JP4232780B2 - 水性加硫接着剤組成物 - Google Patents
水性加硫接着剤組成物 Download PDFInfo
- Publication number
- JP4232780B2 JP4232780B2 JP2005504928A JP2005504928A JP4232780B2 JP 4232780 B2 JP4232780 B2 JP 4232780B2 JP 2005504928 A JP2005504928 A JP 2005504928A JP 2005504928 A JP2005504928 A JP 2005504928A JP 4232780 B2 JP4232780 B2 JP 4232780B2
- Authority
- JP
- Japan
- Prior art keywords
- phenol resin
- adhesive composition
- weight
- aqueous
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
メチルエチルケトン(20℃における水に対する溶解度27%)500gを攪拌しながら、そこにノボラック型フェノール樹脂(大日本インキ化学製品フェノライトTD-2106)500gを徐々に添加し、添加終了後約1〜2時間攪拌を継続し、完全に溶解させた(フェノール樹脂溶液a)。
(配合例I)
NBR(JSR製品N237) 100重量部
SRFカーボンブラック 93 〃
ジオクチルフタレート 15 〃
亜鉛華 5 〃
ステアリン酸 3 〃
老化防止剤(大内新興化学製品ノクラック224) 1 〃
テトラメチルチウラムジサルファイド 1 〃
メルカプトベンゾチアゾール 1 〃
ジチオカルバミン酸亜鉛 0.8 〃
イオウ 0.2 〃
(配合例II)
活性塩素含有アクリルゴム(ユニマテック製品PA402) 100重量部
HAFカーボンブラック 40 〃
粉末状シリカ 2 〃
マイクロクリスタリンワックス 6 〃
ステアリン酸 3 〃
4,4′-ビス(2,2′-ジメチルベンジル)ジフェニルアミン 2 〃
イオウ 1 〃
ステアリン酸ナトリウム 3.5 〃
メチルエチルケトン330gを攪拌しながら、そこにノボラック型フェノール樹脂(群栄化学製品PSF-2803)350gおよびレゾール型フェノール樹脂(同社製品レヂトップPL-2108;固形分濃度47重量%のメチルエチルケトン溶液)320gを徐々に添加し、添加終了後約1〜2時間攪拌を継続し、完全に溶解させた(フェノール樹脂溶液b)。
メチルエチルケトン330gを攪拌しながら、そこにノボラック型フェノール樹脂(フェノライトTD-2106)350gを徐々に添加し、添加終了後約1〜2時間攪拌を継続し、完全に溶解させた。その後レゾール型フェノール樹脂(レヂトップPL-2108;固形分濃度47重量%メチルエチルケトン溶液)320gを添加し、数分間混合、攪拌した(フェノール樹脂溶液c)。
常温の水900gを攪拌しながら、そこにアセトアセチル基変性ポリビニルアルコール(日本合成化学製品ゴーセファイマーZ-320;けん化度93モル%、変性度5.7モル%)100gを徐々に添加し、添加終了後約1時間かけて85℃迄昇温させ、さらにその温度を保ちながら1時間攪拌して完全に溶解させた後、室温迄戻した。
実施例1において、フェノール樹脂溶液aの代わりに比較例3において用いられたフェノール樹脂溶液cが同量用いられた。
実施例1において、フェノール樹脂溶液aの代わりにフェノール樹脂溶液cが同量用いられ、またフェノール樹脂エマルジョンを調製後、さらにジヒドロキシチタンビスラクテート2gを添加し、約3000rpmで約3分間攪拌したものが用いられた。
実施例1において、加硫接着剤組成物としてノボラック型フェノール樹脂(フェノライトTD-2106)90g、ヘキサメチレンテトラミン4.5gおよびメタノール905.5gからなる溶剤系加硫接着剤組成物(有機溶剤含有率90.6%)が用いられた。
表1
例 接着強度(N/mm) ゴム残留面積率(%)
初期 温水70時間 温水140時間 初期 温水70時間 温水140時間
比較例1 19.2 5.6 4.8 100 0 0
〃 2 19.4 8.0 5.0 100 20 0
〃 3 19.1 7.9 5.0 100 10 0
実施例1 19.3 18.0 16.3 100 90 50
〃 2 19.3 18.5 17.8 100 100 70
〃 3 19.2 19.0 18.2 100 100 95
参 考 例 19.3 19.2 19.2 100 100 100
表2
例 接着強度(N/mm) ゴム残留面積率(%)
初期 温水70時間 温水140時間 初期 温水70時間 温水140時間
比較例1 9.0 2.5 1.9 100 0 0
〃 2 9.1 3.0 2.0 100 10 0
〃 3 8.9 3.4 2.3 100 5 0
実施例1 9.1 7.3 6.0 100 95 80
〃 2 9.1 7.7 6.2 100 100 90
〃 3 9.2 7.7 6.8 100 100 100
参 考 例 9.0 7.7 6.8 100 100 100
Claims (14)
- 水不溶性フェノール樹脂のメチルエチルケトン溶液とアセトアセチル基変性ポリビニルアルコール水溶液とから調製されたフェノール樹脂エマルジョンおよびフェノール樹脂用硬化剤を含有してなり、メチルエチルケトン含有量が10重量%以下である水性加硫接着剤組成物。
- 水不溶性フェノール樹脂が5〜25重量%、アセトアセチル基変性ポリビニルアルコールが0.2〜6重量%、メチルエチルケトンが3〜40重量%、そして残部が水となる混合比率を有するフェノール樹脂エマルジョンが用いられた請求項1記載の水性加硫接着剤組成物。
- 水不溶性フェノール樹脂がノボラック型フェノール樹脂またはそれとレゾール型フェノール樹脂との混合物である請求項1記載の水性加硫接着剤組成物。
- ノボラック型フェノール樹脂100重量部当り200重量部以下のレゾール型フェノール樹脂が併用された請求項3記載の水性加硫接着剤組成物。
- 水不溶性フェノール樹脂が濃度40〜60重量%のメチルエチルケトン溶液として用いられた請求項1記載の水性加硫接着剤組成物。
- さらに有機金属化合物が添加された請求項1記載の水性加硫接着剤組成物。
- フェノール樹脂用硬化剤がヘキサメチレンテトラミンである請求項1記載の水性加硫接着剤組成物。
- ヘキサメチレンテトラミンがフェノール樹脂エマルジョン 100 重量部当り 0.1 〜 5 重量部の割合で用いられた請求項7記載の水性加硫接着剤組成物。
- ヘキサメチレンテトラミンと共に水が用いられた請求項7記載の水性加硫接着剤組成物。
- 水がフェノール樹脂エマルジョン 100 重量部当り 1000 重量部以下の割合で用いられた請求項9記載の水性加硫接着剤組成物。
- 金属または樹脂とゴムとの加硫接着に用いられる請求項1記載の水性加硫接着剤組成物。
- ゴムがニトリルゴム、水素化ニトリルゴムまたはアクリルゴムである請求項11記載の水性加硫接着剤組成物。
- 請求項1記載の水性加硫接着剤組成物で加硫接着されたゴムと金属または樹脂との複合体。
- 水不溶性フェノール樹脂のメチルエチルケトン溶液とアセトアセチル基変性ポリビニルアルコール水溶液とから調製されたフェノール樹脂エマルジョン。