JP4267478B2 - Grass protection sheet - Google Patents
Grass protection sheet Download PDFInfo
- Publication number
- JP4267478B2 JP4267478B2 JP2004041393A JP2004041393A JP4267478B2 JP 4267478 B2 JP4267478 B2 JP 4267478B2 JP 2004041393 A JP2004041393 A JP 2004041393A JP 2004041393 A JP2004041393 A JP 2004041393A JP 4267478 B2 JP4267478 B2 JP 4267478B2
- Authority
- JP
- Japan
- Prior art keywords
- component
- acid
- aliphatic
- polymer
- melting point
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、生分解性を有する防草シートに関するものである。 The present invention relates to a herbicidal sheet having biodegradability.
近年、公園、庭園、宅地、道路等の緑化が盛んになっている。それに伴って植物栽培や美観保持のために、雑草を防ぐための努力がなされており、特に近年では雑草の繁殖を抑える手段として、人手による雑草除去や除草剤の使用に代えて、各種の防草シートが用いられるようになっており、例えば、生分解性を有しないポリエチレンテレフタレート等からなる樹脂シート、金属製シート、紙製シート等が知られている。 In recent years, greening of parks, gardens, residential land, roads, etc. has become popular. Along with this, efforts have been made to prevent weeds for plant cultivation and aesthetic preservation.In recent years, as a means to suppress the growth of weeds, various weeds have been used instead of manual weed removal and use of herbicides. For example, a resin sheet made of polyethylene terephthalate or the like that does not have biodegradability, a metal sheet, a paper sheet, and the like are known.
生分解性を有しない樹脂シート、金属製シートは土壌表面や土中で分解しないため、使用後に回収しなければならず手間がかかるばかりか、回収後、不要になったシートの廃棄処理が環境汚染の点から問題がある。一方、紙製シートでは、強力が低いため、施工時に破れ等が生じやすく、また、透水性に劣るため、雨水が溜まる等の問題がある。 Resin sheets and metal sheets that do not have biodegradability do not decompose on the soil surface or in the soil, so they must be collected after use, which can be troublesome. There is a problem in terms of contamination. On the other hand, the paper sheet has a low strength, so that it easily breaks during construction, and has a problem that rainwater accumulates due to poor water permeability.
このような問題を解決する防草シートとして、本件出願人は、特許文献１に生分解性の熱可塑性脂肪族ポリエステルからなる不織布にて構成された防草シートを提案している。このシートによれば、生分解性を有しているため回収の手間を要せず、耐候性を有しているため使用時に分解しにくい。 As a herbicidal sheet that solves such a problem, the present applicant has proposed a herbicidal sheet composed of a non-woven fabric made of a biodegradable thermoplastic aliphatic polyester in Patent Document 1. According to this sheet, since it has biodegradability, it does not require time and effort for collection, and since it has weather resistance, it is difficult to decompose during use.
しかし、防草シートを施工する現場は平坦な地面ばかりでなく、石等による凹凸が多数存在する場所もあり、このような場所に防草シートを敷設する際には、施工者が防草シートの上から石を踏んだ場合の負荷に対して破れ難い高い機械的強力が防草シートに求められる。また、施工法として釘や杭等を打ちつけて施工する場合には、打ち付けた部位より容易に引裂かれない防草シートが求められる。
本発明は、生分解性を有する防草シートであって、より高い機械的強力を有するものを提供することを課題とする。 An object of the present invention is to provide a herbicidal sheet having biodegradability, which has higher mechanical strength.
本発明者等は、生分解性を有する防草シートにおいて、より強力を向上するために鋭意検討を行なった。機械的強力を向上するためには不織布にバインダー樹脂を含浸させることが考えられるが、強力向上のために樹脂含浸量を増すと防草シートが硬くなり、施工性、地面の起伏や凹凸への追随性に劣るものとなる。 The present inventors have intensively studied to improve the strength of the biodegradable herbicidal sheet. In order to improve the mechanical strength, it is conceivable to impregnate the nonwoven fabric with a binder resin.However, increasing the resin impregnation amount to improve the strength will harden the herbicidal sheet, improving workability, unevenness of the ground and unevenness. It will be inferior to following.
本発明者等は、バインダー樹脂を用いなくとも防草シートの強力を向上させるために、不織布を構成する重合体に着目した。そして、特定の重合体を用い、特定の複合形態の繊維を採用することにより、自己接着性を向上させ、かつ繊維の機械的強力を向上させることによって、防草シートに求められる不織布としての強力を向上させることを見出し本発明に到達した。 The present inventors paid attention to the polymer constituting the nonwoven fabric in order to improve the strength of the herbicidal sheet without using a binder resin. And by using a specific polymer and adopting a specific composite form of fiber, the self-adhesiveness is improved and the mechanical strength of the fiber is improved. The present invention has been found.
本発明は、脂肪族ジオール、脂肪族ジカルボン酸および脂肪族ヒドロキシカルボン酸を構成成分とする脂肪族ポリエステル共重合体（ａ）と、ポリ乳酸系重合体とがブレンドしてなる重合体（Ａ成分）が鞘成分、ポリ乳酸系重合体（Ｂ成分）が芯成分に配された芯鞘型複合長繊維からなり、ポリ乳酸系重合体が、ポリ−Ｄ−乳酸、ポリ−Ｌ−乳酸、Ｄ−乳酸とＬ−乳酸との共重合体、あるいはこれらのブレンド体であり、該複合長繊維を構成する重合体は下記（１）〜（３）の溶融特性を満足し、Ａ成分の少なくとも一部が溶融または軟化することにより、繊維同士が熱接着して形態保持している不織布によって構成され、該複合長繊維はＡ成分またはＢ成分の少なくともいずれかに顔料が含有されている原着繊維であることを特徴とする防草シート。
（１）Ａ成分およびＢ成分に用いるポリ乳酸系重合体の融点が共に１５０℃以上である。
（２）脂肪族ポリエステル共重合体（ａ）の融点がＢ成分の融点よりも低い。
（３）脂肪族ポリエステル共重合体（ａ）が結晶融点を有している。
The present invention relates to a polymer (component A) obtained by blending an aliphatic polyester copolymer (a ) containing an aliphatic diol, an aliphatic dicarboxylic acid and an aliphatic hydroxycarboxylic acid as constituents and a polylactic acid polymer. ) Is a sheath-component, and a poly-lactic acid polymer (B component) is a core-sheath type composite continuous fiber arranged in the core component, and the polylactic acid-based polymer is poly-D-lactic acid, poly-L-lactic acid, D -A copolymer of lactic acid and L-lactic acid, or a blend thereof , and the polymer constituting the composite long fiber satisfies the melting characteristics (1) to (3) below, and is at least one of the components A The composite fiber is composed of a non-woven fabric in which the fibers are thermally bonded to each other by melting or softening the part, and the composite long fiber is a raw fiber containing a pigment in at least one of the A component and the B component Protection characterized by Grass sheet.
(1) The melting points of the polylactic acid polymers used for the A component and the B component are both 150 ° C. or higher.
(2) melting point of the aliphatic polyester copolymer (a) is lower than the melting point of the B component.
(3) The aliphatic polyester copolymer (a ) has a crystalline melting point.
まず、芯鞘型複合長繊維を構成するＡ成分、Ｂ成分に用いるポリ乳酸系重合体について説明する。 First, the polylactic acid polymer used for the A component and the B component constituting the core-sheath type composite continuous fiber will be described.
本発明に用いるポリ乳酸系重合体は、ポリ−Ｄ−乳酸、ポリ−Ｌ−乳酸、Ｄ−乳酸とＬ−乳酸との共重合体（Ｄ、Ｌ−乳酸共重合体）であって融点が１５０℃以上のもの、あるいはこれらのブレンド体である。ポリ乳酸系重合体の融点が１５０℃以上であると、高い結晶性を有しているため、紡糸の際の冷却性が良好となり、例えばスパンボンド法により良好に不織布を得ることができる。また、スパンボンド法による高速紡糸によってポリ乳酸系重合体の結晶配向が進み、得られる防草シートの耐熱性、耐候性、機械的強力が優れたものとなる。 Polylactic acid polymer used in the present invention include poly -D- acid, poly -L- acid, D- copolymer of lactic acid and L- lactic acid (D, L- lactic acid copolymer) A melting point 0.99 ° C. or more of, or blends thereof bodies. When the melting point of the polylactic acid polymer is 150 ° C. or higher, it has high crystallinity, so that the cooling property during spinning is good, and a nonwoven fabric can be obtained satisfactorily by, for example, a spunbond method. Moreover, the crystal orientation of the polylactic acid polymer advances by high-speed spinning by the spunbond method, and the heat resistance, weather resistance, and mechanical strength of the resulting herbicidal sheet become excellent.
ポリ乳酸系重合体として共重合体を用いる場合には、共重合体の融点が１５０℃以上となるようにＤ−乳酸とＬ−乳酸の共重合比を決定する。Ｄ、Ｌ−乳酸共重合体において、共重合比（モル比）が、Ｌ−乳酸あるいはＤ−乳酸のいずれかが９５モル％以上１００モル％未満のものを用いるとよい。共重合比が、前記範囲を外れると、共重合体の融点が１５０℃未満となり、または非晶性となり、本発明の目的を達成しにくい。 When a copolymer is used as the polylactic acid polymer, the copolymerization ratio of D-lactic acid and L-lactic acid is determined so that the melting point of the copolymer is 150 ° C. or higher. In the D, L-lactic acid copolymer, a copolymer having a copolymerization ratio (molar ratio) of 95 mol% or more and less than 100 mol% of either L-lactic acid or D-lactic acid may be used. When the copolymerization ratio is outside the above range, the melting point of the copolymer becomes less than 150 ° C. or becomes amorphous, and it is difficult to achieve the object of the present invention.
なお、Ａ成分に用いるポリ乳酸系重合体と、Ｂ成分に用いるポリ乳酸系重合体とは、同一のものであっても、異なるものであってもよい。 The polylactic acid polymer used for the component A and the polylactic acid polymer used for the component B may be the same or different.
次に、Ａ成分に用いる脂肪族ジオール、脂肪族ジカルボン酸および脂肪族ヒドロキシカルボン酸を構成成分とする脂肪族ポリエステル共重合体（ａ）について説明する。 Next, the aliphatic polyester copolymer (a) having an aliphatic diol, an aliphatic dicarboxylic acid and an aliphatic hydroxycarboxylic acid used as the component A as constituent components will be described.
脂肪族ジオールとしては、エチレングリコール、１，３−プロパンジオール、１，４−ブタンジオール、１，５−ペンタンジオール、１，６−ヘキサンジオール、１，４−シクロヘキサンジオール、１，４−シクロヘキサンジメタノールが挙げられる。これらは単独で用いても、またはこれらを併用して用いてもよい。なかでも、得られる脂肪族ポリエステル共重合体（ａ）の物性を考慮して、１，４−ブタンジオールを用いることが好ましい。 Aliphatic diols include ethylene glycol, 1,3-propanediol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,4-cyclohexanediol, 1,4-cyclohexanedi Methanol. These may be used alone or in combination. Of these, it is preferable to use 1,4-butanediol in consideration of the physical properties of the aliphatic polyester copolymer (a) to be obtained.
脂肪族ジカルボン酸としては、シュウ酸、コハク酸、グルタル酸、アジピン酸、セバシン酸、スベリン酸、ドデカン二酸等、が挙げられ、これらの誘導体である酸無水物を用いてもよい。なかでも、得られる脂肪族ポリエステル共重合体（ａ）の物性を考慮して、コハク酸または無水コハク酸、あるいはこれらとアジピン酸とを併用したものであることが好ましい。 Examples of the aliphatic dicarboxylic acid include oxalic acid, succinic acid, glutaric acid, adipic acid, sebacic acid, suberic acid, dodecanedioic acid, and the like, and acid anhydrides that are derivatives thereof may be used. Among these, in view of the physical properties of the resulting aliphatic polyester copolymer (a), succinic acid or succinic anhydride, or a combination of these with adipic acid is preferable.
脂肪族ヒドロキシカルボン酸としては、乳酸、グリコール酸、２−ヒドロキシ−ｎ−酪酸、２−ヒドロキシカプロン酸、２−ヒドロキシイソカプロン酸、２−ヒドロキシ−３，３−ジメチル酪酸、２−ヒドロキシ−３−メチル乳酸、ロイシン酸、３−ヒドロキシ酪酸、４−ヒドロキシ酪酸、メチル乳酸、カプロラクトン、バレロラクトン等が挙げられる。なかでも、乳酸を用いることが好ましい。 Examples of the aliphatic hydroxycarboxylic acid include lactic acid, glycolic acid, 2-hydroxy-n-butyric acid, 2-hydroxycaproic acid, 2-hydroxyisocaproic acid, 2-hydroxy-3,3-dimethylbutyric acid, and 2-hydroxy-3. -Methyl lactic acid, leucine acid, 3-hydroxybutyric acid, 4-hydroxybutyric acid, methyl lactic acid, caprolactone, valerolactone and the like. Of these, lactic acid is preferably used.
本発明においては、脂肪族ジオールが１，４−ブタンジオール、脂肪族ジカルボン酸がコハク酸、脂肪族ヒドロキシカルボン酸が乳酸である脂肪族ポリエステル共重合体（ａ）を好ましく用いることができる。 In the present invention, an aliphatic polyester copolymer (a) in which the aliphatic diol is 1,4-butanediol, the aliphatic dicarboxylic acid is succinic acid, and the aliphatic hydroxycarboxylic acid is lactic acid can be preferably used.
脂肪族ポリエステル共重合体（ａ）は、上記した脂肪族ジオール、脂肪族ジカルボン酸および脂肪族ヒドロキシカルボン酸が重縮合してなるものであり、ブロック共重合体であっても、ランダム共重合体であってもよい。 The aliphatic polyester copolymer (a) is obtained by polycondensation of the above-mentioned aliphatic diol, aliphatic dicarboxylic acid and aliphatic hydroxycarboxylic acid. Even if it is a block copolymer, it is a random copolymer. It may be.
本発明において用いる脂肪族ポリエステル共重合体（ａ）としては、例えば、特許第３４１８０７０号公報に記載されている脂肪族ポリエステル共重合体を使用することが好ましい。特許第３４１８０７０号公報に記載されている脂肪族ポリエステル共重合体とは、脂肪族ジカルボン酸と脂肪族ジオールと脂肪族ヒドロキシカルボン酸からなり、脂肪族ヒドロキシカルボン酸の少なくとも一部が乳酸であるものである。 As the aliphatic polyester copolymer (a) used in the present invention, for example, an aliphatic polyester copolymer described in Japanese Patent No. 3418070 is preferably used. The aliphatic polyester copolymer described in Japanese Patent No. 3418070 is composed of an aliphatic dicarboxylic acid, an aliphatic diol, and an aliphatic hydroxycarboxylic acid, and at least a part of the aliphatic hydroxycarboxylic acid is lactic acid. It is.
上記した脂肪族ポリエステル共重合体（ａ）は、いずれもその融点がＢ成分であるポリ乳酸系重合体の融点よりも低く、かつ結晶融点を有している。その融点がＢ成分よりも低いことにより、繊維同士を熱接着する際の接着成分として機能し、また、結晶融点を有することにより、熱接着工程においてトラブルが発生しにくく、高い接着強力を保持でき、ひいては機械的強力に優れた防草シートを得ることができる。結晶融点を有するとは、示差走査熱量分析におけるＤＳＣ融解吸熱曲線において、明確な融点ピークを有するものである。なお、熱加工安定性、接着強力を考慮すると、脂肪族ポリエステル共重合体（ａ）は、Ｂ成分の融点より５０℃以上低いことが好ましい。 The above-mentioned aliphatic polyester copolymer (a ) has a melting point lower than the melting point of the polylactic acid polymer as the B component and a crystalline melting point. Since its melting point is lower than that of the B component, it functions as an adhesive component when heat-bonding fibers together, and because it has a crystalline melting point, it is less likely to cause trouble in the thermal bonding process and can maintain high adhesive strength. As a result, a herbicidal sheet having excellent mechanical strength can be obtained. Having a crystalline melting point has a clear melting point peak in the DSC melting endothermic curve in differential scanning calorimetry. In view of thermal processing stability and adhesive strength, the aliphatic polyester copolymer (a) is preferably 50 ° C. or more lower than the melting point of the component B.
Ａ成分は、上記した脂肪族ポリエステル共重合体（ａ）と、ポリ乳酸系重合体とがブレンドしてなるものであるが、そのブレンド比率（質量比）は、脂肪族ポリエステル共重合体（ａ）が、Ａ成分中に５〜３０質量％ブレンドされていることが好ましい。脂肪族ポリエステル共重合体（ａ）のブレンド比率が５質量％未満であると、熱接着成分として寄与する成分が減少するため熱接着性に劣る傾向となり、また、十分な機械的強力および伸度が得られにくい。一方、脂肪族ポリエステル共重合体（ａ）のブレンド比率が３０質量％を超えると、スパンボンド法により長繊維不織布を得る場合、製糸時の冷却性が劣り、紡糸・延伸した糸条同士が密着し、開繊できない傾向となる。 The component A is formed by blending the above-described aliphatic polyester copolymer (a ) and a polylactic acid-based polymer, and the blend ratio (mass ratio) of the aliphatic polyester copolymer (a ) Is preferably blended in the component A by 5 to 30% by mass. When the blend ratio of the aliphatic polyester copolymer (a ) is less than 5% by mass, the component contributing as a thermal adhesive component decreases, so that the thermal adhesiveness tends to be inferior, and sufficient mechanical strength and elongation are obtained. Is difficult to obtain. On the other hand, when the blend ratio of the aliphatic polyester copolymer (a ) exceeds 30% by mass, when a long fiber nonwoven fabric is obtained by the spunbond method, the cooling property during spinning is inferior, and the spun and drawn yarns are in close contact with each other. However, it tends to be unable to be opened.
芯鞘型複合長繊維を構成するＡ成分およびＢ成分のメルトフローレート（以下、ＭＦＲと略記する。）は、いずれも２０ｇ／１０分〜８０ｇ／１０分であることが好ましい。ここで、ＭＦＲは、ＡＳＴＭ−Ｄ−１２３８に記載の方法に準じて、温度２１０℃、荷重２０．２Ｎ（２１６０ｇｆ）で測定した値である。 The melt flow rate (hereinafter abbreviated as MFR) of the A component and B component constituting the core-sheath type composite continuous fiber is preferably 20 g / 10 min to 80 g / 10 min. Here, MFR is a value measured at a temperature of 210 ° C. and a load of 20.2 N (2160 gf) according to the method described in ASTM-D-1238.
本発明に用いる重合体には、各々必要に応じて、艶消し剤、結晶核剤等の各種添加剤を本発明の効果を損なわない範囲で添加してもよい。とりわけ、タルク、酸化チタン、炭酸カルシウム、炭酸マグネシウム等の結晶核剤を添加することにより、紡出・冷却工程での糸条間の融着（ブロッキング）を防止し、また、不織布の製造工程において、繊維の結晶配向化を向上させ、得られる防草シートの機械的強力、耐熱性、耐候性を向上させることができる。添加する結晶核剤の量は、０．１〜３質量％の範囲が有用である。 Various additives such as a matting agent and a crystal nucleating agent may be added to the polymer used in the present invention as necessary, as long as the effects of the present invention are not impaired. In particular, by adding crystal nucleating agents such as talc, titanium oxide, calcium carbonate, magnesium carbonate, etc., fusing (blocking) between yarns in the spinning / cooling process is prevented, and in the manufacturing process of the nonwoven fabric The fiber crystal orientation can be improved, and the mechanical strength, heat resistance, and weather resistance of the resulting herbicidal sheet can be improved. The amount of the crystal nucleating agent to be added is useful in the range of 0.1 to 3% by mass.
本発明における芯鞘型複合長繊維は、Ａ成分またはＢ成分の少なくともいずれかに顔料が含有されている原着繊維である。原着繊維は、顔料を予め練り込んだ重合体を溶融紡糸して得られる繊維であり、このような原着繊維を用いることにより、後加工による染色が不要となり、染色により繊維が熱劣化することなく、経時的な強力低下が少なく耐候性に優れた防草シートを得ることができる。なお、顔料の含有量は、Ａ、Ｂ成分のそれぞれの成分について０．５〜２質量％であるとよい。 The core-sheath type composite continuous fiber in the present invention is an original fiber in which a pigment is contained in at least one of the A component and the B component. The original fiber is a fiber obtained by melt spinning a polymer in which a pigment is previously kneaded. By using such an original fiber, dyeing by post-processing becomes unnecessary, and the fiber is thermally deteriorated by dyeing. Therefore, it is possible to obtain a herbicidal sheet with less deterioration in strength over time and excellent weather resistance. In addition, content of a pigment is good in it being 0.5-2 mass% about each component of A and B component.
本発明においては、Ａ成分およびＢ成分の両方に顔料が含有していてもよいが、紡糸工程での配向結晶化を考慮すると、どちらか一成分に含有していることが好ましい。重合体に顔料を添加すると、紡糸工程における配向結晶化が進みにくくなるためである。より好ましくは、接着成分として機能するＡ成分に顔料を含有させ、熱接着処理を施しても熱の影響を受けにくく骨格として機能するＢ成分には顔料を含有させずに、得られる芯鞘型複合長繊維のＡ成分（鞘成分）においては、配向結晶化を抑制して熱接着時の接着強力を向上させ、一方、骨格となるＢ成分（芯成分）においては、配向結晶化を高めて繊維としての強力を担わせて、接着強力と繊維強力の両者を向上させることにより、防草シートとしての機械的強力を向上させることが好ましい。 In the present invention, the pigment may be contained in both the A component and the B component, but considering oriented crystallization in the spinning process, it is preferable that the pigment is contained in one of the components. This is because when the pigment is added to the polymer, orientation crystallization is difficult to proceed in the spinning process. More preferably, the core-sheath type obtained by containing a pigment in the A component that functions as an adhesive component, and not including the pigment in the B component that functions as a skeleton that is not easily affected by heat even when subjected to thermal bonding treatment. In the component A (sheath component) of the composite long fiber, the orientation crystallization is suppressed to improve the adhesive strength at the time of thermal bonding, while in the B component (core component) serving as the skeleton, the orientation crystallization is increased. It is preferable to improve the mechanical strength as the herbicidal sheet by improving the adhesive strength and the fiber strength by imparting the strength as the fiber.
本発明の防草シートは、前記の原着繊維からなるものであり、Ｌ＊値が４０以下であることが好ましい。Ｌ＊値は、明度を表すものであり、Ｌ＊値が１００に近づくほど明度が高く白色になり、一方、Ｌ＊値が０に近づくほど明度が低く黒色になることを示す。防草シートのＬ＊値を４０以下にすることにより、防草シートの遮光性を高め、防草シート下に光を透過しにくくして雑草の生育を妨げることができる。防草シートのＬ＊値を４０以下とするために、芯鞘型複合長繊維に含有させる顔料を選定する。例えば、カーボンブラック等の黒色顔料を選択することによりＬ＊値を４０以下とすることができる。また、敷設する場所や美観等に応じて他の顔料を添加し、色度を適宜選択して、茶、緑等の色彩にするとよい。本発明の防草シートは、その色調として、ａ＊値が＋２〜＋１０、ｂ＊値が＋２〜＋１５の範囲であることが好ましく、この範囲であることにより、雑草の生育を抑制すると共に周囲の美観を損なわない防草シートを得ることができる。なお、Ｌ＊値、ａ＊値、ｂ＊値とは、ＪＩＳ Ｚ ８７２９によるものである。 The herbicidal sheet of the present invention is composed of the above-mentioned original fibers, and the L * value is preferably 40 or less. The L * value represents the lightness, and as the L * value approaches 100, the lightness becomes high and white, while on the other hand, the lightness becomes low and black as the L * value approaches 0. By making the L * value of the herbicidal sheet 40 or less, the light shielding property of the herbicidal sheet can be improved, and it is difficult to transmit light under the herbicidal sheet, thereby preventing the growth of weeds. In order to make the L * value of the herbicidal sheet 40 or less, a pigment to be contained in the core-sheath type composite continuous fiber is selected. For example, the L * value can be made 40 or less by selecting a black pigment such as carbon black. Moreover, it is good to add other pigments according to a laying place, the beauty | look, etc., select chromaticity suitably, and to make colors, such as brown and green. The herbicidal sheet of the present invention preferably has an a * value in the range of +2 to +10 and a b * value in the range of +2 to +15 as the color tone. Can be obtained. The L * value, a * value, and b * value are those according to JIS Z 8729.
本発明における芯鞘型複合長繊維の芯部と鞘部の複合比（質量比）は、芯部／鞘部=５／１〜１／１であることが好ましい。芯部の比率が５／１を超えると、鞘部の比率が小さくなりすぎるため、熱接着性能に劣る傾向となり、防草シートの機械的強力が劣る傾向となる。一方、芯部の比率が１／１未満となると、スパンボンド製造工程において、紡糸糸条の冷却性に劣り、製糸性・開繊性が悪く、紡糸・延伸した糸条同士が密着しやすい。 In the present invention, the composite ratio (mass ratio) of the core part to the sheath part of the core-sheath composite long fiber is preferably core part / sheath part = 5/1 to 1/1. When the ratio of the core part exceeds 5/1, the ratio of the sheath part becomes too small, so that the thermal bonding performance tends to be inferior, and the mechanical strength of the herbicidal sheet tends to be inferior. On the other hand, when the ratio of the core portion is less than 1/1, in the spunbond manufacturing process, the spinning yarn is inferior in cooling property, the spinning property / opening property is poor, and the spun and drawn yarns are likely to adhere to each other.
芯鞘型複合長繊維の単糸繊度は、特に限定しないが、１〜１１デシテックス程度であればよい。単糸繊度が１デシテックス未満であると、得られる防草シートの機械的強力が劣る傾向となり、一方、単糸繊度が１１デシテックスを超えると、スパンボンド製造工程において、紡糸糸条の冷却性に劣り、糸条同士が密着し易くなる。 The single yarn fineness of the core-sheath type composite continuous fiber is not particularly limited, but may be about 1 to 11 dtex. When the single yarn fineness is less than 1 dtex, the mechanical strength of the resulting herbicidal sheet tends to be inferior. On the other hand, when the single yarn fineness exceeds 11 dtex, in the spunbond manufacturing process, the cooling property of the spun yarn is reduced. Inferior, it becomes easy for the yarns to adhere to each other.
本発明の防草シートは、前述した芯鞘型複合長繊維がスパンボンド法等により堆積されてなる不織布によって構成され、鞘成分に配されたＡ成分の少なくとも一部が溶融または軟化することにより、繊維同士が熱接着して形態保持している。ここで、熱接着の形態としては、熱風等を吹き付けることにより、繊維同士の接点において溶融または軟化したＡ成分を介して熱接着したもの、また、熱エンボス装置に通すことにより、熱圧着部と非熱圧着部とを形成し、熱圧着部において、Ａ成分を溶融または軟化させて不織布として形態保持しているものであってもよい。本発明においては、機械的強力がより優れることから、熱エンボス装置に通すことにより熱圧着部と非熱圧着部とを形成した不織布であることが好ましい。 The herbicidal sheet of the present invention is composed of a nonwoven fabric in which the core-sheath composite long fibers described above are deposited by the spunbond method or the like, and at least a part of the A component disposed in the sheath component is melted or softened. The fibers are heat-bonded to maintain the shape. Here, as a form of thermal bonding, by hot air or the like, it is thermally bonded via a component A melted or softened at the contact between fibers, or by passing through a hot embossing device, A non-thermocompression bonding part may be formed, and in the thermocompression bonding part, the component A may be melted or softened and retained as a nonwoven fabric. In this invention, since it is more excellent in mechanical strength, it is preferable that it is the nonwoven fabric which formed the thermocompression bonding part and the non-thermocompression bonding part by letting it pass through a hot embossing apparatus.
本発明の防草シートの目付は、施工する場所や使用等に応じて適宜選択すればよいが、５０〜３００ｇ／ｍ2程度であることが好ましい。目付が５０ｇ／ｍ2未満であると機械的強力に劣り実用的でない。一方、目付が３００ｇ／ｍ2を超えると過剰品質となり、またコスト面で不利で、また作業性にも劣る傾向にある。 Basis weight of the weed sheet of the present invention may be appropriately selected depending on the location and use like the construction, but is preferably about 50 to 300 g / m 2. If the basis weight is less than 50 g / m 2 , the mechanical strength is inferior and it is not practical. On the other hand, if the basis weight exceeds 300 g / m 2 , the quality becomes excessive, the cost is disadvantageous, and the workability tends to be inferior.
本発明においては、防草シートの縦方向（ＭＤ方向）の引張強力が１．９Ｎ／（ｇ／ｍ2）以上であることが好ましい。また、破断伸度が２０％以上であることが好ましい。縦方向の引張強力が１．９Ｎ／（ｇ／ｍ2）未満あるいは、破断伸度が２０％未満であると、防草シートとして実用的な機械的強力を有しているとはいい難く、施工時に破れやすく作業性に劣る傾向となる。引張強力および破断伸度は、ＪＩＳ−Ｌ−１９０６に準じて、以下の方法により測定した値をいう。すなわち、長さ２０ｃｍ、幅５ｃｍの試料片１０点を作成し、各試料について、定速伸張型引張試験機（オリエンテック社製テンシロンＵＴＭ−４−１−１００）を用い、つかみ間隔１０ｃｍ、引張速度２０ｃｍ／分で伸張し、得られた切断時荷重値（Ｎ／５ｃｍ幅）の平均値を目付で除した値を引張強力（Ｎ／（ｇ／ｍ2））とする。破断伸度は、上記により得られた切断時の伸度の平均値を破断伸度とする。なお、破断伸度においては、防草シートの縦方向（ＭＤ方向）と横方向（ＣＤ方向）とを測定し、得られた値の平均値を破断伸度（％）とした。なお、破断伸度の上限は５０％程度あればよい。 In this invention, it is preferable that the tensile strength of the vertical direction (MD direction) of a weedproof sheet is 1.9 N / (g / m < 2 >) or more. Further, the elongation at break is preferably 20% or more. When the tensile strength in the longitudinal direction is less than 1.9 N / (g / m 2 ) or the elongation at break is less than 20%, it is difficult to say that the material has practical mechanical strength as a herbicidal sheet. It tends to be broken during construction and tends to be inferior in workability. The tensile strength and elongation at break are values measured by the following method according to JIS-L-1906. That is, 10 sample pieces having a length of 20 cm and a width of 5 cm were prepared, and for each sample, a constant speed extension type tensile tester (Tensilon UTM-4-1-100 manufactured by Orientec Co., Ltd.) was used. The tensile strength (N / (g / m 2 )) is obtained by stretching at a speed of 20 cm / min and dividing the average value of the obtained cutting load values (N / 5 cm width) by the basis weight. The elongation at break is the average value of the elongation at the time of cutting obtained as described above. In addition, in breaking elongation, the vertical direction (MD direction) and the horizontal direction (CD direction) of the herbicidal sheet were measured, and the average value of the obtained values was defined as the breaking elongation (%). In addition, the upper limit of breaking elongation should just be about 50%.
また、本発明の防草シートの破裂強力は、５００ｋＰａ以上であることが好ましい。破裂強力が５００ｋＰａ以上とすることにより、防草シートを施工する際や施工後に防草シート上を歩行する際に、防草シート下の石等の突起物によりシートが容易には破れることを防ぐことができる。 Moreover, it is preferable that the bursting strength of the weedproof sheet of this invention is 500 kPa or more. By setting the bursting strength to 500 kPa or more, when constructing the weedproof sheet or walking on the weedproof sheet after construction, the sheet is prevented from being easily torn by protrusions such as stones under the weedproof sheet. be able to.
本発明の防草シートの透水係数は０．０２ｃｍ／秒以上であることが好ましい。透水係数が０．０２／秒以上であることにより、降雨等による水が防草シート表面に溜まることなく、すみやかに防草シートの厚み方向に水を浸透させることができる。また、防草シートを用いて植栽を行っている場合は、植物に充分な水分を補給することができ、さらには液肥の散布も可能である。透水係数の上限については、特に限定しないが、シートを構成している繊維間空隙との関係から０．８ｃｍ／秒程度であればよい。また、防草シートに親水性油剤を付与することにより透水係数を制御することができる。 The water permeability coefficient of the herbicidal sheet of the present invention is preferably 0.02 cm / second or more. When the water permeability coefficient is 0.02 / second or more, water due to rainfall or the like does not accumulate on the surface of the weedproof sheet, and can quickly penetrate into the thickness direction of the weedproof sheet. Moreover, when planting using a herbicidal sheet, a sufficient water | moisture content can be replenished to a plant and also spraying of liquid manure is possible. Although the upper limit of the water permeability coefficient is not particularly limited, it may be about 0.8 cm / second from the relationship with the inter-fiber gap constituting the sheet. Moreover, a water-permeable coefficient can be controlled by providing a hydrophilic oil agent to a herbicidal sheet.
本発明の防草シートは、生分解性を有する重合体にて構成されているため、使用後に回収の手間を要しないものである。 Since the herbicidal sheet of the present invention is composed of a polymer having biodegradability, it does not require recovery after use.
また、本発明の防草シートは、脂肪族ジオール、脂肪族ジカルボン酸および脂肪族ヒドロキシカルボン酸を構成成分とする脂肪族ポリエステル共重合体（ａ）とポリ乳酸系重合体とがブレンドしてなる重合体（Ａ成分）が鞘成分、ポリ乳酸系重合体（Ｂ成分）が芯成分に配された芯鞘型複合長繊維からなり、Ａ成分の少なくとも一部が溶融または軟化することにより、繊維同士が熱接着して形態保持している不織布によって構成される。 In addition, the herbicidal sheet of the present invention is obtained by blending an aliphatic polyester copolymer (a ) having an aliphatic diol, an aliphatic dicarboxylic acid and an aliphatic hydroxycarboxylic acid as constituents and a polylactic acid-based polymer. A polymer (A component) consists of a core-sheath type composite continuous fiber in which a sheath component and a polylactic acid polymer (B component) are arranged in a core component, and at least a part of the A component melts or softens, It is comprised with the nonwoven fabric which mutually heat-bonds and hold | maintains a form.
接着成分となるＡ成分には、脂肪族ポリエステル共重合体（ａ）がブレンドされていることにより、繊維同士の接着強力が向上するため、得られる防草シートの機械的強力、伸度が向上し優れたタフネスを有するものとなる。したがって、本発明の防草シートを施工する際に施工者が防草シートの上からシートを踏みつけても、またシート下の石等の突起物を踏んだ場合であっても容易に破れることはない。 Adhesive component A is blended with aliphatic polyester copolymer (a ) to improve the adhesive strength between fibers, thus improving the mechanical strength and elongation of the resulting herbicidal sheet. And it has excellent toughness. Therefore, when constructing the weedproof sheet of the present invention, even if the installer steps on the sheet from above the weedproof sheet, it can be easily torn even if it steps on a protrusion such as a stone under the sheet. Absent.
Ａ成分およびＢ成分に用いるポリ乳酸系重合体の融点が、共に１５０℃以上であることから、結晶性が高く、熱的安定性を有する。したがって、紡糸の際の冷却性が良好となり、例えばスパンボンド法により良好に不織布を得ることができ、スパンボンド法による高速紡糸によって結晶配向が進み、得られる防草シートの耐熱性、耐候性、機械的強力が優れたものとなる。 Since the melting points of the polylactic acid polymers used for the A component and the B component are both 150 ° C. or higher, the crystallinity is high and the thermal stability is obtained. Therefore, the cooling property during spinning becomes good, for example, a non-woven fabric can be obtained satisfactorily by the spunbond method, the crystal orientation proceeds by high-speed spinning by the spunbond method, and the heat resistance, weather resistance, Mechanical strength is excellent.
また、複合長繊維は顔料が含有されている原着繊維であり、後加工による染色が不要となり、染色により繊維が熱劣化することなく、経時的な強力低下が少なく耐候性に優れた防草シートを得ることができる。 In addition, composite long fibers are original fibers that contain pigments and do not require dyeing by post-processing, and the fibers do not thermally deteriorate due to dyeing. A sheet can be obtained.
以下、実施例により本発明を具体的に説明する。なお、本発明はこれらの実施例のみに限定されるものではない。下記の実施例および比較例における各物性値等は、以下により求めた。
（１）重合体の融点（℃）；パーキンエルマ社製示差走査型熱量計ＤＳＣ−７型を用い、試料質量を５ｍｇ、昇温速度を１０℃／分として測定して得られた融解吸熱曲線の吸熱ピークの極値を与える温度を融点Ｔｍ（℃）とした。
（２）目付（ｇ／ｍ2）；不織布から縦１０ｃｍ×横１０ｃｍの試料片各１０点を作製し、標準状態における各試料片の質量（ｇ）を秤量し、得られた値の平均値を単位面積当たりに換算して、不織布の目付（ｇ／ｍ2）とした。
（３）Ｌ＊値、ａ＊値、ｂ＊値：色彩色差計（データプロセッサ ＤＰ−３００、測定ヘッド ＣＲ−３１０：ミノルタ社製）を用い、測定箇所の試料の目付が３００ｇ／ｍ2以上となるように、シートを折りたたみ、設置して測定した。測定の際は、測定個所を変えて４個所測定し、得られた値の平均値をＬ＊値、ａ＊値、ｂ＊値とした。なお、シートの表裏面の形態が異なるものについては、各面共に２個所づつ測定し、それらの平均値をＬ＊値、ａ＊値、ｂ＊値とした。
（４）破裂強力（ｋＰａ）：ＪＩＳ Ｌ １９０６ ミューレン形法に基づき測定した。
Hereinafter, the present invention will be described specifically by way of examples. In addition, this invention is not limited only to these Examples. The physical property values and the like in the following examples and comparative examples were determined as follows.
(1) Melting point (° C.) of polymer; melting endothermic curve obtained by using a differential scanning calorimeter DSC-7 manufactured by Perkin Elma Co., Ltd. with a sample mass of 5 mg and a heating rate of 10 ° C./min. The temperature giving the extreme value of the endothermic peak was defined as the melting point Tm (° C.).
(2) Weight per unit area (g / m 2 ); 10 pieces each of 10 cm long × 10 cm wide sample pieces were prepared from the nonwoven fabric, the weight (g) of each sample piece in the standard state was weighed, and the average value of the obtained values Was converted to unit weight per unit area to obtain the basis weight of the nonwoven fabric (g / m 2 ).
(3) L * value, a * value, b * value: Using a color difference meter (data processor DP-300, measuring head CR-310: manufactured by Minolta), the basis weight of the sample at the measurement location is 300 g / m 2 or more. Then, the sheet was folded and placed and measured. At the time of measurement, the measurement locations were changed and four locations were measured, and the average values obtained were taken as L * values, a * values, and b * values. In addition, about the thing from which the form of the front and back of a sheet | seat differs, each surface measured two places, and those average values were made into L * value, a * value, and b * value.
(4) Burst strength (kPa): Measured based on JIS L 1906 Murren method.
実施例１
融点１５５℃、ＭＦＲ６０ｇ／１０分のＤ、Ｌ−乳酸共重合体（共重合比 Ｌ−乳酸／Ｄ−乳酸＝９５.５／４.５（モル％）：以下、ＰＬＡ１という。）と、融点１１０℃、ＭＦＲ４０ｇ／１０分である１，４−ブタンジオール、コハク酸および乳酸からなる脂肪族ポリエステル共重合体（ａ）（三菱化学社製 商品名ＧＳＰｌａ）と、添加剤としてタルクとを、質量比でＰＬＡ１／脂肪族ポリエステル共重合体（ａ）＝７９／２０（質量部）となるように溶融ブレンドし、これに１質量部のタルクを添加し、３者がブレンドしてなる重合体（Ｐ１）を用意した。
また、融点１６８℃、ＭＦＲ７０ｇ／１０分のＤ、Ｌ−乳酸共重合体（共重合比 Ｌ−乳酸／Ｄ−乳酸＝９８.６／１.４（モル％）：以下、ＰＬＡ２という。）８０質量部にタルク２０質量部を含有させたマスターバッチ（Ｍ１）と、ＰＬＡ１（７６．７質量部）に下記（１）〜（３）の顔料を含有させたマスターバッチ（Ｍ２）とを用意した。
（１）イエロー系顔料 １４．７質量部
（２）レッド系顔料 ４．８質量部
（３）カーボンブラック ３．８質量部
Ａ成分中の顔料の含量合計が１．７質量％となるように、Ｐ１とＭ２とを配合したものをＡ成分とした。
一方、重合体中のタルクの含量が１．５質量％となるようにＰＬＡ２とＭ１とを配合したものをＢ成分とした。
Ｂ成分を芯部、Ａ成分を鞘部に配し、芯部／鞘部＝１．２５／１（質量比）となるように個別に溶融計量した後、個別のエクストルーダー型押し出し機を用いて紡糸温度２１０℃で溶融し、芯鞘型複合断面となるように単孔吐出量１.３８ｇ／分の条件下で溶融紡糸した。
紡出糸条を公知の冷却装置にて冷却した後、引き続いて紡糸口金の下方に設けたエア−サッカーにて高速で牽引細化し、公知の開繊器具を用いて開繊し、移動するスクリーンコンベア上に捕集堆積させウエブを得た。なお、開繊性は良好であり、堆積させた芯鞘型複合長繊維の単糸繊度は３.３デシテックスであった。
次いで、得られたウエブをエンボスロールとフラットロールとからなるエンボス装置（ロール表面温度９５℃）に通して部分的に熱圧着し、次いで、親水性油剤を付与（繊維質量に対して固形分質量で０．２質量％）して目付１１０ｇ／ｍ2の不織布を得た。得られた不織布を所定の大きさに裁断し、本発明の防草シートを得た。
Example 1
Melting point 155 ° C., MFR 60 g / 10 min D, L-lactic acid copolymer (copolymerization ratio L-lactic acid / D-lactic acid = 95.5 / 4.5 (mol%): hereinafter referred to as PLA1), melting point An aliphatic polyester copolymer (a) (trade name GSPla, manufactured by Mitsubishi Chemical Corporation) composed of 1,4-butanediol, succinic acid and lactic acid at 110 ° C. and MFR 40 g / 10 min, and talc as an additive, PLA1 / aliphatic polyester copolymer (a) = 79/20 (parts by mass) by melt blending, 1 part by mass of talc is added thereto, and a polymer obtained by blending the three ( P1) was prepared.
Further, a D, L-lactic acid copolymer having a melting point of 168 ° C. and an MFR of 70 g / 10 min (copolymerization ratio L-lactic acid / D-lactic acid = 98.6 / 1.4 (mol%): hereinafter referred to as PLA2) 80 A masterbatch (M1) containing 20 parts by mass of talc in a mass part and a masterbatch (M2) containing the following pigments (1) to (3) in PLA1 (76.7 parts by mass) were prepared. .
(1) Yellow pigment 14.7 parts by mass (2) Red pigment 4.8 parts by mass (3) Carbon black 3.8 parts by mass The total pigment content in component A is 1.7% by mass. , P1 and M2 were blended as component A.
On the other hand, what mixed PLA2 and M1 so that the content of talc in a polymer might be 1.5 mass% was made into B component.
B component is placed in the core, A component is placed in the sheath, and melted and measured separately so that the core / sheath is 1.25 / 1 (mass ratio), and then an individual extruder type extruder is used. The melt was melted at a spinning temperature of 210 ° C., and melt-spun at a single-hole discharge rate of 1.38 g / min so as to have a core-sheath composite cross section.
After the spinning yarn is cooled by a known cooling device, it is subsequently pulled at high speed with an air-soccer provided below the spinneret, opened using a known opening device, and moved. The web was obtained by collecting and depositing on a conveyor. In addition, the fiber opening property was good, and the single yarn fineness of the deposited core-sheath type composite continuous fiber was 3.3 dtex.
Next, the obtained web was partially thermocompression-bonded through an embossing device (roll surface temperature 95 ° C.) composed of an embossing roll and a flat roll, and then a hydrophilic oil agent was applied (solid mass to fiber mass) 0.2 mass%) to obtain a nonwoven fabric having a basis weight of 110 g / m 2 . The obtained nonwoven fabric was cut into a predetermined size to obtain a herbicidal sheet of the present invention.
実施例２
Ａ成分として下記のものを用いたこと、得られたウエブを熱圧着する際のエンボス装置のロール表面温度を１２０℃としたこと以外は、実施例１と同様にして防草シートを得た。
（Ａ成分）
ＰＬＡ２と、融点１１０℃、ＭＦＲ４０ｇ／１０分である１，４−ブタンジオール、コハク酸および乳酸からなる脂肪族ポリエステル共重合体（ａ）（三菱化学社製 商品名ＧＳＰｌａ）と、添加剤としてタルクとを、質量比でＰＬＡ２／脂肪族ポリエステル共重合体（ａ）＝７９／２０（質量部）となるように溶融ブレンドし、これに１質量部のタルクを添加し、３者がブレンドしてなる重合体（Ｐ２）を用意した。
また、ＰＬＡ２（７６．７質量部）に下記（１）〜（３）の顔料を含有させたマスターバッチ（Ｍ３）とを用意した。
（１）イエロー系顔料 １４．７質量部
（２）レッド系顔料 ４．８質量部
（３）カーボンブラック ３．８質量部
Ａ成分中の顔料の含量合計が１．７質量％となるように、Ｐ２とＭ３とを配合したものをＡ成分として用いた。
Example 2
A herbicidal sheet was obtained in the same manner as in Example 1 except that the following were used as the component A, and the roll surface temperature of the embossing device when the obtained web was thermocompression bonded was 120 ° C.
(A component)
PLA2, an aliphatic polyester copolymer (a) (trade name GSPla, manufactured by Mitsubishi Chemical Corporation) composed of 1,4-butanediol, succinic acid and lactic acid having a melting point of 110 ° C. and an MFR of 40 g / 10 min, and talc as an additive Are melt blended so that PLA2 / aliphatic polyester copolymer (a) = 79/20 (parts by mass) in mass ratio, and 1 part by mass of talc is added thereto, and the three parties blend. A polymer (P2) was prepared.
Moreover, the masterbatch (M3) which made PLA2 (76.7 mass parts) contain the pigment of following (1)-(3) was prepared.
(1) Yellow pigment 14.7 parts by mass (2) Red pigment 4.8 parts by mass (3) Carbon black 3.8 parts by mass The total pigment content in component A is 1.7% by mass. , P2 and M3 were used as the A component.
実施例３
Ａ成分として下記を用いたこと以外は、実施例２と同様にして防草シートを得た。
（Ａ成分）
ＰＬＡ２（８０質量部）にカーボンブラックを２０質量部含有させたマスターバッチ（Ｍ４）を用意した。
Ａ成分中の顔料の含量合計が０．５質量％となるように、Ｐ２とＭ４とを配合したものをＡ成分として用いた。
Example 3
A herbicidal sheet was obtained in the same manner as in Example 2 except that the following was used as the component A.
(A component)
A master batch (M4) in which 20 parts by mass of carbon black was contained in PLA2 (80 parts by mass) was prepared.
A blend of P2 and M4 was used as the A component so that the total content of pigments in the A component was 0.5% by mass.
参考例
ＰＬＡ２、Ｍ１、Ｍ３を用意し、重合体中のタルクの含量が０．５質量％、顔料の含量が１．７質量％となるように、ＰＬＡ２とＭ１、Ｍ３とを配合したものをエクスとルーダー型押し出し機を用いて紡糸温度２１０℃で溶融し、単相型断面となるように単孔吐出量１.６７ｇ／分の条件下で溶融紡糸した。
紡出糸条を公知の冷却装置にて冷却した後、引き続いて紡糸口金の下方に設けたエア−サッカーにて高速で牽引細化し、公知の開繊器具を用いて開繊し、移動するスクリーンコンベア上に捕集堆積させウエブを得た。なお、開繊性は良好であり、堆積させた芯鞘型複合長繊維の単糸繊度は３.３デシテックスであった。
次いで、得られたウエブをエンボスロールとフラットロールとからなるエンボス装置（ロール表面温度１３０℃）に通して部分的に熱圧着し、次いで、親水性油剤を付与（繊維質量に対して固形分質量で０．２質量％）して目付１１０ｇ／ｍ2の不織布を得た。得られた不織布を所定の大きさに裁断し、参考例の防草シートを得た。
Reference Example PLA2, M1, M3 were prepared and blended with PLA2, M1, and M3 so that the talc content in the polymer was 0.5% by mass and the pigment content was 1.7% by mass. The mixture was melted at a spinning temperature of 210 ° C. using an ex and a rudder type extruder, and melt-spun at a single hole discharge rate of 1.67 g / min so as to have a single-phase cross section.
After the spinning yarn is cooled by a known cooling device, it is subsequently pulled at high speed with an air-soccer provided below the spinneret, opened using a known opening device, and moved. The web was obtained by collecting and depositing on a conveyor. In addition, the fiber opening property was good, and the single yarn fineness of the deposited core-sheath type composite continuous fiber was 3.3 dtex.
Next, the obtained web is partially thermocompression-bonded through an embossing device (roll surface temperature 130 ° C.) composed of an embossing roll and a flat roll, and then a hydrophilic oil agent is applied (solid mass to fiber mass). 0.2 mass%) to obtain a nonwoven fabric having a basis weight of 110 g / m 2 . The obtained nonwoven fabric was cut into a predetermined size to obtain a herbicidal sheet of a reference example.
得られた実施例１〜３、参考例の防草シートについて、その物性を表１に示した。また、防草効果について下記方法により評価し、その結果も表１に示した。
（防草効果）
植物を植栽している土壌表面に敷設し、一定期間（６ヶ月）経過後、防草シート下の状況を観察して防草シートによる効果を評価した。評価は書きの基準により目視にて行った。
○：雑草の繁殖はなく、十分な防草効果があった。
×：雑草が繁殖している。
The physical properties of the obtained herbicidal sheets of Examples 1 to 3 and Reference Example are shown in Table 1. The herbicidal effect was evaluated by the following method, and the results are also shown in Table 1.
(Weed prevention effect)
The plant was laid on the surface of the soil, and after a certain period (six months), the situation under the herbicidal sheet was observed to evaluate the effect of the herbicidal sheet. The evaluation was made visually according to the writing standard.
○: There was no weed breeding and there was a sufficient herbicidal effect.
X: Weeds are breeding.
本発明の実施例１〜３の防草シートは、参考例の防草シートの物性と比較すると、引張強力については概ね３倍以上、破断伸度については２倍以上も向上し、また、破裂強力については１．５倍以上向上したものである。したがって、本発明の防草シートは、機械的強力がより向上し、タフネスに優れたものであることが分かる。
As compared with the physical properties of the reference herbicidal sheet, the herbicidal sheets of Examples 1 to 3 of the present invention are approximately 3 times or more in terms of tensile strength and 2 times or more in terms of elongation at break. The strength is improved by 1.5 times or more. Therefore, it can be seen that the weedproof sheet of the present invention has improved mechanical strength and excellent toughness.
Claims (4)
（１）Ａ成分およびＢ成分に用いるポリ乳酸系重合体の融点が共に１５０℃以上である。
（２）脂肪族ポリエステル共重合体（ａ）の融点がＢ成分の融点よりも低い。
（３）脂肪族ポリエステル共重合体（ａ）が結晶融点を有している。 The sheath component is a polymer (component A) obtained by blending an aliphatic polyester copolymer (a ) having an aliphatic diol, an aliphatic dicarboxylic acid and an aliphatic hydroxycarboxylic acid as constituent components and a polylactic acid polymer. , Composed of core-sheath type composite filaments in which a polylactic acid polymer (component B) is arranged as a core component, and the polylactic acid polymer is poly-D-lactic acid, poly-L-lactic acid, D-lactic acid and L -A copolymer with lactic acid or a blend thereof , and the polymer constituting the composite long fiber satisfies the melting characteristics (1) to (3) below, and at least a part of the component A is melted or It is constituted by a nonwoven fabric in which the fibers are thermally bonded to each other by softening, and the composite long fiber is an original fiber in which a pigment is contained in at least one of the A component and the B component. Characteristic herbicidal sheet.
(1) The melting points of the polylactic acid polymers used for the A component and the B component are both 150 ° C. or higher.
(2) melting point of the aliphatic polyester copolymer (a) is lower than the melting point of the B component.
(3) The aliphatic polyester copolymer (a ) has a crystalline melting point.
The L * value of a nonwoven fabric is 40 or less, The weedproof sheet of any one of Claims 1-3 characterized by the above-mentioned.