JP4135741B2 - Tetrafluoroethylene copolymer film - Google Patents
Tetrafluoroethylene copolymer film Download PDFInfo
- Publication number
- JP4135741B2 JP4135741B2 JP2005315677A JP2005315677A JP4135741B2 JP 4135741 B2 JP4135741 B2 JP 4135741B2 JP 2005315677 A JP2005315677 A JP 2005315677A JP 2005315677 A JP2005315677 A JP 2005315677A JP 4135741 B2 JP4135741 B2 JP 4135741B2
- Authority
- JP
- Japan
- Prior art keywords
- copolymer
- film
- layer
- tetrafluoroethylene
- tetrafluoroethylene copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、テトラフルオロエチレン共重合体フィルムに関し、さらに詳しくは、種々の有機材料や無機材料からなる基材に対して強固に接着しうる透明性に優れるテトラフルオロエチレン共重合体からなるフィルムに関する。 The present invention relates to a tetrafluoroethylene copolymer film , and more particularly to a film made of a tetrafluoroethylene copolymer excellent in transparency that can be firmly bonded to a substrate made of various organic materials and inorganic materials. .
従来一般的に使用されている成形用フッ素樹脂には、テトラフルオロエチレン／ヘキサフルオロプロピレン共重合体（ＦＥＰ）、テトラフルオロエチレン／パーフルオロアルキルビニルエーテル共重合体（ＰＦＡ）、テトラフルオロエチレン／エチレン共重合体（ＥＴＦＥ）などがある。 Conventionally used fluororesins for molding include tetrafluoroethylene / hexafluoropropylene copolymer (FEP), tetrafluoroethylene / perfluoroalkyl vinyl ether copolymer (PFA), and tetrafluoroethylene / ethylene copolymer. There are polymers (ETFE) and the like.
これらフッ素樹脂は、優れた耐熱性、耐薬品性、耐溶剤性、耐候性、摺動性、電気絶縁性、難燃性を有しているので、自動車、産業機械、ＯＡ機器、電気・電子機器などの分野で広く用いられている。 These fluororesins have excellent heat resistance, chemical resistance, solvent resistance, weather resistance, slidability, electrical insulation, and flame resistance, so they can be used in automobiles, industrial machines, office automation equipment, electrical / electronics. Widely used in fields such as equipment.
一方、フッ素樹脂は、一般的に機械的強度や寸法安定性が不十分であったり、価格的に高価であったりする。
そこでフッ素樹脂の長所を最大限に生かし、欠点を最小とするため、フッ素樹脂と他の有機材料または無機材料との接着または積層化の検討が行われている。
しかし、フッ素樹脂は表面エネルギーが小さいので、一般に他の材料との親和性が乏しく、接着力が低く、フッ素樹脂と他の材料（基材）とを直接接着することは困難である。フッ素樹脂と他の材料と熱融着しても、接着強度はなお不十分である。
On the other hand, a fluororesin generally has insufficient mechanical strength and dimensional stability or is expensive in price.
Therefore, in order to make the best use of the advantages of the fluororesin and minimize the drawbacks, studies have been made on adhesion or lamination of the fluororesin with other organic or inorganic materials.
However, since the fluororesin has a small surface energy, it generally has poor affinity with other materials, has low adhesive strength, and it is difficult to directly bond the fluororesin and another material (base material). Even if the fluororesin and other materials are heat-sealed, the adhesive strength is still insufficient.
フッ素樹脂と他の材料とを接着させる方法として、次のような方法が主に検討されている：
１．フッ素樹脂フィルムの表面を、ナトリウムエッチング、プラズマ処理、光化学的処理などの表面処理に付した後、両者を接着する方法。
２．基材の表面を、サンドブラスター処理などで物理的に粗面化した後、両者を接着する方法。
３．接着剤を用いて両者を接着する方法。
The following methods are mainly studied as a method of bonding the fluororesin and other materials:
1. A method in which the surface of a fluororesin film is subjected to a surface treatment such as sodium etching, plasma treatment, photochemical treatment, and the like, and then both are adhered.
2. A method in which the surface of the substrate is physically roughened by sandblasting or the like, and then both are bonded.
3. A method of bonding the two using an adhesive.
前記１および２の方法は、前処理工程を必要とし、全体の工程が複雑となるので、生産性が悪い。その上、接着力が不十分であり、得られた積層体の外観上の問題、例えば着色や傷も生じやすい。
前記３の方法で用いる接着剤の検討も種々行われている。一般にハイドロカーボン等の接着剤はフッ素樹脂との接着性が不十分であり、積層体も、接着剤層の耐薬品性、耐水性、耐候性が不十分であるために、温度変化や環境変化により接着力が維持できなくなり、信頼性に欠ける。
The methods 1 and 2 require a pretreatment process, and the entire process becomes complicated, so that productivity is poor. In addition, the adhesive strength is insufficient, and problems in appearance of the obtained laminate, such as coloring and scratches, are likely to occur.
Various studies on the adhesive used in the above method 3 have also been conducted. Generally, adhesives such as hydrocarbons have insufficient adhesion to fluororesins, and laminates also have insufficient chemical resistance, water resistance, and weather resistance. As a result, the adhesive force cannot be maintained, and reliability is lacking.
ところで、従来のフッ素樹脂の融点は２５０℃以上であるため、成形を通常３００℃以上の温度で行う必要があるが、この成形温度は、汎用樹脂（例えば、ポリアミド、ポリエステル、ポリメタクリレート、ポリ塩化ビニル、ポリスチレン、ＡＢＳ、ポリアセタール、ポリカーボネート、エポキシ樹脂、ポリウレタンなど）やこれら汎用樹脂を用いた繊維強化樹脂（ＦＲＰ）の適切な成形温度範囲より高い。従って、このような汎用樹脂のフィルムとフッ素樹脂フィルムとを熱融着させるためには、３００℃以上の温度を必要とするが、そのような高い温度では、汎用樹脂が分解、発泡または着色を起こし、実用的でない。またこれら汎用樹脂とフッ素樹脂を多層共押出をすることは、前記の成形温度の違いから困難である。 By the way, since the melting point of the conventional fluororesin is 250 ° C. or higher, it is necessary to perform molding usually at a temperature of 300 ° C. or higher. This molding temperature is a general-purpose resin (for example, polyamide, polyester, polymethacrylate, polychlorinated). Vinyl, polystyrene, ABS, polyacetal, polycarbonate, epoxy resin, polyurethane, and the like) and a fiber reinforced resin (FRP) using these general-purpose resins. Accordingly, in order to thermally bond such a general-purpose resin film and a fluororesin film, a temperature of 300 ° C. or higher is required. At such a high temperature, the general-purpose resin is decomposed, foamed or colored. Waking up and impractical. In addition, it is difficult to perform multilayer coextrusion of these general-purpose resins and fluororesins due to the difference in the molding temperature.
ポリテトラフルオロエチレンの性質を改良する為に、種々のコモノマーをテトラフルオロエチレンと共重合させることは、古くから知られている。
例えば、特開昭４９−９８４８８号公報は、テトラフルオロエチレン（ＴＦＥ）２０〜３０モル％、エチレン（Ｅt）４０〜６０モル％、およびヘキサフルオロプロピレン（ＨＦＰ）１０〜３０モル％からなるターポリマーを開示している。この公開公報は、開示されたターポリマーの有利な性質が、特定した組成範囲内でのみ達成されうることを明記している。その実施例に挙げられたターポリマーは、４６〜５０モル％のＥtを含んでいる。従って、ＴＦＥの含有量が相対的に少なく、フッ素樹脂特有の性質である耐候性、耐薬品性、難燃性、非粘着性、防汚性が低下する。
It has long been known to copolymerize various comonomers with tetrafluoroethylene to improve the properties of polytetrafluoroethylene.
For example, JP-A-49-98488 discloses a terpolymer comprising tetrafluoroethylene (TFE) 20 to 30 mol%, ethylene (Et) 40 to 60 mol%, and hexafluoropropylene (HFP) 10 to 30 mol%. Is disclosed. This publication specifies that the advantageous properties of the disclosed terpolymers can only be achieved within the specified composition range. The terpolymers mentioned in the examples contain 46-50 mol% Et. Accordingly, the content of TFE is relatively small, and the weather resistance, chemical resistance, flame retardancy, non-adhesiveness, and antifouling properties, which are properties unique to fluororesins, are reduced.
米国特許第４３３８２３７号は、ＴＦＥ−Ｅt−ＨＦＰターポリマーを含む安定したコロイド水性分散体の製造方法を開示している。モノマー組成は、ＴＦＥ３０〜６０モル％、Ｅt４０〜６０モル％、およびＨＦＰ０〜１５モル％である。その実施例に挙げられたターポリマーは、４.５または４.７モル％のＨＦＰとそれに対応して４６.５または４６.８モル％のＥtを含んでいる。しかし、同特許明細書には、種々の基材に対する接着性を向上させるポリマー組成を示す記載は含まれていない。 U.S. Pat. No. 4,338,237 discloses a process for preparing a stable colloidal aqueous dispersion comprising a TFE-Et-HFP terpolymer. The monomer composition is 30-60 mol% TFE, 40-60 mol% Et, and 0-15 mol% HFP. The terpolymers mentioned in the examples contain 4.5 or 4.7 mol% HFP and correspondingly 46.5 or 46.8 mol% Et. However, the patent specification does not include a description showing a polymer composition that improves adhesion to various substrates.
特開平８−４１１３１号公報は、ＴＦＥ４５〜５５モル％、ＨＦＰ１０〜２０モル％およびＥｔ２５〜４０モル％を含み、約１４０〜１７０℃の融点を有するターポリマーを開示している。この公開公報は、重合開始剤としてパーオキシカーボネートを用いること、またはポリマー鎖末端をカーボネート末端とすることは記載していない。 Japanese Patent Application Laid-Open No. 8-41131 discloses a terpolymer having a melting point of about 140 to 170 ° C. containing 45 to 55 mol% of TFE, 10 to 20 mol% of HFP and 25 to 40 mol% of Et. This publication does not describe the use of peroxycarbonate as a polymerization initiator or the use of a polymer chain terminal as a carbonate terminal.
特公昭５２−２４０７２号公報は、ＴＦＥ、ＨＦＰおよびＥｔの懸濁重合を開示し、モノマー組成として、ＴＦＥ２０〜８０モル％、ＨＦＰ２〜３０モル％およびＥｔ２０〜６０モル％を記載している。しかし、得られたポリマーの性質として、融点以外は具体的に記載されていない。
Japanese Patent Publication No. 52-24072 discloses suspension polymerization of TFE, HFP and Et, and describes the monomer composition of
近年、石油や石炭などの化石エネルギー源の枯渇が問題とされ、加えて、それらの燃焼時に発生するＣＯ２に起因する地球温暖化現象等の環境破壊が先進国および開発途上国を問わず、重要な問題となっている。そのような状況の下、太陽光発電は、無尽蔵の太陽輻射エネルギーを利用するクリーンな代替エネルギー源としてすでに実用化されている。 In recent years, depletion of fossil energy sources such as oil and coal has been a problem, and in addition, environmental destruction such as global warming due to CO 2 generated during the combustion of both these in developed and developing countries, It has become an important issue. Under such circumstances, photovoltaic power generation has already been put into practical use as a clean alternative energy source that uses inexhaustible solar radiation energy.
しかし、太陽電池の製造原価が高いので、広く一般に普及する段階まで至っていないのが現状である。そこで、結晶シリコン、多結晶シリコン、アモルファスシリコン、銅インジウムセレナイド、化合物半導体等の光起電力素子自体の光電変換効率の向上と同時に、太陽電池モジュール全体としての光電変換効率の向上や生産加工方法の改良を行う必要がある。
特に、太陽電池モジュールとしての光電変換効率の向上や生産加工方法の改良に関しては、光起電力素子の被覆材料特性、例えば透明性が大きく関係している。
However, since the manufacturing cost of solar cells is high, it has not yet reached the stage of widespread use. Therefore, improvement of the photoelectric conversion efficiency of the photovoltaic device itself such as crystalline silicon, polycrystalline silicon, amorphous silicon, copper indium selenide, compound semiconductor, etc., and improvement of the photoelectric conversion efficiency as a whole solar cell module and production processing method It is necessary to make improvements.
In particular, regarding the improvement of the photoelectric conversion efficiency as a solar cell module and the improvement of the production processing method, the coating material characteristic of the photovoltaic element, for example, transparency is greatly related.
太陽電池モジュールの基本構造の概略断面図を図３に示す。絶縁基板４に光起電力素子３が設けられ、該光起電力素子３の保護層として透明充填材層２、さらに最外層（表面に露出している層）として表面フィルム１が設けられている。したがって、表面フィルムとしては、光の透過性が良く、長期間屋外で太陽光に暴露されることから、耐候性や耐熱性に優れたものでなければならない。また外部からの衝撃に対して光起電力素子を保護できる耐衝撃性、透明性を疎外するような異物の付着防止性や、またそのような異物を簡単に除去できる防汚性が要求される。さらに透明充填材層または直接光起電力素子上に貼り合わせて使用する場合、充填材層や素子との接着性が必要となる。 A schematic cross-sectional view of the basic structure of the solar cell module is shown in FIG. A photovoltaic element 3 is provided on an insulating substrate 4, a transparent filler layer 2 is provided as a protective layer of the photovoltaic element 3, and a surface film 1 is provided as an outermost layer (layer exposed on the surface). . Therefore, the surface film must be excellent in weather resistance and heat resistance because it has good light transmittance and is exposed to sunlight outdoors for a long time. In addition, impact resistance that can protect the photovoltaic device against external impact, anti-adhesion of foreign matters that can alienate transparency, and antifouling properties that can easily remove such foreign matters are required. . Furthermore, when using it by bonding on a transparent filler layer or a direct photovoltaic element, the adhesiveness with a filler layer or an element is needed.
こうした要求を考慮して、表面フィルム１としてテトラフルオロエチレン−エチレン共重合体（ＥＴＦＥ）、ポリクロロトリフルオロエチレン（ＰＣＴＦＥ）、テトラフルオロエチレン−パーフルオロアルキルビニルエーテル共重合体（ＰＦＡ）、ポリフッ化ビニル（ＰＶＦ）、ポリフッ化ビニリデン（ＰＶＤＦ）、テトラフルオロエチレン−ヘキサフルオロプロピレン共重合体（ＦＥＰ）、ポリフッ化ビニリデン共重合体などの含フッ素重合体を用い、充填材層２にエチレン−酢酸ビニル共重合体（ＥＶＡ）またはブチラール樹脂を用いた太陽電池モジュールが特開平７−２９７４３９号公報に記載されている。しかし、含フッ素重合体は本質的に他の材料との接着性に劣り、その結果、表面フィルム１や充填材層２のズレ、剥離が生じてしまう。 In consideration of these requirements, the surface film 1 is made of tetrafluoroethylene-ethylene copolymer (ETFE), polychlorotrifluoroethylene (PCTFE), tetrafluoroethylene-perfluoroalkyl vinyl ether copolymer (PFA), polyvinyl fluoride. (PVF), polyvinylidene fluoride (PVDF), tetrafluoroethylene-hexafluoropropylene copolymer (FEP), polyvinylidene fluoride copolymer, etc. are used, and ethylene-vinyl acetate copolymer is used for the filler layer 2. A solar cell module using a polymer (EVA) or a butyral resin is described in JP-A-7-297439. However, the fluoropolymer is essentially inferior in adhesion to other materials, and as a result, the surface film 1 and the filler layer 2 are displaced and peeled off.
そこで、含フッ素重合体に無水マレイン酸やビニルメトキシシランなどに代表されるカルボキシル基、カルボン酸無水物残基、エポキシ基、加水分解性シリル基を有するハイドロカーボン系単量体をグラフト重合した含フッ素重合体を接着剤に用いた発明（たとえば、特開平７−１８０３５号公報、特開平７−２５９５２号公報、特開平７−２５９５４号公報、特開平７−１７３２３０号公報、特開平７−１７３４４６号公報、特開平７−１７３４４７号公報など）や、ヒドロキシルアルキルビニルエーテルのような官能基を含むハイドロカーボン系単量体をテトラフルオロエチレンやクロロトリフルオロエチレンと共重合した含フッ素共重合体とイソシアナート系硬化剤とを含む接着性組成物を硬化させ、ポリ塩化ビニルとコロナ放電処理されたＥＴＦＥとの接着剤としてに用いる発明（たとえば、特開平７−２２８８４８号公報）が成されている。 Therefore, the fluorine-containing polymer is grafted with a hydrocarbon monomer having a carboxyl group typified by maleic anhydride, vinyl methoxysilane, etc., a carboxylic anhydride residue, an epoxy group, or a hydrolyzable silyl group. Inventions using a fluoropolymer as an adhesive (for example, JP-A-7-18035, JP-A-7-259592, JP-A-7-25594, JP-A-7-173230, JP-A-7-173446 And fluorine-containing copolymers obtained by copolymerizing a hydrocarbon monomer containing a functional group such as hydroxyl alkyl vinyl ether with tetrafluoroethylene or chlorotrifluoroethylene, and isocyanate. Curing adhesive composition containing natto curing agent, polyvinyl chloride and corona discharge treatment Invention (e.g., JP-A-7-228848) is used to as an adhesive and ETFE which have been made.
これら、ハイドロカーボン系の官能基モノマーをグラフト重合または共重合した含フッ素樹脂を用いた接着剤組成物は耐熱性が不十分で、含フッ素樹脂フィルムとの複合体の製造工程において高温で加工するときに、分解や発泡が生じて、接着強度を低下させたり、剥離したり、着色したりする。
本発明の第１の目的は、前記のような従来技術の問題点を解決し、フッ素樹脂の優れた耐薬品性、耐候性、耐溶剤性、非粘着性、電気絶縁性、防汚性、難燃性を維持したまま、汎用樹脂や金属、ガラス、結晶シリコン、多結晶シリコン、アモルファスシリコンなどの他の材料に対して直接、強固に接着できるフッ素樹脂からなるフィルムを提供することである。
本発明の第２の目的は、従来のフッ素樹脂より低温で成形ができ、耐熱性のない汎用樹脂との熱融着、共押出が可能であるフッ素樹脂からなるフィルムを提供することである。
本発明の第３の目的は、従来のフッ素樹脂に比べて非常に透明性が高いフッ素樹脂からなるフィルムを提供することである。
The first object of the present invention is to solve the above-mentioned problems of the prior art, and the excellent chemical resistance, weather resistance, solvent resistance, non-adhesiveness, electrical insulation, antifouling property of fluororesin, An object is to provide a film made of a fluororesin that can be directly and firmly adhered to other materials such as general-purpose resin, metal, glass, crystalline silicon, polycrystalline silicon, and amorphous silicon while maintaining flame retardancy.
A second object of the present invention is to provide a film made of a fluororesin that can be molded at a lower temperature than conventional fluororesins and can be heat-sealed and coextruded with a general-purpose resin having no heat resistance.
The third object of the present invention is to provide a film made of a fluororesin that is very transparent as compared with conventional fluororesins.
上記目的を達成するために、本発明は、テトラフルオロエチレン４０モル％〜８１モル％とエチレン、ヘキサフルオロプロピレンおよび式：
ＣＨ２＝ＣＦＲf （Ｉ）
（式中、Ｒfは炭素数２〜１０のフルオロアルキル基である。）
で示されるフルオロビニル化合物からなる群から選択される少なくとも１種の他のモノマー６０〜１９モル％からなり、ポリマー鎖末端がカーボネート末端であり、１．０〜１００ｇ／１０分のメルトフローレート（２００℃，５kg荷重）、９０〜２００℃の融点、および２３０℃で１０〜１０３sec−１の臨界剪断速度
を有し、赤外線吸収スペクトルにおける主鎖のＣＨ２基に起因する２８８１cm−１での吸収ピークの高さに対する、末端カーボネート基に起因する１８０８cm−１での吸収ピークの高さの比が、少なくとも０.７である接着性テトラフルオロエチレン共重合体からなるフィルムを提供する。
In order to achieve the above object, the present invention relates to tetrafluoroethylene 40 mol% to 81 mol%, ethylene , hexafluoropropylene and the formula:
CH 2 = CFRf (I)
(In the formula, Rf is a fluoroalkyl group having 2 to 10 carbon atoms.)
A melt flow rate (1.0 to 100 g / 10 min) consisting of 60 to 19 mol% of at least one other monomer selected from the group consisting of fluorovinyl compounds represented by 200 ° C., 5 kg load), a melting point of 90-200 ° C., and a critical shear rate of 10-10 3 sec −1 at 230 ° C., at 2881 cm −1 due to the CH 2 group of the main chain in the infrared absorption spectrum A film made of an adhesive tetrafluoroethylene copolymer having a ratio of the height of the absorption peak at 1808 cm −1 due to the terminal carbonate group to the height of the absorption peak of at least 0.7 is provided.
本発明のテトラフルオロエチレン共重合体の特徴の１つは、他の材料との接着性が優れていることであるが、この優れた接着性は、ポリマー鎖末端構造と共重合体の溶融粘度特性に起因していると考えられる。
本発明のテトラフルオロエチレン共重合体のポリマー鎖末端は、カーボネート末端である。このようなカーボネート末端は、重合開始剤としてパーオキシカーボネートを用いることにより導入することができる。
One of the characteristics of the tetrafluoroethylene copolymer of the present invention is that it has excellent adhesion to other materials. This excellent adhesion is due to the polymer chain end structure and the melt viscosity of the copolymer. This is thought to be due to the characteristics.
The polymer chain terminal of the tetrafluoroethylene copolymer of the present invention is a carbonate terminal. Such a carbonate terminal can be introduced by using peroxycarbonate as a polymerization initiator.
このカーボネート末端が、本発明のテトラフルオロエチレン共重合体の他の材料に対する接着性を非常に向上させている。
このカーボネート末端は、他の材料が、例えばポリアミドの場合は、主鎖のアミド結合や末端のアミノ基またはカルボキシル基との、芳香族ポリエステルの場合は主鎖のエステル結合や末端のヒドロキシ基またはカルボキシ基との、エポキシ樹脂の場合は主鎖中のヒドロキシ基やカルボキシル基との反応性が高い。
This carbonate terminal greatly improves the adhesion of the tetrafluoroethylene copolymer of the present invention to other materials.
In the case of the other end of the carbonate terminal, for example, in the case of polyamide, the main chain amide bond or terminal amino group or carboxyl group, and in the case of aromatic polyester, the main chain ester bond or terminal hydroxy group or carboxyl group. In the case of an epoxy resin with a group, the reactivity with a hydroxy group or a carboxyl group in the main chain is high.
接着に寄与するカーボネート末端の含有量が、赤外線吸収スペクトルにおける主鎖のＣＨ２基に起因する２８８１cm−１での吸収ピークの高さに対する、末端カーボネート基に起因する１８０８cm−１での吸収ピークの高さの比（１８０８cm−１／２８８１cm−１）で表して、０.７以上であると、テトラフルオロエチレン共重合体は優れた接着性を有する。
この比の好ましい範囲は、０.７〜５.０であり、さらに好ましくは１.０〜３.０である。
この比が大きくなると、分子量が低くなり、上記範囲より大きいと機械的強度が低下し、実用上、好ましくない。
The content of contributing carbonate end to adhesion, the absorption peak at 2881cm -1 due to CH 2 groups of the main chain in the infrared absorption spectrum to the height of the absorption peak at 1808cm -1 due to end carbonate groups Expressed by a height ratio (1808 cm −1 / 2881 cm −1 ) and having a ratio of 0.7 or more, the tetrafluoroethylene copolymer has excellent adhesiveness.
A preferable range of this ratio is 0.7 to 5.0, and more preferably 1.0 to 3.0.
When this ratio is increased, the molecular weight is decreased, and when it is larger than the above range, the mechanical strength is lowered, which is not practically preferable.
なお、上記の「吸収ピークの高さ」とは、赤外吸収スペクトルにおける１つの吸収ピークをとり、そのピークの両裾部を結ぶ線分およびピークの最高点からの垂線の交点と、ピーク最高点とを結ぶ線分の長さを意味する。
さらに本発明において重要なことは、熱融着において、相手基材の材料、例えば汎用樹脂が熱分解しない温度で融着できることであり、テトラフルオロエチレン共重合体が、そのような温度で、十分に流動できる粘度であることが必要である。例えば、ポリアミド１２、ポリアミド６、ポリブチレンテレフタレート、ポリメタクリレート等の汎用樹脂の好ましい熱融着温度範囲は約１５０℃〜２６０℃である。従って、本発明のテトラフルオロエチレン共重合体もこの温度範囲で溶融でき、流動できる溶融粘度を有している必要がある。
The above-mentioned “height of the absorption peak” means that one absorption peak in the infrared absorption spectrum is taken, the intersection of the line connecting both hems of the peak and the perpendicular from the highest point of the peak, and the highest peak. This means the length of the line connecting the points.
Further, in the present invention, it is important that the material of the mating base material, for example, a general-purpose resin, can be fused at a temperature that does not thermally decompose, and the tetrafluoroethylene copolymer is sufficient at such a temperature. It is necessary for the viscosity to be able to flow into the surface. For example, the preferred heat-sealing temperature range of general-purpose resins such as polyamide 12, polyamide 6, polybutylene terephthalate, and polymethacrylate is about 150 ° C to 260 ° C. Therefore, the tetrafluoroethylene copolymer of the present invention must also have a melt viscosity that can be melted and flowed in this temperature range.
そこで、本発明のテトラフルオロエチレン共重合体は、２００℃、５kg荷重において、１.０〜１００ｇ／１０分、好ましくは１.０〜５０ｇ／１０分のメルトフローレート（ＭＦＲ）を有し、９０〜２００℃の融点を有している。 Therefore, tetrafluoroethylene copolymer of the present invention, chromatic 200 ° C., at 5kg load, 1 .0~100g / 10 min, a good Mashiku is 1.0~50g / 10 min melt flow rate (MFR) And has a melting point of 90-200 ° C.
さらに本発明のテトラフルオロエチレン共重合体は、２３０℃で１０〜１０３sec−１の範囲の臨界剪断速度を有しており、従来のフッ素樹脂よりも低温で成形できる。この臨界剪断速度の故に、本発明のテトラフルオロエチレン共重合体は、単独でフィルム、チューブ、パイプ等の成形品に成形できることはもちろんのこと、汎用樹脂との共押出成形もできる。 Furthermore, the tetrafluoroethylene copolymer of the present invention has a critical shear rate in the range of 10 to 10 3 sec −1 at 230 ° C., and can be molded at a lower temperature than conventional fluororesins. Because of this critical shear rate, the tetrafluoroethylene copolymer of the present invention can be molded into a molded product such as a film, a tube, or a pipe, and can be co-extruded with a general-purpose resin.
好ましい１つの形態では、本発明のテトラフルオロエチレン共重合体は、ＴＦＥ４０〜８１モル％、Ｅt６〜４３モル％、ＨＦＰ１０〜３０モル％のモノマー組成を有している。
ＴＦＥの割合があまり多くなると重合速度が低下するので、より好ましいモノマー組成は、ＴＦＥ４０〜６０モル％、Ｅt２４〜４３モル％、ＨＦＰ１０〜３０モル％である。
本発明のテトラフルオロエチレン共重合体は、ＨＦＰの含有量の増加と共に連続的にその融点が降下し、また結晶性も低下するので透明性は向上する。
In one preferred form, the tetrafluoroethylene copolymer of the present invention has a monomer composition of TFE 40-81 mol%, Et 6-43 mol%, and HFP 10-30 mol%.
Since the polymerization rate decreases when the proportion of TFE is too large, more preferable monomer compositions are
Since the tetrafluoroethylene copolymer of the present invention continuously decreases in melting point and crystallinity as the HFP content increases, the transparency is improved.
別の好ましい形態では、本発明のテトラフルオロエチレン共重合体は、ＴＦＥ、ＨＦＰおよびＥｔに加えて、変性モノマーとして、式:
ＣＨ２＝ＣＦＲf （Ｉ）
（式中、Ｒfは炭素数２〜１０のフルオロアルキル基である。）で示されるフルオロビニル化合物を含んでいてよい。
In another preferred form, the tetrafluoroethylene copolymer of the present invention has the formula: in addition to TFE, HFP and Et, as a modifying monomer:
CH 2 = CFRf (I)
(Wherein Rf is a fluoroalkyl group having 2 to 10 carbon atoms).
Ｒfの炭素数が２より少ないとテトラフルオロエチレン共重合体の改質（たとえば、共重合体の成形時や成形品のクラック発生の抑制）が十分になされず、一方１０より多くなると重合反応性の点で不利になるので、好ましい炭素数範囲は２〜１０である。 If the number of carbon atoms in Rf is less than 2, the modification of the tetrafluoroethylene copolymer (for example, suppression of cracking of the molded product or molded product) is not sufficient, while if it exceeds 10, the polymerization reactivity is increased. Therefore, the preferred carbon number range is 2-10.
得られる共重合体の耐熱性の点からは、Ｒf基はパーフルオロアルキル基、ω−ハイドロまたはω−クロロパーフルオロアルキル基であるのが最も好ましい。 From the viewpoint of heat resistance of the resulting copolymer, the Rf group is most preferably a perfluoroalkyl group, an ω-hydro or an ω-chloroperfluoroalkyl group.
このようなフルオロビニル化合物のうち、共重合性、モノマーの製造時の経済性、得られた共重合体の物性から、式:
ＣＨ２＝ＣＦ(ＣＦ２)ｎＨ （II）
（式中、ｎは２〜１０の数である。）
で表されるフルオロビニル化合物が好ましく、とりわけｎが３〜５の数であるフルオロビニル化合物（II）が好ましい。
Among such fluorovinyl compounds, from the viewpoint of copolymerization, economics at the time of production of the monomer, and physical properties of the obtained copolymer, the formula:
CH 2 = CF (CF 2 ) n H (II)
(In the formula, n is a number of 2 to 10.)
Is preferable, and in particular, the fluorovinyl compound (II) in which n is a number of 3 to 5 is preferable.
変性モノマーとしてフルオロビニル化合物（Ｉ）を用いる場合のモノマー組成は、テトラフルオロエチレンとエチレンのモル比が４０:６０〜９０:１０であり、フルオロビニル化合物の含有量が（共重合体全体に対して）０〜１０モル％であり、ヘキサフルオロプロピレンの含有量が（共重合体全体に対して）１０〜３０モル％である When the fluorovinyl compound (I) is used as the modifying monomer, the molar ratio of tetrafluoroethylene to ethylene is 40:60 to 90:10, and the content of the fluorovinyl compound is (with respect to the entire copolymer). 0) -10 mol%, and the content of hexafluoropropylene is 10-30 mol% (relative to the entire copolymer).
本発明のテトラフルオロエチレン共重合体は、ＥＴＦＥの重合に採用されている重合方法によって製造することができる。
ポリマー鎖末端にカーボネート基を導入する為に、本発明のテトラフルオロエチレン共重合体の製造には、パーオキシカーボネートを重合開始剤として用いる。パーオキシカーボネートとしては、下記式（１）〜（４）：
（式中、ＲおよびＲ'は、炭素数１〜１５の直鎖状または分岐状の一価飽和炭化水素基、もしくは末端にアルコキシ基を含有する炭素数１〜１５の直鎖状または分岐状の一価飽和炭化水素基、Ｒ"は、炭素数１〜１５の直鎖状または分岐状の二価飽和炭化水素基、もしくは末端にアルコキシ基を含有する炭素数１〜１５の直鎖状または分岐状の二価飽和炭化水素基を表す。）
で示される化合物が好ましく用いられる。
The tetrafluoroethylene copolymer of the present invention can be produced by a polymerization method employed for ETFE polymerization.
In order to introduce a carbonate group at the end of the polymer chain, peroxycarbonate is used as a polymerization initiator in the production of the tetrafluoroethylene copolymer of the present invention. As peroxycarbonate, the following formulas (1) to (4):
(In the formula, R and R ′ are linear or branched monovalent saturated hydrocarbon groups having 1 to 15 carbon atoms, or linear or branched structures having 1 to 15 carbon atoms containing an alkoxy group at the terminal. Monovalent saturated hydrocarbon group, R ″ is a linear or branched divalent saturated hydrocarbon group having 1 to 15 carbon atoms, or a straight chain having 1 to 15 carbon atoms containing an alkoxy group at the end, or Represents a branched divalent saturated hydrocarbon group.)
Is preferably used.
とりわけ、ジイソプロピルパーオキジカーボネート、ジ−ｎ−プロピルパーオキシジカーボネート、t−ブチルパーオキシイソプロピルカーボネート、ビス(４−t−ブチルシクロヘキシル)パーオキシジカーボネート、ジ−２−エチルヘキシルパーオキシジカーボネートなどが好ましい。 In particular, diisopropyl peroxycarbonate, di-n-propyl peroxydicarbonate, t-butyl peroxyisopropyl carbonate, bis (4-t-butylcyclohexyl) peroxydicarbonate, di-2-ethylhexyl peroxydicarbonate, etc. Is preferred.
重合方法としては、工業的にはフッ素系溶媒を用い、重合開始剤としてパーオキシカーボネートを使用した水性媒体中での懸濁重合が好ましいが、他の重合方法、例えば溶液重合、塊状重合、なども採用できる。 As the polymerization method, suspension polymerization in an aqueous medium using a fluorinated solvent industrially and using peroxycarbonate as a polymerization initiator is preferable, but other polymerization methods such as solution polymerization, bulk polymerization, etc. Can also be adopted.
フッ素系溶媒としては、ハイドロクロロフルオロアルカン類（例えば、ＣＨ３ＣＣｌＦ２，ＣＨ３ＣＣｌ２ＦＣＦ３ＣＦ２ＣＣｌ２Ｈ，ＣＦ２ＣｌＣＦ２ＣＦＨＣｌ）、クロロフルオロアルカン類（例えば、ＣＦ２ＣｌＣＦＣｌＣＦ２ＣＦ３，ＣＦ３ＣＦＣｌＣＦＣｌＣＦ３）、パーフルオロアルカン類（例えば、パーフルオロシクロブタン，ＣＦ３ＣＦ２ＣＦ２ＣＦ３，ＣＦ３ＣＦ２ＣＦ２ＣＦ２ＣＦ３，ＣＦ３ＣＦ２ＣＦ２ＣＦ２ＣＦ２ＣＦ３）が使用でき、中でもパーフルオロアルカン類が好ましい。
溶媒の使用量は、懸濁性、経済性の面から、水に対し１０〜１００重量％とするのが好ましい。
Examples of the fluorine-based solvent include hydrochlorofluoroalkanes (for example, CH 3 CClF 2 , CH 3 CCl 2 FCF 3 CF 2 CCl 2 H, CF 2 ClCF 2 CFHCl), chlorofluoroalkanes (for example, CF 2 ClCFClCF 2 CF 3 , CF 3 CFClCFClCF 3 ), perfluoroalkanes (eg perfluorocyclobutane, CF 3 CF 2 CF 2 CF 3 , CF 3 CF 2 CF 2 CF 2 CF 3 , CF 3 CF 2 CF 2 CF 2 CF 2 CF 3 ) can be used, and perfluoroalkanes are particularly preferable.
The amount of the solvent used is preferably 10 to 100% by weight with respect to water from the viewpoint of suspendability and economy.
重合温度は特に限定されないが、０〜１００℃でよい。共重合体中のエチレン−エチレン連鎖生成による耐熱性の低下を避けるためには、一般に低温が好ましい。
重合圧力は、用いる溶媒の種類、量および蒸気圧、重合温度などの他の重合条件に応じて適宜定められるが、通常０〜５０kgf／cm２Ｇであってよい。
The polymerization temperature is not particularly limited, but may be 0 to 100 ° C. In order to avoid a decrease in heat resistance due to ethylene-ethylene chain formation in the copolymer, a low temperature is generally preferred.
The polymerization pressure is appropriately determined according to other polymerization conditions such as the type, amount and vapor pressure of the solvent to be used, and the polymerization temperature, but may be usually 0 to 50 kgf / cm 2 G.
本発明のテトラフルオロエチレン共重合体の製造に際しては、分子量調整のために、通常の連鎖移動剤、例えばイソペンタン、n−ペンタン、n−ヘキサン、シクロヘキサンなどの炭化水素；メタノール、エタノールなどのアルコール；四塩化炭素、クロロホルム、塩化メチレン、塩化メチルなどのハロゲン化炭化水素を用いることができる。 In the production of the tetrafluoroethylene copolymer of the present invention, in order to adjust the molecular weight, conventional chain transfer agents, for example, hydrocarbons such as isopentane, n-pentane, n-hexane and cyclohexane; alcohols such as methanol and ethanol; Halogenated hydrocarbons such as carbon tetrachloride, chloroform, methylene chloride, and methyl chloride can be used.
本発明のテトラフルオロエチレン共重合体を積層できる相手材料としては、
（本発明のテトラフルオロエチレン共重合体以外の）フッ素樹脂；
熱可塑性樹脂、例えばポリアミド（ナイロン６、ナイロン６６、ナイロン１１、ナイロン１２、ナイロン６１０、ナイロン４６、ナイロン６１２など）、ポリエステル（ポリブチレンテレフタレート、ポリエチレンテレフタレートなど)、ポリカーボネート、ポリアセタール、ポリ(メタ)アクリレート、スチレン系樹脂、ＡＢＳ樹脂、ポリ塩化ビニル、エチレンビニルアルコール樹脂、セルロース系プラスチック、変性ポリフェニレンエーテル；
熱硬化性樹脂、例えばエポキシ樹脂（グリシジルエーテル型、グリシジルエステル型、グリシジルアミン型など)、不飽和ポリエステル樹脂、フェノール樹脂（ノボラック樹脂）、ポリウレタン樹脂、シリコーン樹脂；
珪素質材料、例えばガラス系材料（硬質ガラス、軟質ガラス、ガラス繊維など）、結晶シリコン、多結晶シリコン、アモルファスシリコン、粘土類、セメント；
金属材料、例えばアルミニウム系金属材料、鉄系金属材料、銅系金属材料、ニッケル、チタン：
合成ゴム；天然繊維；木材；紙類；皮革類
などが挙げられる。
As a partner material capable of laminating the tetrafluoroethylene copolymer of the present invention,
Fluororesin (other than the tetrafluoroethylene copolymer of the present invention);
Thermoplastic resins such as polyamide (nylon 6, nylon 66, nylon 11, nylon 12, nylon 610, nylon 46, nylon 612, etc.), polyester (polybutylene terephthalate, polyethylene terephthalate, etc.), polycarbonate, polyacetal, poly (meth) acrylate Styrene resin, ABS resin, polyvinyl chloride, ethylene vinyl alcohol resin, cellulose plastic, modified polyphenylene ether;
Thermosetting resins such as epoxy resins (glycidyl ether type, glycidyl ester type, glycidyl amine type, etc.), unsaturated polyester resins, phenol resins (novolak resins), polyurethane resins, silicone resins;
Siliceous materials such as glass-based materials (hard glass, soft glass, glass fiber, etc.), crystalline silicon, polycrystalline silicon, amorphous silicon, clays, cement;
Metal materials such as aluminum-based metal materials, iron-based metal materials, copper-based metal materials, nickel, titanium:
Synthetic rubber; natural fiber; wood; papers; leathers and the like.
本発明のテトラフルオロエチレン共重合体が積層できる相手材料の中でも、最も強固に接着しうる材料は、分子鎖中にアミド基または／およびエポキシ基を含有するポリマー材料であり、これを中間層とし、少なくとも１つの本発明のテトラフルオロエチレン共重合体の層を有する３層またはそれ以上の積層体を形成することができる。 Among the counterpart materials on which the tetrafluoroethylene copolymer of the present invention can be laminated, the most adhesive material is a polymer material containing an amide group or / and an epoxy group in the molecular chain, and this is used as an intermediate layer. Three or more laminates having at least one layer of the tetrafluoroethylene copolymer of the present invention can be formed.
本発明のテトラフルオロエチレン共重合体をポリアミド樹脂から成形された物品の表面に積層することにより、ポリアミド樹脂に、耐溶剤性、特にアルコール（例えば、メタノール、エタノールなど）またはメチル−t−ブチルエーテルなどを含む改質ガソリン、酸などに対する耐薬品性や不透過性を付与することができる。 By laminating the tetrafluoroethylene copolymer of the present invention on the surface of an article molded from a polyamide resin, the polyamide resin has a solvent resistance, particularly an alcohol (for example, methanol, ethanol, etc.) or methyl-t-butyl ether. Chemical resistance and impermeability to reformed gasoline, acids and the like can be imparted.
中間層として使用できる分子鎖中にアミド基を有するポリマーの具体例として、（１）ポリアミド系樹脂、（２）ポリアミド系エラストマー、（３）ポリアミド系樹脂アロイなどが例示できる。 Specific examples of the polymer having an amide group in the molecular chain that can be used as the intermediate layer include (1) polyamide-based resin, (2) polyamide-based elastomer, and (3) polyamide-based resin alloy.
具体例は以下の通りである。
（１）環状脂肪族ラクタムの開環重合；脂肪族ジアミンと脂肪族ジカルボン酸または芳香族ジカルボン酸との縮合；アミノ酸の縮重合；不飽和脂肪酸の二量化により得られる炭素数３６のジカルボン酸を主成分とするいわゆるダイマー酸と短鎖二塩基酸との共重合等で合成されるポリアミド系樹脂。
例えば、ナイロン６、ナイロン６，６、ナイロン１０、ナイロン６，１２、ナイロン４，６、ナイロン３，４、ナイロン６，９、ナイロン１２、ナイロン１１、ナイロン４、またナイロン６／６，１０、ナイロン６／６，１２、ナイロン６／４，６、ナイロン６／１２、ナイロン６／６，６、ナイロン６／６，６／６，１０、ナイロン６／４，６／６，６、ナイロン６／６，６／６，１２、ナイロン６／４，６／６，１０、ナイロン６／４，６／１２などの共重合ポリアミド類。
ポリアミド樹脂の平均分子量は、通常５,０００〜５００,０００である。これらのポリアミド樹脂の中でも積層チューブに好ましく使用されるのは、ポリアミド１１、１２、６，１０である。
Specific examples are as follows.
(1) Ring-opening polymerization of cycloaliphatic lactam; condensation of aliphatic diamine and aliphatic dicarboxylic acid or aromatic dicarboxylic acid; condensation polymerization of amino acid; 36 carbon dicarboxylic acid obtained by dimerization of unsaturated fatty acid A polyamide-based resin synthesized by copolymerization of a so-called dimer acid having a main component and a short-chain dibasic acid.
For example, nylon 6, nylon 6,6, nylon 10, nylon 6,12, nylon 4,6, nylon 3,4, nylon 6,9, nylon 12, nylon 11, nylon 4, and nylon 6 / 6,10, Nylon 6/6, Nylon 6/4, 6, Nylon 6/12, Nylon 6/6, 6, Nylon 6/6, 6/6, 10, Nylon 6/4, 6/6, 6, Nylon 6 / 6,6 / 6,12, nylon 6 / 4,6 / 6,10, nylon 6 / 4,6 / 12, and other copolymerized polyamides.
The average molecular weight of the polyamide resin is usually 5,000 to 500,000. Among these polyamide resins, polyamides 11, 12, 6, and 10 are preferably used for the laminated tube.
（２）ポリアミド成分を結晶性のハードセグメントとし、ポリエーテルをソフトセグメントとするＡＢ型ブロックタイプのポリエーテルエステルアミドおよびポリエーテルアミドエラストマーであるポリアミドエラストマー。これは、例えば、ラウリルラクタムとジカルボン酸およびテトラメチレングリコールとの縮合反応から得られる。
ハードセグメント部のポリアミドの炭素数およびソフトセグメント部の炭素数の種類並びにそれらの割合、あるいはそれぞれのブロックの分子量は、柔軟性と弾性回復性面から自由に設計できる。
(2) Polyamide elastomer which is an AB block type polyether ester amide and polyether amide elastomer having a polyamide component as a crystalline hard segment and a polyether as a soft segment. This is obtained, for example, from the condensation reaction of lauryl lactam with dicarboxylic acid and tetramethylene glycol.
The number of carbon atoms of the polyamide in the hard segment part and the kind and ratio of the carbon number in the soft segment part, or the molecular weight of each block can be freely designed from the viewpoint of flexibility and elastic recovery.
（３）ポリアミド系アロイ
（３．１）ポリアミド／ポリオレフィン系アロイ
例えば、デュポン社製ザイテルＳＴ、旭化成株式会社製レオナ４３００、三菱化学株式会社製ノパミッドＳＴ２２０、株式会社ユニチカ製ナイロンＥＸ１０２０等。
（３．２）ポリアミド／ポリプロピレン系アロイ
例えば、昭和電工製システマーＳ。
（３．３）ポリアミド／ＡＢＳ系アロイ
例えば、東レ株式会社製トヨラックＳＸ。
（３．４）ポリアミド／ポリフェニレンエーテル系アロイ
例えば、日本ＧＥプラスチックス製ノリルＧＴＸ６００、三菱化学株式会社製レマロイＢ４０等。
（３．５）ポリアミド／ポリアリレート系アロイ
例えば、株式会社ユニチカ製Ｘ９。
分子鎖中にエポキシ基を有するポリマーの具体例は、エポキシ基を含有したポリエチレン樹脂(例えば、日本ポリオレフィン株式会社製レクスパールＲＡ３１５０)、エポキシ樹脂等である。
(3) Polyamide alloy (3.1) Polyamide / polyolefin alloy For example, DuPont Zytel ST, Asahi Kasei Corporation Leona 4300, Mitsubishi Chemical Corporation Nopamid ST220, Unitika Nylon EX1020, etc.
(3.2) Polyamide / polypropylene alloy For example, Systemer S manufactured by Showa Denko.
(3.3) Polyamide / ABS alloy For example, Toyolac SX manufactured by Toray Industries, Inc.
(3.4) Polyamide / polyphenylene ether alloy For example, Noryl GTX600 manufactured by Japan GE Plastics, Remalloy B40 manufactured by Mitsubishi Chemical Corporation, and the like.
(3.5) Polyamide / polyarylate alloy For example, X9 manufactured by Unitika Ltd.
Specific examples of the polymer having an epoxy group in the molecular chain include a polyethylene resin containing an epoxy group (for example, Lexpearl RA3150 manufactured by Nippon Polyolefin Co., Ltd.), an epoxy resin, and the like.
中間層をはさんで本発明のポリテトラフルオロエチレン共重合体の層と反対側の層を形成する材料の具体例は以下の通りである。
ポリエステル、ポリアミド、ポリフェニレンスルフィド、アクリル系樹脂、酢酸ビニル系樹脂、ポリオレフィン系樹脂、塩化ビニル系樹脂、ポリカーボネート、スチレン系樹脂、ＡＢＳ樹脂、ポリアミドイミド、ポリエーテルエーテルケトン（ＰＥＥＫ）、ポリエーテルスルホン（ＰＥＳ）、ポリスルホン、ポリフェニレンオキサイド（ＰＰＯ）、ポリアラミド、ポリアセタール、ポリエーテルイミド、シリコーン樹脂、ポリウレタン、ポリイミド、エポキシ樹脂、フェノール樹脂、アミノ樹脂、不飽和ポリエステル、セロハンなどの樹脂；
ニトリルブタジエンゴム、イソプレンゴム、スチレンブタジエンゴム、ブタジエンゴム、クロロプレンアクリロゴム、エチレンプロピレンゴム、ウレタンゴム、シリコーンゴム、フッ素ゴム、クロロスルホン化ポリエチレンゴム、アクリルゴム、エピクロロヒドリンゴム、多硫化ゴム、塩素化ポリエチレンゴム等の合成ゴムおよび天然ゴム。
スチレン系、塩化ビニル系、オレフィン系、ポリエステル系、ポリアミド系、およびウレタン系熱可塑性エラストマー。
The specific example of the material which forms the layer on the opposite side to the layer of the polytetrafluoroethylene copolymer of this invention across an intermediate | middle layer is as follows.
Polyester, polyamide, polyphenylene sulfide, acrylic resin, vinyl acetate resin, polyolefin resin, vinyl chloride resin, polycarbonate, styrene resin, ABS resin, polyamideimide, polyetheretherketone (PEEK), polyethersulfone (PES) ), Polysulfone, polyphenylene oxide (PPO), polyaramide, polyacetal, polyetherimide, silicone resin, polyurethane, polyimide, epoxy resin, phenol resin, amino resin, unsaturated polyester, cellophane, and the like;
Nitrile butadiene rubber, isoprene rubber, styrene butadiene rubber, butadiene rubber, chloroprene acrylo rubber, ethylene propylene rubber, urethane rubber, silicone rubber, fluorine rubber, chlorosulfonated polyethylene rubber, acrylic rubber, epichlorohydrin rubber, polysulfide rubber, Synthetic rubber and natural rubber such as chlorinated polyethylene rubber.
Styrene, vinyl chloride, olefin, polyester, polyamide, and urethane thermoplastic elastomers.
アルミニウム、鉄、ニッケル、チタン、モリブデン、マグネシウム、マンガン、銅、銀、鉛、錫、クロム、ベリリウム、タングステン、コバルト等の金属や金属化合物、およびこれら金属の２種以上からなる合金類。
合金類の具体例としては、炭素鋼、Ｎi鋼、Ｃr鋼、Ｎi−Ｃr鋼、Ｃr−Ｍo鋼、ステンレス鋼、ケイ素鋼、パーマロイなどの合金鋼；Ａl−Ｃl、Ａl−Ｍg、Ａl−Ｓi、Ａl−Ｃu−Ｎi−Ｍg、Ａl−Ｓi−Ｃu−Ｎi−Ｍgなどのアルミニウム合金；黄銅、青銅(ブロンズ)、珪素青銅、珪素黄銅、洋白、ニッケル青銅などの銅合金；ニッケルマンガン(Ｄニッケル)、ニッケル−アルミニウム(Ｚニッケル)、ニッケル−珪素、モネルメタル、コンスタンタン、ニクロムインコネル、ハステロイなどのニッケル合金等が挙げられる。
Metals and metal compounds such as aluminum, iron, nickel, titanium, molybdenum, magnesium, manganese, copper, silver, lead, tin, chromium, beryllium, tungsten, cobalt, and alloys composed of two or more of these metals.
Specific examples of alloys include carbon steel, Ni steel, Cr steel, Ni-Cr steel, Cr-Mo steel, stainless steel, silicon steel, permalloy alloy steels; Al-Cl, Al-Mg, Al-Si. Aluminum alloys such as Al-Cu-Ni-Mg and Al-Si-Cu-Ni-Mg; Copper alloys such as brass, bronze, silicon bronze, silicon brass, silicon white, nickel bronze; nickel manganese (D Nickel), nickel-aluminum (Z nickel), nickel-silicon, monel metal, constantan, nichrome inconel, nickel alloy such as hastelloy, and the like.
また、金属の腐食防止などを目的として、金属表面に電気メッキ、溶融メッキ、クロマイジンク、シリコナイジンク、カロライジンク、シェラダイジング、溶射などによって他の金属を被膜したり、リン酸塩処理によりリン酸塩被膜を形成させたり、陽極酸化や加熱酸化により金属酸化物を形成させたり、電気化学的防食を施してもよい。 In addition, for the purpose of preventing metal corrosion, other metals can be coated on the metal surface by electroplating, hot dipping, chromic zinc, siliconizing zinc, carolinizing zinc, sheridizing, thermal spraying, etc. An acid salt film may be formed, a metal oxide may be formed by anodic oxidation or heat oxidation, or electrochemical corrosion protection may be performed.
接着性をさらに向上させることを目的として、金属表面にリン酸塩、硫酸、クロム酸、シュウ酸などによる化成処理を施したり、サンドブラスト、ショットブラスト、グリットブラスト、ホーニング、ペーパースクラッチ、ワイヤースクラッチ、ヘアーライン処理などの表面粗面化処理を施してもよい。 In order to further improve the adhesion, the metal surface is subjected to chemical conversion treatment with phosphate, sulfuric acid, chromic acid, oxalic acid, etc., sand blasting, shot blasting, grit blasting, honing, paper scratch, wire scratch, hairline Surface roughening treatment such as treatment may be performed.
アルミニウム系金属材料としては、純アルミニウム、アルミニウムの酸化物、Ａl−Ｃu系、Ａl−Ｓi系、Ａl−Ｍg系およびＡl−Ｃu−Ｎi−Ｍg系、Ａl−Ｓi−Ｃu−Ｎi−Ｍg系合金、高力アルミニウム合金、耐食アルミニウム合金などの鋳造用または展伸用のアルミニウム合金を用いることができる。また、さらに上記アルミニウムまたはアルミニウム合金表面に、防食、表面硬化、接着性の向上などを目的に、苛性ソーダ、シュウ酸、硫酸、クロム酸を用いた陽極酸化を行って酸化被膜を形成したもの(アルマイト)や、そのほか前述の表面処理を施したものを用いることもできる。 Aluminum metal materials include pure aluminum, aluminum oxide, Al-Cu, Al-Si, Al-Mg, Al-Cu-Ni-Mg, and Al-Si-Cu-Ni-Mg alloys. Further, an aluminum alloy for casting or spreading such as a high-strength aluminum alloy or a corrosion-resistant aluminum alloy can be used. Furthermore, an anodized film is formed on the surface of the aluminum or aluminum alloy by anodizing with caustic soda, oxalic acid, sulfuric acid, or chromic acid for the purpose of anticorrosion, surface hardening, adhesion improvement, etc. ), And those subjected to the above-described surface treatment can also be used.
鉄系金属材料としては、純鉄、酸化鉄、炭素鋼、Ｎｉ鋼、Ｃｒ鋼、Ｎｉ−Ｃｒ鋼、Ｃｒ−Ｍｏ鋼、Ｎｉ−Ｃｒ−Ｍｏ鋼、ステンレス鋼、ケイ素鋼、パーマロイ、不感磁性鋼、磁石鋼、鋳鉄類などを用いることができる。
さらに上記鉄系金属材料の表面に他の金属をメッキしたもの、例えば溶融亜鉛メッキ鋼板、合金化溶融亜鉛メッキ鋼板、アルミニウムメッキ鋼板、亜鉛ニッケルメッキ鋼板、亜鉛アルミニウム鋼板など；浸透法、溶射法により他の金属を被膜したもの；クロム酸系やリン酸系の化成処理または加熱処理により酸化被膜を形成させたもの；電気的防食法を施したもの(例えば、ガルバニック鋼板)などを用いることができる。
Ferrous metal materials include pure iron, iron oxide, carbon steel, Ni steel, Cr steel, Ni-Cr steel, Cr-Mo steel, Ni-Cr-Mo steel, stainless steel, silicon steel, permalloy, and dead magnetic steel Magnetic steel, cast iron, etc. can be used.
Further, the surface of the iron-based metal material plated with other metals, such as hot dip galvanized steel sheet, alloyed hot dip galvanized steel sheet, aluminum plated steel sheet, zinc nickel plated steel sheet, zinc aluminum steel sheet, etc .; Coated with other metals; Chromic acid-based or phosphoric acid-based chemical treatment or heat-treated oxide film; Electrocorrosion-protected (eg, galvanic steel plate), etc. can be used. .
結晶化ガラス、発泡ガラス、熱線反射ガラス、熱線吸収ガラス、複層ガラスなどのガラス系材料、タイル、大型陶板、セラミックパネル、レンガなどの窯業系基材、御影石、大理石などの天然石、高強度コンクリート、ガラス繊維強化コンクリート(ＧＲＣ)、炭素繊維強化コンクリート(ＣＦＲＣ)、軽量気泡発泡コンクリート(ＡＬＣ)、複合ＡＬＣなどのコンクリート系基材、押出成形セメント、複合成形セメントなどのセメント系基材、その他石綿スレート、ホーロー鋼板、単結晶シリコン、多結晶シリコン、アモルファスシリコン、粘土類、ホウ素系、炭素系材料など。
天然繊維、木材、紙類、皮革類などの天然の有機物。
Glass-based materials such as crystallized glass, foamed glass, heat-reflective glass, heat-absorbing glass and double-glazed glass, ceramics base materials such as tiles, large ceramic plates, ceramic panels and bricks, natural stones such as granite and marble, high-strength concrete , Concrete base materials such as glass fiber reinforced concrete (GRC), carbon fiber reinforced concrete (CFRC), lightweight cellular foam concrete (ALC), composite ALC, cement base materials such as extruded cement, composite molded cement, and other asbestos Slate, enamel steel, single crystal silicon, polycrystalline silicon, amorphous silicon, clays, boron-based and carbon-based materials.
Natural organic materials such as natural fibers, wood, papers and leathers.
反対側の層は、１種またはそれ以上の層から形成することができ、また、意匠性を目的として、反対側層の外側または内側に着色、印刷、エッチングなどを施してもよい。 The opposite layer can be formed of one or more layers, and for the purpose of design, the outer layer or the inner side of the opposite layer may be colored, printed, etched, or the like.
また、本発明のテトラフルオロエチレン共重合体の層、中間層および反対側層それぞれが持つ特性を損なわない範囲で、それぞれの層に適当な補強剤、充填剤、安定剤、紫外線吸収剤、顔料、その他の適当な添加剤を含有させることも可能である。
このような添加剤によって、熱安定性、表面硬度、耐摩耗性、帯電性、耐候性、その他の性質を向上することができる。
Further, as long as the characteristics of the tetrafluoroethylene copolymer layer, the intermediate layer and the opposite layer of the present invention are not impaired, appropriate reinforcing agents, fillers, stabilizers, ultraviolet absorbers and pigments for the respective layers. It is also possible to contain other suitable additives.
Such additives can improve thermal stability, surface hardness, abrasion resistance, charging properties, weather resistance, and other properties.
このような積層体の製法は、本発明のテトラフルオロエチレン共重合体の形態、中間層に用いる材料の形態、および有機材料の種類や形態、無機材料の種類や形状に応じて、適宜選択される。 The production method of such a laminate is appropriately selected according to the form of the tetrafluoroethylene copolymer of the present invention, the form of the material used for the intermediate layer, the kind and form of the organic material, and the kind and form of the inorganic material. The
例えば、反対側層が熱可塑性樹脂の場合、多層共押出しで各層を同時に一体化し、フィルム形状、チューブ形状、ホース形状、ボトル形状、タンク形状の成形品を製造することができる。
また、そのようにして得られた多層フィルムの反対側層面に、グラビア印刷、フレキソ印刷、シルクスクリーン印刷、オフセット印刷により、意匠を付与してもよい。さらに、印刷されたフィルムを金属板、合板、石膏ボード、石綿スレート板等に貼り合わせ、建材の化粧パネルやシステムキッチン材として使用できる。
For example, when the opposite side layer is a thermoplastic resin, the layers can be simultaneously integrated by multilayer coextrusion to produce a molded product having a film shape, a tube shape, a hose shape, a bottle shape, or a tank shape.
Moreover, you may give a design to the other layer surface of the multilayer film obtained in this way by gravure printing, flexographic printing, silk screen printing, and offset printing. Furthermore, the printed film can be bonded to a metal plate, plywood, gypsum board, asbestos slate plate or the like and used as a decorative panel for building materials or a system kitchen material.
反対側層が金属、合板、ゴム、ガラス、シリコーンなどを含む場合は、あらかじめ、中間層と本発明のテトラフルオロエチレン共重合体を共押出しによりフィルム状、チューブ状、シート状、ホース状、ボトル状に成形し、熱活性化によって反対側層と積層すればよい。 When the opposite side layer contains metal, plywood, rubber, glass, silicone, etc., the intermediate layer and the tetrafluoroethylene copolymer of the present invention are co-extruded in advance to form a film, tube, sheet, hose, bottle And then laminated with the opposite layer by thermal activation.
このようにして得られた多層フィルムまたは多層シートは、ＳＰモールド成形、インモールド成形等においてインサートフィルム表皮材として利用でき、成形品の最外層として、耐候性、耐汚染性、耐湿性、耐薬品性に優れた本発明のテトラフルオロエチレン共重合体の層を提供することができる。 The multilayer film or multilayer sheet thus obtained can be used as an insert film skin material in SP molding, in-mold molding, etc., and as the outermost layer of the molded product, weather resistance, contamination resistance, moisture resistance, chemical resistance A layer of the tetrafluoroethylene copolymer of the present invention having excellent properties can be provided.
このようにして得られる成形品の例として、自動車のバンパー、ドアトリム、計器板、装飾モール等、家庭電化製品、ＯＡ機器等の表示板、電照式看板、ディスプレイ、また、携帯電話等が挙げられる。 Examples of molded articles obtained in this way include automobile bumpers, door trims, instrument panels, decorative malls, home appliances, display boards for OA equipment, electric signboards, displays, mobile phones, and the like. It is done.
近年、自動車燃料配管におけるフィラーホースが、低級アルコールを含むガソリンに対するバリアー性改善の目的で、ゴム単体(ＮＢＲ等)ホースから、ゴムとポリアミド樹脂の積層ホースやゴムとフッ素ゴムの積層ホース、ポリアミド単体ホース等へ移行している。
しかしながら、ポリアミド樹脂およびフッ素ゴムは共に、燃料透過に対するバリアー性の点で不十分である。
In recent years, filler hoses in automobile fuel pipes have been developed to improve barrier properties against gasoline containing lower alcohols, from rubber single-piece (NBR, etc.) hoses, rubber-polyamide resin-layered hose, rubber-fluorine rubber-layered hose, and polyamide single-piece. It has shifted to hoses.
However, both polyamide resin and fluororubber are insufficient in terms of barrier properties against fuel permeation.
反対側層をゴム層、例えばＮＢＲ単体、又はＮＢＲと塩化ビニルのコンパウンドとし、該層を最外層とした３層ホース、さらに、最内層に導電ＮＢＲ層を用いた４層ホースは、フィラーホースとしての燃料透過バリアー性と、燃料等に添加されているアミンに対する耐食性に優れている。また、最外層のゴム層は、アラミド繊維等で補強してもよい。 The opposite layer is a rubber layer, for example, NBR alone or a compound of NBR and vinyl chloride, and a three-layer hose with the outermost layer as the outer layer, and a four-layer hose with a conductive NBR layer as the innermost layer is a filler hose. It has excellent fuel permeation barrier properties and corrosion resistance against amines added to fuel and the like. The outermost rubber layer may be reinforced with aramid fibers or the like.
本発明のテトラフルオロエチレン共重合体は、粉体の形状で使用することができ、この場合、あらかじめ形成された反体側層と中間層とからなる積層フィルム、チューブ、ホース、ボトル、タンク等に、テトラフルオロエチレン共重合体の粉体を静電塗装等で積層することができる。 The tetrafluoroethylene copolymer of the present invention can be used in the form of a powder. In this case, it can be used in a laminated film, tube, hose, bottle, tank, etc., which is formed of a reaction body side layer and an intermediate layer. The powder of tetrafluoroethylene copolymer can be laminated by electrostatic coating or the like.
また、本発明のテトラフルオロエチレン共重合体は、有機溶剤分散体または水性分散体として使用してもよく、この場合も粉体の場合と同じく、反対側層と中間層との積層フィルム、チューブ、ホース、ボトル、タンク等に、常套の方法でコーティングすることができる。 Further, the tetrafluoroethylene copolymer of the present invention may be used as an organic solvent dispersion or an aqueous dispersion, and in this case as well as a powder, a laminated film of an opposite side layer and an intermediate layer, a tube The hose, bottle, tank, etc. can be coated by a conventional method.
近年、農業ハウス用フィルムは、環境に与える影響を考慮して、塩化ビニル樹脂フィルムの代替としてのポリオレフィンフィルムを用いた農業ハウスの需要が増している。一方、長期耐候性に優れるフッ素樹脂(ＥＴＦＥ)のフィルムも市場を伸ばしつつある。しかしながら、フッ素樹脂フィルムは、流滴加工性や、防霧加工性に問題があり、その改善が望まれている。 In recent years, the demand for an agricultural house using an polyolefin film as an alternative to a vinyl chloride resin film is increasing in consideration of the environmental impact of the film for an agricultural house. On the other hand, fluororesin (ETFE) films with excellent long-term weather resistance are also growing. However, the fluororesin film has a problem in the droplet processability and the fogproof processability, and an improvement thereof is desired.
本発明のテトラフルオロエチレン共重合体を用いた３層フィルムの反対側層として流滴剤と防霧剤(フッソ系界面活性剤、例えばダイキン工業(株)ユニダインＤＳ−４０１)により処理したポリオレフィンを用いた場合、積層フィルムは、長期耐候性と流滴、防霧性に優れた農業ハウスフィルムとして使用することができる。 As the opposite layer of the three-layer film using the tetrafluoroethylene copolymer of the present invention, a polyolefin treated with a dropping agent and an antifogging agent (a fluorosurfactant, for example, Daikin Industries, Ltd. Unidyne DS-401) When used, the laminated film can be used as an agricultural house film excellent in long-term weather resistance, droplets, and fog resistance.
その他の用途例として、以下のような用途がある。
反対側層をポリエチレン(例えば、高密度ポリエチレン)やポリアミド等から形成すると、積層体から形成したボトルは、薬液用ボトル(特に半導体用薬液ボトル)として使用できる。
反対側層を塩化ビニル樹脂、ポリオレフィン、紙などから形成すると、積層フィルムは、建材用壁紙材として使用できる。
反対側層をポリエステル、ポリアミド、ポリオレフィンなどから形成すると、積層体は、表面に撥水機能を必要とする傘、雨具、人工芝等にも使用できる。
反対側層を塩化ビニル樹脂等から形成すると、積層チューブまたはパイプは、配管として使用できる。
Other application examples include the following applications.
When the opposite layer is formed of polyethylene (for example, high density polyethylene), polyamide, or the like, the bottle formed from the laminate can be used as a chemical solution bottle (particularly, a semiconductor chemical solution bottle).
When the opposite side layer is formed from vinyl chloride resin, polyolefin, paper or the like, the laminated film can be used as a wallpaper material for building materials.
When the opposite side layer is made of polyester, polyamide, polyolefin, etc., the laminate can be used for umbrellas, rain gear, artificial turf and the like that require a water repellent function on the surface.
When the opposite side layer is formed from a vinyl chloride resin or the like, the laminated tube or pipe can be used as a pipe.
本発明に従った積層体は、雑貨、ごみ箱、漁業・養魚タンク、食品包装材、浴槽、ユニットバス、換気扇、照明枠等に使用できる。
反対側層をＥＰＤＭ等のゴムから形成し、本発明のテトラフルオロエチレン共重合体を最内層とする積層チューブは、耐ロングライフクーラント(ＬＬＣ)性に優れたラジエターチューブとして使用できる。
The laminate according to the present invention can be used for miscellaneous goods, trash cans, fishery / fish farming tanks, food packaging materials, bathtubs, unit baths, ventilation fans, lighting frames, and the like.
The laminated tube having the opposite side layer made of rubber such as EPDM and having the tetrafluoroethylene copolymer of the present invention as the innermost layer can be used as a radiator tube having excellent long life coolant (LLC) resistance.
積層体の厚さは、３層の場合２５〜１００００μm、好ましくは４０〜４０００μmであってよい。本発明のテトラフルオロエチレン共重合体の厚さは、５〜２０００μm、好ましくは１０〜１０００μmであってよい。 The thickness of the laminate may be 25 to 10,000 μm, preferably 40 to 4000 μm in the case of three layers. The thickness of the tetrafluoroethylene copolymer of the present invention may be 5 to 2000 μm, preferably 10 to 1000 μm.
中間層の厚さは、５〜１０００μm、好ましくは、５〜５００μmであってよく、反対側層の厚さは、１０〜５０００μm、好ましくは１５〜３０００μmであってよい。 The thickness of the intermediate layer may be 5 to 1000 μm, preferably 5 to 500 μm, and the thickness of the opposite layer may be 10 to 5000 μm, preferably 15 to 3000 μm.
本発明のテトラフルオロエチレン共重合体を単独でフィルムとする場合、その厚さは用途や目的により選択され、特に限定されないが、通常１０〜３０００μm、好ましくは２０〜５００μm、より好ましくは２０〜３００μmである。 When the tetrafluoroethylene copolymer of the present invention is used alone as a film, its thickness is selected according to the use and purpose and is not particularly limited, but is usually 10 to 3000 μm, preferably 20 to 500 μm, more preferably 20 to 300 μm. It is.
薄すぎるフィルムは、特殊な製造方法が必要であったり、接着操作を行う時の取り扱いが困難で、しわや破損、外観不良が起こりやすく、また接着強度、機械的強度、耐薬品性の点でも不十分となる場合がある。厚すぎるフィルムはコストや、接合して他の材料と一体化するときの作業の点で不利である。 Films that are too thin require special manufacturing methods, are difficult to handle during bonding operations, are prone to wrinkles, breakage, and poor appearance, and are also adhesive, mechanical, and chemical resistant. It may be insufficient. Films that are too thick are disadvantageous in terms of cost and work when joined and integrated with other materials.
本発明のテトラフルオロエチレン共重合体のフィルムには、特性を損なわない範囲で適当な補助剤、充填材、安定剤、紫外線吸収剤、顔料、その他適宜添加剤を含有させることもできる。
このような添加剤の配合によって、熱安定性、表面硬度、耐摩耗性、耐候性、帯電性、その他の性質を改良することができる。
The tetrafluoroethylene copolymer film of the present invention may contain appropriate auxiliary agents, fillers, stabilizers, ultraviolet absorbers, pigments, and other appropriate additives as long as the properties are not impaired.
By blending such an additive, thermal stability, surface hardness, abrasion resistance, weather resistance, chargeability, and other properties can be improved.
本発明のテトラフルオロエチレン共重合体のフィルムは、目的とするフィルムの形状に応じて、溶融押出成形法、粉体塗装法、水性または有機溶剤分散体を塗装したのち連続した皮膜としてフィルムを得る方法などにより製造できる。特に、生産性、得られるフィルムの品質などの観点から、溶融押出成形法が好ましい。 The film of the tetrafluoroethylene copolymer of the present invention is obtained as a continuous film after applying a melt extrusion molding method, a powder coating method, an aqueous or organic solvent dispersion according to the shape of the target film. It can be manufactured by a method or the like. In particular, the melt extrusion molding method is preferable from the viewpoints of productivity and the quality of the obtained film.
本発明のテトラフルオロエチレン共重合体と他の材料との一体化は、テトラフルオロエチレン共重合体フィルムと他の材料の基材とを重ね合わせて圧縮成形する方法；一方の材料に他方を塗装する方法；多層共押出成形法、多層ブロー成形法、インサート成形法、多層トランスファー成形法、多層射出成形法などによりフィルム成形と同時に一体化する方法などが採用でき、なかでも、生産性や品質などの観点から、多層共押出成形法、多層ブロー成形法が好ましい。 The integration of the tetrafluoroethylene copolymer of the present invention with another material is a method in which a tetrafluoroethylene copolymer film and a base material of another material are superimposed and compression molded; one material is coated with the other Methods that can be integrated: film co-extrusion molding, multilayer blow molding, insert molding, multilayer transfer molding, multilayer injection molding, etc. From this point of view, a multilayer coextrusion molding method and a multilayer blow molding method are preferred.
本発明のテトラフルオロエチレン共重合体と他の材料との接着は、加熱などによる熱活性化によって行うことができ、さらには熱溶融接着が好ましい。代表的な接着方法として、熱ロール法や、熱プレス法が挙げられ、更に、高周波加熱法、マイクロ法、真空圧着法（真空プレスなど）、空気圧法なども採用でき、材料の種類や形状、などによって適宜選択できる。 Adhesion between the tetrafluoroethylene copolymer of the present invention and another material can be performed by thermal activation by heating or the like, and thermal melt adhesion is more preferable. Typical bonding methods include a hot roll method and a hot press method, and furthermore, a high-frequency heating method, a micro method, a vacuum pressure bonding method (such as a vacuum press), and a pneumatic method can also be adopted. It can be appropriately selected depending on the above.
本発明のテトラフルオロエチレン共重合体フィルムは、前記のごとく、種々の形状、大きさ、厚さを持つように製造でき、種々の材料に対する優れた接着性と、フッ素樹脂のもつ優れた特性により、広範囲の用途に使用されうる。 As described above, the tetrafluoroethylene copolymer film of the present invention can be produced with various shapes, sizes, and thicknesses, and has excellent adhesion to various materials and excellent characteristics of fluororesin. Can be used in a wide range of applications.
用途の具体例としては、化学プラント配管に巻き付ける防食テープ、船舶のデッキなどの配管に巻き付けるテープ、その他の配管用防食テープ；看板、農業用温室、その他の温室の屋根材あるいは側壁、外装材の表面のような、耐候性を付与する用途；太陽電池の光起電素子の光入射側表面に設ける透明な表面被覆材；耐汚染性に優れた内装材、などである。さらに、食品包装材、薬品包装材のような耐薬品性を必要とする用途にも使用できる。 Specific examples of applications include anticorrosion tapes wound around chemical plant piping, tapes wrapped around piping on ship decks, other anticorrosion tapes for piping; signs, agricultural greenhouses, roofing or side walls of other greenhouses, exterior materials, etc. Use for imparting weather resistance such as the surface; transparent surface covering material provided on the light incident side surface of the photovoltaic element of the solar cell; interior material excellent in contamination resistance. Furthermore, it can be used for applications that require chemical resistance such as food packaging materials and chemical packaging materials.
さらに、本発明のテトラフルオロエチレン共重合体は、ＯＡ機器のハウジング、食品加工装置、調理機器などの防汚性、非粘着性、低摩擦性を必要とする装置・機器、撥水撥油性ガラス、液晶ディスプレイなどの液晶関連材料、自動車関連材料などに使用できる。 Furthermore, the tetrafluoroethylene copolymer of the present invention is a device / equipment that requires antifouling, non-adhesive, and low friction properties, such as a housing for OA equipment, food processing equipment, and cooking equipment, and water / oil repellent glass. It can be used for liquid crystal related materials such as liquid crystal displays and automobile related materials.
次に本発明のテトラフルオロエチレン共重合体層と他の材料の層とからなる積層体について、他の材料の具体例と共に説明する。
本発明のテトラフルオロエチレン共重合体層を中間層として、他のフッ素樹脂の層と熱可塑性樹脂層とを積層することができる。
Next, the laminated body which consists of the tetrafluoroethylene copolymer layer of this invention and the layer of another material is demonstrated with the specific example of another material.
Using the tetrafluoroethylene copolymer layer of the present invention as an intermediate layer, other fluororesin layers and thermoplastic resin layers can be laminated.
そのような他のフッ素樹脂の具体例は、テトラフルオロエチレン−フルオロ(アルキルビニルエーテル)共重合体（ＰＦＡ）、テトラフルオロエチレン−ヘキサフルオロプロピレン共重合体（ＦＥＰ）、エチレン−テトラフルオロエチレン共重合体（ＥＴＦＥ）、エチレン−クロロトリフルオロエチレン共重合体（ＥＣＴＦＥ）、プロピレン−テトラフルオロエチレン共重合体、ポリビニリデンフルオライド（ＰＶＤＦ）、ビニリデンフルオライド共重合体、ポリクロロトリフルオロエチレン（ＰＣＴＦＥ）、エチレン−含フッ素オレフィン系共重合体などである。 Specific examples of such other fluororesins include tetrafluoroethylene-fluoro (alkyl vinyl ether) copolymer (PFA), tetrafluoroethylene-hexafluoropropylene copolymer (FEP), and ethylene-tetrafluoroethylene copolymer. (ETFE), ethylene-chlorotrifluoroethylene copolymer (ECTFE), propylene-tetrafluoroethylene copolymer, polyvinylidene fluoride (PVDF), vinylidene fluoride copolymer, polychlorotrifluoroethylene (PCTFE), And ethylene-fluorine-containing olefin copolymer.
他のフッ素樹脂の平均分子量は、通常、２,０００〜１,０００,０００であってよい。これらフッ素樹脂の中でも、比較的融点の低い、ＰＶＤＦ、ビニリデンフルオライド共重合体またはエチレン−含フッ素オレフィン系共重合体が好ましい。 The average molecular weight of the other fluororesin may usually be 2,000 to 1,000,000. Among these fluororesins, PVDF, vinylidene fluoride copolymer or ethylene-fluorinated olefin copolymer having a relatively low melting point is preferable.
ビニリデンフルオライド共重合体とは、ビニリデンフルオライドと、これと共重合可能な少なくとも一種の含フッ素モノマーからなる樹脂状共重合体である。ここでビニリデンフルオライドと共重合可能な含フッ素モノマーとしては、テトラフルオロエチレン（ＴＦＥ）、ヘキサフルオロプロピレン（ＨＦＰ）、クロロトリフルオロエチレン（ＣＴＦＥ）、ヘキサフルオロイソブチレン、ヘキサフルオロアセトン、ペンタフルオロプロピレン、トリフルオロエチレン、ビニルフルオライド、フルオロ(アルキルビニルエーテル)などが例示される。 The vinylidene fluoride copolymer is a resinous copolymer composed of vinylidene fluoride and at least one fluorine-containing monomer copolymerizable therewith. Examples of the fluorine-containing monomer copolymerizable with vinylidene fluoride include tetrafluoroethylene (TFE), hexafluoropropylene (HFP), chlorotrifluoroethylene (CTFE), hexafluoroisobutylene, hexafluoroacetone, pentafluoropropylene, Examples include trifluoroethylene, vinyl fluoride, and fluoro (alkyl vinyl ether).
エチレン−含フッ素オレフィン系共重合体とは、エチレンとＴＦＥおよび／またはＣＴＦＥとの、モル比が１０／９０〜６０／４０である樹脂状共重合体である場合により、それらと共重合可能な第３の含フッ素モノマーを、エチレンとＴＦＥおよび／またはＣＴＦＥとの合計量に対して０〜１５モル％含んでいてよい。第３の含フッ素モノマーとしては、ＣＺ２＝ＣＺ(ＣＦ２)wＺ、ＣＦ２＝ＣＦＯ(ＣＦ２)wＺ（式中、Ｚは水素原子またはフッ素原子、wは１〜８の整数である。）、ＣＨ２＝Ｃ(ＣＦ３)２で示される化合物が挙げられる。 The ethylene-fluorine-containing olefin copolymer is a resinous copolymer having a molar ratio of 10/90 to 60/40 of ethylene and TFE and / or CTFE, and can be copolymerized therewith. The third fluorine-containing monomer may be contained in an amount of 0 to 15 mol% with respect to the total amount of ethylene and TFE and / or CTFE. As the third fluorine-containing monomer, CZ 2 = CZ (CF 2 ) w Z, CF 2 = CFO (CF 2) in w Z (wherein, Z is a hydrogen atom or a fluorine atom, w is an integer of 1 to 8. The values And a compound represented by CH 2 ═C (CF 3 ) 2 .
このような比較的融点の低いＰＶＤＦ、ビニリデンフルオライド共重合体またはエチレン−含フッ素オレフィン系共重合体を、熱可塑性樹脂としてのポリアミド樹脂と共押出しする場合、ポリアミド樹脂の著しい劣化を伴わない混練温度および成形温度範囲で充分な溶融流動性を確保するためには、剪断速度１００sec−１で２５０℃での溶融粘度が１０〜１０５poiseであるＰＶＤＦ、ビニリデンフルオライド共重合体またはエチレン−含フッ素オレフィン系共重合体を使用することが好ましい。中でも、剪断速度１００sec−１で２５０℃での溶融粘度が１０〜１０５poiseであるエチレン／テトラフルオロエチレン共重合体は、積層体の燃料透過性を低く維持しながら柔軟性、低温耐衝撃性などを保持し、しかも、本発明のテトラフルオロエチレン共重合体層を中間層として、熱可塑性樹脂との同時多層押出しにより積層体を作成するのに最適である。 When such a relatively low melting point PVDF, vinylidene fluoride copolymer or ethylene-fluorinated olefin copolymer is coextruded with a polyamide resin as a thermoplastic resin, kneading without significant deterioration of the polyamide resin In order to ensure sufficient melt fluidity in the temperature and molding temperature range, PVDF, vinylidene fluoride copolymer or ethylene-containing material having a melt viscosity of 10 to 10 5 poise at 250 ° C. at a shear rate of 100 sec −1. It is preferable to use a fluoroolefin copolymer. Among them, an ethylene / tetrafluoroethylene copolymer having a melt viscosity of 10 to 10 5 poise at 250 ° C. at a shear rate of 100 sec −1 is flexible and has low temperature impact resistance while maintaining low fuel permeability of the laminate. In addition, it is optimal for making a laminate by simultaneous multilayer extrusion with a thermoplastic resin using the tetrafluoroethylene copolymer layer of the present invention as an intermediate layer.
エチレン−テトラフルオロエチレン系共重合体の特性を損なうことなく、比較的高価な第３の含フッ素モノマーの使用量を低減できる点において、エチレン／テトラフルオロエチレンのモル比が１０／９０〜３８／６２で、それらと共重合しうる第３の含フッ素モノマーがエチレンとテトラフルオロエチレン合計量に対して約０．１〜５モル％含まれるエチレン−テトラフルオロエチレン系共重合体が最も好ましい（特公昭６２−５８６１５号公報参照）。 The ethylene / tetrafluoroethylene molar ratio is 10/90 to 38/38 in that the amount of the relatively expensive third fluorine-containing monomer can be reduced without impairing the properties of the ethylene-tetrafluoroethylene copolymer. 62, an ethylene-tetrafluoroethylene copolymer in which the third fluorine-containing monomer copolymerizable therewith is contained in an amount of about 0.1 to 5 mol% relative to the total amount of ethylene and tetrafluoroethylene is most preferred (special No. 62-58615).
本発明のテトラフルオロエチレン共重合体を用いた積層体におけるそれぞれの層は、本発明の目的を損なわない範囲で、ガラス繊維、セラミック繊維、チタン酸カリウム繊維、アラミド繊維、芳香族ポリエステル繊維などの繊維状の強化材；炭酸カリシウム、タルク、マイカ、クレイ、カーボン粉末、グラファイト、ガラスピースなどの無機充填材料；金属粉末；ポリオレフィン、ポリテトラフルオロエチレン、ポリイミドなどの耐熱性樹脂；着色剤；難燃剤；摺動用添加剤などの充填材を含んでよい。その配合量は、樹脂１００重量部に対して１〜７０重量部である。
先に例示した珪素質材料のなかで、とりわけガラス系材料に対して本発明のテトラフルオロエチレン共重合体は良好な接着性を示す。
Each layer in the laminate using the tetrafluoroethylene copolymer of the present invention is a glass fiber, a ceramic fiber, a potassium titanate fiber, an aramid fiber, an aromatic polyester fiber, etc., as long as the object of the present invention is not impaired. Fibrous reinforcements; inorganic fillers such as calcium carbonate, talc, mica, clay, carbon powder, graphite, glass pieces; metal powders; heat-resistant resins such as polyolefin, polytetrafluoroethylene, polyimide; colorants; flame retardants A filler such as a sliding additive may be included. The compounding quantity is 1-70 weight part with respect to 100 weight part of resin.
Among the silicon-based materials exemplified above, the tetrafluoroethylene copolymer of the present invention exhibits excellent adhesion particularly to glass-based materials.
本発明のテトラフルオロエチレン共重合体の層とガラス系材料とからなる積層体は透明性を有し、テトラフルオロエチレン共重合体がガラス表面に撥水性、撥油性、反射防止性、低屈折率性などを与えるので、この積層体は、光学関連部品、液晶関連部品、自動車用ガラスなどに用いることができる。 The laminate comprising the tetrafluoroethylene copolymer layer of the present invention and a glass-based material has transparency, and the tetrafluoroethylene copolymer has water repellency, oil repellency, antireflection, low refractive index on the glass surface. Therefore, this laminate can be used for optical related parts, liquid crystal related parts, automotive glass and the like.
また、この積層体は、難燃性、透明性、耐候性、破損時の飛散防止性を兼ね備えた建材用防火安全ガラスとして使用することができる。
車両、航空機、建築物などに用いる内壁、天井、ドアなどの表面材として、従来、樹脂板にウールやアクリルなどからなる布を貼り付けてなる積層体が知られているが、布を用いているので、防炎性に劣る。そこで、防炎性に優れた表面材としてガラスクロスなどのガラス繊維布を用いることが考えられるが、ガラス繊維は皮膚刺激性を有する場合がある。本発明のテトラフルオロエチレン共重合体は、ガラスクロスに対しても優れた接着性を示すので、これをガラスクロスに積層すれば、ガラスクロスの持つ欠点を解決することができる。
Moreover, this laminated body can be used as fireproof safety glass for building materials having flame retardancy, transparency, weather resistance, and anti-scattering property at the time of breakage.
As a surface material for inner walls, ceilings, doors, etc. used in vehicles, aircraft, buildings, etc., a laminated body in which a cloth made of wool or acrylic is pasted on a resin plate is conventionally known. Therefore, it is inferior in flameproofness. Therefore, it is conceivable to use a glass fiber cloth such as a glass cloth as a surface material having excellent flameproofing properties, but the glass fiber may have skin irritation. Since the tetrafluoroethylene copolymer of the present invention exhibits excellent adhesion to glass cloth, the disadvantage of the glass cloth can be solved by laminating it on the glass cloth.
耐候性や耐汚染性に優れた化粧板として、ポリビニリデンフルオライドとアクリル樹脂を共押出して成膜した２層フィルムのアクリル樹脂面と塩化ビニル樹脂フィルムとを熱ラミネートした化粧板が知られている。しかし、ポリビニリデンフルオライドの耐溶剤性および耐汚染性は不十分である。 As a decorative board excellent in weather resistance and stain resistance, a decorative board is known in which an acrylic resin surface of a two-layer film formed by co-extrusion of polyvinylidene fluoride and an acrylic resin and a vinyl chloride resin film are thermally laminated. Yes. However, the solvent resistance and stain resistance of polyvinylidene fluoride are insufficient.
本発明のテトラフルオロエチレン共重合体は、ポリビニリデンフルオライドと同等またはそれ以上の溶融押出適性を有しているので、ポリビニリデンフルオライドと同様に共押出しによりアクリル樹脂との２層フィルムが製造でき、さらに塩化ビニルと熱ラミネートして化粧板を得ることができる。このようにして製造した化粧板は、優れた耐溶剤性、耐候性、耐汚染性を有している。 Since the tetrafluoroethylene copolymer of the present invention has a melt-extrusion suitability equal to or higher than that of polyvinylidene fluoride, a two-layer film with an acrylic resin is produced by co-extrusion in the same manner as polyvinylidene fluoride. Further, a decorative board can be obtained by heat laminating with vinyl chloride. The decorative board manufactured in this way has excellent solvent resistance, weather resistance, and contamination resistance.
積層体の外側（ホース、チューブ、パイプなどの場合は外層）または内側（ホース、チューブ、パイプなどの場合は内層）に、補強、防汚、帯電防止、または低温衝撃性改良を目的として、熱可塑性樹脂層（例えばＰＶＣ）または熱可塑性エラストマーを含むゴム層（例えばＥＰＤＭ）を同時共押出時にあるいは同時共押出後に設けることもできる。また、コルゲート加工によりチューブに柔軟性を付与することもできる。 Heat is applied to the outside of the laminate (outer layer for hoses, tubes, pipes, etc.) or inside (inner layer for hoses, tubes, pipes, etc.) for the purpose of reinforcement, antifouling, antistatic or low temperature impact resistance. A plastic resin layer (for example, PVC) or a rubber layer (for example, EPDM) containing a thermoplastic elastomer may be provided at the time of co-extrusion or after the co-extrusion. Moreover, a softness | flexibility can also be provided to a tube by corrugating.
積層体の形状は、成形体、例えばホース、パイプ、チューブ、シート、ガスケット、パッキング、フィルム、タンク、ローラー、ボトル、容器等であり、多層共押出成形、多層ブロー成形、多層射出成形を用いれば任意の形状の成形体が得られる。 The shape of the laminated body is a molded body such as a hose, pipe, tube, sheet, gasket, packing, film, tank, roller, bottle, container, etc., if multilayer coextrusion molding, multilayer blow molding, multilayer injection molding is used. A molded body having an arbitrary shape is obtained.
積層体の特に好ましい用途は、耐サワーガソリン用、耐アルコール燃料用、耐メチルｔ−ブチルエーテル用、耐ガソリン添加剤（アミンなど）入燃料用、インク、塗料用、廃液輸送用、高温液体輸送用、スチーム配管用のチューブ、パイプ、容器や、ラジエーターホースなどである。積層体がチューブである場合、フッ素樹脂層が最内層であることが好ましい。 Particularly preferred uses of the laminates are for sour gasoline resistant, alcohol resistant fuel, methyl t-butyl ether resistant, gasoline resistant fuel (such as amine) fuel, ink, paint, waste liquid transportation, high temperature liquid transportation Tubes, pipes, containers and radiator hoses for steam piping. When the laminate is a tube, the fluororesin layer is preferably the innermost layer.
本発明のテトラフルオロエチレン共重合体は、図３に示した太陽電池モジュールの表面フィルム１として、及びまたは透明充填材層２として使用することができる。 The tetrafluoroethylene copolymer of the present invention can be used as the surface film 1 of the solar cell module shown in FIG. 3 and / or as the transparent filler layer 2.
本発明のテトラフルオロエチレン共重合体を表面フィルムとして使用する場合、その厚さは、通常１０〜５００μm、好ましくは３０〜２００μmである。表面フィルム中には、透明性、耐候性を損なわない程度にガラス等からなる繊維、不織布、ビーズ、紫外線吸収剤、顔料、その他適宜添加剤を添加することも可能である。 When using the tetrafluoroethylene copolymer of this invention as a surface film, the thickness is 10-500 micrometers normally, Preferably it is 30-200 micrometers. In the surface film, fibers, nonwoven fabrics, beads, ultraviolet absorbers, pigments, and other additives as appropriate can be added to such an extent that the transparency and weather resistance are not impaired.
また、起電力素子は前記表面フィルムにて直接被覆することもできるし、外部からの衝撃からの保護、表面フィルム起電力素子との密着性をより強固にする目的で、透明充填材層を設けても良い。 In addition, the electromotive force element can be directly covered with the surface film, and a transparent filler layer is provided for the purpose of protecting from external impact and further strengthening the adhesion with the surface film electromotive force element. May be.
その場合の透明充填材層には、従来から使用されているエチレン−酢酸ビニル共重合体（ＥＶＡ）、エチレン−メチルアクリレート共重合体、エチレン−エチルアクリレート共重合体、エチレン−エチルアクリレート−無水マレイン酸共重合体、ウレタン樹脂、ブチラール樹脂、シリコーン樹脂、ポリアミド樹脂、ポリエステル系熱可塑性エラストマー、ポリオレフィン系熱可塑性エラストマー、ポリウレタン系熱可塑性エラストマー、ポリアミド系熱可塑性エラストマー、エポキシ基含有ポリエチレン、フッ素ゴム等があり、特にＥＶＡが透明性、柔軟性、接着性、安価であることから好ましい。さらに、有機過酸化物で架橋したＥＶＡが耐熱性、耐候性の面で好ましい。 In that case, the transparent filler layer includes conventionally used ethylene-vinyl acetate copolymer (EVA), ethylene-methyl acrylate copolymer, ethylene-ethyl acrylate copolymer, ethylene-ethyl acrylate-anhydrous maleic anhydride. Acid copolymer, urethane resin, butyral resin, silicone resin, polyamide resin, polyester thermoplastic elastomer, polyolefin thermoplastic elastomer, polyurethane thermoplastic elastomer, polyamide thermoplastic elastomer, epoxy group-containing polyethylene, fluoro rubber, etc. In particular, EVA is preferable because it is transparent, flexible, adhesive, and inexpensive. Furthermore, EVA crosslinked with an organic peroxide is preferable in terms of heat resistance and weather resistance.
一方、本発明のテトラフルオロエチレン共重合体を透明充填材層として使用する場合、その厚さは、通常１０〜１０００μm、好ましくは５０〜５００μmであり、表面フィルムとしては従来のフッ素樹脂表面フィルムを用いることが出来る。透明充填材層には、耐傷付性や耐衝撃性を改善する目的で、透明性等を損なわない程度にガラス等からなる繊維、不織布、ビーズを配合または一体成形してよい。その他、硬化促進剤、紫外線吸収剤などの添加剤を配合してもよい。 On the other hand, when the tetrafluoroethylene copolymer of the present invention is used as a transparent filler layer, the thickness is usually 10 to 1000 μm, preferably 50 to 500 μm, and the surface film is a conventional fluororesin surface film. Can be used. In the transparent filler layer, for the purpose of improving scratch resistance and impact resistance, fibers, nonwoven fabrics, and beads made of glass or the like may be blended or integrally molded to such an extent that transparency and the like are not impaired. In addition, you may mix | blend additives, such as a hardening accelerator and a ultraviolet absorber.
次に実施例を示し、本発明を具体的に説明する。
実施例で得た共重合体の組成および物性は、次のようにして測定した。
ポリマー中のモノマー組成
１９Ｆ−ＮＭＲチャートから求める。
融点
セイコー型ＤＳＣ装置を用い、１０℃／分の速度で昇温したときの融解ピークを記録し、極大値に対応する温度を融点とする。
Next, an Example is shown and this invention is demonstrated concretely.
The composition and physical properties of the copolymers obtained in the examples were measured as follows.
Monomer composition in polymer
It calculates | requires from a 19 F-NMR chart.
Using a melting point Seiko-type DSC apparatus, record the melting peak when the temperature is raised at a rate of 10 ° C./min, and set the temperature corresponding to the maximum value as the melting point.
ＭＦＲ
東洋精機製作所株式会社製メルトインデクサーを用い、２００℃、５kg荷重下で、直径２mm、長さ８mmのノズルから単位時間（１０分間）に流出する共重合体の重量（g）を測定する。
MFR
Using a melt indexer manufactured by Toyo Seiki Seisakusho Co., Ltd., the weight (g) of the copolymer flowing out in a unit time (10 minutes) from a nozzle having a diameter of 2 mm and a length of 8 mm under a load of 200 kg and 5 kg is measured.
赤外線吸収スペクトル（１８０８ｃｍ−１／２８８１cm−１の吸収比）
パーキンエルマー社製フーリエ変換赤外分光光度計を用い、約０.４mm厚のフィルムについて赤外線吸収スペクトルを測定し、１８０８cm−１での吸収ピークの高さの、２８８１cm−１での吸収ピークの高さに対する比を計算する。
Infrared absorption spectrum (absorption ratio of 1808 cm −1 / 2881 cm −1 )
Using a Fourier transform infrared spectrophotometer manufactured by PerkinElmer, an infrared absorption spectrum was measured for a film having a thickness of about 0.4 mm, and the height of the absorption peak at 1808 cm −1 was high as the absorption peak at 2881 cm −1. Calculate the ratio to thickness.
ヘイズ値（曇度）
東洋精機製作所株式会社製ヘイズメーターを用いて測定した。試料の厚みは２ｍｍである。
臨界剪断速度
東洋精機製作所株式会社製キャピログラフを使用し、キャピラリー（ダイ長さ１０mm、ダイ穴直径１mm）を用いて２３０℃で測定し、メルトフラクチャーの発生しはじめる剪断速度を臨界剪断速度とする。
Haze value (cloudiness)
It measured using the Toyo Seiki Seisakusho Co., Ltd. haze meter. The thickness of the sample is 2 mm.
Critical shear rate Using a capillograph manufactured by Toyo Seiki Seisakusho Co., Ltd., using a capillary (die length 10 mm, die hole diameter 1 mm) at 230 ° C., the shear rate at which melt fracture starts to occur is defined as the critical shear rate.
実施例１
内容積４Ｌのガラスライニング製オートクレーブに脱酸素した水１Ｌを入れ、真空にした後、パーフルオロシクロブタン４００gおよびヘキサフルオロプロピレン８００gを入れ、槽内温度を３５℃、攪拌速度を５８０rpmに保った。さらに、ＣＨ２＝ＣＦ(ＣＦ２)3Ｈ２.０gおよびシクロヘキサン１.５gを仕込んだ後、テトラフルオロエチレン／エチレン／パーフルオロシクロブタンの混合ガス（モル比＝７８.９：１６.６：４.５）を１２kgf／ｃｍ２Ｇまで圧入した。
Example 1
1 L of deoxygenated water was put into a glass lining autoclave with an internal volume of 4 L, and after evacuating, 400 g of perfluorocyclobutane and 800 g of hexafluoropropylene were put, and the temperature in the tank was kept at 35 ° C. and the stirring speed was 580 rpm. Further, after charging 2.0 g of CH 2 ═CF (CF 2 ) 3 H and 1.5 g of cyclohexane, a mixed gas of tetrafluoroethylene / ethylene / perfluorocyclobutane (molar ratio = 78.9: 16.6: 4. 5) was press-fitted to 12 kgf / cm 2 G.
次いで、ジノルマルプロピルパーオキシジカーボネート８.０gを仕込んで重合を開始した。重合の進行とともに圧力が低下するので、テトラフルオロエチレン／エチレン／パーフルオロシクロブタンの混合ガス（モル比＝５２.８：４２.７：４.５）を追加圧入して重合圧力を１２kgf／cm2Ｇに保ちながら重合を続け、途中、ＣＨ２＝ＣＦ(ＣＦ２)3Ｈ１.１５gを９回に分割してマイクロポンプで仕込んだ。また重合開始から５時間経過した時点でジノルマルプロピルパーオキシジカーボネート４.０gを追加し、重合を合計で１０時間行った。
重合終了後、内容物を回収し、水洗して、重合体粉末１２７gを得た。得られたポリマーの物性を表１に示す。
Next, 8.0 g of dinormalpropyl peroxydicarbonate was charged to initiate polymerization. Since the pressure decreases as the polymerization proceeds, a mixed gas of tetrafluoroethylene / ethylene / perfluorocyclobutane (molar ratio = 52.8: 42.7: 4.5) is additionally injected to bring the polymerization pressure to 12 kgf / cm 2. Polymerization was continued while maintaining G, and CH 2 ═CF (CF 2 ) 3 H (1.15 g) was divided into 9 times and charged with a micropump. When 5 hours had elapsed from the start of polymerization, 4.0 g of dinormalpropyl peroxydicarbonate was added, and the polymerization was carried out for a total of 10 hours.
After completion of the polymerization, the contents were collected and washed with water to obtain 127 g of polymer powder. The physical properties of the obtained polymer are shown in Table 1.
実施例２
シクロヘキサンの仕込量を０.８５gにし、重合途中でジノルマルプロピルパーオキシジカーボネートを追加しない以外は実施例１と同様の手順を繰り返して、１１時間の重合で粉末状重合体１３７gを得た。得られたポリマーの物性を表１に示す。
Example 2
A procedure similar to Example 1 was repeated except that the amount of cyclohexane charged was 0.85 g and dinormalpropyl peroxydicarbonate was not added during the polymerization, and 137 g of a powdery polymer was obtained by polymerization for 11 hours. The physical properties of the obtained polymer are shown in Table 1.
実施例３
最初に仕込むパーフルオロシクロブタンおよびヘキサフルオロプロピレンの量をそれぞれ６００gおよび６００gとし、シクロヘキサンの仕込量を１.６gとし、ジノルマルプロピルパーオキシジカーボネートの量を１０.０gとする以外は、実施例１と同様の操作を繰り返して、８時間の重合で、粉末状重合体１５３gを得た。得られたポリマーの物性を表１に示す。
Example 3
Example 1 except that the amounts of perfluorocyclobutane and hexafluoropropylene initially charged were 600 g and 600 g, respectively, the amount of cyclohexane charged was 1.6 g, and the amount of dinormal propyl peroxydicarbonate was 10.0 g. The same operation as above was repeated, and 153 g of a powdery polymer was obtained by polymerization for 8 hours. The physical properties of the obtained polymer are shown in Table 1.
実施例４
パーフルオロシクロブタンを仕込まずに、最初に仕込むヘキサフルオロプロピレンの量を１０００gとし、重合途中でジノルマルプロピルパーオキシジカーボネートを追加しない以外は、実施例１と同様の操作を繰り返して、１９時間の重合で、粉末状重合体１３０gを得た。得られたポリマーの物性を表１に示す。
Example 4
The same procedure as in Example 1 was repeated except that the amount of hexafluoropropylene initially charged was 1000 g without adding perfluorocyclobutane, and no dinormalpropyl peroxydicarbonate was added during the polymerization. By polymerization, 130 g of a powdery polymer was obtained. The physical properties of the obtained polymer are shown in Table 1.
比較例１
シクロヘキサンの量を０.３g、ジノルマルプロピルパーオキシジカーボネートの量を６gとし、重合途中でジノルマルプロピルパーオキシジカーボネートを追加しない以外は、実施例１と同様の操作を繰り返して、９時間の重合で、粉末状重合体１４０gを得た。得られたポリマーの物性を表１に示す。
Comparative Example 1
The same procedure as in Example 1 was repeated for 9 hours except that the amount of cyclohexane was 0.3 g, the amount of dinormalpropyl peroxydicarbonate was 6 g, and no dinormalpropyl peroxydicarbonate was added during the polymerization. In this polymerization, 140 g of a powdery polymer was obtained. The physical properties of the obtained polymer are shown in Table 1.
比較例２
最初に仕込むパーフルオロシクロブタンおよびヘキサフルオロプロピレンの量をそれぞれ７００gおよび５００gとし、シクロヘキサンの仕込量を１.５gとする以外は、同様の操作を繰り返して、４.５時間の重合で、粉末状重合体１３６gを得た。得られたポリマーの物性を表１に示す。
Comparative Example 2
The same procedure was repeated except that the amount of perfluorocyclobutane and hexafluoropropylene charged first was 700 g and 500 g, respectively, and the amount of cyclohexane charged was 1.5 g. 136g of union was obtained. The physical properties of the obtained polymer are shown in Table 1.
比較例３
最初に仕込むパーフルオロシクロブタンおよびヘキサフルオロプロピレンの量をそれぞれ１０５０gおよび１５０gとし、ＣＨ２＝ＣＦ(ＣＦ２)３Ｈの仕込量を４.０g、シクロヘキサンの仕込量を５.０g、ジノルマルプロピルパーオキシジカーボネートの量を４.０gとし、重合途中でジノルマルプロピルパーオキシジカーボネートを追加しない以外は、実施例１と同様の操作を繰り返して、４時間の重合で、粉末状重合体１２３gを得た。得られたポリマーの物性を表１に示す。
Comparative Example 3
The amount of perfluorocyclobutane and hexafluoropropylene charged first is 1050 g and 150 g, respectively, CH2 = CF (CF2) 3H is charged 4.0 g, cyclohexane is charged 5.0 g, and dinormal propyl peroxydicarbonate. The same procedure as in Example 1 was repeated, except that di-normal propyl peroxydicarbonate was not added during the polymerization, and 123 g of a powdery polymer was obtained by polymerization for 4 hours. The physical properties of the obtained polymer are shown in Table 1.
応用例１
実施例１と実施例２で得たポリマーは２００℃で、実施例３と比較例１で得たポリマーは２３０℃で、実施例４で得たポリマーは１８０℃で、比較例２で得たポリマーは２５０℃で、比較例３で得たポリマーは３００℃で、それぞれ溶融させ、内径１２０mmの金型を用いて、約５０kgf／cm2の圧力でプレスして、０.５mm厚のシートを作成した。
Application example 1
The polymer obtained in Example 1 and Example 2 was 200 ° C., the polymer obtained in Example 3 and Comparative Example 1 was 230 ° C., the polymer obtained in Example 4 was 180 ° C., and obtained in Comparative Example 2. The polymer was 250 ° C., the polymer obtained in Comparative Example 3 was melted at 300 ° C., respectively, and pressed at a pressure of about 50 kgf / cm 2 using a mold having an inner diameter of 120 mm to form a sheet having a thickness of 0.5 mm. Created.
別途、ポリアミド１２（宇部興産株式会社製、商品名：ＵＢＥ ３０３５ＭＪ１）を２００℃で、上記と同様の方法によりプレスして０.５mm厚のシートを作成した。 Separately, polyamide 12 (manufactured by Ube Industries, Ltd., trade name: UBE 3035MJ1) was pressed at 200 ° C. in the same manner as described above to prepare a 0.5 mm thick sheet.
次に、自動溶着機（嶋倉電子工業株式会社製型番ＳＫＤ−ＦＡ４８）を用い、ポリアミド１２の適切な成形温度範囲である２３０℃で実施例１〜実施例４および比較例１〜比較例３で得たポリマーから作成したシートそれぞれとポリアミド１２を重ね、０.２５kgf／cm2の圧力で５０秒間加圧して、溶着させた。この時、重ね合わせた２枚のシートの一部の間に、ポリイミドのフィルムを挟み、フッ素樹脂とポリアミド１２の非接触部分を作り、引張り測定時のつかみ部分とする。 Next, using an automatic welding machine (model number SKD-FA48 manufactured by Shimakura Electronics Co., Ltd.) at 230 ° C., which is an appropriate molding temperature range of polyamide 12, in Examples 1 to 4 and Comparative Examples 1 to 3. Each sheet prepared from the obtained polymer and the polyamide 12 were overlapped and welded by pressing at a pressure of 0.25 kgf / cm 2 for 50 seconds. At this time, a polyimide film is sandwiched between a part of the two overlapped sheets to form a non-contact portion between the fluororesin and the polyamide 12 and serve as a grip portion at the time of tensile measurement.
得られた溶着シートの接着剥離強度を、オリエンテック株式会社製テンシロン万能試験機により測定した。測定値は、最大剥離強度である。結果を表２に示す。
応用例２
応用例１と同様にして、実施例１〜実施例４および比較例１〜比較例３で得たポリマーそれぞれから０.４mm厚のシートを作成し、図１に示すように、１２mmの長さで端部分を重ね合わせた上側と下側のパイレックス（商標）ガラス板（幅２０mm、長さ３０mm、厚さ５mm）の間にはさみ、上側のガラス板の他端は、０.４mm厚のＦＥＰフィルムをスペーサとして、もう一枚の下側ガラス板と重ね合わせ、全体を２枚のステンレス鋼（ＳＵＳ）板の間に置き、ステンレス鋼板の重さと合わせて０.１８kｇ／cm２になるように荷重をのせ、電気炉のなかで２３０℃（比較例３のみ３００℃）、３０分間放置して試験片を得た。
Application example 2
In the same manner as in Application Example 1, a 0.4 mm thick sheet was prepared from each of the polymers obtained in Examples 1 to 4 and Comparative Examples 1 to 3, and a length of 12 mm was obtained as shown in FIG. Is sandwiched between the upper and lower Pyrex glass plates (
引張剪断法により、ポリマーで接着したガラス板間の接着強度を測定した。
図２に示すように、ポリマーで接着した２枚のガラス板の外形にあわせた試験用治具を、オリエンテック株式会社製テンシロン万能試験機にセットし、クロスヘッドスピード２０mm／分で引張剪断試験を行った。測定値は最大接着強度である。結果を表３に示す。
The adhesion strength between the glass plates bonded with the polymer was measured by a tensile shear method.
As shown in FIG. 2, a test jig that fits the outer shape of two glass plates bonded with polymer is set on a Tensilon universal testing machine manufactured by Orientec Co., Ltd., and a tensile shear test is performed at a crosshead speed of 20 mm / min. Went. The measured value is the maximum adhesive strength. The results are shown in Table 3.
応用例３
マルチマニホールドダイを使用し、押出し速度８m／分で、表４に示した温度条件下、表５に示す樹脂を用いて３種３層の同時押出しにより多層チューブを成形した。
チューブは、内層、中間層および外層からなり、外径８mmおよび内径６mmであり、内層の厚みは０．２mmであり、中間層の厚みは０．１mmであり、外層の厚みは０．７mmであった。
Application example 3
Using a multi-manifold die, a multilayer tube was formed by coextrusion of three types and three layers using the resins shown in Table 5 under the temperature conditions shown in Table 4 at an extrusion speed of 8 m / min.
The tube is composed of an inner layer, an intermediate layer, and an outer layer, and has an outer diameter of 8 mm and an inner diameter of 6 mm, an inner layer thickness of 0.2 mm, an intermediate layer thickness of 0.1 mm, and an outer layer thickness of 0.7 mm. there were.
応用例４
マルチマニホールドダイを使用し、押出し速度８m／分で、表４に示した温度条件下、表５に示す樹脂を用いて２種２層の同時押出しにより多層チューブを成形した。
チューブは、内層および外層からなり、外径８mmおよび内径６mmであり、内層の厚みは０．３５mmであり、外層の厚みは０．６５mmであった。
Using a multi-manifold die, a multilayer tube was formed by coextrusion of two types and two layers using the resins shown in Table 5 under the temperature conditions shown in Table 4 at an extrusion speed of 8 m / min.
The tube was composed of an inner layer and an outer layer, and had an outer diameter of 8 mm and an inner diameter of 6 mm. The inner layer had a thickness of 0.35 mm and the outer layer had a thickness of 0.65 mm.
比較応用例１
内径６mm、層厚み０．２mmのＥＴＦＥの単層チューブを押出し、その表面をコロナ放電処理した後、ＰＡ１２を０．８mmの層厚みで溶融被覆した。
Comparative application example 1
An ETFE single-layer tube having an inner diameter of 6 mm and a layer thickness of 0.2 mm was extruded, and its surface was subjected to corona discharge treatment, and then PA12 was melt-coated with a layer thickness of 0.8 mm.
応用例３〜８および比較応用例１で製造したチューブについて、以下の試験を行った。
剥離強度
チューブから５mm幅のテストピースを切り取り、５０mm／分の引張速度で１８０度剥離試験を行って、層間の接着強度を測定した。
The following tests were performed on the tubes manufactured in Application Examples 3 to 8 and Comparative Application Example 1.
Peel strength A test piece having a width of 5 mm was cut from the tube, and a 180 ° peel test was performed at a tensile speed of 50 mm / min to measure the adhesive strength between the layers.
バリヤー性
チューブを３０cmの長さに切り、fuelＣ（イソオクタン／トルエン 体積比５０：５０）／メタノール（体積比:８５／１５）をチューブ内部に充填し、両端をシールし、４０℃で放置し、重量変化を測定して、燃料透過速度（１m２当たり、１日当たりの燃料減少量（ｇ））を計算した。
Cut the barrier tube into a length of 30 cm, fill fuel C (isooctane / toluene volume ratio 50:50) / methanol (volume ratio: 85/15) inside the tube, seal both ends, and leave at 40 ° C., The change in weight was measured, and the fuel permeation rate (the amount of fuel decrease per day (g) per m 2) was calculated.
低温衝撃強度
チューブを２０cmの長さに切り、−４０℃で５時間放置した後、−４０℃の雰囲気のまま、チューブの上、高さ３０．５cmから４５０gの荷重を落としチューブの割れを見る。１０回測定を行う。ｎ／１０で示す（ｎは割れた数）。
上記試験の結果を、表５に示す。
Cut low temperature impact strength tube into 20cm length and let stand at -40 ° C for 5 hours, then keep the atmosphere at -40 ° C and drop the load from 30.5cm to 450g on the tube to see the crack in the tube . Take 10 measurements. It shows by n / 10 (n is the number of cracks).
The results of the above test are shown in Table 5.
応用例５
本発明の実施例２で得た共重合体と、テトラフルオロエチレン−エチレン共重合体（ＥＴＦＥ）について、太陽電池用表面フィルムとして要求される耐候性、光透過性、接着性、耐傷付性、耐引裂性を、以下の方法により評価した。
Application example 5
About the copolymer obtained in Example 2 of the present invention and the tetrafluoroethylene-ethylene copolymer (ETFE), weather resistance, light transmittance, adhesion, scratch resistance required as a surface film for solar cells, The tear resistance was evaluated by the following method.
耐候性
サンシャインウエザオメーターを用い、ＡＳＴＭ Ｄ６３８に準拠するテストピースに成形したサンプル（厚み５００μm）を、以下の条件で２０００時間暴露した。
条件：６３℃、９８％湿度雰囲気
純水を１８分／２時間スプレー、光源カーボンアーク法
暴露前と暴露後の引張り強度を、テンシロン万能試験機（オリエンテック株式会社製）により測定した。最大破断強度と破断伸度の保持率（％）を、耐候性の尺度として示す。
また、暴露前と暴露後の色差をスガ試験機（株）製ＳＭカラーコンンピューター（ＳＭ−７）を用い、白色標準板を合わせて測定した。尚、△Ｅ＝｛(△Ｌ)2＋(△ａ)2＋(△ｂ)2}1/2である。
Using a weather-resistant sunshine weatherometer, a sample (thickness 500 μm) molded into a test piece in accordance with ASTM D638 was exposed for 2000 hours under the following conditions.
Conditions: 63 ° C., 98% humidity atmosphere Pure water sprayed for 18 minutes / 2 hours, light source carbon arc method The tensile strength before and after exposure was measured with a Tensilon universal testing machine (Orientec Co., Ltd.). The maximum breaking strength and the retention rate (%) of elongation at break are shown as a measure of weather resistance.
In addition, the color difference before and after the exposure was measured by using a SM color computer (SM-7) manufactured by Suga Test Instruments Co., Ltd. together with the white standard plate. ΔE = {(ΔL) 2 + (Δa) 2 + (Δb) 2 } 1/2 .
光透過性
全光線透過率およびＨＡＺＥ値を、東洋精機製作所(株)製ヘイズメーターを用いて測定した。
条件：室温
試料厚み：５００μm
The light transmissive total light transmittance and the HAZE value were measured using a haze meter manufactured by Toyo Seiki Seisakusho.
Condition: Room temperature Sample thickness: 500 μm
ガラスとの接着強度
応用例２と同様にして測定した。
フィルム引裂き強度
エルメンドルフ引裂き試験機を用い測定した。フィルム厚みは２００μmであった。試験片の寸法およびスリット位置は図４に示す。
Measurement was performed in the same manner as in Application Example 2 for Adhesive Strength with Glass .
Film tear strength was measured using an Elmendorf tear tester. The film thickness was 200 μm. The dimensions of the test piece and the slit position are shown in FIG.
フィルムスクラッチ試験
カーボンスチール製ブレードの刃先に２ポンドの荷重を加え、厚み２５０μmのフィルム上を引っ掻いた後の傷の状態を、目視で観察した。
結果を表６に示す。
Film Scratch Test A 2 pound load was applied to the cutting edge of a carbon steel blade, and the state of scratches after scratching on a 250 μm thick film was visually observed.
The results are shown in Table 6.
応用例６
３層のフィードブロックダイを使用し、押出し速度１０m／分で表７に示した温度条件下、表８に示す樹脂を用いて３種３層の同時押出しにより多層フィルムを成形した。
フィルムは、ポリエチレン層（厚さ０.１７mm）、中間層(レクスパールＲＡ３１５０)（厚さ０.０５mm）、実施例２の共重合体層（厚さ０.０８mm）からなる３層フィルムであった。
Application example 6
Using a three-layer feed block die, a multilayer film was formed by co-extrusion of three types and three layers using the resins shown in Table 8 under the temperature conditions shown in Table 7 at an extrusion speed of 10 m / min.
The film was a three-layer film consisting of a polyethylene layer (thickness 0.17 mm), an intermediate layer (Lexpearl RA3150) (thickness 0.05 mm), and the copolymer layer of Example 2 (thickness 0.08 mm). It was.
応用例７
応用例６と同様に表７の温度条件下、表８に示す樹脂を用いて３層フィルムを成形した。フィルムは、ポリエステル層（厚さ０.１７mm）、中間層(ＴＰＡＥ−８)（厚さ０.０５mm）、実施例２の共重合体層（厚さ０.０８mm）を有していた。
Application example 7
Similarly to Application Example 6, a three-layer film was molded using the resin shown in Table 8 under the temperature conditions shown in Table 7. The film had a polyester layer (thickness 0.17 mm), an intermediate layer (TPAE-8) (thickness 0.05 mm), and the copolymer layer of Example 2 (thickness 0.08 mm).
2)日本ポリオレフィン株式会社製エポキシ基含有ポリエチ
レン樹脂（融点１００℃）。
3)三菱レイヨン株式会社製ポリエチレンテレフタレート樹脂
（融点２４０℃）。
4)富士化成工業株式会社製重合脂肪酸系ポリアミドエラスト
マー（ポリエーテルエステルアミド）。
2) Epoxy group-containing polyethylene resin (melting point: 100 ° C.) manufactured by Nippon Polyolefin Co., Ltd.
3) Polyethylene terephthalate resin (melting point 240 ° C.) manufactured by Mitsubishi Rayon Co., Ltd.
4) Polymerized fatty acid polyamide elastomer (polyether ester amide) manufactured by Fuji Chemical Industry Co., Ltd.
剥離強度測定
応用例６および１１で得たフィルムから１cm幅のテストピースを切り取り、中間層と反対側層間の剥離強度を、５０mm／分の引張り速度での１８０度剥離試験で測定した。結果を上記表８に示す。
Peel Strength Measurement A test piece having a width of 1 cm was cut from the films obtained in Application Examples 6 and 11, and the peel strength between the intermediate layer and the opposite side layer was measured by a 180 degree peel test at a pulling speed of 50 mm / min. The results are shown in Table 8 above.
Claims (4)
ＣＨ２＝ＣＦＲf （Ｉ）
（式中、Ｒfは炭素数２〜１０のフルオロアルキル基である。）
で示されるフルオロビニル化合物からなる群から選択される少なくとも１種の他のモノマー６０〜１９モル％からなり、ポリマー鎖末端がカーボネート末端であり、
１．０〜１００ｇ／１０分のメルトフローレート（２００℃，５kg荷重）、
９０〜２００℃の融点、および
２３０℃で１０〜１０３sec−１の臨界剪断速度
を有し、赤外線吸収スペクトルにおける主鎖のＣＨ２基に起因する２８８１cm−１での吸収ピークの高さに対する、末端カーボネート基に起因する１８０８cm−１での吸収ピークの高さの比が、少なくとも０.７である接着性テトラフルオロエチレン共重合体からなるフィルム。 Tetrafluoroethylene 40 mol% to 81 mol% and ethylene , hexafluoropropylene and the formula:
CH 2 = CFRf (I)
(In the formula, Rf is a fluoroalkyl group having 2 to 10 carbon atoms.)
And at least one other monomer selected from the group consisting of fluorovinyl compounds represented by the formula:
Melt flow rate (200 ° C., 5 kg load) of 1.0 to 100 g / 10 minutes,
With a melting point of 90-200 ° C. and a critical shear rate of 10-10 3 sec −1 at 230 ° C., relative to the height of the absorption peak at 2881 cm −1 due to the CH 2 group of the main chain in the infrared absorption spectrum A film made of an adhesive tetrafluoroethylene copolymer having an absorption peak height ratio at 1808 cm −1 due to the terminal carbonate group of at least 0.7.
ＣＨ２＝ＣＦ(ＣＦ２)ｎＨ
（式中、ｎは３〜５の整数である。）
で示される化合物である請求項１または３に記載のフィルム。 The fluorovinyl compound has the formula:
CH 2 = CF (CF 2 ) n H
(In the formula, n is an integer of 3 to 5.)
The film of Claim 1 or 3 which is a compound shown by these.