteristics of the curled thread shape than in the case of a loop pile, and the bent and curled thread shape like poodle dog hair is maintained. A carpet with a soft texture can be obtained. Further, since the tip of the pile is appropriately untwisted and opened, and is bent, it is possible to obtain a carpet with a soft texture with good covering properties.

［７］の発明では、パイルが図１に示すように、捲縮による屈曲と、編地の熱セットによる屈曲をの二つの屈曲を形成しているので、カバーリング性のよい柔らかい風合いのカーペットを得ることができる。   In the invention of [7], as shown in FIG. 1, the pile forms two bends, a bend caused by crimping and a bend caused by heat setting of the knitted fabric. Therefore, the carpet has a soft texture with good covering properties. Can be obtained.

［８］の発明では、編地の熱セットによる屈曲が、１パイルに一回以上屈曲しているのでカバーリング性が向上した柔らかい風合いのカーペットを得ることができる。   In the invention of [8], since the bending of the knitted fabric by heat setting is bent at least once per pile, a soft texture carpet with improved covering properties can be obtained.

以下、この発明に係るカーペット用糸の製造方法について説明する。異形断面を有する捲縮糸は、基本的に公知の溶融紡糸、冷却、給油、延伸、捲縮の各工程からなる通常の方法によって製造され、溶融吐出する際の口金の吐出口の形状と吐出量、引き取り速度などの紡糸条件を目的に合わして調整することによって得られる。まず、本発明のカーペット用糸を得るために、単繊維繊度が１〜１０デシテックス、単繊維の異形度が１．２〜３．５、捲縮伸長率が５．０〜３５％となるように紡糸条件を設定しフィラメント糸を得る。つぎにこのフィラメント糸を４０〜１５０回／ｍで撚り合わせて、総繊度が６００〜３５００デシテックスの繊維糸条を得、その後丸編機にて編み上げ、テンションを掛けずに無緊張状態で熱セットし、冷却後ワインダーにて糸端を引出しながら解編してカーペット用糸を巻き取る。   Hereinafter, a method for producing carpet yarn according to the present invention will be described. A crimped yarn having a modified cross-section is manufactured by a conventional method basically consisting of known melt spinning, cooling, oiling, stretching, and crimping processes, and the shape and discharge of the discharge port of the die at the time of melting and discharging. It can be obtained by adjusting the spinning conditions such as amount and take-up speed in accordance with the purpose. First, in order to obtain the carpet yarn of the present invention, the single fiber fineness is 1 to 10 dtex, the single fiber irregularity is 1.2 to 3.5, and the crimp elongation is 5.0 to 35%. Set the spinning conditions to obtain filament yarn. Next, the filament yarn is twisted at 40 to 150 times / m to obtain a fiber yarn having a total fineness of 600 to 3500 dtex, then knitted by a circular knitting machine, and heat set in a tensionless state without applying tension. After cooling, the yarn is knitted while being pulled out by a winder to wind up the carpet yarn.

前記カーペット用糸の単繊維繊度は１〜１０デシテックスが好ましく、１デシテックスを下回ると製糸性が悪く、カーペットとしての腰がなくなり、パイルが柔らかくなり過ぎるので好ましくない。また１０デシテックスを超えると硬い風合いのカーペットとなるので好ましくない。マルチフィラメントは熱可塑性樹脂繊維からなり、特に限定されるものではないが、ポリエステル繊維、ナイロン繊維、アクリル繊維等が家庭用カーペットとして好ましく使用される。   The single fiber fineness of the carpet yarn is preferably 1 to 10 decitex, and if it is less than 1 decitex, the yarn-making property is poor, the waist as a carpet is lost, and the pile becomes too soft. On the other hand, if it exceeds 10 dtex, it becomes a hard texture carpet, which is not preferable. The multifilament is made of thermoplastic resin fiber and is not particularly limited, but polyester fiber, nylon fiber, acrylic fiber, and the like are preferably used as household carpets.

前記異形断面を有するカーペット用糸の単繊維断面の異形度は、１．２〜３．５が好ましい。１．２を下回るとカーペット用糸として品位の良い糸とならないので好ましくない。また３．５を超えると紡糸中に糸切れや毛羽が発生しやすくなるので好ましくない。より好ましい異形度は１．５〜３．０がよい。本発明において異形度とは、繊維断面の外接円直径（Ｂ）と内接円直径（Ａ）の比Ｂ／Ａから算出する。   The degree of irregularity of the single fiber cross section of the carpet yarn having the irregular cross section is preferably 1.2 to 3.5. If the ratio is less than 1.2, it is not preferable because the yarn does not become high-quality as carpet yarn. On the other hand, if it exceeds 3.5, yarn breakage and fluff are likely to occur during spinning, which is not preferable. More preferably, the degree of profile is 1.5 to 3.0. In the present invention, the degree of irregularity is calculated from the ratio B / A of the circumscribed circle diameter (B) and the inscribed circle diameter (A) of the fiber cross section.

前記カーペット用糸の捲縮伸長率は５．０〜３５％が好ましい。５．０％を下回ると捲縮発現が不足しカバーリング性が不足し、柔らかな風合いが得られなくなるので好ましくない。また３５％を超えると捲縮発現が大きく単繊維の先端の屈曲が著しく、風合いが硬くなりカーペットとしての品位のないフェルト調のものとなるので好ましくない。   The crimp elongation of the carpet yarn is preferably 5.0 to 35%. If it is less than 5.0%, the expression of crimp is insufficient, the covering property is insufficient, and a soft texture cannot be obtained. On the other hand, if it exceeds 35%, the occurrence of crimp is large and the bending of the tip of the single fiber is remarkable, and the texture becomes hard and the felt becomes inferior as a carpet.

本発明における捲縮伸長率とは、無荷重状態で３０分間沸騰水で浸漬処理した後、平衡水分率まで乾燥し、次式により算出する値で、捲縮発現の程度を示す指標である。
捲縮伸長率（％）＝［（Ｌ_２−Ｌ_１）／Ｌ_２］×１００ ここでＬ_１は試料糸に２ｍｇ／ｄｔｅｘの初期荷重をかけ３０秒経過後に試料長５０ｃｍ（Ｌ_１）に印を入れ、次いで同試料に１００ｍｇ／ｄｔｅｘの荷重をかけて３０秒経過後に伸びた試料長（Ｌ_２）を測定し捲縮伸長率（％）を求める。 The crimp elongation rate in the present invention is an index indicating the degree of crimp development by a value calculated by the following equation after being dipped in boiling water for 30 minutes in an unloaded state and then dried to an equilibrium moisture content.
Crimp elongation (%) = [(L ₂ −L ₁ ) / L ₂ ] × 100 Here, L ₁ applies an initial load of 2 mg / dtex to the sample yarn, and after 30 seconds, the sample length becomes 50 cm (L ₁ ). Then, a 100 mg / dtex load is applied to the same sample, and the length (L ₂ ) of the sample stretched after 30 seconds is measured to obtain the crimp elongation (%).

前記カーペット用糸の総繊度は６００〜３５００デシテックスであることが好ましい。６００デシテックスを下回るとカーペットとしての腰がなく品格のないものとなる。また、３５００デシテックスを超えるとカールされた糸形状が得にくく柔らかな風合いが得られなくなるので好ましくない。   The total fineness of the carpet yarn is preferably 600 to 3500 dtex. Below 600 decitex, there is no dignity as a carpet and it will be dignified. On the other hand, if it exceeds 3500 dtex, it is difficult to obtain a curled yarn shape and a soft texture cannot be obtained.

本発明のカーペット用糸の撚数は、４０〜１５０回／ｍであるのが好ましい。撚りは、編み立ておよび解編等の工程通過性をよくするためにおこなうが１５０回／ｍを超えると、カーペットのパイルとなった時にカバーリング性が劣り好ましくない。また、４０回／ｍを下回る撚数では工程通過性が悪くなり好ましくない。   The number of twists in the carpet yarn of the present invention is preferably 40 to 150 times / m. Twist is performed to improve processability such as knitting and knitting, but if it exceeds 150 times / m, the covering property is inferior when the carpet is piled. On the other hand, if the number of twists is less than 40 times / m, the process passability is deteriorated.

次にこのカーペット用糸を使って丸編機で編地を作り、そのまま無緊張状態でネットに入れ、真空スチームセッターに投入して熱セットする。この熱セット機は、乾熱式、湿熱式等特に限定されるものではない。また、熱セット温度は７５〜１４０℃が好ましく、セット時間は１〜２時間程度必要である。   Next, a knitted fabric is made with a circular knitting machine using this carpet yarn, put in a net without any tension, put into a vacuum steam setter and heat set. The heat setting machine is not particularly limited, such as a dry heat type or a wet heat type. The heat setting temperature is preferably 75 to 140 ° C., and the setting time is about 1 to 2 hours.

本発明における無緊張状態で熱セットするというのは、前述の丸編機で編地を作り、いったん巻き取った後に熱セット機に投入するのではなく、丸編機で編まれた直後の編地をそのまま張力を加えずにネットに入れてから熱セット機に入れ、セット温度で一定時間経過させることをいい、このあと一旦巻きとってから解編機を使って糸に戻してもよいし、巻き取らずにそのままワインダー等で解編してもよい。無緊張状態で熱セットするのと緊張状態で熱セットするのでは、糸のふくらみ方に差が生じカーペットとなった時に、カバーリング性に差が見られる。   In the present invention, heat setting in a non-tensioned state means that a knitted fabric is made by the circular knitting machine described above, and is not wound and then put into the heat setting machine, but immediately after being knitted by the circular knitting machine. Put the ground in the net without applying tension, put it in the heat setting machine, let it elapse for a certain time at the set temperature, then wind it up and then use the deknitting machine to return it to the yarn Alternatively, it may be disassembled with a winder or the like without winding. There is a difference in covering properties between the heat setting in a non-tensioned state and the heat setting in a tensioned state when a difference occurs in how the yarn swells and the carpet is formed.

このようにして作成したカーペット用糸を、パイル糸として用い、タフティング機によってカーペット生機を作成し、続いて公知の方法によってバッキング加工しカーペットとするものである。本発明のカーペットのパイル高さは目的に応じて適宜設定すれば良いが、ハイカットローループのような柄カーペットの場合パイル高さは５ｍｍ〜３０ｍｍ、好ましくは５ｍｍ〜２５ｍｍの範囲が、カール状の柔らかいな風合いの柄カーペットを得るにはよい。プレーンカットカーペットの場合のパイル高さは８ｍｍ〜３０ｍｍ、より好ましくは１２ｍｍ〜２５ｍｍの範囲がよい。   The carpet yarn produced in this way is used as a pile yarn, a carpet living machine is produced by a tufting machine, and then backed by a known method to obtain a carpet. The pile height of the carpet of the present invention may be appropriately set according to the purpose, but in the case of a patterned carpet such as a high cut low loop, the pile height is 5 mm to 30 mm, preferably in the range of 5 mm to 25 mm. Good for getting a soft textured carpet. In the case of a plain cut carpet, the pile height is 8 mm to 30 mm, more preferably 12 mm to 25 mm.

以下、実施例によって本発明をより詳しく説明する。上述の説明中、および以下に述べる実施例における各物性は下記の方法で測定した値である。
［総繊度］ＪＩＳ Ｌ１０９０により測定した。
［単繊維繊度］総繊度を単繊維数で除して求める。
［カーペットのタッチ感］素手による触感によった官能評価で、カーペットの柔らかさ、肌触りを相対的に下記のような基準で評価した。
◎極めて柔らかく、肌触りがよい。
○柔らかく、肌触りがよい。
△やや柔らかさと肌触りに劣る。
×柔らかさと肌触りに劣る。
［製糸性］紡糸時の糸切れの回数から相対的に下記のような基準で評価した。
◎糸切れが発生しない。
○糸切れがほとんど発生しない。
△糸切れがやや発生しする。
×糸切れが頻発する。
［カバーリング性］カーペットを真上から目視し基布の見え方から相対的に下記のような基準で評価した。
◎基布が全く見えない。
○基布がほとんど見えない。
△基布が見えるが、パイルを手で触れると見えなくなる。
×基布がよく見える。パイルを手で触れても見える。
［カーペットの総合評価］家庭用カーペットとしての適合性を相対的に下記のような基準で評価した。
◎極めて適合性良好。
○適合性良好。
△適合性にやや劣る。
×適合性不良。 Hereinafter, the present invention will be described in more detail with reference to examples. Each physical property in the above description and in the examples described below is a value measured by the following method.
[Total Fineness] Measured according to JIS L1090.
[Single fiber fineness] The total fineness is divided by the number of single fibers.
[Carpet touch feeling] By the sensory evaluation based on the touch feeling with bare hands, the softness and touch of the carpet were relatively evaluated according to the following criteria.
◎ Extremely soft and soft to the touch.
○ Soft and soft to the touch.
ΔSlightly inferior in softness and touch.
× Inferior to softness and touch.
[Yarn-making property] Evaluation was made based on the following criteria relative to the number of yarn breaks during spinning.
◎ No thread breakage occurs.
○ There is almost no thread breakage.
△ Some thread breakage occurs.
× Thread breaks occur frequently.
[Covering property] The carpet was visually observed from directly above, and was evaluated according to the following criteria relative to the appearance of the base fabric.
◎ The base fabric is not visible at all.
○ The base fabric is hardly visible.
△ You can see the base fabric, but it disappears when you touch the pile with your hand.
× The base fabric is clearly visible. It can be seen by touching the pile.
[Comprehensive evaluation of carpets] The compatibility as a household carpet was relatively evaluated based on the following criteria.
◎ Extremely good compatibility.
○ Good compatibility.
△ Slightly inferior to suitability.
× Poor suitability.

＜実施例１＞
総繊度は２８００デシテックス（１４００ｄｔｅｘ／２ｐ、撚り数６０回／ｍ）、単繊維繊度が２．５デシテックス、単繊維の断面形状をトライローバルとし異形度が１．５、捲縮伸長率が２５．０％の原着ポリエステルマルチフィラメント糸を２．５ゲージの丸編機で編地を作成し、そのままネットに入れ、真空スチームセット機に無緊張状態で投入し１３０℃、９０分間経過後取り出し冷却してから、ワインダーで解編した。得られた糸には屈曲が形成され、伸縮性に優れた糸であった。この糸を５／３２インチゲージカットのタフティング機に仕掛け、基布としてポリエステルスパンボンド不織布（目付１００ｇ／ｍ^２）を用い、ステッチ６．０／インチ、パイル長１８ｍｍのカーペット表皮を作成し、バッキング加工を施してカーペットとした。加工性には問題なく、得られたカーペットの表面のタッチ感は非常に柔らかく、風合いはカールされた糸形状を保ったままの凹凸感に富んだランダム風合いとなり、カバーリング性も良好なものであった。 <Example 1>
The total fineness is 2800 dtex (1400 dtex / 2p, number of twists 60 times / m), the single fiber fineness is 2.5 dtex, the cross-sectional shape of the single fiber is trilobal, the deformity is 1.5, and the crimp elongation is 25. Create a knitted fabric with 0% original polyester multifilament yarn with a 2.5 gauge circular knitting machine, put it into a net as it is, put it into a vacuum steam set machine in a non-tensioned state, take it out at 130 ° C for 90 minutes and cool it down Then, it was disassembled with a winder. The obtained yarn was bent and formed with excellent stretchability. This yarn was put on a 5/32 inch gauge cut tufting machine, a polyester spunbond nonwoven fabric (100 g / m ² per unit area) was used as a base fabric, and a carpet skin having a stitch of 6.0 / inch and a pile length of 18 mm was prepared. Backing was applied to make the carpet. There is no problem in processability, the touch feeling of the surface of the obtained carpet is very soft, the texture is a random texture rich in unevenness while maintaining the curled thread shape, and the covering property is also good there were.

＜実施例２＞
次に、単繊維の異形度が２．０、総繊度は６００（３００ｄｔｅｘ／２ｐ、撚り数５０回／ｍ）、ステッチ８．０／インチとした以外は実施例１と同様にしたところ実施例１と同様にタッチ感は柔らかく、カールされた糸形状を保ったままランダム方向にパイルが倒れ、カバーリング性にはやや劣るものの、凹凸感に富んだ風合いとなり良好なものであった。 <Example 2>
Next, Example 1 was carried out in the same manner as Example 1 except that the single fiber had a deformity of 2.0, a total fineness of 600 (300 dtex / 2p, 50 twists / m), and a stitch of 8.0 / inch. The touch feeling was soft as in No. 1, and the pile collapsed in the random direction while maintaining the curled yarn shape, and the covering property was slightly inferior, but the texture was rich in unevenness and good.

＜実施例３＞
スチームセット機に緊張状態で投入した以外は実施例１と同様にしたところ、パイル糸のふくらみはやや劣るものの、また趣のかわった風合いとなり、タッチ感も柔らかく良好なものであった。 <Example 3>
Except for being put into a steam setting machine in a tensioned state, the same procedure as in Example 1 was performed, but the pile yarn bulge was slightly inferior, but also had a different texture, and the touch feeling was soft and good.

＜比較例１＞
次に、実施例１においてスチームセット機に通さずに解編した糸を使用した以外は実施例１と同様にしたところ、カールされた糸形状がバッキング加工を行なった時にとれ、タッチ感は柔らかいものの、プードル犬の体毛を触るような感覚は無く、単なる柔らかい風合いのカーペットとなってしまった。 <Comparative Example 1>
Next, the same procedure as in Example 1 was performed except that the yarn knitted without passing through the steam setting machine was used in Example 1, and the curled yarn shape was removed when backing processing was performed, and the touch feeling was soft. However, there was no sensation of touching the poodle dog's hair, and it was just a soft carpet.

＜比較例２＞
実施例１において、総繊度は９００デシテックス（４５０ｄｔｅｘ／２ｐ、撚り数６０回／ｍ）、単繊維繊度が０．８デシテックス、とした以外は実施例１と同様にしたところ、カールされた糸形状を保ったままの、柔らかな風合いのカーペットが得られたが、製糸性が悪く採用されなかった。 <Comparative example 2>
In Example 1, when the total fineness was 900 dtex (450 dtex / 2p, number of twists 60 times / m) and the single fiber fineness was 0.8 dtex, the same curled yarn shape was used as in Example 1. A carpet with a soft texture was obtained, but the yarn production was poor and was not adopted.

＜比較例３＞
実施例１において、単繊維の異形度を４．５とした以外は実施例１と同様にしたところ、比較例２と同様に製糸性が悪く採用されなかった。 <Comparative Example 3>
In Example 1, except that the monofilament profile was changed to 4.5, the same procedure as in Example 1 was carried out.

＜比較例４＞
実施例１において、捲縮付与時の熱処理を強化し捲縮伸長率を３８．０％とした以外は実施例１と同様にしたところ、バッキング工程で捲縮が大きく発現し、フェルトのような風合いになってしまった。 <Comparative example 4>
In Example 1, except that the heat treatment at the time of crimping was strengthened and the crimp elongation rate was set to 38.0%, it was performed in the same manner as in Example 1. It has become a texture.

このようにして得られたカーペットの「タッチ感」「製糸性」「カバーリング性」「総合評価」について評価した結果を表１に示す。

Table 1 shows the evaluation results of “touch feeling”, “yarn-making property”, “covering property”, and “overall evaluation” of the carpet thus obtained.

この発明のカーペットの一例を示す概略図であるIt is the schematic which shows an example of the carpet of this invention.

符号の説明Explanation of symbols

１…カーペット
２…パイル糸
３…基布
４…バッキング材 1 ... carpet 2 ... pile yarn 3 ... base fabric 4 ... backing material

Claims (8)

カーペット用原着ポリエステルマルチフィラメント糸の製造方法であって、単繊維繊度が１〜１０デシテックス、単繊維の異形度が１．２〜３．５、捲縮伸長率が５．０〜３５％の原着ポリエステルマルチフィラメントからなる無撚もしくは有撚の繊維糸条で編地を作成する工程と、該編地を熱セットする工程と、該編地を熱セット後に解編する工程とを包含することを特徴とするカーペット用原着ポリエステルマルチフィラメント糸の製造方法。 A method for producing a polyester multifilament yarn for carpet, wherein the single fiber fineness is 1 to 10 dtex, the single fiber irregularity is 1.2 to 3.5, and the crimp elongation is 5.0 to 35%. It includes a step of creating a knitted fabric with untwisted or twisted fiber yarns composed of an original polyester multifilament, a step of heat setting the knitted fabric, and a step of knitting the knitted fabric after heat setting. A method for producing an initial polyester multifilament yarn for carpets. 前記編地を熱セットする時、無緊張状態で熱セットすることを特徴とする請求項１記載のカーペット用原着ポリエステルマルチフィラメント糸の製造方法。 The method for producing a polyester multifilament yarn for carpet according to claim 1, wherein when the knitted fabric is heat-set, the knitted fabric is heat-set without tension. 請求項１または２のいずれかの項に記載の製造方法で製造されたカーペット用原着ポリエステルマルチフィラメント糸。 A polyester original multifilament yarn for carpet produced by the production method according to claim 1. 前記カーペット用原着ポリエステルマルチフィラメント糸が、総繊度が６００〜３５００デシテックス、撚数が４０〜１５０回／ｍあることを特徴とする請求項３に記載のカーペット用原着ポリエステルマルチフィラメント糸。 Carpet dyed polyester multifilament yarn according to claim 3 wherein the carpet dyed polyester multifilament yarn, the total fineness of 600 to 3500 dtex, the number of twists is characterized in that there 40-150 times / m. 請求項３または４に記載のカーペット用原着ポリエステルマルチフィラメント糸をパイル糸として少なくとも一部または全てに用いて構成されたカーペット。 A carpet constructed by using the polyester multifilament yarn for carpet according to claim 3 or 4 as at least a part or all as a pile yarn. 請求項３または４に記載のカーペット用原着ポリエステルマルチフィラメント糸をパイル糸として用いて構成されたカットパイルである請求項５に記載のカーペット。 The carpet according to claim 5, wherein the carpet is a cut pile constituted by using the polyester multifilament yarn for carpet as described in claim 3 or 4 as a pile yarn. 請求項３または４に記載のカーペット用原着ポリエステルマルチフィラメント糸をパイル糸として用いて構成されたカーペットであって、パイル糸が捲縮による屈曲と、編地の熱セットによる屈曲を形成していることを特徴とする請求項５又は６に記載のカーペット。 A carpet configured using the polyester multifilament yarn for carpet according to claim 3 or 4 as a pile yarn, wherein the pile yarn is bent by crimping and bent by heat setting of a knitted fabric. The carpet according to claim 5 or 6, wherein 前記編地の熱セットによる屈曲が、１パイルに一回以上屈曲していることを特徴とする請求項７に記載のカーペット。   The carpet according to claim 7, wherein the bending of the knitted fabric by heat setting is bent at least once per pile.

Images