JP4076309B2 - Lining material for molten aluminum - Google Patents
Lining material for molten aluminum Download PDFInfo
- Publication number
- JP4076309B2 JP4076309B2 JP2000049033A JP2000049033A JP4076309B2 JP 4076309 B2 JP4076309 B2 JP 4076309B2 JP 2000049033 A JP2000049033 A JP 2000049033A JP 2000049033 A JP2000049033 A JP 2000049033A JP 4076309 B2 JP4076309 B2 JP 4076309B2
- Authority
- JP
- Japan
- Prior art keywords
- molten aluminum
- alumina
- weight
- matrix
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【0001】
【発明の属する技術分野】
本発明は、アルミニウム(以下、単にアルミと言う)の鋳造設備に用いられるライニング部材に関する。より具体的には、ストーク、ラドル、樋、湯溜まり等のアルミ溶湯を扱う部材のアルミ溶湯が接する部分にライニングされる部材の改良に関する。
【0002】
【従来の技術】
アルミ鋳造設備におけるストークやラドル等においては、アルミ溶湯に接触する部分を鋳鉄や一体成形した窒化珪素セラミックスで構成したものが知られている。また、これらの部材の溶損を抑制するために、それらの材質の表面に窒化ホウ素(BN)等のコーティング材を塗布することが知られている。
【0003】
【発明が解決しようとする課題】
鋳鉄は、溶損が激しく、部材を頻繁に交換しなければならないという問題がある。この問題に対処する手段として、鋳鉄のアルミ溶湯に接する表面に窒化ホウ素等をコーティングする技術がある。しかし、コーティング材は、基材(鋳鉄)との熱膨張係数の違いにより剥がれやすく、頻繁な保守作業(コーティングのやり直し作業)が必要とされ、メンテナンスの点で問題がある。
【0004】
他方、窒化珪素セラミックス材料は、アルミ溶湯に対する耐久性に優れているが、複雑な形状を作製するのに適していない(高コストで作製も難しい)という問題がある。また、熱衝撃に弱く、頻繁にアルミニウム溶湯のくみ出し、流し出しが行われる部位に利用することには問題があった。
【0005】
また、ストークを加熱することで内部を移動する溶湯の温度が低下しないようにする構造が採用される場合があるが、鋳鉄でストークを構成した場合、加熱によりさらにストーク自体を傷めてしまうという問題がある。
【0006】
本発明は、上述したような問題を発生することがなく、アルミ溶湯に対する耐久性が高い新規なアルミ溶湯用ライニング材を提供することを課題とする。
【0007】
【課題を解決するための手段】
本発明はアルミ溶湯を扱う部材の表面にライニングする部材であって、該部材は、ムライト成分を80重量%以上含むアルミナシリカ長繊維でなるクロスと、アルミナシリカを主成分として調製したマトリックスとで構成されていることを要旨としている。
【0008】
アルミナシリカ繊維は、ムライト成分を80重量%以上含むものであることが好ましい。これはマトリックス中で生成されるムライト成分との共通性を高めることで、複合材料としての一体性を高めるために必要とされる。
【0009】
本発明におけるアルミナシリカ繊維は、アルミナ成分とシリカ成分でなるもの、あるいは両成分を主としたものとして定義される。
そして、ムライト成分を80重量%以上含むというのは、耐熱材料として実際に使用している状態におけるもの、あるいは焼成または高温環境下で耐熱材料として利用されることで、ムライト成分が生成され、その割合が80重量%以上となるようなアルミナシリカ繊維として定義される。
これは、本発明においては、実際に耐熱材料として使用する段階におけるアルミナシリカ繊維中のムライト成分の割合が重要であるからである。
【0010】
焼成前の段階や高温にさらされていない状態では、アルミナ成分とシリカ成分が所定の配合で含まれていてもムライト質を示さない、あるいはアルミナ成分とシリカ成分の配合割合から算出される割合でムライト成分が観察されないアルミナシリカ繊維も存在する。
【0011】
即ち、アルミナ成分とシリカ成分をムライト成分が生成される程度の配合で含んでいても、X線回折による結晶構造の観察において、ムライト成分のピークが観察されなかったり、ピークの強度が想定されるものより弱いアルミナシリカ繊維も存在する。
これは、繊維中において、アルミナ成分とシリカ成分がムライト成分と認められる結晶構造を構成しておらず、単に混在している状態(アルミナ成分とシリカ成分がムライト成分の生成に寄与していない状態)もあるからである。
【0012】
このような繊維であってもアルミナ成分とシリカ成分とが所定の配合で含まれていれば、1000℃以上の温度にさらされた状態でその配合割合に従ってムライト成分が生成される。即ち、焼成後、あるいは使用状態においてムライト成分が生成される。
このようなアルミナシリカ繊維もムライト成分が生成された状態において、その割合が80重量%以上となるものであれば、本発明における「ムライト成分を80重量%以上含むアルミナシリカ繊維」として使用することができる。
【0013】
アルミナシリカを主成分として調製したマトリックスは、配合時において、
▲1▼アルミナゾルバインダー
▲2▼アルミナ粒子とシリカ粒子、またはアルミナ粒子とムライト粒子、またはアルミナ粒子とシリカ粒子とムライト粒子、またはシリカ粒子とムライト粒子、またはムライト粒子
を必須の構成材料とする。
【0014】
この中で特に好ましいのは、アルミナ粒子とシリカ粒子の組み合わせである。この組み合わせの時に最もセラミックス複合体として最も高い耐熱性と強度が得られる。一般的な傾向として配合の段階でムライト粒子が含まれると強度が低下する。
【0015】
これは、アルミナ粒子とシリカ粒子の組み合わせにおいては、焼成時にムライト成分が生成され、それによりマトリックス中に骨格構造となる繊維のムライト成分との共通性が発現して繊維をマトリックスがしっかりと捕獲した強固な構造が得られることによる。
【0016】
他方で、予めムライト粒子が焼成の段階で配合されていると、焼成の段階でその分ムライト成分の生成が進行せず、上述した作用が損なわれて、セラミックス複合体としての強度が低下すると考えられる(ムライト粒子は安定でありそれ以上の反応が進みにくく、そのためマトリックスの緻密性が損なわれる)。
【0017】
なお、マトリックス中に含ませる充填剤としては、粒子以外に繊維や短繊維を単独あるいは複合して用いても良い。ただし、マトリックス中において均一に分散し、またマトリックスが骨格構造を構成する繊維間に十分に滲透するようにその寸法や混合割合を設定することが必要である。
【0018】
焼成後の使用状態において、マトリックス中におけるムライト成分は40重量%以上であることが好ましい。これは、骨格構造であるアルミナシリカ繊維とマトリックス材料との材質の共通性を得るために必要とされる。
【0019】
本発明の他の構成としては、アルミ溶湯を扱う部材の表面にライニングされる複合セラミックス材料であって、前記複合セラミックス材料が、耐熱性長繊維でなる骨格構造とアルミニウム塩を含むマトリックスとで構成されていることを要旨としている。
【0020】
上記構成においても耐熱性長繊維でなる骨格構造が、ムライト成分を80重量%以上含むアルミナシリカ長繊維でなるクロスであることが好ましい。
【0021】
アルミニウム塩としては、燐酸アルミニウム、塩基性乳酸アルミニウム、塩基性塩化アルミニウム、塩基性酢酸アルミニウムから選ばれた一種または複数種類の材料が用いられる。
なお、マトリックスは、アルミナやシリカ等の耐熱性粒子(あるいは繊維や短繊維)とアルミニウム塩でもって構成される。
【0022】
本発明のセラミックス複合体においては、骨格構造が6〜30重量%を占め、マトリックスが70〜94重量%を占めるようにすることが好ましい。骨格構造が占める割合が6重量%以下だと強度が得られず、また30重量%以上だとマトリックスの存在が部分的に疎になったりし、局部的に強度が低下したり、局部的な破壊を起こしやすくなるので好ましくない。
【0023】
本発明の他の構成は、アルミ溶湯を扱う部材の表面にライニングされる複合セラミックス材料であって、該材料は金属酸化物でなる連続繊維、金属酸化物粉体でなるフィラーおよびバインダーが主材とされ、構成物質の90重量%以上が金属酸化物または加熱により金属酸化物となる材料で占められていることを要旨とする。
【0030】
【発明の実施の形態】
本発明の好ましい実施の形態を図1に示す。図1に示す例では、アルミ溶湯用ストークにおいて、鋳造された金属構造体10の内面に複合セラミックス材料11のライニングを設けて構成している。金属構造体10と複合セラミックス材料11とのライニングとのあいだには、セラミックペーパー12、金網13が配設されている。
【0031】
金属構造体10は、安価な鋳鉄やステンレスが利用できる。また、セラミックス材料であってもよい。
本発明では、金属構造体10で示されるようなストーク等のアルミ溶湯を扱う部材は直接アルミ溶湯に接触しないので、広い範囲から材料を選択することができる。
【0032】
14は抵抗加熱ヒータである。この加熱ヒータは、ストークを外部から加熱し、ストーク内においてアルミ溶湯の温度が低下しないようにするためのものである。
加熱の手段としては、抵抗加熱ヒータによるもの以外に、ストークに誘導電流を誘起させてなる誘導加熱によるものやストークを直接火炎で加熱するものがある。
【0033】
ここで、金属構造体10は、ストークの形状を形作るものである。複合セラミックス材料11は、アルミ溶湯に対する耐性を発揮するライニング層として機能する。
【0034】
セラミックペーパー12と金網13とは、金属構造体10と複合セラミックス材料11の間で緩衝材として機能する。
この緩衝材は、溶湯の熱によって生じる金属構造体10の膨張を許容するための機能を有している。
【0035】
アルミ溶湯に対するライニング層である複合セラミックス材料11としては、以下の2通りのものが利用できる。
▲1▼第1のマトリックス材料
骨格構造としてムライト成分を80重量%以上含むアルミナシリカ長繊維でなるクロスを採用し、マトリックスとしてアルミナシリカを主成分とした粒子を充填剤とし、無機バインダーとしてアルミナゾルを用いたもの。
▲2▼第2のマトリックス材料
耐熱性長繊維でなる骨格構造とアルミニウム塩を含むマトリックスでなるもの。
複合セラミックス材料でなるライニング層の作製方法の概略を以下に示す。まず、▲1▼の作製方法の一例を示す。この場合、充填剤としてアルミナ粒子とシリカ粒子を用い、無機バインダーとしてアルミナゾルを用いる。またその他、有機バインダーを用いる。
【0036】
上記原材料を混合し、ペースト状であるマトリックスの出発材料を得る。このペースト状の出発材料をムライト成分が80重量%以上、好ましくは90重量%以上のアルミナシリカ繊維で編まれた連続繊維に塗布し、さらに乾燥と焼成を行って複合セラミックス材料を得る。ここで、アルミナシリカ繊維で編まれた連続繊維が骨格構造となる。
【0037】
一般に上記基本構造を多層に構成することで、必要な厚さのライニング材を確保することができる。
なお、骨格構造となるクロスは織布以外に不織布を用いることができる。
次に▲2▼の場合の作製工程の一例を示す。この場合、骨格構造は▲1▼の場合と同じであり、マトリックスとして、アルミナ粒子とシリカ粒子を充填剤として用い、無機バインダーとして燐酸アルミニウムまたは乳酸アルミニウムを用いる。
なお、複合セラミックス材料の作製方法は、▲1▼の場合と同じである。
【0038】
【実施例】
実施例1
図1に示すのは、アルミ溶湯用のライニングを内面に施したストークの断面の概略図である。図1において、ステンレスでなる鋳造して得た金属構造体10によってストークの外観及び構造が形成されている。
そして、その内面にシリカとアルミナの成分をそれぞれ50重量%含むセラミックス繊維をバインダーで結合させた厚さ1.5mmの複合セラミックス材料11がセラミックペーパー12、金網13を介して設けられている。また、ストークの外側には、抵抗加熱ヒータ14が配置されている。
【0039】
前記複合セラミックス材料11の作製方法を以下に示す。まず、骨格構造として、アルミナが68重量%、シリカが27重量%、酸化ホウ素が5重量%の組成を有し、使用時においてはムライト成分がほぼ94重量%以上である連続繊維でなるクロス(ニチアス社製CP−20)を用意する。
【0040】
次に、前記クロスに下記の配合でなるペースト状のマトリックスの出発材料を1500g/cm2の密度で塗布する。
アルミナ粒子(平均粒径5μm)(昭和電工A-42-2) 56重量%
アルミナ粒子(平均粒径1μm)(昭和電工AL160-SG-3) 15重量%
シリカ粉末(平均粒径1μm)(ホウリュウ化学H) 4重量%
アルミナゾル(日産化学)(AS520) 25重量%
有機酸(90%試薬) 0.5重量%(外掛け)
有機バインダー(5%水溶液) 4重量%(外掛け)
【0041】
なお、予めクロスを構成しているアルミナシリカ繊維を収束させている収束剤を分離させる処理を行い、繊維をほぐしておく。こうすることで、繊維にマトリックスの出発材料が良く含浸し、最終的に得られる複合セラミックス材料の材質が緻密となり、高強度が得られる。
【0042】
上記マトリックスの出発材料をクロスに1500g/cm2の密度で塗布する。この際、図1に示すストークの内面形状に合う型にクロスを押し付けながらマトリックスの出発材料を塗布する。そしてこれを3層に積層して厚さ1.5mmの複合体を得る。
前記複合体を100℃のオーブンで1時間乾燥させる。そしてその内表面(アルミ溶湯に接する面)にシリカゾルを塗布し、さらに乾燥させる。
【0043】
次に、1400℃で2時間の条件で焼成を行う。こうして図1の11a,11bで示される形状を有する複合セラミックス材料を得る。この複合セラミックス材料は、その内面にシリカゾルを塗布したことによるシリカ層が形成されており、気密性と強度が高められている。
【0044】
前記構成の複合セラミックス材料は、それを3cm角に切断し、700℃のアルミ溶湯に2ヶ月間浸漬しても何らの変質も観察されず、またアルミ溶湯に対する非濡れ性(アルミ溶湯を弾く性質)も失われないことが確認されている。なお、3cm角で厚さ2mmの鉄とステンレスのサンプルに対して同様な試験を課したところどちらも1日で溶損が進み焼失してしまうことが確認されている。
【0045】
前記複合セラミックス材料11a,11bをセラミックペーパー12及びステンレス金網13を介してステンレス構造体10の内側にはめ込む。こうして図1に示す構造を得る。
【0046】
本実施例で示すストークは、複合セラミックス材料11がアルミ溶湯に対する優れた耐性を発揮するので、従来構造に比較して、使用時間を伸ばすことができ、メンテナンス費用を低減することができる。
【0047】
また、前記複合セラミックス材料11自体が薄く、またセラミックペーパー12もその厚さが薄いので、ストーク内部での溶湯の温度低下を防止するための加熱をヒータ14によって行った場合に加熱を効果的に行うことができる。さらに、前記複合セラミックス材料11の耐熱性が高いので、外部からのストークの加熱による悪影響がほとんど現れないという優位性もある。
【0048】
実施例2
本実施例では、実施例1に示したマトリックスとして、下記の配合の出発材料を用いた例を示す。
アルミナ粒子(平均粒径5μm)(昭和電工A-42-2) 67重量%
燐酸アルミニウム液(多木化学製アシドホス75) 13重量%
水 20重量%
【0049】
なお、燐酸アルミニウム液はAl2O3とP2O5とのモル比が1:4のものを用いた。他の作製工程は実施例1の場合と同じである。
この複合セラミックス材料も、700℃のアルミ溶湯に2ヶ月間浸漬しても何らのも観察されず、またアルミ溶湯に対する非濡れ性(アルミ溶湯を弾く性質)も失われないことが確認されている。
【0050】
実施例3
本実施例は、実施例2に示すマトリックスの配合において、下記の配合を採用した場合の例である。他は実施例2と同様である。
アルミナ粉末(昭和電工(株)A-42-2) 100重量部
乳酸アルミニウム(多木化学(株)#2500F) 15重量部
増粘剤(昭和高分子(株)コーガムHW-62) 5重量部
水 20重量部
【0051】
実施例4
本実施例は、実施例1または実施例2に示す構成において、複合セラミックス材料の内面(アルミ溶湯に接触する面)に窒化ホウ素(BN)層をさらに設けた場合の例である。こうすることで、さらにアルミ溶湯に対する濡れ性を小さくでき、アルミ溶湯に対する耐性をさらに高めることができる。
なお、窒化ホウ素層が剥離しても基材となる複合セラミックス材料がアルミ溶湯に対する耐性を備えているので、特に問題とはならない。
また、BNマトリックス中に添加することで、複合セラミックス材料のアルミ溶湯に対する耐性を高めてもよい。
【0057】
上述した組成でなるサンプルの試験結果を下記表1に示す。なお、比較例は、厚さ10mmの窒化珪素平板(比較例1)と厚さ1.5mmの鉄板に窒化珪素被膜を溶射によって形成したもの(比較例2)である。
【表1】
【0058】
【発明の効果】
以上詳述したように、本発明によって構成した複合セラミックス材料をアルミ溶湯に対するライニング材として使用した構造にあっては、
(イ)アルミ溶湯に対する高い耐圧、
(ロ)高い非濡れ性、
が得られ、メンテナンス費用を低減することができる。
また、薄手である程度の熱の伝導を許容するので、加熱が必要とされるストーク等に利用した場合に外部からの加熱を効率良く行うことができる。
また、薄くて軽く扱いやすいので、取り付けやメンテナンスが容易で、また成形や切断加工が容易なので複雑な形状のものを容易に得ることができるという優位性がある。
【図面の簡単な説明】
【図1】本発明の一実施例を示すストークの断面構造図である。
【符号の説明】
11 11a,11b 複合セラミックス材料
10 ステンレス製のストーク構造
12 セラミックペーパー
13 ステンレス製金網
14 加熱用ヒータ[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a lining member used in a casting facility for aluminum (hereinafter simply referred to as aluminum). More specifically, the present invention relates to an improvement in a member that is lined to a portion where a molten aluminum is in contact with a member that handles the molten aluminum, such as stalk, ladle, jar, and hot water pool.
[0002]
[Prior art]
As for stalks, ladles, and the like in aluminum casting equipment, a structure in which a portion in contact with molten aluminum is made of cast iron or integrally formed silicon nitride ceramics is known. It is also known to apply a coating material such as boron nitride (BN) to the surface of these materials in order to suppress melting damage of these members.
[0003]
[Problems to be solved by the invention]
Cast iron has a problem that the melting damage is severe and the members must be frequently replaced. As a means for coping with this problem, there is a technique of coating boron nitride or the like on the surface in contact with the cast aluminum melt. However, the coating material is easily peeled off due to the difference in thermal expansion coefficient from the base material (cast iron), and frequent maintenance work (coating reworking work) is required, which is problematic in terms of maintenance.
[0004]
On the other hand, silicon nitride ceramic materials have excellent durability against molten aluminum, but have a problem that they are not suitable for producing complicated shapes (high cost and difficult to produce). In addition, it is vulnerable to thermal shock, and there has been a problem in using it for a portion where molten aluminum is frequently drawn and poured out.
[0005]
In addition, there is a case where a structure is employed in which the temperature of the molten metal moving inside is not lowered by heating the stalk, but when the stalk is made of cast iron, the stalk itself is further damaged by the heating. There is.
[0006]
This invention makes it a subject to provide the novel lining material for molten aluminum which does not generate | occur | produce the problem as mentioned above but has high durability with respect to molten aluminum.
[0007]
[Means for Solving the Problems]
The present invention is a member that is lined on the surface of a member that handles molten aluminum, the member comprising a cloth made of alumina silica long fibers containing 80% by weight or more of a mullite component, and a matrix prepared using alumina silica as a main component. The gist is that it is composed.
[0008]
The alumina silica fiber preferably contains 80% by weight or more of a mullite component. This is required to increase the unity as a composite material by increasing the commonality with the mullite component produced in the matrix.
[0009]
The alumina silica fiber in the present invention is defined as one composed of an alumina component and a silica component, or mainly composed of both components.
And, when the mullite component is contained in an amount of 80% by weight or more, the mullite component is generated by using the mullite component in a state where it is actually used as a heat-resistant material, or by being used as a heat-resistant material in a fired or high-temperature environment It is defined as an alumina silica fiber whose ratio is 80% by weight or more.
This is because, in the present invention, the proportion of the mullite component in the alumina silica fiber at the stage where it is actually used as a heat resistant material is important.
[0010]
In the stage before firing or in a state not exposed to high temperature, even if the alumina component and the silica component are included in the prescribed blending, it does not show mullite quality, or is a ratio calculated from the blending ratio of the alumina component and the silica component. There are also alumina silica fibers in which no mullite component is observed.
[0011]
That is, even when the alumina component and the silica component are included in such a composition that the mullite component is generated, the peak of the mullite component is not observed or the peak intensity is assumed in the observation of the crystal structure by X-ray diffraction. There are also alumina silica fibers that are weaker than those.
This is because the fiber does not constitute a crystal structure in which the alumina component and the silica component are recognized as mullite components, but is simply mixed (the alumina component and the silica component do not contribute to the generation of the mullite component). Because there is also.
[0012]
Even in such a fiber, if an alumina component and a silica component are contained in a predetermined composition, a mullite component is generated in accordance with the composition ratio in a state where the fiber is exposed to a temperature of 1000 ° C. or higher. That is, a mullite component is generated after firing or in use.
Such alumina silica fibers should be used as “alumina silica fibers containing 80% by weight or more of the mullite component” in the present invention if the ratio is 80% by weight or more when the mullite component is generated. Can do.
[0013]
The matrix prepared with alumina silica as the main component is
(1) Alumina sol binder (2) Alumina particles and silica particles, or alumina particles and mullite particles, or alumina particles and silica particles and mullite particles, or silica particles and mullite particles, or mullite particles are essential constituent materials.
[0014]
Among these, a combination of alumina particles and silica particles is particularly preferable. In this combination, the highest heat resistance and strength as the ceramic composite can be obtained. As a general tendency, the strength decreases when mullite particles are included in the blending stage.
[0015]
This is because, in the combination of alumina particles and silica particles, a mullite component is generated at the time of firing, thereby expressing the commonality with the mullite component of the fiber that becomes a skeleton structure in the matrix, and the fibers are firmly captured by the matrix. This is because a strong structure is obtained.
[0016]
On the other hand, if the mullite particles are blended in advance in the firing stage, the generation of mullite components does not proceed correspondingly in the firing stage, the above-described action is impaired, and the strength as a ceramic composite is considered to decrease. (The mullite particles are stable and the reaction does not proceed further, so the denseness of the matrix is impaired).
[0017]
In addition, as a filler contained in the matrix, fibers or short fibers other than particles may be used alone or in combination. However, it is necessary to set the dimensions and mixing ratio so that the matrix is uniformly dispersed in the matrix and the matrix is sufficiently permeated between the fibers constituting the skeleton structure.
[0018]
In the use state after firing, the mullite component in the matrix is preferably 40% by weight or more. This is required in order to obtain the commonality of the alumina silica fiber which is a skeleton structure and the matrix material.
[0019]
Another structure of the present invention is a composite ceramic material lined on the surface of a member that handles molten aluminum, wherein the composite ceramic material is composed of a skeleton structure composed of heat-resistant long fibers and a matrix containing an aluminum salt The gist of this is.
[0020]
Also in the above configuration, the skeleton structure made of heat-resistant long fibers is preferably a cloth made of alumina silica long fibers containing 80% by weight or more of a mullite component.
[0021]
As the aluminum salt, one or more kinds of materials selected from aluminum phosphate, basic aluminum lactate, basic aluminum chloride, and basic aluminum acetate are used.
The matrix is composed of heat-resistant particles (or fibers and short fibers) such as alumina and silica and an aluminum salt.
[0022]
In the ceramic composite of the present invention, it is preferable that the skeleton structure occupies 6 to 30% by weight and the matrix occupies 70 to 94% by weight. If the proportion of the skeletal structure is 6% by weight or less, the strength cannot be obtained, and if it is 30% by weight or more, the presence of the matrix is partially sparse, the strength is locally reduced, or the local It is not preferable because it tends to cause destruction.
[0023]
Another structure of the present invention is a composite ceramic material that is lined on the surface of a member that handles molten aluminum, and the material is mainly composed of continuous fibers made of metal oxide, filler made of metal oxide powder, and a binder. In summary, 90% by weight or more of the constituent material is occupied by a metal oxide or a material that becomes a metal oxide by heating.
[0030]
DETAILED DESCRIPTION OF THE INVENTION
A preferred embodiment of the present invention is shown in FIG. In the example shown in FIG. 1, in the molten aluminum stalk, the inner surface of a
[0031]
As the
In the present invention, since the member that handles the molten aluminum such as stalk as shown by the
[0032]
As a heating means, there are those by induction heating in which induction current is induced in stalk and those in which stalk is directly heated by a flame, in addition to those by a resistance heater.
[0033]
Here, the
[0034]
The
This buffer material has a function for allowing expansion of the
[0035]
As the composite
(1) As a first matrix material skeleton structure, a cloth composed of alumina silica long fibers containing 80% by weight or more of a mullite component is employed, particles containing alumina silica as a main component as a matrix as a filler, and alumina sol as an inorganic binder. What was used.
(2) Second matrix material A matrix structure comprising a heat-resistant long fiber and a matrix containing an aluminum salt.
An outline of a method for producing a lining layer made of a composite ceramic material is shown below. First, an example of the manufacturing method of (1) is shown. In this case, alumina particles and silica particles are used as the filler, and alumina sol is used as the inorganic binder. In addition, an organic binder is used.
[0036]
The raw materials are mixed to obtain a matrix starting material that is in the form of a paste. This pasty starting material is applied to continuous fibers knitted with alumina silica fibers having a mullite component of 80% by weight or more, preferably 90% by weight or more, followed by drying and firing to obtain a composite ceramic material. Here, the continuous fiber knitted with the alumina silica fiber has a skeleton structure.
[0037]
Generally, a lining material having a necessary thickness can be secured by forming the basic structure in multiple layers.
In addition, the cloth used as a skeleton structure can use a nonwoven fabric other than a woven fabric.
Next, an example of a manufacturing process in the case of (2) is shown. In this case, the skeleton structure is the same as in the case of (1), alumina particles and silica particles are used as a matrix as a matrix, and aluminum phosphate or aluminum lactate is used as an inorganic binder.
The method for producing the composite ceramic material is the same as in the case of (1).
[0038]
【Example】
Example 1
FIG. 1 is a schematic view of a cross section of a stalk having an inner surface provided with a lining for molten aluminum. In FIG. 1, the appearance and structure of Stoke are formed by a
A composite
[0039]
A method for producing the composite
[0040]
Next, a pasty matrix starting material having the following composition is applied to the cloth at a density of 1500 g / cm 2 .
Alumina particles (average particle size 5μm) (Showa Denko A-42-2) 56% by weight
Alumina particles (average particle size 1μm) (Showa Denko AL160-SG-3) 15% by weight
Silica powder (average particle size 1 μm) (Horyu Chemical H) 4% by weight
Alumina sol (Nissan Chemical) (AS520) 25% by weight
Organic acid (90% reagent) 0.5% by weight (outer)
Organic binder (5% aqueous solution) 4% by weight (outer)
[0041]
In addition, the process which isolate | separates the sizing agent which has converged the alumina silica fiber which comprises the cloth previously is performed, and the fiber is loosened. By doing so, the fibers are well impregnated with the matrix starting material, the material of the finally obtained composite ceramic material becomes dense, and high strength is obtained.
[0042]
The matrix starting material is applied to the cloth at a density of 1500 g / cm 2 . At this time, the matrix starting material is applied while pressing the cloth against a mold that matches the inner shape of the Stokes shown in FIG. And this is laminated | stacked on three layers and the composite body of thickness 1.5mm is obtained.
The composite is dried in an oven at 100 ° C. for 1 hour. And silica sol is apply | coated to the inner surface (surface which contacts aluminum molten metal), and it is made to dry further.
[0043]
Next, baking is performed at 1400 ° C. for 2 hours. Thus, a composite ceramic material having the shape shown by 11a and 11b in FIG. 1 is obtained. This composite ceramic material has a silica layer formed by applying a silica sol to the inner surface thereof, and has improved airtightness and strength.
[0044]
The composite ceramic material having the above structure is cut into a 3 cm square and immersed in a molten aluminum at 700 ° C. for 2 months. No deterioration is observed, and the non-wetting property (a property of repelling the molten aluminum) with respect to the molten aluminum. ) Has also been confirmed not to be lost. In addition, when a similar test was applied to a 3 cm square and 2 mm thick iron and stainless steel sample, it was confirmed that both of them melted and burned out in one day.
[0045]
The composite
[0046]
In the stalk shown in this embodiment, since the composite
[0047]
Further, since the composite
[0048]
Example 2
In this example, as the matrix shown in Example 1, an example using starting materials having the following composition is shown.
Alumina particles (average particle size 5μm) (Showa Denko A-42-2) 67% by weight
Aluminum phosphate solution (Acidphos 75, manufactured by Taki Chemical) 13% by weight
20% by weight of water
[0049]
The aluminum phosphate solution used had a molar ratio of Al 2 O 3 and P 2 O 5 of 1: 4. Other manufacturing steps are the same as those in the first embodiment.
Even when this composite ceramic material is immersed in a molten aluminum at 700 ° C. for 2 months, nothing is observed, and it has been confirmed that the non-wetting property (the property of repelling the molten aluminum) with respect to the molten aluminum is not lost. .
[0050]
Example 3
This example is an example in which the following formulation is adopted in the formulation of the matrix shown in Example 2. Others are the same as in the second embodiment.
Alumina powder (Showa Denko A-42-2) 100 parts by weight Aluminum lactate (Taki Chemical Co., Ltd. # 2500F) 15 parts by weight Thickener (Showa Polymer Co., Ltd. Kogham HW-62) 5 parts by weight 20 parts by weight of water [0051]
Example 4
This example is an example in which a boron nitride (BN) layer is further provided on the inner surface of the composite ceramic material (the surface in contact with the molten aluminum) in the configuration shown in Example 1 or Example 2. By doing so, the wettability with respect to the molten aluminum can be further reduced, and the resistance to the molten aluminum can be further increased.
Even if the boron nitride layer is peeled off, there is no particular problem because the composite ceramic material serving as the base material has resistance against molten aluminum.
Moreover, you may improve the tolerance with respect to molten aluminum of composite ceramic material by adding in a BN matrix.
[0057]
Table 1 shows the test results of the sample having the above-described composition. In the comparative example, a silicon nitride flat plate (Comparative Example 1) having a thickness of 10 mm and an iron plate having a thickness of 1.5 mm are formed by thermal spraying (Comparative Example 2).
[Table 1]
[0058]
【The invention's effect】
As detailed above, in the structure using the composite ceramic material constructed according to the present invention as a lining material for molten aluminum,
(I) High pressure resistance against molten aluminum,
(B) High non-wetting,
Thus, maintenance costs can be reduced.
In addition, since it is thin and allows heat conduction to a certain extent, it can be efficiently heated from the outside when used for stalk or the like that requires heating.
In addition, since it is thin and light and easy to handle, it is easy to mount and maintain, and since it is easy to form and cut, it has the advantage of being able to easily obtain a complex shape.
[Brief description of the drawings]
FIG. 1 is a sectional structural view of Stoke showing an embodiment of the present invention.
[Explanation of symbols]
11 11a, 11b Composite
Claims (6)