Abstract

【課題】敷設する床面またはメディアを傷めることがなく、防炎性能にも優れたフロアマーキングシート及びフロアマーキングシートの施工方法を提供する。
【解決手段】床面Ｆに密着させるゴム面６と反対の面に接着剤層４が設けられているゴムシート２と、広告や誘導サインまたは装飾用の模様などが記録されているシート状のメディア３とを、メディア３の一方の面に設けられている粘着剤層９とゴムシート２の接着剤層４とを対向させた状態で積層し、メディア３の他方の面に、難燃性を有する樹脂からなる保護層１２を設ける。
【選択図】図１The present invention provides a floor marking sheet that does not damage a floor surface or a medium to be laid and has an excellent flameproof performance, and a method for constructing the floor marking sheet.
SOLUTION: A rubber sheet 2 provided with an adhesive layer 4 on a surface opposite to a rubber surface 6 to be in close contact with a floor surface F, and a sheet-like shape on which an advertisement, a guide sign or a decorative pattern is recorded. The medium 3 is laminated with the pressure-sensitive adhesive layer 9 provided on one surface of the medium 3 and the adhesive layer 4 of the rubber sheet 2 facing each other, and the other surface of the medium 3 is flame retardant. A protective layer 12 made of a resin having
[Selection] Figure 1

Description

本発明は、店舗、展示会場、駅構内、官公庁舎、公共施設、工事現場、駐車場など、屋内外を問わず、施設の床面に敷設して宣伝広告や案内表示または床面装飾などを行なうフロアマーキングシート及びフロアマーキングシートの施工方法に関する。   The present invention lays on the floor of a facility, whether indoors or outdoors, such as stores, exhibition halls, station buildings, public office buildings, public facilities, construction sites, parking lots, etc. The present invention relates to a floor marking sheet and a floor marking sheet construction method.

フロアマーキングシートは、おもて面に広告や誘導サインなどが印刷されているメディアを、その裏面に塗布されている接着剤によって床面（例えば、プラスチックタイル、コンクリート床、塗装床）に直接貼着するタイプが一般的に使用されているが、次のような問題点を有している。
（１）接着剤の接着力が低下しないように、敷設時に床面のワックスや汚れを落とす必要があり、また、メディアを撤去したあとは、敷設時に落としたワックスを復旧する必要がある。
（２）接着剤の接着力が強い場合、メディアを床面にしっかりと定着させることができるが、その反面剥がれにくいため、撤去する際の作業が煩雑になるほか、塗装が剥離して床材を傷めたり、接着剤が残って床面を汚したりすることがある。
（３）接着剤の接着力が弱い場合、床面から剥離し易くて撤去作業が比較的簡単に行えるものの、清掃やワックスがけ作業や、人の通行や機器の運搬等によって周縁部が床面から剥離し、通行人や運搬中の機器の転倒などの事故を招くおそれがある。
（４）敷設ならびに撤去の際に、専門の清掃業者や施工業者が必要で時間も要する。 A floor marking sheet is used to attach media with advertisements or guidance signs printed on the front side directly to the floor (for example, plastic tiles, concrete floors, painted floors) with adhesive applied to the back side. Although the type to wear is generally used, it has the following problems.
(1) It is necessary to remove wax and dirt on the floor surface during laying so that the adhesive strength of the adhesive does not decrease, and after removing the media, it is necessary to restore the wax dropped during laying.
(2) If the adhesive has a strong adhesive force, the media can be firmly fixed on the floor surface. However, since it is difficult to peel off, the removal work becomes complicated and the coating is peeled off to remove the floor material. May be damaged, or the adhesive may remain and soil the floor surface.
(3) If the adhesive has a weak adhesive force, it can be easily removed from the floor surface, and the removal work can be performed relatively easily. However, the peripheral edge of the floor surface can be removed by cleaning, waxing, passing people or transporting equipment. May cause accidents such as the fall of passersby or equipment being transported.
(4) When installing and removing, a specialized cleaning company or construction company is required and it takes time.

そこで、これらの問題を解消するため、以下のようなフロアマーキングシートの提案がなされている。即ち、ゴム基材と同ゴム基材の上に配設される図柄の付いたグラフィックシート材（メディア）とからなり、ゴム基材の下面には滑り止めのためのパターンが形成され、グラフィックシート材は図画が描かれた下地層と同下地層の上に設けられる保護層とにより構成されている広告シートである（例えば、特許文献１参照）。この広告シートは接着剤などを用いることなく床面に敷設されるので、施工作業や撤去作業が容易で、且つ接着剤などによって床面を傷めることがない。
特開２００５−２３４３９２号公報（第４頁〜第６頁、第１図〜第２図） In order to solve these problems, the following floor marking sheet has been proposed. That is, it consists of a rubber base material and a graphic sheet material (media) with a pattern arranged on the rubber base material, and a pattern for preventing slippage is formed on the bottom surface of the rubber base material. The material is an advertising sheet composed of a base layer on which a drawing is drawn and a protective layer provided on the base layer (see, for example, Patent Document 1). Since this advertising sheet is laid on the floor without using an adhesive or the like, construction work and removal work are easy, and the floor is not damaged by the adhesive or the like.
JP-A-2005-234392 (pages 4 to 6, FIGS. 1 to 2)

しかしながら、上記広告シートにも次のような問題点がある。即ち、一般に加硫ゴムシートは可塑剤やオイルを多量に含有しているため、これらが滲出し塗装床やプラスチックタイル（Ｐタイル）の床面、さらにグラフィックシートに付着し、これらを変質させたり、汚染したりする場合がある。特に近年では、フロアマーキングシートにおいても、インクジェットをはじめとするデジタル印刷を用いて高彩色でデザイン性の高いグラフィックデザインなどが採用され始めており、このような品質の高いデザインを損なわないためにも、加硫ゴムシートがグラフィックシートに悪影響を及ぼさないような対策が強く求められている。また、フロアマーキングシートは、利用者が多い公共性の高い施設で使用されることが多いため、火災に対する安全性の確保が望まれている。   However, the advertisement sheet has the following problems. In other words, since vulcanized rubber sheets generally contain a large amount of plasticizers and oils, they adhere to the floor surface of exuded paint floors and plastic tiles (P tiles) and further to graphic sheets, It may become contaminated. In particular, in recent years, even in floor marking sheets, graphic designs with high color and high design using digital printing such as inkjet have begun to be adopted, and in order not to impair such high quality designs, There is a strong demand for measures to prevent the vulcanized rubber sheet from adversely affecting the graphic sheet. In addition, since the floor marking sheet is often used in public facilities with many users, it is desired to ensure safety against fire.

そこで本発明は、敷設する床面およびメディアの汚染や損傷を避けることができ、防炎性能にも優れたフロアマーキングシート及びフロアマーキングシートの施工方法を提供することを目的としている。   SUMMARY OF THE INVENTION An object of the present invention is to provide a floor marking sheet and a floor marking sheet construction method that can avoid contamination and damage to the floor surface and media to be laid and have excellent flameproof performance.

請求項１記載のフロアマーキングシートは、床面に敷設して宣伝広告や案内表示または床面装飾などを行うフロアマーキング用シートにおいて、前記床面と密着する面と反対側の面に接着剤層が設けられている加硫ゴムシートと、一方の面に粘着剤層が設けられ他方の面に広告や誘導サインまたは装飾用の模様などが記録されているシート状のメディアとが、当該メディアの粘着剤層と前記加硫ゴムシートの接着剤層とを対向させた状態で積層され、前記メディアの他方の面に、難燃性を有する樹脂からなる保護層が設けられていることを特徴としている。
The floor marking sheet according to claim 1, wherein the floor marking sheet is laid on a floor surface for advertising, guidance display, or floor decoration, and has an adhesive layer on a surface opposite to the surface in close contact with the floor surface. A vulcanized rubber sheet on which one side is provided, and a sheet-like medium on which an adhesive layer is provided on one side and an advertisement, a guide sign, or a decorative pattern is recorded on the other side . The adhesive layer and the adhesive layer of the vulcanized rubber sheet are laminated so as to face each other, and a protective layer made of a flame retardant resin is provided on the other surface of the media. Yes.

このフロアマーキングシートによれば、前記床面に対して前記加硫ゴムシートを密着させることによって定着させるため接着剤などが不要になり、敷設する際（施工時）に前記床面をワックスがけするなど特別な清掃作業を行う必要がない。また、撤去後も接着剤の居着きによる前記床面の汚染や、塗装やコーティングの剥離による前記床面の損傷を回避することができる。したがって、専門業者でなくとも施工作業や撤去作業が行えるとともに、敷設後の一時的な撤去や位置の修正などを手軽に行うことができる。
According to this floor marking sheet, since the vulcanized rubber sheet is fixed to the floor surface by fixing it, an adhesive or the like becomes unnecessary, and the floor surface is waxed when laying (at the time of construction). There is no need for special cleaning work. Further, even after the removal, the floor surface can be prevented from being contaminated due to the adhesion of the adhesive, and the floor surface can be prevented from being damaged due to paint or coating peeling. Therefore, construction work and removal work can be performed without being a specialized contractor, and temporary removal or position correction after laying can be easily performed.

また、前記メディアの前記粘着剤層と前記加硫ゴムシートの前記接着剤層とを対向させた状態で積層するので、前記加硫ゴムシートから滲出した成分が前記メディアに移行することが防止され、前記メディアが変質したり、記録されている広告や誘導サインまたは装飾用の模様などが損傷することを避けることができる。
Further, since the pressure-sensitive adhesive layer of the media and the adhesive layer of the vulcanized rubber sheet are laminated facing each other, it is possible to prevent components that have exuded from the vulcanized rubber sheet from transferring to the media. It is possible to prevent the media from being altered or the recorded advertisements, guide signs or decorative patterns from being damaged.

それから、前記接着剤層と前記粘着剤層とを分離して前記メディアを前記加硫ゴムシートから剥離することができるため、前記メディアだけを交換して使用することができ、前記加硫ゴムシートを繰り返し使用することができる。また、前記メディアと前記加硫ゴムシートとを別々に現場に持ち込み、現場において前記メディアと前記加硫ゴムシートとを一体にすることができるため、印刷機などの記録装置を現場に持ち込んで、前記メディアに記録を行いながら施工することが可能になる。これにより、現場の状況に応じて記録する広告や誘導サインおよび装飾模様などの調整を行いながら施工することが可能になる。前記メディアに記録を行う方法としては、デジタル印刷のほかにも、グラビア印刷やスクリーン印刷をはじめとするアナログ印刷などの公知の方法が適用可能である。また、前記メディアに切り文字を貼り付けて記録を行う方法なども適用可能である。
Then, since the adhesive layer and the pressure-sensitive adhesive layer can be separated and the media can be peeled from the vulcanized rubber sheet, only the media can be used for replacement, and the vulcanized rubber sheet can be used. Can be used repeatedly. In addition, the media and the vulcanized rubber sheet can be brought separately to the site, and the media and the vulcanized rubber sheet can be integrated at the site, so that a recording device such as a printing machine is brought to the site, It is possible to perform construction while recording on the medium. This makes it possible to perform construction while adjusting advertisements, guidance signs, decorative patterns, and the like to be recorded according to the situation at the site. As a method for recording on the medium, in addition to digital printing, known methods such as analog printing including gravure printing and screen printing can be applied. Further, a method of recording by pasting cut characters on the medium can be applied.

前記メディアの前記他方の面には、難燃性を有する樹脂からなる前記保護層が設けられているため防炎性能に優れ、タバコの不始末などによる火災の発生や延焼などを防止することができる。また、前記メディアを汚れや傷などから保護することができるとともに、前記メディアの耐久性を向上させることができる。前記保護層としては、裏面に粘着剤（または接着剤）が塗布されたラミネートフィルと呼ばれる公知の透明フィルムを使用することができる。その中でも耐擦傷性や透明性の観点から塩化ビニル樹脂製のフィルムが好ましい。   The other surface of the media is provided with the protective layer made of a flame-retardant resin, so that it has excellent flameproofing performance, and it is possible to prevent the occurrence of fire or the spread of fire due to tobacco mistreatment. it can. In addition, the media can be protected from dirt and scratches, and the durability of the media can be improved. As the protective layer, a known transparent film called a laminate film having a back surface coated with a pressure-sensitive adhesive (or adhesive) can be used. Among them, a vinyl chloride resin film is preferable from the viewpoint of scratch resistance and transparency.

そして、前記保護層の表面に凹凸を設ければ、水に濡れたときの摩擦係数の低下を抑え、通行人のスリップによる転倒事故を予防することができる。また、前記加硫ゴムシートの前記床面に密着させる面に、エンボス加工等による凹凸を設けることで吸盤に似た効果を生じさせることができ、前記床面にしっかりと定着させることができる。特に、前記床面が水に濡れている場合でも、前記床面と前記加硫ゴムシートとの摩擦係数の低下が抑えられ、前記床面に対してずれにくくなる。また、撤去する際は凹凸があるので剥がしやすいし、見かけの単位体積（厚さ×面積）当りの重量を抑えることができるため、軽量化を図ることができて施工時の作業者の負担を軽減することができる。
If the surface of the protective layer is provided with unevenness, it is possible to suppress a decrease in the coefficient of friction when wetted with water and prevent a fall accident due to a slip of a passerby. Further, by providing unevenness by embossing or the like on the surface of the vulcanized rubber sheet that is brought into close contact with the floor surface, an effect similar to a suction cup can be produced, and the floor surface can be firmly fixed. In particular, even when the floor surface is wet with water, a decrease in the friction coefficient between the floor surface and the vulcanized rubber sheet is suppressed, and the floor surface is less likely to be displaced. In addition, since there are irregularities when removing, it is easy to peel off, and the weight per apparent unit volume (thickness x area) can be suppressed, so it is possible to reduce the weight and burden the operator during construction Can be reduced.

なお、前記メディアとしては塩化ビニル樹脂製が一般的であるが、ポリプロピレンやポリエチレンテレフタレートなどの塩化ビニル樹脂以外の樹脂組成物フィルムや、紙、合成紙なども使用することができる。   The medium is generally made of vinyl chloride resin, but resin composition films other than vinyl chloride resin such as polypropylene and polyethylene terephthalate, paper, and synthetic paper can also be used.

請求項２記載のフロアマーキングシートのように、難燃性を有する樹脂を、塩化ビニル樹脂とすることができる。このとき、塩化ビニル樹脂からなる前記保護層の厚さとしては、少なくとも０．０５ｍｍ以上であればフロアマーキングシートとして防炎性を有するが、フロア敷物としての十分な耐久性を持たせるためには、０．１０ｍｍから０．３０ｍｍであることが望ましい。   As in the floor marking sheet according to claim 2, the resin having flame retardancy can be a vinyl chloride resin. At this time, the thickness of the protective layer made of vinyl chloride resin is flameproof as a floor marking sheet if it is at least 0.05 mm or more, but in order to have sufficient durability as a floor covering. 0.10 mm to 0.30 mm is desirable.

請求項３記載のフロアマーキングシートは、保護層の縁部を、その下方に位置するメディアから加硫ゴムシートまでのいずれの層よりも外方にはみ出した構成にすることを特徴としている。このフロアマーキングシートによれば、前記メディアから前記加硫ゴムシートまでの各層をより一層火炎から効果的に保護できるようになる。特に、積層方向上方から当る火炎が前記保護層を回り込み前記メディア以下の層に到達することを阻止することができる。前記保護層の縁部は、前記フロアマーキングシートの全周にわたってはみ出している構成にすることもできるし、また、複数枚の前記フロアマーキングシートを突き合せた状態にして敷設する場合などは、隣接する前記フロアマーキングシートがない方だけ前記縁部をはみ出させた構成にすることもできる。
The floor marking sheet according to claim 3 is characterized in that the edge portion of the protective layer protrudes outward from any layer from the media positioned below the vulcanized rubber sheet. According to this floor marking sheet, each layer from the media to the vulcanized rubber sheet can be more effectively protected from the flame. In particular, it is possible to prevent a flame that hits from above in the stacking direction from going around the protective layer and reaching the layer below the media. The edge of the protective layer can be configured to protrude over the entire circumference of the floor marking sheet, or adjacent when a plurality of the floor marking sheets are laid in contact with each other. It is also possible to adopt a configuration in which the edge portion protrudes only in the direction where there is no floor marking sheet.

請求項４記載のフロアマーキングシートは、メディアに、粘着剤層側に位置するシート状の基材と、前記保護層側に位置するインク受容層との積層構造を具備させることを特徴としている。このフロアマーキングシートによれば、前記インク受容層にインクを吸収させることによって、前記基材の材質によらず広告や誘導サインまたは装飾用の模様などを前記基材に定着させることができる。また、前記インク受容層によって、インクが前記基材と直接的に接触することを避けることができるため、特に、溶剤系インクによる前記基材の膨潤を防ぐことができ、前記フロアマーキングシートの縁部の捲くれ上がりを抑えることができる。これは、インク中の溶剤を吸収して膨潤した前記基材が、乾燥する際に収縮を起こし、前記加硫ゴムシートとのあいだに寸法差が生じて前記フロアマーキングシートに反りが発生するからである。なお、前記基材の乾燥の進行は遅いので、前記基材が前記メディアに加工されて前記フロアマーキングシートとして前記床面に敷設された状態になっても乾燥が継続し、反りが次第に大きくなって前記フロアマーキングシートの縁部が巻き上がるのである。
The floor marking sheet according to claim 4 is characterized in that the medium is provided with a laminated structure of a sheet-like base material located on the pressure-sensitive adhesive layer side and an ink receiving layer located on the protective layer side. According to this floor marking sheet, by allowing ink to be absorbed by the ink receiving layer, an advertisement, a guide sign, a decorative pattern, or the like can be fixed to the substrate regardless of the material of the substrate. In addition, since the ink receiving layer can prevent the ink from coming into direct contact with the base material, it is possible to prevent the base material from swelling due to the solvent-based ink. It is possible to suppress the rolling up of the club. This is because the base material, which has swollen after absorbing the solvent in the ink, shrinks when dried, causing a dimensional difference between the vulcanized rubber sheet and warping the floor marking sheet. It is. Since the drying of the base material is slow, the drying continues even when the base material is processed into the media and laid on the floor surface as the floor marking sheet, and the warpage gradually increases. Thus, the edge of the floor marking sheet is rolled up.

このように、前記基材の収縮が抑えられることによって、防炎対策においても有利になる。つまり、前記基材に収縮が生じた場合、前記粘着剤層と前記接着剤との結合が弱いと、前記加硫ゴムシート上で前記メディアが滑り、前記加硫ゴムシートが前記メディアからはみ出た状態になるし、結合が強いと反りが発生して前記フロアマーキングシートの縁部が捲くれ上がるから、前記メディアや前記加硫ゴムシートが火炎に曝されて燃えやすくなるからである。
In this way, the suppression of the shrinkage of the base material is advantageous in terms of flameproofing. That is, when shrinkage occurs in the base material, if the bond between the pressure-sensitive adhesive layer and the adhesive is weak, the media slips on the vulcanized rubber sheet, and the vulcanized rubber sheet protrudes from the media. This is because if the connection is strong, warping occurs and the edge of the floor marking sheet is rolled up, so that the media and the vulcanized rubber sheet are exposed to a flame and easily burned.

このような前記メディアとしては、例えば、合成紙がある。合成紙は、通常の繊維質の紙は持ち込むことができないクリーンルームなどでの筆記用紙として使用されている。   An example of such media is synthetic paper. Synthetic paper is used as writing paper in clean rooms where normal fiber paper cannot be brought in.

請求項５記載のフロアマーキングシートは、基材をポリオレフィン系の合成樹脂で構成することを特徴としている。このフロアマーキングシートによれば、汎用樹脂を用いることで価格を抑えることができる。また、ポリオレフィン樹脂は、インクの溶剤を吸収しにくいので、基材に乾燥時の収縮が起こりにくく、その結果として、フロアマーキングシートの反りが生じにくい。   The floor marking sheet according to claim 5 is characterized in that the base material is made of a polyolefin-based synthetic resin. According to this floor marking sheet, the price can be reduced by using a general-purpose resin. In addition, since the polyolefin resin hardly absorbs the ink solvent, the base material is unlikely to shrink during drying, and as a result, the floor marking sheet is unlikely to warp.

請求項６記載のフロアマーキングシートのように、基材をポリプロピレンを素材とする合成紙で構成することができる。合成紙とは、高分子化合物を繊維状に延伸し、それを縦横に組み合わせて圧着し一枚のシート状にしたものであり、一般のプラスチックフィルムと比較して寸法変化がほとんど無く、かつ等方的であるという特長がある。また、素材もポリオレフィン樹脂の一種であるポリプロピレンを結晶状態で使用しているので、耐溶剤性に優れている。これらのことから、基材の乾燥時の収縮が極めて起こりにくく、フロアマーキングシートに反りが発生しない。   As in the floor marking sheet according to claim 6, the base material can be made of synthetic paper made of polypropylene. Synthetic paper is obtained by stretching a polymer compound into a fiber shape and combining it vertically and horizontally into a single sheet, with almost no dimensional change compared to a general plastic film, etc. It has the feature of being ideal. Moreover, since the raw material also uses polypropylene which is a kind of polyolefin resin in a crystalline state, it is excellent in solvent resistance. From these things, shrinkage | contraction at the time of drying of a base material does not occur easily, and a floor marking sheet does not warp.

請求項７記載のフロアマーキングシートの施工方法は、一方の面に粘着剤層が設けられ他方の面に広告や誘導サインまたは装飾用の模様などが記録されているシート状のメディアと、加硫ゴムシートとの積層構造を有するフロアマーキングシートの施工方法であって、前記メディアの他方の面に、難燃性を有する樹脂からなる保護層を積層し、前記メディアと前記加硫ゴムシートとを、前記メディアの一方の面に設けられている前記粘着剤層と、前記加硫ゴムシートの一方の面に設けられている接着剤層とを対向させた状態で積層し、前記加硫ゴムシートの他方の面を床面に密着させて敷設することを特徴としている。
A method of constructing a floor marking sheet according to claim 7, comprising: a sheet-like medium on which an adhesive layer is provided on one side and an advertisement, a guidance sign or a decorative pattern is recorded on the other side; a floor marking sheet construction method having the laminated structure of the rubber Mushito, on the other surface of the medium, and a protective layer made of a resin having a flame retardancy, and the said medium vulcanized rubber sheet , and the adhesive layer provided on one surface of the medium, the stacked while a state in which an adhesive layer provided on a surface to face the vulcanized rubber sheet, the vulcanized rubber sheet It is characterized by laying in contact with the other surface of the floor.

このフロアマーキングシートの施工方法によれば、接着剤などを用いることなく前記床面に定着させるため、専門技術を有していなくても防炎性能を備えた前記フロアマーキングシートを簡単に敷設することができる。また、前記メディアは、前記粘着剤層と前記接着剤層とを分離することによって前記加硫ゴムシートから剥離することができるため、前記フロアマーキングシートを前記床面に敷設したあとでも、前記メディアを手軽に交換することができる。
According to this floor marking sheet construction method, the floor marking sheet having flameproof performance can be laid easily even if it does not have specialized technology in order to be fixed on the floor surface without using an adhesive or the like. be able to. Further, since the media can be separated from the vulcanized rubber sheet by separating the pressure-sensitive adhesive layer and the adhesive layer, the media can be removed even after the floor marking sheet is laid on the floor surface. Can be replaced easily.

請求項８記載のフロアマーキングシートの施工方法は、フロアマーキングシートを床面に敷設したのち、その縁部を係止部材によって周囲に係止することを特徴としている。このフロアマーキングシートの施工方法は、前記フロアマーキングシートの万が一の捲れ上がりを防止することができる。前記係止部材は、捲くれ上がりを防止することができれば前記フロアマーキングシートの全周に設けても良いし、必要な箇所のみに設けても良い。なお、前記係止部材としては、一般的な粘着テープを用いることができるが、例えば、前記保護層を構成している粘着剤（または接着剤）付き透明フィルムを用いると、フロアマーキングシートの外観を損なわず、かつ歩行時の違和感が軽減される。   The construction method of the floor marking sheet according to claim 8 is characterized in that after the floor marking sheet is laid on the floor surface, its edge is locked to the periphery by a locking member. The floor marking sheet construction method can prevent the floor marking sheet from being rolled up. The locking member may be provided on the entire circumference of the floor marking sheet or may be provided only in a necessary portion as long as it can prevent the rolling up. In addition, although a general adhesive tape can be used as the locking member, for example, when a transparent film with an adhesive (or adhesive) constituting the protective layer is used, the appearance of the floor marking sheet The feeling of discomfort during walking is reduced.

請求項１のフロアマーキングシートによれば、１）接着剤などを使用せずに床面に定着させることができるため、専門的な技術を必要とせず容易に施工することができる。また、施工の際に接着剤などを使用しないため床面を汚すことがなく、撤去後の床面の復元作業が簡単に行える。２）加硫ゴムシートを繰り返し使用することができるため、資源の有効利用を図ることができるとともに、宣伝広告や案内表示、床面装飾などにかかる費用を抑えることができる。３）メディアは、汚染や損傷が起こりにくいため長期間使用することができる一方、交換が簡単に行えるため、短いサイクルで模様替えを行うような場合でも容易に対応することができる。４）保護層による防炎性能を備えているため、火災に対する安全性を確保することができる。
According to the floor marking sheet of the first aspect, 1) since it can be fixed on the floor surface without using an adhesive or the like, it can be easily constructed without requiring a special technique. Moreover, since no adhesive is used during construction, the floor surface is not soiled, and the restoration work of the floor surface after removal can be easily performed. 2) Since the vulcanized rubber sheet can be used repeatedly, it is possible to effectively use resources and to suppress costs for advertising, guidance display, floor decoration and the like. 3) The media can be used for a long period of time because contamination and damage are unlikely to occur. On the other hand, since the media can be easily replaced, it is possible to easily cope with a case where the pattern is changed in a short cycle. 4) Since it has a flameproof performance due to the protective layer, safety against fire can be ensured.

請求項２のフロアマーキングシートによれば、汎用樹脂を用いることにより容易かつ安価に製造することができる。   According to the floor marking sheet of Claim 2, it can manufacture easily and cheaply by using a general purpose resin.

請求項３のフロアマーキングシートによれば、炎が保護層を回り込みメディアや加硫ゴムシートに到達することが阻止されるので、防炎性能を高めることができる。 According to the floor marking sheet of the third aspect, since the flame is prevented from reaching the media and the vulcanized rubber sheet through the protective layer, the flameproof performance can be enhanced.

請求項４のフロアマーキングシートによれば、インクの媒体の種類やメディアの基材の種類によらず、縁部の捲くれ上がりを防止することができるため、視認性や見栄えが損なわれることがなく、かつ防炎性能の低下を避けることができる。   According to the floor marking sheet of claim 4, it is possible to prevent the edge from rolling up regardless of the type of ink medium or the type of base material of the media, so that visibility and appearance may be impaired. And a reduction in flameproof performance can be avoided.

請求項５および請求項６のフロアマーキングシートによれば、汎用樹脂を用いることにより容易かつ安価に製造することができるうえ、縁部の捲くれ上がりを効果的に防止することができる。   According to the floor marking sheet of Claim 5 and Claim 6, it can manufacture easily and cheaply by using a general purpose resin, and can also prevent the edge part from rising up effectively.

請求項７のフロアマーキングシートによれば、１）床面の塵や埃などを取り除いて敷設するだけであるため、専門技術が不要で施工に要する人員の削減および施工時間の短縮を図ることができる。これにより、施工コストの低減を実現することができる。２）フロアマーキングシートを撤去する際、床面から簡単に剥がすことができるため、専門の技術者による特殊資材を用いての作業が不要となるとともに、撤去作業の時間を短縮することができる。これにより、撤去作業のコスト低減を実現することができる。３）フロアマーキングシートの移動および復元が簡単に行えるため、フロアマーキングシートが敷設されている床面の清掃を容易に行うことができる。４）メディアの交換を簡単に行うことができ、かつメディアを交換したフロマーキングシートを元の位置に敷設する作業が容易に行えるようになる。   According to the floor marking sheet of claim 7, 1) it is only necessary to remove dust and dirt from the floor surface and lay it down, so that it is possible to reduce the number of personnel required for construction and shorten the construction time without requiring specialized techniques. it can. Thereby, reduction of construction cost is realizable. 2) Since the floor marking sheet can be easily peeled off from the floor surface, work using special materials by a specialized engineer is not necessary, and the time for the removal work can be shortened. Thereby, cost reduction of removal work is realizable. 3) Since the floor marking sheet can be easily moved and restored, the floor surface on which the floor marking sheet is laid can be easily cleaned. 4) Media can be easily exchanged, and the work of laying the flow marking sheet with the media exchanged at the original position can be easily performed.

請求項８のフロアマーキングシートによれば、フロアマーキングシートの縁部の捲くれ上がりを確実に防止することができるので外観を損なうことがなく、かつ躓きなどによる歩行者の転倒事故を防止することができる。   According to the floor marking sheet of claim 8, it is possible to reliably prevent the edge of the floor marking sheet from rolling up, so that it does not impair the appearance and prevents a pedestrian from falling over due to rolling or the like. Can do.

本発明に係るフロアマーキングシートの実施形態を第１図〜第３図に基づいて説明する。   An embodiment of a floor marking sheet according to the present invention will be described with reference to FIGS.

第１図（ａ）はフロアマーキングシート１の一つの実施形態を模式的に示した側面図であり、図中の符号Ｆは床面を示している。このフロアマーキングシート１は、ゴムシート２と、広告や誘導サインまたは装飾用の模様などが記録されているシート状のメディア３とを主要な構成部材として備え、これらを積層したものである。   FIG. 1 (a) is a side view schematically showing one embodiment of the floor marking sheet 1, and the symbol F in the drawing indicates the floor surface. The floor marking sheet 1 includes a rubber sheet 2 and a sheet-like medium 3 on which an advertisement, a guide sign, or a decorative pattern is recorded as main constituent members, and these are laminated.

ゴムシート２は、エチレン−プロピレンゴム（ＥＰＤＭ）１００重量部に対して充填剤５０〜１００重量部と可塑剤２０〜５０重量部とを配合し、比重が１．２〜１．４になるように調整したＥＰＤＭ組成物の生地を、ロータリープレスにて連続加硫して厚み１ｍｍ〜３ｍｍのシート状に形成したものである。そして、片面にのみクロロプレンゴム（ＣＲ）組成物を含有する接着剤が塗布されて接着剤層４が形成されており、この接着剤層４が形成されている接着面５と反対の面は、接着剤や粘着剤などによる表面加工がなされていないゴム面６になっている。このようなゴムシート２の具体例としては、例えば、バンドー化学株式会社製のバンドーシートＣＤＥ（商品名）を挙げることができる。このバンドーシートＣＤＥは、ＥＰＤＭを主成分とするＪＩＳＡ６００８に適合した加硫ゴムルーフィングシート（均質加硫ゴム）で耐候性、耐オゾン性、耐摩耗性、耐熱性耐寒性、さらに耐酸、耐アルカリ性などの特徴を備えている。   The rubber sheet 2 contains 50 to 100 parts by weight of a filler and 20 to 50 parts by weight of a plasticizer with respect to 100 parts by weight of ethylene-propylene rubber (EPDM) so that the specific gravity is 1.2 to 1.4. The dough of the EPDM composition adjusted to the above is continuously vulcanized with a rotary press to form a sheet having a thickness of 1 mm to 3 mm. And the adhesive layer 4 is formed by applying an adhesive containing a chloroprene rubber (CR) composition only on one surface, and the surface opposite to the adhesive surface 5 on which the adhesive layer 4 is formed is The rubber surface 6 is not subjected to surface processing with an adhesive or an adhesive. Specific examples of such a rubber sheet 2 include Bando Sheet CDE (trade name) manufactured by Bando Chemical Co., Ltd. This bando sheet CDE is a vulcanized rubber roofing sheet (homogeneous vulcanized rubber) conforming to JISA6008 mainly composed of EPDM. Weather resistance, ozone resistance, abrasion resistance, heat resistance, cold resistance, acid resistance, alkali resistance It has the characteristics of

ゴムシート２のエチレン−プロピレンゴム組成物は、エチレン−プロピレンゴム１００重量部に対して充填剤５０〜１００重量部と可塑剤２０〜５０重量部とを配合したものであるため、施工性を損なったり、床面Ｆを汚したりすることがなく、床面Ｆにしっかりと定着させることができる重さとしなやかさとを兼ね備えている。仮に、充填剤の合計量が５０重量部未満の場合はゴムシートが柔らかくなりすぎて施工性に欠け、２００重量部を超える場合はゴムシート２が硬くなり、床面Ｆに密着しにくくなる。さらに、充填剤が５０重量部未満或いは２００重量部を超える場合は、通常使用可能な充填剤を用いて所望の比重を実現させるのが困難になる。一方、可塑剤が２０重量部未満の場合はゴムシートが硬くなって床面に密着しにくくなり、５０重量部を超える場合は、可塑剤の種類によっては温度の急激な変化でゴムシートからブリード（滲出）することがある。充填剤としては、通常のゴムの配合に使用されるものを用いることができるが、なかでも種々のカーボンブラック、重質炭酸カルシウム、タルクなどがゴムシートとしての比重の実現性や、充填剤の添加量を高めてもしなやかさが損なわれない点、コストパフォーマンスの観点などから特に好ましい。また、可塑剤はＥＰＤＭの可塑剤として通常使用されるものを使用することができる。特にパラフィンオイルが好ましい。これらの充填剤及び可塑剤ともに複数種類を組み合わせて使用しても良い。   Since the ethylene-propylene rubber composition of the rubber sheet 2 is obtained by blending 50 to 100 parts by weight of a filler and 20 to 50 parts by weight of a plasticizer with respect to 100 parts by weight of ethylene-propylene rubber, the workability is impaired. Or the floor surface F is not soiled, and it has both weight and flexibility that can be firmly fixed on the floor surface F. If the total amount of the filler is less than 50 parts by weight, the rubber sheet becomes too soft and lacks workability, and if it exceeds 200 parts by weight, the rubber sheet 2 becomes hard and hardly adheres to the floor surface F. Furthermore, when the filler is less than 50 parts by weight or more than 200 parts by weight, it becomes difficult to achieve a desired specific gravity using a normally usable filler. On the other hand, when the plasticizer is less than 20 parts by weight, the rubber sheet becomes hard and hardly adheres to the floor surface. When the plasticizer exceeds 50 parts by weight, depending on the type of plasticizer, the rubber sheet bleeds due to a rapid change in temperature. (Exudation) may occur. As the filler, those used for normal rubber compounding can be used. Among them, various carbon blacks, heavy calcium carbonate, talc, etc. can be used to achieve the specific gravity as a rubber sheet, It is particularly preferable from the viewpoint of cost performance and the like that the flexibility is not impaired even if the addition amount is increased. Moreover, what is normally used as a plasticizer of EPDM can be used for a plasticizer. Paraffin oil is particularly preferable. A plurality of these fillers and plasticizers may be used in combination.

メディア３は、ポリオレフィン系合成樹脂であるポリプロピレンを繊維状に延伸し、それを縦横に組み合わせて圧着し一枚のシート状にした合成紙を基材７として、片面にインクを吸収して保持するインク受容層８が形成されるとともに、もう片方の面にアクリル系粘着剤が塗布されて粘着剤層９が形成されている。メディア３のインク受容層８が形成されている面は印刷面１０になっており、広告や誘導サイン、装飾用の模様などが記録される。記録は、インクジェットプリンタなどによるデジタル印刷や、グラビア印刷やスクリーン印刷などのアナログ印刷などにより行なわれる。特に、インクジェットプリンタによるデジタル印刷は、少量多品種のデザインに容易にかつ低コストで対応できるようになるとともに、プリンタを施工現場に持ち込み敷設場所の周囲の状況や床面の状態に応じて図柄や色調などを微調整しながら施工することができる。一方、粘着剤層９が形成されている面は、メディア３とゴムシート２とを積層する際にゴムシート２の接着面と貼り合せる粘着面１１になっている。このメディア３の具体例としては、ゴムシート２との粘着性が良好で実用性に優れた合成紙である、バンドー化学株式会社製の水系インクジェット用メディアのグランメッセＫＳＧ（商品名）を挙げることができる。このほかに、塩化ビニル樹脂からなる溶剤系のグランメッセＭＹＣ、ＧＹＣ、ＳＰＶＧ、ＳＰＶＭ（いずれも商品名）や、水系インクジェット用メディアである合成紙のグランメッセＰＳＰ（商品名）なども使用可能である。なお、粘着剤層のアクリル系粘着剤は高極性であるため、ゴムシート２に含まれる低極性の可塑剤がメディア３に移行しにくく、メディア３への悪影響を防ぐことができる。   The media 3 is made of a synthetic synthetic resin, which is a polyolefin-based synthetic resin, drawn into a fiber and is combined into a single sheet in the form of a single sheet to absorb and hold ink on one side. An ink receiving layer 8 is formed, and an acrylic adhesive is applied to the other surface to form an adhesive layer 9. The surface of the medium 3 on which the ink receiving layer 8 is formed is a printing surface 10 on which advertisements, guidance signs, decorative patterns, and the like are recorded. Recording is performed by digital printing using an inkjet printer or the like, or analog printing such as gravure printing or screen printing. In particular, digital printing by inkjet printers can easily handle low-volume, high-variety designs at low cost, bring the printer to the construction site, and change the design and pattern according to the conditions around the laying site and the floor surface. Construction can be done while finely adjusting the color tone. On the other hand, the surface on which the pressure-sensitive adhesive layer 9 is formed is a pressure-sensitive adhesive surface 11 that is bonded to the adhesive surface of the rubber sheet 2 when the media 3 and the rubber sheet 2 are laminated. Specific examples of the media 3 include Grand Messe KSG (trade name), a water-based inkjet media manufactured by Bando Chemical Co., Ltd., which is a synthetic paper having good adhesiveness to the rubber sheet 2 and excellent practicality. Can do. In addition, solvent-based Grand Messe MYC, GYC, SPVG, SPVM (all trade names) made of vinyl chloride resin and synthetic paper Grand Messe PSP (trade name), which is a water-based inkjet media, can also be used. is there. Since the acrylic pressure-sensitive adhesive in the pressure-sensitive adhesive layer is highly polar, it is difficult for the low-polarity plasticizer contained in the rubber sheet 2 to migrate to the media 3, and adverse effects on the media 3 can be prevented.

メディア３の印刷面１０には、塩化ビニル樹脂からなる厚み１００μｍ〜３００μｍのラミネートフィルムを積層して貼り合せることで保護層１２が設けられている。このような保護層１２をメディア３の印刷面１０に設けることによって、塩化ビニル樹脂の優れた耐久性や耐候性および透明性により、メディア３を傷や退色から保護し記録されている広告や誘導サイン、装飾用の模様などを長期間クリアな状態に保つことができる。さらに、塩化ビニル樹脂は優れた難燃性を備えているため、フロアマーキングシート１に防炎性能を付加することができる。なお、保護層１２のおもて面１３にエンボス加工などにより凹凸を形成して防滑機能を持たせることで、特に、滑り易い雨天時における歩行者の転倒を防止することができ安全性を高めることができる。この保護層１２の具体例としては、防滑性に優れたバンドー化学株式会社製のオーバーラミネートフィルムのグランメッセＳＴＦＬ（商品名）を挙げることができる。   A protective layer 12 is provided on the printing surface 10 of the medium 3 by laminating and laminating a laminate film made of vinyl chloride resin and having a thickness of 100 μm to 300 μm. By providing such a protective layer 12 on the printing surface 10 of the media 3, advertisements and guidance recorded to protect the media 3 from scratches and fading due to the excellent durability, weather resistance and transparency of the vinyl chloride resin. Signs, decorative patterns, etc. can be kept clear for a long time. Furthermore, since the vinyl chloride resin has excellent flame retardancy, flameproof performance can be added to the floor marking sheet 1. In addition, by forming unevenness on the front surface 13 of the protective layer 12 by embossing or the like to provide an anti-slip function, it is possible to prevent a pedestrian from falling down especially in a slippery rainy weather and improve safety. be able to. Specific examples of the protective layer 12 include Grand Messe STFL (trade name), which is an overlaminate film manufactured by Bando Chemical Co., Ltd., which is excellent in slip resistance.

以上のような構成を有するゴムシート２とメディア３とを、ゴムシート２の接着面５とメディア３の粘着面１１とを貼り合せ、ゴムシート２の接着剤層４とメディア３の粘着剤層９とを対向させた状態で積層し一体化している。このように、ゴムシート２とメディア３とが積層されて一体になっているフロアマーキングシート１を、ゴムシート２のゴム面６を床面Ｆに密着させることにより床面Ｆに定着させている。   The rubber sheet 2 and the media 3 having the above-described configuration are bonded to the adhesive surface 5 of the rubber sheet 2 and the adhesive surface 11 of the media 3, and the adhesive layer 4 of the rubber sheet 2 and the adhesive layer of the media 3 are combined. 9 are stacked and integrated in a state of facing each other. Thus, the floor marking sheet 1 in which the rubber sheet 2 and the medium 3 are laminated and integrated is fixed to the floor surface F by bringing the rubber surface 6 of the rubber sheet 2 into close contact with the floor surface F. .

このフロアマーキングシート１は、ゴムシート２のゴム面６を床面Ｆに密着させることで定着させているため、接着剤などが不要であり専門的な技術を備えていなくても簡単に敷設することができ、かつ移動や撤去も簡単に行うことができる。撤去する際には、床面に残った接着剤を除去する作業などの手間を要する後始末が不要であるため、作業を手早く短時間で終わらせることができる。   Since the floor marking sheet 1 is fixed by bringing the rubber surface 6 of the rubber sheet 2 into close contact with the floor surface F, an adhesive or the like is not required, and the floor marking sheet 1 can be easily laid even without a specialized technique. Can be moved and removed easily. When removing, it is not necessary to clean up the work, such as the work of removing the adhesive remaining on the floor, so that the work can be completed quickly and quickly.

また、トップの層に、難燃性を有する保護層１２を設けているため、火災に対するが安全性が高く、タバコのポイ捨て等の火の不始末による火災の発生を防ぐとともに、火災時の延焼を防いで被害を最小限に抑えることができる。   In addition, since the protective layer 12 with flame retardancy is provided on the top layer, it is highly safe against fires and prevents fires caused by misfires such as littering of cigarettes. Can be prevented and damage can be minimized.

一方、メディア３にインク受容層８を設けることにより、印刷面１０に付着したインクをインク受容層８で吸収し保持するため、インクに含まれる溶剤によって基材７が膨潤することを回避することができる。したがって、インクの乾燥に伴って基材７が収縮し、これによってゴムシート２の縁部が基材７側に反り、フロアマーキングシート１の縁部が捲くれ上がる不具合が生じない。このことは、防炎性能の向上にも寄与している。つまり、基材７がインクに含まれる溶剤によって膨潤すれば、インクの乾燥が進むにつれて収縮が起こり、基材７とゴムシート２とのあいだに寸法差を生じる。このため、メディア３の粘着剤層９とゴムシート２の接着剤層４との結合が弱ければ、基材７の収縮に伴ってメディア３がゴムシート２上で滑り、縁部においてゴムシート２が保護層１２よりも外にはみ出した状態になる。一方、粘着剤層９と接着剤層４との結合が強ければ、基材７の収縮に伴ってゴムシート２の縁部が基材７側に反り、フロアマーキングシート１の縁部が捲くれ上がった状態になる。これにより、捲くれ上がった縁部のゴムシート２やメディア３に火炎が当ることにより燃え易い状態になるからである。なお、メディア３にインク受容層８を形成したことにより、印刷用のインクとしては溶剤インク、低溶剤インク、ＵＶインク、油性顔料インク、水性顔料インク、染料インク、分散染料インクなど様々なインクが使用可能である。   On the other hand, by providing the ink receiving layer 8 on the medium 3, the ink adhering to the printing surface 10 is absorbed and held by the ink receiving layer 8, thereby avoiding swelling of the base material 7 due to the solvent contained in the ink. Can do. Therefore, the base material 7 contracts with the drying of the ink, whereby the edge portion of the rubber sheet 2 is warped toward the base material 7 and the edge portion of the floor marking sheet 1 is not raised. This also contributes to the improvement of the flameproof performance. That is, if the base material 7 is swollen by the solvent contained in the ink, the ink shrinks as the ink is dried, and a dimensional difference is generated between the base material 7 and the rubber sheet 2. For this reason, if the bonding between the pressure-sensitive adhesive layer 9 of the medium 3 and the adhesive layer 4 of the rubber sheet 2 is weak, the medium 3 slides on the rubber sheet 2 as the base material 7 contracts, and the rubber sheet 2 at the edge. Will protrude beyond the protective layer 12. On the other hand, if the bonding between the pressure-sensitive adhesive layer 9 and the adhesive layer 4 is strong, the edge of the rubber sheet 2 warps toward the substrate 7 as the substrate 7 contracts, and the edge of the floor marking sheet 1 is curled up. It goes up. This is because the rubber sheet 2 and the media 3 at the edge of the rolled-up edge are easily burned by a flame. Since the ink receiving layer 8 is formed on the medium 3, various inks such as solvent ink, low solvent ink, UV ink, oil pigment ink, water pigment ink, dye ink, and disperse dye ink can be used as printing ink. It can be used.

ちなみに、防炎性能の評価基準としては、消防法施行規則第４条の３第３号から第７項までと、消防庁予防課長通知第５７号（平成９年３月２８日）を根拠法令とした防炎性能試験基準が知られている。前記法令において、フロアマーキングシートは「じゅうたん等」に分類され、試験法として「４５度エアーミックスバーナー法」が適用される。この試験法においては、水平に固定したエアーミックスバーナーから２４ｍｍの炎を出し、この炎を、水平面に対して４５度傾けた試料台に固定した試験体の表面に３０秒間あてて加熱したときの残炎時間や炭化長などにより評価が行われる。じゅうたん類の場合、残炎時間が２０秒以下で、かつ炭化長が１０ｃｍ以下であれば防炎性能を有すると評価される。本発明にかかるフロアマーキングシートを、上記の防炎性能試験基準に準じて試験したところ、上記評価基準をクリアすることができた。   By the way, as evaluation standard of flameproof performance, firefighting law enforcement regulations Article 4-3 from 3rd to 7th and fire department prevention section manager notice 57th (March 28, 1997) based law The flameproof performance test standard is known. In the above law, the floor marking sheet is classified as “carpet etc.”, and “45 degree air mix burner method” is applied as a test method. In this test method, a flame of 24 mm is emitted from a horizontally fixed air mix burner, and this flame is heated for 30 seconds against the surface of a test specimen fixed to a sample table inclined by 45 degrees with respect to a horizontal plane. Evaluation is based on the afterflame time and carbonization length. In the case of carpets, if the afterflame time is 20 seconds or less and the carbonization length is 10 cm or less, it is evaluated as having flameproofing performance. When the floor marking sheet according to the present invention was tested according to the above-mentioned flameproof performance test standard, the above evaluation standard could be cleared.

また、ゴムシート２が低極性の有機高分子材料であるＥＰＤＭであるため、可塑剤などの配合剤にはパラフィンオイルをはじめとする低極性オイルが用いられる。この低極性オイルに対して、床面の塗料や床材（例えば、プラスチックタイル）として用いられることが多い高極性の有機高分子材料は膨潤しないため、床面の汚染や、強度低下、剥離、ひび割れなどの不具合が発生しにくい。また、ＥＰＤＭ組成物は離型性が高いため、ゴムシート２が床面Ｆにこびりつくことがない。そして、ゴムシート２の接着剤層４は、高極性のＣＲゴム組成物を含有する接着剤からなるので、ゴムシート２中の低極性の可塑剤などの含有成分がメディア３へ移行しにくく、かつメディア３の粘着剤層９によっても移行が阻止されるので、メディア３が汚れたり変質したりすることを回避できる。また、ＣＲゴム組成物を含有する接着剤は、ほとんどの粘着剤に対して良好な密着性を示すので、メディア３が使用中に不用意に剥がれるおそれがない。   Moreover, since the rubber sheet 2 is EPDM which is a low-polar organic polymer material, low-polar oil such as paraffin oil is used as a compounding agent such as a plasticizer. High-polar organic polymer materials often used as floor paints and flooring materials (for example, plastic tiles) do not swell against this low-polar oil. It is difficult for defects such as cracks to occur. Further, since the EPDM composition has high releasability, the rubber sheet 2 does not stick to the floor surface F. And since the adhesive layer 4 of the rubber sheet 2 is made of an adhesive containing a high-polarity CR rubber composition, it is difficult for components such as a low-polarity plasticizer in the rubber sheet 2 to migrate to the media 3, Moreover, since the migration is also prevented by the adhesive layer 9 of the medium 3, it is possible to avoid the medium 3 from being soiled or denatured. In addition, since the adhesive containing the CR rubber composition exhibits good adhesion to most pressure-sensitive adhesives, there is no possibility that the media 3 is inadvertently peeled off during use.

さらに、ゴムシート２は厚さが１ｍｍ〜３ｍｍで且つ比重が１．２〜１．４であるため、その重量としなやかさによって床面Ｆに密着し、フロアマーキングシート１の上を通行人が歩いてもずれたりすることがない。厚さが１ｍｍ以下の場合は、使用中に端部がめくれあがるおそれがあり、３ｍｍ以上の場合は、床面Ｆとの段差が顕著になり、この段差で通行人がつまずくおそれがある。一方、比重が１.２未満の場合は、ゴムシート２が軽くなりすぎ床面Ｆに密着させることができず、１.４を超える場合は、使用中において特に問題は発生しないものの、重量が重くなるので施工および撤去作業時の作業者の負担が大きくなる。   Furthermore, since the rubber sheet 2 has a thickness of 1 mm to 3 mm and a specific gravity of 1.2 to 1.4, the rubber sheet 2 is in close contact with the floor surface F due to its weight and flexibility, and a passerby on the floor marking sheet 1 There is no slippage even when walking. When the thickness is 1 mm or less, the end may be turned up during use. When the thickness is 3 mm or more, a step with the floor surface F becomes prominent, and a passerby may stumble at this step. On the other hand, when the specific gravity is less than 1.2, the rubber sheet 2 becomes too light to be brought into close contact with the floor F. When it exceeds 1.4, no particular problem occurs during use, but the weight is Since it becomes heavier, the burden on the operator during construction and removal work increases.

なお、フロアマーキングシート１の各層は、互いに端が揃った状態になっているが、縁部が保護層１２より外方にはみ出していない条件を満たしていれば、端が揃っていなくても差し支えはない。   In addition, although each layer of the floor marking sheet 1 is in a state where the edges are aligned with each other, the edges may not be aligned as long as the edge does not protrude outward from the protective layer 12. There is no.

それから、第１図（ｂ）は本願発明のフロアマーキングシート１’の別の実施形態を示しており、積層方向の断面を模式的に示したものである。なお、保護層以外は上記実施形態のフロアマーキングシート１と同じ構成を有しているため、同一の符号を用いて表している。このフロアマーキングシート１’の保護層１２’は、その縁部１２ａ’がその下方に位置するメディア３からゴムシート２までのいずれの層よりも外方にはみ出した状態になっており、かつ各層の側方を覆って床面Ｆまで達する状態で設けられている。このため、フロアマーキングシート１’は、メディア３以下の層が保護層１２’によって火炎から完全に隔離された状態になるので、より高い防炎性能を示すようになる。   Then, FIG. 1 (b) shows another embodiment of the floor marking sheet 1 'of the present invention, and schematically shows a cross section in the stacking direction. In addition, since it has the same structure as the floor marking sheet 1 of the said embodiment except a protective layer, it represents using the same code | symbol. The protective layer 12 ′ of the floor marking sheet 1 ′ is in a state where the edge 12 a ′ protrudes outward from any layer from the media 3 to the rubber sheet 2 positioned below the edge layer 12 a ′. It is provided in a state of covering the side of and reaching the floor surface F. For this reason, the floor marking sheet 1 ′ is in a state in which the layers below the medium 3 are completely isolated from the flame by the protective layer 12 ′, and thus exhibits higher flameproof performance.

次に、本願発明に係るフロアメーキングシート１の施工方法の実施形態について説明する。第２図のフロー図に示すように、あらかじめメディア３の印刷面１０に広告や誘導サインまたは装飾用の模様などをインクジェットプリンタでデジタル印刷する（手順１）。この手順１は、メディア３の粘着面１１に表面を保護するためのセパレータ（離型紙）を貼着したままで行なう。このように、記録にインクジェットプリンタを用いれば、施工現場にプリンタを持ち込んで印刷が可能になるため、敷設場所の状況や床面の状態に応じて図柄や色調などを微調整しつつ施工することができる。   Next, an embodiment of a construction method of the floor making sheet 1 according to the present invention will be described. As shown in the flowchart of FIG. 2, an advertisement, a guide sign, or a decorative pattern is digitally printed in advance on the printing surface 10 of the medium 3 by an inkjet printer (procedure 1). This procedure 1 is performed while a separator (release paper) for protecting the surface of the adhesive surface 11 of the medium 3 is adhered. In this way, if you use an inkjet printer for recording, you can bring the printer to the construction site and print, so you can perform construction while finely adjusting the pattern and color tone according to the situation of the laying place and the state of the floor surface. Can do.

次に、保護層１２となるラミネートフィルムをメディア３の印刷面１０に貼着する（手順２）。ラミネートフィルムには、裏面にあらかじめ粘着剤が塗布されセパレータが取り付けられているため、このセパレータを剥離してメディア３に貼り付ける。   Next, a laminate film to be the protective layer 12 is attached to the printing surface 10 of the media 3 (procedure 2). Since an adhesive is previously applied to the back surface of the laminate film and a separator is attached, the separator is peeled off and attached to the medium 3.

次に、ゴムシート２の接着面５に取り付けられているセパレータを剥離し、ゴムシート２の接着面５とセパレータが取り付けられているメディア３の粘着面１１とを対向させた状態で積層し、ゴムシート２とメディア３との位置合わせを行う（手順３）。   Next, the separator attached to the adhesive surface 5 of the rubber sheet 2 is peeled off, and the adhesive surface 5 of the rubber sheet 2 and the adhesive surface 11 of the medium 3 to which the separator is attached are laminated so as to face each other. The rubber sheet 2 and the media 3 are aligned (procedure 3).

次に、メディア３の粘着面１１に取り付けられているセパレータを剥離しながら端から順に両者を貼り合わせ、ゴムシート２の接着剤層４とメディア３の粘着剤層９とを対向させた状態で積層する（手順４）。   Next, the separator attached to the adhesive surface 11 of the media 3 is peeled off, and the two are bonded together in order from the end, and the adhesive layer 4 of the rubber sheet 2 and the adhesive layer 9 of the media 3 are opposed to each other. Laminate (procedure 4).

次に、ゴムシート２とメディア３が積層され一体となったフロアマーキングシート１を、あらかじめ塵や埃などを取り除いた床面Ｆの所定の位置にゴムシート２のゴム面６を床面Ｆに密着させながら敷設する（手順５）。   Next, the floor marking sheet 1 in which the rubber sheet 2 and the media 3 are laminated and integrated is placed at a predetermined position on the floor surface F from which dust or dust has been removed in advance, and the rubber surface 6 of the rubber sheet 2 is placed on the floor surface F. Lay it in close contact (Procedure 5).

なお、フロアマーキングシート１を移設する場合には、床面Ｆから剥がして移設先の床面Ｆに置くだけで作業が完了し、接着剤の跡を除去するなどの後始末をする必要がない。また、メディア３の交換を行なう場合は、ゴムシート２の接着面５とメディア３の粘着面１１とを剥離してメディア３をゴムシート２から分離し、代わりに別のメディア３の粘着面１１をゴムシート２の接着面５に貼り合わせれば作業が終了する。このように、フロアマーキングシート１は、ゴムシート２の接着剤層４とメディア３の粘着剤層９とを対向させているため、メディア３のみを交換すればゴムシート２は繰り返し使用することができ、経済的で、資源の浪費を抑えることもできる。   When the floor marking sheet 1 is transferred, the work is completed simply by peeling off the floor surface F and placing the floor marking sheet 1 on the transfer destination floor surface F, and it is not necessary to clean up after removing the trace of the adhesive. . When the medium 3 is exchanged, the adhesive surface 5 of the rubber sheet 2 and the adhesive surface 11 of the medium 3 are peeled off to separate the media 3 from the rubber sheet 2. Instead, the adhesive surface 11 of another medium 3 is used. Is attached to the adhesive surface 5 of the rubber sheet 2 to complete the operation. Thus, since the floor marking sheet 1 has the adhesive layer 4 of the rubber sheet 2 and the adhesive layer 9 of the medium 3 facing each other, the rubber sheet 2 can be used repeatedly if only the medium 3 is replaced. It is economical and can save resources.

また、フロアマーキングシートを床面に敷設したのち、万一の場合に備えて縁部の捲くれ上がりを防止するための処置を行なう場合がある。即ち、床面に敷設したフロアマーキングシートの縁部を、係止部材によって周囲に係止するのである。例えば、第３図に示すように、フロアマーキングシート１が床面Ｆに隙間なく敷設されているような場合、粘着テープ１４を、隣接するフロアマーキングシート１の境目に沿って両方のフロアマーキングシート１の縁部１ａに跨るようにして貼着する。粘着テープ１４はメディア３に印刷されている広告や誘導サインまたは装飾用の模様に影響を与えないように無色透明のものが好適で、上記実施形態の場合であれば保護層１２と同じ塩化ビニル樹脂製で厚み１００μｍ以下の粘着剤付きテープを使用すれば良い。   Further, after laying the floor marking sheet on the floor surface, there is a case in which a measure for preventing the edge from rolling up is prepared in case of an emergency. That is, the edge of the floor marking sheet laid on the floor surface is locked around by the locking member. For example, as shown in FIG. 3, when the floor marking sheet 1 is laid on the floor surface F without any gaps, the adhesive tape 14 is placed on both floor marking sheets along the boundary between the adjacent floor marking sheets 1. It sticks so that it may straddle the 1 edge part 1a. The pressure-sensitive adhesive tape 14 is preferably colorless and transparent so as not to affect the advertisement printed on the medium 3, the guide sign, or the decorative pattern. In the case of the above embodiment, the same vinyl chloride as the protective layer 12 is used. A tape with an adhesive having a thickness of 100 μm or less may be used.

ところで、本願発明にかかるフロアマーキングシートの実施形態について、縁部の捲くれ上がりに関する評価を行った結果を以下に示す。   By the way, about the embodiment of the floor marking sheet concerning this invention, the result of having performed evaluation regarding the rolling up of an edge is shown below.

フロアマーキングシートは、メディアにベタ印刷（ＣＭＹＫ各１００％）を施し、２０分間乾燥後、オーバーラミネートフィルム（保護層）ならびにゴムシートと貼りあわせることにより得たもので、メディアの材質やプリンタ・インクの種類が異なる４種類を用意した。そして、これらから２０ｃｍ×２０ｃｍ角の試験片をそれぞれ切り出し、２３℃の温度雰囲気下に静置して、７日間放置した。評価は、試験片を水平面に置いたときに、最も水平面から浮き上がっている縁部の高さを測定し、その測定値を捲くれ上がりの指標として行なった。   The floor marking sheet is obtained by applying solid printing (100% each of CMYK) to the media, drying for 20 minutes, and pasting it with an overlaminate film (protective layer) and a rubber sheet. Four types with different types were prepared. Then, a 20 cm × 20 cm square test piece was cut out from each of them, left in a 23 ° C. temperature atmosphere, and left for 7 days. In the evaluation, when the test piece was placed on a horizontal plane, the height of the edge that floated the most from the horizontal plane was measured, and the measured value was used as an index for raising.

なお、各フロアマーキングシートの詳細は表１に示す通り。ゴムシートに使用したバンドーシートＣＤＥ（商品名）は、バンドー化学株式会社製のＥＰＤＭを主成分とする均質加硫ゴムシートである。メディアに使用したグランメッセＫＳＧ、グランメッセＰＳＰは共にバンドー化学株式会社製の水系インクジェットプリント用の合成紙（基材：ポリプピレン）である。これらは、粘着剤層のアクリル系樹脂のグレードが異なっている。グランメッセＭＹＣは、同じくバンドー化学株式会社製の溶剤系のメディア（基材：塩ビ）である。保護層として使用したグランメッセＳＴＦＬは、塩化ビニル樹脂製のオーバーラミネートフィルムである。プリンタインクは、水性顔料インクあるいは溶剤系インクを使用した。   The details of each floor marking sheet are as shown in Table 1. Bando sheet CDE (trade name) used for the rubber sheet is a homogeneous vulcanized rubber sheet mainly composed of EPDM manufactured by Bando Chemical Co., Ltd. Grand Messe KSG and Grand Messe PSP used for the media are both synthetic paper (base: polypropylene) for water-based inkjet printing manufactured by Bando Chemical Co., Ltd. These differ in the grade of the acrylic resin of the pressure-sensitive adhesive layer. Grand Messe MYC is a solvent-based medium (base material: polyvinyl chloride) also manufactured by Bando Chemical Co., Ltd. Grand Messe STFL used as a protective layer is an overlaminate film made of vinyl chloride resin. As the printer ink, water-based pigment ink or solvent-based ink was used.

上記表１に示すように、５ｍｍの捲くれ上がりが生じたＮｏ．３の試験片以外のＮｏ．１、２、４の試験片については捲くれ上がりが発生しなかった。これにより、インクを定着させるためのインク受容層を基材表面に有する合成紙を基材とするメディアは、水系インクと溶剤インクとのいずれに対しても、反りが生じにくく、フロアマーキングシートのメディアとして好適であることが推察できる。

As shown in Table 1 above, no. No. 3 other than No. 3 test piece. No curling up occurred for the test pieces of 1, 2, and 4. As a result, media based on synthetic paper having an ink receiving layer for fixing ink on the substrate surface is less likely to warp against both water-based inks and solvent inks. It can be inferred that it is suitable as a medium.

（ａ）は本発明に係るフロアマーキングシートの実施形態の1つを模式的に示した側面図であり、（ｂ）は別の実施形態を示している。(A) is the side view which showed typically one of the embodiment of the floor marking sheet which concerns on this invention, (b) has shown another embodiment. 本発明に係るフロアマーキングシートの施工方法を示すフロー図である。It is a flowchart which shows the construction method of the floor marking sheet which concerns on this invention. 本発明に係るフロアマーキングシートの施工方法の実施形態により敷設したフロアマーキングシートを模式的に示した側面図。The side view which showed typically the floor marking sheet laid by embodiment of the construction method of the floor marking sheet which concerns on this invention.

符号の説明Explanation of symbols

１ フロアマーキングシート
１ａ 縁部
２ ゴムシート
３ メディア
４ 接着剤層
５ 接着面
６ ゴム面
７ 基材
８ インク受容層
９ 粘着剤層
１０ 印刷面
１１ 粘着面
１２ 保護層
１３ おもて面
１４ 粘着テープ DESCRIPTION OF SYMBOLS 1 Floor marking sheet 1a Edge 2 Rubber sheet 3 Media 4 Adhesive layer 5 Adhesive surface 6 Rubber surface 7 Base material 8 Ink receiving layer 9 Adhesive layer 10 Printing surface 11 Adhesive surface 12 Protective layer 13 Front surface 14 Adhesive tape

Claims (8)

床面に敷設して宣伝広告や案内表示または床面装飾などを行うフロアマーキング用シートにおいて、
前記床面と密着する面と反対側の面に接着剤層が設けられている加硫ゴムシートと、一方の面に粘着剤層が設けられ他方の面に広告や誘導サインまたは装飾用の模様などが記録されているシート状のメディアとが、当該メディアの粘着剤層と前記加硫ゴムシートの接着剤層とを対向させた状態で積層され、
前記メディアの他方の面に、難燃性を有する樹脂からなる保護層が設けられていることを特徴とするフロアマーキングシート。 In floor marking sheets that are laid on the floor and used for advertising, guidance display, or floor decoration,
A vulcanized rubber sheet provided with an adhesive layer on the surface opposite to the surface closely contacting the floor surface, an adhesive layer provided on one surface, and a pattern for advertisement, induction sign or decoration on the other surface Are laminated in a state where the adhesive layer of the media and the adhesive layer of the vulcanized rubber sheet are opposed to each other,
A floor marking sheet, wherein a protective layer made of a flame-retardant resin is provided on the other surface of the media. 前記難燃性を有する樹脂が、塩化ビニル樹脂であることを特徴とする請求項１記載のフロアマーキングシート。   The floor marking sheet according to claim 1, wherein the flame-retardant resin is a vinyl chloride resin. 前記保護層の縁部が、その下方に位置する前記メディアから前記加硫ゴムシートまでのいずれの層よりも外方にはみ出した状態になっていることを特徴とする請求項１または２記載のフロアマーキングシート。 The edge part of the said protective layer is the state protruded outward from any layer from the said medium located below to the said vulcanized rubber sheet, The claim 1 or 2 characterized by the above-mentioned. Floor marking sheet. 前記メディアが、前記粘着剤層側に位置するシート状の基材と、前記保護層側に位置するインク受容層との積層構造を有していることを特徴とする請求項１〜３のいずれかに記載のフロアマーキングシート。   4. The medium according to claim 1, wherein the medium has a laminated structure of a sheet-like base material positioned on the pressure-sensitive adhesive layer side and an ink receiving layer positioned on the protective layer side. The floor marking sheet of crab. 前記基材がポリオレフィン系の合成樹脂からなることを特徴とする請求項４記載のフロアマーキングシート。   The floor marking sheet according to claim 4, wherein the base material is made of a polyolefin-based synthetic resin. 前記基材がポリプロピレンを素材とする合成紙であることを特徴とする請求項５記載のフロアマーキングシート。   The floor marking sheet according to claim 5, wherein the base material is a synthetic paper made of polypropylene. 一方の面に粘着剤層が設けられ他方の面に広告や誘導サインまたは装飾用の模様などが記録されているシート状のメディアと、加硫ゴムシートとの積層構造を有するフロアマーキングシートの施工方法であって、
前記メディアの他方の面に、難燃性を有する樹脂からなる保護層を積層し、前記メディアと前記加硫ゴムシートとを、前記メディアの一方の面に設けられている前記粘着剤層と、前記加硫ゴムシートの一方の面に設けられている接着剤層とを対向させた状態で積層し、
前記加硫ゴムシートの他方の面を床面に密着させて敷設することを特徴とするフロアマーキングシートの施工方法。 One and the sheet-shaped media, such as are recorded pattern for advertising or inductive sign or decorative adhesive layer on the other surface provided on the surface, construction of the floor marking sheet having a laminated structure of the Ka硫Go Mushito A method,
On the other surface of the medium, and the flame-retardant laminated a protective layer made of a resin having, and said vulcanized rubber sheet and the medium, the pressure-sensitive adhesive layer provided on one surface of the medium, Laminating with the adhesive layer provided on one side of the vulcanized rubber sheet facing,
A method for constructing a floor marking sheet, wherein the other surface of the vulcanized rubber sheet is laid in close contact with the floor surface. 前記フロアマーキングシートを前記床面に敷設したのち、その縁部を係止部材によって周囲に係止することを特徴とする請求項７記載のフロアマーキングシートの施工方法。   8. The method of constructing a floor marking sheet according to claim 7, wherein after the floor marking sheet is laid on the floor surface, its edge is locked to the periphery by a locking member.

Images